The present invention relates to methods for forming a metal oxide surface on a metal layer, and more particularly, to methods for forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state.
The metal layer(s) in a semiconductor device are usually damaged from exposure of the metal layer to oxygen during the dielectric etching process. Even though the metal oxide created from the oxygen exposure is removed, for example, with an acidic solution, the exposure results in substantial diffusion and penetration of oxygen into the metal layer. Moreover, extensive metal oxide formation and subsequent removal can easily result in retrograde profiles in a structure, which will reduce the amount of metal available for assembly plating and wire bonding.
Thus there remains a need to develop methods for limiting oxidation to the surface of the metal layer to not only minimize the diffusion and penetration of oxygen in the metal layer, but also to avoid substantial reduction in the amount of metal available for assembly plating and wire bonding.
These needs are met by embodiments of the present invention that provide methods for forming a metal oxide surface on a metal layer that is enriched with metal oxide in its higher oxidation state.
In accordance with one embodiment of the present invention, a method of forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state is provided. The method comprises: providing a metal layer; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. The step of forming the enriched metal oxide surface comprises: oxidizing the metal layer to form a metal oxide surface, wherein the metal oxide surface comprises metal oxide in a first oxidation state; reducing the metal oxide surface, wherein the reduced metal oxide surface comprises metal oxide in a first oxidation state and metal atom; and re-oxidizing the reduced metal oxide surface to form a metal oxide surface that is enriched with metal oxide in its higher oxidation state, wherein the enriched metal oxide surface comprises metal oxide in a first oxidation state and metal oxide in a second oxidation state. The metal comprises at least two oxidation states.
In accordance with another embodiment of the present invention, a method of forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state is provided. The method comprises: providing a semiconductor substrate assembly comprising a metal layer and a dielectric layer; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. The step of forming the enriched metal oxide surface comprises: etching the dielectric layer thereby resulting in exposure of the metal layer, wherein the exposure of the metal layer creates a metal oxide surface comprising a metal oxide in a first oxidation state; reducing the metal oxide surface, wherein the reduced metal oxide surface comprises metal oxide in a first oxidation state and metal atom; and oxidizing the reduced metal oxide surface to form a metal oxide surface that is enriched with metal oxide in its higher oxidation state, wherein the enriched metal oxide surface comprises metal oxide in a first oxidation state and metal oxide in a second oxidation state. The metal comprises at least two oxidation states.
In accordance with another embodiment of the present invention, a method of forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state is provided. The method comprises: providing a metal layer with metal oxide surface, wherein the metal oxide surface comprises metal oxide in a first oxidation state; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. The step of forming the enriched metal oxide surface comprises: reducing the metal oxide surface layer, wherein the reduced metal oxide surface layer comprises metal oxide in a first oxidation state and metal atom; and oxidizing the reduced metal oxide surface to form a metal oxide surface that is enriched with metal oxide in its higher oxidation state, wherein the enriched metal oxide surface comprises metal oxide in a first oxidation state and metal oxide in a second oxidation state. The metal comprises at least two oxidation states.
In accordance with another embodiment of the invention, a method of forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state is provided. The method comprises: providing a metal layer; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. The step of forming the enriched metal oxide surface comprises oxidizing and reducing the metal oxide surface layer repeatedly until the metal oxide surface is enriched with metal oxide in its higher oxidation state. The metal comprises at least two oxidation states.
In accordance with another embodiment of the present invention, a method of forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state is provided. The method comprises: providing a metal layer with a metal oxide surface, wherein the metal oxide surface comprises metal oxide in a first oxidation state; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer, wherein the step of forming the enriched metal oxide surface comprises reducing and oxidizing the metal oxide surface layer repeatedly until the metal oxide surface is enriched with metal oxide in its higher oxidation state. The metal comprises at least two oxidation states.
In accordance with another embodiment of the present invention, a metal oxide surface that is enriched with metal oxide in its higher oxidation state comprises: a metal layer; and a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. The enriched metal oxide surface comprises metal oxide in a first oxidation state and metal oxide in a second oxidation state.
The present invention is directed to methods for forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state for use in a semiconductor device. The methods of the present invention limit diffusion and penetration of oxygen into the metal layer by providing a metal oxide surface that is enriched with metal oxide in its higher oxidation state. This enriched metal oxide surface is a more stable oxide and therefore promotes less net oxidation over time by protecting the underlying metal layer.
In one embodiment, the methods comprise providing a metal layer supported by a semiconductor substrate; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. One skilled in the art will appreciate the various metal layers which may be used in accordance with the present invention, any of which may be employed herein. In one embodiment, the metal layer comprises a metal with at least two oxidation states. Examples of metal which have at least two oxidation states include, but are not limited to, copper, silver, gold, pulladium platinum and nickel. For purposes of defining and describing the invention, the term “semiconductor substrate” is defined to mean any construction comprising semiconductive materials including, but not limited to, bulk semiconductive materials such as a semiconductive wafer, either alone or in assemblies comprising other materials thereon, and semiconductive material layers, either along or in assemblies comprising other materials. For purposes of defining and describing the invention, the term “substrate” refers to any supporting structure including but not limited to the semiconductor substrates described above. One skilled in the art will appreciate the various materials that can be used to make a semiconductor substrate, any of which may be employed herein. For example, the semiconductor substrate may be made of silicon or any other semiconductive material.
After the metal layer supported by the semiconductor substrate is provided, a metal oxide surface that is enriched with metal oxide in its higher oxidation state is formed on the metal layer. Specifically, the method of forming the enriched metal oxide surface comprises oxidizing the metal layer to form a metal oxide surface, wherein the metal oxide surface comprises metal oxide in a first oxidation state; reducing the metal oxide surface, wherein the reduced metal oxide surface comprises metal oxide in a first oxidation state and metal ion; and oxidizing the reduced metal oxide surface to form a metal oxide surface that is enriched with metal oxide in its higher oxidation state, wherein the enriched metal oxide surface comprises metal oxide in a first oxidation state and metal oxide in a second oxidation state. In another embodiment, the step of forming the enriched metal oxide surface comprises oxidizing and reducing the metal oxide surface layer repeatedly until the metal oxide surface is enriched with metal oxide in its higher oxidation state.
One skilled in the art will appreciate the various methods which may be used for oxidizing and reducing steps to form the enriched metal oxide surface, any of which may be employed herein. In one embodiment, the step of forming the enriched metal oxide surface is performed in a plasma processing chamber. Accordingly, in one embodiment, the step of oxidizing the metal layer and/or oxidizing the reduced metal oxide surface in a plasma processing chamber comprises: flowing an oxidizing gas mixture comprising at least one oxygen contain gas into the plasma processing chamber; striking a plasma in the plasma processing chamber from the oxidizing gas mixture to form an oxidizing plasma; and utilizing the oxidizing plasma to oxidize the metal layer. Alternatively, the step of oxidizing the metal layer and/or oxidizing the reduced metal oxide surface in a plasma processing chamber comprises oxidizing the metal layer to form a metal oxide surface in the plasma processing chamber comprises flowing an oxidizing gas mixture comprising at least one oxygen containing gas and at least one inert gas into the plasma processing chamber; striking a plasma in the plasma processing chamber from the oxidizing gas mixture to form an oxidizing plasma; and utilizing the oxidizing plasma to oxidize the metal layer. In either oxidation method discussed above, the step of reducing the metal oxide surface in a plasma processing chamber comprises: flowing a reducing gas mixture comprising at least one hydrogen containing gas and at least one inert gas into the plasma processing chamber; striking a plasma in the plasma processing chamber from the reducing gas mixture to form a reducing plasma; and utilizing the reducing plasma to reduce the metal oxide surface.
Additionally, in the oxidation and reduction steps discussed in detail above, one skilled in the art will appreciate the various inert gases which may be employed, any of which may be used herein. In one embodiment, the inert gas is selected from the group consisting of argon and nitrogen. Moreover, the oxidizing plasma and/or the reducing plasma may be removed from the plasma processing chamber after the respective oxidizing or reducing step is performed.
The present invention is also directed to methods which comprise providing a semiconductor substrate assembly comprising a metal layer and a dielectric layer and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. For purposes of defining and describing the invention, the term “semiconductor substrate assembly” refers to a semiconductor substrate having one or more layers or structures formed thereon. In addition, one skilled in the art will appreciate the various materials which may be employed for the dielectric layer, any of which may be used herein.
In methods comprising a semiconductor substrate assembly, in accordance with the present invention, the first oxidation step is performed by etching the dielectric layer which results in exposure of the metal layer. The exposure of the metal layer creates a metal oxide surface which comprises metal oxide in a first oxidation state. One skilled in the art will appreciate the various means for etching a dielectric layer, any of which may be employed herein. In one embodiment, the etching is performed by an isotropic etch. In addition, as discussed in detail above, the subsequent reduction and oxidation steps may be performed by any methods known in the art. In one embodiment, the subsequent reduction and oxidation steps are conducted in a plasma processing chamber, which steps are discussed in detail above. Moreover, the subsequent reduction and oxidation steps may also be performed repeatedly until the metal oxide surface is enriched with metal oxide in its higher oxidation state.
The present invention is also directed to methods which comprise providing a metal layer with a metal oxide surface supported by a semiconductor substrate, wherein the metal oxide surface comprises metal oxide in a first oxidation state; and forming a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. In such methods, the subsequent reduction and oxidation steps may be performed by any means known in the art. In one embodiment, the subsequent reduction and oxidation steps are performed in a plasma processing chamber, which steps as discussed in detailed above. Moreover, the subsequent reduction and oxidation steps may also be performed repeatedly until the metal oxide surface is enriched with metal oxide in its higher oxidation state.
The invention is also directed to a metal oxide surface that is enriched with metal oxide in its higher oxidation state for use in a semiconductor device which comprises: a metal layer supported by a semiconductor substrate; and a metal oxide surface that is enriched with metal oxide in its higher oxidation state on the metal layer. The enriched metal oxide surface comprises metal oxide in a first oxidation state and metal oxide in a second oxidation state.
In each of the various embodiments of the present invention, set out in detail above, the steps of reducing and oxidizing the metal oxide surface may be conducted for about 5 to about 30 seconds. In another embodiment, each step of reducing and oxidizing the metal oxide surface is conducted for about 10 seconds. In addition, the metal oxide surface may be between about 20 Å to about 50 Å thick. In another embodiment the metal oxide surface may be between about 20 Å to about 30 Å thick.
In order that the invention may be more readily understood, reference is made to the following examples, which are intended to be illustrative of the invention, but are not intended to be limiting in scope.
A copper bond pad surface was cleaned in a plasma processing chamber. The copper layer was exposed to an oxidizing plasma followed by a reducing plasma comprising hydrogen gas and nitrogen gas. X-ray photoelectron spectroscopy (XPS) was used to determine the oxidation state(s) of the copper surface layer.
A copper bond pad surface was cleaned in a plasma processing chamber. The copper layer was exposed to was exposed to three alternating oxidation and reduction sequences of an oxidizing plasma followed by a reducing plasma comprising hydrogen gas and nitrogen gas in accordance with an embodiment of the present invention. X-ray photoelectron spectroscopy (XPS) was used to determine the oxidation state(s) of the copper surface layer.
While certain representative embodiments and details have been shown for the purpose of illustrating the invention, it will be apparent to those skilled in the art that various changes in the methods and apparatus disclosed herein may be made without departing from the scope of the invention, which is defined in the appended claims.
This application is a divisional application of U.S. application Ser. No. 11/487,080, filed Jul. 14, 2006 entitled “METHODS FOR FORMING AN ENRICHED METAL OXIDE SURFACE,” now U.S. Pat. No. 7,396,774, issued Jul. 8, 2008, and U.S. application Ser. No. 10/929,173 filed Aug. 30, 2004 entitled “METHODS FOR FORMING AN ENRICHED METAL OXIDE SURFACE FOR USE IN A SEMICONDUCTOR DEVICE,” U.S. Pat. No. 7,166,542, issued Jan. 23, 2007. The entire contents of those applications are incorporated by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5468445 | Casey et al. | Nov 1995 | A |
| 6143657 | Liu et al. | Nov 2000 | A |
| 6261953 | Uozumi | Jul 2001 | B1 |
| 6319842 | Khosla et al. | Nov 2001 | B1 |
| 6380083 | Gross | Apr 2002 | B1 |
| 6417112 | Peyne et al. | Jul 2002 | B1 |
| 6602653 | Geusic et al. | Aug 2003 | B1 |
| 20020027261 | Besser et al. | Mar 2002 | A1 |
| 20020053461 | Leijon et al. | May 2002 | A1 |
| 20030034251 | Chikarmane et al. | Feb 2003 | A1 |
| 20030227073 | Yurino | Dec 2003 | A1 |
| 20040084670 | Tripsas et al. | May 2004 | A1 |
| 20040152336 | Miura et al. | Aug 2004 | A1 |
| 20040159835 | Krieger et al. | Aug 2004 | A1 |
| 20040160801 | Krieger et al. | Aug 2004 | A1 |
| 20040207056 | Seki et al. | Oct 2004 | A1 |
| 20040217347 | Tripsas et al. | Nov 2004 | A1 |
| 20040227242 | Noguchi et al. | Nov 2004 | A1 |
| 20050006643 | Lan et al. | Jan 2005 | A1 |
| 20050030823 | Tsuyuno et al. | Feb 2005 | A1 |
| 20050048794 | Brask et al. | Mar 2005 | A1 |
| 20050189041 | Mantese et al. | Sep 2005 | A1 |
| 20050250332 | Hwu et al. | Nov 2005 | A1 |
| 20090078583 | Kobata et al. | Mar 2009 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20080254314 A1 | Oct 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11487080 | Jul 2006 | US |
| Child | 12146077 | US | |
| Parent | 10929173 | Aug 2004 | US |
| Child | 11487080 | US |