Structure having embedded flush circuitry features and method of fabricating

Abstract

Embedded flush circuitry features are provided by depositing a conductive seed layer on the front side of a sacrificial carrier; plating a layer of conductive metal onto the seed layer and personalizing circuitry features. The front side of the carrier film is embedded into a dielectric material and the sacrificial carrier film is removed.

Description

FIELD OF THE INVENTION

The present invention relates to providing a structure having circuitry features and in particular to embedded flush circuitry features. The present invention is especially advantageous for fabricating buried interconnection levels that are in close proximity to one another in a printed circuit board structure.

BACKGROUND OF THE INVENTION

Printed circuit boards find a wide variety of uses in the electronics industry with the demand for high performance, printed wiring, or circuit boards for various applications steadily increasing. For instance, the complexity, compactness and electrical performance requirements of printed boards have significantly increased over the last several years.

The demands on printed circuit boards require high density packaging, fine interconnection, multilayer formation and the need to form a plurality of interconnections in a small space.

Currently, printed circuit board interconnection levels are built on top of a dielectric thin film layer. Circuitry features are formed using photolithographic and subtractive etch techniques. In a typical method, a metallic foil and especially copper foil is laminated to the substrate followed by using photolithographic and subtractive etching to create the circuitry. The copper foil includes a roughened or dendritic backside surface for inducing mechanical adhesion to the substrate. Smooth copper layers do not adequately bond without an auxiliary bonding agent.

Great difficulties exist in adequately etching dendrites especially when dealing with small spaces. Moreover, along with the concern created by dendrites, the width of the lines (e.g. about 0.5 mils wide), and photolithographic issues (e.g. resolution of fine features, 0.7 mil wire with 1.1 mil space, in a thin photo resist film), and subtractive etch undercut/pad rounding, render clearly and fully resolving small line spaces such as the 1.8 mil pitch features presently desired very difficult. Additionally, this subtractive etch approach results in unprotected circuitry features referred to as “skyscrapers” that extend above an underlying plane of dielectric barrier material.

In many structures, it is important to plate another metal such as gold or nickel gold onto the copper circuitry. The “skyscraper” structure causes a problem of bridging or shorting between lines especially where there exist closely spaced features.

SUMMARY OF THE INVENTION

The present invention provides for obtaining a structure having dense embedded flush circuitry features. The present invention makes it possible to create circuitry features that are much more densely configured than those fabricated using current methods. This is made possible since the final structure is a circuitry feature having dielectric regions and conductive features that are coplanar.

In particular, the present invention relates to a structure comprising a substrate having a surface; a polymeric dielectric applied to said surface of said substrate; conductive circuitry features embedded in said polymeric dielectric, wherein said conductive circuitry features are substantially flush with and surrounded by said polymeric dielectric.

The present invention also relates to a method for fabricating a structure having embedded flush circuitry features. The method comprises:

• • providing a sacrificial carrier film having a front side and a back side;
  • depositing a conductive seed layer on said front side of said sacrificial carrier film;
  • plating a layer of conductive metal onto said seed layer;
  • personalizing circuitry features on said layer of conductive metal;
  • embedding said front side of said sacrificial carrier film having the circuitry features into a dielectric material; and
  • removing said sacrificial carrier film.

The present invention also relates to a structure obtained by the above process. Still other objects and advantages of the present invention will become readily apparent by those skilled in the art from the following detailed description, wherein it is shown and the preferred embodiments of the invention are described, simply by way of illustration of the best mode contemplated of carrying out the invention. As will be realized the invention is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects, without departing from the invention. Accordingly, the description is to be regarded as illustrative in nature and not as restrictive.

SUMMARY OF THE DRAWINGS

FIGS. 1-6 are schematic drawings illustrating a structure at various stages of fabrication according to the present invention.

DETAILED DESCRIPTION OF THE INVENTION

As shown in FIG. 1, the structure of the present invention having embedded flush or coplanar circuitry features can be produced by employing a sacrificial carrier film 1 having a front side 2 and a back side 3. Typical sacrificial films include polyimides such as Kapton and Upilex. The sacrificial films are typically about 20 to about 250 microns thick, and more typically about 50 to about 100 microns thick.

The carrier is preferably smooth thereby eliminating metallic dendrites in the subsequently to be provided metal layer.

Next a relatively thin seed layer of a conductive metal 4 is deposited onto the front side of the sacrificial carrier film 1, as illustrated in FIG. 2. Typical metals include copper and chromium with copper being preferred. The seed layer is typically about 500 to about 2000 angstroms thick, a particular example being about 1000 angstroms. The seed layer can be deposited by electroless plating.

A conductive thin film 5 such as copper is then plated onto the seed layer 4 as shown in FIG. 3. The conductive film is typically up to about 20 microns, more typically about 5 to about 20 microns and preferably about 5 to about 10 microns. The conductive film can be deposited by electroless plating, or electroplating that are well known in the art. The preferred method of depositing the conductive film is by electroless plating.

It is preferred that the coated metal be free of dendrites, which cause skyscrapers and density issues.

Circuitry features 6 as shown in FIG. 4 on the layer of the conductive metal are then personalized by photolithographic and subtractive etching techniques, as are well known to those skilled in the art.

The circuit lines are typically about 0.5 to about 1 mil wide and about 0.5 to about 2 mils separated apart.

The structure with the front side having the circuitry features 6 is then embedded into the polymeric dielectric material 7 such as by laminating as shown in FIG. 5.

The dielectric material can be a thermoplastic resin or thermosetting resin. When a thermosetting resin is employed it is in the uncured or partially cured (B-stage) until after the embedding is completed. At that point, the thermosetting resin can be fully cured.

Typical thermosetting resins include epoxy resins, polyimides, bis-maleimide-triazine resins, and melamine resins.

Typical thermoplastic resins include polyimides, polytetrafluoroethylene resins, hexafluoro propylene resin, polyether sulfone resins and polyolefins such as polyethylene and polypropylene.

Typically the dielectric material is about 20 to about 200 microns and more typically about 50 to about 100 microns thick.

The preferred dielectric materials employed are epoxy resins and polyimide resins.

The sacrificial carrier film 1 is next removed such as by dissolving it in a suitable solvent, which does not attack the remaining constituents of the structure or preferably by peeling. Suitable solvents for a polyimide sacrificial film include KOH aqueous solutions. The sacrificial carrier film should therefore differ from the dielectric material.

The resulting structure contains circuitry features 6 that are protected within the surrounding dielectric material 7 thereby eliminating many contamination, bridging, topography, and electromigration issues.

The above process of the present invention can also be used with a rough carrier that would leave the dendrite surface exposed after removing the sacrificial carrier film. In that event a chemical mechanical polish operation would be used to “smooth” the exposed copper feature surfaces. In this case the sacrificial carrier film is removed such as by dissolving it in a suitable solvent, which does not attack the remaining constituents of the structure. Suitable solvents for a polyimide sacrificial film include KOH aqueous solutions.

In addition, if desired, the copper circuit lines can be plated with another conductive metal such as gold or nickel-gold as well known in the art.

Moreover, the resulting structure obtained pursuant to the above processing can then be joined together to form a multilayer circuit board.

The foregoing description of the invention illustrates and describes the present invention. Additionally, the disclosure shows and describes only the preferred embodiments of the invention but, as mentioned above, it is to be understood that the invention is capable of use in various other combinations, modifications, and environments and is capable of changes or modifications within the scope of the inventive concept as expressed herein, commensurate with the above teachings and/or the skill or knowledge of the relevant art. The embodiments described hereinabove are further intended to explain best modes known of practicing the invention and to enable others skilled in the art to utilize the invention in such, or other, embodiments and with the various modifications required by the particular applications or uses of the invention. Accordingly, the description is not intended to limit the invention to the form disclosed herein. Also, it is intended that the appended claims be construed to include alternative embodiments.

Claims

1. A structure comprising a polymeric dielectric substrate; conductive circuitry lines embedded in said polymeric dielectric substrate, wherein said conductive circuitry lines are substantially flush with and surrounded by said polymeric dielectric; wherein said conductive circuitry lines are about 0.5 to about 1 mils wide and wherein the separation between said conductive circuitry lines is about 0.5 to about 2 mils.

2. The structure of claim 1 wherein said conductive circuitry lines are metal.

3. The structure of claim 1 wherein the conductive circuitry lines comprise copper.

4. The structure of claim 1 wherein the dielectric substrate comprises an epoxy resin or polyimide resin.

5. The structure of claim 1 wherein the conductive circuitry lines comprise copper and another conductive metal located on top of the copper.

6. The structure of claim 5 wherein the another conductive metal comprises gold or nickel-gold.

7. The structure of claim 1 which comprises at least two of said polymeric dielectric substrates stacked together.

8. The structure of claim 3 which comprises at least two of said polymeric dielectric substrates stacked together.