Process for supplying a gas, especially of diborane and silane

Abstract

A process for supplying a gas to a reactor comprising the steps of:(i) continuously measuring density of the gas, the gas including at least one component which is susceptible to formation of an undesired side product as shown by a variation in density of the gas; and(ii) modifying feed conditions of the gas if formation of the undesired side product is shown by a variation in the density of the gas.The process can be employed to continuously monitor the content of diborane (B.sub.2 H.sub.6) in a mixture with silane (SiH.sub.4) in a process for producing a borophosphosilicate glass.An apparatus for supplying a gas to a reactor is also disclosed.

Description

BACKGROUND OF THE INVENTION

The present invention relates to the supplying of gas, such as a gaseous mixture based on diborane (B.sub.2 H.sub.6) and of silane (SiH.sub.4), destined for a reactor for growing layers of glass having a base of boron, phosphate, silicate (BPSG) ("boro-phospho-silicate glass) beginning with an initial feed of B.sub.2 H.sub.6/ SiH.sub.4 in determined proportions.

It is known that this type of mixture is modified with time by virtue of the tendency of diborane (B.sub.2 H.sub.6) to be transformed to higher boranes, notably those such as tetraborane (B.sub.4 H.sub.10), pentaborane 11 (B.sub.5 H.sub.11) which, on one hand, release hydrogen (H.sub.2) and, on the other hand, are sometimes transformed to a liquid or even solid form which is not transferred with the gaseous flow. As a result, even when starting from perfectly suitable starting materials, the mixture transferred to the reactor is of improper composition notably, the mixture being of lower boron content, which forestalls against proper growing of the BPSG glass layer. This is the reason that, currently, analyses of the gaseous mixture being transferred to the reactor are carried out such as by chromatography which is not very practical because such method is discontinuous and requires frequent recalibration.

SUMMARY AND OBJECTS OF THE INVENTION

The present invention has as its goal the perfecting of this measurement by substituting therefore a method of completely different type, which is particularly well adapted to the type of application discussed above and which is reliable, continuous, simple and by virtue of which there is permitted an immediate correction, in the event of a deviation in the measured value of the content of B.sub.2 H.sub.6 as compared to the consigned value.

These objects are attained, according to the invention, by continuously measuring the density of the gas or mixture and subsequently determining the variation of the composition, in particular of the content of B.sub.2 H.sub.6 in a manner such that, if necessary, the conditions of gaseous feeding of the gas or notably of the mixture (B.sub.2 H.sub.6) (SiH.sub.4) (S.sub.2) can be modified. The measurement of the density is preferably carried out by means of a gaseous density meter, of the type comprising a vibrating tube which is under the effect of electrical excitation, the frequency of the vibration depending on the density of the mixture crossing said vibrating tube, and then by processing the frequency information, optionally as a function of other information such as the pressure and temperature of the gaseous mixture, in order to continuously determine the value of the density of said mixture.

Information such as the density can be used in order to modify the conditions of feeding, particularly of the mixture B.sub.2 H.sub.6 -SiH.sub.4, for example by controlling the flow of gas or the flow of the gaseous mixture and/or by combining it with a additional corrector flow stream, for example one having a diborane (B.sub.2 H.sub.6) base in combination with an inert gas.

The invention also relates to the implementation of this process.

It is noted that although the present method focusses primarily on a process wherein a diborane gas is fed to a reactor in order to produce a borophosphosilicate glass, it is equally applicable to other processes wherein a gaseous feedstock is susceptible to side reactions forming undesired side products, such side products causing a change in the density of the gas which can be monitored so that, if necessary, adjustments in the feed materials can be carded out.

Thus, in a first aspect, the present invention relates to a process for supplying a gas to a reactor comprising the steps of:

(i) continuously measuring the density of the gas, the gas including at least one component which is susceptible to formation of an undesired side product as shown by a variation in density of the gas; and (ii) modifying feed conditions of the gas if formation of the undesired side product is shown by a variation in the density of the gas.

In a more preferred aspect, the present invention relates to a process for supplying a gas comprising a mixture of B.sub.2 H.sub.6 and SiH.sub.4 to a reactor for growing layers of borophosphosilicate glass comprising the steps of:

(i) continuously measuring the density of the gas by (a) passing a stream of the gas across a vibrating tube under the effect of electrical excitation; and (b) measuring the density of the gas as a function of frequency of the vibrating tube, a variation in density of the gas being indicative of the formation of undesired side products of B.sub.2 H.sub.6 including higher boranes; and, if formation of higher boranes is shown by a variation in density of the gas, (ii) modifying feed conditions of the gas.

In another aspect, the present invention relates to an apparatus for supplying a gas to a reactor comprising;

(i) a reservoir including a stock material which is a gas; (ii) a reactor into which the gas is fed; (iii) an input conduit between the stock material reservoir and the reactor, the input conduit being provided with a means for continuously measuring density of the gas, a variation in density of the gas being indicative of formation of an undesired side product in the gas; and (iv) means for modifying feed conditions of the gas in response to formation of the undesired side product as shown by a variation in the density of the gas.

With the foregoing as well as other objects, advantages, and features of the invention that will become hereinafter apparent, the nature of the invention may be more clearly understood by reference to the following Detailed Description of Preferred Embodiments, the Figure, and the appended claims.

DESCRIPTION OF THE DRAWING

The FIG. depicts a cross-sectional view of the density meter of the invention as part of a schematic illustration of the overall process of the invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Below there is set forth in detail a preferred embodiment for carrying out the process in the reference drawing, which is now discussed in detail.

A conduit (1) links a reservoir of stock material (2) containing an initial gaseous mixture comprising diborane and silane to a utilization reactor (3). On the conduit (1) is mounted a gaseous density meter (10) having a frame (11) incorporating, between an intake (12) and an output (13), a vibrating tube (14) under the effect of an electrical excitation via a conductor (15), all of which are associated with a pressure gauge (16) and a temperature gauge (17). The gaseous density meter (10) including the vibrating tube (14) is commercially available from SARATOSA AUTOMATION. The precise type which has been used for the present invention is type FD 771 EBZT 4. It is noted that the supplier of such device provides the requisite information for determining density of a gas based on the frequency of vibration of the tube.

While the temperature and the pressure of the gaseous stream are advantageously continuously monitored, such measurement is not essential as there typically will not occur over the course of a process very wide variations therein. For this reason, it is the measurement of the density of the stream based on the frequency of vibration of the vibrating tube which is the most important measurement. The frequency of vibration of the tube (14) is displayed on a frequency meter (18), the information relating to frequency as well as that relating to pressure and temperature being processed in a processing unit (19) in order to calculate and display a density value and, if necessary, to in addition be transferred in a comparator (20) of the displayed value which is used to modify the opening of a valve (21) in the conduit (1), and/or open more or less the valve (22) controlling the flow of additional diborane starting from an auxiliary stock (23) of a mixture of diborane and inert gas (nitrogen, argon).

By way of example, there is given in the table below for a mixture B.sub.2 H.sub.6 /SiH.sub.4 /H.sub.2 the content in hydrogen (% H.sub.2) determined starting from pressure readings (in bars), from temperature readings (.degree. C.), and of measured frequency (.mu.s) determining a density thus permitting calculation of the hydrogen content. It should be apparent that calculation of the hydrogen content permits calculation of the content of diborane in the mixture. These calculations can be carried out using classical thermodynamical concepts by relating, at given conditions of temperature and pressure, the density of the mixture to the partial densities of each component, taking into account data such as the constant of gases "R", the compressibility factors "Z" of each gas (that are given in tables as a function of pressure and temperature), and also the conversion factor ".lambda." of the decomposition reactions (.lambda.B.sub.2 H.sub.6 H.sub.2) etc. For example, in the case of (SiH.sub.4, B.sub.2 H.sub.6) as the original feed, one can designate the components as follows:

______________________________________ Silane .alpha. Diborane .beta. Hydrogen .gamma.______________________________________ wherein .alpha., .beta. and .gamma. are in volume and wherein .alpha.+.beta.+.gamma.=s. As the mixture changes, it is evidenced by a change in the density ".rho.", the percent H.sub.2 of this new mixture is as follows: ##EQU1## wherein .lambda.=the conversion factor of the reaction (1<.lambda.<3). ##EQU2## wherein .rho..sub.0,SiH4, .rho..sub.0,B2H6, and .rho..sub.0,H2 represent the densities of each constituent at "normal" conditions (0.degree. C., 1 attm.) and wherein Z.sub.i represents the compressibility factors for each constituent and wherein R represents the gas constant.

It is the above correlation which enables the density calculated using the process of the invention to be used in determining how to adjust a feedstream, if necessary, due to transformation of the desired diborane feed into heavier non-desired boranes.

__________________________________________________________________________ Pressure Temperature Frequency Flow DensityHour bar .degree.C. .mu.s cc/min B.sub.2 H.sub.6 /SiH.sub.4 /H.sub.2 % H.sub.2-__________________________________________________________________________07:02:13 3.352 18.6 373.3318 199.5 1.420213 .799029907:03:39 3.353 18.6 373.3384 199.5 1.419841 .826752407:05:04 3.361 18.6 373.3621 199.4 1.419879 .823884207:06:31 3.354 18.6 373.3465 199.4 1.419862 .825154107:07:56 3.353 18.6 373.3474 199.5 1.420088 .808344707:09:22 3.361 18.6 373.3694 199.4 1.420316 .791348907:10:48 3.35 18.7 373.3328 199.4 1.420167 .802448607:12:14 3.353 18.7 373.3368 199.4 1.420599 .770321807:13:41 3.356 18.7 373.3415 199.4 1.42063 .768013107:15:06 3.353 18.7 373.3402 199.4 1.42018 .801462907:16:32 3.35 18.7 373.3314 199.4 1.420238 .797209607:17:58 3.354 18.7 373.336 199.4 1.420184 .801196607:19:24 3.35 18.7 373.3373 199.4 1.420401 .785053307:20:50 3.352 18.7 373.3374 199.4 1.420518 .776333407:22:16 3.349 18.7 373.3308 199.4 1.420447 .781572407:23:42 3.352 18.7 373.328 199.5 1.420415 .783978807:25:08 3.345 18.7 373.3081 199.5 1.420134 .80492607:26:34 3.348 18.7 373.3202 199.5 1.420195 .80035307:27:59 3.347 18.7 373.3164 199.4 1.420172 .802111107:29:25 3.345 18.7 373.3018 199.4 1.420145 .804091307:30:52 3.343 18.7 373.3015 202.2 1.420177 .801711607:32:17 3.348 18.7 373.309 199.4 1.420302 .792387907:33:43 3.344 18.8 373.3008 199.4 1.420213 .799012207:35:09 3.34 18.8 373.2899 199.4 1.420393 .785621507:36:35 3.336 18.8 373.2789 199.4 1.420628 .768128507:38:01 3.337 18.8 373.2755 199.4 1.420274 .79451907:39:27 3.338 18.8 373.2745 199.4 1.420701 .762720807:40:53 3.337 18.8 373.2733 199.4 1.420268 .794927507:42:19 3.337 18.8 373.2708 199.4 1.420457 .780853207:43:44 3.334 18.8 373.2673 199.4 1.420311 .791748507:45:11 3.335 18.8 373.2741 199.4 1.42041 .784360607:46:37 3.338 18.8 373.2753 199.4 1.420066 .809978607:48:02 3.342 18.8 373.2851 199.4 1.420515 .776537607:49:28 3.332 18.8 373.2645 199.4 1.420063 .810236107:50:54 3.333 18.8 373.2585 199.4 1.420448 .781554607:52:20 3.329 18.8 373.2497 199.4 1.420441 .782060807:53:46 3.332 18.8 373.2585 199.5 1.420482 .778970707:55:12 3.332 18.8 373.2602 199.4 1.420282 .793906307:56:38 3.33 18.8 373.2485 199.4 1.420051 .81113307:58:04 3.329 18.9 373.2466 199.5 1.420538 .774850407:59:30 3.332 18.9 373.2489 199.4 1.420727 .760713908:00:56 3.327 18.9 373.2392 199.4 1.420414 .784085308:02:22 3.328 18.9 373.2387 199.4 1.420523 .775969308:03:48 3.328 18.9 373.2393 199.4 1.420513 .776697509:05:14 3.326 18.9 373.2292 199.4 1.420829 .753157308:06:40 3.324 18.9 373.2231 199.4 1.420798 .755474908:08:06 3.323 18.9 373.2176 199.4 1.42029 .793302508:09:32 3.319 18.9 373.2126 199.4 1.42031 .79178408:10:58 3.322 18.9 373.2158 199.4 1.420668 .765153808:12:23 3.319 18.9 373.2078 199.5 1.420544 .774379808:13:49 3.322 18.9 373.2116 199.4 1.420047 .81142608:15:16 3.319 18.9 373.2003 199.4 1.420154 .80345208:16:41 3.317 18.9 373.1939 199.4 1.420165 .802626208:18:07 3.317 18.9 373.199 199.4 1.420003 .81467608:19:33 3.319 18.9 373.2029 199.4 1.419958 .818014708:21:00 3.315 19 373.1924 199.4 1.420605 .769815608:22:26 3.315 19 373.1944 199.4 1.420534 .7750991__________________________________________________________________________

Although only preferred embodiments have been specifically illustrated and described above, it will be appreciated that many modifications and variations of the invention are possible in view of the above teachings without deviating from the spirit and intended scope of the invention.

Claims

1. A process for supplying a gas to a reactor comprising the steps of:

(i) continuously measuring density of the gas, said gas including at least one component which is susceptible to formation of an undesired side product as shown by a variation in density of said gas; and

(ii) modifying feed conditions of said gas if formation of the undesired side product is shown by a variation in the density of said gas.

2. The process according to claim 1 wherein said component susceptible to formation of an undesired side product is diborane (B.sub.2 H.sub.6).

3. The process according to claim 1 wherein the step of measuring the density of the gas further comprises the steps of:

(i) passing a stream of said gas across a vibrating tube under the effect of electrical excitation; and

(ii) measuring the density of said gas as a function of frequency of said vibrating tube.

4. The process according to claim 2 wherein the gas supplied to the reactor comprises a mixture of B.sub.2 H.sub.6 and SiH.sub.4.

5. The process according to claim 4 wherein the B.sub.2 H.sub.6 and SiH.sub.4 are present in amounts effective for growing layers of borophosphosilicate glass.

6. The process according to claim 4 wherein the undesired side product is a higher borane including tetraborane (Bhd 4H.sub.10) and/or pentaborane 11 (B.sub.5 H.sub.11).

7. The process according to claim 3 wherein the step of measuring the density of the gas further comprises, in addition to measuring the frequency of the vibration of said tube, the steps of measuring pressure, temperature, or both of the gas.

8. The process according to claim 4 wherein said step of modifying the feed conditions of said gas further comprises modifying feeding conditions of the mixture of B.sub.2 H.sub.6 and SiH.sub.4.

9. The process according to claim 8 wherein the feeding conditions for the mixture of B.sub.2 H.sub.6 and SiH.sub.4 are modified by controlling the flow of the gas and/or by combining the gas with an additional correcting stream having a base of B.sub.2 H.sub.6.

10. A process for supplying a gas comprising a mixture of B.sub.2 H.sub.6 and SiH.sub.4 to a reactor for growing layers of borophosphosilicate glass comprising the steps of:

(i) continuously measuring the density of the gas by (a) passing a stream of said gas across a vibrating tube under the effect of electrical excitation; and (b) measuring the density of said gas as a function of frequency of said vibrating tube, a variation in density of said gas being indicative of the formation of undesired side products of B.sub.2 H.sub.6 including higher boranes; and, if formation of higher boranes is shown by a variation in density of said gas,

(ii) modifying feed conditions of said gas.

11. The process according to claim 1, wherein said undesired side product is a gaseous side product.