The present invention relates, in general, to semiconductor components and, more particularly, to semiconductor components having an extrusion monitoring structure.
Semiconductor component manufacturers are constantly striving to increase the speed of their components. Because a semiconductor component, such as a microprocessor, contains up to a billion transistors or devices, the focus for increasing speed has been to decrease gate delays of the semiconductor devices that make up the semiconductor component. As a result, the gate delays have been decreased to the point that speed is now primarily limited by the propagation delay of the metallization system used to interconnect the semiconductor devices with each other and with elements external to the semiconductor component. Metallization systems are typically comprised of a plurality of interconnect layers vertically separated from each other by a dielectric material and electrically coupled to each other by metal-filled vias or conductive plugs. Each layer contains metal lines, metal-filled vias, or combinations thereof separated by an insulating material. A figure of merit describing the delay of the metallization system is the Resistor-Capacitance (RC) delay. The RC delay can be derived from the resistance of the metal layer and the associated capacitance within and between different layers of metal in the metallization system.
The RC delay can be reduced by lowering either the capacitance of the metallization system, the resistance of the metallization system, or both. The capacitance can be lowered by decreasing the dielectric constant of the dielectric material and/or increasing the thickness of the dielectric material. The resistance of the metallization system can be lowered by decreasing the resistivity of the metallic interconnect layers, decreasing the resistivity of the conductive plugs that electrically couple the interconnect layers to each other, decreasing the length of the metallic interconnect, or increasing the thickness of the metal. Increasingly, semiconductor manufacturers are switching to metallization systems comprising copper because of its low resistivity and dielectric material having a low dielectric constant, i.e., low κ dielectrics. A drawback of this type of metallization system is that as the current density is increased, copper extrusion occurs which shorts adjacent conductor lines thereby causing the semiconductor component to fail. Detection of these types of shorts can be very difficult because of the number of metallization layers in high performance semiconductor components and their complex routing structure.
Accordingly, what is needed is a semiconductor component having an extrusion monitoring structure and a method for manufacturing the semiconductor component and monitoring the integrity of the metallization system.
The present invention satisfies the foregoing need by providing a semiconductor component having a metallization monitoring structure, a method for monitoring extrusion in a metallization system of a semiconductor component, and a method for manufacturing the monitoring structure. In accordance with one aspect, the present invention comprises a semiconductor component having a monitoring structure suitable for monitoring metal migration of a metallization system. The semiconductor component comprises first and second extrusion monitoring elements overlying a major surface of a semiconductor substrate. A test element is positioned between the first and second extrusion elements.
In accordance with another aspect, the present invention includes a method for monitoring extrusion in a metallization system of a semiconductor component. A semiconductor substrate is provided and first and second extrusion monitoring elements are formed over the semiconductor substrate. A test element is formed between the first and second extrusion monitoring elements. A test signal is applied through the test element, and a response parameter is monitored. The condition of the metallization system is indicated by the state of the response parameter.
In accordance with yet another aspect, the present invention comprises a method for manufacturing a monitoring structure which includes forming a test element between two extrusion monitoring elements.
The present invention will be better understood from a reading of the following detailed description, taken in conjunction with the accompanying drawing figures, in which like reference numbers designate like elements and in which:
Generally, the present invention provides a semiconductor component, a method for manufacturing a monitoring structure for use in the semiconductor component, and a method for monitoring the condition or state of a metallization system in the semiconductor component. In one aspect, the semiconductor component includes a semiconductor device formed in or from a semiconductor material and a metallization test structure formed over the semiconductor material. The semiconductor material is also referred to as a semiconductor substrate. In one embodiment, the metallization test structure comprises an active metal interconnect vertically positioned between a pair of passive metal interconnects, where the active metal interconnect includes a vertically oriented notch. One of the passive metal interconnects includes an extension or protrusion aligned to the notch.
In another embodiment, the active metal interconnect has vertically oriented notches on both top and bottom sides. In other words, a first vertically oriented notch extends into the top side of the active metal interconnect, i.e., towards the semiconductor substrate and a second vertically oriented notch extends into the second or bottom side of the active metal interconnect, i.e., away from the semiconductor substrate. The passive metal interconnect on the top side has an extension aligned to the first notch in the active metal interconnect and the passive metal interconnect on the bottom side has an extension aligned to the second notch in the active metal interconnect.
In yet another embodiment, the metallization test structure comprises an active metal interconnect positioned between a pair of passive metal interconnects, where the active metal interconnect includes a laterally oriented notch positioned on one side. One of the passive metal interconnects includes an extension or protrusion aligned to the notch.
In yet another embodiment, the active metal interconnect has laterally oriented notches on both sides. In other words, a first laterally oriented notch extends into a first side of the active metal interconnect, i.e., towards the semiconductor substrate and a second laterally oriented notch extends into the second or opposite side of the active metal interconnect, i.e., away from the semiconductor substrate. The passive metal interconnect on the first side has an extension aligned to the first notch in the active metal interconnect and the passive metal interconnect on the second side has an extension aligned to the second notch in the active metal interconnect.
In yet another embodiment, the metallization test structure comprises an active metal interconnect vertically positioned between upper and lower passive metal interconnects and laterally positioned between adjacent passive metal interconnects, where the active metal interconnect includes a vertically oriented notch and a laterally oriented notch. At least one of the upper and lower passive metal interconnects includes an extension or protrusion aligned to the notch and at least one of the laterally adjacent passive metal interconnects.
The active metal interconnect is referred to as being active because it is used to conduct electrons. In the absence of a short, the passive metal interconnects do not conduct electrons, hence they are referred to as passive metal interconnects. When the active metal interconnect is formed using a damascene process, it is referred to as a damascene structure. Likewise, when the passive metal interconnects are formed using a damascene process, they are referred to as damascene structures. The damascence strucutre may be formed using a single damascene process to form single damascene structures or using a dual damascene process to form dual damascene structures.
In yet another aspect, the present invention includes a method of monitoring the condition or state of the metallization system. The condition of the metallization system is monitored by applying a current to the active metal interconnect and measuring an electrical parameter, such as resistance, between the active metal interconnect and one of the vertically or laterally positioned passive metal interconnects. If the resistance is high, e.g., nearly infinite, the active metal interconnect is electrically isolated from the passive metal interconnects. A low resistance, e.g., approximately zero, indicates that some of the metal from the active metal interconnect has extruded or migrated into the adjacent dielectric material and contacted the passive metal interconnect. In other words, a short has been created indicating a change in state in the metallization system such that it has failed. Because the metal of the active metal interconnect has migrated or become extruded, the passive metal interconnects are referred to as extrusion monitoring elements and the active metal interconnect is referred to as a test element or a notched test element. Because of the presence of notches and or extensions, the notched test element is also referred to as a non-continuous test element. In addition, the notches are referred to as U-shaped portions. It should be understood that the term U-shaped is intended to include notch or extension shapes having corners and substantially planar portions in addition to having the rounded bottom shape of a U.
A dielectric material 18 having a major surface 20 is formed on semiconductor substrate 12 and an electrically conductive portion 22 having a major surface 24 is formed in a portion of dielectric material 18. By way of example, electrically conductive portion 22 is metal. Metal layer 22 may be referred to as Metal-1 or a lower electrically conductive level. The combination of dielectric material 18 and electrically conductive portion 22 is referred to as an interconnect layer. When electrically conductive portion 22 is metal, the interconnect layer is also referred to as a metal interconnect layer. Techniques for forming semiconductor devices such as device 14, dielectric material 18, and metal layer 22 are known to those skilled in the art.
A layer of dielectric or insulating material 30 having a thickness ranging between approximately 100 Angstroms (Å) and approximately 10,000 Å is formed on major surfaces 20 and 24. Preferably, insulating layer 30 has a thickness ranging between 1,000 Å and 5,000 Å. By way of example, dielectric layer 30 is silicon dioxide (SiO2) having a thickness of about 2,500 Å. Other suitable materials for dielectric layer 30 include silicon nitride (SiN), diamond-like carbon (DLC), and hydrogenated oxidized silicon carbon material (SiCOH). In addition, the material of dielectric layer 30 may be an organic dielectric material such as, for example, polyimide, spin-on polymers, poly(arylene ether) (PAE), parylene, xerogel, fluorinated aromatic ether (FLARE), fluorinated polyimide (FPI), dense SiLK, porous SiLK (p-SiLK), polytetrafluoroethylene, and benzocyclobutene (BCB). Suitable inorganic low KC dielectric materials include, but are not limited to, hydrogen silsesquioxane (HSQ), methyl silsesquioxane (MSQ), fluorinated glass, or NANOGLASS. It should be understood that the type of dielectric material for dielectric layer 30 is not a limitation of the present invention and that other organic and inorganic dielectric materials may be used. Similarly, the method for forming dielectric layer 30 is not limitation of the present invention. For example, insulating layer 30 may be formed using, among other techniques, spin-on coating, spray-on coating, Chemical Vapor Deposition (CVD), Plasma Enhanced Chemical Vapor Deposition (PECVD), Physical Vapor Deposition (PVD), sputter deposition, reactive sputter deposition, ion-beam deposition, or the like.
A barrier layer 32 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on dielectric layer 30. By way of example, barrier layer 32 is a tantalum layer formed using Chemical Vapor Deposition (CVD), Plasma Enhanced Chemical Vapor Deposition (PECVD), sputtering, evaporation, or the like. Tantalum layer 32 serves as a barrier layer to prevent diffusion from a subsequently deposited metal into insulating layer 30 or into semiconductor device 14. In addition, tantalum layer 32 provides a low contact resistance between an underlying conductive layer (not shown) and a subsequently deposited electrically conductive layer 34. Other suitable materials for barrier layer 32 include titanium, titanium nitride, tantalum nitride, a combination of tantalum and tantalum nitride, tungsten (W), tungsten nitride (WN), titanium silicon nitride (TiSiN), and refractory metal compounds such as refractory metal nitrides, refractory metal carbides, or refractory metal borides.
A film or layer of an electrically conductive material 34 having a thickness ranging between approximately 100 Å and approximately 9,000 Å is formed on barrier layer 32. By way of example, layer 34 is copper which is plated on barrier layer 32. Techniques for plating copper on a barrier layer are known to those skilled in the art. Optionally, copper layer 34 is planarized using chemical mechanical planarization. The technique for planarizing copper layer 34 is not a limitation of the present invention. Other suitable planarization techniques include electropolishing, electrochemical polishing, chemical polishing, and chemical enhanced planarization. Alternatively, layer 34 may be aluminum or silver. A barrier layer 36 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on copper layer 34. Barrier layer 36 may be made using the same processing techniques and the same material as barrier layer 32 as described hereinbefore. Barrier layer 36 prevents diffusion of the electrically conductive material of layer 34, e.g., copper, into other portions of semiconductor 10 which would decrease its reliability.
A layer of dielectric or insulating material 38 having a thickness ranging between approximately 100 Angstroms and approximately 10,000 Å is formed on barrier layer 36. Preferably, dielectric layer 38 has a thickness ranging between 1,000 Å and 5,000 Å. By way of example, dielectric layer 38 has a thickness of about 2,500 Å and comprises a low dielectric constant (low κ) material, i.e., a material having a dielectric constant lower than that of silicon dioxide, silicon nitride, and hydrogenated oxidized silicon carbon material (SiCOH). Suitable organic dielectric materials include, but are not limited to, polyimide, spin-on polymers, poly(arylene ether) (PAE), parylene, xerogel, fluorinated aromatic ether (FLARE), fluorinated polyimide (FPI), dense SiLK, porous SiLK (p-SiLK), polytetrafluoroethylene, and benzocyclobutene (BCB). Suitable inorganic low κ dielectric materials include, but are not limited to, hydrogen silsesquioxane (HSQ), methyl silsesquioxane (MSQ), fluorinated glass, or NANOGLASS. It should be understood that the type of dielectric material for dielectric layer 38 is not a limitation of the present invention and that other organic and inorganic low κ dielectric materials may be used. Similarly, the method for forming dielectric layer 38 is not limitation of the present invention. For example, dielectric layer 38 may be formed using, among other techniques, spin-on coating, Chemical Vapor Deposition (CVD), Plasma Enhanced Chemical Vapor Deposition (PECVD), or Physical Vapor Deposition (PVD).
Still referring to
Referring now to
A film or layer of an electrically conductive material having a thickness ranging between approximately 100 Å and approximately 9,000 Å is formed on barrier layer 48. The film has a thickness at least as great as the depth of opening 42. By way of example, the layer is formed by plating copper on barrier layer 48. A portion 52 of the copper film fills barrier-lined opening 42. Techniques for plating copper on a barrier layer are known to those skilled in the art. Alternatively, the layer of conductive material may be aluminum or silver. The copper film is planarized using, for example, a Chemical Mechanical Polishing (CMP) technique having a high selectivity to dielectric layer 38. Thus, the planarization stops on dielectric layer 38. After planarization, portion 52 of the copper film remains in opening 42 (shown in
A barrier layer 55 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on copper film 52. Preferably barrier layer 55 is made using the same material and processing techniques as barrier layer 48 which was described with reference to
A layer of dielectric or insulating material 54 having a thickness ranging between approximately 100 Angstroms and approximately 10,000 Å is formed on dielectric layer 38 and barrier layer 55. Preferably, dielectric layer 54 has a thickness ranging between 1,000 Å and 5,000 Å. By way of example, dielectric layer 54 has a thickness of about 2,500 Å and comprises a low κ dielectric material. Suitable examples of low κ dielectric materials have been described hereinbefore with reference to
Referring now to
A barrier layer 62 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on dielectric portion 58 of dielectric layer 54 and on the portions of dielectric layer 38 not covered by portion 56. Preferably barrier layer 62 is made from the same material as barrier layer 48 using the processing techniques described with reference to
A layer of dielectric or insulating material 68 having a thickness ranging between approximately 100 Angstroms and approximately 10,000 Å is formed on barrier layer 65. Preferably, dielectric layer 68 has a thickness ranging between 1,000 Å and 5,000 Å. By way of example, dielectric layer 68 has a thickness of about 2,500 Å and comprises a low κ dielectric material. Suitable examples of low κ dielectric materials have been described hereinbefore with reference to
Referring now to
A barrier layer 74 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on dielectric portions 72 of dielectric layer 68 and on the portions of barrier layer 65 not covered by dielectric portions 72. Preferably barrier layer 74 is made from the same material as barrier layer 48 using the same processing technique described with reference to
Referring now to
Referring now to
A barrier layer 88 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on dielectric portions 72 and 86. Preferably barrier layer 88 is made using the same material and processing techniques as barrier layer 48 as described with reference to
A barrier layer 92 having a thickness ranging between approximately 10 Å and approximately 1,000 Å is formed on copper film 90. Preferably barrier layer 92 is made using the same material and processing techniques as barrier layer 48 as described with reference to
Layers 88, 90, and 92 cooperate to form an extrusion monitoring element 96. By way of example, layers 88, 90, and 92 cooperate to form a vertically oriented extension facing major surface 16. Extrusion monitoring elements 53 and 96 cooperate with notced test element 80 to form a flux divergence induced monitoring structure suitable for monitoring the formation of conductor extrusion in a direction towards or away from major surface 16, i.e., in a vertical direction.
For the sake of clarity,
In addition, semiconductor component 10 includes a flux divergence induced monitoring structure suitable for monitoring conductor extrusion in a direction substantially parallel to major surface 16. Referring now to
Extrusion monitoring element 104 is patterned to have a plurality of extensions 120 alternating with notches 122. Extensions 120 are adjacent corresponding notches 110 of test element 102 and notches 122 are adjacent corresponding conductive portions 114 of test element 102. Extrusion monitoring element 106 is patterned to have a plurality of extensions 124 alternating with notches 126. Extensions 124 are adjacent corresponding notches 112 of test element 102 and notches 126 are adjacent corresponding conductive portions 116 of test element 102.
In operation, a current is introduced into test element 102 as indicated by arrows 130 of
By now it should be appreciated that a semiconductor component having a flux divergence induced failure monitoring structure, a method for manufacturing the semiconductor component, and a method for monitoring flux divergence induced failure have been provided. An advantage of the present invention is that the monitoring structure can be integrated with a semiconductor device which allows monitoring whether adjacent electrical interconnects of the metallization system have become shorted together. Further, the monitoring structure is a multi-dimensional monitoring structure capable of detecting whether vertically adjacent electrical conductors have become shorted, whether laterally adjacent electrical conductors have become shorted, or whether both vertically and laterally adjacent electrical conductors have become shorted. The present invention provides a method for detecting electrical shorts in metallization systems in general and in copper metallization systems using a low κ dielectric materials.
Although certain preferred embodiments and methods have been disclosed herein, it will be apparent from the foregoing disclosure to those skilled in the art that variations and modifications of such embodiments and methods may be made without departing from the spirit and scope of the invention. It is intended that the invention shall be limited only to the extent required by the appended claims and the rules and principles of applicable law. For example, rather than forming the extrusion monitoring elements on both sides of the notched test element, an extrusion monitoring element may be formed on only one side. Moreover, notches may be formed in the extrusion monitoring elements and extensions formed in the notched test element, wherein the extensions are aligned to the notches. In addition, the notched test element can be a unitary structure having vertically and laterally extending notches, where the notched test element is vertically positioned between a pair of extrusion monitoring elements and laterally positioned between a pair of extrusion monitoring elements.
Number | Name | Date | Kind |
---|---|---|---|
3983479 | Lee et al. | Sep 1976 | A |
5264377 | Chesire et al. | Nov 1993 | A |
5472774 | Goad et al. | Dec 1995 | A |
6768323 | Hau-Riege et al. | Jul 2004 | B1 |