Patent Application
20090159845
1. Field of the Invention
The present invention relates to a polishing slurry for chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal used in a substrate for a semiconductor device such as a light emitting element, an electronic element and a semiconductor sensor, a method of treating a surface of a GaxIn1-xAsyP1-y crystal using the polishing slurry, and a GaxIn1-xAsyP1-y crystal substrate obtained by the surface treating method.
2. Description of the Background Art
A GaxIn1-xAsyP1-y crystal (0≦x≦1, 0≦y≦1) such as a GaAs crystal and an InP crystal is very useful as a material for forming a substrate of a semiconductor device such as a light emitting element, an electronic element and a semiconductor sensor.
The GaxIn1-xAsyP1-y crystal substrate (0≦x≦1, 0≦y≦1) used as a substrate for a semiconductor device is obtained by subjecting an external circumference of a GaxIn1-xAsyP1-y crystal to shape forming processing, slicing the crystal to have a predetermined thickness, and grinding or lapping a surface thereof and, by such the slicing and, grinding or lapping, a procession denatured layer (this refers to a layer in which crystal lattices are disturbed, which is formed on a surface side region of a crystal by processing a crystal surface; the same hereinafter) is formed on a surface side region of the GaxIn1-xAsyP1-y crystal, and a roughness of a surface of the GaxIn1-xAsyP1-y crystal becomes great.
As a thickness of the procession denatured layer of this GaxIn1-xAsyP1-y crystal substrate becomes greater, or as a surface roughness thereof becomes greater, quality of a substrate surface is deteriorated, irregularities of a surface of a Group III-V compound crystal layer which is epitaxial-grown on this GaxIn1-xAsyP1-y crystal become great, and crystallizability of the surface is deteriorated. For this reason, a semiconductor device of better quality cannot be formed.
For this reason, as a method of forming a GaxIn1-xAsyP1-y crystal substrate from a GaxIn1-xAsyP1-y crystal, the following method is widely performed: GaxIn1-xAsyP1-y crystal is sliced to have a predetermined thickness, a surface thereof is ground or lapped and, further, the surface is polished chemically and mechanically, thereby, a procession denatured layer of a GaxIn1-xAsyP1-y crystal is removed, and a surface roughness is reduced.
As a polishing slurry for chemically mechanically polishing a surface of the GaxIn1-xAsyP1-y crystal, a polishing slurry containing spherical colloidal silica abrasive grains, an inorganic salt, and alkali metal chlorinated isocyanurate which is an oxidizing agent (e.g. see Japanese Patent Publication No. 3077665 (hereinafter, referred to as Patent Document 1)), and a polishing slurry containing spherical colloidal silica abrasive grains, a mineral acid and persulfate which is an oxidizing agent (e.g. see Japanese Patent Laying-Open No. 64-087147 (hereinafter, referred to as Patent Document 2)) are proposed. In chemical mechanical polishing (hereinafter, referred to as CMP) using these polishing slurries, a surface of a GaxIn1-xAsyP1-y crystal is oxidized with an oxidizing agent and a mineral acid to form an oxidized layer, and this oxidized layer is removed with colloidal silica abrasive grains.
However, in polishing slurries shown in Patent Document 1 and Patent Document 2, since spherical colloidal silica abrasive grains are used as abrasive grains, a rate of polishing a GaxIn1-xAsyP1-y crystal is low due to a low rate of removing the oxidized layer, and an efficiency of CMP is low. When a colloidal silica abrasive grain having a large particle diameter is used, a polishing rate can be enhanced, but a surface roughness is increased. In addition, also when an abrasive grain having a higher hardness than that of a colloidal silica abrasive grain, such as an Al2O3 abrasive grain is used, a polishing rate can be enhanced, but since a new procession denatured layer is formed due to this abrasive grain having a high hardness, better surface quality can not be obtained.
An object of the present invention is to provide a polishing slurry which can form a crystal surface having a small surface roughness on a GaxIn1-xAsyP1-y crystal at a high polishing rate and effectively, a method of treating a surface of a GaxIn1-xAsyP1-y crystal using such the polishing slurry, and a GaxIn1-xAsyP1-y crystal substrate obtained by such the surface treating method.
The present invention provides a polishing slurry for chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal (0≦x≦1, 0≦y≦1), characterized in that this polishing slurry contains abrasive grains formed of SiO2, this abrasive grain is a secondary particle in which primary particles are associated, and a ratio d2/d1 of an average particle diameter d2 of a secondary particle to an average particle diameter d1 of a primary particle is not less than 1.6 and not more than 10.
In the polishing slurry of the present invention, an average particle diameter d2 of a secondary particle of an abrasive grain can be not less than 30 nm and not more than 300 nm. In addition, a shape of an abrasive grain may be at least any shape of a cocoon shape, a mass shape and a chain shape. In addition, the abrasive grain content can be not less than 5 mass % and not more than 40 mass %. In addition, an abrasive grain can be formed of colloidal silica. In addition, a value X of a pH and a value Y (mV) of a oxidation-reduction potential of the polishing slurry can satisfy both relationships of the following equation (1) and equation (2):
Y≧−50X+1000 (1)
Y≦−50X+1900 (2)
In addition, a pH of the polishing slurry can be not more than 5 or not less than 8. In addition, the polishing slurry can contain the aforementioned abrasive grains, an organic acid and/or a salt thereof, and an oxidizing agent.
Also, the present invention provides a method of treating a surface of a GaxIn1-xAsyP1-y crystal (0≦x≦1, 0≦y≦1) using a polishing slurry, and this surface treating method is a method of treating a surface of a GaxIn1-xAsyP1-y crystal including the steps of: preparing a polishing slurry characterized in that the polishing slurry contains abrasive grains formed of SiO2, this abrasive grain is a secondary particle in which primary particles are associated, and a ratio d2/d1 of an average particle diameter d2 of a secondary particle to an average particle diameter d1 of a primary particle is not less than 1.6 and not more than 10; and chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal using the polishing slurry.
In the method of treating a surface of a GaxIn1-xAsyP1-y crystal of the present invention, a step of chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal using the polishing slurry can be performed by rotating a polishing pad and a GaxIn1-xAsyP1-y crystal on different rotation axes at a rotation number of not less than 10/min and not more than 200/min and at a polishing pressure of not less than 4.9 kPa (50 gf/cm2) and not more than 98 kPa (1000 gf/cm2) by interposing the polishing slurry between the polishing pad and the GaxIn1-xAsyP1-y crystal.
The method of treating a surface of a GaxIn1-xAsyP1-y crystal of the present invention can include a step of washing a surface of the chemically mechanically polished GaxIn1-xAsyP1-y crystal with pure water after the step of chemically mechanically polishing. Alternatively, the step may include a step of polishing a surface of the chemically mechanically polished GaxIn1-xAsyP1-y crystal using a polishing solution formed of an acidic aqueous solution or a basic aqueous solution after the step of chemical mechanical polishing. Further, the method may include a step of washing a surface of the GaxIn1-xAsyP1-y crystal which has been polished using the polishing solution with pure water after the step of polishing using the polishing solution.
Also, the present invention provides a GaxIn1-xAsyP1-y crystal substrate obtained by a method of treating a surface of a GaxIn1-xAsyP1-y crystal, in which the surface treating method includes the steps of: preparing a polishing slurry characterized in that the polishing slurry contains abrasive grains formed of SiO2, this abrasive grain is a secondary particle in which primary particles are associated, and a ratio d2/d1 of an average particle diameter d2 of a secondary particle to an average particle diameter d1 of a primary particle is not less than 1.6 and not more than 10; and chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal using this polishing slurry.
According to the present invention, a polishing slurry which can form a crystal surface having a small surface roughness on a GaxIn1-xAsyP1-y crystal at a high polishing rate and effectively, a method of treating a surface of a GaxIn1-xAsyP1-y crystal using such the polishing slurry, and a GaxIn1-xAsyP1-y crystal substrate obtained by such the surface treating method can be provided.
The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
One embodiment of a polishing slurry of the present invention is a polishing slurry for chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal (0≦x≦1, 0≦y≦1), characterized in that this polishing slurry contains abrasive grains formed of SiO2, this abrasive grain is a secondary particle in which primary particles are associated, and a ratio d2/d1 of an average particle diameter d2 of a secondary particle to an average particle diameter d1 of a primary particle is not less than 1.6 and not more than 10.
Herein, chemical mechanical polishing refers to smoothing chemically and mechanically a surface of a subject to be abraded, using a polishing slurry. Referring to
Polishing slurry 17 of the present embodiment, by containing abrasive grains 16 formed of SiO2, can remove a procession denatured layer 1a of GaxIn1-xAsyP1-y crystal 1 to reduce a surface roughness.
In addition, since abrasive grain 16 is a secondary particle in which primary particles are associated, a polishing rate is increased, and it becomes possible to effectively treat a surface of GaxIn1-xAsyP1-y crystal 1. By association of primary particles to become a secondary particle, an abrasive grain having an edgeless irregular shape on its surface is formed, and a polishing rate can be enhanced without generating a scratch. When an abrasive grain having a surface on which an edge is present is used, a scratch is generated upon polishing, and it becomes difficult to reduce a surface roughness. In addition, from a viewpoint of formation of an edgeless irregular shape, it is preferable that a primary particle is spherical or a shape of a spheroid.
Herein, from a viewpoint that a primary particle is spherical or a shape of a spheroid, and a secondary particle having an edgeless irregular shape on its surface is easily formed, it is preferable that an abrasive grain is formed of SiO2 such as fumed silica and colloidal silica, particularly, colloidal silica. As a method of synthesizing colloidal silica, there are a synthesis method using a water glass (sodium silicate etc.) as a raw material, and a synthesis method using alkoxysilane as a raw material (sol-gel method). The former is low cost, and easily produces colloidal silica in a large amount, and the latter affords an abrasive grain having a high purity. By regulating the synthesis condition, a particle diameter of a primary particle, an association degree of a primary particle, and a particle diameter of a secondary particle can be freely controlled.
In addition, an association degree of abrasive grain 16 is not particularly limited, but from a viewpoint of easy formation of an edgeless irregular shape on its surface, a ratio (d2/d1 ratio) of an average particle diameter d2 of a secondary particle to an average particle diameter d1 of a primary particle is not less than 1.6 and not more than 10. Further, a d2/d1 ratio is preferably not less than 2.0 and not more than 8. Herein, an average particle diameter d1 of a primary particle of abrasive grain 16 is calculated by the following equation (4):
d
1=6/(ρ×S) (4)
from measurement of an adhesion specific surface area (referred to as BET specific surface area; the same hereinafter) by a gas adsorption method. In the equation (4), ρ represents a density of a particle, and S represents a BET specific surface area. In addition, an average particle diameter d2 of a secondary particle of an abrasive grain is calculated by the following equation (5):
d
2=(k×T)/(3×π×η0×D) (5)
from measurement of a diffusion coefficient in Brownian movement of a particle by a dynamic light scattering method. In the equation (5), k represents a Boltzmann constant, T represents an absolute temperature, a represents a ratio of a circumference of a circle to its diameter, η0 represents a viscosity of a solvent, and D represents a diffusion coefficient.
An average particle diameter d2 of a secondary particle of abrasion grain 16 is not particularly limited, but from a viewpoint of enhancement of a polishing rate, the diameter is preferably 30 nm or more and, from a viewpoint of reduction in a surface roughness, the diameter is preferably 300 nm or less. From such the viewpoint, an average particle diameter d2 of a secondary particle of abrasive grain 16 is more preferably 60 nm or more, and preferably 250 nm or less.
In addition, a shape of abrasive grain 16 is not particularly limited. Referring to
Polishing slurry 17 of the present embodiment is specifically such that abrasive grains 16 (preferably, colloidal silica abrasive grains) formed of SiO2 are dispersed in water which is a dispersing medium. The abrasive grain content in polishing slurry 17 is not particularly limited, but from a viewpoint of enhancement of a polishing rate, the content is preferably 2 mass % or more and, from a viewpoint of reduction in a surface roughness and enhancement of surface quality, the content is preferably 40 mass % or less. From such the point of view, the abrasive grain content in polishing slurry 17 is more preferably 5 mass % or more, and more preferably 20 mass % or less.
In addition, it is preferable that a value X of a pH and a value Y (mV) of oxidation-reduction potential (referred to as ORP; the same hereinafter) of the polishing slurry of the present embodiment satisfy both relationships of the following equation (1) and equation (2):
Y≧−50X+1000 (1)
Y≦−50X+1900 (2)
Herein, ORP means an energy level (potential) determined by the equilibrium state between an oxidized entity and a reduced entity which are present together in a solution. ORP obtained by measurement is a value relative to a reference electrode and, when a kind of a reference electrode is different, a measured value of the same solution is apparently different. In general academic articles, as a reference electrode, a normal hydrogen electrode (N.H.E) is used in many cases. ORP in the present application is expressed as a value using a normal hydrogen electrode (N.H.E) as a reference electrode.
When a value X of a pH and a value Y (mV) of ORP of polishing slurry 17 of the present embodiment are: Y≧−50X+1000, an oxidizing power of polishing slurry 17 is weak, and a rate of polishing a surface of GaxIn1-xAsyP1-y crystal 1 is lowered. On the other hand, when Y≧−50X+1900, an oxidizing power of polishing slurry 17 becomes too strong, the corroding action on polishing facilities such as a polishing pad and a platen becomes too strong, and stable CMP becomes difficult.
In addition, from a viewpoint of more enhancement of a polishing rate, further, Y≧−50X+1300 is preferable. That is, it is preferable that a value X of a pH and a value Y (mV) of ORP of polishing slurry 17 satisfy both relationships of the following equation (2) and equation (3):
Y≦−50X+1900 (2)
Y≧−50X+1300 (3)
An acid such as hydrochloric acid and sulfuric acid, and a base such as KOH and NaOH which are contained in a conventional polishing slurry are weak in a force of oxidizing a surface of GaxIn1-xAsyP1-y crystal. For this reason, it is preferable that an oxidizing agent is added to the polishing slurry of the present embodiment to enhance ORP, that is, enhance an oxidizing power. An amount of an oxidizing agent to be added is adjusted so that a value X of a pH and a value Y (mV) of ORP of polishing slurry 17 satisfy both relationships of Y≧−50X+1000 (equation (1)) and Y≦−50X+1900 (equation (2)).
Herein, an oxidizing agent to be added to a polishing slurry is not particularly limited, but from a viewpoint of enhancement of a polishing rate, chlorinated isocyanuric acid such as trichloroisocyanuric acid, chlorinated isocyanurate such as sodium dichloroisocyanurate, permanganate such as sodium permanganate, dichromate such as potassium dichromate, bromate such as potassium bromate, thiosulfate such as sodium thiosulfate, persulfate such as ammonium persulfate and potassium persulfate, hypochlorous acid, nitric acid, aqueous hydrogen peroxide, ozone, and the like are preferably used. These oxidizing agents may be used alone, or two or more may be used together.
In addition, it is preferable that a pH of polishing slurry 17 of the present embodiment is not more than 5 or not less than 8. By contacting an acidic polishing slurry having a pH of 5 or less or a basic polishing slurry having a pH of 8 or more with a GaxIn1-xAsyP1-y crystal to oxidize procession denatured layer 1a of a GaxIn1-xAsyP1-y crystal, a polishing rate can be enhanced. From a viewpoint of further enhancement of a polishing rate, a pH of polishing slurry 17 is more preferably not more than 4 or not less than 9, further preferably not more than 3 or not less than 10.
Herein, an acid, a base and a salt which are used for adjusting a pH are not particularly limited, but an inorganic acid such as hydrochloric acid, nitric acid, sulfuric acid, phosphoric acid and carbonic acid, an organic acid such as formic acid, acetic acid, citric acid, malic acid, tartaric acid, succinic acid, phthalic acid and fumaric acid, a base such as KOH, NaOH, NH4OH and amine, and salts containing these acids or bases can be used. Alternatively, the aforementioned oxidizing agent may be added to adjust a pH.
In particular, in a polishing slurry using the aforementioned organic acid and/or a salt thereof for adjusting a pH, a rate of polishing a GaxIn1-xAsyP1-y crystal is enhanced as compared with a polishing slurry using the aforementioned inorganic acid and/or a salt thereof to realize the same pH. From a viewpoint of enhancement of a polishing rate, it is preferable that the organic acid and a salt thereof are carboxylic acid containing 2 or more carboxyl groups in one molecule and a salt thereof, respectively. Herein, preferable examples of dicarboxylic acid include malic acid, succinic acid, phthalic acid and tartaric acid. Preferable examples of tricarboxylic acid include citric acid. Therefore, it is preferable that a polishing slurry contains the abrasive grains, the oxidizing agent, the organic acid and/or a salt thereof.
Referring to
In the method of treating a surface of a GaxIn1-xAsyP1-y crystal of the present embodiment, it is preferable that the step of chemically mechanically polishing a surface of a GaxIn1-xAsyP1-y crystal using the polishing slurry is performed by rotating a polishing pad and a GaxIn1-xAsyP1-y crystal on different rotating axes at a rotation number of 10/min or more and 200/min or less and at a polishing pressure (corresponding to a pressure applied to GaxIn1-xAsyP1-y crystal 1 by pressing against polishing pad 18 in
When a polishing pressure is less than 4.9 kPa (50 gf/cm2) or a rotation number is less than 10/min, a polishing rate is lowered and, when a polishing pressure is more than 98 kPa (1000 gf/cm2) or a rotation number is more than 2000/min, surface quality of a crystal is deteriorated. From such the viewpoint, in CMP of a GaAs crystal, it is preferable that a polishing pressure is not less than 9.8 kPa (100 gf/cm2) and not more than 49 kPa (500 gf/cm2), and a rotation number of a polishing pad and a GaAs crystal is not less than 30/min and not more than 70/min. In addition, in a GaxIn1-xAsyP1-y crystal (0x≦1, 0≦y≦1), as x and y are nearer 1, a hardness of a crystal is lowered, and it is further preferable that a polishing pressure of a GaAs crystal is not less than 9.8 kPa (100 gf/cm2) and not more than 29.4 kPa (300 gf/cm2), and a polishing pressure of an InP crystal is not less than 14.7 kPa (150 gf/cm2) and not more than 49 kPa (500 gf/cm2).
It is preferable that the method of treating a surface of a GaxIn1-xAsyP1-y crystal of the present embodiment includes a step of washing a surface of the chemically mechanically polished GaxIn1-xAsyP1-y crystal with pure water after the step of chemical mechanical polishing. Impurities such as a polishing slurry (abrasive grains and a polishing solution) attached to a surface of a GaxIn1-xAsyP1-y crystal during a step of chemical mechanical polishing can be removed by washing a surface of a GaxIn1-xAsyP1-y crystal with pure water. A method of washing a GaxIn1-xAsyP1-y crystal is not particularly limited, but from a viewpoint of that impurities are effectively removed by mechanical action, an ultrasound washing method, and a scrub washing method are preferably used.
Referring to
Herein, a step of polishing using a polishing solution refers to a step which is performed for removing the impurities attached to a surface of a subject to be abraded using a polishing solution not containing a solid matter such as abrasive grains, like an acidic aqueous solution or a basic aqueous solution. Referring to
By polishing a surface of GaxIn1-xAsyP1-y crystal 1 using polishing solution 37 of the present embodiment formed of an acidic aqueous solution or a basic aqueous solution, impurities such as a polishing slurry (abrasive grains and a polishing solution) attached to a surface of a GaxIn1-xAsyP1-y crystal during the step of chemical mechanical polishing can be effectively removed. From a viewpoint of removal of impurities attached to a GaxIn1-xAsyP1-y crystal, it is preferable that a polishing solution is an acidic aqueous solution having a pH of 5 or lower, or a basic aqueous solution having a pH of 9 or higher. Herein, an acidic aqueous solution is not particularly limited, but an aqueous solution of an inorganic acid such as hydrochloric acid, nitric acid, sulfuric acid and phosphoric acid, an aqueous solution of an organic acid such as formic acid, acetic acid, citric acid, malic acid, tartaric acid, succinic acid, phthalic acid and fumaric acid, or an aqueous solution containing 2 or more of acids from the inorganic acids and organic acids are preferably used. In addition, a basic aqueous solution is not particularly limited, an aqueous solution of a base such as KOH, NaOH, NH4OH and amine is preferably used.
Further, it is preferable that the method of treating a surface of a GaxIn1-xAsyP1-y crystal of the present embodiment includes a step of washing a surface of the GaxIn1-xAsyP1-y crystal which has been polished using a polishing solution with pure water after the step of polishing using the polishing solution. A metal ion and an ion containing a light element of an atomic number of 1 to 18 in an acidic aqueous solution or a basic aqueous solution which are impurities attached to a surface of a GaxIn1-xAsyP1-y crystal during a step of polishing using a polishing solution can be effectively removed by washing a surface of a GaxIn1-xAsyP1-y crystal with pure water. A method of washing a GaxIn1-xAsyP1-y crystal is not particularly limited, but from a viewpoint that the impurities are effectively removed by mechanical action, an ultrasound washing method and a scrub washing method are preferably used.
A GaxIn1-xAsyP1-y crystal substrate (0≦x≦1, 0≦y≦1) of the present invention is obtained by the surface treating method of the embodiment 2. By the surface treatment method of the embodiment 2, a GaxIn1-xAsyP1-y crystal substrate having a low surface roughness is effectively obtained. Herein, as an index expressing a surface roughness, there are a surface roughness Ry and a surface roughness Ra. A surface roughness Ry refers to a sum obtained by extracting only a 10 μm square (10 μm×10 μm=100 μm2; hereinafter the same) as a standard area of a rough curved surface in its average plane direction, and summing a height from an average plane from this extracted part to a highest summit and a depth from the average plane to a lowest valley bottom. In addition, a surface roughness Ra refers to a value obtained by extracting only a 10 μm square as a standard area from a rough curved surface in its average plane direction, summing an absolute value of a deviation from an average plane of this extracted part to a measurement curved surface and averaging it by a standard area. Herein, measurement of surface roughnesses Ry and Ra can be performed by using AFM (by an atomic force microscope; hereinafter the same).
By reducing surface roughnesses Ry and/or Ra of a main plane of a GaxIn1-xAsyP1-y crystal substrate, an epitaxial layer having better morphology and crystallizability can be formed on a main plane of a GaxIn1-xAsyP1-y crystal, and a semiconductor device having better property can be manufactured. In order to obtain a device having better property, it is preferable that, in a main surface of a GaxIn1-xAsyP1-y crystal substrate, a surface roughness Ry is 10 nm or lower, and a surface roughness Ra is 1 nm or lower.
A polishing slurry, a method of treating a surface of a GaxIn1-xAsyP1-y crystal using such the polishing slurry, and a GaxIn1-xAsyP1-y crystal obtained by such the surface treating method regarding the present invention will be further specifically explained based on the following Examples and Comparative Examples.
(A-1) Lapping of GaAs crystal
A GaAs crystal grown by a VB (Vertical Bridgeman) method was sliced with a plane parallel with a (100) plane to obtain a GaAs crystal substrate of diameter 50 mm×thickness 0.5 mm. A (100) plane of this GaAs crystal substrate was lapped as follows: a lapping pad was disposed on a platen of a diameter of 300 mm arranged on a lapping apparatus, and a platen and a GaAs crystal substrate were rotated to each other with rotation axes shifted while a lapping slurry with Al2O3 abrasive grains dispersed therein was supplied to a lapping pad, and a (100) plane of a GaAs crystal substrate fixed to a crystal holder was pressed against a platen. Herein, as a lapping pad, a non-woven pad (Suba800 manufactured by Nitta Haas Incorporated) was used and, as a platen, a stainless platen was used. As an Al2O3 abrasive grain, three kinds having an abrasive grain diameter of 10 μm, 5 μm and 2 μm were prepared and, as lapping progresses, an abrasive grain diameter was lowered stepwisely. An abrading pressure was 4.9 kPa (50 gf/cm2) to 98 kPa (1000 gf/cm2), and rotation numbers of a GaAs crystal substrate and a platen were 10/min to 200/min. By such the lapping, a surface of a GaAs crystal substrate became specular. In a GaAs crystal substrate after this lapping, a surface roughness Ry was 8.4 nm, and a surface roughness Ra was 0.86 nm. An abrading time in this lapping was 20 min. An average lapping rate was 1.6 μm/min.
(A-2) Chemical mechanical polishing (CMP) of GaAs crystal
A (100) plane of a GaAs crystal substrate after the lapping was chemically mechanically polished as follows. Referring to
Herein, polishing slurry 17 was prepared by dispersing and diluting colloidal silica (SiO2) (Quotron PL-10H manufactured by Fuso Chemical Co., Ltd.) (SiO2 solid matter 24 mass %) having an average particle diameter of a primary particle of 90 nm and an average particle diameter of a secondary particle of 220 nm as abrasive grain 16 in water to a SiO2 solid matter of 15 mass %, and sodium carbonate (Na2CO3), sodium sulfate (Na2SO4), sodium tripolyphosphate (Na-TPP), and sodium dichloroisocyanurate (Na-DCIA) as an oxidizing agent were appropriately added to adjust a pH to 9.0, and ORP to 1050 mV. In addition, as polishing pad 18, a suede pad of polyurethane (Supreme RN-R manufactured by Nitta Haas Incorporated) was used and, as platen 15, a stainless platen was used. A polishing pressure was 19.6 kPa (200 gf/cm2), and both of rotation numbers of a GaAs crystal substrate (GaxIn1-xAsyP1-y crystal 1) and polishing pad 18 were 40/min.
A polishing rate in this CMP was 1.5 μm/min. In addition, when surface roughnesses Ry and Ra of a GaAs crystal substrate after CMP were measured using AFM, they were 2.4 nm and 0.25 nm, respectively. The results are summarized in Table 1.
According to the same manner as that of Example 1 except that a polishing slurry containing colloidal silica abrasive grains having an average particle diameter d1 of a primary particle, an average particle diameter d2 of a secondary particle, and a d2/d1 ratio shown in Table 1 as the abrasive grains were used in the (A-2), lapping and CMP of a GaAs crystal substrate were performed. Surface roughnesses Ry and Ra of the resulting GaAs crystal substrate were measured. The results are summarized in Table 1.
In a polishing slurry of each Example, as an abrasive grain material, Quotron PL-3H (SiO2 solid matter 20 mass %) manufactured by Fuso Chemical Co., Ltd. having d1 of 30 nm, d2 of 80 nm and a d2/d1 ratio of 2.7 was used in Example 2, Quotron PL-7 (SiO2 solid matter 20 mass %) manufactured by Fuso Chemical Co., Ltd. having d1 of 70 nm, d2 of 130 nm and a d2/d1 ratio of 1.9 was used in Example 3, Snowtex PS-MO (SiO2 solid matter 18 to 19 mass %) manufactured by Nissan Chemical Industries, Ltd. having d1 of 20 nm, d2 of 150 nm and a d2/d1 ratio of 7.5 was used in Example 4, and unassociated colloidal silica (SiO2) was used in Comparative Examples 1 to 3, and abrasive grains material were diluted in water to a SiO2 solid matter of 15 mass % in all cases. A pH and ORP of polishing slurries of each Example and each Comparative Example were adjusted as in Example 1. In addition, in a polishing slurry of each Comparative Example, as an abrasive grain material, unassociated colloidal silica having d1 of 40 nm was used in Comparative Example 1, unassociated colloidal silica having d1 of 100 nm was used in Comparative Example 2, and unassociated colloidal silica (SiO2) having d1 of 200 nm was used in Comparative Example 3, and any silica was diluted in water to a SiO2 solid matter of 15 mass %. A pH and ORP of polishing slurries of each Example and each Comparative Example were adjusted as in Example 1.
As shown in Comparative Examples 1 to 3, when polishing is performed using a polishing slurry containing unassociated spherical colloidal silica abrasive grains, as a particle diameter of an abrasive grain grows larger, a polishing rate is enhanced, but both of surface roughnesses Ry and Ra are increased, and surface quality is deteriorated.
To the contrary, as shown in Examples 1 to 4, by performing CMP using a polishing slurry containing colloidal silica abrasive grains in which the grains are a secondary particle (average particle diameter d2) obtained by association of primary particles (average particle diameter d1), a d2/d1 ratio is not less than 1.6 and not more than 10, and d2 is not less than 30 nm and not more than 300 nm, and in which a value X of a pH and a value Y (mV) of ORP satisfy a relationship of −50X+1000≦Y≦−50X+1900, and a pH is 8 or more, under the condition of a polishing pressure of 19.6 Pa (200 gf/cm2), and a rotation number of a polishing pad and a GaAs crystal of 40/min, a GaAs crystal substrate having a surface having small surface roughnesses Ry and Ra was obtained at a high polishing rate.
According to the same manner as that of Example 1 except that a polishing slurry having a pH and ORP shown in Table 2 was used, lapping and CMP of a GaAs crystal substrate were performed. Surface roughnesses Ry and Ra of the resulting GaAs crystal substrate were measured. The results are summarized in Table 2.
In addition, in a polishing slurry of each Example, a pH and ORP were adjusted to each pH and each ORP shown in Table 2 using the same colloidal silica abrasive grain as that of Example 2, using malic acid, sodium malate, and trichloroisocyanuric acid (TCIA) which is an oxidizing agent in Example 5, and using sodium carbonate (Na2CO3), sodium sulfate (Na2SO4), sodium tripolyphosphate (Na-TPP), and sodium dichloroisocyanurate (Na-DCIA) which is an oxidizing agent in Example 6. In Example 7, all of an acid, a base, a salt and an oxidizing agent were not added.
As shown in Examples 5 and 6, by performing CMP using a polishing slurry containing colloidal silica abrasive grains in which primary particles (average particle diameter d1) are associated to be a secondary particle (average particle diameter d2), a ratio d2/d1 is not less than 1.6 and not more than 10, and d2 is not less than 30 nm and not more than 300 nm, and in which a value X of a pH and a value Y (mV) of ORP satisfy a relationship of −50X+1000≦Y≦−50x+1900, and a pH is not higher than 5 or not lower than 8, a GaAs crystal substrate having small surface roughnesses Ry and Ra was obtained at a high polishing rate. In Example 7, a relationship between a value X of a pH and a value Y (mV) of ORP of a polishing slurry is Y≦−50X+1000, a polishing rate was lowered, and both of surface roughnesses Ry and Ra of a GaAs crystal substrate after CMP were increased.
(B-1) Lapping of InP crystal
An InP crystal which had been grown by a LEC (liquid Encapsulated Czochralski) method was sliced with a plane parallel with a (100) plane to obtain an InP crystal substrate of diameter 50 mm×thickness 0.5 mm. A (100) plane of this InP crystal substrate was lapped like (A-1) of Example 1.
(B-2) Chemical mechanical polishing (CMP) of InP crystal
According to the same manner as that of Example 1 except that a polishing slurry obtained by diluting colloidal silica (SiO2) (Quotron PL10H manufactured by Fuso Chemical Co., Ltd.) (SiO2 solid matter 24 mass %) having an average particle diameter d1 of a primary particle of 90 nm, and an average particle diameter d2 of a secondary particle of 220 nm, and a d2/d1 ratio of 2.4 in water to a SiO2 solid matter of 10 mass %, and adjusting a pH of a polishing slurry to 4, and ORP of a polishing slurry to 1200 mV using citric acid and triochloroisocyanuric acid (TCIA) which is an oxidizing agent was used, a polishing pressure was 29.4 kPa (300 gf/cm2), and a rotation number of a polishing pad and an InP crystal was 50/min, CMP of a (100) plane of InP crystal substrate after lapping was performed. Surface roughnesses Ry and Ra of the resulting InP crystal substrate were measured. The results are summarized in Table 3.
According to the same manner as that of Example 8 except that a polishing slurry containing colloidal silica abrasive grains having an average particle diameter d1 of a primary particle, an average particle diameter d2 of a secondary particle and a d2/d1 ratio shown in Table 2 as the abrasive grains were used in the (B-2), lapping and CMP of an InP crystal substrate were performed. Surface roughnesses Ry and Ra of the resulting InP crystal substrate were measured. The results are summarized in Table 3.
In addition, in a polishing slurry of each Example, as abrasive grain material, Quotron PL-3H (SiO2 solid matter 20 mass %) manufactured by Fuso Chemical Co., Ltd. having d1 of 30 nm, d2 of 80 nm and a d2/d1 ratio of 2.7 was used in Example 9, Quotron PL-7 (SiO2 solid matter 20 mass %) manufactured by Fuso Chemical Co., Ltd. having d1 of 70 nm, d2 of 130 nm, and a d2/d1 ratio of 1.9 was used in Example 10, Snowtex PS-MO (SiO2 solid matter 18 to 19 mass %) manufactured by Nissan Chemical Industries, Ltd. having d1 of 20 nm, d2 of 150 nm, and a d2/d1 ratio of 7.5 was used in Example 11, and unassociated colloidal silica (SiO2) was used in Comparative Examples 4 to 6, and any of them was diluted in water to a SiO2 solid matter of 10 mass %. In addition, in a polishing slurry of each Comparative Example, as an abrasive grain material, unassociated colloidal silica having d1 of 40 nm was used in Comparative Example 4, unassociated colloidal silica of d1 of 100 nm was used in Comparative Example 5, and unassociated colloidal silica having d1 of 200 nm was used in Comparative Example 6, and any of them was diluted in water to a SiO2 solid matter of 10 mass %. A pH and ORP of polishing slurries of each Example and each Comparative Example were adjusted as in Example 8.
As shown in Comparative Examples 4 to 6, when polishing is performed using a polishing slurry containing unassociated spherical colloidal silica abrasive grains, as a particle diameter of the abrasive grain grows larger, a polishing rate is enhanced, but both of surface roughnesses Ry and Ra are increased, and surface quality of an InP crystal substrate is deteriorated.
To the contrary, as shown in Examples 8 to 11, by performing CMP using a polishing slurry containing colloidal silica abrasive grains in which primary particles (average particle diameter d1) are associated to be a secondary particle (average particle diameter d2), a d2/d1 ratio is not less than 1.6 and not more than 10, and d2 is not less than 30 nm and not more than 300 nm, and in which a value X of a pH and a value Y (mV) of ORP satisfy a relationship of −50X+1000≦Y≦−50X+1900, and a pH is 5 or lower, under the condition of a polishing pressure of 29.4 kPa (300 gf/cm2), and a rotation number of a polishing part and an InP crystal of 50/min, an InP crystal substrate having a surface having small surface roughnesses Ry and Ra was obtained at a high polishing rate.
According to the same manner as that of Example 8 except that a polishing slurry having a pH and ORP shown in Table 4, and the condition of a polishing pressure and a rotation number of a polishing pad and an InP crystal shown in Table 4 were used, lapping and CMP of an InP crystal substrate were performed. Surface roughnesses Ry and Ra of the resulting InP crystal substrate were measured. The results are summarized in Table 4.
In addition, in a polishing slurry of each Example, a pH and ORP were adjusted to each pH and each ORP shown in Table 4 using the same colloidal silica abrasive grain as that of Example 9, using malic acid and trichloroisocyanuric acid (TCIA) which is an oxidizing agent in Example 12, using sodium malate and trichloroisocyanuric acid (TCIA) which is an oxidizing agent in Example 13, and using nitric acid and trichloroisocyanuric acid (TCIA) which is an oxidizing agent in Example 14. In Example 15, all of an acid, a base, a salt and an oxidizing agent were not added.
As shown in Examples 12 to 14, by performing CMP using a polishing slurry containing colloidal silica abrasive grains in which primary particles (average particle diameter d1) are associated to be a secondary particle (average particle diameter d2), a ratio d2/d1 is not less than 1.6 and not more than 10, and d2 is not less than 30 nm and not more than 300 nm, and in which a value X of a pH and a value Y (mV) of ORP satisfy a relationship of −50X+1000≦Y≦−50X+1900, and a pH is 5 or lower, an InP crystal substrate having small surface roughnesses Ry and Ra was obtained at a high polishing rate. Further, as shown in Examples 12 and 13, by using a polishing slurry containing malic acid or sodium malate which is dicarboxylic acid or a salt thereof as a pH adjusting agent, a rate of polishing an InP crystal substrate was further enhanced.
In Example 1, a step of polishing a GaAs crystal substrate after a CMP step using a KOH aqueous solution having a concentration of 2 normal (referred to as 2N; the same hereinafter) as a basic aqueous solution as shown in Table 5, and/or a step of washing with an ultrasound of 1 MHz (1×106 Hz using pure water were performed.
Referring to
In addition, an ultrasound washing step with pure water was performed by immersing a GaAs crystal substrate after the CMP step or after a chemical polishing step in pure water, and applying an ultrasound of 1 MHz to this pure water. A washing time was 10 min.
Elemental analysis of impurities remaining on a surface of the GaAs crystal substrate after a chemical polishing step or after a pure water washing step was performed using TXRF (total reflection fluorescent X-ray analysis method). The results are summarized in Table 5. As a reference, the results of analysis of impurities remaining on a surface of a GaAs crystal substrate after a CMP step in Example 1 are also described in Table 5.
As shown in Example 17, by providing a pure water washing step after a CMP step, impurities on a GaAs crystal substrate surface could be reduced. In addition, as shown in Example 16, by providing a chemical polishing step after a CMP step, impurities on a GaAs crystal substrate surface, particularly, a Si atom-containing substance derived from a colloidal silica abrasive grain upon CMP could be remarkably reduced. Further, as shown in Example 18, by providing a pure water washing step after a chemical polishing step, impurities on a GaAs crystal substrate surface, particularly, a K atom-containing substance derived from a polishing solution upon a chemical polishing step could be remarkably reduced.
Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2005-288278 (P) | Sep 2005 | JP | national |
This application is a Divisional of U.S. application Ser. No. 11/527,682, filed Sep. 27, 2006, claiming priority of Japanese Patent Application No. 2005-288278, filed Sep. 30, 2005, the entire contents of each of which are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11527682 | Sep 2006 | US |
| Child | 12389828 | US |