The present invention generally relates to processing of materials for growth of crystals. More particularly, the present invention provides a method for obtaining a gallium-containing nitride crystal by an ammonobasic or ammonoacidic technique, but there can be others. In other embodiments, the present invention provides an apparatus for large scale processing of nitride crystals, but it would be recognized that other crystals and materials can also be processed. Such crystals and materials include, but are not limited to, GaN, AlN, InN, InGaN, AlGaN, and AlInGaN, and others for manufacture of bulk or patterned substrates. Such bulk or patterned substrates can be used for a variety of applications including optoelectronic devices, lasers, light emitting diodes, solar cells, photoelectrochemical water splitting and hydrogen generation, photodetectors, integrated circuits, and transistors, among other devices.
Gallium nitride containing crystalline materials serve as a starting point for manufacture of conventional optoelectronic devices, such as blue light emitting diodes and lasers. Such optoelectronic devices have been commonly manufactured on sapphire or silicon carbide substrates that differ in composition from the deposited nitride layers. In the conventional Metal-Organic Chemical Vapor Deposition (MOCVD) method, deposition of GaN is performed from ammonia and organometallic compounds in the gas phase. Although successful, conventional growth rates achieved make it difficult to provide a bulk layer of GaN material. Additionally, dislocation densities are also high and lead to poorer optoelectronic device performance.
Other techniques have been proposed for obtaining bulk monocrystalline gallium nitride. Such techniques include use of epitaxial deposition employing halides and hydrides in a vapor phase and is called Hydride Vapor Phase Epitaxy (HVPE) [“Growth and characterization of freestanding GaN substrates” K. Motoku et al., Journal of Crystal Growth 237-239, 912 (2002)]. Unfortunately, drawbacks exist with HVPE techniques. In some cases, the quality of the bulk monocrystalline gallium nitride is not generally sufficient for high quality laser diodes because of issues with dislocation density, stress, and the like.
Techniques using supercritical ammonia have been proposed. Peters has described the ammonothermal synthesis of aluminum nitride [J. Cryst. Growth 104, 411-418 (1990)]. R. Dwiliński et al. have shown, in particular, that it is possible to obtain a fine-crystalline gallium nitride by a synthesis from gallium and ammonia, provided that the latter contains alkali metal amides (KNH2 or LiNH2). These and other techniques have been described in “AMMONO method of BN, AlN, and GaN synthesis and crystal growth”, Proc. EGW-3, Warsaw, Jun. 22 24, 1998, MRS Internet Journal of Nitride Semiconductor Research, http://nsr.mij.mrs.org/3/25, “Crystal growth of gallium nitride in supercritical ammonia” J. W. Kolis et al., J. Cryst. Growth 222, 431-434 (2001), and Mat. Res. Soc. Symp. Proc. Vol. 495, 367-372 (1998) by J. W. Kolis et al. However, using these supercritical ammonia processes, no wide scale production of bulk monocrystalline was achieved.
Dwiliński, in U.S. Pat. Nos. 6,656,615 and 7,335,262, and D′Evelyn, in U.S. Pat. Nos. 7,078,731 and 7,101,433, discuss apparatus and methods for conventional ammonothermal crystal growth of GaN. These methods are useful for growth of relatively small GaN crystals. Unfortunately, such methods have limitations for large scale manufacturing. The conventional apparatus with an inner diameter of 40 mm is useful for growing smaller diameter GaN crystals but is not suitable for large scale growth of GaN boules. Additionally, conventional suspension of seed crystals using wires passing through single laser-drilled holes may be adequate for small crystals but is likely to be tedious and ineffective for large scale manufacturing. Other limitations may also exist.
From the above, it is seen that techniques for large scale crystal growth are highly desired.
According to the present invention, techniques related to processing of materials for growth of crystal are provided. More particularly, the present invention provides a method for obtaining a gallium-containing nitride crystal by an ammonobasic technique, but there can be others. In other embodiments, the present invention provides an apparatus for large scale processing of nitride crystals, but it would be recognized that other crystals and materials can also be processed. Such crystals and materials include, but are not limited to, GaN, AlN, InN, InGaN, AlGaN, and AlInGaN, and others for manufacture of bulk or patterned substrates. Such bulk or patterned substrates can be used for a variety of applications including optoelectronic devices, lasers, light emitting diodes, solar cells, photoelectrochemical water splitting and hydrogen generation, photodetectors, integrated circuits, and transistors, among other devices.
In a specific embodiment, the present invention provides a method for growth of a gallium-containing nitride crystal, e.g., GaN. The method includes providing gallium-containing source material and providing a mineralizer. In a specific embodiment, the method includes providing at least two seed plates, including a first seed plate and a second seed plate. The method includes supporting the first seed plate and the second seed plate in a first site and a second site of a seed rack. In a preferred embodiment, the first seed plate and the second seed plate have substantially an equivalent crystallographic orientation to within five degrees. Each of the first seed plate and the second seed plate have a length of at least 1 centimeter according to a specific embodiment. The method includes placing the source material, mineralizer, and seed plates in a sealable container and introducing a nitrogen containing solvent into the sealable container. In a specific embodiment, the method includes processing the source material, mineralizer, and seed plates contained in the sealable container in a supercritical fluid at a temperature higher than about 400 degrees Celsius and a pressure higher than about 2 kbar.
In an alternative specific embodiment, the present invention provides a method for growth a gallium-containing nitride crystal. The method includes providing gallium-containing source material and providing a mineralizer. The method also includes providing at least a first seed plate and a second seed plate. In a specific embodiment, the first seed plate has a first side having a first crystallographic orientation and a second side has a second crystallographic orientation. In a specific embodiment, the second seed plate has a first side having a first crystallographic orientation and a second side has a second crystallographic orientation. In a specific embodiment, the method also includes supporting the first seed plate and the second seed plate such that the first side of the first seed crystal faces the first side of the second seed crystal and spaced by a predetermined gap between the first side of the first seed crystal and the first side of the second seed crystal. The method includes placing the source material, mineralizer, and the seed plates in a sealable container. The method introduces a nitrogen-containing solvent in the sealable container and processes the source material, mineralizer, and seed plates contained in the sealable container in a supercritical fluid at a temperature higher than about 400 degrees Celsius and a pressure higher than about 2 kbar.
Still further, the present invention provides a method for growth a gallium-containing nitride crystal, e.g., GaN. The method includes providing gallium-containing source material. In a specific embodiment, the method also includes providing a mineralizer and providing at least a first seed plate and a second seed plate. In a specific embodiment, the first seed plate has a first side having a first a-plane crystallographic orientation and a second side has a second a-plane crystallographic orientation. In a specific embodiment, the second seed plate has a first side having a first a-plane crystallographic orientation and a second side has a second a-plane crystallographic orientation. In a specific embodiment, the method includes supporting the first seed plate and the second seed plate. Each of the first seed plate and the second seed plate has a length of at least 1 centimeters according to a specific embodiment. In a specific embodiment, the method includes placing the source material, mineralizer, and the seed plates in a sealable container and introducing a nitrogen-containing solvent in the sealable container. In a preferred embodiment, the method includes processing the source material, mineralizer, and seed plates contained in the sealable container in a supercritical fluid at a temperature higher than about 400 degrees Celsius and a pressure higher than about 2 kbar. The method causes any spatial portion of the first side or the second side of the first seed plate or the first side or the second side of the second seed plate to change in character from an a-plane characteristic to an m-plane orientation characteristic. Preferably, the method also generally thickens each of the seed plates by way of crystal growth.
Benefits are achieved over pre-existing techniques using the present invention. In particular, the present invention enables a cost-effective high pressure apparatus for growth of crystals such as GaN, AlN, InN, InGaN, and AlInGaN and others. In a specific embodiment, the present method and apparatus can operate with components that are relatively simple and cost effective to manufacture. Depending upon the embodiment, the present apparatus and method can be manufactured using conventional materials and/or methods according to one of ordinary skill in the art. The present apparatus and method enable cost-effective crystal growth and materials processing under extreme pressure and temperature conditions in batch volumes larger than 0.3 liters, larger than 1 liter, larger than 3 liters, larger than 10 liters, larger than 30 liters, larger than 100 liters, and larger than 300 liters according to a specific embodiment. Depending upon the embodiment, one or more of these benefits may be achieved. These and other benefits may be described throughout the present specification and more particularly below.
The present invention achieves these benefits and others in the context of known process technology. However, a further understanding of the nature and advantages of the present invention may be realized by reference to the latter portions of the specification and attached drawings.
a and 1b are crystal growth frame structures according to embodiments of the present invention.
a, 2b, and 2c are crystal growth seed rack structures according to embodiments of the present invention.
a and 3b are simplified diagrams illustrating processing methods for crystal growth apparatus according to embodiments of the present invention.
a, 4b, and 4c are simplified diagrams illustrating crystal growth processes according to embodiments of the present invention.
a and 6b are simplified diagrams illustrating a recycling operation for crystal growth according to embodiments of the present invention.
According to the present invention, techniques related to processing of materials for growth of crystal are provided. More particularly, the present invention provides a method for obtaining a gallium-containing nitride crystal by an ammonobasic or ammonoacidic technique, but there can be others. In other embodiments, the present invention provides an apparatus for large scale processing of nitride crystals, but it would be recognized that other crystals and materials can also be processed. Such crystals and materials include, but are not limited to, GaN, AlN, InN, InGaN, AlGaN, and AlInGaN, and others for manufacture of bulk or patterned substrates. Such bulk or patterned substrates can be used for a variety of applications including optoelectronic devices, lasers, light emitting diodes, solar cells, photoelectrochemical water splitting and hydrogen generation, photodetectors, integrated circuits, and transistors, among other devices.
In the discussion that follows, the present apparatus is described as being vertically oriented. In another embodiment, the apparatus is instead horizontally oriented or oriented at an oblique angle intermediate between vertical and horizontal, and may be rocked so as to facilitate convection of the supercritical fluid within the high pressure apparatus. The present methods may be used in conjunction with a sealable container and high pressure apparatus. Examples of representative applicable apparatus are described in U.S. Pat. Nos. 7,101,433, 7,125,453, and 7,160,388, in U.S. Published Patent Application No. 200601777362, and in U.S. Patent Application No. 61/073,687, Ser. Nos. 12/133,365 and 12/133,364, all of which are hereby incorporated by reference in their entirety. Reference should also be made to
A schematic of a frame for seed crystals and raw material is shown in
The frame may include, as components, a baffle, a raw material basket, and a rack for suspending seed crystal plates, plus a means for attaching at least two of the aforementioned components. In one set of embodiments, illustrated in
The baffle provides a means for dividing the high pressure apparatus into which the frame is to be inserted into two separate regions, and comprises one or more disks. The two regions are in fluid communication with each other, as the baffle has a plurality of through-holes, or openings. Thus, a fraction of the cross-sectional area of the baffle is open. In a specific embodiment, the baffle has a fractional open area of between about 0.5% and about 30%, but can also have other percentages. In other embodiments, the baffle has a fractional open area between 2% and 20%, or between 5% and 15%. Baffle serves the purpose of confining the at least one (or more) source material to a specific region or end of chamber 108 while permitting solvent and, under high pressure high temperature (HPHT) conditions, supercritical fluid, to migrate throughout the high pressure apparatus by passing freely through through-holes in baffle. Often times, this feature is particularly useful in applications such as crystal growth, in which the supercritical fluid transports the at least one material, a nutrient material, from one region of the chamber, defined by placement of baffle, to another region where crystal growth on seed crystals take place. In one specific embodiment, the diameter of the baffle is equal to the maximum diameter of the overall frame. In other embodiments, the diameter of the baffle is slightly less than the maximum diameter of the overall frame, providing an annular space through which fluid can flow under crystal growth conditions. The diameter of the baffle may be less than the maximum diameter of the overall frame by 0.5 inch or less. The openings in the baffle should be large enough so as not to clog readily. In one specific embodiment, the diameters of the openings in the baffle are between 0.020 inch and 0.5 inch. In another embodiment, the diameters of the openings in the baffle are between 0.050 inch and 0.25 inch. In one specific embodiment, the baffle comprises a single disk with a thickness between 0.020 inch and 0.5 inch. In another embodiment, the baffle comprises a single disk with a thickness between 0.050 inch and 0.25 inch. In some embodiments, the baffle comprises two disks, three disks, or more. In some multi-disk embodiments one or more of the openings in the disks lie above one another. In other multi-disk embodiments, one or more of the openings in the disks do not lie above one another. The effective fractional open area in multi-disk baffle embodiments may therefore lie between the fractional open area of each disk, as an upper bound, and the product of the fractional open areas of each disk.
The raw material basket provides a convenient means for transferring the raw material, including source material and mineralizer, into the high pressure apparatus, for permitting facile fluid communication from the region between source material particles within the basket and the crystal growth region, and for removing un-consumed source material from the reactor at the conclusion of a growth run. In one embodiment, the basket comprises wire mesh or wire cloth, as indicated schematically in the Figures. The diameter of the wire in the mesh or cloth may be between 0.001 inch and 0.25 inch, between 0.005 inch and 0.125 inch, or between 0.010 inch and 0.080 inch. The wire mesh or wire cloth may be contained within and, optionally, attached to a frame comprising larger-diameter wire so as to provide improved mechanical support. In another embodiment, the basket comprises foil or plate with a plurality of through-holes or openings. The size of the openings in the wire mesh, wire cloth, or foil or plate should be small enough so that raw material particles do not pass through them during crystal growth, even after a significant portion of the raw material has been etched and/or consumed by the crystal growth operation. In one specific embodiment, the openings in the wire mesh, wire cloth, or foil or plate have a diameter between 0.005 inch and 0.5 inch. In other embodiments, the openings have a diameter between 0.010 inch and 0.125 inch, or between 0.025 inch and 0.080 inch. In some embodiments, hollow pipes, with openings that are covered by wire mesh, are placed within the basket prior to loading of the raw material so as to improve fluid communication between the region between raw material particles within the basket and the crystal growth region. Suitable configurations for such hollow pipes are taught by U.S. Pat. No. 3,245,760, which is hereby incorporated by reference in its entirety.
In some embodiments, the source material is placed in the basket prior to placement of seed crystals on the seed rack, so as to minimize the likelihood of breakage of the latter. The source material may be supplied in various forms. In some embodiments, the source material comprises single crystals or chunks or grit of polycrystalline material. In other embodiments, the source material comprises chunks of sintered polycrystalline material. In the case of gallium nitride, the source material may be derived from by-product single- or poly-crystalline GaN deposited on the wall or miscellaneous surfaces with a hydride vapor phase epitaxy (HVPE) reactor. In another specific embodiment, the source material comprises plates of single- or polycrystalline GaN grown on a substrate by HVPE. In another specific embodiment, the source material is derived from sintered GaN powder, as disclosed by U.S. Pat. No. 6,861,130, which is hereby incorporated by reference in its entirety. In another specific embodiment, the source material is derived from polycrystalline GaN plates comprising a columnar microstructure, as disclosed by US patent application 2007/0142204A1, which is hereby incorporated by reference in its entirety. The source material may contain oxygen at a concentration below 1019 cm−3, below 1018 cm−3, or below 1017 cm−3. The source material may contain an n-type dopant, such as Si or O, a p-type dopant, such as Mg or Zn, a compensatory dopant, such as Fe or Co, or a magnetic dopant, such as Fe, Ni, Co, or Mn, at concentrations between 1016 cm−3 and 1021 cm−3. In one specific embodiment, the particle size distribution of the source material lies between about 0.020 inch and about 5 inches. In another embodiment, the particle size distribution of the source material lies between about 0.050 inch and about 0.5 inch. In a preferred embodiment, the total surface area of the source material is greater, by at least a factor of three, than the total surface area of all the seed crystal plates that are placed in the seed rack.
In some embodiments, the source material comprises a metal that will become molten at elevated temperatures, for example, gallium or indium. In some embodiments, the mineralizer comprises a metal that will become molten at elevated temperatures, for example, sodium, potassium, or lithium. If placed in direct contact with the inner surface of an autoclave or a capsule, the metal may form an alloy, compromising the integrity of the autoclave or capsule. In some embodiments, therefore, at least one crucible is placed within or proximate to the raw material basket and contains at least one metal. The crucible should be chemically inert with respect to the supercritical fluid crystal growth environment and should not react or alloy with the at least one metal. In one specific embodiment, the crucible comprises molybdenum, tantalum, niobium, iridium, platinum, palladium, gold, silver, or tungsten. In another specific embodiment, the crucible comprises alumina, magnesia, calcia, zirconia, yttria, aluminum nitride or gallium nitride. The crucible may comprise a sintered or other polycrystalline material.
The seed rack provides a convenient means for transferring the seed crystals or plates into the high pressure apparatus, for permitting facile fluid communication between the seed crystals or plates and the nutrient region on the other side of the baffle, and for removing the grown crystals from the reactor at the conclusion of a growth run. The seed rack should be easy to load and unload, enable efficient usage of the available crystal growth volume, and minimize breakage and other yield losses of the crystals.
In preferred embodiments, the seed crystals or plates comprise gallium nitride. In other embodiments, the seed crystals or plates may comprise aluminum nitride, sapphire, silicon carbide, MgAl2O4 spinel, zinc oxide, or the like. The seed plates have a minimum lateral dimension of at least one centimeter. In some embodiments, the seed plates have a maximum lateral dimension of at least two centimeters and a minimum lateral dimension of at least one centimeter. In other embodiments, the seed plates have minimum lateral dimensions of at least three centimeters, at least four centimeters, at least five centimeters, at least six centimeters, at least eight centimeters, or at least ten centimeters. In some embodiments, the seed plates are bulk single crystals of gallium nitride. In some embodiments the seed plates are prepared from crystals that were grown by hydride vapor phase epitaxy. In other embodiments, the seed plates are prepared from crystals that were grown ammonothermally. In still other embodiments, the seed plates are prepared from crystals that were grown from solution in a flux. In one specific embodiment, the seed plates are prepared by the method disclosed in U.S. Patent Application No. 61/078,704, which is incorporated by reference herein. In some embodiments, the dislocation density at the large-area surfaces of the seed plates is less than about 106 cm−2. In some embodiments, the dislocation density at the large-area surfaces of the seed plates is less than about 105 cm−2, less than about 104 cm−2, less than about 103 cm−2, or less than about 102 cm−2. In some embodiments, the full width at half maximum of the x-ray diffraction line corresponding to the crystallographic orientation of the large-area face is less than 300 arc seconds, less than 150 arc seconds, less than 100 arc seconds, or less than 50 arc seconds.
Gallium nitride is a hexagonal, wurtzite-structure crystal (space group P63mc; point group 6 mm) with distinct growth sectors. Under a given set of growth conditions, growth occurs at different rates in the +c direction, the −c direction, the m directions, the a directions, and in other crystallographic directions. In general, fast-growing directions tend to grow themselves out of existence, so that the resulting crystals are terminated mainly by facets associated with the slower-growing directions. The most commonly occurring facets under ammonothermal growth conditions are c-plane (0 0 0 1) and (0 0 0-1), and m-plane {1 −1 0 0}. Other planes, for example, a-plane {1 1 −2 0} and semi-polar {1 −1 0 −1} occur less frequently or with smaller areas. Manufacturing efficiency is enhanced by using seed crystals or plates that are already large in a relatively slow-growing dimension, and performing the predominant crystal growth in a relatively faster growing direction. In preferred embodiments, the large area faces of the seed plates are stable under the pre-selected growth conditions, i.e., do not facet, which is facilitated by selecting seed plates with (0 0 0 1), (0 0 0 −1), {1 −1 0 0}, {1 1 −2 0}, or {1 −1 0 −1} orientations.
In addition, the tendency for impurity uptake differs from one growth sector to another. For example, as shown by Frayssinet and co-workers, writing in the Journal of Crystal Growth, volume 230, pages 442-447 (2001), the concentration of free carriers, caused by point defects, is markedly different in the +c and −c growth sectors of unintentionally-doped bulk GaN crystals grown by a particular technique. Similar results have been reported by other authors, with the general tendency that the [0 0 0 −1], or −c, growth sector incorporates a higher impurity concentration than does the [0 0 0 1], or +c, growth sector. Differential impurity uptake is undesirable for at least two reasons. First, the presence of concentration gradients within crystals makes it more difficult for the crystal manufacturer to maintain consistent product specifications. Second, the presence of concentration gradients within the crystal generates strain (typically, impurities in GaN cause a slight increase in the lattice constants), which can lead to bow, cracking, dislocation generation, and other detrimental effects. Manufacturing efficiency, including yield, product quality, and product consistency, is enhanced by restricting the predominant crystal growth to occur in only one growth sector.
In one or more embodiments, manufacturing growth is desired to occur predominantly on m planes. For example, under a predetermined set of growth conditions crystal growth may occur more rapidly in the a direction than in the m direction, and more rapidly in the m direction than in the +c or −c directions. Under such a predetermined set of growth conditions, spontaneously nucleated and grown crystals will take the shape of hexagonal platelets, with large c facets and long m-plane-terminated side edges and a thickness that is less than the diameter. Growth in the m direction could also be preferred by virtue of improved crystallographic quality, reduced impurity incorporation, or, conversely, by increased capability for incorporation of dopants or band-gap modifiers such as Al or In. Growth in the m direction may also be ideal for producing m-plane-oriented wafers. Opposite faces on an m-plane oriented seed crystal or plate will both constitute m planes, so use of such a seed crystal would produce growth in a single crystallographic growth sector.
In one set of embodiments, the seed crystals are attached to the seed rack as shown schematically in
In some embodiments, holes or slots are provided in the seed crystals or plates, and the seed crystals or plates are suspended from the seed rack by at least one wire or foil strip. In some embodiments, the seed crystals are suspended by at least two wires or foil strips. The holes or slots in the seed crystals or plates may be formed by laser drilling or cutting, by ultrasonic drilling, by mechanical drilling or milling, by grinding, by sanding, by electric discharge machining, by water jet cutting, or the like.
In one set of embodiments, manufacturing growth is desired to occur predominantly on m planes. Growth in the m direction may provide a useful means for preparing non-polar substrate orientations. Growth in the a direction could also be preferred by virtue of improved crystallographic quality, reduced impurity incorporation, or, conversely, by increased capability for incorporation of dopants or band-gap modifiers such as Al or In. Opposite faces on an m-plane oriented seed crystal or plate will both constitute m planes, so use of such a seed crystal would produce growth in a single crystallographic growth sector.
In one set of embodiments, manufacturing growth is desired to occur predominantly on a planes. Growth in the a direction may provide a useful means for preparing non-polar and/or semi-polar substrate orientations. Growth in the a direction could also be preferred by virtue of improved crystallographic quality, reduced impurity incorporation, or, conversely, by increased capability for incorporation of dopants or band-gap modifiers such as Al or In. Opposite faces on an a-plane oriented seed crystal or plate will both constitute a planes, so use of such a seed crystal would produce growth in a single crystallographic growth sector.
In another set of embodiments, manufacturing growth is desired to occur predominantly on c planes, either in the +c direction (the [0 0 0 1] Ga-polar direction) or −c direction (the [0 0 0 −1] N-polar direction). For example, under a predetermined set of growth conditions crystal growth may occur more rapidly in the +c or −c direction than in the m direction. Under such a predetermined set of growth conditions, spontaneously nucleated and grown crystals will take the shape of hexagonal pillars, prisms, or needles, with small c facets and long m-plane-terminated side edges and a length that is less than the diameter. Growth in the +c or −c direction could also be preferred by virtue of improved crystallographic quality, reduced impurity incorporation, or, conversely, by increased capability for incorporation of dopants or band-gap modifiers such as Al or In. Growth in the +c or −c direction may also be ideal for producing c-plane-oriented wafers. Opposite faces on an c-plane oriented seed crystal or plate constitute different planes, so use of such a seed crystal alone would produce growth in two distinct crystallographic growth sectors. Growth in a single crystallographic growth sector may be achieved by stacking pairs of c-plane-oriented seed crystals or plates back to back, with like faces facing one another. For example, the −c face of two c-plane-oriented seed crystals or plates could be faced proximate to one another, so that the +c faces of the two c-plane-oriented seed crystals or plates face outward and would yield growth in a single crystallographic orientation. Conversely, the +c face of two c-plane-oriented seed crystals or plates could be faced proximate to one another, so that the −c faces of the two c-plane-oriented seed crystals or plates face outward and would yield growth in a single crystallographic orientation. The pairs of seed crystals could be placed in direct contact with one another or could be separated by a crystal separator plate. The pairs of seed crystals placed back to back may be separated by a predetermined gap. The predetermined gap may be, less than 5 millimeters, less than 2 millimeters, less than 1 millimeter, less than 0.3 millimeter, less than 0.1 millimeter, less than 0.03 millimeter, or less than 0.01 millimeter. The predetermined gap may be essentially zero, that is, with the seed crystals in direct contact. If the pairs of seed crystals or plates grew together during a growth run they could be separated after the run, if desired, or could be left together for use as a seed (bi-)crystal in a subsequent run. A c-plane-oriented bi-crystal, on which both large-area faces constitute +c or −c surfaces, is suitable for use as a seed, as growth on the large area faces will occur in only a single crystallographic direction. At least one contact twin or stacking fault, oriented substantially parallel to the large-area surfaces, may be present in the bi-crystal.
In yet another set of embodiments, manufacturing growth is desired to occur predominantly on the semi-polar {1 −1 0 −1} plane. Growth in this semipolar direction could be preferred by virtue of improved crystallographic quality, reduced impurity incorporation, or, conversely, by increased capability for incorporation of dopants or band-gap modifiers such as Al or In. Growth perpendicular to the {1 −1 0 −1} plane may also be ideal for producing {1 −1 0 −1}-oriented wafers. Opposite faces on an {1 −1 0 −1}-oriented seed crystal or plate constitute different planes, so use of such a seed crystal alone would produce growth in two distinct crystallographic growth sectors. Growth in a single crystallographic growth sector may be achieved by stacking pairs of {1 −1 0 −1}-oriented seed crystals or plates back to back, with the {1 −1 0 1}-oriented faces facing one another. The pairs of seed crystals could be placed in direct contact with one another or could be separated by a crystal separator plate. If the pairs of seed crystals or plates grew together during a growth run they could be separated after the run, if desired, or could be left together for use as a seed (bi-)crystal in a subsequent run. A {1 −1 0 −1}-oriented bi-crystal, on which both large-area faces constitute {1 −1 0 −1} surfaces, is suitable for use as a seed, as growth on the large area faces will occur in only a single crystallographic direction. At least one contact twin, oriented substantially parallel to the large-area surfaces, may be present in the bi-crystal.
In still another set of embodiments, manufacturing growth is desired to occur predominantly on semi-polar planes. Semipolar planes may be designated by (hkil) Miller indices, where i=−(h+k), l is nonzero and at least one of h and k are nonzero. For example, growth on (1 0 −1 −1) planes may be preferred over growth on (1 0 −1 1) planes because of a higher growth rate, improved crystallographic quality, reduced impurity incorporation, or, conversely, by increased capability for incorporation of dopants or band-gap modifiers such as Al or In. Growth in semipolar directions may be ideal for producing semi-polar-oriented wafers. Opposite faces on a semi-polar oriented seed crystal or plate constitute different planes, so use of such a seed crystal alone would produce growth in two distinct crystallographic growth sectors. Growth in a single crystallographic growth sector may be achieved by stacking pairs of semi-polar-oriented seed crystals or plates back to back, with like faces facing one another. For example, the (1 0 −1 1) face of two semi-polar seed crystals or plates could be faced proximate to one another, so that the (1 0 −1 −1) faces of the two seed crystals or plates face outward and would yield growth in a single crystallographic orientation. More generally, the (h k i l) face of two semipolar seed crystals or plates could be placed proximate to one another, so that the (h k i −l) faces of the two seed crystals or plates face outward and would yield growth in a single crystallographic orientation. The pairs of seed crystals could be placed in direct contact with one another or could be separated by a crystal separator plate. If the pairs of seed crystals or plates grew together during a growth run they could be separated after the run, if desired, or could be left together for use as a seed (bi-)crystal in a subsequent run. A semi-polar bi-crystal, on which both large-area faces constitute the same semi-polar orientation, is suitable for use as a seed, as growth on the large area faces will occur in only a single crystallographic direction.
In some embodiments, the seed crystals or plates have a rectangular or approximately rectangular shape. An approximately rectangular shape may be particularly appropriate for m-plane or a-plane seed plates. In some embodiments, the corners of the seed crystals or plates are rounded or chamfered so as to minimize the likelihood of breakage. Rectangular shapes are convenient for mounting and for efficiently utilizing space within the high pressure crystal growth reactor. In other embodiments, the seed crystals or plates have a hexagonal or approximately hexagonal shape. A hexagonal shape may be particularly convenient when working with c-plane-oriented seed crystals or plates. In still other embodiments, the seed crystals or plates have a circular, oval, or approximately circular or oval shape.
In some embodiments, particularly those with non-rectangular seed crystals or plates, the seeds may be arranged in a non-rectangular, close-packed way, as shown in
In some embodiments, particularly those involving the use of an autoclave as the high pressure apparatus, the frame further comprises a set of stacked disks or baffles on the top end of the frame. The stacked disks or baffles reduce convective heat transfer from the supercritical fluid during crystal growth to the upper end of the autoclave so that the seal of the autoclave may be at a reduced temperature relative to the upper end of the interior of the autoclave. In other embodiments, one or more disks or baffles are placed on top of the frame after insertion of the latter into a high pressure apparatus.
After loading the frame with seed crystals and raw material, the frame is placed inside a sealable container. The sealable container may constitute an autoclave or a capsule designed for use with an internally-heated high pressure apparatus. At least one mineralizer may be added. The mineralizer may comprise an alkali metal such as Li, Na, K, Rb, or Cs, an alkaline earth metal, such as Mg, Ca, Sr, or Ba, or an alkali or alkaline earth hydride, amide, imide, amido-imide, nitride, or azide. The mineralizer may comprise an ammonium halide, such as NH4F, NH4Cl, NH4Br, or NH4I, a gallium halide, such as GaF3, GaCl3, GaBr3, GaI3, or any compound that may be formed by reaction of one or more of HF, HCl, HBr, HI, Ga, and NH3. The mineralizer may comprise other alkali, alkaline earth, or ammonium salts, other halides, urea, sulfur or a sulfide salt, or phosphorus or a phosphorus-containing salt. The mineralizer may be provided as a metal, a loose powder, as granules, or as at least one densified compact or pill. The mineralizer may be added to the raw material basket, may be placed in a crucible, or may be placed directly in the high pressure apparatus or capsule. In a preferred embodiment, the mineralizer is added to the high pressure apparatus or capsule in the absence of exposure to air, such as inside a glove box.
The sealable container is then closed and sealed except for a connection to a gas, liquid, or vacuum manifold. In one embodiment, the sealable container comprises an autoclave, as taught by U.S. Pat. No. 7,335,262, which is hereby incorporated by reference in its entirety. In another embodiment, the sealable container comprises a metal can, as discussed by U.S. Pat. No. 7,125,453, a container, as discussed by U.S. Patent Application No. 2007/0234946, or a capsule, as discussed by U.S. patent application Ser. No. 12/133,365, entitled “Improved capsule for high pressure processing and method of use for supercritical fluids,” all of which are hereby incorporated by reference in their entirety. The inner diameter of the autoclave or capsule may be between 1 inch and 2 inches, between 2 inches and 3 inches, between 3 inches and 4 inches, between 4 inches and 6 inches, between 6 inches and 8 inches, between 8 inches and 10 inches, between 10 inches and 12 inches, between 12 inches and 16 inches, between 16 inches and 24 inches, or greater than 24 inches. The clearance between the inner diameter of the autoclave or capsule and the outer diameter of the frame may be between 0.005 inch and 1 inch, or between 0.010 inch and 0.25 inch. The ratio of the inner height of the autoclave or capsule to its inner diameter may be between 1 and 2, between 2 and 4, between 4 and 6, between 6 and 8, between 8 and 10, between 10 and 12, between 12 and 15, between 15 and 20, or greater than 20.
In some embodiments, the autoclave or capsule is evacuated, so as to remove air, moisture, and other volatile contaminants. In some embodiments, the high pressure apparatus or capsule is heated during evacuation, to a temperature between about 25 degrees Celsius and about 500 degrees Celsius. In some embodiments, the autoclave or capsule are heated using the same heating elements that are used during high pressure processing. In one specific embodiment, the capsule is heated by placing it inside an internally-heated pressure apparatus and heated using the heater for the latter.
In another set of embodiments, the autoclave or capsule containing the filled frame is purged to remove air, moisture, and other volatile contaminants, as shown in
In a specific embodiment, the inlet of the gas flow, for example, the second fill tube or the purge tube is then coupled to a source of liquid solvent. The autoclave or capsule and fill tube(s) may be cooled, or the liquid solvent delivery system and transfer lines heated, so that the former are cooler by between one and 50 degrees Celsius than the latter. Liquid solvent is then introduced into the autoclave or capsule at a rate between 0.1 and 1000 grams per minute. At room temperature, the vapor pressure of ammonia is approximately 10 atmospheres. Depending on the temperature of the solvent source, therefore, the system pressure during solvent delivery may be above 7 atmospheres, above 8 atmospheres, above 9 atmospheres, or above 10 atmospheres. In one embodiment, the purge exhaust is closed and the solvent vapor above the liquid is forced to condense into liquid during the filling operation. In this embodiment, the autoclave or capsule may be actively cooled in order to dissipate the heat released by condensation of the solvent vapor. In another embodiment, the purge exhaust is fitted with a check valve so that residual purge gas or solvent vapor is allowed to exit when the pressure exceeds a predetermined threshold, but air or other gases are not allowed to flow backward into the autoclave. The quantity of solvent in the autoclave or capsule may be determined by using a liquid delivery system with the capability for accurately monitoring and controlling the mass of liquid delivered. An example of suitable equipment for delivery of precision-metered, high-purity liquid ammonia is the InScale™ system manufactured by iCon Dynamics, LLC. In some embodiments, the amount of ammonia delivered to the autoclave or capsule is quantified by the loss in weight of at least one ammonia supply cylinder. If solvent gas is allowed to exhaust during liquid filling, in the case where ammonia is the solvent, the quantity of vented solvent may be determined by trapping it in aqueous solution and measuring the change in pH and this quantity subtracted from the total liquid delivered to determine the quantity of liquid in the autoclave or capsule. An analogous method for determining the quantity of vented solvent may be performed in cases where the solvent is different from ammonia.
In an alternative embodiment, the solvent is delivered to the autoclave or capsule as a vapor at elevated pressure. The inlet of the gas flow, for example, the second fill tube or the purge tube is then coupled to a source of vapor-phase solvent. The autoclave or capsule and fill tube(s) may be cooled, or the solvent delivery system and transfer lines heated, so that the former are cooler by between one and 50 degrees Celsius than the latter. Vapor-phase solvent is then introduced into the autoclave or capsule at a rate between 0.1 and 1000 grams per minute and allowed to condense in the autoclave or capsule. The pressure of the solvent vapor should be higher than the equilibrium vapor pressure at the temperature of the autoclave or capsule. Depending on the temperature of the autoclave or capsule and of the solvent delivery system, the pressure during solvent delivery may be above 7 atmospheres, above 8 atmospheres, above 9 atmospheres, or above 10 atmospheres. In one embodiment, the purge exhaust is closed and the solvent vapor above the liquid is forced to condense into liquid during the filling operation. In this embodiment, the autoclave or capsule may be actively cooled in order to dissipate the heat released by condensation of the solvent vapor. In another embodiment, the purge exhaust is fitted with a check valve so that residual purge gas or solvent vapor is allowed to exit when the pressure exceeds a predetermined threshold, but air or other gases are not allowed to flow backward into the autoclave. The quantity of solvent in the autoclave or capsule may be determined by using a vapor delivery system equipped with a mass flow meter. In some embodiments, the amount of ammonia delivered to the autoclave or capsule is quantified by the loss in weight of at least one ammonia supply cylinder. If solvent gas is allowed to exhaust during liquid filling, in the case where ammonia is the solvent, the quantity of vented solvent may be determined by trapping it in aqueous solution and measuring the change in pH and this quantity subtracted from the total liquid delivered to determine the quantity of liquid in the capsule. An analogous method for determining the quantity of vented solvent may be performed in cases where the solvent is different from ammonia.
Following filling of the autoclave or capsule, the inner purge tube, if present, may be removed. In some embodiments, the inner purge tube is removed after the purging step but before the filling step. A gate valve to the autoclave, or the fill tube(s) to the capsule, are then sealed. Once sealed, the interior of the autoclave or of the capsule is substantially air-free, and the at least one material contained therein can be processed with reduced risk of contamination. Of course, there can be other variations, modifications, and alternatives.
In some embodiments, the autoclave is then heated to crystal growth conditions. In other embodiments, the capsule is placed inside an autoclave, an internally-heated pressure apparatus, or other high pressure apparatus, and heated to crystal growth conditions. In some embodiments, the thermal cycle includes a pre-reaction segment to form mineralizer, polycrystalline gallium nitride, dissolved gallium containing complexes, or the like. In some embodiments, the atmosphere in the autoclave may be modified during the run. For example, excess H2 formed by reaction of gallium metal with ammonia may be bled off through the gate valve or allowed to diffuse through a heated palladium membrane. Excess nitrogen formed by decomposition of an azide mineralizer may be bled off through the gate valve. Additional ammonia may be added to replenish the solvent in the high pressure apparatus.
Suitable thermal cycles for crystal growth are discussed by U.S. Pat. Nos. 6,656,615 and 7,078,731, which are hereby incorporated by reference in their entirety. The crystals grow predominantly perpendicular to the large-diameter faces, but may also grow somewhat in lateral directions as well. With the possible exception of c-plane or {1 −1 0 ±1} seeds stacked back-to-back, the crystals are prevented from growing into one another by the crystal separator plates.
After performing crystal growth for a predetermined period of time, the autoclave or high pressure apparatus is cooled. When the autoclave or capsule has cooled to below 100 degrees Celsius, below 75 degrees Celsius, below 50 degrees Celsius, or below 35 degrees Celsius, a valve to the autoclave is opened, or the capsule is vented, and the ammonia is removed. In one embodiment, gas-phase ammonia is allowed to exit the autoclave or capsule and is bubbled through an acidic aqueous solution in order to be chemically trapped. In another embodiment, gas phase ammonia is passed through a flame so as to burn the ammonia, forming H2O and N2. In a preferred embodiment, illustrated in
Referring to
Referring to
For recycling purposes, a purifying agent, for example, sodium metal, may be placed in the receiving/purification tank. The sodium will react with residual oxygen and/or water in the ammonia, restoring a very high degree of purity. After a period of one hour to thirty days, the ammonia may be transferred to a delivery tank. In a preferred embodiment, the transfer is performed through the gas phase, via a condenser, so as to leave the purifying agent in the receiving/purification tank. Liquid ammonia may be delivered from the delivery tank, via a dip tube, to the autoclave for the next crystal growth run. In an alternative embodiment, vapor-phase ammonia may be delivered from the delivery tank to an autoclave or capsule for the next crystal growth run.
After cooling, removal of the ammonia, and opening of the autoclave or internally-heated high pressure apparatus and capsule, the frame is removed from the autoclave or capsule, and the grown crystals are removed from the seed rack. If necessary, portions of the clips that have been overgrown by crystalline material may be removed by etching in an appropriate acid, such as at least one of hydrochloric acid, sulfuric acid, nitric acid, and hydrofluoric acid.
The crystals are sliced into pre-selected orientations, as summarized in
In other embodiments, the seed crystals have a crystallographic orientation such that at least one large face is a relatively fast-growing face. In one specific embodiment, the seed crystal has an a-plane orientation. In other embodiments, the seed crystal has a semi-polar orientation. In specific embodiments, the orientation of the seed crystal is {1 −1 0 ±1}, {1 −1 0 ±2}, {1 −1 0 ±3}, or {1 1 −2 ±2}. In some embodiments, two seed crystals are placed together back-to-back, so that opposite faces of the co-mounted seed crystals have an equivalent crystallographic orientation. The use of fast-growing orientations may allow for an overall faster production rate of high quality production crystals. In one specific embodiment, shown in
After slicing, the crystal wafers may be lapped, polished, and chemical-mechanically polished by methods that are known in the art.
The crystal wafers are useful as substrates for fabrication into optoelectronic and electronic devices such as at least one of a light emitting diode, a laser diode, a photodetector, an avalanche photodiode, a transistor, a rectifier, and a thyristor; one of a transistor, a rectifier, a Schottky rectifier, a thyristor, a p-i-n diode, a metal-semiconductor-metal diode, high-electron mobility transistor, a metal semiconductor field effect transistor, a metal oxide field effect transistor, a power metal oxide semiconductor field effect transistor, a power metal insulator semiconductor field effect transistor, a bipolar junction transistor, a metal insulator field effect transistor, a heterojunction bipolar transistor, a power insulated gate bipolar transistor, a power vertical junction field effect transistor, a cascade switch, an inner sub-band emitter, a quantum well infrared photodetector, a quantum dot infrared photodetector, a solar cell, and a diode for photoelectrochemical water splitting and hydrogen generation.
In a specific embodiment, any of the above sequence of steps provides a method according to an embodiment of the present invention. In a specific embodiment, the present invention provides a method and resulting crystalline material provided by a pressure apparatus having a basket structure. Other alternatives can also be provided where steps are added, one or more steps are removed, or one or more steps are provided in a different sequence without departing from the scope of the claims herein.
While the above is a full description of the specific embodiments, various modifications, alternative constructions and equivalents may be used. Therefore, the above description and illustrations should not be taken as limiting the scope of the present invention which is defined by the appended claims.
This application claims priority to U.S. Provisional Application No. 61/087,122 filed Aug. 7, 2008, commonly assigned and incorporated by reference in its entirely herein for all purposes. This application is also related to U.S. Patent Application Nos. 61/073,687, 61/078,704, Ser. Nos. 12/133,365, and 12/133,364, commonly assigned and incorporated by reference in its entirely herein for all purposes. This application is also related to U.S. Pat. Nos. 3,245,760, 6,656,615, 6,861,130, 7,078,731, 7,101,433, 7,125,453, 7,160,388, and 7,335,262, and in U.S. published Patent Application Nos. 2006/01777362, 2007/0142204, and 2007/0234946, all of which are hereby incorporated by reference in their entirety for all purposes.
Number | Date | Country | |
---|---|---|---|
61087122 | Aug 2008 | US |