Thermal Effect Measurement with Near-Infrared Spectroscopy

Abstract

A method of determining a physical property of a composite material includes providing a series of composite materials surfacing films, which are subjected to increasing thermal experience to create a set of thermal effect standards, collecting near-IR spectra on those standards, performing data pre-processing and then multivariate calibration on the spectra of the composite materials surfacing films, and using that calibration to predict the thermal effect for samples in question.

Description

FIELD OF THE INVENTION

The disclosure relates to methods for determining thermal effect in composite materials. More particularly, the disclosure relates to a method for accurately assessing thermal effect in a composite material or surfacing film using near-infrared spectroscopy.

BACKGROUND OF THE INVENTION

Resin-fiber composite materials are utilized in a variety of applications including the aerospace industry, for example. Structures which are constructed of resin-fiber composite materials may be exposed to heat, which may affect the composite materials in various ways. These heat-induced effects may include chemical degradation in which changes such as oxidation, material loss and the breaking and/or forming of chemical bonds occurs in the polymer chemical structure of the composite materials. Resin decomposition, charring and fiber decomposition of the composite materials may occur at increasing temperatures.

Composite materials and epoxy-based surfacing films are typically cured under a vacuum at 250-350° F. for several hours. Repairs to the composite materials or surfacing films can become necessary if voids are found during an NDI inspection or if a flaw is found. These repairs may require the use of heating blankets that are notorious for having hot spots. Thus, during the repair some areas of the composite material or surfacing film may become overheated; in the case of epoxy-based surfacing films, a color change (dark or blackened) may be noticeable. Thermal effect may affect the mechanical and structural integrity of composite materials and surfacing films.

Repair or removal of heat-affected composite materials or surfacing films on a structure may involve first determining the degree of harmful heat effect to the composite materials or surfacing films. Although determining the degree of heat effect to composite materials or surfacing films may be performed by visual inspection, heat effect may not be visually apparent. Current methods of determining the presence and extent of heat effect in composite materials and surfacing films includes obtaining an infrared spectrum of a heat-affected composite standard and correlating the infrared spectrum obtained from the composite standard with the degree of thermal effect of the composite standard. An infrared spectrum obtained from the composite material or surfacing film the heat effect of which is in question can then be compared to the infrared spectrum obtained from the composite standard to determine the presence and assess the degree of thermal effect in the composite material or surfacing film.

Calibration of infrared sensors to residual strength in composite materials or surfacing films correlates the resin condition as read from the infrared spectrum to the residual strength of the material or film which degrades as the resin degrades with progressively increasing temperatures. Therefore, the infrared sensors may be calibrated using time-controlled thermal soak standards which are obtained by exposing various composite materials or surfacing film controls to various temperatures for a particular time period such as one hour, for example. One method of preparing the standards includes placing the standards in an oven which is calibrated periodically and monitored continuously.

Near infrared radiation is capable of penetrating paint layers on a composite material or surfacing film to detect underlying composite material or film conditions. Hand-held near IR devices are generally less expensive than hand-held FT-IR devices and are often lighter and easier to use as well. Therefore, a method for accurately assessing thermal effect in a composite material or surfacing film using near-infrared spectroscopy is needed.

SUMMARY OF THE INVENTION

The disclosure is further generally directed to a method of determining a physical property of a composite material. An illustrative embodiment of the method includes providing a series of composite material standards with increasing thermal exposure (with or without a surfacing film), irradiating the composite material standards and/or the surfacing films with near-IR infrared energy, detecting near-infrared energy reflected from the composite material standards surfacing films, performing multivariate calibration on the series of the near-infrared spectra reflected from the composite material standards surfacing films, performing a multivariate calibration to the near-infrared spectra from the standards to make a model of the spectral changes with increasing thermal exposure (or decreasing mechanical properties), and using the multivariate model to predict the thermal exposure or mechanical properties of composite materials in question.

BRIEF DESCRIPTION OF THE ILLUSTRATIONS

FIG. 1 is a series of near-IR spectra on thermally exposed graphite composite (CFRP) standards. These standards were exposed for 1 hour each at 400, 450, 500° F. and there is also one with no thermal exposure.

FIG. 2 is the same series of near-IR spectra from FIG. 1 but with first derivative and 7 point smoothing pre-processing with the Savitzky Golay method.

FIG. 3 is the regression vector from the multivariate calibration of the near-IR spectra to the un-notched compression test stress results of the standards using the PLS (partial least squares) multivariate calibration method.

FIG. 4 is a flow diagram which illustrates the multivariate calibration and prediction method.

FIG. 4A is a flow diagram which illustrates important details in the multivariate calibration and prediction method.

FIG. 5 is a flow diagram of an aircraft production and service methodology.

FIG. 6 is a block diagram of an aircraft.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Referring initially to FIGS. 1-4, an illustrative embodiment of a method of multivariate calibration for thermal effect with near-IR spectra is shown. As shown in block 402 of flow diagram 400 in FIG. 4, the thermal effect calibration begins with CFRP standards that are carefully cooked and then tested to obtain residual mechanical properties. Block 404 shows the mid-IR spectral data collection step and the raw infrared spectra are shown in FIG. 1. Block 406 shows the data pre-processing step and FIG. 2 shows the results of a typical pre-processing method. Block 408 shows the multivariate calibration step and FIG. 3 shows the regression coefficients that result from that calibration. Block 410 shows the step where the multivariate calibration is saved in an appropriate format and then loaded into the hand-held near-IR device that will be used to read thermal effect on CFRP material in question. Block 412 shows material in question being predicted for residual stress values that would indicate the extent of thermal effect in the material in question. If the original standards are predicted here, one can develop an accuracy figure for the methods based on the difference between the known stress numbers and those predicted by the method just developed.

Referring next to FIG. 4A, a flow diagram 400a which illustrates an illustrative embodiment of a method of optimizing the data pre-processing method for CFRP thermal effect calibration with multivariate methods. In block 402a, a thermal effect standard is provided. The thermal effect standard may have been fabricated according to the method which was heretofore described in a co-pending patent application assigned to the common assignee of the present disclosure under attorney docket number 82,000-175. In block 404a, the infrared spectra of the thermal effect standards are made using the near-IR wavelength range of from about 1.6 μm to about 2.4 μm. In block 404a, a surface of the thermal effect standard is irradiated with near-infrared energy having a wavelength of from about 0.75 μm to about 1.4 μm.

Referring next to FIGS. 5 and 6, embodiments of the disclosure may be used in the context of an aircraft manufacturing and service method 78 as shown in FIG. 5 and an aircraft 94 as shown in FIG. 6. During pre-production, exemplary method 78 may include specification and design 80 of the aircraft 94 and material procurement 82. During production, component and subassembly manufacturing 84 and system integration 86 of the aircraft 94 takes place. Thereafter, the aircraft 94 may go through certification and delivery 88 in order to be placed in service 90. While in service by a customer, the aircraft 94 may be scheduled for routine maintenance and service 92 (which may also include modification, reconfiguration, refurbishment, and so on).

Each of the processes of method 78 may be performed or carried out by a system integrator, a third party, and/or an operator (e.g., a customer). For the purposes of this description, a system integrator may include without limitation any number of aircraft manufacturers and major-system subcontractors; a third party may include without limitation any number of vendors, subcontractors, and suppliers; and an operator may be an airline, leasing company, military entity, service organization, and so on.

As shown in FIG. 6, the aircraft 94 produced by exemplary method 78 may include an airframe 98 with a plurality of systems 96 and an interior 100. Examples of high-level systems 96 include one or more of a propulsion system 102, an electrical system 104, a hydraulic system 106, and an environmental system 108. Any number of other systems may be included. Although an aerospace example is shown, the principles of the invention may be applied to other industries, such as the automotive industry.

The apparatus embodied herein may be employed during any one or more of the stages of the production and service method 78. For example, components or subassemblies corresponding to production process 84 may be fabricated or manufactured in a manner similar to components or subassemblies produced while the aircraft 94 is in service. Also, one or more apparatus embodiments may be utilized during the production stages 84 and 86, for example, by substantially expediting assembly of or reducing the cost of an aircraft 94. Similarly, one or more apparatus embodiments may be utilized while the aircraft 94 is in service, for example and without limitation, to maintenance and service 92.

Although the embodiments of this disclosure have been described with respect to certain exemplary embodiments, it is to be understood that the specific embodiments are for purposes of illustration and not limitation, as other variations will occur to those of skill in the art.

Claims

1. A method of determining a physical property of a composite material, comprising: providing at least one of a composite material and a surfacing film;irradiating said at least one of a composite material and a surfacing film with near-infrared energy;detecting near-infrared energy reflected from said at least one of a composite material and a surfacing film;performing multivariate analysis on a spectrum of said near-infrared energy reflected from said at least one of a composite material and a surfacing film;providing at least one thermal effect standard;obtaining a correlation of a spectrum of near-infrared energy reflected from said at least one thermal effect standard and a residual strength of said at least one thermal effect standard; andquantifying a degree of heat effect to said at least one of a composite material and a surfacing film by comparing results of said multivariate analysis with said correlation.

2. The method of claim 1 wherein said at least one of a composite material and a surfacing film comprises a resin-fiber composite material.

3. The method of claim 1 wherein said at least one of a composite material and a surfacing film comprises an epoxy-based surfacing film.

4. The method of claim 1 wherein said providing at least one thermal effect standard comprises providing at least one of a composite material specimen and a surfacing film specimen and heating said at least one of a composite material specimen and a surfacing film specimen.

5. The method of claim 1 wherein said obtaining a correlation of a spectrum of near-infrared energy reflected from said at least one thermal effect standard and a residual strength of said at least one thermal effect standard comprises subjecting said at least one thermal effect standard to mechanical tests to obtain said residual strength of said at least one thermal effect standard.

6. The method of claim 1 wherein said providing a thermal effect standard comprises providing a specimen oven, precisely calibrating said specimen oven to at least one exposure temperature, placing at least one of a composite material specimen and a surfacing film specimen in said specimen oven and operating said specimen oven at said at least one exposure temperature.

7. The method of claim 6 wherein said precisely calibrating said specimen oven to at least one exposure temperature comprises providing at least one thermocouple, placing said at least one thermocouple in said specimen oven and operating said specimen oven at said exposure temperature as indicated by said at least one thermocouple.

8. The method of claim 1 wherein said providing at least one thermal effect standard comprises providing a plurality of thermal effect standards having various degrees of heat effect.

9. A method of determining a physical property of a composite material, comprising: providing at least one of a composite material and a surfacing film;irradiating said at least one of a composite material and a surfacing film with near-infrared energy having a wavelength of from about 0.75 μm to about 1.4 μm;detecting near-infrared energy reflected from said at least one of a composite material and a surfacing film;performing multivariate analysis on a spectrum of said near-infrared energy reflected from said at least one of a composite material and a surfacing film;providing at least one thermal effect standard;obtaining a correlation of a spectrum of near-infrared energy reflected from said at least one thermal effect standard and a residual strength of said at least one thermal effect standard; andquantifying a degree of heat effect to said at least one of a composite material and a surfacing film by comparing results of said multivariate analysis with said correlation.

10. The method of claim 9 wherein said at least one of a composite material and a surfacing film comprises a resin-fiber composite material.

11. The method of claim 9 wherein said at least one of a composite material and a surfacing film comprises an epoxy-based surfacing film.

12. The method of claim 9 wherein said providing at least one thermal effect standard comprises providing at least one of a composite material specimen and a surfacing film specimen and heating said at least one of a composite material specimen and a surfacing film specimen.

13. The method of claim 9 wherein said obtaining a correlation of a spectrum of near-infrared energy reflected from said at least one thermal effect standard and a residual strength of said at least one thermal effect standard comprises subjecting said at least one thermal effect standard to mechanical tests to obtain said residual strength of said at least one thermal effect standard.

14. The method of claim 9 wherein said providing a thermal effect standard comprises providing a specimen oven, precisely calibrating said specimen oven to at least one exposure temperature, placing at least one of a composite material specimen and a surfacing film specimen in said specimen oven and operating said specimen oven at said at least one exposure temperature.

15. The method of claim 14 wherein said precisely calibrating said specimen oven to at least one exposure temperature comprises providing at least one thermocouple, placing said at least one thermocouple in said specimen oven and operating said specimen oven at said exposure temperature as indicated by said at least one thermocouple.

16. The method of claim 9 wherein said providing at least one thermal effect standard comprises providing a plurality of thermal effect standards having various degrees of heat effect.

17. A method of determining a physical property of a composite material, comprising: providing at least one of a composite material and a surfacing film;irradiating said at least one of a composite material and a surfacing film with near-infrared energy;detecting near-infrared energy reflected from said at least one of a composite material and a surfacing film;performing multivariate analysis on a spectrum of said near-infrared energy reflected from said at least one of a composite material and a surfacing film;providing at least one thermal effect standard by: providing an oven;placing at least one thermocouple at a measurement location in said oven;operating said oven;monitoring a temperature output of said at least one thermocouple;providing at least one of a composite material specimen and a surfacing film specimen;placing said at least one of a composite material specimen and a surfacing film specimen at said measurement location in said oven; andheat treating said at least one of composite material specimen and a surfacing film specimen as at least one thermal effect standard by operating said oven according to said temperature output of said at least one thermocouple;obtaining a correlation of a spectrum of near-infrared energy reflected from said at least one thermal effect standard and a residual strength of said at least one thermal effect standard; and quantifying a degree of heat effect to said at least one of a composite material and a surfacing film by comparing results of said multivariate analysis with said correlation.

18. The method of claim 17 wherein said irradiating said at least one of a composite material and a surfacing film with near-infrared energy comprises irradiating said at least one of a composite material and a surfacing film with near-infrared energy having a wavelength of from about 0.75 μm to about 1.4 μm.

19. The method of claim 17 further comprising obtaining values for said residual strength in said at least one thermal effect standard by subjecting said at least one thermal effect standard to a mechanical test.

20. The method of claim 17 further comprising placing metal plates at said measurement location in said oven and wherein said placing at least one thermocouple at a measurement location in said oven comprises placing a bundle of thermocouples between said metal plates.