Photosensitive black matrix

Abstract

A spin coatable, photosensitive black matrix coating having high surface resistivity and exhibiting an optical density greater than 3 at film thicknesses of ≦1 micron has been developed for flat panel display applications where a chrome/chrome oxide black matrix is usually employed. It possesses excellent thermal, light, and chemical stability and good shelf life. It is deposited and patterned by a simple photolithographic processes excellent thermal, light, and chemical stability and good shelf life. It is deposited and patterned by a simple photolithographic process, thereby reducing the cost of processing in relation to chrome/chrome oxide black matrix fabrication processes.

Description

FIELD OF THE INVENTION

[0002] The present invention relates to black matrix coating compositions, and particularly those which, after deposition, can be photolithographically patterned at high resolution.

BACKGROUND OF THE INVENTION

[0003] Flat panel displays use an optically opaque black matrix structure around the light-emitting elements to improve display contrast. Display manufacturers have relied primarily on vacuum-deposited chrome/chrome oxide materials for forming thin (<1 μm) black matrix structures with high optical density (>3) and high volume resistivity (>108 ohm-cm). Such processes are described, for example, in U.S. Pat. Nos. 5,378,274 to Yokoyama et al.; 5,587,818 to S. Lee; and 5,592,317 to Fujikawa et al. However, there is a strong desire on the part of the industry to replace chromium-based materials with lower cost, easily patternable organic black matrix coatings which, unlike chromium materials, pose little or no threat to the environment.

[0004] A host of organic black matrix materials have been demonstrated over the past ten years. Latham et al., in U.S. Pat. No. 4,822,718 and Shimamura et al. in U.S. Pat. No. 5,176,971 disclosed dyed black matrix compositions containing a polyimide precursor binder. However, these compositions suffered from certain drawbacks, e.g., short storage life, relatively low optical density (after deposition), poor thermal stability, and fading resistance. The dye based compositions ere also prone to dye leaching from the composition during subsequent processing steps. The coatings were not inherently photoimageable, and therefore could not be patterned without a separate photoresist layer.

[0005] A variety of pigment-dispersed (as distinguished from “dye-based”) black matrix coating systems were developed to achieve higher optical density, improved thermal stability, and greater resistance to both fading and chemical attack. None of these compositions met the full requirements for a thin, high optical density black matrix system with high electrical resistivity. The various systems are discussed below.

[0006] U.S. Pat. No. 5,251,071 to Kusukawa et al. described black-pigmented polyimide precursor compositions. Though improved thermal stability and optical density of the black matrix was achieved over dyed systems, the compositions required separate application of a photoresist for patterning and had short shelf lives stemming from the use of the polyimide precursor binder.

[0007] Photosensitive, carbon black filled compositions were developed to simplify black matrix deposition and further increase optical density. For example, Hesler et al., in the article “Pigment-dispersed organic black matrix photoresists for LCD color filters” (SID Digest, vol. 26, p. 446, 1995), disclosed that carbon black dispersed in a photosensitive acrylic polymer provided an average optical density of 2.8 for a film thickness of 1.5 μm, however, the composition showed poor coating properties and poor image quality. Similar results were reported by Hasumi et al. in the article, “Carbon dispersed organic black matrix on thin film transistor”, (Proc. of Int. Display Res. Conf. (EuroDisplay-96), vol. 16, p. 237, 1996).

[0008] U.S. Pat. No. 5,718,746 by Nagasawa et al. also disclosed carbon black filled compositions. Nagasawa therein reported that if the pigment concentration exceeded 30% in the coating, the stability of the dispersion was poor. Also, the high conductivity of the high carbon black loading in the coating was desirable for Nagasawa's purposes.

[0009] The use of carbon black to obtain high optical density in thin films invariably creates a trade-off with black matrix resistivity. Accordingly these materials have found acceptable utility only where carbon black's conductivity can be tolerated. Our co-pending U.S. patent application Ser. No. 08/982,233, for example, describes an improved carbon black filled coating for use in such situations.

[0010] Japanese Patent application 9-166869 (unexamined) by Tokyo Ohka Kogyo Co., Ltd. describes a black matrix composition where carbon black pigment particles are coated with a polymer layer to reduce their conductivity. This coating carbon black is then dispersed in a photoresist resin system to form the black matrix composition. Although the cured coatings show high resistivity, the optical density is only about half of what is required for a chrome black matrix replacement.

[0011] photosensitive black matrix coating compositions comprising nonconductive organic and inorganic pigments, sometimes in admixture with carbon black, have been developed recently to simultaneously achieve medium optical density, easy patternability, and high volume resistivity at film thicknesses of 1.5-2.0 microns. For example, U.S. Pat. No. 5,368,976 by Tajima et al. discloses pigment-dispersed color filter compositions useful for the production of LCD and charged coupled devices. The molecular weight of the copolymer binder has to be carefully controlled to obtain good image quality. Japanese Patent application 8-34923 (unexamined) by Sekisui Chemical Industries, Ltd. discloses a two-step black matrix process wherein a photosensitive, pigmented black layer is deposited on the substrate, patterned, and then further colored by diffusing a black dye into the patterns. This process is too cumbersome for commercial use. Japanese Patent application 8-36257 (unexamined) by Sekisui Chemical Industries, Ltd. describes black matrix coating compositions which use silica-coated metal oxide pigments to reduce the conductivity of the pigment particles. They claim to achieve resistivities greater than 106 ohm-cm. However resistivity of 108 ohm-cm is necessary to fulfill the requirements for a chrome black matrix replacement, therefore it is doubtful these compositions can be used at ≦1 micron film thicknesses. Related compositions with improved shelf life are described, for example, in U.S. Pat. Nos. 5,626,796 to Tsujimura et al.; 5,639,579 to Hayashi et al.; and 5,714,286 to Uchikawa et al. However, none of these shelf life-improved compositions exhibit the high optical density which is achieved by chrome black matrix systems. Therefore, the pigment dispersed systems, until now, have not met the more demanding requirements for black matrix systems which chrome seems to satisfy.

[0012] Titanium black, a metal oxide pigment, is treated with an organosilane or reactive silicone agent to reduce its conductivity in the black matrix coating composition disclosed in Japanese Patent application 9-54431 (unexamined) by Nippon Kayaku Co.l, Ltd. However resistivity of this composition is 105 ohm-cm which is not a high enough resistivity to fulfill the requirements for chrome black matrix compositions.

[0013] An easily applied, photodefinable organic black matrix coating complete with other critical performance characteristics would represent a welcomed advancement in the art and satisfy a long felt need.

SUMMARY OF INVENTION

[0014] The principal object of the present invention is to provide an improved photodefinable black matrix coating which negates the need for a photoresist and which exhibits high optical density and high volume resistivity when applied at film thicknesses of ≦1 micron.

[0015] A second object of the present invention is to provide improved processes for making and using the above-described coating composition to construct flat panel displays and other optoelectronic devices requiring light-blocking layers.

[0016] A further object of the present invention is to provide a more environmentally acceptable yet more efficient black matrix system than chrome/chrome oxide.

[0017] We have discovered that these objectives are met by a black matrix coating containing (a) a photosensitive binder system, (b) at last one silica-coated black metal oxide pigment which has been pretreated with a silane coupling agent, and (c) a pre-determined solvent-soluble dye.

[0018] The organic black matrix of the present invention generally is characterized by the following performance properties:

[0019] 1. optical density≧3 across the 400-700 nm optical wavelength region when applied at film thicknesses of ≧1 micron;

[0020] 2. high volume resistivity, >108 ohm-cm;

[0021] 3. excellent coating quality; that is having no particles or pinholes observable by light microscopy;

[0022] 4. adequate shelf life (of 3 months under refrigeration and >1 week at room temperature);

[0023] 5. high thermal stability, ΔEab>3 after heating at 230° C. for 7 hrs in air (See FIG. 7);

[0024] 6. high fading resistance, ΔEab<3 after 108 lux-hrs illumination with simulated solar radiation (See FIG. 8);

[0025] 7. photodefinable characteristics without the need for a separate photoresist material.

BRIEF DESCRIPTION OF THE DRAWINGS

[0026] FIG. 1 is a flow chart explaining the method of use for the black matrix coating composition of the present invention.

[0027] FIG. 2 is the optical transmission spectra of a 1 μm-thick cured film of the coating composition prepared in Example 1.

[0028] FIG. 3 is a graph showing the optical absorbance spectra of a 1 μm-thick cured film of the coating composition prepared in Example 1, where optical density is defined as the absorbance (A) of the coating layer at 540 nm.

[0029] FIG. 4 is a photomicrograph of a resolution dagger feature on the test mask used to evaluate the lithographic properties of the black matrix coating of Example 1.

[0030] FIG. 5 is a scanning electron microphotograph of the surface of a cured film of the coating composition prepared in Example 1.

[0031] FIG. 6 is a graph illustrating the typical surface roughness of a cured film of the coating composition prepared in Example 1.

[0032] FIG. 7 shows the change in percent transmittance across the visible spectrum for a one micron-thick coating of the Example 1 composition when it was baked at 230° C. for increasing amounts of time. The ΔEab (thermal stability) calculated from the spectral data after 7 hours baking was 1.9.

[0033] FIG. 8 shows the change in percent transmittance across the visible spectrum for a one micron-thick coating of the Example 1 composition when it was exposed to artificial solar radiation at a cumulative dosage of one million lux-hrs. The ΔEab (fading resistance) calculated from the spectral data was 1.23

DETAILED DESCRIPTION OF THE INVENTION

[0034] The improved black matrix coatings are comprised of the following constituents:

[0035] a) a photopolymerizable binder system;

[0036] b) silica-coated metal oxide pigment(s);

[0037] c) a silane coupling agent;

[0038] d) a free-radical generating photoinitiator or photoinitiator system;

[0039] e) a solvent vehicle with drying characteristics suitable for spin coating on glass and semiconductor substrates; and

[0040] f) a solvent-soluble organic dye(s) present at less than 3 wt. % based on dry pigment solids

[0041] The binder system preferably comprises a) an alkali-soluble copolymer containing acrylic or methacrylic acid and b) a polyfunctional acrylate or methacrylate co-monomer or mixture of co-monomers.

COMPONENTS OF THE COMPOSITION

[0042] a. Binder System

[0043] The alkali-soluble polymer binder is preferably a vinyl polymer or copolymer containing acrylic or methacrylic acid or other ethylenically unsaturated monomers having carboxylic acid, sulfonic acid, sulfonamide, phenolic, or other functional groups which are capable of conferring solubility in aqueous bases to the binder. Especially preferred polymer binders are copolymers formulated from (a.) one or more of the above-described acidic monomers, particularly the methacrylic acid or acrylic acid monomer and (b.) one or more non-acidic (meth)acrylic monomers. The desired level of acidic monomer in the especially preferred copolymer binder is an amount which effectively allows residue-free wet etching of the overall black matrix composition in traditional alkaline developer solutions during photoimaging, i.e. patterning. Our especially preferred polymer binder of this type, for use in the present invention, is a copolymer comprising about 70 mole % benzyl methacrylate and about 30 mole % methacrylic acid.

[0044] The acrylic co-monomer component of the binder system will have at least one ethylenically unsaturated double bond capable of free radical-initiated photopolymerization which facilitates highly effective patterning. The use of a co-monomer or a mixture of co-monomers having two or more ethylenically unsaturated double bonds per molecule is even more preferred for purposes of obtaining high photospeed and good resolution. Examples of suitable co-monomers include widely-known (meth)acrylate esters such as 2-hydroxyethyl (meth)acrylate, hydroxypropyl methacrylate, benzyl methacrylate, isobutyl (meth)acrylate, and phenyl (meth)acrylate, and the like. Also suitable are ethylene glycol dimethacrylate, pentaerythritol triacrylate and tetraacrylate; dipentaerythritol pentaacrylate and hexaacrylate; polyester (meth)acrylates obtained by reacting (meth)acrylic acid with polyester prepolymers; urethane (meth)acrylates; epoxy (meth)acrylates prepared by reacting (meth)acrylic acid with epoxy resins such as bisphenol-A type resins, bisphenol-F type epoxy resins, and novolak-type epoxy resins; and tris(2-acryloyloxyethyl) isocyanurate. Of these, polyfunctional acrylate monomers such as pentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, and dipentaerythritol hexaacrylate are preferred for use in the present invention. The use of pentaerythritol tetraacrylate is especially preferred.

[0045] The preferred molecular weight range of the acrylic polymer binder is 25,000-150,000 weight average molecular weight. Most preferred is 50,000-120,000 weight average molecular weight.

[0046] b. Silica-Coated Metal Oxide Pigments

[0047] Silica-coated pigments comprised of single or mixed metal oxides of copper, manganese, cobalt, nickel, chromium and iron are preferred or use in the present invention because they impart high optical density and high resistivity to the final black matrix structure and show superior dispersibility when further treated with silane coupling agents. Suitable pigments include, for example, Pigment Black 22 (C.I. 77429), Pigment Black 26 (C.I. 77494), Pigment Black 27 (C.I. 77502), and Pigment Black 28 (C.I. 77428). The pigments may be used singly or in admixture, including admixtures with organic pigments. The use of Pigment Black 26 (for example, Daipyroxide® Black-3551 obtained form Dainichiseika Color & Chemicals Mfg. Co. Ltd., Japan), which is a silica-coated mixed metal oxide of copper, manganese, and iron, is especially preferred for obtaining a black matrix structure with high optical density and low surface conductivity.

[0048] The silica coating of the pigment particles preferably should comprise 0.5-5% of total pigment weight, and more preferably 1-3% of pigment weight.

[0049] The silica-coated pigment should have particle sizes sufficient to allow filtration at resolutions smaller than 1 micron. For example, a primary particle size of 0.01-0.02 microns for the preferred silica-coated metal oxide pigments works well, especially when at least 50 wt. % of the particles have a primary particle size smaller than 0.02 microns.

[0050] c. Silane Coupling Agents

[0051] Trialkoxyorganosilane coupling agents are present in the improved black matrix coating compositions to improve the dispersibility of the silica-coated pigments in organic media, increase their compatibility with and wettability by the organic components of the coatings, and enhance the overall adhesion of the coating to the display substrate. The structure of the coupling agents can be represented generally as:

(R′O)3—Si—R″

[0052] where R′ is typically methyl or ethyl and R″ is a nonhydrolyzable radical that possesses a functionality which enables the coupling agent to bond, either physically or chemically, with the organic components of the coating. It is assumed that the trialkoxysilane function of the coupling agent forms chemical bonds with hydroxyl groups on the surface of the silica-coated pigments, leaving the more hydrophobic R″ groups to interact with the solvent and binder components. Coupling agent molecules may additionally condense into surface-bound polymeric layers.

[0053] Examples of trialkoxyorganosilane coupling agents which may be used suitably in the present invention include methyl trimethoxysilane, n-butyl trimethoxysilane, 3-chloropropyl-trimethoxysilane, ethyl trimethoxysilane, n-propyl trimethoxysilane, phenyl trimethoxysilane, 3-(trimethoxysilyl) propyl methacrylate, 3-glycidoxypropyltrimethoxysilane, vinyl trimethoxysilane, n-octadecyl triethoxysilane, amyl triethoxysilane, chloromethyl triethoxysilane, chlorophenyl triethoxysilane, benzyl triethoxysilane, n-octyl triethoxysilane, phenyl triethoxysilane, vinyl triethoxysilane, vinyl triphenoxysilane, and n-octadecyl triethoxysilane. The coupling agents may be used singly or in admixture and are typically added at about 5 wt. % based on pigment solids. The use of methyl trimethoxysilane is highly preferred for obtaining good dispersion stability and pigment wetting.

[0054] d. Photopolymerization Initiators or Initiator Systems

[0055] All known free radical initiators or initiator systems which operate effectively at <400 nm exposing wavelengths can be substantially employed as the photopolymerization initiator or initiator system for the present invention. Examples thereof include:

[0056] 1) trihalomethyl-substituted triazines such as p-methoxy-phenyl-2,4-bis(trichloromethyl)-s-triazine;

[0057] 2) trihalomethyl-substituted oxadiazoles such as

[0058] 2 -(p-butoxy-styryl)-5-trichloromethyl-1,3,4-oxadiazole;

[0059] 3) imidazole derivatives such as 2-(2′-chlorophenyl)-4,5-diphenylimidazole dimer (with a proton donor such as mercaptobenzimidazole);

[0060] 4) hexaaryl biimidazoles such as 2,2′-bis(o-chlorophenyl)-4,4′,5,5′-tetraphenylbiimidazole;

[0061] 5) benzoin alkyl ethers such as benzoin isopropyl ether;

[0062] 6) anthraquinone derivatives such as 2-ethylanthraquinone;

[0063] 7) benzanthrones;

[0064] 8) benzophenones such as Michler's ketone;

[0065] 9) acetophenones such as 2,2-diethoxy-2-phenylacetophenone and 2-benzyl-2-N,N-dimethylamino-1-(4-morpholinophenyl)-1-butanone;

[0066] 10) thioxanthones such as 2-isopropylthioxanthone;

[0067] 11) benzoic acid ester derivatives such as octyl p-dimethyl-aminobenzoate;

[0068] 12) acridines such as 9-phenylacridine;

[0069] 13) phenazines such as 9,10-dimethylbenzphenazine; and,

[0070] 14) titanium derivatives such as bis(cyclopentadienyl)-bis (2,6-difluoro-3-(pyl-1-yl)titanium.

[0071] Photopolymerization initiators may be used alone or in admixture, for example, by combining 2-isopropylthioxanthone with octyl p-dimethylaminobenzoate (ODAB). The use of amine-substituted acetophenones such as 2-benzyl-2-N,N-dimethylamino-1-(4-morpholino-phenyl)-1-butanone (IRGACURE 369® Ciba Geigy Corporation) in combination with thioxanthone-ODAB mixtures are preferred for obtaining high photospeed and sharp imaging properties.

[0072] e. Solvent Vehicle

[0073] Suitable solvents for the improved black matrix compositions include alcohols, esters, glymes, ethers, glycol ether, ketones, dialkylamides, lactams, lactones and their admixtures. Examples of useful solvents include N-methyl-2-pyrrolidone (NMP), dimethylacetamide (DMAc), dimethylformamide (DMF), cyclohexanone, bis-2-methylethyl ether (diglyme), tetrahydrofurfuyl alcohol (THFA), dimethylsulfoxide (DMSO), xylense, 2-heptanone, ethyl lactate, ethyl 3-ethoxypropionate, methyl 3-methoxypropionate, propylene glycol methyl ether acetate. The use of mixtures of NMP and cyclohexanone are especially preferred for obtaining good coating quality and long storage life.

[0074] f. Solvent-Soluble Organic Dyes

[0075] Solvent-soluble organic dyes are added in small proportions to the improved black matrix composition to critically enhance coating properties such as coating quality and shelf life. The addition of selected dyes significantly reduces the occurrence of particulates, voids, pinholes, and striations in the coated composition and extends room temperature shelf life of the coating formulation from typically a few hours to 5-10 days. Dye addition may also provide marginal improvements in coating optical density and volume resistivity.

[0076] The chemical nature of the dye is critical for achieving the desired improvements. For example, preferred azo-1,2-chrome complex dyes such as Solvent Black 28, Solvent Black 27, Solvent Black 29, and Solvent Black 45 significantly enhance coating quality and shelf life, whereas solvent-soluble dyes from other classes generally give no improvement or actually diminish coating properties. Examples of poorly performing dyes include Solvent Black 35, Solvent Brown 44, Solvent Blue 67, Solvent Black 3, Solvent Black 5, Solvent Black 7, Solvent Black 46, and Solvent Black 47. Within the azo-1,2-chrome complex dye class, Solvent Black 28 is the most preferred because it not only improves shelf life and coating quality, but enables high resolution (3 μm) patterning of black matrix features with sharply vertical side walls.

[0077] The amount of dye is also critical for obtaining the desired enhancements in coating performance and stability. The solvent-soluble dyes are preferably used at 0.2-3.0 wt. % based on the weight of added pigment(s), and more preferably at 1.0-2.0 wt. % based on pigment weight. If more than 5 wt. % is used, the coating will develop too rapidly, reducing pattern resolution or causing the formation of residues during development.

PREFERRED COMPOSITIONAL RANGES

[0078] The improved black matrix coating compositions are preferably formulated at 20-50wt. % total solids in solution to obtain coatings having a layer thickness of 1-2 microns after application and curing. A coating solids level of 30-40 wt. % is especially preferred for obtaining good quality spin coatings with layer thicknesses of about one micron. The chart below gives the preferred and most preferred loadings (expressed as wt. % of total coating solids) for each major component in the coatings.

	Preferred Wt. %	Most Preferred Wt. %
Component	of Coating Solids	of Coating Solids
polymer binder	5-15	8-12
polyfunctional	2-7	3-5
co-monomer(s)
pigment(s)	40-70	50-60
trialkoxyorganosilane	1-5	2-4
photoinitiator(s)	10-40	20-30
solvent-soluble dye(s)	0.2-3.0*	1.0-2.0*
*(based on dry pigment solids)

[0079] The desired range of silane coupling agent to solvent-soluble dye(s) is 10/1-1/4 by weight; preferably 5/1-1/2 by weight, and most preferably 5/1 by weight.

METHOD OF USE

[0080] The improved black matrix coating compositions are applied, patterned, and cured in a photolithographic process to obtain thermally stable black matrix structures exhibiting high optical density and electrical resistivity. The deposition process may be summarized as follows (FIG. 1). The display structure, typically glass, is cleaned. The black matrix coating is spin coated onto the glass substrate at 1000-1200 rpm for 90 seconds and then α-baked on a hot plate at 100° C. for 60 seconds to obtain a uniform layer which is approximately one micron in thickness. The coating is exposed at 200-2000 mJ/cm2, preferably at 500-1200 mJ/cm2 through a negative-tone mask using a mid-ultraviolet light source to form a latent image in the black matrix layer. It is then developed in a potassium carbonate solution for 30 seconds, spray rinsed for 10 seconds, and spun dry to etch away the non-light-struck areas in the layer. Finally, the patterned black matrix coating is cured at 230° C. in a convection oven for 1 hour to make it fully resistant to subsequently applied coating layers during the formation of flat panel displays and other optoelectronic devices which require light-blocking layers.

EXAMPLES

[0081] The following examples illustrate the process and product of the present invention. The intermediate pigment dispersions were prepared in a Eiger MINI-100 motormill using 0.5 mm glass beads as the grinding media. The process described in Example 1 was used to prepare all of the examples. A different dye was used for each example.

[0082] The Example 1 composition, which used the dye Solvent Black 28 was free of particles, voids, and pinholes, and striations showed low surface roughness (FIGS. 5 & 6). The addition of Solvent Black 28 also increased the shelf life of the composition to from less than one day to about 5-10 days while enabling the highest resolution patterning. The patterns were residue-free and had sharp vertical side walls (FIG. 4). Transmittance values for black matrix coatings should be below 1.0% across the wavelength range, 400-700 nm. FIG. 2 shows the transmittance for the black matrix coating composition of Example 1 to be well below this value. The optical density of the coating in Example 1 is 3.1, where optical density is defined as the absorbance of the coating layer at 540 nm (FIG. 3).

[0083] The use of the non-preferred Solvent Black 35 in Example 7 resulted in poor quality coatings with many particles and pinholes. This indicates the importance of using the correct dye in obtaining superior results. See Table 1.

					VOLUME
	DYE	OD	REFLEC-		RESIS-
EXAMPLE	Color	@	TANCE	SURFACE	TIVITY
#	Index Name	1 μm	%	μm	Ω cm
EXAMPLE	Orasol	3.1	2.1	0.05	3.4 × 109
1	Black CN
	Solvent
	Black 28
EXAMPLE	Orasol	3.5	2.0	0.04	7.0 × 109
2	Black RLI
	Solvent
	Black 29
EXAMPLE	Neopen	3.4	1.8	0.06	5.9 × 109
3	Black X53
	Solvent
	Black 27
EXAMPLE	Zapon	3.1	3.1	0.03	1.9 × 109
4	Black X 51
	Solvent
	Black 27
EXAMPLE	Savinyl	3.1	2.9	0.05	5.7 × 109
5	Black RLS
	Solvent
	Black 45

EXAMPLE 1

[0084] Preparation of Intermediate Pigment Dispersion. Into a plastic beaker was added 20 g of N-methylprrolidone (NMP), 111 g of cyclohexanone, 3.12 g of methyl trimethoxysilane, 62.4 g of Pigment Black 26 (silica-coated) and 20 g of polymer binder solution. The latter was a 25 wt. % NMP solution of an acrylic copolymer comprising 70 mole % benzyl methacrylate and 30 mole % methacrylic acid.) The mixture was stirred with a spatula for about 5 minutes until it became homogenous. This pigment slurry was then introduced into the grinding mill turning at 1000 rpm over a period of 15 minutes. The contents were rinsed into the mill with 10 g of NMP. The grind speed was slowly increased to 3000 rpm. The pigment was then ground at this speed for 2 hours.

[0085] In a separate plastic breaker was added 20 g of polymer binder solution and 0.62 g of ORASOL Black CN (® Ciba-Geigy Corporation, aka Solvent Black 28, 1 wt. % based on silica-coated pigment). The mixture was stirred for 10 minutes and then added to the contents of the mill after they had been grinding for 2 hours. The dye solution was rinsed into the mill with 34.2 g of fresh NMP. The mill contents were then further ground at 3000 rpm for 90 minutes. The pigment dispersion was discharged from the mill and filtered through 0.2 μm pore size filters.

[0086] Preparation of Black Matrix Coating Formulation. 30 g of the above pigment dispersion, 0.5 g of pentaerythritol tetraacrylate, 0.6 g of isopropylthioxanthone, 1.2 g of octyl-p-dimethylamino-benzoate, and 1.2 g IRGACURE 369 were combined by stirring under yellow light for 15 minutes. The resulting product composition was filtered through a 0.2 μm pore size filter. Shelf life of the black matrix is more than 3 months under refrigeration.

[0087] Applying the Black Matrix

[0088] The black matrix was spincoated on glass substrate at 1 μm film thickness and prebaked on a hot plate at 100° C. for 1 min. The black matrix is photosensitive and does not require a photoresist coating. The black matrix was exposed with a high pressure mercury lamp at 500-1000 mJ/cm2, developed in dilute alkaline developer for 30 sec, rinsed in DI water for 30 sec. The resulting image was final cured in a convection oven at 230° C. for 1 hour. Resolution in the range of 3-6 μm was achieved. Volume resistivity measurements made in accordance with ASTM D257 methods for a 1 μm film were on the order of 109-1011 Ω-cm. Reflectance of the 1 μm black matrix after final cure was 2.1%. Surface roughness was in the range of 0.03-0.05 μm.

[0089] Thermal Stability

[0090] The black matrix must exhibit high thermal stability during the alignment layer formation step. FIG. 7 shows the spectral change at 1 μm film thickness before and after heating. The chromatic changes (ΔE*ab) are less than 3 (ΔE*ab=1.9) after heating in a convection oven at 230° C. in air for 7 hours, thus showing excellent thermal stability.

[0091] Light Resistance

[0092] The light resistance of pixels is important because these pixels are illuminated with back light of LCDs. The black matrix was exposed to a Mercury-Xenon lamp (200-1300 lux) with a UV filter. FIG. 8 shows the spectral changes of the black matrix after 1 million lux hours. The chromatic changes (ΔE*ab) are less than 3 (ΔE*ab=1.2), demonstrating the superior light resistance of the black matrix.

[0093] Chemical Resistance

TABLE 2
                Chromatic changes after dipping
Chemicals       for 1 min (ΔE*ab)
NMP             0.40
Ethanlol        0.46
Acetone         0.13
g-Butyrolactone 0.68
Isopropanol     0.65
Cyclohexanone   0.27
PGMEA           0.37
5% HCl          1.06
5% Na2CO3       1.31
5% TMAH         1.24

[0094] Since color filters are exposed to solvents, acids and bases during the LCD fabrication process, the chemical stability is a key factor. The cured film must be resistant to alignment layer solvents such as NMP and g-butyrolactone, towards acids during etching of the indium tin oxide (ITO) or towards bases used in the development system. The chemical stability of black resist was evaluated by both pattern observation and chromatic changes. After dipping the pixels in solvents, acids and alkaline solution for 1 min, patterns were found to be stable and neither swelling nor peeling was observed. The chromatic changes (ΔE*ab) are less than 3, indicating very good chemical stability of the black matrix (Table 2).

EXAMPLE 2

[0095] A black matrix coating composition of the present invention was prepared identically to that in Example 1 except that ZAPON Black X51 (® BASF Corporation, aka Solvent Black 27/Cation 1, 1 wt. % based on silica-coated pigment) was used in place of ORASOL Black CN.

EXAMPLE 3

[0096] A black matrix coating composition of the present invention was prepared identically to that in Example 1 except that ORASOL Black RLI (®Ciba-Geigy Corporation, aka Solvent Black 29)was used in place of ORASOL Black CN.

EXAMPLE 4

[0097] A black matrix coating composition of the present invention was prepared identically to that in Example 1 except that NEOPON Black X53 (®BASF Corporation, aka solvent Black 27/Cation 2) was used in place of 0.6 g of ORASOL Black CN (1 wt. % based on silica-coated pigment).

EXAMPLE 5

[0098] A black matrix coating composition of the present invention was prepared identically to that in Example 1 except that 1.2 g of SAVINYL Black RLS (®Clariant Corporation, aka Solvent Black 45, 2 wt. % based on silica-coated pigment) was used in place of 0.62 g of ORASOL Black CN.

EXAMPLE 6

[0099] A black matrix coating composition of the present invention was prepared identically to that in Example 1 except that no dye was used.

EXAMPLE 7

[0100] A black matrix coating composition of the present invention was prepared identically to that in Example 1 except that Solvent Black 35 was used in place of Solvent Black 28.

Claims

1. In a photosensitive black matrix composition comprising a polymer binder, a pigment, and a dye dissolved or dispersed in a solvent system, the improvement being that said dye comprises an azo-1,2-chrome complex dye.

2. The composition of claim 1, wherein said dye is present in said composition at a level of from 0.2-3.0 wt. %, based upon the total weight of pigment solids taken as 100% by weight.

3. The composition of claim 1, wherein said pigment comprises a silica-coated metal oxide.

4. The composition of claim 1, said composition further comprising a coupling agent.

5. The composition of claim 4, wherein said coupling agent is a trialkoxyorganosilane coupling agent.

6. The composition of claim 4, wherein said coupling agent is present in said composition at a level of about 5 wt. %, based upon the total weight of the pigment solids taken as 100% by weight.

7. The composition of claim 1, wherein said polymer binder is alkali-soluble.

8. The composition of claim 1, said composition further comprising a photopolymerizable polyfunctional acrylate or methacrylate monomer or mixture of monomers, with each monomer having one or more ethylenically unsaturated double bond per molecule.

9. The composition of claim 1, said composition further comprising a free-radical generating photoinitiator capable of operating effectively at exposure wavelengths of less than 400 nm.

10. The composition of claim 9, wherein said photoinitiator comprises an amine-substituted acetophenone combined with thioxanthone and octyl N,N-dimethylaminobenzoate.

11. The composition of claim 3, wherein said pigment comprises a metal oxide selected from the group consisting of copper oxides, manganese oxides, cobalt oxides, nickel oxides, chromium oxides, iron oxides, and mixtures thereof.

12. The composition of claim 1, wherein said dye is selected from the group consisting of Solvent Black 27, Solvent Black 28, Solvent Black 29, and Solvent Black 45.

13. The composition of claim 12, wherein said dye is Solvent Black 28 and is present in the composition at a level of 1 wt. %, based upon the total weight of the pigment solids taken as 100% by weight.

14. The composition of claim 1, wherein said composition, when formed into a film having a thickness of 1 micron or less and cured, has a volume resistivity of greater than 108 ohm-cm and an optical density of greater than 3.0.

15. The composition of claim 3, wherein said pigment has a primary particle size sufficient to allow filtration at resolutions smaller than 1 micron.

16. The composition of claim 15, wherein said pigment particle size is form 0.01-0.02 micron, and at least 50 wt. % of the pigment particles have a primary particle size of less than 0.02 microns.

17. The composition of claim 3, wherein said silica-coated metal oxide pigment is Pigment Black 26.

18. The combination of a substrate having a surface and the composition of claim 1 applied to said substrate surface.

19. The combination of claim 18, wherein said substrate comprises glass.

20. The combination of claim 18, wherein said composition comprises a cured film on said substrate.

21. The combination of claim 20, wherein said film has a thickness of 1 micron or less, a volume resistivity of greater than 108 ohm-cm, and an optical density of greater than 3.0.

22. In a photosensitive black matrix composition comprising a polymer binder dissolved or dispersed in a solvent system, the improvement being that said composition further comprises an azo-1,2-chrome complex dye, a coupling agent, and a metal oxide pigment.

23. The composition of claim 22, wherein said coupling agent is a trialkoxyorganosilane coupling agent.

24. The composition of claim 22, wherein said pigment comprises silica-coated metal oxide pigment.

25. The composition of claim 23, wherein said pigment comprises silica-coated metal oxide pigment.

26. The composition of claim 22, wherein said dye is present in said composition at a level of 0.2-3.0 wt %, based upon the total weight of the pigment solids taken as 100% by weight.

27. The combination of a substrate having a surface and the composition of claim 22 applied to said substrate surface.

28. The combination of claim 27, wherein said substrate comprises glass.

29. The combination of claim 27, wherein said composition comprises a cured film on said substrate.

30. The combination of claim 29, wherein said film has a thickness of 1 micron or less, a volume resistivity of greater than 108 ohm-cm, and an optical density of greater than 3.0.

31. A method of forming a photosensitive black matrix comprising the steps of: applying a quantity of the composition of claim 1 to a substrate so as to form a film thereon; baking said film; exposing said baked film to energy; developing said exposed film; and curing said exposed film.

32. The method of claim 31, wherein said exposing step comprises exposing said film at 200-2000 mJ/cm2 of energy.

33. A method of forming a photosensitive black matrix comprising the steps of: applying a quantity of the composition of claim 22 to a substrate so as to form a film thereon; baking said film; exposing said baked film to energy; developing said exposed film; and curing said exposed film.

34. The method of claim 33, wherein said exposing step comprises exposing said film at 200-2000 mJ/cm2 of energy.