The present invention is directed to devices and methods of fabricating devices utilizing deposition printers and, more specifically, to printed circuits and methods of fabricating such printed circuits. In addition, the present invention involves utilization of deposition printers to fabricate RFID devices, such as RFID antennas.
It is a first aspect of the present invention to provide a method of fabricating a printed circuit comprising: (a) depositing a first conductive material to form a first conductive pathway upon a substrate; (b) depositing a dielectric material directly over at least a first portion of the conductive pathway utilizing an electrophotographic process; and (d) depositing a second conductive material over at least a portion of the dielectric material to form a second conductive pathway, where the second conductive pathway is in electrical communication with the first conductive pathway.
It is a second aspect of the present invention to provide a method of fabricating a printed circuit comprising: (a) depositing a conductive material to form a first conductive pathway upon a substrate; (b) depositing a dielectric material in contact with at least a first portion of the first conductive pathway; and (c) depositing a conductive material directly over the dielectric material to form a second conductive pathway in a stacked structure, where the act of depositing a dielectric material in contact with at least a first portion of the first conductive pathway includes the act of vertically electrically insulating the first portion of the conductive pathway from the second conductive pathway.
It is a third aspect of the present invention to provide an RFID antenna, comprising: (a) a first conductive material forming a first conductive pathway; (b) a dielectric material directly contacting a portion of the first conductive pathway and likewise leaving exposed a portion of the first conductive pathway; and (c) a second conductive material directly in concurrent contact with the first conductive material and the dielectric material, where a majority of the second conductive material is vertically elevated and physically separated from the majority of the first conductive material.
The exemplary embodiments of the present invention are described and illustrated below to encompass methods of fabricating printed circuits as well as the resulting products of such methods. Of course, it will be apparent to those of ordinary skill in the art that the preferred embodiments discussed below are exemplary in nature and may be reconfigured without departing from the scope and spirit of the present invention. However, for clarity and precision, the exemplary embodiments as discussed below may include optional steps, methods, and features that one of ordinary skill should recognize as not being a requisite to fall within the scope of the present invention.
Referencing
Those skilled in the art are aware that inkjet printing apparatus, such as inkjet printers, utilize a fluid-based ink comprising pigments and dyes disbursed in a carrier fluid. Some inkjet printers utilize thermal inkjet technology having thermal resistors that are selectively energized and are operative to vaporize a portion of the carrier fluid approximate a nozzle to create a bubble that forces a droplet of ink from the nozzle. This technique is repeated numerous times a second, along with repositioning of the nozzles, to deposit droplets of ink upon a substrate in a predetermined pattern. As the carrier fluid evaporates, the pigment is left behind on the surface of the substrate to form an image, while the dye tends to penetrate into the surface. Exemplary images include, without limitation, alpha-numeric characters, diagrams, bar codes, and fanciful pictures. Another subset of inkjet printers utilizes piezoelectric actuators to expel droplets of ink from inkjet nozzles. The piezoelectric actuators are subjected to an applied voltage causing the actuators to deform and physically push the ink from the nozzle analogous to a paddle in water. It is to be understood, however, that when the exemplary embodiments of the present invention refer to inkjet printers, the invention is not limited to printers utilizing piezoelectric actuators or thermal resistors for depositing droplets of ink onto a substrate. Moreover, the inkjet printers referenced in the explanation of the instant invention utilize inks comprising a carrier fluid and a particulate component having conductive or insulative properties depending upon the intended application.
Those skilled in the art are also aware that an electrophotographic process, such as used in laser printers, utilize toner to form images upon a substrate. More specifically, the electrophotographic process utilizes the common principal that oppositely charged materials attract one another, and that more highly/densely charged materials will attract oppositely charged materials to a greater extent than lower/ less densely charged materials. In a very simplistic explanation of how a typical laser printer operates, for example, a revolving drum is charged, opposite to that of the toner, to form a mirror image of the eventual image to be printed upon the substrate. As the drum is rotated, the opposite charge of the image portions of the drum attract toner particles. These toner particles are then in the form of a mirror image on the drum and are brought into contact with a more highly charged substrate so that the toner is attracted to the substrate. Thus, the toner leaves the drum and becomes deposited onto the substrate to form the image. Optionally, the toner may be heated or fused to bind the toner to the substrate using a pair of heated rollers through which the substrate is compressed and conveyed. It is to be understood, however, that when the exemplary embodiments of the present invention refer to laser printers, the invention is not limited to printers utilizing a revolving drum for depositing charged toner onto a substrate, nor necessarily requires printers incorporating fusers. Moreover, the laser printers referenced in the explanation of the instant invention utilize toners comprising waxes and particulate components, where the particulate components have conductive or insulative properties depending upon the intended application.
In this first exemplary circuit 10, the conductive pathways 12, 14, 16, 18 are formed using an inkjet ink that includes conductive particles distributed throughout the carrier fluid. The conductive particles comprise one or more materials operative to conduct electrical current; i.e., materials having a relatively low resistance to the flow of electric current. Thus, the conductive particles may be chosen from a plethora of conductive materials, where the conductive material is reduced to particles having sizes less than the inkjet nozzle cross-sectional area. Otherwise, the particles will be too large and plug the plumbing of the inkjet conduits feeding the nozzles. The carrier fluid, in which the conductive particles are disbursed, may be organic or inorganic, polar or non-polar, and, for purposes of explanation only, is a water-based fluid in the exemplary embodiments. However, solvent based inks may also be used with inkjet printers, such as those equipped with piezoelectric actuators. Exemplary conductive inks for use with the present invention include silver ink, copper ink, and gold inks available from Nippon Kayaku America Inc., and Cima NanoTech, Inc. (www.cimananotech.com). For purposes of explanation, conductive particles will generally have particle sizes ranging between five and two hundred nanometers. Nevertheless, the particle size must be compatible with the dimensions of the nozzle openings of the inkjet printer to ensure that large particles do not clog the nozzles. In other words, larger particles can be printed with larger opening nozzles, where as small particles can be printed using larger opening nozzles of smaller opening nozzles.
Referring to
An inkjet printer (not shown) can be utilized to deposit droplets of a conductive ink onto the substrate 20 in a pattern to create the first conductive pathway 12. The pattern derives from the orientation established by a programmer and automatically rendered by a computer software package after the programmer inputs a series of design rules providing a metes and bounds for the layout of the circuit 10. The computer software package compiles an electronic design file with instructions specific to a printer engine, where the instructions characterize the location (in two dimensions) upon the substrate where conductive ink should be deposited and the frequency with which conductive ink should be deposited at a given location (thickness; i.e., a third dimension) to eventually form the conductive pathways 12, 14, 16, 18. Likewise, the electronic design file may also include instructions regarding the location (in two dimensions) upon the substrate where dielectric and/or ink receiving layer material should be deposited and the frequency with which the dielectric and/or ink receiving layer material should be deposited at a given location (thickness; i.e., a third dimension) to isolate the conductive pathways and possibly provide vias to receive the conductive ink and also to provide porosity or channels to divert the carrier fluid in subsequent depositions of conductive ink if necessary. When multiple printers are utilized to deposit the conductive ink, the dielectric material, the ink receiving layer and the “electronic design file” may actually comprise two or more design files separate and distinct from one anther with instructions specifically designed for each printer utilized. Those of ordinary skill should be familiar with the computer software packages and the general concept of design rules sufficient to program and bring about an electronic representation of an exemplary printed circuit 10 by following the teachings of the present invention.
In accordance with the instructions embedded in the electronic design file, the printer engine of the inkjet printer orients at least one of the substrate 20 and the printer nozzles to initiate the deposition sequence. Once the printer nozzles are oriented with respect to the substrate 20 at a starting location, the deposition instructions are carried out by the printer to selectively deposit droplets of conductive ink onto the substrate, thereby forming the first conductive pathway 12 on the top of the substrate 20.
The highly uniform nature of the ceramic particles 24 comprising the first layer of the substrate 20 provide relatively uniform channels 28 or pore volume between the ceramic particles for the diversion of the carrier fluid from the conductive particles. As droplets of conductive ink are deposited onto the surface of the ceramic particles, a portion of the carrier fluid from each droplet is immediately drawn into one or more of the channels 28 or pores. This diversion of the carrier fluid acts to decrease the surface area of the substrate 20 that the droplet covers. This substrate and its associated diversion layer of silica 24 is in contrast to a substrate where the bulk of the fluid is retained on the surface of the substrate for a significant period of time, which allows the droplet to spread outward after initially contacting the substrate and further cover a greater surface area with a droplet having an analogous volume. It should be noted that the silica can be supplemented or replaced by alumina.
A vacuum may be applied to the substrate 20 during and/or after droplet deposition to further draw the carrier fluid away from the conductive particles. In this manner, the lower pressure area created by the vacuum draws the carrier fluid downward and into the channels 28 at a faster rate than by mere gravitational feed teamed with capillary actions. The vacuum also helps reduce the footprint of the ink droplet to allow a greater density of conductive particles to be deposited at a given location.
It is also within the scope of the invention that the substrate 20, having the conductive ink deposited thereon, be placed in an elevated temperature environment to hasten evaporation of the carrier fluid. This technique may be used independent of the vacuum discussed above or in combination with the vacuum. An exemplary elevated temperature environment can be brought about by placing the substrate 20 in proximity to a heat or light source such as, without limitation, a furnace, an oven, or a kiln to evaporate the carrier fluid using at least one of conduction, convection, and radiation. The volume of carrier fluid on the surface of the substrate along with the volume of carrier fluid within the channels 28 or pores directly impacts the footprint of successive droplets of conductive ink. Therefore, when building the conductive particles upon one another, the rate by which the carrier fluid is drawn off or evaporated has a direct impact on the time between successive droplets in a single location. In this manner, the elevated temperature environment may be useful to decrease the time between successive droplets in a single location, thereby increasing the production rate of printed circuits 10.
It is to be understood that a number of practical considerations may impact the number and size of droplets of conductive ink deposited to form the first conductive pathway 12. Examples of such considerations include, without limitation, the dimensions of the conductive paths, the number of nozzles associated with the inkjet printer that are operative to eject the conductive ink, the conductive ink utilized, the substrate chosen, the capacity of the subsequent ink receiving layers to receive carrier fluid if it is needed and environmental conditions such as the ambient temperature and the substrate temperature. As will be apparent hereafter, these exemplary considerations may also affect the deposition of conductive material comprising the second 14, third 16, and fourth 18 conductive pathways.
Referring to
Subsequent to dielectric material 22 deposition, the dielectric material 22 may be fused at 140-185° C. utilizing the C750 fuser or analogous fuser of a comparable laser printer. It is important to note that if the dielectric material 22 is not fused, gaps may be present between the dielectric particles that may work to draw off the carrier fluid from subsequently deposited conductive ink. In this manner, it may be advantageous to deposit the dielectric material 22 in separate layers, where a first layer 22A isolates the first conductive pathways 12 and the second layer 22B defines the vias 36. Thus, the first layer of dielectric material 22A may be fused to more densely pack the dielectric material to ensure electrical isolation of those portions of the first conductive pathway 12 covered, and afterwards deposit the second layer of dielectric material 22B having gaps that are operative to draw off the carrier fluid of any subsequently deposited conductive ink. The dielectric material 22B can also be thought of as forming the ink receiving layer if a subsequent ink jet ink is used that requires channels to receive the carrier fluid.
In general, the dielectric material 22 may comprise a single layer with more or less uniform chemistry or comprise multiple layers having differing chemistries. For example, the chemistry of the layers of dielectric material may be altered to improve the wetability and adhesion of the ink, whether the carrier fluid is polar or nonpolar, but still allow good adhesion between successive layers of dielectric material, even where the dielectric material have differing chemistries. By way of example, and not by way of limitation, the first dielectric material 22A is deposited to isolate the segments of the first conductive path 12 from one another may be strongly hydrophobic, whereas the dielectric material 22B that comes into contact with conductive ink may be formulated to have increased hydrophilicity and preferred interaction characteristics to allow greater density and more precise deposition of the conductive ink. As discussed above, the dielectric material 22, in addition to isolating those aspects of the first conductive path 12 not intended to be vertically interconnected with subsequent conductive path(s), defines vias 36 to facilitate interconnection 38 formation (see
While the second exemplary intermediate 34 has been described using a two-step dielectric material deposition process, it is within the scope of the invention to sequentially deposit a single dielectric layer and ink receiving layer or concurrently deposit different dielectric material layers using one or more printers, each having one or more toner bays, followed by subsequently depositing the ink receiving layer from one or more printers each having one or more toner bays. For example, utilizing a color laser printer having toners bays adapted to house multiple toner cartridges, an isolating layer of dielectric material 22A may be deposited utilizing cyan, yellow, and magenta toner bays, while a conductive ink receiving layer 22B may be deposited utilizing the black toner bay. Further, the cyan, yellow, magenta, and black toner bays may all be utilized or utilized in combination to deposit a single layer of dielectric material. Alternatively the cyan cartridge may be used for the conductive layer, the yellow for the dielectric layer and the magenta and black for the ink receiving layer. The ink receiving layer would primarily be necessary if the conductive material was part of a liquid ink as opposed to a dry toner, for example if the ink contained a carrier fluid, such as water or alcohol for thermal ink jet printers. Such an ink receiving layer would not be necessary if the conductive ink was printed from a laser printer. In other words it is possible to print one or more layers using one or more printers of one or more technologies, laser followed by ink jet followed by laser. In this way the advantages of the printing technique can be used to optimize the layer to be printed. Those of ordinary skill will readily understand the obvious variances that may be harnessed utilizing a combination of one or more laser printers and/or one or more ink jet printers. In sum, each cartridge bay may include toners having the same or unique electrical and physical properties to tailor the layering of the dielectric material and the ink receiving material 22 if necessary. Likewise each ink cartridge may include inks having the same or unique electrical and physical properties to tailor the layering of the dielectric material. It is also possible that the ink receiving layer provide more function than just to receive the carrier fluid from a liquid based ink. This layer could be considered a compatibilizing layer to improve the integrity and adhesion between the layers in the stack of layers for resistance to wear during handling.
For purposes of the present invention, the dielectric material 22 may be any material operative to electrically insulate one conductive body from another conductive body or substantially reduce the efficiency of electrical transfer between bodies. Exemplary dielectric materials for use with the present invention include, without limitation, a polyester based toner, 10B041M (commercially available from Lexmark International, Inc.), and a styrene butyl acrylate toner, NR231A (commercially available from Lexmark International, Inc.).
It is also within the scope of the present invention that the toner include silicas or other materials that foster separation of the carrier fluid from the conductive particles disbursed therein. For instance, silicas may be added to dielectric toner deposited as a conductive receiving layer 22B to provide gaps within the layer sufficient to drain away the carrier fluid, but retain the conductive particles of the conductive ink within the vias 36, similar to the functionality provided by the channels 28 or pores within the Pictorico® paper. Alternatively, a silica layer is printed over the dielectric material 22A using an interface inkjet ink with silica particles. This silica layer may be printed over the dielectric material 22A, whether or not the dielectric material has been fused. In this instance, it is advantageous to incorporate a surfactant into the carrier fluid of the interface ink to provide a better bonding interface between the dielectric material and the silica particulates. Exemplary silicas for use within inkjet media include, without limitation, CAB-O-SPERSE® fumed silicas ( ), AEROSIL® fumed silicas and precipitated silicas ( ), SNOWTEX® colloidal silicas ( ), and SYLOJET® & SYLOID® silica gels (http://www.gracedavison.com/products/silgelap.htm).
As discussed previously, the toner comprising the dielectric material 22 is generally hydrophobic, which tends to bead the ink droplet and inhibit proper coverage of the conductive particles that are deposited directly on top of the toner. A principal reason for this hydrophobic property is the presence of waxes in the toner to help in fusing the toner. However, the waxes in the toner may be manipulated to generate a toner that is more or less hydrophobic. Exemplary waxes that may be incorporated into the dielectric toner to reduce hydrophobicity include, without limitation, Unilin, Unicid, Ceramer, and Unithox Unilin, available from Baker Petrolite (www.bakerhughes.com). Those of ordinary skill will readily understand that the particular formulation of toner chosen will depend on the various operating conditions and processing steps chosen to implement the instant invention.
Referring to
Referring to
Referring to
Referring to
Where:
Bayhydur® VP LS 2310 is a product of Bayer Corp.;
Joncryl 678 is a product of Johnson Polymer;
Macrynal® VSM 2521 is a product of UCB;
Surfynol® 465 is a product of Dow Air Products, Corp.; and
Exemplary dielectric inks for use with the present invention may be formulated by combining two groups of compounds. The first group comprises compounds with functional groups capable of reacting with active hydrogen, such as an isocyanate group. The second group comprises compounds with functional groups containing active hydrogen, such as hydroxyl, amino, thiol, urethane, or urea groups (such as polyols or acrylic acids) or functional groups that can be converted into active hydrogen containing functional groups, such as carboxylic acid derivatives (such as anhydride groups).
The material selected from the second group may also act as a humectant. This is an advantage because humectants in the ink improve jetting reliability, however, the presence of these compounds/additives in the final film can adversely affect its physical, chemical, and electrical properties. Most notably, this can lead to higher water uptake than is tolerable in a dielectric material and the presence of non-volatile humectants on the surface of the film. Typically, these chemicals are removed by absorption in a substrate or evaporation during curing. If they can be reacted to form part of the cured film, then they are no longer detrimental to its properties.
Crosslinking material and crosslikable polymers can be formulated in one ink system or two separated ink systems. The ratios of both crosslinker and crosslikable materials in the exemplary formulations were calculated based on the equivalent weights necessary to achieve a 1:1 to 3:1 ratios of crosslinking-to-crosslinkable functional groups. A small amount of excess crosslinker was added to the ink formulation to react with humectant additives containing hydroxyl or active hydrogen groups. This improves the dielectric properties of the film. Crosslinking reaction will not occur without heating above the de-block temperature of the blocking agent of the blocked isocyanate. This is the property which allows both polyol and isocyanate groups to be present in a single formulation without reacting in the printhead before printing on the substrate. For one-ink system, both blocked polyisocyanate and polyols are added to the same ink. For two ink systems, blocked isocyanate and polyol are added into two separate ink formulations with the humectants, surfactants, and additives.
These dielectric inkjet inks may also include ceramic or metal oxide nano-particulates, such as, without limitation, titanium dioxide. Exemplary weight percentage ranges for these nano-particulates are between zero percent and twenty percent.
Referencing
Referring to
Referring to
Referencing to
It is also within the scope of the present invention that a laser printer, for example, can be utilized to deposit the conductive material, the dielectric material and the ink receiving layer. Moreover, it is further within the scope of the present invention that an inkjet printer can be utilized to deposit the conductive material the dielectric material and the ink receiving layer. Likewise, multiple laser printers and/or multiple inkjet printers, for example, may be utilized to carry out one or more aspects of the present invention.
It is also within the scope of the invention to omit the interconnections, thereby forming conductive layers that are electrically isolated from one another. In this manner, multiple RFID antenna may be printed upon a single substrate. Moreover, the stacked structure of multiple RFID antennas may include interposed disposable layers to facilitate separation of the antennas subsequent to fabrication.
Finally, it is to be understood that the dimensions of the conductive pathways and interposed dielectric material are within the purview of one of ordinary skill and may be dependent upon the particular printed circuit application.
Following from the above description and invention summaries, it should be apparent to those of ordinary skill in the art that, while the methods and apparatuses herein described constitute exemplary embodiments of the present invention, the invention contained herein is not limited to this precise embodiment and that changes may be made to such embodiments without departing from the scope of the invention as defined by the claims. Additionally, it is to be understood that the invention is defined by the claims and it is not intended that any limitations or elements describing the exemplary embodiments set forth herein are to be incorporated into the interpretation of any claim element unless such limitation or element is explicitly stated. Likewise, it is to be understood that it is not necessary to meet any or all of the identified advantages or objects of the invention disclosed herein in order to fall within the scope of any claims, since the invention is defined by the claims and since inherent and/or unforeseen advantages of the present invention may exist even though they may not have been explicitly discussed herein.
The present application claims the benefit of U.S. Provisional Patent Application Ser. No. 60/636,631, entitled “MULTIPLE PRINTING TECHNIQUES FOR FABRICATING PRINTED CIRCUITS, filed Dec. 16, 2004, the disclosure of which is hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 60636631 | Dec 2004 | US |