The present invention relates generally to improved semiconductor imaging devices and in particular to a silicon imaging device that can be fabricated using a standard CMOS process.
There are a number of different types of semiconductor-based imagers, including charge coupled devices (CCDs), photodiode arrays, charge injection devices and hybrid focal plane arrays. CCD technology is often employed for image acquisition and enjoys a number of advantages which makes it the incumbent technology, particularly for small size imaging applications. CCDs are capable of large formats with small pixel size and they employ low noise charge domain processing techniques.
However, CCD imagers also suffer from a number of disadvantages. For example, they are susceptible to radiation damage, they exhibit destructive read-out over time, they require good light shielding to avoid image smear and they have a high power dissipation for large arrays. Additionally, while offering high performance, CCD arrays are difficult to integrate with CMOS processing in part due to a different processing technology and to their high capacitances, complicating the integration of on-chip drive and signal processing electronics with the CCD array. While there have been some attempts to integrate on-chip signal processing with CCD arrays, these attempts have not been entirely successful. CCDs also must transfer an image by line charge transfers from pixel to pixel, requiring that the entire array be read out into a memory before individual pixels or groups of pixels can be accessed and processed. This takes time. CCDs may also suffer from incomplete charge transfer from pixel to pixel which results in image smear.
Because of the inherent limitations in CCD technology, there is an interest in CMOS imagers for possible use as low cost imaging devices. A fully compatible CMOS sensor technology enabling a higher level of integration of an image array with associated processing circuits would be beneficial to many digital applications such as, for example, in cameras, scanners, machine vision systems, vehicle navigation systems, video telephones, computer input devices, surveillance systems, auto focus systems, star trackers, motion detection systems, image stabilization systems and data compression systems for high-definition television.
The advantages of CMOS imagers over CCD imagers are that CMOS imagers have a low voltage operation and low power consumption; CMOS imagers are compatible with integrated on-chip electronics (control logic and timing, image processing, and signal conditioning such as A/D conversion); CMOS imagers allow random access to the image data; and CMOS imagers have lower fabrication costs as compared with the conventional CCD because standard CMOS processing techniques can be used. Additionally, low power consumption is achieved for CMOS imagers because only one row of pixels at a time needs to be active during the readout and there is no charge transfer (and associated switching) from pixel to pixel during image acquisition. On-chip integration of electronics is particularly advantageous because of the potential to perform many signal conditioning functions in the digital domain (versus analog signal processing) as well as to achieve a reduction in system size and cost.
A CMOS imager circuit includes a focal plane array of pixel cells, each one of the cells including either a photogate, photoconductor or a photodiode overlying a substrate for accumulating photo-generated charge in the underlying portion of the substrate. A readout circuit is connected to each pixel cell and includes at least an output field effect transistor formed in the substrate and a charge transfer section formed on the substrate adjacent the photogate, photoconductor or photodiode having a sensing node, typically a floating diffusion node, connected to the gate of an output transistor. The imager may include at least one electronic device such as a transistor for transferring charge from the underlying portion of the substrate to the floating diffusion node and one device, also typically a transistor, for resetting the node to a predetermined charge level prior to charge transference.
In a CMOS imager, the active elements of a pixel cell perform the necessary functions of: (1) photon to charge conversion; (2) accumulation of image charge; (3) transfer of charge to the floating diffusion node accompanied by charge amplification; (4) resetting the floating diffusion node to a known state before the transfer of charge to it; (5) selection of a pixel for readout; and (6) output and amplification of a signal representing pixel charge. Photo charge may be amplified when it moves from the initial charge accumulation region to the floating diffusion node. The charge at the floating diffusion node is typically converted to a pixel output voltage by a source follower output transistor. The photosensitive element of a CMOS imager pixel is typically either a depleted p-n junction photodiode or a field induced depletion region beneath a photogate. For photodiodes, image lag can be eliminated by completely depleting the photodiode upon readout.
CMOS imagers of the type discussed above are generally known as discussed, for example, in Nixon et al., “256×256 CMOS Active Pixel Sensor Camera-on-a-Chip,” IEEE Journal of Solid-State Circuits, Vol. 31(12), pp. 2046-2050 (1996); Mendis et al., “CMOS Active Pixel Image Sensors,” IEEE Transactions on Electron Devices, Vol. 41(3), pp. 452-453 (1994), as well as U.S. Pat. No. 5,708,263 and U.S. Pat. No. 5,471,515, which are herein incorporated by reference.
To provide context for the invention, an exemplary CMOS imaging circuit is described below with reference to FIG. 1. The circuit described below, for example, includes a photogate for accumulating photo-generated charge in an underlying portion of the substrate. It should be understood that the CMOS imager may include a photodiode or other image to charge converting device, in lieu of a photogate, as the initial accumulator for photo-generated charge.
Reference is now made to
The photodetector circuit 14 is shown in part as a cross-sectional view of a semiconductor substrate 16 typically a p-type silicon, having a surface well of p-type material 20. An optional layer 18 of p-type material may be used if desired, but is not required. Substrate 16 may be formed of, for example, Si, SiGe, Ge, or GaAs. Typically the entire substrate 16 is p-type doped silicon substrate and may contain a surface p-well 20 (with layer 18 omitted), but many other options are possible, such as, for example p on p− substrates, p on p+ substrates, p-wells in n-type substrates or the like. The terms wafer or substrate used in the description includes any semiconductor-based structure having an exposed surface in which to form the circuit structure used in the invention. Wafer and substrate are to be understood as including silicon-on-insulator (SOI) technology, silicon-on-sapphire (SOS) technology, doped and undoped semiconductors, epitaxial layers of silicon supported by a base semiconductor foundation, and other semiconductor structures. Furthermore, when reference is made to a wafer or substrate in the following description, previous process steps may have been utilized to form regions/junctions in the base semiconductor structure or foundation.
An insulating layer 22 such as, for example, silicon dioxide is formed on the upper surface of p-well 20. The p-type layer may be a p-well formed in substrate 16. A photogate 24 thin enough to pass radiant energy or of a material which passes radiant energy is formed on the insulating layer 22. The photogate 24 receives an applied control signal PG which causes the initial accumulation of pixel charges in n+ region 26. The n+ type region 26, adjacent one side of photogate 24, is formed in the upper surface of p-well 20. A transfer gate 28 is formed on insulating layer 22 between n+ type region 26 and a second n+ type region 30 formed in p-well 20. The n+ regions 26 and 30 and transfer gate 28 form a charge transfer transistor 29 which is controlled by a transfer signal TX. The n+ region 30 is typically called a floating diffusion region. It is also a node for passing charge accumulated thereat to the gate of a source follower transistor 36 described below.
A reset gate 32 is also formed on insulating layer 22 adjacent and between n+ type region 30 and another n+ region 34 which is also formed in p-well 20. The reset gate 32 and n+ regions 30 and 34 form a reset transistor 31 which is controlled by a reset signal RST. The n+ type region 34 is coupled to voltage source VDD, e.g., 5 volts. The transfer and reset transistors 29, 31 are n-channel transistors as described in this implementation of a CMOS imager circuit in a p-well. It should be understood that it is possible to implement a CMOS imager in an n-well in which case each of the transistors would be p-channel transistors. It should also be noted that while
Photodetector circuit 14 also includes two additional n-channel transistors, source follower transistor 36 and row select transistor 38. Transistors 36, 38 are coupled in series, source to drain, with the source of transistor 36 also coupled over lead 40 to voltage source VDD and the drain of transistor 38 coupled to a lead 42. The drain of row select transistor 38 is connected via conductor 42 to the drains of similar row select transistors for other pixels in a given pixel row. A load transistor 39 is also coupled between the drain of transistor 38 and a voltage source VSS, e.g. 0 volts. Transistor 39 is kept on by a signal VLN applied to its gate.
The imager includes a readout circuit 60 which includes a signal sample and hold (S/H) circuit including a S/H n-channel field effect transistor 62 and a signal storage capacitor 64 connected to the source follower transistor 36 through row transistor 38. The other side of the capacitor 64 is connected to a source voltage VSS. The upper side of the capacitor 64 is also connected to the gate of a p-channel output transistor 66. The drain of the output transistor 66 is connected through a column select transistor 68 to a signal sample output node VOUTS and through a load transistor 70 to the voltage supply VDD. A signal called “signal sample and hold” (SHS) briefly turns on the S/H transistor 62 after the charge accumulated beneath the photogate electrode 24 has been transferred to the floating diffusion node 30 and from there to the source follower transistor 36 and through row select transistor 38 to line 42, so that the capacitor 64 stores a voltage representing the amount of charge previously accumulated beneath the photogate electrode 24.
The readout circuit 60 also includes a reset sample and hold (S/H) circuit including a S/H transistor 72 and a signal storage capacitor 74 connected through the S/H transistor 72 and through the row select transistor 38 to the source of the source follower transistor 36. The other side of the capacitor 74 is connected to the source voltage VSS. The upper side of the capacitor 74 is also connected to the gate of a p-channel output transistor 76. The drain of the output transistor 76 is connected through a p-channel column select transistor 78 to a reset sample output node VOUTR and through a load transistor 80 to the supply voltage VDD. A signal called “reset sample and hold” (SHR) briefly turns on the S/H transistor 72 immediately after the reset signal RST has caused reset transistor 31 to turn on and reset the potential of the floating diffusion node 30, so that the capacitor 74 stores the voltage to which the floating diffusion node 30 has been reset.
The readout circuit 60 provides correlated sampling of the potential of the floating diffusion node 30, first of the reset charge applied to node 30 by reset transistor 31 and then of the stored charge from the photogate 24. The two samplings of the diffusion node 30 charges produce respective output voltages VOUTR and VOURS of the readout circuit 60. These voltages are then subtracted (VOUTS−VOUTR) by subtractor 82 to provide an output signal terminal 81 which is an image signal independent of pixel to pixel variations caused by fabrication variations in the reset voltage transistor 31 which might cause pixel to pixel variations in the output signal.
A transfer gate voltage TX, similar to the reset pulse RST, is then applied to transfer gate 28 of transistor 29 to cause the charge in n+ region 26 to transfer to floating diffusion node 30. It should be understood that for the case of a photogate, the transfer gate voltage TX may be pulsed or held to a fixed DC potential. For the implementation of a photodiode with a transfer gate, the transfer gate voltage TX must be pulsed. The new output voltage on line 42 generated by source follower transistor 36 current is then sampled onto capacitor 64 by enabling the sample and hold switch 62 by signal SHS. The column select signal is next applied to transistors 68 and 70 and the respective charges stored in capacitors 64 and 74 are subtracted in subtractor 82 to provide a pixel output signal at terminal 81. It should also be noted that CMOS imagers may dispense with the transfer gate 28 and associated transistor 29, or retain these structures while biasing the transfer transistor 29 to an always “on” state.
The operation of the charge collection of the CMOS imager is known in the art and is described in several publications such as Mendis et al., “Progress in CMOS Active Pixel Image Sensors,” SPIE Vol. 2172, pp. 19-29 (1994); Mendis et al., “CMOS Active Pixel Image Sensors for Highly Integrated Imaging Systems,” IEEE Journal of Solid State Circuits, Vol. 32(2) (1997); and Eric R Fossum, “CMOS Image Sensors: Electronic Camera on a Chip,” IEDM Vol. 95, pp. 17-25 (1995) as well as other publications. These references are incorporated herein by reference.
Quantum efficiency is a problem in some imager applications due to the diffusion of signal carriers out of the photosite and into the substrate, where they become effectively lost. The loss of signal carriers results in decreased signal strength, increased cross talk, and the reading of an improper value for the adjacent pixels.
There is needed, therefore, an improved pixel sensor cell for use in an imager that exhibits improved quantum efficiency, a better signal-to-noise ratio, and reduced cross talk. A method of fabricating a pixel sensor cell exhibiting these improvements is also needed.
The present invention provides a pixel sensor cell formed in a retrograde well in a semiconductor substrate having improved quantum efficiency, an improved signal-to-noise ratio, and reduced cross talk. The retrograde well comprises a doped region with a vertically graded dopant concentration that is lowest at the substrate surface, and highest at the bottom of the well. The retrograde well would have an entire array of pixels formed therein, and may also have peripheral circuitry formed therein. If the peripheral circuitry is formed in the retrograde well, the well may have a different dopant profile in the peripheral region than in the array region. The highly concentrated region at the bottom of the retrograde well reflects signal carriers back to the photosensor so that they are not lost to the substrate. Also provided are methods for forming a pixel sensor cell in the retrograde well of the present invention.
Additional advantages and features of the present invention will be apparent from the following detailed description and drawings which illustrate preferred embodiments of the invention.
In the following detailed description, reference is made to the accompanying drawings which form a part hereof, and in which is shown by way of illustration specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention, and it is to be understood that other embodiments may be utilized, and that structural, logical and electrical changes may be made without departing from the spirit and scope of the present invention.
The terms “wafer” and “substrate” are to be understood as including silicon-on-insulator (SOI) or silicon-on-sapphire (SOS) technology, doped and undoped semiconductors, epitaxial layers of silicon supported by a base semiconductor foundation, and other semiconductor structures. Furthermore, when reference is made to a “wafer” or “substrate” in the following description, previous process steps may have been utilized to form regions or junctions in the base semiconductor structure or foundation. In addition, the semiconductor need not be silicon-based, but could be based on silicon-germanium, germanium, or gallium arsenide. For exemplary purposes an imager formed of n-channel devices in a retrograde p-well is illustrated and described, but it should be understood that the invention is not limited thereto, and may include other combinations such as an imager formed of p-channel devices in a retrograde n-well.
The term “pixel” refers to a picture element unit cell containing a photosensor and transistors for converting electromagnetic radiation to an electrical signal. For purposes of illustration, a representative pixel is illustrated in the figures and description herein, and typically fabrication of all pixels in an imager will proceed simultaneously in a similar fashion. The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is defined by the appended claims.
The structure of pixel cells 14 formed in retrograde wells 20 of the first embodiment are shown in more detail in
A second retrograde well (not shown) may be formed in the substrate 16, and may have peripheral circuitry, such as, e.g., logic circuitry, formed therein. This second well may be doped similarly or differently from the first retrograde well 20, for example, the first retrograde well 20 may be doped to a first dopant level such as about 3×1017 atoms per cm3 at the bottom of the well and the second well may be doped to a second dopant level such as 5×1016 at the bottom of the well.
The transistor gates form the pixel cell 14 as shown: a photogate 24, a transfer gate 28 for transfer transistor 29, and a reset transistor gate 32 for the reset transistor 31. In addition, the photosensitive element in the pixel cell 14 is shown to be a photogate 24, but other photosensitive elements such as a photodiode or a photoconductor could be used. The source follower transistor and the row select transistor are not shown. The transfer gate 28 and the reset gate 32 include a gate oxide layer 106 on the retrograde well 20, and a conductive layer 108 of doped polysilicon, tungsten, or other suitable material over the gate oxide layer 106. An insulating cap layer 110 of, for example, silicon dioxide, silicon nitride, or ONO (oxide-nitride-oxide), may be formed if desired; also a more conductive layer such as a silicide layer (not shown) may be used between the conductive layer 108 and the cap 110 of the transfer gate stack 28, source follower gate, row select gate, and reset gate stack 32, if desired. Insulating sidewalls 112 are also formed on the sides of the gate stacks 28, 32. These sidewalls may be formed of, for example, silicon dioxide or silicon nitride or ONO. The transfer gate is not required but may advantageously be included. The photogate 24 is a semitransparent conductor and is shown as an overlapping gate. In this case there is a second gate oxide 105 over the retrograde well and under the photogate.
Underlying the photogate 24 is a doped region 26 called the photosite, where photogenerated charges are stored. In between the reset transistor gate 32 and the transfer gate 28 is a doped region 30 that is the source for the reset transistor 31, and on the other side of the reset transistor gate 32 is a doped region 34 that acts as a drain for the reset transistor 31. The doped regions 26, 30, 34 are doped to a second conductivity type, which for exemplary purposes is treated as n-type. The second doped region 30 is the floating diffusion region, sometimes also referred to as a floating diffusion node, and it serves as the source for the reset transistor 31. The third doped region 34 is the drain of the reset transistor 31, and is also connected to voltage source Vdd.
As shown in
The retrograde well 20 is manufactured through a process described as follows, and illustrated by
Ion implantation is performed by placing the substrate 16 in an ion implanter, and implanting appropriate dopant ions into the substrate 16 at an energy of 100 keV to 5 MeV to form retrograde wells 20 having a dopant concentration that is lowest at the surface, and highest at the bottom of the well. The dopant concentration at the top of the retrograde well 20 is within the range of about 5×1014 to about 1×1017 atoms per cm3, and is preferably within the range of about 1×1015 to about 5×1016 atoms per cm3, and most preferably is about 5×1015 atoms per cm3. At the bottom of the retrograde well 20, the dopant concentration is within the range of about 1×1016 to about 2×1018 atoms per cm3, and is preferably within the range of about 5×1016 to about 1×1018 atoms per cm3, and most preferably is about 3×1017 atoms per cm3. If the retrograde well is to be a p-type well, a p-type dopant, such as boron, is implanted, and if the well 20 is to be an n-type well, an n-type dopant, such as arsenic, antimony, or phosphorous is implanted. The resultant structure is shown in FIG. 8. Multiple high energy implants may be used to tailor the profile of the retrograde well 20.
Referring now to
Subsequent to formation of the retrograde well 20, the devices of the pixel sensor cell 14, including the photogate 24, the transfer gate 28, reset transistor 31, the source follower 36 and the row select transistor 38 are formed by well-known methods. Doped regions 26, 30, and 34 are formed in the retrograde well 20, and are doped to a second conductivity type, which for exemplary purposes will be considered to be n-type. The doping level of the doped regions 26, 30, 34 may vary but should be higher than the doping level at the top of the retrograde well 20, and greater than 5×1016 atoms per cm3. If desired, multiple masks and resists may be used to dope these regions to different levels. Doped region 26 may be variably doped, such as either n+ or n− for an n-channel device. Doped region 34 should be strongly doped, i.e., for an n-channel device, the doped region 34 will be doped as n+. Doped region 30 is typically strongly doped (n+), and would not be lightly doped (n−) unless a buried contact is also used.
The pixel sensor cell 14 is essentially complete at this stage, and conventional processing methods may be used to form contacts and wiring to connect gate lines and other connections in the pixel cell 14. For example, the entire surface may then be covered with a passivation layer of, e.g., silicon dioxide, BSG, PSG, or BPSG, which is CMP planarized and etched to provide contact holes, which are then metallized to provide contacts to the photogate, reset gate, and transfer gate. Conventional multiple layers of conductors and insulators may also be used to interconnect the structures in the manner shown in FIG. 1.
A typical processor based system which includes a CMOS imager device according to the present invention is illustrated generally at 400 in
A processor system, such as a computer system, for example generally comprises a central processing unit (CPU) 444, e.g., a microprocessor, that communicates with an input/output (I/O) device 446 over a bus 452. The CMOS imager 442 also communicates with the system over bus 452. The computer system 400 also includes random access memory (RAM) 448, and, in the case of a computer system may include peripheral devices such as a floppy disk drive 454 and a compact disk (CD) ROM drive 456 which also communicate with CPU 444 over the bus 452. CMOS imager 442 is preferably constructed as an integrated circuit which includes pixels containing a photosensor such as a photogate or photodiode formed in a retrograde well, as previously described with respect to
As can be seen by the embodiments described herein, the present invention encompasses a pixel sensor cell formed in a retrograde well. The pixel sensor cell has improved quantum efficiency and an improved signal-to-noise ratio due to the presence of a doping gradient induced electric field created in the bottom of the retrograde well which reflects signal carriers back to the photosensitive node. By reflecting photogenerated carriers back to the storage node the retrograde p-well also reduces the number of carriers diffusing to adjacent pixels and so also reduces cross talk.
It should again be noted that although the invention has been described with specific reference to CMOS imaging circuits having a photogate and a floating diffusion region, the invention has broader applicability and may be used in any CMOS imaging apparatus. Similarly, the process described above is but one method of many that could be used. The above description and drawings illustrate preferred embodiments which achieve the objects, features and advantages of the present invention. It is not intended that the present invention be limited to the illustrated embodiments. Any modification of the present invention which comes within the spirit and scope of the following claims should be considered part of the present invention.
This application is a divisional of U.S. patent application Ser. No. 09/918,450, filed Aug. 1, 2001 now U.S. Pat. No. 6,483,129, which is a divisional of U.S. patent application Ser. No. 09/334,261, filed Jun. 6, 1999, now U.S. Pat. No. 6,310,366 entitled Retrograde Well Structure For CMOS Imager, each of which is herein incorporated by reference in its entirety.
Number | Name | Date | Kind |
---|---|---|---|
4374700 | Scott et al. | Feb 1983 | A |
4831426 | Kimata et al. | May 1989 | A |
4851890 | Miyatake | Jul 1989 | A |
4859624 | Goto | Aug 1989 | A |
4907050 | Yamada | Mar 1990 | A |
4963973 | Watanabe et al. | Oct 1990 | A |
4980735 | Yamawaki | Dec 1990 | A |
5150177 | Robinson et al. | Sep 1992 | A |
5151385 | Yamamoto et al. | Sep 1992 | A |
5268316 | Robinson et al. | Dec 1993 | A |
5293237 | Yonemoto | Mar 1994 | A |
5319604 | Imondi et al. | Jun 1994 | A |
5428239 | Okumura et al. | Jun 1995 | A |
5461425 | Fowler et al. | Oct 1995 | A |
5471515 | Fossum et al. | Nov 1995 | A |
5541402 | Ackland et al. | Jul 1996 | A |
5576763 | Ackland et al. | Nov 1996 | A |
5608243 | Chi et al. | Mar 1997 | A |
5614744 | Merrill | Mar 1997 | A |
5625210 | Lee et al. | Apr 1997 | A |
5705846 | Merrill | Jan 1998 | A |
5708263 | Wong | Jan 1998 | A |
5747840 | Merrill | May 1998 | A |
5757045 | Tsai et al. | May 1998 | A |
5773863 | Burr et al. | Jun 1998 | A |
5814866 | Borland | Sep 1998 | A |
5859450 | Clark et al. | Jan 1999 | A |
6072206 | Yamashita et al. | Jun 2000 | A |
6096573 | Chen | Aug 2000 | A |
6147366 | Drottar et al. | Nov 2000 | A |
6150683 | Merrill et al. | Nov 2000 | A |
6156596 | Jwo | Dec 2000 | A |
6184055 | Yang et al. | Feb 2001 | B1 |
6268250 | Helm | Jul 2001 | B1 |
Number | Date | Country |
---|---|---|
2-178864 | Jul 1990 | JP |
02178964 | Jul 1990 | JP |
Number | Date | Country | |
---|---|---|---|
20030180982 A1 | Sep 2003 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 09918450 | Aug 2001 | US |
Child | 10291670 | US | |
Parent | 09334261 | Jun 1999 | US |
Child | 09918450 | US |