TFT SUBSTRATE AND DISPLAY DEVICE INCLUDING THE SAME

Information

  • Patent Application
  • 20190363194
  • Publication Number
    20190363194
  • Date Filed
    May 21, 2019
    5 years ago
  • Date Published
    November 28, 2019
    5 years ago
Abstract
A thin film transistor (TFT) substrate includes a TFT on the substrate. The TFT includes an active patterned layer which is made of a polycrystalline silicon, which includes a channel portion, a source portion and a drain portion, and in which protrusions are formed at boundaries between grains and recess spaces are formed between the protrusions. A barrier pattern film fills the recess spaces and forms a flat surface with the protrusions. A gate electrode is on a gate insulating layer located on the barrier pattern film and the protrusions and overlays or corresponds to the channel portion. A source electrode and a drain electrode are on the gate electrode and respectively contact the source portion and the drain portion.
Description
CROSS REFERENCE TO RELATED APPLICATIONS

The present application claims the priority benefit of Korean Patent Application No. 10-2018-0059462 filed in Republic of Korea on May 25, 2018, which is hereby incorporated by reference in its entirety for all purposes as if fully set forth herein.


BACKGROUND
Technical Field

The present disclosure relates to a thin film transistor (TFT) substrate and a display device including the same.


Description of the Related Art

Generally, a thin film transistor (TFT) substrate is used for a flat display device such as a liquid crystal display device (LCD), an organic light emitting diode (OLED) display device, or the like.


A TFT uses an amorphous silicon or polycrystalline silicon for an active layer. The polycrystalline silicon is better in a charge mobility property or the like than the amorphous silicon, and thus a TFT including the polycrystalline silicon is used for a display device requiring a high performance such as a high resolution or the like.


The polycrystalline silicon may be generally formed using an excimer laser annealing (ELA) method. In this case, there is a problem that a protrusion as a defect is produced at a grain boundary.


BRIEF SUMMARY

Accordingly, the present disclosure is directed to a TFT substrate and a display device including the same that substantially obviate one or more of the problems due to limitations and disadvantages of the related art.


An advantage of the present disclosure is to provide a TFT substrate and a display device including the same which can improve a property of a TFT including a polycrystalline silicon.


Additional features and advantages of the disclosure will be set forth in the description which follows, and in part will be apparent from the description, or may be learned by practice of the disclosure. These and other advantages of the disclosure will be realized and attained by the structure particularly pointed out in the written description and claims hereof as well as the appended drawings.


To achieve these and other advantages and in accordance with the purpose of the present disclosure, as embodied and broadly described herein, a thin film transistor (TFT) substrate includes: a TFT on a substrate, wherein the TFT includes an active patterned layer which is made of a polycrystalline silicon, which includes a channel portion, a source portion and a drain portion, and in which protrusions are formed at boundaries between grains and recess spaces are formed between the protrusions; a barrier pattern film which fills the recess spaces and forms a flat surface with the protrusions; a gate electrode which is on a gate insulating layer located on the barrier pattern film and the protrusions and overlays or corresponds to the channel portion; and a source electrode and a drain electrode which are on the gate electrode and respectively contact the source portion and the drain portion.


In another aspect, a display device includes: a thin film transistor (TFT) substrate which includes a TFT on a substrate; and a first electrode connected to a drain electrode of the TFT, wherein the TFT includes: an active patterned layer which is made of a polycrystalline silicon, which includes a channel portion, a source portion and a drain portion, and in which protrusions are formed at boundaries between grains and recess spaces are formed between the protrusions; a barrier pattern film which fills the recess spaces and forms a flat surface with the protrusions; a gate electrode which is on a gate insulating layer located on the barrier pattern film and the protrusions and overlays or corresponds to the channel portion; and a source electrode and the drain electrode which are on the gate electrode and respectively contact the source portion and the drain portion.


It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the described embodiments of the disclosure.





BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

The accompanying drawings, which are included to provide a further understanding of the disclosure and are incorporated in and constitute a part of this specification, illustrate embodiments of the disclosure and together with the description serve to explain the principles of the described embodiments of the disclosure. In the drawings:



FIG. 1 is a plan view schematically illustrating a TFT substrate of an OLED display device according to an embodiment of the present disclosure;



FIG. 2 is a cross-sectional view schematically illustrating a portion of a pixel region of FIG. 1;



FIG. 3 is a view enlarging a TFT of FIG. 2;



FIGS. 4 to 7 are cross-sectional views illustrating a method of manufacturing a TFT substrate according to an embodiment of the present disclosure;



FIG. 8 is a cross-sectional view schematically illustrating a structure of a TFT for a driving circuit formed in a scan driving circuit according to an embodiment of the present disclosure; and



FIG. 9 is a cross-sectional view schematically illustrating an example a conductive connection patterned layer using a polycrystalline silicon according to an embodiment of the present disclosure.





DETAILED DESCRIPTION

Reference will now be made in detail to exemplary embodiments, examples of which are illustrated in the accompanying drawings. The same reference numbers may be used throughout the drawings to refer to the same or like parts.


A TFT substrate of an embodiment of the present disclosure may be applied to all sorts of electronic devices using a TFT as a driving element. For example, a TFT substrate may be applied to various electronic devices including a display device, a sensor panel, and the like.


For the purpose of explanations, an embodiment of the present disclosure is described with a TFT substrate used for an OLED display device by way of example.



FIG. 1 is a plan view schematically illustrating a TFT substrate of an OLED display device according to an embodiment of the present disclosure. FIG. 2 is a cross-sectional view schematically illustrating a portion of a pixel region of FIG. 1. FIG. 3 is a view enlarging a TFT of FIG. 2.


Referring to FIGS. 1 to 2, the TFT 10 of this embodiment may include a display region AA as an active region to display an image, and a non-display region NA as a non-active region which is located around (or surrounds) the display region AA


In the display region AA, a plurality of pixel regions P may be arranged in a matrix form. The plurality of pixel regions P may include, for example, red, green and blue pixel regions P respectively displaying red, green and blue. The red, green and blue pixel regions P may be located alternately in a direction.


Each pixel region P may include driving elements to operate the pixel region P. For example, a plurality of TFTs and an organic light emitting diode OP may be formed in the pixel region P.


For the purpose of explanations, a driving TFT Tr out of the plurality of TFTs in the pixel region P is shown by way of example. The other TFTs in the pixel region P may have substantially the same structure as the driving TFT Tr.


In the non-display region NA, a driving circuit to drive the pixel regions P in the display region AA may be located.


For example, a scan driving circuit SDC which outputs a scan signal such as a gate signal and provides the scan signal to the pixel region P may be located in the non-display region NA. The scan driving circuit SDC may be formed directly in the TFT substrate 10.


The scan driving circuit SDC formed directly in the TFT substrate 10 may be referred to as a GIP (gate in panel) type driving circuit, which may be formed in processes of manufacturing the TFT substrate 10. The GIP type scan driving circuit SDC may include a plurality of TFTs for a driving circuit, and the plurality of TFTs may have substantially the same structure as the driving TFT Tr of the pixel region P.


A structure of the pixel region P is explained in detail with reference to FIGS. 2 and 3.


The TFT substrate 10 is a substrate where array elements to operate the display device are formed and may be referred to as an array substrate


In the TFT substrate 10, a plurality of TFTs including the driving TFT Tr may be formed in each pixel region P on an inner surface of a substrate 11.


Each of the plurality of TFTs including the driving TFT Tr may include an active patterned layer (or semiconductor patterned layer) 21.


A buffer layer 15 may be formed below the active patterned layer 21 and entirely over the substrate 11.


The active patterned layer 21 may be made of a polycrystalline silicon.


For example, a laser annealing method such as an ELA method may be applied to an amorphous silicon deposited on the buffer layer 15 to perform a crystallization, and thus a polycrystalline silicon layer may be produced.


In the crystallization, an amorphous silicon is melted, and grains GR are grown in a lateral direction parallel with a surface of a substrate. Accordingly, the crystallization is performed.


At boundaries between the grains GR, i.e., grain boundaries, the grains GR are uplifted by the lateral growth and thus protrusions having an upwardly peaky (or upwardly sharp) shape are produced.


The protrusion may serve as a defect causing a gate voltage variation or the like due to its electric field concentration effect.


In this embodiment, the protrusions are removed from the polycrystalline silicon layer as much as possible using a polishing process such as a CMP (chemical mechanical polishing) process, and thus a property of the TFT can be improved.


In this regard, at the boundaries between the grains GR of the active patterned layer 21 which is formed through patterning the polycrystalline silicon layer, residual protrusions 23 which are partially removed through the CMP process are formed. Since the residual protrusions 23 are formed by the CMP process, top surfaces of the residual protrusions 23 are substantially flat (or even).


In the active patterned layer 21, recess spaces OS which are surrounded by the residual protrusions 23 and are dented downwardly may be defined. The recess space OS may have side surfaces of the residual protrusions 23 and a top surface of the grain GR as its boundary surfaces, and may be open upwardly.


The active patterned layer 21 may have an uneven (or concavo-convex) shape with the residual protrusions 23 and the recess spaces OS arranged alternately.


The recess space OS of the active patterned layer 21 may be filled with a barrier film as an insulating film, i.e., a barrier pattern film 32. The barrier pattern film 32 may be made of an inorganic insulating material, for example, silicon oxide SiO2 or silicon nitride SiNx.


The barrier pattern film 32 is a residual barrier film that does not remove and remains on the polycrystalline silicon layer after the CMP process.


In this regard, the barrier film is formed on the polycrystalline silicon layer in which peaky protrusions are formed before the CMP process, and the CMP process is conducted for the TFT substrate 10 having this barrier film.


The CMP process may be conducted to the extent that the peaky protrusions of the polycrystalline silicon layer are partially removed and a top surface of the TFT substrate 10 are substantially in a uniformly even state. Further, a process of patterning the polycrystalline silicon layer may be conducted after the CMP process to form the active patterned layer 21 and the barrier pattern film 32.


Accordingly, for the active patterned layer 21, the residual protrusion 23 which is reduced in height (or thickness) by the polishing is formed at the boundary between the grains GR, and the barrier pattern film 32 as a residual barrier film which is partially removed by the polishing remains in the recess space OS.


As such, since the protrusion and the barrier film are partially removed by the CMP process, the active patterned layer 21 in a state that the barrier pattern film 32 remains after the CMP process substantially has an entirely flat top surface.


In other words, after the CMP process is finished, the top surface of the residual protrusion 23 is not covered by the barrier pattern film 32 to be exposed, and the side surface of the residual protrusion 23 substantially entirely contacts the barrier pattern film 32. The barrier pattern film 32 remains to substantially fully fill the recess space OS on the side surface of the residual protrusion 23 so that the top surface of the barrier pattern film 32 has substantially the same height as the top surface of the residual protrusion 23.


Since the recess space OS of the active patterned layer 21 is filled with the barrier pattern film 32, the top surface of the active patterned layer 21 substantially has a flat form.


When conducting the CMP process, the grains GR of the active pattern layer 21 are not affected by the CMP because of the barrier pattern film 32 remaining thereon. Accordingly, the grains GR being exposed to the CMP and thus being damaged can be substantially prevented.


Accordingly, an influence of the CMP on the grains GR can be prevented while the protrusions being partially removed, thus a defect of the active patterned layer 21 can be minimized, and thus a property of the TFT can be maximized.


The active patterned layer 21 of the driving TFT Tr may include a channel portion CH, and a source portion S and a drain portion D respectively located at both sides of the channel portion CH.


The channel portion CH may be a non-doped portion, which is not doped with impurities, as a pure silicon region. The source portion S and the drain portion D may be a doped portion which is highly doped with impurities, for example, P (positive) or N (negative) type impurities according to a type of the TFT.


A gate insulating layer 40 may be formed on a substantially entire surface of the substrate 11 having the active patterned layer 21.


The gate insulating layer 40 may be made of an inorganic insulating material, for example, silicon oxide (SiO2) or silicon nitride (SiNx). It is preferable, but not limited, that the gate insulating layer 40 is made of the same material as the barrier pattern film 32 therebelow. When the gate insulating layer 40 is made of the same material as the barrier pattern film 32, an effect such as an improved adhesion property therebetween may be achieved.


In the gate insulating layer 40, a first contact hole H1 and a second contact hole H2 respectively exposing the source portion S and the drain portion D of the active patterned layer below the gate insulating layer 40 may be formed.


At portions where the first contact hole H1 and the second contact hole H2 are formed, i.e., at a region of a part of the source portion S and a region of a part of the drain portion D, the barrier pattern film 32 is substantially removed entirely.


In other words, a source electrode 51 directly contacts the region of the part of the source portion S, and a drain electrode 53 directly contacts the region of the part of the drain portion D. Accordingly, it is preferable that at the region of the part of the source portion S contacting the source electrode 51 and the region of the part of the drain portion D contacting the drain electrode 53, the barrier pattern film 32 does not exist and is fully removed.


Thus, at a contact region as the region of the part of the source portion S and a contact region as the region of the part of the drain portion D, the barrier pattern film 32 is removed in the recess space OS and the top surfaces of the corresponding grains GR are in an exposed state. In other words, the top surface of the active patterned layer 21 below the first and second contact holes H1 and H2 is in an exposed state.


As such, the gate insulating layer 40 may fully cover the active patterned layer 21 except for parts of the active patterned layer 21 corresponding to the first and second contact holes H1 and H2.


In this regard, for the active patterned layer 21 except for the parts of the active patterned layer 21 corresponding to the first and second contact holes H1 and H2, the gate insulating layer 40 may be formed over the residual protrusions 23 to directly contact the residual protrusions 23, and the gate insulating layer 40 may be formed over the grains GR with the barrier pattern film 32 interposed therebetween between.


Further, side surfaces of the active patterned layer 21 may directly contact and be covered by the gate insulating layer 40.


The gate insulating layer 40 may be formed on the active patterned layer 21 which has a substantially flat state because of the barrier pattern film 32. Thus, the gate insulating layer 40 on the active patterned layer 21 may also have a substantially flat state.


Accordingly, a gate electrode 45 on the gate insulating layer 40 may also have a substantially flat state, and thus a stable property of the TFT can be obtained.


Further, as a resolution of a display device increases, a size of the TFT is reduced and the gate insulating layer 40 is required to have a small thickness. In this case, if the barrier pattern film 32 does not exist and the gate insulating layer 40 having a small thickness is deposited on the active patterned layer 21 with peaky protrusions not being removed, there may happen a defect that the peaky protrusions penetrate the gate insulating layer 40 and contact the gate electrode 45.


However, in this embodiment, with the barrier pattern film 32 being formed below the gate insulating layer 40, the top surface of the active patterned layer 21 substantially becomes flat. Thus, it can be prevented that the residual protrusions 23 of the active patterned layer 21 penetrate the gate insulating layer 40 and contact the gate electrode 45 to make a short-circuit.


Accordingly, a defect of the TFT caused by the short-circuit between the protrusions of the active patterned layer 21 and the gate electrode 45 can be prevented.


The gate electrode 45 may be formed on the gate insulating layer 40 to substantially overlie or correspond to the channel portion CH.


As described above, the gate insulating layer 40 has a substantially flat surface on the active patterned layer 21, and thus the gate electrode 45 may be formed to be substantially flat.


A first passivation layer 50 as an insulating layer may be formed on the gate electrode 45. The first passivation layer 50 may be made of an inorganic insulating material or organic insulating material.


The first passivation layer 50 may include the first and second contact holes H1 and H2 respectively exposing the source and drain portions S and D.


The source and drain electrodes 51 and 53 may be formed on the first passivation layer 50 to be spaced apart from each other with the gate electrode 45 located therebetween.


The source electrode 51 may be connected to the source portion S through the first contact hole H1, and the drain electrode 53 may be connected to the drain portion D through the second contact hole H2.


In an etching process to form the first and second contact holes H1 and H2 in the first passivation layer 50 and the gate insulating layer 40, removing the barrier pattern film 32 in the regions of the source and drain portions S and D below the first and second contact holes H1 and H2 may be conducted.


Accordingly, the source electrode 51 may stably contact the source portion S of the active patterned layer 21, and the drain electrode 53 may stably contact the drain portion D of the active patterned layer 21.


The active patterned layer 21, the gate electrode 45, and the source and drain electrodes 51 and 53 form the driving TFT Tr.


A second passivation layer 60 as an insulating layer may be formed on the source and drain electrodes 51 and 53, as seen in FIG. 2.


The second passivation layer 60 may be made of an inorganic insulating material or organic insulating material. The second passivation layer 60 may include a third contact hole H3 exposing the drain electrode 53.


A first electrode 71 may be formed on the second passivation layer 60 and be patterned to correspond to each pixel region P.


A bank 73 may be formed on the first electrode 71 to cover edge portions of the first electrode 71 and separate the pixel regions P.


An organic light emitting layer 75 may be formed on the first electrode 71 and in an opening of the bank 73.


A second electrode 80 may be formed on the organic light emitting layer 75 and entirely over the substrate 11.


The first electrode 71, the organic light emitting layer 75 and the second electrode 80 form an organic light emitting diode OD. One of the first and second electrodes 71 and 80 serves as an anode, and the other of the first and second electrodes 71 and 80 serves as a cathode.


One of the first and second electrodes 71 and 80 may be made of a transparent conductive material according to an emission type of the display device. For example, in a case of a bottom emission type display device, the first electrode 71 may be transparent, and in a case of a top emission type display device, the second electrode 80 may be transparent.


When an LCD is used as the display device, a switching TFT having the same structure as the driving TFT Tr described above may be formed in a pixel region, and a pixel electrode corresponding to the first electrode 71 described above may be connected to a drain electrode of the switching TFT.


A method of manufacturing the TFT substrate of this embodiment is explained with reference to FIGS. 4 to 7.


Referring to FIG. 4, a buffer layer 15 is formed on a substrate 11, and an amorphous silicon layer is formed on the buffer layer 15. After forming the amorphous silicon layer, a dehydrogenation using a heat treatment may be conducted.


Then, a laser annealing process is conducted for the amorphous silicon layer to crystallize the amorphous silicon layer, and thus a polycrystalline silicon layer 20 is formed.


In the crystallization process, grains GR are grown laterally, and thus protrusions 22 which protrude in an upward direction from the substrate 11 are formed at boundaries between the grains GR.


In this regard, the polycrystalline silicon layer 20 may have a thickness, for example, 500 Å or less, and the protrusions 22 may have a thickness, for example, but not limited to, 500 Å to 1000 Å.


Then, referring to FIG. 5, a barrier film 30 is formed on the polycrystalline silicon layer 20. The barrier film 30 may be made of an inorganic insulating material, for example, silicon oxide (SiO2) or silicon nitride (SiNx).


The barrier film 30 may have a thickness, for example, but not limited to, 200 Å to 300 Å.


Since a surface state of the polycrystalline silicon layer 20 is reflected in the barrier film 30, the barrier film 30 is formed to have protrusions corresponding to the protrusions 22 of the polycrystalline silicon layer 20.


Then, referring to FIG. 6, a CMP process is conducted for the substrate 11 having the barrier film 30 to planarize the substrate 11.


In the CMP process, a surface of the substrate 11 is polished using a polishing pad of a CMP apparatus in a state that a slurry is provided on the surface of the substrate 11.


The CMP process may be conducted such that a part of the barrier film 30 remains. When the CMP process is finished, a residual barrier film 31 as the barrier film 30 which is removed partially in a thickness direction and residual protrusions 23 as the protrusions 22 which are removed partially in a thickness direction are formed.


A surface of the residual barrier film 31 and surfaces of the residual protrusions 23 are substantially equal in height, and thus the substrate 11 having the residual barrier film 31 and the residual protrusions 23 has a substantially flat surface.


In other words, the recess space OS between the residual protrusions 23, i.e., a space on the grain GR is filled with the residual barrier film 31, and the residual protrusion 23 is exposed to the outside.


In this regard, the residual protrusions 23 and the residual barrier film 31 remaining have a thickness, for example, but not limited to, 200 Å to 300 Å.


As described above, in this embodiment, the CMP process is conducted in a state that the surface of the polycrystalline silicon layer 20 having the protrusions 22 is covered by the barrier film 30. Thus, a damage of the grains GR by the CMP can be prevented, and the protrusions 22 of the polycrystalline silicon layer 20 can be removed partially.


Accordingly, a defect of the polycrystalline silicon layer 20, i.e., a defect of an active patterned layer 21, which is formed by patterning the polycrystalline silicon layer 20, can be minimized, and thus a property of a TFT can be maximized.


Further, since the surface of the polycrystalline silicon layer 20 having the residual barrier film 31 formed thereon is substantially flat with the residual protrusions 23 not coming out upwardly, a defect of the active patterned layer 21 and a gate electrode 45 being short-circuited by the protrusions in a later process can be prevented.


Then, referring to FIG. 7, a mask process is conducted for the polycrystalline silicon layer 20 and the residual barrier film 31 to pattern them. Accordingly, the active patterned layer 21 is formed in the pixel region P, and the barrier pattern film 32 having substantially the same shape in plane as the active patterned layer 21 is formed.


Then, a gate insulating layer 40 is formed on the active patterned layer 21 and entirely over the substrate 11, and the gate electrode 45 is formed on the gate insulating layer corresponding to a channel portion CH of the active patterned layer 21. The gate electrode 45 may be made of a conductive material including a metal.


The gate insulating layer 40 may be made of an inorganic insulating material, for example, silicon oxide (SiO2) or silicon nitride (SiNx). The gate insulating layer 40 may be made of the same material as the barrier pattern film 32.


The gate insulating layer 40 may entirely cover the active patterned layer 21 having the barrier pattern film 32 thereon.


Accordingly, the gate insulating layer 40 is stacked on the residual protrusions 23 to directly contact the residual protrusions 23, and the barrier pattern film 32 and the gate insulating layer 40 are stacked on the grains GR at sides of the residual protrusions 23.


Side surfaces of the active patterned layer 21 may be slanted at a predetermined angle with a surface of the substrate 11 because of the mask process to form the active patterned layer 21, and may directly contact and be covered by the gate insulating layer 40.


Then, a doping process is conducted to dope source and drain portions S and D of the active patterned layer 21 with impurities. In the doping process, the gate electrode 45 may serve as a doping mask.


Then, a first passivation layer 50 may be formed on the gate electrode 45 and entirely over the substrate 11.


Then, a mask process is conducted for the first passivation layer 50 to form first and second contact holes H1 and H2.


In this mask process, etching the first passivation layer 50, the gate insulating layer 40 and the barrier pattern film 32 may be conducted. Accordingly, the first passivation layer 50 and the gate insulating layer 40 are etched to form the first and second contact holes H1 and H2, and the barrier pattern film 32 remaining at a region of a part of the source portion S and a region of a part of the drain portion D is etched and fully removed.


Then, a source electrode 51 and a drain electrode 53 may be formed on the first passivation layer 50 and be made of a conductive material including a metal.


The source electrode 51 may be stably connected to the substantially entire region of the part of the source portion S below the first contact hole H1 through the first contact hole H1, and the drain electrode 53 may be stably connected to the substantially entire region of the part of the drain portion D below the second contact hole H2 through the second contact hole H2.


Through the above processes, a driving TFT Tr is formed in the pixel region P of the TFT substrate 10, and at least one TFT, having substantially the same structure as the driving TFT Tr, other than the driving TFT Tr, may be formed in the pixel region P.


Then, an organic light emitting diode (OD of FIG. 2) connected to the driving TFT Tr is formed at the TFT substrate 10.


The TFT(s), which may be referred to as a TFT(s) for a pixel, formed in the pixel region P is described above by way of example, and the structure of the TFT may be applied equally to a TFT(s), which may be referred to as a TFT(s) for a driving circuit, formed in a GIP type scan driving circuit (SDC of FIG. 1).


This refers to FIG. 8 which is a cross-sectional view schematically illustrating a structure of a TFT for a driving circuit formed in a scan driving circuit according to an embodiment of the present disclosure.


Referring to FIG. 8, a TFT Trs for a driving circuit may be formed to have the same structure as the TFT (Tr of FIG. 2) for a pixel.


In other words, in the TFT Trs for a driving circuit, an active patterned layer 121 is formed on the buffer layer 15. A barrier pattern film 132 is formed on the active patterned layer 121 to fill recess spaces OS between residual protrusions 123 and have the same height as the residual protrusions 123, and thus a top surface of the active patterned layer 121 having the barrier pattern film 132 is planarized.


The gate insulating layer 40 extends along an entire surface of the active patterned layer 121 and covers the active patterned layer 121 entirely.


A gate electrode 145 is formed on the gate insulating layer 40 to correspond to a channel portion CH of the active patterned layer 121.


Source and drain electrodes 151 and 153 are formed on a first passivation layer 50 located on the gate electrode 145.


In the first passivation layer 50 and the gate insulating layer 30, a first contact hole H1 to connect the source electrode 151 and a source portion S and a second contact hole H2 to connect the drain electrode 153 and a drain portion D are formed.


The barrier pattern film 32 at a region of a part of the source portion S below the first contact hole H1 is substantially fully removed, and the barrier pattern film 32 at a region of a part of the drain portion S below the second contact hole H2 is substantially fully removed


A second passivation layer 60 is formed on the source and drain electrodes 151 and 153.


The active patterned layer (21 of FIG. 2) described above as a semiconductor layer for a TFT may be applied similarly as a conductive connection patterned layer.


An example of this is explained with reference to FIG. 9. FIG. 9 shows that a first metal patterned layer 255 and a second metal patterned layer 251 are formed at a TFT substrate, and a driving signal is transferred from one of the first and second metal patterned layers 255 and 251 to the other of the first and second metal patterned layers 255 and 251.


The first and second metal patterned layers 255 and 251 may be formed at the same layer, and it is assumed that the first metal patterned layer 255 is a power line to supply a power voltage, the second metal patterned layer 251 is a source electrode of a driving TFT supplied with the power voltage, and the first and second metal patterned layers 255 and 251 located at the same layer are not connected directly to each other because a large number of array elements are arranged at the TFT substrate.


A conductive connection patterned layer 221 may be formed such that the conductive connection patterned layer 221 is located with at least one insulating layer (e.g., the gate insulating layer 40 and the first passivation layer 50) between the conductive connection patterned layer 221 and the first and second metal patterned layers 255 and 251, and electrically connects the first and second metal patterned layers 255 and 251.


The conductive connection patterned layer 221 may be formed of a polycrystalline silicon doped with impurities like the source or drain portion (S or D of FIG. 2) of the active patterned layer (21 of FIG. 2) of the TFT to substantially have a conductivity to transfer an electrical signal.


Similarly to the active patterned layer of the TFT, the conductive connection patterned layer 221 may have residual protrusions 223, and a barrier pattern film 232 may be formed in recess spaces OS between the protrusions 223.


The conductive connection patterned layer 221 is located in a signal transfer path between the first and second metal patterned layers 255 and 251 to electrically connect them.


Further, a first connection electrode 266 may be formed to connect the first metal patterned layer 255 to the conductive connection pattern 221, and a second connection electrode 267 may be formed to connect the second metal patterned layer 251 to the conductive connection patterned layer 221.


In this case, a first connection contact hole Hic to connect the first connection electrode 266 to the conductive connection patterned layer 221 may be formed in at least one insulating layer (e.g., the gate insulating layer 40, and the first and second passivation layers 50 and 60) between the first connection electrode 266 and the conductive connection patterned layer 221, and a second connection contact hole H2c to connect the second connection electrode 267 to the conductive connection patterned layer 221 may be formed in at least one insulating layer (e.g., the gate insulating layer 40, and the first and second passivation layers 50 and 60) between the second connection electrode 267 to the conductive connection patterned layer 221. The barrier pattern film 232 at regions of parts of the conductive connection patterned layer 221 below the first and second connection contact holes H1c and H2c are fully removed to stably contact the first and second connection electrodes 266 and 267.


Further, a third connection contact hole H3c to connect the first connection electrode 266 to the first metal patterned layer 255 may be formed in at least one insulating layer (e.g., the second passivation layer 60) between the first connection electrode 266 and the first metal patterned layer 255, and a fourth connection contact hole H4c to connect the second connection electrode 267 to the second metal patterned layer 251 may be formed in at least one insulating layer (e.g., the second passivation layer 60) between the second connection electrode 267 to the second metal patterned layer 251.


The first and second metal patterned layers 255 and 251 being located at the same layer is described above by way of example. Alternatively, the first and second metal patterned layers 255 and 251 may be located at different layers with at least one insulating layer interposed therebetween. The first and second metal patterned layers 255 and 251 may be configured to directly contact the conductive connection patterned layer 221 without using corresponding connection electrodes.


In the above embodiment, the CMP process is conducted in a state that the surface of the polycrystalline silicon layer having the protrusions is covered by the barrier film. Thus, a damage of the grains GR by the CMP can be prevented, and the protrusions of the polycrystalline silicon layer can be removed partially.


Accordingly, a defect of the polycrystalline silicon layer can be minimized, and thus a property of a TFT can be maximized.


Further, since the surface of the polycrystalline silicon layer having the barrier film formed thereon is substantially flat with the residual protrusions not coming out upwardly, a defect of the active patterned layer and the gate electrode being short-circuited by the protrusions in a later process can be prevented and a property of a TFT can be secured.


It will be apparent to those skilled in the art that various modifications and variation can be made in the present disclosure without departing from the spirit or scope of the disclosure. Thus, it is intended that the present disclosure cover the modifications and variations of the described embodiments in this disclosure.


The various embodiments described above can be combined to provide further embodiments. These and other changes can be made to the embodiments in light of the above-detailed description. In general, in the following claims, the terms used should not be construed to limit the claims to the specific embodiments disclosed in the specification and the claims, but should be construed to include all possible embodiments along with the full scope of equivalents to which such claims are entitled. Accordingly, the claims are not limited by the disclosure.

Claims
  • 1. A thin film transistor (TFT) substrate, comprising: a thin film transistor (TFT) on a substrate, the TFT including: an active patterned layer of a polycrystalline silicon including a channel portion, a source portion and a drain portion, and including protrusions at boundaries between grains, and recess spaces formed between the protrusions;a barrier pattern film filling the recess spaces and forming a flat surface with the protrusions;a gate electrode on a gate insulating layer on the barrier pattern film and the protrusions, and the gate electrode overlaying the channel portion; anda source electrode and a drain electrode on the gate insulating layer and respectively contacting the source portion and the drain portion.
  • 2. The TFT substrate of claim 1, wherein the gate insulating layer directly contacts the barrier pattern film and the protrusions.
  • 3. The TFT substrate of claim 1, further comprising: a passivation layer on the gate electrode and below the source and drain electrodes;wherein the passivation layer and the gate insulating layer include first and second contact holes respectively exposing the source and drain portions; andwherein the barrier pattern film is removed at a part of the source portion below the first contact hole and a part of the drain portion below the second contact hole.
  • 4. The TFT substrate of claim 1, wherein a part of the gate insulating layer on the barrier pattern film and the protrusions is flat.
  • 5. The TFT substrate of claim 4, wherein the gate electrode is flat.
  • 6. The TFT substrate of claim 1, wherein the gate insulating layer covers side surfaces of the active patterned layer.
  • 7. The TFT substrate of claim 1, wherein the substrate includes an active region where a plurality of pixel regions are arranged, and wherein the TFT is formed in one of the plurality of pixel regions.
  • 8. The TFT substrate of claim 7, wherein the substrate includes a non-active region around the active region, and wherein another TFT is formed in a driving circuit in the non-active region.
  • 9. The TFT substrate of claim 1, further comprising: a connection patterned layer with at least one insulating layer interposed between the connection patterned layer and each of a first metal patterned layer and a second metal patterned layer, the connection patterned layer electrically connecting the first metal patterned layer and the second metal patterned layer, and the connection patterned layer being of a polycrystalline silicon doped with impurities and having other protrusions and other recess spaces; andwherein the other recess spaces of the connection patterned layer are filled with other barrier pattern film.
  • 10. The TFT substrate of claim 9, further comprising: a first connection electrode connecting the first metal patterned layer and the connection patterned layer; anda second connection electrode connecting the second metal patterned layer and the connection patterned layer; andwherein the other barrier pattern film is removed at a part of the connection patterned layer below a first connection contact hole through which the first connection electrode contacts the connection patterned layer and a part of the connection patterned layer below a second connection contact hole through which the second connection electrode contacts the connection patterned layer.
  • 11. A display device, comprising: a first electrode;a thin film transistor (TFT) substrate including a TFT, the TFT including a drain electrode connected to the first electrode, and the TFT including: an active patterned layer of a polycrystalline silicon including a channel portion, a source portion and a drain portion, and including protrusions at boundaries between grains and recess spaces between the protrusions;a barrier pattern film in the recess spaces and forming a flat surface with the protrusions;a gate electrode on a gate insulating layer located on the barrier pattern film and the protrusions, and the gate electrode overlaying the channel portion; anda source electrode and the drain electrode on the gate insulating layer and respectively contacting the source portion and the drain portion.
  • 12. The display device of claim 11, wherein the gate insulating layer directly contacts the barrier pattern film and the protrusions.
  • 13. The display device of claim 11, further comprising: a passivation layer on the gate electrode and below the source and drain electrodes;wherein the passivation layer and the gate insulating layer include first and second contact holes respectively exposing the source and drain portions; andwherein the barrier pattern film is removed at a part of the source portion below the first contact hole and a part of the drain portion below the second contact hole.
  • 14. The display device of claim 11, wherein a part of the gate insulating layer on the barrier pattern film and the protrusions is flat.
  • 15. The display device of claim 14, wherein the gate electrode is flat.
  • 16. The display device of claim 11, wherein the gate insulating layer extends to cover side surfaces of the active patterned layer.
  • 17. The display device of claim 11, wherein the substrate includes an active region where a plurality of pixel regions are arranged, and wherein the TFT is formed in one of the plurality of pixel regions.
  • 18. The display device of claim 17, wherein the substrate includes a non-active region around the active region, and wherein another TFT is formed in a driving circuit in the non-active region.
  • 19. The display device of claim 11, further comprising: a connection patterned layer having at least one insulating layer interposed between the connection patterned layer and each of a first metal patterned layer and a second metal patterned layer, the connection patterned layer electrically connecting the first metal patterned layer to the second metal patterned layer, and the connection patterned layer being of a polycrystalline silicon doped with impurities and having other protrusions and other recess spaces; andwherein the other recess spaces of the connection patterned layer include other barrier pattern film.
  • 20. The display device of claim 19, further comprising: a first connection electrode connecting the first metal patterned layer and the connection patterned layer;a second connection electrode connecting the second metal patterned layer and the connection patterned layer; andwherein the other barrier pattern film is removed at a part of the connection patterned layer below a first connection contact hole through which the first connection electrode contacts the connection patterned layer and a part of the connection patterned layer below a second connection contact hole through which the second connection electrode contacts the connection patterned layer.
  • 21. The display device of claim 11, further comprising: an organic light emitting layer on the first electrode; anda second electrode on the organic light emitting layer.
  • 22. A thin film transistor, comprising: a polycrystalline silicon layer including a channel portion, a source portion and a drain portion, the polycrystalline silicon layer having protrusions at boundaries between grains of the polycrystalline layer, and having recess spaces between the protrusions;a barrier layer in the recess spaces, the barrier layer having upper surfaces at a same level as upper surfaces of the protrusions;a gate insulating layer on the upper surfaces of the barrier layer and the protrusions;a gate electrode on the gate insulating layer over the channel portion; anda source electrode and a drain electrode on the gate insulating layer and respectively contacting the source portion and the drain portion.
  • 23. The thin film transistor of claim 22, wherein the gate electrode has an upper surface at a same level from a surface of the substrate.