Process for producing foams based on thermoplastic polyurethanes

Information

  • Patent Grant
  • 11052570
  • Patent Number
    11,052,570
  • Date Filed
    Tuesday, February 9, 2016
    8 years ago
  • Date Issued
    Tuesday, July 6, 2021
    3 years ago
Abstract
A process for producing foamed thermoplastic polyurethane particles comprises the steps of a) melting a thermoplastic polyurethane in a first extruder (E1), b) injecting a gaseous blowing agent in a second extruder (E2), c) impregnating the gaseous blowing agent homogeneously into the thermoplastic polyurethane melt in a third extruder (E3), d) extruding the impregnated thermoplastic polyurethane melt through a die plate and granulating the melt in an underwater granulation device under temperature and pressure conditions to form foamed thermoplastic polyurethane particles.
Description
DESCRIPTION

This invention relates to a process for production of expanded pellets from a polymer melt comprising a blowing agent. Expanded pellets of thermoplastic polymers, especially of thermoplastic polyurethane (TPU), have elastic and tribological properties and so are useful in a wide variety of applications. Examples of uses for expanded pellets of thermoplastic polyurethane include reusable gymnastics mats, body protectors, trim elements in automobile building, sound and vibration absorbers, packaging or in shoe soles. High elasticity and good homogeneity on the part of the pellets are of decisive importance for all these sectors.


WO 2007/082838 discloses a process for production of expanded thermoplastic polyurethane comprising a blowing agent. A first step of the process comprises extruding a thermoplastic polyurethane into pellets. The pellets are impregnated with a blowing agent in an aqueous suspension under pressure in a second step and expanded in a third step. In a further embodiment of the process, the thermoplastic polyurethane is melted in an extruder together with a blowing agent and the melt is pelletized without a device to prevent foaming. Volatile organic compounds are used as blowing agents in the production via extrusion.


WO 2013/153190 relates to a method for producing expanded granules from a propellant-containing polymer melt, comprising the steps: a) pressing the propellant-containing polymer melt through a perforated plate controlled to a temperature between 150′C. and 280′C. into a granulation chamber; b) comminuting the polymer melt pressed through the temperature-controlled perforated plate into individual expanding granules with a cutting device; c) discharging the granules from the granulation chamber with a fluid stream, wherein the propellant contains CO2 or N2 or a combination of CO2 and N2, and a fluid controlled to a temperature between 10′C. and 60′C. and having a pressure between 0.7 bar and 20 bar above the ambient pressure is caused to flow through the granulation chamber, and wherein the pressure and temperature of the fluid in the granulation chamber as well as the temperature of the perforated plate are selected such that the granules in the fluid under pressure are expanded by the propellant they contain in such a manner that expanded granules with a closed skin are created.


IF only one extruder to produce foamed thermoplastic polyurethane particles (E-TPU) is used it is sometimes difficult to control all processing parameters, such as temperature, pressure and rotation speed, in order to achieve the desired product properties, such as cell size, density, thickness of the skin layer and independent cell ratio. Retention time and variation of rotation speed in the production process is limited.


Object of the present invention was to solve above-mentioned problems and to provide a precise and flexible process for producing foamed thermoplastic polyurethane particles. This problem was solved by a process for producing foamed thermoplastic polyurethane particles comprising the steps of

  • a) melting a thermoplastic polyurethane in a first extruder E1,
  • b) injecting a gaseous blowing agent in a second extruder E2,
  • c) impregnating the gaseous blowing agent homogeneously into the thermoplastic polyurethane melt in a third extruder E3,
  • d) extruding the impregnated thermoplastic polyurethane melt through a die plate and granulating the melt in an underwater granulation device under temperature and pressure conditions to form foamed thermoplastic polyurethane particles.


In step a) the thermoplastic polyurethane is melted in the first extruder E1, which is preferably a single screw extruder. The melt viscosity of the thermoplastic polyurethane (TPU) is controlled in certain range by adjusting the parameters such as temperature, pressure and rotation speed to get suitable viscosity for gas dozing and steady feed to the second extruder E2. Using an extruder E1 only for melting TPU enables to select a wide range of TPU which are independent of hardness and molecular weight.


The thermoplastic polyurethane may be any desired thermoplastic polyurethane (TPU) known to a person skilled in the art. Thermoplastic polyurethanes and their methods of making have been extensively described, for example in Gerhard W. Becker and Dietrich Braun, Kunststoffhandbuch, volume 7, “Polyurethane”, Carl Hanser Verlag, Munich, Vienna, 1993.


In step b) a gaseous blowing agent is injected into the thermoplastic polyurethane melt in the second extruder E2, which is preferably a twin screw extruder. Preferably CO2 and/or N2 and more preferably a combination of CO2 and N2 are used as gaseous blowing agents. A co-blowing agent can additionally be added to the polymer melt. Useful co-blowing agents include alkanes such as ethane, propane, butane, pentane, alcohols such as ethanol, isopropanol, halo-genated hydrocarbons or CFCs or a mixture thereof. The sole use of CO2 and/or N2 and also their combination as blowing agent is particularly advantageous, since they are inert gases, which are nonflammable, so that no potentially explosive atmospheres can arise in manufacture. Using a separate extruder E2 for injecting gaseous blowing agents enables to prolong gaseous blowing agent injection time.


If step c) is not used, the gaseous blowing agent would then have to be dispersed properly by controlling the parameters of the second extruder and cooling would have to be done in the latter half of the second extruder E2 by adjusting screw shape and controlling temperature.


The three extruders E1, E2 and E3 are connected in series, preferably extruder E1 is directly connected to Extruder E2 and Extruder E2 is directly connected to Extruder E3. Most preferably a single screw extruder is used as extruder E1 and extruder E3 and a twin extruder is used as Extruder E2.


Impregnating the gaseous blowing agent homogeneously into the thermoplastic polyurethane melt is carried out in a third extruder E3. Stabilization and cool down of TPU by low rotation and low sheer rate by controlling the parameters of the third extruder E3, which has cooling unit in the special shaped screw, to get aimed sell size, gravity, thickness of skin layer and independent sell ratio. Using a separate extruder E3 for impregnating the gaseous blowing agent into the thermoplastic polyurethane melt enables better gas diffusion in the melted TPU.


In step d) extruding the impregnated thermoplastic polyurethane melt through a die plate and granulating the melt in an underwater granulation device under temperature and pressure conditions to form foamed thermoplastic polyurethane particles (E-TPU).


Preferably the bulk density of the foamed thermoplastic polyurethane particles formed in step d) is in the range from 30 to 250 kg/m3 , preferably in the range from 100 to 200 kg/m3.


Preferably the water in the underwater granulation device has a pressure in the range from 1 to 20 bar and a temperature in the range from 10 to 50° C. in order to achieve the desired bulk density the foamed thermoplastic polyurethane particles.







EXAMPLES

Raw Materials:


Elastollan 1180A (commercially available TPU of BASF SE)


Elastollan 1196A (commercially available TPU of BASF Japa)


Elastollan ET880 (commercially available TPU of BASF Japan)


Elastollan SP9324 (commercially available TPU of BASF SE)


Crosslinking agent Polyether polyol -MDI-based prepolymer


Binder for TPU form


Elastan® C8008 C-B: 15% /MCP


Following Set-up of the machine was used for examples 1-12:


3 different types of extruders are connected and following equipment is attached respectively;


1. Dryer to the 1st extruder. 2. Gas dosing system to the 2nd extruder. 3. Underwater pelletize system to the 3rd extruders.


TPU was melted in a 1st Extruder. Temperature conditions were adjusted dependent on TPU grade used.


Nitrogen and/or carbon dioxide were injected into the 2nd Extruder (46 mmcp twin extruder) using injection pumps.


Setting Temperature of heater zone C1 to C12 and AD (Adapter)


























C1
C2
C3
C4
C5
C6
C7
C8
C9
C10
C11
C12
C13
C14
AD







200
200
190
190
190
190
190
190
190
190
190
190
190
180
180









Control conditions


Rotating speed: 47 rpm


Exit pressure : 7.5 MPa


Blowing agents:


N2: Pressure 8 MPa (0.4˜0.5% vs TPU)


CO2: Pressure 4 MPa (1.1˜.4% vs TPU)


A 3rd Extruder (65 mmcp single extruder with cooling able quadruple thread screw) was used for gas diffusion in the melted TPU


Setting Temperature of heater zone C1 to C4 and AD (Adapter)




















Screw
C1
C2
C3
C4
AD









160
170
190
190
190
180










Control conditions


Rotating speed: 24 rpm


Entrance pressure: 8 MPa


Die pressure: 9 MPa


Underwatergranulation:


Setting Temperature of adapter (between filter and die) and die
















Adapter
Die









188
200










Following Set-up of the machine was used for comparative examples 13-15:


Comparative examples were used only 1 extruder which are implemented TPU melting, gas dosing and gas diffusion.


Setting Temperature of heater zone C1 to C12 and AD (Adapter)


























C1
C2
C3
C4
C5
C6
C7
C8
C9
C10
C11
C12
C13
C14
AD







160
180
190
190
190
190
190
190
190
190
190
190
190
180
180









Underwatergranulation:


Setting Temperature of adapter (between filter and die) and die
















Adapter
Die









188
200










Molding Conditions:


TPU-foam particles from example 1-15 were molded using PU binder Elastan C8008 and pressed 30 minutes at 80° C. Physical properties of the moldings are summarized in Table 1.


Testing:


Mold density and compressive strength were determined according to JIS K 6767.


Tensile strength and elongation at break were determined according to JIS K 6400.


Tear strength and Rebound resilience were determined according to JIS K 7311.


Compression set was determined









TABLE 1





Physical properties of Examples 1-15

















Example

















1
2
3
4
5
6
7
8
9















Base TPU

1180A
1180A
1196


gas

CO2
CO2 + N2
CO2

















melt viscosity

5.4
5.4
16
16
5.4
5.4
1.1
1.1
1.1


MFR [g/10 min]


crosslinker [%]

5
5
5

5
5
5
5
5


particle
(g/l)
170
200
170
170
160
200
160
180
190


bulk density


Compressive
10%
0.05
0.06
0.05
0.05
0.03
0.07
0.11
0.12
0.13


strength
25%
0.13
0.15
0.13
0.11
0.08
0.14
0.35
0.40
0.50



50%
0.28
0.30
0.27
0.25
0.15
0.25
0.75
0.90
0.95


Compressive
(MPa)
0.40
0.50
0.40
0.39
0.25
0.40
0.90
0.90
1.00


elasticity modulus


rebound resilience
(%)
53
53
49
47
49
50
27
26
26


Compression
(%)
23
20
37
50
33
30
27
22
20


set


(23° C. × 22 hr)












Example














10
11
12
13
14
15



















Base TPU

ET880
SP9324
1180A
SP9324
1196A



gas

CO2
CO2
CO2 + N2
CO2 + N2
CO2 + N2
















melt viscosity

10.2
10.2
23
5.4
23
1.1



MFR [g/10 min]



crosslinker [%]

5
5
5






particle
(g/l)
210
230
240
110
230
Not expanded



bulk density



Compressive
10%
0.05
0.06
0.07
0.03
0.05



strength
25%
0.13
0.14
0.15
0.08
0.12




50%
0.24
0.25
0.27
0.16
0.24



Compressive
(MPa)
0.52
0.53
0.54
0.19
0.49



elasticity modulus



rebound resilience
(%)
56
56
58
57
59



Compression
(%)
16
15
17



set



(23° C. × 22 hr)









Claims
  • 1. A process for producing foamed thermoplastic polyurethane particles, the process comprising: a) melting a thermoplastic polyurethane in a first extruder E1, which is a single screw extruder,b) injecting a gaseous blowing agent in a second extruder E2, which is a twin extruder,c) impregnating the gaseous blowing agent homogeneously into the thermoplastic polyurethane melt in a third extruder E3, which is a single screw extruder operating at a lower rotation and lower sheer rate than said second extruder E2, andd) extruding the impregnated thermoplastic polyurethane melt through a die plate and granulating the melt in an underwater granulation device under temperature and pressure conditions to form foamed thermoplastic polyurethane particles,wherein a bulk density of the foamed thermoplastic polyurethane particles formed in step d) is from 30 to 250 kg/m3.
  • 2. The process according to claim 1, wherein the gaseous blowing agent comprises CO2, N2, or a combination of CO2 and N2.
  • 3. The process according to claim 1, wherein a single screw extruder is used as the first extruder E1 and the third extruder E3, and a twin extruder is used as the second Extruder E2.
  • 4. The process according to claim 1, wherein the water in the underwater granulation device has a pressure in the range from 1 to 20 bar and a temperature in the range from 10 to 50° C.
  • 5. The process according to claim 1, wherein the bulk density of the foamed thermoplastic polyurethane particles formed in step d) is from 100 to 200 kg/m3.
  • 6. The process according to claim 1, wherein the bulk density of the foamed thermoplastic polyurethane particles formed in step d) is from 160 to 230 kg/m3.
  • 7. The process according to claim 1, wherein the thermoplastic polyurethane further comprises a crosslinking agent that is polyether polyol-MDI-based prepolymer.
  • 8. The process according to claim 7, wherein the gaseous blowing agent comprises CO2, N2, or a combination of CO2 and N2.
Priority Claims (1)
Number Date Country Kind
15155374 Feb 2015 EP regional
PCT Information
Filing Document Filing Date Country Kind
PCT/EP2016/052676 2/9/2016 WO 00
Publishing Document Publishing Date Country Kind
WO2016/131671 8/25/2016 WO A
US Referenced Citations (10)
Number Name Date Kind
5674916 Shmidt Oct 1997 A
9884947 Prissok Feb 2018 B2
20070100008 Chang May 2007 A1
20120053255 Koerner Mar 2012 A1
20120329892 Prissok Dec 2012 A1
20130078445 Ramesh Mar 2013 A1
20140343184 Axelrad Nov 2014 A1
20150174808 Rudolph et al. Jun 2015 A1
20150183989 Manitiu Jul 2015 A1
20170246765 Huang Aug 2017 A1
Foreign Referenced Citations (3)
Number Date Country
2007082838 Jul 2007 WO
2013153190 Oct 2013 WO
WO-2013153190 Oct 2013 WO
Non-Patent Literature Citations (8)
Entry
Machine Translation of WO2013153190A1 (Year: 2013).
Website: Clextral /Technologies & lines/Technologies & processes/Benefits of Twin Screw Extrusion (Year: 2013).
Website:Tecnomatic/Facts You Need to Know about Single Screw Extruders (Year: 2017).
Website: bufca.co.uk/polyurethane-foam-benefits/ (Year: 2018).
Machine Translation of WO2013153190 (Year: 2013).
Extended Search Report dated Apr. 7, 2015 in European Patent Application No. 15155374.0.
International Search Report and Written Opinion dated Mar. 22, 2016 in corresponding Patent Application No. PCT/EP2016/052676.
International Search Report dated Mar. 22, 2016 in PCT/EP2016/052676 filed Feb. 9, 2016.
Related Publications (1)
Number Date Country
20180066122 A1 Mar 2018 US