The present invention relates to tires and tire forming molds, and more particularly, to tires that are excellent in on-ice performance and on-snow performance, and tire forming molds used for manufacturing the same.
Conventionally, various contrivances have been made for improving the on-ice performance and on-snow performance of winter tires.
For example, a technology which increases edge components present in a contact patch and simultaneously improves the snow-gripping effect and the travelling performance on icy and snowy road surfaces (iced road surfaces and snowed road surfaces) of tires, by providing a plurality of sipes on each block formed on a tread portion, is proposed in JP 2002-192914 A (PTL 1).
In addition, for example, JP H11-301217 A (PTL 2) proposes a technology which uses foamed rubber as a cap rubber on a tire having a tread rubber with a so-called cap-and-base structure comprising a cap rubber and a base rubber, thereby significantly improving the drainage performance and the on-ice performance and on-snow performance of the tire.
Also, for example, JP 2009-67378 A (PTL 3) proposes, as is shown in
PTL 1: JP 2002-192914 A
PTL 2: JP H11-301217 A
PTL 3: JP 2009-67378 A
However, in the technology disclosed in PTL 1 which provides sipes on each block, there is a problem that if the number of sipes is increased too much, the block rigidity will be decreased and collapsing of a block may easily happen, which causes a reduction in the ground contact area and, rather, degrades the on-ice performance and on-snow performance.
In addition, in the technology disclosed in PTL 2 using foamed rubber for the cap rubber, there are cases where a reduction in the rigidity of the entire blocks is caused by usage of foamed rubber, so that the wear resistance of the tire is not always sufficient.
Further, for example, in the technology disclosed in PTL 3 which provides protrusions with a sharp-ended shape on the surface of the tread portion, due to the fact that the rigidity of the protrusion is low, there are cases where the protrusions collapse and the desirable performance cannot be obtained, particularly when a large load is placed on the tire, such as when the load on the front wheel is increased due to nose diving of the vehicle, etc. Namely, in the technology providing protrusions with a sharp-ended shape on the surface of the tread portion, there are cases that protrusions 2 collapse due to the contacting with road surface T, the volume of gaps 3 for water removing is reduced, the drainage is reduced, and consequently the desirable on-ice performance and on-snow performance may not be obtained, as is shown in
In addition, as the result of repeated study by the inventors on tires applying the technologies disclosed in PTL 1 to 3, a problem is also found that the on-ice performance and on-snow performance cannot be sufficiently obtained on those conventional tires, particularly new tires, though the reason is not clear. Therefore, there is still room for further improvement of the on-ice performance and on-snow performance of, in particular, new tires, in the technologies disclosed in PTL 1 to 3.
An object of the present invention is to solve the aforementioned problems, and to provide a tire with improved on-ice performance and on-snow performance and a tire forming mold used for manufacturing (forming) the same.
The inventors have intensively studied to solve the problems aforementioned.
As a result, the present inventor has completed the present invention by finding that by forming a predetermined microstructure on the tread surface of the tread portion, it is possible to suppress the reduction of the block rigidity and the drainage performance of a tire, thereby to obtain further improved on-ice performance and on-snow performance of the tire, and to allow the tire to exhibit sufficient on-ice performance and on-snow performance even when the tire is brand new.
The present invention is made based on the findings above, and the primary features thereof are summarized as follows.
The tire of the present invention is characterized in that at least a part of the tread surface of the tread portion has a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less. In this way, by having at least a part of the tread surface of the tread portion (the surface in contact with the road surface when travelling) having a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less, it is possible to suppress the degradation of the block rigidity, and simultaneously improve the on-ice performance and on-snow performance of the tire, by increasing the frictional force between the tire surface and the road surface. Here, “Rku” refers to the kurtosis of the assessed profile (JIS B 0601 (2001)) of the tread surface of the tread portion.
In addition, the tire forming mold tire of the present invention is a tire forming mold, and is characterized in having a tread-surface molding surface for molding the tread surface of the tread portion of the tire, at which at least a part of the tread-surface molding surface has a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less.
This is because that in this way, it is possible to form the aforementioned tire excellent in on-ice performance and on-snow performance, in which at least a part of the tread surface of the tread portion has a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less.
According to the present invention, it is possible to provide a tire with improved on-ice performance and on-snow performance and also a tire forming mold that can be used for forming the same.
The present invention will be further described below with reference to the accompanying drawings, wherein:
a) is a schematic sectional view schematically showing the tread surface of the tread portion of a conventional tire.
a) to (c) are other examples of the shape of a part of the tread surface of the tread portion of the tire.
The tire and the tire forming mold of the present invention is explained hereinafter. The tire of the present invention is characterized in that a predetermined microstructure is formed on at least a part of the tread surface (the surface that contacts a road surface) of the tread portion, and the tread portion has predetermined surface properties (tread surface properties). Additionally, the tire forming mold of the present invention is used for manufacturing the tire of the present invention, characterized in that the tread-surface molding surface has predetermined surface properties by forming a predetermined microstructure on the inner surface of the mold, specifically at least a part of the tread-surface molding surface for molding the tread surface of the tire.
<Tire>
As is shown in
In addition, the tire 20 of the embodiment has a carcass 7 toroidally extending between a pair of bead cores 4a which are embedded in the pair of bead portions 4, and a belt 8 including belt layers 8a and 8b which are disposed on the outside of the carcass 7 in the tire radial direction. Further, a tread rubber made from non-foamed rubber is disposed on the outside of belt 8 in the tire radial direction.
Here, micro protrusions with a predetermined shape are formed on at least a part of the tread surface of the tread portion (in this embodiment, the entire tread surface) of the tire 20. Specifically, according to an enlarged plan view of a surface 6a of the tread portion 6 shown in
Further, although
Additionally, in the tire 20, the tread surface of the tread portion has surface properties with a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less, and consequently it is possible to suppress the degradation of the block rigidity and the drainage performance, and simultaneously improve the on-ice performance and on-snow performance of the tire sufficiently.
Namely, in the tire 20, the tread surface of the tread portion has surface properties with a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less, and consequently it is possible to remove a water film on the road surface (to allow the tire to exhibit a better drainage performance) by utilizing the gaps among protrusions 9 when the tire becomes in contact with the road surface. In addition, it is possible to improve the on-ice performance and on-snow performance of the tire by increasing the frictional force between the tread surface of the tread portion and the road surface.
Further, in the tire 20, the suppression of the degradation of the drainage performance and the improvement of the on-ice performance and on-snow performance is accomplished by forming micro protrusions 9 having a predetermined shape, therefore there is no need to form an excessive number of sipes, or utilize foamed rubber, etc.
In addition, the tire 20 may exhibit sufficient on-ice performance and on-snow performance even when the tire is new (in unused state), although the reason is not clear.
Therefore, with the tire 20, it is possible to further improve the on-ice performance and on-snow performance of the tire even when it is new, by suppressing the degradation of the block rigidity and the drainage performance.
Here, for the tire 20, it is more preferable that the part with protrusions formed thereon has surface properties with a surface roughness at which the kurtosis of the assessed profile Rku is 1.5 or less, for the same reason.
In addition, for the tire 20, it is preferable that the protrusions 9 have a hemispherical shape. This is because that if the protrusions 9 have a hemispherical shape, the protrusions 9 are unlikely to collapse and the drainage performance may be ensured.
Further, for the tire 20, it is preferable that the height H of the protrusions 9 formed on the tread surface of the tread portion is 1 to 50 μm. This is because that if the height H is set to be 1 μm or more, it is possible to improve the drainage performance by ensuring a sufficient volume of gaps among the protrusions 9. In addition, if the height H of the protrusions 9 is set to be 50 μm or less, it is possible to sufficiently ensure the drainage performance by increasing the rigidity of the protrusions 9.
Here, the height of the protrusions 9 refers to the distance along the tire radial direction between a first imaginary plane perpendicular to a tire radial direction line extending across the distal ends of the protrusions 9 (the outer ends in the tire radial direction), and a second imaginary plane closest to the aforementioned first imaginary plane among the imaginary planes contacting the outer contour line of the protrusions 9 and perpendicular to the aforementioned tire radial direction line.
Note that the height of the protrusions 9 may be measured with an SEM or microscope.
In addition, it is preferable that the tire of the present invention has a surface roughness satisfying the condition that
Rsk<0
on at least a part of the tread surface of the tread portion.
In this way, it is possible to further suppress the degradation of block rigidity and drainage performance, and simultaneously improve the on-ice performance and on-snow performance of tires. Namely, the skewness of the assessed profile Rsk of the tread surface of the tread portion satisfies the condition:
Rsk<0
Therefore, it is possible to further suppress the degradation of the block rigidity and the drainage performance, and simultaneously further improve the on-ice performance and on-snow performance of the tire sufficiently. Namely, the aforementioned tire has surface properties that Rsk<0, and consequently, even in the case where a large load is placed on the tire, the protrusions are unlikely to collapse, and therefore it is possible to ensure the block rigidity and water-removing paths, because that the protrusions are of a shape of a high rigidity.
Further, it is more preferable that in the tire of the present invention, the part with protrusions 9 formed thereon has surface properties satisfying the following condition:
Rsk<−0.1
Here, “Rsk” refers to the skewness of the assessed profile (JIS B 0601 (2001)) of the tread surface of the tread portion. Further, the “Rsk” and “Rku” are the values measured in a unit length (1 mm).
Here, it is preferable that the tire of the present invention has surface properties satisfying the following condition:
50 μm≦RSm≦250 μm
In this way, by setting the RSm of at least a part of the tread surface of the tread portion to be 50 to 250 μm, it is possible to further suppress the degradation of the block rigidity, increase the frictional force between the tire surface and the road surface, and simultaneously further improve the on-ice performance and on-snow performance of tires. In addition, it is possible to suppress the degradation of the drainage performance. It is also possible to further suppress the degradation of the block rigidity and the drainage performance, and simultaneously further improve the on-ice performance and on-snow performance of the tire sufficiently, because that the RSm of the tread surface of the tread portion is 50 to 250 μm.
Namely, since the RSm of the tread surface of the tread portion is 50 μm or more, it is possible to obtain a sufficiently large protrusion external diameter and a sufficiently large distance between the protrusions. Therefore, it is possible to achieve both the water-film removing on a road when the tread surface of the tread portion comes in contact with the road surface by utilizing the gaps among protrusions 9, and the improvement of the on-ice performance and on-snow performance by increasing the frictional force between the tread surface of the tread portion and the road surface.
Further, since the RSm of the tread surface of the tread portion is 250 μm or less, it is possible to sufficiently increase the frictional force between the tread surface of the tread portion and the road surface by forming a sufficient number of protrusions in a high density on the tread surface of the tread portion.
Further, for the tire of the present invention, it is preferable that the RSm is 50 to 250 μm in the range of 90% or more of the area of the tread surface of the tread portion. This is because that by setting the Rsm to be 50 to 250 μm in the range of 90% or more of the area of the tread surface of the tread portion, it is possible to sufficiently increase the effect to be obtained by setting the surface properties in a predetermined range.
Here, in the tire 20, it is more preferable that the RSm of the tread surface of the tread portion is 60 to 150 μm. This is because that by setting the RSm of the tread surface of the tread portion to be 60 μm or more, it is possible to improve the drainage performance sufficiently, and simultaneously increase the frictional force between the tread surface of the tread portion and the road surface sufficiently. Additionally, by setting the RSm of the tread surface of the tread portion to be 150 μm or more, it is possible to increase the frictional force between the tread surface of the tread portion and the road surface sufficiently.
Here, “RSm” refers to the mean width of the profile elements of the tread surface of the tread portion. Additionally, “RSm” may be measured according to JIS B 0601 (2001).
In addition, it is preferable that the tire of the present invention has a surface roughness at which Ra is 1 μm or more and 50 μm or less, on at least a part of the tread surface of the tread portion.
In this way, it is possible to further suppress the degradation of block rigidity and drainage performance, and simultaneously further improve the on-ice performance and on-snow performance of tires. Additionally, by setting the surface roughness of the tread surface of the tread portion to have an Ra of 1 μm or more and 50 μm or less, it is possible to further suppress the degradation of the block rigidity and the drainage performance, and simultaneously further improve the on-ice performance and on-snow performance of the tire sufficiently. Namely, for the surface properties of the tread surface of the tread portion, Ra is a 1 μm or more, and consequently it is possible to ensure water-removing paths. On the other hand, since Ra is 50 μm or less, it is possible to maintain the block rigidity even under large load. Further, it is preferable that the part with micro protrusions 9 formed thereon has surface properties with a surface roughness at which Ra is 10 μm or more and 40 μm or less.
Here, “Ra” refers to the arithmetic mean roughness (JIS B 0601 (2001)) of the tread surface of the tread portion.
Here, it is preferable that the ten-point average roughness Rz of the tread surface of the tread portion of the tire with protrusions with a hemispherical shape formed thereon is 1.0 to 50 μm.
The reason is that by setting Rz to be 1.0 μm or more, the gaps for water removing may be ensured, while by setting Rz to be 50 μm or less, the contacting area with the road surface may be ensured, and thereby it is possible to further improve the on-ice performance and on-snow performance of the tire.
Here, “ten-point average roughness Rz” refers to a value measured in accordance with the provisions of JIS B 0601 (1994), based on the reference length of 0.8 mm and the evaluation length of 4 mm.
In addition, it is preferable that the mean spacing S of local peaks of the protrusions 9 formed on the tread surface of the tread portion of the tire is set to be 5.0 to 100 μm.
The reason is that by setting spacing S to be 5.0 μm or more, the gaps for water removing may be ensured, while by setting spacing S to be 100 μm or less, the contacting area with the road surface may be ensured, and thereby it is possible to further improve the on-ice performance and on-snow performance of the tire.
As used herein, the term “mean spacing of local peaks” refers to a value measured in accordance with the provisions of JIS B 0601 (1994), based on the reference length of 0.8 mm and the evaluation length of 4 mm.
Additionally, the aforementioned tire is not particularly limited and may be manufactured with the tire forming mold as follows. Further, the forming of the tire utilizing the tire forming mold as follows may be performed with ordinary methods.
<Tire Forming Mold>
As is shown in
The molding surface 11 has a tread-surface molding surface 11a for molding the tread surface of the tread portion, and according to the example as shown, it also has a sidewall-portion molding surface 11b for molding the outside surface of a sidewall portion, and a bead-portion molding surface 11c for molding the outside surface of the bead portion.
The molding surface 11 is not particularly limited, and may be formed with aluminum, for example.
The tread surface of the tread portion of the tread portion of the tire of the present invention having the aforementioned surface properties may be formed with the tire vulcanization mold 10 comprising the tread-surface molding surface 11a having the aforementioned surface properties. Specifically, as shown in the enlarged plan view of the tread-surface molding surface 11a in
Namely, in the tire vulcanization process utilizing the mold 10, the surface shape of the tread-surface molding surface 11a of mold 10 is transferred as the surface shape of the tread surface of the tread portion of the tire. Additionally, the tread surface of the tread portion of the manufactured tire has a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less. Therefore, it is possible to form a tire excellent in on-ice performance and on-snow performance.
The method for molding the tread-surface molding surface 11a of mold 10 will be explained hereinafter.
The aforementioned tread-surface molding surface 11a may be formed via a blast material blasting process whereby blast materials of a particular shape are blasted and forced to impact the molding surface. Additionally, the tire forming mold obtained via the blast material blasting process has a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less on the tread-surface molding surface, as above, and consequently the tread surface of the tread portion of the vulcanization formed tire utilizing the mold has a surface roughness at which the kurtosis of the assessed profile Rku is 2 or less.
Here, in the blast material blasting process, it is preferable that the aforementioned tread-surface molding surface 11a (entirely or partially) is formed by blasting spherical blast materials with a sphericity of 15 μm or less and forcing the same to impact the tread-surface molding surface.
This is because that by setting the sphericity of the blast materials to be 15 μm or less, recesses with desirable properties may be formed on the tread-surface molding surface of the mold, and it is possible to shape the tread surface of the tread portion of the tire formed by utilizing the mold into a desirable surface shape.
Further, it is more preferable that the sphericity of the blast materials herein is set to be 10 μm or less.
This is because that a large number of recesses with desirable properties may be easily formed on the tread-surface molding surface of the mold by setting the sphericity of the blast materials to be 10 μm or less, and consequently, it is possible to form tires with further improved on-ice performance and on-snow performance by forming a large number of protrusions with a desirable shape on the tread surface of the tread portion of the tire formed by utilizing the mold.
In addition, it is more preferable that the sphericity of the blast materials herein is set to be 5 μm or less.
This is because that in this way, recesses with desirable properties may be more easily formed on the tread-surface molding surface of the mold.
Here, it is preferable that the average particle size of the blast materials utilized in the blast material blasting process is set to be 10 μm to 1 mm.
This is because that by setting the average particle size of the blast materials to be 10 μm or more, a mold having recesses of desirable shape on its tread-surface molding surface may be obtained easily, and in the blast material blasting process, it is possible to suppress the splashing around of the blast materials in the case of high-pressure blasting, while by setting the average particle size of the blast materials to be 1 mm or less, it is possible to suppress the rapid wearing of the mold surface.
For the same reason, it is more preferable that the average particle size of the blast materials is set to be 20 μm to 0.7 mm, still more preferably 30 μm to 0.5 mm.
As used herein, the term “average particle size” refers to the value obtained by imaging blasting materials with SEM, then randomly taking out 10 blasting materials therefrom, obtaining the average value of the diameter of the inscribed circle and the diameter of the circumscribed circle of each blast material, and averaging the results of the 10 blast materials.
In addition, it is preferable that the Mohs hardness of the blast materials is set to be 2 to 10.
This is because that by setting the Mohs hardness of the blast materials to be 2 or more, a mold having recesses of desirable shape on its tread-surface molding surface may be obtained more easily. On the other hand, by setting the Mohs hardness of the blast materials to be 10 or less, the mold may be less prone to rapid deterioration.
For the same reason, it is more preferable that the Mohs hardness of the blast materials is set to be 3.0 to 9.0, still more preferably 5.0 to 9.0.
In addition, it is preferable that the Mohs hardness of the tread-surface molding surface of the tire forming mold is set to be 2.0 to 5.0, and that the difference between the Mohs hardness of the tread-surface molding surface of the tire forming mold and the Mohs hardness of the blast materials is set to be 3.0 to 5.0.
Additionally, it is preferable that the specific gravity of the blast materials is set to be 0.5 to 20.
This is because that by setting the specific gravity of the blast materials to be 0.5 or more, the operability may be improved by suppressing the splashing around of the blast materials in the blasting process. On the other hand, by setting the specific gravity of the blast materials to be 20 or less, it is possible to reduce the energy needed for accelerating the blast materials, and to suppress the rapid wearing of the mold.
For the same reason, it is more preferable that the specific gravity of the blast materials is set to be 0.8 to 18, still more preferably 1.2 to 15.
Here, the material of the blast materials is not particularly limited, and it is preferable to utilize, for example, gyricon, iron, cast steel or ceramics.
In addition, in the blast material blasting process, it is preferable that the blast materials are blasted with high-pressure air of 100 to 1000 kPa onto the tread-surface molding surface of the aforementioned mold for 30 seconds to 10 minutes.
This is because that by blasting the blast materials for 30 seconds or more under a pressure of 100 kPa or more, it is possible to shape the tread-surface molding surface into the aforementioned desirable shape thoroughly, while by blasting the blast materials for 10 minutes or less under a pressure of 1000 kPa or more, it is possible to suppress the damage to the tread-surface molding surface.
Further, it is preferable that the blasting speed of the blast materials is set to be 0.3 to 10 (m/s), more preferably 0.5 to 7 (m/s), by adjusting the specific gravity and blasting pressure of the materials.
In this case, it is preferable that the distance between the nozzle for blasting the blast materials and the tire forming mold is set to be 50 to 200 (mm).
Here, the aforementioned blasting time of the blast materials refers to the blasting time for a single mold, for example, in the case that a single tire is formed utilizing 9 molds, it is preferable that blast materials are blasted for 270 seconds to 90 minutes in total onto the tread-surface molding surface of the 9 molds for forming a single tire.
In addition, the blasting of the blast materials onto the tread-surface molding surface of a single mold may be performed by the operator displacing the blasting position while considering the shape of the mold, etc. In this way, it is possible to blast the blast materials more uniformly.
Here, for the mold 10, it is preferable that the tread-surface molding surface has surface properties having a surface roughness at which the kurtosis of the assessed profile Rku is 1.5 or less. This is because that it is possible to mold a tread surface of the tread portion of the formed tire with surface properties having a surface roughness at which the kurtosis of the assessed profile Rku is 1.5 or less, and it is possible to form a tire exhibiting even better on-ice performance and on-snow performance. Further, it is possible to control the kurtosis of the assessed profile Rku of the tread-surface molding surface of the mold by adjusting the particle size, the speed and the particle number when blasting. Specifically, if the speeder is increased, the kurtosis Rku may be reduced.
In addition, in the mold 10, it is preferable that the shape of each recess 12 is hemispherical. This is because that by shaping each recess 12 into a hemispherical shape, it is possible to form protrusions 9 of hemispherical shape on the tread surface of the tread portion of the tire. Further, it is possible to control the shape of recesses 12 by adjusting the particle size, the blasting speed and the blasting angle of the blast materials.
Further, in the mold 10, it is preferable that the depth h of each recess 12 is set to be 1 to 50 μm. This is because that by setting the depth h of each ruptured-bubble-like recess 12 to be 1 to 50 μm, it is possible to form solid-bubble-like protrusions 9 with a height of 1 to 50 μm on the tread surface of the tread portion of the tire. Further, it is possible to control the depth h of each ruptured-bubble-like recess 12 by adjusting the blasting speed of the blast materials. Specifically, if the blasting speed of the blast materials is increased, the depth h may be increased.
Here, the depth of each recess 12 refers to the distance along the radial direction between a third imaginary plane perpendicular to a radial direction line extending across the deepest portions (the inner ends in the radial direction) of the recesses 12 and a fourth imaginary plane closest to the third imaginary plane among the imaginary planes contacting the outer contour line of the recesses 12 and perpendicular to the radial direction line. Note that the term “radial direction” refers to a direction corresponding to the radial direction of the toroidal tread-surface molding surface, namely a direction corresponding to the tire radial direction of the tire formed by utilizing the mold 10.
Further, the depth of recesses 12 may be measured with an SEM or a microscope.
In addition, the tire forming mold of the present invention is a tire forming mold, having a tread-surface molding surface for molding the tread surface of the tread portion of the tire, and it is preferable that at least a part of the tread-surface molding surface has a surface roughness satisfying the following condition:
Rsk<0
This is because that in this way, it is possible to form the aforementioned tire excellent in on-ice performance and on-snow performance, and at which at least a part of the tread surface of the tread portion has a surface roughness satisfying the condition that Rsk<0.
Here, it is more preferable that the tread-surface molding surface of the mold has a surface properties satisfying the condition that Rsk<−0.1. This is because that it is possible to mold a tread surface of the tread portion of the formed tire with surface properties satisfying the condition that Rsk<−0.1, and it is possible to form a tire excellent in on-ice performance and on-snow performance.
It is possible to control the Rsk of the tread-surface molding surface by adjusting the blasting time of the blast materials. Specifically, if the blasting time of the blast materials is increased, the Rsk may be reduced.
Here, the tire forming mold of the present invention is a mold for tire forming, having a tread-surface molding surface for molding the tread surface of the tread portion of the tire, and it is preferable that at least a part of the tread-surface molding surface has surface properties satisfying the following relational expression:
50 μm≦RSm≦250 μm
This is because that in this way, by setting Rsm to be 50 to 250 μm on at least a part of the tread-surface molding surface, it is possible to form a tire excellent in on-ice performance and on-snow performance, and having surface properties at which the RSm is 50 to 250 μm.
Further, it is preferable that the mold of the present invention satisfies the relational expression above in the range of 90% or more of the area of the tread-surface molding surface. This is because that by setting the Rsm to be 50 to 250 μm in the range of 90% or more of the area of the tread-surface molding surface, it is possible to obtain surface properties in a predetermined range of 90% or more of the tread surface of the tread portion of the tire.
Here, in the mold, it is preferable that the RSm of the tread-surface molding surface is 60 to 150 μm. This is because that by setting the Rsm of the tread-surface molding surface to be 60 to 150 μm, it is possible to set the Rsm of the tread surface of the tread portion of the tire to be 60 to 150 μm. Further, it is possible to control the Rsm of the tread-surface molding surface by adjusting the particle size of the blast materials. Specifically, if the particle size of the blast materials is increased, the Rsm may be increased.
Here, in the present invention, “RSm” refers to the mean width of the profile elements of the tread-surface molding surface, as mentioned above. Additionally, “RSm” may be measured according to JIS B 0601 (2001), as mentioned above.
Further, the tire forming mold of the present invention is a mold for tire forming, having a tread-surface molding surface for molding a tread surface of the tread portion, and it is preferable that at least a part of the tread-surface molding surface has a surface roughness at which the Ra is 1 μm or more and 50 μm or less.
This is because that in this way, it is possible to form the aforementioned tire excellent in on-ice performance and on-snow performance, and at which at least a part of the tread surface of the tread portion has a surface roughness at which the Ra is 1 μm or more and 50 μm or less.
Here, it is more preferable that the tread-surface molding surface of the mold has surface properties having a surface roughness at which the Ra is 10 μm or more and 40 μm or less. This is because that it is possible to mold a tread surface of the tread portion of the formed tire with surface properties such that the Ra is 10 μm or more and 40 μm or less, and it is possible to form a tire excellent in on-ice performance and on-snow performance.
It is possible to control the Ra of the tread-surface molding surface by adjusting the blasting speed of the blast materials. Specifically, if the blasting speed is increased, the Ra may be increased.
Here, it is preferable that the ten-point average roughness Rz of the tread-surface molding surface of the mold is 1.0 to 50 μm. This is because that it is possible to form a tire with a tread surface of the tread portion having a ten-point average roughness Rz of 1.0 to 50 μm.
Further, by setting the average particle size of the blast materials used in the blast material blasting process to be 50 to 400 μm, it is possible to obtain a tire-forming mold provided with a tread-surface molding surface having a ten-point average roughness Rz in the aforementioned range.
In addition, it is preferable that the recesses of the tread-surface molding surface of the mold have a mean spacing of local peaks of 5.0 to 100 μm. This is because that it is possible to form a tire with the protrusions formed on the tread surface of the tread portion having a mean spacing S of local peaks of 5.0 to 100 μm.
Further, by setting the average particle size of the blast materials utilized in the blast material blasting process to be 50 to 400 μm, it is possible to obtain a tire forming mold including a tread-surface molding surface having an mean spacing S in the aforementioned range.
The present invention will be explained in further detail below according to examples, although the present invention is not limited to the disclosed examples.
(Manufacture of Tire Forming Mold)
Tire forming molds 1 to 4 having tread-surface molding surfaces with surface properties as shown in Table 1 were manufactured by blasting (ceramic-based) blast materials to the tread-surface molding surfaces of tire forming molds made from aluminum, while changing the blasting conditions (such as blasting pressure and blasting speed). Further, the surface properties of the tread surfaces of the manufactured molds were measured with an SEM and a microscope.
(Manufacture of Tire)
Tires 1 to 4 of tire size 205/55R16 were manufactured according to ordinary methods, by utilizing the manufactured tire forming molds 1 to 4, respectively. Additionally, the surface properties of the tread surfaces of the tread portion of the manufactured tires were measured by utilizing an SEM and a microscope. The results are as shown in Table 2.
In addition, the on-ice performance and on-snow performance of each manufactured tire were evaluated with the evaluation method as follows. The results are as shown in Table 2.
<On-Ice Performance>
As soon as each tire was manufactured, the tire was mounted on an approved rim, filled with a normal internal pressure specified by JATMA and installed onto a vehicle. Then, the on-ice friction coefficient was measured under the conditions of 4.3 KN load on each front wheel and a speed of 30 km/h on icy road. The on-ice friction coefficient of each tire was evaluated, with a score of 100 representing the on-ice friction coefficient of tire 1. The results are as shown in Table 2. The larger the value, the higher the on-ice friction coefficient is and the more excellent the on-ice performance is, as is shown in Table 2.
<On-Snow Performance>
As soon as each tire was manufactured, the tire was mounted on an approved rim, filled with a normal internal pressure specified by JATMA and installed onto a vehicle. Additionally, the on-snow friction coefficient was measured under the conditions of 4.3 KN load on each front wheel and a speed of 30 km/h on snowy road. The on-snow friction coefficient of each tire was evaluated, with a score of 100 representing the on-snow friction coefficient of tire 1. The results are as shown in Table 2. The larger the value, the higher the on-snow friction coefficient is and the more excellent the on-snow performance is, as is shown in Table 2.
It can be understood that comparing to tires according to the comparative example and the conventional example, the tire according to the examples of the present invention is more excellent in on-ice performance and on-snow performance, as is shown in Table 2.
According to the present invention, it is possible to provide a tire with improved on-ice performance and on-snow performance and also a tire forming mold that can be used for forming the same.
1 tread portion
2 protrusion
3 gap
4 bead portion
4
a bead core
5 sidewall portion
6 tread portion
7 carcass
8 belt
8
a,
8
b belt layer
9 protrusion
10 mold
11 molding surface
11
a tread-surface molding surface
11
b sidewall-portion molding surface
11
c bead-portion molding surface
12 recess
20 tire
T road surface
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-289749 | Dec 2011 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2012/084303 | 12/28/2012 | WO | 00 | 6/10/2014 |