This disclosure relates generally to semiconductor crystal growth using the Czochralski method and more particularly to supplying stock material such as chunk or granular polysilicon to a crucible melt.
In the production of silicon crystals grown by the continuous Czochralski method, polycrystalline silicon is melted within a crucible of a crystal pulling device to form a silicon melt. A seed crystal is then lowered to the melt and slowly raised back up. As the seed crystal is continuously grown from the melt, solid polysilicon such as granular polysilicon is added to the melt to replenish the melt. The feed rate of the additional solid polysilicon added to the melt is typically controlled to maintain process parameters. In the production of silicon crystals grown by the batch Czochralski method, solid polysilicon, such as chunk polysilicon, is not added to the melt while the seed crystal is grown but is added between sequential growing processes. The feed rate of the additional polysilicon is controlled to maintain process parameters.
The solid polysilicon added to the crucible melt is typically granular polysilicon, and it is fed into the crucible using a polysilicon feeder that is optimized for use with granular polysilicon. In some cases, solid polysilicon added to a crucible melt is chunk polysilicon. Chunk polysilicon has a greater size (e.g., in at least one dimension) than that of granular polysilicon. Chunk polysilicon is fed into a crucible using a polysilicon feeder optimized for use with chunk polysilicon. A more satisfactory apparatus and method for feeding either chunk or granular polysilicon is needed.
This Background section is intended to introduce the reader to various aspects of art that may be related to various aspects of the present disclosure, which are described and/or claimed below. This discussion is believed to be helpful in providing the reader with background information to facilitate a better understanding of the various aspects of the present disclosure. Accordingly, it should be understood that these statements are to be read in this light, and not as admissions of prior art.
An aspect is directed to a feed assembly for supplying polysilicon to a growth chamber for growing a crystal ingot from a melt. The feed assembly includes a housing having support rails for receiving one of a granular tray and a chunk tray. The feed assembly also includes a feed material reservoir positioned above the support rails to selectively feed from one of either the granular tray or the chunk tray.
According to another aspect, a valve mechanism controls the flow of polysilicon from a granular tray of a polysilicon feed assembly to a growth chamber for growing a crystal ingot from a melt. The valve mechanism includes a seal that selectively obstructs an exit of the granular tray. A driver is configured to raise and lower the seal between a sealed position obstructing the exit and an open position in which the seal does not obstruct the exit. A linkage connects the seal to the driver. The seal is shaped to permit a gap between the seal and a portion of the exit of the granular tray such that granular polysilicon within the exit does not prevent a seal between the seal and the exit.
According to another aspect, a magnetic pulse vibrator controls the flow of polysilicon from one of either a granular tray or a chunk tray of a polysilicon feed assembly to a growth chamber for growing a crystal ingot from a melt. The magnetic pulse vibrator includes an electromagnetic energy source that vibrates one of either the granular tray or the chunk tray through the emission of electromagnetic energy. The magnetic pulse vibrator also includes a controller that controls a feed rate of one of either the granular tray or the chunk tray through control of the voltage supplied to the electromagnetic energy source.
According to a further aspect, an interchangeable granular tray, for a feed assembly for supplying polysilicon to a growth chamber for growing a crystal ingot from a melt, includes an exterior portion. The exterior portion removably receives a support rail of the feed assembly. The interchangeable granular tray further includes an interior profile that receives granular polysilicon from a feed material reservoir of the feed assembly. The granular tray is removable from the feed system.
According to another aspect, an interchangeable chunk tray, for a feed assembly for supplying polysilicon to a growth chamber for growing a crystal ingot from a melt, includes an exterior portion. The exterior portion removably receives a support rail of the feed assembly. The interchangeable chunk tray further includes an interior profile that receives chunk polysilicon from a feed material reservoir of the feed assembly. The chunk tray is removable from the feed system.
Various refinements exist of the features noted in relation to the above-mentioned aspects. Further features may also be incorporated in the above-mentioned aspects as well. These refinements and additional features may exist individually or in any combination. For instance, various features discussed below in relation to any of the illustrated embodiments may be incorporated into any of the above-described aspects, alone or in any combination.
Corresponding reference characters indicate corresponding parts throughout the several views of the drawings.
Referring now to
Interchangeable tray 106 may be either a granular tray 300 (shown in
Using interchangeable tray 106 allows polysilicon feeder 100 to be quickly and easily adapted for use with either granular polysilicon or chunk polysilicon. Interchangeable tray 106 may be removed and replaced with a second interchangeable tray that is configured for use with a different type of polysilicon. For example, a granular tray 300 may have features such as a shallow depth relative to that of a chunk tray 400, a funnel portion, a substantially vertical exit portion, or other features suitable for use with granular polysilicon. A chunk tray 400 may have features such as a greater depth than that of the granular tray 300, sloped sides, a slopping exit, or other features suitable for use with chunk polysilicon. Switching one type of interchangeable tray 106 for another converts polysilicon feeder 100 for use with a different type of polysilicon. For example, removing a granular tray 300 and replacing it with a chunk tray 400 converts polysilicon feeder 100 from a feeder to be used with granular polysilicon to a feeder to be used with chunk polysilicon. Interchangeable trays 106, including granular trays 300 and chunk trays 400, are described in greater detail with reference to
Polysilicon feeder 100 includes a vibrator 104 that causes interchangeable tray 106 to vibrate. Vibrator 104 is a magnetic pulse vibrator that vibrates interchangeable tray 106 using magnetic pulses. The magnetic pulse vibrator is discussed in greater detail with reference to
By vibrating interchangeable tray 106, vibrator 104 causes polysilicon to exit interchangeable tray 106 (e.g., through an exit opposite hopper 102). Polysilicon exiting interchangeable tray 106 enters guide tube 108. By controlling the vibration of vibrator 104, and the vibration of interchangeable tray 106, the feed rate of polysilicon from polysilicon feeder 100 is controlled. A control system (e.g., a programmable logic controller) may control vibrator 104.
Polysilicon feeder 100 also includes a guide tube 108. Guide tube 108 is configured to receive polysilicon that exits interchangeable tray 106 due to vibration caused by vibrator 104. Guide tube 108 directs polysilicon from polysilicon feeder 100 to enter a crucible used in generating a silicon crystal using the Czochralski method. Guide tube 108 may be positioned such that polysilicon is added to a melt within the crucible as a silicon crystal is drawn out of the melt. For example, guide tube 108 may be positioned off center relative to a crystal puller.
Referring now to
As shown in
In this embodiment, vibrator 104 includes a magnetic pulse vibrator. The magnetic pulse vibrator controls the flow of polysilicon from interchangeable tray 106 (e.g., one of either a granular tray 300 or a chunk tray 400) to the crucible. The magnetic pulse vibrator includes an electromagnetic energy source that vibrates one of either the granular tray 300 or the chunk tray 400 through the emission of electromagnetic energy. The magnetic pulse vibrator also includes a controller that controls a feed rate of one of either the granular tray 300 or the chunk tray 400 through control of the voltage supplied to the electromagnetic energy source.
In one embodiment, the magnetic pulse vibrator uses magnetic pulses to drive a spring-biased table. The magnetic pulse may be generated, for example, by selectively applying a voltage having a variable amplitude and/or variable frequency of application to a coil. This results in a magnetic pulse that interacts with a core to drive (e.g., move or displace) the core. The core is connected to the table such that when the core is displaced by a magnetic pulse from the coil, the core displaces the table. A spring or other suitable mechanism biases the table and connected core to a rest position from which the core is displaced by the magnetic pulse. The movement of the core generates vibrations that in turn drive interchangeable tray 106. For example, interchangeable tray 106 may be connected to the table which is driven by the connected core and the coil.
The magnetic pulse vibrator may be controlled by both voltage and frequency. The voltage and frequency are linked control parameters which interact to control the magnetic pulse vibrator and feed rate of polysilicon feeder 100. By varying the amplitude of the voltage applied, the strength of the magnetic pulse and the amount of displacement of the core and table is varied. This control determines the strength of the vibration applied to interchangeable tray 106. By varying the frequency with which the voltage is applied, the frequency of the vibration applied to interchangeable tray 106 is controlled. One or more of voltage frequency and voltage amplitude may be used to vibrate interchangeable tray 106 to meet a set point for a polysilicon feed rate (e.g., in kg of polysilicon per hour).
In an alternative embodiment, the magnetic pulse vibrator drives interchangeable tray 106 directly with magnetic pulses. For example, interchangeable tray 106 may include one or more portions that are magnetic and that are displaced by the magnetic pulses generated by the magnetic pulse vibrator.
Referring now to
In operation, granular tray 300 may be removed from the feed system of polysilicon feeder 100. This allows granular tray 300 to be replaced by chunk tray 400 when polysilicon feeder 100 is to be used with chunk polysilicon rather than granular polysilicon. Granular tray 300 is interchangeable with chunk tray 400 as polysilicon feeder 100 includes support rails and a cavity sized to receive either granular tray 300 or chunk tray 400. The exterior portion of granular tray 300 includes two exterior channels 312 on opposing sides that removably receive the support rails of the feed assembly included in polysilicon feeder 100. This allows granular tray 300 to be removed and replaced with chunk tray 400. As explained in greater detail with reference to
Referring now to
In alternative embodiments, bottom 302 includes a first portion at a first depth prior to funnel 308 and a second portion at a greater depth past funnel 308, the second portion including exit 310. This stepped bottom 302 may facilitate feeding of granular polysilicon by granular tray 300. In alternative embodiments, bottom 302 has other configurations. For example, bottom 302 may include a sloped portion that slopes towards exit 310.
Funnel 308 is defined by raised sections that extend above bottom 302. The raised sections have a height less than that of top surface 304. In alternative embodiments, the raised sections forming funnel 308 extend to the same height as that of top portion 304. Funnel 308 facilitates feeding of granular polysilicon when granular tray 300 is vibrated by vibrator 104. For example, funnel 308 may prevent granular polysilicon exiting hopper 102 from exiting granular tray 300 through exit 310 when vibrator 104 is not driving granular tray 300. Funnel 308 may impede the travel of granular polysilicon from hopper 102 when granular tray 300 is not vibrating.
Granular tray 300 includes outer dimensions defined by exterior surfaces 316 including at least the top surface 304, the exterior channels 312 formed in side portions 314, a side 322, an angled side 320, a front 318, a back 324, and a bottom 325. The dimensions and exterior surfaces of granular tray 300 are sized and shaped such that granular tray 300 can be inserted into polysilicon feeder 100. For example, the height of granular tray 300, defined by top surface 304 and bottom 325; the width of granular tray 300, defined by side portions 314; and the length of granular tray 300, define by front 318 and back 324, are sized to fit within an opening in polysilicon feeder 100. When inserted into the opening in polysilicon feeder 100, granular tray 300 is positioned below hopper 102 and above vibrator 104. Exterior channels 312 receive guide rails of polysilicon feeder 100 that position granular tray 300 vertically. Bottom 325 may be in contact with vibrator 104 or a vibration table driven by vibrator 104. Alternatively, granular tray 300 is supported above vibrator 104 by the guide rails and exterior channel 312. Top surface 304 may be in contact with hopper 102 or other portions of portions of polysilicon feeder 100.
Exterior channels 312 are included within side portions 314 that extend from side 322. Side portions 314, exterior channel 312, and side 322 extend from back 324. Sides 322 taper to front 318 creating angled sides 320. In some embodiments, the opening in polysilicon feeder 100 is dimensioned such that granular tray 300 may not be fully inserted if inserted back 324 first rather than front 318 first.
Referring now to
Bottom 302 is recessed from top surface 304. Wall 306 extends downward from top surface 304 to bottom 302 and is chamfered at the junction between bottom 302 and wall 306. Funnel 308 is located between back 324 and exit 310 such that a flow of polysilicon entering granular tray 300 from hopper 102 must pass through a narrower section defined by funnel 308 before exiting granular tray 300. Exit 310 is circular with a chamfered opening portion 326 that has a decreasing radius to a second portion 328 of exit 310. Second portion 328 has a fixed radius. As described with reference to
Referring now to
Referring specifically to
In operation, chunk tray 400 is inserted into polysilicon feeder 100 such that the support rails of polysilicon feeder 100 are inserted within channels 312. The support rails support chunk tray 400. The support rails and channels 312 allow chunk tray 400 to be removed and replaced with a granular tray 300.
Referring now to
Sides 406 extend downward from wall 408 and meet bottom 402. Sides 406 also extend horizontally between bowl 404 and wall 408 opposite bowl 404. Sides 406 are angled to extend inwards toward exit 410 as sides 406 approach bottom 402. Exit 410 has a circular opening through bottom 402. Bottom 402 is flat. In alternative embodiments, bottom 402 is slopped towards exit 410.
Referring now to
Referring to
Referring again to
Granular tray 300 and chunk tray 400 are suitably made of, or include a substantial portion of, silicon. Use of silicon inhibits contamination of the crucible melt, for example, in the event that the tray is chipped. If the chip enters the melt and the tray is made of silicon, minimal contamination will result. In alternative embodiments, granular tray 300 and chunk tray 400 may be constructed of different material(s) such as polytetrafluoroethylene, quartz, or other suitable materials. For example, the interchangeable trays 106 may be constructed of one or more materials with a relatively high hardness, such as quartz, to resist chipping.
Referring now to
Each rail 501 is connected to a table 503 of vibrator 104. For example, each rail 501 is connected to table 503 by brackets, fasteners, or other suitable components. Each rail 501 extends above table 503 and extends inward towards the center of table 503. Each rail 501 extends for at least a portion of the length of table 503. Each rail 501 further includes a rear stop 505 which prevents over insertion of chunk tray 400. Each rear stop 505 extends inward towards the center of table 503 from each rail 501.
When chunk tray 400 is attached to vibrator 104, each rail 501 extends within a corresponding exterior channel 312. Each rail 501 extends within side portion 314 in the space defined by exterior channel 312. Interference between exterior channel 312 in side 314 and rail 501 prevents lateral movement and vertical movement of chunk tray 400. The bottom 325 of chunk tray 400 rests on table 503. The back 324 of chunk tray 400 is in contact with each rear stop 505. Interference between back 324 and each rear stop 505 prevents rearward movement of chunk tray 400. Granular tray 300 is connected to vibrator 104 by the pair of rails 501, table 503, and rear stops 505 in the same manner.
In some embodiments, chunk tray 400, or granular tray 300, is partially covered with cover 321. Cover 321 includes lips which extend over top surface 304 and partially over side 322, and angled side 320 to secure cover 321.
Referring now to
In the parked position, vibrator 104 and interchangeable tray 106 are rotated away from guide tube 108. For example, the parked position may be seventy degrees from the feeding position. The parked position provides access to interchangeable tray 106 such that interchangeable tray 106 may be replaced with a different interchangeable tray 106. For example, in the parked position, a granular tray 300 may be replaced with a chunk tray 400.
In operation, guide tube 108 is lowered. Vibrator 104 and interchangeable tray 106 are moved into the feeding position from the parked position prior to feeding polysilicon to a crucible. Vibrator 104 is rotated from the parked position to the feeding position. In one embodiment, vibrator 104 is rotated using a motor. In an alternative embodiment, vibrator 104 is rotated by hand. Interchangeable tray 106 rotates with vibrator 104 due to the connection described above. In some embodiments, guide tube 108 is contact with interchangeable tray 106.
Once vibrator 104 and interchangeable tray 106 are in the feeding position, vibrator 104 is turned on. Vibrations from vibrator 104 cause polysilicon from interchangeable tray 106 to exit into guide tube 108. Guide tube 108 guides the polysilicon exiting interchangeable tray 106 into a crucible. Hopper 102 feeds polysilicon into interchangeable tray 106 to replace polysilicon exiting interchangeable tray 106. Vibrator 104 is turned off.
Vibrator 104 and interchangeable tray 106 are moved into the parked position from the feeding position. Vibrator 104 is rotated from the feeding position to the parked position. Interchangeable tray 106 rotates with vibrator 104. In some embodiments, guide tube 108 is raised after vibrator 104 is rotated to the parked position.
While in the parked position, interchangeable tray 106 may be removed from vibrator 104. For example, granular tray 300 may be removed from vibrator 104. A replacement interchangeable tray 106, for example a chunk tray 400, may be connected to vibrator 104. The parked position allows for the swapping of interchangeable trays 106.
In some embodiments, a valve mechanism (shown in
Valve mechanism 200 controls the flow of polysilicon through exit 310 of granular tray 300. As shown in
Driving system 500 of this embodiment is a solenoid for moving seal 512 between a sealed position and an open position. In the sealed position (as shown in
Valve mechanism 200 is normally closed. When driver 502 is not active, the force of gravity causes seal 512 to lower into the sealed position. In some further embodiments, driving system 500 includes a spring to return seal 512 to the normally closed position. In alternative embodiments, valve mechanism 200 is normally open. A spring maintains linkage 510 and seal 512 in the open position. When activated, driver 502 applies a magnetic field to linkage 510 that drives linkage 510 downward causing sealing portion 512 to move to the sealed position.
Driving system 500 also includes an upper position switch 506 and a lower position switch 504. Position switches 504, 506 each include a lever positioned to interfere with a top portion 508 of linkage 510. Interference between top portion 508 of linkage 510 and one of upper position switch 506 or lower position switch 504 causes the respective switch to provide an indication of the position of seal 512, open and sealed, respectively.
Seal 512 is shaped to interface with exit 310 and bottom 302 of granular tray 300. The shape of seal 512 obstructs exit 310 when in the sealed position and prevents polysilicon from exiting granular tray 300 through exit 310. In the open position, seal 512 does not contact granular tray 300. Seal 512 includes a first section 514, a second section 516, and a third section 518. Each section corresponds to a different portion of granular tray 300 (e.g., angled portion 326 and second portion 328) to facilitate obstruction of exit 310. For example, exit 310 is circular when viewed from above and each section of seal 512 is circular when viewed from above.
Referring now to
Second section 516 of seal 512 extends from third section 518 to first section 514. Second section 516 has a decreasing radius from the larger radius of first section 514 to the smaller radius of third section 518. The radius of second section 516 decreases linearly. The decreasing radius of second section 516 matches the decreasing radius of angled portion 326 of exit 310. The radius of second section 516 decreases at the same rate as the radius of angled portion 326. The slope of second section 516 is equal to that of angled portion 326. When in the sealed position, second section 516 is in contact with angled portion 326 of exit 310. This seals exit 310 and prevents polysilicon from exiting granular tray 300. The height of second section 516 is less than the height of angled portion 326. Second section 516 terminates at first section 514.
First section 514 has a fixed radius equal to the largest radius of second section 516. First section 514 extends upward from section 516 and is coupled to linkage 510. First section 514 has a radius less than the largest radius of angled portion 326 of exit 310. This creates a gap 522 between first section 514 and the opening of exit 310 when seal 512 is in the sealed position. First section 514 extends at least partially into angled portion 326 of exit 310. First section 514 may also extend above exit 310.
Gap 522 between seal 512 and exit 310 ensures that no granular polysilicon within exit 310 blocks seal 512 from contacting exit 310 which would prevent a seal from forming. Angled portion 326 of exit 310 causes any polysilicon within angled portion 326 to pass through exit 310 prior to seal 512 being moved to the sealed position. Angled portion 326 is free of polysilicon due to the angle. Therefore, no polysilicon can prevent a seal between seal 512 and exit 310 as second section 516 only contacts angled portion 326 where no polysilicon is present. First section 514 does not contact bottom 302 and is separated from bottom 302 by gap 522 such that polysilicon on bottom 302 does not impede seal 512 from sealing within exit 310.
Referring now to
Position switches 504, 506 are triggered when a top portion 508 of linkage 510 contacts a lever portion of limit switches 504, 506. When top portion 508 of linkage 510 contacts and moves the lever portion of upper position switch 506, upper position switch 506 is triggered and indicates that seal 512 is in the open position. When top portion 508 of linkage 510 contacts and moves the lever portion of lower position switch 504, lower position switch 504 is triggered and indicates that seal 512 is in the sealed position.
Referring now to
The interchangeable trays described herein allow the polysilicon feeder to supply either granular or chunk polysilicon to a crucible for silicon crystal generation using the Czochralski method. By inserting the corresponding tray, the polysilicon feeder is capable of supplying a controlled rate of granular or chunk polysilicon to the crucible used in generating the silicon crystal. Advantageously, this allows the polysilicon feeder to use either source of polysilicon. For example, where only one source is available (e.g., chunk polysilicon), the corresponding tray is inserted into the polysilicon feeder and the crucible is supplied with polysilicon according to the parameters for crystal generation (e.g., a rate of polysilicon supply). Only a single source may be available due to supply issues or supply chain issues. The ability to easily switch from one polysilicon source to another provides greater supply security as different types of polysilicon may be used and therefore a greater number of supply sources are available. In some cases, it may be more economical to use a particular source of polysilicon (granular or chunk) depending on fluctuations in price. The polysilicon feeder is capable of operating more economically than a fixed source polysilicon feeder as the polysilicon feeder can adapt to either source using the interchangeable trays.
Granular polysilicon has several advantages including providing for easy and precise control of the feed rate due to the smaller size. However, the cost of granular polysilicon is typically higher than that of chunk polysilicon due to the chemical vapor deposition process or other manufacturing methods used in its production. Chunk polysilicon has the advantage of being cheaper and being capable of a higher feed rate given its larger size. By being capable of supplying either granular polysilicon or chunk polysilicon to a melt for crystal growth, the polysilicon feeder can selectively make use of the advantages of either polysilicon type and provides increased supply security by being compatible with either polysilicon type.
In some embodiments, the polysilicon feeder includes a magnetic pulse vibrator that supports the use of interchangeable polysilicon trays. The magnetic pulse vibrator vibrates either interchangeable polysilicon tray (e.g., the granular tray or the chunk tray) at variable rates using magnetic pulses. The rate may be controlled based on the frequency and/or magnitude of voltage supplied to the magnetic pulse vibrator. The magnetic pulse vibrator is capable of providing a wide range of vibration rates, magnitudes, or both which allows the polysilicon feeder to provide a specific feed rate when using either granular polysilicon, with the granular tray, or chunk polysilicon, with the chunk tray.
In further embodiments, the polysilicon feeder includes a valve mechanism. The valve mechanism engages and disengages with one of the two interchangeable trays (e.g., the granular tray) to selectively prevent polysilicon from feeding into the crucible regardless of the state of the vibrator driving the tray. For example, the polysilicon feeder may be moved or shifted (e.g., when the vibrator is not active). This movement may cause polysilicon to fall from the tray and enter the crucible at an unintended time. This polysilicon inadvertently added to the melt in the crucible functions as an impurity and degrades crystal quality. The valve mechanism engages with the interchangeable tray to seal an exit preventing polysilicon from exiting the interchangeable tray into the melt.
When introducing elements of the present invention or the embodiment(s) thereof, the articles “a”, “an”, “the” and “said” are intended to mean that there are one or more of the elements. The terms “comprising”, “including” and “having” are intended to be inclusive and mean that there may be additional elements other than the listed elements. The use of terms indicating a particular orientation (e.g., “top”, “bottom”, “side”, “down”, “up”, etc.) is for convenience of description and does not require any particular orientation of the item described.
As various changes could be made in the above constructions and methods without departing from the scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawing[s] shall be interpreted as illustrative and not in a limiting sense.
This application is the § 371 national stage of International Application No. PCT/US2016/047575, filed on Aug. 18, 2016, which claims priority to U.S. Provisional Patent Application Ser. No. 62/207,773 filed on 20 Aug. 2015, each of which is hereby incorporated by reference in its entirety.
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/US2016/047575 | 8/18/2016 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2017/031328 | 2/23/2017 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
5580171 | Lim | Dec 1996 | A |
5588339 | Dulger | Dec 1996 | A |
5690733 | Nagai et al. | Nov 1997 | A |
5868835 | Nagai et al. | Feb 1999 | A |
5919303 | Holder | Jul 1999 | A |
20040035960 | Arvidson et al. | Feb 2004 | A1 |
20040211358 | Fickett | Oct 2004 | A1 |
20130098290 | Luter | Apr 2013 | A1 |
20160060787 | Park | Mar 2016 | A1 |
Number | Date | Country |
---|---|---|
1553214 | Jul 2005 | EP |
H01177275 | Dec 1989 | JP |
101209185 | Dec 2012 | KR |
Number | Date | Country | |
---|---|---|---|
20180237948 A1 | Aug 2018 | US |
Number | Date | Country | |
---|---|---|---|
62207773 | Aug 2015 | US |