The present disclosure relates to a power inductor, and more particularly, to a power inductor having superior inductance properties and improved insulation properties and thermal stability.
A power inductor is mainly provided in a power circuit such as a DC-DC converter within a portable device. The power inductor is increasing in use, instead of an existing wire wound choke coil as the power circuit is switched at a high frequency and miniaturized. Also, the power inductor is being developed in the manner of miniaturization, high current, low resistance, and the like as the portable device is reduced in size and multi-functionalized.
The power inductor according to the related art is manufactured in a shape in which a plurality of ferrites or ceramic sheets mode of a dielectric having a low dielectric constant are laminated. Here, a coil pattern is formed on each of the ceramic sheets. The coil pattern formed on each of the ceramic sheets is connected to the ceramic sheet by a conductive via, and the coil patterns overlap each other in a vertical direction in which the sheets are laminated. Also, in the related art, the body in which the ceramic sheets are laminated may be generally manufactured by using a magnetic material composed of a four element system of nickel (Ni), zinc (Zn), copper (Cu), and iron (Fe).
However, the magnetic material has a relatively low saturation magnetization value when compared to that of the metal material. Thus, the magnetic material may not realize high current properties that are required for the recent portable devices. As a result, since the body constituting the power inductor is manufactured by using metal magnetic powder, the power inductor may relatively increase in saturation magnetization value when compared to the body manufactured by using the magnetic material. However, if the body is manufactured by using the metal, an eddy current loss and a hysteresis loss of a high frequency wave may increase to cause serious damage of the material.
To reduce the loss of the material, a structure in which the metal magnetic powder is insulated from each other by a polymer is applied. That is, sheets in which the metal magnetic powder and the polymer are mixed with each other are laminated to manufacture the body of the power inductor. Also, a predetermined base material on which a coil pattern is formed is provided inside the body. That is, the coil pattern is formed on the predetermined base material, and a plurality of sheets are laminated and compressed on top and bottom surfaces of the coil pattern to manufacture the power inductor.
However, since the power inductor using the metal magnetic powder and the polymer has low magnetic permeability because the metal magnetic powder does not maintain its proper physical property as it is. Also, since the polymer surrounds the metal magnetic powder, the magnetic permeability of the body may be reduced.
The present disclosure provides a power inductor that is capable of improving magnetic permeability.
The present disclosure also provides a power inductor that is capable of improving magnetic permeability of a body to improve overall magnetic permeability.
The present disclosure also provides a power inductor that is capable of preventing an external electrode from being short-circuited.
In accordance with an exemplary embodiment, a power inductor includes: a body; at least one base material disposed within the body; at least one coil pattern disposed on at least one surface of the base material; an insulation film disposed between the coil pattern and the body; and an external electrode disposed outside the body and connected to the coil pattern, wherein the body includes a plurality of magnetic layers and insulation layers, which are alternately laminated.
The power inductor may further include an insulation capping layer disposed on an upper portion of the body.
The magnetic layer may be amorphous and include metal ribbon having magnetic permeability of 200 or more.
The magnetic layer may include at least one of plate-shaped sendust, Ni-based ferrite, and Mn-based ferrite.
The magnetic layer may have a size less than that of the insulation layer.
At least a portion of the magnetic layer may be insulated from the external electrode on the same plane.
The insulation layer may contain metal magnetic powder and thermal conductive filler.
The thermal conductive filler may include at least one selected from the group consisting of MgO, AlN, carbon-based materials, Ni-based ferrite, and Mn-based ferrite.
At least a region of the base material may be removed, and the body may be filled into the removed region.
The magnetic layer and the insulation layer may be vertically or horizontally alternately disposed, the insulation layer containing at least one of the metal magnetic powder and the thermal conductive filler is disposed, or a magnetic material is disposed on the removed region of the base material.
The coil patterns disposed on one surface and the other surface of the base material may have the same height.
The coil pattern may include a first plated layer disposed on the base material and a second plated layer covering the first plated layer.
At lest a region of the coil pattern may have a different width.
The insulation film may be disposed on top and side surfaces of the coil pattern at the uniform thickness and have the same thickness as each of top and side surfaces of the coil pattern on the base material.
At least a portion of the external electrode may be made of the same material as the coil pattern.
The coil pattern may be formed on at least one surface of the base material through a plating process, and an area of the external electrode, which contacts the coil pattern, may be formed through the plating process.
In accordance with another exemplary embodiment, a power inductor includes: a body; at least one base material disposed within the body; at least one coil pattern disposed on at least one surface of the base material; an insulation film disposed between the coil pattern and the body; and an external electrode disposed outside the body and connected to the coil pattern, wherein an area of the external electrode, which contacts the coil pattern, is made of the same material as the coil pattern.
The coil pattern may be formed on at least one surface of the base material through a plating process, and an area of the external electrode, which contacts the coil pattern, may be formed through the plating process.
The power inductor may further include an insulation capping layer disposed on at least one surface of the body.
The insulation capping layer may be disposed on at least a portion of an area except for an area on which the external electrode is mounted on a printed circuit board.
The external electrode may extend from each of first and second surfaces in a longitudinal direction of the body to each of third to sixth surfaces in width and height directions of the body, and the insulation capping layer may be disposed on an area facing the area on which the external electrode is mounted on the printed circuit board.
In the power inductor in accordance with the exemplary embodiments, the body may be manufactured by laminating the metal ribbon and the polymer. Since the body is manufactured by using the metal ribbon of which the proper magnetic permeability is maintained as it is, the magnetic permeability of the body may be improved. Therefore, the overall magnetic permeability of the power inductor may be improved.
Also, since the parylene is applied on the coil pattern, the parylene having the uniform thickness may be formed on the coil pattern, and thus, the insulation between the body and the coil pattern may be improved.
Also, the base material that is provided inside the body and on which the coil pattern is formed may be manufactured by using the metal magnetic material to prevent the power inductor from being deteriorated in magnetic permeability. In addition, at least a portion of the base material may be removed to fill the body in the removed portion of the base material, thereby improving the magnetic permeability. Also, at least one magnetic layer may be disposed on the body to improve the magnetic permeability of the power inductor.
The insulation capping layer maybe formed on the top surface of the body, on which the external electrode is formed, to prevent the external electrode, the shield can, and the adjacent components from being short-circuited therebetween.
Exemplary embodiments can be understood in more detail from the following description taken in conjunction with the accompanying drawings, in which:
Hereinafter, specific embodiments will be described in detail with reference to the accompanying drawings. The present invention may, however, be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the present invention to those skilled in the art.
Referring to
1. Body
The body 100 may have a hexahedral shape. That is, the body 100 may have an approximately hexahedral shape having a predetermined length in an X direction, a predetermined width in a Y direction, and a predetermined height in a Z direction. Here, the body 100 may have the length that is greater than each of the width and height and have the width that is equal to or different from the height. Alternatively, the body 100 may have a polyhedral shape in addition to the hexahedral shape. The body 100 may include a plurality of magnetic layers 110 and a plurality of insulation layers. The magnetic layers 110 and the insulation layers 120 may be alternately laminated on each other. Here, the magnetic layer 110 may include a metal ribbon, and the insulation layer 120 may include a polymer.
The magnetic layer 110 may have a predetermined thickness and a size corresponding to the length and width of the body 100. Alternatively, the magnetic layer 110 may have a size that is less than the length and width of the body 100. That is, to prevent the magnetic layer 110 from being exposed to the outside, the magnetic layer 110 may have a length and width that are less than those of the body 100. Here, the length and width of the body 100 may correspond to a length and width of the insulation layer 120. Thus, the magnetic layer 110 may have the length and width that are less than those of the insulation layer 120. Also, at least a portion of the magnetic layer 110 may not contact the external electrode 400. That is, when one side of the magnetic layer 110 contacts a first external electrode 410, the other side of the magnetic layer 110 may be spaced apart from a second external electrode 420. When the one side and the other side of the magnetic layer 110 contact the first and second external electrodes 410 and 420, one area of the magnetic layer 110 may be spaced apart from the first and second external electrodes 410 and 420. Thus, the two external electrodes 400 are not electrically connected to each other by the magnetic layer 110. The magnetic layer 110 may have a shape of a metal ribbon made of an amorphous alloy. To form the metal ribbon made of the amorphous alloy, a molten metal of the alloy may be injected into a cooling wheel that rotates at a high speed to form the metal ribbon. That is, since the molten metal is injected into the cooling wheel, the molten metal may be quickly cooled, for example, from a temperature of 1600 degrees to a predetermined temperature, e.g., a temperature of approximately several hundreds degrees per second, and thus, the magnetic layer 110 may be formed into an amorphous state. The magnetic layer 110 may have various widths and thicknesses. For example, the magnetic layer 110 may have various thicknesses in accordance with a rotating rate of the cooling wheel and various widths in accordance with a width of the cooling width. The amorphous magnetic layer 110 may be used by being cut to match the size of the body 100. Also, at least two magnetic layers 110 may be disposed on the same plane, i.e., the same layer. That is, at least two magnetic layers 110 may be horizontally disposed between the two insulation layers 120 that are vertically laminated. The at least two magnetic layers 110 that are horizontally disposed may be spaced apart from each other so that the magnetic layers 110 do not contact each other. Alternatively, the at least two magnetic layers 110 may contact each other. Here, the at least two magnetic layers 110 that are horizontally disposed may have sizes and shapes different from each other. That is, the at least two magnetic layers 110 having the same size and shape may be disposed on the same plane. Alternatively, the at least two magnetic layers 110 having sizes and shapes different from each other may be disposed on the same plane. Also, the magnetic layer 110 may be pulverized, and thus, a plurality of pieces of the magnetic layer 110 may be provided in the same layer. For this, the magnetic layer 110 may be disposed between insulation tapers, and then, a predetermined pressure may be applied to break the magnetic layer 110 so that a plurality of pieces of the magnetic layer 110 are disposed between the insulation layers 120. Alternatively, at least a portion of the magnetic layer 110 may be broken in the lamination process of the magnetic layer 110 and the insulation layer 120. The magnetic layer 110 may be manufactured by using an alloy to which Si, B, Nb, Cu, and the like are added on the basis of Fe. For example, the magnetic layer 110 may include at least one metal selected from the group consisting of Fe—Si, Fe—Ni—Si, Fe—Si—B, Fe—Si—Cr, Fe—Si—Al, Fe—Si—B—Cr, Fe—Al—Cr, Fe—Si—B—Nb—Cu, and Fe—Si—Cr—B—Nb—Cu. That is, the magnetic layer 110 may be formed using at least one ribbon of an FeSi-based ribbon, an FeNiSi-based ribbon, an FeSiB-based ribbon, an FeSiCr-based ribbon, an FeSiAl-based ribbon, an FeSiBCr-based ribbon, an FeAlCr-based ribbon, an FeSiBNbCu-based ribbon, and an FeSiCrBNbCu-based ribbon. The amorphous magnetic layer 110 may become a state in which crystal particles and/or crystal particle systems do not exist and thus may have many special properties. That is, the amorphous magnetic layer 110 may have superior magnetic properties, corrosion resistance, wear resistance, high strength, hardness and toughness, and high specific resistance. The magnetic layer 110 is different from a magnetic sheet. That is, although the magnetic layer 110 is made of a pure metal, the magnetic sheet is formed by molding a mixture, in which metal magnetic powder and a polymer are mixed with each other, in a predetermined shape. Also, since the metal magnetic powder is manufactured in a fine powder shape by cooling the metal by using a gas, the proper property of the magnetic metal power may not be maintained. Thus, the metal magnetic powder may have low magnetic permeability. Also, since the magnetic metal power is surrounded by the polymer, the magnetic sheet may have low magnetic permeability. However, since the magnetic layer 110 in accordance with an exemplary embodiment is made of a pure metal and formed in the amorphous state by the quick cooling, the proper property of the magnetic layer 110 may be maintained as it is. Thus, the magnetic layer 110 may have high magnetic permeability. The magnetic layer 110 may have magnetic permeability of, for example, 200 or more, i.e., may have magnetic permeability ranging from 200 to 14,000 in accordance with a kind of material. The magnetic layer 110 may be formed of sendust, i.e., Fe—Al—Si, instead of the metal ribbon. Alternatively, the magnetic layer 110 may be formed of Ni-based or Mn-based ferrite. The Ni-based ferrite may include NiO.ZnO.CuO—Fe2O3, and the Mn-based ferrite may include MnO.ZnO.CuO—Fe2O3. Each of the materials is provided in a plate shape having a predetermined thickness, like the magnetic layer 110, and the plate-shaped materials and the insulation layer 120 may be alternately laminated. Each of the materials may be filled into a through hole 220 defined in a central portion of the base material 200. That is, each of the materials may be filled into the through hole 220 to serve as a magnetic core, and the magnetic layer 110 and the insulation layer 120 may be laminated on top and bottom surfaces of the base material 200.
The insulation layer 120 may be disposed between the magnetic layers 110 to insulate the magnetic layers 110 from each other. Here, the insulation layer 120 may be disposed on the outside of the body 100. That is, the insulation layer 120 may be disposed outside the body 100 to prevent the magnetic layer 110 from contacting the external electrode 400 and a circuit. For this, as described above, the insulation layer 120 may be provided so that the insulation layer 120 has a length and width corresponding to those of the body 100, and the magnetic layer 110 may have a length and width that are less than those of the insulation layer 120. The insulation layer 120 may have the same thickness as the magnetic layer 110. Alternatively, the insulation layer may have a thickness that is greater or less than that of the magnetic layer 110. Here, as a ration of the magnetic layer 110 to the body 100 increases, the magnetic permeability may increase. Thus, it is preferable that the magnetic layer 110 has a thickness greater than that of the insulation layer 120. For example, a thickness ratio between the magnetic layer 110 and the insulation layer 120 may be 1:1 to 3:1. The insulation layer 120 may include at least one selected from the group consisting of epoxy, polyimide, and liquid crystalline polymer (LCP), but is not limited thereto. Also, the insulation layer 120 may be disposed between the magnetic layers 110 and made of a thermosetting resin. For example, the thermosetting resin may include at least one selected from the group consisting of a novolac epoxy resin, a phenoxy type epoxy resin, a BPA type epoxy resin), a BPF type epoxy resin), a hydrogenated BPA epoxy resin), a dimer acid modified epoxy resin, an urethane modified epoxy resin), a rubber modified epoxy resin, and a DCPD type epoxy resin. The bodies 100a and 100b disposed on upper and lower portions of the base material 200 with the base material 200 therebetween may be connected to each other through the base material 200. That is, at least a portion of the base material 200 may be removed to form a through hole 220, and a portion of the body 100 may be filled into the through hole 220. Since the body 100 is filled into the through hole 220 defined in at least a portion of the base material 200, the base material 200 may be reduced in area, and a rate of the body 100 in the same volume may increase to improve the magnetic permeability of the power inductor. Here, the body 100 filled into the through hole 220 may be manufactured by laminating the magnetic layer 110 and the insulation layer 120. In the body 100 filled into the through hole 220, the magnetic layer 110 and the insulation layer 120 may be laminated in a direction parallel to the base material 200. Alternatively, the magnetic layer 110 and the insulation layer 120 may be laminated in a direction perpendicular to the base material 200. That is, in the body 100 filled into the through hole 220, the magnetic layer 110 and the insulation layer 120 may be laminated in a vertical or horizontal direction.
The insulation layer 120 may further include thermal conductive filler (not shown) for releasing heat of the body 100 to the outside. That is, the body 100 may be heated by external heat. Thus, the thermal conductive filler may be provided in the insulation layer 120 to release the heat of the body 100 to the outside. The thermal conductive filler may include at least one selected from the group consisting of MgO, AlN, carbon-based materials, Ni-based ferrite, and Mn-based ferrite, but is not limited thereto. Here, the carbon-based material may include carbon and have various shapes. For example, the carbon-based material may include graphite, carbon black, graphene, and the like. Also, the Ni-based ferrite may include NiO.ZnO.CuO—Fe2O3, and the Mn-based ferrite may include MnO.ZnO.CuO—Fe2O3. Here, the thermal conductive filler may be made of a ferrite material to improve the magnetic permeability or prevent the magnetic permeability from being deteriorated. The thermal conductive filler may be dispersed and contained in the insulation layer 120 in the form of powder. Here, the thermal conductive filler may be contained at a content of 5 wt % to 60 wt % with respect to 100 wt % of a polymer. That is, the thermal conductive filler may be contained at a content of 5 wt % to 60 wt % with respect to 100 wt % of a polymer for forming the insulation layer 120. When the thermal conductive filler has a content less than the above-described range, it may be difficult to obtain a heat releasing effect. On the other hand, when the thermal conductive filler has a content exceeding the above-described range, a content of the insulation layer 120 within the body 100 may be reduced to deteriorate the insulation effect. Also, the thermal conductive filler may have a size of, for example, 0.5 μm to 100 μm. The heat releasing effect may be adjusted in accordance with a size and content of the thermal conductive filler. For example, the more the size and content of the thermal conductive filler increase, the more the heat releasing effect may increase. The body 100 may be manufactured by laminating the magnetic layer 110 and the insulation layer 120. Here, contents of the thermal conductive fillers within the insulation layers 120 may be different from each other. For example, the more the thermal conductive filler is away upward and downward from the center of the base material 200, the more the content of the thermal conductive filler within the insulation layer 120 may increase.
2. Base Material
The base material 200 may be provided in the body 100. For example, the base material 200 may be provided in the body 100 in an X direction of the body 100, i.e., a direction of the external electrode 400. Also, at least one base material 200 may be provided. For example, at least two base materials 200 may be spaced a predetermined distance from each other in a direction perpendicular to a direction in which the external electrode 400 is disposed, i.e., in a vertical direction. Alternatively, at least two base materials 200 may be arranged in the direction in which the external electrode 400 is disposed. For example, the base material 200 may be manufactured by using copper clad lamination (CCL) or a metal magnetic material. Here, the base material 200 may be manufactured by using the metal magnetic material to improve the magnetic permeability and facilitate capacity realization. That is, the CCL is manufactured by bonding copper foil to a glass reinforced fiber. Since the CCL has the magnetic permeability, the power inductor may be deteriorated in magnetic permeability. However, when the metal magnetic material is used as the base material 200, the metal magnetic material may have the magnetic permeability. Thus, the power inductor may not be deteriorated in magnetic permeability. The base material 200 using the metal magnetic material may be manufactured by bonding copper foil to a plate having a predetermined thickness, which is made of a metal containing iron, e.g., at least one metal selected from the group consisting of Fe—Ni, Fe—Ni—Si, Fe—Al—Si, and Fe—Al—Cr. That is, an alloy made of at least one metal containing iron may be manufactured in a plate shape having a predetermined thickness, and copper foil may be bonded to at least one surface of the metal plate to manufacture the base material 200.
Also, at least one conductive via 210 may be formed in a predetermined area of the base material 200. The coil patterns 310 and 320 disposed on the upper and lower portions of the base material 200 may be electrically connected to each other through the conductive via 210. A via (not shown) passing through the base material 200 in a thickness direction of the base material 200 may be formed in the base material 200 and then filled during a plating process for forming the coil pattern 300 to form the conductive via 210. Alternatively, the via may be formed, and then, conductive paste may be filled into the via to form the conductive via. Here, at least one of the coil patterns 310 and 320 may be grown from the conductive via 210. Thus, at least one of the coil patterns 310 and 320 may be integrated with the conductive via 210. Also, at least a portion of the base material 200 may be removed. That is, at least a portion of the base material 200 may be removed or may not be removed. As illustrated in
3. Coil Pattern
The coil pattern 300 (310 and 320) may be disposed on at least one surface, preferably, both side surfaces of the base material 200. Each of the coil patterns 310 and 320 may be formed in a spiral shape on a predetermined area of the base material 200, e.g., outward from a central portion of the base material 200. The two coil patterns 310 and 320 disposed on the base material 200 may be connected to each other to form one coil. That is, each of the coil patterns 310 and 320 may have a spiral shape from the outside of the through hole 220 defined in the central portion of the base material 200. Also, the coil patterns 310 and 320 may be connected to each other through the conductive via 210 provided in the base material 200. Here, the upper coil pattern 310 and the lower coil pattern 320 may have the same shape and the same height. Also, the coil patterns 310 and 320 may overlap each other. Alternatively, the coil pattern 320 may be disposed to overlap an area on which the coil pattern 310 is not disposed. An end of each of the coil patterns 310 and 320 may extend outward in a linear shape and also extend along a central portion of a short side of the body 100. Also, an area of each of the coil patterns 310 and 320 contacting the external electrode 400 may have a width greater than that of the other area as illustrated in
The coil patterns 310 and 320 may be electrically connected to each other by the conductive via 210 provided in the base material 200. The coil patterns 310 and 320 may be formed through methods such as, for example, thick-film printing, coating, deposition, plating, and sputtering. Here, the coil patterns 310 and 320 may preferably formed through the plating. Also, each of the coil patterns 310 and 320 and the conductive via 210 may be made of a material including at least one of silver (Ag), copper (Cu), and a copper alloy, but is not limited thereto. When the coil patterns 310 and 320 are formed through the plating process, a metal layer, e.g., a cupper layer is formed on the base material 200 through the plating process and then patterned through a lithography process. That is, the copper layer may be formed by using the copper foil disposed on the surface of the base material 200 as a seed layer and then patterned to form the coil patterns 310 and 320. Alternatively, a photosensitive pattern having a predetermined shape may be formed on the base material 200, and the plating process may be performed to grow a metal layer from the exposed surface of the base material 200, thereby forming the coil patterns 310 and 320, each of which has a predetermined shape. The coil patterns 310 and 320 may be disposed to form a multilayer structure. That is, a plurality of coil patterns may be further disposed above the coil pattern 310 disposed on the upper portion of the base material 200, and a plurality of coil patterns may be further disposed below the coil pattern 320 disposed on the lower portion of the base material 200. When the coil patterns 310 and 320 have the multilayer structure, the insulation layer may be disposed between a lower layer and an upper layer. Then, the conductive via (not shown) may be formed in the insulation layer to connect the multilayered coil patterns to each other. Each of the coil patterns 310 and 320 may have a height that is greater 2.5 times than a thickness of the base material 200. For example, the base material may have a thickness of 10 μm to 50 μm, and each of the coil patterns 310 and 320 may have a height of 50 μm to 300 μm.
Also, the coil patterns 310 and 320 in accordance with an exemplary embodiment may have a double structure. That is, as illustrated in
Also, the coil pattern 300 may be formed by laminating at least two plated layers. Here, each of the plated layers may have a vertical side surface and be laminated in the same shape and at the same thickness. That is, the coil pattern 300 may be formed on a seed layer through a plating process. For example, three plated layers may be laminated on the seed layer to form the coil pattern 300. The coil pattern 300 may be formed through an anisotropic plating process and have an aspect ratio of approximately 2 to approximately 10.
Also, the coil pattern 300 may have a shape of which a width gradually increases from the innermost circumference to the outermost circumference thereof. That is, the coil pattern 300 having the spiral shape may include n patterns from the innermost circumference to the outermost circumference. For example, when four patterns are provided, the patterns may have widths that gradually increase in order of a first pattern that is disposed on the innermost circumference, a second pattern, a third pattern, and a fourth pattern that is disposed on the outermost circumference. For example, when the width of the first pattern is 1, the second pattern may have a ratio of 1 to 1.5, the third pattern may have a ratio of 1.2 to 1.7, and the fourth pattern may have a ratio of 1.3 to 2. That is, the first to fourth patterns may have a ratio of 1:1 to 1.5:1.2 to 1.7:1.3 to 2. That is, the second pattern may have a width equal to or greater than that of the first pattern, the third pattern may have a width greater than that of the first pattern and equal to or greater than that of the second pattern, and the fourth pattern may have a width greater than that of each of the first and second patterns and equal to or greater than that of the third pattern. The seed layer may have a width that gradually increases from the innermost circumference to the outermost circumference so that the coil pattern has the width that gradually increases from the innermost circumference to the outermost circumference. Also, widths of at least one region of the coil pattern in a vertical direction may be different from each other. That is, a lower end, an intermediate end, and an upper end of the at least one region may have widths different from each other.
4. External Electrode
The external electrodes 410 and 420 (400) may be disposed on two surface facing each other of the body 100. For example, the external electrodes 410 and 420 may be disposed on two side surfaces of the body 100, which face each other in the X direction. The external electrodes 410 and 420 may be electrically connected to the coil patterns 310 and 320 of the body 100, respectively. Also, the external electrodes 410 and 420 may be disposed on the two side surfaces of the body 100 to contact the coil patterns 310 and 320 at central portions of the two side surfaces, respectively. That is, an end of each of the coil patterns 310 and 320 may be exposed to the outer central portion of the body 100, and the external electrode 400 may be disposed on the side surface of the body 100 and then connected to the end of each of the coil patterns 310 and 320. The external electrode 400 may be formed by using conductive paste. That is, both side surfaces of the body 100 may be immersed into the conductive paste, or the conductive paste may be printed on both side surfaces of the body 100 to form the external electrode 400. Also, the external electrode 400 may be formed through various methods such as deposition, sputtering, and plating. The external electrode 400 may be formed on both side surfaces and only the bottom surface of the body 100. Alternatively, the external electrode 400 may be formed on the top surface or front and rear surfaces of the body 100. For example, when the body 100 is immersed into the conductive paste, the external electrode 400 may be formed on both side surfaces in the X direction, the front and rear surfaces in the Y direction, and the top and bottom surfaces in the Z direction. On the other hand, when the external electrode 400 is formed through the methods such as the printing, the deposition, the sputtering, and the plating, the external electrode 400 may be formed on both side surfaces in the X direction and the bottom surface in the Y direction. That is, the external electrode 400 may be formed on other areas in accordance with the formation method or process conditions as well as both side surfaces in the X direction and the bottom surface on which a printed circuit board is mounted. The external electrode 400 may be made of a metal having electrical conductivity, e.g., at least one metal selected from the group consisting of gold, silver, platinum, copper, nickel, palladium, and an alloy thereof. Here, at least a portion of the external electrode 400 connected to the coil pattern 300, i.e., a portion of the external electrode 400 connected to the coil pattern 300 disposed on the surface of the body 100 may be formed of the same material as the coil pattern 300. For example, when the coil pattern 300 is formed by using copper through the plating process, at least a portion of the external electrode 400 may be formed by using copper. Here, as described above, the copper may be deposited or printed through the immersion or printing method using the conductive paste or may be deposited, printed, or plated through the methods such as the deposition, sputtering, and plating. Preferably, the external electrode 400 may be formed through the plating. The seed layer is formed on both side surfaces of the body 100 so that the external electrode 400 is formed through the plating process, and then, the plated layer may be formed from the seed layer to form the external electrode 400. Here, at least a portion of the external electrode 400 connected to the coil pattern 300 may be the entire side surface or a portion of the body 100 on which the external electrode 400 is disposed. The external electrode 400 may further include at least one plated layer. That is, the external electrode 400 may include a first layer connected to the coil pattern 300 and at least plated layer disposed on a top surface of the first layer. For example, the external electrode 400 may further include a nickel-plated layer (not shown) and a tin-plated layer (not shown). That is, the external electrode 400 may have a laminated structure of a copper layer, an Ni-plated layer, and an Sn-plated layer or a laminated structure of a copper layer, an Ni-plated layer, and an Sn/Ag-plated layer. Here, the plated layer may be formed through electrolytic plating or electroless plating. The Sn-plated layer may have a thickness equal to or greater than that of the N-plated layer. For example, the external electrode 400 may have a thickness of 2 μm to 100 μm. Here, the Ni-plated layer may have a thickness of 1 μm to 10 μm, and the Sn or Sn/Ag-plated layer may have a thickness of 2 μm to 10 μm. Also, the external electrode 400 may be formed by mixing, for example, multicomponent glass frit using Bi2O3 or SiO2 of 0.5% to 20% as a main component with metal powder. Here, the mixture of the glass frit and the metal powder may be manufactured in the form of paste and applied to the two surface of the body 100. That is, when a portion of the external electrode 400 is formed by using the conductive paste, the glass frit may be mixed with the conductive paste. As described above, since the glass frit is contained in the external electrode 400, adhesion force between the external electrode 400 and the body 100 may be improved, and a contact reaction between the coil pattern 300 and the external electrode 400 may be improved.
5. Insulation Film
The insulation film 500 may be disposed between the coil patterns 310 and 320 and the body 100 to insulate the coil patterns 310 and 320 from the magnetic layer 110. That is, the insulation film 500 may cover the top and side surfaces of each of the coil patterns 310 and 320. Here, the insulation film 500 may be formed on the top and side surfaces of each of the coil patterns 310 and 320 at substantially the same thickness. For example, the insulation film 500 may have a thickness ratio of 1 to 1.2:1 at the top and side surfaces of each of the coil patterns 310 and 320. That is, each of the coil patterns 310 and 320 may have the top surface having a thickness greater by 20% than that of the side surface. Preferably, the top and side surfaces may have the same thickness. Also, the insulation film 500 may cover the base material 200 exposed by the coil patterns 310 and 320 as well as the top and side surfaces of each of the coil patterns 310 and 320. That is, the insulation film 500 may be formed on an area exposed by the coil patterns 310 and 320 of the base material 200 of which a predetermined region is removed, i.e., a surface and side surface of the base material 200. The insulation film 500 on the base material 200 may have the same thickness as the insulation film 500 on each of the coil patterns 310 and 320. That is, the insulation film 500 on the top surface of the base material 200 may have the same thickness as the insulation film 500 on the top surface of each of the coil patterns 310 and 320, and the insulation film 500 on the side surface of the base material 200 may have the same thickness as the insulation film 500 on the side surface of each of the coil patterns 310 and 320. The parylene may be used so that the insulation layer 500 has substantially the same thickness on the coil patterns 310 and 320 and the base material 200. For example, the base material 200 on which the coil patterns 310 and 320 are formed may be provided in a deposition chamber, and then, the parylene may be evaporated and supplied into the vacuum chamber to deposit the parylene on the coil patterns 310 and 320. For example, the parylene may be primarily heated and evaporated in a vaporizer to become a dimer state and then be secondarily heated and pyrolyzed into a monomer state. Then, when the parylene is cooled by using a cold trap connected to the deposition chamber and a mechanical vacuum pump, the parylene may be converted from the monomer state to a polymer state and thus be deposited on the coil patterns 310 and 320. Alternatively, the insulation film 500 may be formed of an insulation polymer in addition to the parylene, for example, at least one material selected from epoxy, polyimide, and liquid crystal crystalline polymer. However, the parylene may be applied to form the insulation film 500 having the uniform thickness on the coil patterns 310 and 320. Also, although the insulation film 500 has a thin thickness, the insulation property may be improved when compared to other materials. That is, when the insulation film 500 is coated with the parylene, the insulation film 500 may have a relatively thin thickness and improved insulation property by increasing a breakdown voltage when compared to a case in which the insulation film 500 is made of the polyimide. Also, the parylene may be filled between the coil patterns 310 and 320 at the uniform thickness along a gap between the patterns or formed at the uniform thickness along a stepped portion of each of the patterns. That is, when a distance between the patterns of the coil patterns 310 and 320 is far, the parylene may be applied at the uniform thickness along the stepped portion of the pattern. On the other hand, the distance between the patterns is near, the gap between the patterns may be filled to form the parylene at a predetermined thickness on the coil patterns 310 and 320. In case of the parylene, although the parylene has a relatively thin thickness along the stepped portion of each of the coil patterns 310 and 320, the polyimide may have a thickness greater than that of the parylene. The insulation film 500 may have a thickness of 3 μm to 100 μm by using the parylene. When the parylene is formed to a thickness of 3 μm or less, the insulation property may be deteriorated. When the parylene is formed to a thickness exceeding 100 μm, the thickness occupied by the insulation film 500 within the same size may increase to reduce a volume of the body 100, and thus, the magnetic permeability may be deteriorated. Alternatively, the insulation film 500 may be manufactured in the form of a sheet having a predetermined thickness and then formed on the coil patterns 310 and 320.
6. Surface Modification Member
A surface modification member (not shown) may be formed on at least one surface of the body 100. The surface modification member may be formed by dispersing oxide onto the surface of the body 100 before the external electrode 400 is formed. Here, the oxide may be dispersed and distributed onto the surface of the body 100 in a crystalline state or an amorphous state. The surface modification member may be distributed on the surface of the body 100 before the plating process when the external electrode 400 is formed through the plating process. That is, the surface modification member may be distributed before the printing process is performed on a portion of the external electrode 400 or be distributed before the plating process is performed after the printing process is performed. Alternatively, when the printing process is not performed, the plating process may be performed after the surface modification member is distributed. Here, at least a portion of the surface modification member distributed on the surface may be melted.
At least a portion of the surface modification member may be uniformly distributed on the surface of the body with the same size, and at least a portion may be non-uniformly distributed with sizes different from each other. Also, a concave part may be formed in a surface of at least a portion of the body 100. That is, the surface modification member may be formed to form a convex part. Also, at least a portion of an area on which the surface modification member is not formed may be recessed to form the concave part. Here, at least a portion of the surface modification member may be recessed from the surface of the body 100. That is, a portion of the surface modification member, which has a predetermined thickness, may be inserted into the body 100 by a predetermined depth, and the rest portion of the surface modification member may protrude from the surface of the body 100. Here, the portion of the surface modification member, which is inserted into the body 100 by the predetermined depth, may have a diameter corresponding to 1/20 to 1 of a mean diameter of oxide particles. That is, all the oxide particles may be impregnated into the body 100, or at least a portion of the oxide particles may be impregnated. Alternatively, the oxide particles may be formed on only the surface of the body 100. Thus, each of the oxide particles may be formed in a hemispherical shape on the surface of the body 100 and in a globular shape. Also, as described above, the surface modification member may be partially distributed on the surface of the body or distributed in the form of a film on at least one area of the body 100. That is, the oxide particles may be distributed in the form of an island on the surface of the body 100 to form the surface modification member. That is, the oxide particles having the crystalline state or the amorphous state may be spaced apart from each other on the surface of the body 100 and distributed in the form of the island. Thus, at least a portion of the surface of the body 100 may be exposed. Also, at least two oxide particles may be connected to each other to form the film on at least one area of the surface of the body 100 and the island shape on at least a portion of the surface of the body 100. That is, at least two oxide particles may be aggregated, or the oxide particles adjacent to each other may be connected to each other to form the film. However, although the oxide exists in the particle state, or at least two particles are aggregated with or connected to each other, at least a portion of the surface of the body 100 may be exposed to the outside by the surface modification member.
Here, the total area of the surface modification member may correspond to 5% to 90% of the entire area of the surface of the body 100. Although a plating blurring phenomenon on the surface of the body 100 is controlled in accordance with the surface area of the surface modification member, if the surface modification member is widely formed, the contact between the conductive pattern and the external electrode 400 may be difficult. That is, when the surface modification member is formed on an area of 5% or less of the surface area of the body 100, it may be difficult to control the plating blurring phenomenon. When the surface modification member is formed on an area exceeding 90%, the conductive pattern may not contact the external electrode 400. Thus, it is preferable that a sufficient area on which the plating blurring phenomenon of the surface modification member is controlled, and the conductive pattern contacts the external electrode 400 is formed. For this, the surface modification member may be formed with a surface area of 10% to 90%, preferably, 30% to 70%, more preferably, 40% to 50%. Here, the surface area of the body 100 may be a surface area of one surface thereof or a surface area of six surfaces of the body 100, which define a hexahedral shape. The surface modification member may have a thickness of 10% or less of the thickness of the body 100. That is, the surface modification member may have a thickness of 0.01% to 10% of the thickness of the body 100. For example, the surface modification member may have a size of 0.1 μm to 50 μm. Thus, the surface modification member may have a thickness of 0.1 μm to 50 μm from the surface of the body 100. That is, the surface modification member may have a thickness of 0.1% to 50% of the thickness of the body 100 except for the portion inserted from the surface of the body 100. Thus, the surface modification member may have a thickness greater than that of 0.1 μm to 50 μm when the thickness of the portion inserted into the body 100 is added. That is, when the surface modification member has a thickness of 0.01% or less of the thickness of the body 100, it may be difficult to control the plating blurring phenomenon. When the surface modification member has a thickness exceeding 10%, the conductive pattern within the body 100 may not contact the external electrode 400. That is, the surface modification member may have various thicknesses in accordance with material properties (conductivity, semiconductor properties, insulation, magnetic materials, and the like) of the body 100. Also, the surface modification member may have various thicknesses in accordance with sizes, distributed amount, whether the aggregation occurs, and the like) of the oxide powder.
Since the surface modification member is formed on the surface of the body 100, two areas, which are mode of components different from each other, of the surface of the body 100 may be provided. That is, components different from each other may be detected from the area on which the surface modification member is formed and the area on which the surface modification member is not formed. For example, a component due to the surface modification member, i.e., oxide may exist on the area on which the surface modification member is formed, and a component due to the body 100, i.e., a component of the sheet may exist on the area on which the surface modification member is not formed. Since the surface modification member is distributed on the surface of the body before the plating process, roughness may be given to the surface of the body 100 to modify the surface of the body 100. Thus, the plating process may be uniformly performed, and thus, the shape of the external electrode 400 may be controlled. That is, resistance on at least an area of the surface of the body 100 may be different from that on the other area of the surface of the body 100. When the plating process is performed in a state in which the resistance is non-uniform, ununiformity in growth of the plated layer may occur. To solve this limitation, the oxide that is in a particle state or melted state may be dispersed on the surface of the body 100 to form the surface modification member, thereby modifying the surface of the body 100 and controlling the growth of the plated layer.
Here, at least one oxide may be used as the oxide, which is in the particle or melted state, for realizing the uniform surface resistance of the body 100. For example, at least one of Bi2O3, BO2, B2O3, ZnO, Co3O4, SiO2, Al2O3, MnO, H2BO3, Ca(CO3)2, Ca(NO3)2, and CaCO3 may be used as the oxide. The surface modification member may be formed on at least one sheet within the body 100. That is, the conductive pattern having various shapes on the sheet may be formed through the plating process. Here, the surface modification member may be formed to control the shape of the conductive pattern.
7. Insulation Capping Layer
As illustrated in
As described above, in the power inductor in accordance with an exemplary embodiment, the body 100 may be manufactured by alternately laminating the magnetic layer 110 and the insulation layer 120. Also, the magnetic layer 110 may be formed by using the amorphous metal ribbon. Thus, since the magnetic layer 110 has a predetermined thickness, the body 100 may be improved in magnetic permeability when compared to the body in accordance with the related art, in which the metal magnetic powder is dispersed in the polymer. Also, since the insulation film 500 is formed between the coil patterns 310 and 320 and the body 100 by using the parylene, the insulation layer 500 may be formed with a thin thickness on the side surface and the top surface of each of the coil patterns 310 and 320 to improve the insulation property. Also, since the base material 200 within the body 100 is made of the metal magnetic material, the decreases of the magnetic permeability of the power inductor may be prevented. Also, at least a portion of the base material 200 may be removed, and the body 100 may be filled into the removed portion to improve the magnetic permeability.
The power inductor in accordance with an exemplary embodiment may be variously modified by forming at least a portion of the body 100 by using the magnetic layer 110. A power inductor in accordance with another exemplary embodiment will be described with reference to
Referring to
The second magnetic layers 610 and 620 (600) may be disposed on at least one area of the body 100. That is, the second-1 magnetic layer 610 may be disposed on the top surface of the body 100, and the second-2 magnetic layer 620 may be disposed on the bottom surface of the body 100. Here, the second magnetic layer 600 may be provided to more improve magnetic permeability of the body 100. Thus, the second magnetic layer 600 may be made of a material having magnetic permeability grater than that of the insulation layer 120. That is, the second magnetic layer 600 may be formed instead of at least one insulation layer 120. The second magnetic layer 600 may be manufactured by using, for example, metal magnetic powder and polymer. Here, the polymer may be added to a content of 15 wt % with respect to 100 wt % of the metal magnetic powder. Also, the metal magnetic powder may use at least one selected from the group consisting of Ni ferrite, Zn ferrite, Cu ferrite, Mn ferrite, Co ferrite, Ba ferrite and Ni—Zn—Cu ferrite or at least one oxide magnetic material thereof. That is, the second magnetic layer 600 may be formed by using metal alloy power including iron or metal alloy oxide containing iron. Also, a magnetic material may be applied to the metal alloy powder to form magnetic powder. For example, at least one oxide magnetic material selected from the group consisting of a Ni oxide magnetic material, a Zn oxide magnetic material, a Cu oxide magnetic material, a Mn oxide magnetic material, a Co oxide magnetic material, a Ba oxide magnetic material, and a Ni—Zn—Cu oxide magnetic material may be applied to the metal alloy powder including iron to form the magnetic powder. That is, the metal oxide including iron may be applied to the metal alloy powder to form the magnetic powder. Alternatively, at least one oxide magnetic material selected from the group consisting of a Ni oxide magnetic material, a Zn oxide magnetic material, a Cu oxide magnetic material, a Mn oxide magnetic material, a Co oxide magnetic material, a Ba oxide magnetic material, and a Ni—Zn—Cu oxide magnetic material may be mixed with the metal alloy powder including iron to form the magnetic powder. That is, the metal oxide including iron may be mixed with the metal alloy powder to form the magnetic powder. The second magnetic layer 600 may further include a thermal conductive filler in addition to the metal magnetic powder and the polymer. Here, the thermal conductive filler may have a content of 0.5 wt % to 3 wt % with respect to 100 wt % of the metal magnetic powder. The second magnetic layer 600 may be manufactured in the form of a sheet and disposed on each of the top and bottom surfaces of the body 100 on which the plurality of magnetic layers 110 and the insulation layer 120 are laminated. Also, the second magnetic layer 600 may be formed by using paste. That is, a magnetic material may be applied to the top and bottom surfaces of the body 100 to form the second magnetic layer 600.
As described above, the at least one second magnetic layer 600 may be disposed on the body 100 to improve the magnetic permeability of the power inductor. That is, the second magnetic layer 600 instead of at least one insulation layer 120 may be provided to more improve the magnetic permeability of the power inductor.
As illustrated in
As illustrated in
As illustrated in
As illustrated in
As illustrated in
As illustrated in
As illustrated in
As illustrated in
Referring to
The at least two base materials 200a and 200b (200) may be provided in the body 100 and spaced a predetermined distance from each other a short axial direction of the body 100. That is, the at least two base materials 200 may be spaced a predetermined distance from each other in a direction perpendicular to the external electrode 400, i.e., in a thickness direction of the body 100. Also, conductive vias 210a and 210b (210) may be formed in the at least two base materials 200, respectively. Here, at least a portion of each of the at least two base materials 200 may be removed to form each of through holes 220a and 220b (220). Here, the through holes 220a and 220b may be formed in the same position, and the conductive vias 210a and 210b may be formed in the same position or positions different from each other. Alternatively, an area of the at least two base materials 200, in which the through holes 220 and the coil patterns 300 are not provided, may be removed, and then, the body 100 may be filled. The body 100 may be disposed between the at least two base materials 200. The body 100 may be disposed between the at least two base materials 200 to improve magnetic permeability of the power inductor. Alternatively, since the insulation film 500 is disposed on the coil pattern 300 disposed on the at least two base materials 200, the body 100 may not be provided between the base materials 200. In this case, the power inductor may be reduced in thickness.
The coil patterns 310, 320, 330, and 340 (300) may be disposed on at least one surface of each of the at least two base materials 200, preferably, both surfaces of each of the at least two base materials 200. Here, the coil patterns 310 and 320 may be disposed on lower and upper portions of a first substrate 200a and electrically connected to each other by the conductive via 210a provided in the first base material 200a. Similarly, the coil patterns 330 and 340 may be disposed on lower and upper portions of a second substrate 200b and electrically connected to each other by the conductive via 210b provided in the second base material 200b. Each of the plurality of coil patterns 300 may be formed in a spiral shape on a predetermined area of the base material 200, e.g., outward from the through holes 220a and 220b in a central portion of the base material 200. The two coil patterns 310 and 320 disposed on the base material 200 may be connected to each other to form one coil. That is, at least two coils may be provided in one body 100. Here, the upper coil patterns 310 and 330 and the lower coil patterns 320 and 340 of the base material 200 may have the same shape. Also, the plurality of coil patterns 300 may overlap each other. Alternatively, the lower coil patterns 320 and 340 may be disposed to overlap an area on which the upper coil patterns 310 and 330 are not disposed.
The external electrodes 410 and 420 (400) may be disposed on both ends of the body 100. For example, the external electrodes 400 may be disposed on two side surfaces of the body 100, which face each other in a longitudinal direction. The external electrode 400 may be electrically connected to the coil patterns 300 of the body 100. That is, at least one end of each of the plurality of coil patterns 300 may be exposed to the outside of the body 100, and the external electrode 400 may be connected to the end of each of the plurality of coil patterns 300. For example, the external electrode 410 may be connected to the coil pattern 310, and the external pattern 420 may be connected to the coil pattern 340. That is, the external electrodes 400 may be respectively connected to the coil patterns 310 and 340 disposed on the base materials 200a and 200b.
The connection electrode 700 may be disposed on at least one side surface of the body 100, on which the external electrode 400 is not provided. For example, the external electrode 400 may be disposed on each of first and second side surfaces facing each other, and the connection electrode 700 may be disposed on each of third and fourth side surfaces on which the external electrode 400 is not provided. The connection electrode 700 may be provided to connect at least one of the coil patterns 310 and 320 disposed on the first base material 200a to at least one of the coil patterns 330 and 340 disposed on the second base material 200b. That is, the connection electrode 710 may connect the coil pattern 320 disposed below the first base material 200a to the coil pattern 330 disposed above the second base material 200b at the outside of the body 100. That is, the external electrode 410 may be connected to the coil pattern 310, the connection electrode 710 may connect the coil patterns 320 and 330 to each other, and the external electrode 420 may be connected to the coil pattern 340. Thus, the coil patterns 310, 320, 330, and 340 disposed on the first and second base materials 200a and 200b may be connected to each other in series. Although the connection electrode 710 connects the coil patterns 320 and 330 to each other, the connection electrode 720 may not be connected to the coil patterns 300. This is done because, for convenience of processes, two connection electrodes 710 and 720 are provided, and only one connection electrode 710 is connected to the coil patterns 320 and 330. The connection electrode 700 may be formed by immersing the body 100 into conductive paste or formed on one side surface of the body 100 through various methods such as printing, deposition, and sputtering. The connection electrode 700 may include a metal have electrical conductivity, e.g., at least one metal selected from the group consisting of gold, silver, platinum, copper, nickel, palladium, and an alloy thereof. Here, a nickel-plated layer (not show) and a tin-plated layer (not shown) may be further disposed on a surface of the connection electrode 700.
As described above, in the power inductor in accordance with further another exemplary embodiment and the modified example, the at least two base materials 200 on which each of the coil patterns 300 is disposed on at least one surface may be spaced apart from each other within the body 100, and the coil pattern 300 disposed on the other base material 200 may be connected by the connection electrode 700 outside the body 100. As a result, the plurality of coil patterns may be provided within one body 100, and thus, the power inductor may increase in capacity. That is, the coil patterns 300 respectively disposed on the base materials 200 different from each other may be connected to each other in series by using the connection electrode 700 outside the body 100, and thus, the power inductor may increase in capacity on the same area.
Referring to
At least two, e.g., three base materials 200a, 200b, and 200c (200) may be provided in the body 100. Here, the at least two base materials 200 may be spaced a predetermined distance from each other in a longitudinal direction that is perpendicular to a thickness direction of the body 100. That is, in the further another exemplary embodiment and the modified example, the plurality of base materials 200 are arranged in the thickness direction of the body 100, e.g., in a vertical direction. However, in the current embodiment, the plurality of base materials 200 may be arranged in a direction perpendicular to the thickness direction of the body 100, e.g., a horizontal direction. Also, conductive vias 210a, 210b, and 210c (210) may be formed in the plurality of base materials 200, respectively. Here, at least a portion of each of the plurality of base materials 200 may be removed to form each of through holes 220a, 220b, and 220c (220). Alternatively, an area of the plurality of base materials 200, in which the through holes 220 and the coil patterns 300 are not provided, may be removed as illustrated in
The coil patterns 310, 320, 330, 340, 350, and 360 (300) may be disposed on at least one surface of each of the plurality of base materials 200, preferably, both surfaces of each of the plurality of base materials 200. Here, the coil patterns 310 and 320 may be disposed on one surface and the other surface of a first substrate 200a and electrically connected to each other by the conductive via 210a provided in the first base material 200a. Also, the coil patterns 330 and 340 may be disposed on one surface and the other surface of a second substrate 200b and electrically connected to each other by the conductive via 210b provided in the second base material 200b. Similarly, the coil patterns 350 and 360 may be disposed on one surface and the other surface of a third substrate 200c and electrically connected to each other by the conductive via 210c provided in the third base material 200c. Each of the plurality of coil patterns 300 may be formed in a spiral shape on a predetermined area of the base material 200, e.g., outward from the through holes 220a, 220b, and 200c in a central portion of the base material 200. The two coil patterns 310 and 320 disposed on the base material 200 may be connected to each other to form one coil. That is, at least two coils may be provided in one body 100. Here, the coil patterns 310, 330, and 350 that are disposed on one side of the base material 200 and the coil patterns 320, 340, and 360 that are disposed on the other side of the base material 200 may have the same shape. Also, the coil patterns 300 may overlap each other on the same base material 200. Alternatively, the coil patterns 320, 330, and 350 that are disposed on the one side of the base material 200 may be disposed to overlap an area on which the coil patterns 320, 340, and 360 that are disposed on the other side of the base material 200 are not disposed.
The external electrodes 410, 420, 430, 440, 450, and 460 (400) may be spaced apart from each other on both ends of the body 100. The external electrode 400 may be electrically connected to the coil patterns 300 respectively disposed on the plurality of base materials 200. For example, the external electrodes 410 and 420 may be respectively connected to the coil patterns 310 and 320, the external electrode 430 and 440 may be respectively connected to the coil patterns 330 and 340, and the external electrodes 450 and 460 may be respectively connected to the coil patterns 350 and 360. That is, the external electrodes 400 may be respectively connected to the coil patterns 300 and 340 disposed on the base materials 200a, 200b, and 200c.
As described above, in the power inductor in accordance with further another exemplary embodiment, the plurality of inductors may be realized in one body 100. That is, the at least two base materials 200 may be arranged in the horizontal direction, and the coil patterns 300 respectively disposed on the base materials 200 may be connected to each other by the external electrodes different from each other. Thus, the plurality of inductors may be disposed in parallel, and at least two power inductors may be provided in one body 100.
Referring to
As described above, in accordance with the foregoing embodiment, the plurality of base materials 200, on which the coil patterns 300 disposed on the at least one surface within the body 10 are disposed, may be laminated in the thickness direction (i.e., the vertical direction) of the body 100 or arranged in the direction perpendicular to (the horizontal direction) the body 100. Also, the coil patterns 300 respectively disposed on the plurality of base materials 200 may be connected to the external electrodes 400 in series or parallel. That is, the coil patterns 300 respectively disposed on the plurality of base materials 200 may be connected to the external electrodes 400 different from each other and arranged in parallel, and the coil patterns 300 respectively disposed on the plurality of base materials 200 may be connected to the same external electrode 400 and arranged in series. When the coil patterns 300 are connected in series, the coil patterns 300 respectively disposed on the base materials 200 may be connected to the connection electrodes 700 outside the body 100. Thus, when the coil patterns 300 are connected in parallel, two external electrodes 400 may be required for the plurality of base materials 200. When the coil patterns 300 are connected in series, two external electrodes 400 and at least one connection electrode 700 may be required regardless of the number of base materials 200. For example, when the coil patterns 300 disposed on the three base materials 200 are connected to the external electrodes in parallel, six external electrodes 400 may be required. When the coil patterns 300 disposed on the three base materials 200 are connected in series, two external electrodes 400 and at least one connection electrode 700 may be required. Also, when the coil patterns 300 are connected in parallel, a plurality of coils may be provided within the body 100. When the coil patterns 300 are connected in series, one coil may be provided within the body 100.
Referring to
Referring to
Referring to
The present invention may, however, be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the present invention to those skilled in the art. Further, the present invention is only defined by scopes of claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2015-0144935 | Oct 2015 | KR | national |
| 10-2016-0126742 | Sep 2016 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2016/011501 | 10/13/2016 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2017/065528 | 4/20/2017 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5583474 | Mizoguchi | Dec 1996 | A |
| 20050068150 | Matsutani et al. | Mar 2005 | A1 |
| 20060290460 | Waffenschmidt | Dec 2006 | A1 |
| 20090003191 | Inuzuka et al. | Jan 2009 | A1 |
| 20100182116 | Ishimoto | Jul 2010 | A1 |
| 20140167897 | Choi et al. | Jun 2014 | A1 |
| 20140191838 | Yoshida | Jul 2014 | A1 |
| 20140266543 | Park | Sep 2014 | A1 |
| 20150002255 | Kim et al. | Jan 2015 | A1 |
| 20150270053 | Cha | Sep 2015 | A1 |
| 20150287516 | Park | Oct 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 1407564 | Apr 2003 | CN |
| 1993780 | Jul 2007 | CN |
| 101447275 | Jun 2009 | CN |
| 100580825 | Jan 2010 | CN |
| 1993780 | May 2010 | CN |
| 103180919 | Jun 2013 | CN |
| 202996472 | Jun 2013 | CN |
| 103383886 | Nov 2013 | CN |
| 104051145 | Sep 2014 | CN |
| 104347228 | Feb 2015 | CN |
| 104766715 | Jul 2015 | CN |
| H0955316 | Feb 1997 | JP |
| 2001102235 | Apr 2001 | JP |
| 2007503716 | Feb 2007 | JP |
| 2007287904 | Nov 2007 | JP |
| 2010087030 | Apr 2010 | JP |
| 2010278301 | Dec 2010 | JP |
| 2011124420 | Jun 2011 | JP |
| 2012235080 | Nov 2012 | JP |
| 2012248629 | Dec 2012 | JP |
| 2013062459 | Apr 2013 | JP |
| 2014130988 | Jul 2014 | JP |
| 2014183307 | Sep 2014 | JP |
| 2015032625 | Feb 2015 | JP |
| 2016143887 | Aug 2016 | JP |
| 20070032259 | Mar 2007 | KR |
| 20140077346 | Jun 2014 | KR |
| 20140085997 | Jul 2014 | KR |
| 20150080800 | Jul 2015 | KR |
| 2007119426 | Oct 2007 | WO |
| Entry |
|---|
| Extended European Search Report for Application No. 16855745.2 dated May 22, 2019. |
| International Search Report for PCT/KR2016/011501 dated Jan. 10, 2017. |
| Written Opinion for PCT/KR2016/011501 dated Jan. 10, 2017. |
| Number | Date | Country | |
|---|---|---|---|
| 20180308612 A1 | Oct 2018 | US |