Claims
- 1. A photographic element comprised of a reflective or diffusely transmissive support, and coated on said support,
- at least one radiation-sensitive silver halide emulsion layer,
- characterized in that said support is comprised of a continuous polyester phase having dispersed therein microbeads of cellulose acetate which are at least partially bordered by void space, said microbeads of cellulose acetate being present in an amount of 10-30% by weight based on the weight of said polyester, said void space occupying 2-50% by volume of said support, said polyester having an I.V. of at least 0.55 and said cellulose acetate having an acetyl content of about 28-44.8% by weight, a viscosity of about 0.02-90 seconds and the microbeads thereof having an average diameter of about 0.1-50 microns.
- 2. A photographic element according to claim 1 further characterized in that said support is comprised of a continuous polyester phase having dispersed therein microbeads of cellulose acetate which are at least partially bordered by void space, said microbeads of cellulose acetate being present in an amount of 10-30% by weight based on the weight of said polyester, said void space occupying 2-50% by volume of said support, said polyester having an I.V. of at least 0.55 and said cellulose acetate having an acetyl content of about 28-44.8% by weight, a viscosity of about 0.02-90 seconds and the microbeads thereof having an average diameter of about 0.1-50 microns, the composition of said support when consisting only of said polyester continuous phase and said microbeads at least partially bordered by void space characterized by having a Kubelka-Munk R value (infinite thickness) of 0.90 to 1.0 and the following Kubelka-Munk values when formed into a 3 mil (76.2 micron) thick film:
- ______________________________________ Opacity 0.78 to 1.0 SX 25 or less KX 0.001 to 0.2 T(i) 0.02 to 1.0______________________________________
- 3. A photographic element according to claim 2 further characterized in that said polyester is poly(ethylene terephthalate) having an I.V. of at least 0.55.
- 4. A photographic element according to claim 2 further characterized in that said void spaces completely encircle said microbeads.
- 5. A photographic element according to claim 2 further characterized in that said void spaces surround said microbeads, said void spaces being oriented such that they lie in generally the same or parallel planes.
- 6. A photographic element according to claim 2 further characterized in that said support is a sheet of 0.10-20 mils (2.54-508 microns) thickness.
- 7. A photographic element according to claim 1 further characterized in that said support is a paper-like sheet having a continuous phase of poly(ethylene terephthalate) having dispersed therein microbeads of cellulose acetate encircled by void space when viewed in a direction perpendicular to the plane of the sheet,
- (a) said poly(ethylene terephthalate) having a Tg of 60.degree.-100.degree. C. and an I.V. of at least 0.55,
- (b) said cellulose acetate having an acetyl content of about 28 to 44.8% by weight, a viscosity of about 0.01-90 seconds, and a Tg of at least 20.degree. C. higher than the Tg of said poly(ethylene terephthalate),
- (c) said microbeads having an average diameter of about 0.1-50 microns and being present in an amount of about 10-30% by weight based on the weight of said poly(ethylene terephthalate),
- (d) said void space occupying about 2-50% by volume of said sheet, and
- (e) said sheet when consisting only of said polyester continuous phase and said microbeads at least partially bordered by void space characterized by having a Kubelka-Munk R value (infinite thickness) of about 0.90 to about 1.0 and the following Kubelka-Munk values when formed into a 3 mil (76.2 microns) thick film:
- ______________________________________Opacity about 0.78 to about 1.0SX 25 or lessKX about 0.001 to 0.2T(i) about 0.02 to 1.0______________________________________
- 8. A photographic element comprised of
- a reflective or diffusely transmissive support and, coated on said support,
- at least one radiation-sensitive silver halide emulsion layer,
- characterized in that said support is comprised of a continuous polyester phase having dispersed therein microbeads of cellulose acetate which are at least partially bordered by void space, said microbeads of cellulose acetate being present in an amount of 10-30% by weight based on the weight of said polyester, said void space occupying 2-50% by volume of said support, said polyester having an I.V. of at least 0.55 and said cellulose acetate having an acetyl content of about 28 to 44.8% by weight, a viscosity of about 0.01 to 90 seconds, and the microbeads thereof having an average diameter of about 0.1 to 50 microns.
Parent Case Info
This is a continuation-in-part of U.S. Ser. No. 47,821, filed May 5, 1987 now U.S. Pat. No. 4,770,931, issued Sept. 13, 1988.
US Referenced Citations (4)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
47821 |
May 1987 |
|