1. Field of the Invention
The present invention relates to stacked capacitor structures of semiconductor devices. In particular, the present invention relates to semiconductor device structures which include aluminum plugs disposed between the active device regions and bit lines thereof. More specifically, the present invention relates to semiconductor device structures which include an aluminum-filled trench that electrically connects a bit line to an active device region positioned between adjacent stacked capacitor structures.
2, Background of Related Art
Stacked capacitors are employed in many state of the art semiconductor devices to maintain high storage capacitance despite the ever-increasing densities of such semiconductor devices. Stacked capacitors typically make an electrical connection with a diffusion region, or active device region, of a semiconductor substrate, such as silicon, polysilicon, gallium arsenide, or indium phosphide. Some conventional processes for fabricating stacked capacitors on semiconductor device structures facilitate increased densities by employing electrically conductive layers (e.g., polysilicon layers) that are somewhat convoluted or have large surface areas, and which project outwardly relative to and electrically contact their associated active device regions. The remainders of the capacitor structures are then fabricated on the electrically conductive layers.
Many stacked capacitor structures include electrically conductive contacts between the active device regions and the bit lines thereof. Typically, such electrically conductive contacts are fabricated from polysilicon, which withstands the high temperature processes (e.g., thermal oxidation processes or thermal anneal processes) that are usually performed subsequent to the fabrication of contacts on semiconductor device structures. Such contacts, however, may create a somewhat undesirable amount of contact resistance during operation of the semiconductor device.
Metals have also been employed as the contact material between the active device region and bit lines of semiconductor devices and through the stacked capacitor structures thereof. Again, due to the high process temperatures that are employed following the fabrication of the contacts, metals that will withstand high process temperatures are typically employed in the contacts. Metals that will withstand such high process temperatures are commonly referred to as “refractory metals” and include titanium (Ti), tungsten (W), molybdenum (Mo), and tantalum (Ta). While these metals and their silicides have low resistivities relative to other metals, their resistivities (ρTi=43-47 μΩ-cm, ρw=5.3 μΩ-cm, ρMo=5 μΩ-cm, and ρTa=13-16 μΩ-cm) may be somewhat undesirable during the operation of state of the art very large scale integration (VLSI) and ultra large scale integration (ULSI) semiconductor devices. As metals of higher resistivity are employed in such semiconductor devices, the power requirements and operating temperature of such semiconductor devices increase undesirably.
Conventionally, aluminum (Al) has been widely employed as an electrically conductive material in semiconductor devices, as it has low resistivity (ρAl=2.7 μΩ-cm) and is compatible with both silicon (Si) and silicon dioxide (SiO2). Aluminum is not, however, typically employed in self-aligned processes due to its inability to withstand high temperature processing, such as the rapid thermal anneal processes that may be employed in fabricating self-aligned silicide layers.
What is needed is a process for fabricating a stacked capacitor structure on a semiconductor device structure which increases the speed of the semiconductor device and reduces the interconnect resistance and power consumption thereof and a stacked capacitor structure and semiconductor device structure fabricated by such a process.
The present invention includes a stacked capacitor structure and methods of fabricating the stacked capacitor structure which address the foregoing needs.
The stacked capacitor structure of the present invention includes a trench disposed over an active device region of a semiconductor device structure. The trench extends downward through the stacked capacitor structure to the active device region of the semiconductor substrate (e.g., silicon, gallium arsenide, indium phosphide), exposing same through the stacked capacitor structure. A layer of self-aligned metal silicide, or “salicide,” is disposed within the trench, adjacent the active device region and preferably defining a buried metal diffusion (BMD) layer with the active device region. An aluminum interconnect, or “contact,” is disposed within the trench in contact with the metal silicide and substantially filling the trench. The aluminum interconnect preferably provides an electrical link between the active device region and a bit line that extends above the stacked capacitor structure and electrically contacts the interconnect.
A method of fabricating a stacked capacitor structure is also within the scope of the present invention. The method includes fabricating a stacked capacitor structure over a semiconductor device structure and defining a trench through the stacked capacitor structure and over an active device region of the semiconductor device structure. Processes for fabricating stacked capacitor structures and defining trenches therethrough to an underlying active device region, which may be employed in the method of the present invention, are disclosed in U.S. Pat. No. 5,498,562 (“the '562 patent”), which issued to Dennison et al. on Mar. 12, 1996, the disclosure of which is hereby incorporated by reference in its entirety.
A layer of a metal that will form a salicide with the silicon exposed through the trench, such as titanium or tungsten, is then deposited over the semiconductor device structure. Known processes, such as rapid thermal anneal (RTA) or silicide deposition processes, may then be employed to form the salicide layer, such as titanium silicide (TiSix, predominantly TiSi2) or tungsten silicide (WSix, predominantly WSi2), which is typically referred to as a “selective” contact, over the active device region of the semiconductor device structure. The formation of silicides such as TiSi2 and WSi2 is said to be self-aligned since the silicide forms only over exposed semiconductor substrate (e.g., silicon and polysilicon) regions of a semiconductor device structure. Everywhere else, the metal film overlies an insulative, substantially non-reactive oxide layer, and may subsequently be removed. Preferably, the metal silicide diffuses into the silicon and defines a BMD layer. A metal nitride layer may also be fabricated over the selective contact by known techniques. Such metal nitride layers are typically referred to as “barrier” layers, as they prevent the diffusion of silicon and silicide into any metal layer or structure that is subsequently fabricated adjacent thereto.
An interconnect is fabricated in the trench by depositing aluminum over the semiconductor device structure in a manner that substantially fills the trench. Known processes, such as physical vapor deposition (PVD) and chemical vapor deposition (CVD) techniques, may be employed to deposit aluminum over the semiconductor device structure. The aluminum that covers other areas of the semiconductor device structure may then be removed by known processes, such as by known planarization (e.g., by chemical-mechanical polishing (CMP) techniques) or etching techniques, which do not remove aluminum from the trench. Additional layers and structures may then be fabricated or defined above the stacked capacitor, including, without limitation, bit lines that are in electrical contact with one or more corresponding aluminum interconnects.
Alternatively, portions of the aluminum layer that overlie the semiconductor device structure may be selectively removed therefrom by known techniques, such as masking and etching processes, in order to define bit lines that are integral with the aluminum interconnects and extend over an active surface of the semiconductor device structure. Such aluminum bit lines may be desirable since they may further reduce contact resistance and are compatible with the adjacent silicon dioxide of the semiconductor device structure.
The advantages of the present invention will become apparent to those of skill in the art through a consideration of the ensuing description, the accompanying drawings, and the appended claims.
With reference to
A trench 22 extends through stacked capacitor structure 20, exposing a source/drain 24, or p-n region, of active device region 16 to an active surface 11 of semiconductor device structure 10. A metal silicide selective contact 38 may be disposed over source/drain 24, and preferably defines a buried metal diffusion layer 39 in the semiconductor substrate 12 of source/drain 24. Selective contact 38 preferably comprises titanium silicide. A metal nitride layer 40, preferably titanium nitride (TiN), may be disposed over selective contact 38. The remainder of trench 22 is filled with aluminum, which defines an aluminum interconnect 34, or contact or plug.
Aluminum interconnect 34 is in electrical communication with a bit line 36 that extends over semiconductor device structure 10 above the stacked capacitor structures 20 thereof. Bit line 36 may be fabricated from an electrically conductive material, including, without limitation, metals such as aluminum, tungsten and titanium, electrically conductive polymers, and doped polysilicon. If bit line 36 is fabricated from aluminum, bit line 36 and aluminum interconnect 34 are preferably integral.
Referring now to
Turning now to
With reference to
Alternatively, selective contact 38 may be selectively deposited onto source/drain 24 by chemical vapor deposition (CVD) of a metallic precursor and a silicon-containing compound. For example, when titanium silicide selective contacts are desired, a titanium tetrahalide, such as titanium tetrachloride (TiCl4), is reacted with either silane (SiH4) or dichlorosilane (DCS, SiH2Cl2) as follows:
TiCl4+SiH4→TiSi2↓
TiCl4+SiH2Cl2→TiSi2↓
In order to optimize the selectivity of these titanium silicide deposition reactions for the semiconductor substrate 12, which is exposed through trench 22, a deposition temperature in the range of about 650° C. to about 750° C. is preferable. Since minimal amounts of the semiconductor substrate 12 are consumed by these reactions, the deposition reaction is allowed to continue until a selective contact 38 of the desired thickness is formed.
Other exemplary metal silicide deposition processes that may be employed in the present invention to fabricate selective contact 38 include the reaction of a titanium halide and/or a gaseous titanium organometallic precursor with a silicon-containing compound of the formula SinH2n+2, as disclosed in U.S. Pat. No. 5,240,739, issued to Trung Doan et al. on Aug. 31, 1993; U.S. Pat. No. 5,278,100, issued to Trung Doan et al. on Jan. 11, 1994; and U.S. Pat. No. 5,376,405, issued to Trung Doan et al. on Dec. 27, 1994, the disclosures of each of which are hereby incorporated by reference in their entirety. Titanium halides that may be employed in the deposition of selective contact 38 over source/drain 24 include, without limitation, TiCl4, titanium tetraboride, titanium tetrafluoride, titanium tetraiodide, and subhalides. Titanium organometallic precursors which may be used to fabricate selective contact 38 include, but are not limited to, compounds of the formula Ti(NR2)4, where the titanium atom is bonded to the nitrogen atom and R comprises hydrogen or a carbon-containing radical. Exemplary compounds include tetradimethylamido titanium (TDMAT or Ti(N(CH3)2)4 and Ti(N(C2H5)2)4).
The following are exemplary chemical reactions for depositing metal silicide on source/drain 24:
nTiCl4+SinH2n+2→nTiSi+4nHCl+H2+by-products;
nTiCl4+2SinH2n+2→nTiSi+4nHCl+2H2+by-products;
TiCl4+SinH2n+2→Ti5Si3+HCl+H2+by-products;
TDMAT+Si2H6→TiSi2+organic by-products;
TDMAT+SinH2n+2→(n/2)TiSi2+organic by-products; and
Ti(NR2)4+SiH4→TiSix+TiSiyN1-y+organic by-products,
where x is predominantly equal to two, y is zero or one and n is an integer equal to zero or more. The reaction between TiCl4 and Si2H6 may be employed to deposit selective contact 38 over source/drain 24 at a temperature as low as about 400° C. The reaction of TiCl4 and Si3H8 deposits a titanium silicide selective contact 38 on a semiconductor substrate at a temperature of about 300° C. or higher.
Preferably, selective contact 38 and semiconductor substrate 12 diffuse into each other to define a buried metal diffusion layer 39.
Although silicide deposition in accordance with the foregoing processes is selective for semiconductor substrate 12, residual metal silicide may be deposited above stacked capacitor structure 20. Thus, cleaning of semiconductor device structure 10 may be desirable in order to remove any residual metal silicide from above stacked capacitor structure 20. Cleaning agents such as chlorine (Cl2), hydrochloric acid (HCl) and hydrofluoric acid (HF) may be employed in known cleaning techniques (e.g., thermal gas, plasma assisted, and remote plasma activated cleaning) to clean any residual metal silicides from field oxide layer 14.
Referring now to
TiCl4+NH3→TiN↓,
including above the stacked capacitor structures 20 and selective contacts 38 of the semiconductor device structure 10 (i.e., a “blanket” deposition occurs). The duration of the foregoing reaction is dependent upon the desired thickness of metal nitride layer 40. This reaction may also be carried out in the presence of nitrogen gas (N2), as discussed in U.S. Pat. No. 5,416,045 (“the '045 patent”), issued to Ralph E. Kauffman et al. on May 16, 1995, the disclosure of which is hereby incorporated by reference in its entirety. As explained in the '045 patent, nitrogen gas facilitates the deposition of titanium nitride at temperatures of about 500° C. or lower. Hydrogen gas (H2) may also be introduced into the reaction chamber to facilitate the formation of hydrochloric acid from chlorine.
Other chemical reactions are also useful for depositing metal nitride layer 40. U.S. Pat. No. 5,399,379 (“the '379 patent”), issued to Gurtej S. Sandhu on Mar. 21, 1995, the disclosure of which is hereby incorporated by reference in its entirety, describes such a reaction, whereby one or more organometallic compounds of the formula Ti(NR2)4, which is also referred to as a tetrakis-dialkylamido-titanium, are reacted with a halide gas (e.g., F2, Cl2, Br2) to form a titanium nitride film on a semiconductor device. In each Ti(NR2)4 molecule, the titanium atom is single-bonded to four nitrogen atoms, each of which are also single-bonded to two carbon-containing radical (R) groups, which include hydrogen atoms or alkyl groups.
Another exemplary titanium nitride deposition reaction is disclosed in U.S. Pat. No. 5,254,499 (“the '499 patent”), issued to Gurtej S. Sandhu et al. on Oct. 19, 1993, the disclosure of which is hereby incorporated by reference in its entirety. According to the '499 patent, a titanium nitride layer may also be deposited by reacting one or more compounds of the general formula Ti(NR2)4, where the titanium atom is bonded to a nitrogen atom, which is in turn bonded to two hydrogen atoms or a carbon-containing radical (R), with ammonia (NH3). The following United States Patents disclose various other methods for depositing titanium nitride films, wherein the second reactants are Ti(NR2)4 and ammonia: U.S. Pat. No. 5,192,589, issued to Gurtej S. Sandhu on Mar. 9, 1993; U.S. Pat. No. 5,139,825, issued to Roy G. Gordon et al. on Aug. 18, 1992; and U.S. Pat. No. 5,089,438, issued to Avishay Katz on Feb. 18, 1992, the disclosures of each of which are hereby incorporated by reference in their entirety.
U.S. Pat. No. 5,246,881, issued to Gurtej S. Sandhu et al. on Sep. 21, 1993, the disclosure of which is hereby incorporated by reference in its entirety, discloses another method for depositing a titanium nitride film, wherein the second reactants are one or more compounds of the formula Ti(NR2)4, where the titanium atom is bonded to the nitrogen atom which is, in turn, bonded to two hydrogen atoms or a carbon-containing radical (R), and an activated species which attacks the R-nitrogen bonds of the Ti(NR2)4, and which will convert the activated species to a volatile compound. The activated species include halogens, ammonia, and hydrogen, and are radiofrequency (RF) activated remote from the Ti(NR2)4.
Another titanium nitride deposition reaction that is useful in the method of the present invention is disclosed in U.S. Pat. No. 5,227,334, issued to Gurtej S. Sandhu on Jul. 13, 1993, which is hereby incorporated by reference in its entirety. The second reactants of that process include a titanium-containing compound, such as Ti(NR2)4, and nitrogen trifluoride (NF3).
Alternatively, metal nitride layer 40 may comprise a mixed phase layer, such as the TiN/TiSix layer deposited by the method disclosed in U.S. Pat. No. 5,252,518 (“the '518 patent”), issued to Gurtej S. Sandhu et al. on Oct. 12, 1993, the disclosure of which is hereby incorporated by reference in its entirety. The process of the '518 patent includes reacting Ti(NR2)4, where the titanium atom is bonded to the nitrogen atom which is, in turn, bonded to two hydrogen atoms or a carbon-containing radical (R), with an organic silane reactive gas, such as tris(dimethylamino) silane (SIN).
With reference to
Referring to
Additional structures and layers may then be fabricated over the active surface 11 of semiconductor device structure 10 by known processes.
The semiconductor device structure 10 (see
In addition, the aluminum interconnects 34 of semiconductor device structure 10 of the present invention may also facilitate further increases in the density of semiconductor device structures due to the low resistivity of aluminum and, thus, the potentially thinner interconnects 34 that may be fabricated through the stacked capacitor structures 20 of such semiconductor devices.
Although the foregoing description contains many specifics, these should not be construed as limiting the scope of the present invention, but merely as providing illustrations of some of the presently preferred embodiments. Similarly, other embodiments of the invention may be devised which do not depart from the spirit or scope of the present invention. Features from different embodiments may be employed in combination. The scope of the invention is, therefore, indicated and limited only by the appended claims and their legal equivalents, rather than by the foregoing description. All additions, deletions and modifications to the invention as disclosed herein which fall within the meaning and scope of the claims are to be embraced thereby.
This application is a continuation of application Ser. No. 10/180,846, filed Jun. 26, 2002, now U.S. Pat. No. 6,787,428, issued Sep. 7, 2004, which is a continuation of application Ser. No. 09/651,384, filed Aug. 29, 2000, now U.S. Pat. No. 6,465,319, issued Oct. 15, 2002, which is a continuation of application Ser. No. 09/102,331, filed Jun. 22, 1998, now U.S. Pat. No. 6,165,863, issued Dec. 26, 2000.
Number | Date | Country | |
---|---|---|---|
Parent | 10180846 | Jun 2002 | US |
Child | 10931181 | Aug 2004 | US |
Parent | 09651384 | Aug 2000 | US |
Child | 10180846 | Jun 2002 | US |
Parent | 09102331 | Jun 1998 | US |
Child | 09651384 | Aug 2000 | US |