1. Field
The invention herein disclosed relates to optical tape and methods and systems of production and use thereof.
2. Description of the Related Art
Vacuum roll coating has long been used to deposit single and multiple layers of metallic and non-metallic materials on flexible substrates. One particular advantage of vacuum roll coating may be in its ability to coat large substrate areas, with the largest vacuum coating machines being capable of handling rolls of substrate exceeding 10 feet in width and coating speeds in excess of several thousand feet per minute (41st Annual Technical Conference Proceedings, Society of Vacuum Coaters, Boston Mass. 18 Apr. 1998, pg. 26).
Vacuum roll coaters utilize one or more techniques to deposit the desired film layers, the most common techniques being thermal evaporation, electron beam (e-beam) evaporation, and sputtering. The first two are characterized by relatively high material deposition rates but generally do not produce as high a degree of deposition uniformity as the sputtering process.
Deposition quality in roll coating may be often stated in terms of transverse (cross-web) and longitudinal (machine direction) uniformity, corresponding to thickness or compositional variations across the width and along the length of the roll, respectively. Cross-web and machine direction variations can arise from several sources, including non-uniform spatial and temporal distributions of the flux from the material source.
There are a number of techniques known to the art to control and minimize such fluctuations, including use of sensors to control the rate of material deposition through a feedback means (crystal monitors, reflectometers, etc.), which typically affect temporal variations from the source, and shutters or e-beam scanning, which typically affects the spatial material distribution.
It may be typically more difficult to maintain an extremely high degree of uniformity in the cross-web direction than the machine direction, particularly with high deposition rate e-beam and thermal evaporation processes. Contributing factors include non-uniform heating, depletion of the source material during the deposition process, material buildup at the source, etc. Uniformity can decrease as the material may be depleted until the coating process must stop to refill the material reservoirs, although in larger systems the material may be replenished continuously, for example by means of wire or screw fed devices. For precision coatings requiring very high thickness tolerances, the cross-web uniformity achievable by high deposition rate thermal and e-beam processes may be often unacceptable.
Following the vacuum coating process, it may be common to slit the coated material into narrower widths, such as in the case of tape-like materials. The slitting process typically uses a mechanical means to effect the slitting, such as a knife box or other shearing device, and this operation can be a source of problems for the coated substrate. Slitting can result in disruption or delamination of the coating at the slit edges, with the concomitant generation of coating and substrate particles. The particulates thus generated not only contaminate the slit rolls, but they also can be incorporated into the spools under tension during rewind, which can irreversibly damage the rolls, a particular problem in the case of sensitive coatings or substrates.
It may also be common in tape-like substrates to coat both the front and back surfaces. This requires either a second pass through the coating machine or incorporation of a tandem coating station and related web-handling equipment, both of which can add to the cost of process and/or equipment.
The vacuum coating method described herein has been developed to substantially eliminate the shortcomings and disadvantages of the prior art as noted above, and thereby provide a means for coating tape-like substrates with improved uniformity, edge quality, cleanliness, and at higher throughput.
Disclosed herein are aspects of optical tape technology, tape manufacturing, and tape usage. Methods and systems of tape technology disclose optical tape media including: configurations, formulations, markings, and structure; optical tape manufacturing methods, systems, and apparatus methods and systems including: curing processes, coating methods, embossing, drums, testing, tracking alignment stamper strip; optical tape methods and systems including: pick up head adapted for the disclosed optical tape; and optical tape uses including optical storage media devices for multimedia applications.
A method of producing optical tape, comprising: providing an embossing drum constructed using two or more discrete electroforms for writing wobble cycles including an adjustment zone on an optical tape; providing adjustable shims for embossing a tape, wherein the shims are adjustably assembled around the drum and aligned; providing an initializer for initializing a state of the tape; providing an optical shredder for normalizing the state of the tape; providing a continuous sputter coating facility for depositing tape layers; providing an adjustable height tape guide roller for optical tape guidance; providing a helical transport assembly for optical tape transport; providing a tape support apparatus for positioning and planarizing the optical tape under an optical pickup head; providing a tape reel assembly for facilitating spooling an optical tape; providing a variable speed rotating testing facility for testing aspects of the optical tape; providing an optical tape drive system adapted for testing the optical tape in a configuration substantially similar to that found in a typical use environment; providing an ultraviolet light curing apparatus for post-curing the optical tape; providing a uniform vacuum coating facility for coating one or more layers on the optical tape; providing a base film oven-extruder and stretcher; combining the oven-extruder and stretcher, drum, shims, continuous sputter coating facility, adjustable tape roller guide, helical tape transport assembly; tape support apparatus; tape reel assembly; ultraviolet curing apparatus, and uniform vacuum coating facility into a facility for the producing the optical tape; producing the optical tape with the optical tape producing facility; combining the initializer, shredder, variable speed rotating testing facility, and adapted optical tape drive into a facility for testing the optical tape; and testing the produced optical tape with the optical tape testing facility.
A phase change optical tape, comprising: a plurality of layers assembled into a substantially flat narrow tape; the plurality of layers comprising one or more of: a top coat, an overcoat, a phase change layer, a reflective layer, a dielectric, an embossed layer, a substrate layer, a backcoat; wherein a pulsed laser beam projected from an optical head assembly onto the optical tape results in a phase change one or more layers of the tape; the tape further including a substantially sinusoidal optical servo mark along the length of the tape for operating with a servo control system for controlling the optical head, wherein the servo mark is produced using one or more of phase changing, burning, or grooving; wherein the tape further includes coding patterns; and wherein the tape is one of WORM, rewritable, and REWORM based on the number and order of layers used to assemble the tape.
An optical media storage and retrieval system, comprising: an optical media formed in one of a drum shape, a flexible disk, a compact reel-to-reel, and a storage card; an optical media drive adapted to interface to the optical media; a processor for controlling the optical media drive to read information from and/or write information to the optical media; and wherein the optical media is used in one or more applications including data, video, and audio storage and retrieval.
These and other systems, methods, objects, features, and advantages of the present invention will be apparent to those skilled in the art from the following detailed description of the possible embodiment and the drawings. All documents mentioned herein are hereby incorporated in their entirety by reference.
The invention and the following detailed description of certain embodiments thereof is understood by reference to the following figures:
Optical tape technology, manufacturing, and application may be highly interconnected to achieve cost, performance, density, and other goals required to deliver a commercially viable solution. A goal such as low manufacturing cost while also manufacturing reliable, high quality optical tape may require substantial innovation in manufacturing technology methods and systems. To produce optical tape that supports high density storage and high performance may require substantial innovation in tape technology as well as manufacturing methods and systems. Therefore, the methods and systems of manufacturing the optical tape herein disclosed may be used to make the optical tape herein disclosed, and the methods and systems of optical tape usage herein disclosed may be used to utilize the optical tape herein disclosed.
Disclosed herein are aspects of optical tape technology, tape manufacturing, and tape usage. Methods and systems of tape technology disclose optical tape media including: configurations, formulations, markings, and structure; optical tape manufacturing methods, systems, and apparatus methods and systems including: curing processes, coating methods, embossing, drums, testing, tracking alignment stamper strip; optical tape methods and systems including: pick up head adapted for the disclosed optical tape; and optical tape uses including optical storage media devices for multimedia applications.
An optical servo mark on an optical tape media, generated using a method that results in the optical servo mark being distinguishable from data marks on the optical tape media, as described herein may be used in an optical data storage tape drive.
Referring to
Optical servo mark 110 can be included on optical media by using one or more optical heads (not shown) to mark the optical media. The process for marking the optical media may include one or more of Phase Changing, Burning, or Grooving. The process may include using either an optical servo track writing device, or an optical storage media drive. Methods of generating optical servo mark 110 includes controlling the one or more optical heads with a signal generator set to a frequency that generates optical servo mark 110 in sinusoidal pattern as the optical media moves under the one or more optical heads with a constant linear speed. The frequency of the signal generator may be chosen such that it would meet the sampling requirement of a servo tracking system of a tape drive system on which the optical media would be used.
The one or more optical heads may each be dedicated to the band of tracks 130 on the optical media, each optical head having its own actuator for the purpose of tracking and focusing within band 130. The range of motion of each head may overlap bands of adjacent optical heads.
Once the optical media may be completely marked, an optical head reading along data track 140 will detect servo mark 110 as a pattern of read pulses 150 as the marked media passes by the optical head. Pulse read pattern 150 has a frequency 160 defined by the servo mark 110 pattern and the speed of the tape as it moves by the optical head.
Pulse read pattern 150 also has a duty cycle 170 which may be proportional to the position of the head relative to the edge of the band dedicated to that head. Frequency 160 of the pulse read pattern 150 may be substantially the same for all head positions across the band of tracks. Duty cycle 170, calculated by the equation (Td1/Tf) % may be different for each track as shown by read pulse patterns 111 and 113.
Pulse read pattern 150 may be used to position the optical head in a substantially stationary manner over any desired track. A phase lock loop of a predetermined frequency may be used to qualify pulse read pattern 150 in positioning the optical head.
A method for generating a tracking servo pattern on optical tape media, as described herein may be performed using an adapted optical tape processing apparatus herein described.
Referring to
Additionally die 230 can move from side to side, substantially perpendicular to the axis of motion of base film 210, as well as up and down, substantially perpendicular to the plane of base film 210. The motion of base film 210 through die 230 results in a pattern of fine grooves 240 in base film 210. One possible use of grooves 240 may be for servo tracking.
The up and down motion of die 230 allows precise groove depth control. Carefully controlling the side to side motion of die 230 will generate groves of a predetermined pattern. One such possible pattern may be a sinusoidal pattern which may be known to be beneficial for proper servo tracking Die 230 can generate a predetermined groove pitch 260 and a predetermined groove depth 270. While die 230 can be constructed for generating a plurality of groove to groove spacing and groove widths, one possible groove to groove spacing may be approximately 0.74 um.
Optical tape media, as herein described may be constructed to support write-once read many operation, or re-writable operation. The operation supported may be partially determined by the type of layer material and the order of layers in the optical tape media.
Referring to
Topcoat 302, an organic, scratch-resistant film applied by a sputter process, provides a protective layer for the other layers of the media. Topcoat 302 may include anti-reflective properties (e.g. low index of refraction) to prevent unwanted reflections of laser light 320 from layers within the media.
In the possible embodiment of
In this possible embodiment, the phase change coating 308 may be a phase-change alloy such as Ge—Sb—Te, (germanium-antimony-tellurium), however other phase change materials known as a write-bright phase change material may be included. Write-bright material changes from an amorphous to a crystalline phase when subjected to sufficient heat from laser 320. Once changed, the composition of the material prevents it from changing back to the amorphous phase. The resulting crystalline spots, being more reflective than the surrounding amorphous material, creating a high contrast against the surrounding area, may be means for storing data in the WORM optical tape media. Phase change film 308, in this possible embodiment, may be created using a sputter process.
Reflective layer 310, made of a metal material such as aluminum, or antimony, reflects light from laser 320 that passes through phase change layer 308. Reflective layer 310 may be created using an electron-beam, may be thermally evaporated, may be sputtered, may be ion beam deposited, or a like process. Reflective layer 310 further attenuates light from above, and it also reflects light from below, thus attenuating and blocking any light from above and below from passing through and mixing with laser light 320, which may introduce noise in the nominal reflected laser light 320. Reflective layer 310 may also aid in the crystallization of phase change 308, creating a suitable thermal profile by facilitating nucleation.
Embossed layer 312, contains the physical land and groove structures used for servo tracking Embossed layer 312 may be formed from a monomer fluid by a drum embossing and UV curing apparatus where it may be embossed with the land and groove structures and cured at the same time. While curing, it coverts from a liquid monomer to a solid polymer and may be permanently attached to substrate 314.
Below embossed layer 312 may be substrate or basefilm 314 which provides mechanical support. Basefilm 314 may be created from a high-performance thermoplastic polyester film such as polyethylene naphthalate (PEN), polyethylene terephthalate (PET), or similar material having appropriate mechanical, thermal, and hydroscopic properties for a data storage product.
A backcoat 318 may be deposited on a back side of basefilm 314. Backcoat 318 may be a partially conductive layer to minimize the buildup of static charge, and has a textured surface acting as a conduit to release entrapped air generated during tape subsystem operation. In addition, backcoat 318 optical properties absorb and scatter incident laser light 320 that penetrates reflective layer 310. Backcoat 318 may be one of a material selected from a set including carbon black film created by slurry-coating, aluminum sputtered layer, and nickel chromium sputtered layer.
In an embodiment, the possible embodiment of
Referring to
In the media of possible embodiment of
Referring to
The embodiment of
Referring to
Optical tape media may be adapted as herein described to allow high optical contrast as a result of the media transitioning between non-crystalline and crystalline phases.
Referring to
In the possible embodiment of
Referring to
Referring to
Referring to
Referring to
An optical tape system may include a servo tracking system as herein described for use with optical tape media employing a preformatted track layout.
Referring to
In Initialization mode, servo system 1150 performs initialization steps. In Calibration mode, servo system 1150 may determine optimum settings for Jump-gap, Jump-track, and Tracking mode. Initialization and Calibration modes may take place during servo system 1150 power-up.
Referring to
Referring to
Since tracks 1220 may not line up across gap 1310, while in Tracking mode, demodulator/decoder within servo system 1150 processes synchronization 1250 and address 1260 information to synchronize and decode the address of the track over which sensing element 1120 may be positioned. Based on the decoded address, servo system 1150 determines a number of tracks to Jump in order to move to a desired track, and may initiate a Jump-track operation.
Using the settings determined in Calibration mode, sensing element 1120 moves to the desired track location and initiates Tracking mode. Tracking mode once again decodes the track address and, based on this information, either initiates another Jump-track, or continues in Tracking mode. Once the desired track may be verified, Tracking mode may simply utilize a feedback system to follow a tracking signal (not shown) embedded in the media.
An optical tape media, coded with predetermined patterns, as herein described may be useful to an optical tape system adapted to interpret the coded patterns.
Referring to
Discriminator filter output signal 1404 may be a representation of index bit 1410 of sinusoidal servo signal 1402. In an embodiment, index bit 1410 signal amplitude may be greater than a predetermined index threshold to indicate index bit 1410; index bit 1410 may signal the beginning of address field 1412.
Address field 1412 of a track may be repeated many times in the to provide data signal robustness and improved signal to noise; address field 1412 may have M cells for the 2̂m tracks of an optical tape. The address field 1412 may be interleaved by PLL field 1414 of the same length and may insure the proper operation of PLL field 1414 and a sequencer.
Referring to
Discriminator filter 1504 may detect an index pulse from a pattern signal detected from the media. Index pulse (IdxPls) signal 1604 may be used for Phase Lock Loop (PLL) 1510. A VCO signal from PLL 1510 may be synchronized by synchronizer 1512 and used for synchronized rectification 1514 and resettable integration 1518 of SigIn 1522. Threshold detector 1520, receiving out of synchronized resettable integrator 1518 may enable the detection address 1412.
Referring to
Writing permanent and distinguishable servo marks on optical tape phase change media, as herein described, may be useful to an optical tape system adapted to interpret the coded patterns.
Methods and systems disclosed herein may include a unique method of writing servo marks on optical media that may be permanent in nature and easily distinguishable from the data.
Referring to
Referring to
Referring to
Referring to
Topcoat 2002 may be an organic, scratch-resistant film applied by a sputter process, provides a protective layer for the other layers of the media. Topcoat 2002 may include anti-reflective properties (e.g. low index of refraction) to prevent unwanted reflections of laser light 2020 from layers within the media.
In the possible embodiment of
In this possible embodiment, the phase change coating 2008 may be a phase-change alloy such as Te—Ge—Sb, (tellurium-germanium-antimony), however other phase change materials known as a write-bright phase change material may be included. When composed of Te—Ge—Sb, phase change coating 2008 may be approximately nineteen nano-meters thick. Write-bright material changes from an amorphous to a crystalline phase when subjected to sufficient heat from laser 2020. Once changed, the composition of the material prevents it from changing back to the amorphous phase. The resulting crystalline spots, being more reflective than the surrounding amorphous material, creating a high contrast against the surrounding area, may be means for storing data in the WORM optical tape media. Phase change film 2008, in this possible embodiment, may be created using a sputter process.
Metal layer 2030 may be a very thin aluminum layer. In this embodiment, metal layer 2030 may be approximately composed of aluminum approximately one to two nano-meters thick.
The energy of a laser impacting a phase change material transfers its energy to the material with a three dimensional Gaussian profile. The center of the laser impact area will quickly rise in temperature to the phase change material melting point while the wing area will rise only to the crystallization temperature, which may be lower than the melting temperature. This energy transfer process produces a “donut” like mark with a hole in the middle surrounded by a bright ring. Such marks produce the advantages of high contrast and high signal to noise ratio. In addition, the process may be very fast, rendering it possible to use such media for recording at very fast data rates. However, without metal layer 2030 a laser with read power greater than approximately 0.3 mW may cause read etching, which may be unintended bright tracks in the phase change layer of the media.
Metal layer 2030 enhances the media such that it not only provides all the desirable characteristics of a high contrast and fast WORM media, but also may be very resistant to read etching. A laser with read power as high as at least 0.8 up to as much as 1 mW will not cause a read etching problem with this embodiment. In this embodiment, not only may be the sensitivity to read etching reduced, but also the carrier to noise ratio of write marks may be improved by about 5 to 10 dB over optical media without metal layer 2030.
Metal layer 2030 may contribute these advantages by acting as a barrier to prevent migration of metal in reflective layer 2010 into phase change layer 2008 during laser writing. Alternatively it may be possible that some atomic aluminum in metal layer 2030 may migrate into phase change layer 2008 during deposition. Such migration may retard the phase change layer 2008 crystallization process while not materially altering the melting temperature.
Reflective layer 2010, made of a metal material such as aluminum, or antimony, reflects light from laser 2020 that passes through phase change layer 2008 and thin metal layer 2030. When composed of antimony, reflective layer 2010 may be approximately twenty to thirty nano-meters thick. Reflective layer 2010 may be created using an electron-beam, may be thermally evaporated, may be sputtered, may be ion beam deposited, or a like process. Reflective layer 2010 further reflects light from below, attenuating and blocking any light from below from passing through and mixing with laser light 2020, which may introduce noise in reflect laser light 2020. Reflective layer 2010 may also aid in the crystallization of phase change 2008, creating a suitable thermal profile by facilitating nucleation.
Embossed layer 2012, contains the physical land and groove structures used for servo tracking Embossed layer 2012 may be formed from a monomer fluid by a drum embossing and UV curing apparatus where it may be embossed with the land and groove structures and cured at the same time. While curing, it coverts from a liquid monomer to a solid polymer and may be permanently attached to substrate 2014.
Below embossed layer 2012 may be substrate or basefilm 2014 which provides mechanical support. Basefilm 2014 may be created from a high-performance thermoplastic polyester film such as polyethylene naphthalate (PEN), polyethylene terephthalate (PET), or similar material having appropriate mechanical, thermal, and hydroscopic properties for a data storage product.
A backcoat 2018 may be deposited on a back side of basefilm 2014. Backcoat 2018 may be a partially conductive layer to minimize the buildup of static charge, and has a textured surface acting as a conduit to release entrapped air generated during tape subsystem operation. In addition, backcoat 2018 optical properties absorb and scatter incident laser light 2020 that penetrates reflective layer 2010. Backcoat 2018 may be one of a material selected from a set including carbon black film created by slurry-coating, aluminum sputtered layer, and nickel chromium sputtered layer. Backcoat 2018, when made of aluminum, nickel chromium, or other metallic material may also be applied to magnetic tape media to achieve similar static discharge and release of entrapped air.
Signal 2110 depicts a time domain voltage measurement of a read signal representing the results of reading laser marks on the media. Signal 2120 depicts a control signal used to determine when the read signal has relevant data. As can be seen in
Sensitivity plots may be a derivative tool showing the effect of “micro” changes on a “macro” property.
In both designs shown in
For example, a conventional DVD disk would not work properly in a WORM disk player because the WORM disk player would be looking for an increase in reflectivity when the disk may be exposed the WORM laser beam while the DVD disk would decrease in reflectivity when exposed to the laser beam.
However a LOTS drive may be a WORM drive and the only way erasable tape could be used in a LOTS drive may be if erasable tape could be made such that its reflectivity increases when exposed to a laser beam. The design depicted in
In embodiments, a four layer optical tape, composed of phase change layers, amorphous to crystalline reflectivity change may change from positive to negative as the thickness of the layers changes.
A media (e.g. optical tape media) with amorphous and crystalline reflectivity curves which cross can be either high reflectivity in the amorphous state and low reflectivity in the crystalline state, or high reflectivity in the crystalline state and low reflectivity in the amorphous state. This may be either a write bright or a write dark system.
In embodiments, a four layer optical tape, composed of phase change layers, amorphous to crystalline reflectivity change may change from positive to negative as the thickness of the layers changes.
An initializer for optical media may comprise a high power laser delivering energy to an optical media sufficient to initialize a phase change media to a crystalline state. The high power laser may be automatically focused onto the phase change layer of the media by a lower power laser. However a lower power laser may be saturated when a media with parallel reflectivity curves (e.g. as shown in
In embodiments a four layer optical tape, whose phase change reflectivity curves may be not parallel, may be initialized with a high power laser automatically focused by a lower power laser wherein the lasers' wavelength may be approximately at that which the reflectivity curves intersect (e.g. as shown in
A novel formulation (REWORM) would include depositing in a high reflectivity amorphous state, initialization to a low reflectivity crystalline state, and writing to a high reflectivity amorphous state.
An advantage of this formulation may include faster erase times because writing to the amorphous state from the crystalline state does not depend on the phase change media's intrinsic crystal growth mechanism which includes a constraint of minimum time to change from amorphous to crystalline states.
An apparatus may be disclosed herein which can erase a tape by returning the phase change media to a low reflectivity state. Such an apparatus would erase any information written on a tape in a high reflectivity state by changing the high reflectivity information to a low reflectivity state.
Such an apparatus may be useful as a stand alone device, separate from another device used to write and read information on the tape.
In particular, such an apparatus may be useful in applications using write bright tape.
An apparatus may be herein disclosed which, when used with optical tape media, writes information to the tape, masking any previously written information on the tape, rendering the previously written information unreadable by an optical tape reading apparatus.
This invention may have the advantage of preventing sensitive information on a tape to be masked such that the sensitive information previously written to the tape would not be readable. This advantage would benefit a first user with sensitive information on optical tapes that must be erased by an optical tape system because it prevents a second user of the optical tape system from reading the sensitive information before performing the erasing.
Erasable phase change tape media may be manufactured on a continuous sputter coating machine in which all the layers may be simultaneously deposited to the media. This may be accomplished by depositing a second layer on top of a first deposited layer shortly after the first layer may be deposited, and simultaneously depositing the first layer on further portions of the media. In an embodiment, this may achieved by positioning sputter (layer depositing) sources around a rotating heat extracting drum (chill drum) and moving the media past each sputter source sequentially. Thin films may be deposited as described above with the first layer being deposited on a web of polymer type material which may be in contact with the chill drum as the media moves past each sputter source.
Applying this technique to Tellurium-based erasable phase change formulations of one or more of the deposited layers, may enable producing graded material interfaces between layers.
Advantages of this media with graded material interfaces between layers may include strain relief or thermal conductivity transition, which may result in improved performance to the resultant phase change structure. Such improved performance may be exhibited as reduced signal jitter or increased erase cycleability.
In embodiments, different gradations for each interface throughout the multilayer media may be desirable.
Aspects of this invention relate to improved optical pick up head systems adapted for reading and/or writing data from/to optical tape. The optical head may be capable of reading and/or writing data on an optical tape. The optical tape may include formatted digital data in a phase change layer and it may be adapted to be written upon, re-written upon, erased and/or read from. The optical head may include a transport facility for the optical head, a read head, a write head, a read/write head, a direct read after write head, an articulation unit for optical head positioning, demodulation facility for decoding the data on the optical tape, and the like. The optical head may include a light source, a lens, an actuator, a beam splitter, a beam polarizer, an electro-optic integrated circuit, and/or other systems.
It should be understood that the optical head may be capable of reading, writing, reading and writing, directly reading after writing, or it may be otherwise configured to meet the needs of the particular application. Several different aspects of the optical head and related facilities are described herein; the different aspects may be combined into an optical head or may be used individually.
In an embodiment, an optical pickup head (OPH) as described herein may be used in a direct read after write (DRAW) mode with optical tape media.
In an embodiment, a low power direct read after write (DRAW) laser diode may be used in conjunction with a higher power laser diode in a pick up head (PUH). The two laser diodes may have essentially the same wavelength. In an embodiment, a Holographic Optical Element (HOE) may be inserted in the DRAW laser beam path, and the +1 (first order) and −1 beams may be used for the DRAW function. The +1 first order beam may be used in a first of media motion while the −1 first order beam may be used in a second direction.
There may be two methods of realizing the DRAW function in the PUH in this invention. An embodiment of the first method may be having a higher power laser diode LD12902 for writing only and a lower power second laser LD22914 that may have essentially the same wavelength for read, servo read, and DRAW. The beams from the two lasers may be combined to produce all the required functions in the PUH in addition to DRAW. An embodiment of the second method may be having LD12902 be used for the write, read, and servo functions, while the lower power LD22914 may be for the DRAW.
Referring to
The path associated with LD22914 may be more complex to provide the read, servo loop, and DRAW functions. The holographic optical element (HOE2) 2920 associated with this path may contain a grating and a hologram as shown in
The two collimated beams from LD12902 and LD22914 may be combined at the objective lens to maintain the focus of LD12902 and LD22914.
The distance between the focus point of the 0th order beam and the +,−1st order beams may be controlled by the focal length of the objective lens, fobj, and the grating 202 pitch, A, of HOE22920 through the formula:
λ
d=f
obj·α±1=——fobj
Λ
where λ may be the LD wavelength.
For example, if a Λ of 0.1 mm, LD wavelength of 650 nm, and fobj, of 2.5 mm may be used, then α+1, equals 37 degrees and d equals 13 microns.
Referring to
The light source LD12902 may be collimated by lens COL12904 and then through holographic optical element (HOE1) 3008. The HOE1 structure may be the same as described in
The laser source LD22914 may be collimated by lens COL22918 and then by HOE22920. Since the purpose of the second beam may be direct read after write, HOE22920 may be for this purpose. The grating in HOE22920 may be a 0th (zeroeth) order suppression grating with most of the energy diffracted in the +/−1 orders as shown in
It may be important to have the right groove depth in holographic element HOE13008 in order to control the 0th order suppression. For example, if the holographic element HOE13008 may be a glass plate with a refractive index of 1.55, the groove depth may need to be 550 nm when using a light source with a wavelength of 655 nm to completely suppress the 0th order beam. Complete suppression of the 0th order beam may be desirable but may not be necessary. That is, one may use smaller groove depths. For example, at a depth of 380 nm, the energy may be evenly distributed in the three order beams—0, +1, and −1. This may work adequately in the present invention. More 0th order energy may be undesirable since it could cause more Relative Intensity Noise (RIN) noise.
As shown in
Referring to both
Referring to
Many other versions of optical path arrangements for the two beams may be possible if the laser diodes are not integrated into the electro-optic integrated circuit detector array. However, such configurations may be less compact than the integrated LD-EOIC array. Another version of the DRAW pickup head may be shown in
Since mounting two laser diodes on one silicon chip at an angle of 90° to each other, as shown in
Since, in embodiments, light source LD12902 may be used for writing while light source LD22914 may be used for DRAW read, the light source LD22914 power requirements may be much less demanding, and less costly, lower power lasers may be used for light source LD22914.
In an embodiment, an optical pickup head (OPH) may be adapted to permit a large tracking range of optical media (e.g. optical tape) as described herein.
Referring to
Referring to
When the track under consideration moves downward from a first position 3804 to a second position 3808 due to media runout, the servo loop may cause the lens to also move downward. The focal point will thus try to follow the track center; however, this may cause the Gaussian beam profile impinging on the objective lens to be no longer centered on the aperture. This slight imbalance may cause the push-pull pattern at the detector 3802 to also be imbalanced, resulting in a small error signal. A finite conjugate objective lens 3810 may be used where the beam impinging on the objective lens has a divergent wave front. When the lens moves to follow the track runout, the return beam may suffer from a beam walking problem on the detector 3812.
In the conventional PUH embodiment, the imbalanced push-pull pattern and beam walking at the detector may create less desirable beam position at the electro-optic integrated circuit EOIC. The less than desirable beam position may limit the number of tracks that the PUH may be able to cover to tens of tracks.
Referring to
In the integrated design, the laser diode LD 3904 may be mounted directly on the electro-optic integrated circuit EOIC 3902. The electro-optic integrated circuit EOIC 3902 may include a silicon chip with a segmented detector, a current amplifier, and a voltage amplifier. A simple grating may be used for the holographic element HOE 3910; the holographic element HOE 3910 may divide the beam into 0th and 1 orders. The 0th order may have 50% efficiency while the 1 orders may have approximately 25% efficiency each. The 0th order beam may be used for read/write, as well as the focus/track functions. When the 0th order beam may be returned to the holographic element HOE 3910, the two first order beams may be diffracted to the left and right six-segment detectors of the electro-optic integrated circuit EOIC 3902. Each one of the diffracted beams may be used for focus/track and read/write functions. The signals in the two segments may be equivalent and may be summed to improve the SNR (signal-to-noise ratio) by 3 dB.
In another embodiment, the simple grating may be replaced by an on-axis hologram. It may provide both positive and negative lensing effects such that, for example, one six-element segment may receive light from before the best focus, while the other six-element segment may receive light from after the best focus on the media. This may allow for a differential spot focusing method to be used. Another significant advantage of the hologram may be that the two first order beams in the outgoing beam may be out of focus; this may produce a low amount of return light into the detector. The two first order spots may be unwanted and therefore the low return light may be ignored.
In an embodiment, by moving the entire assembly when tracking the optical tape media, the optical-electric assembly may maintain a balanced push-pull pattern without beam walking at the detector on the electro-optic integrated circuit EOIC 3902. The improved focus with a consistent balanced push-pull pattern of the optical-electric assembly may provide for a greater number of covered tracks on the optical tape; the integrated optical-electric assembly may be able to cover thousands of tracks.
Referring to
In an embodiment, a transport as described herein may be adapted for transporting multiple optical heads used to interface with optical tape in an optical tape facility.
The tape drive in this invention may have a tape guiding system without any discrete guiding mechanism between a removable cartridge reel and a take-up reel. When the removable cartridge may be inserted into the tape drive the media may be pulled onto the take up reel using a take up leader that may attach to the leader material in the media cartridge.
Referring to
Multiple heads may be used in a single head transport facility to increase the data transfer rate of an optical drive. Each individual head may use it's own servo control positioning system for the accurate positioning of the head, then the head transport facility 4102 may be used to approximately position the array of heads close to the tape. This may greatly minimize the complexity of using many optical heads.
Referring to
Referring again to the tape drive of
Systems and methods according to aspects of the present invention may also allow for a head transport facility 4102 on both sides 4110 of the media, at least two head transport facilities 41024110 may be connected to the same head transport system.
In an embodiment, an optical tape drive may be adapted as described herein for high density storage using optical tape media.
In a typical tape drive there may be rotating rollers that guide the media from the cartridge reel, past the head transport facility to the take up reel. One of the purposes of these machined rollers may be to reduce the lateral tape motion created by the cartridge and take up reels; however the rollers themselves may create lateral tape motion at higher frequencies than the reels. In embodiments, servo controlled positioning systems for the head assemblies may create the ability for such a system to compensate for low frequency motion from the reels may be improved and may be superior to that for the roller higher frequencies.
Referring to
The head transport facility 4102 may be positioned between the cartridge reel 4104 and the take up reel 4108. The head transport facility 4102 may be located on a mechanism that allows for lateral positioning such that the distance from the head assembly to the media may be accurately controlled. In the case of a no contact recording, the head may be required to be a certain distance from the media. As the media may be moved from the cartridge reel 4104 to the take up reel 4108 the angle of the tape may be constantly changing as the amount of tape on each reel changes. As the media may be moved from the cartridge reel 4104 to the take up reel 4108 the head transport facility 4102 may adjust for the changing distance to the media. The head transport facility 4102 may adjust for the changing angle of the media to the head transport assembly 4102. The exact position of the head transport facility 4102 may be determined by an algorithm in the compensation system of the servo controlled mechanism.
The lateral tape motion (LTM) in this tape path may originate from the supply reel 4104 and the take up reel 4108 only. In an embodiment, the manufacturing tolerances for these two components may be controlled to several thousandths of an inch larger than the tape width; therefore, the tape may be provided with adequate guidance without the use of guide rollers. The frequency of the LTM may be substantially at the rotation frequency of the reels; the frequency may be 10 to 400 Hz. This frequency may be significantly less than the frequency the guide rollers may introduce; guide roller 4112 LTM frequencies may be many hundreds of hertz. At the lower frequencies, the servo controlled head transport facility 4102 positioning system may be very efficient using a bandwidth of about 1 kHz. The head transport facility 4102 servo controls may be able to better adjust for the lower frequency LTM created by the reel-to-reel tape motion. The efficient positioning head transport facility 4102 may have improved tape tracking and therefore may be able to read and write higher density tape tracks.
While this invention relies on the absence of rotating guiding 4112 members, in an embodiment, it may be possible to have one or more fixed non-rotating guides 4112 for maintaining positional consistency of the media at the head transport facility 4102.
In an embodiment, this invention may also allow for using head transport facilities 41024110 on both sides of the media since there may not be extra wear on one side due to guiding rollers 4112. The use of a second head transport facility 4110 and recording data on the other side of the media may also increase the high density recording.
A laser head tracking system may track the position of data on a moving optical tape media for the purpose of writing data in the correct position on the media in relation to previously written data on the media.
Referring to
The position of information on the media may be determined by using the transducer 4402 that may measure the position of information that may have been previously written to the media. In an embodiment, there may be a processor that may calculate the next correct position for information to be written by a writer 4414. The writer 4414 may include a laser source, beam splitter, detector, and moveable lens. The writer 4414 may have actuators 4424 that may position the writer 4414 to a position to write data; the actuator 4424 may move the moveable lens or may move the entire writer 4414 assembly. The writer 4414 may write the new information on the media.
In an embodiment, the writer 4414 may receive positioning information from the transducer 4402 through an error correction feedback facility 4418. In an embodiment, the transducer 4402 may read the previously written data 4420 on the media and may feed the positioning information to the error correction facility 4418; the feed of information may be in real time. The previously written data 4420 may be received by the transducer detector 4410; the detector 4410 may feed the previously written data 4420 position to the error correction feedback facility 4418. The correction feedback facility 4418 may also receive previously written data 4420 positioning information from the moveable lens actuators. In an embodiment, the error correction feedback facility 4418 may contain logic to combine the previously written data 4420 positioning information from both the transducer detector 4410 and moveable lens actuator. In an embodiment, the error correction feedback facility 4418 may calculate the next position 4422 to write information; the next position 4422 may be feed to the writer 4414.
In an embodiment, the writer 4414 may receive the positioning information from the error correction feedback facility 4418. In an embodiment, the writer 4414 may receive the positioning information directly to the writer actuators 4424. In an embodiment, the writer 4414 may receive the positioning information to a processor that may calculate the next position 4422 for writing data to the media. In an embodiment, the next position 4422 for writing data may be in relation to the previously written data 4420 read by the transducer 4402.
In an embodiment, the next written data 4422 may be a set position from the previously written data 4420; the set position may be part of the read/write logic and therefore may not require positioning information to be written into the written data 4422.
In an embodiment, the next written data 4422 may not be a set position from the previously written data 4420; the data spacing may be written as part of the data written to the media.
In an embodiment, the next written data 4422 may be a set position based on a system variable; the system variable may be based on the required data density. In an embodiment, the position information may not be written into the written data 4422. In an embodiment, the system variable may be stored in the transducer 4402, the writer 4414, the error correction feedback facility 4418, or the like.
In an embodiment, multi-demodulation of received signals may be included in an optical tape facility for fast and accurate signal processing.
Modulated signals received by a multi-demodulator may represent a plurality of information such as amplitude, phase, frequency, and the like. The information may be a transmitted communication signal, a temperature, a position and velocity of an electromechanical device received electronically, or the like.
These modulated signals may also identify different types of products and their properties such as product type, product serial number, product distinguishing factors, attributes transmittable electronically or optically, and the like.
The multi-demodulator may determine the type of the received signal and an instantaneous value based upon the shape and carrier frequency; this information may be provided to a host device. The host device may apply a set of rules and decisions for the operation of the device based on the type and instantaneous value information provided by the demodulator.
The real time demodulation capability of this system may enable an application a fast and accurate signal processing for applications such as real time data and signal processing in communication systems, electromechanical control systems, and the like.
Referring to
S(t)={S1(t)*sin(w1*t)} Or {S2(t)*sin(w2*t)} . . . Or {Sk(t)*sin(wk*t)} (Eq1)
Or
S(t)={S1(t)*sin(w1*t)}+{S2(t)*sin(w2*t)}+{Sk(t)*sin(wk*t)} (Eq2)
The demodulator 4500 may be able to determine the presence of the plurality of Sk(t) signals in the received signal S(t) and may also be able to demodulate the instantaneous values of any Sk(t) signals presented in S(t).
Referring to
[FP1&FQ1], [FP2&FQ2], [FPk&FQk]
The complimentary filters may determine the presence and type of the different signals Sk(t) in the S(t) signal and may report the type of signal by a set of output signals.
TYP1, TYP2, . . . TYPk
and their instantaneous (real-time) magnitudes by:
S1(t), S2(t), Sk(T)
The demodulation process may be either analog or digital. The function of the Din 4502 in the analog design may be to adjust the level and amplitude of input signal S(t) for processing. In the digital design the Din 4502 may be an analog to digital converter (ADC) and the level and amplitude of S(t)n (S(t)n=sampled S(t) at Ts sample rate) may be adjusted later in by a system microprocessor or an application specific integrated circuit (ASIC). The operation of the complementary filters may be:
[FP1&FQ1], [FP2&FQ2], . . . [FPk&FQk]
The received signal S(t) may be described in the set of equations:
Where L(t)k may be a rectangular function with the frequency wk associated with the carrier frequency for signal {Sk(t)*sin(wk*T)}. M(t)k may be a rectangular function with a frequency wk, the frequency may be 90 degrees out of phase with L(t)k signal.
Further processing may produce:
Where AVE (Pk) and AVE Q(k) may be the running sum averages in real time of the Pk and Qk signals.
From the Fourier Transformation theorem the following derivations may be made:
Where indicates the proportionality.
Thus, the amplitude of any signal Sk(t) or its presence or non presence in S(t) may be determined in this method.
In an embodiment, an optical tape facility as described herein may be configured for error correction using multi-channel ECC interleaved with in-line ECC.
User data may be formatted into logical Kbyte blocks of data. For the logical Kbyte blocks of data, ECC symbol blocks may be generated to create an ECC entity that may include the logical Kbyte blocks of data and the ECC symbol blocks. This ECC entity may be referred to as the ECC coding scheme (C+D, D) where C+D may be the total number of blocks that make up the ECC entity and D may be the number of ECC blocks that may be generated. D may also be the number of blocks that may be corrected in the ECC entity during reading of the tape.
Once data may be formatted into ECC entities, the blocks of data that may make up the entity may be encoded with a per channel ECC that may correct bytes of error data out of the Kbytes blocks of data. The formatted data blocks may be interleaved to create an ECC block to be recorded on the tape. The ECC block may be a multiple interleaved block from the channel ECC entity to form a multi-block recorded ECC frame on the tape.
In an embodiment, during the read process the inline ECC may correct up to 10 bytes of data in error per logical Kbyte blocks of interleaved data. As data may be read, any blocks that may be in error may be corrected for up to about 10 bytes. If the ECC cannot correct the data, the block in error may be corrected by the cross-channel ECC that may use data recorded in other tracks on tape.
In an embodiment, a servo tracking system may be described for multiple optical heads of a transport facility that may provide a feed forward tracking signal for the multiple optical heads.
Referring to
Each multiple track zone 4702 may have it's own dedicated optical read/write head 4708. In this manner, data may be written and read from the optical media 4710 in a parallel data streaming fashion as the optical tape moves past the stationary heads 4708.
A track misregistration (TMh) for each multiple track zone 4702 may be governed by two major components. The track misregistration may be the movement of an individual track in relation to the optical head 4708. Lateral tape motion (LTM) 4712 may be common for all the heads 4708 and a residual motion 4714 (RMh) of each head 4708, which may be specific to each head. LTM 4712 may be the motion of the optical tape media 4710 in relation to the head transport facility. Thus:
The servo sensing head for each multiple track zone 4702, which may be the same as the read/write head 4708, may only be able to detect the relative motion of each track with respect to the specific head 4708 dedicated to that multiple track zone 4702. The servo sensing head may only be able to determine the total value of the TMh for a particular multiple track zone 4702. TMh may be a relative motion signal and it may be used as a feedback signal in the device servo system for each multiple track zone 4702 and the device servo system may have predetermined bandwidth capabilities for the servo performance.
A head transport facility that may use multiple heads 4708 and for multiple track zones 4702 the summation of all TMh's (SUM) may be computed by the device servo processor to aid the servo system in determining the TMh and RMh contributions to the total TMh for each head as follows:
Since the LTM 4712 may be the same for all heads, from EQU 1, the sum of all optical head misregistrations is:
SUM=TM1+TM2+TM3+ - - - +TMN=N*LTM+(RM1+RM2+RM3+ - - - RMN)
Thus to determine LTM:
LTM=SUM/N+(RM1+RM2+RM3+ - - - RMn)/N EQU 2
The combined RMh may be a non-correlated component for the combined TMh contribution in the term (RM1+RM2+RM3+ - - - RMn)/N of EQU 2 and it's value may be reduced considerably as N increases. Therefore, the LTM 4712 value may be approximated by the following equation;
LTM=SUM/N (Approximated) EQU 3
The LTM 4712 may be an absolute and common value with respect to all the heads 4708 and LTM 4712 may be independent from the motion of the individual head sensor. The approximated LTM of EQU 3 may be used as a Feed-Forward signal for each head 4708 and multiple track zone 4702 servo system to improve the servo error suppression performance for each head 4708. The LTM 4712 Feed-Forward signal may be combined with each individual optical head 0708 RM signal for improved optical head tracking.
In an embodiment, a method and system may be described for reading, demodulating, and decoding servo information.
Servo track information may be preformatted information on an optical tape media. This preformatted information may include data and coding synchronization patterns and track addresses. Servo markings may be placed on the optical tape media to create a sinusoidal pattern that may be retrieved from the media by the servo demodulator.
Referring to
In an embodiment, the frequency of the sinusoidal may determine the carrier frequency of the modulation and may provide timing for a synchronous demodulator/decoder. Each eight cycles of the pattern may represent a cell. In an embodiment, any N cycle pattern may be used for the sinusoidal signal. Each cell may carry information on synchronization and address bits. A 4-cycle reversal of the phase of the sinusoidal in the cell may indicate a “1-1” bit 4802 that may also be a synchronization pattern bit. The synchronization pattern may signal the beginning of the address subfields and may be used for synchronization. In the address subfield, the reversal of phase of the two first sinusoidal cycles in the cell may indicate “1-0” 4804 which may be decoded as bit “1” for the address and the reversal of phase for the second two cycles “0-1” 4808 in the cell may be decoded as bit “0” for the address.
The decoder may use an analog or digital delay 4810 in order to delay the detected sinusoidal signal and subtract it from the detected signal. In
In addition, a synchronous rectifier 4812, a rest-able integrator 4814, and a level detector 4818 may be used to decode the synchronization and address patterns as shown in
Referring to
Referring to
The invention herein disclosed includes a method for producing tools for creating nickel electroformed shims for optical tape embossing. The tools may be also called PDMS shim fathers.
Referring to
A blank quartz plate 5110 may be oxygen plasma cleaned 5124, generating a cleaned quartz plate 5126. Raw PDMS 5128 (Dow-Corning Sylgard 184 or equivalent) may be degassed 5130, generating degassed PDMS 5132. Degassed PDMS 5132 may be applied to siliconized surface master 5122, and cleaned quartz plate 5126 may be vacuum bagged or pneumatic pressed bonding 5134 against exposed surface of degassed PDMS 5132, resulting in uncured plate stack 5135.
Uncured plate stack 5135 may be then cured on a hot plate 5136. Cured plate stack 5138 may be then separated 5140, resulting in an embossed PDMS film 5142, cured siliconized surface master 5144, and cured quartz plate 5146.
Embossed PDMS film 5142 may be a near zero shrinkage replica of quartz untreated master 5116, and may be further used to electroform 5148 nickel shims (not shown). Embossed PDMS film 5142 has advantages over photopolymer or photoresist replications that include ease of releasing of the nickel electroformed father and very faithful pattern replication.
The invention herein described includes a method for producing an electroformed nickel embossing drum using two or more discrete nickel electroforms.
Referring to
Nickel electroforms 5210 may be precision-cut to align their edges along the electroformed format. The cutting may be done with a grinding machine using a resin bond diamond grinding wheel.
Stainless steel or aluminum perforated shim stock 5230, having a possible thickness ranging from 0.003″ to 0.010″, may be cut to approximately the nickel electroform width and a multiple of the nickel electroform length, resulting in a stainless steel or aluminum shim 5230 whose length substantially equals the circumference of an embossing drum (not shown).
Shim stock 5230 may be placed on a magnetic chuck on a measuring microscope, and may be aligned parallel to the axis of travel of a stage.
A first nickel form 5210A may be placed with a leading edge 5215 offset shim stock 130 and may be held in place by the magnetic chuck, the magnetic force adjusted to permit movement of nickel electroform 5210. Nickel electroform 5210 may be adjusted parallel to the axis of travel of the stage. Full force may be applied to the magnetic chuck to draw nickel electroform 5210 in intimate contact with shim stock 5230, and cryanoacrylate may be used to tack down the edges of nickel electroform 5210.
A second nickel electroform 5210B may be placed beside first nickel electroform 5210A, aligned first nickel electroform 5210A, and tacked in place. Subsequent nickel electro forms 5210 may be placed beside and aligned to previously placed electroforms 5210 and tacked. This place, align, tack procedure may be repeated until the desired number of nickel electroforms 5210 may be reached.
Shim stock 5230 with bonded nickel electroforms 5210 may be laser welded at each electroform seam 5250 that may be perpendicular to the long axis of the shim stock 5230. Leading edge 5215 seam aligning and bonding may be performed on a convex magnetic chuck having the appropriate radius of curvature. Leading edge 5215 seam may be also laser welded on the convex magnetic chuck.
The assembly may be removed from the magnetic chuck and an inner diameter seam of shim stock 5230 may be laser welded, and cryanoacrylate may be applied to all perforations on the inner diameter of the resulting drum.
A roller guide apparatus for transporting optical tape media in an optical tape system may be herein described.
Referring to
Flange inner surface 5350 may be flexible under appropriate force. The flexibility of inner surface 5350 allows precise adjustment of the height of roller shaft 5310 relative to the base plate. As the screw securing roller shaft 100 to the base plate may be further tightened, center post 5330 may be drawn further into the hole in the base plate. With surface 5315 of annulus 5340 resting on the surface of the base plate, inner surface 5350 flexes, allowing center post 5330 to be adjusted in height while maintaining precise perpendicularity to the base plate. Flange inner surface 5350 acts as a built-in spring and allows very precise height control, typically better than 1 micron. Factors that contribute to the range of motion and precision of adjustment include material for roller shaft 5300, diameter of center post 5330, thickness of flange inner surface 5350, and screw thread pitch in threaded end 5320.
Referring to
Stops 5420 may be substantially round disks having a diameter slightly greater than roller body 5410 and may be assembled to each end of roller body 5410. Stops 5420 may be polished to achieve appropriate flatness. Stops 5420 perform the vertical guiding of the tape, may be used to reduce the effects of lateral tape motion, and increase the ability of the tape drive to produce dense data recording. Transition area 5440 between stops 5420 and roller body 5410 may be a precision 90 degree corner. The distance between stops 5420 may be designed to be slightly wider (approximately 5 microns) than the width of the tape.
By the nature of the tape, one edge of the tape will run against one of stops 5420. Thus transition area 5440 where roller body 5410 and stop 5420 meet will exert an influence on the tape. The absence of a fillet in transition area 5440 allows the tape to remain planar, eliminating deformation of the tape. This will increase the life of the edge of the tape, thus preserving the tape drive's ability to control LTM.
Roller bearings 5430, assembled to stops 5420, opposite of roller body 5410, provide a smooth bearing surface for the assembly of roller body 5410 and stops 5420 to roll smoothly around roller shaft 5300.
Herein described may be a helical transport apparatus and method for using the helical transport with optical tape media in an optical tape system.
Referring to
Rollers 5540 may be mounted to a frame (not shown) such that rollers 5540 axis of rotation 5560 may be perpendicular to helical path 5550. Lower reel 5510 and upper reel 5520 axis of rotation may be also substantially perpendicular to helical path 5550. The resulting tape path distance from lower reel 5510 to upper reel 5520 may be dependent on the number of, and spacing of rollers 5540.
In another embodiment of the invention, the number of loops of helical path 5550 may be a value greater or less than that shown in
In another embodiment of the invention, interface heads 5560 may be placed along helical path 5550 for performing operations such as reading information from or writing information to tape 5530. Tape 5530 may include media from a set including optical media, and magnetic media, or may be of another type. The number and type of head 5560 may be more or less than that shown in
Referring to
In another embodiment of the invention, lower reel 5510 and upper reel 5520 may be replaced by other means of providing tape 5530 for transport including tape manufacturing means, tape format means, and the like.
An adjustable roller guide, as herein described may be used for precisely adjusting the height of optical tape media in an optical tape system.
Referring to
In response to a lateral position error signal delivered to coil 5750, a current may be applied that changes a magnetic field of coil 5750, causing magnet 5720 (and consequently attached roller 5710) to move along shaft 5730. The objective of the movement of roller 5710 may be to adjust a tape being guided by roller 5710 to compensate for an unwanted shift in the tape lateral position. As roller 5710 compensates for a shift in tape position, the position error signal may be reduced.
The invention may also be used to adjust roller 5710 position to account for tape of differing widths. In an embodiment with a second, stationary roller, roller 5710 can be moved along shaft 5730 to “trap” the tape between a top or bottom flange 5760 on roller 5710 and a bottom or top flange on the second roller. This embodiment may be well suited for use with narrow width tapes. Alternatively, for wide width tapes, roller 5710 can be positioned so that the top or bottom flange 5760 may be coincident with the position of the top or bottom flange of the stationary roller.
In another embodiment with a plurality of rollers 5710, each roller can be positioned based on the tape width to allow high density tracking.
Writing wobble cycles on a seamless drum, as herein described may be useful for embossing optical tape media, resulting in an adjustment zone beneficial to an optical tape system adapted to use the adjustment.
Referring to
Referring to
Referring to
An apparatus, as herein described may provide positional and planarizing support for positioning optical tape media under an optical pickup head in an optical tape system.
Focus channel 6030 may be a narrow channel separating entry surface 6020 from exit surface 6040, forming a possible separation width of between approximately 0.1 mm and approximately 3 mm. The tape media travels over focus channel 6030 as it moves from entry surface 6020 to exit surface 6040 wherein exit surface 6040 may remove planar perturbations of the tape media.
Referring to
Referring to
A reel, as herein described may be used with optical tape media in an optical tape system to reduce cost and increase speed of optical tape motion.
Referring to
In addition to providing low inertia characteristics, the mass reduction openings 6304 may also create bleed holes for the air to enter and exit the reel with the media during the winding process. The air entering and exiting the reel with the media may promote even stacking of the media on the reel; this may positively impact lateral tape motion. The mass reduction openings 6304 may also provide a monitoring technique for media stacking on the reel. As the media may be stacked onto the reel, there may be a tendency for the media to stack unevenly on the reel. If there may be uneven stacking, there may occur a shift of the tape position through the tape path that may reduce the tracking accuracy of the closed-loop servo system of the head transport facility.
The mass reduction openings 6304 may allow a monitoring technique to be used to identify if the media may be stacking evenly. A visual method may be used to see if the media has stacked correctly. The media stack may be sensed by a tape drive sensor such as an optical sensor to predict when an uneven stack may occur; this information may be feed to the closed-loop servo system that may compensate for the tape position change.
In an embodiment, this reel design may also have the capability of providing positive and negative pressure conditions in the drive area. The positive pressure may be used to cool the electronics in the drive or may create an air film between the tape layers when the tape may be being wound. The negative pressure may be used to draw air out from the media when the reel may be being unwound.
Referring to
In an embodiment, the mass reduction openings 6304 of the two halves 6302 may be aligned from the first half to the second half.
In an embodiment, the mass reduction openings 6304 of the two halves 6302 may not be aligned from the first half to the second half.
A stamper strip and a process resulting in precise alignment across a seam of the stamper strip, as herein described, may be used to generate optical tape media with precision tracking alignment.
Referring to
In an embodiment, the drum base 6502 may be magnetic and the outer surface may be polished optically smooth. The drum base 6502 may be made of a magnetic material, may be non-magnetic and have an outer layer of magnetic material; the outer layer may be a magnetic coating applied to drum base 6502. The stamper shim 6504 material may be a paramagnetic material such as nickel or Nichrome that may allow stamper shim 6504 to magnetically attach to drum base 6502 surface. In another embodiment, a non-magnetic stamper shim 6504 may be bonded to a paramagnetic material such as nickel or Nichrome to permit attachment of bonded stamper shim 6504 to magnetic drum base 6502.
In embodiment, the drum base 6502 may be made of a paramagnetic material such as nickel or Nichrome or may have an outer layer of paramagnetic material; the outer layer may be a paramagnetic coating applied to drum base 6502. The stamping shim 6504 may be a magnetic material. In another embodiment, the stamping shim 6504 may be made of a non-magnetic material with a bonded magnetic material to permit attachment of bonded stamper shim 6504 to paramagnetic drum base 6502.
In an embodiment, the stamper shim 6504 may be further held in place to drum base 6502 using an adhesive through glue holes 6508 in the drum base 6502 after alignment has been achieved.
Embossing features, that may be used to provide a format to the optical tape, may be on the outer surface or outer diameter of the stamper shim 6504. At least one stamper shim 6504 may be used to provide one complete set of tracks around the outer diameter of drum base 6502. With the at least one stamper shim 6504 applied around drum base 6502, at least one seam will be formed where the stamper shim 6504 ends meet. It may be important for the corresponding tracks to align accurately across the seam and/or seams. A plurality of stamper shims 6504 may be used around the circumference of the drum base 6502 for practical and manufacturing reasons. In embodiments, when multiple stamper shims 6504 may be wrapped around the drum base 6502, accurate alignment of the tracks across the multiple seams may be required.
In an embodiment, the stamper strip 6504 and the drum base 6502 may be attached by magnetic force and it may be relatively easy to laterally adjust the stamper shim 6504 ends on the drum base 6502 to align the stamper shim ends.
Referring to
In the coarse alignment step, a microscope such as a stereo microscope may be used to focus on the seam 6604 area of the stamper shims 6504. While viewing through the microscope, the stamper shims 6504 tracks may be aligned to within approximately +/−10 microns. Fiducial marks along the outer tracks and in between tracks may be used for this coarse alignment.
After the coarse alignment has been completed for all the stamper shim 6504 seams 6604, a fine alignment step may be performed for the final alignment of the embossing features.
In this step, the drum may be mounted on a spindle and rotated at a relatively slow rotational speed. This step may be accomplished using an optical media tester such as a Shibu Soku machine. An optical pickup head on the tester may focus on the surface features of the stamping shim 6504. The optical pickup head may focus and lock onto a track, may read the track, and may decode the track address. The optical pickup head may perform this process for the tracks on both sides of the seam. Electronic circuitry may be designed to accommodate the presence of the stamper seam 6604. Once the track addresses are determined for the tracks on both sides of the stamper shim 6504 seam 6604, the track may be aligned. For a drum with multiple shims, the alignment of each pair of stamper shims 6504 seam 6604 may be adjusted laterally with the process described above for each pair of stamper shims 6504 seam until the tracks are aligned.
Continuing to refer to
Referring to
An automated closed loop system may be developed by using a pickup head 6704 to read stamper shim 6504 tracks and feed the track information into a processor 6708. The processor 6708 may be a microprocessor, microcomputer, microcontroller, or the like. The processor 6708 may contain memory for storing the stamper shim 6504 track position information. The processor 6708 may also be able to provide feedback to piezoelectric transducers 6702 for alignment of the stamper shim 6502. The close loop system may also include an amplifier 6710 to provide the proper signal level for piezoelectric transducer 6702.
The pickup head 6704 may be allowed to move across all the tracks of the stamper shims 6504 to determine the track alignment. As the drum assembly 6500 may be slowly rotated around a center axis, the pickup head 6704 may read and send adjustment signals through the processor 6708 to at least one of piezoelectric transducers 6702 to align the track of the stamper shim 6504. The drum assembly 6500 may be rotated one or more revolutions to align the tracks across the stamper shims 6504.
In an embodiment, after a first pair of stamper shims 6504 across a seam are aligned, the pickup head of the close loop system may move to a second pair of stamper shims 6504 to achieve alignment. In an embodiment, the pickup head 6704 may align all of the shims of the drum assembly 6500.
In an embodiment, the close loop system may use an average of all stamper shim 6504 tracks to provide alignment to all the tracks.
In an embodiment, the close loop system may require perfect alignment of several given tracks for all the shims 6504 around the entire drum perimeter.
A testing apparatus, as described herein may be useful for testing various aspects of optical tape media.
Referring to
When energized, drum 6810 rotates at a desired speed, and head 6850 reads the features on media 6840, transferring any information read from these features to a computer (not shown) for analysis. One such analysis that can be performed may be a measure of quality of the media.
An adapted optical tape drive, when combined with an optical media tester, results in a test system, as described herein that may be useful for testing optical tape media in a configuration substantially similar to that found in an optical tape system.
Referring to
Optical head 6940 includes functions selected from a set including focus, tracking servo, and data interpretation. Information collected from optical head 6940 while performing one or more of the functions, may be analyzed to assess factors selected from a set including, lateral tape motion, tension variation, tape surface defects, and characteristics that exist in tape drives such as non-uniformities in the reels 6950, rollers 6960, and tape servo system (not shown).
An aligned, seamed, embossing drum and a process for production thereof, as herein described may be used to emboss optical tape media.
Referring to
In other embodiments, distribution channels 7030 along chucking drum 7010 outer surface may be included for disbursing adhesive from through holes 7020. Alternatively, through holes 7020 may be omitted and distribution channels 7030 may be included, extending to either end of drum 7010 for adhesive application.
Adhesive applied via through holes 7020 and/or distribution channels 7030 may be approximately a UV curable adhesive. However other types of adhesive may be used.
Referring further to
Referring to
Referring to
In another aspect of the invention the hollow, modified vacuum chucking drum 7010 can be fabricated from metal. This requires UV lamp 7220 be mounted outside completed drum assembly 7210 such that UV light passes through tape base 7250.
In another aspect of the invention, vacuum modulation and control may be controllable for each shim individually, allowing none, one, or any plurality of shims to be adjusted simultaneously prior to adhesive curing.
A process herein disclosed improves performance of multilayer optical media (e.g. optical tape) including a monomer layer on a substrate layer. The process disclosed for monomer curing includes exposure of the monomer to ultraviolet light. The process may improve performance by increasing adhesion of the monomer to a substrate, increasing cohesion within the cured monomer, and decreasing tackiness of the exposed surface of the cured monomer.
Referring to
In embodiments use of a broader band ultraviolet energy source may provide a broader foundation for monomer curing in first curing step 7310 while possibly increasing temperature of the media and embossing drum.
Referring to
Referring to
(I) Mod2 Embosser
Alignment of machine has been demonstrated beneficial for facilitating proper web tracking of both 2 mils and 6 micron PEN.
Coated idler roll surfaces may reduce friction and facilitate improved web tracking resulting in fewer creases. For example:
PTFE, Ni-impregnated Teflon on metal and plastic was found to effectively reduce friction in our systems; and
TFE coated of Embossing tools (Ni electroforms and Hg′x) may facilitate improved release.
sequencing of the drive system while Operating Mod2 with 6 micron substrate may facilitate avoiding web breaks. For example:
Setting and engaging web tension prior to driving the web; and
Setpoints for the sections of the machine may include:
Main drive set at 26 rpm (resulting in virtually no web movement, but the motor may be engaged);
Motor 3 Rewind tension set at 1 lb;
Motor 4 Unwind tension set at 0.6 lb;
After tension may be set, rewind tension may be raised in 0.5-0.75 increments up to 2.5 lbs;
Unwind tension may be raised to 0.65-1lb; and
After tensions may be at aim, main drive line speed can be increased in 1-2 rpm increments
Sequencing of the drive while Operating Mod2 with 2 mils substrate may facilitate avoiding overload of motors. For example:
Setting and engaging web tension prior to driving the web; and
Setpoints for the sections of the machine include:
Main drive set at 26 rpm (resulting in virtually no web movement, but the motor may be engaged);
Motor 3 Rewind tension set at 1lb;
Motor 4 Unwind tension set at 1lb;
After tension may be set, rewind tension may be raised in 0.5-0.75 increments up to 3.5-4 lbs;
Unwind tension may be raised to 2-3 lbs; and
After tensions may be at aim, main drive line speed can be increased in 1-2 rpm increments.
Sufficiently high rewind tension may facilitate quick machine recovery from temporary perturbations in tension such as those caused by engaging nip rolls.
The above sequencing and operating responses may be built into the control system logic reducing the possibility of operator error during machine operation.
Edge Guides
Unwind edge guide control system may be modified to facilitate dampened response time and reduced creasing which may be due to rapid and excessive changes in the magnitude of the unwind positioning system.
Rewind edge guide control system may be modified to facilitate dampened response time and reduced creasing which may be due to rapid and excessive changes in the magnitude of the unwind positioning system.
Rewind edge guide may be mounted on the moving mechanism of the motor (lateral motion) which may facilitate ensuring that the edge guide may be controlling to the edge of the winding roll, rather than to the backplane of Mod2. This may allow improved uniformity of the edge of the winding roll, which may be likely to be important for the subsequent vacuum coating processes.
Corona Treating
For the monomers tested on Mod2 a power level of 0.75 kw appears to provide good adhesion, assuming that the curing of the monomer may be sufficient. This process window was defined by corona treating substrate, cutting out a stop-action sample, and manually laminating the sample with monomer and curing in the Oriel lamp system for 3 minutes (known to be a sufficient curing level).
For a power level>0.75 kw, measured surface energy of the substrate 54 dynes.
Monomer Coating
Monomer coating using a manual syringe may be adequate for preliminary testing of the embossing process. At a web speed ˜6 fpm, a sinusoidal pattern of droplets on the web at a frequency of ˜1 drop/sec may provide a sufficient supply of monomer to the embossing process to yield a generally cross-web embossed CD pattern (with the CD drum). A significantly lower supply of monomer may reduce cross-web coverage. A higher supply of monomer may result in squeeze out from the edges of the drum.
As an example, a coating application technique using an Anilox-to-rubber-to-web was found to produce well-controlled, uniform coatings.
Substrate Anti-Stat Protection
Use of anti-stat devices, may facilitate avoiding poor performance areas.
For example improvements using anti-stat devices may include:
Web tracking may be improved for 6 micron PEN; and
Droplets may be better formed on the web surface coating of monomer when using a syringe.
The above may be achieved with the use of Po-210 nuclear antistat bars at 4 locations. The possible locations include:
Post-unwind
Post-corona treat unit
Post-embossing
Pre-rewind
Electrostatic antistat bars were also evaluated and found to work as effectively (in addition to presenting a shock hazard) as nuclear bars.
Embossing Process and Equipment
A nip pressure of at least 15 psi may provide sufficient force to result in good lamination using the CD drum.
Use of a single nip roll (infeed only) appears to allow a higher tension operating point on the embossing drum. This may be a result of
Less Isolation from the Rewind Tension Level Set
Inertia in nip roll #2, the impact of which may be exacerbated when the roll in engaged
Use of two nip rolls (infeed and exit) macroscopically results in acceptable operation. Some examples include:
Use of a seamed drum with regular seams may facilitate monitor evenness and ease of flow;
Engaging the two nip rolls with a good match of pressure facilitates tracking; and
A better controlled release point of the web from the drum; i.e., with the exit nip roll engaged, the web's drum release point may be “pinned” better due the pressure on the web from the closed nip roll.
The following input nip roller characteristics may be beneficial for thin webs: durometer (harder may be better), surface finish (pattern can print through backside of thin film, and diameter (larger diameter imparts less differential tension to infeed web).
Lamination Process Control
Precise Side-to-side lamination control of nip pressure may facilitate lamination.
Curing Process and Equipment
Equivalent degree of curing was found within the operating range of several different curing systems, for example:
Oriel “solar simulator” which may be a broad spectrum system;
The “belt UV system” which may be a broad spectrum system;
The Xenon flash lamp system; and
Infinilux & UVPS UV LEDs, which output a narrow wavelength light distribution centered at 395 nm.
For all of the above systems, good curing was found at some combination of light intensity setting and exposure time. Using certain monomer formulations may facilitate further good curing.
For the lamp systems, there may be a well defined curing “position” for the substrate which may be based at least on focal point or uniform exposure point of the lamp system
For the LED system, UV intensity was measured across the LED “triplet strips” at distances of ½″ and 1″ from the surface of the strip. It was found that a relatively uniform energy profile exists at a distance of 1″ from the strip; at the ½″ distance, a significant variation of intensity was measured with a large drop between the LED sources
For the Oriel system, using a possible monomer such as ACT2-158-1, good curing was observed with exposure times as low as 5 seconds or less.
The above exposure process operating point may be important, because the Mod2 exposure time using the 4″ diameter CD drum, with the placement of the UV LEDs on the unit, may be on the order of 3 seconds (approximately 2 inch exposure window at 6 fpm).
Substrate Rewinding
Substrate rewinding may be affected by surface roughness of the web (a low level of roughness may be incorporated by the substrate manufacturer, generally) to enable some air entrainment and may reduce surface friction and wrinkling at the windup.
By proper set up of the machine (either Mod2 or the Mill Lane; alignment and operating parameters), may facilitate good rolls of substrate being completed (i.e. roll may be “hard”, well formed, and has minimal wrinkling; at least as good as incoming substrate).
Web rewinding quality may vary depending on the processing conditions. Note that all of the conditions below utilize no special equipment to assist rewinding (i.e. lay-on rolls or bowed spreader rolls):
2 mils PEN without coating yielded a good roll
6 micron PEN without coating yielded a good roll
2 mils PEN coated with polymer (cured monomer) using a uniform drum without seams yielded a good roll
2 mils PEN coated with polymer (cured monomer) using a patterned drum with seams yielded significant air entrapment in the area of the seam; probably due to excessive level of tackiness in areas where the monomer coating was thicker due to the seams and undercured at these locations. Manifestation was in “bubbled TD areas on the winding roll” which subsequently caused creasing.
6 micron PEN with polymer (cured monomer) using a uniform drum without seams yielded significant creasing in the winding roll coincident with the polymer coated surface contacting the backside surface on the substrate on the rewind
6 micron PEN with polymer (cured monomer) using a patterned drum with seams yielded significant creasing in the winding roll coincident with the polymer coated surface contacting the backside surface on the substrate on the rewind. The bubbling seen with 2 mils PEN appears to be overwhelmed by the creasing problem, or may be simply not present due to the lower beam strength of the thin substrate passing through lamination nip.
Very uniform x-web tension at the rewind may facilitate high quality results when using thin films.
(II) Vacuum Coater
Pilot Roll Coater
Designed and installed new web transport/guide assy featuring backside-only idler and bowed (stretcher) rolls for optimization of thin web handling.
Improved Software Machine Controls
Upgraded deposition capability for 4 tandem sputter targets (2 DC & 2 RF magnetron) to allow doubling the SiO2/ZnS deposition rate.
Designed and implemented in-line reflectance measuring capability based on use of fiber-optic height sensor configured to measure reflectance. One bank of each linear array can be situated between each deposition zone.
Developed hardware to modify degree of isolation between each deposition zone to control interlayer mixing.
Pilot Batch Coater (Sharon)
Installed spiral wrap device to allow coating of discrete lengths of tape
Added “auto-indexer” to precisely rotate substrate holder over targets
Monomer Materials:
Monomer formulations were developed by several custom formulation suppliers to predetermined specifications and characteristics. Key parameters specified included:
Spectral sensitivity (for curing through PEN film);
Viscosity (aim may be low for good flow-out during the embossing process) such that low viscosity generally results may be lower chemical resistance
Temperature modulation was identified as a method of controlling viscosity (hence embossed layer thickness);
Curing rate (aim may be fast to increase process throughput);
Adhesion to plastic (for some Micon programs);
Low-adhesion to plastic (for other Micon programs); and
Release from “nickel tooling” for all Micon programs (assuming Ni tooling in the future).
Surface treatment (and volumetric treatment in the case of polymeric tools) were found to reduce the adhesion between the tool and the replication polymer.
Preliminary testing has occurred using a silicone release agent to improve separation of the cured monomer from the tooling surface. In addition, the release additive may be intended to provide some slip between the surface of the cured monomer and the backside of the web during rewinding (see rewinding section).
Monomer formulations which were sensitized into the blue region of the spectrum may be highly reactive and avoiding exposure to room lighting may be possible. This may be generally accomplished with the syringe dispensing method by wrapping the syringe with tape (e.g. Kapton tape) to filter the ambient blue light. This avoids the complexity of using entirely closed fluid handling systems.
Polymer Adhesion:
Polymer adhesion may be modified by several influences, including:
Intrinsic adhesion of the cured monomer to various surfaces;
Substrate treatment (note that both corona and flame treatment have been shown to improve adhesion); and
Substrate sub-coating with adhesion promoting layers (adhesion promoting sub-coats displayed improvement in most cases, but in some testing, there was no impact).
Vacuum-Deposited Layers:
WORM layer recipe used Al and Sb as first layer
Alloy layer used Ge2Sb2Te5 nominal alloy
Overcoat used ZnS/SiO2 layer
Thicknesses of each layer varied for optimum performance
Using a vacuum-deposited layer as backside anti-static coating was evaluated using Al; preliminary test result in tape transport were positive
Discreet Tooling:
As a near-term achievable alternative to developing a seamless drum for OT preformatting, a process was used which includes the precision pre-cutting of multiple Ni electroforms (“shims”) having the desired pre-format pattern and laser welding the individual segments into a drum.
Original format designs were created (via standard CAD processes) and an original relief representation (“master”) was made by patterning a glass substrate using lithographic techniques.
Ficucial cutting marks were included in the CAD pattern for later use in precision cutting of the pattern tooling.
Polymer-on-glass submasters were made directly from the master.
Reverse-image submasters (“mothers”) were also made from the submaster.
Ni electroforms were made from polymer submasters
Submasters may also be made from master
One or more of the following methods may achieve clean separation after a vacuum deposition process such as sputtering 40-70 nm of NiV, the method include:
Additional treatment of the polymer submasters to increase hardness;
Additional treatment of the polymer submasters to reduce adhesion to polymer surface;
Use thinner NiV layer;
Ramp sputter power to reduce temperature of initial deposit; and
Passivate NiV (as may be dome during Ni-to-Ni replication).
Both the polymer submasters and Ni masters were used as discreet flat shims in producing test replicas of the preformat pattern by a UV process which includes:
Flat lamination through pressure rollers at 50-75 psi with UV curing fluid [described previously] injected at point of lamination (“nip”); and
Cure by UV or optical radiation (4 sec to 6 min); 2-200 mw/cm2.
Drum Tool Fabrication:
Flat Ni shims were precision mill cut (“trimmed”) using carbide cutting tools based on pre-determined distance from fiducial marks embedded in Ni shim enabling four virtually identical shims to be made by this technique. Also a plastic protective film was laminated to patterned surface of Ni shim, and peeled back temporarily to view fiducial marks prior to trimming
Laser welding was used to join the 4 shims into a drum
All 4 shims were aligned to one (bottom) edge and 3 welds were made from the back side, ˜75% through the Ni, then the welded strip was flipped over and the finish weld was made from the front (patterned) side
The final weld to form (close) the drum was made through the front side
Optical measurements showed the highest weld precision (least offset of one track across the welded seam) was 0.00015 inches (3.7 microns) for the first drum processed by this method.
It was determined that a set of custom welding fixtures and additional testing may facilitate further reducing the offsets and improve the smoothness of the welding process.
Installation and Operation in Mod2:
Substitute Ni drums with CD patterns were installed in the Mod2 for preliminary process and machine testing [see above]. The drum was fixtured into the machine by sliding it over a rubber sleeve, which in turn was slid over the machine's drive shaft and was secured by compression of an end bell by use of a nut on the end of the threaded drive shaft.
Product application may include
¼, ½, ¾, 1, 4″ inch tape width
Possible may be ½″
Referring to
Top reading version (laser incident on “topcoat” side):
7410 Topcoat
Organic cured layer
PML (vac polymer deposition—acrylic) planarization
UV cure
EBeam cure
Solvent/aqueous coating
Purpose may be to protect the structure
Optical properties
7420 WORM Layer #3 (a.k.a. “Topcoat 1”)
An optional layer as part of the stack
Protects during manufacturing
Provides some optical tuning
Possibly (ZnS/SiO2, 80/20); alternates are SiO2, YF2, other transparent oxides and compounds
Thermal properties
Optical properties (T, R, A)
Flexibility
Adhesion (high)
Surface roughness
7430 & 7440 WORM layers
Possible may be Te alloy (GST=Ge2Sb2Te5 nom)
Metal (possible may be Sb, Al)
Thickness depends on product performance
7450 Pre-format layer
Possible may be UV cured polymer
Possible may be acrylic (possible epoxy or polyurethane)
Possible may be Viscosity (<200)
Possible may be Spectral sensitization (400 nm)
Possible may be Adhesion to substrate (high)
Possible may be Adhesion to tooling (low)
Possible may be Flexibility (high)
Layer thickness (0.5-1 u)
Preformat layer formation processes (options: single or multi-step sequence)
7460 Substrate
Materials
Possible may be PEN
PET
PC
CTA (cellulose triacetate)
Thickness
1 u-25 u (possible ˜4-8 u) Possible may be 6 u
Other Properties
Surface roughness
Subcoats
Fillers
Heat stabilization
Mechanically balanced stress
Surface treatment and or chemical treatment
7470 Backcoat(s)
Surface roughness
Optical properties
Possible may be Antistatic
Anti-stiction
Possible may be thin metal layer (Al, Ni, NiCr)
Carbon black may be alternate backcoat (as standard industry practice at this time)
(Anti-Curl Layer as Option)
Texturizing by embossing or formulation and additives (particulates) or drying
Purposeful reticulation
Other Considerations:
Possible may be Write dark and light (final tbd)
Tuning of chemistry to the correct write wavelength
Texturing of surfaces for improved drive performance
A second version exists may be read from the other side
Backcoat
Topcoat (?)
WORM layers
Pre-format layer
Substrate
Topcoat
Clear, protective
Texture control
Transparent (to R/W wavelength)
Antistat
WORM to R/W
May have erasable capability
Possible may be phase change
Possible may be pre-formatted layer in the structure
A seamed drum with a restart zone, zeroing zone, and the like, plus a method for forming the seamed drum
The following description refers to several possible embodiments of the disclosure and it may be understood that the variations of the invention and methods described herein may be envisioned by one skilled in the art, and such variations and improvements are intended to fall within the scope of the disclosure and therefore the disclosure and methods are not limited to the following embodiments.
In a typical configuration, shown both in
In the figures of this disclosure, motors, speed control elements, tension controls, web guides and the like are not shown in the figures of this disclosure for clarity, but such control systems are well known to the art (D. R. Roisum, The Mechanics of Rollers, TAPPI Press, Atlanta, 1996).
Now referring to
In order to reduce the heat load from the deposition process, rollers 42/43 in
The beneficial effects of the multi-pass averaging technique of this disclosure can be seen by examining the diagram in
It can be appreciated from this illustration that improvement in uniformity may be achieved from most source configurations, since the averaging effect may be based on the width of the substrate being small compared to the width of the source, and multiple passes sample many sections of the material source distribution.
In another embodiment, shown in
It may be also a feature of this disclosure that a means for collecting excess (“stray”) material from the source may be provided, as shown in
Yet another embodiment, shown in
As can be seen in
Drum shaped optical storage media 8410, 8420 may offer transfer rates from approximately 6.5 MB/s to approximately 13.5 MB/s and storage capacity from approximately 5.6 GB to approximately 102 GB.
Compact reel-to-reel tape 8440 shaped optical storage media (also known as mini-optical tape) may offer transfer rates from approximately 3.2 MB/s to approximately 6.7 MB/s and storage capacity from approximately 255 GB to approximately 1130 GB.
Optical storage media may be selected from a set including alternative optical media form 8400 for a particular application such that the physical size, and/or storage capacity, and/or transfer rate satisfies requirements of the application.
Optical flexible disk 8430, compact reel-to-reel 8440, and optical card 8450 may be incorporated into a housing providing easy portability and protection of the media, and may be appropriate for applications in which the media may be frequently handled by a user.
In this embodiment, optical drive 8520 communicates with PC 8540 hard drive 8530, using a portion of a predetermined size of hard drive 8540 to improve random access to information on alternative optical media form 8400. It may be possible that alternative optical media form 8400, through optical drive 8520 offers a transfer rate that may be faster than disk drive 8530. This may be accomplished in various ways, with one way being increasing the number of pickup heads in optical drive 8520 used to record or read alternative optical media form 8400. An increase in pickup heads may directly enable faster data transfer rate to/from alternative optical media form 8400.
When system 8500 may be used in an audio or video entertainment application, there may be unique algorithms and formats applied to the portion of hard drive 8540 that allow users to rapidly access portions of the information stored on alternative optical media form 8400. As an example, the algorithms may allow a user to view thumbnails of movie scenes located a different physical locations on alternative optical media form 8400, and then access a selected movie. These algorithms and formats may include index or location information of the movies associated with the thumbnails on alternative optical media form 8400, enabling fast access to the selected movie. Information stored on disk drive 8530 may include tracking data that determines what information may be only on alternative optical media form 8400 and what has been transferred to hard drive 8530. Other uses for system 8500 include archive and backup of images, home movies, business information, or archive library services.
Another possible embodiment of an optical storage system may be shown in
System 8600 may connect to a PC via a wired or wireless LAN. It may also allow recording a plurality of programs using standard TV format and HDTV format onto alternative optical media form 8400. Using means similar to the embodiment of
System 8600A may also be used as an expandable storage Digital Video Recorder (DVR). Since a DVR records video information to a hard drive, the storage capacity may be based on the capacity of the hard drive. Unwanted results such as users losing recorded programs, or recording of new shows being halted occur when the capacity of the hard drive limit may be reached.
By including an alternative optical media form 8400 and optical drive 8520 in an embodiment of system 8600 being used as a DVR, video storage may be now augmented beyond the hard drive limit to include alternative optical media form 8400. In an embodiment of system 8600 wherein optical storage media may be removable, the amount of storage capacity of system 8600 may be unlimited. Compact reel-to-reel 8440 optical storage media may be a possible embodiment of alternative optical media form 8400 because of its high volumetric storage density.
The format of information of each recording on alternative optical media form 8400 in this embodiment may be selected from a set including DVD and HDVD formats.
Optical storage media used in camera 8700 may be used interchangeably for recording or reading with any of the other system embodiment herein disclosed. Embodiments of alternative optical media form 8400 that meet the electrical, physical, and interface requirements of DVD media may also be used on standard PC or home entertainment equipment.
The elements depicted in flow charts and block diagrams throughout the figures may imply logical boundaries between the elements. However, according to software or hardware engineering practices, the depicted elements and the functions thereof may be implemented as parts of a monolithic software structure, as standalone software modules, or as modules that employ external routines, code, services, and so forth, or any combination of these, and all such implementations are within the scope of the present disclosure. Thus, while the foregoing drawings and description set forth functional aspects of the disclosed systems, no particular arrangement of software for implementing these functional aspects should be inferred from these descriptions unless explicitly stated or otherwise required by the context.
Similarly, it will be appreciated that the various steps identified and described above may be varied, and that the order of steps may be adapted to particular applications of the techniques disclosed herein. All such variations and modifications are intended to fall within the scope of this disclosure. As such, the depiction and/or description of an order for various steps should not be understood to require a particular order of execution for those steps, unless required by a particular application, or explicitly stated or otherwise clear from the context.
The methods or processes described above, and steps thereof, may be realized in hardware, software, or any combination of these suitable for a particular application. The hardware may include a general-purpose computer and/or dedicated computing device. The processes may be realized in one or more microprocessors, microcontrollers, embedded microcontrollers, programmable digital signal processors or other programmable device, along with internal and/or external memory. The processes may also, or instead, be embodied in an application specific integrated circuit, a programmable gate array, programmable array logic, or any other device or combination of devices that may be configured to process electronic signals. It will further be appreciated that one or more of the processes may be realized as computer executable code created using a structured programming language such as C, an object oriented programming language such as C++, or any other high-level or low-level programming language (including assembly languages, hardware description languages, and database programming languages and technologies) that may be stored, compiled or interpreted to run on one of the above devices, as well as heterogeneous combinations of processors, processor architectures, or combinations of different hardware and software.
Thus, in one aspect, each method described above and combinations thereof may be embodied in computer executable code that, when executing on one or more computing devices, performs the steps thereof. In another aspect, the methods may be embodied in systems that perform the steps thereof, and may be distributed across devices in a number of ways, or all of the functionality may be integrated into a dedicated, standalone device or other hardware. In another aspect, means for performing the steps associated with the processes described above may include any of the hardware and/or software described above. All such permutations and combinations are intended to fall within the scope of the present disclosure.
While the invention has been disclosed in connection with certain possible embodiments, other embodiments would be understood by one of ordinary skill in the art and are encompassed herein.
This application claims the benefit of the following provisional applications, each of which may be hereby incorporated by reference in its entirety: U.S. application No. 60/764,856, filed on Feb. 2, 2006 entitled “OPTICAL STORAGE MEDIA DEVICE AND SYSTEM WITH RANDOM ACCESS NONVOLATILE STORAGE FOR MULTIMEDIA APPLICATIONS”; U.S. application No. 60/787,737, filed on Mar. 31, 2006 entitled “OPTICAL STORAGE MEDIA DEVICE AND SYSTEM WITH RANDOM ACCESS NONVOLATILE STORAGE FOR MULTIMEDIA APPLICATIONS”; U.S. application No. 60/764,913, filed on Feb. 2, 2006 entitled “PICK UP HEAD FACILITIES FOR OPTICAL TAPE”; U.S. application No. 60/777,445, filed on Feb. 27, 2006 entitled “PICK UP HEAD FACILITIES FOR OPTICAL TAPE”; U.S. application No. 60/764,911, filed on Feb. 2, 2006 entitled “APPARATUS AND METHODS FOR PRODUCTION, TESTING, AND USE OF OPTICAL TAPE MEDIA”; U.S. application No. 60/788,012, filed on Mar. 31, 2006 entitled “PRODUCTION, TESTING, AND USE OF OPTICAL TAPE MEDIA”; U.S. application No. 60/764,912, filed on Feb. 2, 2006 entitled “STAMPER STRIP WITH PRECISION TRACKING ALIGNMENT ACROSS A SEAM AND PROCESS FOR FABRICATING THEREOF”; U.S. application No. 60/787,788, filed on Mar. 31, 2006 entitled “STAMPER STRIP WITH PRECISION TRACKING ALIGNMENT ACROSS A SEAM AND PROCESS FOR FABRICATING THEREOF”; U.S. application No. 60/764,910, filed on Feb. 2, 2006 entitled “OPTICAL TAPE MEDIA TESTER”; U.S. application No. 60/764,859, filed on Feb. 2, 2006 entitled “ADAPTED OPTICAL TAPE DRIVE AND OPTICAL MEDIA TESTER FOR TESTING OPTICAL TAPE MEDIA”; U.S. application No. 60/764,855, filed on Feb. 2, 2006 entitled “A METHOD FOR PRODUCING SHIMS FOR USE IN TAPE EMBOSSING”; U.S. application No. 60/765,094, filed on Feb. 2, 2006 entitled “A METHOD FOR PRODUCING AN EMBOSSING DRUM USING TWO OR MORE DISCRETE ELECTROFORMS”; U.S. application No. 60/764,872, filed on Feb. 2, 2006 entitled “ALIGNED SEAMED DRUM FOR TAPE MEDIA MANUFACTURING, USE AND PRODUCTION PROCESS THEREOF”; U.S. application No. 60/777,438, filed on Feb. 27, 2006 entitled “ULTRAVIOLET POST-CURING PROCESS FOR MULTILAYER OPTICAL MEDIA”; U.S. application No. 60/777,440, filed on Feb. 27, 2006 entitled “OPTICAL TAPE PROCESS, MATERIALS, TOOLING, AND MEDIA STRUCTURE”; U.S. application No. 60/777,441, filed on Feb. 27, 2006 entitled “IMPROVED VACUUM COATING METHOD”; U.S. application No. 60/764,860, filed on Feb. 2, 2006 entitled “OPTICAL TAPE MEDIA, MARKING, AND PROCESS FOR PRODUCING THEREOF”; U.S. application No. 60/777,439, filed on Feb. 27, 2006 entitled “OPTICAL TAPE MEDIA, MARKING, AND PROCESS FOR PRODUCING THEREOF”; U.S. application No. 60/777,369, filed on Feb. 27, 2006 entitled “HIGH-CONTRAST WRITE-ONCE READ-MANY OPTICAL MEDIA”; and U.S. application No. 60/777,442, filed on Feb. 27, 2006 entitled “OPTICAL MEDIA FORMULATION, METHOD, AND APPARATUS”.
Number | Date | Country | |
---|---|---|---|
60764856 | Feb 2006 | US | |
60787737 | Mar 2006 | US | |
60764913 | Feb 2006 | US | |
60777445 | Feb 2006 | US | |
60764911 | Feb 2006 | US | |
60788012 | Mar 2006 | US | |
60764912 | Feb 2006 | US | |
60787788 | Mar 2006 | US | |
60764910 | Feb 2006 | US | |
60764859 | Feb 2006 | US | |
60764855 | Feb 2006 | US | |
60765094 | Feb 2006 | US | |
60764872 | Feb 2006 | US | |
60777438 | Feb 2006 | US | |
60777440 | Feb 2006 | US | |
60777441 | Feb 2006 | US | |
60764860 | Feb 2006 | US | |
60777439 | Feb 2006 | US | |
60777369 | Feb 2006 | US | |
60777442 | Feb 2006 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11670812 | Feb 2007 | US |
Child | 12628030 | US |