Patent Grant
8178261
This application claims priority to non-provisional application Ser. No. 12/550,521 filed on Aug. 31, 2009, the entire contents of which are hereby incorporated by reference.
The present disclosure relates to optical data storage media. More particularly the present disclosure relates to holographic storage media as well as methods of making and using the same.
The rapid growth of information technology industry has led to an increasing demand for data storage systems. Optical data storage, wherein reading or writing of data is accomplished by shining light on, for example a disc, provides advantages over data recorded in media which must be read by other means, for example a magnetically sensitive head for reading magnetic media, or a needle for reading media recorded in vinyl. And, more data can be stored in smaller media optically than can be stored in vinyl media. Further, since contact is not required to read the data, optical media are not as vulnerable to deterioration over periods of repeated use as vinyl media.
Nonetheless, conventional optical data storage media does have limitations as known to one skilled in the art. Alternative data storage methods include holographic storage. This is an optical data storage method in which the data is represented as holograms. Early attempts at holographic storage relied on a page-based approach, i.e., where the bits of digital information are encoded into volume holograms as two-dimensional arrays of logical zeros and ones that traversed a ‘slice’ of the necessarily linear media onto which the holograms were recorded. More recent research into holographic data storage has focused on a bit-wise approach, where each bit (or few bits) of information is represented by a hologram localized to a microscopic volume within a medium to create a region that reflects the readout light. Materials capable of accommodating a bit-wise data storage approach are highly sought after as the equipment utilized to read and write to such material is either currently commercially available, or readily provided with modifications to readily commercially available reading and writing equipment. Further, holographic data storage by the bit-wise approach is more robust to temperature, wavelength, intensity variations, and vibration than holographic data stored using the page-based approach. In order to be optimally useful in the recordation of holograms, and in particular, micro-holograms, bit-wise data storage materials must be non-linear and further exhibit desirable refractive index change in response to recording light. The magnitude of the refractive index modulations produced in the material by the recording light defines the diffraction efficiency for a given system configuration, which translates to the signal to noise ratio, bit error rate, and the achievable data density.
Thus, there remains a need for optical data storage media that can exhibit a nonlinear (or “threshold”) response to the recording light intensity and that is suitable for bit-wise holographic data storage. In particular, it would be advantageous for holograms stored in the media to be limited in depth so that increased capacity could be realized. It would be further desirable for such data storage media to be written in such a way that refractive index of the surrounding media is not significantly altered and that a substantial degradation of hologram efficiency at various depths is not seen. Desirably, any such materials provided would have sufficient refractive index change to support diffraction efficiencies so as to be capable of recording high-density micro-holographic data, thereby further expanding the storage capacity of the material.
In one embodiment an optical data storage medium is provided. The optical data storage medium includes a polymer matrix; a reactant capable of undergoing a change upon triplet excitation, thereby causing a refractive index change; and a non-linear sensitizer capable of absorbing actinic radiation to cause upper triplet energy transfer to said reactant. The refractive index change capacity of the medium is at least about 0.1. The reactant comprises polyvinyl chlorocinnamate (PVClCm), polyvinyl methoxycinnamate (PVMeOCm), or a combination thereof.
In another embodiment, a method for optical data storage is provided. The method comprises providing an optical data storage medium. The optical data storage medium includes a polymer matrix; a reactant capable of undergoing a change upon triplet excitation, thereby causing a refractive index change; and a non-linear sensitizer capable of absorbing actinic radiation to cause upper triplet energy transfer to said reactant. The refractive index change capacity of the medium is at least about 0.1. The reactant comprises polyvinyl chlorocinnamate, polyvinyl methoxycinnamate, or a combination thereof. A microhologram is recorded in said optical data storage medium.
These and other features, aspects, and advantages of the present invention will become better understood when the following detailed description is read with reference to the accompanying drawings in which like characters represent like parts throughout the drawings, wherein:
Approximating language, as used herein throughout the specification and claims, may be applied to modify any quantitative representation that could permissibly vary without resulting in a change in the basic function to which it is related. Accordingly, a value modified by a term such as “about” is not to be limited to the precise value specified. In some instances, the approximating language may correspond to the precision of an instrument for measuring the value. Similarly, “free” may be used in combination with a term, and may include an insubstantial number, or trace amounts, while still being considered free of the modified term.
As used herein, the terms “may” and “may be” indicate a possibility of an occurrence within a set of circumstances; a possession of a specified property, characteristic or function. These terms may also qualify another verb by expressing one or more of an ability, capability, or possibility associated with the qualified verb. Accordingly, usage of “may” and “may be” indicates that a modified term is apparently appropriate, capable, or suitable for an indicated capacity, function, or usage, while taking into account that in some circumstances the modified term may sometimes not be appropriate, capable, or suitable. For example, in some circumstances, an event or capacity can be expected, while in other circumstances the event or capacity cannot occur—this distinction is captured by the terms “may” and “may be”.
One or more specific embodiments of the present invention will be described below. In an effort to provide a concise description of these embodiments, all features of an actual implementation may not be described in the specification. It should be appreciated that in the development of any such actual implementation, as in any engineering or design project, numerous implementation-specific decisions must be made to achieve the developers' specific goals, such as compliance with system-related and business-related constraints, which may vary from one implementation to another. Moreover, it should be appreciated that such a development effort might be complex and time consuming, but would nevertheless be a routine undertaking of design, fabrication, and manufacture for those of ordinary skill having the benefit of this disclosure.
When introducing elements of various embodiments of the present invention, the articles “a,” “an,” and “the,” are intended to mean that there are one or more of the elements. The terms “comprising,” “including,” and “having” are intended to be inclusive, and mean that there may be additional elements other than the listed elements. Furthermore, the terms “first,” “second,” and the like, herein do not denote any order, quantity, or importance, but rather are used to distinguish one element from another.
Embodiments of the invention described herein address the noted shortcomings of the state of the art. These embodiments advantageously provide an improved optical data storage medium. In one embodiment, an optical data storage medium is provided. The optical data storage medium includes a polymer matrix; a reactant capable of undergoing a change upon triplet excitation, thereby causing a refractive index change; and a non-linear sensitizer capable of absorbing actinic radiation to cause upper triplet energy transfer to said reactant. The refractive index change capacity of the medium is at least about 0.1. The reactant comprises polyvinyl chlorocinnamate (PVClCm), polyvinyl methoxycinnamate (PVMeOCm), or a combination thereof. Diffraction efficiency of the order greater that about 1 percent at numerical aperture (NA) of 0.4 is achievable using a relatively lower laser fluence of about 190 Joules per centimeter than what is typically used in the art, such as, a laser fluence of about 300 Joules per centimeter. This may be attributed to two reasons a) increased index change capacity at the wavelength of interest (405 nanometers), for example index change capacity of polyvinyl 4-methoxycinnamate is 0.18 vs. that of polyvinyl cinnamate (PVCm) which is 0.08; and (b) pre-alignment of the cinnamate pairs due to charge transfer donor-acceptor type of complex as described herein can give rise to increased sensitivity of the material to the laser fluence. Moreover the sensitivity of the optical storage medium is of the order of about 10−4 square centimeters per Joule as obtained from quantum efficiency data compared to the PVCm, which is in the order of 10−5.
As used herein, “diffraction efficiency” means a fraction of the beam power reflected by a hologram as measured at the hologram location with respect to the incident probe beam power, while “quantum efficiency” means a probability of an absorbed photon to result in a chemical change that produces a refractive index change. “Fluence” means the amount of optical beam energy that has traversed a unit area of the beam cross-section (measured, for example, in Joule per square centimeter), while “intensity” means optical radiative flux density, for example amount of energy traversing a unit area of beam cross-section in unit time (measured in, for example, Watt per square centimeter).
As used herein, the term “non-linear sensitizer” refers to a material that has a sensitivity having a dependence to the light intensity, i.e., the sensitivity has to be high enough at the high (recording) intensity, and low enough at the lower (readout) intensity. For example, in a situation where the read intensity is about 20 to about 50 times lower than the write intensity, the sensitivity (based on a specific assumptions on the readout life time and/or number of readout cycles the material has to survive) may decrease by an order greater than about 104 times to about 105 times the initial sensitivity. This difference in the intensity and sensitivity constitutes the amount of nonlinearity the material has to exhibit.
There is provided herein optical data storage media suitable for recording microholographic data in a bit-wise approach. The media desirably exhibits a nonlinear response to actinic radiation, i.e., experiences no substantial change in refractive index for incident laser light below a threshold, and significant changes in refractive index above the threshold. Advantageously, recording into such a medium is only possible with the light having a power, or intensity, exceeding a threshold value and the recorded data can be repeatedly and substantially non-destructively read with light having intensity below the threshold. Microholograms recorded in the present optical data storage media are expected to be smaller in size than the beam used to record them.
In one embodiment, the optical data storage medium comprises a non-linear sensitizer and a reactant dispersed within a polymer matrix and can exhibit refractive index change suitable for the recordation of microholograms at high data densities. In one embodiment, the refractive index change capacity of the medium is at least about 0.1. In one embodiment, the refractive index change capacity is in a range of from about 0.1 to about 0.25. In yet another embodiment, the refractive index change capacity is in a range of from about 0.11 to about 0.2. In still yet another embodiment, the refractive index change capacity is in a range of from about 0.12 to about 0.18.
Although other properties can also impact the ability of an optical data storage media to record microholographic data in a bit-wise fashion, such as recording speed, recording intensity, and transparency to name a few, it is believed that the achievable diffraction efficiency and/or refractive index change of a particular media will be controlling the ability of the media to record microholographic data in a bit-wise fashion. Because of the diffraction efficiencies achievable by the present optical data storage media, the media may be capable of storing about 1 terabyte of information on a disk comparable in size to a single CD or single DVD.
In one embodiment, the present media comprises reactants capable of undergoing a change upon triplet excitation (Tn; n>1). As used herein, the term “change” is meant to include any indirect photochemical reaction of the reactant, for example photodimerization or isomerization. Photodimerization is a bimolecular photochemical process involving an electronically excited unsaturated molecule that undergoes addition with an unexcited molecule of a structurally similar and/or identical species (e.g. two olefins combining to form a cyclobutane ring structure). The covalent bonding that occurs in this reaction produces a new moiety which can be generally classified as a photoproduct. When the word “indirect” is used in conjunction with terms such as photodimerization, photochemical reaction or photoreaction, it means that the reactant did not receive the energy directly from absorption of a photon, but rather from another molecule (such as, for example, a sensitizer or mediator) that first absorbed the photon and then transferred a portion of that energy to the reactant that subsequently underwent dimerization.
In certain embodiments, the reactants suitable for use in the optical data storage media described may include the following properties and functionalities. In one embodiment, the reactants may be capable of undergoing dimerization so that less volume change is required to go from reactant to product, for example, reactants that undergo dimerization processes not by direct photoexcitation of the reactant but by indirect “non-radiative energy transfer” (in the present case triplet-to-triplet energy transfer) pathway from the photoexcited sensitizer to the reactant. The reactants wherein a nonlinear sensitizer receives energy from a two-photon process and delivers that energy to one reactant that subsequently condenses with a second reactant to provide a product. The reactants that, when derivatized on a polymer backbone can provide a very large refractive index change, which corresponds to the available capacity of the material, for example, a refractive index change capacity of at least about 0.1 may be achieved if greater that about 85 percent of the reactants are converted to product. Finally, those that, when derivatized on a polymer backbone, are capable of undergoing both inter- and intramolecular condensation reactions, thereby accelerating the consumption thereof. The reactants may be capable of providing desired refractive index changes with incident fluence of less than 10 joules per square centimeter as a result of higher quantum efficiency of the sensitized photo-reaction, which in turn may also provide greater diffraction efficiencies and shorter recording times.
As used herein, the term “sensitivity” is defined as the amount of index change obtained with respect to the amount of fluence used to irradiate a spot of the film with the laser light. If we know the fluence (Fo) value and the amount of index change we can estimate sensitivity of the energy transfer (ET) process using the formula:
ET=dn(maximum)/Fo
wherein dn(maximum) is the maximum capacity index change material.
In one embodiment, the linear sensitizer capable of absorbing actinic radiation may include cinnamate materials. In one embodiment, the cinnamate materials may be capable of undergoing [2+2] indirect photodimerization and indirect photopolymerization may be used. These cinnamate materials, due to their transperancy (negligible ultraviolet absorption) at about 405 nanometers or at about 532 nanometers keep the linear bleaching of the cinnamate to a minimum and facilitate only the triplet-triplet energy transfer from the excited sensitizer. In one embodiment, the cinnamate materials includes polyvinyl chlorocinnamate (PVClCm), polyvinyl methoxycinnamate (PVMeOCm), or a combination thereof. In one embodiment, the cinnamate content of the polyvinyl backbone is in a range of from about 54 weight percent to about 75 weight percent based upon the total weight of the polyvinylcinnamate. Suitable examples of polyvinyl chorocinnamate include polyvinyl 4-chlorocinnamate, polyvinyl 3-chlorocinnamate, and 2-chlorocinnamate. Suitable examples of polyvinyl methoxycinnamate include polyvinyl 4-methoxycinnamate, polyvinyl 3-methoxycinnamate, and polyvinyl 2-methoxycinnamate.
As used herein, the phrase “polyvinyl chlorocinnamate (PVClCm), polyvinyl methoxycinnamate (PVMeOCm), or a combination thereof” includes PVCm derivatives consisting of PVClCm, PVMeOCm, a physical blend of PVClCm and PVMeOCm, and a polyvinyl cinnamate derivative wherein the polyvinyl backbone consists of both chlorocinnamate and methoxycinnamate groups. The PVCm derivatives may be represented by using the formula I:
wherein “R” is H or cinnamate; and “X” is chloro or methoxy. In one embodiment, the value of “p”, “q”, and “r” is such that the polymer has a molecular weight of about 100000. One skilled in the art will appreciate that a polymer having an appropriate molecular weight may be prepared by adjusting the quantities of the various reactants employed.
It is well known in the literature that the quantum efficiency of cinnamate dimerization can be improved by preordering the adjacent cinnamate molecules prior to [2+2] photodimerization with the help of electron donor and electron acceptor groups substitution on the cinnamate molecules [Pure and Appl. Chem., 1992, Vol. 64, 1299-1303 and Macromolecules, 1991, 24 (16), 4600-4604]. The reaction schematic shown below represents the electron donating and elector accepting capacities of the PVCm derivatives disclosed herein.
In one embodiment, the reactant(s) utilized in the present optical data storage media are capable of undergoing a change upon triplet excitation. Referring to
In addition to the aforementioned benefits, the use of such materials as the reactant in the optical data storage media described herein may also provide the possibility of a higher loading when derivatized on a polymer backbone than conventional reactants. For example, loading of conventional reactants when derivatized on a polymer backbone may be limited to about 30 mole percent. In certain embodiments, reactants described herein may be loaded onto polymer backbones at much greater loadings, i.e., up to about 90 mole percent when derivatized onto a polymer backbone.
In certain embodiments, the use of the reactants provided herein provide a significant decrease in birefringence as compared to conventional reactants. In certain other embodiments, the optical recording media described provides the ability to rapidly create high-resolution micro-holograms with minimal heat formation and signal leakage to neighboring locations that can result in smearing of the captured holographic pattern.
The reactant is usually present in relatively high concentrations both to yield large changes in optical properties within the polymer matrix and to promote efficient triplet energy transfer. In one embodiment, the reactant may be present in the optical data storage media in amounts in a range from about 2 mole percent to about 90 mole percent, based upon the total weight of the optical data storage media. In another embodiment, the reactant may be present in the optical data storage media in amounts in a range from about 5 mole percent to about 85 mole percent, based upon the total weight of the optical data storage media. In yet another embodiment, the reactant may be present in the optical data storage media in amounts in a range from about 10 mole percent to about 80 mole percent, based upon the total weight of the optical data storage media.
The reactant may be covalently attached, or otherwise associated with, the polymer matrix. For example, polymers functionalized with chlorocinnamates and methoxycinnamates may be utilized as the polymer matrix. In this case, In one embodiment, the optical data storage media may comprise higher loading amounts of the reactants, for example, up to about 90 weight percent, based upon the total weight of the optical data storage media.
In addition to the reactants described above, the present optical data storage media comprises one or more non-linear sensitizers. The non-linear sensitizers are capable of absorbing incident actinic radiation, for example in the form of one or more photons, and then transferring the energy to the reactant molecule to induce a molecular rearrangement of the reactant into a product that, in turn, gives rise to modulations in the refractive index of the medium. This modulation records both the intensity and phase information from the incident actinic radiation as the hologram. The advantages of the use of nonlinear (or “threshold”) sensitizers as opposed to linear sensitizers can be further understood with references to
Referring to
As a result, and as is shown in
The nonlinear sensitizers used in the present optical data storage media are capable of transferring energy from an upper triplet state (Tn, wherein n>1), which has a very short lifetime (nanoseconds to a few micro seconds), to the reactant. The ability to transfer energy from the Tn state provides the optical storage media provided herein with its nonlinear, threshold properties. That is, Tn excited state absorption is only appreciable when the sensitizer is excited by high-intensity light, for example light having an intensity at least 2 orders of magnitude or more greater than ambient light, and negligibly small when subjected to low-energy radiation. This allows for the present optical data storage media, comprising the nonlinear sensitizers, to remain substantially transparent and inert to low intensity radiation, for example, reading or ambient light, and to only change its properties (absorbance and thus, refractive index) in response to high energy recording light at or near the focal points. As a result, the present optical data storage media exhibits the threshold behavior desired and/or necessary for the bit-wise recordation of microholographic data.
As mentioned above
In some embodiments, the present nonlinear sensitizers may absorb two photons, typically, sequentially. Also, once the sensitizers described herein transfer the absorbed energy to the reactant (as shown at 418,
In one embodiment, the nonlinear sensitizers comprise reverse saturable absorbers (RSAs). For the purposes of this application, a reverse saturable absorber (RSA) is a compound that has extremely low linear absorption at a given wavelength (such as 532 or 405 nanometers) and transmits nearly all of the light. However, when subjected to high intensity laser power at these given wavelengths, low level linear absorption can lead to a state where the molecule has a higher absorption cross section and becomes highly absorbing at that same wavelength; causing it to strongly absorb subsequent photons. This nonlinear absorption is often referred to as sequential two-photon absorption. Examples of RSAs suitable for use in the present optical data storage media are disclosed in Perry et al., “Enhanced reverse saturable absorption and optical limiting in heavy atom-substituted phthalocyanines”, Optics Letters, May 1, 1994, Vol. 19, No. 9, pages 625-627, hereby incorporated by reference herein in its entirety.
Many RSAs experience photoexcitation when impinged upon by incident actinic radiation having a wavelength of 532 nanometers. Because this wavelength is within the green color portion of the visible spectrum, these RSA's may typically be referred to as “green” RSA's. Any of these green RSA's that are capable of entering into the upper triplet (T2) state upon photoexcitation may be utilized in the present optical data storage media. Examples of green RSAs include metal/ligand complexes, such as phthalocyanines, naphthalocyanines or porphyrins; fullerenes; or transition metal cluster compounds, including transition metals, group IIA-VIA metals, and/or rare earth metals. In some embodiments, phthalocyanines and porphyrins, and in particular those comprising indium, lead, copper or zinc, may be used. Suitable examples phthalocyanines that can be employed include, but are not limited to lead(II)tetrakis(4-cumylphenoxy)phthalocyanine, copper(II)tetrakis(4-cumylphenoxy)phthalocyanine, zinc 2,9,16,23-tetra-tert-butyl-29H, 31H-phthalocyanine or indium 2,9,16,23-tetra-tert-butyl-29H-31H-phthalocyanine.
Lesser known are RSA's capable of undergoing photoexcitation upon impingement with incident actinic radiation at a wavelength of 405 nanometers, or “blue” RSA's. Several new RSA's have been recently discovered and are disclosed in U.S. patent application Ser. Nos. 12/551,410, and 12/551,455, respectively, filed concurrently herewith, and incorporated herein by reference in their entirety for any and all purposes, so long as not directly contradictory with the teachings herein. Generally speaking, these new blue RSA's include subphthalocyanines, and platinum ethynyl based dyes, specific examples of which include, but are not limited to, 3,5-dibromophenoxysubphthalocyaninato]-boron(III), 3-iodophenoxysubphthalocyaninato]boron(III), trans-Bis(tributylphosphine)-bis(4-ethynylbiphenyl)platinum (PPE), trans-Bis(tributylphosphine)bis(4-ethynyl-1-(2-phenylethynyl)benzene)platinum (PE2).
The reverse saturable absorbing molecules listed herein are exemplary, and many more varieties of reverse saturable absorbing molecules, or other molecules exhibiting non-linear absorption, may be used in the optical data storage media disclosed herein.
The amount of nonlinear sensitizer used in the optical data storage media may depend on its optical density at the wavelength of light used to record the hologram. Solubility of the sensitizer may also be a factor. In one embodiment, the sensitizer may be used in an amount of from about 0.002 weight percent to about 15 weight percent, based upon the total weight of the data storage media. In another embodiment, the sensitizer may be used in an amount of from about 0.01 weight percent to about 4.5 weight percent. In yet another embodiment, the sensitizer may be used in an amount of from about 1 weight percent to about 5 weight percent.
In certain embodiments, photostabilizers may also be included in the optical data storage media described herein. Typically, the photo stabilizers assist in the photostabilization of the non-linear sensitizer utilized herein. Those of ordinary skill in the art are aware of compounds/materials useful for this purpose, and useful amounts of these, and any of these may be used, in any suitable amount. In one exemplary embodiment, the compound that may assist in the photostabilization of a phthalocyanine dye, for example, includes bisdithiobenzil nickel.
Optionally, the data storage media may further comprise a mediator to assist in upper triplet energy transfer from the sensitizer to the reactant. The triplet state (T1m) of the mediator will desirably be (a) below the triplet state (Tn; n>1) of the sensitizer but above the T1 of the sensitizer and (b) above the triplet state (T1r) of the reactant, or ideally between about 50 kilocalories per mole to about 90 kilocalories per mole.
In certain embodiments, where the mediator is employed, presence of mediator in the samples may help in improving the sensitivitiy at write intensities. One of the factors that may limit the sensitivity in energy-transfer systems is a larger energy difference between the T2 state of the RSA dye (3-Iodophenoxysubphthalocyaninato]boron(III) (3IphOSubPc), about 110) and the T1 state (about 58 kilocalories per mole) of the acceptor (cinnamate) molecule about 58 kilocalories per mole. The triptlet-triplet-energy-transfer (TTET) is typically found to be more efficient only when the Donor-Acceptor energy difference is less than about 20 kilocalories per mole. In order to overcome this limitation, we use a mediator—a molecule that does not absorb light directly, but participate in the energy transfer by receiving the energy from the RSA dye molecules and transferring it further to the index change material molecules with the efficiency that is higher than that of the direct transfer from the sensitizer to the acceptor. The mediator is chosen such that its triplet energy (T1) is below the T2 state of the RSA dye but above the acceptor T1 state. Being a nonlinear function of the donor-acceptor energy difference, the resulting efficiency of two sequential energy transfer processes (donor→mediator→acceptor) may be more efficient than a director donor→acceptor transfer.
Examples of suitable mediators include, but are not limited to, acetophenone (T1≈78 kilocalories per mole), dimethylphthalate (T1≈73 kilocalories per mole), propiophenone (T1≈72.8 kilocalories per mole), isobutyrophenone (T1≈71.9 kilocalories per mole), cyclopropylphenylketone (T1≈71.7 kilocalories per mole), deoxybenzoin (T1≈71.7 kilocalories per mole), carbazole (T1≈69.76 kilocalories per mole), diphenyleneoxide (T1≈69.76 kilocalories per mole), dibenzothiophene (T1≈69.5 kilocalories per mole), 2-dibenzoylbenzene (T1≈68.57 kilocalories per mole), benzophenone (T1≈68 kilocalories per mole), polyvinylbenzophenone (T1≈68 kilocalories per mole), 1,4-diacetylbenzene (T1≈67.38 kilocalories per mole), 9H-fluorene (T1≈67 kilocalories per mole), triacetylbenzene (T1≈65.7 kilocalories per mole), thioxanthone (T1≈65.2 kilocalories per mole), biphenyl (T1≈65 kilocalories per mole), phenanthrene (T1≈62 kilocalories per mole), phenanthrene (T1≈61.9 kilocalories per mole), flavone (T1≈61.9 kilocalories per mole), 1-napthonirile (T1≈57.2 kilocalories per mole), poly (β-naphthoylstyrene) (T1≈55.7 kilocalories per mole), Fluorenone (T1≈55 kilocalories per mole), and combinations thereof.
If utilized, the mediator may, if desired, be covalently attached to, or otherwise associated with, the polymer matrix. Incorporating the mediator into the polymer matrix in this way can allow for higher concentrations of the mediator to be utilized, which, in turn, can increase recording efficiency of the data storage media.
The amount of mediator used, if any, should not be so much as to cause self-quenching, i.e., when two triplets of the mediator meet each other to generate a singlet state and a ground state of the mediator. Optimal amounts of any mediator may also depend on the particular sensitizer. In one embodiment, if the mediator is dispersed within the polymer matrix the mediator may be present in an amount in a range from about 1 weight percent to about 20 weight percent in the polymer matrix. In another embodiment, the mediator may be present in an amount in a range from about 1.5 weight percent to about 10 weight percent in the polymer matrix. In yet another embodiment, the mediator may be present in an amount in a range from about 2 weight percent to about 8 weight percent in the polymer matrix. In one embodiment, if the mediator is covalently attached to the polymer matrix the mediator may be present in an amount in a range from about 2 weight percent to about 50 weight percent in the polymer matrix. within the polymer matrix. In another embodiment, the mediator may be present in an amount in a range from about 5 weight percent to about 40 weight percent in the polymer matrix. In yet another embodiment, the mediator may be present in an amount in a range from about 4 weight percent to about 30 weight percent in the polymer matrix.
The desired sensitizer and reactant may be substantially uniformly dispersed through a polymer matrix, or may be dispersed in any fashion so that bit-wise data recordation is facilitated within the medium. The polymer matrix may comprise a linear, branched or cross-linked polymer or co-polymer. Any polymer may be used so long as the sensitizer and reactant can be substantially uniformly dispersed therein. Further, any polymer utilized will desirably not substantially interfere with the upper triplet energy transfer process. The polymer matrix may desirably comprise a polymer that is optically transparent, or at least has a high transparency at the wavelength contemplated for recording and reading the optical data storage medium.
Particular examples of suitable polymers for use in the polymer matrix include, but are not limited to, poly(alkyl methacrylates), such as poly(methyl methacrylate) (PMMA), polyvinyl alcohols, poly(alkyl acrylates), polystyrenes, polycarbonates, polyacrylates, poly(vinylidene chloride), poly(vinyl acetate), and the like. As mentioned above, the sensitizer may also be covalently attached, or otherwise associated with, the polymer matrix. For example, polymers such as polyesters, polycarbonates and polyacrylates including stilbene are readily available, or, are readily functionalized to include stilbene units.
The polymer matrix may also contain a plasticizer, such as dibutyl phthalate, dibutyl sebacate or di(2-ethylbexy) adipate. Plasticizers can enhance recording efficiencies by facilitating molecular motion. Typical plasticizer levels may be in a range from about 1 weight percent to about 20 weight percent, or from about or from about 2 weight percent to about 10 weight percent, based upon the total weight of the storage media.
The optical data storage media described herein may be in a self-supporting form. Or, the data storage media may be coated onto a support material, such as polymethyl(methacrylate) (PMMA), polycarbonate, poly(ethylene terephthalate), poly(ethylene naphthalate), polystyrene, or cellulose acetate Inorganic support materials such as glass, quartz or silicon may also be used, in those embodiments wherein use of a support material may be desired.
In such embodiments, the surface of the support material may be treated in order to improve the adhesion of the optical data storage media to the support. For example, the surface of the support material may be treated by corona discharge prior to applying the optical data storage media. Alternatively, an undercoating, such as a halogenated phenol or partially hydrolyzed vinyl chloride-vinyl acetate copolymer can be applied to the support material to increase the adhesion of the storage media thereto.
Generally speaking, the optical data storage media described herein can be prepared by blending the desired sensitizer, reactant, mediator (if desired) and polymer matrix. Proportions of these may vary over a wide range, and the optimum proportions and methods of blending may be readily determined by those of ordinary skill in the art. For example, the sensitizer may be present in concentrations of from about 0.01 weight percent to about 90 weight percent, and the reactant may be present in concentrations of from about 2 weight percent to about 80 weight percent, or even up to about 90 weight percent, based upon the total weight of the optical data storage media.
Starting materials were bought commercially or made from known methods. Cinnamoyl chloride, oxalyl chloride, p-methoxy cinnamic acid, p-chloro cinnamic acid, Boron subphthalocyanine chloride, dimethoxy benzene, iodine, 2- and 4-bromoresorcinol, 3,5-dibromorescorcinol, 3-iodophenol, 2-bromophenol, 4-bromophenol, 3,5-dibromophenol, 10 percent Pd/C (all Aldrich) were used as received.
Thin film samples for demonstrating microholograms and recording the reflectivity after writing microholograms were prepared as follows. The sensitivities at Read and Write intensities were determined based on quantum efficiency measurement studies.
To 250 milliliters round bottom flask were added polyvinyl alcohol, 88 percent hydrolysed (1.4 grams, 0.0292 moles repeat unit) and 25 milliliters of N-methyl pyrrolidinone. The resultant mixture was heated to about 80 degrees Celsius under an atmosphere of nitrogen for about 2 hours. The heating resulted in the complete dissolution of polyvinyl alcohol. The resultant mixture was cooled to about 50 degrees Celsius. The cinnamoyl chloride derivatives were added in portions as a solid over a period of about two hours. In Example 3, where a mixture of 4-methoxy and 4-chloro cinnamoyl chloride derivatives were added, the cinnamoyl chloride derivatives were added as a 1:1 mixture of 4-methoxy and 4-chloro cinnamoyl chloride. After the addition of about 40 mole percent of the cinnamoyl chloride derivatives was completed, in each example, 2 milliliters of a corresponding weight percent solution of boron subphthalocyanine 3-iodo-5-glutarylphenoxide in methylene chloride acid chloride was added to the mixture. After the rest of cinnamoyl chloride was added the mixture was stirred for about one more hour at about 50 degrees Celsius. The resultant mixture was precipitated into a blender containing 75 milliliters of methanol. The resulting solid was collected by suction filtration then dissolved in 30 milliliters of methylene chloride and again precipitated into 75 milliliters of methanol. The resulting solid was dried in a vacuum oven at room temperature for 4 hours then overnight at 50 degrees Celsius. The quantities of various reactants added is included below in Table 1.
2.2 weight percent solutions of boron subphthalocyanine 3-iodo-5-glutarylphenoxide polyvinyl cinnamoyl derivative prepared in E-1, E-2, and E-3 and CE-1 and CE-2, in tetrachloroethane were prepared independently. Benzophenone was added to each of these solutions. For each solution: The contents were dissolved by heating the solution on a hot plate at about 70 degrees Celsius. The solution was filtered through a 0.45 micrometer Whatman filter. The filtered solution was poured onto a 50 millimeters×25 millimeters microscopic slide and the solution was spin casted on a spin coater at about 2000 revolutions per minute for 30 seconds. Then the slide was dried for about 20 minutes to about 30 minutes in an oven at a temperature of about 70 degrees Celsius. The thickness of the polymer film formed was approximately about 100 nanometers. The amount of boron subphthalocyanine 3-iodo-5-glutarylphenoxide polyvinyl cinnamoyl derivative and benzophenone mediator added is included in Table 2 below.
Examples 4, 5, 6, and 7, and CE-4 and CE-5 utilize sensitizers functional at approximately 405 nanometers, therefore the performance was evaluated using the 405 nanometers apparatus. It is further expected that optical data storage media according to examples 7, 8, 9, and 10 exhibit refractive index change capacity of at least about 0.1. Additionally, the use of benzophenone as a mediator whose triplet energy (T1) is 74 kcal/mol has been used to improve the sensitivities due to better energy transfer efficiency from the RSAdye-Mediator-PVCm. For example comparison of CE-3 and CE-4 (in the absence and presence of benzophenone respectively) improvement in sensitivites at the write intensities are observed. Since the mediators receive the triplet energy from the RSA dyes, the sensitizers are chosen in such a way that they do not directly absorb 405 nanometers light.
While only certain features of the invention have been illustrated and described herein, many modifications and changes will occur to those skilled in the art. It is, therefore, to be understood that the appended claims are intended to cover all such modifications and changes as fall within the true spirit of the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4877717 | Suzuki et al. | Oct 1989 | A |
| 5223356 | Kumar et al. | Jun 1993 | A |
| 5459174 | Merrill et al. | Oct 1995 | A |
| 7459263 | Farid et al. | Dec 2008 | B2 |
| 20040175656 | Baer et al. | Sep 2004 | A1 |
| 20070147214 | Erben et al. | Jun 2007 | A1 |
| 20080144146 | Boden et al. | Jun 2008 | A1 |
| 20100302927 | Natarajan et al. | Dec 2010 | A1 |
| 20110051586 | Natarajan et al. | Mar 2011 | A1 |
| 20110053054 | Natarajan et al. | Mar 2011 | A1 |
| 20110053055 | Natarajan et al. | Mar 2011 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20110081602 A1 | Apr 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12550521 | Aug 2009 | US |
| Child | 12967409 | US |