Patent Grant
9765181
The present invention generally relates to polyester compositions made from terephthalic acid, an ester thereof, or mixtures thereof; 2,2,4,4-tetramethyl-1,3-cyclobutanediol; and 1,4-cyclohexanedimethanol, the polyester having a certain combination of inherent viscosity and glass transition temperature (Tg). These compositions are believed to have a certain combination of two or more of high impact strengths, high glass transition temperature (Tg), toughness, e.g., low ductile-to-brittle transition temperatures, certain inherent viscosities, good color and clarity, low densities, chemical resistance, hydrolytic stability, and long crystallization half-times, which allow them to be easily formed into articles.
Poly(1,4-cyclohexylenedimethylene terephthalate (PCT), a polyester based solely on terephthalic acid or an ester thereof or mixtures thereof and 1,4-cyclohexanedimethanol, is known in the art and is commercially available. This polyester crystallizes rapidly upon cooling from the melt, making it very difficult to form amorphous articles by methods known in the art such as extrusion, injection molding, and the like. In order to slow down the crystallization rate of PCT, copolyesters can be prepared containing additional dicarboxylic acids or glycols such as isophthalic acid or ethylene glycol. These ethylene glycol- or isophthalic acid-modified PCTs are also known in the art and are commercially available.
One common copolyester used to produce films, sheeting, and molded articles is made from terephthalic acid, 1,4-cyclohexanedimethanol, and ethylene glycol. While these copolyesters are useful in many end-use applications, they exhibit deficiencies in properties such as glass transition temperature and impact strength when sufficient modifying ethylene glycol is included in the formulation to provide for long crystallization half-times. For example, copolyesters made from terephthalic acid, 1,4-cyclohexanedimethanol, and ethylene glycol with sufficiently long crystallization half-times can provide amorphous products that exhibit what is believed to be undesirably higher ductile-to-brittle transition temperatures and lower glass transition temperatures than the compositions revealed herein.
The polycarbonate of 4,4′-isopropylidenediphenol (bisphenol A polycarbonate) has been used as an alternative for polyesters known in the art and is a well known engineering molding plastic. Bisphenol A polycarbonate is a clear, high-performance plastic having good physical properties such as dimensional stability, high heat resistance, and good impact strength. Although bisphenol-A polycarbonate has many good physical properties, its relatively high melt viscosity leads to poor melt processability and the polycarbonate exhibits poor chemical resistance. It is also difficult to thermoform.
Polymers containing 2,2,4,4-tetramethyl-1,3-cyclobutanediol have also been generally described in the art. Generally, however, these polymers can exhibit high inherent viscosities, high melt viscosities and/or high Tgs (glass transition temperatures) such that the equipment used in industry can be insufficient to manufacture or post-polymerization process these materials.
Thus, there is a need in the art for a polymer having a combination of two or more properties chosen from at least one of the following: toughness, high glass transition temperatures, high impact strength, hydrolytic stability, chemical resistance, long crystallization half-times, low ductile to brittle transition temperatures, good color and clarity, lower density and/or thermoformability of polyesters while retaining processability on the standard equipment used in the industry.
It is believed that certain compositions formed from terephthalic acid residues, or an ester thereof, 1,4-cyclohexanedimethanol residues; and 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues with a certain combination of inherent viscosity and glass transition temperatures are superior to polyesters known in the art and to polycarbonate with respect to one or more of high impact strengths, hydrolytic stability, toughness, chemical resistance, good color and clarity, long crystallization half-times, low ductile to brittle transition temperatures, lower specific gravity and/or thermoformability. These compositions are believed to be similar to polycarbonate in heat resistance and are still processable on the standard industry equipment.
In one aspect, the invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising:
(A) at least one polyester which comprises:
(B) residues of at least one branching agent;
wherein the total mole % of the dicarboxylic acid component is 100 mole %, and
the total mole % of the glycol component is 100 mole %; and
wherein the inherent viscosity of said polyester is from 0.35 to 1.2 dL/g as determined in 60/40 (wt/wt)phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.; wherein said polyester has a Tg from 110 to 200° C.
In one aspect, this invention relates to a polyester composition comprising:
(A) at least one polyester which comprises:
(B) residues of at least one branching agent;
wherein the total mole % of the dicarboxylic acid component is 100 mole %, and
the total mole % of the glycol component is 100 mole %; and
wherein the inherent viscosity of said polyester is from 0.35 to 1.2 dL/g as determined in 60/40 (wt/wt)phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.; wherein said polyester has a Tg from 110 to 200° C.
In one aspect, this invention relates to a polyester composition comprising:
(A) at least one polyester which comprises:
(B) residues of at least one branching agent;
wherein the total mole % of the dicarboxylic acid component is 100 mole %, and
the total mole % of the glycol component is 100 mole %; and
wherein the inherent viscosity of said polyester is from 0.35 to 0.75 dL/g as determined in 60/40 (wt/wt)phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.; wherein said polyester has a Tg from 110 to 200° C.
In one aspect, this invention relates to a polyester composition comprising:
(A) at least one polyester which comprises:
(B) at least one thermal stabilizer or reaction products thereof;
wherein the total mole % of the dicarboxylic acid component is 100 mole %, and the total mole % of the glycol component is 100 mole %; and
wherein the inherent viscosity of said polyester is from 0.35 to 1.2 dL/g as determined in 60/40 (wt/wt)phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.;
wherein said polyester has a Tg from 110 to 200° C.
In one aspect, this invention relates to a polyester composition comprising:
(A) at least one polyester which comprises:
(B) at least one thermal stabilizer or reaction products thereof;
wherein the total mole % of the dicarboxylic acid component is 100 mole %, and the total mole % of the glycol component is 100 mole %; and
wherein the inherent viscosity of said polyester is from 0.35 to 1.2 dL/g as determined in 60/40 (wt/wt)phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.;
wherein said polyester has a Tg from 110 to 200° C.
In one aspect, this invention relates to a polyester composition comprising:
(A) at least one polyester which comprises:
and
(B) at least one thermal stabilizer or reaction products thereof;
wherein the total mole % of the dicarboxylic acid component is 100 mole %, and the total mole % of the glycol component is 100 mole %; and
wherein the inherent viscosity of said polyester is from 0.35 to 0.75 dL/g as determined in 60/40 (wt/wt)phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.;
wherein said polyester has a Tg from 110 to 200° C.
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
This invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, this invention relates to a polyester composition comprising at least one polyester which comprises:
(a) a dicarboxylic acid component comprising:
(b) a glycol component comprising:
In one aspect, the polyester compositions contain at least one polycarbonate.
In one aspect, the polyester compositions contain no polycarbonate.
In one aspect, the polyester useful in the invention contain less than 15 mole % ethylene glycol residues, such as, for example, 0.01 to less than 15 mole % ethylene glycol residues.
In one aspect, the polyesters useful in the invention contain no ethylene glycol residues.
In one aspect, the polyester compositions useful in the invention contain at least one thermal stabilizer and/or reaction products thereof.
In one aspect, the polyesters useful in the invention contain no branching agent, or alternatively, at least one branching agent is added either prior to and/or during polymerization of the polyester.
In one aspect, the polyesters useful in the invention contain at least one branching agent without regard to the method or sequence in which it is added.
In one aspect, the polyesters useful in the invention are made from no 1,3-propanediol, or 1,4-butanediol, either singly or in combination. In other aspects, 1,3-propanediol or 1,4-butanediol, either singly or in combination, may be used in the making of the polyesters useful in this invention.
In one aspect of the invention, the mole % of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol useful in certain polyesters useful in the invention is greater than 50 mole % or greater than 55 mole % of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol or greater than 70 mole % of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol; wherein the total mole percentage of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol and trans-2,2,4,4-tetramethyl-1,3-cyclobutanediol is equal to a total of 100 mole %.
In one aspect of the invention, the mole % of the isomers of 2,2,4,4-tetramethyl-1,3-cyclobutanediol useful in certain polyesters useful in the invention is from 30 to 70 mole % of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol or from 30 to 70 mole % of trans-2,2,4,4-tetramethyl-1,3-cyclobutanediol, or from 40 to 60 mole % of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol or from 40 to 60 mole % of trans-2,2,4,4-tetramethyl-1,3-cyclobutanediol, wherein the total mole percentage of cis-2,2,4,4-tetramethyl-1,3-cyclobutanediol and trans-2,2,4,4-tetramethyl-1,3-cyclobutanediol is equal to a total of 100 mole %.
In one aspect, the polyester compositions are useful in articles of manufacture including, but not limited to, calendered, extruded and/or molded articles including, but not limited to, injection molded articles, extruded articles, cast extrusion articles, profile extrusion articles, melt spun articles, thermoformed articles, extrusion molded articles, injection blow molded articles, injection stretch blow molded articles, extrusion blow molded articles, and extrusion stretch blow molded articles. These articles can include, but are not limited to, films, bottles (including but not limited to baby bottles), film, sheet and/or fibers. In one aspect, the polyester compositions useful in the invention may be used in various types of film and/or sheet, including but not limited to extruded film(s) and/or sheet(s), calendered film(s) and/or sheet(s), compression molded film(s) and/or sheet(s), solution casted film(s) and/or sheet(s). Methods of making film and/or sheet include but are not limited to extrusion, calendering, compression molding, and solution casting.
Also, in one aspect, use of the polyester compositions of the invention can minimize and/or eliminate the drying step prior to melt processing and/or thermoforming.
In one aspect, certain polyesters useful in the invention can be amorphous or semicrystalline. In one aspect, certain polyesters useful in the invention can have a relatively low crystallinity. Certain polyesters useful in the invention can thus have a substantially amorphous morphology, meaning that the polyesters comprise substantially unordered regions of polymer.
The present invention may be understood more readily by reference to the following detailed description of certain embodiments of the invention and the working examples. In accordance with the purpose(s) of this invention, certain embodiments of the invention are described in the Summary of the Invention and are further described herein below. Also, other embodiments of the invention are described herein.
It is believed that polyesters and/or polyester compositions useful in the invention described herein can have a combination of two or more physical properties such as high impact strengths, high glass transition temperatures, chemical resistance, hydrolytic stability, toughness, e.g., low ductile-to-brittle transition temperatures, good color and clarity, low densities, and long crystallization half-times, and good processability thereby easily permitting them to be formed into articles. In some of the embodiments of the invention, the polyesters have a unique combination of the properties of good impact strength, heat resistance, chemical resistance, density and/or the combination of the properties of good impact strength, heat resistance, and processability and/or the combination of two or more of the described properties, that have never before been believed to be present in a polyester.
As used herein, the term “polyester” includes copolyesters and is understood to mean a synthetic polymer prepared by the reaction of one or more difunctional and/or multifunctional carboxylic acids with one or more difunctional hydroxyl compounds and/or multifunctional hydroxyl compounds. Typically the difunctional carboxylic acid can be a dicarboxylic acid and the difunctional hydroxyl compound can be a dihydric alcohol such as, for example, glycols and diols. The term “glycol” as used in this application includes, but is not limited to, diols, glycols, and/or multifunctional hydroxyl compounds, for example, branching agents. Alternatively, the difunctional carboxylic acid may be a hydroxy carboxylic acid such as, for example, p-hydroxybenzoic acid, and the difunctional hydroxyl compound may be an aromatic nucleus bearing 2 hydroxyl substituents such as, for example, hydroquinone. The term “residue”, as used herein, means any organic structure incorporated into a polymer through a polycondensation and/or an esterification reaction from the corresponding monomer. The term “repeating unit”, as used herein, means an organic structure having a dicarboxylic acid residue and a diol residue bonded through a carbonyloxy group. Thus, for example, the dicarboxylic acid residues may be derived from a dicarboxylic acid monomer or its associated acid halides, esters, salts, anhydrides, or mixtures thereof. As used herein, therefore, the term dicarboxylic acid is intended to include dicarboxylic acids and any derivative of a dicarboxylic acid, including its associated acid halides, esters, half-esters, salts, half-salts, anhydrides, mixed anhydrides, or mixtures thereof, useful in a reaction process with a diol to make polyester. Furthermore, as used in this application, the term “diacid” includes multifunctional acids, for example, branching agents. As used herein, the term “terephthalic acid” is intended to include terephthalic acid itself and residues thereof as well as any derivative of terephthalic acid, including its associated acid halides, esters, half-esters, salts, half-salts, anhydrides, mixed anhydrides, or mixtures thereof or residues thereof useful in a reaction process with a diol to make polyester.
In one embodiment, terephthalic acid may be used as the starting material. In another embodiment, dimethyl terephthalate may be used as the starting material. In another embodiment, mixtures of terephthalic acid and dimethyl terephthalate may be used as the starting material and/or as an intermediate material.
The polyesters used in the present invention typically can be prepared from dicarboxylic acids and diols which react in substantially equal proportions and are incorporated into the polyester polymer as their corresponding residues. The polyesters of the present invention, therefore, can contain substantially equal molar proportions of acid residues (100 mole %) and diol (and/or multifunctional hydroxyl compounds) residues (100 mole %) such that the total moles of repeating units is equal to 100 mole %. The mole percentages provided in the present disclosure, therefore, may be based on the total moles of acid residues, the total moles of diol residues, or the total moles of repeating units. For example, a polyester containing 30 mole % isophthalic acid, based on the total acid residues, means the polyester contains 30 mole % isophthalic acid residues out of a total of 100 mole % acid residues. Thus, there are 30 moles of isophthalic acid residues among every 100 moles of acid residues. In another example, a polyester containing 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol, based on the total diol residues, means the polyester contains 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues out of a total of 100 mole % diol residues. Thus, there are 30 moles of 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues among every 100 moles of diol residues.
In other aspects of the invention, the Tg of the polyesters useful in the polyester compositions of the invention include, but are not limited to 85 to 200° C.; 85 to 190° C.; 85 to 180° C.; 85 to 170° C.; 85 to 160° C.; 85 to 155° C.; 85 to 150° C.; 85 to 145° C.; 85 to 140° C.; 85 to 138° C.; 85 to 135° C.; 85 to 130° C.; 85 to 125° C.; 85 to 120° C.; 85 to 115° C.; 85 to 110° C.; 85 to 105° C.; 85 to 100° C.; 85 to 95° C.; 85 to 90° C.; 90 to 200° C.; 90 to 190° C.; 90 to 180° C.; 90 to 170° C.; 90 to 160° C.; 90 to 155° C.; 90 to 150° C.; 90 to 145° C.; 90 to 140° C.; 90 to 138° C.; 90 to 135° C.; 90 to 130° C.; 90 to 125° C.; 90 to 120° C.; 90 to 115° C.; 90 to 110° C.; 90 to 105° C.; 90 to 100° C.; 90 to 95° C.; 95 to 200° C.; 95 to 190° C.; 95 to 180° C.; 95 to 170° C.; 95 to 160° C.; 95 to 155° C.; 95 to 150° C.; 95 to 145° C.; 95 to 140° C.; 95 to 138° C.; 95 to 135° C.; 95 to 130° C.; 95 to 125° C.; 95 to 120° C.; 95 to 115° C.; 95 to 110° C.; 95 to 105° C.; 95 to less than 105° C.; 95 to 100° C.; 100 to 200° C.; 100 to 190° C.; 100 to 180° C.; 100 to 170° C.; 100 to 160° C.; 100 to 155° C.; 100 to 150° C.; 100 to 145° C.; 100 to 140° C.; 100 to 138° C.; 100 to 135° C.; 100 to 130° C.; 100 to 125° C.; 100 to 120° C.; 100 to 115° C.; 100 to 110° C.; 105 to 200° C.; 105 to 190° C.; 105 to 180° C.; 105 to 170° C.; 105 to 160° C.; 105 to 155° C.; 105 to 150° C.; 105 to 145° C.; 105 to 140° C.; 105 to 138° C.; 105 to 135° C.; 105 to 130° C.; 105 to 125° C.; 105 to 120° C.; 105 to 115° C.; 105 to 110° C.; greater than 105 to 125° C.; greater than 105 to 120° C.; greater than 105 to 115° C.; greater than 105 to 110° C.; 110 to 200° C.; 110 to 195° C.; 110 to 190° C.; 110 to 185° C.; 110 to 180° C.; 110 to 175° C.; 110 to 170° C.; 110 to 165° C.; 110 to 160° C.; 110 to 155° C.; 110 to 150° C.; 110 to 145° C.; 110 to 138° C.; 110 to 140° C.; 110 to 135° C.; 110 to 130° C.; 110 to 125° C.; 110 to 120° C.; 110 to 115° C.; 115 to 200° C.; 115 to 195° C.; 115 to 190° C.; 115 to 185° C.; 115 to 180° C.; 115 to 175° C.; 115 to 170° C.; 115 to 165° C. 115 to 160° C.; 115 to 155° C.; 115 to 150° C.; 115 to 145° C.; 115 to 140° C.; 115 to 138° C.; 115 to 135° C.; 115 to 125° C.; 115 to 120° C.; 120 to 200° C.; 120 to 195° C.; 120 to 190° C.; 120 to 185° C. 120 to 180° C.; 120 to 175° C. 120 to 170° C.; 120 to 165° C.; 120 to 160° C.; 120 to 155° C.; 120 to 150° C.; 120 to 145° C.; 120 to 140° C.; 120 to 138° C.; 120 to 135° C.; 125 to 180° C.; 125 to 170° C.; 125 to 160° C.; 125 to 155° C.; 125 to 150° C.; 125 to 145° C.; 125 to 140° C.; 125 to 138° C.; 125 to 135° C.; 135 to 180° C.; 127 to 180° C.; 127 to 170° C.; 127 to 160° C.; 127 to 150° C.; 127 to 145° C.; 127 to 140° C.; 127 to 138° C.; 127 to 135° C.; 130 to 200° C.; 130 to 195° C.; 130 to 190° C.; 130 to 185° C.; 130 to 180° C.; 130 to 175° C.; 130 to 170° C.; 130 to 165° C. 130 to 160° C.; 130 to 155° C.; 130 to 150° C.; 130 to 145° C.; 130 to 140° C.; 130 to 138° C.; 130 to 135° C.; 135 to 170° C.; 135 to 160° C.; 135 to 155° C.; 135 to 150° C.; 135 to 145° C.; 135 to 140° C.; 135 to 135° C.; 140 to 200° C.; 140 to 195° C.; 140 to 190° C.; 140 to 185° C.; 140 to 180° C.; 140 to 170° C.; 140 to 165° C.; 140 to 160° C.; 140 to 155° C.; 140 to 150° C.; 140 to 145° C.; 148 to 200° C.; 148 to 190° C.; 148 to 180° C.; 148 to 170° C.; 148 to 160° C.; 148 to 155° C.; 148 to 150° C.; 150 to 200° C.; 150 to 195° C.; 150 to 190° C.; 150 to 185° C.; 150 to 180° C.; 150 to 175° C.; 150 to 170° C.; 150 to 165° C.; 150 to 160° C.; 150 to 155° C.; 155 to 200° C.; 150 to 190° C.; 150 to 180° C.; 150 to 170° C.; 150 to 160; 155 to 190° C.; 155 to 180° C.; 155 to 170° C.; and 155 to 165° C.; greater than 124° C. up to 200° C.; greater than 125° C. up to 200° C.; greater than 126° C. up to 200° C.; greater than 148° C. up to 200° C.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 1 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 99 mole % 1,4-cyclohexanedimethanol, 1 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 25 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 75 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 20 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 80 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 15 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 85 to 99 mole % 1,4-cyclohexanedimethanol; 1 to 10 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 90 to 99 mole % 1,4-cyclohexanedimethanol; and 1 to 5 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 95 to 99 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 5 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 95 mole % 1,4-cyclohexanedimethanol; 5 to less than 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 65 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 25 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 75 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 20 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 80 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 15 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 85 to 95 mole % 1,4-cyclohexanedimethanol; 5 to 10 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 90 to 95 mole % 1,4-cyclohexanedimethanol; greater than 5 to less than 10 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and less than 90 to greater than 95 mole 1,4-cyclohexanedimethanol; 5.5 mole % to 9.5 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 94.5 mole % to 90.5 mole % 1,4-cyclohexanedimethanol; and 6 to 9 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 94 to 91 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 10 to 100 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 0 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 90 mole % 1,4-cyclohexanedimethanol, 10 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 90 mole % 1,4-cyclohexanedimethanol; 10 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 90 mole % 1,4-cyclohexanedimethanol; 10 to less than 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 65 to 90% 1,4-cyclohexanedimethanol; 10 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 25 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 75 to 90 mole % 1,4-cyclohexanedimethanol; 10 to 20 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 80 to 90 mole % 1,4-cyclohexanedimethanol; and 10 to 15 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 85 to 90 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 14 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 86 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 14 to 86 mole % 1,4-cyclohexanedimethanol, 14 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 86 mole % 1,4-cyclohexanedimethanol; 14 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 86 mole % 1,4-cyclohexanedimethanol; 14 to 24 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 76 to 86 mole % 1,4-cyclohexanedimethanol; and 14 to 25 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 75 to 86 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 15 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 86 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 86 mole % 1,4-cyclohexanedimethanol, 15 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 85 mole % 1,4-cyclohexanedimethanol; 15 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 85 mole % 1,4-cyclohexanedimethanol; 15 to 25 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 75 to 85 mole % 1,4-cyclohexanedimethanol; and 15 to 24 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 76 to 85 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 20 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 80 mole % 1,4-cyclohexanedimethanol, 20 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 80 mole % 1,4-cyclohexanedimethanol; 20 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 80 mole % 1,4-cyclohexanedimethanol; 20 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 80 mole % 1,4-cyclohexanedimethanol; and 20 to 25 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 75 to 80 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 25 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 75 mole % 1,4-cyclohexanedimethanol, 25 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 75 mole % 1,4-cyclohexanedimethanol; 25 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 75 mole % 1,4-cyclohexanedimethanol; 25 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 75 mole % 1,4-cyclohexanedimethanol; and 25 to 30 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 70 to 75 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 30 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 70 mole % 1,4-cyclohexanedimethanol, 30 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 70 mole % 1,4-cyclohexanedimethanol; 30 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 70 mole % 1,4-cyclohexanedimethanol; 30 to 35 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 65 to 70 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 35 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 65 mole % 1,4-cyclohexanedimethanol, 35 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 65 mole % 1,4-cyclohexanedimethanol; 35 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 65 mole % 1,4-cyclohexanedimethanol; 35 to 40 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 60 to 65 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 40 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 60 mole % 1,4-cyclohexanedimethanol, 40 to less than 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 20 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 60 mole % 1,4-cyclohexanedimethanol; 40 to less than 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and greater than 50 to 60 mole % 1,4-cyclohexanedimethanol; 40 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 60 mole % 1,4-cyclohexanedimethanol; and 40 to 45 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 55 to 60 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 45 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 55 mole % 1,4-cyclohexanedimethanol, 45 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 55 mole % 1,4-cyclohexanedimethanol; greater than 45 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to less than 55 mole % 1,4-cyclohexanedimethanol; 45 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 55 mole % 1,4-cyclohexanedimethanol; 45 to 50 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 50 to 55 mole % 1,4-cyclohexanedimethanol; greater than 45 to 52 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 48 to 55 mole % 1,4-cyclohexanedimethanol; 46 to 55 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 45 to 54 mole % 1,4-cyclohexanedimethanol; and 48 to 52 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 48 to 52 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: greater than 50 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to less than 50 mole % 1,4-cyclohexanedimethanol; greater than 50 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to less than 50 mole % 1,4-cyclohexanedimethanol; greater than 50 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to less than 50 mole % 1,4-cyclohexanedimethanol; greater than 50 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to less than 50 mole % 1,4-cyclohexanedimethanol, greater than 50 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to less than 50 mole % 1,4-cyclohexanedimethanol; greater than 50 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to less than 50 mole % 1,4-cyclohexanedimethanol; greater than 50 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to less than 50 mole % 1,4-cyclohexanedimethanol; greater than 50 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to less than 50 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 55 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 45 mole % 1,4-cyclohexanedimethanol; 55 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 45 mole % 1,4-cyclohexanedimethanol; 55 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 45 mole % 1,4-cyclohexanedimethanol; 55 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 45 mole % 1,4-cyclohexanedimethanol; 55 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 45 mole % 1,4-cyclohexanedimethanol, 55 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 45 mole % 1,4-cyclohexanedimethanol; 55 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 45 mole % 1,4-cyclohexanedimethanol; 55 to 65 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 35 to 45 mole % 1,4-cyclohexanedimethanol; and 55 to 60 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 40 to 45 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 60 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 40 mole % 1,4-cyclohexanedimethanol; 60 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 40 mole % 1,4-cyclohexanedimethanol; 60 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 40 mole % 1,4-cyclohexanedimethanol; 60 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 40 mole % 1,4-cyclohexanedimethanol; 60 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 40 mole % 1,4-cyclohexanedimethanol, 60 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 40 mole % 1,4-cyclohexanedimethanol; and 60 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 40 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 65 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 35 mole % 1,4-cyclohexanedimethanol; 65 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 35 mole % 1,4-cyclohexanedimethanol; 65 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 35 mole % 1,4-cyclohexanedimethanol; 65 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 35 mole % 1,4-cyclohexanedimethanol; 65 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 35 mole % 1,4-cyclohexanedimethanol, 65 to 75 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 25 to 35 mole % 1,4-cyclohexanedimethanol; and 65 to 70 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 30 to 35 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 70 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 30 mole % 1,4-cyclohexanedimethanol; 70 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 30 mole % 1,4-cyclohexanedimethanol; 70 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 30 mole % 1,4-cyclohexanedimethanol; 70 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 30 mole % 1,4-cyclohexanedimethanol; 70 to 80 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 20 to 30 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 75 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 25 mole % 1,4-cyclohexanedimethanol; 75 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 25 mole % 1,4-cyclohexanedimethanol; 75 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 25 mole % 1,4-cyclohexanedimethanol; and 75 to 85 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 15 to 25 mole % 1,4-cyclohexanedimethanol.
In other aspects of the invention, the glycol component for the polyesters useful in the invention include but are not limited to at least one of the following combinations of ranges: 80 to 99 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 1 to 20 mole % 1,4-cyclohexanedimethanol; 80 to 95 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 5 to 20 mole % 1,4-cyclohexanedimethanol; 80 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to 20 mole % 1,4-cyclohexanedimethanol; greater than 80 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to less than 20 mole % 1,4-cyclohexanedimethanol; and greater than 81 to 90 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol and 10 to less than 19 mole % 1,4-cyclohexanedimethanol.
In addition to the diols set forth above, the polyesters useful in the polyester compositions of the invention may also be made from 1,3-propanediol, 1,4-butanediol, or mixtures thereof. It is contemplated that compositions of the invention made from 1,3-propanediol, 1,4-butanediol, or mixtures thereof can possess at least one of the Tg ranges described herein, at least one of the inherent viscosity ranges described herein, and/or at least one of the glycol or diacid ranges described herein. In addition or in the alternative, the polyesters made from 1,3-propanediol or 1,4-butanediol or mixtures thereof may also be made from 1,4-cyclohexanedmethanol in at least one of the following amounts: from 0.1 to 99 mole %; from 0.1 to 95 mole %; from 0.1 to 90 mole %; from 0.1 to 85 mole %; from 0.1 to 80 mole %; from 0.1 to 75 mole %; from 0.1 to 70 mole %; from 0.1 to 60 mole %; from 0.1 to 50 mole %; from 0.1 to 40 mole %; from 0.1 to 35 mole %; from 0.1 to 30 mole %; from 0.1 to 25 mole %; from 0.1 to 20 mole %; from 0.1 to 15 mole %; from 0.1 to 10 mole %; from 0.1 to 5 mole %; from 1 to 99 mole %; from 1 to 95 mole; from 1 to 90 mole %; from 1 to 85 mole %; from 1 to 80 mole %; from 1 to 70 mole %; from 1 to 60 mole %; from 1 to 50 mole %; from 1 to 40 mole %; from 1 to 35 mole %; from 1 to 30 mole %; from 1 to 25 mole %; from 1 to 20 mole %; from 1 to 15 mole %; from 1 to 10 mole %; from 1 to 5 mole %; 5 to 99 mole %; from 5 to 95 mole; from 5 to 90 mole %; from 5 to 85 mole %; from 5 to 80 mole %; from 5 to 75 mole %; 5 to 70 mole %; from 5 to 60 mole %; from 5 to 50 mole %; from 5 to 40 mole %; from 5 to 35 mole %; from 5 to 30 mole %; from 5 to 25 mole %; from 5 to 20 mole %; and from 5 to 15 mole %; from 5 to 10 mole %; from 10 to 99 mole %; from 10 to 95 mole; from 10 to 90 mole %; from 10 to 85 mole %; from 10 to 80 mole %; from 10 to 75 mole %; from 10 to 70 mole %; from 10 to 60 mole %; from 10 to 50 mole %; from 10 to 40 mole %; from 10 to 35 mole %; from 10 to 30 mole %; from 10 to 25 mole %; from 10 to 20 mole %; from 10 to 15 mole %; from 20 to 99 mole %; from 20 to 95 mole; from 20 to 90 mole %; from 20 to 85 mole %; from 20 to 80 mole %; from 20 to 75 mole %; from 20 to 70 mole %; from 20 to 60 mole %; from 20 to 50 mole %; from 20 to 40 mole %; from 20 to 35 mole %; from 20 to 30 mole %; and from 20 to 25 mole %.
For certain embodiments of the invention, the polyesters may exhibit any of the following inherent viscosities as determined in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.: 0.35 to less than 0.70 dL/g; 0.35 to 0.68 dL/g; 0.35 to less than 0.68 dL/g; 0.35 to 0.65 dL/g; 0.40 to 0.70 dL/g; 0.40 to less than 0.70 dL/g; 0.40 to 0.68 dL/g; 0.40 to less than 0.68 dL/g; 0.40 to 0.65 dL/g; 0.45 to less than 0.70 dL/g; 0.45 to 0.68 dL/g; 0.45 to less than 0.68 dL/g; 0.45 to 0.65 dL/g; 0.50 to less than 0.70 dL/g; 0.50 to 0.68 dL/g; 0.50 to less than 0.68 dL/g; 0.50 to 0.67 dL/g; 0.50 to 0.66 dL/g; 0.50 to 0.65 dL/g; 0.55 to less than 0.70 dL/g; 0.55 to 0.68 dL/g; 0.55 to less than 0.68 dL/g; 0.55 to 0.65 dL/g; 0.58 to less than 0.70 dL/g; 0.58 to 0.68 dL/g; 0.58 to less than 0.68 dL/g; or 0.58 to 0.65 dL/g.
For embodiments of the invention where the inherent viscosity of the polyesters of the invention ranges from 0.35 to 0.75 or higher dL/g, these polyesters may also exhibit any of the following inherent viscosities as determined in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.: 0.35 to less than 0.75 dL/g; 0.35 to 0.72 dL/g; or 0.35 to 0.70 dl/g.
For embodiments of the invention, the polyesters useful in the invention may exhibit at least one of the following inherent viscosities as determined in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.: 0.10 to 1.2 dL/g; 0.10 to 1.1 dL/g; 0.10 to 1 dL/g; 0.10 to less than 1 dL/g; 0.10 to 0.98 dL/g; 0.10 to 0.95 dL/g; 0.10 to 0.90 dL/g; 0.10 to 0.85 dL/g; 0.10 to 0.80 dL/g; 0.10 to 0.75 dL/g; 0.10 to less than 0.75 dL/g; 0.10 to 0.72 dL/g; 0.10 to 0.70 dL/g; 0.10 to less than 0.70 dL/g; 0.10 to 0.68 dL/g; 0.10 to less than 0.68 dL/g; 0.10 to 0.65 dL/g; 0.10 to 0.6 dL/g; 0.10 to 0.55 dL/g; 0.10 to 0.5 dL/g; 0.10 to 0.4 dL/g; 0.10 to 0.35 dL/g; 0.20 to 1.2 dL/g; 0.20 to 1.1 dL/g; 0.20 to 1 dL/g; 0.20 to less than 1 dL/g; 0.20 to 0.98 dL/g; 0.20 to 0.95 dL/g; 0.20 to 0.90 dL/g; 0.20 to 0.85 dL/g; 0.20 to 0.80 dL/g; 0.20 to 0.75 dL/g; 0.20 to less than 0.75 dL/g; 0.20 to 0.72 dL/g; 0.20 to 0.70 dL/g; 0.20 to less than 0.70 dL/g; 0.20 to 0.68 dL/g; 0.20 to less than 0.68 dL/g; 0.20 to 0.65 dL/g; 0.20 to 0.6 dL/g; 0.20 to 0.55 dL/g; 0.20 to 0.5 dL/g; 0.20 to 0.4 dL/g; and 0.20 to 0.35 dL/g.
For embodiments of the invention where the inherent viscosity ranges from 0.35 to 1.2 dL/g, these polyesters may also exhibit any of the following inherent viscosities as determined in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.: 0.35 to 1.2 dL/g; 0.35 to 1.1 dL/g; 0.35 to 1 dL/g; 0.35 to less than 1 dL/g; 0.35 to 0.98 dL/g; 0.35 to 0.95 dL/g; 0.35 to 0.9 dL/g; 0.35 to 0.85 dL/g; 0.35 to 0.8 dL/g; 0.35 to 0.75 dL/g; 0.35 to less than 0.75 dL/g; 0.35 to 0.72 dL/g; 0.40 to 1.2 dL/g; 0.40 to 1.1 dL/g; 0.40 to 1 dL/g; 0.40 to less than 1 dL/g; 0.40 to 0.98 dL/g; 0.40 to 0.95 dL/g; 0.40 to 0.9 dL/g; 0.40 to 0.85 dL/g; 0.40 to 0.8 dL/g; 0.40 to 0.75 dL/g; 0.40 to less than 0.75 dL/g; 0.40 to 0.72 dL/g; greater than 0.42 to 1.2 dL/g; greater than 0.42 to 1.1 dL/g; greater than 0.42 to 1 dL/g; greater than 0.42 to less than 1 dL/g; greater than 0.42 to 0.98 dL/g; greater than 0.42 to 0.95 dL/g; greater than 0.42 to 0.9 dL/g; greater than 0.42 to 0.85 dL/g; greater than 0.42 to 0.80 dL/g; greater than 0.42 to 0.75 dL/g; greater than 0.42 to less than 0.75 dL/g; 0.42 to 0.70 dL/g; 0.42 to less than 0.70 dL/g; greater than 0.42 to 0.72 dL/g; greater than 0.42 to 0.70 dL/g; greater than 0.42 to 0.68 dL/g; greater than 0.42 to less than 0.68 dL/g; 0.42 to 0.68 dL/g; greater than 0.42 to 0.65 dL/g; 0.45 to 1.2 dL/g; 0.45 to 1.1 dL/g; 0.45 to 1 dL/g; 0.45 to 0.98 dL/g; 0.45 to 0.95 dL/g; 0.45 to 0.9 dL/g; 0.45 to 0.85 dL/g; 0.45 to 0.80 dL/g; 0.45 to 0.75 dL/g; 0.45 to less than 0.75 dL/g; 0.45 to 0.72 dL/g; 0.45 to 0.70 dL/g; 0.50 to 1.2 dL/g; 0.50 to 1.1 dL/g; 0.50 to 1 dL/g; 0.50 to less than 1 dL/g; 0.50 to 0.98 dL/g; 0.50 to 0.95 dL/g; 0.50 to 0.9 dL/g; 0.50 to 0.85 dL/g; 0.50 to 0.80 dL/g; 0.50 to 0.75 dL/g; 0.50 to less than 0.75 dL/g; 0.50 to 0.72 dL/g; 0.50 to 0.70 dL/g; 0.55 to 1.2 dL/g; 0.55 to 1.1 dL/g; 0.55 to 1 dL/g; 0.55 to less than 1 dL/g; 0.55 to 0.98 dL/g; 0.55 to 0.95 dL/g; 0.55 to 0.9 dL/g; 0.55 to 0.85 dL/g; 0.55 to 0.80 dL/g; 0.55 to 0.75 dL/g; 0.55 to less than 0.75 dL/g; 0.55 to 0.72 dL/g; 0.55 to 0.70 dL/g; 0.58 to 1.2 dL/g; 0.58 to 1.1 dL/g; 0.58 to 1 dL/g; 0.58 to less than 1 dL/g; 0.58 to 0.98 dL/g; 0.58 to 0.95 dL/g; 0.58 to 0.9 dL/g; 0.58 to 0.85 dL/g; 0.58 to 0.80 dL/g; 0.58 to 0.75 dL/g; 0.58 to less than 0.75 dL/g; 0.58 to 0.72 dL/g; 0.58 to 0.70 dL/g; 0.60 to 1.2 dL/g; 0.60 to 1.1 dL/g; 0.60 to 1 dL/g; 0.60 to less than 1 dL/g; 0.60 to 0.98 dL/g; 0.60 to 0.95 dL/g; 0.60 to 0.90 dL/g; 0.60 to 0.85 dL/g; 0.60 to 0.80 dL/g; 0.60 to 0.75 dL/g; 0.60 to less than 0.75 dL/g; 0.60 to 0.72 dL/g; 0.60 to 0.70 dL/g; 0.60 to less than 0.70 dL/g; 0.60 to 0.68 dL/g; 0.60 to less than 0.68 dL/g; 0.60 to 0.65 dL/g; 0.65 to 1.2 dL/g; 0.65 to 1.1 dL/g; 0.65 to 1 dL/g; 0.65 to less than 1 dL/g; 0.65 to 0.98 dL/g; 0.65 to 0.95 dL/g; 0.65 to 0.90 dL/g; 0.65 to 0.85 dL/g; 0.65 to 0.80 dL/g; 0.65 to 0.75 dL/g; 0.65 to less than 0.75 dL/g; 0.65 to 0.72 dL/g; 0.65 to 0.70 dL/g; 0.65 to less than 0.70 dL/g; 0.68 to 1.2 dL/g; 0.68 to 1.1 dL/g; 0.68 to 1 dL/g; 0.68 to less than 1 dL/g; 0.68 to 0.98 dL/g; 0.68 to 0.95 dL/g; 0.68 to 0.90 dL/g; 0.68 to 0.85 dL/g; 0.68 to 0.80 dL/g; 0.68 to 0.75 dL/g; 0.68 to less than 0.75 dL/g; 0.68 to 0.72 dL/g; greater than 0.70 dL/g to 1.2 dL/g; greater than 0.76 dL/g to 1.2 dL/g; greater than 0.76 dL/g to 1.1 dL/g; greater than 0.76 dL/g to 1 dL/g; greater than 0.76 dL/g to less than 1 dL/g; greater than 0.76 dL/g to 0.98 dL/g; greater than 0.76 dL/g to 0.95 dL/g; greater than 0.76 dL/g to 0.90 dL/g; greater than 0.80 dL/g to 1.2 dL/g; greater than 0.80 dL/g to 1.1 dL/g; greater than 0.80 dL/g to 1 dL/g; greater than 0.80 dL/g to less than 1 dL/g; greater than 0.80 dL/g to 1.2 dL/g; greater than 0.80 dL/g to 0.98 dL/g; greater than 0.80 dL/g to 0.95 dL/g; greater than 0.80 dL/g to 0.90 dL/g.
It is contemplated that the compositions of the invention can possess at least one of the inherent viscosity ranges described herein and at least one of the monomer ranges for the compositions described herein unless otherwise stated. It is also contemplated that compositions of the invention can posses at least one of the Tg ranges described herein and at least one of the monomer ranges for the compositions described herein unless otherwise stated. It is also contemplated that compositions of the invention can posses at least one of the Tg ranges described herein, at least one of the inherent viscosity ranges described herein, and at least one of the monomer ranges for the compositions described herein unless otherwise stated.
For the desired polyester, the molar ratio of cis/trans 2,2,4,4-tetramethyl-1,3-cyclobutanediol can vary from the pure form of each or mixtures thereof. In certain embodiments, the molar percentages for cis and/or trans 2,2,4,4,-tetramethyl-1,3-cyclobutanediol are greater than 50 mole % cis and less than 50 mole % trans; or greater than 55 mole % cis and less than 45 mole % trans; or 30 to 70 mole % cis and 70 to 30% trans; or 40 to 60 mole % cis and 60 to 40 mole % trans or 50 to 70 mole % trans and 50 to 30% cis or 50 to 70 mole % cis and 50 to 30% trans; or 60 to 70 mole % cis and 30 to 40 mole % trans; or greater than 70 mole % cis and up to 30 mole % trans; wherein the total sum of the mole percentages for cis- and trans-2,2,4,4-tetramethyl-1,3-cyclobutanediol is equal to 100 mole %. The molar ratio of cis/trans 1,4-cyclohexandimethanol can vary within the range of 50/50 to 0/100, e.g., between 40/60 to 20/80.
In certain embodiments, terephthalic acid or an ester thereof, such as, for example, dimethyl terephthalate, or a mixture of terephthalic acid and an ester thereof, makes up most or all of the dicarboxylic acid component used to form the polyesters useful in the invention. In certain embodiments, terephthalic acid residues can make up a portion or all of the dicarboxylic acid component used to form the polyesters of the invention at a concentration of at least 70 mole %, such as at least 80 mole %, at least 90 mole %, at least 95 mole %, at least 99 mole %, or even a mole % of 100. In certain embodiments, higher amounts of terephthalic acid residues can be used in order to produce a higher impact strength polyester. In one embodiment, dimethyl terephthalate is part or all of the dicarboxylic acid component used to make the polyesters useful in the present invention. For the purposes of this disclosure, the terms: terephthalic acid and “dimethyl terephthalate” are used interchangeably herein. In all embodiments, ranges of 70 to 100 mole %; or 80 to 100 mole %; or 90 to 100 mole %; or 99 to 100 mole %; or 100 mole terephthalic acid and/or dimethyl terephthalate may be used.
In addition to terephthalic acid residues, the dicarboxylic acid component of the polyesters useful in the invention can comprise up to 30 mole %, up to 20 mole %, up to 10 mole %, up to 5 mole %, or up to 1 mole of one or more modifying aromatic dicarboxylic acids. Yet another embodiment contains 0 mole % modifying aromatic dicarboxylic acids. Thus, if present, it is contemplated that the amount of one or more modifying aromatic dicarboxylic acids can range from any of these preceding endpoint values including, for example, from 0.01 to 30 mole %, 0.01 to 20 mole %, from 0.01 to 10 mole %, from 0.01 to 5 mole % and from 0.01 to 1 mole %. In one embodiment, modifying aromatic dicarboxylic acids that may be used in the present invention include but are not limited to those having up to 20 carbon atoms, and which can be linear, para-oriented, or symmetrical. Examples of modifying aromatic dicarboxylic acids which may be used in this invention include, but are not limited to, isophthalic acid, 4,4′-biphenyldicarboxylic acid, 1,4-, 1,5-, 2,6-, 2,7-naphthalenedicarboxylic acid, and trans-4,4′-stilbenedicarboxylic acid, and esters thereof. In one embodiment, the modifying aromatic dicarboxylic acid is isophthalic acid.
The carboxylic acid component of the polyesters useful in the invention can be further modified with up to 10 mole %, such as up to 5 mole % or up to 1 mole % of one or more aliphatic dicarboxylic acids containing 2-16 carbon atoms, such as, for example, malonic, succinic, glutaric, adipic, pimelic, suberic, azelaic and dodecanedioic dicarboxylic acids. Certain embodiments can also comprise 0.01 or more mole %, such as 0.1 or more mole %, 1 or more mole %, 5 or more mole %, or 10 or more mole % of one or more modifying aliphatic dicarboxylic acids. Yet another embodiment contains 0 mole % modifying aliphatic dicarboxylic acids. Thus, if present, it is contemplated that the amount of one or more modifying aliphatic dicarboxylic acids can range from any of these preceding endpoint values including, for example, from 0.01 to 15 mole % and from 0.1 to 10 mole %. The total mole % of the dicarboxylic acid component is 100 mole %.
Esters of terephthalic acid and the other modifying dicarboxylic acids or their corresponding esters and/or salts may be used instead of the dicarboxylic acids. Suitable examples of dicarboxylic acid esters include, but are not limited to, the dimethyl, diethyl, dipropyl, diisopropyl, dibutyl, and diphenyl esters. In one embodiment, the esters are chosen from at least one of the following: methyl, ethyl, propyl, isopropyl, and phenyl esters.
The 1,4-cyclohexanedimethanol may be cis, trans, or a mixture thereof, such as a cis/trans ratio of 60:40 to 40:60. In another embodiment, the trans-1,4-cyclohexanedimethanol can be present in an amount of 60 to 80 mole %.
The glycol component of the polyester portion of the polyester compositions useful in the invention can contain 25 mole % or less of one or more modifying glycols which are not 2,2,4,4-tetramethyl-1,3-cyclobutanediol or 1,4-cyclohexanedimethanol; in one embodiment, the polyesters useful in the invention may contain less than 15 mole % of one or more modifying glycols. In another embodiment, the polyesters useful in the invention can contain 10 mole % or less of one or more modifying glycols. In another embodiment, the polyesters useful in the invention can contain 5 mole % or less of one or more modifying glycols. In another embodiment, the polyesters useful in the invention can contain 3 mole % or less of one or more modifying glycols. In another embodiment, the polyesters useful in the invention can contain 0 mole % modifying glycols. Certain embodiments can also contain 0.01 or more mole %, such as 0.1 or more mole %, 1 or more mole %, 5 or more mole %, or 10 or more mole % of one or more modifying glycols. Thus, if present, it is contemplated that the amount of one or more modifying glycols can range from any of these preceding endpoint values including, for example, from 0.01 to 15 mole % and from 0.01 to 10 mole %.
Modifying glycols useful in the polyesters useful in the invention can refer to diols other than 2,2,4,4,-tetramethyl-1,3-cyclobutanediol and 1,4-cyclohexanedimethanol and may contain 2 to 16 carbon atoms. Examples of suitable modifying glycols include, but are not limited to, ethylene glycol, diethylene glycol, 1,2-propanediol, 1,3-propanediol, neopentyl glycol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, p-xylene glycol, or mixtures thereof. In one embodiment, the modifying glycol is ethylene glycol. In another embodiment, the modifying glycols include, but are not limited to, 1,3-propanediol and/or 1,4-butanediol. In another embodiment, ethylene glycol is excluded as a modifying diol. In another embodiment, 1,3-propanediol and 1,4-butanediol are excluded as modifying diols. In another embodiment, 2,2-dimethyl-1,3-propanediol is excluded as a modifying diol.
The polyesters and/or the polycarbonates useful in the polyesters compositions of the invention can comprise from 0 to 10 mole percent, for example, from 0.01 to 5 mole percent, from 0.01 to 1 mole percent, from 0.05 to 5 mole percent, from 0.05 to 1 mole percent, or from 0.1 to 0.7 mole percent, or 0.1 to 0.5 mole percent, based the total mole percentages of either the diol or diacid residues; respectively, of one or more residues of a branching monomer, also referred to herein as a branching agent, having 3 or more carboxyl substituents, hydroxyl substituents, or a combination thereof. In certain embodiments, the branching monomer or agent may be added prior to and/or during and/or after the polymerization of the polyester. The polyester(s) useful in the invention can thus be linear or branched. The polycarbonate can also be linear or branched. In certain embodiments, the branching monomer or agent may be added prior to and/or during and/or after the polymerization of the polycarbonate.
Examples of branching monomers include, but are not limited to, multifunctional acids or multifunctional alcohols such as trimellitic acid, trimellitic anhydride, pyromellitic dianhydride, trimethylolpropane, glycerol, pentaerythritol, citric acid, tartaric acid, 3-hydroxyglutaric acid and the like. In one embodiment, the branching monomer residues can comprise 0.1 to 0.7 mole percent of one or more residues chosen from at least one of the following: trimellitic anhydride, pyromellitic dianhydride, glycerol, sorbitol, 1,2,6-hexanetriol, pentaerythritol, trimethylolethane, and/or trimesic acid. The branching monomer may be added to the polyester reaction mixture or blended with the polyester in the form of a concentrate as described, for example, in U.S. Pat. Nos. 5,654,347 and 5,696,176, whose disclosure regarding branching monomers is incorporated herein by reference.
Glass transition temperature (Tg) can be determined using a TA DSC 2920 from Thermal Analyst Instrument at a scan rate of 20° C./min.
Because of the long crystallization half-times (e.g., greater than 5 minutes) at 170° C. exhibited by certain polyesters useful in the present invention, it can be possible to produce articles, including but not limited to, injection molded parts, injection blow molded articles, injection stretch blow molded articles, extruded film, extruded sheet, extrusion blow molded articles and fibers. The polyesters of the invention can be amorphous or semicrystalline. In one aspect, certain polyesters useful in the invention can have relatively low crystallinity. Certain polyesters useful in the invention can thus have a substantially amorphous morphology, meaning that the polyesters comprise substantially unordered regions of polymer.
In one embodiment, an “amorphous” polyester can have a crystallization half-time of greater than 5 minutes at 170° C. or greater than 10 minutes at 170° C. or greater than 50 minutes at 170° C. or greater than 100 minutes at 170° C. In one embodiment, of the invention, the crystallization half-times can be greater than 1,000 minutes at 170° C. In another embodiment of the invention, the crystallization half-times of the polyester useful in the invention can be greater than 10,000 minutes at 170° C. The crystallization half time of the polyester, as used herein, may be measured using methods well-known to persons of skill in the art. For example, the crystallization half time of the polyester, t1/2, can be determined by measuring the light transmission of a sample via a laser and photo detector as a function of time on a temperature controlled hot stage. This measurement can be done by exposing the polymers to a temperature, Tmax, and then cooling it to the desired temperature. The sample can then be held at the desired temperature by a hot stage while transmission measurements were made as a function of time. Initially, the sample can be visually clear with high light transmission and became opaque as the sample crystallizes. The crystallization half-time is the time at which the light transmission is halfway between the initial transmission and the final transmission. Tmax is defined as the temperature required to melt the crystalline domains of the sample (if crystalline domains are present). The sample can be heated to Tmax to condition the sample prior to crystallization half time measurement. The absolute Tmax temperature is different for each composition. For example PCT can be heated to some temperature greater than 290° C. to melt the crystalline domains.
As shown in Table 1 and
The polyester can exhibit an improvement in toughness combined with processability for some of the embodiments of the invention. For example, lowering the inherent viscosity slightly of the polyesters useful in the invention results in a more processable melt viscosity while retaining good physical properties of the polyesters such as toughness and heat resistance.
Increasing the content of 1,4-cyclohexanedimethanol in a copolyester based on terephthalic acid, ethylene glycol, and 1,4-cyclohexanedimethanol can improve toughness, which can be determined by the brittle-to-ductile transition temperature in a notched Izod impact strength test as measured by ASTM D256. This toughness improvement, by lowering of the brittle-to-ductile transition temperature with 1,4-cyclohexanedimethanol, is believed to occur due to the flexibility and conformational behavior of 1,4-cyclohexanedimethanol in the copolyester. Incorporating 2,2,4,4-tetramethyl-1,3-cyclobutanediol into PCT is believed to improve toughness, by lowering the brittle-to-ductile transition temperature, as shown in Table 2 and
In one embodiment, the melt viscosity of the polyester(s) useful in the invention is less than 30,000 poise as measured a 1 radian/second on a rotary melt rheometer at 290° C. In another embodiment, the melt viscosity of the polyester(s) useful in the invention is less than 20,000 poise as measured a 1 radian/second on a rotary melt rheometer at 290° C.
In one embodiment, the melt viscosity of the polyester(s) useful in the invention is less than 15,000 poise as measured at 1 radian/second (rad/sec) on a rotary melt rheometer at 290° C.
In one embodiment, the melt viscosity of the polyester(s) useful in the invention is less than 10,000 poise as measured at 1 radian/second (rad/sec) on a rotary melt rheometer at 290° C. In another embodiment, the melt viscosity of the polyester(s) useful in the invention is less than 6,000 poise as measured at 1 radian/second on a rotary melt rheometer at 290° C. Viscosity at rad/sec is related to processability. Typical polymers have viscosities of less than 10,000 poise as measured at 1 radian/second when measured at their processing temperature. Polyesters are typically not processed above 290° C. Polycarbonate is typically processed at 290° C. The viscosity at 1 rad/sec of a typical 12 melt flow rate polycarbonate is 7000 poise at 290° C.
The present polyesters useful in the invention can possess one or more of the following properties. Notched Izod impact strength, as described in ASTM D256, is a common method of measuring toughness. The present polyesters useful in this invention can possess one or more of the following properties. In one embodiment, the polyesters useful in the invention exhibit a impact strength of at least 150 J/m (3 ft-lb/in) at 23° C. with a 10-mil notch in a 3.2 mm (⅛-inch) thick bar determined according to ASTM D256; in one embodiment, the polyesters useful in the invention exhibit a notched Izod impact strength of at least (400 J/m) 7.5 ft-lb/in at 23° C. with a 10-mil notch in a 3.2 mm (⅛-inch) thick bar determined according to ASTM D256; in one embodiment, the polyesters useful in the invention exhibit a notched Izod impact strength of at least 1000 J/m (18 ft-lb/in) at 23° C. with a 10-mil notch in a 3.2 mm (⅛-inch) thick bar determined according to ASTM D256. In one embodiment, the polyesters useful in the invention exhibit a notched Izod impact strength of at least 150 J/m (3 ft-lb/in) at 23° C. with a 10-mil notch in a 6.4 mm (¼-inch) thick bar determined according to ASTM D256; in one embodiment, the polyesters useful in the invention exhibit a notched Izod impact strength of at least (400 J/m) 7.5 ft-lb/in at 23° C. with a 10-mil notch in a 6.4 mm (¼-inch) thick bar determined according to ASTM D256; in one embodiment, the polyesters useful in the invention exhibit a notched Izod impact strength of at least 1000 J/m (18 ft-lb/in) at 23° C. with a 10-mil notch in a 6.4 mm (¼-inch) thick bar determined according to ASTM D256.
In another embodiment, certain polyesters useful in the invention can exhibit an increase in notched Izod impact strength when measured at 0° C. of at least 3% or at least 5% or at least 10% or at least 15% as compared to the notched Izod impact strength when measured at −5° C. with a 10-mil notch in a ⅛-inch thick bar determined according to ASTM D256. In addition, certain other polyesters can also exhibit a retention of notched Izod impact strength within plus or minus 5% when measured at 0° C. through 30° C. with a 10-mil notch in a ⅛-inch thick bar determined according to ASTM D256.
In yet another embodiment, certain polyesters useful in the invention can exhibit a retention in notched Izod impact strength with a loss of no more than 70% when measured at 23° C. with a 10-mil notch in a ¼-inch thick bar determined according to ASTM D256 as compared to notched Izod impact strength for the same polyester when measured at the same temperature with a 10-mil notch in a ⅛-inch thick bar determined according to ASTM D256.
In one embodiment, the polyesters useful in the invention can exhibit a ductile-to-brittle transition temperature of less than 0° C. based on a 10-mil notch in a ⅛-inch thick bar as defined by ASTM D256.
In one embodiment, the polyesters useful in the invention can exhibit at least one of the following densities as determined using a gradient density column at 23° C.: a density of less than 1.2 g/ml at 23° C.; a density of less than 1.18 g/ml at 23° C.; a density of 0.8 to 1.3 g/ml at 23° C.; a density of 0.80 to 1.2 g/ml at 23° C.; a density of 0.80 to less than 1.2 g/ml at 23° C.; a density of 1.0 to 1.3 g/ml at 23° C.; a density of 1.0 to 1.2 g/ml at 23° C.; a density of 1.0 to 1.1 g/ml at 23° C.; a density of 1.13 to 1.3 g/ml at 23° C.; a density of 1.13 to 1.2 g/ml at 23° C.
In one embodiment, the polyesters useful in this invention can be visually clear. The term “visually clear” is defined herein as an appreciable absence of cloudiness, haziness, and/or muddiness, when inspected visually. In another embodiment, when the polyesters are blended with polycarbonate, including but not limited to, bisphenol A polycarbonates, the blends can be visually clear.
In other embodiments of the invention, the polyesters useful in the invention may have a yellowness index (ASTM D-1925) of less than 50 or less than 20.
In one embodiment, the polyesters useful in the invention and/or the polyester compositions of the invention, with or without toners, can have color values L*, a* and b* which can be determined using a Hunter Lab Ultrascan Spectra Colorimeter manufactured by Hunter Associates Lab Inc., Reston, Va. The color determinations are averages of values measured on either pellets of the polyesters or plaques or other items injection molded or extruded from them. They are determined by the L*a*b* color system of the CIE (International Commission on Illumination) (translated), wherein L* represents the lightness coordinate, a* represents the red/green coordinate, and b* represents the yellow/blue coordinate. In certain embodiments, the b* values for the polyesters useful in the invention can be from −10 to less than 10 and the L* values can be from 50 to 90. In other embodiments, the b* values for the polyesters useful in the invention can be present in one of the following ranges: from −10 to 9; −10 to 8; −10 to 7; −10 to 6; −10 to 5; −10 to 4; −10 to 3; −10 to 2; from −5 to 9; −5 to 8; −5 to 7; −5 to 6; −5 to 5; −5 to 4; −5 to 3; −5 to 2; 0 to 9; 0 to 8; 0 to 7; 0 to 6; 0 to 5; 0 to 4; 0 to 3; 0 to 2; 1 to 10; 1 tog; 1 to 8; 1 to 7; 1 to 6; 1 to 5; 1 to 4; 1 to 3; and 1 to 2. In other embodiments, the L* value for the polyesters useful in the invention can be present in one of the following ranges: 50 to 60; 50 to 70; 50 to 80; 50 to 90; 60 to 70; 60 to 80; 60 to 90; 70 to 80; 79 to 90.
In some embodiments, use of the polyester compositions useful in the invention minimizes and/or eliminates the drying step prior to melt processing and/or thermoforming.
The polyester portion of the polyester compositions of the invention can be made by processes known from the literature such as, for example, by processes in homogenous solution, by transesterification processes in the melt, and by two phase interfacial processes. Suitable methods include, but are not limited to, the steps of reacting one or more dicarboxylic acids with one or more glycols at a temperature of 100° C. to 315° C. at a pressure of 0.1 to 760 mm Hg for a time sufficient to form a polyester. See U.S. Pat. No. 3,772,405 for methods of producing polyesters, the disclosure regarding such methods is hereby incorporated herein by reference.
In another aspect, the invention relates to a process for producing a polyester. The process comprises:
(I) heating a mixture comprising the monomers useful in any of the polyesters in the invention in the presence of a catalyst at a temperature of 150 to 240° C. for a time sufficient to produce an initial polyester;
(II) heating the initial polyester of step (I) at a temperature of 240 to 320° C. for 1 to 4 hours; and
(III) removing any unreacted glycols.
Suitable catalysts for use in this process include, but are not limited to, organo-zinc or tin compounds. The use of this type of catalyst is well known in the art. Examples of catalysts useful in the present invention include, but are not limited to, zinc acetate, butyltin tris-2-ethylhexanoate, dibutyltin diacetate, and/or dibutyltin oxide. Other catalysts may include, but are not limited to, those based on titanium, zinc, manganese, lithium, germanium, and cobalt. Catalyst amounts can range from 10 ppm to 20,000 ppm or 10 to 10,000 ppm, or 10 to 5000 ppm or 10 to 1000 ppm or 10 to 500 ppm, or 10 to 300 ppm or 10 to 250 based on the catalyst metal and based on the weight of the final polymer. The process can be carried out in either a batch or continuous process.
Typically, step (I) can be carried out until 50% by weight or more of the 2,2,4,4-tetramethyl-1,3-cyclobutanediol has been reacted. Step (I) may be carried out under pressure, ranging from atmospheric pressure to 100 psig. The term “reaction product” as used in connection with any of the catalysts useful in the invention refers to any product of a polycondensation or esterification reaction with the catalyst and any of the monomers used in making the polyester as well as the product of a polycondensation or esterification reaction between the catalyst and any other type of additive.
Typically, Step (II) and Step (III) can be conducted at the same time. These steps can be carried out by methods known in the art such as by placing the reaction mixture under a pressure ranging, from 0.002 psig to below atmospheric pressure, or by blowing hot nitrogen gas over the mixture.
In one embodiment, the invention further relates to a polyester product made by the process described above.
The invention further relates to a polymer blend. The blend comprises:
(a) 5 to 95 wt % of at least one of the polyesters described above; and
(b) 5 to 95 wt % of at least one polymeric components.
Suitable examples of the polymeric components include, but are not limited to, nylon, polyesters different from those described herein, polyamides such as ZYTEL® from DuPont; polystyrene, polystyrene copolymers, stryrene acrylonitrile copolymers, acrylonitrile butadiene styrene copolymers, poly(methylmethacrylate), acrylic copolymers, poly(ether-imides) such as ULTEM® (a poly(ether-imide) from General Electric); polyphenylene oxides such as poly(2,6-dimethylphenylene oxide) or poly(phenylene oxide)/polystyrene blends such as NORYL 1000® (a blend of poly(2,6-dimethylphenylene oxide) and polystyrene resins from General Electric); polyphenylene sulfides; polyphenylene sulfide/sulfones; poly(ester-carbonates); polycarbonates such as LEXAN® (a polycarbonate from General Electric); polysulfones; polysulfone ethers; and poly(ether-ketones) of aromatic dihydroxy compounds; or mixtures of any of the foregoing polymers. The blends can be prepared by conventional processing techniques known in the art, such as melt blending or solution blending. In one embodiment, the polycarbonate is not present in the polyester composition. If polycarbonate is used in a blend in the polyester compositions useful in the invention, the blends can be visually clear. However, the polyester compositions useful in the invention also contemplate the exclusion of polycarbonate as well as the inclusion of polycarbonate.
Polycarbonates useful in the invention may be prepared according to known procedures, for example, by reacting the dihydroxyaromatic compound with a carbonate precursor such as phosgene, a haloformate or a carbonate ester, a molecular weight regulator, an acid acceptor and a catalyst. Methods for preparing polycarbonates are known in the art and are described, for example, in U.S. Pat. No. 4,452,933, where the disclosure regarding the preparation of polycarbonates is hereby incorporated by reference herein.
Examples of suitable carbonate precursors include, but are not limited to, carbonyl bromide, carbonyl chloride, or mixtures thereof; diphenyl carbonate; a di(halophenyl)carbonate, e.g., di(trichlorophenyl) carbonate, di(tribromophenyl) carbonate, and the like; di(alkylphenyl)carbonate, e.g., di(tolyl)carbonate; di(naphthyl)carbonate; di(chloronaphthyl)carbonate, or mixtures thereof; and bis-haloformates of dihydric phenols.
Examples of suitable molecular weight regulators include, but are not limited to, phenol, cyclohexanol, methanol, alkylated phenols, such as octylphenol, para-tertiary-butyl-phenol, and the like. In one embodiment, the molecular weight regulator is phenol or an alkylated phenol.
The acid acceptor may be either an organic or an inorganic acid acceptor. A suitable organic acid acceptor can be a tertiary amine and includes, but is not limited to, such materials as pyridine, triethylamine, dimethylaniline, tributylamine, and the like. The inorganic acid acceptor can be either a hydroxide, a carbonate, a bicarbonate, or a phosphate of an alkali or alkaline earth metal.
The catalysts that can be used include, but are not limited to, those that typically aid the polymerization of the monomer with phosgene. Suitable catalysts include, but are not limited to, tertiary amines such as triethylamine, tripropylamine, N,N-dimethylaniline, quaternary ammonium compounds such as, for example, tetraethylammonium bromide, cetyl triethyl ammonium bromide, tetra-n-heptylammonium iodide, tetra-n-propyl ammonium bromide, tetramethyl ammonium chloride, tetra-methyl ammonium hydroxide, tetra-n-butyl ammonium iodide, benzyltrimethyl ammonium chloride and quaternary phosphonium compounds such as, for example, n-butyltriphenyl phosphonium bromide and methyltriphenyl phosphonium bromide.
The polycarbonates useful in the polyester compositions of the invention also may be copolyestercarbonates such as those described in U.S. Pat. Nos. 3,169,121; 3,207,814; 4,194,038; 4,156,069; 4,430,484, 4,465,820, and 4,981,898, where the disclosure regarding copolyestercarbonates from each of the U.S. patents is incorporated by reference herein.
Copolyestercarbonates useful in this invention can be available commercially and/or can prepared by known methods in the art. For example, they can be typically obtained by the reaction of at least one dihydroxyaromatic compound with a mixture of phosgene and at least one dicarboxylic acid chloride, especially isophthaloyl chloride, terephthaloyl chloride, or both.
In addition, the polyester compositions and the polymer blend compositions containing the polyesters of this invention may also contain from 0.01 to 25% by weight or 0.01 to 20% by weight or 0.01 to 15% by weight or 0.01 to 10% by weight or 0.01 to 5% by weight of the total weight of the polyester composition of common additives such as colorants, dyes, mold release agents, flame retardants, plasticizers, nucleating agents, stabilizers, including but not limited to, UV stabilizers, thermal stabilizers and/or reaction products thereof, fillers, and impact modifiers. Examples of typical commercially available impact modifiers well known in the art and useful in this invention include, but are not limited to, ethylene/propylene terpolymers; functionalized polyolefins, such as those containing methyl acrylate and/or glycidyl methacrylate; styrene-based block copolymeric impact modifiers; and various acrylic core/shell type impact modifiers. For example, UV additives can be incorporated into articles of manufacture through addition to the bulk, through application of a hard coat, or through coextrusion of a cap layer. Residues of such additives are also contemplated as part of the polyester composition.
The polyesters of the invention can comprise at least one chain extender.
Suitable chain extenders include, but are not limited to, multifunctional (including, but not limited to, bifunctional) isocyanates, multifunctional epoxides, including for example, epoxylated novolacs, and phenoxy resins. In certain embodiments, chain extenders may be added at the end of the polymerization process or after the polymerization process. If added after the polymerization process, chain extenders can be incorporated by compounding or by addition during conversion processes such as injection molding or extrusion. The amount of chain extender used can vary depending on the specific monomer composition used and the physical properties desired but is generally about 0.1 percent by weight to about 10 percent by weight, preferably about 0.1 to about 5 percent by weight based on the total weight of the polyester.
Thermal stabilizers are compounds that stabilize polyesters during polyester manufacture and/or post polymerization, including but not limited to phosphorous compounds including but not limited to phosphoric acid, phosphorous acid, phosphonic acid, phosphinic acid, phosphonous acid, and various esters and salts thereof. These can be present in the polyester compositions useful in the invention. The esters can be alkyl, branched alkyl, substituted alkyl, difunctional alkyl, alkyl ethers, aryl, and substituted aryl. In one embodiment, the number of ester groups present in the particular phosphorous compound can vary from zero up to the maximum allowable based on the number of hydroxyl groups present on the thermal stabilizer used. The term “thermal stabilizer” is intended to include the reaction product(s) thereof. The term “reaction product” as used in connection with the thermal stabilizers of the invention refers to any product of a polycondensation or esterification reaction between the thermal stabilizer and any of the monomers used in making the polyester as well as the product of a polycondensation or esterification reaction between the catalyst and any other type of additive.
Reinforcing materials may be useful in the compositions of this invention. The reinforcing materials may include, but are not limited to, carbon filaments, silicates, mica, clay, talc, titanium dioxide, Wollastonite, glass flakes, glass beads and fibers, and polymeric fibers and combinations thereof. In one embodiment, the reinforcing materials are glass, such as fibrous glass filaments, mixtures of glass and talc, glass and mica, and glass and polymeric fibers.
In another embodiment, the invention further relates to articles of manufacture comprising any of the polyesters and blends described above.
In another embodiment, the invention further relates to articles of manufacture comprising any of the polyesters and blends described herein. extruded, calendered, and/or molded articles including but not limited to, injection molded articles, extruded articles, cast extrusion articles, profile extrusion articles, melt spun articles, thermoformed articles, extrusion molded articles, injection blow molded articles, injection stretch blow molded articles, extrusion blow molded articles, and extrusion stretch blow molded articles. These articles can include, but are not limited, to films, bottles (including, but not limited to, baby bottles), containers, sheet and/or fibers.
The present polyesters and/or polyester blend compositions can be useful in forming fibers, films, molded articles, containers, and sheeting. The methods of forming the polyesters into fibers, films, molded articles, containers, and sheeting are well known in the art. Examples of potential molded articles include without limitation: medical devices such as dialysis equipment, medical packaging, healthcare supplies, commercial food service products such as food pans, tumblers and storage boxes, baby bottles, food processors, blender and mixer bowls, utensils, water bottles, crisper trays, washing machine fronts, and vacuum cleaner parts. Other potential molded articles could include, but are not limited to, ophthalmic lenses and frames. For instance, this material can be used to make bottles, including but not limited to, baby bottles, as it is clear, tough, heat resistant, and displays good hydrolytic stability.
In another embodiment, the invention further relates to articles of manufacture comprising the film(s) and/or sheet(s) containing polyester compositions described herein.
The films and/or sheets useful in the present invention can be of any thickness which would be apparent to one of ordinary skill in the art. In one embodiment, the film(s) of the invention have a thickness of no more than 40 mils. In one embodiment, the film(s) of the invention have a thickness of no more than 35 mils. In one embodiment, the film(s) of the invention have a thickness of no more than 30 mils. In one embodiment, the film(s) of the invention have a thickness of no more than 25 mils. In one embodiment, the film(s) of the invention have a thickness of no more than 20 mils.
In one embodiment, the sheet(s) of the invention have a thickness of no less than 20 mils. In another embodiment, the sheet(s) of the invention have a thickness of no less than 25 mils. In another embodiment, the sheet(s) of the invention have a thickness of no less than 30 mils. In another embodiment, the sheet(s) of the invention have a thickness of no less than 35 mils. In another embodiment, the sheet(s) of the invention have a thickness of no less than 40 mils.
The invention further relates to the film(s) and/or sheet(s) comprising the polyester compositions of the invention. The methods of forming the polyesters into film(s) and/or sheet(s) are well known in the art. Examples of film(s) and/or sheet(s) of the invention including but not limited to extruded film(s) and/or sheet(s), calendered film(s) and/or sheet(s), compression molded film(s) and/or sheet(s), solution casted film(s) and/or sheet(s). Methods of making film and/or sheet include but are not limited to extrusion, calendering, compression molding, and solution casting.
Examples of potential articles made from film and/or sheet include, but are not limited, to uniaxially stretched film, biaxially stretched film, shrink film (whether or not uniaxially or biaxially stretched, liquid crystal display film (including but not limited to diffuser sheets, compensation films and protective films), thermoformed sheet, graphic arts film, outdoor signs, skylights, coating(s), coated articles, painted articles, laminates, laminated articles, and/or multiwall films or sheets.
Examples of graphic arts film include, but are not limited to, nameplates, membrane switch overlays; point-of-purchase displays; flat or in-mold decorative panels on washing machines; flat touch panels on refrigerators; flat panel on ovens; decorative interior trim for automobiles; instrument clusters for automobiles; cell phone covers; heating and ventilation control displays; automotive console panels; automotive gear shift panels; control displays or warning signals for automotive instrument panels; facings, dials or displays on household appliances; facings, dials or displays on washing machines; facings, dials or displays on dishwashers; keypads for electronic devices; keypads for mobile phones, PDAs (hand-held computers) or remote controls; displays for electronic devices; displays for hand-held electronic devices such as phones and PDAs; panels and housings for mobile or standard phones; logos on electronic devices; and logos for hand-held phones.
Multiwall film or sheet refers to sheet extruded as a profile consisting of multiple layers that are connected to each other by means of vertical ribs. Examples of multiwall film or sheet include but are not limited to greenhouses and commercial canopies.
Examples of extruded articles include but are not limited to film for graphic arts, applications, outdoor signs, skylights, film for plastic glass laminates, and liquid crystal display (LCD) films, including, but not limited to, diffuser sheets, compensation films, and protective films.
As used herein, the abbreviation “wt” means “weight”.
The following examples further illustrate how the polyesters and/or polyester compositions of the invention can be made and evaluated, and are intended to be purely exemplary of the invention and are not intended to limit the scope thereof. Unless indicated otherwise, parts are parts by weight, temperature is in degrees C. or is at room temperature, and pressure is at or near atmospheric.
Measurement Methods
The inherent viscosity of the polyesters was determined in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C.
Unless stated otherwise, the glass transition temperature (Tg) was determined using a TA DSC 2920 instrument from Thermal Analyst Instruments at a scan rate of 20° C./min according to ASTM D3418.
The glycol content and the cis/trans ratio of the compositions were determined by proton nuclear magnetic resonance (NMR) spectroscopy. All NMR spectra were recorded on a JEOL Eclipse Plus 600 MHz nuclear magnetic resonance spectrometer using either chloroform-trifluoroacetic acid (70-30 volume/volume) for polymers or, for oligomeric samples, 60/40 (wt/wt) phenol/tetrachloroethane with deuterated chloroform added for lock. Peak assignments for 2,2,4,4-tetramethyl-1,3-cyclobutanediol resonances were made by comparison to model mono- and dibenzoate esters of 2,2,4,4-tetramethyl-1,3-cyclobutanediol. These model compounds closely approximate the resonance positions found in the polymers and oligomers.
The crystallization half-time, t½, was determined by measuring the light transmission of a sample via a laser and photo detector as a function of time on a temperature controlled hot stage. This measurement was done by exposing the polymers to a temperature, Tmax, and then cooling it to the desired temperature. The sample was then held at the desired temperature by a hot stage while transmission measurements were made as a function of time. Initially, the sample was visually clear with high light transmission and became opaque as the sample crystallized. The crystallization half-time was recorded as the time at which the light transmission was halfway between the initial transmission and the final transmission. Tmax is defined as the temperature required to melt the crystalline domains of the sample (if crystalline domains are present). The Tmax reported in the examples below represents the temperature at which each sample was heated to condition the sample prior to crystallization half time measurement. The Tmax temperature is dependant on composition and is typically different for each polyester. For example, PCT may need to be heated to some temperature greater than 290° C. to melt the crystalline domains.
Density was determined using a gradient density column at 23° C.
The melt viscosity reported herein was measured by using a Rheometrics Dynamic Analyzer (RDA II). The melt viscosity was measured as a function of shear rate, at frequencies ranging from 1 to 400 rad/sec, at the temperatures reported. The zero shear melt viscosity (η0) is the melt viscosity at zero shear rate estimated by extrapolating the data by known models in the art. This step is automatically performed by the Rheometrics Dynamic Analyzer (RDA II) software.
The polymers were dried at a temperature ranging from 80 to 100° C. in a vacuum oven for 24 hours and injection molded on a Boy 22S molding machine to give ⅛×½×5-inch and ¼×½×5-inch flexure bars. These bars were cut to a length of 2.5 inch and notched down the ½ inch width with a 10-mil notch in accordance with ASTM D256. The average Izod impact strength at 23° C. was determined from measurements on 5 specimens.
In addition, 5 specimens were tested at various temperatures using 5° C. increments in order to determine the brittle-to-ductile transition temperature. The brittle-to-ductile transition temperature is defined as the temperature at which 50% of the specimens fail in a brittle manner as denoted by ASTM D256.
Color values reported herein were determined using a Hunter Lab Ultrascan Spectra Colorimeter manufactured by Hunter Associates Lab Inc., Reston, Va. The color determinations were averages of values measured on either pellets of the polyesters or plaques or other items injection molded or extruded from them. They were determined by the L*a*b* color system of the CIE (International Commission on Illumination) (translated), wherein L* represents the lightness coordinate, a* represents the red/green coordinate, and b* represents the yellow/blue coordinate.
In addition, 10-mil films were compression molded using a Carver press at 240° C.
Unless otherwise specified, the cis/trans ratio of the 1,4 cyclohexanedimethanol used in the following examples was approximately 30/70, and could range from 35/65 to 25/75. Unless otherwise specified, the cis/trans ratio of the 2,2,4,4-tetramethyl-1,3-cyclobutanediol used in the following examples was approximately 50/50.
The following abbreviations apply throughout the working examples and figures:
This example illustrates that 2,2,4,4-tetramethyl-1,3-cyclobutanediol is more effective at reducing the crystallization rate of PCT than ethylene glycol or isophthalic acid. In addition, this example illustrates the benefits of 2,2,4,4-tetramethyl-1,3-cyclobutanediol on the glass transition temperature and density.
A variety of copolyesters were prepared as described below. These copolyesters were all made with 200 ppm dibutyl tin oxide as the catalyst in order to minimize the effect of catalyst type and concentration on nucleation during crystallization studies. The cis/trans ratio of the 1,4-cyclohexanedimethanol was 31/69 while the cis/trans ratio of the 2,2,4,4-tetramethyl-1,3-cyclobutanediol is reported in Table 1.
For purposes of this example, the samples had sufficiently similar inherent viscosities thereby effectively eliminating this as a variable in the crystallization rate measurements.
Crystallization half-time measurements from the melt were made at temperatures from 140 to 200° C. at 10° C. increments and are reported in Table 1. The fastest crystallization half-time for each sample was taken as the minimum value of crystallization half-time as a function of temperature, typically occurring around 170 to 180° C. The fastest crystallization half-times for the samples are plotted in
The data shows that 2,2,4,4-tetramethyl-1,3-cyclobutanediol is more effective than ethylene glycol and isophthalic acid at decreasing the crystallization rate (i.e., increasing the crystallization half-time). In addition, 2,2,4,4-tetramethyl-1,3-cyclobutanediol increases Tg and lowers density.
1The balance of the diol component of the polyesters in Table 1 is 1, 4-cyclohexanedimethanol; and the balance of the dicarboxylic acid component of the polyesters in Table 1 is dimethyl terephthalate; if the dicarboxylic acid is not described, it is 100 mole % dimethyl terephthalate.
2100 mole % 1,4-cyclohexanedimethanol.
3A film was pressed from the ground polyester of Example 1G at 240° C. The resulting film had an inherent viscosity value of 0.575 dL/g.
4A film was pressed from the ground polyester of Example 1H at 240° C. The resulting film had an inherent viscosity value of 0.0.652 dL/g.
As shown in Table 1 and
Preparation of the polyesters shown on Table 1 is described below.
This example illustrates the preparation of a copolyester with a target composition of 80 mol % dimethyl terephthalate residues, 20 mol % dimethyl isophthalate residues, and 100 mol % 1,4-cyclohexanedimethanol residues (28/72 cis/trans).
A mixture of 56.63 g of dimethyl terephthalate, 55.2 g of 1,4-cyclohexanedimethanol, 14.16 g of dimethyl isophthalate, and 0.0419 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 210° C. The stirring speed was set to 200 RPM throughout the experiment. The contents of the flask were heated at 210° C. for 5 minutes and then the temperature was gradually increased to 290° C. over 30 minutes. The reaction mixture was held at 290° C. for 60 minutes and then vacuum was gradually applied over the next 5 minutes until the pressure inside the flask reached 100 mm of Hg. The pressure inside the flask was further reduced to 0.3 mm of Hg over the next 5 minutes. A pressure of 0.3 mm of Hg was maintained for a total time of 90 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 87.5° C. and an inherent viscosity of 0.63 dl/g. NMR analysis showed that the polymer was composed of 100 mol % 1,4-cyclohexanedimethanol residues and 20.2 mol % dimethyl isophthalate residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 20 mol % ethylene glycol residues, and 80 mol % 1,4-cyclohexanedimethanol residues (32/68 cis/trans).
A mixture of 77.68 g of dimethyl terephthalate, 50.77 g of 1,4-cyclohexanedimethanol, 27.81 g of ethylene glycol, and 0.0433 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 200° C. The stirring speed was set to 200 RPM throughout the experiment. The contents of the flask were heated at 200° C. for 60 minutes and then the temperature was gradually increased to 210° C. over 5 minutes. The reaction mixture was held at 210° C. for 120 minutes and then heated up to 280° C. in 30 minutes. Once at 280° C., vacuum was gradually applied over the next 5 minutes until the pressure inside the flask reached 100 mm of Hg. The pressure inside the flask was further reduced to 0.3 mm of Hg over the next 10 minutes. A pressure of 0.3 mm of Hg was maintained for a total time of 90 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 87.7° C. and an inherent viscosity of 0.71 dl/g. NMR analysis showed that the polymer was composed of 19.8 mol % ethylene glycol residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 20 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues, and 80 mol % 1,4-cyclohexanedimethanol residues (31/69 cis/trans).
A mixture of 77.68 g of dimethyl terephthalate, 48.46 g of 1,4-cyclohexanedimethanol, 17.86 g of 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 0.046 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. This polyester was prepared in a manner similar to that described in Example 1A. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 100.5° C. and an inherent viscosity of 0.73 dl/g. NMR analysis showed that the polymer was composed of 80.5 mol % 1,4-cyclohexanedimethanol residues and 19.5 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 40 mol % dimethyl isophthalate residues, and 100 mol % 1,4-cyclohexanedimethanol residues (28/72 cis/trans).
A mixture of 42.83 g of dimethyl terephthalate, 55.26 g of 1,4-cyclohexanedimethanol, 28.45 g of dimethyl isophthalate, and 0.0419 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 210° C. The stirring speed was set to 200 RPM throughout the experiment. The contents of the flask were heated at 210° C. for 5 minutes and then the temperature was gradually increased to 290° C. over 30 minutes. The reaction mixture was held at 290° C. for 60 minutes and then vacuum was gradually applied over the next 5 minutes until the pressure inside the flask reached 100 mm of Hg. The pressure inside the flask was further reduced to 0.3 mm of Hg over the next 5 minutes. A pressure of 0.3 mm of Hg was maintained for a total time of 90 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 81.2° C. and an inherent viscosity of 0.67 dl/g. NMR analysis showed that the polymer was composed of 100 mol % 1,4-cyclohexanedimethanol residues and 40.2 mol % dimethyl isophthalate residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 40 mol % ethylene glycol residues, and 60 mol % 1,4-cyclohexanedimethanol residues (31/69 cis/trans).
A mixture of 81.3 g of dimethyl terephthalate, 42.85 g of 1,4-cyclohexanedimethanol, 34.44 g of ethylene glycol, and 0.0419 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 200° C. The stirring speed was set to 200 RPM throughout the experiment. The contents of the flask were heated at 200° C. for 60 minutes and then the temperature was gradually increased to 210° C. over 5 minutes. The reaction mixture was held at 210° C. for 120 minutes and then heated up to 280° C. in 30 minutes. Once at 280° C., vacuum was gradually applied over the next 5 minutes until the pressure inside the flask reached 100 mm of Hg. The pressure inside the flask was further reduced to 0.3 mm of Hg over the next 10 minutes. A pressure of 0.3 mm of Hg was maintained for a total time of 90 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 82.1° C. and an inherent viscosity of 0.64 dl/g. NMR analysis showed that the polymer was composed of 34.5 mol % ethylene glycol residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 40 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues, and 60 mol % 1,4-cyclohexanedimethanol residues (31/69 cis/trans).
A mixture of 77.4 g of dimethyl terephthalate, 36.9 g of 1,4-cyclohexanedimethanol, 32.5 g of 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 0.046 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 210° C. The stirring speed was set to 200 RPM throughout the experiment. The contents of the flask were heated at 210° C. for 3 minutes and then the temperature was gradually increased to 260° C. over 30 minutes. The reaction mixture was held at 260° C. for 120 minutes and then heated up to 290° C. in 30 minutes. Once at 290° C., vacuum was gradually applied over the next 5 minutes until the pressure inside the flask reached 100 mm of Hg. The pressure inside the flask was further reduced to 0.3 mm of Hg over the next 5 minutes. A pressure of 0.3 mm of Hg was maintained for a total time of 90 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 122° C. and an inherent viscosity of 0.65 dl/g. NMR analysis showed that the polymer was composed of 59.9 mol % 1,4-cyclohexanedimethanol residues and 40.1 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 20 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues (98/2 cis/trans), and 80 mol % 1,4-cyclohexanedimethanol residues (31/69 cis/trans).
A mixture of 77.68 g of dimethyl terephthalate, 48.46 g of 1,4-cyclohexanedimethanol, 20.77 g of 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 0.046 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 210° C. The stirring speed was set to 200 RPM throughout the experiment. The contents of the flask were heated at 210° C. for 3 minutes and then the temperature was gradually increased to 260° C. over 30 minutes. The reaction mixture was held at 260° C. for 120 minutes and then heated up to 290° C. in 30 minutes. Once at 290° C., vacuum was gradually applied over the next 5 minutes until the pressure inside the flask reached 100 mm of Hg and the stirring speed was also reduced to 100 RPM. The pressure inside the flask was further reduced to 0.3 mm of Hg over the next 5 minutes and the stirring speed was reduced to 50 RPM. A pressure of 0.3 mm of Hg was maintained for a total time of 60 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 103° C. and an inherent viscosity of 0.65 dl/g. NMR analysis showed that the polymer was composed of 85.7 mol % 1,4-cyclohexanedimethanol residues and 14.3 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
This example illustrates the preparation of a copolyester with a target composition of 100 mol % dimethyl terephthalate residues, 20 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues (5/95 cis/trans), and 80 mol % 1,4-cyclohexanedimethanol residues (31/69 cis/trans).
A mixture of 77.68 g of dimethyl terephthalate, 48.46 g of 1,4-cyclohexanedimethanol, 20.77 g of 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 0.046 g of dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 210° C. The stirring speed was set to 200 RPM at the beginning of the experiment. The contents of the flask were heated at 210° C. for 3 minutes and then the temperature was gradually increased to 260° C. over 30 minutes. The reaction mixture was held at 260° C. for 120 minutes and then heated up to 290° C. in 30 minutes. Once at 290° C., vacuum was gradually applied over the next 5 minutes with a set point of 100 mm of Hg and the stirring speed was also reduced to 100 RPM. The pressure inside the flask was further reduced to a set point of 0.3 mm of Hg over the next 5 minutes and the stirring speed was reduced to 50 RPM. This pressure was maintained for a total time of 60 minutes to remove excess unreacted diols. It was noted that the vacuum system failed to reach the set point mentioned above, but produced enough vacuum to produce a high melt viscosity, visually clear and colorless polymer with a glass transition temperature of 99° C. and an inherent viscosity of 0.73 dl/g. NMR analysis showed that the polymer was composed of 85 mol % 1,4-cyclohexanedimethanol residues and 15 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
This example illustrates that 2,2,4,4-tetramethyl-1,3-cyclobutanediol improves the toughness of PCT-based copolyesters (polyesters containing terephthalic acid and 1,4-cyclohexanedimethanol).
Copolyesters based on 2,2,4,4-tetramethyl-1,3-cyclobutanediol were prepared as described below. The cis/trans ratio of the 1,4-cyclohexanedimethanol was approximately 31/69 for all samples. Copolyesters based on ethylene glycol and 1,4-cyclohexanedimethanol were commercial polyesters. The copolyester of Example 2A (Eastar PCTG 5445) was obtained from Eastman Chemical Co. The copolyester of Example 2B was obtained from Eastman Chemical Co. under the trade name Spectar. Example 2C and Example 2D were prepared on a pilot plant scale (each a 15-lb batch) following an adaptation of the procedure described in Example 1A and having the inherent viscosities and glass transition temperatures described in Table 2 below. Example 2C was prepared with a target tin amount of 300 ppm (Dibutyltin Oxide). The final product contained 295 ppm tin. The color values for the polyester of Example 2C were L*=77.11; a*=−1.50; and b*=5.79. Example 2D was prepared with a target tin amount of 300 ppm (Dibutyltin Oxide). The final product contained 307 ppm tin. The color values for the polyester of Example 2D were V=66.72; a*=−1.22; and b*=16.28.
Materials were injection molded into bars and subsequently notched for Izod testing. The notched Izod impact strengths were obtained as a function of temperature and are also reported in Table 2.
For a given sample, the Izod impact strength undergoes a major transition in a short temperature span. For instance, the Izod impact strength of a copolyester based on 38 mol % ethylene glycol undergoes this transition between 15 and 20° C. This transition temperature is associated with a change in failure mode; brittle/low energy failures at lower temperatures and ductile/high energy failures at higher temperatures. The transition temperature is denoted as the brittle-to-ductile transition temperature, Tbd, and is a measure of toughness. Tbd is reported in Table 2 and plotted against mol % comonomer in
The data shows that adding 2,2,4,4-tetramethyl-1,3-cyclobutanediol to PCT lowers Tbd and improves the toughness, as compared to ethylene glycol, which increases Tbd of PCT.
1The balance of the glycol component of the polyesters in the Table is 1,4-cyclohexanedimethanol. All polymers were prepared from 100 mole % dimethyl terephthalate.
This example illustrates that 2,2,4,4-tetramethyl-1,3-cyclobutanediol can improve the toughness of PCT-based copolyesters (polyesters containing terephthalic acid and 1,4-cyclohexanedimethanol). Polyesters prepared in this example fall comprise more than 25 to less than 40 mol % of 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
Copolyesters based on dimethyl terephthalate, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 1,4-cyclohexanedimethanol (31/69 cis/trans) were prepared as described below, having the composition and properties shown on Table 3. The balance up to 100 mol % of the diol component of the polyesters in Table 3 was 1,4-cyclohexanedimethanol (31/69 cis/trans).
Materials were injection molded into both 3.2 mm and 6.4 mm thick bars and subsequently notched for Izod impact testing. The notched Izod impact strengths were obtained at 23° C. and are reported in Table 3. Density, Tg, and crystallization halftime were measured on the molded bars. Melt viscosity was measured on pellets at 290° C.
21.24 lb (49.71 gram-mol) dimethyl terephthalate, 11.82 lb (37.28 gram-mol) 1,4-cyclohexanedimethanol, and 6.90 lb (21.77 gram-mol) 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in the presence of 200 ppm of the catalyst butyltin tris(2-ethylhexanoate). The reaction was carried out under a nitrogen gas purge in an 18-gallon stainless steel pressure vessel fitted with a condensing column, a vacuum system, and a HELICONE-type agitator. With the agitator running at 25 RPM, the reaction mixture temperature was increased to 250° C. and the pressure was increased to 20 psig. The reaction mixture was held for 2 hours at 250° C. and 20 psig pressure. The pressure was then decreased to 0 psig at a rate of 3 psig/minute. The temperature of the reaction mixture was then increased to 270° C. and the pressure was decreased to 90 mm of Hg. After a 1 hour hold time at 270° C. and 90 mm of Hg, the agitator speed was decreased to 15 RPM, the reaction mixture temperature was increased to 290° C., and the pressure was decreased to <1 mm of Hg. The reaction mixture was held at 290° C. and at a pressure of <1 mm of Hg until the power draw to the agitator no longer increased (50 minutes). The pressure of the pressure vessel was then increased to 1 atmosphere using nitrogen gas. The molten polymer was then extruded from the pressure vessel. The cooled, extruded polymer was ground to pass a 6-mm screen. The polymer had an inherent viscosity of 0.714 dL/g and a Tg of 113° C. NMR analysis showed that the polymer was composed of 73.3 mol % 1,4-cyclohexane-dimethanol residues and 26.7 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
The polyester of Example 3B was prepared following a procedure similar to the one described for Example 3A. The composition and properties of this polyester are shown in Table 3.
This example illustrates that 2,2,4,4-tetramethyl-1,3-cyclobutanediol can improve the toughness of PCT-based copolyesters (polyesters containing terephthalic acid and 1,4-cyclohexanedimethanol). Polyesters prepared in this example comprise 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues in an amount of 40 mol % or greater.
Copolyesters based on dimethyl terephthalate, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 1,4-cyclohexanedimethanol were prepared as described below, having the composition and properties shown on Table 4. The balance up to 100 mol % of the diol component of the polyesters in Table 4 was 1,4-cyclohexanedimethanol (31/69 cis/trans).
Materials were injection molded into both 3.2 mm and 6.4 mm thick bars and subsequently notched for Izod impact testing. The notched Izod impact strengths were obtained at 23° C. and are reported in Table 4. Density, Tg, and crystallization halftime were measured on the molded bars. Melt viscosity was measured on pellets at 290° C.
21.24 lb (49.71 gram-mol) dimethyl terephthalate, 8.84 lb (27.88 gram-mol) 1,4-cyclohexanedimethanol, and 10.08 lb (31.77 gram-mol) 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in the presence of 200 ppm of the catalyst butyltin tris(2-ethylhexanoate). The reaction was carried out under a nitrogen gas purge in an 18-gallon stainless steel pressure vessel fitted with a condensing column, a vacuum system, and a HELICONE-type agitator. With the agitator running at 25 RPM, the reaction mixture temperature was increased to 250° C. and the pressure was increased to 20 psig. The reaction mixture was held for 2 hours at 250° C. and 20 psig pressure. The pressure was then decreased to 0 psig at a rate of 3 psig/minute. Then the agitator speed was decreased to 15 RPM, the temperature of the reaction mixture was then increased to 290° C. and the pressure was decreased to 2 mm of Hg. The reaction mixture was held at 290° C. and at a pressure of 2 mm of Hg until the power draw to the agitator no longer increased (80 minutes). The pressure of the pressure vessel was then increased to 1 atmosphere using nitrogen gas. The molten polymer was then extruded from the pressure vessel. The cooled, extruded polymer was ground to pass a 6-mm screen. The polymer had an inherent viscosity of 0.657 dL/g and a Tg of 119° C. NMR analysis showed that the polymer was composed of 56.3 mol % 1,4-cyclohexane-dimethanol residues and 43.7 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues. The polymer had color values of: V=75.04, a*=−1.82, and b*=6.72.
The polyesters described in Example 4B to Example 4D were prepared following a procedure similar to the one described for Example 4A. The composition and properties of these polyesters are shown in Table 4.
21.24 lb (49.71 gram-mol) dimethyl terephthalate, 6.43 lb (20.28 gram-mol 1,4-cyclohexanedimethanol, and 12.49 lb (39.37 gram-mol) 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in the presence of 200 ppm of the catalyst butyltin tris(2-ethylhexanoate). The reaction was carried out under a nitrogen gas purge in an 18-gallon stainless steel pressure vessel fitted with a condensing column, a vacuum system, and a HELICONE-type agitator. With the agitator running at 25 RPM, the reaction mixture temperature was increased to 250° C. and the pressure was increased to 20 psig. The reaction mixture was held for 2 hours at 250° C. and 20 psig pressure. The pressure was then decreased to 0 psig at a rate of 3 psig/minute. Then the agitator speed was decreased to 15 RPM, the temperature of the reaction mixture was then increased to 290° C. and the pressure was decreased to 2 mm of Hg. The reaction mixture was held at 290° C. and at a pressure of <1 mm of Hg until the power draw to the agitator no longer increased (50 minutes). The pressure of the pressure vessel was then increased to 1 atmosphere using nitrogen gas. The molten polymer was then extruded from the pressure vessel. The cooled, extruded polymer was ground to pass a 6-mm screen. The polymer had an inherent viscosity of 0.604 dL/g and a Tg of 139° C. NMR analysis showed that the polymer was composed of 40.8 mol % 1,4-cyclohexanedimethanol residues and 59.2 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues. The polymer had color values of: V=80.48, a*=−1.30, and b*=6.82.
21.24 lb (49.71 gram-mol) dimethyl terephthalate, 8.84 lb (27.88 gram-mol) 1,4-cyclohexanedimethanol, and 10.08 lb (31.77 gram-mol) 2,2,4,4-tetramethyl-1,3-cyclobutanediol were reacted together in the presence of 200 ppm of the catalyst butyltin tris(2-ethylhexanoate). The reaction was carried out under a nitrogen gas purge in an 18-gallon stainless steel pressure vessel fitted with a condensing column, a vacuum system, and a HELICONE-type agitator. With the agitator running at 25 RPM, the reaction mixture temperature was increased to 250° C. and the pressure was increased to 20 psig. The reaction mixture was held for 2 hours at 250° C. and 20 psig pressure. The pressure was then decreased to 0 psig at a rate of 3 psig/minute. The temperature of the reaction mixture was then increased to 270° C. and the pressure was decreased to 90 mm of Hg. After a 1 hour hold time at 270° C. and 90 mm of Hg, the agitator speed was decreased to 15 RPM and the pressure was decreased to 4 mm of Hg. When the reaction mixture temperature was 270° C. and the pressure was 4 mm of Hg, the pressure of the pressure vessel was immediately increased to 1 atmosphere using nitrogen gas. The molten polymer was then extruded from the pressure vessel. The cooled, extruded polymer was ground to pass a 6-mm screen. The polymer had an inherent viscosity of 0.475 dL/g and a Tg of 121° C. NMR analysis showed that the polymer was composed of 55.5 mol % 1,4-cyclohexane-dimethanol residues and 44.5 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues. The polymer had color values of: V=85.63, a*=−0.88, and b*=4.34.
This example shows data for comparative materials are shown in Table 5. The PC was Makrolon 2608 from Bayer, with a nominal composition of 100 mole % bisphenol A residues and 100 mole % diphenyl carbonate residues. Makrolon 2608 has a nominal melt flow rate of 20 grams/10 minutes measured at 300 C using a 1.2 kg weight. The PET was Eastar 9921 from Eastman Chemical Company, with a nominal composition of 100 mole % terephthalic acid, 3.5 mole % cyclohexanedimenthanol (CHDM) and 96.5 mole % ethylene glycol. The PETG was Eastar 6763 from Eastman Chemical Company, with a nominal composition of 100 mole % terephthalic acid, 31 mole % cyclohexanedimenthanol (CHDM) and 69 mole % ethylene glycol. The PCTG was Eastar DN001 from Eastman Chemical Company, with a nominal composition of 100 mole % terephthalic acid, 62 mole % cyclohexanedimenthanol (CHDM) and 38 mole % ethylene glycol. The PCTA was Eastar AN001 from Eastman Chemical Company, with a nominal composition of 65 mole % terephthalic acid, 35 mole % isophthalic acid and 100 mole % cyclohexanedimenthanol (CHDM). The Polysulfone was Udel 1700 from Solvay, with a nominal composition of 100 mole % bisphenol A residues and 100 mole % 4,4-dichlorosulfonyl sulfone residues. Udel 1700 has a nominal melt flow rate of 6.5 grams/10 minutes measured at 343 C using a 2.16 kg weight. The SAN was Lustran 31 from Lanxess, with a nominal composition of 76 weight % styrene and 24 weight % acrylonitrile. Lustran 31 has a nominal melt flow rate of 7.5 grams/10 minutes measured at 230 C using a 3.8 kg weight. The examples of the invention show improved toughness in 6.4 mm thickness bars compared to all of the other resins.
This example illustrates the effect of the amount of 2,2,4,4-tetramethyl-1,3-cyclobutanediol used for the preparation of the polyesters of the invention on the glass transition temperature of the polyesters.
The polyester of this example was prepared by carrying out the ester exchange and polycondensation reactions in separate stages. The ester exchange experiments were conducted in a continuous temperature rise (CTR) reactor. The CTR was a 3000 ml glass reactor equipped with a single shaft impeller blade agitator, covered with an electric heating mantle and fitted with a heated packed reflux condenser column. The reactor was charged with 777 g (4 moles) of dimethyl terephthalate, 230 g (1.6 moles) of 2,2,4,4-tetramethyl-1,3,-cyclobutanediol, 460.8 g (3.2 moles) of cyclohexane dimethanol and 1.12 g of butyltin tris-2-ethylhexanoate (such that there will be 200 ppm tin metal in the final polymer). The heating mantle was set manually to 100% output. The set points and data collection were facilitated by a Camile process control system. Once the reactants were melted, stirring was initiated and slowly increased to 250 rpm. The temperature of the reactor gradually increased with run time. The weight of methanol collected was recorded via balance. The reaction was stopped when methanol evolution stopped or at a pre-selected lower temperature of 260° C. The oligomer was discharged with a nitrogen purge and cooled to room temperature. The oligomer was frozen with liquid nitrogen and broken into pieces small enough to be weighed into a 500 ml round bottom flask.
In the polycondensation reaction, a 500 ml round bottom flask was charged with approximately 150 g of the oligomer prepared above. The flask was equipped with a stainless steel stirrer and polymer head. The glassware was set up on a half mole polymer rig and the Camile sequence was initiated. The stirrer was positioned one full turn from the flask bottom once the oligomer melted. The temperature/pressure/stir rate sequence controlled by the Camile software for this example is reported in the following table.
The resulting polymer was recovered from the flask, chopped using a hydraulic chopper, and ground to a 6 mm screen size. Samples of each ground polymer were submitted for inherent viscosity in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C., catalyst level (Sn) by x-ray fluorescence, and color (L*, a*, b*) by transmission spectroscopy. Polymer composition was obtained by 1H NMR. Samples were submitted for thermal stability and melt viscosity testing using a Rheometrics Mechanical Spectrometer (RMS-800).
The table below shows the experimental data for the polyester of this example.
This example illustrates the effect of the amount of 2,2,4,4-tetramethyl-1,3-cyclobutanediol used for the preparation of the polyesters of the invention on the glass transition temperature of the polyesters. Polyesters prepared in this example fall comprise more than 25 to less than 40 mol % of 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
Dimethyl terephthalate, 1,4-cyclohexanedimethanol, and 2,2,4,4-tetramethyl-1,3-cyclobutanediol were weighed into a 500-ml single neck round bottom flask. NMR analysis on the 2,2,4,4-tetramethyl-1,3-cyclobutanediol starting material showed a cis/trans ratio of 53/47. The polyesters of this example were prepared with a 1.2/1 glycol/acid ratio with the entire excess coming from the 2,2,4,4-tetramethyl-1,3-cyclobutanediol. Enough dibutyltin oxide catalyst was added to give 300 ppm tin in the final polymer. The flask was under a 0.2 SCFC nitrogen purge with vacuum reduction capability. The flask was immersed in a Belmont metal bath at 200° C. and stirred at 200 RPM after the reactants had melted. After about 2.5 hours, the temperature was raised to 210° C. and these conditions were held for an additional 2 hours. The temperature was raised to 285° C. (in approximately 25 minutes) and the pressure was reduced to 0.3 mm of Hg over a period of 5 minutes. The stirring was reduced as the viscosity increased, with 15 RPM being the minimum stirring used. The total polymerization time was varied to attain the target inherent viscosities. After the polymerization was complete, the Belmont metal bath was lowered and the polymer was allowed to cool to below its glass transition temperature. After about 30 minutes, the flask was reimmersed in the Belmont metal bath (the temperature had been increased to 295° C. during this 30 minute wait) and the polymer mass was heated until it pulled away from the glass flask. The polymer mass was stirred at mid level in the flask until the polymer had cooled. The polymer was removed from the flask and ground to pass a 3 mm screen. Variations to this procedure were made to produce the copolyesters described below with a targeted composition of 32 mol %.
Inherent viscosities were measured as described in the “Measurement Methods” section above. The compositions of the polyesters were determined by 1H NMR as explained before in the Measurement Methods section. The glass transition temperatures were determined by DSC, using the second heat after quench at a rate of 20° C./min.
The table below shows the experimental data for the polyesters of this example.
This example illustrates the effect of the amount of 2,2,4,4-tetramethyl-1,3-cyclobutanediol used for the preparation of the polyesters of the invention on the glass transition temperature of the polyesters. Polyesters prepared in this example comprise 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues in an amount of 40 mol % or greater.
These polyesters were prepared by carrying out the ester exchange and polycondensation reactions in separate stages. The ester exchange experiments were conducted in a continuous temperature rise (CTR) reactor. The CTR was a 3000 ml glass reactor equipped with a single shaft impeller blade agitator, covered with an electric heating mantle and fitted with a heated packed reflux condenser column. The reactor was charged with 777 g of dimethyl terephthalate, 375 g of 2,2,4,4-tetramethyl-1,3,-cyclobutanediol, 317 g of cyclohexane dimethanol and 1.12 g of butyltin tris-2-ethylhexanoate (such that there will be 200 ppm tin metal in the final polymer). The heating mantle was set manually to 100% output. The set points and data collection were facilitated by a Camile process control system. Once the reactants were melted, stirring was initiated and slowly increased to 250 rpm. The temperature of the reactor gradually increased with run time. The weight of methanol collected was recorded via balance. The reaction was stopped when methanol evolution stopped or at a pre-selected lower temperature of 260° C. The oligomer was discharged with a nitrogen purge and cooled to room temperature. The oligomer was frozen with liquid nitrogen and broken into pieces small enough to be weighed into a 500 ml round bottom flask.
In the polycondensation reactions, a 500 ml round bottom flask was charged with 150 g of the oligomer prepared above. The flask was equipped with a stainless steel stirrer and polymer head. The glassware was set up on a half mole polymer rig and the Camile sequence was initiated. The stirrer was positioned one full turn from the flask bottom once the oligomer melted. The temperature/pressure/stir rate sequence controlled by the Camile software for these examples is reported in the following table, unless otherwise specified below.
For Examples B, D, F, the same sequence in the preceding table was used, except the time was 80 min in Stage 7. For Examples G and J, the same sequence in the preceding table was used, except the time was 50 min in Stage 7. For Example L, the same sequence in the preceding table was used, except the time was 140 min in Stage 7.
For Example I, the same sequence in the preceding table was used, except the vacuum was 8 torr in Stages 6 and 7. For Example O, the same sequence in the preceding table was used, except the vacuum was 6 torr in Stages 6 and 7. For Example P, the same sequence in the preceding table was used, except the vacuum was 4 torr in Stages 6 and 7. For Example Q, the same sequence in the preceding table was used, except the vacuum was 5 torr in Stages 6 and 7.
For Example U and AA, the same sequence in the preceding table was used, except the vacuum was 6 torr in Stages 6 and 7. For Example V and X, the same sequence in the preceding table was used, except the vacuum was 6 torr and stir rate was 15 rpm in Stages 6 and 7. For Example Z, the same sequence in the preceding table was used, except the stir rate was 15 rpm in Stages 6 and 7.
For Example M, the same sequence in the preceding table was used, except the vacuum was 8 torr in Stages 6 and 7. For Example N, the same sequence in the preceding table was used, except the vacuum was 7 torr in Stages 6 and 7.
The resulting polymers were recovered from the flask, chopped using a hydraulic chopper, and ground to a 6 mm screen size. Samples of each ground polymer were submitted for inherent viscosity in 60/40 (wt/wt) phenol/tetrachloroethane at a concentration of 0.5 g/100 ml at 25° C., catalyst level (Sn) by x-ray fluorescence, and color (L*, a*, b*) by transmission spectroscopy. Polymer composition was obtained by 1H NMR. Samples were submitted for thermal stability and melt viscosity testing using a Rheometrics Mechanical Spectrometer (RMS-800).
The polyesters of these examples were prepared as described above for Examples A to AC, except that the target tin amount in the final polymer was 150 ppm for examples AD to AK and AS. The following tables describe the temperature/pressure/stir rate sequences controlled by the Camile software for these examples.
For Example AD, the stirrer was turned to 25 rpm with 95 min left in Stage 7.
For Example AK, the same sequence in the preceding table was used, except the time was 75 min in Stage 7.
Dimethyl terephthalate, 1,4-cyclohexanedimethanol, and 2,2,4,4-tetramethyl-1,3-cyclobutanediol were weighed into a 500-ml single neck round bottom flask. The polyesters of this example were prepared with a 1.2/1 glycol/acid ratio with the entire excess coming from the 2,2,4,4-tetramethyl-1,3-cyclobutanediol. Enough dibutyltin oxide catalyst was added to give 300 ppm tin in the final polymer. The flask was under a 0.2 SCFC nitrogen purge with vacuum reduction capability. The flask was immersed in a Belmont metal bath at 200° C. and stirred at 200 RPM after the reactants had melted. After about 2.5 hours, the temperature was raised to 210° C. and these conditions were held for an additional 2 hours. The temperature was raised to 285° C. (in approximately 25 minutes) and the pressure was reduced to 0.3 mm of Hg over a period of 5 minutes. The stirring was reduced as the viscosity increased, with 15 RPM being the minimum stirring used. The total polymerization time was varied to attain the target inherent viscosities. After the polymerization was complete, the Belmont metal bath was lowered and the polymer was allowed to cool to below its glass transition temperature. After about 30 minutes, the flask was reimmersed in the Belmont metal bath (the temperature had been increased to 295° C. during this 30 minute wait) and the polymer mass was heated until it pulled away from the glass flask. The polymer mass was stirred at mid level in the flask until the polymer had cooled. The polymer was removed from the flask and ground to pass a 3 mm screen. Variations to this procedure were made to produce the copolyesters described below with a targeted composition of 45 mol %.
Inherent viscosities were measured as described in the “Measurement Methods” section above. The compositions of the polyesters were determined by 1H NMR as explained before in the Measurement Methods section. The glass transition temperatures were determined by DSC, using the second heat after quench at a rate of 20° C./min.
The table below shows the experimental data for the polyesters of this example. The data shows that an increase in the level of 2,2,4,4-tetramethyl-1,3-cyclobutanediol raises the glass transition temperature in an almost linear fashion, for a constant inherent viscosity.
This example illustrates the effect of the predominance of the type of 2,2,4,4-tetramethyl-1,3-cyclobutanediol isomer (cis or trans) on the glass transition temperature of the polyester.
Dimethyl terephthalate, 1,4-cyclohexanedimethanol, and 2,2,4,4-tetramethyl-1,3-cyclobutanediol were weighed into a 500-ml single neck round bottom flask. The polyesters of this example were prepared with a 1.2/1 glycol/acid ratio with the entire excess coming from the 2,2,4,4-tetramethyl-1,3-cyclobutanediol. Enough dibutyltin oxide catalyst was added to give 300 ppm tin in the final polymer. The flask was under a 0.2 SCFC nitrogen purge with vacuum reduction capability. The flask was immersed in a Belmont metal bath at 200° C. and stirred at 200 RPM after the reactants had melted. After about 2.5 hours, the temperature was raised to 210° C. and these conditions were held for an additional 2 hours. The temperature was raised to 285° C. (in approximately 25 minutes) and the pressure was reduced to 0.3 mm of Hg over a period of 5 minutes. The stirring was reduced as the viscosity increased, with 15 RPM being the minimum stirring used. The total polymerization time was varied to attain the target inherent viscosities. After the polymerization was complete, the Belmont metal bath was lowered and the polymer was allowed to cool to below its glass transition temperature. After about 30 minutes, the flask was reimmersed in the Belmont metal bath (the temperature had been increased to 295° C. during this 30 minute wait) and the polymer mass was heated until it pulled away from the glass flask. The polymer mass was stirred at mid level in the flask until the polymer had cooled. The polymer was removed from the flask and ground to pass a 3 mm screen. Variations to this procedure were made to produce the copolyesters described below with a targeted composition of 45 mol %.
Inherent viscosities were measured as described in the “Measurement Methods” section above. The compositions of the polyesters were determined by 1H NMR as explained before in the Measurement Methods section. The glass transition temperatures were determined by DSC, using the second heat after quench at a rate of 20° C./min.
The table below shows the experimental data for the polyesters of this Example. The data shows that cis 2,2,4,4-tetramethyl-1,3-cyclobutanediol is approximately twice as effective as trans 2,2,4,4-tetramethyl-1,3-cyclobutanediol at increasing the glass transition temperature for a constant inherent viscosity.
This example illustrates the preparation of a copolyester containing 100 mol % dimethyl terephthalate residues, 55 mol % 1,4-cyclohexanedimethanol residues, and 45 mol % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues.
A mixture of 97.10 g (0.5 mol) dimethyl terephthalate, 52.46 g (0.36 mol) 1,4-cyclohexanedimethanol, 34.07 g (0.24 mol) 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 0.0863 g (300 ppm) dibutyl tin oxide was placed in a 500-milliliter flask equipped with an inlet for nitrogen, a metal stirrer, and a short distillation column. The flask was placed in a Wood's metal bath already heated to 200° C. The contents of the flask were heated at 200° C. for 1 hour and then the temperature was increased to 210° C. The reaction mixture was held at 210° C. for 2 hours and then heated up to 290° C. in 30 minutes. Once at 290° C., a vacuum of 0.01 psig was gradually applied over the next 3 to 5 minutes. Full vacuum (0.01 psig) was maintained for a total time of about 45 minutes to remove excess unreacted diols. A high melt viscosity, visually clear and colorless polymer was obtained with a glass transition temperature of 125° C. and an inherent viscosity of 0.64 dl/g.
This example illustrates that a polyester based on 100% 2,2,4,4-tetramethyl-1,3-cyclobutanediol has a slow crystallization half-time.
A polyester based solely on terephthalic acid and 2,2,4,4-tetramethyl-1,3-cyclobutanediol was prepared in a method similar to the method described in Example 1A with the properties shown on Table 10. This polyester was made with 300 ppm dibutyl tin oxide. The trans/cis ratio of the 2,2,4,4-tetramethyl-1,3-cyclobutanediol was 65/35.
Films were pressed from the ground polymer at 320° C. Crystallization half-time measurements from the melt were made at temperatures from 220 to 250° C. at 10° C. increments and are reported in Table 10. The fastest crystallization half-time for the sample was taken as the minimum value of crystallization half-time as a function of temperature. The fastest crystallization half-time of this polyester is around 1300 minutes. This value contrasts with the fact that the polyester (PCT) based solely on terephthalic acid and 1,4-cyclohexanedimethanol (no comonomer modification) has an extremely short crystallization half-time (<1 min) as shown in
Sheets comprising a polyester that had been prepared with a target composition of 100 mole % terephthalic acid residues, 80 mole 1,4-cyclohexanedimethanol residues, and 20 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues were produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 177 mil and then various sheets were sheared to size. Inherent viscosity and glass transition temperature were measured on one sheet. The sheet inherent viscosity was measured to be 0.69 dl/g. The glass transition temperature of the sheet was measured to be 106° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 2 weeks. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example G). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 106° C. can be thermoformed under the conditions shown below, as evidenced by these sheets having at least 95% draw and no blistering, without predrying the sheets prior to thermoforming.
Sheets comprising a polyester that had been prepared with a target composition of 100 mole % terephthalic acid residues, 80 mole 1,4-cyclohexanedimethanol residues, and 20 mole % 2,2,4,4-tetramethyl-1,3-cyclobutanediol residues were produced using a 3.5 inch single screw. A sheet was extruded continuously, gauged to a thickness of 177 mil and then various sheets were sheared to size. Inherent viscosity and glass transition temperature were measured on one sheet. The sheet inherent viscosity was measured to be 0.69 dl/g. The glass transition temperature of the sheet was measured to be 106° C. Sheets were then conditioned at 100% relative humidity and 25° C. for 2 weeks. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 60/40/40% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example G). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 106° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having at least 95% draw and no blistering, without predrying the sheets prior to thermoforming.
Sheets consisting of Kelvx 201 were produced using a 3.5 inch single screw extruder. Kelvx is a blend consisting of 69.85% PCTG (Eastar from Eastman Chemical Co. having 100 mole % terephthalic acid residues, 62 mole % 1,4-cyclohexanedimethanol residues, and 38 mole % ethylene glycol residues); 30% PC (bisphenol A polycarbonate); and 0.15% Weston 619 (stabilizer sold by Crompton Corporation). A sheet was extruded continuously, gauged to a thickness of 177 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 100° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 2 weeks. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example E). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 100° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having at least 95% draw and no blistering, without predrying the sheets prior to thermoforming.
Sheets consisting of Kelvx 201 were produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 177 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 100° C. Sheets were then conditioned at 100% relative humidity and 25° C. for 2 weeks. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 60/40/40% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example H). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 100° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
Sheets consisting of PCTG 25976 (100 mole % terephthalic acid residues, 62 mole % 1,4-cyclohexanedimethanol residues, and 38 mole % ethylene glycol residues) were produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 87° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.17 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example A). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 87° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 20 wt % Teijin L-1250 polycarbonate (a bisphenol-A polycarbonate), 79.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. Sheets consisting of the blend were then produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 94° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.25 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example A). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 94° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 30 wt % Teijin L-1250 polycarbonate, 69.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. Sheets consisting of the blend were then produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 99° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.25 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example A). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 99° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 40 wt % Teijin L-1250 polycarbonate, 59.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. Sheets consisting of the blend were then produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 105° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.265 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Examples 8A to 8E). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 105° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 50 wt % Teijin L-1250 polycarbonate, 49.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 111° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.225 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Examples A to D). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 111° C. can be thermoformed under the conditions shown below, as evidenced by the production of sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 60 wt % Teijin L-1250 polycarbonate, 39.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. Sheets consisting of the blend were then produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 117° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.215 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example A). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 117° C. cannot be thermoformed under the conditions shown below, as evidenced by the inability to produce sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 65 wt % Teijin L-1250 polycarbonate, 34.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. Sheets consisting of the blend were then produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 120° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.23 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example A). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 120° C. cannot be thermoformed under the conditions shown below, as evidenced by the inability to produce sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
A miscible blend consisting of 70 wt % Teijin L-1250 polycarbonate, 29.85 wt % PCTG 25976, and 0.15 wt % Weston 619 was produced using a 1.25 inch single screw extruder. Sheets consisting of the blend were then produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 123° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.205 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw, and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Examples A and B). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 123° C. cannot be thermoformed under the conditions shown below, as evidenced by the inability to produce sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
Sheets consisting of Teijin L-1250 polycarbonate were produced using a 3.5 inch single screw extruder. A sheet was extruded continuously, gauged to a thickness of 118 mil and then various sheets were sheared to size. The glass transition temperature was measured on one sheet and was 149° C. Sheets were then conditioned at 50% relative humidity and 60° C. for 4 weeks. The moisture level was measured to be 0.16 wt %. Sheets were subsequently thermoformed into a female mold having a draw ratio of 2.5:1 using a Brown thermoforming machine. The thermoforming oven heaters were set to 70/60/60% output using top heat only. Sheets were left in the oven for various amounts of time in order to determine the effect of sheet temperature on the part quality as shown in the table below. Part quality was determined by measuring the volume of the thermoformed part, calculating the draw and visually inspecting the thermoformed part. The draw was calculated as the part volume divided by the maximum part volume achieved in this set of experiments (Example A). The thermoformed part was visually inspected for any blisters and the degree of blistering rated as none (N), low (L), or high (H). The results below demonstrate that these thermoplastic sheets with a glass transition temperature of 149° C. cannot be thermoformed under the conditions shown below, as evidenced by the inability to produce sheets having greater than 95% draw and no blistering, without predrying the sheets prior to thermoforming.
It can be clearly seen from a comparison of the data in the above relevant working examples that the polyesters of the present invention offer a definite advantage over the commercially available polyesters with regard to glass transition temperature, density, slow crystallization rate, melt viscosity, and toughness.
The invention has been described in detail with reference to the embodiments disclosed herein, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.
The invention has been described in detail with reference to embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.
This application is a continuation of U.S. Ser. No. 13/776,038 filed on Feb. 25, 2013. U.S. Ser. No. 13/776,038 filed on Feb. 25, 2013 is a division of U.S. Ser. No. 13/348,677 filed on Jan. 12, 2012, now U.S. Pat. No. 8,415,450. U.S. Ser. No. 13/348,677 filed on Jan. 12, 2012, now U.S. Pat. No. 8,415,450 is a continuation application of U.S. Ser. No. 11/390,794 filed on Mar. 28, 2006, now U.S. Pat. No. 8,119,761; which application claims the benefit under 35 U.S.C. §119(e) to U.S. Provisional Application Ser. No. 60/691,567 filed on Jun. 17, 2005; U.S. Provisional Application Ser. No. 60/731,454 filed on Oct. 28, 2005; U.S. Provisional Application Ser. No. 60/731,389, filed on Oct. 28, 2005; U.S. Provisional Application Ser. No. 60/739,058, filed on Nov. 22, 2005; U.S. Provisional Application Ser. No. 60/738,869, filed on Nov. 22, 2005; U.S. Provisional Application Ser. No. 60/750,692 filed on Dec. 15, 2005; U.S. Provisional Application Ser. No. 60/750,693, filed on Dec. 15, 2005; U.S. Provisional Application Ser. No. 60/750,682, filed on Dec. 15, 2005; and U.S. Provisional Application Ser. No. 60/750,547, filed on Dec. 15, 2005, all of which are hereby incorporated by this reference in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1602699 | Nightingale | Oct 1926 | A |
| 2160841 | Dreyfus | Jun 1939 | A |
| 2202046 | Dreyfus et al. | May 1940 | A |
| 2278537 | Dreyfus et al. | Apr 1942 | A |
| 2720507 | Caldwell | Oct 1955 | A |
| 2806064 | McKlveen | Sep 1957 | A |
| 2901466 | Kibler | Aug 1959 | A |
| 2936324 | Hasek et al. | May 1960 | A |
| 3000906 | Hasek et al. | Sep 1961 | A |
| 3030335 | Goldberg | Apr 1962 | A |
| 3062852 | Martin et al. | Nov 1962 | A |
| 3075952 | Coover et al. | Jan 1963 | A |
| 3091600 | Caldwell et al. | May 1963 | A |
| 3169121 | Goldberg et al. | Feb 1965 | A |
| 3190928 | Elam et al. | Jun 1965 | A |
| 3201474 | Hasek et al. | Aug 1965 | A |
| 3207814 | Goldberg et al. | Sep 1965 | A |
| 3218372 | Okamura et al. | Nov 1965 | A |
| 3227764 | Martin et al. | Jan 1966 | A |
| 3236899 | Clark | Feb 1966 | A |
| 3249652 | Quisenberry | May 1966 | A |
| 3259469 | Painter et al. | Jul 1966 | A |
| 3287390 | Poos et al. | Nov 1966 | A |
| 3288854 | Martin | Nov 1966 | A |
| 3312741 | Martin | Apr 1967 | A |
| 3313777 | Elam et al. | Apr 1967 | A |
| 3317466 | Caldwell et al. | May 1967 | A |
| 3329722 | Rylander | Jul 1967 | A |
| 3360547 | Wilson et al. | Dec 1967 | A |
| 3366689 | Maeda et al. | Jan 1968 | A |
| 3386935 | Jackson et al. | Jun 1968 | A |
| 3403181 | Painter et al. | Sep 1968 | A |
| T858012 | Caldwell et al. | Jan 1969 | I4 |
| 3484339 | Caldwell | Dec 1969 | A |
| 3502620 | Caldwell | Mar 1970 | A |
| T873016 | Gilkey et al. | Apr 1970 | I4 |
| 3541059 | Schaper | Nov 1970 | A |
| 3546177 | Kibler et al. | Dec 1970 | A |
| 3629202 | Gilkey et al. | Dec 1971 | A |
| RE27682 | Schell et al. | Jun 1973 | E |
| 3772405 | Hamb | Nov 1973 | A |
| 3799953 | Freitag et al. | Mar 1974 | A |
| 3907754 | Tershansy et al. | Sep 1975 | A |
| 3915913 | Jackson, Jr. et al. | Oct 1975 | A |
| 3962189 | Russin et al. | Jun 1976 | A |
| 4001184 | Scott | Jan 1977 | A |
| 4010145 | Russin et al. | Mar 1977 | A |
| 4046933 | Stefanik | Sep 1977 | A |
| 4056504 | Grundmeier et al. | Nov 1977 | A |
| 4084889 | Vischer, Jr. | Apr 1978 | A |
| 4125572 | Scott | Nov 1978 | A |
| 4156069 | Prevorsek et al. | May 1979 | A |
| 4160383 | Rauschenberger | Jul 1979 | A |
| 4185009 | Idel et al. | Jan 1980 | A |
| 4188314 | Fox et al. | Feb 1980 | A |
| 4194038 | Baker et al. | Mar 1980 | A |
| 4263364 | Seymour et al. | Apr 1981 | A |
| 4264751 | Scheibelhoffer | Apr 1981 | A |
| 4356299 | Cholod et al. | Oct 1982 | A |
| 4367186 | Adelmann et al. | Jan 1983 | A |
| 4384106 | Go et al. | May 1983 | A |
| 4391954 | Scott | Jul 1983 | A |
| 4424140 | Weinberg et al. | Jan 1984 | A |
| 4426512 | Barbee et al. | Jan 1984 | A |
| 4427614 | Barham et al. | Jan 1984 | A |
| 4430484 | Quinn | Feb 1984 | A |
| 4431793 | Rosenquist | Feb 1984 | A |
| 4452933 | McCready | Jun 1984 | A |
| 4465820 | Miller et al. | Aug 1984 | A |
| 4469861 | Mark et al. | Sep 1984 | A |
| 4480086 | O'Neill | Oct 1984 | A |
| 4525504 | Morris et al. | Jun 1985 | A |
| 4578295 | Jabarin | Mar 1986 | A |
| 4578437 | Light et al. | Mar 1986 | A |
| 4642959 | Swiech, Jr. et al. | Feb 1987 | A |
| 4738880 | Asada et al. | Apr 1988 | A |
| 4749773 | Weaver et al. | Jun 1988 | A |
| 4786692 | Allen et al. | Nov 1988 | A |
| 4816308 | Shimizu et al. | Mar 1989 | A |
| 4826903 | Weaver et al. | May 1989 | A |
| 4845188 | Weaver et al. | Jul 1989 | A |
| 4880592 | Martini et al. | Nov 1989 | A |
| 4882412 | Weaver et al. | Nov 1989 | A |
| 4892922 | Weaver et al. | Jan 1990 | A |
| 4892923 | Weaver et al. | Jan 1990 | A |
| 4937134 | Schrenk et al. | Jun 1990 | A |
| 4939186 | Nelson et al. | Jul 1990 | A |
| 4976057 | Bianchi | Dec 1990 | A |
| 4981898 | Bassett | Jan 1991 | A |
| 4985342 | Muramoto et al. | Jan 1991 | A |
| 5017679 | Chang et al. | May 1991 | A |
| 5017680 | Sublett | May 1991 | A |
| 5034252 | Nilsson et al. | Jul 1991 | A |
| 5104450 | Sand et al. | Apr 1992 | A |
| 5118760 | Blakely et al. | Jun 1992 | A |
| 5118847 | Jackson et al. | Jun 1992 | A |
| 5142088 | Phelps et al. | Aug 1992 | A |
| 5169994 | Sumner, Jr. et al. | Dec 1992 | A |
| 5183863 | Nakamura et al. | Feb 1993 | A |
| 5191038 | Krabbenhoft et al. | Mar 1993 | A |
| 5207967 | Small et al. | May 1993 | A |
| 5219510 | Machell et al. | Jun 1993 | A |
| 5224958 | Warunek et al. | Jul 1993 | A |
| 5239020 | Morris | Aug 1993 | A |
| 5256761 | Blount, Jr. | Oct 1993 | A |
| 5258556 | Sumner, Jr. et al. | Nov 1993 | A |
| 5268219 | Harada et al. | Dec 1993 | A |
| 5288715 | Machell et al. | Feb 1994 | A |
| 5288764 | Rotter et al. | Feb 1994 | A |
| 5292783 | Buchanan et al. | Mar 1994 | A |
| 5310611 | Okabe et al. | May 1994 | A |
| 5310787 | Kutsuwa et al. | May 1994 | A |
| 5326584 | Kamel et al. | Jul 1994 | A |
| 5331034 | Pfahler et al. | Jul 1994 | A |
| 5333073 | Suzuki | Jul 1994 | A |
| 5354791 | Gallucci | Oct 1994 | A |
| 5372864 | Weaver et al. | Dec 1994 | A |
| 5372879 | Handa et al. | Dec 1994 | A |
| 5378796 | George et al. | Jan 1995 | A |
| 5382292 | Conroy et al. | Jan 1995 | A |
| 5384377 | Weaver et al. | Jan 1995 | A |
| 5475144 | Watson et al. | Dec 1995 | A |
| 5480926 | Fagerburg et al. | Jan 1996 | A |
| 5486562 | Borman et al. | Jan 1996 | A |
| 5489665 | Yamato et al. | Feb 1996 | A |
| 5494992 | Kanno et al. | Feb 1996 | A |
| 5498668 | Scott | Mar 1996 | A |
| 5498688 | Oshino et al. | Mar 1996 | A |
| 5506014 | Minnick | Apr 1996 | A |
| 5523382 | Beavers et al. | Jun 1996 | A |
| 5534609 | Lewis et al. | Jul 1996 | A |
| 5552512 | Sublett | Sep 1996 | A |
| 5591530 | Warner et al. | Jan 1997 | A |
| 5633340 | Hoffman et al. | May 1997 | A |
| 5650453 | Eckberg et al. | Jul 1997 | A |
| 5654347 | Khemani et al. | Aug 1997 | A |
| 5656715 | Dickerson et al. | Aug 1997 | A |
| 5668243 | Yau et al. | Sep 1997 | A |
| 5681918 | Adams et al. | Oct 1997 | A |
| 5688874 | Hoffman | Nov 1997 | A |
| 5696176 | Khemani et al. | Dec 1997 | A |
| 5705575 | Kelsey | Jan 1998 | A |
| 5783307 | Fagerburg et al. | Jul 1998 | A |
| 5804617 | Hoffman et al. | Sep 1998 | A |
| 5814679 | Eckberg et al. | Sep 1998 | A |
| 5859116 | Shih | Jan 1999 | A |
| 5863622 | Jester | Jan 1999 | A |
| 5902631 | Wang et al. | May 1999 | A |
| 5907026 | Factor et al. | May 1999 | A |
| 5942585 | Scott et al. | Aug 1999 | A |
| 5955565 | Morris et al. | Sep 1999 | A |
| 5958539 | Eckart et al. | Sep 1999 | A |
| 5958581 | Khanarian et al. | Sep 1999 | A |
| 5959066 | Charbonneau et al. | Sep 1999 | A |
| 5962625 | Yau | Oct 1999 | A |
| 5977347 | Shuto et al. | Nov 1999 | A |
| 5989663 | Morris et al. | Nov 1999 | A |
| 6001910 | Blumenthal et al. | Dec 1999 | A |
| 6005059 | Scott et al. | Dec 1999 | A |
| 6011124 | Scott et al. | Jan 2000 | A |
| 6012597 | Nishihara et al. | Jan 2000 | A |
| 6022603 | Umeda et al. | Feb 2000 | A |
| 6025061 | Khanarian et al. | Feb 2000 | A |
| 6030671 | Yang et al. | Feb 2000 | A |
| 6037424 | Scott et al. | Mar 2000 | A |
| 6043322 | Scott et al. | Mar 2000 | A |
| 6044996 | Carew et al. | Apr 2000 | A |
| 6063464 | Charbonneau et al. | May 2000 | A |
| 6063465 | Charbonneau et al. | May 2000 | A |
| 6063495 | Charbonneau et al. | May 2000 | A |
| 6084019 | Matayabas et al. | Jul 2000 | A |
| 6096854 | Morris et al. | Aug 2000 | A |
| 6114575 | McMahon et al. | Sep 2000 | A |
| 6120477 | Campbell et al. | Sep 2000 | A |
| 6120889 | Turner et al. | Sep 2000 | A |
| 6126992 | Khanarian et al. | Oct 2000 | A |
| 6127492 | Nagashima et al. | Oct 2000 | A |
| 6146228 | Mougin et al. | Nov 2000 | A |
| 6150494 | Wang et al. | Nov 2000 | A |
| 6183848 | Turner et al. | Feb 2001 | B1 |
| 6191209 | Andrews et al. | Feb 2001 | B1 |
| 6211309 | McIntosh et al. | Apr 2001 | B1 |
| 6221556 | Gallucci et al. | Apr 2001 | B1 |
| 6225436 | Eiffler et al. | May 2001 | B1 |
| 6232504 | Barteau et al. | May 2001 | B1 |
| 6239210 | Kim et al. | May 2001 | B1 |
| 6255523 | Panandiker et al. | Jul 2001 | B1 |
| 6287656 | Turner et al. | Sep 2001 | B1 |
| 6307006 | Konig et al. | Oct 2001 | B1 |
| 6309718 | Sprayberry | Oct 2001 | B1 |
| 6320042 | Michihata et al. | Nov 2001 | B1 |
| 6323291 | Mason et al. | Nov 2001 | B1 |
| 6323304 | Lemmon et al. | Nov 2001 | B1 |
| 6342304 | Buchanan et al. | Jan 2002 | B1 |
| 6352783 | Fagerburg | Mar 2002 | B1 |
| 6354986 | Hlavinka et al. | Mar 2002 | B1 |
| 6359070 | Khanarian et al. | Mar 2002 | B1 |
| 6406792 | Briquet et al. | Jun 2002 | B1 |
| 6437083 | Brack et al. | Aug 2002 | B1 |
| 6448334 | Verhoogt et al. | Sep 2002 | B1 |
| 6458468 | Moskala et al. | Oct 2002 | B1 |
| 6504002 | Karlik et al. | Jan 2003 | B1 |
| 6559272 | Jeon et al. | May 2003 | B1 |
| 6573328 | Kropp et al. | Jun 2003 | B2 |
| 6576717 | Kuo | Jun 2003 | B1 |
| 6599994 | Shelby et al. | Jul 2003 | B2 |
| 6639067 | Brinegar et al. | Oct 2003 | B1 |
| 6656577 | Adelman et al. | Dec 2003 | B1 |
| 6669980 | Hansen | Dec 2003 | B2 |
| 6723768 | Adams et al. | Apr 2004 | B2 |
| 6733716 | Belcher | May 2004 | B2 |
| 6740377 | Pecorini et al. | May 2004 | B2 |
| 6773653 | Miller et al. | Aug 2004 | B2 |
| 6818293 | Keep et al. | Nov 2004 | B1 |
| 6818730 | Brandenburg et al. | Nov 2004 | B2 |
| 6846440 | Flynn et al. | Jan 2005 | B2 |
| 6846508 | Colas et al. | Jan 2005 | B1 |
| 6896966 | Crawford et al. | May 2005 | B2 |
| 6908650 | Odorisio et al. | Jun 2005 | B2 |
| 6914120 | Germroth et al. | Jul 2005 | B2 |
| 7037576 | Willham et al. | May 2006 | B2 |
| 7048978 | Tanaka et al. | May 2006 | B2 |
| 7053143 | Mori et al. | May 2006 | B2 |
| 7122661 | Fleche et al. | Oct 2006 | B2 |
| 7169880 | Shelby et al. | Jan 2007 | B2 |
| 7273894 | Shelby et al. | Sep 2007 | B2 |
| 7297755 | Shelby et al. | Nov 2007 | B2 |
| 7354628 | Steube | Apr 2008 | B2 |
| 7375154 | Stafford et al. | May 2008 | B2 |
| 7427430 | Rhee et al. | Sep 2008 | B2 |
| 7468409 | Pearson et al. | Dec 2008 | B2 |
| 7482397 | Pearson et al. | Jan 2009 | B2 |
| 7893188 | Crawford et al. | Feb 2011 | B2 |
| 8415450 | Crawford et al. | Apr 2013 | B2 |
| 8501292 | Pecorini et al. | Aug 2013 | B2 |
| 20010029324 | Walker et al. | Oct 2001 | A1 |
| 20010031805 | Buhler | Oct 2001 | A1 |
| 20010034419 | Kanayama et al. | Oct 2001 | A1 |
| 20010044003 | Gallucci et al. | Nov 2001 | A1 |
| 20020055586 | Dalgewicz, III et al. | May 2002 | A1 |
| 20020128357 | Goossens et al. | Sep 2002 | A1 |
| 20020132963 | Quillen | Sep 2002 | A1 |
| 20020137856 | Andrews et al. | Sep 2002 | A1 |
| 20020188092 | Moskala et al. | Dec 2002 | A1 |
| 20020198297 | Odorisio et al. | Dec 2002 | A1 |
| 20030032737 | Andrews et al. | Feb 2003 | A1 |
| 20030060546 | Moskala et al. | Mar 2003 | A1 |
| 20030075516 | Rothman et al. | Apr 2003 | A1 |
| 20030077546 | Donovan et al. | Apr 2003 | A1 |
| 20030135015 | Fujimaki et al. | Jul 2003 | A1 |
| 20030139497 | Odorisio et al. | Jul 2003 | A1 |
| 20030149177 | Andrews et al. | Aug 2003 | A1 |
| 20030169514 | Bourdelais et al. | Sep 2003 | A1 |
| 20030187151 | Adams et al. | Oct 2003 | A1 |
| 20030195295 | Mahood et al. | Oct 2003 | A1 |
| 20030221716 | Olson | Dec 2003 | A1 |
| 20030229181 | Hariharan et al. | Dec 2003 | A1 |
| 20040022526 | Kuno et al. | Feb 2004 | A1 |
| 20040063864 | Adams et al. | Apr 2004 | A1 |
| 20040101687 | Crawford et al. | May 2004 | A1 |
| 20040106707 | Su et al. | Jun 2004 | A1 |
| 20040106767 | Simon et al. | Jun 2004 | A1 |
| 20040108623 | Deeter et al. | Jun 2004 | A1 |
| 20040138381 | Blasius et al. | Jul 2004 | A1 |
| 20040145700 | Miniutti et al. | Jul 2004 | A1 |
| 20040164279 | Stevenson et al. | Aug 2004 | A1 |
| 20040202822 | Bourdelais et al. | Oct 2004 | A1 |
| 20040214984 | Keep et al. | Oct 2004 | A1 |
| 20050008885 | Blakely et al. | Jan 2005 | A1 |
| 20050072060 | Moncho et al. | Apr 2005 | A1 |
| 20050096453 | Flynn et al. | May 2005 | A1 |
| 20050101759 | Odorisio et al. | May 2005 | A1 |
| 20050113556 | Strand et al. | May 2005 | A1 |
| 20050119359 | Shelby et al. | Jun 2005 | A1 |
| 20050124779 | Shelby et al. | Jun 2005 | A1 |
| 20050181155 | Share et al. | Aug 2005 | A1 |
| 20060004151 | Shaikh et al. | Jan 2006 | A1 |
| 20060036012 | Hayes et al. | Feb 2006 | A1 |
| 20060094858 | Turner et al. | May 2006 | A1 |
| 20060111481 | Pearson et al. | May 2006 | A1 |
| 20060111519 | Strand et al. | May 2006 | A1 |
| 20060135668 | Hayes | Jun 2006 | A1 |
| 20060146228 | Sogo et al. | Jul 2006 | A1 |
| 20060151907 | Kashiwabara et al. | Jul 2006 | A1 |
| 20060180560 | Robinson | Aug 2006 | A1 |
| 20060197246 | Hale et al. | Sep 2006 | A1 |
| 20060199904 | Hale et al. | Sep 2006 | A1 |
| 20060199919 | Hale et al. | Sep 2006 | A1 |
| 20060228507 | Hale et al. | Oct 2006 | A1 |
| 20060234073 | Hale et al. | Oct 2006 | A1 |
| 20060235167 | Hale et al. | Oct 2006 | A1 |
| 20060247388 | Hale et al. | Nov 2006 | A1 |
| 20060270773 | Hale et al. | Nov 2006 | A1 |
| 20060270806 | Hale | Nov 2006 | A1 |
| 20070071930 | Shelby et al. | Mar 2007 | A1 |
| 20080092776 | Stockl et al. | Apr 2008 | A1 |
| 20100096589 | Crawford et al. | Apr 2010 | A1 |
| 20100204413 | Powell et al. | Aug 2010 | A1 |
| 20130072628 | Crawford et al. | Mar 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 615850 | Jul 1962 | BE |
| 2035149 | Apr 1962 | CA |
| 197 27 709 | Aug 1991 | DE |
| 198 11 773 | Jun 1997 | DE |
| 29 21 868 | Sep 1999 | DE |
| 0 039 838 | Dec 1980 | EP |
| 0 273 144 | Nov 1981 | EP |
| 0 282 277 | May 1987 | EP |
| 0 372 846 | Sep 1988 | EP |
| 0 544 008 | Jun 1990 | EP |
| 0 595 413 | Jun 1993 | EP |
| 0 698 631 | May 1994 | EP |
| 0 714 764 | Feb 1996 | EP |
| 0 902 052 | Jun 1996 | EP |
| 0 930 531 | Mar 1999 | EP |
| 1 035 167 | Jul 1999 | EP |
| 1 066 825 | Sep 2000 | EP |
| 1 674 496 | Jan 2001 | EP |
| 1 705 124 | Jun 2006 | EP |
| 2168752 | Mar 2010 | EP |
| 1291273 | Dec 1961 | FR |
| 1432471 | May 1965 | FR |
| 1434658 | Feb 1966 | FR |
| 2112400 | Feb 1966 | FR |
| 1044015 | Sep 1966 | GB |
| 1047043 | Sep 1966 | GB |
| 1130558 | Nov 1966 | GB |
| 1041651 | Nov 1967 | GB |
| 1 278 284 | Oct 1968 | GB |
| 1090241 | Jun 1972 | GB |
| 1364732 | Jun 1972 | GB |
| 2216919 | Aug 1974 | GB |
| 962913 | Oct 1989 | GB |
| 03207743 | Jul 1964 | JP |
| 65-01040 | Dec 1979 | JP |
| 9-59371 | Sep 1991 | JP |
| 2000-352620 | Feb 1994 | JP |
| 11-222516 | Apr 1997 | JP |
| 56-88440 | Aug 1999 | JP |
| 2001-098086 | Aug 1999 | JP |
| 2001-066701 | Dec 2000 | JP |
| 2001-214049 | Apr 2001 | JP |
| 2004-058565 | Aug 2001 | JP |
| 2004-066624 | Feb 2004 | JP |
| 2004-244497 | Mar 2004 | JP |
| 2004-292558 | Sep 2004 | JP |
| 2005-254757 | Oct 2004 | JP |
| 2007-069914 | Sep 2005 | JP |
| 2007-253491 | Mar 2007 | JP |
| 2003-054611 | Oct 2001 | KR |
| 2001-089942 | Oct 2007 | KR |
| WO 01-06981 | Jan 1997 | WO |
| WO 01-85824 | Feb 2001 | WO |
| WO 02-055570 | Nov 2001 | WO |
| WO 02-059207 | Jul 2002 | WO |
| WO2004-009146 | Aug 2002 | WO |
| WO 8804279 | Jul 2003 | WO |
| WO 2004-039860 | Jan 2004 | WO |
| WO 2004-104077 | May 2004 | WO |
| WO 2004-106988 | Dec 2004 | WO |
| WO 2005-007735 | Dec 2004 | WO |
| WO 2005-026241 | Jan 2005 | WO |
| WO 2005110874 | Mar 2005 | WO |
| WO 2006-127755 | Mar 2006 | WO |
| WO 2006-127831 | Nov 2006 | WO |
| WO 2007-053434 | Nov 2006 | WO |
| WO 2007-053548 | May 2007 | WO |
| WO 2007-053549 | May 2007 | WO |
| WO 2007-053550 | May 2007 | WO |
| WO 2009130033 | May 2007 | WO |
| WO 2007-123631 | Nov 2007 | WO |
| WO 2009070238 | Apr 2010 | WO |
| Entry |
|---|
| Abstract of U.S. Defense Publication T869,015, 869 O.G. 714, Dec. 16, 1969. |
| Abstract of U.S. Defense Publication T875,010, 875 O.G. 342, Jun. 9, 1970. |
| Chen et al., “The molecular basis for the relationship between the secondary relaxation and mechanical properties of a series of polyester copolymer glasses,” Marcromolecules, 32:5944-5955 (1999). |
| Coover, H. et al., “Copolyester Molding Compositions,” Chemical Abstracts Service, XP002391844, Jun. 1970. |
| Kelsey, E. et al., “High Impact, Amorphous Terephthalate Copolyesters of Rigid 2,2,4,4-Tetramethy1-1,3-cyclobutanediol with Flexible Diols,” Macromolecules, vol. 33, 2000, pp. 5810-5818, American Chemical Society. |
| Notification of transmittal of the International Search Report and the written opinion of the International Searching Authority or the declaration date of mailing Sep. 26, 2012, received in International Application No. PCT/US022012/038314, Filing Date: May 17, 2012. |
| “Plastic Additives Handbook,” 5th Edition, 2001, pp. 98-108 and pp. 109-112 (Hanser Gardner Publications, Inc., Cincinnati, OH. |
| Bergen, R. L., Jr., “Stress Cracking of Rigid Thermoplastics,” SPE Journal, Jun. 1962. |
| Scheirs, John, et al., “Modern Polyesters: Chemistry and Technology of Polyesters and Copolyesters,” Technology & Engineering, 2003, p. 287. |
| English language Abstract of JP 02-305816 from Patent Abstracts of Japan, Dec. 19, 1990. |
| English language translation of Belgian Patent No. BE 615,850, Apr. 13, 1962. |
| English language translation of French Patent No. FR 1,432,471, Feb. 7, 1966. |
| English language translation of French Patent No. FR 1,434,658, Feb. 28, 1966. |
| U.S. Appl. No. 11/390,555, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,563, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,629, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,630, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,631, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,654, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,655, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,671, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,672, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,722, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,750, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,751, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,752, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,773, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,793, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,794, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,809, filed Mar. 28, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/390,811, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,812, filed Mar. 28, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/390,814, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,826, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,827, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,836, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,846, filed Mar. 28, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/390,847, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,853, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,858, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,864, filed Mar. 28, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/390,865, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,882, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/390,883, filed Mar. 28, 2006, Thomas Joseph Pecorini, et al. |
| U.S. Appl. No. 11/390,908, filed Mar. 28, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/391,063, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,124, filed Mar. 28, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/391,125, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,137, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,156, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,485, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,495, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,505, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,565, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,571, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,576, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,642, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/391,659, filed Mar. 28, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/588,524, filed Oct. 27, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/588,458, filed Oct. 27, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/588,907, filed Oct. 27, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/588,527, filed Oct. 27, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/588,906, filed Oct. 27, 2006, Ted Calvin Germroth, et al. |
| U.S. Appl. No. 11/588,883, filed Oct. 27, 2006, Ted Calvin Germroth, et al. |
| U.S. Appl. No. 11/588,554, filed Oct. 27, 2006, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 11/635,434, filed Dec. 7, 2006, Emmett Dudley Crawford. |
| U.S. Appl. No. 11/635,433, filed Dec. 7, 2006, Emmett Dudley Crawford. |
| U.S. Appl. No. 11/439,062, filed May 23, 2006, Wesley Raymond Hale, et al. |
| U.S. Appl. No. 11/439,340, filed May 23, 2006, Wesley Raymond Hale. |
| U.S. Appl. No. 11/706,476, filed Feb. 14, 2007, Leslie Shane Moody, et al. |
| U.S. Appl. No. 11/706,791, filed Feb. 14, 2007, Leslie Shane Moody, et al. |
| U.S. Appl. No. 12/091,568, filed Apr. 25, 2008, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 12/091,566, filed Apr. 25, 2008, Emmett Dudley Crawford, et al. |
| U.S. Appl. No. 12/091,570, filed Apr. 25, 2008, Ted Calvin Germroth, et al. |
| U.S. Appl. No. 12/091,572, filed Apr. 25, 2008, Ted Calvin Germroth, et al. |
| U.S. Appl. No. 12/294,690, filed Sep. 26, 2008, Ted Calvin Germroth et al. |
| U.S. Appl. No. 12/294,686, filed Sep. 26, 2008, Ted Calvin Germroth et al. |
| U.S. Appl. No. 12/274,692, filed Nov. 20, 2008, Thomas Joseph Pecorini et al. |
| U.S. Appl. No. 12/361,779, filed Jan. 29, 2009, Emmett Dudley Crawford. |
| U.S. Appl. No. 12/365,515, filed Feb. 4, 2009, Emmett Dudley Crawford. |
| Chapter 4—Processing of Plastics in “Plastics Engineering, 3rd ed”, R.J. Crawford, Butterworth-Heinemann Publisher, 1998, Oxford, England, pp. 245-342. |
| Fox equation (T.G. Fox, Session J, Bull. Am. Phys. Soc., 1, 123 (1956)). |
| The Technology of Plasticizers, by J. Kern Sears and Joseph R Darby, published by Society of Plastic Engineers—Wiley and Sons, New York, 1982; pp. 136-139. |
| Coleman et al., “Polymer Reviews—A Practical Guide to Polymer Miscibility,” Polymer 31, pp. 1187-1203 (1990). |
| “Hansen Solubility Parameters, a Users Handbook”, by Charles M. Hansen, Chapter 1, CRC Press, 2000, pp. 1-24. |
| Martinez et al., “Phase Behavior and Mechanical Properties of Injection Molded Poly (Ethylene Terephthalate)—Polyarylate Blends”; Journal of Applied Polymer Science, John Wiley and Sons Inc. New York, US, vol. 45, No. 7, Jul. 5, 1992 (Jul. 5, 1992), p. 1135-1143. |
| Won Ho Jo et al. : :Miscibility of poly(ether imide)-poly(ethylene terephthalate)blends; Polymer Bulletin, Springer, Heidelberg, DE, vol. 33, No. 1, Jun. 1, 1994 (Jun. 1, 1994), p. 113-118 (1994). |
| Anonymous: “Poly (ethylene naphthalenedicarboxylate)-polyetherimide blends” Research Disclosure, Mason Publications, Hampshire, GB, vol. 283, No. 38, Nov. 1987 (Nov. 1987). |
| ASTM D1525-06, Standard Test Method for Vicat Softening Temperature of Plastics, Mar. 15, 2006. |
| ASTM D648-06, Standard Test Method for Deflection Temperature of Plastics Under Flexural Load in the Edgewise Position, Mar. 15, 2006. |
| ASTM D256-06, Standard Test Methods for Determining the Izod Pendulum Impact Resistance of Plastics, Mar. 15, 2006. |
| ASTM D790-03, Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials, Mar. 10, 2003. |
| ASTM D638-03, Standard Test Method for Tensile Properties of Plastics, Dec. 1, 2003. |
| ASTM D3418-03, Transition Temperatures and Enthalpies of Fusion and Crystallization of Polymers by Differential Scanning Calorimetry, Dec. 1, 2003. |
| Color Index Constitution No. 515240, SciFinder, Nov. 6, 2006. |
| Color Index Constitution No. 515245, SciFinder, Nov. 6, 2006. |
| Database WPI, Section Ch, Week 200536, Derwent Publications Ltd., London, GB; AN 2005-355258, XP002396922 & WO 2005-030833 A1 (Kanebo Ltd) Apr. 7, 2005 (Apr. 7, 2005) abstract. |
| Shearer, N.H., “T18-Type 1 Polyesters,” Mar. 1966, SPE Annual Technical Conference and Exhibition, XP009080224. |
| Gachter, Muller, “Taschenbuch der Kunststoff-Additive,” 1990, Carl Hanser Verlag Munchen Wien, XP02450422, pp. 96-97. |
| Gachter, Muller, “Kunstoff-Additive,” 1990, Carl Hanser Verlag Munchen Wien, XP 02449987, pp. 96-99. |
| Brown, R., “Taschenbuch Kunstoff-Additive”, 1990, Carl Hanswer Verlag Munchen Wiel, XP002455247, pp. 361-363. |
| Chang, S. et al., “Effect of Stabilizers on the Preparation of Poly(ethylene Terephthalate)”, Journal of Polymer Science, Polymer Chemistry Edition, 1982, vol. 20, pp. 2053-2061, John Wiley & Sons, Inc. |
| USPTO Office Action dated Mar. 11, 2008 for copending U.S. Appl. No. 11/391,642. |
| USPTO Office Action dated Mar. 24, 2008 for copending U.S. Appl. No. 11/390,908. |
| USPTO Office Action dated Apr. 15, 2008 for copending U.S. Appl. No. 11/390,629. |
| USPTO Office Action dated Apr. 16, 2008 for copending U.S. Appl. No. 11/390,751. |
| USPTO Office Action dated Apr. 17, 2008 for copending U.S. Appl. No. 11/390,814. |
| USPTO Office Action dated Jun. 3, 2008 for copending U.S. Appl. No. 11/391,063. |
| USPTO Office Action dated Sep. 10, 2008 for copending U.S. Appl. No. 11/390,752. |
| USPTO Office Action dated Sep. 10, 2008 for copending U.S. Appl. No. 11/390,794. |
| USPTO Office Action dated Sep. 19, 2008 for copending U.S. Appl. No. 11/391,565. |
| USPTO Office Action dated Oct. 2, 2008 for copending U.S. Appl. No. 11/390,671. |
| USPTO Office Action dated Sep. 24, 2008 for copending U.S. Appl. No. 11/390,631. |
| USPTO Office Action dated Oct. 1, 2008 for copending U.S. Appl. No. 11/390,655. |
| USPTO Office Action dated Sep. 29, 2008, for copending U.S. Appl. No. 11/391,137. |
| USPTO Office Action dated Sep. 9, 2008 for copending U.S. Appl. No. 11/391,571. |
| USPTO Office Action dated Oct. 22, 2008 for copending U.S. Appl. No. 11/391,125. |
| USPTO Office Action dated Oct. 20, 2008 for copending U.S. Appl. No. 11/390,672. |
| USPTO Office Action dated Oct. 8, 2008 for copending U.S. Appl. No. 11/390,853. |
| USPTO Office Action dated Oct. 9, 2008 for copending U.S. Appl. No. 11/391,505. |
| USPTO Notice of Allowance dated Oct. 7, 2008 for copending U.S. Appl. No. 11/390,908. |
| USPTO Office Action dated Oct. 14, 2008 for copending U.S. Appl. No. 11/390,811. |
| USPTO Office Action dated Oct. 22, 2008 for copending U.S. Appl. No. 11/390,750. |
| USPTO Office Action dated Oct. 22, 2008 for copending U.S. Appl. No. 11/390,865. |
| USPTO Office Action dated Oct. 14, 2008 for copending U.S. Appl. No. 11/390,654. |
| USPTO Office Action dated Oct. 20, 2008 for copending U.S. Appl. No. 11/390,836. |
| Copending application, U.S. Appl. No. 12/254,894, filed Oct. 21, 2008, Gary Michael Stack, et al. |
| USPTO Office Action dated Oct. 29, 2008 for copending U.S. Appl. No. 11/390,955. |
| USPTO Notice of Allowance dated Nov. 3, 2008 for copending U.S. Appl. No. 11/391,642. |
| USPTO Office Action dated Nov. 3, 2008 for copending U.S. Appl. No. 11/391,485. |
| USPTO Office Action dated Oct. 29, 2008 for copending U.S. Appl. No. 11/390,864. |
| USPTO Office Action dated Oct. 30, 2008 for copending U.S. Appl. No. 11/391,495. |
| USPTO Office Action dated Oct. 31, 2008 for copending U.S. Appl. No. 11/391,156. |
| USPTO Office Action dated Nov. 3, 2008 for copending U.S. Appl. No. 11/390,883. |
| USPTO Office Action dated Dec. 19, 2008 for copending U.S. Appl. No. 11/390,751. |
| USPTO Office Action dated Dec. 31, 2008 for copending U.S. Appl. No. 11/390,827. |
| USPTO Office Action dated Dec. 31, 2008 for copending U.S. Appl. No. 11/390,826. |
| USPTO Office Action dated Nov. 14, 2008 for copending U.S. Appl. No. 11/390,630. |
| USPTO Office Action dated Dec. 19, 2008 for copending U.S. Appl. No. 11/391,576. |
| USPTO Office Action dated Dec. 19, 2008 for copending U.S. Appl. No. 11/390,629. |
| USPTO Office Action dated Dec. 31, 2008 for copending U.S. Appl. No. 11/390,773. |
| USPTO Office Action dated Dec. 12, 2008 for copending U.S. Appl. No. 11/391,063. |
| USPTO Office Action dated Dec. 19, 2008 for copending U.S. Appl. No. 11/390,814. |
| USPTO Office Action dated Dec. 31, 2008 for copending U.S. Appl. No. 11/390,722. |
| USPTO Office Action dated Nov. 14, 2008 for copending U.S. Appl. No. 11/390,882. |
| USPTO Office Action dated Jan. 29, 2009 for copending U.S. Appl. No. 11/588,524. |
| USPTO Office Action dated Jan. 30, 2009 for copending U.S. Appl. No. 11/588,458. |
| USPTO Office Action dated Feb. 2, 2009 for copending U.S. Appl. No. 11/390,853. |
| USPTO Office Action dated Jan. 21, 2009 for copending U.S. Appl. No. 11/390,847. |
| USPTO Office Action dated Jan. 12, 2009 for copending U.S. Appl. No. 11/390,858. |
| USPTO Office Action dated Jan. 26, 2009 for copending U.S. Appl. No. 11/391,659. |
| USPTO Office Action dated Jan. 26, 2009 for copending U.S. Appl. No. 11/588,554. |
| USPTO Office Action dated Feb. 3, 2009 for copending U.S. Appl. No. 11/391,505. |
| USPTO Office Action dated Feb. 10, 2009 for copending U.S. Appl. No. 11/390,865. |
| USPTO Office Action dated Feb. 12, 2009 for copending U.S. Appl. No. 11/439,062. |
| USPTO Office Action dated Feb. 13, 2009 for copending U.S. Appl. No. 11/439,340. |
| USPTO Office Action dated Feb. 25, 2009 for copending U.S. Appl. No. 11/588,907. |
| USPTO Office Action dated Feb. 25, 2009 for copending U.S. Appl. No. 11/588,527. |
| USPTO Office Action dated Feb. 27, 2009 for copending U.S. Appl. No. 11/390,955. |
| USPTO Office Action dated Feb. 25, 2009 for copending U.S. Appl. No. 11/588,906. |
| USPTO Office Action dated Feb. 25, 2009 for copending U.S. Appl. No. 11/588,883. |
| USPTO Office Action dated Mar. 5, 2009 for copending U.S. Appl. No. 11/390,864. |
| USPTO Office Action dated Mar. 6, 2009 for copending U.S. Appl. No. 11/391,156. |
| USPTO Office Action dated Feb. 25, 2009 for copending U.S. Appl. No. 11/390,811. |
| USPTO Office Action dated Feb. 27, 2009 for copending U.S. Appl. No. 11/390,654. |
| USPTO Office Action dated Feb. 27, 2009 for copending U.S. Appl. No. 11/390,836. |
| USPTO Office Action dated Mar. 13, 2009 for copending U.S. Appl. No. 11/390,883. |
| USPTO Office Action dated Mar. 11, 2009 for copending U.S. Appl. No. 11/390,630. |
| USPTO Office Action dated Mar. 9, 2009 for copending U.S. Appl. No. 11/391,495. |
| USPTO Office Action dated Mar. 9, 2009 for copending U.S. Appl. No. 11/390,750. |
| USTPO Office Action dated Mar. 16, 2009 for copending U.S. Appl. No. 11/390,882. |
| USPTO Office Action dated Apr. 27, 2009 for copending U.S. Appl. No. 11/390,655. |
| USPTO Office Action dated Apr. 27, 2009 for copending U.S. Appl. No. 11/391,137. |
| USPTO Office Action dated Mar. 16, 2009 for copending U.S. Appl. No. 11/391,485. |
| USPTO Office Action dated Apr. 15, 2009 for copending U.S. Appl. No. 12/091,566. |
| USPTO Notice of Allowance dated Apr. 13, 2009 for copending U.S. Appl. No. 11/391,063. |
| USPTO Office Action dated Apr. 16, 2009 for copending U.S. Appl. No. 12/091,570. |
| USPTO Office Action dated Apr. 17, 2009 for copending U.S. Appl. No. 11/390,671. |
| USPTO Office Action dated Apr. 17, 2009 for copending U.S. Appl. No. 11/391,565. |
| USPTO Office Action dated Apr. 20, 2009 for copending U.S. Appl. No. 11/390,631. |
| USPTO Office Action dated Mar. 31, 2009 for copending U.S. Appl. No. 11/390,563. |
| USPTO Office Action dated Apr. 2, 2009 for copending U.S. Appl. No. 11/390,793. |
| USPTO Office Action dated Mar. 23, 2009 for copending U.S. Appl. No. 11/390,752. |
| USPTO Office Action dated Mar. 23, 2009 for copending U.S. Appl. No. 11/390,794. |
| USPTO Office Action dated May 13, 2009 for copending U.S. Appl. No. 12/361,779. |
| USPTO Office Action dated May 13, 2009 for copending U.S. Appl. No. 12/365,515. |
| USPTO Office Action dated May 21, 2009 for copending U.S. Appl. No. 11/706,476. |
| USPTO Office Action dated May 22, 2009 for copending U.S. Appl. No. 11/706,791. |
| USPTO Office Action dated May 18, 2009 for copending U.S. Appl. No. 11/391,505. |
| USPTO Office Action dated Apr. 14, 2009 for copending U.S. Appl. No. 11/635,434. |
| USPTO Office Action dated Apr. 14, 2009 for copending U.S. Appl. No. 11/635,433. |
| USPTO Office Action dated May 18, 2009 for copending U.S. Appl. No. 11/390,846. |
| USPTO Office Action dated Jun. 11, 2009 for copending U.S. Appl. No. 11/390,809. |
| USPTO Office Action dated Jul. 2, 2009 for copending U.S. Appl. No. 11/390,827. |
| USPTO Office Action dated Aug. 7, 2009 for copending U.S. Appl. No. 11/390,773. |
| USPTO Office Action dated Aug. 27, 2009 for copending U.S. Appl. No. 11/390,826. |
| USPTO Office Action dated Aug. 10, 2009 for copending U.S. Appl. No. 11/390,722. |
| Dixon, E.R. et al., “The Inter-Relation of Some Mechanical Properties with Molecular Weight and Crystallinity in Poly(ethylene terephthalate)”, 1968, pp. 464-470, Journal of Materials Science, vol. 3. |
| USPTO Office Action dated Sep. 4, 2009, for copending U.S. Appl. No. 11/391,124. |
| USPTO Office Action dated Sep. 10, 2009, for copending U.S. Appl. No. 11/390,812. |
| New Copending U.S. Appl. No. 12/479,893, filed Jun. 8, 2009, Emmett Dudley Crawford, et al. |
| USPTO Office Action dated Sep. 14, 2009 for copending U.S. Appl. No. 11/391,576. |
| Ellis, Thomas S., “Miscibility of Polyamide Blends: Effects of Configuration,” 1995, Polymer, vol. 36, Issue 20, pp. 3919-3926. |
| Buschow, K.H.J., et al., “Packaging: Papers for Sacks and Bags,” 2001, Encyclopedia of Materials: Science and Technology, vol. 8, Elsevier, pp. 6646-6652. |
| Coles, Richard, et al., “Food Packaging Technology,” 2003, pp. 194-195 and 224-229, Blackwell Publishing. |
| Sajiki, Junko, et al., “Leaching of Bisphenol A (BPA) to Seawater from Polycarbonate Plastic and its Degradation by Reactive Oxygen Species,” 2003, Chemosphere, 51, pp. 55-62. |
| USPTO Office Action dated Oct. 2, 2009 for copending U.S. Appl. No. 11/588,524. |
| USPTO Office Action dated Oct. 7, 2009 for copending U.S. Appl. No. 11/588,458. |
| USPTO Office Action dated Sep. 29, 2009 for copending U.S. Appl. No. 11/390,751. |
| USPTO Office Action dated Sep. 24, 2009 for copending U.S. Appl. No. 11/588,883. |
| USPTO Office Action dated Sep. 28, 2009 for copending U.S. Appl. No. 11/390,847. |
| USPTO Office Action dated Sep. 24, 2009 for copending U.S. Appl. No. 11/390,858. |
| USPTO Office Action dated Sep. 29, 2009 for copending U.S. Appl. No. 11/390,629. |
| USPTO Office Action dated Sep. 29, 2009 for copending U.S. Appl. No. 11/390,814. |
| USPTO Office Action dated Oct. 19, 2009 for copending U.S. Appl. No. 11/390,563. |
| USPTO Office Action dated Oct. 20, 2009 for copending U.S. Appl. No. 11/588,907. |
| USPTO Office Action dated Oct. 21, 2009 for copending U.S. Appl. No. 11/391,156. |
| Gupta, V.B. et al., “PET Fibers, Films, and Bottles: Section 5-7”, Handbook of Thermoplastic Polyesters: Homopolymers, Copolymers, Blends, and Composites, 2005, pp. 362-388, Wiley InterScience. |
| USPTO Office Action dated Oct. 22, 2009 for copending U.S. Appl. No. 11/588,906. |
| USPTO Office Action dated Nov. 3, 2009 for copending U.S. Appl. No. 11/390,883. |
| USPTO Office Action dated Nov. 4, 2009 for copending U.S. Appl. No. 11/390,750. |
| USPTO Office Action dated Nov. 4, 2009 for copending U.S. Appl. No. 11/390,864. |
| USPTO Office Action dated Nov. 17, 2009 for copending U.S. Appl. No. 12/254,894. |
| USPTO Office Action dated Nov. 18, 2009 for copending U.S. Appl. No. 11/390,630. |
| USPTO Office Action dated Nov. 30, 2009 for copending U.S. Appl. No. 11/391,495. |
| Turner, S.R., et al., “Amorphous and Crystalline Polyesters based on 1,4-Cyclohexanedimethanol”, Chapter 7, Modern Polyesters: Chemistry and Technology of Polyesters and Copolyesters, Edited by J. Sheirs and T.E. Long, 2003 John Wiley & Sons, Ltd., pp. 267-292. |
| USPTO Office Action dated Nov. 18, 2009 for copending U.S. Appl. No. 11/390,794. |
| USPTO Office Action dated Nov. 20, 2009 for copending U.S. Appl. No. 11/391,485. |
| USPTO Office Action dated Nov. 20, 2009 for copending U.S. Appl. No. 11/390,882. |
| USPTO Office Action dated Dec. 1, 2009 for copending U.S. Appl. No. 12/091,570. |
| USPTO Office Action dated Dec. 3, 2009 for copending U.S. Appl. No. 11/395,505. |
| USPTO Office Action dated Dec. 4, 2009 for copending U.S. Appl. No. 12/091,566. |
| Zipper, Marcus D.,et al., “A Free Volume Study of Miscible Polyester Blends,” 1995, pp. 127-136, Polymer, vol. 36. |
| “APEC High-Heat Polycarbonate Resin,” 2004, Bayer Material Science Product Information Not Prior Art; Submitted for State of the Art. |
| Lobo, Hubert et al, “Handbook of Plastics Analysis,” 2003, pp. 20 and 21, Marcel Dekker, Inc. |
| Turner, S.R., et al. “Amorphous and Crystalline Polyesters based on 1,4-Cyclohexanedimethanol,” 2003, Modern Polyesters: Chemistry and Technology of Polyesters and Copolyesters, pp. 268, 284-285, J. Sheirs and T.E. Long, ed., John Wiley and Sons, Ltd. |
| USPTO Notice of Allowance dated Dec. 11, 2009 for copending U.S. Appl. No. 12/365,515. |
| USPTO Office Action dated Dec. 18, 2009 for copending U.S. Appl. No. 11/390,846. |
| USPTO Notice of Allowance dated Dec. 22, 2009 for copending U.S. Appl. No. 12/361,779. |
| USPTO Office Action dated Jan. 7, 2010 for copending U.S. Appl. No. 12/091,568. |
| USPTO Office Action dated Jan. 13, 2010 for copending U.S. Appl. No. 11/635,433. |
| USPTO Office Action dated Jan. 14, 2010 for copending U.S. Appl. No. 11/390,809. |
| USPTO Notice of Allowance dated Jan. 27, 2010 for copending U.S. Appl. No. 11/635,434. |
| USPTO Office Action dated Mar. 11, 2010, for copending U.S. Appl. No. 11/391,124. |
| Copending U.S. Appl. No. 12/724,492, filed Mar. 16, 2010. |
| Copending U.S. Appl. No. 12/724,480, filed Mar. 16, 2010. |
| Copending U.S. Appl. No. 12/724,468, filed Mar. 16, 2010. |
| USPTO Office Action dated Mar. 19, 2010, for copending U.S. Appl. No. 11/588,527. |
| USPTO Notice of Allowance dated Mar. 24, 2010 for copending U.S. Appl. No. 11/391,565. |
| USPTO Office Action dated Mar. 29, 2010 for copending U.S. Appl. No. 11/390,812. |
| USPTO Notice of Allowance dated Apr. 15, 2010 for copending U.S. Appl. No. 11/391,505. |
| USPTO Office Action dated Apr. 19, 2010 for copending U.S. Appl. No. 12/724,480. |
| USPTO Office Action dated Apr. 21, 2010 for copending U.S. Appl. No. 12/724,468. |
| USPTO Office Action dated Apr. 21, 2010 for copending U.S. Appl. No. 12/724,492. |
| USPTO Office Action dated May 6, 2010 for copending U.S. Appl. No. 12/254,894. |
| New copending U.S. Appl. No. 12/784,193, filed May 20, 2010, Emmett Dudley Crawford, et al. |
| USPTO Notice of Allowance dated May 13, 2010 for copending U.S. Appl. No. 11/390,629. |
| USPTO Notice of Allowance dated May 13, 2010 for copending U.S. Appl. No. 11/390,751. |
| USPTO Notice of Allowance dated May 21, 2010 for copending U.S. Appl. No. 11/391,156. |
| USPTO Notice of Allowance dated May 26, 2010 for copending U.S. Appl. No. 11/391,495. |
| USPTO Notice of Allowance dated Jun. 24, 2010 for copending U.S. Appl. No. 11/391,576. |
| USPTO Office Action dated Jun. 24, 2010 for copending U.S. Appl. No. 11/390,846. |
| USPTO Office Action dated Jul. 8, 2010 for copending U.S. Appl. No. 11/390,809. |
| USPTO Notice of Allowance dated Jul. 8, 2010 for copending U.S. Appl. No. 11/390,630. |
| USPTO Notice of Allowance dated Jul. 8, 2010 for copending U.S. Appl. No. 11/390,883. |
| USPTO Office Action dated Jul. 12, 2010 for copending U.S. Appl. No. 11/390,794. |
| Notice of Allowance dated Jul. 13, 2010 for copending U.S. Appl. No. 11/391,505. |
| USPTO Office Action dated Jul. 22, 2010 for copending U.S. Appl. No. 12/479,893. |
| USPTO Notice of Allowance dated Jul. 22, 2010 for copending U.S. Appl. No. 11/391,485. |
| USPTO Notice of Allowance dated Aug. 3, 2010 for copending U.S. Appl. No. 11/390,864. |
| USPTO Office Action dated Aug. 6, 2010 for copending U.S. Appl. No. 11/773,275. |
| New copending U.S. Appl. No. 12/853,717, filed Aug. 10, 2010, Emmett Dudley Crawford, et al. |
| USPTO Notice of Allowance dated Aug. 11, 2010 for copending U.S. Appl. No. 11/390,631. |
| USPTO Notice of Allowance dated Sep. 2, 2010 for copending U.S. Appl. No. 11/390,811. |
| USPTO Office Action dated Sep. 2, 2010 for copending U.S. Appl. No. 11/391,124. |
| New copending U.S. Appl. No. 12/888,648, filed Sep. 23, 2010, Thomas Joseph Pecorini et al. |
| USPTO Office Action dated Oct. 5, 2010 for copending U.S. Appl. No. 11/390,655. |
| New copending U.S. Appl. No. 12/900,060, filed Oct. 7, 2010, Thomas Joseph Pecorini, et al. |
| USPTO Office Action dated Oct. 8, 2010 for copending U.S. Appl. No. 11/390,812. |
| USPTO Notice of Allowance dated Oct. 28, 2010 for copending U.S. Appl. No. 11/390,827. |
| USPTO Office Action dated Oct. 27, 2010 for copending U.S. Appl. No. 12/294,690. |
| New Copending U.S. Appl. No. 12/900,060, filed on Oct. 7, 2010, Joseph Thomas Pecorini. |
| USPTO Notice of Allowance dated Oct. 14, 2010 for copending U.S. Appl. No. 11/390,722. |
| USPTO Notice of Allowance dated Nov. 2, 2010 for copending U.S. Appl. No. 12/724,480. |
| USPTO Notice of Allowance dated Nov. 4, 2010 for copending U.S. Appl. No. 12/724,468. |
| USPTO Notice of Allowance dated Nov. 4, 2010 for copending U.S. Appl. No. 11/390,955. |
| USPTO Office Action dated Nov. 4, 2010 for copending U.S. Appl. No. 12/294,686. |
| USPTO Notice of Allowance dated Nov. 4, 2010 for copending U.S. Appl. No. 11/390,826. |
| USPTO Office Action dated Oct. 27, 2010 for copending U.S. Appl. No. 11/390,836. |
| USPTO Notice of Allowance dated Nov. 23, 2010 for copending U.S. Appl. No. 11/390,563. |
| New copending U.S. Appl. No. 12/943,217, filed Nov. 10, 2010, Emmett Dudley Crawford et al. |
| New copending U.S. Appl. No. 13/007,838, filed Jan. 17, 2011, Emmett Dudley Crawford et al. |
| USTPO Office Action dated Jan. 24, 2011 for copending U.S. Appl. No. 11/773,275. |
| New copending U.S. Appl. No. 13/016,147, filed Jan. 28, 2011, Emmett Dudley Crawford, et al. |
| New copending U.S. Appl. No. 13/017,069, filed Jan. 31, 2011, Emmett Dudley Crawford, et al. |
| New Copending U.S. Appl. No. 13/017,352, filed Jan. 31, 2011, Emmett Dudley Crawford, et al. |
| USPTO Office Action dated Jan. 25, 2011 for copending U.S. Appl. No. 12/853,717. |
| Al-Malaika, S., “Stabilization”, Encyclopedia of Polymer Science and Technology, vol. 4, 2001, pp. 179-229, John Wiley & Sons, Inc. |
| USPTO Notice of Allowance dated Jan. 26, 2011 for copending U.S. Appl. No. 11/390,858. |
| USPTO Office Action dated Feb. 2, 2011 for copending U.S. Appl. No. 11/390,655. |
| USPTO Office Action dated Mar. 17, 2011 for copending U.S. Appl. No. 12/479,893. |
| USPTO Notice of Allowance dated Mar. 17, 2011 for copending U.S. Appl. No. 11/391,137. |
| USPTO Office Action dated Feb. 14, 2011 for copending U.S. Appl. No. 12/294,690. |
| USPTO Notice of Allowance dated Feb. 18, 2011 for copending U.S. Appl. No. 11/390,809. |
| USPTO Notice of Allowance dated Feb. 17, 2011 for copending U.S. Appl. No. 11/390,812. |
| USPTO Notice of Allowance dated Aug. 12, 2011 for copending U.S. Appl. No. 11/390,752. |
| USPTO Office Action dated Jul. 19, 2011 for copending U.S. Appl. No. 11/390,794. |
| USPTO Notice of Allowance dated Jul. 21, 2011 for copending U.S. Appl. No. 11/390,671. |
| USPTO Notice of Allowance dated Aug. 3, 2011 for copending U.S. Appl. No. 11/390,655. |
| New copending U.S. Appl. No. 13/162,870, filed Jun. 17, 2011, Emmett Dudley Crawford, et al. |
| USPTO Office Action dated Jul. 7, 2011 for copending U.S. Appl. No. 11/588,906. |
| USPTO Office Action dated Jun. 22, 2011 for copending U.S. Appl. No. 12/091,570. |
| USPTO Office Action dated Jun. 8, 2011 for copending U.S. Appl. No. 11/588,883. |
| USPTO Office Action dated Aug. 17, 2011 for copending U.S. Appl. No. 12/274,692. |
| New copending U.S. Appl. No. 13/215,511, filed Aug. 23, 2011, Emmett Dudley Crawford, et al. |
| USPTO Office Action dated Sep. 14, 2011 for copending U.S. Appl. No. 13/017,069. |
| USPTO Notice of Allowance dated Sep. 16, 2011 for copending U.S. Appl. No. 11/390,671. |
| USPTO Notice of Allowance dated Sep. 16, 2011 for copending U.S. Appl. No. 12/784,193. |
| USPTO Office Action dated Oct. 17, 2011 for copending U.S. Appl. No. 12/853,717. |
| USPTO Notice of Allowance dated Oct. 17, 2011 for copending U.S. Appl. No. 11/390,794. |
| USPTO Notice of Allowance dated Oct. 25, 2011 for copending U.S. Appl. No. 12/900,060. |
| USPTO Office Action dated Nov. 2, 2011 for copending U.S. Appl. No. 12/479,893. |
| USPTO Notice of Allowance dated Nov. 10, 2011 for copending U.S. Appl. No. 12/943,217. |
| USPTO Notice of Allowance dated Nov. 28, 2011 for copending U.S. Appl. No. 12/274,692. |
| USPTO Office Action dated Dec. 21, 2011 for copending U.S. Appl. No. 12/091,570. |
| New copending U.S. Appl. No. 13/348,677, filed Jan. 12, 2012, Emmett Dudley Crawford, et al. |
| USPTO Notice of Allowance dated Feb. 14, 2012 for copending U.S. Appl. No. 11/588,906. |
| New copending U.S. Appl. No. 13/398,262, filed Feb. 26, 2012, Emmett Dudley Crawford et al. |
| USPTO Notice of Allowance dated Mar. 8, 2012 for copending U.S. Appl. No. 12/274,692. |
| USPTO Notice of Allowance dated Mar. 21, 2012 for copending U.S. Appl. No. 12/390,694. |
| Notice of Allowance and Fee(s) Due mailing date Jul. 18, 2012 received in co-pending U.S. Appl. No. 13/348,677. |
| Notice of Allowance and Fee(s) Due mailing date Jun. 21, 2012 received in co-pending U.S. Appl. No. 12/091,570. |
| Notice of Allowance and Fee(s) Due mailing date Jun. 11, 2012 received in co-pending U.S. Appl. No. 12/274,692. |
| Office Action notification date May 21, 2012 received in co-pending U.S. Appl. No. 13/215,511. |
| USPTO Notice of Allowance dated Sep. 28, 2012 for co-pending U.S. Appl. No. 13/016,147. |
| USPTO Office Action dated Oct. 2, 2012 for co-pending U.S. Appl. No. 13/596,754. |
| New co-pending U.S. Appl. No. 13/596,754, filed Aug. 28, 2012; Thomas Joseph Pecorini et al. |
| New co-pending U.S. Appl. No. 13/596,805, filed Aug. 28, 2012; Ted Calvin Germroth et al. |
| USPTO Non-Final Office Action received in co-pending U.S. Appl. No. 13/162,870 received Oct. 18, 2012. |
| New co-pending U.S. Appl. No. 13/658,249, filed Oct. 23, 2012; Emmett Dudley Crawford et al. |
| USPTO Office Action dated Dec. 7, 2012 for co-pending U.S. Appl. No. 13/398,262. |
| Notice of Allowance and Fee(s) Due mailing date Nov. 23, 2012 received in co-pending U.S. Appl. No. 13/348,677. |
| Notice of Allowance and Fee(s) Due mailing date Jan. 24, 2013 received in co-pending U.S. Appl. No. 13/215,511. |
| Notice of Allowance notification date Apr. 3, 2013 received in co-pending U.S. Appl. No. 12/888,648. |
| Notice of Allowance notification date Apr. 4, 2013 received in co-pending U.S. Appl. No. 13/596,754. |
| Notice of Allowance notification date Apr. 12, 2013 received in co-pending U.S. Appl. No. 13/215,511. |
| Non-Final Office Action notification date Oct. 25, 2013 received in co-pending U.S. Appl. No. 13/007,838. |
| Notice of Allowance notification date Oct. 11, 2013 received in co-pending U.S. Appl. No. 13/162,870. |
| Non-Final Office Action notification date Feb. 13, 2014 received in co-pending U.S. Appl. No. 13/162,870. |
| USPTO Notice of Allowance dated Apr. 12, 2014 for copending U.S. Appl. No. 13/596,805. |
| USPTO Notice of Allowance dated May 12, 2014 for copending U.S. Appl. No. 13/596,805. |
| USPTO Notice of Allowance dated May 15, 2014 for copending U.S. Appl. No. 13/709,097. |
| USPTO Office Action dated Aug. 21, 2014 for copending U.S. Appl. No. 13/398,262. |
| USPTO Office Action dated Dec. 10, 2014 for copending U.S. Appl. No. 13/658,249. |
| USPTO Notice of Allowance dated Dec. 12, 2014 for copending U.S. Appl. No. 13/162,870. |
| USPTO Notice of Allowance dated Jan. 28, 2015 for copending U.S. Appl. No. 13/007,838. |
| USPTO Notice of Allowance dated Feb. 25, 2015 for copending U.S. Appl. No. 13/162,870. |
| USPTO Notice of Allowance dated Mar. 19, 2015 for copending U.S. Appl. No. 13/709,097. |
| USPTO Notice of Allowance dated Apr. 6, 2015 for copending U.S. Appl. No. 13/007,838. |
| USPTO Office Action dated Apr. 8, 2015 for copending U.S. Appl. No. 13/658,249. |
| USPTO Notice of Allowance dated Apr. 10, 2015 for copending U.S. Appl. No. 13/596,805. |
| USPTO Office Action dated Apr. 30, 2015 for copending U.S. Appl. No. 13/941,362. |
| USPTO Notice of Allowance dated Jul. 6, 2015 for copending U.S. Appl. No. 13/709,097. |
| USPTO Office Action dated Jul. 28, 2015 for copending U.S. Appl. No. 13/658,249. |
| USPTO Notice of Allowance dated Jul. 31, 2015 for copending U.S. Appl. No. 13/596,805. |
| USPTO Notice of Allowance dated Aug. 21, 2015 for copending U.S. Appl. No. 13/007,838. |
| USPTO Notice of Allowance dated Sep. 2, 2015 for copending U.S. Appl. No. 13/162,870. |
| USPTO Notice of Allowance dated Sep. 3, 2015 for copending U.S. Appl. No. 13/709,097. |
| USPTO Notice of Allowance dated Sep. 16, 2015 for copending U.S. Appl. No. 13/596,805. |
| Number | Date | Country | |
|---|---|---|---|
| 20160009951 A1 | Jan 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60691567 | Jun 2005 | US | |
| 60731454 | Oct 2005 | US | |
| 60731389 | Oct 2005 | US | |
| 60739058 | Nov 2005 | US | |
| 60738869 | Nov 2005 | US | |
| 60750692 | Dec 2005 | US | |
| 60750693 | Dec 2005 | US | |
| 60750682 | Dec 2005 | US | |
| 60750547 | Dec 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13348677 | Jan 2012 | US |
| Child | 13776038 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13776038 | Feb 2013 | US |
| Child | 14865705 | US | |
| Parent | 11390794 | Mar 2006 | US |
| Child | 13348677 | US |