SPUTTERING TARGETS COMPRISING ALUMINIDES OR SILICIDES

Abstract

Described is an in situ method for producing articles of metal aluminide or silicide by reactive sintering and vacuum hot pressing powders and products, such as sputtering targets, produced.

Description

BACKGROUND

[0001] Refractory metals and their suicides are widely used in CD CMOS DRAMs and logic circuits. Silicides offer lower resistivity in compared to doped silicon. In addition, silicides also offer higher thermal stability compared to conventional interconnect materials such as aluminum. There are several ways to obtain refractory metal silicide films on the wafer. The most common method to obtain metal silicide is through the salicide process. The salicide process for obtaining titanium silicide film on a wafer is described below:

[0002] 1. a layer of T1 is deposited on a wafer by sputtering;

[0003] 2. first rapid thermal anneal (RTA) step: titanium reacts with silicon forming TiSi2 ((C49) phase). This step is done in a nitrogen atmosphere to avoid forming TiSi2 on the oxide and forms a TiN layer on the titanium;

[0004] 3. the wafer is removed and selectively etched to the TiN and unreacted Ti;

[0005] a second RTA step is performed whereby TiSi2 is transformed from the high resistivity phase (C49) to the low resistivity phase (C54)

[0006] The process involves four steps including two high temperature rapid annealing steps. The advantage of RTA versus conventional annealing is that RTA reduces the “thermal budget”, defined as the time the wafer stays in the furnace at high temperature. In general, reducing the thermal budget is desirable.

[0007] An alternative way to obtain a silicide film on a wafer would be by depositing a silicide film by sputtering a silicide target. Sputter deposition of silicide film using a silicide target offers the following advantages:

[0008] 1. eliminates the need for high temperature rapid thermal annealing steps, provided a C54 film can be deposited;

[0009] 2. reduces silicon consumption from the wafer;

[0010] 3. eliminates the phase transformation step; and

[0011] 4. provides an opportunity to deposit an amorphous film.

[0012] Aluminides of Ti and Ta are useful barrier materials in the manufacture of integrated circuits. During the manufacture of integrated circuits Ti and Al layers often react to form titanium aluminide during wafer processing. However, formation of titanium aluminide during wafer processing is detrimental to the wafer because it introduces additional stresses in the film and also consumes Ti and Al from interconnect wiring. In order to prevent titanium aluminide formation and consumption of interconnect metal in the wafer during processing, it is desirable to deposit titanium aluminide by sputtering a titanium aluminide target. Depositing a titanium aluminide film eliminates the introduction of stresses associated with formation of titanium aluminide and unnecessary consumption of interconnect metal.

SUMMARY

[0013] The invention relates to a method of making enhanced purity stoichiometric and non-stoichiometric articles, such as targets for sputtering and related microelectronics applications, and to such articles, including targets. Stoichiometric articles are defined as single phase microstructure having a chemical composition as predicted by the phase diagram of the constituent elements e.g. TiAl3, WSi2, TiSi2, etc. Non-stoichiometric articles are defined as articles, such as targets, having a composition slightly away from the stoichiometric composition as predicted by the phase diagram of the constituent elements e.g. TiSi2,4, WSi2,8, etc. By practicing the invention it is possible to fabricate single phase stoichiometric articles, such as targets and dual-phase non-stoichiometric articles, such as targets, with high densities, higher purity than the starting material, and fine microstructure. Higher purity targets are beneficial for sputtering because they lead to less defects on the silicon wafer thereby increasing yields.

[0014] Enhanced purity stoichiometric and non-stoichiometric articles, such as sputtering targets, in accordance with one aspect of the invention which possess a density of 95% or higher of theoretical density and a microstructure not exceeding 20 microns, depending on the chemistry and composition of the article, e.g. target, and its constituent elements.

[0015] Enhanced purity articles, such as targets, are defined as having an overall purity (combination of metallic, non-metallic and gaseous components) higher than that of the starting material. The articles may be manufactured by using a combination of reactive sintering, sintering and vacuum hot pressing. It has been found that such a combination can be performed in situ in a vacuum hot press which enables the process to be a one-step process to manufacture stoichiometric and non-stoichiometric, such as sputtering targets starting from elemental powders, i.e. elements in powder form.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016] FIG. 1 is a photomicrograph of the grain structure of TiAl3 target produced in accordance with an embodiment of the invention (100×, grain size 18 microns);

[0017] FIG. 2 is a graph showing the x-ray diffraction pattern of a target produced in accordance with one embodiment of the invention;

[0018] FIG. 3 is a graph of an analysis of titanium suicide; and

[0019] FIG. 4 is a photomicrograph of the grain structure of TiSi2 target produced in accordance with one embodiment of the invention (100×, grain size, 18 microns; cracks observed are an artifact of the sample mounting, grinding and polishing process).

DETAILED DESCRIPTION

[0020] One aspect of the invention comprises a one-step method of making enhanced purity, high density, fine microstructure sputtering targets using a combination of reactive sintering and vacuum hot pressing. While the basic fundamentals of the process remain the same, there may be some variations in the process depending on the starting material and final composition required.

[0021] A preferred embodiment of the method of the invention comprises a process that includes reactive sintering and vacuum hot pressing together. This process results in a high density blank, i.e., greater than 95% density, for sputtering targets, and to sputtering targets produced therefrom. The invention includes a method of making an article particularly useful as a sputtering target having enhanced purity comprising metal (M) and either silicon (Si) or aluminum (Al), from powder. For the method for producing an aluminide sputtering target, M comprises Ti, Fe, Co, Ni and/or Ta, for producing a silicide target, M comprises Ti, Ta, Ni, Cr, Co and/or Pt. The preferred embodiment of the method may comprise the following steps, which may be combined or rearranged in order:

[0022] (a) providing a heat-resisting pressing die having a cavity with a configuration and dimensions desirable for producing the desired article, for example a sputtering target. the die has at least one movable pressing ram adapted for application of axial compaction forces to material in said cavity;

[0023] (b) blending metal (M) and either silicon (Si) or aluminum (Al) powder is proportionate ratio to provide the desired composition, advantageously both powders have sizes less than or equal to 45 mm;

[0024] (c) adding sufficient amounts of the blended mix into the cavity of the heat-resistant die so as to be able to yield a dense compact having substantially desired dimensions, for example, of a sputtering target;

[0025] (d) placing the die a the vacuum hot-press chamber;

[0026] (e) applying a containment pressure to the mixture in the die adapted to be under high vacuum conditions by means of at least one moving ram capable of applying uniaxial compaction forces; advantageously, the containment pressure is sufficient to contain said mixture in said die;

[0027] (f) evacuating said chamber and said die, preferably about 10−4 torr or less;

[0028] (g) heating said die containing the said mixture in the vacuum hot-press chamber to a first temperature sufficient to remove moisture and to volatilize alkali metals while maintaining uniaxial compaction pressure and a pressure of not more than about 10−4 torr;

[0029] (h) maintaining said first temperature for a time period sufficient to substantially remove gases and alkali metals from the mixture;

[0030] (i) heating the said die containing the said mixture in the vacuum hot-press chamber to a second temperature preferably ranging from about 500 -1500° C. to allow the powders to reactively sinter under a containing pressure and high vacuum;

[0031] (j) increasing uniaxial compaction pressure, preferably about 1000-6000 psi;

[0032] (k) maintaining said compaction force under said vacuum and at said second temperature for a time sufficient to allow for reactive sintering process to complete and effect desired compaction of the said mixture;

[0033] (l) releasing said compaction force while maintaining high vacuum of preferably about 10−4 torr or less;

[0034] (m) slowly cooling said die to relieve stresses in the compact while maintaining high vacuum, preferably to about 300° C. or less and about 10−4 torr or less;

[0035] (n) releasing vacuum;

[0036] (o) removing cooled compact from die; and

[0037] (p) recovering the article, and further processing as necessary to produce a sputtering target with desired composition and enhanced purity.

[0038] Other preferred conditions are:

[0039] metal powder having particle sizes smaller than about 45 microns, including aluminum or silicon powder of a size smaller than about 45 microns;

[0040] mixing in an inert gas atmosphere;

[0041] using a containment pressure in step (e) in the range of about 200-1000 psi;

[0042] heating the die at a rate of up to about 5° C./min to a first temperature range of about 300 to 500° C. while maintaining a containment pressure ranging from about 200 to 1000 psi and a vacuum of at least 10−4 torr;

[0043] heating the die at a rate of up to about 10° C./min to a second temperature range of about 500-1000° C. while maintaining a containment pressure of up to 6000 psi and vacuum pressure of 10−4 torr or less;

[0044] heating the die at a rate of up to 10° C./min to a densification and purification temperature range of 900-1500° C. while maintaining a containment pressure of up to 6000 psi and vacuum of at least 10−4 torr or less;

[0045] slowly cooling the die under a containment pressure of up to about 6000 psi until the temperature reaches a minimum of 1300° C., whereafter the containment pressure is released, while maintaining a vacuum pressure at 10−4 torr or less;

[0046] cooling the die in a vacuum pressure of 10−4 torr or less until the temperature reaches about 500° C. whereafter the die is further cooled by a flowing inert gas;

[0047] the inert gas used to cool the die is helium;

[0048] the stoichiometric product, for example a sputtering target, comprises or consists essentially of one phase with the second phase not exceeding more than about 1%;

[0049] the non-stoichiometric product, for example a sputtering target, comprises or consists essentially of two phases with any and all additional phases not exceeding about 1%;

[0050] the characteristics of the enhanced purity stoichiometric and non-stoichiometric article, for example a sputtering target, has a density of at least 95% of theoretical density, substantially no porosity, and impurities that have been reduced by at least 5%;

[0051] the density is at least equal to the theoretical density; and

[0052] the cooled compact has substantially the desired dimensions of the article, for example a sputtering target, which is then ground to the final desired dimensions.

EXAMPLES

[0053] One preferred process route is outlined in Table 1. In this and all following examples, some of the steps may be combined, and the process may be performed “in situ” in the same equipment.

TABLE 1
PROCESS STEP	GENERAL	PREFERRED CONDITIONS
Blending	Blend appropriate proportions	Ar atmosphere for 30-90
	of elemental powders	minutes depending on
		starting material
Loading	Pour into graphite dies and
	load dies into vacuum hot
	press
Evacuate	Evacuate chamber to achieve a
	pressure of 10 torr or less
Pre-compaction	To produce “green” compact	200-1000 psi
Degassing	To remove volatile gases and	300-500° C.
	moisture
Reactive	Powders are sintered	500-1000° C., 104 torr, 60-
sintering	reactively to form desired	240 minutes
	compounds
Densification and	Apply additional pressure to	1000-6000 psi, 104 torr,
Purification	achieve desired density and	900-1500° C.
	removal of volatile reaction
	products
Cooling	Slow cooling to prevent	Furnace cool under
	thermal shock	atmosphere control

[0054] The process parameters are defined in ranges because it has been found that in order to achieve the desired chemical composition and phases in the sputtering target, temperatures, heating and cooling rates, vacuum, hold times and pressure should be controlled. The specific process parameters will depend on the starting materials and desired composition.

[0055] It has also been found that sintering powders which react exothermically results in adiabatic temperature rises. This sudden rise in temperature causes impurities to volatilize which can then be evacuated with a vacuum system. The resulting grain size of the near-net sized product depends on the particle size distribution of elemental powders, and the nucleation and growth of new phases. Since the reaction occurs between powders which are uniformly blended, there are innumerable nucleation sites for new phases. Grain growth requires high temperatures but the new phases are not held at elevated temperature for extended periods of time, and grain growth is restricted, which results in a fine grain structure on the sputtering target. The exact grain size or range depends on the starting material. High pressures for densification are applied when the temperature rises because the reacted powders are then more ductile and easy to compact. Accomplishing this results in high densities. As mentioned previously, achieving desired phases in the product depends on control of the reactive sintering and densification processes in the vacuum hot press. The following examples illustrate the process. The invention described above describes a method to achieve success.

[0056] One example of the process for producing TiAl3 articles is described in Table 2.

TABLE 2
PROCESS STEP	GENERAL	PREFERRED CONDITIONS
Blending	Blend 37.15 wt % Ti and 62.85	Ar atmosphere for 60
	wt % Al powders in a V-blender	minutes
Loading	Pour into graphite dies and
	lead into vacuum hot press
Evacuate	Evacuate chamber to achieve 10−4
	torr pressure
Pre-compaction	Apply pressure to form a	600 psi
	compact
First	Remove volatile gases and	350° C.
Degassing	moisture
Compaction	To assist the reactive	4000 psi for 180
	sintering process	minutes
Reactive	Powders are sintered reactively	600° C., 10−4 ton′, hold
sintering	to form desired compounds	for 90 minutes
Densification	Apply additional pressure to	5000 psi, 10−4 torr,
and	achieve desired density and	600° C. hold for 90
Purification	removal of volatile reaction	minutes
	products	Note: Pressure for
		densification can be
		applied either
		continuously or in
		small increments
Second	To remove volatile gases which	5000 psi, 10−4 tort,
Degassing	were not removed by the first	1050° C., hold for 60
	degassing step.	minutes
Cooling	Slow cooling to prevent thermal	Furnace cool under
	shock	vacuum
Release	release pressure	release pressure
pressure

[0057] Since the reactive sintering process is initiated by diffusion and the rate of sintering depends on the packing density of the powders, a compaction step prior to reactive sintering assists in increasing the reaction rate. The degassing step removes moisture. During the reactive sintering process step, the titanium and aluminum powders in this example react to produce TiAl3. Control of process parameters ensures that the reaction occurs uniformly throughout the powder mixture resulting in a fine-grained (due to several nucleating sites) single phase near-net shaped TiAl3 blank. The exothermic nature of the reaction leads to a temperature increase which makes the reacted powder mixture plastic and thus easy to densify. The second degassing step removes the gases given out during the exothermic reactive process. The combination of two degassing steps at low and elevated temperatures prior to and after the reactive sintering step results in reduction of alkali and gaseous impurities and an enhanced purity article especially useful as a sputtering target.

[0058] The advantage of the process is reflected by absence of elemental Ti and Al powders in the finished article. This is determined by analyzing the near-net shaped blank using x-ray diffraction, SEM/EDS, and Atomic Absorption.

[0059] FIG. 1 shows the grain structure of a TiAl3 target processed using the process described above. The photomicrograph clearly sows that the grain size is less than 20 microns. FIG. 2 shows the x-ray diffraction pattern of a sample piece obtained from the target. The x-ray diffraction pattern shows the presence of a single phase TiAl3 compound.

[0060] Chemical analysis using GDMS, LECO and SIMS confirm that the purity of the finished product was higher than that of the original starting powders.

[0061] An example of a method of making non-stoichiometric TiSi2 blank useful as a sputtering target is described in Table 3.

TABLE 3
PROCESS STEP	GENERAL	PREFERRED
Blending	Blend-325 mesh proportions of	Ar atmosphere for 60 minutes
	elemental titanium and
	silicon powders
Loading	Pour into graphite dies and
	load dies into vacuum hot
	press
Evacuate	Evacuate chamber to achieve
	104 torr pressure
Pre-compaction	Apply pressure to compact	736 psi
Degassing	To remove volatile gases and	315° C.
	moisture
Reactive sintering	Powders are sintered	965° C., 10−4 torr, 120 minutes
	reactively to form desired	Note: Pressure for
	compounds	densification can be applied
		either continuously or in
		small increments
Densification and	Apply additional pressure to	5000 psi, 10−4 torr, hold for
Purification	achieve desired density and	120 minutes at 965° C.
	removal of volatile reaction
	products
Second Degassing	To remove volatile gases	1360° C. for 90 minutes; 5000
	which were not removed by the	psi
	first deqassing step.
Cooling	Slow cooling to prevent	Furnace cool under vacuum
	thermal shock	until temperature reaches
		1100° C. followed by
		backfilling with He and
		cooling fans
		Note: Cooling rates can be
		varied depending on product
		requirements
Release pressure	To prevent mechanical shock	Release pressure at 1100° C.
	during cooling

[0062] FIG. 3, which represents the analysis of titanium silicide target using x-ray diffraction revealed that the target contained two phases as expected. The two phases were TiSi2 and Si. Further analysis indicated that the TiSi2 is in the C54 phase, which is a low resistivity phase. The microstructural analysis showed a fine microstructure with an average grain size less than 20 microns (FIG. 4). GDMS, LECO and SIMS analysis showed that the overall purity of the target was higher than that of the staring powders.

[0063] Tables 4, 5 and 6 describe typical compositions of titanium aluminide, titanium silicide and tungsten silicide, respectively, which may be produced. Furthermore, when these compositions are produced as sputtering targets, it has been confirmed that the targets will produce films of titanium aluminide, titanium silicide and tungsten silicide, respectively, on a substrate.

TABLE 4
99.98% pure TiAl3
Units = ppm
Element	Maximum	Element	Maximum	Element	Maximum
Ag	1.00	K	0.50	Si	50
Al	MC	Li	0.10	Sn	5.00
As	1.00	Mg	10.00	Th	0.10
B	2.00	Mn	10.00	U	0.10
Ca	10.00	Mo	1.00	V	5.00
Cl	10.00	Na	1.00	Zn	5.00
Co	2.00	Nb	1.00	Zr	5.00
Cr	10.00	Ni	15.00
Cu	15.00	P	15.00	O	3000
Fe	25.00	Pb	5.00	C	100
In	5.00	S	15.00	N	300
Maximum Total Metallic Impurities: 200 ppm
Method of Analysis: C, O, N, by LECO; Na, K, Li by SIMS; all others by GDMS
Molar Ratio controlled to within +/− 0.1 of nominal value. Major constituents analyzed by Flame A. A.
Metallographic analysis is routinely performed on each manufactured lot of TiAl3 ensuring lot-to-lot and target-to-target consistency. Incoming powders must meet stringent particle size requirements.

[0064]

TABLE 5
99.995% pure TiSi2xx
Units = ppm
Element	Maximum	Element	Maximum	Element	Maximum
Ag	0.10	K	0.10	Si	MC
Al	15.00	L	0.0001	Sn	3.00
As	1.00	Mg	0.05	Th	0.001
B	2.00	Mn	0.30	U	0.001
Ca	2.00	Mo	1.00	V	1.00
Cl	10.00	Na	5.00	Zn	0.50
Co	2.00	Nb	1.00	Zr	2.50
Cr	10.00	Ni	5.00
Cu	2.00	P	2.50	O	3000
Fe	15.00	Pb	0.10	C	100
In	0.10	S	5.00	N	100
Maximum Total metallic Impurities: 50 ppm
Method of Analysis: C, O, N, by LECO; Na, K, Li by SIMS; all others by GDMS
Molar Ratio controlled to within +/− 0.1 of nominal value. Silicon concentration analyzed by Inductively Coupled Plasma Mass Spectrograph or Atomic Absorption techniques.

[0065]

TABLE 6
99.995% pure Wsi2xx
Units = ppm
Element	Maximum	Element	Maximum	Element	Maximum
Ag	0.10	K	0.50	Si	MC
Al	2.00	Li	0.001	Sn	1.00
As	1.00	Mg	0.05	Th	0.001
B	0.10	Mn	0.30	U	0.001
Ca	2.00	Mo	1.00	V	1.00
Cl	2.00	Na	0.50	Zn	0.50
Co	2.00	Nb	0.50	Zr	0.50
Cr	4.00	Ni	1.00
Cu	2.00	P	2.50	O	1000
Fe	5.00	Pb	0.10	C	70
In	0.50	S	2.00	N	20
Maximum Total Metallic Impurities: 50 ppm
Method of Analysis: C, O, N, by LECO; Na, K, Li by SIMS; all others by GDMS
Molar Ratio controlled to within +/− 0.1 of nominal value. Silicon concentration analyzed by Inductively Coupled Plasma Mass Spectrograph or Atomic Absorption techniques.

[0066] It is apparent from the foregoing that various changes and modifications may be made without departing from the invention. Accordingly, the scope of the invention should be limited only by the appended claims.

Claims

1. A method of making enhanced purity stoichiometric and non-stoichiometric articles, such as sputtering targets, comprising in situ reactive sintering and hot pressing powders of metal (M) and either silicon (Si) or aluminum (Al) where, for producing an aluminide article M comprises Ti, Fe, Co, Ni and/or Ta, and for producing a silicide article M comprises Ti, Ta, Ni, Cr, Co and/or Pt.

2. A method according to claim 1 to produce an article of enhanced purity such that the purity is enhanced by at least 5% of the original purity of the powders from which it is made.

3. An article of enhanced purity made form powders according to claim 1 wherein the purity is enhanced by an amount in the range of about 25 to 50% of the original purity of the powders from which it is made.

4. A method of making an article particularly useful as a sputtering target having enhanced purity comprising metal (M) and either silicon (Si) or aluminum (Al) from powder where, for producing an aluminide article M comprises Ti, Fe, Co, Ni and/or Ta, and for producing a silicide article M comprises Ti, Ta, Ni, Cr, Co and/or Pt comprising the following steps, which may be combined or rearranged in order: (a) providing a heat-resisting pressing die having a cavity with a configuration and dimensions for producing the desired article, the die having at least one movable pressing ram adapted for application of axial compaction forces to material in said cavity; (b) blending powders of metal (M) and either silicon (Si) or aluminum (Al) in proportionate ratio to provide a blended mix of the desired composition; (c) adding sufficient amounts of the blended mix into the cavity of the heat-resistant die so as to be able to yield a dense compact having substantially desired dimensions; (d) placing the die in a chamber for vacuum hot pressing; (e) applying a containment pressure to the mixture in the die adapted to be under high vacuum conditions by means of at least one movable ram capable of applying uniaxial compaction forces; (f) evacuating said chamber and said die to a vacuum pressure; (g) heating said die containing the mixture in the chamber to a temperature range sufficient to remove moisture and to volatilize alkali metals while maintaining uniaxial compaction pressure and vacuum pressure; (h) maintaining said temperature for a time period sufficient to substantially remove gases and alkali metals from the mixture: (i) heating the die containing the mixture in the chamber to a temperature range to allow the powders-to reactively sinter under pressure and high vacuum; (j) increasing uniaxial compaction pressure; (k) maintaining said compaction force under vacuum at said temperature for a time sufficient to allow for reactive sintering process to complete and effect desired compaction of the said mixture; (l) releasing said compaction force while maintaining high vacuum; (m) slowly cooling the die to relieve stresses in the compact while maintaining high vacuum; (n) releasing vacuum; and (o) removing the cooled compact produced from the die.

5. A method according to claim 4 wherein the die is heated at a rate of up to about 5° C./min to a first temperature range of about 300 to 500° C. while maintaining a containment pressure ranging from about 200 to 1000 psi and a vacuum of at least 10−4 torr.

6. A method according to claim 4 wherein the die is heated at a rate of up to about 10° C./min to a second temperature range of about 500-1000° C. while maintaining a containment pressure of up to 6000 psi and vacuum pressure of 10−4 torr or less.

7. A method according to claim 4 wherein the die is heated at a rate of up to 10° C./min to a densification and purification temperature range of 900-1500° C. while maintaining a containment pressure of up to 6000 psi and vacuum of at least 10−4 torr or less.

8. A method according to claim 4 wherein the die is slowly cooled under a containment pressure of up to about 6000 psi until the temperature reaches a minimum of 1300° C., whereafter the containment pressure is released, while maintaining a vacuum pressure at about 10−4 torr or less.

9. A method according to claim 4 wherein the die is cooled under a vacuum pressure of about 10−4 torr or less until the temperature reaches about 500° C. whereafter the die is further cooled by a flowing inert gas.

10. A method according to claim 9 wherein the inert gas used to cool the die is helium.

11. A method according to claim 4 wherein the stoichiometric product comprises one phase, and may contain a second phase not exceeding more than about 1%.

12. A method according to claim 4 wherein the non-stoichiometric product comprises two phases with any and all additional phases not exceeding about 1%.

13. A method according to claim 4 wherein the enhanced purity stoichiometric or non-stoichiometric article produced has a density of at least 95% of theoretical density, substantially no porosity, and impurities that have been reduced by at least 5% from the amount of impurities in the starting material.

14. A method according to claim 13 wherein the density is at least equal to the theoretical density.

15. A method according to claim 4 further comprising processing the compact to the final desired dimensions.

16. A method according to claim 15 wherein the compact is processed to produce a sputtering target.

17. A method according to claim 4 wherein the powders are not more than about 45 mm.

18. A method according to claim 4 wherein the aluminum or silicon powders are not more than about 45 microns.

19. A method according to claim 4 wherein the metal powder is not more than about 45 microns.

20. A method according to claim 4 wherein the vacuum pressure recited in step f) is about 10−4 torr or less.

21. A method according to claim 4 wherein the compaction pressure in step (j) is increased to about 1000 -6000 psi.

22. A method according to claim 4 wherein in step (m) the die is cooled to about 300° C. or less and the high vacuum maintained is a pressure of about 10−4 torr or less.

23. A method according to claim 4 wherein blending in step (b) is an inert atmosphere.

24. A method according to claim 4 wherein containment pressure in step (e) is about 200-1000 psi.

25. A aluminide or silicide sputtering target made form powders comprising a metal (M), and either silicon (Si) or aluminum (Al) where for producing an aluminide target M comprises Ti, Fe, Co, Ni and/or Ta, and for producing a silicide target M comprises Ti, Ta, Ni, Cr, Co and/or Pt, said target having density of at least 95% of theoretical.

26. A target according to claim 25 which comprises one phase and not more than about 1% additional phase.

27. A target according to claim 25 comprising two phases with any and all additional phases not exceeding about 1%.

28. A target according to claim 25 having substantially no porosity and at least 5% less impurities than the amount of impurities in the powders from which it is made.