Structurally-colored articles and methods for making and using structurally-colored articles

Information

  • Patent Grant
  • 11614563
  • Patent Number
    11,614,563
  • Date Filed
    Thursday, February 3, 2022
    2 years ago
  • Date Issued
    Tuesday, March 28, 2023
    a year ago
Abstract
One or more aspects of the present disclosure are directed to bladders that incorporate a multi-layer optical film that impart a structural color to the bladder. The present disclosure is also directed to articles including the bladders having a multi-layer optical film, and methods for making articles and bladders having a multi-layer optical film.
Description
BACKGROUND

Structural color is caused by the physical interaction of light with the micro- or nano-features of a surface and the bulk material as compared to color derived from the presence of dyes or pigments that absorb or reflect specific wavelengths of light based on the chemical properties of the dyes or pigments. Color from dyes and pigments can be problematic in a number of ways. For example, dyes and pigments and their associated chemistries for fabrication and incorporation into finished goods may not be environmentally friendly.





BRIEF DESCRIPTION OF THE DRAWINGS

Further aspects of the present disclosure will be more readily appreciated upon review of the detailed description of its various embodiments, described below, when taken in conjunction with the accompanying drawings.



FIG. 1 illustrates an article of footwear that includes the multi-layer optical films of the present disclosure.



FIG. 2 illustrates a side view of a portion of a bladder having an exemplary multi-layer optical film of the present disclosure.



FIGS. 3A-3B illustrate side views of exemplary multi-layer optical films of the present disclosure.





DESCRIPTION

The present disclosure provides for a bladder that is structurally colored. The bladder includes a multi-layer optical film disposed on a surface of the bladder. The multi-layer optical film as disposed on the bladder has the characteristic of imparting a structural color (e.g., a single-hue structural color, a multi-hue structural color, an iridescent structural color, etc.). The structural color imparts an aesthetically appealing color to the bladder without requiring the use of dyes or pigments and the environmental issues associated with their use. In one embodiment, the bladder can be used in articles of footwear, components of footwear, articles of apparel, components of apparel, articles of sports equipment, components of sports equipment, and the like. Additionally, the bladder can be used in other types of consumer goods.


The multi-layer optical film alone or optionally in combination with a textured surface (e.g., a textured layer or textured surface), or optionally in combination with a primer layer, or optionally in combination with both a textured surface and a primer layer, can impart the structural color. The optional textured surface and/or the primer layer can be part of the multi-layer optical film or can be separate from the multi-layer optical film, but, when used with the multi-layer optical film, combine to impart the structural color. In other words, while the multi-layer optical film alone can impart a first structural color, the combination of the multi-layer optical film with the optional textured structure or primer layer or both can impart a second structural color, which differs from the first structural color multi-layer optical film based on a color parameter such as hue, lightness, iridescence type. In such cases, the combination of the multi-layer optical film and the textured surface and/or the primer layer can impart the structural color to the bladder.


After disposing the multi-layer optical film onto a side or surface of a bladder wall or another component of the bladder, the bladder (e.g., bladder wall) appears to be colored (i.e., to have a new, different color than the surface of the bladder wall or component had prior to the disposition) without the application of pigments or dyes to the bladder, although dyes and/or pigments can be used in conjunction with the structural color. The multi-layer optical film can be disposed (e.g., affixed, attached, adhered, bonded, joined) to an exterior-facing side of the bladder, or an interior-facing side of the bladder. The bladder can then be incorporated into an article, such as a sole or an upper for an article of footwear, for example. The article (e.g., the sole and/or upper) can be designed so that one or more portions of the bladder including the structurally colored bladder wall or component is visible in the finished article, by including an opening, or a transparent component covering the structurally colored component, and the like.


The present disclosure provides for an article comprising: a bladder having a first bladder wall having a first bladder wall thickness and an exterior-facing side comprising a first thermoplastic material and an interior-facing side comprising a second thermoplastic material, wherein the first bladder wall has a gas transmission rate of 15 cm3/m2·atm·day or less for nitrogen for an average wall thickness of 20 mils; and an multi-layer optical film has a first side and a second side, wherein the first side and the second side are on opposing sides, wherein the first side of the multi-layer optical film, the second side of the multi-layer optical film, or both result in a structural color, wherein the multi-layer optical film is disposed on the exterior-facing side surface or the interior-facing side surface of the bladder or wherein the multi-layer optical film is disposed in an internal cavity of the bladder. The multi-layer optical film can include an optical layer. A textured surface and/or a primer layer in combination with the optical layer can result in the structural color. The present disclosure also provides for an article of footwear or an article of sporting equipment, comprising cushioning element, wherein the cushioning element includes a bladder. The present disclosure also provides for methods of making such an article.


The present disclosure also provides for an inflated bladder comprising a bladder wall having an interior-facing side and an exterior-facing side, wherein the interior-facing side defines at least a portion of an interior region of the inflated bladder, and wherein the bladder wall further includes an average wall thickness between the interior-facing side and exterior-facing side that is less than 5 millimeters; and a multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is operably disposed on the exterior-facing side of the bladder wall, and wherein the multi-layer optical film imparts a structural color to the bladder wall. The present disclosure also provides for methods of making such an article. The present disclosure also provides for a bladder comprising a bladder wall having an interior-facing side and an exterior-facing side, wherein the interior-facing side defines at least a portion of an interior region of the bladder; a plurality of topographical structures extending from the exterior-facing side of the bladder wall; and a multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is disposed on the exterior-facing side of the bladder wall and covering the plurality of topographical structures, and wherein the multi-layer optical film imparts a structural color to the bladder wall. The present disclosure also provides for methods of making such an article.


The present disclosure also provides for an article of footwear comprising a footwear upper; and an inflated bladder comprising a top wall operably secured to the footwear upper; a bottom wall opposite the top wall; and one or more sidewalls extending between the top wall and the bottom wall of the inflated bladder, wherein the top wall, the bottom wall, and the one or more sidewalls collectively define an interior region of the inflated bladder, and wherein the one or more sidewalls each comprise an exterior-facing side; and a multi-layer optical film operably disposed on the exterior-facing side at least one of the one or more sidewalls to impart a structural color to the one or more sidewalls. The present disclosure also provides for methods of making such an article.


In particular examples, a primer layer or a textured surface or both is included in the multi-layer optical film, or on the bladder. While many possible materials can be used to form the primer layer, it has been found that using titanium dioxide in the primer material of the primer layer, or using a primer material consisting essentially of titanium dioxide, results in a primer layer which adheres well to flexible polymeric materials including polyurethanes.


While in many examples of this disclosure, an iridescent structural color (i.e., a color which shifts over a wide range of hues when viewed from different angles) can be obtained, in other examples a structural color which does not shift over a wide range of hues when viewed from different angles (e.g., a structural color which does not shift hues, or which shifts over a limited number of hues) also can be obtained.


In one example, the present disclosure provides for the multi-layer optical film, as disposed onto the bladder, when measured according to the CIE 1976 color space under a given illumination condition at three observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and a1* and b1*, and a second color measurement at a second angle of observation having coordinates L2* and a2* and b2*, and a third color measurement at a third angle of observation having coordinates L3* and a3* and b3*, wherein the L1*, L2*, and L3* values may be the same or different, wherein the a1*, a2*, and a3* coordinate values may be the same or different, wherein the b1*, b2*, and b3* coordinate values may be the same or different, and wherein the range of the combined a1*, a2* and a3* values is less than about 40% of the overall scale of possible a* values.


In another example, the present disclosure provides for the multi-layer optical film, as disposed onto the bladder, when measured according to the CIE 1976 color space under a given illumination condition at two observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and a1* and b1*, and a second color measurement at a second angle of observation having coordinates L2* and a2* and b2*, wherein the L1* and L2* values may be the same or different, wherein the a1* and a2* coordinate values may be the same or different, wherein the b1* and b2* coordinate values may be the same or different, and wherein the ΔE*ab between the first color measurement and the second color measurement is less than or equal to about 100, where ΔE*ab=[(L1*−L2*)2+(a1*−a2*)2+(b1*−b2*)2]1/2.


In yet another example, the present disclosure provides for the multi-layer optical film, as disposed onto the bladder, when measured according to the CIELCH color space under a given illumination condition at three observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and C1* and h1°, and a second color measurement at a second angle of observation having coordinates L2* and C2* and h2°, and a third color measurement at a third angle of observation having coordinates L3* and C3* and h3°, wherein the L1*, L2*, and L3* values may be the same or different, wherein the C1*, C2*, and C3* coordinate values may be the same or different, wherein the h1°, h2° and h3° coordinate values may be the same or different, and wherein the range of the combined h1°, h2° and h3° values is less than about 60 degrees.


In an embodiment, the present disclosure provides for a method of making an article of footwear comprising: providing a bladder as described above and herein; and incorporating the bladder onto a sole structure. In addition, the method includes affixing the sole structure to an upper structure to form the article of footwear.


The present disclosure provides for a method of making a bladder, comprising: disposing a multi-layer optical film on a surface of a bladder. The bladder can be a bladder having a first bladder wall having a first bladder wall thickness and an exterior-facing side comprising a first thermoplastic material and an interior-facing side comprising a second thermoplastic material. Optionally, the first bladder wall has a gas transmission rate of 15 cm3/m2·atm·day or less for nitrogen for an average wall thickness of 20 mils; and disposing a multi-layer optical film onto at least one region of the bladder. The multi-layer optical film has a first side and a second side, wherein the first side and the second side are on opposing sides, wherein the first side of the multi-layer optical film, the second side of the multi-layer optical film, or both impart a structural color. The multi-layer optical film can be disposed on the exterior-facing side surface or the interior-facing side surface of the bladder, or can be disposed in an internal cavity of the bladder. The present disclosure also provides for a bladder formed using the method described above and herein.


Now having described embodiments of the present disclosure generally, additional discussion regarding embodiments will be described in greater details.


This disclosure is not limited to particular embodiments described, and as such may, of course, vary. The terminology used herein serves the purpose of describing particular embodiments only, and is not intended to be limiting, since the scope of the present disclosure will be limited only by the appended claims.


Where a range of values is provided, each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that stated range, is encompassed within the disclosure. The upper and lower limits of these smaller ranges may independently be included in the smaller ranges and are also encompassed within the disclosure, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the disclosure.


As will be apparent to those of skill in the art upon reading this disclosure, each of the individual embodiments described and illustrated herein has discrete components and features which may be readily separated from or combined with the features of any of the other several embodiments without departing from the scope or spirit of the present disclosure. Any recited method may be carried out in the order of events recited or in any other order that is logically possible.


Embodiments of the present disclosure will employ, unless otherwise indicated, techniques of material science, chemistry, textiles, polymer chemistry, and the like, which are within the skill of the art. Such techniques are explained fully in the literature.


Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art of material science, chemistry, textiles, polymer chemistry, and the like. Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present disclosure, suitable methods and materials are described herein.


As used in the specification and the appended claims, the singular forms “a,” “an,” and “the” may include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a support” includes a plurality of supports. In this specification and in the claims that follow, reference will be made to a number of terms that shall be defined to have the following meanings unless a contrary intention is apparent.


The present disclosure provides for bladder that have structural color. The structural color can be produced using a multi-layer optical film incorporated with the bladder. The multi-layer optical film can be incorporated into bladder, for example, on an exterior-facing side or surface or an interior-facing side or surface of the bladder. The bladder can be incorporated into a sole structure that can be affixed to the upper optionally with other components to form the article of footwear. The sole structure and/or upper can be designed so that one or more portions including the structural color are not covered up, include an opening, or otherwise exposed so that the structural color is visible in the finished article of footwear and provides an aesthetically pleasing appearance.


In an aspect, the bladder can be incorporated into a number of different types of articles of manufacture such as articles of footwear, components of footwear, articles of apparel, components of apparel, articles of sporting equipment, and components of sporting equipment. For example, the bladder can be used as a cushioning element once inflated (e.g., fluid-filled bladder). In particular, the articles of manufacture can include footwear (e.g., dress shoes, athletic footwear, hiking boots, work boots, or the like), skates (e.g., hockey skates, figure skates, in-line skates, roller skates, or the like), apparel (e.g., shirts, jerseys, pants, shorts, gloves, glasses, socks, hats, caps, jackets, undergarments) or components thereof, containers (e.g., backpacks, bags), and upholstery for furniture (e.g., chairs, couches, car seats), bed coverings (e.g., sheets, blankets), table coverings, towels, flags, tents, sails, and parachutes. In addition, the bladder can be used to produce articles or other items that are disposed on the article, where the article can be striking devices (e.g., bats, rackets, sticks, mallets, golf clubs, paddles, etc.), athletic equipment (e.g., golf bags, baseball and football gloves, soccer ball restriction structures), protective equipment (e.g., pads, helmets, guards, visors, masks, goggles, etc.), locomotive equipment (e.g., bicycles, motorcycles, skateboards, cars, trucks, boats, surfboards, skis, snowboards, etc.), balls or pucks for use in various sports, fishing or hunting equipment, furniture, electronic equipment, construction materials, eyewear, timepieces, jewelry, and the like. In an aspect, the bladder can be used as a cushioning element in the strap of a backpack or other bag.


The footwear can be designed for a variety of uses, such as sporting, athletic, military, work-related, recreational, or casual use. Primarily, the article of footwear is intended for outdoor use on unpaved surfaces (in part or in whole), such as on a ground surface including one or more of grass, turf, gravel, sand, dirt, clay, mud, and the like, whether as an athletic performance surface or as a general outdoor surface. However, the article of footwear may also be desirable for indoor applications, such as indoor sports including dirt playing surfaces for example (e.g., indoor baseball fields with dirt infields).


The article of footwear is designed for use in outdoor sporting activities, such as global football/soccer, golf, American football, rugby, baseball, running, track and field, cycling (e.g., road cycling and mountain biking), and the like. The article of footwear can optionally include traction elements (e.g., lugs, cleats, studs, and spikes as well as tread patterns) to provide traction on soft and slippery surfaces, where components of the present disclosure can be used or applied between or among the traction elements and optionally on the sides of the traction elements but on the surface of the traction element that contacts the ground or surface. Cleats, studs and spikes are commonly included in footwear designed for use in sports such as global football/soccer, golf, American football, rugby, baseball, and the like, which are frequently played on unpaved surfaces. Lugs and/or exaggerated tread patterns are commonly included in footwear including boots design for use under rugged outdoor conditions, such as trail running, hiking, and military use.


When the bladder is incorporated into footwear, the bladder can be incorporated into a sole structure that can be affixed to an upper as well as other components to form the footwear. In an aspect, the sole and/or upper can be designed so that one or more portions of the bladder are not covered up, include an opening, or otherwise exposed so that the structural color can be observed.



FIG. 1 illustrates an article of footwear having a bladder 11 that includes the multi-layer optical film of the present disclosure. The multi-layer optical film is represented by hashed area 12. The location of the multi-layer optical film is provided only to indicate one possible area that the multi-layer optical film can be located. Also, one location is illustrated in the figure, but this is done only for illustration purposes as the bladder can include one or a plurality of multi-layer optical films, where the size and location can be determined based on the item. The multi-layer optical film(s) located can represent a number, letter, symbol, design, emblem, graphic mark, icon, logo, or the like.



FIG. 2 illustrates a cross-section of the bladder that illustrate one possible location of the multi-layer optical film on a first bladder wall. As shown in FIG. 2, the first bladder wall 190 has a core layer 206 having a plurality of layers, optionally a cap layer 214, optionally a primer layer 204, optionally a textured structure or a textured layer 202, and a multi-layer optical film 200. Optionally, the position of the primer layer 204 and the textured structure or textured layer 202 can be reversed (not shown). Optionally, the cap layer 214 can be formed of the first thermoplastic material, and can include a textured surface (not shown). Alternatively or additionally, the side of the multi-layer optical film 200 facing the cap layer 214 can include a primer layer, or a textured surface, or both.


Bladders of the present disclosure include the multi-layer optical film that has the characteristic of producing optical effects such as structural color. The multi-layer optical film includes at least one optical layer (e.g., a multilayer reflector or a multilayer filter) optionally in combination with a textured surface (e.g., integral to the multi-layer optical film or as part of the surface of the bladder), optionally with a primer layer, optionally with a protective layer, or optionally with any combination of the textured surface, the primer layer, and the protective layer. The multi-layer optical film or the combination of the multi-layer optical film optionally with the textured surface and/or primer layer impart structural color (e.g., single color, multicolor, iridescent), to the bladder. Following disposing of the multi-layer optical film on the bladder, the bladder appears to be colored, for example a new, different, or more intense color (e.g., in hue or otherwise defined herein) than the surface of the article had prior to the disposing, and this can be achieved with or without the application of pigments or dyes to the bladder to produce aesthetically pleasing effects.


As has been described herein, the structural color can include one of a number of colors. The “color” of an bladder as perceived by a viewer can differ from the actual color of the bladder, as the color perceived by a viewer is determined by the actual color of the bladder, by the viewer's ability to detect the wavelengths of light reflected by the bladder, by the wavelengths of light used to illuminate the bladder, as well as other factors such as the coloration of the environment of the bladder, and the type of incident light (e.g., sunlight, fluorescent light, and the like). As a result, the color of an object as perceived by a viewer can differ from the actual color of the bladder.


Conventionally, color is imparted to man-made objects by applying colored pigments or dyes to the object. More recently, methods of imparting “structural color” to man-made objects have been developed. Structural color is color which is produced, at least in part, by microscopically structured surfaces that interfere with visible light contacting the surface. The structural color is color caused by physical phenomena including the scattering, refraction, reflection, interference, and/or diffraction of light, unlike color caused by the absorption or emission of visible light through coloring matters. For example, optical phenomena which result in structural color can include multilayer interference, thin-film interference, refraction, dispersion, light scattering, Mie scattering, diffraction, and diffraction grating. In various aspects described herein, structural color imparted to an article can be visible to a viewer having 20/20 visual acuity and normal color vision from a distance of about 1 meter from the article.


The structural color can be angle-independent structural color in that the hue, the hue and value, or the hue, value and chroma observed is independent of or substantially (e.g., about 90 percent, about 95 percent, or about 99 percent) independent of the angle of observation. For example, the angle-independent structural color can display the same hue or substantially the same hue when viewed from at least 3 different angles that are at least 15 degrees apart from each other (e.g., single-hue structural color).


As described herein, structural color is produced, at least in part, by the multi-layer optical film, as opposed to the color being produced solely by pigments and/or dyes. The coloration of a structurally-colored bladder can be due solely to structural color (i.e., the bladder, a colored portion of the bladder, or a colored outer layer of the bladder can be substantially free of pigments and/or dyes). Structural color can also be used in combination with pigments and/or dyes, for example, to alter all or a portion of a structural color.


“Hue” is commonly used to describe the property of color which is discernible based on a dominant wavelength of visible light, and is often described using terms such as magenta, red, orange, yellow, green, cyan, blue, indigo, violet, etc. or can be described in relation (e.g., as similar or dissimilar) to one of these. The hue of a color is generally considered to be independent of the intensity or lightness of the color. For example, in the Munsell color system, the properties of color include hue, value (lightness) and chroma (color purity). Particular hues are commonly associated with particular ranges of wavelengths in the visible spectrum: wavelengths in the range of about 700 to 635 nanometers are associated with red, the range of about 635 to 590 nanometers is associated with orange, the range of about 590 to 560 nanometers is associated with yellow, the range of about 560 to 520 nanometers is associated with green, the range of about 520 to 490 nanometers is associated with cyan, the range of about 490 nanometers to 450 nanometers is associated with blue, and the range of about 450 to 400 nanometers is associated with violet.


The color (including the hue) of a bladder as perceived by a viewer can differ from the actual color of the bladder. The color as perceived by a viewer depends not only on the physics of the bladder, but also its environment, and the characteristics of the perceiving eye and brain. For example, as the color perceived by a viewer is determined by the actual color of the bladder (e.g., the color of the light leaving the surface of the bladder), by the viewer's ability to detect the wavelengths of light reflected or emitted by the bladder, by the wavelengths of light used to illuminate the bladder, as well as other factors such as the coloration of the environment of the bladder, and the type of incident light (e.g., sunlight, fluorescent light, and the like). As a result, the color of an object as perceived by a viewer can differ from the actual color of the bladder.


When used in the context of structural color, one can characterize the hue of a structurally-colored article (bladder), i.e., an article (e.g., bladder) that has been structurally colored by incorporating an optical element into the article, based on the wavelengths of light the structurally-colored portion of the article absorbs and reflects (e.g., linearly and non-linearly). While the optical element may impart a first structural color, the presence of an optional textured surface and/or primer layer can alter the structural color. Other factors such as coatings or transparent elements may further alter the perceived structural color. The hue of the structurally colored article can include any of the hues described herein as well as any other hues or combination of hues. The structural color can be referred to as a “single hue” (i.e., the hue remains substantially the same, regardless of the angle of observation and/or illumination), or “multihued” (i.e., the hue varies depending upon the angle of observation and/or illumination). The multihued structural color can be iridescent (i.e., the hue changes gradually over two or more hues as the angle of observation or illumination changes). The hue of an iridescent multihued structural color can change gradually across all the hues in the visible spectrum (e.g., like a “rainbow”) as the angle of observation or illumination changes. The hue of an iridescent multihued structural color can change gradually across a limited number of hues in the visible spectrum as the angle of observation or illumination changes, in other words, one or more hues in the visible spectrum (e.g., red, orange, yellow, etc.) are not observed in the structural color as the angle of observation or illumination changes. Only one hue, or substantially one hue, in the visible spectrum may be present for a single-hued structural color. The hue of a multihued structural color can change more abruptly between a limited number of hues (e.g., between 2-8 hues, or between 2-4 hues, or between 2 hues) as the angle of observation or illumination changes.


The structural color can be a multi-hued structural color in which two or more hues are imparted by the structural color.


The structural color can be iridescent multi-hued structural color in which the hue of the structural color varies over a wide number of hues (e.g., 4, 5, 6, 7, 8 or more hues) when viewed at a single viewing angle, or when viewed from two or more different viewing angles that are at least 15 degrees apart from each other.


The structural color can be limited iridescent multi-hue structural color in which the hue of the structural color varies, or varies substantially (e.g., about 90 percent, about 95 percent, or about 99 percent) over a limited number of hues (e.g., 2 hues, or 3 hues) when viewed from two or more different viewing angles that are at least 15 degrees apart from each other. In some aspects, a structural color having limited iridescence is limited to two, three or four hues selected from the RYB primary colors of red, yellow and blue, optionally the RYB primary and secondary colors of red, yellow, blue, green, orange and purple, or optionally the RYB primary, secondary and tertiary colors of red, yellow, blue, green, orange purple, green-yellow, yellow-orange, orange-red, red-purple, purple-blue, and blue-green.


The structural color can be single-hue angle-independent structural color in which the hue, the hue and value, or the hue, value and chroma of the structural color is independent of or substantially (e.g., about 90 percent, about 95 percent, or about 99 percent) independent of the angle of observation. For example, the single-hue angle-independent structural color can display the same hue or substantially the same hue when viewed from at least 3 different angles that are at least 15 degrees apart from each other (e.g., single-hue structural color).


The structural color imparted can be a structural color having limited iridescence such that, when each color observed at each possible angle of observation is assigned to a single hue selected from the group consisting of the primary, secondary and tertiary colors on the red yellow blue (RYB) color wheel, for a single structural color, all of the assigned hues fall into a single hue group, wherein the single hue group is one of a) green-yellow, yellow, and yellow-orange; b) yellow, yellow-orange and orange; c) yellow-orange, orange, and orange-red; d) orange-red, and red-purple; e) red, red-purple, and purple; f) red-purple, purple, and purple-blue; g) purple, purple-blue, and blue; h) purple-blue, blue, and blue-green; i) blue, blue-green and green; and j) blue-green, green, and green-yellow. In other words, in this example of limited iridescence, the hue (or the hue and the value, or the hue, value and chroma) imparted by the structural color varies depending upon the angle at which the structural color is observed, but the hues of each of the different colors viewed at the various angles of observations varies over a limited number of possible hues. The hue visible at each angle of observation can be assigned to a single primary, secondary or tertiary hue on the red yellow blue (RYB) color wheel (i.e., the group of hues consisting of red, yellow, blue, green, orange purple, green-yellow, yellow-orange, orange-red, red-purple, purple-blue, and blue-green). For example, while a plurality of different colors are observed as the angle of observation is shifted, when each observed hue is classified as one of red, yellow, blue, green, orange purple, green-yellow, yellow-orange, orange-red, red-purple, purple-blue, and blue-green, the list of assigned hues includes no more than one, two, or three hues selected from the list of RYB primary, secondary and tertiary hues. In some examples of limited iridescence, all of the assigned hues fall into a single hue group selected from hue groups a)-j), each of which include three adjacent hues on the RYB primary, secondary and tertiary color wheel. For example, all of the assigned hues can be a single hue within hue group h) (e.g., blue), or some of the assigned hues can represent two hues in hue group h) (e.g., purple-blue and blue), or can represent three hues in hue group h) (e.g., purple-blue, blue, and blue-green).


Similarly, other properties of the structural color, such as the lightness of the color, the saturation of the color, and the purity of the color, among others, can be substantially the same regardless of the angle of observation or illumination, or can vary depending upon the angle of observation or illumination. The structural color can have a matte appearance, a glossy appearance, or a metallic appearance, or a combination thereof.


As discussed above, the color (including hue) of a structurally-colored bladder can vary depending upon the angle at which the structurally-colored bladder is observed or illuminated. The hue or hues of a bladder can be determined by observing the bladder, or illuminating the bladder, at a variety of angles using constant lighting conditions. As used herein, the “angle” of illumination or viewing is the angle measured from an axis or plane that is orthogonal to the surface. The viewing or illuminating angles can be set between about 0 and 180 degrees. The viewing or illuminating angles can be set at 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, and −15 degrees and the color can be measured using a colorimeter or spectrophotometer (e.g., Konica Minolta), which focuses on a particular area of the bladder to measure the color. The viewing or illuminating angles can be set at 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, 75 degrees, 90 degrees, 105 degrees, 120 degrees, 135 degrees, 150 degrees, 165 degrees, 180 degrees, 195 degrees, 210 degrees, 225 degrees, 240 degrees, 255 degrees, 270 degrees, 285 degrees, 300 degrees, 315 degrees, 330 degrees, and 345 degrees and the color can be measured using a colorimeter or spectrophotometer. In a particular example of a multihued bladder colored using only structural color, when measured at 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, and −15 degrees, the hues measured for bladder consisted of “blue” at three of the measurement angles, “blue-green” at 2 of the measurement angles and “purple” at one of the measurement angles.


In other embodiments, the color (including hue, value and/or chroma) of a structurally-colored bladder does not change substantially, if at all, depending upon the angle at which the bladder is observed or illuminated. In instances such as this the structural color can be an angle-independent structural color in that the hue, the hue and value, or the hue, value and chroma observed is substantially independent or is independent of the angle of observation.


Various methodologies for defining color coordinate systems exist. One example is L*a*b* color space, where, for a given illumination condition, L* is a value for lightness, and a* and b* are values for color-opponent dimensions based on the CIE coordinates (CIE 1976 color space or CIELAB). In an embodiment, a structurally-colored bladder having structural color can be considered as having a “single” color when the change in color measured for the bladder is within about 10% or within about 5% of the total scale of the a* or b* coordinate of the L*a*b* scale (CIE 1976 color space) at three or more measured observation or illumination angles selected from measured at observation or illumination angles of 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, and −15 degrees. In certain embodiments, colors which, when measured and assigned values in the L*a*b* system that differ by at least 5 percent of the scale of the a* and b* coordinates, or by at least 10 percent of the scale of the a* and b* coordinates, are considered to be different colors. The structurally-colored bladder can have a change of less than about 40%, or less than about 30%, or less than about 20%, or less than about 10%, of the total scale of the a* coordinate or b* coordinate of the L*a*b* scale (CIE 1976 color space) at three or more measured observation or illumination angles.


A change in color between two measurements in the CIELAB space can be determined mathematically. For example, a first measurement has coordinates L1*, a1* and b1*, and a second measurement has coordinates L2*, a2* and b2*. The total difference between these two measurements on the CIELAB scale can be expressed as ΔE*ab, which is calculated as follows: ΔE*ab=[(L1*−L2*)2+(a1*−a2*)2+(b1*−b2*)2]1/2. Generally speaking, if two colors have a ΔE*ab of less than or equal to 1, the difference in color is not perceptible to human eyes, and if two colors have a ΔE*ab of greater than 100 the colors are considered to be opposite colors, while a ΔE*ab of about 2-3 is considered the threshold for perceivable color difference. In certain embodiments, a structurally colored bladder having structural color can be considered as having a “single” color when the ΔE*ab is less than 60, or less than 50, or less than 40, or less than 30, between three or more measured observation or illumination angles selected from measured at observation or illumination angles of 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, and −15 degrees. The structurally-colored bladder can have a ΔE*ab that is less than about 100, or less than about 80, or less than about 60, between two or more measured observation or illumination angles.


Another example of a color scale is the CIELCH color space, where, for a given illumination condition, L* is a value for lightness, C* is a value for chroma, and h° denotes a hue as an angular measurement. In an embodiment, a structurally-colored bladder having structural color can be considered as having a “single” color when the color measured for the bladder is less than 10 degrees different or less than 5 degrees different at the h° angular coordinate of the CIELCH color space, at three or more measured observation or illumination angles selected from measured at observation or illumination angles of 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, and −15 degrees. In certain embodiments, colors which, when measured and assigned values in the CIELCH system that vary by at least 45 degrees in the h° measurements, are considered to be different colors The structurally-colored bladder can have a change of less than about 60 degrees, or less than about 50 degrees, or less than about 40 degrees, or less than about 30 degrees, or less than about 20 degrees, or less than about 10 degrees, in the h° measurements of the CIELCH system at three or more measured observation or illumination angles.


Another system for characterizing color includes the “PANTONE” Matching System (Pantone LLC, Carlstadt, New Jersey, USA), which provides a visual color standard system to provide an accurate method for selecting, specifying, broadcasting, and matching colors through any medium. In an example, a structurally-colored bladder having a structural color can be considered as having a “single” color when the color measured for the bladder is within a certain number of adjacent standards, e.g., within 20 adjacent PANTONE standards, at three or more measured observation or illumination angles selected from 0 degrees, 15 degrees, 30 degrees, 45 degrees, 60 degrees, and −15 degrees.


Now having described color, additional details regarding the multi-layer optical film are provided. As described herein, the article includes the multi-layer optical film. The multi-layer optical film includes at least one optical layer. The multi-layer optical film that can be or include a single or multilayer reflector or a multilayer filter. The multi-layer optical film can function to modify the light that impinges thereupon so that structural color is imparted to the article. The multi-layer optical film can include at least one optical layer and optionally one or more additional layers (e.g., a protective layer, the textured layer, the primer layer, a polymer layer, and the like).


The method of making the structurally colored article can include disposing (e.g., affixing, attaching, bonding, fastening, joining, appending, connecting, binding and includes operably disposing etc.) the multi-layer optical film onto an article (e.g., an article of footwear, an article of apparel, an article of sporting equipment, etc.). The article includes a component, and the component has a surface upon which the multi-layer optical film can be disposed. The surface of the article can be made of a material such as a thermoplastic material or thermoset material, as described herein. For example, the article has a surface including a thermoplastic material (i.e., a first thermoplastic material), for example an externally-facing surface of the component or an internally-facing surface of the component (e.g., an externally-facing surface or an internally-facing surface a bladder). The multi-layer optical film can be disposed onto the thermoplastic material, for example.


The multi-layer optical film has a first side (including the outer surface) and a second side opposing the first side (including the opposing outer surface), where the first side or the second side is adjacent the article. For example, when the multi-layer optical film is used in conjunction with a component having internally-facing and externally-facing surfaces, such as a film or a bladder, the first side of the multi-layer optical film can be disposed on the internally-facing surface of the component, such as in the following order: second side of the multi-layer optical film/core of the multi-layer optical film/first side of the multi-layer optical film/internally-facing surface of the component/core of the component/externally-facing surface of the component. Alternatively, the second side the multi-layer optical film can be disposed on the internally-facing surface of the component, such as in the following order: first side of the multi-layer optical film/core of the multi-layer optical film/second side of the multi-layer optical film/internally-facing surface of the component/core of the component wall/externally-facing surface of the component. In another example, the first side of the multi-layer optical film can be disposed on the externally-facing surface of the component, such as in the following order: internally-facing surface of the component/core of the component/externally-facing surface of the component/first side of the multi-layer optical film/core of the multi-layer optical film/second side of the multi-layer optical film. Similarly, the second side of the multi-layer optical film can be disposed on the externally-facing surface of the component, such as in the following order: internally-facing surface of the component/core of the component/externally-facing surface of the component/second side of the multi-layer optical film/core of the multi-layer optical film/first side of the multi-layer optical film. In examples where the optional textured surface, the optional primer layer, or both are present, the textured surface and/or the primer layer can be located at the interface between the surface of the component and a side of the multi-layer optical film.


The multi-layer optical film or layers or portions thereof (e.g., optical layer) can be formed using known techniques such as physical vapor deposition, electron beam deposition, atomic layer deposition, molecular beam epitaxy, cathodic arc deposition, pulsed laser deposition, sputtering deposition (e.g., radio frequency, direct current, reactive, non-reactive), chemical vapor deposition, plasma-enhanced chemical vapor deposition, low pressure chemical vapor deposition and wet chemistry techniques such as layer-by-layer deposition, sol-gel deposition, Langmuir-Blodgett, and the like. The temperature of the first side can be adjusted using the technique to form the multi-layer optical film and/or a separate system to adjust the temperature. Additional details are provided herein.


The optical layer(s) of the multi-layer optical film can comprise a multilayer reflector. The multilayer reflector can be configured to have a certain reflectivity at a given wavelength of light (or range of wavelengths) depending, at least in part, on the material selection, thickness and number of the layers of the multilayer reflector. In other words, one can carefully select the materials, thicknesses, and numbers of the layers of a multilayer reflector and optionally its interaction with one or more other layers, so that it can reflect a certain wavelength of light (or range of wavelengths), to produce a desired structural color. The optical layer can include at least two adjacent layers, where the adjacent layers have different refractive indices. The difference in the index of refraction of adjacent layers of the optical layer can be about 0.0001 to 50 percent, about 0.1 to 40 percent, about 0.1 to 30 percent, about 0.1 to 20 percent, about 0.1 to 10 percent (and other ranges there between (e.g., the ranges can be in increments of 0.0001 to 5 percent)). The index of refraction depends at least in part upon the material of the optical layer and can range from 1.3 to 2.6.


The optical layer(s) can include 2 to 20 layers, 2 to 10 layer, 2 to 6 layers, or 2 to 4 layers. Each layer of the optical layer can have a thickness that is about one-fourth of the wavelength of light to be reflected to produce the desired structural color. Each layer of the optical layer can have a thickness of about 10 to 500 nanometers or about 90 to 200 nanometers. The optical layer can have at least two layers, where adjacent layers have different thicknesses and optionally the same or different refractive indices.


The multi-layer optical film can comprise a multilayer filter. The multilayer filter destructively interferes with light that impinges upon the bladder, where the destructive interference of the light and optionally interaction with one or more other layers or structures (e.g., a multilayer reflector, a textured structure) result in the structural color. In this regard, the layers of the multilayer filter can be designed (e.g., material selection, thickness, number of layer, and the like) so that a single wavelength of light, or a particular range of wavelengths of light, make up the structural color. For example, the range of wavelengths of light can be limited to a range within plus or minus 30 percent of a single wavelength, or within plus or minus 20 percent of a single wavelength, or within plus or minus 10 percent of a single wavelength, or within plus or minus 5 percent or a single wavelength. The range of wavelengths can be broader to produce a more iridescent structural color.


The optical layer(s) can include multiple layers where each layer independently comprises a material selected from: the transition metals, the metalloids, the lanthanides, and the actinides, as well as nitrides, oxynitrides, sulfides, sulfates, selenides, and tellurides of these. The material can be selected to provide an index of refraction that when optionally combined with the other layers of the multi-layer optical film achieves the desired result. One or more layers of the optical layer can be made of liquid crystals. Each layer of the optical layer can be made of liquid crystals. One or more layers of the optical layer can be made of a material such as: silicon dioxide, titanium dioxide, zinc sulfide, magnesium fluoride, tantalum pentoxide, aluminum oxide, or a combination thereof. Each layer of the optical layer can be made of a material such as: silicon dioxide, titanium dioxide, zinc sulfide, magnesium fluoride, tantalum pentoxide, aluminum oxide, or a combination thereof.


The multi-layer optical film can be uncolored (e.g., no pigments or dyes added to the structure or its layers), colored (e.g., pigments and/or dyes are added to the structure or its layers (e.g., dark or black color)), reflective, and/or transparent (e.g., percent transmittance of 75 percent or more). The side upon which the multi-layer optical film is disposed can be uncolored (e.g., no pigments or dyes added to the material), colored (e.g., pigments and/or dyes are added to the material (e.g., dark or black color)), reflective, and/or transparent (e.g., percent transmittance of 75 percent or more).


The optical layer(s) can be formed in a layer-by-layer manner, where each layer has a different index of refraction. Each layer of the optical layer can be formed using known techniques such as physical vapor deposition including: chemical vapor deposition, pulsed laser deposition, evaporative deposition, sputtering deposition (e.g., radio frequency, direct current, reactive, non-reactive), plasma enhanced chemical vapor deposition, electron beam deposition, atomic layer deposition, molecular beam epitaxy, cathodic arc deposition, low pressure chemical vapor deposition and wet chemistry techniques such as layer by layer deposition, sol-gel deposition, Langmuir-Blodgett and the like.


As mentioned above, the multi-layer optical film can include one or more layers in addition to the optical layer(s). The multi-layer optical film has a first side (e.g., the side having a surface) and a second side (e.g., the side having a surface), where the first side or the second side is adjacent the surface of the component. The one or more other layers of the multi-layer optical film can be on the first side and/or the second side of the multi-layer optical film. For example, the multi-layer optical film can include a protective layer and/or a polymeric layer such as a thermoplastic polymeric layer, where the protective layer and/or the polymeric layer can be on one or both of the first side and the second side of the multi-layer optical film. In another example, the multi-layer optical film can include a primer layer as described herein. One or more of the optional other layers can include a textured surface. Alternatively or in addition, one or more optical layers of the multi-layer optical film can include a textured surface.


A protective layer can be disposed on the first and/or second side of the optical layer to protect the optical layer. The protective layer is more durable or more abrasion resistant than the optical layer. The protective layer is optically transparent to visible light. The protective layer can be on the first side of the multi-layer optical film to protect the optical layer. All or a portion of the protective layer can include a dye or pigment in order to alter an appearance of the structural color. The protective layer can include silicon dioxide, glass, combinations of metal oxides, or mixtures of polymers. The protective layer can have a thickness of about 3 nanometers to 1 millimeter.


The protective layer can be formed using physical vapor deposition, chemical vapor deposition, pulsed laser deposition, evaporative deposition, sputtering deposition (e.g., radio frequency, direct current, reactive, non-reactive), plasma enhanced chemical vapor deposition, electron beam deposition, cathodic arc deposition, low pressure chemical vapor deposition and wet chemistry techniques such as layer by layer deposition, sol-gel deposition, Langmuir-Blodgett, and the like. Alternatively or in addition, the protective layer can be applied by spray coating, dip coating, brushing, spin coating, doctor blade coating, and the like.


A polymeric layer can be disposed on the first and/or the second side of the multi-layer optical film. The polymeric layer can be used to dispose the multi-layer optical film onto an article, such as, for example, when the article does not include a thermoplastic material to adhere the multi-layer optical film. The polymeric layer can comprise a polymeric adhesive material, such as a hot melt adhesive. The polymeric layer can be a thermoplastic material and can include one or more layers. The thermoplastic material can be any one of the thermoplastic material described herein. The polymeric layer can be applied using various methodologies, such as spin coating, dip coating, doctor blade coating, and so on. The polymeric layer can have a thickness of about 3 nanometers to 1 millimeter.


As described above, one or more embodiments of the present disclosure provide articles that incorporate the multi-layer optical film (e.g., single or multilayer structures) on a side of a component of the article to impart structural color. The multi-layer optical film can be disposed onto the thermoplastic material of the side of the article, and the side of the article can include a textile, including a textile comprising the thermoplastic material.


Having described the structural color structure, additional details will now be described for the optional textured surface. As described herein, the component includes the multi-layer optical film and the multi-layer optical film can include at least one optical layer and optionally a textured surface. The textured surface can be a surface of a textured structure or a textured layer. The textured surface may be provided as part of the multi-layer optical film. For example, the multi-layer optical film may comprise a textured layer or a textured structure that comprises the textured surface. The textured surface may be formed on the first or second side of the multi-layer optical film. For example, a side of the optical layer may be formed or modified to provide a textured surface, or a textured layer or textured structure can be affixed to the first or second side of the multi-layer optical film. The textured surface may be provided as part of the component to which the multi-layer optical film is disposed. For example, the multi-layer optical film may be disposed onto the surface of the component where the surface of the component is a textured surface, or the surface of the component includes a textured structure or a textured layer affixed to it.


The textured surface (or a textured structure or textured layer including the textured surface) may be provided as a feature on or part of another medium, such as a transfer medium, and imparted to a side or layer of the multi-layer optical film or to the surface of the component. For example, a mirror image or relief form of the textured surface may be provided on the side of a transfer medium, and the transfer medium contacts a side of the multi-layer optical film or the surface of the component in a way that imparts the textured surface to the multi-layer optical film or article. While the various embodiments herein may be described with respect to a textured surface of the multi-layer optical film, it will be understood that the features of the textured surface, or a textured structure or textured layer, may be imparted in any of these ways.


The textured surface can contribute to the structural color resulting from the multi-layer optical film. As described herein, structural coloration is imparted, at least in part, due to optical effects caused by physical phenomena such as scattering, diffraction, reflection, interference or unequal refraction of light rays from a multi-layer optical film. The textured surface (or its mirror image or relief) can include a plurality of profile features and flat or planar areas. The plurality of profile features included in the textured surface, including their size, shape, orientation, spatial arrangement, etc., can affect the light scattering, diffraction, reflection, interference and/or refraction resulting from the multi-layer optical film. The flat or planar areas included in the textured surface, including their size, shape, orientation, spatial arrangement, etc., can affect the light scattering, diffraction, reflection, interference and/or refraction resulting from the multi-layer optical film. The desired structural color can be designed, at least in part, by adjusting one or more of properties of the profile features and/or flat or planar areas of the textured surface.


The profile features (also referred to as “topographical structures”) can extend from a side of the flat areas, so as to provide the appearance of projections and/or depressions therein. A profile feature may include various combinations of projections and depressions. For example, a profile feature may include a projection with one or more depressions therein, a depression with one or more projections therein, a projection with one or more further projections thereon, a depression with one or more further depressions therein, and the like. The flat areas do not have to be completely flat and can include texture, roughness, and the like. The texture of the flat areas may not contribute much, if any, to the imparted structural color. The texture of the flat areas typically contributes to the imparted structural color. For clarity, the profile features and flat areas are described in reference to the profile features extending above the flat areas, but the inverse (e.g., dimensions, shapes, and the like) can apply when the profile features are depressions in the textured structure.


The textured surface can comprise a thermoplastic material or a thermoset material. The profile features and the flat areas can be formed using a thermoplastic material. For example, when the thermoplastic material is heated above its softening temperature a textured surface can be formed in the thermoplastic material such as by molding, stamping, printing, compressing, cutting, etching, vacuum forming, etc., the thermoplastic material to form profile features and flat areas therein. The textured surface can be imparted on a side of a thermoplastic material. The textured surface can be formed in a layer of thermoplastic material. The profile features and the flat areas can be made of the same thermoplastic material or a different thermoplastic material. In an embodiment, the exterior-facing side or surface and/or the interior-facing side or surface of the bladder can be made of a thermoplastic material and the textured surface or textured surface can be formed as described.


The textured surface generally has a length dimension extending along an x-axis, and a width dimension extending along a z-axis, and a thickness dimension extending along a y-axis. The textured surface has a generally planar portion extending in a first plane that extends along the x-axis and the z-axis. A profile feature can extend outward from the first plane, so as to extend above or below the plane x. A profile feature may extend generally orthogonal to the first plane, or at an angle greater to or less than 90 degrees to the first plane.


The dimension (e.g., length, width, height, diameter, depending upon the shape of the profile feature) of each profile feature can be within the nanometer to micrometer range. A textured surface can have a profile feature and/or flat area with a dimension of about 10 nanometers to about 500 micrometers. The profile feature can have dimensions in the nanometer range, e.g., from about 10 nanometers to about 1000 nanometers. All of the dimensions of the profile feature (e.g., length, width, height, diameter, depending on the geometry) can be in the nanometer range, e.g., from about 10 nanometers to about 1000 nanometers. The textured surface can have a plurality of profile features having dimensions that are 1 micrometer or less. In this context, the phrase “plurality of the profile features” is meant to mean that about 50 percent or more, about 60 percent or more, about 70 percent or more, about 80 percent or more, about 90 percent or more, or about 99 percent or more of the profile features have a dimension in this range. The profile features can have a ratio of width:height and/or length:height dimensions of about 1:2 and 1:100, or 1:5 and 1:50, or 1:5 and 1:10.


The textured surface can have a profile feature and/or flat area with a dimension within the micrometer range of dimensions. A textured surface can have a profile feature and/or flat area with a dimension of about 1 micrometer to about 500 micrometers. All of the dimensions of the profile feature (e.g., length, width, height, diameter, depending on the geometry) can be in the micrometer range, e.g., from about 1 micrometer to about 500 micrometers. The textured surface can have a plurality of profile features having dimensions that are from about 1 micrometer to about 500 micrometer. In this context, the phrase “plurality of the profile features” is meant to mean that about 50 percent or more, about 60 percent or more, about 70 percent or more, about 80 percent or more, about 90 percent or more, or about 99 percent or more of the profile features have a dimension in this range. The height of the profile features (or depth if depressions) can be about 0.1 and 50 micrometers, about 1 to 5 micrometers, or 2 to 3 micrometers. The profile features can have a ratio of width:height and/or length:height dimensions of about 1:2 and 1:100, or 1:5 and 1:50, or 1:5 and 1:10.


A textured surface can have a plurality of profile features having a mixture of size dimensions within the nanometer to micrometer range (e.g., a portion of the profile features are on the nanometer scale and a portion of the profile features are on the micrometer scale). A textured surface can have a plurality of profile features having a mixture of dimensional ratios. The textured surface can have a profile feature having one or more nanometer-scale projections or depressions on a micrometer-scale projection or depression.


The profile feature can have height and width dimensions that are within a factor of three of each other (0.33w≤h≤3w where w is the width and h is the height of the profile feature) and/or height and length dimensions that are within a factor of three of each other (0.331≤h≤3l where l is the length and h is the height of the profile feature). The profile feature can have a ratio of length:width that is from about 1:3 to about 3:1, or about 1:2 to about 2:1, or about 1:1.5 to about 1.5:1, or about 1:1.2 to about 1.2:1, or about 1:1. The width and length of the profile features can be substantially the same or different.


The profile features can have a certain spatial arrangement. The spatial arrangement of the profile features may be uniform, such as spaced evenly apart or forming a pattern. The spatial arrangement can be random. Adjacent profile features can be about 1 to 100 micrometers apart or about 5 to 100 micrometers apart. The desired spacing can depend, at least in part, on the size and/or shape of the profile surfaces and the desired structural color effect.


The profile features can have a certain cross-sectional shape (with respect to a plane parallel the first plane). The textured surface can have a plurality of profile features having the same or similar cross-sectional shape. The textured surface has a plurality of profile features having a mixture of different cross-sectional shapes. The cross-sectional shapes of the profile features can include polygonal (e.g., square or triangle or rectangle cross section), circular, semi-circular, tubular, oval, random, high and low aspect ratios, overlapping profile features, and the like.


The profile feature (e.g., about 10 nanometers to 500 micrometers) can include an upper, convexly curved surface. The curved surface may extend symmetrically either side of an uppermost point.


The profile feature can include protrusions from the textured surface. The profile feature can include indents (hollow areas) formed in the textured surface. The profile feature can have a smooth, curved shape (e.g., a polygonal cross-section with curved corners).


The profile features (whether protrusions or depressions) can be approximately conical or frusto-conical (i.e. the projections or indents may have horizontally or diagonally flattened tops) or have an approximately part-spherical surface (e.g., a convex or concave surface respectively having a substantially even radius of curvature).


The profile features may have one or more sides or edges that extend in a direction that forms an angle to the first plane of the textured surface. The angle between the first plane and a side or edge of the profile feature is about 45 degrees or less, about 30 degrees or less, about 25 degrees or less, or about 20 degrees or less. The one or more sides or edges may extend in a linear or planar orientation, or may be curved so that the angle changes as a function of distance from the first plane. The profile features may have one or more sides that include step(s) and/or flat side(s). The profile feature can have one or more sides (or portions thereof) that can be orthogonal or perpendicular to the first plane of the textured surface, or extend at an angle of about 10 degrees to 89 degrees to the first plane (90 degrees being perpendicular or orthogonal to the first plane). The profile feature can have a side with a stepped configuration, where portions of the side can be parallel to the first plane of the textured surface or have an angle of about 1 degrees to 179 degrees (0 degrees being parallel to the first plane).


The textured surface can have profile features with varying shapes (e.g., the profile features can vary in shape, height, width and length among the profile features) or profile features with substantially uniform shapes and/or dimensions. The structural color produced by the textured surface can be determined, at least in part, by the shape, dimensions, spacing, and the like, of the profile features.


The profile features can be shaped so as to result in a portion of the surface (e.g., about 25 to 50 percent or more) being about normal to the incoming light when the light is incident at the normal to the first plane of the textured surface. The profile features can be shaped so as to result in a portion of the surface (e.g., about 25 to 50 percent or more) being about normal to the incoming light when the light is incident at an angle of up to 45 degrees to the first plane of the textured surface.


The spatial orientation of the profile features on the textured surface is set to reduce distortion effects, e.g., caused by the interference of one profile feature with another in regard to the structural color of the surface. Since the shape, dimension, relative orientation of the profile features can vary considerably across the textured surface, the desired spacing and/or relative positioning for a particular area (e.g., in the micrometer range or about 1 to 10 square micrometers) having profile features can be appropriately determined. As discussed herein, the shape, dimension, relative orientation of the profile features affect the contours of the optical layer, so the dimensions (e.g., thickness), index of refraction, number of layers in the optical layer are considered when designing the textured side of the texture layer.


The profile features are located in nearly random positions relative to one another across a specific area of the textured surface (e.g., in the micrometer range or about 1 to 10 square micrometers to centimeter range or about 0.5 to 5 square centimeters, and all range increments therein), where the randomness does not defeat the purpose of producing the structural color. In other words, the randomness is consistent with the spacing, shape, dimension, and relative orientation of the profile features, the dimensions (e.g., thickness), index of refraction, and number of layers in the optical layer, and the like, with the goal to achieve the structural color.


The profile features are positioned in a set manner relative to one another across a specific area of the textured surface to achieve the purpose of producing the structural color. The relative positions of the profile features do not necessarily follow a pattern, but can follow a pattern consistent with the desired structural color. As mentioned above and herein, various parameters related to the profile features, flat areas, and optical layer can be used to position the profile features in a set manner relative to one another.


The textured surface can include micro and/or nanoscale profile features that can form gratings (e.g., a diffractive grating), photonic crystal structure, a selective mirror structure, crystal fiber structures, deformed matrix structures, spiraled coiled structures, surface grating structures, and combinations thereof. The textured surface can include micro and/or nanoscale profile features that form a grating having a periodic or non-periodic design structure to produce the desired structural color. The micro and/or nanoscale profile features can have a peak-valley pattern of profile features and/or flat areas to produce the desired structural color. The grading can be an Echelette grating.


The profile features and the flat areas of the textured surface in the multi-layer optical film can appear as topographical undulations in each layer of the optical layer. For example, referring to FIGS. 3A and 3B, a multi-layer optical film 200 includes a textured surface 220 having a plurality of profile features 222 and flat areas 224. As described herein, one or more of the profile features 222 can be projections from a surface of the textured surface 220 (as shown in FIG. 3A), and/or one or more of the profile features 222 can be depressions in a surface of the textured surface 220 (as shown in FIG. 3B). One or more optical layers 240 are disposed on the side or surface of the textured surface 220 having the profile features 222 and flat areas 224. In some embodiments, the resulting topography of the one or more optical layers 240 is not identical to the topography of the textured surface 220, but rather, the one or more optical layers 240 can have elevated or depressed regions 242 which are either elevated or depressed relative to the height of the planar regions 244 and which roughly correspond to the location of the profile features 222 of the textured surface 220. The one or more optical layers 240 also have planar regions 244 that roughly correspond to the location of the flat areas 224 of the textured surface 220. Due to the presence of the elevated or depressed regions 242 and the planar regions 244, the resultant overall topography of the optical layer 240 can be that of an undulating or wave-like surface. The dimension, shape, and spacing of the profile features along with the number of layers of the optical layer, the thickness of each of the layers, refractive index of each layer, and the type of material, can be used to produce a multi-layer optical film which results in a particular structural color.


Now having described the multi-layer optical film and the textured surface, additional details will be provided for the optionally present primer layer. The multi-layer optical film is used to produce the structural color, where the multi-layer optical film can include (e.g., as part of the multi-layer optical film) or use the primer layer to produce the structural color. As described herein, the multi-layer optical film can also include (e.g., as part of multi-layer optical film) the optional textured surface, such as a texture layer and/or a textured surface. The combination of the multi-layer optical film and the optional texture layer and the optional primer layer can form a structure having one of the following designs: texture layer/primer layer/multi-layer optical film or primer layer/texture layer/multi-layer optical film. The primer layer can have a thickness of about 3 nanometers to 200 micrometers, or about 1 to about 200 micrometers, or about 10 to about 100 micrometers, or about 10 to about 80 micrometers. The structure can include the combination of the primer layer, the multi-layer optical film, and (optionally) textured surface. Selection of variables associated with the primer layer, texture layer, and the multi-layer optical film, can be used to control and select the desired structural color.


The structure can include the primer layer, the textured surface (optionally), and the multi-layer optical film (e.g., optical element or layer), where the multi-layer optical film is disposed on the textured surface or the primer layer, depending upon the design. The combination of the primer layer, the textured surface, and the multi-layer optical film imparts structural color, to the bladder, where the structural color is different than the primer color, optionally with or without the application of pigments or dyes to the bladder. The multi-layer optical film can be disposed onto the primer layer and/or the textured surface. The primer layer can include the textured surface as described herein. For example, the primer layer can be formed in a way so that it has the textured surface.


The primer layer can include a paint layer (e.g., dyes, pigments, and a combination thereof), an ink layer, a reground layer, an at least partially degraded polymer layer, a metal layer, an oxide layer, or a combination thereof. The primer layer can have a light or dark color. The primer layer can have a dark color. For example the dark color can be selected from: black, shades of black, brown, dark shades of brown, dark shades of red, dark shades of orange, dark shades of yellow, dark shades of green, dark shades of cyan, dark shades of blue, dark shades of violet, grey, dark shades of gray, dark shades of magenta, dark shades of indigo, tones, tints, shades, or hues of any of these, and a combination thereof. The color can be defined using the L*a*b system, where the value of L* can be about 70 or less, about 60 or less, about 50 or less, about 40 or less, or about 30 or less and a* and b* coordinate values can vary across the positive and negative value scales.


The primer layer can be formed using digital printing, inkjet printing, offset printing, pad printing, screen printing, flexographic printing, heat transfer printing, physical vapor deposition including: chemical vapor deposition, pulsed laser deposition, evaporative deposition, sputtering deposition (radio frequency, direct current, reactive, non-reactive), plasma enhanced chemical vapor deposition, electron beam deposition, cathodic arc deposition, low pressure chemical vapor deposition and wet chemistry techniques such as layer by layer deposition, sol-gel deposition, or Langmuir-Blodgett. Alternatively or in addition, the primer layer can be applied by spray coating, dip coating, brushing, spin coating, doctor blade coating, and the like.


The primer layer can have a percent transmittance of about 40% or less, about 30% or less, about 20% or less, about 15% or less, about 10% or less, about 5% or less, or about 1% or less, where “less” can include about 0% (e.g., 0 to 0.01 or 0 to 0.1), about 1%, about 2.5%, or about 5%.


The paint layer can include a paint composition that, upon applying to the bladder, forms a thin layer. The thin layer can be a solid film having a dark color, such as those described above. The paint can include known paint compositions that can comprise one or more of the following components: one or more paint resin, one or more polymers, one or more dyes, and one or more pigments as well as water, film-forming solvents, drying agents, thickeners, surfactants, anti-skinning agents, plasticizers, mildewcides, mar-resistant agents, anti-flooding agents, and combinations thereof.


The primer layer can comprise a reground, and at least partially degraded, polymer layer. The reground, and at least partially degraded, polymer layer can have a dark color, such as those described above.


The primer layer can include a metal layer or the oxide layer. The metal layer or the oxide layer can have a dark color, such as those described above. The oxide layer can be a metal oxide, a doped metal oxide, or a combination thereof. The metal layer, the metal oxide or the doped metal oxide can include the following: the transition metals, the metalloids, the lanthanides, and the actinides, as well as nitrides, oxynitrides, sulfides, sulfates, selenides, tellurides and a combination of these. The metal oxide can include titanium oxide, aluminum oxide, silicon dioxide, tin dioxide, chromia, iron oxide, nickel oxide, silver oxide, cobalt oxide, zinc oxide, platinum oxide, palladium oxide, vanadium oxide, molybdenum oxide, lead oxide, and combinations thereof as well as doped versions of each. In some aspects, the primer layer can consist essentially of a metal oxide. In some aspects, the primer layer can consist essentially of titanium dioxide or silicon dioxide. In some aspects, the primer layer can consist essentially of titanium dioxide. The metal oxide can be doped with water, inert gasses (e.g., argon), reactive gasses (e.g., oxygen or nitrogen), metals, small molecules, and a combination thereof. In some aspects, the primer layer can consist essentially of a doped metal oxide or a doped metal oxynitride or both.


The primer layer can be a coating on the surface of the bladder. The coating can be chemically bonded (e.g., covalently bonded, ionically bonded, hydrogen bonded, and the like) to the surface of the bladder. The coating has been found to bond well to a surface made of a polymeric material. In an example, the surface of the bladder can be made of a polymeric material such as a polyurethane, including a thermoplastic polyurethane (TPU), as those described herein.


The coating can be a crosslinked coating that includes one or more colorants such as solid pigment particles or dye. The crosslinked coating can be a matrix of crosslinked polymers (e.g., a crosslinked polyester polyurethane polymer or copolymer). The colorants can be entrapped in the coating, including entrapped in the matrix of crosslinked polymers. The solid pigment particles or dye can be physically entrapped in the crosslinked polymer matrix, can be chemically bonded (e.g., covalently bonded, ionically bonded, hydrogen bonded, and the like, with the coating including the polymeric matrix or with the material forming the surface of the bladder to which the coating is applied), or a combination of physically bonded and chemically bonded with the coating or bladder. The crosslinked coating can have a thickness of about 0.01 micrometers to 1000 micrometers.


The coating can be a product (or also referred to as “crosslinked product”) of crosslinking a polymeric coating composition. The polymeric coating composition can include one or more colorants (e.g., solid pigment particles or dye) in a dispersion of polymers. The dispersion of polymers can include a water-borne dispersion of polymers such as a water-borne dispersion of polyurethane polymers, including polyester polyurethane copolymers). The water-borne dispersion of polymers can be crosslinked to entrap the colorants. The colorants can be physically entrapped in the crosslinked product, can be chemically bonded (e.g., covalently bonded, ionically bonded, hydrogen bonded, and the like, with the crosslinked copolymer matrix), or can be both physically bonded and chemically bonded with the crosslinked product. The product can be formed by crosslinking the polymeric coating composition. The product can have a thickness of about 0.01 micrometer to 1000 micrometers.


The coating can include colorants such a pigment (e.g., a solid pigment particle) or a dye. The solid pigment particles can include inorganic pigments such as metal and metal oxides such as homogeneous inorganic pigments, core-shell pigments and the like, as well as carbon pigments (e.g., carbon black), clay earth pigments, and ultramarine pigments. The solid pigment particles can be biological or organic pigments. The solid pigment particles can be of a type known in the art as an extender pigment, which include, but are not limited to, calcium carbonate, calcium silicate, mica, clay, silica, barium sulfate and the like. The amount of the solid pigment particles sufficient to achieve the desired color intensity, shade, and opacity, can be in amounts up to about 5 percent to 25 percent or more by weight of the coating. The pigments can include those sold by KP Pigments such as pearl pigments, color shift pigments (e.g., CALYPSO, JEDI, VERO, BLACKHOLE, LYNX, ROSE GOLD, and the like), hypershift pigments, interference pigments and the like.


The colorant can be a dye such as an anionic dye, a cationic dye, a direct dye, a metal complex dye, a basic dye, a disperse dye, a solvent dye, a polymeric dye, a polymeric dye colorant, or a nonionic dye, where the coating can include one or more dyes and/or types of dyes. The dye can be a water-miscible dye. The dye can be a solubilized dye. The anionic dye can be an acid dye. The dye can be applied separately from the coating (e.g., either before or after the coating is applied and/or cured).


Acid dyes are water-soluble anionic dyes. Acid dyes are available in a wide variety, from dull tones to brilliant shades. Chemically, acid dyes include azo, anthraquinone and triarylmethane compounds. The “Color Index” (C.I.), published jointly by the Society of Dyers and Colourists (UK) and by the American Association of Textile Chemists and Colorists (USA), is the most extensive compendium of dyes and pigments for large scale coloration purposes, including 12000 products under 2000 C.I. generic names. In the C.I. each compound is presented with two numbers referring to the coloristic and chemical classification. The “generic name” refers to the field of application and/or method of coloration, while the other number is the “constitution number.” Examples of acid dyes include Acid Yellow 1, 17, 23, 25, 34, 42, 44, 49, 61, 79, 99, 110, 116, 127, 151, 158:1, 159, 166, 169, 194, 199, 204, 220, 232, 241, 246, and 250; Acid Red, 1, 14, 17, 18, 42, 57, 88, 97, 118, 119, 151, 183, 184, 186, 194, 195, 198, 211, 225, 226, 249, 251, 257, 260, 266, 278, 283, 315, 336, 337, 357, 359, 361, 362, 374, 405, 407, 414, 418, 419, and 447; Acid Violet 3, 5, 7, 17, 54, 90, and 92; Acid Brown 4, 14, 15, 45, 50, 58, 75, 97, 98, 147, 160:1, 161, 165, 191, 235, 239, 248, 282, 283, 289, 298, 322, 343, 349, 354, 355, 357, 365, 384, 392, 402, 414, 420, 422, 425, 432, and 434; Acid Orange 3, 7, 10, 19, 33, 56, 60, 61, 67, 74, 80, 86, 94, 139, 142, 144, 154, and 162; Acid Blue 1, 7, 9, 15, 92, 133, 158, 185, 193, 277, 277:1, 314, 324, 335, and 342; Acid Green 1, 12, 68:1, 73, 80, 104, 114, and 119; Acid Black 1, 26, 52, 58, 60, 64, 65, 71, 82, 84, 107, 164, 172, 187, 194, 207, 210, 234, 235, and combinations of these. The acid dyes may be used singly or in any combination in the ink composition.


Acid dyes and nonionic disperse dyes are commercially available from many sources, including Dystar L.P., Charlotte, N.C. under the tradename TELON, Huntsman Corporation, Woodlands, Tex., USA under the tradename ERIONYL and TECTILON, BASF SE, Ludwigshafen, Germany under the tradename BASACID, and Bezema AG, Montlingen, Switzerland under the tradename Bemacid.


The colorant can include the dye and a quaternary (tetraalkyl) ammonium salt, in particular when the dye is acidic dye. The quaternary (tetraalkyl) ammonium salt can react with the dye (e.g., acid dye) to form a complexed dye that can be used in the coating. The “alkyl” group can include C1 to C10 alkyl groups. The quaternary (tetraalkyl) ammonium salt can be selected from soluble tetrabutylammonium compounds and tetrahexylammonium compounds. The counterion of the quaternary ammonium salt should be selected so that the quaternary ammonium salt forms a stable solution with the dye (e.g., anionic dye). The quaternary ammonium compound may be, for example, a halide (such as chloride, bromide or iodide), hydroxide, sulfate, sulfite, carbonate, perchlorate, chlorate, bromate, iodate, nitrate, nitrite, phosphate, phosphite, hexfluorophosphite, borate, tetrafluoroborate, cyanide, isocyanide, azide, thiosulfate, thiocyanate, or carbon/late (such as acetate or oxalate). The tetraalkylammonium compound can be or include a tetrabutylammonium halide or tetrahexylammonium halide, particularly a tetrabutylammonium bromide or chloride or a tetrahexylammonium bromide or chloride. The coating (e.g., coating, polymeric coating composition (prior to curing) can include about 1 to 15 weight percent of the quaternary ammonium salt. The molar ratio of the acid dye to the quaternary ammonium compound can range from about 3:1 to 1:3 or about 1.5:1 to 1:1.5.


The coating (e.g., coating, polymeric coating composition (prior to curing), monomers and/or polymers of the matrix of crosslinked polymers, or precursors of the coating) can include a cross-linker, which functions to crosslink the polymeric components of the coating. The cross-linker can be a water-borne cross-linker. The cross-linker can include one or more of the following: a polycarboxylic acid crosslinking agent, an aldehyde crosslinking agent, a polyisocyanate crosslinking agent, or a combination thereof. The polycarboxylic acid crosslinking agent can be a polycarboxylic acid having from 2 to 9 carbon atoms. For example, the cross-linker can include a polyacrylic acid, a polymaleic acid, a copolymer of acid, a copolymer of maleic acid, fumaric acid, or 1, 2, 3, 4-butanetetracarboxylic acid. The concentration of the cross-linker can be about 0.01 to 5 weight percent or 1 to 3 weight percent of the coating.


The coating (e.g., coating, polymeric coating composition (prior to curing), monomers and/or polymers of the matrix of crosslinked polymers, or precursors of the coating) can include a solvent. The solvent can be an organic solvent. The organic solvent can be a water-miscible organic solvent. The coating may not include water, or may be essentially free of water. For example, the solvent can be or includes acetone, ethanol, 2-propanol, ethyl acetate, isopropyl acetate, methanol, methyl ethyl ketone, 1-butanol, t-butanol, or any mixture thereof.


Additional details are provided regarding the polymeric materials referenced herein for example, the polymers described in reference to the bladder, components of the bladder, article, structure, layer, film, foam, primer layer, coating, and the like. The polymer can be a thermoset polymer or a thermoplastic polymer. The polymer can be an elastomeric polymer, including an elastomeric thermoset polymer or an elastomeric thermoplastic polymer. The polymer can be selected from: polyurethanes (including elastomeric polyurethanes, thermoplastic polyurethanes (TPUs), and elastomeric TPUs), polyesters, polyethers, polyamides, vinyl polymers (e.g., copolymers of vinyl alcohol, vinyl esters, ethylene, acrylates, methacrylates, styrene, and so on), polyacrylonitriles, polyphenylene ethers, polycarbonates, polyureas, polystyrenes, co-polymers thereof (including polyester-polyurethanes, polyether-polyurethanes, polycarbonate-polyurethanes, polyether block polyamides (PEBAs), and styrene block copolymers), and any combination thereof, as described herein. The polymer can include one or more polymers selected from the group consisting of polyesters, polyethers, polyamides, polyurethanes, polyolefins copolymers of each, and combinations thereof.


The term “polymer” refers to a chemical compound formed of a plurality of repeating structural units referred to as monomers. Polymers often are formed by a polymerization reaction in which the plurality of structural units become covalently bonded together. When the monomer units forming the polymer all have the same chemical structure, the polymer is a homopolymer. When the polymer includes two or more monomer units having different chemical structures, the polymer is a copolymer. One example of a type of copolymer is a terpolymer, which includes three different types of monomer units. The co-polymer can include two or more different monomers randomly distributed in the polymer (e.g., a random co-polymer). Alternatively, one or more blocks containing a plurality of a first type of monomer can be bonded to one or more blocks containing a plurality of a second type of monomer, forming a block copolymer. A single monomer unit can include one or more different chemical functional groups.


Polymers having repeating units which include two or more types of chemical functional groups can be referred to as having two or more segments. For example, a polymer having repeating units of the same chemical structure can be referred to as having repeating segments. Segments are commonly described as being relatively harder or softer based on their chemical structures, and it is common for polymers to include relatively harder segments and relatively softer segments bonded to each other in a single monomeric unit or in different monomeric units. When the polymer includes repeating segments, physical interactions or chemical bonds can be present within the segments or between the segments or both within and between the segments. Examples of segments often referred to as hard segments include segments including a urethane linkage, which can be formed from reacting an isocyanate with a polyol to form a polyurethane. Examples of segments often referred to as soft segments include segments including an alkoxy functional group, such as segments including ether or ester functional groups, and polyester segments. Segments can be referred to based on the name of the functional group present in the segment (e.g., a polyether segment, a polyester segment), as well as based on the name of the chemical structure which was reacted in order to form the segment (e.g., a polyol-derived segment, an isocyanate-derived segment). When referring to segments of a particular functional group or of a particular chemical structure from which the segment was derived, it is understood that the polymer can contain up to 10 mole percent of segments of other functional groups or derived from other chemical structures. For example, as used herein, a polyether segment is understood to include up to 10 mole percent of non-polyether segments.


As previously described, the polymer can be a thermoplastic polymer. In general, a thermoplastic polymer softens or melts when heated and returns to a solid state when cooled. The thermoplastic polymer transitions from a solid state to a softened state when its temperature is increased to a temperature at or above its softening temperature, and a liquid state when its temperature is increased to a temperature at or above its melting temperature. When sufficiently cooled, the thermoplastic polymer transitions from the softened or liquid state to the solid state. As such, the thermoplastic polymer may be softened or melted, molded, cooled, re-softened or re-melted, re-molded, and cooled again through multiple cycles. For amorphous thermoplastic polymers, the solid state is understood to be the “rubbery” state above the glass transition temperature of the polymer. The thermoplastic polymer can have a melting temperature from about 90 degrees C. to about 190 degrees C. when determined in accordance with ASTM D3418-97 as described herein below, and includes all subranges therein in increments of 1 degree. The thermoplastic polymer can have a melting temperature from about 93 degrees C. to about 99 degrees C. when determined in accordance with ASTM D3418-97 as described herein below. The thermoplastic polymer can have a melting temperature from about 112 degrees C. to about 118 degrees C. when determined in accordance with ASTM D3418-97 as described herein below.


The glass transition temperature is the temperature at which an amorphous polymer transitions from a relatively brittle “glassy” state to a relatively more flexible “rubbery” state. The thermoplastic polymer can have a glass transition temperature from about −20 degrees C. to about 30 degrees C. when determined in accordance with ASTM D3418-97 as described herein below. The thermoplastic polymer can have a glass transition temperature (from about −13 degree C. to about −7 degrees C. when determined in accordance with ASTM D3418-97 as described herein below. The thermoplastic polymer can have a glass transition temperature from about 17 degrees C. to about 23 degrees C. when determined in accordance with ASTM D3418-97 as described herein below.


The thermoplastic polymer can have a melt flow index from about 10 to about 30 cubic centimeters per 10 minutes (cm3/10 min) when tested in accordance with ASTM D1238-13 as described herein below at 160 degrees C. using a weight of 2.16 kilograms (kg). The thermoplastic polymer can have a melt flow index from about 22 cm3/10 min to about 28 cm3/10 min when tested in accordance with ASTM D1238-13 as described herein below at 160 degrees C. using a weight of 2.16 kg.


The thermoplastic polymer can have a cold Ross flex test result of about 120,000 to about 180,000 cycles without cracking or whitening when tested on a thermoformed plaque of the thermoplastic polymer in accordance with the cold Ross flex test as described herein below. The thermoplastic polymer can have a cold Ross flex test result of about 140,000 to about 160,000 cycles without cracking or whitening when tested on a thermoformed plaque of the thermoplastic polymer in accordance with the cold Ross flex test as described herein below.


The thermoplastic polymer can have a modulus from about 5 megaPascals (MPa) to about 100 MPa when determined on a thermoformed plaque in accordance with ASTM D412-98 Standard Test Methods for Vulcanized Rubber and Thermoplastic Rubbers and Thermoplastic Elastomers-Tension with modifications described herein below. The thermoplastic polymer can have a modulus from about 20 MPa to about 80 MPa when determined on a thermoformed plaque in accordance with ASTM D412-98 Standard Test Methods for Vulcanized Rubber and Thermoplastic Rubbers and Thermoplastic Elastomers-Tension with modifications described herein below.


The polymer can be a thermoset polymer. As used herein, a “thermoset polymer” is understood to refer to a polymer which cannot be heated and melted, as its melting temperature is at or above its decomposition temperature. A “thermoset material” refers to a material which comprises at least one thermoset polymer. The thermoset polymer and/or thermoset material can be prepared from a precursor (e.g., an uncured or partially cured polymer or material) using thermal energy and/or actinic radiation (e.g., ultraviolet radiation, visible radiation, high energy radiation, infrared radiation) to form a partially cured or fully cured polymer or material which no longer remains fully thermoplastic. In some cases, the cured or partially cured polymer or material may remain thermoelastic properties, in that it is possible to partially soften and mold the polymer or material at elevated temperatures and/or pressures, but it is not possible to melt the polymer or material. The curing can be promoted, for example, with the use of high pressure and/or a catalyst. In many examples, the curing process is irreversible since it results in cross-linking and/or polymerization reactions of the precursors. The uncured or partially cured polymers or materials can be malleable or liquid prior to curing. In some cases, the uncured or partially cured polymers or materials can be molded into their final shape, or used as adhesives. Once hardened, a thermoset polymer or material cannot be re-melted in order to be reshaped. The textured surface can be formed by partially or fully curing an uncured precursor material to lock in the textured surface of the textured structure.


Polyurethane


The polymer can be a polyurethane, such as a thermoplastic polyurethane (also referred to as “TPU”). Alternatively, the polymer can be a thermoset polyurethane. Additionally, polyurethane can be an elastomeric polyurethane, including an elastomeric TPU or an elastomeric thermoset polyurethane. The elastomeric polyurethane can include hard and soft segments. The hard segments can comprise or consist of urethane segments (e.g., isocyanate-derived segments). The soft segments can comprise or consist of alkoxy segments (e.g., polyol-derived segments including polyether segments, or polyester segments, or a combination of polyether segments and polyester segments). The polyurethane can comprise or consist essentially of an elastomeric polyurethane having repeating hard segments and repeating soft segments.


One or more of the polyurethanes can be produced by polymerizing one or more isocyanates with one or more polyols to produce polymer chains having carbamate linkages (—N(CO)O—) as illustrated below in Formula 1, where the isocyanate(s) each preferably include two or more isocyanate (—NCO) groups per molecule, such as 2, 3, or 4 isocyanate groups per molecule (although, mono-functional isocyanates can also be optionally included, e.g., as chain terminating units).




embedded image


Each R1 group and R2 group independently is an aliphatic or aromatic group. Optionally, each R2 can be a relatively hydrophilic group, including a group having one or more hydroxyl groups.


Additionally, the isocyanates can also be chain extended with one or more chain extenders to bridge two or more isocyanates, increasing the length of the hard segment. This can produce polyurethane polymer chains as illustrated below in Formula 2, where R3 includes the chain extender. As with each R1 and R3, each R3 independently is an aliphatic or aromatic functional group.




embedded image


Each R1 group in Formulas 1 and 2 can independently include a linear or branched group having from 3 to 30 carbon atoms, based on the particular isocyanate(s) used, and can be aliphatic, aromatic, or include a combination of aliphatic portions(s) and aromatic portion(s). The term “aliphatic” refers to a saturated or unsaturated organic molecule or portion of a molecule that does not include a cyclically conjugated ring system having delocalized pi electrons. In comparison, the term “aromatic” refers to an organic molecule or portion of a molecule having a cyclically conjugated ring system with delocalized pi electrons, which exhibits greater stability than a hypothetical ring system having localized pi electrons.


Each R1 group can be present in an amount of about 5 percent to about 85 percent by weight, from about 5 percent to about 70 percent by weight, or from about 10 percent to about 50 percent by weight, based on the total weight of the reactant compounds or monomers which form the polymer.


In aliphatic embodiments (from aliphatic isocyanate(s)), each R1 group can include a linear aliphatic group, a branched aliphatic group, a cycloaliphatic group, or combinations thereof. For instance, each R1 group can include a linear or branched alkylene group having from 3 to 20 carbon atoms (e.g., an alkylene having from 4 to 15 carbon atoms, or an alkylene having from 6 to 10 carbon atoms), one or more cycloalkylene groups having from 3 to 8 carbon atoms (e.g., cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, or cyclooctyl), and combinations thereof. The term “alkene” or “alkylene” as used herein refers to a bivalent hydrocarbon. When used in association with the term Cn it means the alkene or alkylene group has “n” carbon atoms. For example, C1-6alkylene refers to an alkylene group having, e.g., 1, 2, 3, 4, 5, or 6 carbon atoms.


Examples of suitable aliphatic diisocyanates for producing the polyurethane polymer chains include hexamethylene diisocyanate (HDI), isophorone diisocyanate (IPDI), butylenediisocyanate (BDI), bisisocyanatocyclohexylmethane (HMDI), 2,2,4-trimethylhexamethylene diisocyanate (TMDI), bisisocyanatomethylcyclohexane, bisisocyanatomethyltricyclodecane, norbornane diisocyanate (NDI), cyclohexane diisocyanate (CHDI), 4,4′-dicyclohexylmethane diisocyanate (H12MDI), diisocyanatododecane, lysine diisocyanate, and combinations thereof.


The isocyanate-derived segments can include segments derived from aliphatic diisocyanate. A majority of the isocyanate-derived segments can comprise segments derived from aliphatic diisocyanates. At least 90% of the isocyanate-derived segments are derived from aliphatic diisocyanates. The isocyanate-derived segments can consist essentially of segments derived from aliphatic diisocyanates. The aliphatic diisocyanate-derived segments can be derived substantially (e.g., about 50 percent or more, about 60 percent or more, about 70 percent or more, about 80 percent or more, about 90 percent or more) from linear aliphatic diisocyanates. At least 80% of the aliphatic diisocyanate-derived segments can be derived from aliphatic diisocyanates that are free of side chains. The segments derived from aliphatic diisocyanates can include linear aliphatic diisocyanates having from 2 to 10 carbon atoms.


When the isocyanate-derived segments are derived from aromatic isocyanate(s)), each R1 group can include one or more aromatic groups, such as phenyl, naphthyl, tetrahydronaphthyl, phenanthrenyl, biphenylenyl, indanyl, indenyl, anthracenyl, and fluorenyl. Unless otherwise indicated, an aromatic group can be an unsubstituted aromatic group or a substituted aromatic group, and can also include heteroaromatic groups. “Heteroaromatic” refers to monocyclic or polycyclic (e.g., fused bicyclic and fused tricyclic) aromatic ring systems, where one to four ring atoms are selected from oxygen, nitrogen, or sulfur, and the remaining ring atoms are carbon, and where the ring system is joined to the remainder of the molecule by any of the ring atoms. Examples of suitable heteroaryl groups include pyridyl, pyrazinyl, pyrimidinyl, pyrrolyl, pyrazolyl, imidazolyl, thiazolyl, tetrazolyl, oxazolyl, isooxazolyl, thiadiazolyl, oxadiazolyl, furanyl, quinolinyl, isoquinolinyl, benzoxazolyl, benzimidazolyl, and benzothiazolyl groups.


Examples of suitable aromatic diisocyanates for producing the polyurethane polymer chains include toluene diisocyanate (TDI), TDI adducts with trimethyloylpropane (TMP), methylene diphenyl diisocyanate (MDI), xylene diisocyanate (XDI), tetramethylxylylene diisocyanate (TMXDI), hydrogenated xylene diisocyanate (HXDI), naphthalene 1,5-diisocyanate (NDI), 1,5-tetrahydronaphthalene diisocyanate, para-phenylene diisocyanate (PPDI), 3,3′-dimethyldiphenyl-4, 4′-diisocyanate (DDDI), 4,4′-dibenzyl diisocyanate (DBDI), 4-chloro-1,3-phenylene diisocyanate, and combinations thereof. The polymer chains can be substantially free of aromatic groups.


The polyurethane polymer chains can be produced from diisocyanates including HMDI, TDI, MDI, H12 aliphatics, and combinations thereof. For example, the polyurethane can comprise one or more polyurethane polymer chains produced from diisocyanates including HMDI, TDI, MDI, H12 aliphatics, and combinations thereof.


Polyurethane chains which are at least partially crosslinked or which can be crosslinked, can be used in accordance with the present disclosure. It is possible to produce crosslinked or crosslinkable polyurethane chains by reacting multi-functional isocyanates to form the polyurethane. Examples of suitable triisocyanates for producing the polyurethane chains include TDI, HDI, and IPDI adducts with trimethyloylpropane (TMP), uretdiones (i.e., dimerized isocyanates), polymeric MDI, and combinations thereof.


The R3 group in Formula 2 can include a linear or branched group having from 2 to 10 carbon atoms, based on the particular chain extender polyol used, and can be, for example, aliphatic, aromatic, or an ether or polyether. Examples of suitable chain extender polyols for producing the polyurethane include ethylene glycol, lower oligomers of ethylene glycol (e.g., diethylene glycol, triethylene glycol, and tetraethylene glycol), 1,2-propylene glycol, 1,3-propylene glycol, lower oligomers of propylene glycol (e.g., dipropylene glycol, tripropylene glycol, and tetrapropylene glycol), 1,4-butylene glycol, 2,3-butylene glycol, 1,6-hexanediol, 1,8-octanediol, neopentyl glycol, 1,4-cyclohexanedimethanol, 2-ethyl-1,6-hexanediol, 1-methyl-1,3-propanediol, 2-methyl-1,3-propanediol, dihydroxyalkylated aromatic compounds (e.g., bis(2-hydroxyethyl) ethers of hydroquinone and resorcinol, xylene-a,a-diols, bis(2-hydroxyethyl) ethers of xylene-a,a-diols, and combinations thereof.


The R2 group in Formula 1 and 2 can include a polyether group, a polyester group, a polycarbonate group, an aliphatic group, or an aromatic group. Each R2 group can be present in an amount of about 5 percent to about 85 percent by weight, from about 5 percent to about 70 percent by weight, or from about 10 percent to about 50 percent by weight, based on the total weight of the reactant monomers.


At least one R2 group of the polyurethane includes a polyether segment (i.e., a segment having one or more ether groups). Suitable polyether groups include, but are not limited to, polyethylene oxide (PEO), polypropylene oxide (PPO), polytetrahydrofuran (PTHF), polytetramethylene oxide (PTMO), and combinations thereof. The term “alkyl” as used herein refers to straight chained and branched saturated hydrocarbon groups containing one to thirty carbon atoms, for example, one to twenty carbon atoms, or one to ten carbon atoms. When used in association with the term Cn it means the alkyl group has “n” carbon atoms. For example, C4 alkyl refers to an alkyl group that has 4 carbon atoms. C1-7 alkyl refers to an alkyl group having a number of carbon atoms encompassing the entire range (i.e., 1 to 7 carbon atoms), as well as all subgroups (e.g., 1-6, 2-7, 1-5, 3-6, 1, 2, 3, 4, 5, 6, and 7 carbon atoms). Non-limiting examples of alkyl groups include, methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl (2-methylpropyl), t-butyl (1,1-dimethylethyl), 3,3-dimethylpentyl, and 2-ethylhexyl. Unless otherwise indicated, an alkyl group can be an unsubstituted alkyl group or a substituted alkyl group.


In some examples of the polyurethane, the at least one R2 group includes a polyester group. The polyester group can be derived from the polyesterification of one or more dihydric alcohols (e.g., ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol, 2-methylpentanediol, 1,5-diethylene glycol,1,5-pentanediol, 1,5-hexanediol, 1,2-dodecanediol, cyclohexanedimethanol, and combinations thereof) with one or more dicarboxylic acids (e.g., adipic acid, succinic acid, sebacic acid, suberic acid, methyladipic acid, glutaric acid, pimelic acid, azelaic acid, thiodipropionic acid and citraconic acid and combinations thereof). The polyester group also can be derived from polycarbonate prepolymers, such as poly(hexamethylene carbonate) glycol, poly(propylene carbonate) glycol, poly(tetramethylene carbonate)glycol, and poly(nonanemethylene carbonate) glycol. Suitable polyesters can include, for example, polyethylene adipate (PEA), poly(1,4-butylene adipate), poly(tetramethylene adipate), poly(hexamethylene adipate), polycaprolactone, polyhexamethylene carbonate, poly(propylene carbonate), poly(tetramethylene carbonate), poly(nonanemethylene carbonate), and combinations thereof.


At least one R2 group can include a polycarbonate group. The polycarbonate group can be derived from the reaction of one or more dihydric alcohols (e.g., ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol, 2-methylpentanediol 1,5-diethylene glycol, 1,5-pentanediol, 1,5-hexanediol, 1,2-dodecanediol, cyclohexanedimethanol, and combinations thereof) with ethylene carbonate.


The aliphatic group can be linear and can include, for example, an alkylene chain having from 1 to 20 carbon atoms or an alkenylene chain having from 1 to 20 carbon atoms (e.g., methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, decylene, undecylene, dodecylene, tridecylene, ethenylene, propenylene, butenylene, pentenylene, hexenylene, heptenylene, octenylene, nonenylene, decenylene, undecenylene, dodecenylene, tridecenylene). The term “alkene” or “alkylene” refers to a bivalent hydrocarbon. The term “alkenylene” refers to a bivalent hydrocarbon molecule or portion of a molecule having at least one double bond.


The aliphatic and aromatic groups can be substituted with one or more pendant relatively hydrophilic and/or charged groups. The pendant hydrophilic group can include one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) hydroxyl groups. The pendant hydrophilic group includes one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) amino groups. In some cases, the pendant hydrophilic group includes one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) carboxylate groups. For example, the aliphatic group can include one or more polyacrylic acid group. In some cases, the pendant hydrophilic group includes one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) sulfonate groups. In some cases, the pendant hydrophilic group includes one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) phosphate groups. In some examples, the pendant hydrophilic group includes one or more ammonium groups (e.g., tertiary and/or quaternary ammonium). In other examples, the pendant hydrophilic group includes one or more zwitterionic groups (e.g., a betaine, such as poly(carboxybetaine (pCB) and ammonium phosphonate groups such as a phosphatidylcholine group).


The R2 group can include charged groups that are capable of binding to a counterion to ionically crosslink the polymer and form ionomers. For example, R2 is an aliphatic or aromatic group having pendant amino, carboxylate, sulfonate, phosphate, ammonium, or zwitterionic groups, or combinations thereof.


When a pendant hydrophilic group is present, the pendant hydrophilic group can be at least one polyether group, such as two polyether groups. In other cases, the pendant hydrophilic group is at least one polyester. The pendant hydrophilic group can be a polylactone group (e.g., polyvinylpyrrolidone). Each carbon atom of the pendant hydrophilic group can optionally be substituted with, e.g., an alkyl group having from 1 to 6 carbon atoms. The aliphatic and aromatic groups can be graft polymeric groups, wherein the pendant groups are homopolymeric groups (e.g., polyether groups, polyester groups, polyvinylpyrrolidone groups).


The pendant hydrophilic group can be a polyether group (e.g., a polyethylene oxide (PEO) group, a polyethylene glycol (PEG) group), a polyvinylpyrrolidone group, a polyacrylic acid group, or combinations thereof.


The pendant hydrophilic group can be bonded to the aliphatic group or aromatic group through a linker. The linker can be any bifunctional small molecule (e.g., one having from 1 to 20 carbon atoms) capable of linking the pendant hydrophilic group to the aliphatic or aromatic group. For example, the linker can include a diisocyanate group, as previously described herein, which when linked to the pendant hydrophilic group and to the aliphatic or aromatic group forms a carbamate bond. The linker can be 4,4′-diphenylmethane diisocyanate (MDI), as shown below.




embedded image


The pendant hydrophilic group can be a polyethylene oxide group and the linking group can be MDI, as shown below.




embedded image


The pendant hydrophilic group can be functionalized to enable it to bond to the aliphatic or aromatic group, optionally through the linker. For example, when the pendant hydrophilic group includes an alkene group, which can undergo a Michael addition with a sulfhydryl-containing bifunctional molecule (i.e., a molecule having a second reactive group, such as a hydroxyl group or amino group), resulting in a hydrophilic group that can react with the polymer backbone, optionally through the linker, using the second reactive group. For example, when the pendant hydrophilic group is a polyvinylpyrrolidone group, it can react with the sulfhydryl group on mercaptoethanol to result in hydroxyl-functionalized polyvinylpyrrolidone, as shown below.




embedded image


At least one R2 group in the polyurethane can include a polytetramethylene oxide group. At least one R2 group of the polyurethane can include an aliphatic polyol group functionalized with a polyethylene oxide group or polyvinylpyrrolidone group, such as the polyols described in E.P. Patent No. 2 462 908, which is hereby incorporated by reference. For example, the R2 group can be derived from the reaction product of a polyol (e.g., pentaerythritol or 2,2,3-trihydroxypropanol) and either MDI-derivatized methoxypolyethylene glycol (to obtain compounds as shown in Formulas 6 or 7) or with MDI-derivatized polyvinylpyrrolidone (to obtain compounds as shown in Formulas 8 or 9) that had been previously been reacted with mercaptoethanol, as shown below.




embedded image


At least one R2 of the polyurethane can be a polysiloxane, in these cases, the R2 group can be derived from a silicone monomer of Formula 10, such as a silicone monomer disclosed in U.S. Pat. No. 5,969,076, which is hereby incorporated by reference:




embedded image


wherein: a is 1 to 10 or larger (e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10); each R4 independently is hydrogen, an alkyl group having from 1 to 18 carbon atoms, an alkenyl group having from 2 to 18 carbon atoms, aryl, or polyether; and each R5 independently is an alkylene group having from 1 to 10 carbon atoms, polyether, or polyurethane.


Each R4 group can independently be a H, an alkyl group having from 1 to 10 carbon atoms, an alkenyl group having from 2 to 10 carbon atoms, an aryl group having from 1 to 6 carbon atoms, polyethylene, polypropylene, or polybutylene group. Each R4 group can independently be selected from the group consisting of methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, s-butyl, t-butyl, ethenyl, propenyl, phenyl, and polyethylene groups.


Each R5 group can independently include an alkylene group having from 1 to 10 carbon atoms (e.g., a methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, or decylene group). Each R5 group can be a polyether group (e.g., a polyethylene, polypropylene, or polybutylene group). Each R5 group can be a polyurethane group.


Optionally, the polyurethane can include an at least partially crosslinked polymeric network that includes polymer chains that are derivatives of polyurethane. The level of crosslinking can be such that the polyurethane retains thermoplastic properties (i.e., the crosslinked thermoplastic polyurethane can be melted and re-solidified under the processing conditions described herein). The crosslinked polyurethane can be a thermoset polymer. This crosslinked polymeric network can be produced by polymerizing one or more isocyanates with one or more polyamino compounds, polysulfhydryl compounds, or combinations thereof, as shown in Formulas 11 and 12, below:




embedded image



wherein the variables are as described above. Additionally, the isocyanates can also be chain extended with one or more polyamino or polythiol chain extenders to bridge two or more isocyanates, such as previously described for the polyurethanes of Formula 2.


The polyurethane chain can be physically crosslinked to another polyurethane chain through e.g., nonpolar or polar interactions between the urethane or carbamate groups of the polymers (the hard segments). The R1 group in Formula 1, and the R1 and R3 groups in Formula 2, form the portion of the polymer often referred to as the “hard segment”, and the R2 group forms the portion of the polymer often referred to as the “soft segment”. The soft segment is covalently bonded to the hard segment. The polyurethane having physically crosslinked hard and soft segments can be a hydrophilic polyurethane (i.e., a polyurethane, including a thermoplastic polyurethane, including hydrophilic groups as disclosed herein).


The polyurethane can be a thermoplastic polyurethane composed of MDI, PTMO, and 1,4-butylene glycol, as described in U.S. Pat. No. 4,523,005. Commercially available polyurethanes suitable for the present use include, but are not limited to those under the tradename “SANCURE” (e.g., the “SANCURE” series of polymer such as “SANCURE” 20025F) or “TECOPHILIC” (e.g., TG-500, TG-2000, SP-80A-150, SP-93A-100, SP-60D-60) (Lubrizol, Countryside, Ill., USA), “PELLETHANE” 2355-85ATP and 2355-95AE (Dow Chemical Company of Midland, Mich., USA.), “ESTANE” (e.g., ALR G 500, or 58213; Lubrizol, Countryside, Ill., USA).


One or more of the polyurethanes (e.g., those used in the primer as the coating (e.g., water-dispersible polyurethane)) can be produced by polymerizing one or more isocyanates with one or more polyols to produce copolymer chains having carbamate linkages (—N(C═O)O—) and one or more water-dispersible enhancing moieties, where the polymer chain includes one or more water-dispersible enhancing moieties (e.g., a monomer in polymer chain). The water-dispersible polyurethane can also be referred to as “a water-borne polyurethane polymer dispersion.” The water-dispersible enhancing moiety can be added to the chain of Formula 1 or 2 (e.g., within the chain and/or onto the chain as a side chain). Inclusion of the water-dispersible enhancing moiety enables the formation of a water-borne polyurethane dispersion. The term “water-borne” herein means the continuous phase of the dispersion or formulation of about 50 weight percent to 100 weight percent water, about 60 weight percent to 100 weight percent water, about 70 weight percent to 100 weight percent water, or about 100 weight percent water. The term “water-borne dispersion” refers to a dispersion of a component (e.g., polymer, cross-linker, and the like) in water without co-solvents. The co-solvent can be used in the water-borne dispersion and the co-solvent can be an organic solvent. Additional detail regarding the polymers, polyurethanes, isocyantes and the polyols are provided below.


The polyurethane (e.g., a water-borne polyurethane polymer dispersion) can include one or more water-dispersible enhancing moieties. The water-dispersible enhancing moiety can have at least one hydrophilic (e.g., poly(ethylene oxide)), ionic or potentially ionic group to assist dispersion of the polyurethane, thereby enhancing the stability of the dispersions. A water-dispersible polyurethane can be formed by incorporating a moiety bearing at least one hydrophilic group or a group that can be made hydrophilic (e.g., by chemical modifications such as neutralization) into the polymer chain. For example, these compounds can be nonionic, anionic, cationic or zwitterionic or the combination thereof. In one example, anionic groups such as carboxylic acid groups can be incorporated into the chain in an inactive form and subsequently activated by a salt-forming compound, such as a tertiary amine. Other water-dispersible enhancing moieties can also be reacted into the backbone through urethane linkages or urea linkages, including lateral or terminal hydrophilic ethylene oxide or ureido units.


The water-dispersible enhancing moiety can be a one that includes carboxyl groups. Water-dispersible enhancing moiety that include a carboxyl group can be formed from hydroxy-carboxylic acids having the general formula (HO)xQ(COOH)y, where Q can be a straight or branched bivalent hydrocarbon radical containing 1 to 12 carbon atoms, and x and y can each independently be 1 to 3. Illustrative examples include dimethylolpropanoic acid (DMPA), dimethylol butanoic acid (DMBA), citric acid, tartaric acid, glycolic acid, lactic acid, malic acid, dihydroxymalic acid, dihydroxytartaric acid, and the like, and mixtures thereof.


The water-dispersible enhancing moiety can include reactive polymeric polyol components that contain pendant anionic groups that can be polymerized into the backbone to impart water dispersible characteristics to the polyurethane. Anionic functional polymeric polyols can include anionic polyester polyols, anionic polyether polyols, and anionic polycarbonate polyols, where additional detail is provided in U.S. Pat. No. 5,334,690.


The water-dispersible enhancing moiety can include a side chain hydrophilic monomer. For example, the water-dispersible enhancing moiety including the side chain hydrophilic monomer can include alkylene oxide polymers and copolymers in which the alkylene oxide groups have from 2-10 carbon atoms as shown in U.S. Pat. No. 6,897,281. Additional types of water-dispersible enhancing moieties can include thioglycolic acid, 2,6-dihydroxybenzoic acid, sulfoisophthalic acid, polyethylene glycol, and the like, and mixtures thereof. Additional details regarding water-dispersible enhancing moieties can be found in U.S. Pat. No. 7,476,705.


Polyamides


The polymer can comprise a polyamide, such as a thermoplastic polyamide, or a thermoset polyamide. The polyamide can be an elastomeric polyamide, including an elastomeric thermoplastic polyamide or an elastomeric thermoset polyamide. The polyamide can be a polyamide homopolymer having repeating polyamide segments of the same chemical structure. Alternatively, the polyamide can comprise a number of polyamide segments having different polyamide chemical structures (e.g., polyamide 6 segments, polyamide 11 segments, polyamide 12 segments, polyamide 66 segments, etc.). The polyamide segments having different chemical structure can be arranged randomly, or can be arranged as repeating blocks.


The polyamide can be a co-polyamide (i.e., a co-polymer including polyamide segments and non-polyamide segments). The polyamide segments of the co-polyamide can comprise or consist of polyamide 6 segments, polyamide 11 segments, polyamide 12 segments, polyamide 66 segments, or any combination thereof. The polyamide segments of the co-polyamide can be arranged randomly, or can be arranged as repeating segments. The polyamide segments can comprise or consist of polyamide 6 segments, or polyamide 12 segments, or both polyamide 6 segment and polyamide 12 segments. In the example where the polyamide segments of the co-polyamide include of polyamide 6 segments and polyamide 12 segments, the segments can be arranged randomly. The non-polyamide segments of the co-polyamide can comprise or consist of polyether segments, polyester segments, or both polyether segments and polyester segments. The co-polyamide can be a block co-polyamide, or can be a random co-polyamide. The copolyamide can be formed from the polycondensation of a polyamide oligomer or prepolymer with a second oligomer prepolymer to form a copolyamide (i.e., a co-polymer including polyamide segments. Optionally, the second prepolymer can be a hydrophilic prepolymer.


The polyamide can be a polyamide-containing block co-polymer. For example, the block co-polymer can have repeating hard segments, and repeating soft segments. The hard segments can comprise polyamide segments, and the soft segments can comprise non-polyamide segments. The polyamide-containing block co-polymer can be an elastomeric co-polyamide comprising or consisting of polyamide-containing block co-polymers having repeating hard segments and repeating soft segments. In block co-polymers, including block co-polymers having repeating hard segments and soft segments, physical crosslinks can be present within the segments or between the segments or both within and between the segments.


The polyamide itself, or the polyamide segment of the polyamide-containing block co-polymer can be derived from the condensation of polyamide prepolymers, such as lactams, amino acids, and/or diamino compounds with dicarboxylic acids, or activated forms thereof. The resulting polyamide segments include amide linkages (—(CO)NH—). The term “amino acid” refers to a molecule having at least one amino group and at least one carboxyl group. Each polyamide segment of the polyamide can be the same or different.


The polyamide or the polyamide segment of the polyamide-containing block co-polymer can be derived from the polycondensation of lactams and/or amino acids, and can include an amide segment having a structure shown in Formula 13, below, wherein R6 group represents the portion of the polyamide derived from the lactam or amino acid.




embedded image


The R6 group can be derived from a lactam. The R6 group can be derived from a lactam group having from 3 to 20 carbon atoms, or a lactam group having from 4 to 15 carbon atoms, or a lactam group having from 6 to 12 carbon atoms. The R6 group can be derived from caprolactam or laurolactam. The R6 group can be derived from one or more amino acids. The R6 group can be derived from an amino acid group having from 4 to 25 carbon atoms, or an amino acid group having from 5 to 20 carbon atoms, or an amino acid group having from 8 to 15 carbon atoms. The R6 group can be derived from 12-aminolauric acid or 11-aminoundecanoic acid.


Optionally, in order to increase the relative degree of hydrophilicity of the polyamide-containing block co-polymer, Formula 13 can include a polyamide-polyether block copolymer segment, as shown below:




embedded image



wherein m is 3-20, and n is 1-8. Optionally, m is 4-15, or 6-12 (e.g., 6, 7, 8, 9, 10, 11, or 12), and n is 1, 2, or 3. For example, m can be 11 or 12, and n can be 1 or 3. The polyamide or the polyamide segment of the polyamide-containing block co-polymer can be derived from the condensation of diamino compounds with dicarboxylic acids, or activated forms thereof, and can include an amide segment having a structure shown in Formula 15, below, wherein the R7 group represents the portion of the polyamide derived from the diamino compound, and the R8 group represents the portion derived from the dicarboxylic acid compound:




embedded image


The R7 group can be derived from a diamino compound that includes an aliphatic group having from 4 to 15 carbon atoms, or from 5 to 10 carbon atoms, or from 6 to 9 carbon atoms. The diamino compound can include an aromatic group, such as phenyl, naphthyl, xylyl, and tolyl. Suitable diamino compounds from which the R7 group can be derived include, but are not limited to, hexamethylene diamine (HMD), tetramethylene diamine, trimethyl hexamethylene diamine (TMD),m-xylylene diamine (MXD), and 1,5-pentamine diamine. The R8 group can be derived from a dicarboxylic acid or activated form thereof, including an aliphatic group having from 4 to 15 carbon atoms, or from 5 to 12 carbon atoms, or from 6 to 10 carbon atoms. The dicarboxylic acid or activated form thereof from which R8 can be derived includes an aromatic group, such as phenyl, naphthyl, xylyl, and tolyl groups. Suitable carboxylic acids or activated forms thereof from which R8 can be derived include adipic acid, sebacic acid, terephthalic acid, and isophthalic acid. The polyamide chain can be substantially free of aromatic groups.


Each polyamide segment of the polyamide (including the polyamide-containing block co-polymer) can be independently derived from a polyamide prepolymer selected from the group consisting of 12-aminolauric acid, caprolactam, hexamethylene diamine and adipic acid.


The polyamide can comprise or consist essentially of a poly(ether-block-amide). The poly(ether-block-amide) can be formed from the polycondensation of a carboxylic acid terminated polyamide prepolymer and a hydroxyl terminated polyether prepolymer to form a poly(ether-block-amide), as shown in Formula 16:




embedded image


The poly(ether block amide) polymer can be prepared by polycondensation of polyamide blocks containing reactive ends with polyether blocks containing reactive ends. Examples include: 1) polyamide blocks containing diamine chain ends with polyoxyalkylene blocks containing carboxylic chain ends; 2) polyamide blocks containing dicarboxylic chain ends with polyoxyalkylene blocks containing diamine chain ends obtained by cyanoethylation and hydrogenation of aliphatic dihydroxylated alpha-omega polyoxyalkylenes known as polyether diols; 3) polyamide blocks containing dicarboxylic chain ends with polyether diols, the products obtained in this particular case being polyetheresteramides. The polyamide block of the poly(ether-block-amide) can be derived from lactams, amino acids, and/or diamino compounds with dicarboxylic acids as previously described. The polyether block can be derived from one or more polyethers selected from the group consisting of polyethylene oxide (PEO), polypropylene oxide (PPO), polytetrahydrofuran (PTHF), polytetramethylene oxide (PTMO), and combinations thereof.


The poly(ether block amide) polymers can include those comprising polyamide blocks comprising dicarboxylic chain ends derived from the condensation of α, ω-aminocarboxylic acids, of lactams or of dicarboxylic acids and diamines in the presence of a chain-limiting dicarboxylic acid. In poly(ether block amide) polymers of this type, a α, ω-aminocarboxylic acid such as aminoundecanoic acid can be used; a lactam such as caprolactam or lauryllactam can be used; a dicarboxylic acid such as adipic acid, decanedioic acid or dodecanedioic acid can be used; and a diamine such as hexamethylenediamine can be used; or various combinations of any of the foregoing. The copolymer can comprise polyamide blocks comprising polyamide 12 or of polyamide 6.


The poly(ether block amide) polymers can include those comprising polyamide blocks derived from the condensation of one or more α, ω-aminocarboxylic acids and/or of one or more lactams containing from 6 to 12 carbon atoms in the presence of a dicarboxylic acid containing from 4 to 12 carbon atoms, and are of low mass, i.e., they have a number-average molecular weight of from 400 to 1000. In poly(ether block amide) polymers of this type, an α, ω-aminocarboxylic acid such as aminoundecanoic acid or aminododecanoic acid can be used; a dicarboxylic acid such as adipic acid, sebacic acid, isophthalic acid, butanedioic acid, 1,4-cyclohexyldicarboxylic acid, terephthalic acid, the sodium or lithium salt of sulphoisophthalic acid, dimerized fatty acids (these dimerized fatty acids have a dimer content of at least 98 weight percent and are preferably hydrogenated) and dodecanedioic acid HOOC—(CH2)10—COOH can be used; and a lactam such as caprolactam and lauryllactam can be used; or various combinations of any of the foregoing. The copolymer can comprise polyamide blocks obtained by condensation of lauryllactam in the presence of adipic acid or dodecanedioic acid and with a number average molecular weight of at least 750 have a melting temperature of from about 127 to about 130 degrees C. The various constituents of the polyamide block and their proportion can be chosen in order to obtain a melting point of less than 150 degrees C., or from about 90 degrees C. to about 135 degrees C.


The poly(ether block amide) polymers can include those comprising polyamide blocks derived from the condensation of at least one α, ω-aminocarboxylic acid (or a lactam), at least one diamine and at least one dicarboxylic acid. In copolymers of this type, a α,ω-aminocarboxylic acid, the lactam and the dicarboxylic acid can be chosen from those described herein above and the diamine such as an aliphatic diamine containing from 6 to 12 atoms and can be acyclic and/or saturated cyclic such as, but not limited to, hexamethylenediamine, piperazine, 1-aminoethylpiperazine, bisaminopropylpiperazine, tetramethylenediamine, octamethylene-diamine, decamethylenediamine, dodecamethylenediamine, 1,5-diaminohexane, 2,2,4-trimethyl-1,6-diaminohexane, diamine polyols, isophoronediamine (IPD), methylpentamethylenediamine (MPDM), bis(aminocyclohexyl)methane (BACM) and bis(3-methyl-4-aminocyclohexyl)methane (BMACM) can be used.


The polyamide can be a thermoplastic polyamide and the constituents of the polyamide block and their proportion can be chosen in order to obtain a melting temperature of less than 150 degrees C., such as a melting point of from about 90 degrees C. to about 135 degrees C. The various constituents of the thermoplastic polyamide block and their proportion can be chosen in order to obtain a melting point of less than 150 degrees C., such as from about and 90 degrees C. to about 135 degrees C.


The number average molar mass of the polyamide blocks can be from about 300 grams per mole to about 15,000 grams per mole, from about 500 grams per mole to about 10,000 grams per mole, from about 500 grams per mole to about 6,000 grams per mole, from about 500 grams per mole to about 5,000 grams per mole, or from about 600 grams per mole to about 5,000 grams per mole. The number average molecular weight of the polyether block can range from about 100 to about 6,000, from about 400 to about 3000, or from about 200 to about 3,000. The polyether (PE) content (x) of the poly(ether block amide) polymer can be from about 0.05 to about 0.8 (i.e., from about 5 mole percent to about 80 mole percent). The polyether blocks can be present in the polyamide in an amount of from about 10 weight percent to about 50 weight percent, from about 20 weight percent to about 40 weight percent, or from about 30 weight percent to about 40 weight percent. The polyamide blocks can be present in the polyamide in an amount of from about 50 weight percent to about 90 weight percent, from about 60 weight percent to about 80 weight percent, or from about 70 weight percent to about 90 weight percent.


The polyether blocks can contain units other than ethylene oxide units, such as, for example, propylene oxide or polytetrahydrofuran (which leads to polytetramethylene glycol sequences). It is also possible to use simultaneously PEG blocks, i.e., those consisting of ethylene oxide units, polypropylene glycol (PPG) blocks, i.e. those consisting of propylene oxide units, and poly(tetramethylene ether)glycol (PTMG) blocks, i.e. those consisting of tetramethylene glycol units, also known as polytetrahydrofuran. PPG or PTMG blocks are advantageously used. The amount of polyether blocks in these copolymers containing polyamide and polyether blocks can be from about 10 weight percent to about 50 weight percent of the copolymer, or from about 35 weight percent to about 50 weight percent.


The copolymers containing polyamide blocks and polyether blocks can be prepared by any means for attaching the polyamide blocks and the polyether blocks. In practice, two processes are essentially used, one being a 2-step process and the other a one-step process.


In the two-step process, the polyamide blocks having dicarboxylic chain ends are prepared first, and then, in a second step, these polyamide blocks are linked to the polyether blocks. The polyamide blocks having dicarboxylic chain ends are derived from the condensation of polyamide precursors in the presence of a chain-stopper dicarboxylic acid. If the polyamide precursors are only lactams or α,ω-aminocarboxylic acids, a dicarboxylic acid is added. If the precursors already comprise a dicarboxylic acid, this is used in excess with respect to the stoichiometry of the diamines. The reaction usually takes place from about 180 to about 300 degrees C., such as from about 200 degrees to about 290 degrees C., and the pressure in the reactor can be set from about 5 to about 30 bar and maintained for approximately 2 to 3 hours. The pressure in the reactor is slowly reduced to atmospheric pressure and then the excess water is distilled off, for example for one or two hours.


Once the polyamide having carboxylic acid end groups has been prepared, the polyether, the polyol and a catalyst are then added. The total amount of polyether can be divided and added in one or more portions, as can the catalyst. The polyether is added first and the reaction of the OH end groups of the polyether and of the polyol with the COOH end groups of the polyamide starts, with the formation of ester linkages and the elimination of water. Water is removed as much as possible from the reaction mixture by distillation and then the catalyst is introduced in order to complete the linking of the polyamide blocks to the polyether blocks. This second step takes place with stirring, preferably under a vacuum of at least 50 millibar (5000 Pascals) at a temperature such that the reactants and the copolymers obtained are in the molten state. By way of example, this temperature can be from about 100 to about 400 degrees C., such as from about 200 to about 250 degrees C. The reaction is monitored by measuring the torque exerted by the polymer melt on the stirrer or by measuring the electric power consumed by the stirrer. The end of the reaction is determined by the value of the torque or of the target power. The catalyst is defined as being any product which promotes the linking of the polyamide blocks to the polyether blocks by esterification. The catalyst can be a derivative of a metal (M) chosen from the group formed by titanium, zirconium and hafnium. The derivative can be prepared from a tetraalkoxides consistent with the general formula M(OR)4, in which M represents titanium, zirconium or hafnium and R, which can be identical or different, represents linear or branched alkyl radicals having from 1 to 24 carbon atoms.


The catalyst can comprise a salt of the metal (M), particularly the salt of (M) and of an organic acid and the complex salts of the oxide of (M) and/or the hydroxide of (M) and an organic acid. The organic acid can be formic acid, acetic acid, propionic acid, butyric acid, valeric acid, caproic acid, caprylic acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, linolenic acid, cyclohexanecarboxylic acid, phenylacetic acid, benzoic acid, salicylic acid, oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, maleic acid, fumaric acid, phthalic acid or crotonic acid. The organic acid can be an acetic acid or a propionic acid. M can be zirconium and such salts are called zirconyl salts, e.g., the commercially available product sold under the name zirconyl acetate.


The weight proportion of catalyst can vary from about 0.01 to about 5 percent of the weight of the mixture of the dicarboxylic polyamide with the polyetherdiol and the polyol. The weight proportion of catalyst can vary from about 0.05 to about 2 percent of the weight of the mixture of the dicarboxylic polyamide with the polyetherdiol and the polyol.


In the one-step process, the polyamide precursors, the chain stopper and the polyether are blended together; what is then obtained is a polymer having essentially polyether blocks and polyamide blocks of highly variable length, but also the various reactants that have reacted randomly, which are distributed randomly along the polymer chain. They are the same reactants and the same catalyst as in the two-step process described above. If the polyamide precursors are only lactams, it is advantageous to add a little water. The copolymer has essentially the same polyether blocks and the same polyamide blocks, but also a small portion of the various reactants that have reacted randomly, which are distributed randomly along the polymer chain. As in the first step of the two-step process described above, the reactor is closed and heated, with stirring. The pressure established is from about 5 to about 30 bar. When the pressure no longer changes, the reactor is put under reduced pressure while still maintaining vigorous stirring of the molten reactants. The reaction is monitored as previously in the case of the two-step process.


The proper ratio of polyamide to polyether blocks can be found in a single poly(ether block amide), or a blend of two or more different composition poly(ether block amide)s can be used with the proper average composition. It can be useful to blend a block copolymer having a high level of polyamide groups with a block copolymer having a higher level of polyether blocks, to produce a blend having an average level of polyether blocks of about 20 to about 40 weight percent of the total blend of poly(amid-block-ether) copolymers, or about 30 to about 35 weight percent. The copolymer can comprise a blend of two different poly(ether-block-amide)s comprising at least one block copolymer having a level of polyether blocks below 35 weight percent, and a second poly(ether-block-amide) having at least 45 weight percent of polyether blocks.


Exemplary commercially available copolymers include, but are not limited to, those available under the tradenames of “VESTAMID” (Evonik Industries, Essen, Germany); “PLATAMID” (Arkema, Colombes, France), e.g., product code H2694; “PEBAX” (Arkema), e.g., product code “PEBAX MH1657” and “PEBAX MV1074”; “PEBAX RNEW” (Arkema); “GRILAMID” (EMS-Chemie AG, Domat-Ems, Switzerland), or also to other similar materials produced by various other suppliers.


The polyamide can be physically crosslinked through, e.g., nonpolar or polar interactions between the polyamide groups of the polymers. In examples where the polyamide is a copolyamide, the copolyamide can be physically crosslinked through interactions between the polyamide groups, and optionally by interactions between the copolymer groups. When the co-polyamide is physically crosslinked through interactions between the polyamide groups, the polyamide segments can form the portion of the polymer referred to as the hard segment, and copolymer segments can form the portion of the polymer referred to as the soft segment. For example, when the copolyamide is a poly(ether-block-amide), the polyamide segments form the hard segments of the polymer, and polyether segments form the soft segments of the polymer. Therefore, in some examples, the polymer can include a physically crosslinked polymeric network having one or more polymer chains with amide linkages.


The polyamide segment of the co-polyamide can include polyamide-11 or polyamide-12 and the polyether segment can be a segment selected from the group consisting of polyethylene oxide, polypropylene oxide, and polytetramethylene oxide segments, and combinations thereof.


The polyamide can be partially or fully covalently crosslinked, as previously described herein. In some cases, the degree of crosslinking present in the polyamide is such that, when it is thermally processed, e.g., in the form of a yarn or fiber to form the articles of the present disclosure, the partially covalently crosslinked thermoplastic polyamide retains sufficient thermoplastic character that the partially covalently crosslinked thermoplastic polyamide is melted during the processing and re-solidifies. In other cases, the crosslinked polyamide is a thermoset polymer.


Polyesters


The polymers can comprise a polyester. The polyester can comprise a thermoplastic polyester, or a thermoset polyester. Additionally, the polyester can be an elastomeric polyester, including a thermoplastic polyester or a thermoset elastomeric polyester. The polyester can be formed by reaction of one or more carboxylic acids, or its ester-forming derivatives, with one or more bivalent or multivalent aliphatic, alicyclic, aromatic or araliphatic alcohols or a bisphenol. The polyester can be a polyester homopolymer having repeating polyester segments of the same chemical structure. Alternatively, the polyester can comprise a number of polyester segments having different polyester chemical structures (e.g., polyglycolic acid segments, polylactic acid segments, polycaprolactone segments, polyhydroxyalkanoate segments, polyhydroxybutyrate segments, etc.). The polyester segments having different chemical structure can be arranged randomly, or can be arranged as repeating blocks.


Exemplary carboxylic acids that can be used to prepare a polyester include, but are not limited to, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, nonane dicarboxylic acid, decane dicarboxylic acid, undecane dicarboxylic acid, terephthalic acid, isophthalic acid, alkyl-substituted or halogenated terephthalic acid, alkyl-substituted or halogenated isophthalic acid, nitro-terephthalic acid, 4,4′-diphenyl ether dicarboxylic acid, 4,4′-diphenyl thioether dicarboxylic acid, 4,4′-diphenyl sulfone-dicarboxylic acid, 4,4′-diphenyl alkylenedicarboxylic acid, naphthalene-2,6-dicarboxylic acid, cyclohexane-1,4-dicarboxylic acid and cyclohexane-1,3-dicarboxylic acid. Exemplary diols or phenols suitable for the preparation of the polyester include, but are not limited to, ethylene glycol, diethylene glycol, 1,3-propanediol, 1,4-butanediol, 1,6-hexanediol, 1,8-octanediol, 1,10-decanediol, 1,2-propanediol, 2,2-dimethyl-1,3-propanediol, 2,2,4-trimethylhexanediol, p-xylenediol, 1,4-cyclohexanediol, 1,4-cyclohexane dimethanol, and bis-phenol A.


The polyester can be a polybutylene terephthalate (PBT), a polytrimethylene terephthalate, a polyhexamethylene terephthalate, a poly-1,4-dimethylcyclohexane terephthalate, a polyethylene terephthalate (PET), a polyethylene isophthalate (PEI), a polyarylate (PAR), a polybutylene naphthalate (PBN), a liquid crystal polyester, or a blend or mixture of two or more of the foregoing.


The polyester can be a co-polyester (i.e., a co-polymer including polyester segments and non-polyester segments). The co-polyester can be an aliphatic co-polyester (i.e., a co-polyester in which both the polyester segments and the non-polyester segments are aliphatic). Alternatively, the co-polyester can include aromatic segments. The polyester segments of the co-polyester can comprise or consist essentially of polyglycolic acid segments, polylactic acid segments, polycaprolactone segments, polyhydroxyalkanoate segments, polyhydroxybutyrate segments, or any combination thereof. The polyester segments of the co-polyester can be arranged randomly, or can be arranged as repeating blocks.


For example, the polyester can be a block co-polyester having repeating blocks of polymeric units of the same chemical structure which are relatively harder (hard segments), and repeating blocks of the same chemical structure which are relatively softer (soft segments). In block co-polyesters, including block co-polyesters having repeating hard segments and soft segments, physical crosslinks can be present within the blocks or between the blocks or both within and between the blocks. The polymer can comprise or consist essentially of an elastomeric co-polyester having repeating blocks of hard segments and repeating blocks of soft segments.


The non-polyester segments of the co-polyester can comprise or consist essentially of polyether segments, polyamide segments, or both polyether segments and polyamide segments. The co-polyester can be a block co-polyester, or can be a random co-polyester. The co-polyester can be formed from the polycondensation of a polyester oligomer or prepolymer with a second oligomer prepolymer to form a block copolyester. Optionally, the second prepolymer can be a hydrophilic prepolymer. For example, the co-polyester can be formed from the polycondensation of terephthalic acid or naphthalene dicarboxylic acid with ethylene glycol, 1,4-butanediol, or 1,3-propanediol. Examples of co-polyesters include polyethylene adipate, polybutylene succinate, poly(3-hydroxbutyrate-co-3-hydroxyvalerate), polyethylene terephthalate, polybutylene terephthalate, polytrimethylene terephthalate, polyethylene napthalate, and combinations thereof. The co-polyamide can comprise or consist of polyethylene terephthalate.


The polyester can be a block copolymer comprising segments of one or more of polybutylene terephthalate (PBT), a polytrimethylene terephthalate, a polyhexamethylene terephthalate, a poly-1,4-dimethylcyclohexane terephthalate, a polyethylene terephthalate (PET), a polyethylene isophthalate (PEI), a polyarylate (PAR), a polybutylene naphthalate (PBN), and a liquid crystal polyester. For example, a suitable polyester that is a block copolymer can be a PET/PEI copolymer, a polybutylene terephthalate/tetraethylene glycol copolymer, a polyoxyalkylenediimide diacid/polybutylene terephthalate copolymer, or a blend or mixture of any of the foregoing.


The polyester can be a biodegradable resin, for example, a copolymerized polyester in which poly(α-hydroxy acid) such as polyglycolic acid or polylactic acid is contained as principal repeating units.


The disclosed polyesters can be prepared by a variety of polycondensation methods known to the skilled artisan, such as a solvent polymerization or a melt polymerization process.


Polyolefins


The polymers can comprise or consist essentially of a polyolefin. The polyolefin can be a thermoplastic polyolefin or a thermoset polyolefin. Additionally, the polyolefin can be an elastomeric polyolefin, including a thermoplastic elastomeric polyolefin or a thermoset elastomeric polyolefin. Exemplary polyolefins can include polyethylene, polypropylene, and olefin elastomers (e.g., metallocene-catalyzed block copolymers of ethylene and α-olefins having 4 to about 8 carbon atoms). The polyolefin can be a polymer comprising a polyethylene, an ethylene-α-olefin copolymer, an ethylene-propylene rubber (EPDM), a polybutene, a polyisobutylene, a poly-4-methylpent-1-ene, a polyisoprene, a polybutadiene, a ethylene-methacrylic acid copolymer, and an olefin elastomer such as a dynamically cross-linked polymer obtained from polypropylene (PP) and an ethylene-propylene rubber (EPDM), and blends or mixtures of the foregoing. Further exemplary polyolefins include polymers of cycloolefins such as cyclopentene or norbornene.


It is to be understood that polyethylene, which optionally can be crosslinked, is inclusive a variety of polyethylenes, including low density polyethylene (LDPE), linear low density polyethylene (LLDPE), (VLDPE) and (ULDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), high density and high molecular weight polyethylene (HDPE-HMW), high density and ultrahigh molecular weight polyethylene (HDPE-UHMW), and blends or mixtures of any the foregoing polyethylenes. A polyethylene can also be a polyethylene copolymer derived from monomers of monolefins and diolefins copolymerized with a vinyl, acrylic acid, methacrylic acid, ethyl acrylate, vinyl alcohol, and/or vinyl acetate. Polyolefin copolymers comprising vinyl acetate-derived units can be a high vinyl acetate content copolymer, e.g., greater than about 50 weight percent vinyl acetate-derived composition.


The polyolefin can be formed through free radical, cationic, and/or anionic polymerization by methods well known to those skilled in the art (e.g., using a peroxide initiator, heat, and/or light). The disclosed polyolefin can be prepared by radical polymerization under high pressure and at elevated temperature. Alternatively, the polyolefin can be prepared by catalytic polymerization using a catalyst that normally contains one or more metals from group IVb, Vb, VIb or VIII metals. The catalyst usually has one or more than one ligand, typically oxides, halides, alcoholates, esters, ethers, amines, alkyls, alkenyls and/or aryls that can be either p- or s-coordinated complexed with the group IVb, Vb, VIb or VIII metal. The metal complexes can be in the free form or fixed on substrates, typically on activated magnesium chloride, titanium(III) chloride, alumina or silicon oxide. The metal catalysts can be soluble or insoluble in the polymerization medium. The catalysts can be used by themselves in the polymerization or further activators can be used, typically a group Ia, IIa and/or IIIa metal alkyls, metal hydrides, metal alkyl halides, metal alkyl oxides or metal alkyloxanes. The activators can be modified conveniently with further ester, ether, amine or silyl ether groups.


Suitable polyolefins can be prepared by polymerization of monomers of monolefins and diolefins as described herein. Exemplary monomers that can be used to prepare the polyolefin include, but are not limited to, ethylene, propylene, 1-butene, 1-pentene, 1-hexene, 2-methyl-1-propene, 3-methyl-1-pentene, 4-methyl-1-pentene, 5-methyl-1-hexene and mixtures thereof.


Suitable ethylene-α-olefin copolymers can be obtained by copolymerization of ethylene with an α-olefin such as propylene, butene-1, hexene-1, octene-1,4-methyl-1-pentene or the like having carbon numbers of 3 to 12.


Suitable dynamically cross-linked polymers can be obtained by cross-linking a rubber component as a soft segment while at the same time physically dispersing a hard segment such as PP and a soft segment such as EPDM by using a kneading machine such as a Banbury mixer and a biaxial extruder.


The polyolefin can be a mixture of polyolefins, such as a mixture of two or more polyolefins disclosed herein above. For example, a suitable mixture of polyolefins can be a mixture of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) or mixtures of different types of polyethylene (for example LDPE/HDPE).


The polyolefin can be a copolymer of suitable monolefin monomers or a copolymer of a suitable monolefin monomer and a vinyl monomer. Exemplary polyolefin copolymers include ethylene/propylene copolymers, linear low density polyethylene (LLDPE) and mixtures thereof with low density polyethylene (LDPE), propylene/but-1-ene copolymers, propylene/isobutylene copolymers, ethylene/but-1-ene copolymers, ethylene/hexene copolymers, ethylene/methylpentene copolymers, ethylene/heptene copolymers, ethylene/octene copolymers, propylene/butadiene copolymers, isobutylene/isoprene copolymers, ethylene/alkyl acrylate copolymers, ethylene/alkyl methacrylate copolymers, ethylene/vinyl acetate copolymers and their copolymers with carbon monoxide or ethylene/acrylic acid copolymers and their salts (ionomers) as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene-norbornene; and mixtures of such copolymers with one another and with polymers mentioned in 1) above, for example polypropylene/ethylene-propylene copolymers, LDPE/ethylene-vinyl acetate copolymers (EVA), LDPE/ethylene-acrylic acid copolymers (EAA), LLDPE/EVA, LLDPE/EAA and alternating or random polyalkylene/carbon monoxide copolymers and mixtures thereof with other polymers, for example polyamides.


The polyolefin can be a polypropylene homopolymer, a polypropylene copolymers, a polypropylene random copolymer, a polypropylene block copolymer, a polyethylene homopolymer, a polyethylene random copolymer, a polyethylene block copolymer, a low density polyethylene (LDPE), a linear low density polyethylene (LLDPE), a medium density polyethylene, a high density polyethylene (HDPE), or blends or mixtures of one or more of the preceding polymers.


The polyolefin can be a polypropylene. The term “polypropylene,” as used herein, is intended to encompass any polymeric composition comprising propylene monomers, either alone or in mixture or copolymer with other randomly selected and oriented polyolefins, dienes, or other monomers (such as ethylene, butylene, and the like). Such a term also encompasses any different configuration and arrangement of the constituent monomers (such as atactic, syndiotactic, isotactic, and the like). Thus, the term as applied to fibers is intended to encompass actual long strands, tapes, threads, and the like, of drawn polymer. The polypropylene can be of any standard melt flow (by testing); however, standard fiber grade polypropylene resins possess ranges of Melt Flow Indices between about 1 and 1000.


The polyolefin can be a polyethylene. The term “polyethylene,” as used herein, is intended to encompass any polymeric composition comprising ethylene monomers, either alone or in mixture or copolymer with other randomly selected and oriented polyolefins, dienes, or other monomers (such as propylene, butylene, and the like). Such a term also encompasses any different configuration and arrangement of the constituent monomers (such as atactic, syndiotactic, isotactic, and the like). Thus, the term as applied to fibers is intended to encompass actual long strands, tapes, threads, and the like, of drawn polymer. The polyethylene can be of any standard melt flow (by testing); however, standard fiber grade polyethylene resins possess ranges of Melt Flow Indices between about 1 and 1000.


The thermoplastic and/or thermosetting material can further comprise one or more processing aids. The processing aid can be a non-polymeric material. These processing aids can be independently selected from the group including, but not limited to, curing agents, initiators, plasticizers, mold release agents, lubricants, antioxidants, flame retardants, dyes, pigments, reinforcing and non-reinforcing fillers, fiber reinforcements, and light stabilizers.


Now having described various aspects of the present disclosure, additional discussion is provided regarding the structure of the bladder. The bladder can be unfilled, partially inflated, or fully inflated when the structural design (e.g., multi-layer optical film) is disposed onto the bladder. The bladder is a bladder capable of including a volume of a fluid. An unfilled bladder is a fluid-fillable bladder and a filled bladder that has been at least partially inflated with a fluid at a pressure equal to or greater than atmospheric pressure. When disposed onto or incorporated into an article of footwear, apparel, or sports equipment, the bladder is generally, at that point, a fluid-filled bladder. The fluid be a gas or a liquid. The gas can include air, nitrogen gas (N2), or other appropriate gas.


The bladder can have a gas transmission rate for nitrogen gas, for example, where a bladder wall of a given thickness has a gas transmission rate for nitrogen that is at least about ten times lower than the gas transmission rate for nitrogen of a butyl rubber layer of substantially the same thickness as the thickness of the bladder described herein. The bladder can have a first bladder wall having a first bladder wall thickness (e.g., about 0.1 to 40 mils). The bladder can have a first bladder wall that can have a gas transmission rate (GTR) for nitrogen gas of less than about 15 cm3/m2·atm·day, less than about 10 m3/m2·atm·day, less than about 5 cm3/m2·atm·day, less than about 1 cm3/m2·atm·day (e.g., from about 0.001 cm3/m2·atm·day to about 1 cm3/m2·atm·day, about 0.01 cm3/m2·atm·day to about 1 cm3/m2·atm·day or about 0.1 cm3/m2·atm·day to about 1 cm3/m2·atm·day) for an average wall thickness of 20 mils. The bladder can have a first bladder wall having a first bladder wall thickness, where the first bladder wall has a gas transmission rate of 15 cm3/m2·atm·day or less for nitrogen for an average wall thickness of 20 mils.


In an aspect, the bladder has a bladder wall having an interior-facing side and an exterior-facing side, where the interior-facing side defines at least a portion of an interior region of the bladder. The multi-layer optical film having a first side and a second opposing side can be disposed on the exterior-facing side of the bladder, the interior-facing side of the bladder, or both. The exterior-facing side of the bladder, the interior-facing side of the bladder, or both can include a plurality of topographical structures extending from the exterior-facing side of the bladder wall, the interior-facing side of the bladder, or both, where the first side or the second side of the multi-layer optical film is disposed on the exterior-facing side of the bladder wall and covering some or all of the plurality of topographical structures, the interior-facing side of the bladder wall and covering some or all of the plurality of topographical structures, or both, and wherein the multi-layer optical film imparts a structural color to the bladder wall. The primer layer can be disposed on the exterior-facing side of the bladder, the interior-facing side of the bladder, or both, between the bladder wall and the multi-layer optical film.


In a particular aspect, the bladder can include a top wall operably secured to the footwear upper, a bottom wall opposite the top wall, and one or more sidewalls extending between the top wall and the bottom wall of the inflated bladder. The top wall, the bottom wall, and the one or more sidewalls collectively define an interior region of the inflated bladder, and wherein the one or more sidewalls each comprise an exterior-facing side. The multi-layer optical film having a first side and a second opposing side can be disposed on the exterior-facing side of the bladder, the interior-facing side of the bladder, or both. The exterior-facing side of the bladder, the interior-facing side of the bladder, or both can include a plurality of topographical structures extending from the exterior-facing side of the bladder wall, the interior-facing side of the bladder, or both, where the first side or the second side of the multi-layer optical film is disposed on the exterior-facing side of the bladder wall and covering some or all of the plurality of topographical structures, the interior-facing side of the bladder wall and covering some or all of the plurality of topographical structures, or both, and wherein the multi-layer optical film imparts a structural color to the bladder wall. The primer layer can be disposed on the exterior-facing side of the bladder, the interior-facing side of the bladder, or both, between the bladder wall and the multi-layer optical film.


An accepted method for measuring the relative permeance, permeability, and diffusion of inflated bladders is ASTM D-1434-82-V. See, e.g., U.S. Pat. No. 6,127,026, which is incorporated by reference as if fully set forth herein. According to ASTM D-1434-82-V, permeance, permeability and diffusion are measured by the following formulae:


Permeance

(quantity of gas)/[(area)×(time)×(pressure difference)]=permeance(GTR)/(pressure difference)=cm3/m2·atm·day (i.e., 24 hours)

Permeability

[(quantity of gas)×(film thickness)][(area)×(time)×(pressure difference)]=permeability [(GTR)×(film thickness)]/(pressure difference)=[(cm3)(mil)]/m2·atm·day (i.e., 24 hours)

Diffusion at One Atmosphere

(quantity of gas)/[(area)×(time)]=GTR=cm3/m2·day (i.e., 24 hours)


The bladder can include a bladder wall that includes a film including at least one polymeric layer or at least two or more polymeric layers. Each of the polymeric layers can be about 0.1 to 40 mils in thickness.


The polymeric layer can be formed of polymer material such as a thermoplastic material as described above and herein. The thermoplastic material can include an elastomeric material, such as a thermoplastic elastomeric material. The thermoplastic materials can include thermoplastic polyurethane (TPU), such as those described above and herein. The thermoplastic materials can include polyester-based TPU, polyether-based TPU, polycaprolactone-based TPU, polycarbonate-based TPU, polysiloxane-based TPU, or combinations thereof. Non-limiting examples of thermoplastic material that can be used include: “PELLETHANE” 2355-85ATP and 2355-95AE (Dow Chemical Company of Midland, Mich., USA), “ELASTOLLAN” (BASF Corporation, Wyandotte, Mich., USA) and “ESTANE” (Lubrizol, Brecksville, Ohio, USA), all of which are either ester or ether based. Additional thermoplastic material can include those described in U.S. Pat. Nos. 5,713,141; 5,952,065; 6,082,025; 6,127,026; 6,013,340; 6,203,868; and 6,321,465, which are incorporated herein by reference.


The polymeric layer can be formed of one or more of the following: ethylene-vinyl alcohol copolymers (EVOH), poly(vinyl chloride), polyvinylidene polymers and copolymers (e.g., polyvinylidene chloride), polyamides (e.g., amorphous polyamides), acrylonitrile polymers (e.g., acrylonitrile-methyl acrylate copolymers), polyurethane engineering plastics, polymethylpentene resins, ethylene-carbon monoxide copolymers, liquid crystal polymers, polyethylene terephthalate, polyether imides, polyacrylic imides, and other polymeric materials known to have relatively low gas transmission rates. Blends and alloys of these materials as well as with the TPUs described herein and optionally including combinations of polyimides and crystalline polymers, are also suitable. For instance, blends of polyimides and liquid crystal polymers, blends of polyamides and polyethylene terephthalate, and blends of polyamides with styrenics are suitable.


Specific examples of polymeric materials of the polymeric layer can include acrylonitrile copolymers such as “BAREX” resins, available from Ineos (Rolle, Switzerland); polyurethane engineering plastics such as “ISPLAST” ETPU available from Lubrizol (Brecksville, Ohio, USA); ethylene-vinyl alcohol copolymers marketed under the tradenames “EVAL” by Kuraray (Houston, Tex., USA), “SOARNOL” by Nippon Gohsei (Hull, England), and “SELAR OH” by DuPont (Wilmington, Del., USA); polyvinylidiene chloride available from S.C. Johnson (Racine, Wis., USA) under the tradename “SARAN”, and from Solvay (Brussels, Belgium) under the tradename “IXAN”; liquid crystal polymers such as “VECTRA” from Celanese (Irving, Tex., USA) and “XYDAR” from Solvay; “MDX6” nylon, and amorphous nylons such as “NOVAMID” X21 from Koninklijke DSM N.V (Heerlen, Netherlands), “SELAR PA” from DuPont; polyetherimides sold under the tradename “ULTEM” by SABIC (Riyadh, Saudi Arabia); poly(vinyl alcohol)s; and polymethylpentene resins available from Mitsui Chemicals (Tokyo, Japan) under the tradename “TPX”.


Each polymeric layer of the film can be formed of a thermoplastic material which can include a combination of thermoplastic polymers. In addition to one or more thermoplastic polymers, the thermoplastic material can optionally include a colorant, a filler, a processing aid, a free radical scavenger, an ultraviolet light absorber, and the like. Each polymeric layer of the film can be made of a different of thermoplastic material including a different type of thermoplastic polymer.


The bladder can be made by applying heat, pressure and/or vacuum to a film. The bladder (e.g., one or more polymeric layers) can be formed using one or more polymeric materials, and forming the bladder using one or more processing techniques including, for example, extrusion, blow molding, injection molding, vacuum molding, rotary molding, transfer molding, pressure forming, heat sealing, casting, low-pressure casting, spin casting, reaction injection molding, radio frequency (RF) welding, and the like. The bladder can be made by co-extrusion followed by heat sealing or welding to give an inflatable bladder, which can optionally include one or more valves (e.g., one way valves) that allows the bladder to be filled with the fluid (e.g., gas).


As described herein, the multi-layer optical film can be disposed onto the interior-facing surface (side) of the bladder or the exterior-facing surface (side) of the bladder. The textured layer can be the interior-facing surface (side) or the exterior-facing surface (side) of the bladder. The multi-layer optical film can include the optical layer and optionally the primer layer and texture structure. The textured layer can be the interior-facing surface (side) or the exterior-facing surface (side) of the bladder (e.g., where the interior-facing or exterior-facing side is made of a thermoplastic material) and the primer layer disposed thereon and the multi-layer optical film disposed on the primer layer.


Now having described embodiments of the disclosure, evaluation of various properties and characteristics described herein are by various testing procedures as described herein below.


Method to Determine the Melting Temperature, and Glass Transition Temperature. The melting temperature and glass transition temperature are determined using a commercially available Differential Scanning calorimeter (“DSC”) in accordance with ASTM D3418-97. Briefly, a 10-15 gram sample is placed into an aluminum DSC pan and then the lead was sealed with the crimper press. The DSC is configured to scan from −100 degrees C. to 225 degrees C. with a 20 degrees C./minute heating rate, hold at 225 degrees C. for 2 minutes, and then cool down to 25 degrees C. at a rate of −10 degrees C./minute. The DSC curve created from this scan is then analyzed using standard techniques to determine the glass transition temperature and the melting temperature.


Method to Determine the Melt Flow Index. The melt flow index is determined according to the test method detailed in ASTM D1238-13 Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer, using Procedure A described therein. Briefly, the melt flow index measures the rate of extrusion of thermoplastics through an orifice at a prescribed temperature and load. In the test method, approximately 7 grams of the material is loaded into the barrel of the melt flow apparatus, which has been heated to a temperature specified for the material. A weight specified for the material is applied to a plunger and the molten material is forced through the die. A timed extrudate is collected and weighed. Melt flow rate values are calculated in grams/10 min.


Various embodiments of the present disclosure are described below in each of the sets of clauses. For each of the clauses, “disposing” can be replaced with “operably disposing”.


Clause 1. An article comprising:


a bladder having a first bladder wall, the first bladder wall having a first bladder wall thickness, an exterior-facing side comprising a first thermoplastic material, and an interior-facing side comprising a second thermoplastic material, wherein the first bladder wall has a gas transmission rate of 15 cm3/m2·atm·day or less for nitrogen for an average wall thickness of 20 mils; and


an multi-layer optical film disposed on or within the bladder, wherein the multi-layer optical film has a first side and a second side, wherein the first side and the second side are on opposing sides, wherein the first side or the second side of the multi-layer optical film is disposed on the exterior-facing side of the first bladder wall, on the interior-facing side of the first bladder wall, or on a side of a component in an internal cavity of the bladder, and wherein the first side of the multi-layer optical film, the second side of the multi-layer optical film, or both impart a structural color to the bladder.


Clause 2. The article of clause 1, wherein the exterior-facing side or the interior-facing side of the first bladder wall, or the first side or the second side of the multi-layer optical film, or any combination thereof, comprise a textured surface, and a combination of the textured surface and the multi-layer optical film impart the structural color.


Clause 3. The article of any of the preceding clauses, wherein the textured surface is part of a textured layer or textured structure.


Clause 4. The article of any of the preceding clauses, wherein the multi-layer optical film comprises the textured surface.


Clause 5. The article of any of the preceding clauses, wherein the textured surface, the textured layer or the textured structure is on the first side of the multi-layer optical film, and wherein the first side of the multi-layer optical film is disposed onto the exterior-facing surface of the first bladder wall.


Clause 6. The article of any of the preceding clauses, wherein the textured surface, the textured layer or the textured structure is on the second side of the multi-layer optical film, wherein the first side of the multi-layer optical film is disposed onto the interior-facing surface of the first bladder wall.


Clause 7. The article of any of the preceding clauses, wherein the textured surface has a plurality of topographical structures and plurality of flat areas.


Clause 8. The article of any of the preceding clauses, wherein the textured surface includes a plurality of topographical structures and flat planar areas, and wherein the topographical structures extend above the flat areas of the textured surface.


Clause 9. The article of any of the preceding clauses, wherein the dimensions of the topographical structures, a shape of the topographical structures, a spacing among the plurality of the topographical structures, in combination with the optical layer impart the structural color.


Clause 10. The article of any of the preceding clauses, wherein, over an area of the textured surface having a surface area of at least 5 square millimeters, the topographical structures are in random positions relative to one another.


Clause 11. The article of any of the preceding clauses, wherein spacing among the topographical structures is set to reduce distortion effects of the topographical structures from interfering with one another in the imparted structural color.


Clause 12. The article of any of the preceding clauses, wherein the topographical structures and the flat areas result in at least one optical layer of the multi-layer optical film having an undulating topography, wherein there is a planar region between neighboring depressions, elevations, or both that is planar with the flat planar areas of the textured surface, wherein the planar region has dimensions relative to the topographical structures to impart the structural color.


Clause 13. The article of any of the preceding clauses, wherein the topographical structures and the flat areas cause at least one layer of the multi-layer optical film to have an undulating topography across the textured structure.


Clause 14. The article of any of the preceding clauses, wherein the topographical structures and the flat areas cause each layer of the multi-layer optical film to have an undulating topography across the textured structure.


Clause 15. The article of any of the preceding clauses, wherein the multi-layer optical film includes at least two optical layers.


Clause 16. The article of any preceding article clause, wherein at least one of the layers of the multi-layer optical film comprises or consists essentially of a metal, wherein optionally the metal is selected from titanium or silicon.


Clause 17. The article of any preceding article clause, wherein the multi-layer optical film comprises at least one layer comprising or consisting essentially of a metal oxide, wherein optionally the metal oxide is titanium dioxide or silicon dioxide.


Clause 18. The article of any preceding article claim, wherein the multi-layer optical film comprises at least three layers, including a first layer comprising a metal, and a second layer comprising a metal oxide.


Clause 19. The article of any of the preceding clauses, wherein the multi-layer optical film comprises a multilayer reflector or a multilayer filter.


Clause 20. The article of any of the preceding clauses, wherein the multilayer reflector has at least two layers, including at least two adjacent layers having different refractive indices.


Clause 21. The article of any of the preceding clauses, wherein the refractive indices of the at least two adjacent layers differ by at least 5 percent, optionally at least 10 percent, or optionally at least 15 percent.


Clause 22. The article of any of the preceding clauses, wherein at least one of the layers of the multilayer reflector has a thickness that is about one fourth of the wavelength of visible light to be reflected by the multi-layer optical film to impart the structural color.


Clause 23. The article of any of the preceding clauses, wherein at least one of the layers of the multilayer reflector comprises a material selected from the group consisting of: silicon dioxide, titanium dioxide, zinc sulfide, magnesium fluoride, tantalum pentoxide, and a combination thereof.


Clause 24. The article of any preceding clause, wherein the structural color of the bladder is visible to a viewer having 20/20 visual acuity and normal color vision from a distance of about 1 meter from the bladder.


Clause 25. The article of any preceding clause, wherein the structural color imparted to the bladder has a single hue across the exterior-facing side of the bladder, regardless of viewing angle.


Clause 26. The article of any preceding clause, wherein the structural color imparted to the bladder includes two or more hues, each of the two or more hues being localized to a single region across the exterior-facing side of the bladder, and wherein the two or more hues do not shift as viewing angle is varied.


Clause 27. The article of any preceding clause, wherein the structural color imparted to the bladder is iridescent.


Clause 28. The article of any preceding clause, wherein the structural color of the bladder has limited iridescence.


Clause 29. The article of the preceding clause, wherein the structural color has limited iridescence such that, when each color visible at each possible angle of observation is assigned to a single hue selected from the group consisting of the primary, secondary and tertiary colors on the red yellow blue (RYB) color wheel, all of the assigned hues fall into a single hue group, wherein the single hue group is one of a) green-yellow, yellow, and yellow-orange; b) yellow, yellow-orange and orange; c) yellow-orange, orange, and orange-red; d) orange-red, and red-purple; e) red, red-purple, and purple; f) red-purple, purple, and purple-blue; g) purple, purple-blue, and blue; h) purple-blue, blue, and blue-green; i) blue, blue-green and green; and j) blue-green, green, and green-yellow.


Clause 30. The article of any of the preceding clauses, wherein the multi-layer optical film, as disposed onto the bladder, when measured according to the CIE 1976 color space under a given illumination condition at three observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and a1* and b1*, and a second color measurement at a second angle of observation having coordinates L2* and a2* and b2*, and a third color measurement at a third angle of observation having coordinates L3* and a3* and b3*, wherein the L1*, L2*, and L3* values may be the same or different, wherein the a1*, a2*, and a3* coordinate values may be the same or different, wherein the b1*, b2*, and b3* coordinate values may be the same or different, and wherein the range of the combined a1*, a2* and a3* values is less than about 40% of the overall scale of possible a* values, optionally is less than about 30% of the overall scale of possible a* values, optionally is less than about 20% of the overall scale of possible a* values, or is less than about 10% of the overall scale of possible a* values.


Clause 31. The article of any of the preceding clauses, wherein the multi-layer optical film, as disposed onto the bladder, when measured according to the CIE 1976 color space under a given illumination condition at three observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and a1* and b1*, and a second color measurement at a second angle of observation having coordinates L2* and a2* and b2*, and a third color measurement at a third angle of observation having coordinates L3* and a3* and b3*, wherein the L1*, L2*, and L3* values may be the same or different, wherein the a1*, a2*, and a3* coordinate values may be the same or different, wherein the b1*, b2*, and b3* coordinate values may be the same or different, and wherein the range of the combined b1*, b2* and b3* values is less than about 40% of the overall scale of possible b* values, optionally is less than about 30% of the overall scale of possible b* values, optionally is less than about 20% of the overall scale of possible b* values, or optionally is less than about 10% of the overall scale of possible b* values.


Clause 32. The article of any of the preceding clauses, wherein the multi-layer optical film, as disposed onto the bladder, when measured according to the CIE 1976 color space under a given illumination condition at two observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and a1* and b1*, and a second color measurement at a second angle of observation having coordinates L2* and a2* and b2*, wherein the L1* and L2* values may be the same or different, wherein the a1* and a2* coordinate values may be the same or different, wherein the b1* and b2* coordinate values may be the same or different, and wherein the ΔE*ab between the first color measurement and the second color measurement is less than or equal to about 100, where ΔE*ab=[(L1*−L2*)2+(a1*−a2*)2+(b1*−b2*)2]1/2, optionally is less than or equal to about 80, or optionally is less than or equal to about 60.


Clause 33. The article of any of the preceding clauses, wherein the multi-layer optical film, as disposed onto the bladder, when measured according to the CIELCH color space under a given illumination condition at three observation angles between −15 degrees and +60 degrees, has a first color measurement at a first angle of observation having coordinates L1* and C1* and h1°, and a second color measurement at a second angle of observation having coordinates L2* and C2* and h1°, and a third color measurement at a third angle of observation having coordinates L3* and C3* and h3°, wherein the L1*, L2*, and L3* values may be the same or different, wherein the C1*, C2*, and C3* coordinate values may be the same or different, wherein the h1°, h2° and h3° coordinate values may be the same or different, and wherein the range of the combined h1°, h2° and h3° values is less than about 60 degrees, optionally is less than about 50 degrees, optionally is less than about 40 degrees, optionally is less than about 30 degrees, or optionally is less than about 20 degrees.


Clause 34. The article of any of the preceding clauses, wherein a primer layer is disposed on the textured surface.


Clause 35. The article of any of the preceding clauses, wherein the primer layer is on the exterior-facing side of the bladder wall or on the interior-facing side of the bladder wall, and the multi-layer optical film is disposed on the primer layer.


Clause 36. The article of any of the preceding clauses, wherein the multi-layer optical film is disposed on the first thermoplastic material of the exterior-facing side or the second thermoplastic material of the interior-facing side of the bladder wall, with the primer layer, the textured surface, or both, positioned between the multi-layer optical film and the first thermoplastic material.


Clause 37. The article of any of the preceding clauses, wherein the primer layer comprises a textured surface, and the textured surface of the primer layer, the primer layer, and the multi-layer optical film impart the structural color.


Clause 38. The article of any of the preceding clauses, wherein the primer layer is a digitally printed layer, an offset printed layer, a pad printed layer, a screen printed layer, a flexographically printed layer, or a heat transfer printed layer.


Clause 39. The article of any of the preceding clauses, wherein the primer layer comprises a paint.


Clause 40. The article of any of the preceding clauses, wherein the primer layer comprises an ink.


Clause 41. The article of any of the preceding clauses, wherein the primer layer comprises a reground, and at least partially degraded polymer.


Clause 42. The article of any of the preceding clauses, wherein the primer layer is an oxide layer.


Clause 43. The article of any of the preceding clauses, wherein the primer layer comprises a metal oxide or a metal oxynitride.


Clause 44. The article of any of the preceding clauses, wherein the metal oxide or metal oxynitride is doped.


Clause 45. The article of any preceding clause, wherein the primer layer consists essentially of a metal oxide, and optionally consists essentially of titanium dioxide.


Clause 46. The article of any preceding clause, wherein the primer layer consists essentially of a doped metal oxide or a doped metal oxynitride or both.


Clause 47. The article of any preceding clause, wherein the primer layer has a thickness of about 1 to about 200 micrometers, or optionally of about 10 to about 100 micrometers, or optionally of about 10 to about 80 micrometers.


Clause 48. The article of any of the preceding clauses, wherein the primer layer is a coating, wherein the coating is a crosslinked coating including a matrix of crosslinked polymers.


Clause 49. The article of any of the preceding clauses, wherein the coating comprises a plurality of solid pigment particles entrapped in the matrix of crosslinked polymers.


Clause 50. The article of any of the preceding clauses, wherein the matrix of crosslinked polymers includes crosslinked elastomeric polymers.


Clause 51. The article of any of the preceding clauses, wherein the crosslinked elastomeric polymers include crosslinked polyurethane homopolymers or copolymers or both.


Clause 52. The article of any of the preceding clauses, wherein the crosslinked polyurethane copolymers include crosslinked polyester polyurethanes.


Clause 53. The article of any of the preceding clauses, wherein, when the solid pigment particles are present, the solid pigment particles are selected from the group consisting of: metal and metal oxide pigments, carbon pigments, clay earth pigments, ultramarine pigments and a combination thereof.


Clause 54. The article of any of the preceding clauses, wherein the coating further comprises a dye.


Clause 55. The article of any of the preceding clauses, wherein, when the dye is present, the dye is an acid dye.


Clause 56. The article of any of the preceding clauses, wherein the coating further comprises a quaternary ammonium compound.


Clause 57. The article of any of the preceding clauses, wherein the quaternary ammonium compound is a tetrabutyl ammonium compound.


Clause 58. The article of any of the preceding clauses, wherein the tetrabutyl ammonium compound is a tetrabutyl ammonium halide.


Clause 59. The article of any of the preceding clauses, wherein the polymeric coating composition, when present, comprises from 1 to 15 weight percent of the quaternary ammonium compound.


Clause 60. The article of any of the preceding clauses, wherein a molar ratio of the acid dye to the quaternary ammonium compound ranges from 3:1 to 1:3


Clause 61. The article of any of the preceding clauses, wherein the molar ratio of the acid dye to the quaternary ammonium compound ranges from 1.5:1 to 1:1.5.


Clause 62. The article of any of the preceding clauses, wherein the matrix of crosslinked polymers of the coating include polyurethane polymers.


Clause 63. The article of any of the preceding clauses, wherein the polyurethane polymers include thermoplastic polyurethane polymers.


Clause 64. The article of any of the preceding clauses, wherein the polyurethane polymers include elastomeric polyurethane polymers.


Clause 65. The article of any of the preceding clauses, wherein the polyurethane polymers include polyester polyurethane copolymers.


Clause 66. The article of any of the preceding clauses, wherein the polyurethane polymers consist essentially of polyester polyurethane copolymers.


Clause 67. The article of any of the preceding clauses, wherein the primer layer has a thickness of about 3 to 200 nanometers.


Clause 68. The article of any of the preceding clauses, wherein the primer layer has a color selected from the group consisting of: black, dark brown, dark red, dark orange, dark yellow, dark green, dark cyan, dark blue, dark violet, grey, dark magenta, dark indigo, tones thereof, tints thereof, shades thereof, and a combination thereof.


Clause 69. The article of any of the preceding clauses, wherein the color of the primer layer is different than the color of the structural color.


Clause 70. The article of any of the preceding clauses, wherein the color of the primer layer is different than the color of the structural color under the criteria of any preceding clause.


Clause 71. The article of any of the preceding clauses, wherein the first polymeric material, the second polymer material, both are a thermoplastic material.


Clause 72. The article of any of the preceding clauses, wherein the thermoplastic material is an elastomeric thermoplastic material.


Clause 73. The article of any of the preceding clauses, wherein the thermoplastic material includes one or more thermoplastic polyurethanes.


Clause 74. The article of any of the preceding clauses, wherein the thermoplastic material includes one or more thermoplastic polyurethanes, polyesters, polyamides, polyolefins, or a combination thereof.


Clause 75. The article of any of the preceding clauses, wherein the elastomeric thermoplastic material includes a polyester polyurethane copolymer.


Clause 76. The article of any of the preceding clauses, wherein the first thermoplastic material and the second thermoplastic material comprise thermoplastic polymers of the same polymer type.


Clause 77. The article of any of the preceding clauses, wherein the first thermoplastic material and the second thermoplastic material comprise thermoplastic polymers of different types.


Clause 78. The article of any of the preceding clauses, wherein the first thermoplastic material comprises thermoplastic polyurethanes, optionally elastomeric thermoplastic polyurethanes, or optionally elastomeric thermoplastic polyester polyurethane copolymers.


Clause 79. The article of any of the preceding clauses, wherein the first thermoplastic material comprises thermoplastic polyester polyurethane copolymers.


Clause 80. The article of any preceding article clause, wherein the first bladder wall incudes a barrier membrane including layers of the first thermoplastic material alternating with layers of a third thermoplastic material.


Clause 81. The article of any preceding article clause, wherein the third thermoplastic material includes ethylene vinyl alcohol copolymers.


Clause 82. The article of any of the preceding clauses, wherein the first side of the multi-layer optical film is disposed on the interior-facing side of the first bladder wall, wherein the primer layer is disposed on the second side of the multi-layer optical film.


Clause 83. The article of any of the preceding clauses, wherein the multi-layer optical film is disposed on the exterior-facing side of the first bladder wall, with the primer layer, the textured structure, or both, positioned between the multi-layer optical film and the exterior-facing side of the first bladder wall.


Clause 84. The article of any of the preceding clauses, wherein the bladder includes a component that includes the multi-layer optical film of any of the clauses, optionally a texture surface of any of the clauses, and optionally a primer of any of the clauses in the internal cavity of the bladder.


Clause 85. The article of any of the preceding clauses, wherein the component is selected from a spacer formed of a solid polymeric material, a spacer formed of a foamed polymeric material, a spacer formed of a textile, or a combination thereof.


Clause 86. An article of apparel, comprising a bladder, wherein the bladder is a bladder of any preceding article clause.


Clause 87. An article of sporting equipment comprising a bladder, wherein the bladder is a bladder of any preceding article clause.


Clause 88. An article of footwear, comprising a bladder, wherein the bladder is a bladder of any preceding article clause.


Clause 89. An article of footwear, comprising a sole, wherein the sole includes a bladder of any preceding article clause.


Clause 90. A method of making an article of footwear, apparel or sporting equipment comprising:


affixing a bladder of any preceding article clause to a second element, forming an article of footwear, apparel or sporting equipment.


Clause 91. The method of any of the preceding clauses, wherein the article is an article of footwear comprising the bladder in a sole, further comprising affixing the sole to an upper to form the article of footwear.


Clause 92. The method of any of the preceding clauses, wherein the method further comprises the step(s) of any of the following method clauses.


Clause 93. A method of making a bladder, comprising:


disposing an multi-layer optical film onto an exterior-facing side or an interior-facing side of a first bladder wall of a bladder, the bladder wall having a first bladder wall thickness and a gas transmission rate of 15 cm3/m2·atm·day or less for nitrogen for an average wall thickness of 20 mils, wherein the exterior-facing side comprises a first thermoplastic material and the interior-facing side comprises a second thermoplastic material, wherein the first bladder wall has; wherein the multi-layer optical film has a first side and a second side, wherein the first side and the second side are on opposing sides, wherein the first side or the second side of the multi-layer optical film is disposed on the external-facing side of the bladder wall, or the interior-facing side of the first bladder wall, or on a component in an internal cavity of the bladder; and wherein the first side of the multi-layer optical film, the second side of the multi-layer optical film, or both impart a structural color to the bladder.


Clause 94. The method of any of the preceding clauses, wherein the method further comprises forming the bladder by applying heat, pressure, vacuum, or a combination thereof to a film, forming the bladder, wherein the film has a gas transmission rate of 15 cm3/m2·atm·day or less for nitrogen for an average film thickness of 20 mils;


wherein the step of forming the bladder is conducted prior to or following the disposing the multi-layer optical film onto the exterior-facing side or the internal-facing side of the bladder wall.


Clause 95. The method of any of the preceding clauses, wherein the method further comprises inflating the bladder after the forming the bladder.


Clause 96. The method of any of the preceding clauses, wherein the disposing the multi-layer optical film is conducted prior to inflating the bladder.


Clause 97. The method of any of the preceding clauses, wherein the disposing the multi-layer optical film is conducted on an inflated bladder.


Clause 98. The method of any of the preceding clauses, wherein a temperature of the inflated bladder is maintained at a temperature below a glass transition temperature of the first thermoplastic material during the disposing.


Clause 99. The method of any of the preceding clauses, wherein a temperature of the inflated bladder is maintained at a temperature at or below 80 degrees C. during the disposing.


Clause 100. The method of any of the preceding clauses, wherein the disposing includes disposing the first side of the multi-layer optical film onto the exterior-facing side of the first bladder wall.


Clause 101. The method of any of the preceding clauses, wherein the method further comprises forming a textured surface, a primer layer, or both, on the exterior-facing side of the first bladder wall, or on the interior-facing side of the first bladder wall, prior to the disposing.


Clause 102. The method of any of the preceding clauses, wherein the multi-layer optical film includes a textured surface, a primer layer, or both.


Clause 103. The method of any of the preceding clauses, wherein the disposing includes disposing the first side of the multi-layer optical film onto the interior-facing side of the first bladder wall.


Clause 104. The method of any of the preceding clauses, wherein the interior-facing side of the first bladder wall includes a textured surface.


Clause 105. The method of any of the preceding clauses, wherein the textured surface is part of a textured layer or a textured structure.


Clause 106. The method of any of the preceding clauses, wherein the multi-layer optical film includes the textured layer or textured structure.


Clause 107. The method of any of the preceding clauses, wherein the textured surface is a textured surface according to any preceding article clause.


Clause 108. The method of any of the preceding clauses, wherein the multi-layer optical film is a multi-layer optical film according to any preceding article clause.


Clause 109. The method of any of the preceding clauses, further comprising disposing a primer layer on the exterior-facing side of the first bladder wall or on the interior-facing side of the first bladder wall prior to the disposing the multi-layer optical film; and, the primer layer and the optical layer impart the structural color.


Clause 110. The method of any of the preceding clauses, wherein the exterior-facing side or the interior-facing side includes a textured surface; the method further comprises forming a primer layer on the textured surface prior to the disposing the multi-layer optical film; interior-facingexterior-facinginterior-facingexterior-facingand the textured surface, the primer layer, and the optical layer impart the structural color.


Clause 111. The method of any of the preceding clauses, wherein forming the primer layer comprises forming the primer layer using digital printing, offset printing, pad printing, screen printing, flexographic printing, or heat transfer printing.


Clause 112. The method of any of the preceding clauses, wherein the disposing includes disposing the multi-layer optical film on a component, and the method further comprises placing the structurally colored component within an internal cavity of the bladder prior to inflating the bladder


Clause 113. The method of any of the preceding clauses, wherein the component is selected from a spacer formed of a solid polymeric material, a spacer formed of a foamed polymeric material, a spacer formed of a textile, or a combination thereof.


Clause 114. The method of any preceding method clause, wherein the article is an article of any preceding article clause.


Clause 115. An article, comprising a bladder formed using the methods of 82-99.


Clause 116. An inflated bladder for use in an article of footwear, the inflated bladder comprising:


a bladder wall having an interior-facing side and an exterior-facing side, wherein the interior-facing side defines at least a portion of an interior region of the inflated bladder, and wherein the bladder wall further includes an average wall thickness between the interior-facing side and exterior-facing side that is less than 5 millimeters; and


a multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is operably disposed on the exterior-facing side of the bladder wall, and wherein the multi-layer optical film imparts a structural color to the bladder wall.


Clause 117. The inflated bladder of any of the preceding clause, wherein the bladder wall exhibits a gas transmission rate of 15 cm3/m2·atm·day or less.


Clause 118. The inflated bladder of any of the preceding clause, wherein the bladder wall further comprises alternating first and second polymeric layers, wherein the first polymeric layers each comprise one or more thermoplastic polyurethanes, and wherein the second polymeric layers each comprise one or more thermoplastic ethylene-vinyl alcohol polymers.


Clause 119. The inflated bladder of any of the preceding clause, wherein the bladder wall comprises one or more thermoplastic polyurethanes.


Clause 120. The inflated bladder of any of the preceding clause, wherein the multi-layer optical film comprises:

    • a first layer compositionally comprising a non-oxide metal; and
    • a second layer compositionally comprising a first metal oxide.


      Clause 121. The inflated bladder of any of the preceding clause, and further comprising a third layer compositionally comprising a second metal oxide that is different from the first metal oxide.


      Clause 122. The inflated bladder of any of the preceding clause, wherein the multi-layer optical film comprises:
    • a first layer compositionally comprising a first metal oxide; and
    • a second layer compositionally comprising a second metal oxide different from the first metal oxide.


      Clause 123. The inflated bladder of any of the preceding clause, further comprising a primer layer disposed on the exterior-facing side of the bladder wall, and wherein the first side of the multi-layer optical film is disposed on the primer layer.


      Clause 124. The inflated bladder of any of the preceding clause, wherein the primer layer has a thickness ranging from about 10 to about 100 micrometers.


      Clause 125. A bladder for use in an article of footwear, the bladder comprising:
    • a bladder wall having an interior-facing side and an exterior-facing side, wherein the interior-facing side defines at least a portion of an interior region of the bladder;
    • a plurality of topographical structures extending from the exterior-facing side of the bladder wall; and
    • a multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is disposed on the exterior-facing side of the bladder wall and covering the plurality of topographical structures, and wherein the multi-layer optical film imparts a structural color to the bladder wall.


      Clause 126. The inflated bladder of any of the preceding clause, wherein the multi-layer optical film comprises:
    • a first layer compositionally comprising a first metal oxide, wherein the first layer at least partially conforms to the plurality of topographical structures; and
    • a second layer disposed on the first layer and compositionally comprising a second metal oxide different from the first metal oxide.


      Clause 127. The inflated bladder of any of the preceding clause, and further comprising a gas retained within the interior region of the bladder.


      Clause 128. The inflated bladder of any of the preceding clause, wherein the gas consists essentially of nitrogen.


      Clause 129. The inflated bladder of any of the preceding clause, wherein the bladder wall exhibits a gas transmission rate of 15 cm3/m2·atm·day or less.


      Clause 130. An article of footwear comprising:
    • a footwear upper; and
    • an inflated bladder comprising:
      • a top wall operably secured to the footwear upper;
      • a bottom wall opposite the top wall; and
      • one or more sidewalls extending between the top wall and the bottom wall of the inflated bladder, wherein the top wall, the bottom wall, and the one or more sidewalls collectively define an interior region of the inflated bladder, and wherein the one or more sidewalls each comprise an exterior-facing side; and
    • a multi-layer optical film operably disposed on the exterior-facing side at least one of the one or more sidewalls to impart a structural color to the one or more sidewalls.


      Clause 131. The article of footwear of any of the preceding clauses, wherein the inflated bladder further comprises a plurality of topographical structures extending from the exterior-facing side of at least one of the one or more sidewalls such that the multi-layer optical film covers the plurality of topographical structures.


      Clause 132. The article of footwear of any of the preceding clauses, wherein the multi-layer optical film comprises:
    • a first layer compositionally comprising a first metal oxide, wherein the first layer at least partially conforms to the plurality of topographical structures; and
    • a second layer disposed on the first layer and compositionally comprising a second metal oxide different from the first metal oxide.


      Clause 133. The article of footwear of any of the preceding clauses, wherein the structural color imparted to the one or more sidewalls has a single hue regardless of viewing angle.


      Clause 134. The article of footwear of any of the preceding clauses, wherein the structural color imparted to the one or more sidewalls has a metallic appearance comprises a metallic color.


      Clause 135. The article of footwear of any of the preceding clauses, wherein the structural color imparted to the one or more sidewalls has two or more hues.


      Clause 136. A method of making a bladder, comprising:


disposing an multi-layer optical film onto an exterior-facing side or an interior-facing side of a first bladder wall of a bladder, wherein the interior-facing side defines at least a portion of an interior region of the inflated bladder, and wherein the bladder wall further includes an average wall thickness between the interior-facing side and exterior-facing side that is less than 5 millimeters,


wherein the multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is operably disposed on the exterior-facing side of the bladder wall, and wherein the multi-layer optical film imparts a structural color to the bladder wall.


Clause 137. The method of footwear of any of the preceding clauses, wherein the method further comprises forming the bladder by applying heat, pressure, vacuum, or a combination thereof to a film, forming the bladder;


wherein the step of forming the bladder is conducted prior to or following the operably disposing the multi-layer optical film onto the exterior-facing side or the internal-facing side of the bladder wall.


Clause 138. The method of footwear of any of the preceding clauses, wherein the methods include the articles of the preceding clauses.


Clause 139. A bladder for use in an article of footwear, the bladder comprising:






    • a bladder wall having an interior-facing side and an exterior-facing side, wherein the interior-facing side defines at least a portion of an interior region of the bladder;

    • a plurality of topographical structures extending from the exterior-facing side of the bladder wall; and

    • a multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is disposed on the exterior-facing side of the bladder wall and covering the plurality of topographical structures, and wherein the multi-layer optical film imparts a structural color to the bladder wall.


      Clause 140. A method of making a bladder, comprising:





disposing an multi-layer optical film onto an exterior-facing side or an interior-facing side of a first bladder wall of a bladder, wherein the interior-facing side defines at least a portion of an interior region of the inflated bladder, wherein a plurality of topographical structures extending from the exterior-facing side of the bladder wall, wherein the multi-layer optical film having a first side and a second opposing side, wherein the first side of the multi-layer optical film is disposed on the exterior-facing side of the bladder wall and covering the plurality of topographical structures, and wherein the multi-layer optical film imparts a structural color to the bladder wall.


Clause 141. A method of making an article of footwear comprising:


operably securing an inflated bladder to a top wall of a footwear upper, wherein the bladder comprises the top wall, a bottom wall opposite the top wall; and one or more sidewalls extending between the top wall and the bottom wall of the inflated bladder, wherein the top wall, the bottom wall, and the one or more sidewalls collectively define an interior region of the inflated bladder, and wherein the one or more sidewalls each comprise an exterior-facing side; and a multi-layer optical film operably disposed on the exterior-facing side at least one of the one or more sidewalls to impart a structural color to the one or more sidewalls.


It should be noted that ratios, concentrations, amounts, and other numerical data may be expressed herein in a range format. It is to be understood that such a range format is used for convenience and brevity, and thus, should be interpreted in a flexible manner to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. To illustrate, a concentration range of “about 0.1 percent to about 5 percent” should be interpreted to include not only the explicitly recited concentration of about 0.1 weight percent to about 5 weight percent but also include individual concentrations (e.g., 1 percent, 2 percent, 3 percent, and 4 percent) and the sub-ranges (e.g., 0.5 percent, 1.1 percent, 2.2 percent, 3.3 percent, and 4.4 percent) within the indicated range. The term “about” can include traditional rounding according to significant figures of the numerical value. In addition, the phrase “about ‘x’ to ‘y’” includes “about ‘x’ to about ‘y’”.


Many variations and modifications may be made to the above-described aspects. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.

Claims
  • 1. An article of footwear comprising: a footwear upper; andan inflated bladder comprising: a top wall operably secured to the footwear upper;a bottom wall opposite the top wall; andone or more sidewalls extending between the top wall and the bottom wall of the inflated bladder, wherein the top wall, the bottom wall, and the one or more sidewalls collectively define an interior region of the inflated bladder, and wherein the one or more sidewalls each comprise an interior-facing side and an exterior-facing side; anda multi-layer optical film operably disposed on the interior-facing side or exterior-facing side of at least one of the one or more sidewalls to impart a structural color having at least one hue to the one or more sidewalls;wherein the exterior-facing side or the interior-facing side of the first bladder wall, or the first side or the second side of the multi-layer optical film, or any combination thereof, comprise a textured surface, and a combination of the textured surface and the multi-layer optical film impart the structural color.
  • 2. The article of claim 1, wherein the multi-layer optical film comprises the textured surface.
  • 3. The article of claim 1, wherein the multi-layer optical film includes a pigment, a dye, or a combination of pigment and dye.
  • 4. The article of claim 1, wherein the multi-layer optical film comprises: a first layer compositionally comprising a non-oxide metal; and a second layer disposed on the first layer and compositionally comprising a first metal oxide.
  • 5. The article of footwear of claim 1, wherein the structural color imparted to the one or more sidewalls has a single hue regardless of viewing angle.
  • 6. The article of footwear of claim 1, wherein the structural color imparted to the one or more sidewalls has two or more hues.
  • 7. The article of claim 1, wherein the textured surface is part of a textured layer or a textured structure.
  • 8. The article of claim 7, wherein the textured surface, the textured layer or the textured structure is on the first side of the multi-layer optical film, and wherein the first side of the multi-layer optical film is disposed onto the exterior-facing surface of the first bladder wall.
  • 9. The article of claim 7, wherein the textured surface, the textured layer or the textured structure is on the second side of the multi-layer optical film, wherein the first side of the multi-layer optical film is disposed onto the interior-facing surface of the first bladder wall.
  • 10. The article of claim 1, wherein the textured surface has a plurality of topographical structures and plurality of flat areas.
  • 11. The article of claim 10, wherein, over an area of the textured surface having a surface area of at least 5 square millimeters, wherein the topographical structures are in random positions relative to one another.
  • 12. The article of claim 3, wherein the dye is an acid dye.
  • 13. The article of claim 3, wherein the pigment is a solid pigment particle selected from the group consisting of: metal and metal oxide pigments, carbon pigments, clay earth pigments, ultramarine pigments and a combination thereof.
  • 14. The article of claim 1, wherein a primer layer is disposed on the textured surface.
  • 15. The article of claim 14, wherein the primer layer is on the exterior-facing side of the bladder wall or on the interior-facing side of the bladder wall, and the multi-layer optical film is disposed on the primer layer.
  • 16. The article of claim 14, wherein the multi-layer optical film is disposed on the first thermoplastic material of the exterior-facing side or the second thermoplastic material of the interior-facing side of the bladder wall, with the primer layer, the textured surface, or both, positioned between the multi-layer optical film and the first thermoplastic material.
  • 17. The article of claim 14, wherein the primer layer comprises a textured surface, and the textured surface of the primer layer, the primer layer, and the multi-layer optical film impart the structural color.
  • 18. The article of claim 14, wherein the primer layer is a digitally printed layer, an offset printed layer, a pad printed layer, a screen printed layer, a flexographically printed layer, or a heat transfer printed layer.
  • 19. The article of claim 14, wherein the primer layer comprises a paint, an ink, or a combination thereof.
  • 20. The article of claim 14, wherein the primer layer comprises a reground, and at least partially degraded polymer.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No. 16/825,629, having the title “STRUCTURALLY-COLORED ARTICLES AND METHODS FOR MAKING AND USING STRUCTURALLY-COLORED ARTICLES”, filed Mar. 20, 2020, which is a divisional of U.S. application Ser. No. 16/146,614, having the title “STRUCTURALLY-COLORED ARTICLES AND METHODS FOR MAKING AND USING STRUCTURALLY-COLORED ARTICLES”, filed on Sep. 28, 2018, now U.S. Pat. No. 10,732,322, which application claims the benefit of and priority to U.S. Provisional Application Ser. No. 62/633,666, having the title “ARTICLES HAVING STRUCTURAL COLOR AND METHODS AND SYSTEMS FOR MAKING ARTICLES HAVING STRUCTURAL COLOR”, filed on Feb. 22, 2018, and to U.S. Provisional Application Ser. No. 62/565,299, having the title “STRUCTURALLY COLORED ARTICLES AND METHODS OF MAKING STRUCTURALLY COLORED ARTICLES”, filed on Sep. 29, 2017, and to U.S. Provisional Application Ser. No. 62/565,306, having the title “STRUCTURALLY COLORED STRUCTURES AND ARTICLES, METHODS OF MAKING STRUCTURES AND ARTICLES”, filed on Sep. 29, 2017, and to U.S. Provisional Application Ser. No. 62/565,313, having the title “STRUCTURES HAVING STRUCTURAL COLOR AND METHODS AND SYSTEMS FOR MAKING STRUCTURES HAVING STRUCTURAL COLOR”, filed on Sep. 29, 2017, and U.S. Provisional Application Ser. No. 62/565,310, having the title “STRUCTURES HAVING STRUCTURAL COLOR AND METHODS AND SYSTEMS FOR MAKING STRUCTURES HAVING STRUCTURAL COLOR”, filed on Sep. 29, 2017, the disclosures which are incorporated herein by reference in their entireties.

US Referenced Citations (279)
Number Name Date Kind
2345533 Graves Mar 1944 A
2394533 Colbert Feb 1946 A
2607130 Pearson Aug 1952 A
2712190 Sobel Jul 1955 A
2929803 Frazer et al. Mar 1960 A
3011383 Sylvester et al. Dec 1961 A
3060513 Klink et al. Oct 1962 A
3338730 Slade et al. Aug 1967 A
3376403 Driga Apr 1968 A
3698930 Fleurquin et al. Oct 1972 A
3822488 Johnson Jul 1974 A
4231369 Sorensen et al. Nov 1980 A
4300294 Riecken Nov 1981 A
4523005 Szycher Jun 1985 A
4533592 Bingham Aug 1985 A
4705356 Berning Nov 1987 A
5009486 Dobrowolski et al. Apr 1991 A
5269995 Ramanathan et al. Dec 1993 A
5334690 Schafheutle et al. Aug 1994 A
5346934 Chriss Sep 1994 A
5500067 Jenkner Mar 1996 A
5572817 Chien Nov 1996 A
5628128 Miller et al. May 1997 A
5671495 Chen Sep 1997 A
5713141 Mitchell et al. Feb 1998 A
5722322 Watanabe Mar 1998 A
5778793 Mello et al. Jul 1998 A
5813148 Guerra Sep 1998 A
5815950 Wang Oct 1998 A
5825548 Bornhorst et al. Oct 1998 A
5928456 Souparis Jul 1999 A
5930921 Sorofman et al. Aug 1999 A
5952065 Mitchell et al. Sep 1999 A
5969076 Lai et al. Oct 1999 A
5979078 McLaughlin Nov 1999 A
6013340 Bonk et al. Jan 2000 A
6082025 Bonk et al. Jul 2000 A
6127026 Bonk et al. Oct 2000 A
6147726 Kubota et al. Nov 2000 A
6157489 Bradley, Jr. et al. Dec 2000 A
6164777 Li et al. Dec 2000 A
6203868 Bonk et al. Mar 2001 B1
6321465 Bonk et al. Nov 2001 B1
6402879 Tawney et al. Jun 2002 B1
6551531 Ford et al. Apr 2003 B1
6666983 Marietti et al. Dec 2003 B2
6761959 Bonkowski et al. Jul 2004 B1
6897281 Lubnin et al. May 2005 B2
6922906 Choi et al. Aug 2005 B2
7006294 Steenblik et al. Feb 2006 B2
7405879 Wild et al. Jul 2008 B2
7476705 Pajerski Jan 2009 B2
7800814 Nishimura et al. Sep 2010 B2
7848008 Nishimura et al. Dec 2010 B2
7903339 Banerjee et al. Mar 2011 B2
7955695 Argoitia Jun 2011 B2
8264637 Cho et al. Sep 2012 B2
8322636 Wu et al. Dec 2012 B2
8339597 Dal Negro et al. Dec 2012 B2
8408470 Komatsu et al. Apr 2013 B2
8486494 Fukazawa et al. Jul 2013 B2
8558137 Yuasa et al. Oct 2013 B2
8685185 Guo et al. Apr 2014 B2
8889234 Kwon et al. Nov 2014 B2
9102195 Raksha et al. Aug 2015 B2
9134468 Noizet et al. Sep 2015 B2
9185947 Spencer Nov 2015 B2
9220951 Comeau Dec 2015 B1
9279771 Aizenberg et al. Mar 2016 B2
9420848 Campos, II et al. Aug 2016 B2
9453943 Miyake et al. Sep 2016 B2
9527340 Szumski et al. Dec 2016 B2
9557457 Gocho et al. Jan 2017 B2
9931804 Le et al. Apr 2018 B2
10048411 Parker Aug 2018 B2
10555580 Peyton Feb 2020 B2
10649113 Bee et al. May 2020 B2
10779617 Iovu Sep 2020 B2
10928553 Bee et al. Feb 2021 B2
11129444 Kovel Sep 2021 B1
11241062 Bee et al. Feb 2022 B1
11254095 Hart et al. Feb 2022 B2
11412817 Kovel Aug 2022 B2
20010028921 Shaw et al. Oct 2001 A1
20010042321 Tawney et al. Nov 2001 A1
20010053454 Higashi et al. Dec 2001 A1
20020015836 Jonza et al. Feb 2002 A1
20020028311 Coppens et al. Mar 2002 A1
20020150629 Nishimura et al. Oct 2002 A1
20020183133 Sano Dec 2002 A1
20020191234 Ishimoto et al. Dec 2002 A1
20030074808 Weaver et al. Apr 2003 A1
20030086030 Taniguchi et al. May 2003 A1
20040006889 Chen Jan 2004 A1
20040135921 Murata et al. Jul 2004 A1
20040142185 Takushima Jul 2004 A1
20040169928 Nilsen et al. Sep 2004 A1
20040172855 Aslanides Sep 2004 A1
20040173855 Masuoka et al. Sep 2004 A1
20040265587 Koyanagi et al. Dec 2004 A1
20050016026 Long Jan 2005 A1
20050031816 Chang et al. Feb 2005 A1
20050056954 Devlin et al. Mar 2005 A1
20050063067 Phillips et al. Mar 2005 A1
20050207007 Shimoda et al. Sep 2005 A1
20050207138 Cheung Sep 2005 A1
20050211114 Fahrenbach et al. Sep 2005 A1
20050260369 Graf et al. Nov 2005 A1
20050268497 Alfaro et al. Dec 2005 A1
20050274041 Collett et al. Dec 2005 A1
20060023327 Coombs et al. Feb 2006 A1
20060048413 Sokolowski et al. Mar 2006 A1
20060090373 Savoie et al. May 2006 A1
20060101671 Berend et al. May 2006 A1
20060101673 Robinson et al. May 2006 A1
20060112599 Braynock et al. Jun 2006 A1
20060128823 Tsuchimura et al. Jun 2006 A1
20060143951 Yang et al. Jul 2006 A1
20060198121 Thorpe et al. Sep 2006 A1
20060270553 Mori Nov 2006 A1
20070008439 Nakayama et al. Jan 2007 A1
20070058260 Steenblik et al. Mar 2007 A1
20070076069 Edwards et al. Apr 2007 A1
20080040951 Kates Feb 2008 A1
20080066347 Suzuki Mar 2008 A1
20080248281 Nakaguma et al. Oct 2008 A1
20080274359 Lawrence et al. Nov 2008 A1
20080316628 Nakajima et al. Dec 2008 A1
20090080076 Fujikura et al. Mar 2009 A1
20090174944 Yuasa et al. Jul 2009 A1
20090301649 Augsberg et al. Dec 2009 A1
20100024597 Dover et al. Feb 2010 A1
20100104810 Fukazawa et al. Apr 2010 A1
20100152065 Nishimura et al. Jun 2010 A1
20100177380 Nagahama et al. Jul 2010 A1
20100199406 Dua et al. Aug 2010 A1
20100215976 Suwa et al. Aug 2010 A1
20100222442 Prissok et al. Sep 2010 A1
20100254007 Toda Oct 2010 A1
20100266946 Shirai et al. Oct 2010 A1
20100290109 Kurt et al. Nov 2010 A1
20100291358 Takahashi et al. Nov 2010 A1
20110026208 Utsuro et al. Feb 2011 A1
20110033670 Nishikawa et al. Feb 2011 A1
20110043911 Kaneiwa et al. Feb 2011 A1
20110090564 Utsuro et al. Apr 2011 A1
20110123754 Shirai et al. May 2011 A1
20110171440 Cheng et al. Jul 2011 A1
20110183111 Yuasa et al. Jul 2011 A1
20110234953 Amimori Sep 2011 A1
20110234969 Amimori Sep 2011 A1
20110253288 Xie et al. Oct 2011 A1
20110262675 Inamiya et al. Oct 2011 A1
20110298207 Despland et al. Dec 2011 A1
20120015118 Zheludev et al. Jan 2012 A1
20120015145 Depres Jan 2012 A1
20120019913 Nishimoto et al. Jan 2012 A1
20120034291 Amsden et al. Feb 2012 A1
20120121820 Cronin-Golomb et al. May 2012 A1
20120133672 Joo May 2012 A1
20120139230 Whiteman et al. Jul 2012 A1
20120186102 Lee et al. Jul 2012 A1
20120204443 Vertuccio Aug 2012 A1
20120231489 Lenhert Sep 2012 A1
20120236415 Nagano et al. Sep 2012 A1
20120249718 Sohn et al. Oct 2012 A1
20120255201 Little Oct 2012 A1
20120255452 Bower et al. Oct 2012 A1
20120297642 Schaefer et al. Nov 2012 A1
20120297643 Shaffer et al. Nov 2012 A1
20130004721 Hara et al. Jan 2013 A1
20130004722 Hara et al. Jan 2013 A1
20130004731 Hara et al. Jan 2013 A1
20130004754 Hara et al. Jan 2013 A1
20130148221 Banerjee et al. Jun 2013 A1
20130182300 Müller et al. Jul 2013 A1
20130183487 Henze et al. Jul 2013 A1
20130243693 Omenei et al. Sep 2013 A1
20130250229 Kaneiwa et al. Sep 2013 A1
20130330710 Amsden et al. Dec 2013 A1
20140016177 Aizenberg et al. Jan 2014 A1
20140020192 Jones et al. Jan 2014 A1
20140050899 Kukoff Feb 2014 A1
20140104686 Yuasa et al. Apr 2014 A1
20140106139 Abrams Apr 2014 A1
20140109442 Thompson Apr 2014 A1
20140118360 Ma et al. May 2014 A1
20140161974 Erho et al. Jun 2014 A1
20140182169 Mack Jul 2014 A1
20140250734 Zheng Sep 2014 A1
20140254017 Manoharan et al. Sep 2014 A1
20150001840 Parker Jan 2015 A1
20150035269 Hooper et al. Feb 2015 A1
20150076808 Kim et al. Mar 2015 A1
20150109657 Baumberg et al. Apr 2015 A1
20150118124 Khorasaninejad et al. Apr 2015 A1
20150146280 Degott et al. May 2015 A1
20150192897 Schilling et al. Jul 2015 A1
20150202834 Free et al. Jul 2015 A1
20150212244 Kim et al. Jul 2015 A1
20150250263 Robinson, Jr. Sep 2015 A1
20150283743 Park et al. Oct 2015 A1
20150309232 Banerjee Oct 2015 A1
20150352883 Schmid et al. Dec 2015 A1
20150352888 Schmid et al. Dec 2015 A1
20160064696 Collier et al. Mar 2016 A1
20160101601 Abrams Apr 2016 A1
20160116645 Parker Apr 2016 A1
20160128433 Downing et al. May 2016 A1
20160131808 Kristensen et al. May 2016 A1
20160146984 Jiang et al. May 2016 A1
20160168386 Aizenberg et al. Jun 2016 A1
20160176223 Degott et al. Jun 2016 A1
20160178493 Kawanaka et al. Jun 2016 A1
20160202394 Clausen et al. Jul 2016 A1
20160202401 Christiansen et al. Jul 2016 A1
20160209642 Aizenberg et al. Jul 2016 A1
20160209678 Nishimoto Jul 2016 A1
20160282527 Saito et al. Sep 2016 A1
20160325310 Schmid et al. Nov 2016 A1
20160327708 Liles et al. Nov 2016 A1
20160331082 Weidl Nov 2016 A1
20170020232 Bello Decurnex Jan 2017 A1
20170023711 Jiang et al. Jan 2017 A1
20170027273 Colon Feb 2017 A1
20170081535 Kohri et al. Mar 2017 A1
20170087691 Yokoyama et al. Mar 2017 A1
20170090084 Wilson et al. Mar 2017 A1
20170129200 Adami et al. May 2017 A1
20170157653 Parker Jun 2017 A1
20170248746 Banerjee et al. Aug 2017 A1
20170347745 Figur et al. Dec 2017 A1
20180252158 Malkamäki et al. Sep 2018 A1
20180257360 Liponkoski Sep 2018 A1
20180284330 Parker Oct 2018 A1
20180357316 Neuvonen et al. Dec 2018 A1
20180372929 Parker Dec 2018 A1
20190098946 Bee et al. Apr 2019 A1
20190098958 Bee et al. Apr 2019 A1
20190099967 Bee et al. Apr 2019 A1
20190099968 Bee et al. Apr 2019 A1
20190099978 Bee et al. Apr 2019 A1
20190099979 Bee et al. Apr 2019 A1
20190113655 Bee et al. Apr 2019 A1
20190113656 Bee et al. Apr 2019 A1
20190163011 Cao May 2019 A1
20190346603 Sahara et al. Nov 2019 A1
20190365047 Larson et al. Dec 2019 A1
20190387830 Dua et al. Dec 2019 A1
20200018876 Chen et al. Jan 2020 A1
20200040882 Kalmari et al. Feb 2020 A1
20200088908 Bee et al. Mar 2020 A1
20200113287 Johnson et al. Apr 2020 A1
20200181550 Kalmari et al. Jun 2020 A1
20200217986 Bee et al. Jul 2020 A1
20200217987 Bee et al. Jul 2020 A1
20200240667 Lind Jul 2020 A1
20200269561 Bee et al. Aug 2020 A1
20200275728 Bee et al. Sep 2020 A1
20200290311 Kim et al. Sep 2020 A1
20200305526 Gantz et al. Oct 2020 A1
20200305527 Gantz et al. Oct 2020 A1
20200308734 Gantz et al. Oct 2020 A1
20200314185 Mäkynen et al. Oct 2020 A1
20200371272 Bee et al. Nov 2020 A1
20200407838 Gantz et al. Dec 2020 A1
20210096289 Guo et al. Apr 2021 A1
20210177096 Park et al. Jun 2021 A1
20210186157 Capone et al. Jun 2021 A1
20210215864 Kawashita Jul 2021 A1
20210244131 Capone et al. Aug 2021 A1
20210373214 Gantz et al. Dec 2021 A1
20210382201 Bee et al. Dec 2021 A1
20220039504 Bee et al. Feb 2022 A1
20220039505 Bee et al. Feb 2022 A1
20220039519 Kovel et al. Feb 2022 A1
20220061450 Bee et al. Mar 2022 A1
20220066079 Trottier-Lapointe et al. Mar 2022 A1
20220107443 Bee et al. Apr 2022 A1
Foreign Referenced Citations (123)
Number Date Country
2007200128 Aug 2007 AU
PI0503224 Jan 2007 BR
702116 May 2011 CH
1324222 Nov 2001 CN
1799857 Jul 2006 CN
101356245 Jan 2009 CN
101381903 Mar 2009 CN
101396884 Apr 2009 CN
101633786 Jan 2010 CN
101666886 Mar 2010 CN
101781860 Jul 2010 CN
102548752 Jul 2012 CN
102691202 Sep 2012 CN
103173039 Jun 2013 CN
103965699 Aug 2014 CN
104334042 Feb 2015 CN
104592971 May 2015 CN
105050442 Nov 2015 CN
105271796 Jan 2016 CN
105862000 Aug 2016 CN
106080001 Nov 2016 CN
107111002 Aug 2017 CN
4307648 Sep 1994 DE
20200346 Apr 2002 DE
102010025159 Dec 2011 DE
0335309 Oct 1989 EP
0905530 Mar 1999 EP
1047961 Nov 2000 EP
1379900 Jan 2004 EP
1560416 Aug 2005 EP
1624026 Feb 2006 EP
1653256 May 2006 EP
1923229 May 2008 EP
2012148 Jan 2009 EP
2077459 Jul 2009 EP
2462908 Jun 2012 EP
2508922 Oct 2012 EP
2538247 Dec 2012 EP
2642321 Sep 2013 EP
3151042 Apr 2017 EP
3244240 Nov 2017 EP
3278150 Feb 2018 EP
3290968 Mar 2018 EP
1358710 Jul 1974 GB
2374818 Oct 2002 GB
2481697 Jan 2012 GB
2524840 Oct 2015 GB
2525020 Oct 2015 GB
S601180 Jan 1985 JP
2001516272 Sep 2001 JP
2002524317 Aug 2002 JP
2002530712 Sep 2002 JP
2005153192 Jun 2005 JP
2005174647 Jun 2005 JP
2005226196 Aug 2005 JP
2006288907 Oct 2006 JP
2008515491 May 2008 JP
2009205123 Sep 2009 JP
2009211077 Sep 2009 JP
2010111974 May 2010 JP
2010201652 Sep 2010 JP
20110859 Apr 2011 JP
2011104931 Jun 2011 JP
2012159589 Aug 2012 JP
2013-041027 Feb 2013 JP
2013029805 Feb 2013 JP
2013080049 May 2013 JP
2014189719 Oct 2014 JP
2015069076 Apr 2015 JP
5740937 Jul 2015 JP
2015520044 Jul 2015 JP
2015529136 Oct 2015 JP
2016502470 Jan 2016 JP
2017032409 Feb 2017 JP
101472929 Dec 2014 KR
200628089 Aug 2006 TW
9701972 Jan 1997 WO
2000031571 Jun 2000 WO
2003046039 Jun 2003 WO
03068525 Aug 2003 WO
2003095657 Nov 2003 WO
2007037393 Apr 2007 WO
2007038097 Apr 2007 WO
2007096914 Aug 2007 WO
2008076339 Jun 2008 WO
2008156138 Dec 2008 WO
2009062341 May 2009 WO
2010047322 Apr 2010 WO
2010119248 Oct 2010 WO
2011161482 Dec 2011 WO
2012055105 May 2012 WO
2013151547 Oct 2013 WO
2014022049 Feb 2014 WO
2014059424 Apr 2014 WO
2014117673 Aug 2014 WO
2014133514 Sep 2014 WO
2015051367 Apr 2015 WO
2015079652 Jun 2015 WO
2015151479 Oct 2015 WO
2015170120 Nov 2015 WO
2015195123 Dec 2015 WO
2016015973 Feb 2016 WO
2016092014 Jun 2016 WO
2016103980 Jun 2016 WO
2016140779 Sep 2016 WO
2016156863 Oct 2016 WO
2016164551 Oct 2016 WO
2016191255 Dec 2016 WO
2016193252 Dec 2016 WO
2017006314 Jan 2017 WO
2017032928 Mar 2017 WO
2017041085 Mar 2017 WO
2017115806 Jul 2017 WO
2017151496 Sep 2017 WO
2018130856 Jul 2018 WO
2018160866 Sep 2018 WO
2019038560 Feb 2019 WO
2019067969 Apr 2019 WO
2019086770 May 2019 WO
2019224426 Nov 2019 WO
2020013229 Jan 2020 WO
2020030844 Feb 2020 WO
2020197774 Oct 2020 WO
Non-Patent Literature Citations (94)
Entry
International Search Report and Written Opinion for PCT/US2021/072456, dated Mar. 17, 2022.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034776, dated Mar. 29, 2022.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034876, dated Mar. 25, 2022.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034897, dated Mar. 29, 2022.
International Preliminary Report on Patentability for PCT/US2021/034880, dated Aug. 17, 2022.
International Preliminary Report on Patentability for PCT/US2021/034865, dated Aug. 17, 2022.
International Preliminary Report on Patentability for PCT/US2021/034897, dated Aug. 12, 2022.
International Preliminary Report on Patentability for PCT/US2021/034876, dated Aug. 12, 2022.
International Preliminary Report on Patentability for PCT/US2021/034891, dated Aug. 12, 2022.
International Preliminary Report on Patentability for PCT/US2021/034872, dated Aug. 17, 2022.
International Preliminary Report on Patentability for PCT/US2021/034888, dated Aug. 12, 2022.
International Preliminary Report on Patentability for PCT/US2021/034781, dated Aug. 12, 2022.
International Preliminary Report on Patentability for PCT/US2021/034921, dated Aug. 17, 2022.
International Preliminary Report on Patentability for PCT/US2021/044893 dated Jun. 17, 2022.
International Preliminary Report on Patentability for PCT/US2021/044890 dated Jul. 6, 2022.
International Preliminary Report on Patentability for PCT/US2021/044894 dated Jul. 6, 2022.
International Preliminary Report on Patentability for PCT/US2021/044891 dated Jul. 6, 2022.
Color—www.dictionary.com, Jun. 2, 2020 (Year: 2020).
CreatexColorsCo: “How To Paint a Candy Fade” YouTube, Mar. 7, 2020 (Mar. 7, 2020), XP054982299, Retrieved from the Internet: URL:https://www.youtube.com/watch?v=q3UyGEkxEHk&ab channel=CreatexColorsCo [retrieved on Sep. 6, 2021].
Dwyer, Ross, “Stranger Things × Nike “Upside Down” Collection Release Date”, SneakerNews.com Available Online at: https://sneakernews.com/2019/08/12/stranger-things-nike-upside-down-collection-release-date/, Aug. 12, 2019, 5 pages.
International Preliminary Report for PCT/US2020/055543, dated Jan. 25, 2022.
International Preliminary Report on Patentability for PCT/US2018/053467 dated on Dec. 17, 2019.
International Preliminary Report on Patentability for PCT/US2018/053478 dated Mar. 31, 2020.
International Preliminary Report on Patentability for PCT/US2018/053488 dated Mar. 31, 2020.
International Preliminary Report on Patentability for PCT/US2018/053510 dated Dec. 20, 2019.
International Preliminary Report on Patentability for PCT/US2018/053516 dated Mar. 31, 2020.
International Preliminary Reporton Patentability for PCT/US2018/053521 dated Sep. 3, 2019.
International Preliminary Reporton Patentability for PCT/US2020/022148 dated Sep. 29, 2021.
International Preliminary Report on Patentability for PCT/US2020/043271 dated Nov. 8, 2021.
International Preliminary Report on Patentability for PCTUS2014015275 dated Mar. 23, 2015.
International Preliminary Report on Patentability for PCTUS2018053529 dated Dec. 18, 2019.
International Search Report and Written Opinion for PCT application No. PCT/US2021/044890, dated Nov. 12, 2021.
International Search Report and Written Opinion for PCT application No. PCT/US2021/044891, dated Nov. 11, 2021.
International Search Report and Written Opinion for PCT/US2018/053478 dated Jun. 4, 2019.
International Search Report and Written Opinion for PCT/US2018/053502 dated May 28, 2019.
International Search Report and Written Opinion for PCT/US2020/022129 dated Jun. 8, 2020.
International Search Report and Written Opinion for PCT/US2020/022148 dated Jul. 15, 2020.
International Search Report and Written Opinion for PCT/US2020/043271 dated Oct. 30, 2020.
International Search Report and Written Opinion for PCT/US2020/043273 dated Oct. 8, 2020.
International Search Report and Written Opinion for PCT/US2020/044624 dated Oct. 30, 2020.
International Search Report and Written Opinion for PCT/US2020/044626 dated Oct. 30, 2020.
International Search Report and Written Opinion for PCT/US2020/044628 dated Oct. 30, 2020.
International Search Report and Written Opinion for PCT/US2020/055543 dated Feb. 5, 2021.
International Search Report and Written Opinion for PCT/US2020/056300 dated Feb. 16, 2021.
International Search Report and Written Opinion for PCT/US2021/034776 dated Nov. 17, 2021.
International Search Report and Written Opinion for PCT/US2021/034781 dated Sep. 24, 2021.
International Search Report and Written Opinion for PCT/US2021/034865 dated Oct. 5, 2021.
International Search Report and Written Opinion for PCT/US2021/034872 dated Oct. 5, 2021.
International Search Report and Written Opinion for PCT/US2021/034876, dated Jan. 3, 2022.
International Search Report and Written Opinion for PCT/US2021/034880, dated Jan. 3, 2022.
International Search Report and Written Opinion for PCT/US2021/034888, dated Jan. 4, 2022.
International Search Report and Written Opinion for PCT/US2021/034891, dated Jan. 3, 2022.
International Search Report and Written Opinion for PCT/US2021/034897, dated Jan. 3, 2022.
International Search Report and Written Opinion for PCT/US2021/034921 dated Oct. 7, 2021.
International Search Report and Written Opinion received for PCT Patent Application No. PCT/US2014/015275, dated Jun. 25, 2014, 11 pages.
International Search Report and Written Opinion received for PCT Patent Application No. PCT/US2021/044893, dated Nov. 16, 2021.
International Search Report and Written Opinion received for PCT Patent Application No. PCT/US2021/044894, dated Nov. 11, 2021.
International Search Report for PCT/2020/022099 dated Jun. 22, 2020.
International Search Report for PCT/US2018/053467 dated Jun. 3, 2019.
International Search Report for PCT/US2018/053488 dated Jun. 4, 2019.
International Search Report for PCT/US2018/053502 dated Mar. 31, 2020.
International Search Report for PCT/US2018/053510 dated May 29, 2019.
International Search Report for PCT/US2018/053516 dated May 31, 2019.
International Search Report for PCT/US2018/053521 dated Jun. 3, 2019.
International Search Report for PCT/US2018/053529 dated Jan. 28, 2019.
International Search Report for PCT/US2020/022109 dated Jul. 13, 2020.
Iohara et al: “Structurally Colored Fibers”, Chemical Fibers International, vol. 50, No. 1, Feb. 1, 2000 (Feb. 1, 2000), p. 38/39, XP000908694, ISSN: 0340-3343.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034781, dated Feb. 16, 2022.
International Preliminary Report on Patentability for PCT/US2020/055543, dated Jan. 25, 2022.
International Preliminary Report on Patentability for PCT/US2020/056300, dated Feb. 17, 2022.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034880, dated Apr. 7, 2022.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034888, dated Apr. 7, 2022.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034891, dated Apr. 7, 2022.
Masanori Iwata et al., Bio-Inspired Bright Structurally Colored Colloidal Amorphous Array Enhanced by Controlling Thickness and Black Background, Advanced Materials, Feb. 21, 2017, 1-8, 1605050, Germany.
Nike's New Air Force 1 “Reveal” Comes With DIY Tear-Away Uppers, hypebeast.com, Available online at: https://hypebeast.com/2021/2/nike-air-force-1-low-reveal-fauna-brown-arctic-punch-pale-vanilla-dj9941-244-info, Feb. 8, 2021, 10 pages.
Northman, Tora, “Nike's Latest Air Force 1 Reveals Hidden Colors”, hypebae.com, Available online at: https://hypebae.com/2020/4/nike-air-force-1-reveal-diy-peel-sneakers-hidden-colors, Apr. 25, 2020, 9 pages.
Ruiz, Derick, “The Nike Air Force 1 “Reveal” Drops This Week”, www.modern-notoriety.com, Available online at https://www.modem-notoriety.com/nike-wmns-air-force-1-air-max-98-lx-tear-away-release-date/, May 23, 2020, 20 pages.
Texture—www.vocabulary.com, Jun. 2, 2020 (Year: 2020).
The ‘Stranger Things’ x Nike “Upside Down”Pack, hypebeast.com, Available online at: https://hypebeast.com/2019/8/stranger-things-nike-upside-down-pack-tailwind-cortez-mid-blazer-sail-deep-royal-blue-release-info, Aug. 7, 2019, 12 pages.
TOPAS: Cycloolefin Copolymer (COC) Brochure. TOPAS Advanced Polymers. Retrieved online Jan. 11, 2021 from https://topas.com/sites/default/files/files/topas_product-brochure_english.pdf. Published 2008. (Year: 2008).
Written Opinion for PCT/US2021/034872, dated Dec. 9, 2021.
Written Opinion of the International Preliminary Examining Authority for PCT/2020/022099 dated Dec. 1, 2020.
Written Opinion of the International Preliminary Examining Authority for PCT/US2018/053510 dated Sep. 24, 2019.
Written Opinion of the International Preliminary Examining Authority for PCT/US2020/022109 dated Dec. 16, 2020.
Written Opinion of the International Preliminary Examining Authority for PCT/US2020/022129 dated Nov. 13, 2020.
Written Opinion of the International Preliminary Examining Authority for PCT/US2020/022148 dated Oct. 13, 2020.
Written Opinion of the International Preliminary Examining Authority for PCT/US2020/043271 dated Feb. 11, 2021.
Written Opinion of the International Preliminary Examining Authority for PCT/US2020055543, dated May 12, 2021.
Written Opinion of the International Preliminary Examining Authority for PCT/US2021/034865 dated Dec. 23, 2021.
Written Opinion of the International Preliminary Examining Report for PCTUS2018053529 dated Aug. 6, 2019.
International Search Report and Written Opinion for PCT/US2022/071922, dated Aug. 31, 2022.
International Search Report and Written Opinion for PCT/US2022/071918, dated Sep. 21, 2022.
International Search Report and Written Opinion for PCT/US2022/071920, dated Oct. 20, 2022.
“Need Shoes In Two Different Sizes? It's Not As Odd As You'd Think”, GBH News, URL: https://www.wgbh.org/news/lifestyle/2018/09/13/need-shoes-in-two-different-sizes-its-not-as-odd-as-youd-think, Accessed Dec. 13, 2022, Published at least as of Sep. 13, 2018 (Year: 2018).
Related Publications (1)
Number Date Country
20220155489 A1 May 2022 US
Provisional Applications (5)
Number Date Country
62633666 Feb 2018 US
62565306 Sep 2017 US
62565310 Sep 2017 US
62565299 Sep 2017 US
62565313 Sep 2017 US
Divisions (1)
Number Date Country
Parent 16146614 Sep 2018 US
Child 16825629 US
Continuations (1)
Number Date Country
Parent 16825629 Mar 2020 US
Child 17649853 US