Patent Application
20050199979
The present invention relates to a semiconductor device which allows packaging of high density for protecting an integrated circuit formed on a semiconductor chip and ensuring electrical connection between the integrated circuit and an external device in its chip shape, and relates to a method for fabricating the same.
In recent years, as electrical equipment becomes more downsized and more sophisticated in functionality, semiconductor devices (semiconductor packages) have been requested to provide multiple terminals resulting from miniaturization and greater packing density of the packages. To respond this request, various types of chip scale packages (CSPs) have been developed as small-size packages having multiple terminals.
In particular, a wafer-level CSP (WL-CSP) has recently received attention as a technique capable of providing the ultimate small-size package having a size similar to that of a bare chip. The WL-CSP is formed by applying an insulating resin film on the entire surface of a semiconductor wafer on which a plurality of integrated circuits are provided, forming on the applied film interconnects for electrically connecting pad electrodes of the integrated circuits to external terminals such as bumps through contact holes, and dividing the semiconductor wafer into chip-size parts in the final process step.
Moreover, an enhanced semiconductor package was announced in which inductors, conventionally provided as separate components from the semiconductor chip, that is, provided as so-called external components, were formed on an insulating resin film of a WL-CSP semiconductor device by the use of materials constituting interconnects of the device to external terminals. The WL-CSP semiconductor device having inductors is also expected as an ultrasmall semiconductor package applicable to applications utilizing a frequency of hundreds of megahertzes (MHz) to several gigahertzes (GHz), such as potable devices and wireless LAN devices.
Hereinafter, a conventional WL-CSP semiconductor device having inductors formed on an insulating resin film covering an integrated circuit will be described with reference to the accompanying drawings.
As shown in
A plurality of lands 104 of substantially flat-circular shape are formed on the first insulating resin film 102. On the film 102, interconnects 105 are also formed of which one end is connected to the corresponding contact hole 103 and of which the other end is connected to the corresponding land 104. Regions of the first insulating resin film 102 provided with the lands 104 relatively sparsely are formed with an inductor 106 of which both terminals are connected to the pad electrodes through the contact holes 103, respectively. In this structure, the land 104, interconnect 105 and inductor 106 are patterned by copper (Cu) plating using a resist pattern as a mask.
On the first insulating resin film 102, a second insulating resin film 107 is formed which covers the interconnects 105 and the inductors 106 and which has a plurality of openings 107a exposing the lands 104. Over each of the openings 107a, an external terminal 108 of a soldering paste material is formed by printing.
The characteristic of an inductor is generally expressed by a Q value. The Q value is obtained by dividing a value of an energy input supplied to an inductor by a value of an energy loss caused by the inductor. Thus, the higher the Q value is, the smaller the energy loss of the inductor becomes.
In the conventional WL-CSP semiconductor device described above, the loss energy of the inductor 106 is the total of a heat loss caused by a resistance component of the inductor 106, a dielectric loss caused in the first and second insulating resin films 102 and 107 or the like, and a loss caused by signal leakage from the inductor 106 into the semiconductor chip 101 through the first insulating resin film 102 (referred hereinafter to as a leakage loss).
The heat loss is substantially determined by the size and the material of the inductor 106, and the dielectric loss is substantially determined by the material of the first and second insulating resin films 102 and 107. To reduce the leakage loss, the first insulating resin film 102 needs only to be thick. Herein,
However, the first insulating resin film 102 of the above conventional WL-CSP semiconductor device has the upper limit in thickness of about 4 μm to 6 μm. The reason for this is that the conventional WL-CSP semiconductor device uses a photosensitive resin material for the first insulating resin film 102, and therefore the first insulating resin film 102 has a limitation of the thickness according to the resolution of light exposure in forming the contact hole 103 in the first insulating resin film 102. This thickness limitation makes it impossible to thicken the first insulating film 102 to such a thickness that a leakage loss in the inductor 106 is reduced sufficiently. Therefore, high-frequency signals leak from the inductor 106 into the semiconductor chip 101 through the first insulating resin film 102. The leakage loss in the inductor 106 thus caused is too great to ignore, so that application of the WL-CSP semiconductor device shown in
An object of the present invention is to solve the foregoing problems, and to provide a WL-CSP semiconductor device having an inductor formed on an insulating resin film of a semiconductor chip and capable of reducing a leakage loss in the inductor through the insulating resin film.
To achieve this object, a semiconductor device of the present invention has the structure in which an inductor formation region of an insulating resin film covering the upper surface of the semiconductor device is formed thicker than the other region. Further, a method for fabricating a semiconductor device of the present invention has the process in which the thickened inductor formation region of the insulating resin film is masked to remove the top of the unmasked surrounding region of the film and therefore the portion of the thickened insulating resin film where a contact hole is to be formed is thinned.
Specifically, a semiconductor device of the present invention comprises: a semiconductor chip including an integrated circuit formed on the main surface of the chip and a plurality of pad electrodes formed on the main surface of the chip and electrically connected to the integrated circuit; a first insulating film of an insulating resin material which is formed over the main surface of the semiconductor chip, covers the integrated circuit, and includes a plurality of contact holes provided on the respective pad electrodes; and an inductor which is formed on an inductor formation region of the first insulating film and of which both terminals are connected to the pad electrodes through the contact holes, respectively. In the semiconductor device, the inductor formation region of the first insulating film is formed to have a greater thickness than a portion of the first insulating film around the contact hole.
The semiconductor device of the present invention makes it possible to reduce a leakage loss caused due to the leakage of high-frequency signals from the inductor into the semiconductor chip through the first insulating film since the thickness of the inductor formation region of the first insulating film is greater than that of the portion of the first insulating film around the contact hole. Moreover, even when the first insulating film is made of photosensitive resin, the formation of the contact hole is insensitive to the upper limit of the resolution. This makes it possible to ensure an appropriate formation of the contact hole. As a result, an inductor having a high Q value can be formed, and therefore the operating characteristic of the device as a high-frequency semiconductor device is surely improved.
Preferably in the inventive device, the inductor formation region has a thickness of 5 μm to 50 μm inclusive, and the portion of the first insulating film around the contact hole has a thickness of 4 μm to 6 μm inclusive.
Preferably, the inventive device further comprises: a land formed on the first insulating film; and an interconnect of which one end is connected to the corresponding pad electrode through the contact hole and of which the other end is connected to the corresponding land.
Preferably, the inventive device further comprises a protruding electrode formed on the land.
Preferably, the inventive device further comprises a second insulating film of an insulating resin material formed over the first insulating film and covering the inductor and interconnect.
A method for fabricating a semiconductor device of the present invention comprises: a first step of forming a first insulating film over the entirety of main surface of a semiconductor wafer including the surfaces of a plurality of pad electrodes, the semiconductor wafer having a plurality of integrated circuits and the plurality of pad electrodes, the plurality of integrated circuits being formed on the main surface of the chip, the plurality of pad electrodes being formed on the main surface of the chip and electrically connected to the corresponding integrated circuits; a second step of masking an inductor formation region of the first insulating film and removing upper portions of the first insulating film other than the masked inductor formation region; a third step of forming a plurality of contact holes exposing therein the respective pad electrodes in portions of the first insulating film whose upper portions have been selectively removed and which are located on the respective pad electrodes; and a fourth step of forming, on the inductor formation region of the first insulating film, an inductor of which both terminals are connected to the pad electrodes through the contact holes, respectively.
With the inventive method for fabricating a semiconductor device, the inductor formation region of the first insulating film is made thicker than a portion of the first insulating film in which a contact hole is to be formed. This ensures that the semiconductor device of the present invention is obtained.
In the inventive method, the first insulating film is preferably made of a positive photosensitive resin material. Thus, only the light-exposed portion of the positive photosensitive resin is removed by development. Therefore, even in the portion of the first insulating film other than the masked region (the contact-hole formation portion), only the top thereof is subjected to light exposure, thereby leaving the contact-hole formation portion of the first insulating film after the subsequent development.
Preferably in this case, the second step comprises the sub-step of exposing the photosensitive resin material to light with the inductor formation region of the photosensitive resin material masked, and then removing the light-exposed portions of the photosensitive resin material by development. Furthermore, the third step comprises the sub-step of selectively exposing to light portions of the photosensitive resin material whose upper portions have been selectively removed by the development and which are located on the respective pad electrodes, and then removing the light-exposed portions by development.
Preferably in this case, the thicknesses of the portions of the photosensitive resin material to be exposed to light in the second step are set to such an extent that the remaining portions of the photosensitive resin material located under the portions thereof to be exposed to light and on the pad electrodes can obtain a desired resolution.
Preferably in the inventive method, the second step further comprises the sub-step of focusing exposure light onto the position in the vicinity of the surface of the photosensitive resin material, and the third step further comprises the sub-step of focusing exposure light onto the position in the vicinity of the surface of each portion of the photosensitive resin material whose upper portion has been selectively removed.
Preferably in the inventive method, the photosensitive resin is cured after the third step.
In the inventive method, the fourth step comprises the sub-steps of: forming a plating seed layer over the entire surface of the first insulating film including the surfaces of the contact holes; forming a resist pattern including a pattern for an inductor and a pattern for a land and an interconnect, the pattern for an inductor being located on the inductor formation region of the plating seed layer, the pattern for a land and an interconnect being located on a region of the plating seed layer other than the inductor formation region; forming a metal film on the plating seed layer by plating using the resist pattern as a mask; and removing the resist pattern and then removing the plating seed layer by etching using the metal film as a mask, thereby forming an inductor, a land and an interconnect from the metal film.
Preferably in this case, the inventive method further comprises, after the fourth step, the steps of: forming a second insulating film over the entire surface of the first insulating film including the surfaces of the inductor, land and interconnect; and forming an opening in a portion of the second insulating film on the land and then forming a protruding electrode in the opening so that it is connected to the land and the top thereof protrudes from the second insulating film.
Preferably in the inventive method, the semiconductor wafer is provided with scribe lines with which the plurality of integrated circuits are defined to each other; and the method comprises the step of dividing the semiconductor wafer along the scribe lines to form a plurality of semiconductor chips after the fourth step.
An embodiment of the present invention will be described below with reference to the accompanying drawings.
As shown in
A plurality of lands 15 of substantially flat-circular shape are formed on the first insulating resin film 12. The upper surfaces of the lands 15 are each provided with a ball bump (protruding electrode) 14 as an external terminal. The lands 15 are connected to the contact holes 13 through interconnects 16, respectively. Regions of the first insulating resin film 12 provided with the lands 15 relatively sparsely are formed with an inductor formation region 12a having a greater thickness than its surrounding region. On the inductor formation region 12a, an inductor 17 is formed of which both terminals are connected to the pad electrodes 21 through the contact holes 13, respectively.
As shown in
As shown in
Thus, the semiconductor device according to this embodiment makes the inductor formation region 12a of the first insulating resin film 12 thicker than the surrounding region, that is, the regions of the first insulating resin film 12 where the contact holes 13, lands 15 and interconnects 16 are formed. This prevents leakage of high-frequency signals from the inductor 17 into the semiconductor chip 11 through the first insulating resin film 12. Therefore, an energy loss caused by signal leakage in the inductor 17 can be reduced.
Hereinafter, a method for fabricating the semiconductor device thus constructed will be described with reference to the drawings.
First as shown in
As shown in
Subsequently, as shown in
Next, as shown in
As shown in
In the first light exposure step shown in
The lower limit of thickness of the contact-hole 13 formation portion of the first insulating resin film 12 is determined according to the insulation performance of the film 12, whereas the upper limit of thickness of the inductor formation region 12a is determined according to whether or not light exposure and development for forming the contact hole 13 are surely performed. In this embodiment, the lower limit of thickness of the first insulating resin film 12 is set preferably at about 4 μm to 6 μm, more preferably at 5 μm. In addition, although the Q value increases as the inductor formation region 12a becomes thicker as shown in
As a developing solution for the first insulating resin film 12, use is made of a weak alkaline or an organic developing solution in which the pad electrode 21 is undissolvable during development.
As shown in
In this process step, prior to the deposition of the barrier layer 31 and the plating seed layer 32, plasma treatment is performed on the surface of the first insulating resin film 12 to change the surface thereof into a microscopically roughened state. This enhances the adhesion strength of the first insulating resin film 12 to the barrier layer 31. Also in this step, the residue of the first insulating resin film 12 left on the pad electrode 21 after the development and a surface oxide film existing on the pad electrode 21 are removed. This reduces the contact resistance between the pad electrode 21 and the barrier layer 31. It is to be noted that the plasma treatment needs only to selectively control the amount of etching on the first insulating resin film 12 relative to the etching amounts of the pad electrode 21 and the passivation film 20. For example, reactive ion etching (RIE) using an oxygen (O2) gas, a mixed gas of oxygen and carbon tetrafluoride (CF4), or a mixed gas of oxygen and argon (Ar) is recommendable for the plasma treatment.
The barrier layer 31 is preferably made of a metal having high adhesion properties to the first insulating resin film 12, the passivation film 20 and the pad electrode 21 and having resistance to an etching solution with which the plating seed layer 32 is etched. In this embodiment, a tungsten titanium alloy (10% Ti-90% W) is used for the barrier layer 31. Considering the resistance of the plating seed layer 32 to the etching solution, the barrier layer 31 preferably has a thickness of about 0.2 μm to 0.5 μm.
The plating seed layer 32 serves as a seed layer in forming a body layer 33 of interconnects 16 and an inductor 17 by electrolytic plating. To ensure appropriate functioning of the seed layer, it is preferably made of a metal having low resistivity. In this embodiment, copper is used for the seed layer. Considering the electric resistance and deposition stress of the plating seed layer 32 and ease of etching on the deposited layer 32, it preferably has a thickness of about 0.3 μm to 0.5 μm.
Then, as shown in
Next, as shown in FIG. SD, using the resist pattern 53 as a mask, a body layer 33 of copper constituting the interconnects or the like is formed on the plating seed layer 32 by electrolytic plating. Considering the electric resistance and mechanical strength of the body layer 33, it preferably has a thickness of about 10 μm to 14 μm.
As shown in
Subsequently, as shown in
Next, as shown in
As shown in
As described above, according to a fabrication method of a semiconductor device of the present invention, an inductor 17 is formed on a first insulating resin film 12 covering an integrated circuit on a semiconductor wafer 11A, before which an inductor formation region 12a of the first insulating resin film 12 is made thicker than a portion of the film 12 in which a contact hole 13 is to be formed. To attain this structure, a positive photosensitive resin is used for the first insulating resin film 12. Of the film 12, the inductor formation region 12a is patterned in the first light exposure and development steps and the contact hole 13 exposing the pad electrode 21 is patterned in the second light exposure and development steps. Thereafter, the whole first insulating resin film 12 is heat cured (post-cured) at a time. This simplifies the fabrication process of the semiconductor device, thereby providing a lower-cost semiconductor device.
Moreover, in the first light exposure, exposure light is focused onto the position in the vicinity of the surface of the first insulating resin film 12, and in the second light exposure, exposure light is focused onto the position in the vicinity of the surface portion of the first insulating resin film 12 whose upper portion has been selectively removed by patterning the inductor formation region 12a. This enables a fine patterning for both the inductor formation region 12a and the contact hole 13. As a result, formation of the contact hole 13 in the light exposure and development steps is not restricted by the thickness of the first insulating resin film 12 after the formation. In addition, the inductor formation region 12a of the first insulating resin film 12 can be thickened to such a thickness that a leakage loss in the inductor 17 is prevented sufficiently.
In this embodiment, the inductor formation region 12a is integrally formed with the first insulating resin film 12. However, such integration is not necessarily required. As an alternative example, an inductor formation region of an first insulating resin film having a uniform thickness may be provided with another insulating film, whereby the inductor formation region is made thicker than its surrounding region.
In this embodiment, the land 15, interconnect 16 and inductor 17 are formed by electrolytic plating. The forming method thereof is not limited to this, and sputtering may be employed instead.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-152822 | May 2002 | JP | national |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10442139 | May 2003 | US |
| Child | 11122094 | May 2005 | US |