Ring-type sputtering target

Abstract

The sputtering target has a design for uniformly depositing a material on a substrate. The target contains a circular disk; and the disk has a radius and a top surface. The top surface has a center region within the inner half of the radius, an outer ring-shaped region within the outer half of the radius and a base region separating the center region from the ring-shaped region. The outer ring-shaped region has a projection height for extending the life of the sputtering target. The center region has a projection height of less than the projection height of the outer ring-shaped region for increasing the sputtering deposition rate on the substrate adjacent the center region.

Description

FIELD OF THE INVENTION

[0001] This invention relates to extended life sputtering targets and a method for using these extended life sputtering targets.

BACKGROUND OF THE INVENTION

[0002] Sputtering is a process that coats semiconductor wafers or other substrates within inert-gas-filled processing chambers. These chambers contain sputtering targets and an electrically biased wafer adjacent the sputtering target. An electric field within the chambers ionizes the inert gas and dislodges atoms from the target to deposit sputter target material on the wafer. Typically, processing chambers may contain magnetrons that generate annular groove patterns in portions of the sputtering targets. Unfortunately, these grooves can dramatically shorten a sputtering targets' life. Furthermore, the adverse effect of these grooves tends to become exaggerated for targets having increased diameters.

[0003] Several patents disclose raised rings or surfaces for increasing target life. For example, Strauss et al., in EP Pat. Pub. No. 1 087 033, disclose sputtering targets having two spaced annular rings. These rings correspond to target areas that experience the greatest erosion during sputtering. Daxinger et al., in U.S. Pat. No. 6,068,742, disclose a reversible sputtering target. Each side of this target contains two circumferentially-shaped protrusions designed to increase target life. Masahura, in Japanese Pat. Pub. No. 4-173965 discloses a target containing a single projection ring. The projection ring has a smooth surface to prevent re-sticking of target material and a rough surface adjacent the smooth-surfaced rings. This combination decreases dusting effects over the sputtering process' entire life.

[0004] Recently, a ring-enhanced design has proven effective for sputtering layers used to construct memory chips. Since memory chips typically contain only two metal layers, film uniformity is not critical for these memory applications. Unlike memory chip applications, logic chip applications often require greater film uniformity. Unfortunately, targets containing ring-enhanced designs fail to produce the stringent film uniformity required for some logic applications. This may result from the increased number of layers deposited or the device design rules. Furthermore, since there are more metal layers in logic applications, poor uniformity becomes accentuated with each succeeding layer when a manufacturer skips chemical mechanical polishing (CMP) of the deposited layers. As the stacked film uniformity decreases, photolithography on the upper layers becomes more difficult.

[0005] Film uniformity is also important from a device fabrication standpoint. There is often some degree of over-etch when etching the device. If the etching is greatest in the wafer's center and the film is thinner in the center, then there is an increased possibility of device yield loss.

[0006] Furthermore, a lack of uniformity has a pronounced effect on film thickness and sheet resistance uniformity for large targets, such as those having a diameter in excess of 250 mm. In these large diameter targets, the rings can have a negative impact upon a target's useful life. As far as known, none of these ring-enhanced designs has received commercial acceptance for stringent device applications due to the above uniformity issue or other sputtering-induced defects.

SUMMARY OF THE INVENTION

[0007] The sputtering target has a design for uniformly depositing a material on a substrate. The target contains a circular disk; and the disk has a radius and a top surface. The top surface has a center region within the inner half of the radius, an outer ring-shaped region within the outer half of the radius and a base region separating the center region from the ring-shaped region. The outer ring-shaped region has a projection height for extending the life of the sputtering target. The center region has a projection height of less than the projection height of the outer ring-shaped region for increasing the sputtering deposition rate on the substrate adjacent the center region.

[0008] The method sputters a material on a substrate with a sputtering target or cathode. First ionizing an inert gas adjacent a cathode in a sputtering chamber prepares the chamber for sputtering. The cathode has an initial wafer to cathode spacing and a second wafer to cathode spacing for uniform sputtering. The second wafer to cathode spacing is greater than the initial wafer to cathode spacing. Dislodging atoms from the cathode with a rotating magnetron deposits a coating on the wafer using the initial wafer to cathode spacing. The initial spacing optimizes sputtering deposition uniformity for an initial period of time. Then dislodging additional atoms from the cathode with the rotating magnetron after the initial period of time deposits the coating on the wafer using the second wafer to cathode spacing. The second wafer to cathode spacing optimizes sputtering deposition uniformity during a second period of time.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] FIG. 1A is a top view of a sputtering target containing a disk-shaped center region.

[0010] FIG. 1B is a cross section of the sputtering target of FIG. 1A taken along line 1-1.

[0011] FIG. 2A is a top view of a sputtering target containing a ring-shaped center region.

[0012] FIG. 2B is a cross section of the sputtering target of FIG. 2A taken along line 2-2.

[0013] FIG. 3 is a schematic drawing that illustrates locations for measuring wafer film thickness.

[0014] FIG. 4 illustrates the improved uniformity achieved with the center region design.

DETAILED DESCRIPTION

[0015] Targets containing a raised outer ring and a lesser-raised inner region have resulted in improved sputter uniformity. This target has successfully performed with a conventional sputtering system and exhibits low sheet resistance (Rs) at the center of the wafer. Sheet resistance is an indirect method for comparing deposit thickness at several locations by measuring resistance to electrical flow.

[0016] The target advantageously has an initial optimal wafer to cathode spacing for uniform sputtering and a second wafer to cathode spacing for uniform sputtering. The second wafer to cathode spacing is greater than the initial wafer to cathode spacing. This shift in optimal wafer to cathode spacing advantageously occurs after sputtering at least about thirty percent of the cathode's life to further improve performance. Most advantageously, the shift occurs after sputtering at least about forty percent of the cathode's life. The exact distance of the initial and second location for optimum sputtering before and after the shift tends to vary from machine to machine. In addition, it is possible to adjust or shift the position more than one time to maintain optimal sputtering performance. But testing has shown that one shift after a set period of time provides excellent uniformity with minimal operator inconvenience.

[0017] Referring to FIGS. 1A and 1B, the target 10 contains a base region 12, a disk-shaped center region 14 and an outer ring-shaped region 16. Advantageously, ring-shaped region 16 extends upwardly adjacent an outer edge region 18 and outer edge 20. Most advantageously, the outer edge region 18 has a thickness equal to the thickness of the base region 14. Optionally, the ring-shaped region 16 can extend outwardly to the outer edge 20.

[0018] The target 10 has a radius R extending from the center 25 to the outer edge 20. The inner half of the radius contains the center region 14 and the outer half of the radius contains the ring-shaped region 16. Advantageously, the center region 14 is within about the inner thirty-five percent of the radial distance from the center 25 and the outer edge 20 and most advantageously within about the inner thirty percent. Similarly, the outer ring-shaped region 16 is most advantageously between seventy and ninety-five percent of the radial distance from the center 25 and the outer edge 20.

[0019] Center regions formed with a solid disk-like projection of uniform height have proven effective. Optionally, tapered regions 22 located between the base region 12 and the center region 14 and between the base region 12 and the ring-shaped region 16 serve to level-out sputtering in areas prone to non-uniform sputtering. In addition, flange 26 containing threaded openings 28 facilitates fastening of the sputtering target within a sputtering chamber.

[0020] FIG. 1B illustrates the difference in projection height between the outer ring-shaped region 16 and the center region 14. The projection height is a measure of the difference in thickness between the base region 12 and the center region 14 or the outer ring-shaped region 16. The decrease in projection height of the center region 14 in relation to the outer ring-shaped region 16 unexpectedly increases uniformity of the deposit. Furthermore, this advantageously results in the dislodging of atoms occurring at a greater rate in the center region and the outer ring-shaped region than in the base region.

[0021] Advantageously, the center region 14 has a projection height of at least less than about 20 percent of the outer ring-shaped region 16. For example, if the outer region 16 had a height of 5 mm, the center region 14 would have a height of 4 mm or less. Preferably, the center region 14 has a projection height that has a projection height of about 20 to 80 percent of the outer region's projection height. If a ring-containing target contains a center region that has no projection height, then the sputtering target performs poorly. Most advantageously, the center region 14 has a height that is about 30 to 70 percent of the outer ring-shaped region's projection height. A nominal center region projection height decrease of about 50 percent of the outer ring-shaped region 16 has proven most effective.

[0022] FIGS. 2A and 2B illustrate an optional embodiment where the center region 14 includes a disk-shaped projection 30. In this embodiment, the disk-shaped projection 30 contains a dimpled region 32. optionally, the dimpled region 32 has a thickness less than, equal to or greater than the base region 32. Most advantageously, the dimpled region 32 has a thickness equal to the base region 12. In addition, the dimpled region 32 may have a circular, star-pattern or other symmetrical or semi-symmetrical shape. Most advantageously, the dimpled region 32 has a symmetrical shape, such as the illustrated cylindrical shape.

COMPARATIVE EXAMPLE

[0023] A partially spent 300 mm diameter AlCu (0.5%) target having two-concentric projecting rings (4 mm height) produced film thickness uniformity out of a narrow specification after approximately 800 kwh of sputtering with an Endura System using an A-Type magnet(target installed in chamber 4 and a standard set of shields)—this system also provided the sputtering device for the Example below. The system's magnetron contains several magnets that spin about an axis to generate a more uniform field. Unfortunately, the spinning magnetron produces higher sheet resistance values at the center of the wafer than on the outside diameter (6 mm from edge)—see FIG. 3. This indicated a lower film thickness in the center of the wafer as compared to the outer area of the wafer.

[0024] Additional tests were run after the center of the target was modified by machining the inner ring to form a thin disc having a height of 2 mm. The target's 4 mm outer ring had worn to form a groove-like depression. After completion of these center modifications, the target was burned-in to 5 kwh prior to the testing. Tables 1 and 2 present the sheet resistance (Rs) uniformity and thickness data respectively for the partially spent 4 mm concentric ring and the modified-center version.

[0025] Table 1 measures Rs uniformity—(Percent 1 Sigma or one standard deviation) for a 200 mm oxide wafer at 49 sites using a 6 mm edge exclusion.

	TABLE 1
	Rs Uniformity (Percent 1 Sigma)
	˜884 kwh	˜890 kwh
Wafer/Cathode	4 mm Concentric	After Center
Spacing	Rings	Modification
(mm)	Wafer A	Wafer B	Wafer C	Wafer D
46	2.81		1.98
48	2.28		1.00
50	1.52		0.72
51	1.39		0.64
52	1.16	1.32	0.85	0.99
53	1.23		0.84

[0026] Table 1 illustrates an unexpected shift in optimum wafer to cathode spacing resulting from reducing the inner ring height. In addition, the modified center design improved Rs uniformity.

	TABLE 2
	Average Film Thickness
	˜884 kwh
	4 mm Concentric	After Center
Location	Rings	Modification
Center	9738 Å	9382 Å
Bottom	10104 Å	9454 Å
Right	10062 Å	9437 Å
Top	10092 Å	9465 Å
Left	10090 Å	9365 Å
Delta	366 Å	100 Å

[0027] Table 2 data originate from operating the Endura system for 60 seconds at 10.6 kw, with an 18 sccm chamber/15 sccm backing plate flow of argon at a temperature of 300° C. with a wafer to cathode spacing of 52 mm and a chamber pressure of 2 milliTorr. Delta measures the maximum difference in thickness (Å) between the center reading and any of the four outside diameter readings top, left, bottom and right at locations near the outside diameter in accordance with FIG. 3 (Standard Five-Point Test). Testing at a greater number of sites tends to lower the standard deviation or sigma value. Therefore, since the Standard Five-Point Test tests at only five sites, it is much more stringent than alternative tests that measure thickness at several locations.

Example

[0028] An Al—Cu(0.5%) sputtering target manufactured with a 4 mm high outer ring, having a 1.18 in. (3.0 cm) width, and a 2 mm high inner disc, having a 3.54 in. (9.0 cm) diameter, improved both sheet resistance and film thickness uniformity. Depositing approximately 1 micron films onto 200 mm thermal oxide wafers provided a basis for measuring targets' performance. Standard process conditions were used for the evaluation as follows:

Power                      10.6 kw
Argon Flow (chamber)       18 sccm
Argon flow (Backing plate) 15 sccm
Chamber pressure           2.04 mTorr
Temperature                300° C.
Target to wafer spacing    46 mm & 52 mm (thickness)
                           Variable (Rs uniformity)

[0029] Rs uniformity was measured at 49 sites on the 200 mm wafers using a 4D automated 4 point probe. A 6 mm edge exclusion was used. The film thicknesses were measured at 5 location on each wafer in accordance with the Standard Five-Point Test. The initial testing was completed at 3, 7 and 15 kwh for Rs Uniformity (Table 3) and 3, 5, 7, 9, 12 and 15 kwh intervals for film thickness (Table 4). The film thickness and Rs Uniformity measurements were made at a standard wafer to cathode spacing of 52 mm. In addition, tests completed at 100, to 1400 kwh relied upon varied wafer to cathode distances (44 to 53 mm) to locate the optimum spacing for the deposition of low Rs uniformity

[0030] Table 3 shows the Rs uniformity results for the target with different wafer to cathode spacings.

	TABLE 3
	Target Life/Rs Uniformity (Percent 1 Sigma)
Wafer/Cathode	3 kwh	7 kwh	15 kwh	100 kwh
Spacing	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer
(mm)	#1	#2	#1	#2	#1	#2	#1	#2
44			1.00%	1.22%	1.12%	1.01%	1.17%	1.08%
46			0.75%	0.80%	0.86%	0.89%	0.70%	0.62%
48			1.16%	1.11%	0.93%	0.72%	0.97%	1.10%
50			1.11%	1.13%	1.39%	1.82%	1.56%	1.45%
52	1.95%	2.02%	1.62%	1.44%	1.79%	1.88%	1.59%	1.89
53			2.02%	1.74%	1.88%	1.93%	2.02%	2.37%
	Target Life/Rs Uniformity (Percent 1 Sigma)
Wafer/Cathode	300 kwh	500 kwh	700 kwh	900 kwh
Spacing	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer
(mm)	#1	#2	#1	#2	#1	#2	#1	#2
44	1.13%	1.10%	1.85%	1.80%	2.12%	2.04%	1.64%	1.84%
46	0.92%	0.77%	0.79%	1.05%	1.14%	1.09%	1.31%	1.54%
48	1.14%	1.18%	0.92%	0.75%	0.75%	0.93%	0.69%	0.84%
50	1.17%	1.46%	1.45%	1.33%	0.75%	0.55%	0.69%	0.57%
52	1.68%	1.54%	1.71%	1.49%	1.24%	1.41%	1.35%	1.01%
53	2.27%	2.03%	1.33%	1.50%	1.29%	1.44%	1.78%	1.58%
	Target Life/Rs Uniformity (Percent 1 Sigma)
Wafer/Cathode	1100 kwh	1300 kwh	1400 kwh
Spacing	Wafer	Wafer	Wafer	Wafer	Wafer	Wafer
(mm)	#1	#2	#1	#2	#1	#2
44	2.24%	2.37%	2.07%	2.39%	2.18%	2.61%
46	1.99%	1.87%	1.42%	2.14%	1.54%	1.60%
48	1.19%	1.08%	1.52%	1.26%	1.28%	1.26%
50	1.23%	1.09%	1.35%	1.33%	0.65%	0.78%
52	0.79%	0.96%	1.19%	1.15%	0.79%	1.08%
53	1.42%	1.18%	1.50%	1.27%	1.00%	1.18%

[0031] These data indicate an unexpected initial decrease in optimum wafer to cathode distance for achieving maximum uniformity. The target having a center region of decreased thickness reduced the initial optimum wafer to cathode spacing to about 46 mm-a 6 mm two-ring target had an optimum uniformity with a wafer to cathode spacing between 50 and 52 mm. Then after approximately 900 kwh of sputtering, the optimum wafer to cathode distance increased to 52 mm.

[0032] Table 4 illustrates the uniformity in film thickness achieved with a wafer to cathode spacing of 52 mm.

TABLE 4
Kwh	Center	Top	Left	Bottom	Right	Delta
3	10394	10263	10225	10287	10245	169
5	10403	10177	10185	10152	10185	251
7	10659	10347	10302	10385	10325	357
9	10620	10320	10357	10317	10337	303
12	10738	10467	10342	10342	10452	396
15	11009	10455	10522	10457	10530	554
100	11042	10535	10435	10477	10457	607
300	10665	10115	10157	10085	10092	580
500	10837	10887	10800	10851	10910	110
700	9480	9563	9510	9472	9521	91
900	9289	9144	9101	9285	9192	188
1100	9008	9021	8960	9080	9011	120
1300	8625	8459	8424	8446	8462	201
1400	8100	7977	7898	8102	8071	204

[0033] As shown above and illustrated in FIG. 4, the delta in film thickness uniformity between the wafer center and outer diameter appears to follow the Rs uniformity data. Accordingly, the thickness differences were minimum at the lower Rs uniformity test points for the bulk of the target's life. Toward the end of the target's life however, there appears to be some divergence in this correlation.

[0034] Table 5 compares the delta thickness measurement results obtained for the target with a Standard Five-Point Test after each test period with a standard wafer to cathode spacing of 52 mm and at an optimum spacing of 46 mm.

	TABLE 5
		Optimum Wafer to	Standard Wafer to
		Cathode Spacing	Cathode Spacing
	Thickness Delta	46 mm	52 mm
	52 mm	46 mm	Rs Uniformity	RB Uniformity
kwh	(Å)	(Å)	(% 1 Sigma)	(% 1 Sigma)
100	607	50	0.70%	1.59%
300	580	80	0.92%	1.68%
500	110	90	0.79%	1.71%
700	91	188	1.14%	1.24%
900	188	161	1.31%	1.01%
1100	120	189	1.99%	0.79%
1300	201	207	1.42%	1.19%
1400	204	95	1.54%	0.79%

[0035] The data of Table 5 and FIG. 4 illustrate a two-part art method for optimizing sheet resistance or Rs uniformity. First, the optimal wafer to cathode spacing shifts inward in comparison to planar targets to 46 mm. Then, after the target burns for at least about 900 hours the spacing increases to 52 mm. This shift enables sputtering manufacturers to maintain Rs uniformity at a level less than about 1.5 percent one sigma and a maximum delta thickness of about 250 Å for the Standard Five Point Test. Most advantageously, it maintains Rs uniformity at a level less than about 1.3 percent one sigma.

[0036] Table 6 provides film thickness data for various 200 mm Al/Cu.5% targets, measured at 100 kwh with optimum wafer to cathode (W/C) spacings.

TABLE 6
Target	Life		W/C	Center	Top	Left	Bottom	Right	Delta
ID	(kwh)	Details	(mm)	(Å)	(Å)	(Å)	(Å)	(Å)	(Å)
A	880	4 mm Rings	52	9738	10104	10062	10092	10090	366
C	100	4 mm No-	52	10610	10730	10650	10620	10652	120
		Rings
D	100	6 mm Rings	52	11477	11040	11015	11212	10972	505
E	100	4 mm outer	52	11577	10682	10797	10737	10635	942
		ring only
A1	885	After center	52	9382	9454	9437	9465	9365	100
		modified
1A	100	4 mm-Outer/	52	11042	10535	10435	10477	10457	607
		2 mm Inner
2B	100	4 mm-Outer/	46	11067	11030	11017	11020	11062	50
		2 mm Inner
1A	300	4 mm-Outer/	52	10665	10115	10157	10085	10092	580
		2 mm Inner
2B	300	4 mm-Outer/	46	10715	10702	10782	10780	10752	80
		2 mm Inner
1A	500	4 mm-Outer/	52	10837	10887	10800	10851	10910	110
		2 mm Inner
2B	500	4 mm-Outer/	46	10189	10180	10200	10270	10245	90
		2 mm Inner

[0037] Targets containing a raised outer ring and a lesser-raised inner region facilitate improved sputter uniformity. This target has been successfully sputtered in a conventional sputtering system to produce high uniformity deposits. The target is particularly effective for aluminum and aluminum alloy sputter target designs. For example, the target coats substrates with a maximum of about 1.5 percent sigma sheet resistance uniformity. Furthermore, it has a life of at least 1000 kwh in a spinning magnetron sputtering chamber using a type A magnet. Most advantageously, the target has a life of at least 1200 kwh and has successfully tested to a life of at least 1400 kwh. This compares favorably to conventional planar designs that have a target life of approximately 900 kwh.

[0038] Many possible embodiments may be made of this invention without departing from the scope thereof, it is understood therefore that all matter set forth herein is to be interpreted as illustrative and not in a limiting sense.

Claims

1. A sputtering target for depositing a material on a substrate comprising a circular disk, the disk having a radius and a top surface, the top surface having a center region within the inner half of the radius, an outer ring-shaped region within the outer half of the radius and a base region separating the center region from the ring-shaped region, the outer ring-shaped region having a projection height for extending the life of the sputtering target and the center region having a projection height of less than the projection height of the outer ring-shaped region for increasing the sputtering deposition rate on the substrate adjacent the center region.

2. The sputtering target of claim 1 wherein the center region is a solid disk-shaped projection of uniform height.

3. The sputtering target of claim 1 wherein the center region contains a disk-shaped projection and a dimpled region within the disk-shaped projection.

4. The sputtering target of claim 1 wherein the center region has a projection height of at least about 20 percent less than the projection height of the outer ring-shaped portion region for decreasing the initial optimal uniformity wafer to cathode distance for sputtering uniformity.

5. A sputtering target for depositing a material on a substrate comprising a circular disk, the disk having a radius and a top surface, the top surface having a center region within the inner thirty-five percent of the radius, an outer ring-shaped region within the outer sixty percent of the radius and a base region separating the center region from the ring-shaped region, the outer ring-shaped region having a projection height for extending the life of the sputtering target and the center region having a projection height of about 20 to 80 percent less than the projection height of the outer ring-shaped region for increasing the sputtering deposition rate on the substrate adjacent the center region and the target having an initial wafer to cathode spacing and a second wafer to cathode spacing for uniform sputtering, the second wafer to cathode spacing being greater than the initial wafer to cathode spacing.

6. The sputtering target of claim 5 wherein the center region is a solid disk-like projection of uniform height.

7. The sputtering target of claim 5 wherein the center region contains a disk-shaped projection and a dimpled region within the disk-shaped region.

8. The sputtering target of claim 5 having tapered regions between the base region and the center region and between the base region and the outer ring-shaped region.

9. The sputtering target of claim 5 wherein the projection height of the center region is about 30 to 70 percent less than the projection height of the outer ring-shaped region.

10. The sputtering target of claim 5 wherein the disk has a center and an outer edge and the center region is within the inner thirty percent of the radial distance from the center and the outer edge and the outer ring-shaped region is between seventy and ninety-five percent of the radial distance from the center and the outer edge.

11. The sputtering target of claim 5 wherein the target is aluminum or an aluminum alloy and the target coats the substrate with a maximum of about 1.5 percent sigma sheet resistance uniformity and has a life of at least 1000 kwh in a spinning magnetron sputtering chamber using a type A magnet.

12. A method for sputtering a material on a substrate comprising: ionizing an inert gas adjacent a cathode in a sputtering chamber, the cathode having an initial wafer to cathode spacing for uniform sputtering and a second wafer to cathode spacing for uniform sputtering, the second wafer to cathode spacing being greater than the initial wafer to cathode spacing; dislodging atoms from the cathode with a rotating magnetron to deposit a coating on the wafer using the initial wafer to cathode spacing to optimize sputtering deposition uniformity for an initial period of time; and dislodging additional atoms from the cathode with the rotating magnetron after the initial period of time to deposit the coating on the wafer using the second wafer to cathode spacing to optimize sputtering deposition uniformity for a second period of time.

13. The method of claim 12 wherein the cathode has a center region, an outer ring-shaped region and a base region and the dislodging of atoms occurs at a greater rate in the center region and in the outer ring-shaped region than in the base region.

14. The method of claim 12 including the additional step of increasing the cathode to wafer distance after sputtering at least about thirty percent of the cathode life.

15. A method for sputtering a material on a substrate comprising: ionizing an inert gas adjacent a circular cathode in a sputtering chamber, the cathode having a radius and a top surface, the top surface having a center region within the inner half of the radius, an outer ring-shaped region within the outer half of the radius and a base region separating the center region from the ring-shaped region, the outer ring-shaped region having a projection height for extending the life of the sputtering target and the center region having a projection height of less than the projection height of the outer ring-shaped region and the cathode having an initial wafer to cathode spacing for uniform sputtering and a second wafer to cathode spacing for uniform sputtering, the second wafer to cathode spacing being greater than the initial wafer to cathode spacing; dislodging atoms from the cathode with a rotating magnetron to deposit a coating on the wafer using the initial wafer to cathode spacing to optimize sputtering deposition uniformity for an initial period of time; and dislodging additional atoms from the cathode with the rotating magnetron after the initial period of time to deposit the coating on the wafer using the second wafer to cathode spacing to optimize sputtering deposition uniformity for a second period of time.

16. The method of claim 15 wherein the dislodging of atoms occurs at a greater rate in the center region and in the outer ring-shaped region than in the base region.

17. The method of claim 15 including the additional step of increasing the cathode to wafer distance after sputtering at least about forty percent half of the cathode life.

18. The method of claim 5 wherein the cathode coats the substrate with a maximum 1.3 percent sigma sheet resistance uniformity and has a life of at least 1000 kwh using a type A magnet.