Patent Grant
7943491
An increasing number of technologies require large-scale integration of disparate classes of separately fabricated objects into spatially organized, functional systems. Here we introduce an approach for heterogeneous integration based on kinetically controlled switching between adhesion and release of solid objects to and from an elastomeric stamp. We describe the physics of soft adhesion that govern this process and demonstrate the method by printing objects with a wide range of sizes and shapes, made of single-crystal silicon and GaN, mica, highly ordered pyrolytic graphite, silica and pollen, onto a variety of substrates, even without specially designed surface chemistries or separate adhesive layers. The process is compatible with procedures that use special surface chemistries or adhesive layers to bind objects to their printing targets. Printed p-n junctions and photodiodes fixed directly on highly curved surfaces illustrate some unique device-level capabilities of this approach.
Examples of systems that rely critically on heterogeneous integration range from optoelectronic systems that integrate lasers, lenses and optical fibers with control electronics, to tools for neurological study that involve cells interfaced to arrays of inorganic sensors, to flexible ‘macroelectronic’ circuits and actuators that combine inorganic device components with thin plastic substrates. The most significant challenges associated with realizing these types of system derive from the disparate nature of the materials and the often vastly different techniques needed to process them into devices. As a result, all broadly useful integration strategies begin with independent fabrication of components followed by assembly onto a single device substrate. The present invention addresses a need in the art for a reliable and robust transfer printing process that can assemble disparate components onto a single device substrate.
The present invention encompasses a deterministic, high-speed approach for manipulation and heterogeneous integration that uses kinetically controlled adhesion to elastomeric transfer devices, or stamps, to transfer print solid objects from one substrate to another. This technique provides an important combination of capabilities that is not offered by other assembly methods, such as those based on ‘pick and place’ technologies, wafer bonding, or directed self-assembly.
The method presented herein allows manipulation of arrays of objects based on kinetically controllable adhesion to a viscoelastic stamp in a massively parallel and deterministic manner. The mechanics suggest paths for optimizing the material properties of the stamps in ways that have not been explored in soft lithography or related areas. Even with existing materials, the printing procedure provides robust capabilities for generating microstructured hybrid materials systems and device arrays with applications in optoelectronics, photonics, non-planar fabrication and biotechnology without the use of precision moving parts, applied electric or magnetic fields. The stamp-based methods of the present invention are invaluable tools for handling the building blocks of nano- and other emerging technologies to construct devices based on these technologies.
The present invention provides methods, systems and system components for transferring, assembling and integrating features and arrays of features having selected nanosized and/or microsized physical dimensions, shapes and spatial orientations. Methods of the present invention utilize principles of ‘soft adhesion’ to guide the transfer, assembly and/or integration of features, such as printable semiconductor elements or other components of electronic devices. Methods of the present invention are useful for transferring features from a donor substrate to the transfer surface of an elastomeric transfer device and, optionally, from the transfer surface of an elastomeric transfer device to the receiving surface of a receiving substrate. The present methods and systems provide highly efficient, registered transfer of features and arrays of features, such as printable semiconductor elements, in a concerted manner that maintains the relative spatial orientations of transferred features.
In one embodiment, the present methods and systems exploit the viscoelastic properties of elastomeric transfer devices to provide kinetic control of adhesion between a transfer surface of the transfer device and features subject to processing via transfer, assembly or integration. The viscoelastic nature of the elastomeric material of the transfer device results in an adhesion force that depends, at least in part, on the rate that the transfer surface is peeled away or otherwise separated from a donor substrate having features disposed thereon, or the rate that the transfer surface having features disposed thereon is peeled away or otherwise separated from a receiving substrate. High separation rates are used in the present invention, for example, to generate adhesion forces large enough to transfer features, such as printable semiconductor elements, from a donor substrate to a transfer surface of an elastomeric transfer device. Low separation rates are used in the present invention, for example, to generate adhesion forces low enough to facilitate transfer of features, such as printable semiconductor elements, disposed on a transfer surface of an elastomeric transfer device to a donor substrate. Methods of this aspect of the present invention are useful for transferring, assembling and integrating a wide range of useful materials and structures, device components and/or functional devices onto or into a receiving substrate with high placement accuracy and pattern fidelity, particularly in the context of transfer contact printing. The methods and systems of the present invention are compatible with a range of receiving substrate compositions including polymer, ceramic, metal, semiconductor, paper, and glass substrates, substrate geometries including planar and contoured substrates, and substrate surface morphologies including smooth and rough substrates.
The invention is particularly useful for generating patterns of features on surfaces of substrates exhibiting excellent reproducibility, pattern fidelity and resolution. The present invention is capable of high throughput patterning of large receiving substrate areas (greater than or equal to about 232 cm2) and, thus, enable a robust and commercially attractive manufacturing pathway to a range of functional systems and devices including electronic device arrays, nano- and micro-electromechanical systems, nano and micro-biological systems, sensors, energy storage devices and integrated electronic circuits. Further, nanopatterning and micropatterning methods and systems of the present invention are compatible with a wide range of substrates and materials, including semiconductors, wafers, metals, metal alloys, semimetals, insulators, crystalline materials, amorphous materials, biological materials, and the methods can be employed under a wide range of processing conditions, including low temperature (<about 400 degrees Celsius) processing.
In one embodiment, the present invention provides methods for transferring features, including nanosized and/or microsized structures, using an elastomeric transfer device to transfer a feature from a first substrate surface to a second substrate surface by applying different kinetic separation (e.g., using a different peeling rate and/or separation rate for example) of surfaces to variably control adhesion of the feature to the transfer surface of an elastomeric transfer device.
In one aspect, the invention provides a method of transferring a feature from a donor substrate surface to a receiving substrate surface, optionally providing registered transfer of features and feature arrays from the donor substrate to the receiving substrate. In one embodiment, a method of this aspect of the present invention comprises the step of providing an elastomeric transfer device having a transfer surface and providing a donor substrate having a donor surface. The donor surface has at least one feature disposed thereon. The method further comprises the step of contacting at least a portion of the transfer surface with at least a portion of the donor surface feature and physically separating the transfer surface from the donor surface at a first separation rate such that at least a portion of the feature is transferred from the donor surface to the transfer surface. The method further comprises the step of providing a receiving substrate having a receiving surface, and contacting at least a portion of the feature disposed on the transfer surface with the receiving surface. The transfer surface having features disposed thereon is separated from the receiving surface at a second separation rate, that is less than the first separation rate, such that at least a portion of the feature disposed on the transfer surface is transferred to the receiving surface, thereby transferring a feature from the donor surface to the receiving surface. In this embodiment, use of a first separation rate greater than the second separation is beneficial for providing efficient transfer from the donor substrate to the receiving substrate. The terms “separation rate” and peel rate” are used synonymously in the present description.
In the context of this description, a “feature” refers to a structure on, or an integral part of, a donor surface to be transferred to an elastomeric transfer device and/or a receiving surface of a receiving substrate. The term feature encompasses a free-standing structure supported by a donor surface, such as an entirely undercut free-standing structure and encompasses a feature that is integral connected to the donor surface (e.g., a monolithic structure, or discrete structures connected by an adhesive layer or by surface forces including van der Waals forces, etc.), such as a completely or partially undercut structure connected to the donor surface via one or more bridge elements and/or other alignment maintenance elements. In some useful embodiments, feature comprises one or more printable semiconductor elements, patterns of printable semiconductor elements and arrays of printable semiconductor elements. Some features useful in the present invention are micro-sized structures or nano-sized structures. The term feature, as used herein, also refers to a pattern or an array of structures, and encompasses patterns of nanostructures, patterns of microstructures or a pattern of microstructures and nanostructures. In an embodiment, a feature comprises a functional device component or functional device.
In the present methods, the viscoelastic properties of an elastomeric transfer device enables precise control of adhesion forces involved in transfer of features from a donor substrate to a transfer surface of a transfer device and from the transfer surface of a transfer device to a receiving substrate. Elastomeric transfer devices of the present invention may comprise any elastomer material, including composite materials, so long as the transfer device exhibits viscoelastic behavior such that adhesion between a feature and the transfer device is rate-sensitive. Accordingly, selection of the composition, physical dimensions (e.g. thickness) and mechanical properties of the elastomeric transfer device used in the present methods is important to provide high yield transfer efficiencies, and optionally registered transfer. In an embodiment, the elastomeric transfer device comprises at least one elastomer layer having a Young's modulus between about 1 MPa and about 20 MPa. In an embodiment, the elastomeric transfer device comprises at least one elastomer layer having a thickness between about 1 micron and about 100 microns. In an embodiment, the elastomeric transfer device comprises an elastomeric stamp, elastomeric mold or elastomeric photomask. In one embodiment, the elastomeric transfer device comprises polydimethylsiloxane. In another embodiment, the transfer device comprises perfluorinated polyether. In another embodiment, the transfer device comprises Scotch® tape.
Use of an elastomeric transfer device is also beneficial in the present methods because it is capable of providing conformal contact with the surfaces of features, donor substrates and/or receiving substrates. In an embodiment, conformal contact is established between the transfer surface of the elastomeric transfer device and an external surface of the feature and optionally, conformal contact is established between the transfer surface having the feature disposed thereon and the receiving surface of the receiving substrate. In the context of this description, the term “external surface” refers to a feature surface that is accessible to the transfer surface.
In the present invention, the rate that the elastomeric transfer device is separated from substrates and/or features on substrates is selected so as to generate adhesive forces useful for transferring, assembling and integrating features. In an embodiment, the first separation rate is at least 10 times larger than the second separation rate, and in some embodiments the first separation rate is at least 100 times larger than the second separation rate. In an embodiment, the first separation rate is greater than or equal to about 10 cm/s so as to provide efficient transfer of one or more features from the surface of a donor substrate to the transfer surface of the transfer device and the second separation rate is less than or equal to about 1 mm/s so as to provide efficient transfer of one or more features from the transfer surface of the transfer device to the receiving surface of a receiving substrate. In one embodiment, features undergoing transfer have lengths selected over the range of about 100 nanometers to about 1000 microns, widths selected over the range of about 100 nanometers to about 1000 microns and thicknesses selected over the range of about 1 nanometer to about 1000 microns, and the first separation rate is selected over the range of about 100 cm/s to 0.1 mm/s and/or the second separation rate is selected over the range of about 0.1 mm/s to 100 cm/s. In an embodiment, the first separation rate selected so as to generate a separation energy between the feature and the transfer surface of the elastomeric transfer device per unit area equal to or greater than 4 J/m2.
Separation rates useful in the present invention may be constant, substantially constant, or variable with respect to time. In this context, the expression “substantially constant with respect to time” refers to a separation rate that varies by less than 10% over a separation time (or peel time) interval. Similarly, a separation rate that is “substantially constant” refers to a separation rate that varies less than 10% over a separation time interval and/or less than 10% over a separation region. The invention optionally further comprises use of a first separation rate, a second separation rate or both first and second separation rates that are substantially constant as a function of time. In another embodiment, the first separation rate, the second separation rate or both the first and second separation rate varies selectively as a function of time, for example increasing, decreasing, or having an interval or region over which the rate increases and a second interval or region over which the rate decreases as separation proceeds across distance or time.
Use of large first separation rates in the present invention is also useful for releasing features connected to and/or supported by a donor substrate. The present invention includes methods wherein the feature is connected to the donor surface, for example by one or more bridge elements or other alignment maintenance elements, and the first separation rate is large enough so as to cause release of the feature from the donor surface. In one embodiment, for example, the feature is connected to the donor surface via at least one bridge element and the first separation rate is large enough to cause fracture of the bridge element(s), thereby resulting in release of the feature from the donor surface. Alternatively, the present invention includes methods wherein the feature is a free standing structure supported by the donor surface, wherein the first separation rate is large enough to release the structure from the donor surface onto the transfer surface of the transfer element.
In an embodiment, the invention provides methods wherein the steps of: contacting at least a portion of the transfer surface with at least a portion of the feature; separating the transfer surface from the donor surface at the first separation rate; contacting at least a portion of the feature disposed on the transfer surface with the receiving surface of the receiving substrate; separating the transfer surface from the feature at a second separation rate or any combination of these steps are carried out via an actuator, such as a roller printing or flexographic printing assembly or a mechanical stage, operationally connected to the transfer device.
In an embodiment, the invention further comprises the steps of: providing a plurality of printable semiconductor elements wherein each of the printable semiconductor element is optionally connected to the donor substrate via at least one bridge element; the method further comprising the steps of: contacting at least a portion of the transfer surface with at least a portion of the pattern of printable semiconductor element; separating the transfer surface from the donor surface at a first separation rate such that at least a portion of the bridge elements are fractured and at least a portion of the pattern of printable semiconductor elements is transferred from the donor surface to the transfer surface, thereby forming the transfer surface having the printable semiconductor elements disposed thereon; contacting at least a portion of the printable semiconductor elements disposed on the transfer surface with the receiving surface of the receiving substrate; and separating the transfer surface from the feature at a second separation rate, wherein the first separation rate is larger than the second separation rate, thereby transferring at least a portion of the pattern of printable semiconductor elements to the receiving surface. In an embodiment, the printable semiconductor element is connected to the donor substrate via one or more bridge elements (or other alignment maintenance elements), wherein the separation rate is large enough to cause fracture of the bridge element(s) (or other alignment maintenance elements), thereby resulting in release of the printable semiconductor element from the donor surface and transfer to the transfer surface of the elastomeric transfer device. In an embodiment, the portion of the pattern of printable semiconductor elements is transferred with good fidelity. In another embodiment, the portion of the pattern of printable semiconductor elements is transferred to a selected region of the receiving surface with a placement accuracy better than or equal to about 25 microns over a receiving surface area equal to about 5 cm2.
In an embodiment, the transferred feature comprises a semiconductor structure composed of one or more of silicon, single crystal silicon, polycrystalline silicon, doped silicon, n-type silicon, p-type silicon, GaN (gallium nitride), GaAs (gallium arsenide), and InP (indium phosphide). Alternatively, the transferred features comprise mica, highly ordered pyrolytic graphite, silica, or pollen. In an embodiment, the transferred feature comprises a silicon photodiode. The feature, in an embodiment, is selected from the group consisting of: an electronic device, a component of an electronic device, a diode, a transistor, a photovoltaic device, a sensor, a light emitting diode, a microelectromechanical device, a nanoelectromechanical device, a photodiode, a laser, a P-N junction, a wire, a pill, and a small container. In an embodiment, the feature comprises a pattern of microstructures, nanostructures or both; and the invention further comprises transferring the pattern of microstructures, nanostructures or both from the donor surface to the receiving surface. The feature, in an embodiment, comprises a pattern of structures wherein substantially all the structures in contact with the transfer surface are transferred to the receiving surface.
Any of the methods disclosed herein can further comprise repeating at least a portion of the steps. In some embodiments, for example, processing steps are repeated so as to generate multi-layered structures on a receiving surface. In some methods, processing steps of the present invention are repeated so as to transfer, assemble and integrate different features, optionally from different donor surfaces, into a multicomponent electronic device or array of electronic devices.
The invention disclosed herein further comprises a method of making an electronic device, array of electronic devices or components of an electronic device such as a p-n junction; a photodiode, a transistor, a light emitting diode, a laser, a photovoltaic device, a memory device, a microelectromechanical device; a nanoelectromechanical device; and a complementary logic circuit.
In an embodiment, the process comprises a transfer device comprising an elastomer layer having a transfer surface, such as a PDMS layer, wherein the rate of separation of the transfer surface from a donor surface or receiving surface is selectively controllable. In some embodiments, a transfer device of the present invention is capable of providing a separation rate of the transfer surface from a donor surface that is about 10 cm/second or greater and providing a separation rate of the transfer surface having a feature disposed thereon from the receiving surface that is about 1 mm/second or less.
In an embodiment, only a portion of the feature is transferred to the receiving substrate. In an embodiment, substantially all the features in contact with the transfer surface are transferred to the transfer surface. In an embodiment, substantially all the features in contact with the receiving surface are transferred from the transfer surface to the receiving surface.
In an embodiment, the donor surface and/or receiving surface is substantially flat. Flatness can be assessed by measuring the surface height relative to a reference line positioned at the average surface location and normalizing the maximum deviation to the length of the surface. Substantially flat refers to a normalized maximum deviation from the reference line that is less than 1%. A surface that is not substantially flat is contoured. In an embodiment one or more of the donor surface, receiving surface and/or transfer surface is contoured. Donor surfaces, receiving surface and transfer surfaces useful in the present methods can have both contoured and flat portions.
In an embodiment, the donor substrate, the receiving substrate, the transferable features, the transfer element, or any combination of the above items may comprise molded, embossed, machined, or otherwise defined topographical relief features that may either aid in the fabrication processes described in the present invention or in the function of the devices and systems fabricated by methods described by the present invention.
In an embodiment, the invention is a method of manufacturing a device comprising: providing an elastomeric stamp having a stamp surface; providing a donor substrate having a donor surface, wherein the donor surface has at least one feature; contacting at least a portion of the stamp surface with at least a portion of the donor surface feature; separating the stamp surface from the donor surface at a first separation rate such that at least a portion of the feature is transferred from the donor surface to the stamp surface; providing a device substrate having a device surface; contacting at least a portion of the stamp surface having the transferred feature with the device surface; and separating the stamp surface from the device surface at a second separation rate such that at least a portion of the stamp surface feature is transferred to the device surface to generate a device on the device substrate.
In an embodiment, the device comprises a p-n junction. In an embodiment, the device is a photodiode. In an embodiment, the device is a component of an optoelectronic system. In an embodiment, the device comprises an actuator. In an embodiment, the device comprises a feature that is a biological entity and the device interacts with a biological system, including a cell isolated from the body.
In an embodiment, the invention comprises means and methods of separating with controlled separation rates, as known in the art. Exemplary means and methods of separation with controlled rate include, but are not limited to, use of rolled and flexographic printer configurations, axis-symmetric separation, and non-axis-symmetric separation. “Axis-symmetric separation” refers to a means of separating a transfer element from a donor or receiver substrate by applying an approximately (within 10%) uniform separation force across the contacted area. “Non-axis-symmetric separation” refers to a means of separating a transfer element from a donor or receiver substrate by applying a non-uniform separation force across the contacted area, for example, by applying a greater separation force at the edges or corners of the contacted area, for example, using a “peeling” motion.
In an embodiment, the radius of curvature or induced radius of curvature of the transfer elements are controlled to facilitate transfer of features, especially rigid features.
The invention provides important functional benefits compared to conventional printing techniques known in the art, including: (1) good placement accuracy, (2) high pattern fidelity, (3) general applicability to systems regardless of surface chemistry, surface curvature and/or geometry and surface morphology, (4) switchable/controllable adhesion strength levels of printed materials to the printing element and (5) good transfer efficiency (i.e. percentage of elements transferred from donor surface to receiving surface).
The receiving surface and/or receiving substrate can be of any composition, so long as the feature to be printed is capable of transferring from the transfer surface to the receiving surface at the second separation rate. In addition, the receiving surface can be of any shape including, but not limited to, planar, contoured, convex, concave or a combination of convex and concave. The surface can be smooth or rough. A surface is said to be “smooth” when there is less than about 3 nm variation in surface height as determined by atomic force microscopy within a region having an area of 1 um2. In an embodiment, the receiving surface has no specially designed surface chemistries, nor any separate adhesive layers. Alternatively, the receiving surface may have one or more planarization or smoothing layers (e.g. spin-on glass), adhesive layers (e.g. a conformable layer), or functionalized regions (e.g. hydrophilic or hydrophobic regions) to facilitate transfer, assembly and integration of features. Embodiments of this aspect of the present invention, therefore, may further comprise the step of providing one or more adhesive layer or functionalized region(s) on the receiving surface, wherein the feature disposed on the transfer surface contacts the adhesive layer. In an embodiment, the receiving substrate is a material selected from the group consisting of: a polymer, a semiconductor wafer, a ceramic material, a glass, a metal, paper, a dielectric material or any combination of these. In an embodiment the receiving substrate comprises a semiconductor, such as silicon, GaAs or InP. In an embodiment, the receiving substrate comprises a wafer, including a single-crystal wafer.
The receiving substrate may comprise one or more viscoelastic and/or elastomeric adhesive layers exhibiting kinetically controllable adhesive strengths. In one embodiment, a receiving substrate is coated with thin layers of PDMS. In this embodiment, features are transferred to the receiving substrate with efficiencies determined by the rate of separation between a transfer element and the receiving substrate and determined by the thickness of the thin PDMS layer (generally from 10 to 100000 nm). In this embodiment transfer printing efficiency may be best at either high or low rates, depending upon the thickness of the thin PDMS layer.
The receiving substrate may comprise a soft, conformable layer partially or fully coated with gold to accept features in a manner that allows electrical connection to the interface between the features and the receiving substrate. In one embodiment, the features may be coated with gold to allow strong bonding of the features and the receiving substrate by cold-welding of the gold layers joined during printing.
The transfer devices of the present invention include use of a transfer device that is a stamp, a mask, or a mold. In an embodiment, the transfer device comprises a single elastomer layer. In an embodiment, the transfer device comprises multiple elastomer layers. In an embodiment, any of the transfer devices comprise ridged backing to facilitate handling. In an embodiment, the invention further comprises incorporation of an actuator for facilitating surface-feature contact including, but not limited, to an actuator that is a roller printing assembly, or a roller that is a flexographic printer assembly. In an embodiment, the transfer device is moved into contact with a donor/receiving surface. In another embodiment, the receiving/donor surface is moved into contact with the transfer device. In yet another embodiment, both the transfer stamp and the receiving/donor surfaces are both moved into contact with each other.
The present invention is particularly suited for methods of transferring, assembling and/or integrating printable semiconductor elements. In an embodiment, the invention transfers features via contact printing, including dry contact printing. In an embodiment the invention transfers features via registered transfer, assembly and/or integration processes. In an embodiment the invention transferred features coated with layers, optionally sacrificial layers, including but not limited to layers composed of polymeric or dielectric materials, that separate features from the surface of the transfer element in order to avoid possible contamination of the feature by the transfer element.
An advantage of the use of controlled separation rates in the transfer methods of the present invention is that patterns of printable semiconductors elements may be transferred and assembled onto substrate surfaces in a manner preserving selected spatial orientations of semiconductor elements which define the pattern. This aspect of the present invention is particularly beneficial for applications wherein a plurality of printable semiconductor elements are fabricated in well defined positions and relative spatial orientations which directly correspond to a selected device configuration or array of device configurations. Transfer methods of the present invention are capable of transferring, positioning and assembling printable semiconductor elements and/or printable semiconductor containing functional devices including, but not limited to, transistors, optical waveguides, microelectromechanical systems, nanoelectromechanical systems, laser diodes, or fully formed circuits.
Another advantage of the use of controlled separation rates in transfer methods is that the levels of adhesion necessary for the removal of certain relatively strongly bound features from donor substrates (including relatively thick (>2 μm) silicon beams joined to SOI substrates by bridge elements and mica sheets ionically bound across their entire footprint to a mica substrate) can be accomplished without chemical modification of the transfer elements or of the features themselves. As a result, a relatively weakly adhering interface (e.g. one bound by van der Waals forces) may be used to divide, thickness-wise, and print features comprised of layered materials, including mica, graphite, and transition-metal chalcogenides.
In an embodiment, the surface of the transfer element may be treated chemically or physically (e.g. roughened by plasma etching, metallized, oxidized, chemically functionalized) to tune the strength of adhesion of features to the transfer surface. In one embodiment, the strength of adhesion of features to the transfer surface may be increased by treating the transfer element with ozone. In another embodiment, the strength of adhesion of features to the transfer surface may be decreased by depositing a thin metal layer (0.1 to 1000 nm) onto the transfer element.
In another embodiment, the present invention provides selective transfer and assembly methods wherein some, but not all, of the printable semiconductors provided are transferred and assembled onto or into a substrate. In this embodiment, the elastomeric transfer device is capable of binding selectively to specific printable semiconductor elements provided. For example, the elastomeric transfer device may have a selected three dimensional relief pattern on its external surface having recessed regions and relief features. In this embodiment, recessed regions and relief features may be positioned such that only selected printable semiconductor elements are contacted by one or more contact surfaces provided by the relief pattern, and subsequently transferred and assembled onto the substrate surface. Alternatively, the elastomeric transfer device may have a contact surface or plurality of contact surfaces having a selected pattern of binding regions, such as chemically modified regions having hydroxyl groups extending from the contact surface and/or regions having one or more adhesive surface coatings. In this embodiment, only those semiconductor elements that are contacted with the binding regions on the contact surface(s) are bound to the transfer device, and subsequently transferred and assembled onto the substrate surface. In another embodiment, the elastomeric transfer device may have a contact surface or plurality of contact surfaces having a selected pattern of anti-binding regions, such as chemically or physically modified regions having, for example, metallized regions extending from the contact surface and/or regions having one or more anti-adhesive surface coatings. In this embodiment, only those semiconductor elements that are contacted with the regions on the contact surface(s) that are not treated with anti-binding modifications are bound to the transfer device, and subsequently transferred and assembled onto the substrate surface. An advantage of selective transfer and assembly methods of the present invention is that a first pattern of printable semiconductor elements characterized by a first set of positions and spatial orientations may be used to generate a second pattern of printable semiconductor elements different from the first pattern and characterized by a second set of positions and spatial orientations, corresponding to a selected device configuration or array of device configurations. Another advantage of selective transfer and assembly in the present invention is that the methods described herein may be used to distribute features on a given donor substrate to features on a larger receiving substrate by successive repetitions of retrieving the features from the donor using a transfer element suitable for selective transfer and transferring those features onto the larger receiving substrate.
An exemplary elastomeric transfer device of the present invention comprises a dry transfer stamp, such as an elastomeric transfer stamp or composite, multi-layer transfer device or other patterning devices. Elastomeric transfer devices useful for the present invention include transfer devices comprising a plurality of polymer layers as described in U.S. patent application Ser. No. 11/115,954, entitled “Composite Patterning Devices for Soft Lithography”, filed with the U.S. Patent and Trademark Office on Apr. 27, 2005, which is hereby incorporated by reference in its entirety. An exemplary patterning device useable as a transfer device in the methods of the present invention comprises a polymer layer having a low Young's Modulus, such as a poly(dimethylsiloxane) (PDMS) layer, preferably for some applications having a thickness selected from the range of about 1 micron to about 100 microns. Use of a low modulus polymer layer is beneficial because it provides transfer devices capable of establishing good conformal contact with one or more printable semiconductor elements, particularly printable semiconductor elements having curved, rough, flat, smooth and/or contoured exposed surfaces, and capable of establishing good conformal contact with substrate surfaces having a wide range of surface morphologies, such as curved, rough, flat, smooth and/or contoured substrate surfaces.
Optionally, transfer devices of the present invention may further comprise a second layer having an external surface opposite an internal surface, and having a high Young's modulus, such as high modulus polymer layer, ceramic layer, glass layer or metal layer. In this embodiment, the internal surface of the first polymer layer and the internal surface of the second high modulus layer are arranged such that a force applied to the external surface of the second high modulus layer is transmitted to the first polymer layer. Use of a high modulus second polymer layer (or backing layer) in transfer devices of the present invention is beneficial because it provides transfer devices having a net flexural rigidity large enough to provide good binding, transfer and assembly characteristics. For example, use of a transfer device having a net flexural rigidity selected from the range of about 1×10−7 Nm to about 1×10−5 Nm minimizes distortions of the positions of semiconductor elements and/or other structures bound to the contact surface(s) upon establishing conformal contact with a substrate surface. Use of a high modulus, rigid backing layer also is beneficial for preventing degradation of the printable semiconductor elements during transfer, for example by prevent cracking of the printable semiconductor layers. This attribute provides methods and devices of assembling printable semiconductor elements exhibiting high placement accuracy and good pattern fidelity. Transfer devices of the present invention may comprise additional layers, including polymer layers, for providing easy handling and maintenance, good thermal properties and for providing uniform distribution of a force applied to the transfer device to the entire contact surface(s), as taught in U.S. patent application Ser. No. 11/115,954, entitled “Composite Patterning Devices for Soft Lithography, filed with the U.S. Patent and Trademark Office on Apr. 27, 2005 which is incorporated by reference in its entirety herein.
In one aspect, the invention provides a method of transferring a feature from a donor substrate surface to a receiving surface of a receiving substrate, the method comprising: providing an elastomeric transfer device having a transfer surface; providing a donor substrate having a donor surface, the donor surface having at least one feature; contacting at least a portion of the transfer surface with at least a portion of the feature; separating the transfer surface from the donor surface at a first separation rate such that at least a portion of the feature is transferred from the donor surface to the transfer surface, thereby forming the transfer surface having the feature disposed thereon; contacting at least a portion of the feature disposed on the transfer surface with the receiving surface of the receiving substrate; and separating the transfer surface from the feature at a second separation rate, wherein the first separation rate is larger than the second separation rate, thereby transferring the feature to the receiving surface.
In another aspect, the invention provides a method of transferring a feature from a donor substrate surface to a receiving surface of a receiving substrate temporarily for processing, and subsequently removing said feature from said receiving substrate, the method comprising: providing an elastomeric transfer device having a transfer surface; providing a donor substrate having a donor surface, the donor surface having at least one feature; contacting at least a portion of the transfer surface with at least a portion of the feature; separating the transfer surface from the donor surface at a first separation rate such that at least a portion of the feature is transferred from the donor surface to the transfer surface, thereby forming the transfer surface having the feature disposed thereon; contacting at least a portion of the feature disposed on the transfer surface with the receiving surface of the receiving substrate; and separating the transfer surface from the feature at a second separation rate, wherein the first separation rate is larger than the second separation rate, thereby transferring the feature to the receiving surface; processing the feature on the receiving surface; contacting at least a portion of the transfer surface with at least a portion of the feature; separating the transfer surface from the receiving surface at a third separation rate such that at least a portion of the feature is transferred from the receiving surface to the transfer surface, thereby removing the feature from the receiving surface. In an embodiment, the same transfer device is used to apply the feature to the receiving surface and to remove the processed feature from the receiving surface. Alternatively, a different transfer device is used.
In another aspect, the invention provides a method of transferring a feature from a donor substrate surface to a receiving surface of a receiving substrate, and subsequently removing said feature from said receiving substrate if said feature is unwanted on said receiving substrate, the method comprising: providing an elastomeric transfer device having a transfer surface; providing a donor substrate having a donor surface, the donor surface having at least one feature; contacting at least a portion of the transfer surface with at least a portion of the feature; separating the transfer surface from the donor surface at a first separation rate such that at least a portion of the feature is transferred from the donor surface to the transfer surface, thereby forming the transfer surface having the feature disposed thereon; contacting at least a portion of the feature disposed on the transfer surface with the receiving surface of the receiving substrate; and separating the transfer surface from the feature at a second separation rate, wherein the first separation rate is larger than the second separation rate, thereby transferring the feature to the receiving surface; contacting at least a portion of the transfer surface with at least a portion of an unwanted feature; separating the transfer surface from the receiving surface at a third separation rate such that at least a portion of the unwanted feature is transferred from the receiving surface to the transfer surface, thereby removing at least a portion of the unwanted feature from the receiving surface.
In another aspect, the invention provides a method of assembling a printable semiconductor element on a receiving surface of a receiving substrate, the method comprising: providing an elastomeric transfer device having a transfer surface; providing a donor substrate having a donor surface, the donor surface having at least one printable semiconductor element, wherein the printable semiconductor element is connected to the donor substrate via at least one bridge element; contacting at least a portion of the transfer surface with at least a portion of the printable semiconductor element; separating the transfer surface from the donor surface at a first separation rate such that the bridge element is fractured and the printable semiconductor element is transferred from the donor surface to the transfer surface, thereby forming the transfer surface having the printable semiconductor element disposed thereon; contacting at least a portion of the printable semiconductor element disposed on the transfer surface with the receiving surface of the receiving substrate; and separating the transfer surface from the feature at a second separation rate, wherein the first separation rate is larger than the second separation rate, thereby transferring the printable semiconductor element to the receiving surface. Optionally, the present invention provides a method of assembling an array of pattern of printable semiconductor elements on a receiving surface of a substrate.
In another aspect, the invention is a method of transferring a printable semiconductor element from a donor substrate surface to a transfer surface of an elastomeric transfer device, the method comprising: providing an elastomeric transfer device having the transfer surface; providing a donor substrate having a donor surface, the donor surface having the printable semiconductor element; contacting at least a portion of the transfer surface with at least a portion of the printable semiconductor element; separating the transfer surface from the donor surface at a separation rate greater than or equal to about 10 cm second−1 such that at least a portion of the printable semiconductor element is transferred from the donor surface to the transfer surface.
In another aspect, the invention provides a method of transferring an array of printable semiconductor elements from a donor substrate surface to a transfer surface of an elastomeric transfer device, the method comprising: providing an elastomeric transfer device having the transfer surface; providing a donor substrate having a donor surface, the donor surface having the array of printable semiconductor elements; contacting at least a portion of the transfer surface with at least a portion of the array printable semiconductor elements; separating the transfer surface from the donor surface at a separation rate greater than or equal to about 10 cm second−1 such that at least a portion of the array of printable semiconductor elements is transferred from the donor surface to the transfer surface.
The invention may be further understood by the following non-limiting examples. All references cited herein are hereby incorporated by reference to the extent not inconsistent with the disclosure herewith. Although the description herein contains many specificities, these should not be construed as limiting the scope of the invention but as merely providing illustrations of some of the presently preferred embodiments of the invention. For example, thus the scope of the invention should be determined by the appended claims and their equivalents, rather than by the examples given.
In the context of the present invention, the term “transferring” or “transfer” relates to features, materials, structures, device components and/or integrated functional devices that are removed from the surface of one substrate and “printed” or applied to the surface of another substrate.
As used herein, “feature” is used broadly to refer to a material, structure, device component and/or functional device to be transferred, for example via printing techniques such as contact printing. The definition of feature encompasses any element that can be transferred from a donor substrate to a stamp and subsequently printed to a receiving surface including, but not limited to, semiconductor structures, metallic structures, ceramic structures, dielectric structures, composite structures. In some embodiments, features of the present invention are printable semiconductor elements and patterns of printable semiconductor elements. The structure can be a three-dimensional pattern, having a pattern on a surface with a depth and/or height to the pattern. Accordingly, the term feature encompasses geometrical features including, but not limited to, any two-dimensional pattern or shape (circle, triangle, rectangle, square), three-dimensional volume (any two-dimensional pattern or shape having a height/depth), as well as systems of interconnected etched “channels” or deposited “walls.” In an embodiment, a feature comprises a biological material or element. In an embodiment, a feature is globular. A globular feature refers to a generally rounded material, for example, microspheres, seeds and other curved objects. The dimensions of the feature can be microsized, nanosized, or both microsized and nanosized. A microstructure is a feature with a dimension on the order of greater than a micron including millimeters and several millimeters. In an embodiment, the transferred feature comprises a plurality of silicon microstructures. A nanostructure is a feature with a dimension on the order of less than about one micron. In an embodiment, a nanosized feature is less than about 100 nm. A “lateral dimension” refers to a distance that is parallel to the contacting transfer surface and partner surface. A “vertical dimension” refers to the vertical height of the feature relative to the supporting surface.
In an embodiment, the feature comprises “microstructures” and/or “nanostructures.” As used herein the terms “microstructures” and “microsized structures” are used synonymously, and the terms “nanostructures” and “nanosized structures” are used synonymously. As used herein, “nanostructures” refer to structures having at least one dimension that is on the order of nanometers to microns, including in the range of tens of nanometers to hundreds of nanometers. In an embodiment the nanostructure has at least one feature that is on the order of tens of nm or smaller. For example, the width of the structure can be on the order of 10's to 100's of nm and the length can be on the order of microns to 1000's of microns. In an embodiment the nanostructure has one or more features that range from an order of tens of nm to hundreds of nm. As used herein microstructures refer to structures that are larger than nanostructures. In an embodiment, a microstructure has at least one feature physical dimension ranging from about 1 micron to about 5000 microns.
Feature encompasses a layer or a layer portion, wherein the thickness of the layer or layer portion is between an order of nanometers to microns, including, but not limited to, between about 3 nm to 12 nm. Feature transfer can involve transfer of one or more of biologics, chemicals or geometrical elements. A biologic is a feature that has use in a device for studying biological systems and encompasses, DNA, RNA, proteins and polypeptides. A device of the present invention is said to interact with a cell when the device can detect a physical property associated with the cell. In an embodiment, the biologic or chemical is integrated within another feature to facilitate transfer of the biologic or chemical from a donor surface to a transfer device surface, and then to a receiving surface.
A “pattern” refers to a plurality of features that are deposited and/or etched on a donor surface. Accordingly, the term encompasses a plurality of geometrical features etched onto a surface, as well as a plurality of geometrical features deposited onto a surface and a plurality of geometrical features freestanding on a surface. The present methods and system are capable of transfer printing patterns of structures, including the features discussed herein, having well defined and selected physical dimensions, spatial orientations and positions.
“Circuit” refers to a feature that is an electrical network and encompasses integrated circuits and arrays of integrated circuits.
As used herein, “substrate” refers to a material that has at least one surface that contains a feature or at least one surface for receiving a feature. In an embodiment, the surface to receive a feature is smooth, preferably with a roughness less than about 3 nm over a 1 μm2 region.
An “elastomeric transfer device” refers to an elastomeric material having a surface that can receive as well as transfer a feature. Exemplary elastomeric transfer devices include stamps, molds and masks. The transfer device affects and/or facilitates feature transfer from a donor material to a receiver material. “Elastomer” or “elastomeric” refers to a polymeric material which can be stretched or deformed and return to its original shape without substantial permanent deformation. Elastomers commonly undergo substantially elastic deformations. Exemplary elastomers useful in the present invention may comprise, polymers, copolymers, composite materials or mixtures of polymers and copolymers. Elastomeric layer refers to a layer comprising at least one elastomer. Elastomeric layers may also include dopants and other non-elastomeric materials. Elastomers useful in the present invention may include, but are not limited to, thermoplastic elastomers, styrenic materials, olefenic materials, polyolefin, polyurethane thermoplastic elastomers, polyamides, synthetic rubbers, silicon-based organic polymers including polydimethylsiloxane (PDMS), polybutadiene, polyisobutylene, poly(styrene-butadiene-styrene), polyurethanes, polychloroprene and silicones.
“Contact” refers to the configuration of two or more surfaces such that a feature on the surface of one element is capable of transfer to another surface. For example, a stamp or transfer device is in contact with a donor material when a transfer surface facing a donor surface is in physical contact with the donor surface. Similarly, a transfer surface is in contact with a receiver substrate surface when the transfer surface physically contacts the receiver substrate surface. In an embodiment, contact refers to at least a portion of the feature is in physical contact with at least a portion of another surface. In an embodiment, contact refers to substantially all the features on a surface in contact with another surface. Elements are in physical contact when they are observable as touching. Preferably, physical contact occurs under an applied force to ensure uniform and intimate contact over the portion of contacting surfaces.
“Pattern” refers to a pair of surfaces that have regions of physical contact and regions of no physical contact. For example, in the processes disclosed herein, a transfer device of the present invention is said to have a “pattern of contacts” with a donor surface so as to generate an inked transfer surface having a surface with relief features.
The transfer device has mechanical attributes and characteristics, including Young's modulus, compressibility modulus, flexural rigidity, that are optimized as known in the art to ensure suitable structures are obtained from any of the processes disclosed herein. At least a portion of the transfer device is elastomeric and/or viscoelastic so that the adhesive force between a solid object and the transfer device is rate-sensitive. As used herein, “separation” and “peeling” are used synonymously and refer to a process at which a first surface in contact with a second surface is separated from the second surface. Separation may be carried out by vertical displacement, horizontal displacement, displacement initiated from the ends of two surfaces and displacement initiated from the interior of two surfaces. Separation encompasses axis-symmetric and non axis-symmetric (“axis-unsymmetric”) separation, as illustrated in
As used herein, transfer of “substantially all” the features in contact with the transfer surface refers to at least 90%, at least 95% and at least 99% of the features in contact with the transfer surface are transferred.
A “multi-layered feature” refers to sequential printing of features onto a receiving surface so that a first printed layer corresponds to features on a first donor surface and a second printed layer corresponds to a second donor surface. Alternatively, the donor surfaces can be identical, and instead the transfer devices contacts different donor surface locations.
A “substantially constant peeling rate” and a “substantially constant separation rate” are used synonymously and refer to the rate of surface-feature separation that does not significantly vary over the separation or peeling time. “Substantially constant” refers to a rate that does not vary by more than 2% relative to the average separation and/or peeling rate during the separation and/or peel time, including variation of less than 1%.
“Printable” relates to materials, structures, device components and/or integrated functional devices that are capable of transfer, assembly, patterning, organizing and/or integrating onto or into substrates, via printing techniques including but not limited to, contact printing and solution printing.
“Printable semiconductor elements” of the present invention comprise semiconductor structures that are able to be assembled and/or integrated onto substrate surfaces, for example using by dry transfer contact printing and/or solution printing methods. In one embodiment, printable semiconductor elements of the present invention are unitary single crystalline, polycrystalline or microcrystalline inorganic semiconductor structures. In one embodiment, printable semiconductor elements are connected to a substrate, such as a mother wafer, via one or more bridge elements. In this context of this description, a unitary structure is a monolithic element having features that are mechanically connected. Semiconductor elements of the present invention may be undoped or doped, may have a selected spatial distribution of dopants and may be doped with a plurality of different dopant materials, including P and N type dopants. The present invention includes microstructured printable semiconductor elements having at least one cross sectional dimension greater than or equal to about 1 micron and nanostructured printable semiconductor elements having at least one cross sectional dimension less than or equal to about 1 micron. Printable semiconductor elements useful in many applications comprises elements derived from “top down” processing of high purity bulk materials, such as high purity crystalline semiconductor wafers generated using conventional high temperature processing techniques. In one embodiment, printable semiconductor elements of the present invention comprise composite structures having a semiconductor operational connected to at least one additional device component or structure, such as a conducting layer, dielectric layer, electrode, additional semiconductor structure or any combination of these. In one embodiment, printable semiconductor elements of the present invention comprise stretchable semiconductor elements and/or heterogeneous semiconductor elements.
“Supported by a substrate” refers to a structure that is present at least partially on a substrate surface or present at least partially on one or more intermediate structures positioned between the structure and the substrate surface. The term “supported by a substrate” may also refer to structures partially or fully embedded in a substrate.
“Semiconductor” refers to any material that is a material that is an insulator at a very low temperature, but which has a appreciable electrical conductivity at a temperatures of about 300 Kelvin. In the present description, use of the term semiconductor is intended to be consistent with use of this term in the art of microelectronics and electrical devices. Semiconductors useful in the present invention may comprise element semiconductors, such as silicon, germanium and diamond, and compound semiconductors, such as group IV compound semiconductors such as SiC and SiGe, group III-V semiconductors such as AlSb, AlAs, Aln, AlP, BN, GaSb, GaAs, GaN, GaP, InSb, InAs, InN, and InP, group III-V ternary semiconductors alloys such as AlxGa1-xAs, group II-VI semiconductors such as CsSe, CdS, CdTe, ZnO, ZnSe, ZnS, and ZnTe, group I-VII semiconductors CuCl, group IV-VI semiconductors such as PbS, PbTe and SnS, layer semiconductors such as Pbl2, MoS2 and GaSe, oxide semiconductors such as CuO and Cu2O. The term semiconductor includes intrinsic semiconductors and extrinsic semiconductors that are doped with one or more selected materials, including semiconductor having p-type doping materials and n-type doping materials, to provide beneficial electrical properties useful for a given application or device. The term semiconductor includes composite materials comprising a mixture of semiconductors and/or dopants. Specific semiconductor materials useful for in some applications of the present invention include, but are not limited to, Si, Ge, SiC, AlP, AlAs, AlSb, GaN, GaP, GaAs, GaSb, InP, InAs, GaSb, InP, InAs, InSb, ZnO, ZnSe, ZnTe, CdS, CdSe, ZnSe, ZnTe, CdS, CdSe, CdTe, HgS, PbS, PbSe, PbTe, AlGaAs, AlInAs, AlInP, GaAsP, GaInAs, GaInP, AlGaAsSb, AlGaInP, and GaInAsP. Porous silicon semiconductor materials are useful for applications of the present invention in the field of sensors and light emitting materials, such as light emitting diodes (LEDs) and solid state lasers. Impurities of semiconductor materials are atoms, elements, ions and/or molecules other than the semiconductor material(s) themselves or any dopants provided to the semiconductor material. Impurities are undesirable materials present in semiconductor materials which may negatively impact the electrical properties of semiconductor materials, and include but are not limited to oxygen, carbon, and metals including heavy metals. Heavy metal impurities include, but are not limited to, the group of elements between copper and lead on the periodic table, calcium, sodium, and all ions, compounds and/or complexes thereof.
“Conformal contact” refers to contact established between surfaces, coated surfaces, and/or surfaces having materials deposited thereon which may be useful for transferring, assembling, organizing and integrating structures (such as printable semiconductor elements) on a substrate surface, such as a receiving substrate surface. In one aspect, conformal contact involves a macroscopic adaptation of one or more contact surfaces of an elastomeric transfer device to the overall shape of a substrate surface. In another aspect, conformal contact involves a microscopic adaptation of one or more contact surfaces of an elastomeric transfer device to a substrate surface leading to an intimate contact with out voids. The term conformal contact is intended to be consistent with use of this term in the art of soft lithography. Conformal contact may be established between one or more bare contact surfaces of an elastomeric transfer device and a substrate surface. Alternatively, conformal contact may be established between one or more coated contact surfaces, for example contact surfaces having a transfer material, printable semiconductor element, device component, and/or device deposited thereon, of an elastomeric transfer device and a substrate surface. Alternatively, conformal contact may be established between one or more bare or coated contact surfaces of an elastomeric transfer device and a substrate surface coated with a material such as a transfer material, solid photoresist layer, prepolymer layer, liquid, thin film or fluid
“Placement accuracy” refers to the ability of a transfer method or device to transfer a printable element, such as a printable semiconductor element, to a selected position, either relative to the position of other device components, such as electrodes, or relative to a selected region of a receiving surface. “Good placement” accuracy refers to methods and devices capable of transferring a printable element to a selected position relative to another device or device component or relative to a selected region of a receiving surface with spatial deviations from the absolutely correct position less than or equal to 50 microns, more preferably less than or equal to 20 microns for some applications and even more preferably less than or equal to 5 microns for some applications. The present invention provides devices comprising at least one printable element transferred with good placement accuracy.
“Fidelity” refers to a measure of how well a selected pattern of elements, such as a pattern of printable semiconductor elements, is transferred to a receiving surface of a substrate. Good fidelity refers to transfer of a selected pattern of elements wherein the relative positions and orientations of individual elements are preserved during transfer, for example wherein spatial deviations of individual elements from their positions in the selected pattern are less than or equal to 500 nanometers, more preferably less than or equal to 100 nanometers.
“Young's modulus” is a mechanical property of a material, device or layer which refers to the ratio of stress to strain for a given substance. Young's modulus may be provided by the expression;
wherein E is Young's modulus, L0 is the equilibrium length, ΔL is the length change under the applied stress, F is the force applied and A is the area over which the force is applied. In an embodiment, Young's modulus varies with stress. Young's modulus may also be expressed in terms of Lame constants via the equation:
wherein λ and μ are Lame constants. High Young's modulus (or “high modulus”) and low Young's modulus (or “low modulus”) are relative descriptors of the magnitude of Young's modulus in a give material, layer or device. In the present invention, a high Young's modulus is larger than a low Young's modulus, preferably about 10 times larger for some applications, more preferably about 100 times larger for other applications and even more preferably about 1000 times larger for yet other applications.
“Polymer” refers to a molecule comprising a plurality of repeating chemical groups, typically referred to as monomers. Polymers are often characterized by high molecular masses. Polymers useable in the present invention may be organic polymers or inorganic polymers and may be in amorphous, semi-amorphous, crystalline or partially crystalline states. Polymers may comprise monomers having the same chemical composition or may comprise a plurality of monomers having different chemical compositions, such as a copolymer. Cross linked polymers having linked monomer chains are particularly useful for some applications of the present invention. Polymers useable in the methods, devices and device components of the present invention include, but are not limited to, plastics, elastomers, thermoplastic elastomers, elastoplastics, thermostats, thermoplastics and acrylates. Exemplary polymers include, but are not limited to, acetal polymers, biodegradable polymers, cellulosic polymers, fluoropolymers, nylons, polyacrylonitrile polymers, polyamide-imide polymers, polyimides, polyarylates, polybenzimidazole, polybutylene, polycarbonate, polyesters, polyetherimide, polyethylene, polyethylene copolymers and modified polyethylenes, polyketones, poly(methyl methacrylate, polymethylpentene, polyphenylene oxides and polyphenylene sulfides, polyphthalamide, polypropylene, polyurethanes, styrenic resins, sulphone based resins, vinyl-based resins or any combinations of these.
In the context of this description, the expressions “registered transfer”, “registered assembly” and “registered integration” refer to concerted processes that maintain the relative spatial orientation of transferred elements, preferably to with about 50% and more preferably for some application to within about 1%. Registered processes of the present invention may also refer to the ability of methods of the present invention to transfer, assemble and/or integrate printable semiconductor elements to specific regions of a receiving substrate preselected to within 100 microns and preferably for some embodiments to with 50 nanometers
Bridge elements are alignment maintaining elements which connect a feature, such as printable semiconductor elements, to a donor substrate, such as a semiconductor wafer. In one embodiment, a bridge element is a partially or fully undercut structure that connects one or more ends of the feature to a donor substrate. In another embodiment, a bridge element connects the bottom of a feature to the donor substrate. Bridge elements are useful for maintaining selected orientations and/or positions of features, such as printable semiconductor elements, during transfer, assembly and/or integration processing steps. Bridge elements are also useful for maintaining relative positions and orientations of a pattern or array of features, such as printable semiconductor elements, during transfer, assembly and/or integration processing steps. In methods of the present invention, bridge elements preserve the positions and spatial orientations of features, such as printable semiconductor elements, during contact, bonding and transfer processes involving a contact surface of a transfer device, such as a conformable elastomeric stamp, thereby enabling registered transfer from a mother wafer to the transfer device. Bridge elements in this aspect of the present invention are capable of disengaging from the printable semiconductor elements without significantly changing the positions and orientations of the printable semiconductor elements upon contact and/or movement of the transfer device. Disengagement is typically achieved by fracture of the bridge elements during contact and/or movement of the transfer device.
In the following description, numerous specific details of the devices, device components and methods of the present invention are set forth in order to provide a thorough explanation of the precise nature of the invention. It will be apparent, however, to those of skill in the art that the invention can be practiced without these specific details.
This invention provides methods for transferring features, including micropatterns, nanopatterns and a combination of micro and nanopatterns. The present invention provides methods of patterning by elastomeric stamping, to provide relief and/or recess features directly to a surface. The viscoeleastic nature of the surface material on the transfer device leads to a separation force (i.e. the force that can lift objects from a surface) that depends on separation rate. In one useful embodiment, at high separation rates, this force is large enough to remove objects from a substrate and transfer them onto a transfer device, even when the static surface energy of the transfer device is lower than that of the substrate. At low separation rates, this separation force is low. Contacting a transfer device that supports an array of objects against a final substrate and then separating the element away slowly leads to the transfer of these objects from the transfer device to the substrate. The process of controlled separation rates for transfer printing disclosed herein can be used in combination with other transfer approaches, including those transfer approaches described in U.S. patent application Ser. No. 11/145,574 filed Jun. 2, 2005, hereby incorporated by reference.
The physics that governs the kinetic dependence of the adhesion process has its origin in the viscoelastic response of the elastomeric stamp. We performed rolling experiments to yield quantitative information on this dependence for the case of a commercially available polydimethylsiloxane (PDMS) rubber (Sylgard® 184, DowCorning). A slab of PDMS (Dow-Sylgard 184) is cast between two 200 mm silicon wafers separated by about 7 mm using PDMS spacers and cured at 65° C. The wafers are treated with (tridecafluoro-1,1,2,2-tetrahydrooctyl)-1-trichlorosilane (United Chemical Technologies) for 1 h in a vacuum desiccator to facilitate the removal of the PDMS slab. The slab is placed against a sturdy inclined glass plate, the inclination of which is measured relative to a level countertop. A steel cylinder (McMaster-Carr, diameter 12.7 mm, length 75.5 mm, 75.2 g) is placed at the top of the slab and allowed to roll. The slab is cleaned with a lint roller (3M) between successive roll tests. Rolling speed is measured with a ruler and a stopwatch. Video footage is captured and analyzed to confirm that the cylinder rolled against the slab at a constant speed.
In these experiments, a steel cylinder rolling down an inclined slab of PDMS rubber reaches a terminal velocity, where gravity works to separate the steel from the PDMS at the trailing edge of the contact region. The loss in gravitational potential is taken as the adhesion energy hysteresis (the difference between the work required to separate the steel from the PDMS and the energy evolved at the advancing contact edge) at the measured rolling or separation speed v. The energy associated with the advancing contact area at the front of the rolling cylinder is typically small, so the adhesion energy hysteresis is taken as the separation energy, or the energy release rate, G.
Pick-up and printing efficiencies in transfer-printing experiments follow a similar trend qualitatively. When a PDMS stamp delaminates slowly from a substrate that supports microstructures, the separation energy GPDMS for the elastomer-microstructure interface is smaller than its counterpart Gsubstrate for the interface between the microstructures and the substrate. Consequently the elastomer-microstructure interface breaks more easily than the microstructure-substrate interface. However, the separation energy GPDMS depends strongly on the speed of delamination (or “separation rate”), v (see, for example,
GPDMS=G0[1+φ(v)]
where φ is an increasing function of v and G0 is a constant.
In contrast, the separation energy for the microstructure-substrate interface Gsubstrate is typically independent of rate. As the speed of delamination increases, GPDMS increases relative to Gsubstrate until the elastomer-microstructure interface becomes strong enough to break the microstructure-substrate interface. Determining which interface fails depends on the geometry of the microstructures and can be established by energy-based arguments similar to those used to compare competing fracture modes in layered materials. Geometrical design considerations can be useful in guiding the transfer of microstructures, for example by providing stress concentration zones to facilitate controlled fracture or by engineering contact zone areas to alter levels of adhesion. A key concept for the transfer-printing criteria is the strongly rate-dependent separation energy of solid objects from an elastomer and the rate-independent separation of solid objects from a substrate interface.
The effect of separation speed on efficiency of feature removal is shown in
The present invention encompasses methods that transfer prints a plurality of structures from a donor substrate surface to a receiving substrate surface. For example,
Unlike wafer-bonding approaches to semiconductor materials integration, the printing processes disclosed herein have the potential for area multiplication, where a single donor substrate of a given area supplies microstructures to several receiving substrates of the same area or a single receiving substrate with a substantially larger area. This capability is important when the printed material is costly and where large-area, sparse coverage is desired. GaN microstructures (prepared as described hereinbelow) and printed onto silicon (100), as shown in
As the transfer process is purely additive, an embodiment of the present invention encompasses repeated printing. Such repeated printing steps, results in easy fabrication of large-area or even multilayer assemblies (
The invention encompasses printing larger sizes (e.g. 100 μm×100 μm×2.5 μm). Such printing size is useful for structures to support elaborate circuits (
The present invention provides reliable printing without the use of conventional adhesives or specialized surface chemistries. This is important in the context of wafer-based microstructure printing because it allows moderate-to-high-temperature processing (˜150° C. and above) and good electrical contact between the printed structure and the receiving substrate. Printed p-n junctions formed by transferring n-type silicon microstructures to a p-type silicon substrate (
The strong adhesion of features to the stamp at high separation rates is essential to achieve reliable, high-yield printing of the classes of objects illustrated in Example 1. This adhesion can be sufficiently strong, in fact, to remove material structures that are ionically bonded to the donor substrate along their entire lengths.
The transfer devices disclosed herein can pick-up and release, for example, highly non-planar, globular structures, such as silica microspheres (
The transfer printing processes disclosed herein have many applications in established technologies: its unusual capabilities create other device opportunities. To illustrate one such capability, silicon structures and photodiodes are printed onto the curved surfaces of lenses. Non-planar printing proceeds by rolling a cylindrical substrate across, or by pressing a spherical substrate against, a flat, compliant stamp.
Donor Substrate Preparation: In an embodiment, silicon microstructures are generated from SOI wafers (Shin-Etsu, top silicon 3.0 μm, buried oxide 1.1 μm, n-type resistivity 5-20 Ωcm; or Soitec, top silicon 100 nm, buried oxide 200 nm, p-type) patterned by conventional photolithography and phase-shift photolithography27 with Shipley 1805 photoresist (PR). The top silicon is etched by SF6 plasma (30 mtorr, 40 s.c.c.m. SF6, 50W) using PR as an etch mask or by aqueous KOH (20 wt %, 100° C.) using an etch mask of Ti/Au (3/30 nm) deposited by electron-beam evaporation. Ti/Au etch masks are removed after KOH etching using KI/I2 (2.67/0.67 wt %) in water. The buried oxide is then etched in concentrated HF.
GaN microstructures are generated from a GaN-on-silicon (111) wafer (Nitronex). The nitride is etched in an inductively coupled plasma reactive ion etcher (3 mtorr, 15 s.c.c.m. Cl2, 5 s.c.c.m. Ar, −100 V bias) using PECVD SiOx (500 nm) and Cr (150 nm) as an etch mask. Microstructures are then undercut by etching the silicon in aqueous KOH (20 wt %, 100° C.).
Mica (grade V-1, Structure Probe) is softened in an inductively coupled plasma reactive ion etcher (3 mtorr, 15 s.c.c.m. BCl3, 5 s.c.c.m. Ar, −90 V bias) using electron-beam evaporated Cr (100 nm) and PR as a mask. Unpatterned grade V-1 mica and graphite substrates (grade SPI-1, Structure Probe) are used as-received.
Silica microsphere films are prepared by casting droplets of IPA and an aqueous suspension of microspheres onto a silicon wafer and allowing them to dry. Pollen films are also prepared by suspension casting and drying on a silicon wafer.
PDMS Transfer Preparation: PDMS stamps (Dow-Sylgard 184) are cast against flat substrates (for example, polystyrene petri dishes, Fisher Scientific) and cut to dimensions typically about 2 cm×2 cm×7 mm thick. Stamps are laminated against donor substrates such that conformal contact is achieved and subsequently removed manually in a peeling manner such that the delamination front traveled at 10 cm/s or faster. The stamps thus ‘inked’ with objects from the donor are then laminated against receiving substrates and subsequently removed by slow (about 1 mm/s) manual separation or peeling to complete the transfer-printing process.
Printed Junction Diode Fabrication: SOI chips (Shin-Etsu) are heavily n-doped at the top surface with spin-on-dopant (Zhue et al.) (P509, Filmtronics) and activation at 950° C. for 5 s. Microstructures generated as described above are printed onto boron-doped test-grade silicon chips (Montco, resistivity 1-100 Ωcm). Before printing, the receiving substrate is dipped in about 1% HF to remove native oxide, rinsed with deionized water and dried in N2. The printed junction is then annealed for 2 min at 600° C. in N2. Metal contacts are defined by photolithography with Shipley 1818 and lift-off of electron-beam-evaporated Al/Au (20/50 nm). The contacts are made non-rectifying by 4 min of annealing at 500° C.
Photodiode Fabrication Silicon photodiodes are generated from an n-type SOI wafer (Shin-Etsu) with selected areas highly n-doped (P509, Filmtronics) and other areas highly p-doped (B-75×, Honeywell). Doped regions are defined using windows in a spin-on glass (700B, Filmtronics) and the dopants are activated by annealing as described above (Zhu et al.) for the printed junction fabrication, first n-type, then p-type. Structures are subsequently micromachined using SF6 plasma and undercut with HF.
Another aspect of the invention is using the elastomeric and/or viscoelastic transfer devices of the present invention to transfer layers, wherein the depth or thickness of the transferred layer is kinetically controllable (
The composition of the transfer layer is a material that comprises layers including, but not limited to, graphite, graphene and mica. The layers can have a structure comprising a series of repeating planar layers, as for graphite, wherein the layers are bound by van der Waals interactions. The present methods are also useful for transferring material and structures from materials comprising a series of nonplanar layers. The layers can also be bound by any one or more of other forces, including London, hydrogen bonding, covalent bonding and ionic bonding. The magnitude of bonding between layers will affect the separation rate required to lift-off a layer of a certain depth, with layers having stronger adhesion requiring higher separation rates.
The depth of the lift-off pattern or layer(s) depends on a number of factors, including: (i) the physical dimension of the masked region; (ii) the composition of the pattern; (iii) the etching or chemical alternation system employed; and (iv) the kinetic rate or separation rate of the transfer device from the donor surface containing the pattern, with faster pull-off rates resulting in a larger number of layers that lift-off and are transferred to the transfer surface device.
All references cited throughout this application, for example patent documents including issued or granted patents or equivalents; patent application publications; and non-patent literature documents or other source material are hereby incorporated by reference herein in their entireties, as though individually incorporated by reference, to the extent each reference is at least partially not inconsistent with the disclosure in this application (for example, a reference that is partially inconsistent is incorporated by reference except for the partially inconsistent portion of the reference).
Every formulation or combination of components described or exemplified herein can be used to practice the invention, unless otherwise stated.
Whenever a range is given in the specification, for example, a temperature range, a size range, a conductivity range, a time range, or a composition or concentration range, all intermediate ranges and subranges, as well as all individual values included in the ranges given are intended to be included in the disclosure. It will be understood that any subranges or individual values in a range or subrange that are included in the description herein can be excluded from the claims herein. All patents and publications mentioned in the specification are indicative of the levels of skill of those skilled in the art to which the invention pertains. References cited herein are incorporated by reference herein in their entirety to indicate the state of the art as of their publication or filing date and it is intended that this information can be employed herein, if needed, to exclude specific embodiments that are in the prior art.
As used herein, “comprising” is synonymous with “including,” “containing,” or “characterized by,” and is inclusive or open-ended and does not exclude additional, unrecited elements or method steps. As used herein, “consisting of” excludes any element, step, or ingredient not specified in the claim element. As used herein, “consisting essentially of” does not exclude materials or steps that do not materially affect the basic and novel characteristics of the claim. In each instance herein any of the terms “comprising”, “consisting essentially of” and “consisting of” may be replaced with either of the other two terms. The invention illustratively described herein suitably may be practiced in the absence of any element or elements, limitation or limitations which is not specifically disclosed herein.
One of ordinary skill in the art will appreciate that starting materials, materials, reagents, synthetic methods, purification methods, analytical methods, assay methods, and methods other than those specifically exemplified can be employed in the practice of the invention without resort to undue experimentation. All art-known functional equivalents, of any such materials and methods are intended to be included in this invention. The terms and expressions which have been employed are used as terms of description and not of limitation, and there is no intention that in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the appended claims.
This application is a continuation-in-part of U.S. patent application Ser. Nos. 11/145,542, filed Jun. 2, 2005 and U.S. patent application Ser. No. 11/145,574, filed Jun. 2, 2005, both of which claim the benefit under 35 U.S.C. 119(e) of U.S. Provisional Patent Application Nos. 60/577,077, 60/601,061, 60/650,305, 60/663,391 and 60/677,617 filed on Jun. 4, 2004, Aug. 11, 2004, Feb. 4, 2005, Mar. 18, 2005, and May 4, 2005, respectively, all of which are hereby incorporated by reference in their entireties to the extent not inconsistent with the disclosure herein.
This invention was made, at least in part, with United States governmental support awarded by National Science Foundation under grant DMI-0328162, DARPA-funded AFRL-managed Macroelectronics Program Contract FA8650-04-C-7101, the US Department of Energy under grant DEFG02-91-ER45439. The United States government has certain rights in this invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4761335 | Aurichio et al. | Aug 1988 | A |
| 4766670 | Gazdik et al. | Aug 1988 | A |
| 5545291 | Smith et al. | Aug 1996 | A |
| 5772905 | Chou | Jun 1998 | A |
| 5783856 | Smith et al. | Jul 1998 | A |
| 5817242 | Biebuyck et al. | Oct 1998 | A |
| 5824186 | Smith et al. | Oct 1998 | A |
| 5904545 | Smith et al. | May 1999 | A |
| 6225149 | Gan et al. | May 2001 | B1 |
| 6274508 | Jacobsen et al. | Aug 2001 | B1 |
| 6281038 | Jacobsen et al. | Aug 2001 | B1 |
| 6291896 | Smith | Sep 2001 | B1 |
| 6316278 | Jacobsen et al. | Nov 2001 | B1 |
| 6334960 | Wilson et al. | Jan 2002 | B1 |
| 6380729 | Smith | Apr 2002 | B1 |
| 6403397 | Katz | Jun 2002 | B1 |
| 6417025 | Gengel | Jul 2002 | B1 |
| 6420266 | Smith et al. | Jul 2002 | B1 |
| 6468638 | Jacobsen et al. | Oct 2002 | B2 |
| 6479395 | Smith et al. | Nov 2002 | B1 |
| 6527964 | Smith et al. | Mar 2003 | B1 |
| 6555408 | Jacobsen et al. | Apr 2003 | B1 |
| 6566744 | Gengel | May 2003 | B2 |
| 6580151 | Vandeputte et al. | Jun 2003 | B2 |
| 6586338 | Smith et al. | Jul 2003 | B2 |
| 6590346 | Hadley et al. | Jul 2003 | B1 |
| 6606079 | Smith | Aug 2003 | B1 |
| 6606247 | Credelle et al. | Aug 2003 | B2 |
| 6608370 | Chen et al. | Aug 2003 | B1 |
| 6623579 | Smith et al. | Sep 2003 | B1 |
| 6655286 | Rogers | Dec 2003 | B2 |
| 6657289 | Craig et al. | Dec 2003 | B1 |
| 6665044 | Jacobson et al. | Dec 2003 | B1 |
| 6683663 | Hadley et al. | Jan 2004 | B1 |
| 6693384 | Vicentini et al. | Feb 2004 | B1 |
| 6723576 | Nozawa et al. | Apr 2004 | B2 |
| 6730990 | Kondo et al. | May 2004 | B2 |
| 6731353 | Credelle et al. | May 2004 | B1 |
| 6780696 | Schatz | Aug 2004 | B1 |
| 6814898 | Deeman et al. | Nov 2004 | B1 |
| 6816380 | Credelle et al. | Nov 2004 | B2 |
| 6844673 | Bernkopf | Jan 2005 | B1 |
| 6848162 | Arneson et al. | Feb 2005 | B2 |
| 6850312 | Jacobsen et al. | Feb 2005 | B2 |
| 6863219 | Jacobsen et al. | Mar 2005 | B1 |
| 6864435 | Hermanns et al. | Mar 2005 | B2 |
| 6864570 | Smith | Mar 2005 | B2 |
| 6872645 | Duan et al. | Mar 2005 | B2 |
| 6878871 | Scher et al. | Apr 2005 | B2 |
| 6949199 | Gauzner et al. | Sep 2005 | B1 |
| 6949206 | Whitford | Sep 2005 | B2 |
| 7169669 | Blakers et al. | Jan 2007 | B2 |
| 7195733 | Rogers et al. | Mar 2007 | B2 |
| 7255919 | Sakata et al. | Aug 2007 | B2 |
| 7374968 | Kornilovich et al. | May 2008 | B2 |
| 7521292 | Rogers et al. | Apr 2009 | B2 |
| 7557367 | Rogers et al. | Jul 2009 | B2 |
| 7622367 | Nuzzo et al. | Nov 2009 | B1 |
| 20030006527 | Rabolt et al. | Jan 2003 | A1 |
| 20030178316 | Jacobs et al. | Sep 2003 | A1 |
| 20030227116 | Halik et al. | Dec 2003 | A1 |
| 20040005723 | Empedocles et al. | Jan 2004 | A1 |
| 20040026684 | Empedocles et al. | Feb 2004 | A1 |
| 20040079464 | Kumakura | Apr 2004 | A1 |
| 20040095658 | Buretea et al. | May 2004 | A1 |
| 20040112964 | Empedocles et al. | Jun 2004 | A1 |
| 20040136866 | Pontis et al. | Jul 2004 | A1 |
| 20040146560 | Whiteford et al. | Jul 2004 | A1 |
| 20040178390 | Whiteford | Sep 2004 | A1 |
| 20040192082 | Wagner et al. | Sep 2004 | A1 |
| 20040206448 | Dubrow | Oct 2004 | A1 |
| 20040250950 | Dubrow | Dec 2004 | A1 |
| 20050038498 | Dubrow et al. | Feb 2005 | A1 |
| 20050238967 | Rogers et al. | Oct 2005 | A1 |
| 20060038182 | Rogers et al. | Feb 2006 | A1 |
| 20060127817 | Ramanujan et al. | Jun 2006 | A1 |
| 20060134893 | Savage et al. | Jun 2006 | A1 |
| 20060244105 | Forbes et al. | Nov 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 2002092984 | Mar 2002 | JP |
| 367570 | Aug 1999 | TW |
| 494257 | Jul 2002 | TW |
| 0046854 | Aug 2000 | WO |
| 0049421 | Aug 2000 | WO |
| 0049658 | Aug 2000 | WO |
| 0055915 | Sep 2000 | WO |
| 0055916 | Sep 2000 | WO |
| 0133621 | May 2001 | WO |
| 0227701 | Apr 2002 | WO |
| 0243032 | May 2002 | WO |
| 02097708 | Dec 2002 | WO |
| 02097724 | Dec 2002 | WO |
| 03032240 | Apr 2003 | WO |
| 03049201 | Jun 2003 | WO |
| 03063211 | Jul 2003 | WO |
| 03085700 | Oct 2003 | WO |
| 03085701 | Oct 2003 | WO |
| 03092073 | Nov 2003 | WO |
| 2004003535 | Jan 2004 | WO |
| 2004022637 | Mar 2004 | WO |
| 2004022714 | Mar 2004 | WO |
| 2004023527 | Mar 2004 | WO |
| 2004024407 | Mar 2004 | WO |
| 2004027822 | Apr 2004 | WO |
| 2004032190 | Apr 2004 | WO |
| 2004032191 | Apr 2004 | WO |
| 2004032193 | Apr 2004 | WO |
| 2004034025 | Apr 2004 | WO |
| 2004086289 | Oct 2004 | WO |
| 2004094303 | Nov 2004 | WO |
| 2004100252 | Nov 2004 | WO |
| 2004099068 | Dec 2004 | WO |
| 2004105456 | Dec 2004 | WO |
| 2005005679 | Jan 2005 | WO |
| 2005015480 | Feb 2005 | WO |
| 2005017962 | Feb 2005 | WO |
| 2005022120 | Mar 2005 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20090199960 A1 | Aug 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60577077 | Jun 2004 | US | |
| 60601061 | Aug 2004 | US | |
| 60650305 | Feb 2005 | US | |
| 60663391 | Mar 2005 | US | |
| 60677617 | May 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11145542 | Jun 2005 | US |
| Child | 11423192 | US | |
| Parent | 11145574 | Jun 2005 | US |
| Child | 11145542 | US |