1. Field of the Invention
This invention relates generally to semiconductor processing, and more particularly to circuit devices incorporating dislocation regions for charge neutralization and to methods of making the same.
2. Description of the Related Art
Integrated circuit fabrication on semiconductor-on-insulator (“SOI”) substrates holds the promise of significant device scaling through increased packing density. In complimentary metal oxide semiconductor (“CMOS”) circuit designs, SOI eliminates some latch-up issues normally present in CMOS design rules. In SOI substrates, junction isolation is provided by surrounding active device regions with an insulator. A typical SOI substrate includes a plurality of silicon islands formed on an insulating layer, usually of oxide. The silicon islands are also isolated laterally by an insulator, again usually an oxide.
Device fabrication on SOI substrates is similar in many respects to conventional device fabrication on conventional semiconductor substrates in which device isolation is provided by trench isolation or field oxide regions and impurity wells. For example, one conventional technique for field effect transistor fabrication on a SOI substrate entails gate dielectric layer and gate electrode fabrication followed by a self-aligned lightly doped drain (“LDD”) implant and a source/drain implant. Spacers may be applied to provide lateral set-off of the impurity regions.
In some conventional processes tailored for device isolation via impurity wells and isolation trenches, an amorphization implant is performed following gate electrode formation but prior to source/drain region implants. The goal of the amorphization implant is to establish surface amorphous regions that are self-aligned to the gate electrode. The surface level amorphous regions make the upper reaches of the device region resistant to ionic channeling during ion implantation. The subsequently-performed LDD implant will exhibit little ionic channeling and produce a relatively shallow p-n junction. The amorphous regions are later recrystallized during an anneal step.
One technical hurdle associated with SOI device fabrication is associated with floating body effects. In a conventional substrate wherein device isolation is provided by isolation trenches and impurity wells, the body of a transistor is coupled electrically to the remainder of the substrate. However, in a SOI substrate, the body of the device is floating. As a consequence, charge can accumulate in the body. The amount and rate of charge accumulation are dependent upon a number of factors, such as the number of times of the transistor is switched on and off and the geometry of the transistor and the device region, to name a few. Accumulated charge in the body can lead to undesirable variances in the switching speed of the transistor. The problem of floating body effects is generally more acute for partially depleted devices, such as partially depleted field effect transistors, than for fully depleted devices.
The present invention is directed to overcoming or reducing the effects of one or more of the foregoing disadvantages.
In accordance with one aspect of the present invention, a method of processing is provided that includes forming an impurity region in a device region of a semiconductor-on-insulator substrate. The impurity region defines a junction. A dislocation region is formed in the device region that traverses the junction.
In accordance with another aspect of the present invention, a method of processing is provided that includes forming an impurity region in a device region of a substrate. The impurity region defines a junction. At least two dislocation regions are formed in the device region that traverse the junction.
In accordance with another aspect of the present invention, a method of processing is provided that includes forming a first impurity region and a second impurity region in a device region of a semiconductor-on-insulator substrate. The first impurity region defines a first junction and the second impurity region defines a second junction. A first dislocation region is formed in the device region that traverses the first junction, and a second dislocation region is formed in the device region that traverses the second junction.
In accordance with another aspect of the present invention, a circuit device is provided that includes a semiconductor-on-insulator substrate that has a device region. An impurity region is in the device region. The impurity region defines a junction. A dislocation region is in the device region that traverses the junction.
In accordance with another aspect of the present invention, a circuit device is provided that includes a semiconductor-on-insulator substrate that has a device region. A first impurity region is in the device region and has a first extension region that defines a first junction. A second impurity region is in the device region and has a second extension region that defines a second junction. The second junction is separated from the first junction to define a channel. A first dislocation region is in the device region and traverses the first junction. A second dislocation region is in the device region and traverses the second junction.
The foregoing and other advantages of the invention will become apparent upon reading the following detailed description and upon reference to the drawings in which:
In the drawings described below, reference numerals are generally repeated where identical elements appear in more than one figure. Turning now to the drawings, and in particular to
The insulator portion of the semiconductor-on-insulator substrate 12 consists of a base substrate 26, an insulator film or substrate 28 positioned on the base substrate 26, and an insulating film 30 positioned on the insulator substrate 28. The base substrate 26 may be an insulator or a semiconductor as desired. Exemplary materials include, for example, oxide, silicon, germanium, polymeric materials, laminates of these or the like.
The insulator substrate 28 may be composed of well-known insulator materials, such as, for example, oxide, silicon nitride, sapphire, laminates of these or the like. Optionally, the insulator substrate 28 may be formed as a buried insulating layer. The insulating film 30 may be composed of the same types of materials.
The insulator substrate 28 and the insulating film 30 subdivide the device regions 20, 22 and 24 into semiconductor islands. That is, the device regions 20, 22 and 24 are laterally and vertically electrically isolated by insulating material.
The dashed oval 32 in
The gate dielectric layer 34, the gate electrode 36, and the spacers 38 and 40 may be fabricated in any of a myriad of well-known ways using well-known materials and techniques. The impurity regions 42 and 44 consist of respective extension regions 46 and 48 and overlapping impurity regions 50 and 52. Optionally, the impurity regions 42 and 44 may be implemented as single-graded regions. The lateral separation between the impurity regions 42 and 44 defines a channel or body 54 of the device 14. The lateral boundaries of the impurity regions 42 and 44 adjacent to the channel or body 54 are defined by junctions 56 and 58 that may be p-n or n-p as desired.
As noted above, the potential for charge build-up within a floating body of a semiconductor-on-insulator circuit device, such as a transistor, can lead to unpredictable permutations in the performance of the device. In order to reduce the impact of charge build-up within the body 54 of the device 14, one or more dislocation regions are provided in the device region 20 that traverse the junctions 56 and 58. In the embodiment illustrated, dislocation regions 60 and 62 are positioned across the respective portions of the junctions 56 and 58 proximate the extension regions 46 and 48, and dislocation regions 64 and 66 are positioned proximate the overlapping impurity region 50 and cross the junction 56 into the body 54. A similar pair of dislocation regions 68 and 70 are positioned proximate the overlapping impurity region 52 and cross therefrom into the body 54. The purpose of the dislocation regions 60, 62, 64, 66, 68 and 70 is to provide regions where charge accumulating in the body 54 can flow into the impurity regions 42 and 44 and become neutralized through the process of charge recombination.
As described more fully below, the dislocations 60, 62, 64, 66, 68 and 70 are deliberately created in the device region 20 by implantation of neutral species to form amorphous regions within the device region 20 followed by an anneal process or processes to initiate recrystallization of the amorphous regions. During the recrystallization process, the dislocations 60, 62, 64, 66, 68 and 70 form. The dislocations 60, 62, 64, 66, 68 and 70 each consist of a plurality of localized crystal structure dislocations that line up along a plane as indicated by the dashed lines in FIG. 2. The planes are shown edge-on in FIG. 2 and thus proceed into and out of the drawing page.
An exemplary method in accordance with the present invention for fabricating the circuit device 14 may be understood by referring now to
An implant of a neutral species 72 is performed with the gate electrode 36 serving as an implant hard mask in order to establish amorphous regions 74 and 76 in the device region 20. The boundaries of the amorphous region 74 are illustrated by the intersecting horizontal dashed line 78 and vertical dashed line 80. The borders of the amorphous region 76 are represented by the intersecting horizontal line 82 and vertical line 84. The neutral species 72 may be any of a variety of substances that may be implanted as neutral species, such as, for example, xenon, silicon, germanium, argon or the like. In an exemplary embodiment, xenon is implanted at an energy of about 30 to 130 keV, a dosage of about 6.0E13 to 3.0E14 ions-cm−2 and an implant angle of about 0°. An off-axis implantation angle may be used for this or any of the other implants disclosed elsewhere herein.
As shown in
As shown in
The skilled artisan will appreciate that the implants of the a neutral species may be implemented using the same substance, e.g., xenon. Optionally, different substances may be used for the implants, e.g., xenon, silicon, germanium, argon, etc.
Referring now to
At this point, an activation anneal is performed to activate the impurity regions 42 and 44. In an exemplary embodiment, the anneal may be performed at about 900 to 1060° C. for about 5 to 120 seconds in a rapid thermal anneal process. The anneal serves the dual purpose of activating the impurity regions 42 and 44 and recrystallizing the amorphous regions 74, 76 and the buried amorphous regions 88, 90, 106 and 108 to produce the dislocation regions 60, 62, 64, 66, 68 and 70 as shown in FIG. 7. As the amorphous region 74 begins to recrystallize, the lateral boundary 80 proceeds laterally away from the channel 54 and the horizontal boundary 78 proceeds upward toward the upper surface 105 of the device region 20. As these boundaries migrate laterally and vertically, the dislocation region 60 is formed. A similar phenomenon occurs with regard to the buried amorphous region 88, that is, the boundaries 92 and 94 of the buried amorphous region 88 move downward and upward, respectively, and the lateral boundary 96 moves away from the channel 54 during recrystallization. The dislocation region 64 is established with small obliquely projecting portions 120 and 122 as shown in FIG. 7. The portions 120 and 122 are due to the interactions of the upper and lower corner intersections between the boundary 96 and the boundaries 92 and 94. As the buried amorphous region 106 recrystallizes, the horizontal boundary 110 moves downward and the lateral boundary 114 moves away from the channel 54, producing the dislocation region 66.
The same mechanisms apply to the amorphous region 76 and the buried amorphous regions 90 and 108, albeit in a flip-flopped spatial orientation relative to the amorphous region 74 and the buried amorphous regions 88 and 106. Indeed, due to the movements of the boundaries 82, 84, 98, 100, 102, 112 and 116, the dislocation regions 62, 68 and 70 are established during recrystallization. Like the dislocation region 64, the dislocation region 68 forms with obliquely oriented projections 124 and 126. Note also that the anneal produces a lateral migration of the impurities of the impurity regions 42 and 44, which produces a slight underlap between the extension regions 46 and 48 and the gate electrode 36 and gate dielectric layer 34.
The number of dislocation regions produced is largely a matter of design discretion. For example, and as illustrated in
In the foregoing illustrative embodiments, the fabrication of the buried amorphous regions 88, 90, 106 and 108 precedes fabrication of the impurity regions 42 and 44. However, considerable flexibility in the order of processing steps is envisioned in accordance with the present invention.
Next, and as shown in
Next, and as shown in
The skilled artisan will appreciate that the devices fabricated in accordance with the present invention alleviate some of the difficulties associated with floating body effects in SOI processing. One or more junction-traversing dislocation regions may be formed in a device region to provide a gateway for accumulated charge to dissipate. Several dislocation regions may be formed at various depths in the device region to provide comprehensive charge dissipation.
While the invention may be susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, it should be understood that the invention is not intended to be limited to the particular forms disclosed. Rather, the invention is to cover all modifications, equivalents and alternatives falling within the spirit and scope of the invention as defined by the following appended claims.
Number | Name | Date | Kind |
---|---|---|---|
5698869 | Yoshimi et al. | Dec 1997 | A |
5825066 | Buynoski | Oct 1998 | A |
6225176 | Yu | May 2001 | B1 |
6380037 | Osanai | Apr 2002 | B1 |
6423993 | Suzuki et al. | Jul 2002 | B1 |
Number | Date | Country |
---|---|---|
0 935 389 | Aug 1999 | EP |
2001244477 | Sep 2001 | JP |
WO 03 012844 | Feb 2003 | WO |
Number | Date | Country | |
---|---|---|---|
20030162336 A1 | Aug 2003 | US |