Claims
- 1. A method of preparing thermoplastically processable starch which is a substantially water free, combination of starch with at least one additive, the method comprising admixing starch with at least 5 weight percent based on the weight of the mixture of at least one additive, said additive being such that it reduces the melting point of the starch in the mixture to below the decomposition temperature of the starch, said additive having a solubility parameter of more than 15 cal.sup.1/2 cm.sup.-2/3, said additive having a vapor pressure of less than 1 bar in said mixture at a temperature of about the melting point of said mixture, and melting and mixing said admixture until it is substantially water free and until the crystalline content is less than 5%.
- 2. A method according to claim 1 wherein said additive has a solubility parameter of 15 to 25 cal.sup.1/2 cm.sup.-3/2 within a temperature range of 150.degree.-300.degree. C. and the interfacial energy between the additive and the starch is not greater than 20% of the individual interfacial energies of the starch and additive with respect to air.
- 3. A method according to claim 1 wherein the portion .delta..sub.P and .delta..sub.H are at least twice as large as the dispersion portion of .delta..sub.d of the solubility parameter .delta. of said at least one additive.
- 4. A method according to claim 1 wherein the additive is about 10 to 35% based on the total weight of said admixture.
- 5. A method according to claim 1 wherein the mixing of the molten starch and additive is effected within a temperature range of 150.degree. to 300.degree. C.
- 6. A method according to claim 5 wherein the mixing of the molten starch and additive is effected within a temperature range of 160.degree. to 190.degree. C.
- 7. A method according to claim 1 wherein the melting and mixing is effected in a plastic processing machine and a total energy supplied to the mixture is at least 0.3-0.35 KWh/kg mass-output of the mixture.
- 8. A method according to claim 1 wherein the additive is selected from the group consisting of dimethyl sulfoxide, sorbitol, glycerin, ethylene glycol, propylene glycol, diglyceride, diglycol ether, formamide, dimethylformamide, methylformamide, dimethylurea, dimethylacetamide, methylacetamide, ethanol amine and propanol amine.
- 9. A method according to claim 1 wherein at least one member of the group consisting of blending component, lubricant, softening agent, flexibilizing agent, pigmenting agent cross-linking agent and mold removal agent is added to said mixture of starch and additive.
- 10. A method according to claim 1 wherein the resulting melt is formed into granulates, flakes, pills, powers, tablets, fibers, extrudates or sheets.
- 11. A method according to claim 1 wherein the starch admixed has an average molecular weight determined by intrinsic viscosity of more than 1 million.
- 12. A method according to claim 11 wherein the average molecular weight lies within the range of 3 million to 10 million.
- 13. A method according to claim 1 wherein said steps are effected under substantially anhydrous conditions.
- 14. A method according to claim 1 wherein up to 50 weight % of one or more blending components consisting of the following materials:
- gelatin
- a protein
- a polysaccharide
- a cellulose derivative
- a synthetic polymer which is at least approximately soluble in the additive for the starch
- a gelatin phthalate
- is combined with said mixture of starch and additive.
- 15. A method according to claim 1 wherein the additive is of the formula: ##STR3## in which K, m and n individually are 0 to 5 provided n=0 if m, k.noteq.0, z is a positive integer, R.sup.1 is H, CH.sub.3, or --(CH.sub.2).sub.4 --C and R.sup.II to R.sup.VI individually are OH or NH.sub.2 provided at least one is OH, or ##STR4## in which R.sub.1 is H, --CH.sub.3, --CH.sub.2 --CH.sub.3 or NR.sup.3 R.sup.4, and R.sup.3 and R.sup.4 are individually H, --CH.sub.3, --CH.sub.2 --CH.sub.3 provided in case that R.sup.1 equal NR.sup.3 R.sup.4, R.sup.4 are not H or alkyl simultaneously.
- 16. A method according to claim 1 wherein the melting and mixing is continued until the starch has a moisture content of less than 1.0%.
- 17. A method according to claim 1 wherein the polar portion .delta..sub.P and the portion .delta..sub.H of the solubility parameter .delta. corresponding to the hydrogen bonds of said additive are each larger than the dispersion portion .delta..sub.d of the solubility parameter .delta..
- 18. A method according to claim 1 wherein the starch has a water content of about 17% before said mixing and melting.
- 19. A method according to claim 1 wherein glycerol in an amount of 5 to 35% is combined with said mixture.
- 20. A thermoplastically processable starch comprising a substantially water free, homogeneous mixture having a crystalline content of less than 5% of starch and at least 5 weight % of at least one additive having a solubility parameter of more than 15 cal.sup.1/2 cm.sup.-3/2, said additive having a vapor pressure in the mixture of less than 1 bar at about the melting point of the homogeneous mixture, and the melting point of the mixture being lower than the decomposition temperature of the starch.
- 21. A thermoplastically processable starch according to claim 20 wherein the average molecular weight of the starch determined by intrinsic viscosity is at least 1 million.
- 22. A thermoplastically processable starch according to claim 20 wherein the average molecular weight of the starch determined by intrinsic viscosity is 3 to 10 million.
- 23. A thermoplastically processable starch according to claim 20 wherein it is present in the form of granulates, flakes, pills, tablets, power or fiber.
- 24. A thermoplastically processable starch according to claim 20 wherein the moisture content is less than 1.0%.
- 25. A thermoplastically processable starch according to claim 20 wherein the additive is at least one member selected from the group consisting of dimethyl sulphoxide, sorbitol, glycerin, ethylene glycol, propylene glycol, triglyceride, diglycol ether, formamide, methylformamide, dimethyl formamide, dimethyl acetamide, methyl acetamide, dimethyl urea, ethanol amine and propanol amine.
- 26. A thermoplastically processable starch according to claim 20 wherein said additive has a solubility parameter of 15 to 25 cal.sup.1/2 cm.sup.-3/2 within a temperature range of 150.degree. to 300.degree. C.
- 27. A thermoplastically processable starch according to claim 20 wherein the polar portion .delta..sub.P and the portion .delta..sub.P of the solubility parameter .delta. corresponding to the hydrogen bonds of said additive are each larger than the dispersion portion .delta..sub.d of the solubility parameter .delta..
Priority Claims (1)
Number |
Date |
Country |
Kind |
4083/88 |
Nov 1988 |
CHX |
|
BACKGROUND OF THE INVENTION
This is a continuation of application Ser. No. 07/785,931 filed on Oct. 31, 1991, now abandoned which was a continuation-in-part of application Ser. No. 07/536,683 filed Jul. 11, 1990 and now abandoned.
US Referenced Citations (1)
Number |
Name |
Date |
Kind |
4330443 |
Rankin |
May 1982 |
|
Foreign Referenced Citations (2)
Number |
Date |
Country |
0327505 |
Sep 1989 |
EPX |
1014801 |
Dec 1965 |
GBX |
Continuations (1)
|
Number |
Date |
Country |
Parent |
785931 |
Oct 1991 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
536683 |
Jul 1990 |
|