1. Field of the Invention
The present invention relates to a semiconductor device and a manufacturing method thereof, and in particular, relates to a semiconductor device in which a cavity (a hole, an opening, a pore, and the like) is prevented from being produced at a crystalline semiconductor film and a manufacturing method thereof.
2. Description of the Related Art
When an amorphous silicon film is added with a metal such as Ni and heat treatment is applied thereto, a crystalline silicon film can be formed at low temperature in short time. Subsequently, a natural oxide film that is formed incidentally on the crystalline silicon film due to the heat treatment is removed by using diluted hydrofluoric acid. As the crystalline silicon film at this stage has many crystal defects, electromagnetic energy is supplied to the crystalline silicon film in the subsequent step. Consequently, a high-quality crystalline silicon film with few crystal defects can be obtained. Laser light such as excimer laser light typifies the electromagnetic energy as a specific example. A crystalline silicon film manufactured by this method can be used for manufacturing an electronic device such as a high-performance thin film transistor (TFT).
In the above-mentioned method of forming a crystalline silicon film, nickel silicide may be separated out in a crystalline silicon film when the heat treatment is applied after adding Ni. Therefore, in removing a natural oxide film on the surface of the crystalline silicon film by diluted hydrofluoric acid, the nickel silicide in the crystalline silicon film is etched. A cavity may be, accordingly, formed in a crystalline silicon film. This cavity may remain even after irradiation of excimer laser light that is electromagnetic energy, and such crystalline silicon film having a cavity causes a defect of a withstand voltage in the case of forming a TFT or a capacitor in many cases.
The invention is made in view of the aforementioned circumstance, and an object of the invention is to provide a semiconductor device in which production of a cavity in a crystalline semiconductor film is suppressed and a manufacturing method thereof.
In order to solve the aforementioned problems, a manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of the amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by a solution containing organic solvent and fluoride.
According to the above-described manufacturing method of a semiconductor device, a silicon oxide film is formed on the surface of a crystalline semiconductor film when forming the crystalline semiconductor film by the heat treatment, and this silicon oxide film is removed from the surface of the crystalline semiconductor film by a solution containing organic solvent and fluoride. Employing such solution containing organic solvent and fluoride contributes to suppress production of a deep cavity in a crystalline semiconductor film. Note that, the deep cavity means a cavity whose bottom portion reaches a base insulating film.
In addition, in a manufacturing method of a semiconductor device according to the invention, after removal of the silicon oxide film by the solution, laser light or strong light is preferably irradiated to the crystalline semiconductor film. It enables not only to reduce crystal defects of the crystalline semiconductor film, but also to eliminate a shallow cavity.
In a manufacturing method of a semiconductor device according to the invention, the organic solvent is preferably any one of isopropyl alcohol, ethanol, denatured alcohol, and ethylene glycol.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon on a substrate having an insulating surface, adding a metal element for promoting crystallization of the amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by a solution containing surfactant and fluoride.
According to the above-described manufacturing method of a semiconductor device, since a solution containing surfactant and fluoride is employed, production of a deep cavity in a crystalline semiconductor film can be suppressed.
In addition, in a manufacturing method of a semiconductor device according to the invention, after removal of the silicon oxide film by the solution, laser light or strong light is preferably irradiated to the crystalline semiconductor film. It enables not only to reduce crystal defects of the crystalline semiconductor film, but also to eliminate a shallow cavity.
In a manufacturing method of a semiconductor device according to the invention, the surfactant preferably contains at least one of alkyl sulfonic acid, ω-hydrofluoro-alkyl-carboxylic acid, aliphatic carboxylic acid, aliphatic amine, aliphatic alcohol, and aliphatic carboxylic acid chloride.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of the amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by dry etching.
According to the above-described manufacturing method of a semiconductor device, since dry etching is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
In addition, in a manufacturing method of a semiconductor device according to the invention, after removal of the silicon oxide film by the dry etching, laser light or strong light is preferably irradiated to the crystalline semiconductor film.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of the amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by plasma treatment using a plasma gas containing CHF3.
According to the above-described manufacturing method of a semiconductor device, since plasma treatment using a plasma gas containing CHF3 is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of the amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by plasma treatment using a plasma gas containing CHF3, and removing CFx which is deposited on the crystalline semiconductor film in removal of the silicon oxide film by the plasma treatment by plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3.
According to the above-described manufacturing method of a semiconductor device, since plasma treatment using a plasma gas containing CHF3 and plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3 are employed, production of a cavity in a crystalline semiconductor film can be suppressed.
In addition, in a manufacturing method of a semiconductor device according to the invention, after removal of the CFx by the plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3, laser light or strong light is preferably irradiated to the crystalline semiconductor film.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of the amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3, and CHF3.
According to the above-described manufacturing method of a semiconductor device, since plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3, and CHF3 is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of an amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by plasma treatment using a plasma gas containing NF3.
According to the above-described manufacturing method of a semiconductor device, since plasma treatment using a plasma gas containing NF3 is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of an amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by plasma treatment using a plasma gas containing NF3 and NH3.
According to the above-described manufacturing method of a semiconductor device, since plasma treatment using a plasma gas containing NF3 and NH3 is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of an amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which is formed on the surface of the crystalline semiconductor film due to the heat treatment by plasma treatment using a plasma gas containing H2.
According to the above-described manufacturing method of a semiconductor device, since plasma treatment using a plasma gas containing H2 is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
In addition, in a manufacturing method of a semiconductor device according to the invention, after removal of the silicon oxide film by the plasma treatment, laser light or strong light is preferably irradiated to the crystalline semiconductor film. It enables to reduce crystal defects of the crystalline semiconductor film.
A manufacturing method of a semiconductor device according to the invention comprises the steps of forming an amorphous film containing silicon over a substrate having an insulating surface, adding a metal element for promoting crystallization of an amorphous film over the amorphous film, applying heat treatment to the amorphous film to crystallize the amorphous film, thereby forming a crystalline semiconductor film over the substrate, and removing a silicon oxide film which on the surface of the crystalline semiconductor film due to the heat treatment by a gas containing a hydrogen atom.
According to the above-described manufacturing method of a semiconductor device, since a gas containing a hydrogen atom is employed, production of a cavity in a crystalline semiconductor film can be suppressed.
In addition, in a manufacturing method of a semiconductor device according to the invention, after removal of the silicon oxide film by the gas, laser light or strong light is preferably irradiated to the crystalline semiconductor film. It enables to reduce crystal defects of the crystalline semiconductor film.
Additionally, in a manufacturing method of a semiconductor device according to the invention, after irradiation of the laser light or the strong light, it is possible to form a gate insulating film so as to contact with the crystalline semiconductor film, form a gate electrode on the gate insulating film, and form source and drain regions in the crystalline semiconductor film. Since a TFT is formed by using such crystalline semiconductor film with production of a cavity suppressed, a defect of a withstand voltage can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by a solution containing organic solvent and fluoride so that production of a cavity in the crystalline semiconductor film can be suppressed.
According to the above-described semiconductor device, since production of a cavity in a crystalline semiconductor film can be suppressed, such crystalline semiconductor film contributes to suppress production of a defect of a withstand voltage in a TFT or a capacitor. Note that a crystalline semiconductor film in which production of a cavity is suppressed means that a cavity density is 1.0×10−4 psc/μm2 or less in the case of employing IPA as the organic solvent. The crystalline semiconductor film in which production of a cavity is suppressed is suppressed means that the number of cavities in each inspection by a scanning electron microscope is 0 psc in the case of employing IPA as the organic solvent. The crystalline semiconductor film in which production of a cavity is suppressed is suppressed also means that the number of cavities in an area of 1000 μm2 inspected by the scanning electron microscope is 0 in the case of employing IPA as the organic solvent.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by a solution containing surfactant and fluoride so that production of a cavity in the crystalline semiconductor film can be suppressed. Note that a crystalline semiconductor film in which production of a cavity is suppressed means that a cavity density is 1.0×10−4 psc/μm2 or less in the case of employing surfactant as the organic solvent. The crystalline semiconductor film in which production of a cavity is suppressed means that the number of cavities in each inspection by a scanning electron microscope is 0 psc in the case of employing surfactant as the organic solvent. The crystalline semiconductor film in which production of a cavity is suppressed also means that the number of cavities in an area of 1000 μm2 inspected by the scanning electron microscope is 0 psc n the case of employing surfactant as the organic solvent.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by dry etching so that production of a cavity in the crystalline semiconductor film can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by using a plasma gas containing CHF3 so that production of a cavity in the crystalline semiconductor film can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by using a plasma gas containing at least one of Ar, H2 and NH3, and CHF3 so that production of a cavity in the crystalline semiconductor film can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by using a plasma gas containing NF3 so that production of a cavity in the crystalline semiconductor film can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by using a plasma gas containing NF3 and NH3 so that production of a cavity in the crystalline semiconductor film can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by using a plasma gas containing H2 so that production of a cavity in the crystalline semiconductor film can be suppressed.
A semiconductor device according to the invention comprises a substrate having an insulating surface and a crystalline semiconductor film containing silicon formed over the substrate, in which a silicon oxide film formed on the surface of the crystalline semiconductor film is removed by using a gas containing a hydrogen atom so that production of a cavity in the crystalline semiconductor film can be suppressed.
According to the above-described semiconductor devices, production of a cavity whose bottom portion reaches a base insulating film can be reduced in a crystalline semiconductor film.
Additionally, in a semiconductor device according to the invention, it is possible to form a gate insulating film so as to contact with the crystalline semiconductor film, form a gate electrode on the gate insulating film, and form source and drain regions in the crystalline semiconductor film. Since a TFT is formed by using such crystalline semiconductor film with production of a cavity suppressed, a defect of a withstand voltage can be suppressed.
According to the invention, as described hereinbefore, a method of removing a silicon oxide film formed on the surface of a crystalline semiconductor film due to heat treatment by a solution containing organic solvent and fluoride or the like is adopted. Accordingly, a semiconductor device in which production of a cavity in a crystalline semiconductor film can be suppressed and a manufacturing method thereof can be provided.
Hereinafter, embodiment modes of the invention are described with reference to the accompanying drawings.
First, as illustrated in
The base insulating film 2 serves to prevent impurity diffusion from the substrate 1 to a semiconductor layer. A light transmissive substrate such as glass or quartz is employed for the substrate 1. In this embodiment mode, low alkali glass is employed for the substrate 1 and a silicon oxynitride film having a thickness of 100 nm formed by plasma CVD (chemical vapor deposition) is employed for the base insulating film 2.
Note that in this embodiment mode, although the base insulating film 2 has a single layer structure, a laminated structure of two or more layers may be adopted as long as it has an effect of prevention of impurity diffusion.
Subsequently, as illustrated in
Then, as illustrated in
As the catalyst metal element, one or more of nickel (Ni), ferrum (Fe), cobalt (Co), ruthenium (Ru), palladium (Pa), osmium (Os), iridium (Ir), platinum (Pt), copper. (Cu), and aurum (Au) is preferably employed. In this embodiment mode, a catalyst metal element is added by coating the surface of the amorphous silicon film 3 with a solution containing Ni.
As for the heat treatment, heat treatment is applied at 400 to 500° C. for 1 hour to eliminate hydrogen in the amorphous silicon film 3 firstly, and then heat treatment is applied using a furnace at 500 to 600° C. (preferably at 550 to 570° C.) for 0.5 to 12 hours (preferably for 4 to 6 hours). Heat treatment using an RTA (Rapid Thermal Annealing) and the like may be performed as well. In this embodiment mode, heat treatment is applied at 500° C. for 1 hour, and subsequently heat treatment is applied using a furnace is applied at 550° C. for 4 hours so that the amorphous silicon film 3 is crystallized to form the crystalline silicon film 5.
When the crystalline silicon film 5 is formed through the heat treatment, a silicon oxide film 6 is formed on the surface of the crystalline silicon film 5 as illustrated in
In the case where such solution containing organic solvent and fluoride is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch. Consequently, production of a cavity whose bottom portion reaches the base insulating film 2 can be suppressed in the crystalline silicon film 5.
Note that the organic solvent is preferably any one of IPA (isopropyl alcohol), ethanol, denatured alcohol, and ethylene glycol. Denatured alcohol is inexpensive because of free liquor tax.
Then, as illustrated in
In this embodiment mode, a solution containing organic solvent and fluoride is used to eliminate a silicon oxide film on the surface of a crystalline silicon film in order to suppress production of a cavity in the crystalline silicon film. However, the method of suppressing production of a cavity may be modified to the following manner.
Modified Mode 1 is described below. The crystalline silicon film 5 after being crystallized is immersed in a solution containing surfactant and fluoride (e.g., BHF; NH4F, HF, and H2O mixed at an arbitrary rate) to eliminate the silicon oxide film 6 formed in the heat treatment for crystallization from the surface of the crystalline silicon film 5. In the case where such solution containing surfactant and fluoride is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch. Consequently, production of a cavity whose bottom portion reaches the base insulating film 2 can be suppressed in the crystalline silicon film 5, resulting in suppression of production of a cavity in a crystalline silicon film. Note that the surfactant preferably contains at least one of alkyl sulfonic acid, ω-hydrofluoro-alkyl-carboxylic acid, aliphatic carboxylic acid, aliphatic amine, aliphatic alcohol, and aliphatic carboxylic acid chloride.
The surfactant serves as follows: in the case where hydrophobic Si is exposed after an oxide film being etched, a hydrophobic group of the surfactant adheres to the Si while a hydrophilic group thereof is aligned in the solution.
Then, laser light (e.g., excimer laser light) or strong light is irradiated to the crystalline silicon film 5 and the surface of the crystalline silicon film is inspected by an electron microscope. Photographs thereof are shown in
Conventional manufacturing method of a semiconductor device and a result thereof, shown in
A manufacturing method of a semiconductor device and a result thereof according to Modified Mode 1, shown in
A manufacturing method of a semiconductor device and a result thereof according to Embodiment Mode 1, shown in
It is evident from the results in
Next, Modified Mode 2 is described. The surface of the crystalline silicon film 5 after being crystallized is dry etched to eliminate the silicon oxide film 6 formed in the heat treatment for crystallization from the surface of the crystalline silicon film 5. In the case where such dry etching is used, production of a cavity in the crystalline silicon film 5 can be suppressed.
Modified Mode 3 is described subsequently. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film 5 by plasma treatment using a plasma gas containing CHF3. In the case where such plasma treatment is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5.
The plasma treatment using a plasma gas containing CHF3 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.2 W/cm2, a pressure of 25 m Torr and a CHF3 gas flow at a flow rate of 35 sccm.
Modified Mode 4 is described. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film by plasma treatment using a plasma gas containing CHF3, and then CFx, that is deposited on the surface of the crystalline semiconductor film 5 in removal of the silicon oxide film 6 by the plasma treatment, is eliminated by plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3. In the case where each of such plasma treatment is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5.
The plasma treatment using a plasma gas containing CHF3 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.2 W/cm2, a pressure of 25 m Torr and a CHF3 gas flow at a flow rate of 35 sccm.
The plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.5 W/cm2, a pressure of 50 m Torr and an Ar gas flow at a flow rate of 50 sccm.
Next, Modified Mode 5 is described. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film 5 by plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3, and CHF3. In the case where such plasma treatment is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5. In addition, deposition of CFx on the crystalline silicon film 5 during the plasma treatment can be suppressed.
The plasma treatment using a plasma gas containing at least one of Ar, H2 and NH3, and CHF3 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.2 W/cm2, a pressure of 25 m Torr and an Ar gas flow at a flow rate of 10 sccm.
Modified Mode 6 is described below. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film 5 by plasma treatment using a plasma gas containing NF3. In the case where such plasma treatment is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5.
The plasma treatment using a plasma gas containing NF3 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.2 W/cm2, a pressure of 25 m Torr and an NF3 gas flow at a flow rate of 35 sccm.
Modified Mode 7 is described. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film 5 by plasma treatment using a plasma gas containing NF3 and NH3. In the case where such plasma treatment is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5.
The plasma treatment using a plasma gas containing NF3 and NH3 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.2 W/cm2, a pressure of 25 m Torr and an NH3 gas flow at a flow rate of 25 sccm.
Next, Modified Mode 8 is described. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film 5 by plasma treatment using a plasma gas containing H2. In the case where such plasma treatment is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5.
The plasma treatment using a plasma gas containing H2 is applied in accordance with the following condition: a processing time of 120 seconds, a power density of 0.5 W/cm2, a pressure of 25 m Torr and an H2 gas flow at a flow rate of 50 sccm.
Modified Mode 9 is described below. The silicon oxide film 6 formed in the heat treatment for crystallization is eliminated from the surface of the crystalline silicon film 5 by a gas containing a hydrogen atom. In the case where such gas is used, nickel silicide, which may be separated out in the crystalline silicon film 5, is difficult to etch, resulting in suppression of production of a cavity in the crystalline silicon film 5.
Description of modified modes terminates now, and hereinafter, description is made back to Embodiment Mode 1. After laser light (e.g., excimer laser light) or strong light is irradiated to the crystalline silicon film 5 as aforedescribed, a channel doping is applied for controlling a threshold value of a TFT, by which boron of a p-type impurity of approximately 5×10 16 to 5×107/cm3 is doped to the crystalline silicon film 7.
The threshold value of a TFT varies depending on various factors including properties of the crystalline silicon film 7 and a gate insulating film which is formed in a subsequent step. Thus, boron is not necessarily added, and alternatively, no impurity may be added or an n-type impurity such as phosphorous may be added if necessary. In addition, the amount of boron for doping is not limited to the above-described density and it can be determined arbitrarily.
Then, as illustrated in
Subsequently, the crystalline silicon film 7 is etched in accordance with the resist pattern 29 as a mask. Consequently, island-shaped semiconductor layers (active layers) 8a and 8b made of the crystalline silicon film 7 are formed on the base insulating film 2.
After removing the resist pattern 29, a gate insulating film 9 having a thickness of 40 to 130 nm is formed by plasma CVD on the semiconductor layers 8a and 8b and the base insulating film 2 as illustrated in
Then, a conductive film 10 having a thickness of 200 to 500 nm is formed on the gate insulating film 9. The conductive film 10 is a tungsten (W) film in this embodiment mode. Note that a material for forming a gate electrode is not limited to this, and an element selected among TaN, Ta, W, Ti, Mo, Al, Cu, Cr, and Nd, an alloy film or a compound material in which such elements are combined, or a semiconductor film typified by a polycrystalline silicon film added with an impurity element such as phosphorous may be employed alternatively.
After that, a photoresist film is coated on the conductive film 10 and the photoresist film is exposed and developed to form a resist pattern 11 on the conductive film 10.
The conductive film 10 is dry etched in accordance with the resist pattern 11 as a mask. Consequently, the conductive film 10 is processed into arbitrarily-shaped gate electrodes 12 and 13 as illustrated in
Subsequently, as illustrated in
An n-type impurity element is added in order to form source and drain regions 15 and 16 of an n-channel TFT as illustrated in
Subsequently, phosphorous of an n-type impurity element is doped into the semiconductor layer 8a by using the resist pattern 19 as a mask. A series of doping of the n-type impurity element described above is performed to satisfy the following condition: n-type impurities are added to the LDD regions 17 and 18, and the source and drain regions 15 and 16 at a density of 1×1016 to 1×1018 atoms/cm3 and a density of 1×1019 to 1×1021 atoms/cm3 respectively.
After that, as illustrated in
After removing the resist pattern 20a, a p-type impurity element is added in order to form source and drain regions 20 and 21 of the p-channel TFT as illustrated in
Subsequently, boron of a p-type impurity element is doped into the semiconductor layer 8b by using the resist pattern 20b as a mask. A series of doping of the p-type impurity element described above is applied to satisfy the following condition: in the LDD regions 22 and 23, and the source and drain regions 20 and 21, a density of boron is higher than the density of phosphorous, that are 3×1017 to 4×1018 atoms/cm3 and 3×1019 to 1×1021 atoms/cm3 respectively.
Then, the resist pattern 20b is removed and laser annealing is applied to activate the added impurities and restore crystallinity of the island-shaped silicon regions 8a and 8b which are damaged due to the doping step.
In this embodiment mode, phosphorous is injected into each of the source and drain regions 15 and 16 of the n-channel TFT and the source and drain regions 20 and 21 of the p-channel TFT at a density of 1×1019 to 1×1021 atoms/cm3 whereas it is injected into each of the LDD regions 17 and 18 of the n-channel TFT and the LDD regions 22 and 23 of the p-channel TFT at a density of 1×1016 to 1×1018 atoms/cm3. When laser is irradiated, a nickel gettering is carried out efficiently by the phosphorous.
As for the laser light, in the case of KrF excimer laser light (a wavelength of 248 nm), the laser light is preferably irradiated in accordance with a condition of an energy density of 200 to 400 mJ/cm2 (e.g., 250 mJ/cm2). In addition, the laser light is preferably irradiated for 2 to 20 shots per point. The substrate temperature in laser irradiation is set at 200° C.
After the laser annealing, thermal annealing is applied for 2 hours at 350° C. under a nitrogen atmosphere. Although the laser annealing and the thermal annealing are both applied in this embodiment mode, only one of them may be applied.
Subsequently, as illustrated in
Contact holes are formed in the interlayer insulating film 42 and the gate insulating film 9 at corresponding positions to the source and drain regions 15, 16, 20, and 21 respectively.
Then, a multiple layer film of, for example, titanium and aluminum is formed in the contact holes and over the interlayer insulating film 42. The multiple layer film is patterned to form source and drain electrodes and a wiring 433, 434, and 435 in the contact holes and over the interlayer insulating film 42. Subsequently, heat treatment is applied for 2 hours under a hydrogen atmosphere at 350° C. The steps described hereinbefore complete a CMOS thin film transistor.
According to Embodiment Mode 1, since the silicon oxide film 6 is formed on the surface of the crystalline silicon film 5 when forming the crystalline silicon film 5 by heat treatment, the crystalline silicon film 5 is immersed in a solution containing organic solvent and fluoride to eliminate the silicon oxide film 6 on the surface of the crystalline silicon film 5. In the case where such solution containing organic solvent and fluoride is used, nickel silicide which may be separated out in the crystalline silicon film 5 is difficult to etch. Consequently, production of a cavity whose bottom portion reaches the base insulating film 2 can be suppressed in the crystalline silicon film 5. In addition, laser light or strong light is irradiated to the crystalline silicon film 5 to eliminate a shallow cavity in the crystalline silicon film 5. Production of a cavity can be suppressed in a crystalline semiconductor film in this manner. Such crystalline semiconductor film enables to suppress production of a defect of a withstand voltage in a TFT or a capacitor.
After a TFT array substrate 57 is formed in accordance with the manufacturing method of a semiconductor device according to Embodiment Mode 1, an alignment film 58 is formed in the TFT side of the TFT array substrate 57 and rubbing treatment is applied. The alignment film 58 comprises a polyimide resin or a polyamic-based resin.
A manufacturing method of an opposing substrate 59 is described below. A light shielding film 61 which is made of metal chromium is formed on a substrate 60. Then, a color filter 62 having three colors of red, blue, and green is provided on the light shielding film 61 arbitrarily. In the case where the color filter 62 is provided, a passivation film 63 which comprises an acrylic resin and the like is formed on the color filter 62 in order to embed and flatten steps between the color filter 62 and the light shielding film 61. An ITO film that is a transparent conductive film is formed on the passivation film 63, which is subsequently processed into a desired shape to form a pixel electrode 64 on the passivation film 63.
An alignment film 65 is formed on the pixel side of the opposing substrate 59 manufactured as above described and rubbing treatment is applied thereto. For adhesion between the opposing substrate 59 and the TFT array substrate 57, a sealing material (not shown) is applied to the opposing substrate 59 and the sealing material is harden temporarily by heat. After temporary hardening, spacers 66 each of a plastic ball are arranged in place in the alignment film 65 side of the opposing substrate 59.
Then, the TFT array substrate 57 and the opposing substrate 59 are attached to each other with high accuracy so as to sandwich the respective alignment films 58 and 65. An unnecessary portion of the attached substrates is cut off to obtain a liquid crystal panel 67 of a desired size. The liquid crystal panel 67 is filled with a liquid crystal member 68, and then the liquid crystal panel 67 is sealed completely by a sealing material.
Embodiment Mode 2 described above yields the identical effect to that of Embodiment Mode 1.
Note that although the invention has been fully described by way of Embodiment Modes, it is to be understood that various changes and modifications will be possible. Therefore, unless such changes and modifications depart from the scope of the invention, they can be implemented as well.
This application is based on Japanese Patent Application serial no. 2003-429552 filed in Japan Patent Office on 25th, Dec. 2003, the contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-429552 | Dec 2003 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5543352 | Ohtani et al. | Aug 1996 | A |
| 5789284 | Yamazaki et al. | Aug 1998 | A |
| 5879977 | Zhang et al. | Mar 1999 | A |
| 6015724 | Yamazaki | Jan 2000 | A |
| 6027960 | Kusumoto et al. | Feb 2000 | A |
| 6071766 | Yamazaki et al. | Jun 2000 | A |
| 6180439 | Yamazaki et al. | Jan 2001 | B1 |
| 6331457 | Yamazaki et al. | Dec 2001 | B1 |
| 6337229 | Yamazaki et al. | Jan 2002 | B1 |
| 6337235 | Miyanaga et al. | Jan 2002 | B1 |
| 6355509 | Yamazaki | Mar 2002 | B1 |
| 6368904 | Yamazaki | Apr 2002 | B1 |
| 6380007 | Koyama | Apr 2002 | B1 |
| 6383852 | Zhang et al. | May 2002 | B2 |
| 6399454 | Yamazaki | Jun 2002 | B1 |
| 6426276 | Ohnuma et al. | Jul 2002 | B1 |
| 6432756 | Ohtani et al. | Aug 2002 | B1 |
| 6433363 | Yamazaki et al. | Aug 2002 | B1 |
| 6451638 | Zhang et al. | Sep 2002 | B1 |
| 6461943 | Yamazaki et al. | Oct 2002 | B1 |
| 6489189 | Yamazaki et al. | Dec 2002 | B2 |
| 6544826 | Yamazaki et al. | Apr 2003 | B1 |
| 6620711 | Yamazaki | Sep 2003 | B2 |
| 6624049 | Yamazaki | Sep 2003 | B1 |
| RE38266 | Yamazaki et al. | Oct 2003 | E |
| 6664144 | Nakajima et al. | Dec 2003 | B2 |
| 6670225 | Ohnuma | Dec 2003 | B2 |
| 6713323 | Yamazaki et al. | Mar 2004 | B2 |
| 6727124 | Nakajima et al. | Apr 2004 | B2 |
| 6743700 | Asami et al. | Jun 2004 | B2 |
| 6756608 | Kasahara et al. | Jun 2004 | B2 |
| 20010036692 | Yamazaki et al. | Nov 2001 | A1 |
| 20010038090 | Rasmussen et al. | Nov 2001 | A1 |
| 20060134891 | Ohnuma et al. | Jun 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 08-213316 | Aug 1996 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20050142702 A1 | Jun 2005 | US |