Abstract
A heat shrinkable film having a shrinkage of at least 10% measured according to ASTM 2732 in water at 90° C. in a least one of MD and TD directions, where the film comprises an outer layer comprising polyester elastomer and a core layer comprising EVOH and/or PVDC. The film can be characterized by a combination of desirable properties, such as high shrinkage, good optical properties, excellent sealability and stack sealability. A method of producing a packaged food item by using a heat shrinkable film is provided. The use of a heat shrinkable film or bags and pouches made therefrom for packaging goods, for example, food products, is also provided.
Description
CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of European Application No. 07107035.3, filed Apr. 26, 2007, the disclosure of which is herein incorporated by reference.


The present invention refers to a multilayer heat shrinkable film characterized by a combination of desirable properties, such as high shrinkage, good optical properties, excellent sealability and stack sealability. The invention further is directed to a method of producing a packaged food item by using said film. The invention is further directed to the use of said film or bags and pouches made therefrom for packaging goods as for example food products.


Generally, the packaging of food items by means of a heat shrinkable bag comprises the following steps

    • 1. Putting the food item inside the bag and removing the air (vacuumizing) with the help of a vacuum device.
    • 2. Sealing of the open end of the bag.
    • 3. Placing the vacuum pack in a heat shrinking media such as hot water under a temperature that ensures the shrink of the pack (eg 90° C.).
    • 4. The pack is ready and is characterized by appealing appearance and long shelf life because of the absence of oxygen.


These films need high shrink properties and good optics to ensure an excellent appearance and excellent sealability so that there is no entrance of oxygen to the pack as this would be detrimental for the shelf life of the food.


In some cases, where the food is stored in frozen conditions for example, there is the possibility to use a non gas barrier film. The other characteristics remain the same.


Packaging films with the above properties are well known in the art.


A problem that is often found in the art is that during the packaging process the operators must put the food in the bags with extra care, as they must avoid the overlapping of the bags. When overlapped or semi overlapped packs are vacuumized and sealed, the outer surfaces of the two (or more) bags seal the one to the other under the temperature and pressure conditions used to guarantee the sealability of the inner surfaces. This may lead to high rejects and loss of productivity. This situation in particular occurs in stack sealing procedures, i.e. in a situation, wherein two or more products are situated one upon the other and then are sealed.


If the operator tries to modify the temperature, seal time, pressure conditions there is a high possibility that the inner surfaces do not seal sufficiently.


Using bags that can be heat sealed when overlapping occurs, without problems of insufficient seal strength and sealing of the outer surfaces could lead to higher productivity, smaller cycle of each packed product and less attention required by the operator.


The problem to be solved has been addressed in the past:


EP 1131205 refers to the use of a high melting point polyamide in the outer layer. The use of this material has the disadvantage that it reduces the shrinkage of the final film because of the high vicat of this resin. Therefore, this approach is not suitable for heat-shrinkable films and products made thereof.


EP0810087 also suggests the use of polyester, polyamide and EVOH materials in coextrusion.


EP 1060077 refers to the use of a polyester material in the outside layer and a polyamide in a core layer. This material also has a high vicat and reduces the shrinkage of the multilayer product.


EP 1415930 A1 refers to the use of peelable combinations comprising polybutylene in the outer layer. The problem in this case is that there is a high risk of deteriorating the optical properties as the outer layer (which contributes a lot to the optical properties of the combination) consists of the blend of two incompatible polymers able to make a cohesive peel. The outer layer should comprise an easily peelable combination so that stack sealability is easily achieved. The peelable composition is applied by “extrusion, co-extrusion or coating of a substrate”.


SUMMARY OF THE INVENTION

Therefore, the problem underlying the invention is to provide a heat sealable film, which can be advantageously be used in stack sealing applications. It is a further problem of the invention to avoid that the outer surfaces of the two (or more) bags in stack sealing applications seal the one to the other under the temperature and pressure conditions used to guarantee the sealability of the inner surfaces. It is a still further problem to provide bags that can be heat sealed when overlapping occurs, without problems of insufficient seal strength and sealing of the outer surfaces. It is an additional problem to provide a film for stack sealing applications which has excellent optical properties and high heat shrinkability. It is still a further problem to avoid the use of polyamide resin in the structure because of the following disadvantages:

    • 1. Polyamide has no dimensional stability in conditions of high humidity. This means that it may potentially create problems to stabilize the length and width of bags exposed to the atmosphere.
    • 2. Shrinkability of polyamide is low.


These problems are overcome by the subject-matter of the independent claims. Preferred embodiments are set forth in the dependent claims.


The inventors have managed to overcome all of these problems by discovering a film combining

    • 1. Excellent overlapping sealability
    • 2. Excellent sealing properties over a big range of machine conditions.
    • 3. Excellent optical properties
    • 4. Manufacturing in a stable and controlled way.
    • 5. High heat shrinkability


This is achieved by a heat shrinkable film which incorporates an outer layer from polyester elastomer and a core layer comprising EVOH and/or PVDC.


DEFINITIONS

In this application the following definitions are used:


The term “film” refers to a flat or tubular flexible structure of thermoplastic material.


The term “heat shrinkable” refers to a film that shrinks at least 10% in at least one of the longitudinal and transverse directions when heated at 90° C. for 4 seconds. The shrinkability is measured according to ASTM 2732.


The phrase “longitudinal direction” or “machine direction” herein abbreviated “MD” refers to a direction along the length of the film.


The phrase “outer layer” refers to the film layer which comes in immediate contact with the outside environment (atmosphere).


The phrase “inner layer” refers to the film layer that comes in direct contact with the product packed. This is also called “sealing layer” as this layer must be hermetically sealed in order to protect the product from ingress of air.


The phrase “core layer” refers to all film layers that exist between the outer and inner film layers.


The phrase “adjacent layer” refers to a layer which is to bond the outer layer to the core barrier layer. The adjacent layer preferably comprises maleic anhydrite modified polyolefin or other polyolefinic tie layer.


As used herein, the term “homopolymer” refers to a polymer resulting from polymerization of a single monomer.


As used herein, the term “copolymer” refers to a polymer resulting from polymerization of at least two different polymers.


As used herein, the term “polymer” includes both above types.


As used herein the term “polyethylene” identifies polymers consisting essentially of the ethylene repeating unit. The ones that have a density more than 0.940 are called high density polyethylene (HDPE), the ones that are have less than 0.940 are low density polyethylene (LDPE).


As used herein the phrase “ethylene alpha olefin copolymer” refers to polymers like linear low density polyethylene (LLDPE), medium density polyethylene (MDPE), very low density polyethylene (VLDPE), ultra low density polyethylene (ULDPE), metallocene catalysed polymers and polyethylene plastomers and elastomers.


As used herein the phrase “styrene polymers” refers to styrene homopolymer such as polystyrene and to styrene copolymers such as styrene-butadiene copolymers, styrene-butadiene-styrene copolymers, styrene-isoprene-styrene copolymers, styrene-ethylene-butadiene-styrene copolymers, ethylene-styrene copolymers and the like.


As used herein the phrase “ethylene methacrylate copolymers” refers to copolymers of ethylene and methacrylate monomer. The monomer content is less than 40%.


As used herein the phrase “ethylene vinyl acetate copolymer” refer to copolymers of ethylene and vinyl acetate.


As used herein, the term EVOH refers to saponified products of ethylene vinyl ester copolymers. The ethylene content is typically in the range of 25 to 50%.


As used herein the term PVDC refers to a vinylidene chloride copolymer wherein a major amount of the copolymer comprises vinylidene chloride and a minor amount of the copolymer comprises one or more monomers such as vinyl chloride and/or alkyl acrylates and methacrylates. Usually the PVDC copolymer may comprise heat stabilizers and plasticizers as is well known in the art.


As used herein the term polyamide refers to homopolymers and copolymers.


As used herein the term “polyester elastomer” refers to block copolymers where hard and soft blocks exist in the chain of the polymer. Examples of this kind of polymers are polyester ether and polyester ester copolymers, such as ARNITEL® from DSM, HYTREL® from Dupont and RITEFLEX® from TICONA.


All measurement methods mentioned herein are readily available for the skilled person. For example, they can be obtained from the American National Standards Institute at: www.webstore.ansi.org







DETAILED DESCRIPTION OF THE INVENTION

According to a first aspect the present invention is directed to a heat shrinkable film having a shrinkage of at least 10% measured according to ASTM 2732 in water at 90° C. in at least one of MD, TD directions, where the film comprises an outer layer of comprising polyester elastomer and a core layer comprising EVOH and/or PVDC.


A preferable resin for the outer layer according to the invention is a polyester elastomer, preferably a polyester ether elastomer. The melting point of this material is preferably 190° C. to 220° C. A blend of this polymer with a non elastomeric copolyester (eg polybutylene terephthalate) is also beneficial.


The adjacent layer comprises preferably maleic anhydrite modified polyolefin or other polyolefinic tie layer. The purpose of this layer is to bond the outer layer to the core barrier layer.


The adjacent layer comprises an oxygen barrier material selected from EVOH and PVDC. PVDC is preferable for higher shrinkability.


In the case of EVOH, a minor proportion of special polyamide can be used to increase the flexibility of EVOH.


Between the sealing layer and the oxygen barrier layer, a tie layer could be used. Preferred materials for this tie layer may be ethylene ester copolymers, such as ethylene vinyl acetate copolymers, ethylene methyl acrylate copolymers and other materials well known in the art. A preferred version might include maleic anhydrite modified ethylene ester copolymers or maleic anhydrite modified LLDPE. Commercial trademarks are for example BYNEL from Dupont and ADMER from Mitsui.


The inner heat sealing layer of the film may comprise ethylene alpha olefin copolymers and/or ethylene propylene copolymers or terpolymers. Typical examples are the homogeneous polymers AFFINITY® (DOW), EXACT® (EXXON), TAFMER® (MITSUI), Ethylene vinyl acetate copolymers and other well known in the art sealing layer polymers.


Between the outer and the barrier layer there may be another layer incorporating a tie layer. Preferred materials for this tie layer may be ethylene ester copolymers, such as ethylene vinyl acetate copolymers, ethylene methyl acrylate copolymers and other materials well known in the art. A preferred version might include maleic anhydrite modified ethylene ester copolymers or maleic anhydrite modified LLDPE. Commercial trademarks are for example BYNEL from Dupont and ADMER from Mitsui.


Any of the layers described above may also include additives well known in the art such as slip agents, antiblock, polymer processing aids, antistatic, antifog, acid scavengers, odour scavengers and the like. A person skilled in the art may select the right additives according to any particular needs.


In a preferred embodiment, the heat shrinkable film is irradiated after the extrusion. E beam is a recommendable process to crosslink the structure and increase mechanical properties.


In a further aspect, the invention is directed to the use of the films or the bag or pouch of the invention for packaging food and a method for packaging a food item. For example, the food item is putted inside the bag and the air is removed (vacuumising) with the help of a vacuum device. Subsequently, the open end of the bag is sealed and the vacuum pack is placed in a heat shrinking media such as hot water under a temperature that ensures the shrink of the pack (eg 90° C.). The pack than is ready and is characterized by appealing appearance and long shelf life because of the absence of oxygen.


The present invention is now described by the following Examples:


EXAMPLE 1

A 5 layer film is produced in a double bubble commercial line with the following recipe


Inner (sealing layer), 32% P1+30% P2+20% E1+10% E2+8% ADDITIVES


The percentage is in wt % unless otherwise indicated.


















Adjacent layer
D1



Barrier layer
PVDC commercial grade



Adjacent layer
D2



Outer layer
PEE1











See table 1


The thickness of the structure is 26/7/7/7/8 starting from the inner and going to the outer layer.


EXAMPLE 2

A 5 layer film is produced in a double bubble commercial line with the following recipe


Inner (sealing layer), 32% P1+30% P2+20% E1+10% E2+8% ADDITIVES


















Adjacent layer
D1



Barrier layer
EVOH 44% ethylene content



Adjacent layer
D2



Outer layer
PEE1











See table 1


The thickness of the structure is 26/7/7/7/8 starting from the inner and going to the outer layer.














TABLE 1








Melt







Index

Melting





g/10
Density
point


Type
Description
Manufacturer
min
g/cm3
° C.




















E1
EVA
Dupont 3135 X
0.35
0.93
95


E2
EVA
1005 VN2
0.40
0.928
102


D1
MODIFIED
MITSUI ADMER
3
0.91



LLDPE
518


P1
Plastomer
Dow Affinity VP
1.0
0.885
74




8770


PEE1
POLYESTER
ARNITEL EM 630
7 at
1.25
213



ELASTOMER

230 C.


D2
EVA
BYNEL 3861



MODIFIED


P2
PLASTOMER
DOW AFFINITY
1.0
0.902
100




PL 1880










Tests


1. Haze measurement. The haze measurement was done according to ASTM D 1003.


2. Gloss measurement. This was done according to BS 2782.


3. Shrinkage measurement done according to ASTM 2732.


4. Sealing window.


This final test was done on a Bosch vacuum sealing machine. We put one piece of the tube of each material on another so that there is an overlap area. We seal this area and then we pull. The material is thought to be OK if the outer surfaces are easily pulled without any delamination or resistance and the inner (sealing layers) are at the same time strongly sealed. Different sealing times were applied in order to see which of the three materials has a more extended operating window.


The results are displayed on table 2














TABLE 2










STACK SEAL





SHRINKAGE
WINDOW



HAZE
GLOSS
(MD/TD)
(sealing times)




















Material 1
6
93
52/40
4-10


Material 2
7
98
42/41
4-10


Comparison
10
95
35/42
4-10









So, the materials have the same stack sealable operating window and they combine much improved shrinkage properties as well as excellent optics in the case of material 1, 2.

Claims
  • 1. A heat shrinkable film having a shrinkage of at least 10% measured according to ASTM 2732 in water at 90° C. in at least one of the longitudinal and transverse directions, where the film comprises (a) an outer layer consisting of a polyester elastomer or a blend of a polyester elastomer and a non elastomeric copolyester, wherein a resin for the polyester elastomer is a polyester ether elastomer, and (b) a core layer consisting of polyvinylidene chloride (PVDC).
  • 2. The film of claim 1, wherein the melting point of the resin is 190° C. to 220° C.
  • 3. The film of claim 1, wherein the film further comprises an adjacent layer between the outer layer and the core layer.
  • 4. The film of claim 1, wherein the heat shrinkable film is irradiated after extrusion.
  • 5. A bag or pouch comprising a film according to claim 1.
  • 6. A method for producing a packaged food item comprising the steps of: a) providing a bag or pouch of claim 5,b) putting a food item inside the bag or pouch;c) removing the air (vacuumising) of the bag or pouch;d) sealing the open end of the bag or pouch; ande) placing the vacuum pack in a heat shrinking media.
  • 7. The method of claim 6, wherein the heat shrinking media is hot water at a temperature that ensures the shrink of the pack.
Priority Claims (1)
Number Date Country Kind
07107035 Apr 2007 EP regional
US Referenced Citations (95)
Number Name Date Kind
3299194 Golike Jan 1967 A
3356192 Cameron Dec 1967 A
3456044 Pahlke Jul 1969 A
3536192 Couper Oct 1970 A
3956229 Bollen et al. May 1976 A
4064296 Bornstein et al. Dec 1977 A
4254869 Heier Mar 1981 A
4399181 Yoshimura et al. Aug 1983 A
4612221 Biel et al. Sep 1986 A
4650721 Ashcraft et al. Mar 1987 A
4786561 Fong Nov 1988 A
4801486 Quacquarella et al. Jan 1989 A
4863769 Lustig et al. Sep 1989 A
4869049 Richards et al. Sep 1989 A
4912149 Robeson et al. Mar 1990 A
4934529 Richards et al. Jun 1990 A
4976898 Lustig et al. Dec 1990 A
4977022 Mueller Dec 1990 A
4990562 Chou et al. Feb 1991 A
5034281 Kawasaki et al. Jul 1991 A
5079051 Garland et al. Jan 1992 A
5179168 Hirasawa Jan 1993 A
5256351 Lustig et al. Oct 1993 A
5256428 Lustig et al. Oct 1993 A
5298202 Schirmer Mar 1994 A
5302402 Dudenhoeffer et al. Apr 1994 A
5397613 Georgelos Mar 1995 A
5562958 Walton et al. Oct 1996 A
5593747 Georgelos Jan 1997 A
5645788 Bekele Jul 1997 A
5698279 Vicik Dec 1997 A
5834077 Babrowicz Nov 1998 A
5837335 Babrowicz Nov 1998 A
5851610 Ristey et al. Dec 1998 A
6013378 White et al. Jan 2000 A
6074715 Lind et al. Jun 2000 A
6146726 Yoshii et al. Nov 2000 A
6221410 Ramesh et al. Apr 2001 B1
6274246 Eggers et al. Aug 2001 B1
6346285 Ramesh Feb 2002 B1
6406763 Wolf et al. Jun 2002 B1
6458437 Ito et al. Oct 2002 B1
6506463 Cahill et al. Jan 2003 B1
6514583 Ahlgren et al. Feb 2003 B1
6516588 Jensen et al. Feb 2003 B2
6534137 Vadhar Mar 2003 B1
6572959 Buongiorno et al. Jun 2003 B1
6592975 Ueyama et al. Jul 2003 B1
6663905 Ennis et al. Dec 2003 B1
6682792 Schmal et al. Jan 2004 B2
6960635 Stevens et al. Nov 2005 B2
7473473 Verrocchi Jan 2009 B2
7611770 Kennedy et al. Nov 2009 B2
7736726 McAllister et al. Jun 2010 B2
8129006 Ginossatis Mar 2012 B2
20020119334 Shepard et al. Aug 2002 A1
20020172834 Rivett et al. Nov 2002 A1
20030012900 Wolf et al. Jan 2003 A1
20030073785 Okada et al. Apr 2003 A1
20030213804 Chomik et al. Nov 2003 A1
20030218022 Chomik et al. Nov 2003 A1
20040065052 Ramesh et al. Apr 2004 A1
20040157077 Roussos Aug 2004 A1
20050064123 Chomik et al. Mar 2005 A1
20050129811 Kraimer et al. Jun 2005 A1
20050147778 Tai et al. Jul 2005 A1
20050191439 Hirose et al. Sep 2005 A1
20050271877 Ginossatis Dec 2005 A1
20060177616 Barber et al. Aug 2006 A1
20060177641 Breese et al. Aug 2006 A1
20060199030 Liang et al. Sep 2006 A1
20060199912 Fuchs et al. Sep 2006 A1
20060272767 Kreitman et al. Dec 2006 A1
20060286323 Siegel et al. Dec 2006 A1
20070042089 Grah Feb 2007 A1
20070082150 Ginossatis Apr 2007 A1
20080003332 Ginossatis Jan 2008 A1
20080070047 Rehkugler et al. Mar 2008 A1
20080095960 Schell et al. Apr 2008 A1
20080115463 Wilson May 2008 A1
20080255311 Chang et al. Oct 2008 A1
20080274328 Gkinosatis Nov 2008 A1
20080305220 Gkinosatis Dec 2008 A1
20090176117 Gkinosatis Jul 2009 A1
20090191392 Gkinosatis Jul 2009 A1
20090196962 Gkinosatis Aug 2009 A1
20090240227 Toro et al. Sep 2009 A1
20090263599 Gkinosatis Oct 2009 A1
20100028574 Gkinosatis Feb 2010 A1
20100034939 Gkinosatis Feb 2010 A1
20110159263 Gkinosatis Jun 2011 A1
20120279181 Gkinosatis Nov 2012 A1
20130019568 Gkinosatis Jan 2013 A1
20130209797 Gkinosatis Aug 2013 A1
20130227916 Gkinosatis Sep 2013 A1
Foreign Referenced Citations (49)
Number Date Country
511 195 Jul 1980 AU
0 005 660 Nov 1979 EP
0 286 407 Oct 1988 EP
0 402 043 Dec 1990 EP
0 472 418 Feb 1992 EP
0 627 465 Dec 1994 EP
0810087 Dec 1997 EP
1 072 632 Jan 2001 EP
0 930 349 Jun 2003 EP
1060077 Jun 2003 EP
1415930 May 2004 EP
1131205 Dec 2004 EP
1 514 680 Mar 2005 EP
1 770 116 Apr 2007 EP
1 854 625 Nov 2007 EP
08162162.5 Aug 2008 EP
1 985 440 Oct 2008 EP
1 985 443 Oct 2008 EP
1 995 058 Nov 2008 EP
2 077 239 Jul 2009 EP
2 077 297 Jul 2009 EP
2 085 216 Aug 2009 EP
2 111 979 Oct 2009 EP
2 147 783 Jan 2010 EP
1 140 765 Jan 1969 GB
2 236 531 Apr 1991 GB
62107810 May 1987 JP
03 200534 Sep 1991 JP
2002-234975 Aug 2002 JP
2003-159761 Jun 2003 JP
2005-047959 Feb 2005 JP
2005-335111 Dec 2005 JP
2006-247870 Sep 2006 JP
WO9601736 Jan 1996 WO
WO9746384 Dec 1997 WO
WO9821274 May 1998 WO
WO9821276 May 1998 WO
WO9944824 Sep 1999 WO
WO9957612 Nov 1999 WO
WO0061439 Oct 2000 WO
WO0123268 Apr 2001 WO
WO0226493 Apr 2002 WO
WO03020515 Mar 2003 WO
WO 2006053885 May 2006 WO
WO2006075141 Jul 2006 WO
WO2006102152 Sep 2006 WO
WO2007053603 May 2007 WO
WO2008091321 Jul 2008 WO
WO2008118554 Oct 2008 WO
Non-Patent Literature Citations (78)
Entry
Annonymous, “Advantages of metallocene ethylene [olymer resins in multilayer stretch films,” Research Disclosure, Mason Publications, Hampshire, GB. vol. 419, No. 26 (1999).
Annonymous, “Some benefits from the use of metallocene ethylene polymers in blown and cast films,” Research Disclosure, Mason Publications, Hampshire, GB. vol. 392, No. 54 (1996).
ASTM D 882-09. Standard Test Method for Tensile Properties of Thin Plastic Sheeting. American National Standards Institute. Jan. 2009. www.astm.org.
ASTM D 1003-07 “Haze and Luminous Transmittance of Transparent Plastics,” ASTM International. pp. 1-7.
ASTM D 1525-07 “Vicat Softening Temperature of Plastics,” ASTM International. pp. 1-9.
ASTM D 2732-03 “Unrestrained Linear Thermal Shrinkage of Plastic Film and Sheeting,” ASTM International. pp. 1-5.
ASTM D 3418-08. Standard Test Method for Transition Temperatures and Enthalpies of Fusion and Crystallization of Polymers by Differential Scanning Calorimetry. American National Standards Institute. Dec. 2008. www.astm.org.
ASTM D 3985. Standard Test Method for Oxygen Gas Transmission Rate Through Plastic Film and Sheeting Using a Coulometric Sensor. American National Standards Institute. pp. 1-7. www.astm.org.
ASTM F 1927-07. Standard Test Method for Determination of Oxygen Gas Transmission Rate, Permeability and Permeance at Controlled Relative Humidity Through Barrier Materials Using a Coulometric Detector. American National Standards Institute. Aug. 2007. www.astm.org.
BS 2782-0:2004 “Methods of Testing Plastics,” British Standards Institution. pp. 1-29 (2004).
English abstract of JP 2005-103902, USUI, Apr. 2005.
European Search Report corresponding to European Patent Application No. 08173056.6-2109 dated Mar. 16, 2009.
European Search Report corresponding to European Patent Application No. 08173057.4-2307 dated Sep. 22, 2009.
Extended European Search Report corresponding to European Patent Application No. 05021541.7-2115 dated Dec. 2, 2005.
Extended European Search Report corresponding to European Patent Application No. 08154742.4-2124 dated Jul. 2, 2009.
Extended European Search Report corresponding to European Patent Application No. 08156814 dated Oct. 9, 2008.
Extended European Search report corresponding to European Patent Application No. 09151289.7-2124 dated Jun. 8, 2009.
Interview Summary corresponding to U.S. Appl. No. 12/150,261 dated Dec. 28, 2010.
Machine Translation of JP 2005-103902, USUI, Apr. 2005.
Official Action corresponding to U.S. Appl. No. 11/528,741 dated Mar. 30, 2010.
Official Action corresponding to U.S. Appl. No. 11/528,741 dated Jan. 4, 2011.
Official Action corresponding to U.S. Appl. No. 11/528,741 dated May 18, 2011.
Official Action corresponding to U.S. Appl. No. 11/801,609 dated Sep. 15, 2009.
Official Action corresponding to U.S. Appl. No. 11/801,609 dated Feb. 5, 2010.
Official Action corresponding to U.S. Appl. No. 11/801,609 dated Jul. 15, 2010.
Official Action corresponding to U.S. Appl. No. 11/801,609 dated Jun. 20, 2011.
Official Action corresponding to U.S. Appl. No. 12/150,261 dated Oct. 27, 2009.
Official Action corresponding to U.S. Appl. No. 12/150,261 dated Jul. 7, 2010.
Official Action corresponding to U.S. Appl. No. 12/150,261 dated Mar. 22, 2011.
Official Action corresponding to U.S. Appl. No. 12/154,662 dated Mar. 29, 2011.
Official Action corresponding to U.S. Appl. No. 12/319,149 dated Oct. 15, 2009.
Official Action corresponding to U.S. Appl. No. 12/319,149 dated Jul. 7, 2010.
Official Action corresponding to U.S. Appl. No. 12/319,149 dated Mar. 22, 2011.
Official Action corresponding to U.S. Appl. No. 12/319,150 dated Oct. 15, 2010.
Official Action corresponding to U.S. Appl. No. 12/319,150 dated Apr. 26, 2011.
Official Action corresponding to U.S. Appl. No. 12/322,347 dated. Sep. 14, 2010.
Official Action corresponding to U.S. Appl. No. 12/322,347 dated Mar. 16, 2011.
Official Action corresponding to U.S. Appl. No. 12/508,233 dated Mar. 9, 2011.
“15.13xEA—Ethylene Vinyl Acetate (EVA) Copolymers (>50% Ethylene)—European Adhesives,” The ChemQuest Group, Inc. http://web.archive.org/web/20080219220919/http://www.chemquest.com/store/ethylene-vinyl-acetate-copolymers-european-adhesives.html (Aug. 26, 2011) (2 pages).
“DuPont™ Elvax® 3170,” DuPont Packaging & Industrial Polymers. 3 pages (2004) http://web.archive.org/web/20060516114601/http://www2.dupont.com/Elvax/en—US/assets/downloads/vax3170.pdf.
“Polymer Blend,” IUPAC Compendium of Chemical Terminology. 2nd Edition (1997).
Harper, “Modern Plastics Handbook,” McGraw-Hill: New York, New York. pp. 3.17-3.22 (2000).
Hough, M., and Dolbey, R., “Modern Plastics Compendium, vol. 1—Key Properties and Sources,” Smithers Rapra Technology. pp. 87-124 (1995).
Huskić, M., and {hacek over (S)}ebenik, A., “Characterization of Crosslinked Ethylene-Vinylacetate Copolymers,” Polymer International. vol. 31, No. 1 pp. 41-44 (1993).
Interview Summary corresponding to U.S. Appl. No. 12/150,261 dated Sep. 21, 2011.
Interview Summary corresponding to U.S. Appl. No. 12/319,149 dated Oct. 17, 2011.
Interview Summary corresponding to U.S. Appl. No. 12/319,150 dated Sep. 23, 2011.
Interview Summary corresponding to U.S. Appl. No. 12/322,347 dated Sep. 21, 2011.
Kipp, “Plastic Material Data Sheets,” MatWeb (2004) (5 pages).
Notice of Allowance corresponding to U.S. Appl. No. 11/528,741 dated Oct. 28, 2011.
Official Action corresponding to U.S. Appl. No. 11/801,609 dated Jan. 30, 2012.
Official Action corresponding to U.S. Appl. No. 12/150,261 dated Jan. 31, 2012.
Official Action corresponding to U.S. Appl. No. 12/154,662 dated Aug. 18, 2011.
Official Action corresponding to U.S. Appl. No. 12/154,662 dated Jan. 18, 2012.
Official Action corresponding to U.S. Appl. No. 12/319,149 dated Dec. 2, 2011.
Official Action corresponding to U.S. Appl. No. 12/319,150 dated Nov. 4, 2011.
Official Action corresponding to U.S. Appl. No. 12/322,347 dated Oct. 26, 2011.
Official Action corresponding to U.S. Appl. No. 12/426,496 dated Feb. 7, 2012.
Official Action corresponding to U.S. Appl. No. 12/508,233 dated Nov. 23, 2011.
Official Action corresponding to U.S. Appl. No. 12/512,361 dated Aug. 31, 2011.
Official Action corresponding to U.S. Appl. No. 12/957,947 dated Jan. 17, 2012.
Petrie, “Handbook of Adhesives and Sealants,” 2nd Edition. McGraw-Hill: New York, New York. pp. 465-466 (2007).
Unisource—Moisture Barrier & Oxygen Barrier Transmission Rates; <http://www.unisourcelink.com/packaging/pdf/MoistureBarrier.pdf> (Retrieved on Jan. 10, 2012).
“Polybutylene terephthalate,” Britannica Online Encyclopedia. pp. 1-3 (Accessed on Sep. 7, 2011) <http://www.britannica.com/EBchecked/topic/468341/polybutylene-terephthalate-PBT>.
“Polybutylene terephthalate (PBT),” 1 page <http://www.britannica.com/EBchecked/topic/468341/polybutylene-terephthalate-PBT> (Accessed on Jun. 13, 2012).
Extended European Search Report corresponding to European Patent Application No. 10193414.9-1217 dated May 9, 2011.
Interview Summary corresponding to U.S. Appl. No. 11/801,609 dated Jul. 31, 2012.
Interview Summary corresponding to U.S. Appl. No. 12/150,261 dated Jun. 12, 2012.
Interview Summary corresponding to U.S. Appl. No. 12/319,149 dated Jun. 15, 2012.
Interview Summary corresponding to U.S. Appl. No. 12/508,233 dated Apr. 26, 2012.
Official Action corresponding to U.S. Appl. No. 12/319,149 dated Aug. 27, 2012.
Official Action corresponding to U.S. Appl. No. 12/322,347 dated May 15, 2012.
Official Action corresponding to U.S. Appl. No. 12/508,233 dated Jun. 6, 2012.
Official Action corresponding to U.S. Appl. No. 12/512,361 dated May 2, 2012.
Official Action corresponding to U.S. Appl. No. 12/957,947 dated Sep. 25, 2012.
Search Report corresponding to French Patent Application No. 1059997 dated Jan. 16, 2012.
Interview Summary corresponding to U.S. Appl. No. 12/319,150 dated Sep. 6, 2013.
Official Action corresponding to U.S. Appl. No. 12/957,947 dated Jul. 24, 2013.
Related Publications (1)
Number Date Country
20080274314 A1 Nov 2008 US