Patent Grant
9275856
There is significant interest in realizing high-performance thin-film transistors (TFTs) based on solution-processible semiconducting materials for applications requiring low-cost, low-temperature manufacturing on large-area, flexible substrates.[1, 2] Much effort has been devoted to low-temperature, solution processible organic semiconductors as a potential alternative to traditional inorganic semiconductors. OTFTs with mobilities of 0.01-0.1 cm2/Vs, good reliability, stability, and device-to-device uniformity have been demonstrated.[3, 8] There are also various approaches to realizing solution-processible inorganic semiconductors, which provide a potential route to significantly higher mobilities, but for which control of electronic defect states when processed from solution at low temperatures can be challenging.[9] Inorganic semiconductors might also provide a route to high performance n-type TFTs required for complementary circuits, which are traditionally difficult to realize with organic TFTs although much progress has been made recently.[10, 11]
A variety of solution-processible inorganic semiconductors for TFTs have been reported.[9] These include tin(II) iodide based organic-inorganic hybrids[12], chalcogenide semiconductors[13], μm-long semiconductor nanowires[14] and spherical nanocrystals[15]. The semiconductor nanowire/nanocrystal approach is very promising, since it allows to decouple the high-temperature growth/synthesis of the nanowire from the low-temperature device fabrication process, and achieve high performance.
Duan et al.[14] have used μm-long semiconductor nanowires as the active layer of TFTs. The long nanowires have a length comparable to the channel length of the TFT and as a result yield very high electrical performance, but are difficult to disperse into a stable solution. They can be deposited and aligned by sophisticated deposition techniques such as flow in capillaries and Langmuir-Blogett techniques, but they do not form stable dispersions with sufficiently long solution shelf lifetime, and as a result are difficult to deposit over large areas, but standard techniques such as printing, spin-coating, or other large-area coating techniques. Another problem with semiconductor nanowires is the low density of nanowires on the substrate. The typical distance between the nanowires in the film is much larger than the nanowire diameter, and the surface coverage is typically less than 20%.
Ridley et al.[15] have used spherical colloidal nanocrystals of CdSe, which can be drop-cast onto a substrate and can re-melt to form a uniform film after annealing at 350° C. due to lowering of the melting point for these ultra-small nanocrystals.[16] However, the mobility of a thin film of spherical nanocrystals is significantly lower than the maximum achievable bulk mobility of the semiconducting material due to a large number of grain boundaries in the sintered nanocrystal network. This is because the nanoparticle diameter needs to be kept small (typically less than 10 nm) in order to be able to sinter the particles by the surface melting mechanism. Another problem with the spherical colloidal nanoparticle approach is that it requires still relatively high annealing temperatures for the sintering process. CdSe nanocrystal devices shows m-type behaviour with mobility of 1 cm2V−1s−1 and on/off ratio of 3.1×104 after annealing at 350° C. and on/off ratio of 3.1×104 after annealing at 350° C.
Some of the important requirements for using semiconductor colloidal nanocrystals in this application include a good dispersing capacity (>50 mg/ml) and adequate stability of the dispersion (at least one week). Although there are many reports to synthesize different kinds of nanocrystals, there is a need for colloidal nanocrystal systems which can meet these requirements.
Zinc oxide (ZnO) is an environmentally friendly transparent semiconductor with a large band gap of 3.37 eV. TFT devices based on polycrystalline ZnO as active layer have been reported with mobility of around 0.2-3 cm2V−1s−1.[17, 18-21] Most fabrication methods use a sputtering process to grow ZnO films. Solution-processing techniques have also been used to fabricate ZnO devices, but have suffered from poor device performance[20] or the need to use high annealing temperature (700° C).[21] ZnO nanospheres can be dispersed at high concentration beyond 75 mg/ml for solar cell applications as shown in recent reports.[22, 23]
The shape of ZnO and other nanocrystals can be controlled from nanosphere to nanorods by adjusting the growth time.[24] Compared to the more commonly studied spherical colloidal nanocrystals nanorods have an elongated cylindrical shape with typical diameters of 3-10 nm and length of 10-100 nm.
The assembly of colloidal nanorods has been studied by Li et al.[25, 26] They used drop-casting to prepare nanorod crystals onto an electron-microscopy grid, and also used capillaries to study the formation of a lyotropic liquid crystalline phase of the nanorod solution. However, they did not report formation of large-area, continuous films of nanorods, nor did they incorporate the nanorods into electronic devices.
The present specification discloses a method for improving the performance and field-effect mobility of a TFT based on a thin; solution-deposited film of an inorganic nanoparticle-based semiconducting material.
According to an aspect of the present invention there is provided an electronic switching device having a semiconducting layer that comprises inorganic semiconducting elongate nanoparticles having a longer dimension and a shorter dimension, the average ratio of the length of the longer dimension to the length of the shorter dimension for the nanoparticles of the layer being in the range 2 to 50 and the average length of the longer dimension of the nanoparticles of the layer being less than 1000 nm, wherein the nanoparticles of the layer are generally mutually aligned.
Preferably the electronic switching device further comprises first and second contacts defining a current transport path through the semiconducting layer extending there between, the nanoparticles being generally aligned along the direction of the current transport path.
Preferably the distance between the first and second contacts defines a channel length and the ratio of the channel length to the average length of the longer dimension of the nanoparticles of the layer is larger than 1.
Preferably the nanoparticles are uniaxially aligned within one or more domains having a diameter greater than 1000 nm.
Preferably at least some of the nanoparticles are fused together.
Suitably the nanoparticles are semiconducting oxide nanoparticles. Many oxide semiconductors exhibit stable surface composition when exposed to atmosphere and moisture, and do not oxidize when exposed to air and moisture during growth or film deposition. Examples of suitable oxide semiconductors include zinc oxide, tin oxide, zinc tin oxide, indium oxide, zinc indium oxide, or indium gallium zinc oxide nanoparticles. Provided that care is taken to avoid surface oxidation also other, more reactive semiconductors such as; but not limited to, Si, Ge, SiGe, GaAs, InP, InAs, ZnS, ZnSe, ZnTe, CdS, CdSe, CdTe, HgS, HgSe, HgTe, PbS, PbSe, PbTe, SnS2, SnSe2, SnTe2 can be used.
Preferably the mobility of the semiconducting layer is at least 0.5 cm2V−1s−1.
Preferably the density of the film is at least 50%, more preferably more than 80%, of the bulk density of the inorganic material of which the nanoparticles are comprised.
According to an aspect of the present invention there is provided a method for fabricating a film of nanoparticles on a substrate, the method comprising: forming a dispersion of elongate inorganic nanoparticles in a solvent, the nanoparticles having one or more ligand molecules attached to their surface, the nanoparticles having a longer dimension and a shorter dimension, and the ligand molecules including a functional group that enhances the stability of the dispersion of the nanoparticles in the solvent; and causing the nanoparticles to be deposited onto the substrate from the dispersion by removal of the solvent at a surface of the dispersion.
Preferably the ligands are organic or partly organic.
Suitably the semiconducting nanoparticles comprise an oxide semiconductor. The oxide semiconductor may be zinc oxide, tin oxide, zinc tin oxide, indium oxide, zinc indium oxide or indium gallium zinc oxide.
Preferably the ligands are selected so as to cause the concentration of nanoparticles to be higher at the surface of the solution than in the bulk of the solution, and the shape of the nanoparticles is selected so as to promote mutual alignment of the nanoparticles.
Preferably the ratio of the length of the longer dimension to the length of the shorter dimension for the nanoparticles in solution is in the range 2 to 50 and the average length of the longer dimension of the nanoparticles in solution is less than 1000 nm.
Preferably the solvent is removed at a surface of the solution in such a way so as to define a direction of preferential orientation for the nanoparticles and cause the nanoparticles to become at least partially aligned along that direction.
Suitably the film defines a geometric plane and the direction is out of the geometric plane defined by the film. Alternatively the direction lies in the geometric plane defined by the film.
Preferably the direction of preferential orientation is defined by the flow of solvent during removal of the solvent at a surface of the solution.
Preferably the concentration of the nanoparticles in the solvent is at least 5 mg/ml.
Preferably the solution has a lower surface tension than the pure solvent due to the presence of the ligands in the solution.
Suitably the ligands are one or more of octylamine, butylamine, hexylamine, and any other alkylamine. The ligands may be bound to the surface of the nanoparticles by a chelating bond.
Suitably the solvent is a mixture of solvents, such as a mixture of a polar solvent which exhibits a favourable interaction with the bare surface of the nanoparticles and a non-polar solvent which exhibits a favourable interaction with the ligand molecule. Suitably, the solvent is a mixture of an alcohol solvent and an organic solvent, such as a mixture of chloroform and methanol.
Preferably, subsequent to causing the nanoparticles to be deposited from solution, the film is heated so as to remove the ligands. Preferably said removal of ligands occurs by heating the film at a temperature less than 250° C. Said heating step may be induced by thermal annealing or by irradiation with light absorbed by the nanoparticles.
Preferably, subsequent to removing the ligands, the film is immersed in a growth solution of nanoparticles in a solvent. Preferably the growth solution is a hydrothermal growth solution. Suitably the hydrothermal growth solution is an aqueous solution comprising zinc nitrate and ethylenediamine.
Preferably the growth solution is heated at a temperature below the bulk melting point of the nanoparticle material so as to cause at least some of the nanoparticles to fuse together. Suitably the temperature to which the film is heated is less than 100° C.
Preferably, subsequent to immersing the film in a growth solution, the film is heated so as to cause annealing of the nanoparticle film. Suitably, subsequent to immersing the film in a growth solution, the film is heated so as to cause annealing of the nanoparticle film. Suitably the film is heated under an atmosphere predominantly comprising nitrogen and hydrogen gases. Suitably the annealing temperature to which the film is heated is less than 250° C.
Suitably the nanoparticles are deposited by means of one of spin coating, drop coating and blade coating, or by a direct printing process such as inkjet printing, offset printing, gravure printing, flexographic printing or screen printing. The nanoparticles may be deposited in a continuous or as a patterned but locally continuous film.
Suitably the nanoparticles are semiconducting. Suitably the nanoparticles are zinc oxide nanoparticles.
Said film of nanoparticles may form part of the active layer of an electronic device. The electronic device may further comprises first and second contacts defining a current transport path through the semiconducting layer extending therebetween, the nanoparticles being generally aligned along the direction of the current transport path.
Said electronic device may be an electronic switching device. Said electronic device may be a diode, such as a light-emitting, light-sensing or photovoltaic diode.
Suitably the elongate nanoparticles are aligned with their long dimension preferentially oriented in the plane of the substrate. Alternatively the elongate nanoparticles may be aligned with their long dimension preferentially oriented normal to the plane of the substrate.
Preferably the field-effect mobility of the active semiconducting layer is at least 0.5 cm2V−1s−1.
Preferably the distance between the first and second contacts defines a channel length and the ratio of the channel length to the average length of the longer dimension of the nanoparticles of the layer is larger than 1.
Preferably the removal of the solvent occurs when the dispersion is in contact with the substrate.
According to an aspect of the present invention there is provided a method for fabricating a film of nanoparticles, the method comprising: forming a dispersion of elongate nanoparticles in a solvent, the nanoparticles having a longer dimension and a shorter dimension and having one or more ligand molecules attached to their surface; and causing the nanoparticles to be deposited from the dispersion by removal of the solvent at a surface of the dispersion; wherein the ligand molecules are selected so as to cause the concentration of nanoparticles to be higher at the surface of the solution than in the bulk of the solution, and the shape of the nanoparticles is selected so as to promote mutual alignment of the nanoparticles.
According to an aspect of the present invention there is provided an active semiconducting layer that comprises inorganic semiconducting elongate nanoparticles having a longer dimension and a shorter dimension, the average ratio of the length of the longer dimension to the length of the shorter dimension for the nanoparticles of the layer being in the range 2 to 50 and the average length of the longer dimension of the nanoparticles of the layer being less than 1000 nm, wherein the nanoparticles of the layer are generally mutually aligned.
Preferably the nanoparticles are uniaxially aligned within domains having a diameter greater than 1000 nm.
Preferably at least some of the nanoparticles are fused together.
Suitably the nanoparticles are zinc oxide nanoparticles.
Preferably the mobility of the semiconducting layer is at least 0.5 cm2V−1s−1.
According to a first aspect of the present invention an electronic switching device is disclosed, wherein the active semiconducting layer is formed from inorganic colloidal semiconducting nanorods deposited from liquid phase. Compared to spherical colloidal crystals nanorods allow achieving better device performance because of a smaller number of grain boundaries in the film.
Compared to long nanowires, which typically have a length exceeding 1 μm, and do not allow formation of stable dispersions, the nanorods can be formulated into stable dispersion with concentrations exceeding 10 mg/ml and processed from solution by techniques such as spin-coating, or other common large-area coating techniques.
To obtain a stable nanoparticle dispersion the long dimension of the nanorods L (for example, in the case of a cylindrical nanorod L is the length of the rod) is preferably less than 1 μm, more preferably less than 500 nm, most preferably less than 300 nm. These dimensions may refer to the size of each nanorod, or to the average size of all nanorods in the dispersion.
Preferably, the ratio between the small dimension of the nanorod D (for example, in the case of a cylindrical nanorod D is the diameter of the rod) and the long dimension of the nanorod is in the following range: 2<L/D<50. More preferably, the ratio L/D is in the range 5<L/D<20.
Preferably, the long (longer) dimension of the nanoparticles is in range of 10 nm<L<300 nm, and the small (shorter) dimension of the nanoparticles is in the range of 3 nm<D<50 nm. The longer dimension of a nanoparticle may be its longest dimension. The shorter dimension of a nanoparticle may be its shortest dimension. The shortest dimension is preferably transverse to the longer dimension. Preferably the nanoparticle is rod-shaped.
Where dimensions, ratios and figures are given herein for a plurality of nanoparticles, such as those nanoparticles comprising a semiconducting layer or film, those dimension, ratios and figures should be taken to be averages over the relevant population of nanoparticles (i.e. those nanoparticles actually comprising a semiconducting layer or film). The average values may be mean, median or modal average values.
Preferably, a ligand is attached to the surface of the nanorod. The ligand is suitably an organic molecule (which could be a partly organic molecule). Preferably it comprises a polar head group which is able to form a bond with the surface of the nanorods. The ligand also preferably comprises a functional group which is soluble in the solvent used for the liquid phase deposition. The ligand molecule may be soluble in the solvent. Preferably, the bond between the ligand and the surface of the nanorods is a weak bond such that it can be broken by low-temperature annealing below typically 250° C. or by exposure to light and/or laser radiation. Preferably, the bond between the ligand and the surface of the nanorod is a chelating bond. Alternatively, the bond between the ligand and the surface is a covalent bond.
Preferably, the nanorods are aligned such that their long-axis is aligned preferentially in the plane of current flow in the electronic switching device. More preferably, the nanorods are aligned uniaxially such that their long-axis is aligned preferentially along the direction of current flow in the electronic switching device.
Preferably, the distance (preferably the typical or average distance) between neighbouring nanorods in the as-deposited films is less than the nanorod diameter, so that a dense film of nanorods is formed. This facilitates the efficient transport of charges in between nanorods. At the interface with the substrate the surface coverage of nanorods is preferably higher than 80%, more preferably higher than 90%. This is significantly higher than what can be achieved with long nanowires[14], for which the spacing between nanowires is more than 10 times the nanowire diameter, and the surface coverage is typically less than 10%.
The density of the film may be at least 50%, and more preferably more than 80%, of the bulk density of the inorganic material of which the nanoparticles are comprised.
In comparison to the longer nanowires (length>1 μm) reported in the prior art[14], which allow spanning the gap between two electrodes by a single nanowire, the use of nanorods according to the present invention means that the channel length in a typical device configuration with channel length of several μm's is more than 5-10 longer than the maximum dimension of the nanorods. Nanorods allow retaining much better dispersion properties for deposition from liquid phase and allow achieving dense, uniform films, such that in spite of the large number of grain boundaries in the channel high field-effect mobility of the transistor in excess of 0.1 cm2/Vs can be achieved.
According to a second aspect of the present invention an electronic switching device is disclosed wherein the active semiconducting layer comprises inorganic semiconducting nanorods of zinc oxide with a length between 10 m and 1 μm.
According to a third aspect of the present invention a method is disclosed for preparing a uniform film of densely packed nanorods by solution processing. By making use of a ligand that lowers the surface tension of the nanorods uniform, densely packed films of nanorods can be solution deposited by techniques such as spin coating. In these films the nanorods can be made to adopt a well defined orientation, such as in-plane or out-of plane orientation of the long axis of the nanorods depending on process conditions. In spin-coated films long ligands with lower surface tension exhibit larger domain size and more pronounced in-plane alignment of the nanorods resulting in significantly better FET device performance than short ligands. The preferential orientation of the nanorods can be influenced by the deposition process, and the presence of a liquid flow during the deposition. In spin-coated films preferential in-plane alignment of the nanorods can be achieved while in drop-cast films with slow evaporation rate nanorods are aligned preferentially normal to the substrate. In films dried slowly between two substrates in-plane alignment was found again with uniaxial nanorod alignment at the edges of the drying film.
According to a fourth aspect of the present invention a method is disclosed for forming an electronic switching device on a substrate, wherein the method comprises depositing the active semiconducting layer of the electronic switching device onto the substrate from a liquid dispersion of colloidal nanorods, and subsequently immersing the substrate into a growth solution to increase the diameter and/or length of the nanorods on the substrate.
Preferably, the as-deposited nanorods are aligned such that their long-axis is aligned preferentially in the plane of current flow in the electronic switching device, more preferably, the as-deposited nanorods are aligned such that their long-axis is aligned preferentially along the direction of current flow in the electronic switching device.
According to a further aspect of the present invention said growth solution is a hydrothermal growth solution.
The invention will now be described by way of example with reference to the following figures:
Scheme 1 shows a schematic TFT device structure.
a) shows transfer characteristics of a device composing of nanospheres in the linear region (Vd=5V) and saturated region (Vd=60V) after post-deposition hydrothermal growth. (b) and (c) Transfer characteristics and output characteristics of a device made from nanorods after post-deposition hydrothermal growth.
Table 1 shows TFT device characteristics of as-deposited ZnO nanorod films, which were synthesized from different mole ratios between potassium hydroxide and zinc acetate. Field effect mobilities μsat were derived from the saturated region. |V0| is the turn-on voltage of the TFTs.
ZnO nanorods are prepared according to a literature method developed by Pacholski [23, 24] with some modification. 0.8182 g (4.46 mmol) zinc acetate [Zn(Ac)2] and 250 μl water was added into a flask containing 42 ml methanol. The solution was heated to 60° C. with magnetic stirring. 0.4859 g (7:22 mmol, purity 85%) potassium hydroxide (KOH) was dissolved into 23 ml methanol as the stock solution which is dropped into the flask within 10-15 min. At a constant temperature of 60° C. it takes 2 hours and 15 minutes to obtain 6 nm diameter nanospheres. A small amount of water was found helpful to increase the ZnO nanocrystal growth rate. In order to grow the nanorods, the solution is condensed to about 10 ml. This was found helpful before further heating to decrease the growth time of the nanorods. Then it is reheated for another five hours before stopping the heating and stirring. The upper fraction of the solution is removed after 30 min. 50 ml methanol is added to the solution and stirred for 5 min. The upper fraction of the solution is discarded again after 30 min. This process is repeated twice. For the second time washing, the upper fraction of the solution is taken away after overnight staying. Finally, 3.3 ml chloroform and 100 μL n-butylamine are used to disperse the nanorods. The nanorods concentration is about 85 mg/ml and the solution is stable for more than two weeks. Using the modified method reported here it only takes 5 hours to obtain 65 nm long-nanorods instead of several days as reported in the literature.[24]
Transmission electron microscopy images of ZnO nanospheres (a) and nanorods (b) synthesized as above are shown in
Nanocrystal films and devices are fabricated on SiO2(300 nm)/Si substrates with photolithographically patterned interdigitated Cr(3 nm)/Au(12 nm) electrodes. The device structure is shown in Scheme 1. Before spin-casting the ZnO solution, the substrate is cleaned in an oxygen plasma at a power of 150 W for 2 min. The film is spin-coated from filtered (0.45 μm PTFE filter) ZnO solution with a speed of 2000 rpm. Then the devices are annealed at 230° C. in N2/H2(V/V, 95:5) for 30 min.
Characteristics for three TFT devices made from ZnO nanorods synthesized with different mole ratios are summarized in Table 1. All devices exhibit n-type field-effect conduction. The optimized mole ratio is 1.62. It is found that the conductivity increases and mobility decreases as the stoichiometry is varied from the experimentally determined optimum mole ration in both directions. The stoichiometry can be characterized by X-ray diffraction. The (002) diffraction signal of the ZnO nanocrystals only comes from zinc atoms in the wurtzite crystal structure. It has been found that the (002) signal of the ZnO nanocrystals in their X-ray diffraction patterns is maximum if the mole ratio is near to its stoichiometric value [27], which means that there will be the lowest oxygen vacancy in this crystal structure at this ratio.
ZnO films containing a low concentration of oxygen vacancies should exhibit low conductivity because oxygen vacancies behave as deep donors.[28] Consistent with this expectation TFT devices based on this ratio show the lowest conductivity. It is worth mentioning that small variations in mole ratio do not appear to have a significant effect on the shape and size of the nanorods, but do greatly affect the TFT device performance. We believe that the large difference of TFTs'. characteristics originates in small changes of the stoichiometry of the ZnO films.
To obtain reproducible TFT performance the formation of high-quality films by techniques such as spin-coating is very important. We have found that high-quality nanocrystal films can be obtained from high concentration solutions (>50 mg/mL). The as-prepared ZnO nanocrystals comprise acetate (CH3COO−) ligand groups chelating with zinc atoms on the surface of nanocrystals. The ligands are very important to facilitate the dispersion of the nanocrystals in the solvent. For small nanospheres (approximately 6 nm), it is quite easy to achieve a high concentration solution using just the short acetate ligands. However, the acetate ligands are not sufficient to achieve high concentration dispersions of the longer nanorods. Alkylamine ligands can be used as ligands to help ZnO nanocrystal suspension.[27] When alkylamine is added to the solution, the 10×65 nm nanorods can be dispersed into chloroform with concentration as high as 90 mg/ml. For the nanospheres there is a large number of microcracks in the spin-cast films if butylamine is not added to the solution. Alkylamine ligands can be removed from the surface by low-temperature annealing at 200° C. due to their low boiling points (butylamine 78° C.) and below, and result in stable dispersion that do not aggregate or sediment for periods of days. We have found that longer alkylamine ligands (octylamine) lead to more stable dispersions than shorter ligands (butylamine). With octylamine dispersions are stable over periods of several weeks. In examples 2 and 3 we use butylamine as a ligand. A comparison between different ligands will be presented in examples 5,6 and 7.
The as-prepared films are annealed under nitrogen/hydrogen atmosphere to increase mobile carrier concentration and field-effect mobility. It has been reported that hydrogen can be incorporated into ZnO films in high concentration at annealing temperatures of 200° C. and behave as a shallow donor acting as a source of conductivity.[28] At the same time, the ligand can be partly removed due to this mild heating. The characteristics of TFTs made from ZnO nanospheres (a) and nanorods (b) are shown in
The TFT device performances can be further enhanced by the post-deposition hydrothermal growth step in aqueous solution. For the additional hydrothermal growth, the substrates are immersed upside-down into a glass beaker filled with an aqueous solution containing zinc nitrate (0.025 M) and ethylenediamine (0.04 M) with slow stirring at 90° C. The devices are taken out after 50 min and rinsed with deionised water. Finally, the device is annealed at 200 ° C. for 15 min in N2/H2 atmosphere after drying with nitrogen. Electric measurements are performed in a nitrogen atmosphere to avoid any possible effect from oxygen and humidity.
The corresponding TFT device characteristics are shown in
To investigate the relationship between film microstructure and device performance and to identify the mechanisms for the observed improvements of device performance we have performed scanning-electron microscopy (SEM) and atomic force microscopy (AFM) (
During post-deposition hydrothermal growth, the nanorods grow further along their c-axis forming longer rods, as shown in
If the film is made from nanospheres and subjected to post-deposition hydrothermal growth the TFTs show only a small improvement of mobility to 0.0024 cm2V−1s−1 and on/off ratio of 5×104. The mobility is more than two orders of magnitude lower than that of TFTs made from nanorods by the same fabrication process. During post-deposition hydrothermal growth the as-spin-cast nanosphere-seed film can grow into an array of ZnO wires, which are, however, aligned randomly with respect to the substrate normal.[33] This is less favourable than the in-plane orientation of nanowires obtained near the substrate interface in films deposited from a nanorod dispersion. The nanosphere films exhibit good uniformity, as shown in
The above observations show the beneficial effects on the device performance, and charge carrier mobility if the long axis of the nanorods is aligned in the plane of current transport. Nanorods of the type used here have been shown to form nematic as well as smectic liquid crystalline phases, in which the nanorods are aligned uniaxially with their long axis parallel to each other in micron size domains.[25, 26] The liquid-crystalline properties of the nanorods can be used to produce uniaxially aligned films of nanorods in which the long nanorod axis is aligned along the direction of current flow in the device (
To align the nanorods uniaxially a range of techniques known from the field of liquid-crystalline anisotropic organic molecules (as used for example, in active matrix liquid crystal displays) can be used. These include, but are not limited to, use of alignment layers with either an aligned molecular structure (such as polyamide alignment layers produced by mechanical rubbing), or aligned topographic structures/grooves, in which the nanorods align along the walls of the grooves during evaporation of the solvent. Alternatively, alignment by exposure to electrical or magnetic fields, polarised light, or through shear, flow or capillary force alignment can be used. The nanorods are formulated preferably in a solvent, in which they exhibit lyotropic behaviour, i.e. in which beyond a certain concentration of nanorods, the solution becomes liquid-crystalline at a temperature near room temperature. The concentration threshold for exhibiting lyotropic properties might be reached in the original solution, or maybe crossed by drying of solvent during deposition of the solution.
As shown in below the nanorods can also be aligned by selecting a ligand that lowers the surface tension of the nanorods and acts as a surfactant in the solvent from which the nanorods are deposited.
The solution self-assembly of semiconducting ZnO nanorods can be sensitively controlled by the surface chemistry of the nanorods, in particular, by tuning the length of the ligand attached to the surface of the nanorods. The use of longer ligands with lower surface tension or ligands with a chemical structure that lowers the surface tension helps the formation of a well-ordered mesophase as observed by polarized microscopy and scanning electron microscopy.
To keep the nanoparticles well dispersed in an organic solvent an organic monolayer ligand is attached to the surface of the inorganic nanoparticle. For the ZnO nanorods acetate group on the surface of ZnO nanorods can be used during the initial synthesis of the nanoparticles. However, acetate group have a short chain length and can result in the nanorods being negatively charged. To make the nanorods to be dispersed in other organic solvents, butylamine (BUTA) was used as ligand. BUTA is attached on the ZnO surface by an interaction between the nitrogen atom of BUTA and the zinc atom of ZnO.
An attractive feature of this ligand is that it can be removed easily by low temperature annealing due to its neutral charge property and low boiling point. This is important for achieving efficient charge transport between the nanorods. In the present work we have used systematically alkylamine ligands with different chain length to tune the surface chemistry of the ZnO nanorods, and study the effect of the different ligand length on the self assembly properties of the nanorods.
We have found that the use of different ligand lengths results in a significant variation of the surface tension of the nanoparticles. A higher water contact angle is observed for nanorod films with longer carbon ligand. As shown in
The particle-air surface tensions γp/a for different ligands are estimated from the measured water contact angles of films of nanoparticles. To do this we make use of a theoretical model [Good, R. J.; Girifalco, L. A. J. Phys. Chem. 1960, 64, 561-565] for estimating the liquid-particle (water/ligand) interfacial tension γl/p from the surface tension of the particles γp/a and the liquid γl/a:
γl/p=γp/a+γl/a−2φ(yp/aγl/a)1/2 (1)
By using equation (1) and Young's equation, γp/a=γl/acosθ+γl/p, γl/p can be eliminated and using the known liquid-air surface tension γl/a for water γp/a can be expressed as:
γp/a=γl/a(1+cosθ)2/(4φ2) (2)
The parameter φ can be shown to be determined by the molar volume of the particle Vp and liquid Vl:
φ=4(VpVl)1/3/(Vp1/3+Vl1/3)2 (3)
The parameter φ can be obtained if the particle molar volume Vp values is estimated from the corresponding ligand alkylamine molar volume because the effective interface is that between the liquid and the ligand molecules on the surface.[1] The parameter φwater/BUTA value of 0.924 is obtained according equation (3) to determine interfacial energy between water and BUTA-ZnO. In the same way, φwater/OCTA value is 0.875 for that between water and OCTA-ZnO. We can estimate γp/a for different ligands using Equation 2 and the known surface tension of 71.98 mJ/m2 of water. We find that there is a difference of 6.16 mJ/m2 between the surface tension of BUTA-ZnO (γp/aBUTA=33.94 mJ/m2) and that of OCTA-ZnO (γp/aOCTA=27.78 mJ/m2).
Using these values for the surface tension of the ligand modified nanorods we then can apply Equation 1 again to the case of the nanorod solution in chloroform/methanol and calculate the interface tension between the nanorods and the solvent using the appropriate values of φ for chloroform/methanol as the solvent. Here the liquid is chloroform/methanol and its surface energy γl/a is 26.74 mJ/m2 which is in between the surface energy of methanol γmethanol/air=22.98 mJ/m2 and that of chloroform γchloroform/air=28.02 mJ/m2 as determined by the ring method. We have not been able to observe surfactant action of the alkylamine molecule in the chloroform/methanol solvent, i.e., no lowering of the solvent surface tension compared to that of the pure solvent was observed when alkylamine molecules were dissolved at a concentration of 1.5%, V/V in chloroform/methanol. The interfacial free energy value for the chloroform/methanol-BUTA-ZnO interface is γp/lBUTA=0.670 mJ/m2 based on the parameter φsolvent/BUTA=0.996. Similarly, the interfacial free energy from chloroform/methanol-OCTA-ZnO (γp/loct) is γp/lOCTA=1.21 mJ/m2 for φsolvent/OCTA=0.978.
We have investigated the nanorod solution self assembly for different film deposition techniques as a function of ligand length, and have compared in particular spin-coating and drop-casting. ZnO nanorods with alkylamine ligands can be well dispersed in chloroform/methanol solvent with high concentration (up to 50 mg/ml) enabling formation of uniform thin films by spin coating. When solutions of ZnO nanorods with different ligand lengths are spin-coated on the substrate, the resulting films exhibit a strong variation of microstructure depending on the length of the ligand. In OCTA-ZnO films with low surface free energy. clear optical contrast is observed in POM images with crossed polarizers indicating the presence of large crystalline domains with uniaxial alignment of the nanorods on a length scale of several 1-10 μms (
The origin of the optical contrast in the POM image was investigated by SEM. The images show clearly that using the method according to the present invention it is possible to form uniform, densely packed films of nanorods by simple solution coating techniques such as spin-coating. In all spin-coated films we observed preferential in-plane alignment of the long-axis of the nanorods (
Different behaviour was observed in the case of drop-casting. When a droplet of nanorod OCTA-ZnO solution was dried on the substrate with a slow evaporating rate we observed preferential out-of-plane alignment of the nanorods in contrast to the in-plane alignment observed in spin-coated films. In some areas well-defined smectic ordering was observed that manifests itself in well-defined steps on the surface of the film with a step height of 90 nm equal to the length of the nanorods (
We also investigated the drying of a drop of nanorod solution in between two substrates (bottom SiO2/Si wafer and top quartz substrate), such that the free solution-air interface was not present, and evaporation occurred at the edges of the liquid film stacked between the two substrates. Under such conditions a well ordered nanorod structure can be observed where nanorods are again oriented parallel to the substrate as in spin-coated films. In the vicinity of the edges of the film the nanorods are aligned uniaxially perpendicular to the contact line. In some areas clear evidence for smectic ordering was obtained, as shown in
Without wanting to be bound by theory the self-assembly behaviour is believed to be determined by the segregation and nucleation of the nanoparticles to the liquid/air interface. The driving force for nanorod segregation to the surface can be estimated by calculating the change of surface potential Δμ when a nanorods segregates from the bulk of the liquid to the surface. For the purpose of this estimate we assume that the nanorods on the surface are oriented vertical to the surface due to vertical liquid flowing, and that a length H of the long axis of the nanorods (total length L, radius R) is protruding out of the surface and is in contact with air (see Scheme 9(h)). There are three contributions to the surface potential of a nanorod on the surface measured with respect to that of the surface of the pure liquid.
The total surface potential can be written:
μtotal=πR2(γp/a+γp/l−γl/a)+2γp/lπRL+H·2πR(γp/a−γp/l) (7)
The liquid is chloroform/methanol in this case. The surface potential μtotal will be a minimum value μmin if H=0, and only the end surface of the nanoparticle is exposed to air since (γp/a−γp/l)>0:
μmin=πR2(γp/a+γp/l−γl/a)+2γp/lπRL=γl/a[πR2(x+y−1)+2yπRL] (8)
with x=γp/a/γl/a and y=γp/l/γl/a. In comparison, the surface potential μliquid of a nanorod totally immersed in liquid is
μliquid=γp/l·(2πR2+2πRL) (9)
The potential barrier for nanoparticles to segregate from the bulk liquid to the surface Δμl is
Δμl=μliquid−μmin=πR2(γp/l−γp/a+γl/a)=πR2γl/a(y−x+1) (10)
Here, the average values for ZnO nanorods are R=5.5 nm and L=92 nm and the difference in size due to nanorods ligands is neglected. In the BUTA-ZnO case, since x=1.269 and y=0.0251, ΔμlBUTA=0.244πR2γl/a is obtained from Equation 10 respectively, i.e. there is no driving force for the particle to expose a portion of its surface to air. However, in the case of OCTA-ZnO, ΔμlBUTA=0.063πR2γl/a can be calculated using x=0.955 and y=0.0433, and this constitutes a potential for trapping the particle at the surface.
In this framework we can rationalize the observed assembly and alignment of the nanorods under different deposition conditions in the following way. We first consider the case of drop-casting at a low evaporation rate. Due to evaporation solvent molecules move towards the interface from the interior to replenish the surface liquid and the surface moves towards the substrate. At the same time nanorods diffuse in solution. Under the conditions used here the diffusion velocity is slower than the velocity of the moving solid-air surface, and therefore nanorods from the interior of the solution are swept towards the surface. The flux of nanorods impinging onto the surface is given by f=c·v, where c and v are the concentration and flow rate of nanorods with respect to the surface, respectively. According to the Onsager-Flory rigid rod model [37] at sufficiently low concentration of the rods in solution, the rod orientation is isotropic. However, as the concentration increases, it becomes increasingly difficult for the rods to point in random directions and a concentrated solution of nanorods will undergo a phase transition into a lyotropic liquid crystalline phase in which the nanorods are aligned uniaxially along a director. This phase transition is expected to occur at a critical volume ratio of nanocrystals to solvent of φ0=c·D/L, where c is a constant with a value c=4.5 for the Onsager model and c=12.5 for the Flory model. D is the rod diameter and L its length. The colloidal nanorod solution is expected to satisfy the assumptions made by the rigid rod model. [37]
A nanorod is considered to be trapped at the liquid-air interface if Δμl is positive, and the surface potential change Δμl is closely related to the diffusion length λ of the nanorods on the surface λ2=2L2exp[Δμl/kbT] where kb and T are Boltzmann's constant and temperature. For the above values of Δμl this relationship shows that small changes of surface potential change due to differences in surface tension between different ligands can result in large differences of diffusion length, as shown in Scheme 9(h). For the BUTA-ZnO, the surface potential change value is negative, which means the nanorods have to overcome a potential bather from interior bulk liquid to interface. This barrier will prevent the nanorods from segregating towards the interface. In contrast, the estimated surface potential change ΔμlOCTA is positive, which means that a driving force exists that favors the nanorod segregation towards the air-liquid interface. Using the interfacial potential change Δμloct=3.89 kbT we estimate the diffusion length λOCTA to be on the order ˜0.91 μm. A long diffusion length is closely related to the critical concentration φ0 for the liquid-crystalline phase transition. A certain minimum flow rate value f0 is needed to reach this concentration, which can be estimated to be f0=4φ0Ddiff/λ2, where Ddiff is the diffusion constant at the liquid-air interface. From this expression it is clear that nanorods with longer diffusion length at the liquid-air interface are more likely to reach the critical concentration to undergo nucleation on the surface. This analysis suggests that the reason for the larger domain size of the OCTA-ZnO films is related to the ability of the OCTA-ZnO nanorods to undergo nucleation at the air-liquid interface. In the case of nanorods which do not have a tendency to segregate to the surface, such as BUTA-ZnO it is more likely that nucleation occurs in the bulk of the liquid leading to poorer alignment of the nanorods.
Within this framework once the lyotropic solution has formed on the drying surface the orientation of the nanorods is expected to be determined by flow alignment due to the solution flow on the surface. This explains why in the case of drop casting the preferred orientation of the nanorods is perpendicular to the substrate since in this case the dominant solution flow is due to evaporation and is normal to the surface (Scheme 9(d)). In the case of the nanorod solution drying between two substrates (Scheme 9(f)) the nucleation is expected to occur at the edges of the drying film where solvent can escape between the two substrates, and where the concentration is highest. Here the solution flow is in the plane perpendicular to the edge and this explains the strong uniaxial alignment, and in some cases even smectic alignment of the rods near the edge of the film. This observation also supports the conclusion that under these conditions the transition from isotropic phase to lyotropic phase happens preferentially at the liquid-air interface where the concentration is highest and not in the bulk interior of the solution.
The case of drop-casting with high evaporation rate (
The case of spin-coating is also complex. The factors that control coating deposition in the spin coating process have been extensively studied [38-42] and include the solution concentration, density, viscosity, surface free energy, solution evaporating rate and rotation speed. When a film is fabricated by spin casting from nanorod solution with high solvent drying rate the liquid flow has both an in-plane component due to rotation of the substrate as well as an out-of plane component due to evaporation at the surface. The spin coating process can be divided into several stages. In the early stages the process is determined by the radial convection flow due to the rotation of the substrate leading to initially rapid thinning of the film while the solute concentration in the liquid remains constant. The radial flow velocity is highest on the surface and drops to zero at the interface with the solid substrate. As the film thins the radial flow velocity and the film thinning rate due to convection slow down, and evaporation of solvent at the surface begins to make an increasingly important contribution to the thinning of the film. In this stage the solute concentration on the surface is expected to become larger than the concentration in the bulk. Finally, the radial flow comes almost to a halt and solvent evaporation results in rapid increase of solute concentration in the film. Several factors might lead to preferential in-plane alignment of the nanorod solution in this process. If the nanorods have a strong tendency to segregate to the surface of the liquid film driven by their low surface tension in the case of OCTA-ZnO it is possible that the critical concentration for forming a lyotropic phase on the surface is reached at a stage when there is still a sufficiently high, in-plane radial flow velocity to align the nanorods in the plane (scheme 9(c)). Ideally, in this situation one might expect a uniform radial alignment of the rods. This is clearly not observed (
This establishes a number of selection criteria for the ligand. of the nanorods. The ligand is preferably selected to lower the surface tension of the nanoparticles. This can be achieved in a number of ways such as using a long alky chain ligand, use of a branched ligand or by incorporating specific chemical groups such as fluorinated groups into the ligand. Preferably the ligand acts as a surfactant in the solvent which is used for deposition of the nanoparticles. This means that when the ligand molecule is dissolved in the solvent it lowers the surface tension of the solvent, i.e., by measuring and comparing the surface tension (for example, by using a Wilhelmy balance) of the solvent with and without ligand added suitable ligands that have a tendency to promote segregation of the nanoparticles to the surface can be selected. Ligands are preferred for which the surface tension of the solution with a certain concentration of ligand molecules is lower than that of the pure solvent.
Similarly, suitable ligands can also be selected by measuring and comparing the surface tension of the solvent with and without ligand modified nanoparticles. Ligands are preferred for which the surface tension of the nanoparticle loaded solution is lower than that of the pure solvent.
The ligand is also selected to have a low boiling point and relatively weak chemical bond with the surface in order to enable removal of the ligand from the surface by low-temperature annealing, typically at or below 250° C. The ligand is selected to interact favorably with the solvent used for the deposition of the nanoparticles in order to enable a high loading of nanoparticles and a stable dispersion. Finally, the length of the ligand is selected to provide an acceptable compromise between the required low surface tension of the nanoparticles and the need for a dense packing of the as-deposited nanoparticles. In the case of alkylamine ligands the use of octylamine provides such a compromise.
The ability to self-assemble the nanorods into well-aligned structures can be exploited to achieve significantly improved electrical transport in solution-processed ZnO films. We can control the alignment of the nanorods in spin-coated films that can easily be integrated into FET structures, and using ligands such as OCTA-ZnO it is possible to produce films with favourable in-plane alignment of the nanorods and domain size of several μm's. Here we investigate the correlation between the field-effect transistor performance and the nanorod alignment in spin-coated ZnO films with different ligands.
FETs were fabricated in a standard bottom-gate, top-contact configuration using highly doped silicon wafers acting as gate electrodes with a 300 nm SiO2 gate dielectric (
The transfer characteristics of the device fabricated from nanorods with different ligands are plotted in
We have also investigated whether the device performance can be enhanced further by subjecting the nanorod films to a post-deposition hydrothermal growth step in aqueous zinc solution. As shown in Example 3 this leads to growth of the nanorods on the substrate, fusing of the rods and results in further device improvement. Initial experiments have shown that after the hydrothermal growth step mobility values of 1.2-1.4 cm2V−1s−1 and ON/OFF ratio of 106˜107 can be achieved in highly crystalline films of OCTA-ZnO.
This self-assembly methods presented here are simple, and they can be applied to solution deposition techniques which are capable of producing uniform films over large areas. Examples are techniques, such as, but not limited to, spin coating, blade coating, curtain coating, gravure coating, capillary coating, zone casting. Particularly preferred are techniques that induce a unaxial, in-plane liquid flow, which can be used to align the low-surface tension ligand-modified nanoparticles uniaxially in the plane along the direction of flow.
Alternatively, printing techniques can be used for the deposition of the low-surface tension ligand-modified nanoparticles, such as, but not limited to, inkjet printing, screen printing, offset printing, gravure printing, or flexographic-printing.
Colloidal nanorods can thus be used for solution-processed electronic devices that can achieve performance levels which are not accessible with solution-processed organic semiconductors. The techniques for nanorod self-assembly can also be applied to other devices, including optoelectronic devices. The self-assembly techniques described in the present invention can also be applied to device configurations which require an out-of-plane alignment of the nanorods, such as solar cells or light-emitting diodes.
The present invention can be applied to other inorganic semiconducting nanorod materials, including, but not limited to, nanorods based on, comprising or consisting of SnO2, Si, Ge, SiGe, GaAs, GaP, InP, InAs, In2O3, ZnO, ZnS, ZnSe, ZnTe, CdS, CdSe, CdTe, HgS, HgSe, HgTe, PbS, PbSe, PbTe, SnO2, SnS2, SnSe2, SnTe2.
The processes and techniques described herein apply to the fabrication of a semiconducting layer and may be used in the manufacture of any devices that comprise a semiconducting layer, such as diodes, FETs, MOSFETs, BJTs and optoelectronic devices.
The present invention can also be applied to more complex shaped elongate nanoparticles that can be dispersed in solution, such as platelets, tetrapods, and other branched nanoparticles.[43] Such particles could be substituted for some or all of the nanorods disclosed in the above examples.
The post-deposition growth of the nanorods on the substrate, that fuses the individual, as-deposited nanorods can be performed by other solution- or vapour-phase growth techniques, such as, but not limited to, liquid phase epitaxy or chemical vapour deposition.
The present invention is not limited to the foregoing examples. Aspects of the present invention include all novel and/or inventive aspects of the concepts described herein and all novel and/or inventive combinations of the features described herein.
The applicant hereby discloses in isolation each individual feature described herein and any combination of two or more such features, to the extent that such features or combinations are capable of being carried out based on the present specification as a whole in the light of the common general knowledge of a person skilled in the art, irrespective of whether such features or combinations of features solve any problems disclosed herein, and without limitation to the scope of the claims. The applicant indicates that aspects of the present invention may consist of any such individual feature or combination of features. In view of the foregoing description it will be evident to a person skilled in the art that various modifications may be made within the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0516401.7 | Aug 2005 | GB | national |
| 0614553.6 | Jul 2006 | GB | national |
This application is a continuation application and claims priorty under 35 U.S.C. §120 to U.S. patent application No. 12/063,345, filed on Jun. 9, 2010, which claims priorty to International Application No. PCT/GB2006/002981, filed on Aug. 9, 2006, which claims priorty to U.K. Application GB0516401.7, filed on Aug. 9, 2005, and also claims priorty to U.K. Application GB0614553.6, filed on Jul. 21, 2006, the entire contents of which are hereby incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 7255846 | Ren et al. | Aug 2007 | B2 |
| 7265037 | Yang et al. | Sep 2007 | B2 |
| 20050072213 | Besnard et al. | Apr 2005 | A1 |
| 20050110064 | Duan et al. | May 2005 | A1 |
| 20060035101 | Yuan et al. | Feb 2006 | A1 |
| 20060284218 | Kaner et al. | Dec 2006 | A1 |
| 20070020771 | Dutta et al. | Jan 2007 | A1 |
| 20100329251 | Rodgers et al. | Dec 2010 | A1 |
| 20120225006 | O'Brien et al. | Sep 2012 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20140170818 A1 | Jun 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12063345 | US | |
| Child | 14187729 | US |