Claims
- 1. A process for sputter coating a substrate in a cathode sputtering apparatus having an alloy target, said process comprising
- selecting a target alloy having gold in a range of 90 to 98 percent by weight and aluminum in a range of 0.5 to 10 percent by weight, the balance comprising copper; and
- sputter coating said substrate with said alloy.
- 2. The process of claim 1 wherein said target alloy is chosen to produce a standard gold color in the substrate coating, said standard color coating being defined by CIELAB units of luster L.sup.* in a range of 85 to 90, redness a.sup.* in a range of 0.5 to 3, and yellowness b.sup.* in a range of 26 to 30.
- 3. The process of claim 11 wherein said target alloy is selected to have aluminum in a range of 0.5 to 5 percent by weight.
- 4. The process of claim 11 wherein said target alloy is selected to have gold in a range of 94 to 98 percent by weight.
- 5. The process of claim 11 wherein said target alloy is selected to have a balance consisting of copper.
- 6. The process of claim 11 wherein said target alloy is selected to have a balance consisting of copper and at least one additional alloy component selected from the group consisting of Co, Ni, Ga, Ti, In, Cd, Sn, Fe and Pd, each additional alloy component being present in said alloy in a range of 0.1 to 5 percent by weight, the total of said additional alloy components not exceeding 6 percent by weight.
- 7. A cathode sputtering apparatus comprising a target of an alloy having gold in a range of 90 to 98 percent by weight and aluminum in a range of 0.5 to 10 percent by weight, the balance comprising copper, whereby, a substrate placed in said apparatus may be sputter coated with said alloy.
- 8. Apparatus as in claim 7 wherein said target alloy is chosen to produce a standard gold color in the substrate coating, said standard color coating being defined by CIELAB units of luster L.sup.* in a range of 85 to 90, redness a.sup.* in a range of 0.5 to 3, and yellowness b.sup.* in a range of 26 to 30.
- 9. Apparatus as in claim 7 wherein said target alloy is selected to have aluminum in a range of 0.5 to 5 percent by weight.
- 10. Apparatus as in claim 7 wherein said target alloy is selected to have gold in a range of 94 to 98 percent by weight.
- 11. Apparatus as in claim 7 wherein said target alloy is selected to have a balance consisting of copper.
- 12. Apparatus as in claim 7 wherein said target alloy is selected to have a balance consisting of copper and at least one additional alloy component selected from the group consisting of Co, Ni, Ga, Ti, In, Cd, Sn, Fe and Pd, each additional alloy component being present in said alloy in a range of 0.1 to 5 percent by weight, the total of said additional alloy components not exceeding 6 percent by weight.
Priority Claims (1)
Number |
Date |
Country |
Kind |
3631830 |
Sep 1986 |
DEX |
|
Parent Case Info
This is a divisional of prior application Ser. No. 921,235, filed on Oct. 20, 1986, now U.S. Pat. No. 4,808,373, issued Feb. 28, 1989.
US Referenced Citations (4)
Divisions (1)
|
Number |
Date |
Country |
Parent |
921235 |
Oct 1986 |
|