Polishing pads having selectively arranged porosity

Information

  • Patent Grant
  • 11813712
  • Patent Number
    11,813,712
  • Date Filed
    Tuesday, September 29, 2020
    4 years ago
  • Date Issued
    Tuesday, November 14, 2023
    a year ago
Abstract
Polishing pads having discrete and selectively arranged regions of varying porosity within a continuous phase of polymer material are provided herein. In one embodiment a polishing pad features a plurality of polishing elements each comprising a polishing surface and sidewalls extending downwardly from the polishing surface to define a plurality of channels disposed between the polishing elements, wherein one or more of the polishing elements is formed of a continuous phase of polymer material having one or more first regions comprising a first porosity and a second region comprising a second porosity, wherein the second porosity is less than the first porosity.
Description
BACKGROUND
Field

Embodiments of the present disclosure generally relate to polishing pads, and methods of manufacturing polishing pads, and more particularly, to polishing pads used for chemical mechanical polishing (CMP) of a substrate in an electronic device fabrication process.


Description of the Related Art

Chemical mechanical polishing (CMP) is commonly used in the manufacturing of high-density integrated circuits to planarize or polish a layer of material deposited on a substrate. A typical CMP process includes contacting the material layer to be planarized with a polishing pad and moving the polishing pad, the substrate, or both, and hence creating relative movement between the material layer surface and the polishing pad, in the presence of a polishing fluid comprising abrasive particles. One common application of CMP in semiconductor device manufacturing is planarization of a bulk film, for example pre-metal dielectric (PMD) or interlayer dielectric (ILD) polishing, where underlying two or three-dimensional features create recesses and protrusions in the surface of the layer to be planarized. Other common applications of CMP in semiconductor device manufacturing include shallow trench isolation (STI) and interlayer metal interconnect formation, where CMP is used to remove the via, contact or trench fill material from the exposed surface (field) of the layer having the STI or metal interconnect features disposed therein.


Often, polishing pads used in the above-described CMP processes are selected based on the material properties of the polishing pad material and the suitability of those material properties for the desired CMP application. One example of a material property that may be adjusted to tune the performance of a polishing pad for a desired CMP application is the porosity of a polymer material used to form the polishing pad and properties related thereto, such as pore size, pore structure, and material surface asperities. Conventional methods of introducing porosity into the polishing pad material typically comprise blending a pre-polymer composition with a porosity forming agent before molding and curing the pre-polymer composition into individual polishing pads or a polymer cake and machining, e.g., skiving, individual polishing pads therefrom. Unfortunately, while conventional methods may allow for the creation of uniform porosity and/or gradual porosity gradients, they are generally unable to provide precision placement of pores within the formed pad and the pad polishing performance-tuning opportunities that might result therefrom.


Accordingly, there is a need in the art for methods of forming discrete respective regions of higher and lower porosity within a polishing pad and polishing pads formed therefrom.


SUMMARY

Embodiments described herein generally relate to polishing pads, and methods for manufacturing polishing pads which may be used in a chemical mechanical polishing (CMP) process, and more particularly, to polishing pad having selectively arranged pores to define discrete regions that include porosity within a polishing element.


In one embodiment, a polishing pad features a plurality of polishing elements each comprising a polishing surface and sidewalls extending downwardly from the polishing surface to define a plurality of channels disposed between the polishing elements. Here, one or more of the polishing elements is formed of a continuous phase of polymer material having one or more first regions comprising a first porosity and a second region comprising a second porosity. Typically, the second porosity is less than the first porosity. In some embodiments, one or more regions of intermediate porosities which have corresponding porosities less than the relatively high porosity region A and more than the relatively low porosity region B may be interposed between the regions A and B. In some embodiments, one or more regions of either higher, lower, or a combination of higher and lower porosities may be interposed between the regions A and B.


In another embodiment, a method of forming a polishing pad includes dispensing droplets of a pre-polymer composition and droplets of a sacrificial material composition onto a surface of a previously formed print layer according to a predetermined droplet dispense pattern. The method further includes at least partially curing the dispensed droplets of the pre-polymer composition to form a print layer comprising at least portions of a polymer pad material having one or more first regions comprising first porosity and one or more second regions comprising a second porosity. At least one of the second regions is disposed adjacent to a first region and the second porosity is less than the first porosity.





BRIEF DESCRIPTION OF THE DRAWINGS

So that the manner in which the above-recited features of the present disclosure can be understood in detail, a more particular description of the disclosure, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this disclosure and are therefore not to be considered limiting of its scope, for the disclosure may admit to other equally effective embodiments.



FIG. 1 is a schematic side view of an exemplary polishing system configured to use a polishing pad formed according to one of, or a combination of, the embodiments described herein.



FIG. 2A is a schematic perspective sectional view of a polishing pad featuring selectively arranged pores, according to one embodiment.



FIGS. 2B-2I are schematic sectional views of polishing elements that illustrate various selective pore arrangements.



FIGS. 3A-3F are schematic plan view of various polishing pad designs which may be used in place of the pad design shown in FIG. 2A, according to some embodiments.



FIG. 4A is a schematic sectional view of an additive manufacturing system, which may be used to form the polishing pads described herein.



FIG. 4B is a close-up cross-sectional view schematically illustrating a droplet disposed on a surface of a previously formed print layer, according to one or more, or a combination of, the embodiments described herein.



FIGS. 5A-5C show portions of CAD compatible print instructions 500a-c, which may be used to form the polishing pads, described herein.



FIG. 6 is a flow diagram setting forth a method of forming a polishing pad, according to one or more, or a combination of, the embodiments described herein.





To facilitate understanding, identical reference numerals have been used, where possible, to designate identical elements that are common to the figures. It is contemplated that elements and features of one implementation may be beneficially incorporated in other implementations without further recitation.


DETAILED DESCRIPTION

Embodiments described herein generally relate to polishing pads, and methods for manufacturing polishing pads, which may be used in a chemical mechanical polishing (CMP) process, and more particularly, to polishing pads having selectively arranged pores to define discrete regions that include porosity within a polishing element.


Generally, the polishing pads described herein feature a foundation layer and a plurality of polishing elements disposed on, and integrally formed with, the foundation layer to form a unitary body comprising a continuous polymer phase. The polishing elements form a polishing surface of the polishing pad and the foundation layer provides support for the polishing elements as a to-be-polished substrate is urged against the polishing surface.


The polishing elements feature pores that are selectively arranged across the polishing surface and/or in a direction orthogonal thereto. As used herein, the term “pore” includes openings defined in the polishing surface, voids formed in the polishing material below the polishing surface, pore-forming features disposed in the polishing surface, and pore-forming features disposed in polishing material below the polishing surface. Pore-forming features typically comprise a water-soluble-sacrificial material that dissolves upon exposure to a polishing fluid thus forming a corresponding opening in the polishing surface and/or void in the polishing material below the polishing surface. In some embodiments, the water-soluble-sacrificial material may swell upon exposure to a polishing fluid thus deforming the surrounding polishing material to provide asperities at the polishing pad material surface. The resulting pores and asperities desirably facilitate transporting liquid and abrasives to the interface between the polishing pad and a to-be-polished material surface of a substrate, and temporarily fixes those abrasives (abrasive capture) in relation to the substrate surface to enable chemical and mechanical material removal therefrom.


The term “selectively arranged pores” as used herein refers to the distribution of pores within the polishing elements. Herein, the pores are distributed in one or both directions of an X-Y plane parallel to the polishing surface of the polishing pad (i.e., laterally) and in a Z-direction which is orthogonal to the X-Y planes, (i.e., vertically).



FIG. 1 is a schematic side view of an example polishing system configured to use a polishing pad formed according to one or a combination of the embodiments described herein. Here, the polishing system 100 features a platen 104, having a polishing pad 102 secured thereto using a pressure sensitive adhesive, and a substrate carrier 106. The substrate carrier 106 faces the platen 104 and the polishing pad 102 mounted thereon. The substrate carrier 106 is used to urge a material surface of a substrate 108, disposed therein, against the polishing surface of the polishing pad 102 while simultaneously rotating about a carrier axis 110. Typically, the platen 104 rotates about a platen axis 112 while the rotating substrate carrier 106 sweeps back and forth from an inner diameter to an outer diameter of the platen 104 to, in part, reduce uneven wear of the polishing pad 102.


The polishing system 100 further includes a fluid delivery arm 114 and a pad conditioner assembly 116. The fluid delivery arm 114 is positioned over the polishing pad 102 and is used to deliver a polishing fluid, such as a polishing slurry having abrasives suspended therein, to a surface of the polishing pad 102. Typically, the polishing fluid contains a pH adjuster and other chemically active components, such as an oxidizing agent, to enable chemical mechanical polishing of the material surface of the substrate 108. The pad conditioner assembly 116 is used to condition the polishing pad 102 by urging a fixed abrasive conditioning disk 118 against the surface of the polishing pad 102 before, after, or during polishing of the substrate 108. Urging the conditioning disk 118 against the polishing pad 102 includes rotating the conditioning disk 118 about an axis 120 and sweeping the conditioning disk 118 from an inner diameter the platen 104 to an outer diameter of the platen 104. The conditioning disk 118 is used to abrade, rejuvenate, and remove polish byproducts or other debris from, the polishing surface of the polishing pad 102.



FIG. 2A is a schematic perspective sectional view of a polishing pad 200a featuring selectively arranged pores, according to one embodiment. The polishing pad 200a may be used as the polishing pad 102 of the exemplary polishing system 100 described in FIG. 1. Here, the polishing pad 200a comprises a plurality of polishing elements 204a, which are disposed on and partially disposed within a foundation layer 206. The polishing pad 200a has a first thickness T(1) of between about 5 mm and about 30 mm. The polishing elements 204a are supported in the thickness direction of the pad 200a by a portion of the foundation layer 206 that has a second thickness of T(2) of between about ⅓ to about ⅔ of the first thickness T(1). The polishing elements 204a have a third thickness T(3) that is between about ⅓ and about ⅔ the thickness T(1). As shown, at least portions of the polishing elements are disposed beneath a surface of the foundation layer 206 and the remaining portions extend upwardly therefrom by a height H. In some embodiments, the height H is about ½ the first thickness T(1) or less.


Here, the plurality of polishing elements 204a comprise a plurality of discontinuous (segmented) concentric rings 207 disposed about a post 205 and extending radially outward therefrom. Here, the post 205 is disposed in the center of the polishing pad 200a. In other embodiments the center of the post 205, and thus the center of the concentric rings 207, may be offset from the center of the polishing pad 200a to provide a wiping type relative motion between a substrate and the polishing pad surface as the polishing pad 200a rotates on a polishing platen. Sidewalls of the plurality of polishing elements 204a and an upward facing surface of the foundation layer 206 define a plurality of channels 218 disposed in the polishing pad 200a between each of the polishing elements 204a and between a plane of the polishing surface of the polishing pad 200a and a surface of the foundation layer 206. The plurality of channels 218 enable the distribution of polishing fluids across the polishing pad 200a and to an interface between the polishing pad 200a and the material surface of a substrate to be polished thereon. Here, the polishing elements 204a have an upper surface that is parallel to the X-Y plane and sidewalls that are substantially vertical, such as within about 20° of vertical (orthogonal to the X-Y plane), or within 10° of vertical. A width W(1) of the polishing element(s) 204a is between about 250 microns and about 10 millimeters, such as between about 250 microns and about 5 millimeters, or between about 1 mm and about 5 mm. A pitch P between the polishing element(s) 204a is between about 0.5 millimeters and about 5 millimeters. In some embodiments, one or both of the width W(1) and the pitch P vary across a radius of the polishing pad 200a to define zones of pad material properties.



FIGS. 2B-2I are schematic sectional views of polishing elements 204b-i that illustrate various selective pore arrangements. Any one or combination of the selective pore arrangements shown and described in FIGS. 2B-2I may be used with, and/or in place of, the selective pore arrangements of the polishing elements 204a of FIG. 2A. As shown in FIGS. 2B-2I, each of the polishing elements 204b-i are formed of a continuous phase of polymer material 212 comprising relatively high porosity regions A and one or more relatively low porosity regions B disposed adjacent thereto. As used herein, “porosity” refers to the volume of void-space as a percentage of the total bulk volume in a given sample. In embodiments where a pore, as defined herein, comprises a pore-forming feature formed of a sacrificial material the porosity is measured after sacrificial material forming the feature is dissolved therefrom. Porosity and pore size may be measured using any suitable method, such as by methods using scanning election microscopy (SEM) or optical microscope. Techniques and systems for characterizing porosity (e.g., area density) and pore size are well known in the art. For example, a portion of the surface can be characterized by any suitable method (e.g., by electron microscope image analysis, by atomic force microscopy, by 3D microscopy, etc.). In one implementation, the porosity (e.g., percentage or ratio of the exposed pore area to exposed non-pore containing area of a sample's surface) and pore size analysis can be performed using a VK-X Series 3D UV Laser Scanning Confocal Microscope, produced by KEYENCE Corporation of America, located in Elmwood Park, N.J., U.S.A.


Typically, the porosity in a region of relatively high porosity A will be about 3% or more, such as about 4% or more, about 5% or more, about 10% or more, about 12.5% or more, about 15% or more, about 17.5% or more, about 20% or more, about 22.5% or more, or about 25% or more. The porosity in a relatively low porosity region B will generally be about 95% or less than the porosity of the region of relatively high porosity A adjacent thereto, such as about 90% or less, about 85% or less, about 80% or less, about 75% or less, about 70% or less, about 60% or less, about 50% or less, about 40% or less, about 30% or less, or about 25% or less. In some embodiments, the relatively low porosity region B will have substantially no porosity. Herein, substantially no porosity comprises regions having a porosity of about 0.5% or less. In some embodiments, the relatively low porosity region B will have a porosity of 0.1% or less.


In some embodiments, such as shown in FIGS. 2B-2E, the relatively high porosity regions A comprise a plurality of pores 210 disposed proximate to one or more of the sidewalls of the polishing elements 204a-e (when viewed from top down). The regions of relatively low (or substantially no) porosity B are disposed inwardly from the sidewalls of the polishing elements 204a-e, i.e., inwardly from the relatively high porosity regions A (when viewed from top down). Here, the relatively high porosity regions A have a width W(2) that is less than the width W(3) of the relatively low porosity region B disposed adjacent thereto. In some embodiments, one or more of the relatively high porosity regions A have a width W(2) in the range of about 50 μm to about 10 mm, such as about 50 μm to about 8 mm, about 50 μm to about 6 mm, about 50 μm to about 5.5 mm, about 50 μm to about 5 mm, about 50 μm to about 4 mm, about 50 μm to about 3 mm, about 50 μm to about 2 mm, such as about 50 μm to about 1.5 mm, about 50 μm to about 1 mm, about 100 μm to about 1 mm, or about 200 μm to about 1 mm. In some embodiments, the width W(2) of the region of relatively high porosity A is about 90% or less of the width of the region of relatively low porosity B disposed adjacent thereto, such as 80% or less, 70% or less, 60% or less, or 50% or less. As shown, the relatively high porosity region A is adjacent to the relatively low porosity region B. In some embodiments, one or more regions of intermediate porosity (not shown) which has a porosity less than the relatively high porosity region A and more than the relatively low porosity region B may be interposed between the regions A and B.


Typically, the pores 210 used to form the relatively high porosity regions A will have one or more lateral (X-Y) dimensions which are about 500 μm or less, such as about 400 μm or less, 300 μm or less, 200 μm or less, or 150 μm or less. In some embodiments, the pores 210 will have at least one lateral dimension that is about 5 μm or more, about 10 μm or more, about 25 μm or more, or about 50 μm or more. In some embodiments, the pores will have at least one lateral dimension in the range of about 50 μm to about 250 μm, such as in the range of about 50 μm to about 200 μm, about 50 μm to about 150 μm. A pore height Z-dimension may be about 1 μm or more, about 2 μm or more, about 3 μm or more, about 5 μm or more, about 10 μm or more, such as about 25 μm or more, about 50 μm or more, about 75 μm, or about 100 μm. In some embodiments, the pore height Z-dimension is about 100 μm or less, such as between about 1 μm and about 50 μm, or between about 1 μm and about 25 μm, such as between about 1 μm and about 10 μm.


As shown in FIGS. 2A-2I the relatively high porosity regions A extend from the surface of the polishing elements 204a to a depth D which may be the same as the height H (FIG. 2A) or the thickness T(3) of the polishing elements 204a-i or may be a fraction thereof. For example, in some embodiments, the relatively high porosity regions A may extend to a depth D that is 90% or less of the thickness T(3), such as about 80% or less, 70% or less, 60% or less, or 50% or less. In some embodiments, the relatively high porosity regions A may extend to a depth D that is about 90% or less of the height H of the polishing element 204a-i, such as 80% or less, 70% or less, 60% or less, or 50% or less.


The pores 210 used to form the relatively high porosity regions A may be disposed in any desired vertical arrangement when viewed in cross-section. For example, in some embodiments, the pores 210 may be vertically disposed in one or more columnar arrangements such as shown in FIGS. 2B, 2D where the pores 210 in each of the columns are in substantial vertical alignment. In other embodiments, the pores 210 may be vertically disposed in one or more staggered columnar arrangements where each pore 210 is offset in one or both of the X-Y directions with respect to a pore 210 that is disposed thereabove and/or therebelow. The orientation of the pores in a columnar arrangement can be used to adjust the compliance of the porosity region A, due to the relative alignment or non-alignment of the pores to a direction in which a load is provided during polishing by a substrate that is being polished. Thus, in one example, the columnar arrangement of pores can be used to adjust and/or control the polishing planarization results for a formed polishing pad.


Here, the pores 210 are spaced apart in the vertical direction by one or more printed layers of the polymer material 212 that has a total thickness T(4) of the one or more printed layers of about 5 μm or more, such as about 10 μm or more, 20 μm or more, 30 μm or more, 40 μm or more, or 50 μm or more. In one example, spacing between pores 210 in a vertical direction in polishing feature is about 40 μm. In this example, the 40 μm spacing can be formed by disposing three or four layers of the polymer material 212 between printed layers that include the pores 210. Thus, as shown, the pores 210 form a substantially closed-celled structure. In other embodiments one or more of the pores 210, or portions thereof, are not spaced apart from one or more of the pores adjacent thereto and thus form a more open-celled structure.


In some embodiments, such as shown in FIGS. 2F-2I, the polishing elements 200f-i comprise at least one relatively low porosity region B disposed proximate to the sidewall of the polishing element 204f-i and at least one adjacent relatively high porosity region A disposed inwardly therefrom. In some embodiments, such as shown in FIGS. 2H-2I, the polishing elements 204h-i alternating relatively high porosity regions A and relatively low porosity regions B. In those embodiments, each of the high porosity regions A may have the same width W(2), as shown, or have different widths (not shown). The alternating high porosity regions A are spaced apart by a low porosity region B and each of the low porosity regions B may have the same width (not shown) or different widths, such as W(4) and W(5) respectively where the widths W(4) and W(5) may be found the ranges set forth above for the width W(3).



FIGS. 3A-3F are schematic plan views of various polishing elements 304a-f shapes which may be used with or in place of the polishing elements 204a of the polishing pad 200a described in FIG. 2A. Each of the FIGS. 3A-3F include pixel charts having white regions (regions in white pixels) that represent the polishing elements 304a-f and black regions (regions in black pixels) that represent the foundation layer 206. Pores and related high porosity regions (not shown in FIGS. 3A-3F) comprise any one or combination of the selective pore arrangements set forth in FIGS. 2B-2I above.


In FIG. 3A, the polishing elements 300a comprise a plurality of concentric annular rings. In FIG. 3B, the polishing elements 300b comprise a plurality of segments of concentric annular rings. In FIG. 3C, the polishing elements 304c form a plurality of spirals (four shown) extending from a center of the polishing pad 300c to an edge of the polishing pad 300c or proximate thereto. In FIG. 3D, a plurality of discontinuous polishing elements 304d are arranged in a spiral pattern on the foundation layer 206.


In FIG. 3E, each of the plurality of polishing elements 304e comprise a cylindrical post extending upwardly from the foundation layer 206. In other embodiments, the polishing elements 304e are of any suitable cross-sectional shape, for example columns with toroidal, partial toroidal (e.g., arc), oval, square, rectangular, triangular, polygonal, irregular shapes in a section cut generally parallel to the underside surface of the pad 300e, or combinations thereof. FIG. 3F illustrates a polishing pad 300f having a plurality of discrete polishing elements 304f extending upwardly from the foundation layer 206. The polishing pad 300f of FIG. 3F is similar to the polishing pad 300e except that some of the polishing elements 304f are connected to form one or more closed circles. The one or more closed circles create damns to retain polishing fluid during a CMP process.



FIG. 4A is a schematic sectional view of an additive manufacturing system, which may be used to form the polishing pads described herein, according to some embodiments. Here, the additive manufacturing system 400 features a movable manufacturing support 402, a plurality of dispense heads 404 and 406 disposed above the manufacturing support 402, a curing source 408, and a system controller 410. In some embodiments, the dispense heads 404, 406 move independently of one another and independently of the manufacturing support 402 during the polishing pad manufacturing process. Here, the first and second dispense heads 404 and 406 are respectively fluidly coupled to a first pre-polymer composition source 412 and sacrificial material sources 414 which are used to form the polymer material 212 and the pores 210 described in FIGS. 2A-2I above. Typically, the additive manufacturing system 400 will feature at least one more dispense head (e.g., a third dispense head, not shown) which is fluidly coupled to a second pre-polymer composition source used to form the foundation layer 206 described above. In some embodiments, the additive manufacturing system 400 includes as many dispense heads as desired to each dispense a different pre-polymer composition or sacrificial material precursor compositions. In some embodiments, the additive manufacturing system 400 further comprises pluralities of dispense heads where two or more dispense heads are configured to dispense the same pre-polymer compositions or sacrificial material precursor compositions.


Here, each of dispense heads 404, 406 features an array of droplet ejecting nozzles 416 configured to eject droplets 430, 432 of the respective pre-polymer composition 412 and sacrificial material composition 414 delivered to the dispense head reservoirs. Here, the droplets 430, 432 are ejected towards the manufacturing support and thus onto the manufacturing support 402 or onto a previously formed print layer 418 disposed on the manufacturing support 402. Typically, each of dispense heads 404, 406 is configured to fire (control the ejection of) droplets 430, 432 from each of the nozzles 416 in a respective geometric array or pattern independently of the firing other nozzles 416 thereof. Herein, the nozzles 416 are independently fired according to a droplet dispense pattern for a print layer to be formed, such as the print layer 424, as the dispense heads 404, 406 move relative to the manufacturing support 402. Once dispensed, the droplets 430 of the pre-polymer composition and/or the droplets of the sacrificial material composition 414 are at least partially cured by exposure to electromagnetic radiation, e.g., UV radiation 426, provided by an electromagnetic radiation source, such as a UV radiation source 408 to form a print layer, such as the partially formed print layer 424.


In some embodiments, dispensed droplets of the pre-polymer compositions, such as the dispensed droplets 430 of the first pre-polymer composition, are exposed to electromagnetic radiation to physically fix the droplet before it spreads to an equilibrium size such as set forth in the description of FIG. 4B. Typically, the dispensed droplets are exposed to electromagnetic radiation to at least partially cure the pre-polymer compositions thereof within 1 second or less of the droplet contacting a surface, such as the surface of the manufacturing support 402 or of a previously formed print layer 418 disposed on the manufacturing support 402.



FIG. 4B is a close up cross-sectional view schematically illustrating a droplet 430 disposed on a surface 418a of a previously formed layer, such as the previously formed layer 418 described in FIG. 4A, according to some embodiments. In a typically additive manufacturing process, a droplet of pre-polymer composition, such as the droplet 430a will spread and reach an equilibrium contact angle α with the surface 418a of a previously formed layer within about one second from the moment in time that the droplet 430a contacts the surface 418a. The equilibrium contact angle α is a function of at least the material properties of the pre-polymer composition and the energy at the surface 418a (surface energy) of the previously formed layer, e.g., previously formed layer 418. In some embodiments, it is desirable to at least the partially cure the dispensed droplet before it reaches an equilibrium size in order to fix the droplets contact angle with the surface 418a of the previously formed layer. In those embodiments, the fixed droplet's 430b contact angle θ is greater than the equilibrium contact angle α of the droplet 430a of the same pre-polymer composition which was allowed to spread to its equilibrium size.


Herein, at least partially curing a dispensed droplet causes the at least partial polymerization, e.g., the cross-linking, of the pre-polymer composition(s) within the droplets and with adjacently disposed droplets of the same or different pre-polymer composition to form a continuous polymer phase. In some embodiments, the pre-polymer compositions are dispensed and at least partially cured to form a well about a desired pore before a sacrificial material composition is dispensed thereinto.


The pre-polymer compositions used to form the foundation layer 206 and the polymer material 212 of the polishing elements described above each comprise a mixture of one or more of functional polymers, functional oligomers, functional monomers, reactive diluents, and photoinitiators.


Examples of suitable functional polymers which may be used to form one or both of the at least two pre-polymer compositions include multifunctional acrylates including di, tri, tetra, and higher functionality acrylates, such as 1,3,5-triacryloylhexahydro-1,3,5-triazine or trimethylolpropane triacrylate.


Examples of suitable functional oligomers which may be used to form one or both of the at least two pre-polymer compositions include monofunctional and multifunctional oligomers, acrylate oligomers, such as aliphatic urethane acrylate oligomers, aliphatic hexafunctional urethane acrylate oligomers, diacrylate, aliphatic hexafunctional acrylate oligomers, multifunctional urethane acrylate oligomers, aliphatic urethane diacrylate oligomers, aliphatic urethane acrylate oligomers, aliphatic polyester urethane diacrylate blends with aliphatic diacrylate oligomers, or combinations thereof, for example bisphenol-A ethoxylate diacrylate or polybutadiene diacrylate, tetrafunctional acrylated polyester oligomers, and aliphatic polyester based urethane diacrylate oligomers.


Examples of suitable monomers which may be used to form one or both of the at least two pre-polymer compositions include both mono-functional monomers and multifunctional monomers. Suitable mono-functional monomers include tetrahydrofurfuryl acrylate (e.g. SR285 from Sartomer®), tetrahydrofurfuryl methacrylate, vinyl caprolactam, isobornyl acrylate, isobornyl methacrylate, 2-phenoxyethyl acrylate, 2-phenoxyethyl methacrylate, 2-(2-ethoxyethoxy)ethyl acrylate, isooctyl acrylate, isodecyl acrylate, isodecyl methacrylate, lauryl acrylate, lauryl methacrylate, stearyl acrylate, stearyl methacrylate, cyclic trimethylolpropane formal acrylate, 2-[[(Butylamino) carbonyl]oxy]ethyl acrylate (e.g. Genomer 1122 from RAHN USA Corporation), 3,3,5-trimethylcyclohexane acrylate, or mono-functional methoxylated PEG (350) acrylate. Suitable multifunctional monomers include diacrylates or dimethacrylates of diols and polyether diols, such as propoxylated neopentyl glycol diacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, 1,3-butylene glycol diacrylate, 1,3-butylene glycol dimethacrylate 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, alkoxylated aliphatic diacrylate (e.g., SR9209A from Sartomer®), diethylene glycol diacrylate, diethylene glycol dimethacrylate, dipropylene glycol diacrylate, tripropylene glycol diacrylate, triethylene glycol dimethacrylate, alkoxylated hexanediol diacrylates, or combinations thereof, for example SR562, SR563, SR564 from Sartomer®.


Typically, the reactive diluents used to form one or more of the pre-polymer compositions are least monofunctional, and undergo polymerization when exposed to free radicals, Lewis acids, and/or electromagnetic radiation. Examples of suitable reactive diluents include monoacrylate, 2-ethylhexyl acrylate, octyldecyl acrylate, cyclic trimethylolpropane formal acrylate, caprolactone acrylate, isobornyl acrylate (IBOA), or alkoxylated lauryl methacrylate.


Examples of suitable photoinitiators used to form one or more of the at least two different pre-polymer compositions include polymeric photoinitiators and/or oligomer photoinitiators, such as benzoin ethers, benzyl ketals, acetyl phenones, alkyl phenones, phosphine oxides, benzophenone compounds and thioxanthone compounds that include an amine synergist, or combinations thereof.


Examples of polishing pad materials formed of the pre-polymer compositions described above typically include at least one of oligomeric and, or, polymeric segments, compounds, or materials selected from the group consisting of: polyamides, polycarbonates, polyesters, polyether ketones, polyethers, polyoxymethylenes, polyether sulfone, polyetherimides, polyimides, polyolefins, polysiloxanes, polysulfones, polyphenylenes, polyphenylene sulfides, polyurethanes, polystyrene, polyacrylonitriles, polyacrylates, polymethylmethacrylates, polyurethane acrylates, polyester acrylates, polyether acrylates, epoxy acrylates, polycarbonates, polyesters, melamines, polysulfones, polyvinyl materials, acrylonitrile butadiene styrene (ABS), halogenated polymers, block copolymers, and random copolymers thereof, and combinations thereof.


The sacrificial material composition(s), which may be used to form the pores 210 described above, include water-soluble material, such as, glycols (e.g., polyethylene glycols), glycol-ethers, and amines. Examples of suitable sacrificial material precursors which may be used to form the pore forming features described herein include ethylene glycol, butanediol, dimer diol, propylene glycol-(1,2) and propylene glycol-(1,3), octane-1,8-diol, neopentyl glycol, cyclohexane dimethanol (1,4-bis-hydroxymethylcyclohexane), 2-methyl-1,3-propane diol, glycerine, trimethylolpropane, hexanediol-(1,6), hexanetriol-(1,2,6) butane triol-(1,2,4), trimethylolethane, pentaerythritol, quinitol, mannitol and sorbitol, methylglycoside, also diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycols, dibutylene glycol, polybutylene glycols, ethylene glycol, ethylene glycol monobutyl ether (EGMBE), diethylene glycol monoethyl ether, ethanolamine, diethanolamine (DEA), triethanolamine (TEA), and combinations thereof.


In some embodiments, the sacrificial material precursor comprises a water soluble polymer, such as 1-vinyl-2-pyrrolidone, vinylimidazole, polyethylene glycol diacrylate, acrylic acid, sodium styrenesulfonate, Hitenol BC10®, Maxemul 6106e, hydroxyethyl acrylate and [2-(methacryloyloxy)ethyltrimethylammonium chloride, 3-allyloxy-2-hydroxy-1-propanesulfonic acid sodium, sodium 4-vinylbenzenesulfonate, [2-(methacryloyloxy)ethyl]dimethyl-(3-sulfopropyl)ammonium hydroxide, 2-acrylamido-2-methyl-1-propanesulfonic acid, vinylphosphonic acid, allyltriphenylphosphonium chloride, (vinylbenzyl)trimethylammonium chloride, allyltriphenylphosphonium chloride, (vinylbenzyl)trimethylammonium chloride, E-SPERSE RS-1618, E-SPERSE RS-1596, methoxy polyethylene glycol monoacrylate, methoxy polyethylene glycol diacrylate, methoxy polyethylene glycol triacrylate, or combinations thereof.


Here, the additive manufacturing system 400 shown in FIG. 4A further includes the system controller 410 to direct the operation thereof. The system controller 410 includes a programmable central processing unit (CPU) 434 which is operable with a memory 435 (e.g., non-volatile memory) and support circuits 436. The support circuits 436 are conventionally coupled to the CPU 434 and comprise cache, clock circuits, input/output subsystems, power supplies, and the like, and combinations thereof coupled to the various components of the additive manufacturing system 400, to facilitate control thereof. The CPU 434 is one of any form of general purpose computer processor used in an industrial setting, such as a programmable logic controller (PLC), for controlling various components and sub-processors of the additive manufacturing system 400. The memory 435, coupled to the CPU 434, is non-transitory and is typically one or more of readily available memories such as random access memory (RAM), read only memory (ROM), floppy disk drive, hard disk, or any other form of digital storage, local or remote.


Typically, the memory 435 is in the form of a computer-readable storage media containing instructions (e.g., non-volatile memory), which when executed by the CPU 434, facilitates the operation of the manufacturing system 400. The instructions in the memory 435 are in the form of a program product such as a program that implements the methods of the present disclosure.


The program code may conform to any one of a number of different programming languages. In one example, the disclosure may be implemented as a program product stored on computer-readable storage media for use with a computer system. The program(s) of the program product define functions of the embodiments (including the methods described herein).


Illustrative computer-readable storage media include, but are not limited to: (i) non-writable storage media (e.g., read-only memory devices within a computer such as CD-ROM disks readable by a CD-ROM drive, flash memory, ROM chips or any type of solid-state non-volatile semiconductor memory) on which information is permanently stored; and (ii) writable storage media (e.g., floppy disks within a diskette drive or hard-disk drive or any type of solid-state random-access semiconductor memory) on which alterable information is stored. Such computer-readable storage media, when carrying computer-readable instructions that direct the functions of the methods described herein, are embodiments of the present disclosure. In some embodiments, the methods set forth herein, or portions thereof, are performed by one or more application specific integrated circuits (ASICs), field-programmable gate arrays (FPGAs), or other types of hardware implementations. In some other embodiments, the polishing pad manufacturing methods set forth herein are performed by a combination of software routines, ASIC(s), FPGAs and, or, other types of hardware implementations.


Here, the system controller 410 directs the motion of the manufacturing support 402, the motion of the dispense heads 404 and 406, the firing of the nozzles 416 to eject droplets of pre-polymer compositions therefrom, and the degree and timing of the curing of the dispensed droplets provided by the UV radiation source 408. In some embodiments, the instructions used by the system controller to direct the operation of the manufacturing system 400 include droplet dispense patterns for each of the print layers to be formed. In some embodiments, the droplet dispense patterns are collectively stored in the memory 425 as CAD-compatible digital printing instructions. Examples of print instructions which may be used by the additive manufacturing system 400 to manufacture the polishing pads described herein are shown in FIGS. 5A-5C.



FIGS. 5A-5C show portions of CAD compatible print instructions 500a-c which may be used by the additive manufacturing system 400 to form embodiments of the polishing pads described herein. Here, the print instructions 500a-c are for print layers used to form polishing elements 504a-c respectively. Each of the polishing elements 504a-c are formed of the polymer material 212 and comprise relatively high porosity regions A disposed proximate to the sidewalls of the polishing elements 504a-c and relatively low porosity regions B disposed inwardly of the relatively high porosity regions A. Droplets of the pre-polymer composition(s) used to form the polymer material 212 will be dispensed in the white regions and droplets of the sacrificial material composition(s) will be dispensed within the black pixels of the high porosity regions A. In this print layer, no droplets will be dispensed in the black regions 506 between the polishing elements 504a-c (outside of the relatively high porosity regions A). The print instructions 500a-c may be used to form relatively high porosity regions A each having a porosity of 25%, 16%, and 11% respectively and relatively low porosity regions B having no intended porosity (e.g., less than about 0.1% porosity). Here, the width W(1) of each polishing element 504a-c is about 2.71 mm, the widths W(2) of the relatively high porosity regions A are each about 460 μm, and the width W(3) of the relatively low porosity region B is about 1.79 mm.


Polishing pads formed according to embodiments described herein show unexpectedly superior performance in dielectric CMP processing when compared to similar polishing pads having uniformly distributed porosity. A comparison of CMP performance between continuous porosity and a selective porosity pad is set forth in Table 1 below. Sample polishing pad D in table 1 was formed using the print instructions 500a of FIG. 5A. Sample polishing pads A-C were formed using the same material precursors and substantially the same print instructions as 500a except the pores of sample polishing pads A-C were uniformly distributed across the polishing elements to achieve uniform porosities of 33%, 11%, and 5% respectively. Each of the sample polishing pads A-D were used to polish a blanket film of silicon oxide film layer disposed on a patterned substrate comprising a design architecture used in manufacture of logic and memory devices. The silicon oxide film was conventionally deposited using a tetraethylorthosilicate (TEOS) precursor. Surprisingly, the sample polishing pad D having selectively arranged regions of relatively high porosity disposed adjacent to regions of relatively low porosity provided desirably higher oxide removal rates when compared to polishing pads have uniformly distributed porosity values both higher and lower than that of the A regions of sample D.
















TABLE 1










Polish




Sample
Segment
Feature


Layer

Normalized


Polishing
Length
Width

Porosity
Hardness
Foundation
Maximum Oxide


Pads
(mm)
(mm)
Comments
(%)
(Shore D)
Layer
Removal Rate







A
100
2.71
Continuous
33%
55D
62D
100.0%


B
100
2.71
Porosity
11%
63D
62D
161.5%


C
100
2.71

 5%
71D
62D
138.5%


D
100
2.71
Porosity
25% on
55D
62D
200.0%





only on
Edge








edge of the
Only








pads










FIG. 6 is a flow diagram setting forth a method of forming a print layer of a polishing pad according to one or more embodiments. Embodiments of the method 600 may be used in combination with one or more of the systems and system operations described herein, such as the additive manufacturing system 400 of FIG. 4A, the fixed droplets of FIG. 4B, and the print instructions of FIGS. 5A-5C. Further, embodiments of the method 600 may be used to form any one or combination of embodiments of the polishing pads shown and described herein.


While FIGS. 5A-5C illustrate a configuration where a polishing feature includes a relatively high porosity regions A disposed proximate to the sidewalls of the polishing elements 504a-c and a relatively low porosity regions B disposed inwardly of the relatively high porosity regions A this configuration is not intended to be limiting as to the scope of the disclosure provided herein, since it may be desirable, depending on the polishing application, to alternately form the relatively high porosity regions A proximate to the inward region of the polishing elements 504a-c and form the relatively low porosity regions B proximate to the sidewalls of the polishing elements 504a-c.


At activity 601 the method 600 includes dispensing droplets of a pre-polymer composition and droplets of a sacrificial material composition onto a surface of a previously formed print layer according to a predetermined droplet dispense pattern.


At activity 602 the method 600 includes at least partially curing the dispensed droplets of the pre-polymer composition to form a print layer comprising at least portions of a polymer pad material having one or more relatively high porosity regions and one or more relatively low porosity regions disposed adjacent to the one or more relatively high porosity regions.


In some embodiments, the method 600 further includes sequential repetitions of activities 601 and 602 to form a plurality of print layers stacked in a Z-direction, i.e., a direction orthogonal to the surface of the manufacturing support or a previously formed print layer disposed thereon. The predetermined droplet dispense pattern used to form each print layer may be the same or different as a predetermined droplet dispense pattern used to form a previous print layer disposed there below.


The polishing pads and polishing pad manufacturing methods described herein beneficially allow for selectively arranged pores and resulting discrete regions of porosity that enable fine tuning of CMP process performance.


While the foregoing is directed to embodiments of the present disclosure, other and further embodiments of the disclosure may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.

Claims
  • 1. A polishing pad, comprising: a plurality of polishing elements, each comprising: an individual surface that forms a portion of a polishing surface of the polishing pad; andone or more sidewalls extending downwardly from the individual surface to define a plurality of channels disposed between the polishing elements, wherein each of the polishing elements is formed of a continuous phase of polymer material having one or more first regions comprising a first porosity and a second region comprising a second porosity,porosity is a volume of void-space or sacrificial material as a percentage of total volume in the respective first and second regions,the second porosity is less than the first porosity,the one or more first regions comprising the first porosity having selectively arranged pores; andthe one or more first regions comprising the first porosity are disposed proximate to the one or more sidewalls and the second region comprising the second porosity is disposed inwardly from the one or more first regions.
  • 2. The polishing pad of claim 1, wherein the first porosity is about 3% or more and the second porosity is less than ⅘ths of the first porosity.
  • 3. The polishing pad of claim 2, wherein the second region comprises substantially no porosity.
  • 4. The polishing pad of claim 3, further comprising: a foundation layer, whereinthe plurality of polishing elements are disposed on the foundation layer,the sidewalls of the individual polishing elements extend upwardly from a surface of the foundation layer, andthe foundation layer is formed of a different pre-polymer composition than a pre-polymer composition used to form the continuous phase of polymer material of the polishing elements.
  • 5. The polishing pad of claim 1, wherein the one or more first regions disposed proximate to the sidewall has a width in a range of about 50 μm to about 2 mm.
  • 6. The polishing pad of claim 5, wherein the second region disposed inwardly from the one or more first regions has a width in a range of about 50 μm to about 5 mm.
  • 7. The polishing pad of claim 1, wherein the selectively arranged pores of the one or more first regions are vertically disposed in one or more columnar arrangements where the selectively arranged pores in each column of the columnar arrangement are in substantial vertical alignment and spaced apart by the continuous phase of polymer material.
  • 8. The polishing pad of claim 1, wherein the selectively arranged pores of the one or more first regions are vertically disposed in one or more staggered columnar arrangements where each pore is offset in one or both of the X-Y directions with respect to a pore that is disposed thereabove and/or therebelow.
  • 9. The polishing pad of claim 1, wherein the plurality of polishing elements comprise a plurality of segmented concentric rings disposed about a post and extending radially outward from the post.
  • 10. The polishing pad of claim 9, wherein the post is disposed in a center of the polishing pad.
  • 11. The polishing pad of claim 9, wherein the post is offset from a center of the polishing pad.
  • 12. A method of polishing a substrate, comprising: urging a substrate against a polishing surface of a polishing pad, the polishing pad comprising a plurality of polishing elements, each comprising: an individual surface that forms a portion of the polishing surface; andone or more sidewalls extending downwardly from the individual surface to define a plurality of channels disposed between the polishing elements, whereineach of the polishing elements is formed of a continuous phase of polymer material having one or more first regions comprising a first porosity and a second region comprising a second porosity,porosity is a volume of void-space or sacrificial material as a percentage of total volume in the respective first and second regions, and the second porosity is less than the first porosity,the one or more first regions comprising the first porosity having selectively arranged pores; andthe one or more first regions comprising the first porosity are disposed proximate to the one or more sidewalls and the second region comprising the second porosity is disposed inwardly from the one or more first regions.
  • 13. The method of claim 12, wherein the first porosity is about 3% or more and the second porosity is less than ⅘ths of the first porosity.
  • 14. The method of claim 12, wherein the polishing pad further comprises a foundation layer,the plurality of polishing elements are disposed on the foundation layer,the sidewalls of the individual polishing elements extend upwardly from a surface of the foundation layer, andthe foundation layer is formed of a different pre-polymer composition than a pre-polymer composition used to form the continuous phase of polymer material of the polishing elements.
  • 15. A polishing pad, comprising: a foundation layer; anda plurality of polishing elements disposed on the foundation layer, each comprising: an individual surface that forms a portion of a polishing surface of the polishing pad; andone or more sidewalls extending downwardly from the individual surface to a surface of the foundation layer, wherein the sidewalls and the surface of the foundation layer define a plurality of channels disposed between the polishing elements, wherein each of the polishing elements is formed of a continuous phase of polymer material having one or more first regions comprising a first porosity and a second region comprising a second porosity,porosity is a volume of void-space or sacrificial material as a percentage of total volume in the respective first and second regions,the second porosity is less than the first porosity,the one or more first regions comprising the first porosity having selectively arranged pores,the one or more first regions comprising the first porosity are disposed proximate to the one or more sidewalls and the second region comprising the second porosity is disposed inwardly from the one or more first regions,the one or more first regions has a height extending from the individual surface of the polishing element to the surface of the foundation layer and a width extending from the one or more sidewalls to the second region comprising the second porosity, andthe width of the one or more first regions is less than a width of the second region comprising the second porosity.
  • 16. The polishing pad of claim 15, wherein the first porosity is about 3% or more and the second porosity is less than ⅘ths of the first porosity and the second region comprises substantially no porosity.
  • 17. The polishing pad of claim 16, wherein the one or more first regions has a width in a range of about 50 μm to about 2 mm and the second region has a width in a range of about 50 μm to about 5 mm.
  • 18. The polishing pad of claim 15, wherein the selectively arranged pores of the one or more first regions are vertically disposed in one or more columnar arrangements where the selectively arranged pores in each column of the columnar arrangement are in substantial vertical alignment and spaced apart by the continuous phase of polymer material.
  • 19. The polishing pad of claim 15, wherein the selectively arranged pores of the one or more first regions are vertically disposed in one or more staggered columnar arrangements where each pore is offset in one or both of the X-Y directions with respect to a pore that is disposed thereabove and/or therebelow.
  • 20. The polishing pad of claim 15, wherein the plurality of polishing elements comprise a plurality of segmented concentric rings disposed about a post and extending radially outward from the post.
CROSS-REFERENCE TO RELATED APPLICATIONS

This patent application claims priority to U.S. Provisional Application No. 62/951,938, filed on Dec. 20, 2019, which is herein incorporated by reference in its entirety.

US Referenced Citations (361)
Number Name Date Kind
2001911 Wooddell et al. May 1935 A
3357598 Kraft Dec 1967 A
3741116 Green et al. Jun 1973 A
4459779 Shen Jul 1984 A
4575330 Hull Mar 1986 A
4836832 Tumey et al. Jun 1989 A
4844144 Murphy et al. Jul 1989 A
4942001 Murphy et al. Jul 1990 A
5096530 Cohen Mar 1992 A
5120476 Scholz Jun 1992 A
5121329 Crump Jun 1992 A
5178646 Barber, Jr. et al. Jan 1993 A
5212910 Breivogel et al. May 1993 A
5287663 Pierce et al. Feb 1994 A
5300417 Lushington et al. Apr 1994 A
5387380 Cima et al. Feb 1995 A
5533923 Shamouilian et al. Jul 1996 A
5605760 Roberts Feb 1997 A
5609517 Lofaro Mar 1997 A
5624303 Robinson Apr 1997 A
5626919 Chapman et al. May 1997 A
5645471 Strecker Jul 1997 A
5738574 Tolles et al. Apr 1998 A
5876268 Lamphere et al. Mar 1999 A
5900164 Budinger et al. May 1999 A
5905099 Everaerts et al. May 1999 A
5906863 Lombardi et al. May 1999 A
5921855 Osterheld et al. Jul 1999 A
5932040 Audisio Aug 1999 A
5932290 Lombardi et al. Aug 1999 A
5940674 Sachs et al. Aug 1999 A
5944583 Cruz et al. Aug 1999 A
5965460 Rach et al. Oct 1999 A
5976000 Hudson Nov 1999 A
5984769 Bennett et al. Nov 1999 A
5989111 Lamphere et al. Nov 1999 A
5989470 Doan et al. Nov 1999 A
6022264 Cook et al. Feb 2000 A
6029096 Manners et al. Feb 2000 A
6036579 Cook et al. Mar 2000 A
6062968 Sevilla et al. May 2000 A
6090475 Robinson et al. Jul 2000 A
6095902 Reinhardt Aug 2000 A
6117000 Anjur et al. Sep 2000 A
6121143 Messner et al. Sep 2000 A
6122564 Koch et al. Sep 2000 A
6126532 Sevilla et al. Oct 2000 A
6155910 Amphere et al. Dec 2000 A
6206759 Agarwal et al. Mar 2001 B1
6210254 Cook et al. Apr 2001 B1
6213845 Elledge Apr 2001 B1
6231942 Blizard et al. May 2001 B1
6241596 Osterheld et al. Jun 2001 B1
6254460 Walker et al. Jul 2001 B1
6273806 Bennett et al. Aug 2001 B1
6322728 Brodkin et al. Nov 2001 B1
6328634 Shen et al. Dec 2001 B1
6361411 Chopra et al. Mar 2002 B1
6361832 Agarwal et al. Mar 2002 B1
6390890 Molnar May 2002 B1
6423255 Hoechsmann et al. Jul 2002 B1
6428586 Yancey Aug 2002 B1
6454634 James et al. Sep 2002 B1
6488570 James et al. Dec 2002 B1
6500053 James et al. Dec 2002 B2
6518162 Ono et al. Feb 2003 B2
6520834 Marshall Feb 2003 B1
6520847 Osterheld et al. Feb 2003 B2
6530829 Kramer Mar 2003 B1
6544373 Chen et al. Apr 2003 B2
6569373 Napadensky May 2003 B2
6582283 James et al. Jun 2003 B2
6585563 Redeker et al. Jul 2003 B1
6592443 Kramer et al. Jul 2003 B1
6641463 Molnar Nov 2003 B1
6641471 Pinheiro et al. Nov 2003 B1
6645061 Bennett et al. Nov 2003 B1
6682402 Roberts et al. Jan 2004 B1
6699115 Osterheld et al. Mar 2004 B2
6719818 Birang et al. Apr 2004 B1
6736709 James et al. May 2004 B1
6746225 McHugh Jun 2004 B1
6749485 James et al. Jun 2004 B1
6749714 Ishikawa et al. Jun 2004 B1
6790883 Ogawa et al. Sep 2004 B2
6796880 Redeker et al. Sep 2004 B2
6811937 Lawton Nov 2004 B2
6833046 Wright Dec 2004 B2
6840843 Jones et al. Jan 2005 B2
6855588 Liao et al. Feb 2005 B1
6860793 Budinger et al. Mar 2005 B2
6860802 Vishwanathan et al. Mar 2005 B1
6869350 Roberts et al. Mar 2005 B2
6875096 Park et al. Apr 2005 B2
6875097 Grunwald Apr 2005 B2
6896593 Prasad May 2005 B2
6913517 Prasad Jul 2005 B2
6935931 Prasad Aug 2005 B2
6955588 Anderson, II et al. Oct 2005 B1
6984163 Roberts Jan 2006 B2
6991517 Redeker et al. Jan 2006 B2
6998166 Prasad Feb 2006 B2
7077879 Ogawa et al. Jul 2006 B2
7120512 Kramer et al. Oct 2006 B2
7132033 Boldizar et al. Nov 2006 B2
7169030 Kulp Jan 2007 B1
7195544 Prasad Mar 2007 B2
7252871 Crkvenac et al. Aug 2007 B2
7264641 Prasad Sep 2007 B2
7267607 Prasad Sep 2007 B2
7300619 Napadensky et al. Nov 2007 B2
7311862 Prasad Dec 2007 B2
7371160 Cruz et al. May 2008 B1
7377840 Deopura et al. May 2008 B2
7425172 Misra et al. Sep 2008 B2
7435161 Prasad et al. Oct 2008 B2
7435165 Prasad Oct 2008 B2
7438636 Kulp et al. Oct 2008 B2
7445847 Kulp Nov 2008 B2
7455571 Kuo et al. Nov 2008 B1
7497885 Kollodge Mar 2009 B2
7517277 Muldowney Apr 2009 B2
7517488 Saikin Apr 2009 B2
7530880 Bajaj et al. May 2009 B2
7531117 Ederer et al. May 2009 B2
7537446 James et al. May 2009 B2
7635290 Muldowney Dec 2009 B2
7699684 Prasad Apr 2010 B2
7704122 Misra et al. Apr 2010 B2
7704125 Roy et al. Apr 2010 B2
7815778 Bajaj Oct 2010 B2
7828634 Jiang et al. Nov 2010 B2
7846008 Bajaj Dec 2010 B2
7976901 Kume et al. Jul 2011 B2
8066555 Bajaj Nov 2011 B2
8075372 Prasad Dec 2011 B2
8075745 Bajaj Dec 2011 B2
8118641 Kulp et al. Feb 2012 B2
8142860 Vanmaele et al. Mar 2012 B2
8142869 Kobayashi et al. Mar 2012 B2
8177603 Bajaj May 2012 B2
8257545 Loyack et al. Sep 2012 B2
8260447 Mattes et al. Sep 2012 B2
8287793 Deopura et al. Oct 2012 B2
8288448 Kulp Oct 2012 B2
8292692 Bajaj Oct 2012 B2
8377623 Fong Feb 2013 B2
8380339 Misra et al. Feb 2013 B2
8398466 Sung et al. Mar 2013 B2
8546717 Stecker Oct 2013 B2
8598523 Stecker et al. Dec 2013 B2
8602851 Lombardo et al. Dec 2013 B2
8702479 Huang et al. Apr 2014 B2
8709114 Cantrell et al. Apr 2014 B2
8715035 Roy et al. May 2014 B2
8784721 Philippi et al. Jul 2014 B2
8801949 Lakrout et al. Aug 2014 B2
8821214 Joseph Sep 2014 B2
8864859 Roy et al. Oct 2014 B2
8883392 Napadensky et al. Nov 2014 B2
8888480 Yoo et al. Nov 2014 B2
8894799 Lakrout Nov 2014 B2
8932116 Deopura et al. Jan 2015 B2
8932511 Napadensky Jan 2015 B2
8986585 Cantrell et al. Mar 2015 B2
9017140 Allison et al. Apr 2015 B2
9067297 Allison et al. Jun 2015 B2
9067299 Bajaj et al. Jun 2015 B2
9108291 Lakrout Aug 2015 B2
9156124 Allison et al. Oct 2015 B2
9162340 Joseph et al. Oct 2015 B2
9162341 LeFevre et al. Oct 2015 B2
9259820 Qian et al. Feb 2016 B2
9259821 Qian et al. Feb 2016 B2
9278424 Roy et al. Mar 2016 B2
9296085 Bajaj et al. Mar 2016 B2
9314897 Qian et al. Apr 2016 B2
9333620 Qian et al. May 2016 B2
9421666 Krishnan et al. Aug 2016 B2
9457520 Bajaj et al. Oct 2016 B2
9587127 Herlihy et al. Mar 2017 B2
9630249 Toyserkani et al. Apr 2017 B2
9744724 Bajaj et al. Aug 2017 B2
9776361 Krishnan et al. Oct 2017 B2
9873180 Bajaj et al. Jan 2018 B2
9925637 Yoshida Mar 2018 B2
9993907 Murugesh et al. Jun 2018 B2
10335994 Napadensky et al. Jul 2019 B2
10456886 Ganapathiappan et al. Oct 2019 B2
20010008830 Tolles et al. Jul 2001 A1
20010020448 Vaartstra et al. Sep 2001 A1
20010041511 Lack et al. Nov 2001 A1
20010046834 Ramana et al. Nov 2001 A1
20020016139 Hirokawa et al. Feb 2002 A1
20020058468 Eppert et al. May 2002 A1
20020077036 Roberts et al. Jun 2002 A1
20020112632 Faibish Aug 2002 A1
20020173248 Doan et al. Nov 2002 A1
20030019570 Chen et al. Jan 2003 A1
20030022611 Bartlett et al. Jan 2003 A1
20030056870 Comb et al. Mar 2003 A1
20030134581 Wang et al. Jul 2003 A1
20030153253 Hanamoto et al. Aug 2003 A1
20030181137 Redeker et al. Sep 2003 A1
20030205325 Boyd et al. Nov 2003 A1
20030220061 Prasad Nov 2003 A1
20040003895 Amano et al. Jan 2004 A1
20040033758 Wiswesser Feb 2004 A1
20040055223 Ono et al. Mar 2004 A1
20040058623 Lin et al. Mar 2004 A1
20040106367 Walker et al. Jun 2004 A1
20040126575 Yoshida et al. Jul 2004 A1
20040133298 Toyserkani et al. Jul 2004 A1
20040154533 Agarwal et al. Aug 2004 A1
20040173946 Pfeifer et al. Sep 2004 A1
20040175451 Maekawa et al. Sep 2004 A1
20040180611 Tajima et al. Sep 2004 A1
20040187714 Napadensky et al. Sep 2004 A1
20040198185 Redeker et al. Oct 2004 A1
20050003189 Bredt et al. Jan 2005 A1
20050020082 Vishwanathan et al. Jan 2005 A1
20050062900 Kim Mar 2005 A1
20050086869 Park et al. Apr 2005 A1
20050098540 Prasad May 2005 A1
20050101228 Prasad May 2005 A1
20050110853 Gardner et al. May 2005 A1
20050153634 Prasad et al. Jul 2005 A1
20050171224 Kulp Aug 2005 A1
20050215177 Prasad Sep 2005 A1
20050227590 Sung Oct 2005 A1
20050250431 Shih et al. Nov 2005 A1
20050284536 Kojima et al. Dec 2005 A1
20060019587 Deopura et al. Jan 2006 A1
20060052040 Prasad Mar 2006 A1
20060125133 Huh et al. Jun 2006 A1
20060160478 Donohue et al. Jul 2006 A1
20060185256 Nevoret et al. Aug 2006 A1
20060192315 Farr et al. Aug 2006 A1
20060226567 James et al. Oct 2006 A1
20060252900 Bowman et al. Nov 2006 A1
20060276109 Roy et al. Dec 2006 A1
20070007698 Sano Jan 2007 A1
20070009606 Serdy et al. Jan 2007 A1
20070054599 Taylor et al. Mar 2007 A1
20070117393 Tregub et al. May 2007 A1
20070128874 Shida et al. Jun 2007 A1
20070128991 Yoon et al. Jun 2007 A1
20070149096 Nishimura et al. Jun 2007 A1
20070212979 Preston Sep 2007 A1
20070221287 Izumoto Sep 2007 A1
20070235133 Benassi Oct 2007 A1
20070235904 Saikin Oct 2007 A1
20080009228 Nagase et al. Jan 2008 A1
20080057845 Prasad Mar 2008 A1
20080105818 Cohen May 2008 A1
20080157436 Patel et al. Jul 2008 A1
20080207100 Roy et al. Aug 2008 A1
20080211141 Deopura et al. Sep 2008 A1
20080255823 Grant Oct 2008 A1
20080314878 Cai et al. Dec 2008 A1
20090011679 Bajaj et al. Jan 2009 A1
20090053976 Roy et al. Feb 2009 A1
20090093201 Kazuno et al. Apr 2009 A1
20090105363 Napadensky Apr 2009 A1
20090206065 Kruth et al. Aug 2009 A1
20090253353 Ogawa et al. Oct 2009 A1
20090270019 Bajaj Oct 2009 A1
20090311955 Kerprich et al. Dec 2009 A1
20090321979 Hiraide Dec 2009 A1
20100007692 Vanmaele et al. Jan 2010 A1
20100087128 Nakayama et al. Apr 2010 A1
20100120249 Hirose et al. May 2010 A1
20100120343 Kato et al. May 2010 A1
20100140850 Napadensky et al. Jun 2010 A1
20100203815 Bajaj Aug 2010 A1
20100210197 Matsumura et al. Aug 2010 A1
20100323050 Kumagai et al. Dec 2010 A1
20110011217 Kojima Jan 2011 A1
20110059247 Kuzusako et al. Mar 2011 A1
20110077321 Napadensky Mar 2011 A1
20110130077 Litke et al. Jun 2011 A1
20110171890 Nakayama et al. Jul 2011 A1
20110180952 Napadensky Jul 2011 A1
20110183583 Joseph Jul 2011 A1
20120178845 Napadensky et al. Jul 2012 A1
20120302148 Bajaj et al. Nov 2012 A1
20120315830 Joseph et al. Dec 2012 A1
20130012108 Li et al. Jan 2013 A1
20130017769 Kimura Jan 2013 A1
20130019570 Weible Jan 2013 A1
20130055568 Dusel et al. Mar 2013 A1
20130059506 Qian et al. Mar 2013 A1
20130059509 Deopura et al. Mar 2013 A1
20130122705 Babu et al. May 2013 A1
20130137350 Allison et al. May 2013 A1
20130172509 Pawloski et al. Jul 2013 A1
20130183824 Kwon et al. Jul 2013 A1
20130212951 Ahn et al. Aug 2013 A1
20130231032 Swedek et al. Sep 2013 A1
20130283700 Bajaj et al. Oct 2013 A1
20130307194 Elsey Nov 2013 A1
20130309951 Benvegnu et al. Nov 2013 A1
20130316081 Kovalcik et al. Nov 2013 A1
20130328228 Pettis et al. Dec 2013 A1
20140048970 Batchelder et al. Feb 2014 A1
20140117575 Kemperle et al. May 2014 A1
20140163717 Das et al. Jun 2014 A1
20140206268 Lefevre et al. Jul 2014 A1
20140239527 Lee Aug 2014 A1
20140324206 Napadensky Oct 2014 A1
20140370214 Araki et al. Dec 2014 A1
20140370788 Nair Dec 2014 A1
20150024233 Gunther Jan 2015 A1
20150031781 Landers et al. Jan 2015 A1
20150037601 Blackmore Feb 2015 A1
20150038066 Tuang et al. Feb 2015 A1
20150045928 Perez et al. Feb 2015 A1
20150056421 Yudovin-Farber et al. Feb 2015 A1
20150056892 Vacassy et al. Feb 2015 A1
20150056895 Fotou et al. Feb 2015 A1
20150061170 Engel et al. Mar 2015 A1
20150065020 Roy et al. Mar 2015 A1
20150084238 Bonassar et al. Mar 2015 A1
20150093977 Deopura et al. Apr 2015 A1
20150115490 Reinarz Apr 2015 A1
20150123298 Napadensky May 2015 A1
20150126099 Krishnan et al. May 2015 A1
20150129798 Napadensky May 2015 A1
20150174826 Murugesh et al. Jun 2015 A1
20150216790 Feng et al. Aug 2015 A1
20160052103 Qian et al. Feb 2016 A1
20160068996 Lau et al. Mar 2016 A1
20160101500 Fung et al. Apr 2016 A1
20160107287 Bajaj et al. Apr 2016 A1
20160107288 Orilall et al. Apr 2016 A1
20160107290 Bajaj et al. Apr 2016 A1
20160107295 Bajaj et al. Apr 2016 A1
20160107381 Krishnan et al. Apr 2016 A1
20160114458 Bajaj et al. Apr 2016 A1
20160136787 Bajaj et al. May 2016 A1
20160176021 Orilall et al. Jun 2016 A1
20160221145 Huang et al. Aug 2016 A1
20160229023 Lugg et al. Aug 2016 A1
20160279757 Qian et al. Sep 2016 A1
20160354901 Krishnan et al. Dec 2016 A1
20170100817 Ganapathiappan et al. Apr 2017 A1
20170120416 Chockalingam et al. May 2017 A1
20170136603 Ganapathiappan et al. May 2017 A1
20170148539 Prestayko et al. May 2017 A1
20170151648 Huang et al. Jun 2017 A1
20170182629 Lehuu et al. Jun 2017 A1
20170203406 Ganapathiappan Jul 2017 A1
20170203408 Ganapathiappan et al. Jul 2017 A1
20170203409 Lefevre et al. Jul 2017 A1
20180043613 Krishnan et al. Feb 2018 A1
20180161954 Bajaj et al. Jun 2018 A1
20180236632 Murugesh et al. Aug 2018 A1
20180339402 Redfield et al. Nov 2018 A1
20190030678 Kumar et al. Jan 2019 A1
20190322031 Kritchman Oct 2019 A1
20200001433 Bajaj et al. Jan 2020 A1
Foreign Referenced Citations (48)
Number Date Country
1897226 Jan 2007 CN
101199994 Jun 2008 CN
101612722 Dec 2009 CN
203542340 Apr 2014 CN
103465155 May 2016 CN
104400998 Oct 2016 CN
104607639 Nov 2016 CN
104625945 Mar 2017 CN
104385595 May 2017 CN
104210108 Nov 2017 CN
19834559 Feb 2000 DE
10314075 Nov 2007 DE
1419876 Apr 2008 EP
H0267171 Mar 1990 JP
H08132342 May 1996 JP
H09076353 Mar 1997 JP
H11254542 Sep 1999 JP
H11347761 Dec 1999 JP
2000061817 Feb 2000 JP
2002151447 May 2002 JP
2003303793 Oct 2003 JP
2004235446 Aug 2004 JP
2004243518 Sep 2004 JP
2004281685 Oct 2004 JP
2005074614 Mar 2005 JP
3801100 Jul 2006 JP
2006231464 Sep 2006 JP
2007049146 Feb 2007 JP
4693024 Jun 2011 JP
4798713 Oct 2011 JP
5143528 Feb 2013 JP
2013107254 Jun 2013 JP
2016023209 Feb 2016 JP
20030020658 Mar 2003 KR
20050052876 Jun 2005 KR
100842486 Jul 2008 KR
20100028294 Mar 2010 KR
9830356 Jul 1998 WO
9849723 Nov 1998 WO
0164396 Sep 2001 WO
0224415 Mar 2002 WO
02070200 Sep 2002 WO
2007055678 May 2007 WO
2009158665 Dec 2009 WO
2010088246 Aug 2010 WO
2012173885 Dec 2012 WO
2014039378 Mar 2014 WO
2015168529 Nov 2015 WO
Non-Patent Literature Citations (23)
Entry
International Search Report and Written Opinion of the International Searching Authority for PCT/US2020/061656 dated Mar. 15, 2021, 11 pages.
Andrews, Rodney J., et al.—“Glass Transition Temperatures of Polymers,” Polymer Handbook, Fourth Edition, J. Brandrup et al., Editors, A Wiley Interscience Publication, John Wiley & Sons, Inc., 1999, VI / 193-198.
Antje M.J. Van Den Berg, “Inkjet Printing of Polyurethane Colloidal Suspensions”, www.rsc.org/softmatter. Jul. 13, 2006.
Byoung-Ho Kwon et al. “Dishing and Ersosion in STI CMP”. System IC R&D Center, Hyundai Electronics Industries Co. Ltd. 1999 IEEE. 3 pages.
H. Yang. “High Viscosity Jetting System for 3D Reactive Inkjet Printing”, Additive Manufacturing and 3D Printing Group, University of Nottingham. 9 pages.
I Hermant et al. “A Comparative Study of Polyurethane-Poly(Methyl Methacrylate) Interpenetrating and Semi-1 Interprenetrating Polymer Networks”, vol. 20, No. 1. pp. 85-89, 1984.
John J. Aklonis et al. “Introduction to Polymer Viscoelasticity”. Second Edition. 1983. 6 pages.
Lee M. Cook. “CMP Consumables II: Pad” Chapter 6. Semiconductors and Semimetals, vol. 63. Published 1999. Chemical Mechanical Polishing in Silicon Processing. ISBN: 978-0-12-752172-5.
U.S. Appl. No. 16/906,992, filed Jun. 19, 2020, entitled “Advanced Polishing Pads and Related Polishing Pad Manufacturing Methods.”
Peter Freeman et al. “A Study of the Variation of Physical Properties in Random Lots of Urethane Polishing Pads for CMP”. A Rodel Publication. vol. 2, Issue 6. Jun. 1996. 8 Pages.
Peter Krober et al. “Reactive Inkjet Printing of Polyurethanes”, www.rsc.org/materials. Journal of Materials Chemistry. Jan. 6, 2009.
Plastics in Action; 3-D Printing Speeds Prototype Development dated May/Jun. 1998; 2 total pages.
Rajeev Bajaj et al. “Effect of Polishing Pad Material Properties on Chemical Mechanical Polishing (CMP) Processes”. 1994. 8 pages.
Rodel. Rodel IC1000 CMP Pad. 1999. 2 pages.
Rodel. Rodel IC1010. 1998. 2 pages.
S. Raghavan et al. “Chemical Mechanical Planariarization in Integrated Circuit Device Manufacturing”. vol. 98-7. 1998. 19 pages.
Shahrubudin, N., et al.—“An Overview on 3D Printing Technology: Technological, Materials, and Applications,” 2nd International Conference on Sustainable Materials Processing and Manufacturing (SMPM 2019), Procedia Manufacturing, 35 (2019), published by Elsevier B.V., pp. 1286-1296.
Sigma-Aldrich—“Thermal Transitions of Homopolymers: Glass Transition & Melting Point” webpage, https://www.sigmaaldrich.com/technical-documents/articles/materials-science/polymer-scie . . . , printed Apr. 8, 2019, 3 pages.
The Dow Chemical Company—“DOW VLDPE DFDB-1085 NT, Very Low Density Polyethylene Resin” Technical Data, UL Prospector, Oct. 2003, 2 pages.
The Dow Chemical Company—“Specialty Elastomers for Automotive TPO Compounds” brochure, Nov. 2006, 8 pages.
Weidan Li et al. “The Effect of the Polishing Pad Treatments on the Chemical-Mechanical Polishing of SiO2 Films”, Thin Solid Films 270 (1995). 6 pages.
Whisnaut, David—“Polymer Chemistry: The Glass Transition” webpage, Engineering Libre Texts, https://eng.libretexts.org/Bookshelves/Materials_Schience?Supplemental_Modules_Materia . . . , printed Apr. 10, 2019, 2 pages.
Yu-Lim Jun et al. “Slicing Bitmap Generation and Patterning Technique a SFF System Using UV-Resin”, International Conference on Control, Automation and Systems 2007. 5 Pages.
Related Publications (1)
Number Date Country
20210187693 A1 Jun 2021 US
Provisional Applications (1)
Number Date Country
62951938 Dec 2019 US