The present invention is in the field of nanostructures. More particularly, the invention provides devices, such as photovoltaic devices, comprising nanostructures, which optionally are part of a nanocomposite. Compositions comprising two populations of nanostructures of different materials or nanostructures and small molecules are also features of the invention, as are doped polymer nanocomposites and compositions useful for making nanocomposites. Methods of and systems for producing photovoltaic and other (e.g., layered) devices are also described.
Solar energy has long been looked to as a potential solution to the ever increasing energy needs of the planet's population. Increasing costs of mining fossil fuels, increased concerns over “greenhouse” emissions, and increasing instabilities in regions that house large reserves of fossil fuels have furthered interest in exploiting alternative energy strategies, including solar energy sources.
To date, solar energy conversion has generally relied upon either the direct harvesting of solar thermal energy, e.g., in heating applications, or in thermoelectric conversion, or through the direct conversion of photonic energy to electrical energy through the use of photovoltaic cells.
Current photovoltaic devices or cells employ thin layers of semiconductor material, e.g., crystalline silicon, gallium arsenide, or the like, incorporating a p-n junction to convert solar energy to direct current. While these devices are useful in certain applications, their efficiency has been somewhat limited, yielding conversion efficiencies, e.g. solar power to electrical power, of typically marginally better than 10%. While efficiencies of these devices have been improving through costly improvements to device structure, it is believed that physical limitations on these devices mean they will, at best, achieve a maximum efficiency of around 30%. For ordinary energy requirements, e.g., public consumption, the relative inefficiency of these devices, combined with their relatively high cost, when compared to other means of energy generation, have combined to inhibit the widespread adoption of solar electricity in the consumer markets. Instead, such systems have been primarily used where conventionally generated electricity is unavailable, e.g., in remote locations, terrestrial or otherwise, or where costs associated with bringing conventionally generated electricity, to a location where it is needed, more closely match the costs of photovoltaic systems.
Because of their construction and efficiency, currently marketed photovoltaics also come with a number of physical requirements. For example, because of their relative inefficiency, as well as their rigid construction, photovoltaic systems typically require adequate flat space that has appropriate sun exposure at all times, or at least during peak times, to meet the requirements for electricity for which the system is used.
Despite the issues with current photovoltaic technology, there is still a desire and a need to expand usage of solar electricity. In particular, there is generally a need for an improved photovoltaic cell that has one or more of: increased energy conversion efficiency, decreased manufacturing costs, greater flexibility and/or reasonable durability and/or longevity. The present invention meets these and a variety of other needs.
The invention includes nanocomposite based photovoltaic devices and their constituent elements, systems that incorporate such devices and elements, and methods of and systems for fabricating such devices and elements. For example, photovoltaic devices that include aligned nanostructures (e.g., nanocrystals) in a photoactive layer are an aspect of the invention. In a related aspect, devices comprising one or more types of nanostructures, including photovoltaic devices comprising multiple types of such structures, whether aligned or not, are another aspect of the invention. In either case, these devices can include or omit non-nanostructure elements in an active layer. For example, the nanostructures of such an active layer can be fused, partially fused or sintered to provide electron and/or hole carrying properties, e.g., between electrodes. Polymers, e.g., conductive polymers, and/or small molecules can be combined with nanostructure elements in a photoactive layer, though such polymers and/or small molecules are not required in many embodiments herein. Photovoltaic devices comprising a plurality of photoactive layers, e.g., in which the photoactive layers are separated by one or more electrode layers and/or recombination materials, are also provided. Systems that comprise such devices, as well as methods and systems for fabricating such devices, are also an aspect of the invention. Active layer compositions, e.g., that can be used in photovoltaic and other devices, as well as related methods and systems, are an additional feature of the invention.
Accordingly, in a first general set of photovoltaic device embodiments, the invention provides photovoltaic devices. The devices include a first electrode layer and a second electrode layer. A first photoactive layer is disposed between the first and second electrode layers. The photoactive layer is disposed in at least partial electrical contact with the first electrode along a first plane, and in at least partial electrical contact with the second electrode along a second plane. The photoactive layer comprises material that exhibits a type II band offset energy profile, and includes a first population of nanostructures (e.g., nanocrystals) each having at least one elongated section oriented predominantly normal to at least the first plane.
The nanostructures can include any of a variety of structures, e.g., branched nanocrystals having more than one elongated segment, e.g., four elongated segments connected at a common apex, and arranged in a substantially tetrahedral geometry (e.g., nanotetrapods). The nanostructures can include materials that facilitate function in the photoactive layer, e.g., optionally including at least a portion that is comprised of a semiconductor selected from Group II-VI, Group III-V or Group IV semiconductors or alloys thereof. For example, the population of nanostructures can include nanocrystals that include one or more of: CdS, CdSe, CdTe, InP, InAs, ZnS, ZnSe, ZnTe, HgTe, GaN, GaP, GaAs, GaSb, InSb, Si, Ge, AlAs, AlSb, PbSe, PbS, or PbTe. The precise form of the nanostructure can vary, e.g., optionally including any of: a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The population of nanostructures can include structures that include more than one subcomponent, e.g., such as nanocrystals that comprise a core of a first semiconductor material and a shell of a second (different) semiconductor material. For photovoltaic devices, the first and second semiconductor materials typically display a type-II band offset profile. Any of a variety of materials can be used to achieve this desirable property, including nanocrystals in which the core comprises CdSe and the shell comprises CdTe, or nanocrystals in which the core comprises InP and the shell comprises GaAs. These nanostructure features are generally applicable to the other device, method, composition and system embodiments noted below.
The photoactive layer optionally comprises a matrix, e.g., in which the nanocrystals are suspended or disposed. For example, the layer can include nanocrystals disposed in a conductive polymer matrix. The nanocrystals are optionally coupled to the polymer matrix, e.g., via a covalent chemical linkage. For example, in one embodiment, the chemical linkage comprises a ligand coupled at a first position to an outer surface of the nanocrystal and at a second position to the polymer matrix. The nanocrystals are optionally electrically coupled to the polymer matrix. As another example, the photoactive layer can include nanocrystals disposed in a matrix comprising a small molecule (e.g., a semiconductive, organic, nonpolymeric molecule, e.g., a molecule with a molecular weight less than 3000, 2000, 1500, 1000, 500, or less). The matrix comprising the small molecule optionally also comprises a polymer, e.g., a nonconductive or conductive polymer (e.g., the photoactive layer can comprise a doped-polymer nanocomposite). Either the nanocrystals or the matrix (or both) can conduct holes or electrons. Furthermore, as noted in more detail herein, the matrix is optionally omitted from the devices herein, with nanostructures providing both electron and hole carrying properties to the electrodes (e.g., where two or more nanocrystal types are fused, partially fused or sintered together, optionally in the absence of any additional conductive (or other) polymer in the matrix).
The arrangement of nanostructures in the photoactive layer can be modified to enhance the activity of the photoactive layer. For example, in one aspect, one or more of the nanostructures or nanostructure types in the layer are positioned predominantly closer to the first electrode than to the second electrode (e.g., to facilitate electron or hole conductance to the relevant electrode). Similarly, the device can include components that similarly facilitate properties of the layer, e.g., the device can include a hole or electron blocking layer disposed between the photoactive layer and the first or second electrode. Similarly, the device optionally includes a hole blocking layer disposed between the photoactive layer and the first electrode and an electron blocking layer disposed between the photoactive layer and the second electrode (e.g., to control flow of electrons or holes to the relevant electrode).
The nanostructures can include multiple distinct subtypes. For example, the population of nanostructures in the photoactive layer can include at least two different nanocrystal subpopulations, each nanocrystal subpopulation, e.g., having a different absorption spectrum. Thus, the different nanocrystal subpopulations optionally include different compositions, different size distributions, different shapes and/or the like.
In one aspect, the nanostructures in the photoactive layer collectively comprise at least two inorganic materials. For example, the nanostructures optionally comprise a core of a first inorganic material and a shell of a second inorganic material, and/or the photoactive layer can comprise at least two types of nanocrystals. Any of the nanostructures in the photoactive layer can optionally be fused, partially fused, and/or sintered. Where the nanostructures are fused, partially fused, and/or sintered, e.g., the cores of at least two adjacent nanostructures in the photoactive layer are optionally in at least partial electrical contact, and the shells of the at least two adjacent nanostructures, or at least two additional nanostructures, are optionally in at least partial direct electrical contact.
The photoactive layer optionally includes one or more sublayers. For example, the photoactive layer can include at least two active sublayers, with each of the active sublayers comprising a plurality of nanocrystals of at least one nanocrystal type. In one such embodiment, at least one of the at least two sublayers comprises an n-type sublayer and at least one of the two sublayers comprises a p-type sublayer, optionally meeting at one or more junction in the photoactive layer (e.g., a p-n or n-p-n or other junction). In an alternate related embodiment, the photoactive layer includes at least one sublayer that includes a blend of p and n nanocrystals. In another example, the photoactive layer includes at least two active sublayers, with at least one of the sublayers comprising the population of nanostructures and at least one of the sublayers (e.g., at least one other sublayer) comprising a small molecule.
In addition to the photoactive layer comprising sublayers, the overall device architecture can also be layered. For example, the device can include a plurality of photoactive layers (at least a second photoactive layer, and, optionally, more than two such layers). One or more electrode (and, typically, two electrodes) can be placed in electrical contact with any such photoactive layer of the device. For example, the device can include a third electrode layer, a fourth electrode layer and a second photoactive layer disposed between the third and fourth electrode layers. In this embodiment, the second photoactive layer is optionally disposed in at least partial electrical contact with the third electrode along a third plane, and in at least partial electrical contact with the fourth electrode along a fourth plane. Optionally, the second photoactive layer exhibits a type II band offset energy profile, and comprises a second population of nanostructures each having at least one elongated section oriented predominantly normal to at least the third plane, and having a different absorption spectrum from the first population of nanostructures. The third electrode layer, fourth electrode layer and second photoactive layer are optionally attached to, but electrically insulated from, the first electrode layer, second electrode layer and first photoactive layer. As another example, the device can include a third electrode layer and a second photoactive layer disposed between the second and third electrode layers. In this embodiment, the second photoactive layer is disposed in at least partial electrical contact with the second electrode and in at least partial electrical contact with the third electrode. As yet another example, the device can include a second photoactive layer and a first recombination material disposed between the first and second photoactive layers. The first recombination material is in at least partial electrical contact with the first and second photoactive layers. The first recombination material can, e.g., be discontinuous or can form a continuous layer between the first and second photoactive layers.
Similar to the elements of the photoactive layer, the electrodes can also be selected to regulate overall device properties. For example, the electrodes can be made of any suitable conductive material, selected based upon charge carrying capabilities, environmental tolerance properties, or the like. For example, in one aspect, at least one of the electrodes optionally comprises aluminum or another metal. Furthermore, the properties of the electrodes or photoactive layers can be selected to provide a desired overall device property. For example, where a flexible photovoltaic device is desirable, the first and/or second electrodes or the photoactive layer can be selected to be flexible. Similarly, the first and/or second electrodes and/or photoactive layer optionally include additional device elements to protect the device from its working environment, and/or to enhance device properties. For example, in one aspect, any of the electrodes or the photoactive layer (or any combination thereof), can include a transparent layer (e.g., a transparent conductive layer). For example, in one aspect, the device includes a transparent support layer at least partially covering the first or second electrode, or at least partially covering the photoactive layer, or at least partially covering a combination thereof. Similarly, the device can include one or more sealing layers, e.g., the photoactive layer and/or one or more of the electrodes can comprise or be sealed within a sealing layer. For example, in one embodiment, the photoactive layer is hermetically sealed. In one example embodiment, the device comprises at least first and second sealing layers, the photoactive layer and first and second electrodes being sandwiched between the first and second sealing layers.
The overall architecture of the device can be selected based upon the use to which the device is to be put. For example, the overall device can comprise a planar or a non-planar architecture. For example, the device optionally comprises a convex architecture to enhance efficiency of the device in settings where convex architecture is desired. Similarly, in one embodiment, the first electrode layer, the photoactive layer and the second electrode layer are optionally oriented in a coiled architecture, or in a reciprocating stacked architecture.
In a related second set of embodiments, the nanocrystals are optionally oriented as noted in the embodiments above, but can, optionally, be oriented differently. That is, the nanostructures can be in any random or non-random orientation with respect to the various planes and electrodes noted above. In these embodiments, the nanostructures include at least one of the inorganic materials of the photovoltaic device, and optionally two or more such materials. The polymer components of the matrix of the photoactive layer noted above is an optional feature of these embodiments (the polymer can be retained or omitted in the photoactive layer).
Thus, in this second set of embodiments, a photovoltaic device is provided. The device includes a first electrode layer and a second electrode layer. A first photoactive layer is disposed between the first and second electrode layers. The photoactive layer is disposed in at least partial electrical contact with the first electrode along a first plane and in at least partial electrical contact with the second electrode along a second plane, wherein the photoactive layer comprises a first inorganic material and a second inorganic material different from the first inorganic material. In PV devices, the first and second inorganic materials typically exhibit a type II band offset energy profile. The photoactive layer includes a first population of nanostructures, which nanostructures comprise the first inorganic material, the second inorganic material, or a combination thereof.
All of the features noted above with respect to nanostructure type, shape and composition, electrode composition and configuration and device architecture apply to these embodiments as well. Any of the optional transparent/blocking/sealing layer embodiments of the first set of embodiments can be features of the second set of embodiments as well. As in the embodiments described above, the device can include a plurality of photoactive layers, optionally with one or more additional electrode layers and/or recombination materials. Similarly, device architecture features noted above are applicable here as well. Unless noted otherwise, any feature of the first class of photovoltaic device embodiments noted above or otherwise herein can be applied to this second class of embodiments.
As above, the first inorganic material is optionally (and typically) a semiconductor, as is the second inorganic material. The materials can be any of those noted for the preceding embodiments. As with the preceding embodiments, the first population of nanostructures can include nanocrystals that comprise a core of the first inorganic material and a shell of the second inorganic material, e.g., any of those noted above. The nanocrystals are optionally fused, partially fused, and/or sintered, as in the preceding embodiments, providing for partial and/or direct electrical contact between nanostructure cores or shells as noted above.
In one such embodiment, the first population of nanostructures comprises nanocrystals comprising the first inorganic material, and the photoactive layer further comprises a second population of nanocrystals comprising nanocrystals which comprise the second inorganic material, e.g., wherein adjacent nanocrystals are in at least partial direct electrical contact with each other.
The nanocrystals of the first population and the nanocrystals of the second population are optionally intermixed in the photoactive layer. Alternately, the photoactive layer comprises at least a first sublayer and a second sublayer, wherein the first sublayer comprises the first population of nanocrystals and the second sublayer comprises the second population of nanocrystals.
As in the embodiments above, the photoactive layer optionally comprises at least two active sublayers, each of which optionally includes a plurality of nanocrystals of at least one nanocrystal type. As noted in the examples above, and as applicable to these embodiments as well, at least one of the at least two sublayers optionally comprises an n-type sublayer and/or a p-type sublayer, e.g., in any of the arrangements noted above (e.g., blended or separate p and/or n nanostructures, in blended or separate layers, optionally separated by one or more junctions).
For this set of embodiments, the photoactive layer can simply consist of nanocrystals, e.g., fused, partially fused or sintered nanocrystals. However, a polymer or matrix can also be included in the photoactive layer. For example, the photoactive layer can include a conductive or non-conductive polymer. The layer can include such a polymer matrix in which nanocrystals are disposed, e.g., in which nanocrystals of the first and/or second populations are electrically coupled to the polymer to provide for conductance of holes or electrons (e.g., to the electrodes of the device). However, such a polymer or other matrix component is not required, and the photoactive layer is optionally substantially free of any conductive and/or non-conductive polymer.
While the orientation of the first set of embodiments is not required in this second set of embodiments, the noted orientation is, optionally, a feature of the second set of embodiments as well. For example, the nanostructures of the first population can each have at least one elongated section oriented predominantly normal to at least the first plane. Similarly, the second population of nanostructures can display the same (or a different) orientation.
Another set of embodiments includes, for example, photovoltaic devices in which the photoactive layer includes nanostructures and a doped polymer or small molecule (e.g., the photoactive layer can include a nanocomposite having nanostructures in a doped polymer or small molecule matrix). Thus, a third general class of embodiments provides a photovoltaic device including a first electrode layer, a second electrode layer, and a first photoactive layer disposed between the first and second electrode layers. The photoactive layer is disposed in at least partial electrical contact with the first electrode (e.g., along a first plane) and in at least partial electrical contact with the second electrode (e.g., along a second plane). The photoactive layer comprises a first population of nanostructures and a small molecule and/or a conductive polymer whose charge carrying properties have been altered by controlled partial oxidation of the polymer. The nanostructures and the oxidized conductive polymer or the small molecule typically exhibit a type II band offset energy profile.
The small molecule typically comprises a semiconductive, organic, nonpolymeric molecule. In most embodiments, the small molecule has a molecular weight less than 3000, less than 2000, less than 1500, less than 1000, or less than 500. Typically, the nanostructures conduct electrons and thus the small molecule conducts holes; however, the small molecule can conduct electrons, holes, or a combination thereof.
In certain embodiments, the photoactive layer comprises a nanocomposite. Thus, in one class of embodiments, the nanostructures are disposed in a matrix comprising the oxidized conductive polymer or the small molecule. In embodiments in which the matrix comprises the small molecule, the matrix optionally comprises a polymer (e.g., a conductive polymer) in which the small molecule and the nanostructures are disposed. In another class of embodiments, the photoactive layer comprises at least two sublayers, with at least one of the sublayers comprising the nanostructures and at least one of the sublayers (e.g., at least one other sublayer) comprising the oxidized conductive polymer or the small molecule.
In embodiments in which the photoactive layer comprises the small molecule, the photoactive layer can be substantially free of polymer. Alternatively, the photoactive layer can include a polymer. For example, the small molecule can dispersed in a polymer (e.g., a nonconductive or a conductive polymer).
All of the features noted above with respect to nanostructure type, shape and composition, electrode composition and configuration, and device architecture apply to these embodiments as well. Any of the optional transparent, blocking, and/or sealing layer embodiments described above can be features of this set of embodiments as well. As in the embodiments described above, the device can include a plurality of photoactive layers, optionally with one or more additional electrode layers and/or recombination materials. Unless noted otherwise, any feature of the photovoltaic device embodiments noted above or otherwise herein can be applied to this class of embodiments.
Yet another set of embodiments includes photovoltaic devices comprising a plurality of photoactive layers, in which adjacent active layers are separated by a recombination material. Thus, one general class of embodiments provides a photovoltaic device including a first electrode layer, a second electrode layer, a first recombination material disposed between the first and second electrode layers, a first photoactive layer disposed between the first electrode layer and the first recombination material, and a second photoactive layer disposed between the first recombination material and the second electrode layer. The first photoactive layer is disposed in at least partial electrical contact with the first electrode (e.g., along a first plane) and with the first recombination material. Similarly, the second photoactive layer is disposed in at least partial electrical contact with the second electrode (e.g., along a second plane) and with the first recombination material. The first photoactive layer comprises a first population of nanostructures, and the second photoactive layer comprises a second population of nanostructures. The first and second photoactive layers typically each comprise a material that exhibits a type II band offset energy profile.
The first recombination material can be, e.g., discontinuous or continuous. Thus, in one class of embodiments, the first recombination material comprises a recombination layer disposed between the first and second photoactive layers. The first recombination material can comprise any of a variety of materials, including, but not limited to, a metal, a conductive polymer, and/or a small molecule (e.g., aluminum, silver, gold, PEDOT:PSS, TPD, NPD, and/or TAZ). The first recombination material is optionally transparent.
All of the features noted above with respect to nanostructure type, shape and composition, electrode composition and configuration and device architecture apply to these embodiments as well. Any of the optional transparent, blocking, and/or sealing layer embodiments described above can be features of this set of embodiments as well. Unless noted otherwise, any feature of the photovoltaic device embodiments noted above or otherwise herein can be applied to this class of embodiments.
For example, the photoactive layer can include oriented nanostructures. Thus, in one class of embodiments, each nanostructure of the first population has at least one elongated section oriented predominantly normal to at least the first plane and/or each nanostructure of the second population has at least one elongated section oriented predominantly normal to at least the second plane. As another example, in certain embodiments, the first photoactive layer comprises a first population of nanocrystals disposed in a conductive polymer matrix and/or the second photoactive layer comprises a second population of nanocrystals disposed in a conductive polymer matrix (e.g., a conductive polymer matrix whose charge carrying properties have been altered by controlled partial oxidation of the polymer). In a similar example, the first photoactive layer comprises a first population of nanocrystals disposed in a matrix comprising a small molecule and/or the second photoactive layer comprises a second population of nanocrystals disposed in a matrix comprising a small molecule (as noted above, the matrix optionally also includes a polymer). In yet another example, the first photoactive layer comprises a first inorganic material and a second inorganic material different from the first inorganic material and/or the second photoactive layer comprises a third inorganic material and a fourth inorganic material different from the third inorganic material. The first and second (or third and fourth) inorganic materials exhibit a type II band offset energy profile. The nanostructures of the first population comprise the first inorganic material, the second inorganic material, or a combination thereof, and/or the nanostructures of the second population comprise the third inorganic material, the fourth inorganic material, or a combination thereof.
The device optionally includes additional photoactive layers and/or recombination materials. For example, the photovoltaic device can include a third photoactive layer disposed between the second photoactive layer and the second electrode and a second recombination material disposed between the second and third photoactive layers, where the third photoactive layer is in at least partial electrical contact with the second recombination material and with the second electrode.
Yet another set of embodiments includes photovoltaic devices comprising a plurality of photoactive layers, in which adjacent active layers are separated by an electrode. Thus, one general class of embodiments provides a photovoltaic device including a first electrode layer, a second electrode layer, a third electrode layer, a first photoactive layer disposed between the first electrode layer and the second electrode layer, and a second photoactive layer disposed between the second electrode layer and the third electrode layer. The first photoactive layer is disposed in at least partial electrical contact with the first electrode (e.g., along a first plane) and with the second electrode (e.g., along a second plane), and the second photoactive layer is disposed in at least partial electrical contact with the second electrode (e.g., along a third plane) and with the third electrode (e.g., along a fourth plane). The first photoactive layer comprises a first population of nanostructures, and the second photoactive layer comprises a second population of nanostructures. Typically, the first and second photoactive layers each comprises a material that exhibits a type II band offset energy profile.
All of the features noted above with respect to nanostructure type, shape and composition, electrode composition and configuration and device architecture apply to these embodiments as well. Any of the optional transparent, blocking, and/or sealing layer embodiments described above can be features of this set of embodiments as well. Unless noted otherwise, any feature of the photovoltaic device embodiments noted above or otherwise herein can be applied to this class of embodiments.
For example, the photoactive layer can include oriented nanostructures. Thus, in one class of embodiments, each nanostructure of the first population has at least one elongated section oriented predominantly normal to at least the first plane and/or each nanostructure of the second population has at least one elongated section oriented predominantly normal to at least the third plane. As another example, in certain embodiments, the first photoactive layer comprises a first population of nanocrystals disposed in a conductive polymer matrix and/or the second photoactive layer comprises a second population of nanocrystals disposed in a conductive polymer matrix (e.g., a conductive polymer matrix whose charge carrying properties have been altered by controlled partial oxidation of the polymer). In a similar example, the first photoactive layer comprises a first population of nanocrystals disposed in a matrix comprising a small molecule and/or the second photoactive layer comprises a second population of nanocrystals disposed in a matrix comprising a small molecule (as noted above, the matrix optionally also includes a polymer). In yet another example, the first photoactive layer comprises a first inorganic material and a second inorganic material different from the first inorganic material and/or the second photoactive layer comprises a third inorganic material and a fourth inorganic material different from the third inorganic material. The first and second (or third and fourth) inorganic materials exhibit a type II band offset energy profile. The nanostructures of the first population comprise the first inorganic material, the second inorganic material, or a combination thereof, and/or the nanostructures of the second population comprise the third inorganic material, the fourth inorganic material, or a combination thereof.
The device optionally includes additional photoactive and/or electrode layers. For example, the photovoltaic device can include a fourth electrode layer and a third photoactive layer disposed between the third and fourth electrode layers, where the third photoactive layer is in at least partial electrical contact with the third and fourth electrode layers.
In addition to photovoltaic devices, the invention further provides compositions useful for constructing photovoltaic and other devices. These compositions can include or be comprised within photovoltaic or other devices (e.g., LEDs, dual crystal devices, etc). For example, a composition comprising a first population of nanostructures and a second population of nanostructures is provided. The first population comprises nanostructures comprising a first material, and the second population comprises nanostructures comprising a second material different from the first material.
As in the preceding embodiments, the nanostructures optionally include nanocrystals and/or nanowires. As in the preceding devices, the nanostructures can also comprise single-crystal nanostructures, double-crystal nanostructures, polycrystalline nanostructures, or amorphous nanostructures. Typically, the first material of the nanostructures is a first inorganic material and the second material is a second inorganic material. Optionally, the first material comprises a first semiconductor and the second material comprises a second semiconductor. For example, the first material optionally comprises an n-type semiconductor and the second material optionally comprises a p-type semiconductor. As in the photovoltaic devices noted above, the first and second materials can exhibit a type II band offset energy profile. However, in certain non-photovoltaic applications (e.g., LEDs), the first and second materials exhibit other energy profiles, e.g., a type I band offset energy profile. As in the photovoltaic devices noted above, adjacent nanostructures are optionally in at least partial (or direct) electrical contact with each other.
Optionally, the nanostructures of the first population and the nanostructures of the second population are in separate layers, or are intermixed. The populations can be located in one or more discrete or mixed regions, zones, layers, or the like. The composition can be formed into a film.
The composition optionally includes at least a first sublayer and a second sublayer. In such embodiments, the first sublayer optionally includes the first population of nanostructures and the second sublayer optionally includes the second population of nanostructures. In several applications, e.g., photovoltaic applications, the film or other composition is disposed between two electrode layers (or between additional electrode layers). As with the photovoltaic applications noted above, the nanostructures of the first and/or second populations are optionally fused, partially fused, and/or sintered (or not fused, partially fused or sintered).
The composition optionally includes a conductive polymer. For example, the composition optionally includes a polymer matrix in which nanostructures are disposed. Optionally, any feature of the nanostructures (surface, core, shell, etc.) are electrically coupled to the polymer. The polymer matrix can alternately or additionally be non-conductively coupled to the nanostructures. Alternately, the composition can be substantially free of conductive and/or non-conductive polymer.
Another general class of embodiments provides a composition including a first population of nanostructures disposed in a matrix. The matrix comprises a conductive polymer whose charge carrying properties have been altered by controlled partial oxidation of the polymer and/or a polymer (e.g., a conductive polymer) and a small molecule.
Any of the features of the device and composition embodiments described above can be applied to this class of embodiments as well, to the extent they are relevant. For example, nanostructure type, shape, and composition can be varied as described above. As another example, the small molecule can, e.g., comprise a semiconductive, organic, nonpolymeric molecule; have a molecular weight less than 3000, 2000, 1500, 1000, or 500; and/or conduct electrons, holes, or a combination thereof. It is worth noting that the nanostructures and the matrix can exhibit, e.g., a type I or a type II band offset energy profile.
Yet another general class of embodiments provides a composition including a first population of nanostructures and a small molecule. Each nanostructure of the first population has at least one elongated section oriented predominantly normal to at least a first plane. Typically, the nanostructures are disposed in a matrix comprising the small molecule. The matrix optionally also includes a polymer, e.g., a conductive polymer.
Any of the features of the device and composition embodiments described above can be applied to this class of embodiments as well, to the extent they are relevant. For example, nanostructure type, shape, and composition can be varied as described above. As another example, the small molecule can, e.g., comprise a semiconductive, organic, nonpolymeric molecule; have a molecular weight less than 3000, 2000, 1500, 1000, or 500; and/or conduct electrons, holes, or a combination thereof. It is worth noting that the composition is optionally formed into a film, e.g., a film in which the elongated section of each nanostructure is oriented predominantly normal to a surface of the film.
Still another general class of embodiments provides a composition that can, e.g., be used to form a nanocomposite layer. The composition includes a population of nanostructures, a polymer and/or a small molecule, a first solvent, and a second solvent. The first solvent has a vapor pressure that is not equal to a vapor pressure of the second solvent. At least one of the first and second solvents is free of chloroform and pyridine.
The nature and relative proportion of the first and second solvents can be varied, e.g., depending on the composition of the nanostructures, the identity of the polymer and/or small molecule, and the desired morphology of the resulting nanocomposite film. For example, the two solvents can have different polarities, and the vapor pressure of the first solvent can be lower or higher than that of the second solvent.
The ratio of the first and second solvents can be varied experimentally to determine a ratio that results in the nanocomposite layer having a selected morphology, e.g., wherein the nanostructures are distributed uniformly throughout the polymer or small molecule matrix. The ratio of the first solvent to the second solvent can have essentially any value that results in the nanocomposite layer having the selected morphology. Typically, the ratio of the first solvent to the second solvent is greater than 0.05:0.95 and less than 0.95:0.05 by volume. For example, the ratio can be greater than 0.1:0.9 and less than 0.9:0.1, greater than 0.15:0.85 and less than 0.85:0.15, greater than 0.2:0.8 and less than 0.8:0.2, or, typically, greater than 0.3:0.7 and less than 0.7:0.3, by volume.
The first and second solvents can be essentially any of the large number of solvents known in the art. Choice of solvents can depend, e.g., on the identity of the polymer or small molecule, the material(s) comprising the nanostructures, the technique used to coat the substrate, and/or the like. Preferably, the solvents each have a polarity such that the nanostructures are soluble in at least one of the two miscible solvents and the polymer and/or small molecule is soluble in at least the other of the two solvents. Suitable solvents include, but are not limited to, chloroform, toluene, tetrahydrofuran (THF), xylene, a hexane, chlorobenzene, and dichlorobenzene. For example, the first solvent (in which, e.g., the nanostructures are dissolved) can be toluene and the second solvent (in which, e.g., the polymer or small molecule is dissolved) can be chloroform. The first mixture optionally includes three or more solvents.
Any of the features of the device and composition embodiments described above can be applied to this class of embodiments as well, to the extent they are relevant. For example, nanostructure type, shape, and composition can be varied as described above.
In addition to the devices and compositions noted above, related methods and systems are also provided. In a first class of methods, methods of producing a photovoltaic device are provided. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided. The first substrate is coated with a photoactive matrix that exhibits a type II band offset energy profile. The photoactive matrix includes at least a first population of elongated semiconductor nanostructures, comprising longitudinal axes, to provide a photoactive layer. The semiconductor nanostructures are oriented such that their longitudinal axes are predominantly oriented normal to the first planar substrate. A second conductive layer is laminated onto the photoactive layer.
Essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix.
The method optionally includes providing a blocking layer on the first substrate prior to coating the first substrate with a photoactive matrix. Similarly, the method can include providing a blocking layer on the photoactive layer prior to laminating the second conductive layer onto the photoactive layer. One or more sealing layers can optionally be provided over opposing surfaces of the photovoltaic device in addition to first substrate and second conductive layer, whereby the one or more sealing layers hermetically seal the photovoltaic device.
A second class of methods of producing a photovoltaic device is also provided. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided. The first substrate is coated with a composition that comprises a population of nanostructures to provide a photoactive layer. The nanostructures comprise a core of a first material and a shell of a second material different from the first material. The nanostructures are fused, partially fused, and/or sintered, and a second conductive layer is laminated onto the photoactive layer.
As in the preceding class of methods, essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix. Typically, the first material is a first inorganic material and the second material is a second inorganic material. For example, the first material optionally includes a first semiconductor and the second material optionally includes a second semiconductor.
As in the preceding class of methods, the methods optionally include providing a blocking layer on the first substrate prior to coating the first substrate with the composition. Similarly, the methods optionally include providing a blocking layer on the photoactive layer prior to laminating the second conductive layer onto the photoactive layer. One or more sealing layers can be provided over opposing surfaces of the photovoltaic device, whereby the one or more sealing layers hermetically seal the photovoltaic device.
In a third class of method embodiments, methods of producing a layered device comprising a first population of nanostructures and a second population of nanostructures are provided. The first population includes nanostructures comprising a first material, and the second population comprises nanostructures comprising a second material different from the first material. The methods include providing a first substrate, and coating the first substrate with a composition comprising the first population of nanostructures to provide a first layer.
As in the preceding classes of methods, essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix. Typically, the first material is a first inorganic material and the second material is a second inorganic material. For example, the first material optionally includes a first semiconductor and the second material optionally includes a second semiconductor.
Coating the first substrate with a composition comprising the first population of nanostructures optionally includes coating the first substrate with a composition comprising a mixture of the first and second populations of nanostructures. This provides a first layer in which the nanostructures of the first and second populations are intermixed.
The method optionally further includes coating the first substrate with a composition comprising the second population of nanostructures, to provide a second layer. For example, the second population of nanostructures can be disposed on the first substrate.
The first substrate can be planar or non-planar, e.g., any of the geometries noted for the devices above. The method can be used to produce a photovoltaic device, a luminescent device, or the like. A first conductive layer can be disposed on the first planar substrate and a second conductive layer can optionally be layered onto the first (or second) layer.
In the methods, a blocking layer is optionally provided on the first substrate prior to coating the first substrate with the composition comprising the first population of nanostructures. Similarly, a blocking layer can be provided on the first layer prior to laminating the second conductive layer onto the first (or second) layer. As in the methods above, one or more sealing layers can be provided over opposing surfaces of the device, whereby the one or more sealing layers optionally hermetically seal the device.
Another class of method embodiments provides methods of producing a photovoltaic device. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided and coated with a composition that comprises a first population of nanostructures to provide a first photoactive layer. A second conductive layer is layered onto the first photoactive layer. The second conductive layer is coated with a composition that comprises a second population of nanostructures to provide a second photoactive layer, and a third conductive layer is layered onto the second photoactive layer.
As in the preceding classes of methods, essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix. Similarly, features of the methods described above can be applied to this class of methods as well, e.g., with respect to provision of blocking and sealing layers.
Yet another class of method embodiments provides methods of producing photovoltaic devices. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided and coated with a composition that comprises a first population of nanostructures to provide a first photoactive layer. A first recombination material is disposed onto the first photoactive layer. The first recombination material (and any exposed portion of the first photoactive layer) is coated with a composition that comprises a second population of nanostructures to provide a second photoactive layer, and a second conductive layer is layered onto the second photoactive layer. In certain embodiments, disposing the first recombination material onto the first photoactive layer comprises coating the first photoactive layer with the first recombination material to provide a first recombination layer.
As in the preceding classes of methods, essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix. Similarly, features of the methods described above can be applied to this class of methods as well, e.g., with respect to provision of blocking and sealing layers.
Yet another class of method embodiments provides methods of forming a nanocomposite layer, for example, during fabrication of a photovoltaic or other layered device. In the methods, a planar substrate and a first mixture are provided, and the substrate is coated with the first mixture to provide the nanocomposite layer. The first mixture includes a population of nanostructures, a polymer and/or a small molecule, a first solvent, and a second solvent. The first and second solvents have different vapor pressures, e.g., at a given temperature, e.g., the temperature at which the substrate is coated with the first mixture. At least one of the first and second solvents is free of chloroform and pyridine. The majority of the first and second solvents (e.g., substantially all of the first and second solvent) is typically permitted to evaporate during or following the coating step, such that little or no solvent remains in the resulting nanocomposite layer.
In one class of embodiments, the nanostructures are provided in the first solvent and the polymer and/or the small molecule is provided in the second solvent. The nanostructures in the first solvent and the polymer and/or small molecule in the second solvent are combined, resulting in the first mixture.
The nature and relative proportion of the first and second solvents can be varied, e.g., depending on the composition of the nanostructures, the identity of the polymer and/or small molecule, and the desired morphology of the resulting nanocomposite film. For example, the vapor pressure of the first solvent can be lower or higher than that of the second solvent, and the first solvent can be more or less polar than the second solvent. To produce a nanocomposite layer including inorganic semiconductor nanocrystals and an organic polymer, for example, the first solvent in which the nanocrystals are suspended typically has a lower vapor pressure (i.e., is less volatile) and is less polar than the second solvent in which the polymer is dissolved; in other embodiments, the first solvent has a higher vapor pressure and/or is more polar than the second solvent.
The ratio of the first and second solvents can be varied experimentally to determine a ratio that results in the nanocomposite layer having a selected morphology, e.g., wherein the nanostructures are distributed uniformly throughout the polymer or small molecule matrix. The ratio of the first solvent to the second solvent can have essentially any value that results in the nanocomposite layer having the selected morphology. Typically, the ratio of the first solvent to the second solvent is greater than 0.05:0.95 and less than 0.95:0.05 by volume. For example, the ratio can be greater than 0.1:0.9 and less than 0.9:0.1, greater than 0.15:0.85 and less than 0.85:0.15, greater than 0.2:0.8 and less than 0.8:0.2, or, typically, greater than 0.3:0.7 and less than 0.7:0.3, by volume.
The first and second solvents can be essentially any of the large number of solvents known in the art. Choice of solvents can depend, e.g., on the identity of the polymer or small molecule, the material(s) comprising the nanostructures, the technique used to coat the substrate, and/or the like. Preferably, the solvents each have a polarity such that the nanostructures are soluble in at least one of the two miscible solvents and the polymer or small molecule is soluble in at least the other of the two solvents. Suitable solvents include, but are not limited to, chloroform, toluene, tetrahydrofuran (THF), xylene, a hexane, chlorobenzene, and dichlorobenzene. For example, the first solvent (in which, e.g., the nanostructures are dissolved) can be toluene and the second solvent (in which, e.g., the polymer or small molecule is dissolved) can be chloroform. The first mixture optionally includes three or more solvents.
The substrate can be coated with the mixture by any of a variety of techniques known in the art. For example, the substrate can be spin coated with the first mixture. As another example, the first mixture can be applied to the substrate with a doctor-blade. As still other examples, the first mixture can be applied to the substrate by screen printing, ink-jet printing, dip coating, sheer coating, tape casting, or film casting.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of blocking and/or sealing layers, and the like. It is worth noting that the planar substrate optionally has a first conductive layer disposed thereon.
Systems for fabricating a photovoltaic device are also provided. For example, such a system can include a source of a first substrate layer, having a first conductive surface. The system can also include a conveyor system for conveying the first substrate layer. A source of a photoactive matrix can be fluidly coupled to a layer deposition system, the layer deposition system being at least partially disposed over the substrate conveyor system, to provide a layer of photoactive matrix on the first substrate layer. A source of a second conductive material is coupled to the layer deposition system positioned over the substrate conveyor system for depositing a layer of the second conductive surface material onto a layer of photoactive matrix deposited on the first substrate layer.
In one example embodiment, the source of first substrate material includes a rolled sheet of the first substrate material. The source of first substrate material optionally includes a source of first conductive material and a deposition system for depositing the first conductive material onto the first substrate material to provide the first conductive surface.
The layer deposition system can include, e.g., a doctor-blade, a screen printing system, an ink-jet printing system, a dip coating system, a sheer coating system, a tape casting system, a film casting system, or a combination thereof.
In a related class of embodiments, a system for fabricating a layered device is also provided. The system includes a first population of nanostructures and a second population of nanostructures. The first population comprises nanostructures comprising a first material, and the second population comprises nanostructures comprising a second material different from the first material. The system also includes a source of a first substrate layer; a conveyor system for conveying the first substrate layer; and, a source of a composition comprising the first and second populations of nanostructures, fluidly coupled to a layer deposition system, the layer deposition system being at least partially disposed over the substrate conveyor system, to provide a layer in which the nanostructures of the first and second populations are intermixed on the first substrate layer.
As in the devices, systems and methods above, the nanostructures can comprise nanocrystals or any of the other nanostructures noted herein or otherwise applicable. For example, the nanostructures can include nanocrystals and/or nanowires. The nanostructures can include, e.g., a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. Similarly, the first and second material can be any of those noted above, e.g., the first material can be a first inorganic material and the second material can be a second inorganic material. Optionally, the first substrate layer has a first conductive surface.
The system optionally includes a source of a second conductive material coupled to the layer deposition system, e.g., positioned over the substrate conveyor system for depositing a layer of the second conductive material onto the layer of intermixed nanostructures deposited on the first substrate layer.
As in the systems above, the source of first substrate material can optionally include a rolled sheet of first substrate material. Similarly, the source of first substrate material can further include a source of first conductive material and a deposition system for depositing the first conductive material onto the first substrate material to provide a first conductive surface. The layer deposition system can be any of those noted above.
In an additional related class of system embodiments, systems for fabricating layered devices comprising a first population of nanostructures and a second population of nanostructures, which first population comprises nanostructures comprising a first material, and which second population comprises nanostructures comprising a second material different from the first material, are provided. The system includes a source of a first substrate layer; a conveyor system for conveying the first substrate layer; a source of a first composition comprising the first population of nanostructures fluidly coupled to a layer deposition system, the layer deposition system being at least partially disposed over the substrate conveyor system, to provide a first layer; and, a source of a second composition comprising the second population of nanostructures fluidly coupled to the layer deposition system, the layer deposition system being at least partially disposed over the substrate conveyor system, to provide a second layer.
The system features noted for the preceding embodiments with respect to nanostructure types, first and/or second material types, conductive surfaces on the substrate layer(s), sources of first or second conductive materials, deposition systems for depositing the materials, use of rolled sheets, layering systems, etc. are applicable here as well.
An additional class of system embodiments provides a system for fabricating a nanocomposite layer, e.g., for use in or as part of a photovoltaic or other layered device. The system includes a layer deposition system and a source of a composition comprising a population of nanostructures, a polymer and/or a small molecule, a first solvent, and a second solvent, fluidly coupled to the layer deposition system. The layer deposition system is configured to deposit the composition on a substrate to provide the nanocomposite layer. The first solvent has a vapor pressure that is not equal to a vapor pressure of the second solvent, and at least one of the first and second solvents is free of chloroform and pyridine.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of conductive, blocking and/or sealing layers, types of layer deposition systems, and the like.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention pertains. The following definitions supplement those in the art and are directed to the current application and are not to be imputed to any related or unrelated case, e.g., to any commonly owned patent or application. Although any methods and materials similar or equivalent to those described herein can be used in the practice for testing of the present invention, the preferred materials and methods are described herein. Accordingly, the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting.
As used in this specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a nanostructure” includes a plurality of nanostructures, and the like.
An “aspect ratio” is the length of a first axis of a nanostructure divided by the average of the lengths of the second and third axes of the nanostructure, where the second and third axes are the two axes whose lengths are most nearly equal each other. For example, the aspect ratio for a perfect rod would be the length of its long axis divided by the diameter of a cross-section perpendicular to (normal to) the long axis.
The terms “crystalline” or “substantially crystalline”, when used with respect to nanostructures, refer to the fact that the nanostructures typically exhibit long-range ordering across one or more dimensions of the structure. It will be understood by one of skill in the art that the term “long range ordering” will depend on the absolute size of the specific nanostructures, as ordering for a single crystal cannot extend beyond the boundaries of the crystal. In this case, “long-range ordering” will mean substantial order across at least the majority of the dimension of the nanostructure. In some instances, a nanostructure can bear an oxide or other coating, or can be comprised of a core and at least one shell. In such instances it will be appreciated that the oxide, shell(s), or other coating need not exhibit such ordering (e.g. it can be amorphous, polycrystalline, or otherwise). In such instances, the phrase “crystalline,” “substantially crystalline,” “substantially monocrystalline,” or “monocrystalline” refers to the central core of the nanostructure (excluding the coating layers or shells). The terms “crystalline” or “substantially crystalline” as used herein are intended to also encompass structures comprising various defects, stacking faults, atomic substitutions, and the like, as long as the structure exhibits substantial long range ordering (e.g., order over at least about 80% of the length of at least one axis of the nanostructure or its core). In addition, it will be appreciated that the interface between a core and the outside of a nanostructure or between a core and an adjacent shell or between a shell and a second adjacent shell may contain non-crystalline regions and may even be amorphous. This does not prevent the nanostructure from being crystalline or substantially crystalline as defined herein.
The term “monocrystalline” when used with respect to a nanostructure indicates that the nanostructure is substantially crystalline and comprises substantially a single crystal. When used with respect to a nanostructure heterostructure comprising a core and one or more shells, “monocrystalline” indicates that the core is substantially crystalline and comprises substantially a single crystal.
The term “heterostructure” when used with reference to nanostructures refers to nanostructures characterized by at least two different and/or distinguishable material types. Typically, one region of the nanostructure comprises a first material type, while a second region of the nanostructure comprises a second material type. In certain embodiments, the nanostructure comprises a core of a first material and at least one shell of a second (or third etc.) material, where the different material types are distributed radially about the long axis of a nanowire, a long axis of an arm of a branched nanocrystal, or the center of a nanocrystal, for example. A shell need not completely cover the adjacent materials to be considered a shell or for the nanostructure to be considered a heterostructure; for example, a nanocrystal characterized by a core of one material covered with small islands of a second material is a heterostructure. In other embodiments, the different material types are distributed at different locations within the nanostructure; e.g., along the major (long) axis of a nanowire or along a long axis of arm of a branched nanocrystal. Different regions within a heterostructure can comprise entirely different materials, or the different regions can comprise a base material (e.g., silicon) having different dopants or different concentrations of the same dopant.
A “nanocrystal” is a nanostructure that is substantially monocrystalline. A nanocrystal thus has at least one region or characteristic dimension with a dimension of less than about 500 nm, e.g., less than about 200 nm, less than about 100 nm, less than about 50 nm, or even less than about 20 nm. Nanocrystals can be substantially homogeneous in material properties, or in certain embodiments can be heterogeneous (e.g. heterostructures). The term “nanocrystal” is intended to encompass substantially monocrystalline nanostructures comprising various defects, stacking faults, atomic substitutions, and the like, as well as substantially monocrystalline nanostructures without such defects, faults, or substitutions. In the case of nanocrystal heterostructures comprising a core and one or more shells, the core of the nanocrystal is typically substantially monocrystalline, but the shell(s) need not be. The nanocrystals can be fabricated from essentially any convenient material or materials. In one aspect, each of the three dimensions of the nanocrystal has a dimension of less than about 500 nm, e.g., less than about 200 nm, less than about 100 nm, less than about 50 nm, or even less than about 20 nm. Examples of nanocrystals include, but are not limited to, substantially spherical nanocrystals, branched nanocrystals, and substantially monocrystalline nanowires, nanorods, nanodots, quantum dots, nanotetrapods, tripods, bipods, and branched tetrapods (e.g., inorganic dendrimers).
A “nanostructure” is a structure having at least one region or characteristic dimension with a dimension of less than about 500 nm, e.g., less than about 200 nm, less than about 100 nm, less than about 50 nm, or even less than about 20 nm. Typically, the region or characteristic dimension will be along the smallest axis of the structure. Examples of such structures include nanowires, nanorods, nanotubes, branched nanocrystals, nanotetrapods, tripods, bipods, nanocrystals, nanodots, quantum dots, nanoparticles, branched tetrapods (e.g., inorganic dendrimers), and the like. Nanostructures can be substantially homogeneous in material properties., or in certain embodiments can be heterogeneous (e.g. heterostructures). Nanostructures can be, e.g., substantially crystalline, substantially monocrystalline, polycrystalline, amorphous, or a combination thereof. In one aspect, each of the three dimensions of the nanostructure has a dimension of less than about 500 nm, e.g., less than about 200 nm, less than about 100 nm, less than about 50 nm, or even less than about 20 nm.
A “nanowire” is a structure (typically, a nanostructure) that has one principle axis that is longer than the other two principle axes and that has an aspect ratio greater than about 10 (e.g., greater than about 20, greater than about 50, or greater than about 100, or even greater than about 10,000). The diameter of a nanowire is typically less than about 500 nm, preferably less than about 200 nm, more preferably less than about 150 nm, and most preferably less than about 100 nm, about 50 nm, or about 25 nm, or even less than about 10 nm or about 5 nm. The length of a nanowire is typically greater than about 100 nm, e.g., greater than 200 nm, greater than 500 nm, or even greater than 1000 nm. The nanowires of this invention can be substantially homogeneous in material properties, or in certain embodiments can be heterogeneous (e.g. nanowire heterostructures). The nanowires can be fabricated from essentially any convenient material or materials, and can be, e.g., substantially crystalline, substantially monocrystalline, polycrystalline, or amorphous. Nanowires can have a variable diameter or can have a substantially uniform diameter, that is, a diameter that shows a variance less than about 20% (e.g., less than about 10%, less than about 5%, or less than about 1%) over the region of greatest variability and over a linear dimension of at least 5 nm (e.g., at least 10 nm, at least 20 nm, or at least 50 nm). Typically the diameter is evaluated away from the ends of the nanowire (e.g. over the central 20%, 40%, 50%, or 80% of the nanowire). A nanowire can be straight or can be e.g. curved or bent, over the entire length of its long axis or a portion thereof. In certain embodiments, a nanowire or a portion thereof can exhibit two- or three-dimensional quantum confinement. Nanowires according to this invention can expressly exclude carbon nanotubes, and, in certain embodiments, exclude “whiskers” or “nanowhiskers”, particularly whiskers having a diameter greater than 100 nm, or greater than about 200 nm.
A “solvent” is a liquid substance capable of dissolving other substances.
Semiconductor nanocrystals, generally referred to as nanodots, nanorods, nanowires, etc., with their photoluminescent and electroluminescent properties have been the subject of a great deal of research into new labeling and luminescent display technologies.
In operation, when a semiconductor nanocrystal is exposed to light, the impact of photons of a given wavelength produces an excited state that is characterized by the displacement of an electron from its orbital. The resulting separated charges, an electron and an electron acceptor or hole, also together termed an “exciton,” would then typically recombine. When the electron and hole recombine, they emit light at a wavelength characteristic of the energy released. By varying the characteristics of the material, one could adjust the wavelength of emitted light.
Thus, to date, nanorod and nanodot research and development has primarily exploited this charge recombination within these nanomaterials to take advantage of the luminescent results. However, it has been shown that by separating the charges in an exciton, e.g., an electron from a hole, one can exploit the resulting electrical potential, thus deriving electric current from optical energy. See, e.g., Huynh, et al., Science 295(5564):2426-2427 (2002), Huynh, et al., Adv. Materials 11(11):923 (1999), Greenham et al., Phys. Rev. B 54(24):17628-17637 (1996), and U.S. Pat. No. 6,239,355, each of which is hereby incorporated herein by reference in its entirety for all purposes. In particular, photovoltaic devices have been reported that exploit a nanocrystal composite active layer in the conversion of light energy to electrical energy.
The present invention provides additional photovoltaic devices comprising a nanocomposite active layer, as well as photovoltaic and other devices in which the active layer comprises nanostructures (e.g., nanocrystals) that are not necessarily part of a composite. Related compositions, methods, and systems are also provided.
I. Active Layers
A. Nanocomposite Active Layers
One general class of embodiments provides photovoltaic devices in which the active layer comprises nanostructures (e.g., nanocrystals, nanowires, single-crystal nanostructures, double-crystal nanostructures, polycrystalline nanostructures, or amorphous nanostructures). Briefly, when light impinges upon the nanocrystal component of the active layer, it is absorbed by the nanocrystal creating an exciton within the nanocrystal. By conducting the electron away from the hole, one creates an electric potential that can be exploited. In the case of nanocomposite photoactive layers, this is accomplished by disposing the nanocrystal component in a conductive polymer (or small molecule) matrix that is able to donate an electron to the nanocrystal (or conduct the hole away from the nanocrystal). Because the nanocrystals comprise semiconductive material, the charge mobility (movement of the electrons) in the nanocrystal component is sufficiently fast at conducting the electron away from the hole in the polymer (or small molecule) matrix, so as to avoid recombination. It will be evident that, in such polymer- or small molecule-containing nanocomposite photoactive layers, the matrix optionally also absorbs light, leading to exciton formation. Electrons from such excitons are similarly conducted by the nanocrystals away from the holes, which are conducted through the matrix.
Once charges are separated, the electrons are selectively conducted through the active layer unidirectionally, e.g., out of the active layer through one electrode and back into the active layer through another electrode, providing useful current flow in the intervening circuit. Unidirectional conduction is also generally discussed in terms of movement of electrons in one direction and movement of holes in the other direction. The operation of one of these devices is schematically illustrated in
While prior researchers have demonstrated the basic functioning of a nanocomposite photovoltaic cell, the previously reported work shows that there is ample room for improvement of these devices, including increasing efficiency, e.g., from approximately 7%, increasing durability and manufacturability. In accordance with the present invention, a number of improvements are provided to the basic nanocomposite photovoltaic device that produces substantial improvements in efficiency across the range of light exposures, improvements in product robustness, as well as a number of other commercially valuable improvements.
The basic architecture of the photovoltaic devices of the invention is substantially as described with reference to
1. Semiconductor Nanocrystals
Nanostructures, especially semiconductor nanocrystals, as noted above, have been described in great detail, previously. As used herein, semiconductor nanocrystals include a wide range of different materials that exist as nanoparticles, e.g., having at least one cross sectional dimension of less than about 500 nm, and preferably, less than 100 nm. These nanocrystals may be comprised of a wide range of semiconductive materials, including for example, group III-V, group II-VI and group IV semiconductors or alloys of these materials. In particularly preferred aspects, CdSe, CdTe, InP, InAs, CdS, ZnS, ZnO, ZnSe, PbSe, PbS, ZnTe, HgTe, GaN, GaP, GaAs, GaSb, InSb, Si, Ge, AlAs, AlSb or PbTe semiconductors or their alloys are used as at least a portion of the nanocrystal component.
Although generally described in terms of nanocrystals, in accordance with most preferred aspects of the invention, the nanocrystal component of the active layer will be comprised, at least in part, and preferably in substantial part, of elongated nanocrystals or nanorods, that include aspect ratios (length:diameter) of 5, 10 or greater, or three dimensional nanostructures that include nanorod-like components, e.g., four branched or tetrahedral structures also termed “nanotetrapods.” The use of rod-like structures in place of substantially spherical structures, e.g., quantum dots, provides substantial advantages in terms of charge separation. In particular, and without being bound to a particular theory of operation, because of their aspect ratio, nanorods are able to separate an electron from a hole, e.g., the electron is conducted along the length of the rod, while the hole is transferred the short distance of the radius of the rod to the surrounding matrix. Particularly preferred nanorods and nanotetrapods and their methods of production are described in detail in, e.g., Peng et al, Nature 404(6773):59-61 (2000), Manna et al., J. Am. Chem. Soc. 122(51):12700-12706 (2000), and Manna et al., J. Am. Chem. Soc. 124(24):7136-7145 (2002), each of which is incorporated herein by reference in its entirety for all purposes.
The semiconductor nanocrystals may optionally comprise additional elements to enhance their function within the active layer. For example, nanocrystals may be dye sensitized to increase light absorption and/or charge injection into the nanocrystal component. Examples of such dyes include those described in U.S. Pat. No. 6,245,988, published PCT Application Nos. WO 94/04497 and 95/29924, each of which is incorporated herein by reference in its entirety for all purposes, where ruthenium based dyes are provided in conjunction with crystalline components to enhance light absorption and charge injection.
In a number of preferred aspects, the nanocrystal component will comprise a nanoheterostructure. In particular, in certain preferred aspects, the nanocrystal component will comprise a core-shell structure where the core portion of the crystal comprises a first material, and is overlaid with a coating or shell of another material. Core-shell nanostructures have been described previously (see, U.S. Pat. Nos. 6,207,229 and 6,322,901, incorporated herein by reference in their entirety for all purposes). Particularly preferred are core-shell nanocrystals, e.g., nanorods, having a type-II band offset between the core and the shell, where the core transports one portion of the exciton, e.g., the electrons, while the shell transports the other, e.g., holes. As a result, the core-shell nanorod efficiently maintains charge separation and carries out charge conduction, both as to electrons and holes. With reference to
Use of core-shell nanocrystals provides additional advantages of being able to eliminate conductive polymers from the active layer. In particular, the inclusion of conductive polymers in carrying out the charge separation operation is believed to result in some lost efficiency associated with transfer of charge from the crystal to the polymer. This may be addressed as described elsewhere herein, e.g., through the inclusion of linking chemistries between crystal and polymer. More concerning in the use of conductive polymers is their susceptibility to oxidation, photooxidation, or other environmental conditions, which can severely limit their durability in many commercial applications if not hermetically sealed. Because inorganic nanocrystals do not have these sensitivities, their use provides for drastic simplification of packaging and manufacturing methods.
2. Polymer Matrix
A variety of different conductive matrices are useful as the supporting and conductive matrix of the active layer. Conductive polymers are generally described in T. A. Skatherin (ed.), Handbook of Conducting Polymers I, which is incorporated herein by reference in its entirety for all purposes. Examples of preferred conductive polymer matrices include, e.g., poly(3-hexylthiophene)(P3HT), poly[2-methoxy, 5-(2′-ethyl-hexyloxy)-p-phenylene-vinylene] (MEH-PPV), poly(phenylene vinylene) (PPV), polyfluorene, and polyaniline. Because of the application of the devices described herein, it will be appreciated that preferred polymer matrices will be light stable, and depending upon the packaging of the devices, oxygen stable as well. The polymer matrix optionally absorbs light, e.g., visible light.
One aspect of active layers where it is believed that efficiencies can be increased is in the charge separation between a semiconductor nanocrystal and a conductive polymer matrix in an active layer. In particular, it is believed that at least some of the inefficiencies of nanocomposite photovoltaic active layers derive from recombination of excitons within the nanocrystal. Accordingly, without being bound to a particular theory of operation, it is expected that by providing a more efficient conduction of holes from the nanocrystal to the polymer matrix, or among the layers of a core-shell nanocrystal, one could obtain a consequent improvement in efficiency of the overall device.
In accordance with certain aspects of the present invention, charge separation efficiency is at least partially addressed by coupling the outer surface or shell of the nanocrystal to the polymer matrix. The coupling comprises an electrically conductive coupling that provides a more direct route of conduction from the nanocrystal to the polymer matrix. Typically, such couplings may comprise any of a variety of covalent chemical, ionic, hydrophobic/hydrophilic interactions between the polymer and the nanocrystal, either directly or through one or more linking molecules. Examples of useful polymer/nanocrystal linkages include, e.g., modifying the polymer side chains, e.g., polymers like P3HT, PPV or their derivatives, to directly bind nanocrystal side chains, i.e., adding phosphonic acid groups, phosphine oxides, phosphine, amine, thiol or other chemistries that will couple to the passivated, partially passivated, and/or unpassivated atoms (e.g., to the cation or anion groups) present on a nanocrystal surface. As noted above, and as should be readily apparent, where the electron carrier and hole carrier are associated as the same structure, e.g., as a core-shell nanocrystal, charge separation efficiencies would be further expected to increase, which may be used in conjunction with or in certain preferred aspects, in lieu of a chemical linkage to a polymer matrix. Examples of useful approaches to surface chemistries for linkage to polymers or otherwise to enhance charge injection and/or extraction from nanocrystals are described in substantial detail in Provisional U.S. Patent Application No. 60/452,232 (Attorney Docket No. 40-002700US), filed Mar. 4, 2003, and U.S. patent application Ser. No. 10/656,910 (Attorney Docket No. 40-002710US), filed Sep. 4, 2003, which are incorporated herein by reference in their entirety for all purposes.
Alternatively, ligands may be coupled to the outer surface of the nanocrystal via conventional chemistries, e.g., as described elsewhere herein and in, e.g., Provisional U.S. Patent Application No. 60/392,205, filed Jun. 27, 2002, which is incorporated herein by reference in its entirety for all purposes. The ligand is then coupled at a second position to the polymer matrix, e.g., via conventional linking chemistries.
Alternative or additional polymer matrix modifications may also be provided in addition to or instead of those described above, including doping of conducting polymers with charged or charge-carrying groups and/or controlled oxidation of the conducting polymer to permit better charge conduction through the polymer.
The charge carrying properties of a conductive polymer can be altered, e.g., by doping the polymer with hole conducting or electron conducting molecules. Such doping can, for example, increase hole or electron mobility within the polymer component of a nanocomposite material. Similarly, doping of the polymer component of a nanocomposite can be used to adjust the relative energy levels of the matrix with respect to the nanostructure component (e.g., to improve charge separation). Since the performance of current nanocomposite-based photovoltaic devices can be limited by the efficiency of hole conduction in the polymer matrix, performance can be improved by facilitating hole conduction by doping the polymer with a hole conducting molecule, e.g., a hole conducting small molecule. Such improved performance can be observed as an increase in the open circuit voltage of the photovoltaic device and thus in a more favorable power conversion efficiency.
Small molecules suitable for use as dopants typically have a molecular weight less than 3000 (e.g., less than 2000, less than 1500, less than 1000, less than 500, or even less), and are optionally semiconductive, organic, nonpolymeric molecules. Example hole conducting small molecules that can be used to dope conductive polymers include, but are not limited to, N,N′-diphenyl-N,N′-bis-(3-methylphenyl)-(1,1′diphenyl)-4,4′-diamine) (TPD), N,N′-diphenyl-N,N′-bis(1-naphthyl)-1,1′-biphenyl-4,4′-diamine (α-NPD), N,N′-biphenyl-N,N′-bis-(1-naphenyl)-[1,1′-biphenyl]-4,4′-diamine (NPB), triplephenylamine (TPA), and triphenylamine tetramer (TPTE). See, e.g., Yang et al. (2003) Synthetic Metals 137:1521-1522.
Alternatively or in addition, the charge carrying properties of a conductive polymer can be similarly altered by controlled partial oxidation of the polymer. See, e.g., Skotheim et al. (1998) Handbook of Conducting Polymers, 2nd Ed. Marcel Dekker: New York.
3. Small Molecule Matrix
In one general class of embodiments, the photoactive layer comprises a small molecule and a population of nanostructures. The nanostructures and the small molecule typically exhibit a type II band offset energy profile. In one class of embodiments, the small molecule has a molecular weight less than 3000 (e.g., less than 2000, less than 1500, less than 1000, less than 500, or even less). The small molecule optionally comprises a semiconductive, organic, nonpolymeric molecule. It is worth noting that the small molecule optionally comprises an oligomer (e.g., an oligomer with a molecular weight less than about 3000) or a molecule that can be but is not polymerized. The small molecule optionally absorbs light, e.g., visible light.
In certain embodiments, the photoactive layer comprises nanostructures disposed in a matrix comprising a small molecule. The nanostructures are optionally electrically and/or covalently coupled to the matrix, and can be randomly or non-randomly oriented. In other embodiments, the photoactive layer comprises at least two sublayers, wherein at least one of the sublayers comprises the nanostructures and at least one of the sublayers (e.g., at least one other sublayer) comprises the small molecule. In either of the above example classes of embodiments, the nanostructures can, e.g., function as the electron conductor while the small molecule functions as the hole conductor.
The photoactive layer is optionally substantially free of conductive and/or nonconductive polymer. Alternatively, the photoactive layer can also include a polymer (e.g., a conductive or nonconductive polymer) in which the small molecule is dispersed. Various relative proportions of the small molecule and the polymer can be selected, e.g., as appropriate for the particular polymer, small molecule, and nanostructure(s). For example, in embodiments in which the photoactive layer comprises nanostructures disposed in a matrix comprising the small molecule and the polymer, the small molecule can form a small portion of the total matrix, resulting in a doped polymer nanocomposite layer (e.g., the small molecule can comprise less than about 50%, 40%, 20%, 10%, 5%, or even less, of the matrix by weight). As another example, the polymer can form a small portion of the matrix, e.g., in embodiments in which it is used a binder or filler (e.g., the small molecule can comprise greater than about 50%, 60%, 75%, 90%, 95%, or even more, of the matrix by weight).
Suitable small molecules and polymers include those mentioned herein, in addition to others known in the art.
4. Active Layer Configuration
As noted above, conduction of electrons is much more rapid through the semiconductor nanocrystals (or other semiconductor nanostructures) than through the surrounding polymer matrix. In cases where an electron is conducted or hops from one crystal to another, there is a consequent loss in energy associated with that hopping. By minimizing losses associated with electron hopping, one can improve the efficiency of the overall device. In order to minimize hopping, therefore, it is desirable to provide as direct a conductive path through the active layer, as possible, e.g., a path with fewer required crystal to crystal hops. In the case of spherical or near spherical nanocrystals, this is best accomplished by providing the nanocrystal component as substantially a monolayer disposed on one electrode. While this provides an advantage in charge conduction, it carries the disadvantage of substantially reduced light absorption from a single thin layer of nanocrystals.
The use of nanorods or nanotetrapods, however, provides significant advantages in this respect. In particular, because these nanorods and nanotetrapods have elongated sections and maintain quantum confinement in one dimension, they provide both increased light absorption, e.g., they absorb well along the entire length of the rod) and a longer conductive path, and thus have the potential for more efficient charge conduction. By orienting this longer conductive path to bridge the space between the electrodes, e.g., normal to the plane of the electrodes, one can further provide a more direct and longer conductive path for electrons.
Accordingly, in preferred aspects, the active layers described herein employ nanostructures that provide an elongated conductive path, which path is oriented predominantly normal to the plane of the two opposing electrodes of the device. As noted above, this can be accomplished by providing elongated nanorods that are oriented such that their longitudinal axes are predominantly normal to the plane of the electrodes. By “oriented predominantly normal to the plane” is generally meant that the average longitudinal dimension of the collection of nanorods within the active layer is oriented more normal to the plane of the two electrodes than would be the case of a completely randomly oriented collection of nanorods.
In preferred aspects, the nanorod component of the active layer is even more stringently oriented, such that at least 50% of the nanorods in a collection of nanorods are oriented such that they include elongated sections that have their longitudinal axes oriented within 45° of normal to the plane of the electrodes. In more preferred aspects, at least 80% of the nanorods in the active layer are oriented such that they have elongated sections that have their longitudinal axes are within 45° of normal to the plane of the electrodes, and in still further aspects, at least 90% or even 95% of the nanorods are so oriented. In some embodiments, the orientation may be more toward normal, with the greater percentage of rods, e.g., the various percentages set forth above, being oriented such that their longitudinal axes are within at least 30° of normal to the plane of the electrodes, and in some cases oriented within 20° or even 15° or less to the plane of the electrodes.
In one aspect, the present invention provides compositions such as photoactive layers having aligned and/or arranged nanostructure elements, as well as methods for preparing aligned and/or arranged nanostructures. Any of a number of nanostructures (or combination of nanostructures) can be used in the compositions and methods of the present invention, including, but not limited to, nanodots, nanospheres, nanorods, nanowires, nanoribbons, nanotetrapods, various branched structures (e.g., dendrimer branching structures), quantum dots, nanodots, and the like.
In one aspect, the present invention provides compositions having a plurality of non-randomly oriented nanostructures in a matrix, e.g., in a PV device, e.g., as part or all of a photoactive layer. The non-randomly oriented nanostructures can include both regularly-ordered arrays of nanostructures, as well as irregularly-ordered arrangements of nanostructures.
In another aspect, the present invention provides compositions having an array of nanostructures in a matrix, e.g., in a photoactive layer, in which the plurality of nanostructure members are non-randomly arranged. Optionally, the nanostructures are non-randomly oriented in addition to being non-randomly arranged.
In a further embodiment, the compositions of the present invention have two or more matrix layers, each member layer comprising a plurality of non-randomly oriented nanostructures and/or non-randomly arranged nanostructures. The member nanostructures in the matrix layers can be aligned with respect to the member nanostructures in an adjacent matrix layer (e.g., where the photoactive layer or the overall device comprises more than one active layer), or not aligned.
In any case, methods of orienting nanorods in a polymer matrix include electric field assisted orientation of nanorods, e.g., applying an electric field to cause magnetic rods to orient in a desired direction, in a polymer matrix which optionally can be hardened to maintain the orientation. Alternatively, rods may be disposed in a polymer matrix which can then be stretched to cause the rods to align in the direction of stretching. In particular, stretching of polymer materials aligns the polymer strands in the direction of stretching which tends to force similar alignment of any nanorods disposed in the polymer material.
Alternatively, aligned rods may be grown substantially in situ as a field of oriented structures that are subsequently integrated into the polymer matrix and active layer. Methods of fabricating such fields of aligned nanostructures are described, in e.g., Published U.S. Patent Application Nos. 2002/0172820 and 2002/0130311, the full disclosures of which are hereby incorporated by reference in their entirety for all purposes.
In alternative preferred aspects, alignment of rods may be achieved through the exploitation of liquid crystal phases of the nanocrystals. For example, CdSe nanorods have been observed to exhibit liquid crystalline phases under certain conditions. Once in these liquid crystal phases, one can readily align such crystals by applying a small electric field as is commonly done with organic liquid crystals, e.g., in display applications.
Alternatively, self assembly methods may be employed that rely on differential treatment of one or both ends of a nanorod, as compared to the side surfaces. In preferred aspects, the rods would be aligned through the incorporation in the matrix of liquid crystals. For example, one could provide a hydrophilic moiety on an end of a nanorod while providing hydrophobic sides, in order to force rods to orient along an aqueous-organic interface with the end extending into the aqueous phase while the side surfaces remained in an organic phase. Curing of the organic phase, e.g., a polymer, would then secure the rods in position. Relatedly, one could provide layers of matrix material that have different affinities for other chemical moieties that are selectively deposited on different portions of rods or wires. For example, a rod may be provided with a first chemical moiety at one end, e.g., that portion that has a wurtzite structure, while a different chemical moiety is coupled to the other end or the remaining portion of the rod or wire. By depositing the rods or wires into a matrix that includes an interface where one side of the interface has a higher affinity for the first chemical moiety and the other side of the interface has a higher affinity for the second chemical moiety, it may result in self orientation of the rods across the interface.
In another alternative method, nanorods may be aligned and oriented by coupling a linker molecule, e.g., an organic surfactant, that bind strongly to only one end of the nanorods. The other end of the surfactant is then functionalized to bind selectively to one electrode. By way of example, in the case of CdSe, alkyl phosphonic acids bind more strongly to the 00-1 face of nanorods than any other face. This selective binding is then taken advantage of in coupling the bound end to an electrode, e.g., the cathode, of a photovoltaic device.
In one general class of embodiments, the photoactive layer includes compositions having a plurality of selectively-oriented nanostructures in which the members nanostructures are associated with one or more alignment ligands (which can be components of a matrix in which the nanostructures are embedded, or can simply be directly attached to the nanostructures). In one example, a first alignment ligand on a first member nanostructure interacts with a second alignment ligand associated with an adjacent member nanostructure, thereby selectively-orienting the plurality of nanostructures. These ligands can include any that ordinarily interact with one another, e.g., as in avidin-biotin, antibody-antibody ligand, aptamer-aptamer binding moiety, complementary nucleic acids, interactive chemical moieties, and/or the like.
In any case, in one embodiment of the present invention, a plurality of selectively-oriented nanostructures are provided in the photoactive layer. The nanostructures are selectively aligned by providing a plurality of nanostructures comprising a first set of nanostructures associated with a first alignment ligand and a second set of nanostructures associated with a second alignment ligand, and interacting the first alignment ligand on a first nanostructure with the second alignment ligand on a second adjacent nanostructure, to selectively orient the plurality of nanostructures.
In another related embodiment, a plurality of non-randomly oriented or non-randomly dispersed nanostructures in a matrix in the photoactive layer are prepared by providing a plurality of nanostructures and a matrix composition, in which the matrix composition includes one or more matrix components that interact to form a plurality of receiving structures capable of accommodating the nanostructures. The composition is heated and cooled in the presence of the plurality of nanostructures, thereby preparing the plurality of non-randomly oriented or non-randomly dispersed nanostructures in the matrix.
In any case, aligned and/or organized nanostructures can be used in any of a number of devices and applications, including, but not limited to, various photovoltaic devices, optoelectronic devices (LEDs, nanolasers), light collectors, and the like.
In certain preferred aspects, branched nanorods, and particularly, branched nanorods having a tetrahedral geometry, e.g., nanotetrapods, are used as the electron conducting component of the active layer. In the case of nanotetrapods, virtually any orientation will provide an effective conductive path that is oriented substantially or predominantly normal to the plane of the electrodes, as described above, and thus no orientation process or step is required. In particular, because nanotetrapods have four branches arranged in a tetrahedral architecture, virtually any rotational disposition of the structure will provide a reasonably direct conductive path through the active layer. For a nanotetrapod, no branch or component of a single nanotetrapod structure will be more than 60° from normal to the electrode, and at least one component or branch will be within 30° of normal to the plane of the electrode. Thus, in terms as described for nanorods, nanotetrapods include at least one elongated section that has a longitudinal dimension or axis that is within 30° of normal.
Although described in terms of active layers that include either spherical nanocrystals, nanorods or nanotetrapods, it will be appreciated that devices of the present invention may include active layers that are comprised of multiple different types of nanostructures, e.g., nanorods and nanotetrapods, nanorods and spherical or nonelongated nanocrystals, or nonelongated nanocrystals and nanotetrapods, or all three types of nanocrystals. Similarly, devices may include multiple active layers sandwiched between multiple electrode layers, where each active layer is made up of homogeneous or heterogeneous mixtures of nanostructure types, and where each layer is the same as or different from at least one other layer.
As noted above, operation of the photovoltaic devices of the invention relies upon unidirectional current flow through the active layer, also referred to as “charge separation.” In the nanocomposite based devices of the invention, unidirectional conduction may be accomplished by a number of different means. For example, in certain cases, blocking layers are employed on the respective electrodes to function as electrical check valves to maintain charge separation. In particular, a blocking layer is provided proximal to the first electrode that blocks electron conduction to the first electrode, while not blocking hole conduction to (or electron conduction from) that first electrode. In contrast, another different blocking layer is provided proximal to the second electrode that permits electron conduction to the second electrode but blocks hole conduction to (or electron conduction from) that second electrode. An example of a device architecture that includes such blocking layers is shown in
Alternatively or additionally, one can enhance unidirectional current flow in the devices of the invention by providing the nanocrystal (or other nanostructure) component positioned proximal to one electrode, versus the other. An example of this type of structure is illustrated in
One method of preferentially locating nanocrystals (or other nanostructures) closer to one electrode than the other is to sequentially deposit the active layer components onto one electrode. In particular for example, one can deposit a portion of the active layer matrix that includes the nanocrystals onto the first electrode, e.g., electrode 108. A second layer of just the matrix material, e.g., the conductive polymer, is then deposited over the portion that contains the nanocrystals. This will result in an increased proportion of nanocrystals closer to one electrode (108) than the other (110). Alternatively, one could perform a modified version of this type of operation in reverse. In particular, one could first deposit a layer of conducting polymer onto one electrode (110). A second layer of conducting polymer/nanocrystal matrix, is then deposited over the pure polymer layer, and the other electrode (108) is deposited onto the active layer. In order to provide direct connection of the nanocrystals to the other electrode (108), one may optionally or additionally then preferentially dissolve the polymer layer away from the matrix, e.g., dissolving 1%, 10%, 20%, 50% or more of the polymer in the matrix layer, to expose the nanocrystal components of the matrix. The second electrode (108) is then deposited upon the exposed nanocrystals to provide such crystals in direct contact with the second electrode, but sufficiently distant from the first electrode, by virtue of the pure polymer layer that was first deposited thereon.
In additional or alternative arrangements, one may enhance charge separation through the use, as noted previously, of core-shell nanorods, where the core and shell have a type II band offset, e.g., conducting one charge carrier through the core and the other through the shell, thereby functioning in the same way as a nanocrystal-conducting polymer composite active layer. In such cases, the core-shell nanocrystal functions as the active layer component as shown in zones II and III in
In a related aspect, an active layer may be fabricated by providing core-shell nanocrystals as a component of the active layer, e.g., as described above. However, in optional additional aspects, the core-shell nanocrystal component of the active layer is sintered or otherwise agglomerated or linked together physically and/or electrically. The resulting active layer is then comprised of an amorphous matrix that includes regions of shell material substantially evenly dispersed in the matrix with regions of core material. These regions retain their functionality as one of the hole or electron conductor, in the active layer. Further, because they originate from nanocrystals, the amorphous matrix appears to be substantially homogeneous, at the micron scale, while actually being heterogeneous at the nanoscale level. While advantageous from some perspectives, e.g., charge separation and conduction, sintered active layers may be less flexible than polymer composite active layers, and thus may be preferred for certain applications and less preferred for others. Sintering is typically accomplished using well known thermal sintering methods whereby the nanocrystal layer is heated to a temperature at which agglomeration occurs, but is still typically below the melting point of the nanocrystal materials. For such sintered active layers, it may be desired to provide the nanocrystals as a substantially contiguous monolayer within the active layer, which is not always necessary for polymer composite active layers.
B. Inorganic Active Layers
One class of embodiments provides photovoltaic devices in which the active layer comprises one or more populations of nanostructures collectively comprising two inorganic materials (e.g., one material that functions as a hole conductor and one that functions as an electron conductor). These photovoltaic devices are similar to those described above, although the nanostructures are not necessarily nonrandomly oriented and/or are not necessarily part of a nanocomposite. Thus, in one class of embodiments, the photovoltaic device comprises a first electrode layer, a second elector layer, and a first photoactive layer disposed between the first and second electrode layers. The photoactive layer is disposed in at least partial electrical contact with the first electrode along a first plane and in at least partial electrical contact with the second electrode along a second plane. The photoactive layer comprises a first inorganic material and a second inorganic material different from the first inorganic material; the first and second inorganic materials exhibit a type II band offset energy profile. In addition, the photoactive layer comprises a first population of nanostructures, which nanostructures comprise the first inorganic material, the second inorganic material, or a combination thereof.
In a preferred class of embodiments, the first and second inorganic materials are semiconductors. Essentially any pair of semiconductor materials with a type II band offset can be used. For example, the first inorganic material can comprise a first semiconductor selected from the group consisting of: a Group II-VI semiconductor, a Group III-V semiconductor, a Group IV semiconductor, and an alloy thereof. Similarly, the second inorganic material can comprise a second semiconductor, different from the first semiconductor, selected from the group consisting of: a Group II-VI semiconductor, a Group III-V semiconductor, a Group IV semiconductor, and an alloy thereof. Example semiconductors include, but are not limited to, CdSe, CdTe, InP, InAs, CdS, ZnS, ZnSe, ZnTe, HgTe, GaN, GaP, GaAs, GaSb, InSb, Si, Ge, AlAs, AlSb, PbSe, PbS, and PbTe.
The nanostructures can be any of a variety of nanostructures. For example, the nanostructures can comprise a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, or an amorphous nanostructure. The nanostructures can comprise, e.g., nanocrystals, nanorods, nanowires, nanotubes, branched nanocrystals, nanotetrapods, tripods, bipods, nanodots, quantum dots, nanoparticles, branched tetrapods, or the like, or a combination thereof (e.g., nanorods and nanotetrapods, or nanorods and spherical or nonelongated nanocrystals, among many other possible combinations).
As noted above, an active layer can be fabricated by providing core-shell nanocrystals. Thus, in one class of embodiments, the first population of nanostructures comprises nanocrystals that comprise a core of the first inorganic material and a shell of the second inorganic material. For example, as noted previously, the first and second inorganic materials can be essentially any two semiconductors with an appropriate type II band offset; for example, the core can comprise CdSe and the shell CdTe, or the core can comprise InP and the shell GaAs.
As noted above, the nanocrystals are optionally fused, partially fused, and/or sintered. In one class of embodiments, the cores of at least two adjacent nanocrystals are in at least partial direct electrical contact and the shells of at least two adjacent nanocrystals are in at least partial direct electrical contact. The cores of one or more nanocrystals are optionally in at least partial direct electrical contact with the first electrode or the second electrode; similarly, the shells of one or more nanocrystals are optionally in at least partial direct electrical contact with the opposite electrode.
Operation of an example embodiment in which adjacent core-shell nanocrystals are fused, partially fused, or sintered such that the cores and/or shells of adjacent nanocrystals are in at least partial direct electrical contact is schematically illustrated in
In a related class of embodiments, the photoactive layer comprises two populations of nanostructures. The first population of nanostructures comprises nanocrystals comprising the first inorganic material, and a second population of nanocrystals comprises nanocrystals which comprise the second inorganic material. As in the preceding embodiments, the first and second materials can be, for example, any two semiconductors with a type II band offset. For example, the first inorganic material can comprise CdSe and the second CdTe, or the first inorganic material can comprise CdS and the second CdTe, or the first inorganic material can comprise CdS and the second ZnSe. Adjacent nanocrystals in the photoactive layer are typically in at least partial direct electrical contact with each other. The nanocrystals of the first and/or second populations are optionally fused, partially fused, and/or sintered (or not fused, partially fused, and/or sintered).
In one class of embodiments, the nanocrystals of the first population and the nanocrystals of the second population are intermixed in the photoactive layer. The nanocrystals of the two populations can be uniformly mixed, or an increased proportion of one population can be closer to one electrode while an increased proportion of the other population is closer to the other electrode.
Operation of an example embodiment in which the photoactive layer comprises two intermixed nanocrystal populations is schematically illustrated in
In another class of embodiments, the nanocrystals of the two populations are segregated into layers rather than being intermixed. In these embodiments, the photoactive layer comprises at least a first sublayer and a second sublayer, wherein the first sublayer comprises the first population of nanocrystals and the second sublayer comprises the second population of nanocrystals.
Operation of an example embodiment in which the photoactive layer comprises two sublayers is schematically illustrated in
As noted, the photoactive layer can comprise at least two active sublayers, e.g., wherein each of the active sublayers comprises a plurality of nanocrystals of at least one nanocrystal type. In one class of embodiments, at least one of the at least two sublayers comprises an n-type sublayer and at least one of the two sublayers comprises a p-type sublayer; optionally, the photoactive layer comprises a junction between the p-type sublayer and the n-type sublayer. At least one of the sublayers is typically nanocrystalline. In another class of embodiments, the photoactive layer comprises a blend of p and n nanocrystals. For example, the photoactive layer can comprise at least one sublayer comprising a blend of p and n nanocrystals.
As noted above, use of inorganic nanostructures to provide both hole and electron conducting materials in the active layer can obviate the need for a conductive polymer component in the active layer. Thus, although in some embodiments the photoactive layer further comprises a conductive polymer (e.g., a conductive polymer matrix in which the nanostructures are disposed), in alternative embodiments, the photoactive layer is substantially free of conductive polymer. In certain embodiments, the photoactive layer also includes a nonconductive polymer or other binder (e.g., a nonconductive polymer matrix in which the nanostructures are disposed, uniformly or nonuniformly). It will be appreciated that preferred polymers will be light stable, and, depending on the packaging of the devices, oxygen stable. Suitable conductive polymers include, e.g., those noted in the above embodiments; suitable nonconductive polymers include, e.g., polyamide and PMMA. The photoactive layer optionally includes components included to modify the properties of the nanostructures, e.g., surface chemistries and ligands such as those described above.
The nanostructures can be, but are not necessarily, nonrandomly oriented in the photoactive layer. Thus, in one class of embodiments, the nanostructures of the first population (and/or the second population, if present) each has at least one elongated section oriented predominantly normal to at least the first plane. Such orientation can be achieved, e.g., as described above, e.g., for nanorods. As one example, the nanostructures can comprise branched nanocrystals having more than one elongated segment, e.g., branched nanocrystals comprising four elongated segments connected at a common apex and arranged in a substantially tetrahedral geometry.
As described above, blocking layers can be employed to maintain charge separation. Thus, in one class of embodiments, the photovoltaic device also includes a hole or electron blocking layer disposed between the photoactive layer and the first or second electrode. For example, the photovoltaic device can include a hole blocking layer disposed between the photoactive layer and the first electrode and an electron blocking layer disposed between the photoactive layer and the second electrode.
As will be discussed in greater detail below, for certain applications, the photovoltaic device is desired to be flexible or otherwise conformable. Thus, at least one of the first and second electrodes are optionally flexible, as is the photoactive layer. The device is optionally hermetically sealed and can assume any of a variety of architectures.
The composition and/or size of nanocrystals can be selected, e.g., to optimize the absorption spectrum of the active layer, as discussed in greater detail in the following section. Thus, the first population of nanostructures optionally comprises at least two different nanocrystal subpopulations, each nanocrystal subpopulation having a different absorption spectrum. For example, the different nanocrystal subpopulations can comprise different compositions and/or the different nanocrystal subpopulations can comprise nanocrystals having different size distributions.
The photovoltaic device optionally comprises at least a second photoactive layer, e.g., optimized for absorption of a wavelength range distinct from that of the first photoactive layer. Thus, in one class of embodiments, the photovoltaic device further comprises a third electrode layer, a fourth electrode layer, and a second photoactive layer disposed between the third and fourth electrode layers. The second photoactive layer is disposed in at least partial electrical contact with the third electrode along a third plane and in at least partial electrical contact with the fourth electrode along a fourth plane. The second photoactive layer comprises a second population of nanostructures having a different absorption spectrum from the first population of nanostructures (typically, a second population of inorganic nanocrystals, similar to that described for the first photoactive layer). The third electrode layer, fourth electrode layer and second photoactive layer are attached to, but electrically insulated from, the first electrode layer, second electrode layer and first photoactive layer.
C. Tuning Nanostructure Absorption
In addition to the physical positioning and orientation of the nanostructure (e.g., nanocrystal) component of the active layer, one can adjust or tune the absorption spectrum of the active layer or layers by adjusting the composition of the nanostructure (e.g., nanocrystal) component or components to fit the needs of the particular application. In particular, as noted previously, the absorption spectrum of semiconductor nanocrystals can be adjusted depending upon the composition and/or size of the nanocrystals. For example, InAs nanorods have a greater absorption in the near IR range, e.g., the absorption is red shifted as compared to other nanorods, InP nanorods have a greater absorption in the visible range, CdSe rods have greater absorption in the visible to blue range, while CdS nanorods have an absorption spectrum that is further blue shifted than CdSe nanorods. A chart of absorption spectra of CdSe nanorod compositions having three different size distributions, e.g., diameters, is shown in
By way of example, where one wishes to produce a device useful in absorbing solar energy, one can select nanocrystals or combinations of nanocrystals for the active layer(s) whose absorption spectra overlap to more directly match that of the sun in order to more efficiently convert more of the solar (or other light source) spectrum. Such heterogeneous selections of nanocrystals may be combined as a mixture in a single active layer, or they may be provided in multiple discrete layers in a multi-layered device. In some preferred aspects, such different collections of nanocrystal sizes and compositions are provided in discrete layers, so as to maximize the energy conversion from a portion of the relevant spectrum, e.g., each layer includes sufficient concentrations of nanocrystals of a given absorption wavelength range to yield optimal conversion of light in that range.
D. Multiple Photoactive Layers
As noted above, the photovoltaic devices of this invention optionally include a plurality of photoactive layers. These photoactive layers can be arranged in a variety of different configurations with various numbers of electrode, recombination, and/or blocking layers and/or the like. In some embodiments, adjacent photoactive layers are at least partially electrically connected to each other, while in other embodiments, they are not. Use of multiple active layers in a photovoltaic device can, e.g., increase absorption, open-circuit voltage, and/or photocurrent.
In one general class of embodiments, as noted above, the photovoltaic device includes two (or more) photoactive layers. A first photoactive layer is disposed between first and second electrode layers, and a second photoactive layer is disposed between third and fourth electrode layers. The first electrode layer, second electrode layer, and first photoactive layer are attached to, but electrically insulated from, the third electrode later, fourth electrode layer, and second photoactive layer.
Another general class of embodiments provides a photovoltaic device that includes a first electrode layer, a second electrode layer, a third electrode layer, a first photoactive layer disposed between the first electrode layer and the second electrode layer, and a second photoactive layer disposed between the second electrode layer and the third electrode layer. The first photoactive layer is disposed in at least partial electrical contact with the first electrode (e.g., along a first plane) and with the second electrode (e.g., along a second plane), and the second photoactive layer is disposed in at least partial electrical contact with the second electrode (e.g., along a third plane) and with the third electrode (e.g., along a fourth plane). In one class of embodiments, the first photoactive layer comprises a first population of nanostructures, and the second photoactive layer comprises a second population of nanostructures. Typically, the first and second photoactive layers each comprises a material that exhibits a type II band offset energy profile.
The device optionally includes additional photoactive and/or electrode layers. For example, the photovoltaic device can include a fourth electrode layer and a third photoactive layer disposed between the third and fourth electrode layers, where the third photoactive layer is in at least partial electrical contact with the third and fourth electrode layers.
Unless noted otherwise, any feature of the photovoltaic device embodiments noted above or otherwise herein can be applied to this class of embodiments. For example, all of the features noted herein with respect to photoactive layer configuration, nanostructure type, shape and composition, electrode composition and configuration, and device architecture apply to these embodiments as well. Any of the optional transparent, blocking, and/or sealing layer embodiments described herein can be features of this set of embodiments as well.
Operation of an example embodiment in which two photoactive layers share an electrode layer is schematically illustrated in
Yet another general class of embodiments provides photovoltaic devices comprising a plurality of photoactive layers, in which at least two adjacent active layers are separated by a recombination material. In this class of embodiments, the photovoltaic device includes a first electrode layer, a second electrode layer, a first recombination material disposed between the first and second electrode layers, a first photoactive layer disposed between the first electrode layer and the first recombination material, and a second photoactive layer disposed between the first recombination material and the second electrode layer. The first photoactive layer is disposed in at least partial electrical contact with the first electrode (e.g., along a first plane) and with the first recombination material. Similarly, the second photoactive layer is disposed in at least partial electrical contact with the second electrode (e.g., along a second plane) and with the first recombination material. The first photoactive layer comprises a first population of nanostructures, and the second photoactive layer comprises a second population of nanostructures. The first and second photoactive layers typically each comprise a material that exhibits a type II band offset energy profile.
The first recombination material can be, e.g., discontinuous or continuous. Thus, in one class of embodiments, the first recombination material comprises a recombination layer disposed between the first and second photoactive layers. In embodiments in which the recombination material forms a continuous layer separating the two active layers, the recombination layer is sufficiently thin that the two photoactive layers remain in at least partial electrical contact with each other.
The first recombination material can comprise any of a variety of materials, including, but not limited to, a metal, a conductive polymer, and/or a small molecule, for example aluminum, silver, gold, PEDOT:PSS, TPD, NPD, and/or 3-(4-biphenyl)-4-phenyl-5-tert-butylphenyl-1,2,4-triazole (TAZ). The first recombination material is optionally transparent and/or flexible.
The device optionally includes additional photoactive layers and/or recombination materials. For example, the photovoltaic device can include a third photoactive layer disposed between the second photoactive layer and the second electrode and a second recombination material disposed between the second and third photoactive layers, where the third photoactive layer is in at least partial electrical contact with the second recombination material and with the second electrode. The second recombination material is typically also in at least partial electrical contact with the second photoactive layer.
Unless noted otherwise, any feature of the photovoltaic device embodiments noted above or otherwise herein can be applied to this class of embodiments. For example, all of the features noted herein with respect to photoactive layer configuration, nanostructure type, shape and composition, electrode composition and configuration and device architecture apply to these embodiments as well. Any of the optional transparent, blocking, and/or sealing layer embodiments described herein can be features of this set of embodiments as well.
Operation of an example embodiment in which two photoactive layers are separated by a recombination layer is schematically illustrated in
Optionally, in any of the above embodiments, the different photoactive layers within a photovoltaic device can comprise populations of nanostructures having identical absorption spectra, or each active layer can comprise a population of nanostructures having a distinct absorption spectrum (i.e., different active layers can be optimized for absorption of different wavelengths of light).
II. Electrodes
As described previously, the active layer is sandwiched between two conductive layers that operate as electrodes for the photovoltaic device. In its simplest form, e.g., as shown in
In the photovoltaic devices described herein, the electrodes that bound the active layer are typically provided to further enhance unidirectional current flow through the overall device. In particular, opposing electrodes are typically provided to have different work functions, so as to permit the flow of electrons from the active layer into one electrode, while permitting the flow of holes from the active layer to the other electrode (or electrons from the other electrode into the active layer). Typically, this is carried out by providing each of the electrodes being fabricated from different materials. For example, by providing one ITO electrode and one aluminum electrode, one can provide for flow of holes into the ITO electrode and the flow of electrons into the aluminum electrode. A variety of different materials may be employed for the electrodes, provided they generally meet these criteria. Further, electrode material selection will depend, in part, upon the architecture of the device, e.g., as described herein. For example, in some cases, transparent conductive materials, e.g., ITO layered on a transparent substrate, will be desired for at least one electrode, to provide light access to the active layer. In other embodiments, opaque electrode materials are easily employed.
In a number of applications, at least one electrode covers the exposed surface of the device, e.g., the portion of the device exposed to solar or other light energy. In such cases, it is necessary that the electrode at this surface be provided as a transparent or translucent layer. Conventional photovoltaic devices typically employ a glass based electrode upon which is provided a conductive coating, such as an Indium-Tin oxide (ITO) layer. The glass and ITO layer are transparent, allowing light to pass through the electrode and impinge on the active layer. Such electrode configurations are readily employed in the nanocomposite and other photovoltaic and layered devices described herein.
However, for a number of applications, the ultimate device is desired to be flexible or otherwise conformable in a way that use of glass layers may not be practical or even possible. In such cases, it will generally be desired that the electrodes used be flexible as well. Where typical sandwich style device architecture is employed, a transparent polymeric material that employs a metallic or other conductive coating may be used as the electrode layer. Examples of such polymeric materials include, e.g., polyester films or sheeting, e.g., Mylar films available from, e.g., DuPont, polycarbonate films, polyacetate films, polystyrene films or the like. Polymer materials are generally widely commercially available from a variety of sources. In certain preferred aspects, a thin glass layer is used in place of or in addition to a polymer layer to prevent oxygen permeability of many polymer films. Such thin glass sheeting, e.g., on the order of 50 μm thickness or less, can retain the flexibility of most polymer sheets. In such cases, an additional polymer coating may be desirable to prevent scratching of the glass sheet which can lead to breakage. Such polymer layers may be made conductive, as noted previously, by providing a conductive coating, i.e., ITO, aluminization, gold, PEDOT, or other thin, e.g., evaporated, conductive metal films.
In some cases, it will be desirable to protect the active layer from excessive or any exposure to oxygen. In particular, a number of conductive polymers described above are relatively unstable to oxygen, and lose their conductivity upon exposure. As such, it will often be desirable to appropriately seal the device to prevent such exposure. In some cases, the sealing operation may be accomplished through the appropriate selection of electrode layer material. For example, by providing an oxygen impermeable electrode layer on both sides of the active layer, one can protect that layer from oxygen exposure. A number of different polymeric films may be used to provide the oxygen barrier, and yet still provide for flexibility and transparency. Similarly, such films may be readily coated or otherwise treated to render the film conductive, so that it may function as one of the electrodes of the device. In at least one preferred example, an aluminized polymer film is provided as the electrode layer. By employing an oxygen getter, e.g., aluminum, magnesium, etc., as the conductive coating on a flexible transparent layer, one can further reduce the potential for oxygen exposure.
Alternatively, the sealing function may be provided by an additional layer that is added separate from the electrode layer. This may be the case for a traditional planar architectures, e.g., non-flexible, or alternatively, for one of the alternate architectures which are discussed in greater detail below. Regardless of the nature of the sealing layer as a portion of the electrode or as a separate layer, it will be appreciated that the sealing function must encompass the entire active layer. As such, the electrode layer may include nonconductive portions that extend beyond the edge of the conductive portion and the active layer, and which provide the region that seals against a corresponding region of the opposing electrode layer, e.g., using a heat-melt or adhesive-based sealing process. An example of this type of assembly is shown in
For other architectures, described in greater detail below, it is not necessary to provide the electrodes as transparent layers, e.g., where light need not pass through such electrodes. In such cases, any of the aforementioned flexible or other electrode configurations can be used. Alternatively, thin, flexible, metal foil electrode layers may be used. Further, in such cases, any sealing layer may not be layered onto the electrode layer, but may exist in a completely separate plane.
Further, in the case of alternative architectures, the function of protecting the polymer matrix from oxygen, where necessary, may be provided by the packaging of the device itself. For example, a flexible, transparent envelope may be provided to seal the device and prevent oxygen exposure of the active layer. Alternatively, where flexibility of the packaged device is not critical, these alternate architecture devices could be housed in more conventional packages, e.g., hermetically sealed behind a glass or other oxygen impermeable barrier. By way of example, and as discussed in greater detail below, side exposed photovoltaic devices may be encased in a transparent or partially transparent package, where one of the sealing layers is disposed over a side edge of the electrode/active layer/electrode portion of the device.
Although described as planar or sheet type electrodes, it will be appreciated that wire electrodes may also be employed in the devices described herein. Such wire electrodes may be an adjunct to one or more sheet or planar electrodes, or they may be in place of such planar electrodes, e.g., integrated into the active layer. By way of example, wire electrodes may be provided within or on one and/or the other surface of the active layer. The wires may be coated with blocking layers depending upon the function they are to serve, e.g., they may be coated with an electron blocking layer or a hole blocking layer. In certain cases, the wires may be integrated into the active layer, e.g., disposed within the interior of the active layer, e.g., as overlapping arrays of wires or interspersed with complementary wires, e.g., of alternate blocking layer coatings. The device may include both electrodes as wires or wire arrays, or may include one wire array electrode and one sheet electrode.
III. Device Architecture
Again, as noted above, the device architecture in its simplest form comprises a basic planar sandwich structure, e.g., as shown in
As noted previously, the basic architecture of a photovoltaic device in accordance with the invention comprises an active layer that is disposed between two electrodes. The active layer (or photoactive layer), as termed herein, generally refers to that portion or layer of the device in which light induced charge separation occurs. By light induced charge separation, is meant the generation of free electrons or electron/hole pairs, as a result of photons impinging on the active layer. Such light induction may be direct, e.g., light impacting a material results in the liberation of an electron, or it may be indirect, e.g., light impacting the active layer results in a chemical, physical or electrical change that later results in the liberation of an electron, e.g., through a chemical or physical pathway.
Through the use of the nanocomposite active layers or certain of the other nanostructure based active layers and certain of the electrode configurations described herein, one can produce photovoltaic devices that are efficient, flexible and lightweight. With these characteristics, it is possible to provide a wide variety of alternative architectures for photovoltaic devices and systems that can address many of the shortcomings of conventional photovoltaic technology.
In a first and likely preferred aspect, the basic photovoltaic device in accordance with the invention comprises a standard planar sandwich format, e.g., as shown in
In alternative aspects, it may be less desirable to provide one electrode layer as a transparent layer, e.g., because of inefficiencies in such layers from either a conductivity, flexibility or transmissivity standpoint. In such cases, alternative architectures may be employed that allow one to employ different electrode materials. For example, in a first aspect, one of the electrodes may be provided as a flexible metal layer, e.g., a metallized polymer sheet, e.g., aluminized Mylar, but including an array of transparent zones, e.g., as a screen. In such cases, one would lose some of the exposed surface area of the active layer in exchange for the ability to provide a more efficient first electrode layer. An example of a device employing this architecture is illustrated in
In a further alternative architecture, the active layer is disposed between two electrode layers, but the exposed surface is a side surface, rather than a surface that is covered by an electrode. A simplified example of this is shown in
The use of flexible active layer components, or overall devices allows for other useful adjustments in device architecture. By way of example, one of the limits on the output of a photovoltaic device is the amount of surface area that is may be impacted by photons from the relevant light source, e.g., the sun. In conventional, planar photovoltaics, the number of photons that impinges upon the active layer is directly related to the surface area of the device that is exposed to the light source. In many applications, the allowable surface area of a device is dictated by the space in which the device must fit, e.g., a roof top, airplane wing, extraterrestrial platform, i.e., satellite, space station, etc. By providing a device architecture that includes a convex exposed surface and active layer, e.g., as enabled by the flexible devices described herein, one can effectively increase the effective surface area of the device without increasing its footprint. This is particularly true where the relevant light source is oriented at a sub-normal angle to the device.
In addition to issues of increasing output without increasing footprint, one of the efficiency issues associated with conventional, planar photovoltaics is that they must be continually rotated, or repositioned in order to provide optimal exposure opportunities, e.g., pointing toward the sun or other light source. For stationary devices, the result is that for a substantial period, the exposed surface will be far from optimally positioned or oriented.
Again, this issue is addressed by the flexible active layer materials that permit the use of contoured exposed surfaces. These contoured exposed surfaces will allow for an optimization of exposure for a wider variety of solar source positions. By way of example, a device may be provided with a convex or concave architecture, e.g., as shown in
While described in terms of solar exposure, it will be appreciated that the devices described herein, and the various architectures are equally useful in other applications where one may wish to alter the angle at which light impinges on the device, e.g., when using alternate light sources to generate power, e.g., lasers, or for use as optical sensors, etc.
IV. Nanostructure Based Compositions
Another aspect of the present invention provides nanostructure based compositions, e.g., compositions such as those used in the active layers described above. One class of embodiments provides compositions comprising at least two populations of nanostructures, which can, but need not, be part of a nanocomposite. Other embodiments provide nanocomposites, e.g., doped polymer or small molecule nanocomposites.
Thus, one general class of embodiments provides a composition comprising a first population of nanostructures and a second population of nanostructures, which first population comprises nanostructures comprising a first material, and which second population comprises nanostructures comprising a second material different from the first material. Adjacent nanostructures are optionally in at least partial direct electrical contact with each other.
The nanostructures can be any of a variety of nanostructures. For example, the nanostructures can comprise a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, or an amorphous nanostructure. The nanostructures can comprise, e.g., nanocrystals, nanorods, nanowires, nanotubes, branched nanocrystals, nanotetrapods, tripods, bipods, nanodots, quantum dots, nanoparticles, branched tetrapods, or the like, or a combination thereof (e.g., nanorods and nanotetrapods, or nanorods and spherical or nonelongated nanocrystals, among many other possible combinations).
In a preferred class of embodiments, the first material is a first inorganic material and the second material is a second inorganic material. In one class of embodiments, the first material comprises a first semiconductor and the second material comprises a second semiconductor. For example, the first material can comprise an n-type semiconductor and the second material can comprise a p-type semiconductor.
In one class of embodiments, the first and second materials exhibit a type II band offset energy profile. Such compositions can, for example, be used as active layers in photovoltaic devices, or in other electronic and optoelectronic devices. In another class of embodiments, the first and second materials exhibit a type I band offset energy profile. Such compositions can, for example, be used in LEDs, or in other electronic and optoelectronic devices (e.g., where charge recombination and photon emission rather than charge separation is desired; as is known in the art, nanostructure emission spectra can be adjusted by controlling the composition and/or size of the nanostructures).
Essentially any pair of semiconductor materials with an appropriate band offset (i.e., type I or type II) can be used. For example, the first material can comprise a first semiconductor selected from the group consisting of: a Group II-VI semiconductor, a Group III-V semiconductor, a Group IV semiconductor, and an alloy thereof. Similarly, the second material can comprise a second semiconductor, different from the first semiconductor, selected from the group consisting of: a Group II-VI semiconductor, a Group III-V semiconductor, a Group IV semiconductor, and an alloy thereof. Example semiconductors include, but are not limited to, CdSe, CdTe, InP, InAs, CdS, ZnS, ZnSe, ZnTe, HgTe, GaN, GaP, GaAs, GaSb, InSb, Si, Ge, AlAs, AlSb, PbSe, PbS, and PbTe.
In one class of embodiments, the nanostructures of the first population and the nanostructures of the second population are intermixed in the composition. The nanostructures of the two populations can be uniformly mixed, or they can be partially or completely segregated, e.g., into two or more distinct regions, zones, layers, or the like.
The composition can, if desired, be formed into a film, which is optionally disposed between two electrode layers, e.g., for used in a photovoltaic device, LED, or other device. In some embodiments, the nanostructures of the two populations are intermixed in the film. In other embodiments, however, the film comprises at least a first sublayer and a second sublayer; the first sublayer comprises the first population of nanostructures and the second sublayer comprises the second population of nanostructures. For example, the first sublayer can comprise p-type semiconductor nanostructures and the second sublayer n-type semiconductor nanostructures, optionally with a p-n junction between the sublayers.
As in the preceding aspects, the nanostructures of the first and/or second populations can, but need not be, fused, partially fused, and/or sintered.
In some embodiments, the composition also includes a conductive polymer (e.g., a conductive polymer matrix in which the nanostructures are disposed. In alternative embodiments (e.g., where the first and second population of nanostructures collectively comprise both hole and electron conducting materials), the composition is substantially free of conductive polymer. In certain embodiments, the composition also includes a nonconductive polymer or other binder (e.g., a nonconductive polymer matrix in which the nanostructures are disposed, uniformly or nonuniformly). The composition optionally includes components included to modify the properties of the nanostructures, e.g., surface chemistries and ligands such as those described above.
The nanostructures of the first and/or second populations can be randomly or nonrandomly oriented. For example, each nanostructure of the first and/or second populations can have at least one elongated section oriented predominantly normal to a first plane (e.g., a surface of a film comprising the composition, or a surface of an electrode); as another example, each nanostructure of the first and/or second populations can have at least one elongated section oriented predominantly parallel to the first plane.
Another general class of embodiments provides a composition including a first population of nanostructures disposed in a matrix. The matrix comprises a conductive first polymer whose charge carrying properties have been altered by controlled partial oxidation of the polymer, a second polymer (e.g., a conductive polymer) and a small molecule, or a combination thereof (e.g., a partially oxidized conductive polymer and a small molecule, or a partially oxidized conductive first polymer, a second polymer, and a small molecule). It is worth noting that the nanostructures and the matrix can exhibit a type I or a type II band offset energy profile, or even a type 0 profile (no offset). Depending on the band offset energy profile and other properties of the compositions, they can be used, e.g., in active layers of photovoltaic devices such as those described herein, or in nanocomposite-based transistors, LEDs, and the like.
Any of the features of the device and composition embodiments described above can be applied to this class of embodiments as well, to the extent they are relevant. For example, nanostructure type, shape, and composition can be varied as described above. As another example, the small molecule can, e.g., comprise a semiconductive, organic, nonpolymeric molecule. Similarly, the small molecule can have a molecular weight less than 3000, 2000, 1500, 1000, or 500 and/or can conduct electrons, holes, or a combination thereof.
Yet another general class of embodiments provides a composition including a first population of nanostructures and a small molecule. Each nanostructure of the first population has at least one elongated section oriented predominantly normal to at least a first plane. Typically, the nanostructures are disposed in a matrix comprising the small molecule. The matrix optionally also includes a polymer, e.g., a conductive or nonconductive polymer, or optionally is substantially free of polymer. It is worth noting that the nanostructures and the small molecule can exhibit a type I or a type II band offset energy profile, or even a type 0 profile (no offset).
Any of the features of the device and composition embodiments described above can be applied to this class of embodiments as well, to the extent they are relevant. For example, nanostructure type, shape, and composition can be varied as described above. As another example, the small molecule can, e.g., comprise a semiconductive, organic, nonpolymeric molecule; have a molecular weight less than 3000, 2000, 1500, 1000, or 500; and/or conduct electrons, holes, or a combination thereof. It is worth noting that the composition is optionally formed into a film, e.g., a film in which the elongated section of each nanostructure is oriented predominantly normal to a surface of the film.
Another general class of embodiments provides a composition that can, e.g., be used to form a nanocomposite layer according to the methods described herein. The composition includes a population of nanostructures, a polymer and/or a small molecule, a first solvent, and a second solvent. The first solvent has a vapor pressure that is not equal to a vapor pressure of the second solvent, e.g., at a given temperature. For example, the vapor pressures of the first and second solvents can differ by at least 1 mm Hg, at least 10 mm Hg, at least 20 mm Hg, at least 50 mm Hg, at least 100 mm Hg, at least 150 mm Hg, or more. At least one of the first and second solvents is free of chloroform and pyridine.
The nature and relative proportion of the first and second solvents can be varied, e.g., depending on the composition of the nanostructures, the identity of the polymer and/or small molecule, and the desired morphology of the resulting nanocomposite film. For example, the two solvents can have different polarities, and the vapor pressure of the first solvent can be lower or higher than that of the second solvent.
The ratio (and/or identity) of the first and second solvents can be varied experimentally to determine a ratio that results in the nanocomposite layer having a desired morphology, e.g., wherein the nanostructures are distributed uniformly throughout the polymer or small molecule matrix. The ratio of the first solvent to the second solvent can have essentially any value that results in the nanocomposite layer having the desired morphology. Typically, the ratio of the first solvent to the second solvent is greater than 0.05:0.95 and less than 0.95:0.05 by volume. For example, the ratio can be greater than 0.1:0.9 and less than 0.9:0.1, greater than 0.15:0.85 and less than 0.85:0.15, greater than 0.2:0.8 and less than 0.8:0.2, or, typically, greater than 0.3:0.7 and less than 0.7:0.3, by volume.
The first and second solvents can be essentially any of the large number of solvents known in the art. Choice of solvents can depend, e.g., on the identity of the polymer or small molecule, the material(s) comprising the nanostructures, the technique used to coat the substrate, and/or the like. Preferably, the solvents each have a polarity such that the nanostructures are soluble in at least one of the two miscible solvents and the polymer or small molecule is soluble in at least the other of the two solvents. Suitable solvents include, but are not limited to, chloroform, toluene, tetrahydrofuran (THF), xylene, a hexane, chlorobenzene, and dichlorobenzene. For example, the first solvent (in which, e.g., the nanostructures are dissolved) can be toluene and the second solvent (in which, e.g., the polymer or small molecule is dissolved) can be chloroform, or vice versa. Other examples include, but are not limited to, chlorobenzene and toluene, xylene and toluene, chlorobenzene and chloroform, and chloroform and THF, as the first and second (or second and first) solvents.
The first mixture optionally includes three or more solvents. The third (or fourth, etc.) solvent is miscible with the first and second solvents, and it typically has a different vapor pressure, different polarity, and/or different solubility for the nanostructures, polymer, and/or small molecule. For example, the first mixture can include toluene, chloroform, and dichlorobenzene, or it can include toluene, chloroform, and pyridine.
Any of the features of the device and composition embodiments described above can be applied to this class of embodiments as well, to the extent they are relevant. For example, nanostructure type, shape, and composition can be varied as described above.
V. Device Manufacturing
The devices and compositions of the present invention also provide significant advantages in terms of manufacturability. In particular, current photovoltaic devices rely upon relatively low volume, high cost manufacturing processes in converting wafer scale semiconductor materials to operable photovoltaic devices. Conventional semiconductor based photovoltaics are typically manufactured in a batch mode with the number of devices being determined by the number of wafers used. Such manufacturing processes, because of the starting materials and processes, can be very expensive, and are also not easily scaled up to large scale manufacturing.
The devices of the present invention, on the other hand, are comprised of materials that are readily and cheaply available, or can be produced in substantial quantities at relatively low costs. Further, because of the nature of the various components of the devices, e.g., the active layer components and sealing and/or electrode layers, the processes for making these devices readily lends itself to ultra-high throughput manufacturing. By way of example, because the devices of the invention are typically in the form of flexible laminate structures, e.g., flexible electrodes laminated together with an active layer in between them, they may be produced using high volume film processing techniques, e.g., roll to roll processes, that are conventionally used in the film manufacturing and industrial laminate industries, e.g., in making reflective films, photographic films, etc.
An example of a roll-to-roll process and system 900 for fabricating devices in accordance with the invention is shown in
In a particular preferred example, using conventional ink-jet or screen printing technologies, e.g., as indicated by screen printer(s) 904, one can begin successively laying down multiple layers of material that form the photovoltaic device, e.g., layers 906, 908, 910, 912 and 914. For example, and as shown, in a first printing step, a first layer of blocking material 906 is printed onto moving substrate 902. Such blocking material may be a hole blocking layer or an electron blocking layer depending upon the resulting orientation of the device. Next, a layer of the photoactive material or composite 908, e.g., the nanocrystal/polymer matrix (or the core shell nanocrystal material) is deposited onto the blocking layer. In the case where a mechanical or electrical orientation step is desired for the nanocrystals (or other nanostructures), that would generally be carried out following deposition of this layer, but prior to the application of the next layer. Heating, drying and/or curing steps may be interjected between the various layering steps, to ensure clean interfaces between the layers, e.g., minimal mixing, among layers. Next, a second blocking layer 910 is applied to the upper surface of the active layer. This blocking layer will be the complement of the first blocking layer 906, e.g., if the first layer 906 was a hole blocking layer, this layer would be an electron blocking layer. A second sheet of substrate material 914, e.g., a transparent conductive electrode sheet, e.g., ITO coated polymer sheet as discussed above, is laminated to the top of second blocking layer. Alternatively, and as shown, an ITO or other conductive layer may be applied as a coating layer 912 over the second blocking layer 910, followed by application of the substrate layer 914 which may form the sealing layer. Further, additional layers, e.g., sealing layers or other electrode, blocking and active layers may be applied in additional steps, e.g., in the case of tandem or multiple active layer devices.
Subsequent process steps then attach electrical connections for the sheets of desired size dimensions.
Thus, one class of embodiments provides methods of producing a photovoltaic device. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided. The first substrate is coated with a photoactive matrix that exhibits a type II band offset energy profile and that comprises at least a first population of elongated semiconductor nanostructures, the nanostructures comprising a longitudinal axis, to provide a photoactive layer. The semiconductor nanostructures are oriented such that their longitudinal axes are predominantly oriented normal to the first planar substrate. A second conductive layer is laminated onto the photoactive layer.
The methods can also include providing a blocking layer on the first substrate prior to coating the first substrate with a photoactive matrix and/or providing a blocking layer on the photoactive layer prior to laminating the second conductive layer onto the photoactive layer. The methods optionally include providing one or more sealing layers over opposing surfaces of the photovoltaic device in addition to the first substrate and second conductive layer, whereby the one or more sealing layers hermetically seal the photovoltaic device. As noted above, heating, drying, and/or curing steps may be inserted between the various layering steps, if desired. In addition, the various composition and device components noted above can be adapted for used in these methods, as appropriate. For example, the nanostructures can comprise a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure.
A related class of embodiments provides a system for fabricating a photovoltaic device. The system comprises a source of a first substrate layer having a first conductive surface, a conveyor system for conveying the first substrate layer, and a source of a photoactive matrix fluidly coupled to a layer deposition system. The layer deposition system is at least partially disposed over the substrate conveyor system, to provide a layer of photoactive matrix on the first substrate layer. The system also includes a source of a second conductive material coupled to the layer deposition system positioned over the substrate conveyor system for depositing a layer of the second conductive material onto a layer of photoactive matrix deposited on the first substrate layer.
In one class of embodiments, the source of first substrate material comprises a rolled sheet of first substrate material. The source of first substrate material optionally also includes a source of first conductive material and a deposition system for depositing the first conductive material onto the first substrate material to provide the first conductive surface. Examples of suitable layer deposition systems include, but are not limited to, a doctor-blade, a screen printing system, an ink-jet printing system, a dip coating system, a sheer coating system, a tape casting system, and a film casting system. Any of the above embodiments can be applied to this embodiment as well, to the extent they are relevant.
Another general class of embodiments provides methods of producing a photovoltaic device. In these methods, a first planar substrate having a first conductive layer disposed thereon is provided. To provide a photoactive layer, the first substrate is coated with a composition that comprises a population of nanostructures. The nanostructures comprise a core of a first material and a shell of a second material different from the first material. The nanostructures are fused, partially fused, and/or sintered, and a second conductive layer is layered onto the photoactive layer.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of blocking and/or sealing layers, and the like.
Yet another class of embodiments provides methods of producing a layered device comprising two (or more) populations of nanostructures (e.g., a photovoltaic device, an LED, or the like). The layered device comprises a first population of nanostructures comprising a first material and a second population of nanostructures comprising a second material different from the first material. In the methods, a first substrate is provided and coated with a composition comprising the first population of nanostructures to provide a first layer.
In one class of embodiments, the nanostructures of the first and second populations are intermixed in the first layer. In this class of embodiments, the first substrate is coated with a composition comprising a mixture of the first and second populations of nanostructures to provide the first layer.
In another class of embodiments, the layered device comprises at least a first layer comprising the first population of nanostructures and a second layer comprising the second population of nanostructures. In this class of embodiments, the methods include coating the first substrate with a composition comprising the second population of nanostructures, to provide the second layer. In a related class of embodiments, the second population of nanostructures is disposed on the first substrate. For example, nanostructures that cannot be solution-processed (e.g., some nanowires) can be grown on the first substrate (e.g., on an electrode); a solvent process can be used to add a layer of solvent dispersible nanostructures, as above, or other layers can be laminated over the first substrate-second nanostructure population layer.
The methods optionally include layering a second conductive layer onto the first layer (or the second layer, depending on the number and orientation of the layers). Similarly, the methods optionally include providing a blocking layer on the first substrate prior to coating the first substrate with the composition comprising the first population of nanostructures and/or providing a blocking layer on the first (or second) layer prior to laminating the second conductive layer onto the first (or second) layer.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, fusing, partial fusing, and/or sintering of nanostructures, and the like.
A related class of embodiments provides a system for fabricating a layered device, where the device comprises a layer in which a first and a second population of nanostructures are intermixed. The nanostructures of the first population comprise a first material, and the nanostructures of the second population comprise a second material different from the first material. The system comprises a source of a first substrate layer, a conveyor system for conveying the first substrate layer, and a source of a composition comprising the first and second populations of nanostructures, fluidly coupled to a layer deposition system. The layer deposition system is at least partially disposed over the substrate conveyor system, to provide a layer in which the nanostructures of the first and second populations are intermixed on the first substrate layer.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of blocking and/or sealing layers, fusing, partial fusing, and/or sintering of nanostructures, provision of a layer of a second conductive material, types of layer deposition systems, and the like. It is worth noting that the first substrate layer optionally has a first conductive surface (or is otherwise conductive).
Another related class of embodiments provides a system for fabricating a layered device, where the device comprises a first layer comprising a first population of nanostructures and a second layer comprising a second population of nanostructures. The nanostructures of the first population comprise a first material, and the nanostructures of the second population comprise a second material different from the first material. The system comprises a source of a first substrate layer, a conveyor system for conveying the first substrate layer, a source of a first composition comprising the first population of nanostructures fluidly coupled to a layer deposition system (the layer deposition system being at least partially disposed over the substrate conveyor system, to provide a first layer), and a source of a second composition comprising the second population of nanostructures fluidly coupled to the layer deposition system (the layer deposition system being at least partially disposed over the substrate conveyor system, to provide a second layer).
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of blocking and/or sealing layers, fusing, partial fusing, and/or sintering of nanostructures, provision of a layer of a second conductive material, types of layer deposition systems, and the like.
Another class of method embodiments provides methods of producing a photovoltaic device. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided and coated with a composition that comprises a first population of nanostructures to provide a first photoactive layer. A second conductive layer is layered onto the first photoactive layer. The second conductive layer is coated with a composition that comprises a second population of nanostructures to provide a second photoactive layer, and a third conductive layer is layered onto the second photoactive layer.
As in the preceding classes of methods, essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix. Additional photoactive and/or conductive layers can be provided. Similarly, features of the methods described above can be applied to this class of methods as well, e.g., with respect to provision of blocking and sealing layers.
Yet another class of method embodiments provides methods of producing photovoltaic devices. In the methods, a first planar substrate having a first conductive layer disposed thereon is provided and coated with a composition that comprises a first population of nanostructures to provide a first photoactive layer. A first recombination material is disposed onto the first photoactive layer. The first recombination material (and any exposed portion of the first photoactive layer) is coated with a composition that comprises a second population of nanostructures to provide a second photoactive layer, and a second conductive layer is layered onto the second photoactive layer. In certain embodiments, disposing the first recombination material onto the first photoactive layer comprises coating the first photoactive layer with the first recombination material to provide a first recombination layer.
As in the preceding classes of methods, essentially any of the features of the devices and compositions noted above can be included in these methods. For example, the nanostructures optionally include a nanocrystal, a nanowire, a single-crystal nanostructure, a double-crystal nanostructure, a polycrystalline nanostructure, and/or an amorphous nanostructure. The nanostructures can be, e.g., any of those noted above, as can any other components of the matrix. Additional photoactive layers and/or recombination materials can be provided. Similarly, features of the methods described above can be applied to this class of methods as well, e.g., with respect to provision of blocking and sealing layers.
The present invention also provides methods of forming nanocomposite layers. At present, to form a nanocomposite layer, a mixture of nanostructures, a polymer, and a solvent is typically used to coat a substrate. However, the solvent typically evaporates more quickly from the polymer than from the nanostructures, leading to uneven deposition of the two components on the substrate. We have found that using a mixture of two (or more) solvents that evaporate at different rates and that have different affinities for the nanostructures and the polymer can increase homogeneity of the resulting nanocomposite layer.
Thus, one general class of embodiments provides methods of forming a nanocomposite layer, for example, during fabrication of a photovoltaic or other layered device. In the methods, a planar substrate and a first mixture are provided, and the substrate is coated with the first mixture to provide the nanocomposite layer. The first mixture includes a population of nanostructures, a polymer and/or a small molecule, a first solvent, and a second solvent. The first and second solvents have different vapor pressures, e.g., at a given temperature, e.g., the temperature at which the substrate is coated with the first mixture. For example, the vapor pressures of the first and second solvents can differ by at least 1 mm Hg, at least 10 mm Hg, at least 20 mm Hg, at least 50 mm Hg, at least 100 mm Hg, at least 150 mm Hg, or more. At least one of the first and second solvents is free of chloroform and pyridine. The majority of the first and second solvents (e.g., substantially all of the first and second solvent) is typically permitted to evaporate during or following the coating step, such that little or no solvent remains in the resulting nanocomposite layer.
In one class of embodiments, the nanostructures are provided in the first solvent and the polymer and/or the small molecule is provided in the second solvent. The nanostructures in the first solvent and the polymer and/or small molecule in the second solvent are combined, resulting in the first mixture.
The nature and relative proportion of the first and second solvents can be varied, e.g., depending on the composition of the nanostructures, the identity of the polymer and/or small molecule, and the desired morphology of the resulting nanocomposite film. For example, the vapor pressure of the first solvent can be lower or higher than that of the second solvent, and the first solvent can be more or less polar than the second solvent. To produce a nanocomposite layer including inorganic semiconductor nanocrystals and an organic polymer, for example, the first solvent in which the nanocrystals are suspended typically has a lower vapor pressure (i.e., is less volatile) and is less polar than the second solvent in which the polymer is dissolved; in other embodiments, the first solvent has a higher vapor pressure and/or is more polar than the second solvent.
The ratio (and/or identity) of the first and second solvents can be varied experimentally to determine a ratio that results in the nanocomposite layer having a selected morphology, e.g., wherein the nanostructures are distributed uniformly throughout the polymer or small molecule matrix. The ratio of the first solvent to the second solvent can have essentially any value that results in the nanocomposite layer having the selected morphology. Typically, the ratio of the first solvent to the second solvent is greater than 0.05:0.95 and less than 0.95:0.05 by volume. For example, the ratio can be greater than 0.1:0.9 and less than 0.9:0.1, greater than 0.15:0.85 and less than 0.85:0.15, greater than 0.2:0.8 and less than 0.8:0.2, or, typically, greater than 0.3:0.7 and less than 0.7:0.3, by volume.
The first and second solvents can be essentially any of the large number of solvents known in the art. Choice of solvents can depend, e.g., on the identity of the polymer or small molecule, the material(s) comprising the nanostructures, the technique used to coat the substrate, and/or the like. Preferably, the solvents each have a polarity such that the nanostructures are soluble in at least one of the two miscible solvents and the polymer or small molecule is soluble in at least the other of the two solvents. Suitable solvents include, but are not limited to, chloroform, toluene, tetrahydrofuran (THF), xylene, a hexane, chlorobenzene, and dichlorobenzene. For example, the first solvent (in which, e.g., the nanostructures are dissolved) can be toluene and the second solvent (in which, e.g., the polymer or small molecule is dissolved) can be chloroform, or vice versa. Other examples include, but are not limited to, chlorobenzene and toluene, xylene and toluene, chlorobenzene and chloroform, and chloroform and THF, as the first and second (or second and first) solvents.
The first mixture optionally includes three or more solvents. The third (or fourth, etc.) solvent is miscible with the first and second solvents, and it typically has a different vapor pressure, different polarity, and/or different solubility for the nanostructures, polymer, and/or small molecule. For example, the first mixture can include toluene, chloroform, and dichlorobenzene, or it can include toluene, chloroform, and pyridine.
The substrate can be coated with the mixture by any of a variety of techniques known in the art. For example, the substrate can be spin coated with the first mixture. As another example, the first mixture can be applied to the substrate with a doctor-blade. As still other examples, the first mixture can be applied to the substrate by screen printing, ink-jet printing, dip coating, sheer coating, tape casting, or film casting.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of blocking and/or sealing layers, and the like. It is worth noting that the planar substrate optionally has a first conductive layer disposed thereon.
A related class of embodiments provides a system for fabricating a nanocomposite layer, e.g., for use in or as part of a photovoltaic or other layered device. The system includes a layer deposition system and a source of a composition comprising a population of nanostructures, a polymer and/or a small molecule, a first solvent, and a second solvent, fluidly coupled to the layer deposition system. The layer deposition system is configured to deposit the composition on a substrate to provide the nanocomposite layer. The first solvent has a vapor pressure that is not equal to a vapor pressure of the second solvent, and at least one of the first and second solvents is free of chloroform and pyridine.
All of the various optional configurations and features noted in the embodiments above apply here as well, to the extent they are relevant; e.g., for types of nanostructures, types of materials, provision of conductive, blocking and/or sealing layers, types of layer deposition systems, and the like.
VI. Synthesis of Nanostructures
Nanostructures can be fabricated and their size can be controlled by any of a number of convenient methods that can be adapted to different materials. For example, synthesis of nanocrystals of various composition is described in, e.g., Peng et al. (2000) “Shape control of CdSe nanocrystals” Nature 404, 59-61; Puntes et al. (2001) “Colloidal nanocrystal shape and size control: The case of cobalt” Science 291, 2115-2117; U.S. Pat. No. 6,306,736 to Alivisatos et al. (Oct. 23, 2001) entitled “Process for forming shaped group III-V semiconductor nanocrystals, and product formed using process”; U.S. Pat. No. 6,225,198 to Alivisatos et al. (May 1, 2001) entitled “Process for forming shaped group II-VI semiconductor nanocrystals, and product formed using process”; U.S. Pat. No. 5,505,928 to Alivisatos et al. (Apr. 9, 1996) entitled “Preparation of III-V semiconductor nanocrystals”; U.S. Pat. No. 5,751,018 to Alivisatos et al. (May 12, 1998) entitled “Semiconductor nanocrystals covalently bound to solid inorganic surfaces using self-assembled monolayers”; U.S. Pat. No. 6,048,616 to Gallagher et al. (Apr. 11, 2000) entitled “Encapsulated quantum sized doped semiconductor particles and method of manufacturing same”; and U.S. Pat. No. 5,990,479 to Weiss et al. (Nov. 23, 1999) entitled “Organo luminescent semiconductor nanocrystal probes for biological applications and process for making and using such probes.”
Growth of nanowires having various aspect ratios, including nanowires with controlled diameters, is described in, e.g., Gudiksen et al (2000) “Diameter-selective synthesis of semiconductor nanowires” J. Am. Chem. Soc. 122, 8801-8802; Cui et al. (2001) “Diameter-controlled synthesis of single-crystal silicon nanowires” Appl. Phys. Lett. 78, 2214-2216; Gudiksen et al. (2001) “Synthetic control of the diameter and length of single crystal semiconductor nanowires” J. Phys. Chem. B 105,4062-4064; Morales et al. (1998) “A laser ablation method for the synthesis of crystalline semiconductor nanowires” Science 279, 208-211; Duan et al. (2000) “General synthesis of compound semiconductor nanowires” Adv. Mater. 12, 298-302; Cui et al. (2000) “Doping and electrical transport in silicon nanowires” J. Phys. Chem. B 104, 5213-5216; Peng et al. (2000) “Shape control of CdSe nanocrystals” Nature 404, 59-61; Puntes et al. (2001) “Colloidal nanocrystal shape and size control: The case of cobalt” Science 291, 2115-2117; U.S. Pat. No. 6,306,736 to Alivisatos et al. (Oct. 23, 2001) entitled “Process for forming shaped group III-V semiconductor nanocrystals, and product formed using process”; U.S. Pat. No. 6,225,198 to Alivisatos et al. (May 1, 2001) entitled “Process for forming shaped group II-VI semiconductor nanocrystals, and product formed using process”; U.S. Pat. No. 6,036,774 to Lieber et al. (Mar. 14, 2000) entitled “Method of producing metal oxide nanorods”; U.S. Pat. No. 5,897,945 to Lieber et al. (Apr. 27, 1999) entitled “Metal oxide nanorods”; U.S. Pat. No. 5,997,832 to Lieber et al. (Dec. 7, 1999) “Preparation of carbide nanorods”; Urbau et al. (2002) “Synthesis of single-crystalline perovskite nanowires composed of barium titanate and strontium titanate” J. Am. Chem. Soc., 124, 1186; and Yun et al. (2002) “Ferroelectric Properties of Individual Barium Titanate Nanowires Investigated by Scanned Probe Microscopy” Nanoletters 2, 447.
Growth of branched nanowires (e.g., nanotetrapods, tripods, bipods, and branched tetrapods) is described in, e.g., Jun et al. (2001) “Controlled synthesis of multi-armed CdS nanorod architectures using monosurfactant system” J. Am. Chem. Soc. 123, 5150-5151; and Manna et al. (2000) “Synthesis of Soluble and Processable Rod-, Arrow-, Teardrop-, and Tetrapod-Shaped CdSe Nanocrystals” J. Am. Chem. Soc. 122, 12700-12706.
Synthesis of nanoparticles is described in, e.g., U.S. Pat. No. 5,690,807 to Clark Jr. et al. (Nov. 25, 1997) entitled “Method for producing semiconductor particles”; U.S. Pat. No. 6,136,156 to El-Shall, et al. (Oct. 24, 2000) entitled “Nanoparticles of silicon oxide alloys”; U.S. Pat. No. 6,413,489 to Ying et al. (Jul. 2, 2002) entitled “Synthesis of nanometer-sized particles by reverse micelle mediated techniques”; and Liu et al. (2001) “Sol-Gel Synthesis of Free-Standing Ferroelectric Lead Zirconate Titanate Nanoparticles” J. Am. Chem. Soc. 123, 4344. Synthesis of nanoparticles is also described in the above citations for growth of nanocrystals, nanowires, and branched nanowires, where the resulting nanostructures have an aspect ratio less than about 1.5.
Synthesis of core-shell nanostructure heterostructures, namely nanocrystal and nanowire (e.g., nanorod) core-shell heterostructures, are described in, e.g., Peng et al. (1997) “Epitaxial growth of highly luminescent CdSe/CdS core/shell nanocrystals with photostability and electronic accessibility” J. Am. Chem. Soc. 119, 7019-7029; Dabbousi et al. (1997) “(CdSe)ZnS core-shell quantum dots: Synthesis and characterization of a size series of highly luminescent nanocrysallites” J. Phys. Chem. B 101, 9463-9475; Manna et al. (2002) “Epitaxial growth and photochemical annealing of graded CdS/ZnS shells on colloidal CdSe nanorods” J. Am. Chem. Soc. 124, 7136-7145; and Cao et al. (2000) “Growth and properties of semiconductor core/shell nanocrystals with InAs cores” J. Am. Chem. Soc. 122, 9692-9702. Similar approaches can be applied to growth of other core-shell nanostructures.
Growth of nanowire heterostructures in which the different materials are distributed at different locations along the long axis of the nanowire is described in, e.g., Gudiksen et al. (2002) “Growth of nanowire superlattice structures for nanoscale photonics and electronics” Nature 415, 617-620; Bjork et al. (2002) “One-dimensional steeplechase for electrons realized” Nano Letters 2, 86-90; Wu et al. (2002) “Block-by-block growth of single-crystalline Si/SiGe superlattice nanowires” Nano Letters 2, 83-86; and U.S. patent application 60/370,095 (Apr. 2, 2002) to Empedocles entitled “Nanowire heterostructures for encoding information.” Similar approaches can be applied to growth of other heterostructures.
In certain embodiments, the collection or population of nanostructures is substantially monodisperse in size and/or shape. See, e.g., US patent application 20020071952 by Bawendi et al entitled “Preparation of nanocrystallites.”
VII. Kits
The devices and compositions herein can be packaged as kits. For example, any of the devices or compositions of the invention can be packaged in one or more containers. Similarly, kits can include instructional materials that can be used to practice the methods herein, operate the devices herein, use the compositions herein and/or operate the systems herein. Kits can include other convenient features, such as protective packaging materials, instructional materials for assembly of components of the devices or systems, electrical couplings to couple devices or systems to an electrical input or output, or the like.
Although described in some detail for purposes of understanding, the scope of the claimed invention herein is not limited to the disclosure and is only limited by the claims appended hereto or to any related patent or application, including without limitation any continuation, in whole or in part, divisional, reissue, reexamination, etc.
The following sets forth a series of experiments that demonstrate construction of nanocomposite and nanostructure based photovoltaic devices. It is understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims. Accordingly, the following examples are offered to illustrate, but not to limit, the claimed invention.
This example describes fabrication of a CdSe nanocrystal-P3HT polymer nanocomposite photovoltaic device. CdSe nanorods have been used; CdSe nanotetrapods can also be used, as can other nanostructure types and/or compositions.
Substrate Cleaning
Substrates (e.g., ITO on glass, from Thin Film Devices, Inc., www.tfdinc.com) are cleaned, e.g., using the following procedure. Substrates are wiped with isopropanol, ultrasonicated in isopropanol, ultrasonicated in 2% Hellmanex™ in deionized water, rinsed very thoroughly under flowing deionized water, ultrasonicated in deionized water, ultrasonicated in semiconductor grade acetone, and ultrasonicated in semiconductor grade isopropanol. Each sonication is for 15 minutes. The substrates are then oxygen plasma cleaned, at 200 W (1% reflected power) for 10 minutes with oxygen introduced at a pressure of approximately 400 mTorr into a vacuum of 80 mTorr.
PEDOT Layer Processing
PEDOT/PSS Poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (e.g., Baytron® P VP AI 4083 from H. C. Starck) is filtered through a 0.2 μm pore size cellulose acetate filter. PEDOT is spin coated onto the substrates at 3000 rpm for 60 seconds. The PEDOT layer is then cured by baking the spincoated substrate on a hotplate at 120° C. for 60 minutes under atmospheric conditions.
Preparation of P3HT in Chloroform (CHCl3) Solution
The P3HT solution is prepared in a glove-box with an inert (e.g., nitrogen, argon or xenon) atmosphere. Anhydrous chloroform (previously filtered with a 0.2 μm pore size PTFE filter) is added to the P3HT, such that the concentration of P3HT in the resulting solution is 20 mg/ml. The solution is vortexed for 5 minutes, stirred for approximately 1 hour on a stir plate, and heated at 56° C. for 10 minutes while stirring. The P3HT:chloroform solution is filtered with a 0.2 μm pore size PTFE filter, and protected from light and oxygen.
Preparation of Nanocrystal Solution
The nanocrystal solution is prepared in the glove-box. CdSe nanocrystals are dissolved in anhydrous chloroform (previously filtered with a 0.2 μm pore size PTFE filter) at a concentration between 70-80 mg/ml. A small aliquot of known volume of the CdSe nanocrystal solution is removed from the glove box, the nanocrystals are dried under nitrogen flow, and the nanocrystals are weighed to determine the concentration of the nanocrystal solution. (These nanocrystals, which have been exposed to oxygen, are then discarded and are not used to fabricate the photovoltaic device.) If necessary, additional chloroform is added to adjust the concentration of the nanocrystal solution remaining in the glove box to 70-80 mg/ml.
Preparation of nanocrystal:P3HT Blend Solution
The CdSe nanocrystal:polymer solution is also prepared in the glove box. The CdSe:CHCl3 solution and the P3HT:CHCl3 solution are combined into a micro-centrifuge tube, such that the ratio of CdSe:P3HT is 90:10 by weight, the concentration of P3HT in the final solution is between 5-7 mg/ml, and the concentration of CdSe nanocrystals in the final solution is between 50-70 mg/ml. For example, if the concentration of CdSe in CHCl3 is 75 mg/ml and the P3HT in CHCl3 is 20.0 mg/ml, 300 μl of CdSe nanocrystal solution and 125 μl of P3HT solution are mixed, such that the resulting ratio of CdSe:P3HT is 90:10, the resulting concentration of P3HT is 5.9 mg/ml, and the resulting concentration of CdSe is 52.9 mg/ml. The solution is vortexed for 2 minutes and centrifuged for 2 minutes at 11,000 rpm in a microcentrifuge.
Spincoating of nanocrystal:P3HT Blend Solution
The CdSe nanocrystal:P3HT blend is spin coated onto the ITO/PEDOT substrates (in the glove box). Typically, 100 μl of solution is used for each substrate, with a spin speed of 1200 rpm for 40 seconds. Any solution on the back side of the substrates is removed by wiping with chloroform.
Evaporation of Aluminum Cathodes
The nanocomposite-PEDOT-coated substrates are transferred without exposure to oxygen into an evaporator. Aluminum (purity 99.999%) is evaporated onto them at a rate of 5 A/s under a vacuum of less than 1×10−7 torr to a thickness of approximately 200 nm.
Silver Paste
Any nanocomposite and/or PEDOT film on top of the ITO electrode contact pins is removed. Silver paste is applied to establish electrical connection to the ITO pins. The resulting devices are then characterized as desired.
This example describes fabrication of a photovoltaic device comprising two intermixed populations of nanocrystals, CdSe nanocrystals and CdTe nanocrystals.
Substrate Cleaning
Substrates (e.g., ITO on glass, from Thin Film Devices, Inc., www.tfdinc.com) are cleaned, e.g., using the following procedure. Substrates are wiped with isopropanol, ultrasonicated in isopropanol, ultrasonicated in 2% Hellmanex™ in deionized water, rinsed very thoroughly under flowing deionized water, ultrasonicated in deionized water, ultrasonicated in semiconductor grade acetone, and ultrasonicated in semiconductor grade isopropanol. Each sonication is for 15 minutes. The substrates are then oxygen plasma cleaned, at 200 W (1% reflected power) for 10 minutes with oxygen introduced at a pressure of approximately 400 mTorr into a vacuum of 80 mTorr.
PEDOT Layer Processing
PEDOT/PSS Poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (e.g., Baytron® P VP AI 4083 from H. C. Starck) is filtered through a 0.2 μm pore size cellulose acetate filter. PEDOT is spin coated onto the substrates at 3000 rpm for 60 seconds. The PEDOT layer is then cured by baking the spincoated substrate on a hotplate at 120° C. for 60 minutes under atmospheric conditions.
Preparation of CdSe:CdTe Bicrystal Blend Solution
The CdSe:CdTe bicrystal blend solution is prepared in a glove-box with an inert (e.g., argon or nitrogen) atmosphere. CdTe nanocrystals are washed by dissolving them in toluene and precipitating them with isopropanol 3 times; CdSe nanocrystals are washed by dissolving them in toluene and precipitating them with methanol 3 times. For surface treatment, both CdSe and CdTe nanocrystals are stirred in a solution of toluene and phenylphosphonic acid (PPA) at 110° C. for 20 hours. (The surface treatment step may not be necessary and could be omitted, or a different nanocrystal cleaning procedure, e.g., using pyridine, followed by treatment with PPA or another ligand may be substituted for this step.) After precipitation with isopropanol, the nanocrystals are dissolved in toluene, e.g., at a concentration of 95 mg/ml (for CdTe) and 110 mg/ml (for CdSe), respectively. The CdTe:toluene solution and the CdSe:toluene solution are combined into a 1.5 ml glass vial, such that the ratio of CdTe:CdSe is 50:50 by weight, and the concentration of nanocrystals in the final solution is between about 80-100 mg/ml. For example, if the concentration of CdTe in toluene is 95 mg/ml and the CdSe in toluene is 110 mg/ml, 500 ul of CdTe nanocrystal solution and 432 ul CdSe nanocrystal solution are mixed, such that the resulting ratio of CdTe:CdSe is 50:50 and the resulting concentration of nanocrystals is 102 mg/ml. The solution is vortexed for 2 minutes, heated at 56° C. for 10 minutes, and ultrasonicated for 15 minutes. After the solution is transferred to a microcentrifuge vial, it is centrifuged for 2 minutes at 11,000 rpm in a microcentrifuge.
Spincoating of CdSe:CdTe Nanocrystal Blend Solution
The CdTe:CdSe solution is spincoated onto the ITO/PEDOT:PSS substrates (in the glove box). Typically, 120 μl of solution is used for each substrate, with a spin speed of 950 rpm for 40 seconds. Any solution on the back side of the substrates is removed by wiping with chloroform.
Evaporation of Aluminum Cathodes
The nanocrystal-PEDOT-coated substrates are transferred without exposure to oxygen into an evaporator. Aluminum (purity 99.999%) is evaporated onto them at a rate of 5 A/s under a vacuum of less than 1×10−7 torr to a thickness of approximately 200 nm.
Silver Paste
Any nanocrystal and/or PEDOT film on top of the ITO electrode contact pins is removed. Silver paste is applied to establish electrical connection to the ITO pins. The resulting devices are then characterized as desired.
This example demonstrates fabrication of nanocomposite photovoltaic devices. The nanocomposite can include, e.g., a polymer matrix, a doped polymer matrix, or a small molecule matrix. As described in the following sections, the example devices include CdSe nanocrystals in a matrix comprising 0-100% P3HT polymer and 100-0% TPD.
Substrate Cleaning
Substrates (e.g., ITO on glass, from Thin Film Devices, Inc., www.tfdinc.com) are cleaned, e.g., using the following procedure. Substrates are wiped with isopropanol, ultrasonicated in isopropanol, ultrasonicated in 2% Hellmanex™ in deionized water, rinsed very thoroughly under flowing deionized water, ultrasonicated in deionized water, ultrasonicated in semiconductor grade acetone, and ultrasonicated in semiconductor grade isopropanol. Each sonication is for 15 minutes. The substrates are then oxygen plasma cleaned, at 200 W (1% reflected power) for 10 minutes with oxygen introduced at a pressure of approximately 400 mTorr into a vacuum of 80 mTorr.
PEDOT Layer Processing
PEDOT/PSS Poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (e.g., Baytron®P VP AI 4083 from H. C. Starck) is filtered through a 0.2 μm pore size cellulose acetate filter. PEDOT is spin coated onto the substrates at 3000 rpm for 60 seconds. The PEDOT layer is then cured by baking the spincoated substrate on a hotplate at 120° C. for 60 minutes under atmospheric conditions.
Preparation of P3HT in Chloroform (CHCl3) Solution
The P3HT solution is prepared in a glove-box with an inert (e.g., nitrogen, argon or xenon) atmosphere. Anhydrous chloroform (previously filtered with a 0.2 μm pore size PTFE filter) is added to the P3HT, such that the concentration of P3HT in the resulting solution is 20 mg/ml. The solution is vortexed for 5 minutes, stirred for approximately 1 hour on a stir plate, and heated at 56° C. for 10 minutes while stirring. The P3HT:chloroform solution is filtered with a 0.2 μm pore size PTFE filter, and protected from light and oxygen.
Preparation of Nanocrystal Solution
The nanocrystal solution is prepared in the glove-box. CdSe nanocrystals are dissolved in anhydrous chloroform (previously filtered with a 0.2 μm pore size PTFE filter) at a concentration between 70-80 mg/ml. A small aliquot of known volume of the CdSe nanocrystal solution is removed from the glove box, the nanocrystals are dried under nitrogen flow, and the nanocrystals are weighed to determine the concentration of the nanocrystal solution. (These nanocrystals, which have been exposed to oxygen, are then discarded and are not used to fabricate the photovoltaic device.) If necessary, additional chloroform is added to adjust the concentration of the nanocrystal solution remaining in the glove box to 70-80 mg/ml.
Alternatively, the nanocrystals are prepared and washed as described in U.S. patent application Ser. No. ______ (Attorney Docket No. 40-003400US), filed of even date herewith, entitled “Methods of Processing Nanocrystals, Compositions, Devices and Systems Including Same” by Erik Scher et al. The washed nanocrystals can, e.g., be dissolved in toluene.
Preparation of TPD Solution
The TPD solution is prepared in a glove-box with an inert atmosphere. Anhydrous chloroform (previously filtered with a 0.2 μm pore size PTFE filter) is added to the TPD, such that the concentration of TPD in the resulting solution is 20 mg/ml. The solution is vortexed for 5 minutes, stirred for approximately 1 hour on a stir plate, and heated at 56° C. for 10 minutes while stirring. The TPD:chloroform solution is filtered with a 0.2 μm pore size PTFE filter, and protected from light and oxygen.
Preparation of Nanocrystal:(P3HT and/or TPD) Blend Solution
The CdSe nanocrystal:polymer:TPD solution is also prepared in the glove box. The TPD:CHCl3 solution and the P3HT:CHCl3 solutions are mixed in the desired ratio, such that the resulting solution is 0-100% TPD:CHCl3 and 100-0% P3HT:CHCl3. The CdSe:CHCl3 (or CdSe:toluene) solution and the (TPD and/or P3HT):CHCl3 solution are combined into a micro-centrifuge tube, such that the ratio of CdSe:(P3HT and/or TPD) is 90:10 by weight, the concentration of the sum of P3HT and TPD in the final solution is 5-7 mg/ml, and the concentration of CdSe nanocrystals in the final solution is 50-70 mg/ml. For example, if the concentration of CdSe in CHCl3 is 75 mg/ml and the concentration of P3HT and/or TPD in CHCl3 is 20.0 mg/ml, 300 μl of CdSe nanocrystal solution and 125 μl of (P3HT and/or TPD) solution are mixed, such that the resulting ratio of CdSe:(P3HT and/or TPD) is 90:10, the resulting concentration of P3HT and/or TPD is 5.9 mg/ml, and the resulting concentration of CdSe is 52.9 mg/ml. (For example, the resulting concentration of P3HT can be 5.9 mg/ml and TPD 0 mg/ml, the resulting concentration of P3HT can be 0 mg/ml and TPD 5.9 mg/ml, or the resulting concentration of P3HT can be x mg/ml and TPD (5.9-x) mg/ml, where x is >0.) The solution is vortexed for 2 minutes and centrifuged for 2 minutes at 11,000 rpm in a microcentrifuge.
Spincoating of Nanocrystal:(P3HT and/or TPD) Blend Solution
The CdSe nanocrystal:(P3HT and/or TPD) blend is spin coated onto the ITO/PEDOT substrates (in the glove box). Typically, 90 μl of solution is used for each substrate, with a spin speed of 3000 rpm for 40 seconds. Any solution on the back side of the substrates is removed by wiping with chloroform.
Evaporation of Aluminum Cathodes
The nanocomposite-PEDOT-coated substrates are transferred without exposure to oxygen into an evaporator. Aluminum (purity 99.999%) is evaporated onto them at a rate of 5 A/s under a vacuum of less than 1×10−7 torr to a thickness of approximately 100-200 nm.
The resulting devices are then characterized as desired.
It will be understood from the foregoing that variations and uses of the present invention are encompassed. For example, any of the compositions of the invention can be used to form devices of the invention. Systems of the invention can be used to make compositions and/or devices of the invention. Methods of the invention can be used to make the compositions, systems or devices herein. Similar variations will be apparent to one of skill.
Furthermore, while the foregoing invention has been described in some detail for purposes of clarity and understanding, it will be clear to one skilled in the art from a reading of this disclosure that various changes in form and detail can be made without departing from the true scope of the invention. For example, all the techniques and apparatus described above can be used in various combinations. All publications, patents, patent applications, and/or other documents cited in this application are incorporated by reference in their entirety for all purposes to the same extent as if each individual publication, patent, patent application, and/or other document were individually indicated to be incorporated by reference for all purposes.
This application is a continuation-in-part of U.S. patent application Ser. No. 10/656,802, filed Sep. 4, 2003, entitled “NANOSTRUCTURE AND NANOCOMPOSITE BASED COMPOSITIONS AND PHOTOVOLTAIC DEVICES” by Erik Scher et al., which claims priority to and benefit of U.S. Provisional Patent Application No. 60/408,722, filed Sep. 5, 2002, “NANOCOMPOSITES” by Mihai Buretea et al., U.S. Provisional Patent Application No. 60/421,353, filed Oct. 25, 2002, “NANOCOMPOSITE BASED PHOTOVOLTAIC DEVICES” by Erik Scher et al., and U.S. Provisional Patent Application No. 60/452,038, filed Mar. 4, 2003, “NANOCOMPOSITE BASED PHOTOVOLTAIC DEVICES” by Erik Scher et al., each of which is incorporated herein by reference in its entirety for all purposes.
Portions of this invention may have been made with United States Government support under National Reconnaissance Office grant NRO-03-C-0042. As such, the United States Government may have certain rights in the invention.
| Number | Date | Country | |
|---|---|---|---|
| 60452038 | Mar 2003 | US | |
| 60421353 | Oct 2002 | US | |
| 60408722 | Sep 2002 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10656802 | Sep 2003 | US |
| Child | 10778009 | Feb 2004 | US |