The present invention relates to methods and apparatuses for processing exfoliated graphite material to modify or enhance its properties, in particular for use in thermal management applications. It also relates to integrated heat removal devices made from patterned graphite sheet material.
Flexible graphite sheet material can be obtained by first intercalating graphite with an intercalating agent to form a graphite intercalation compound that is then exposed to a thermal shock, for example, at a temperature of 700° C.-1,050° C. for a short duration of time (20-60 seconds) to expand or exfoliate the graphite. The exfoliated graphite particles are vermiform in appearance, and are commonly referred to as “worms”. The worm is essentially a network of interconnected, thin graphite flakes, with pores present between flakes that make the worms compressible. The worms can be re-compressed together into flexible sheets (foils or films), referred to as “flexible graphite” or “exfoliated graphite sheet” or “graphite sheet” that can be wound up on a drum to form a roll. U.S. Pat. No. 3,404,061 describes the preparation of flexible graphite from expanded or exfoliated graphite particles.
Most of the graphite flakes in flexible graphite are oriented parallel to the two opposed major exterior surfaces. Although flexible graphite is typically highly electrically conductive (typically around 1,300 S/cm) in the in-plane directions, flexible graphite's through-plane electrical conductivity is significantly less (often only about 15 S/cm). The anisotropy ratio, the ratio of highest electrical conductivity to lowest conductivity values, is typically as high as 86:1 (and often higher than this value). The thermal properties of flexible conventional flexible graphite are similarly highly anisotropic with the in-plane thermal conductivity being many times greater than the through-plane conductivity.
The properties of flexible graphite (such as its density, flexibility and its electrical and thermal conductivity) can be adjusted by incorporating a resin during forming of the material or impregnating it with a resin or another suitable impregnation medium after it is formed. The impregnation medium at least partially fills the pores between the graphite flakes. Resins suitable for impregnation of flexible graphite include phenolic, furan, epoxy and acrylic resins.
During compression or embossing processes, air can become trapped within the flexible graphite as it is compressed. This can cause problems including blistering and/or delamination of the embossed material. This is particularly undesirable for some end-use applications. For example, blistering or delamination in flexible graphite materials can weaken the material and make it more permeable to fluids. The material is also rendered less homogeneous as a result and can exhibit undesirable localized differences in thermal and electrical conductivity. The foregoing problems can be difficult to detect during fabrication and may only surface at a later date. Finally, in applications where the material is subsequently impregnated with a resin, delamination and/or blistering can result in voids in the plate material that become filled with resin. Where the resin employed is electrically nonconductive, this can result in undesirable nonconductive regions within the material.
For thermal management applications, such as heat sinks, heat spreaders and thermal interfaces, flexible graphite offers many advantages over other materials that are commonly used in these applications such as copper, steel and aluminum. For example, relative to these metals, flexible graphite is often lighter, less susceptible to corrosion, has lower thermal expansion and has higher thermal conductivity in the in-plane direction.
The present application relates to methods and apparatuses for processing of flexible graphite that can be used to modify or enhance its properties, in particular for use in thermal management applications.
Methods and apparatus for processing flexible graphite sheet material involve patterning the material, on at least one major surface thereof, prior to further processing of the material such as densification, lamination, folding or shaping into three-dimensional structures. For densification and lamination the patterning is selected to facilitate the removal of air from the flexible graphite sheet material during the densification and lamination process. For folding or shaping, the patterning is selected to render the graphite sheet material more flexible. Methods and apparatus for increasing the through-plane conductivity of flexible graphite sheet material are also provided.
In one aspect, a method of densifying flexible graphite sheet material includes:
In the foregoing method of densifying flexible graphite sheet material, the patterning step can comprise calendering the material with one or more patterned rollers or die pressing the material with one or more patterned dies or screens. The patterning can extend across the entire surface of the sheet material or can be in one or more localized regions. In some preferred embodiments, a subsequent compression step substantially removes the patterning. The compression step can involve, among other things, using substantially smooth or flat rollers or dies. In other embodiments, the compression step can have at least one embossing step using, among other things, patterned rollers, dies or screens. The foregoing methods can further include cutting the densified flexible graphite sheet material.
In one aspect, a method of laminating two pieces of flexible graphite sheet material together includes:
In the foregoing lamination method, the patterning step can include calendering the material with one or more patterned rollers or die pressing the material with, among other things, one or more patterned dies or screens. The patterning can extend across the entire surface of the sheet material or can be in one or more localized regions. In some embodiments, the lamination step can include calendering or die pressing the stacked pieces of patterned material. The foregoing methods can further include cutting the laminated flexible graphite sheet material.
In one aspect, a method of improving the flexibility of a sheet of a graphite sheet material together includes patterning the flexible graphite sheet material, on at least one major surface thereof, to produce patterned graphite sheet material, wherein the patterning is selected to reduce the tendency of the sheet material to splinter or crack when it is bent.
In the foregoing method for improving flexibility, the patterning step can include calendering the material with one or more patterned rollers or die pressing the material with, among other things, one or more patterned dies or screens. The patterning can extend across the entire surface of the sheet material or can be in one or more localized regions.
In the foregoing methods involving patterning flexible graphite sheet material prior to further processing thereof (for example, where the further processing comprises densification, lamination or bending), the patterning can include one or more patterning steps. In some embodiments, the patterning can include roller embossing of the flexible graphite sheet material and/or die pressing the flexible graphite sheet material with a patterned die.
In some embodiments of the foregoing methods, the patterning can include creating a cross-hatched diamond pattern on the at least one surface. This patterning can be performed by a first step patterning a first set of diagonal grooves and a second step patterning a second set of diagonal grooves in the flexible graphite sheet material. In some embodiments the second set of grooves is essentially orthogonal to the first set.
In one aspect, a method for decreasing thermal anisotropy in graphite sheet material includes:
In the foregoing method, the exfoliated graphite can be blended using an industrial blender. The powder can be compacted using a punch.
The foregoing method for decreasing thermal anisotropy can further include:
Graphite sheet materials having decreasing thermal anisotropy that are made by these methods can be used as thermal interface materials.
In one aspect, a method for increasing the through-plane to in-plane thermal conductivity ratio of a graphite sheet material (for example, a conventional anisotropic sheet material prepared by calendering exfoliated graphite) includes patterning the flexible graphite sheet material, on at least one major surface thereof, to produce patterned graphite sheet material. The patterning is selected to alter the orientation of graphite flakes within the sheet material so that more of them are oriented perpendicular to the plane of the material.
The method for increasing the through-plane to in-plane thermal conductivity ratio of a graphite sheet material can further include compressing the patterned graphite sheet material to produce densified flexible graphite sheet material.
In the foregoing methods involving patterning graphite sheet material to increase the through-plane to in-plane thermal conductivity ratio of the material, the patterning can include one or more patterning steps. The patterning can include roller embossing of the graphite sheet material and/or creating a button pattern with an array of circular protrusions on one or both surfaces of the material.
Graphite sheet materials having an increased through-plane to in-plane thermal conductivity ratio that are made by these methods can be used as thermal interface materials.
Embodiments of the various methods described above can be implemented as continuous processes or as batch processes.
Various apparatuses and systems can carry out the above-described methods.
In one aspect, an improved heat sink assembly includes a first folded subassembly consisting essentially of a compressed formable graphite material. In a first embodiment, the first subassembly further includes a base configured to conform to an outer surface of a heat source. In some preferred embodiments, the first subassembly further includes a first fin and a second fin. The first and second fins are configured to extend away from the heat source when the first subassembly is attached to an outer surface of the heat source. In the same or other preferred embodiments, the outer surface of the first subassembly is configured to face away from the heat source and the outside face is embossed to form a plurality of ribs that run a length of the first subassembly.
In one aspect, an improved method of dissipating heat from a heat source includes conforming a heat sink assembly to an outer surface of the heat source, the heat sink assembly consisting essentially of a graphite sheet material.
As described above, graphite sheet material can be patterned in various ways in order to change its properties, including its ability to be densified, laminated, folded or shaped, as well as its in-plane and through-plane thermal and electrical conductivity, and its surface area.
In yet another aspect of the present technology, graphite sheet material is selectively patterned in different regions to impart desirable localized properties to the material. Separate dies can be used to pattern different regions of the material or a single die with multiple different features or patterns in different regions can be used.
An integrated flexible graphite heat removal device can be made from one or more pieces graphite sheet material that is selectively patterned in different ways in different regions to impart desirable localized properties to the device. In some embodiments the device is made from a single sheet of material. In other embodiments at least two pieces of patterned graphite sheet material are laminated together to form an integrated flexible graphite heat removal device.
In some embodiments an integrated heat removal device includes, or consists essentially of, a piece of graphite sheet material that is selectively patterned in at least one localized region with a pattern that enhances the through-plane thermal conductivity of the material. The piece of graphite sheet material can be further patterned in at least one localized region with a pattern that that renders the material more flexible and/or in at least one localized region with a pattern that increases the surface area to facilitate heat dissipation to the surrounding environment.
The integrated heat removal device is made by forming the selectively patterned graphite sheet material into a three-dimensional structure, for example, by bending, folding and/or corrugating.
In some embodiments graphite sheet material prepared using the above-described methods, or devices or components made therefrom, or portions thereof, are impregnated with a resin. In some embodiments graphite devices, such as integrated heat removal devices can be impregnated in one or more regions after they are formed or shaped.
In some embodiments graphite sheet material prepared using the above-described methods, or devices or components made therefrom, or portions thereof, are coated with a coating. In some embodiments graphite devices, such as integrated heat removal devices can be coated in one or more regions after they are formed or shaped. In some embodiments the coating is electrically insulating.
Existing methods to provide a higher density structure than the structure of
A limitation of existing processes for producing flexible graphite sheets is that the graphite flakes can trap air pockets during compression, particularly in the mid-plane of the material, but also near the surface. The presence of air pockets can limit the degree to which the material can be densified by the process, and can cause blistering. Such air pockets can be difficult to avoid or reduce with conventional calendering or other compression processes. Techniques can be used to alleviate problems caused by air pockets, such as deploying vacuum air removal systems during compression, or impregnating the graphite with resin or another suitable medium after compression to fill the voids.
One problem with resin impregnation is that it can prevent, or at least reduce, fluid leakage or permeation if the material is to be used as a gasket, seal or impervious barrier. Furthermore, whether or not they are filled with resin, the pores or air pockets remaining inside the compressed sheet material result in non-uniformity in the structure and properties of the material that can make them less suitable for use in certain applications. Pores or air pockets can also make the material more susceptible to mechanical degradation and delamination or flaking of the layers.
Apparatuses and methods for improved densification of sheet materials made using exfoliated graphite involve patterning the graphite sheet material prior to performing further processing steps that are used, for example, to form it into a material with a desired thickness and/or desired surface features, and/or to laminate it with other sheets. Such patterning can be selected to facilitate the removal of air from the material during subsequent processing steps. Thus, appropriate patterning prior to further processing of graphite sheet material can offer benefits including:
Various patterns can be used including, but not limited to, a cross-hatched diamond pattern, a cross-hatched square pattern, and an array of protrusions such as circular features or buttons. Patterning can be performed in one or more steps. In one embodiment, cross-hatched diamond patterning can be performed by a first step patterning a first set of diagonal grooves and a second step patterning a second set of diagonal grooves, where the second set of grooves can be at a non-orthogonal angle to the first set. Similarly a square-grid pattern can be obtained by patterning two sets of grooves at 90° to one another.
At step 330, the patterned graphite sheet material is compressed to increase its density. This can be accomplished, for example, in a platen press, die press or through a calendering process. Generally this step will significantly reduce or eliminate the initial patterning from the surface(s) of the graphite sheet material.
At step 340, the compressed graphite sheet material is tested to see if it is at the desired thickness (or density). If the material is not at a desired thickness, then method 300 returns to step 330 where it is compressed further, or (optionally) to step 320 where it is patterned and subsequently compressed further at step 330.
If the material is at the desired thickness, then method 300 proceeds to optional step 350 where two or more sheets from step 340 are laminated to form a single laminated graphite sheet. This can be accomplished by bringing the patterned surfaces of two or more sheets of graphite material adjacent to each other and compressing the laminate together. Lamination at step 350 is optional, and method 300 can proceed directly to step 360 from step 340 when the material is at a desired thickness.
At step 360, the compressed graphite sheet from step 340 or laminated graphite sheet from step 350 is embossed, for example to form surface features that are desirable for a particular end-use application. At step 370, the embossed graphite sheet is cut to a desired shape and size. Method 300 ends at step 380.
Although the present approach, involving patterning graphite sheet material to facilitate air removal, can be employed in a batch compression system (for example, involving a platen presses) it is particularly suitable for use in a multi-step calendering/embossing process as described in further detail below.
Apparatus 400 comprises infeed and patterning station 405, densification station 410, embossing station 420, cutting station 430 and drive motor system 440. Drive motor system 440 provides the drive to rotate the calendering drums and drive other machinery in stations 405, 410, 420 and 430.
Graphite sheet material is fed into apparatus 400 at infeed and patterning station 405 using a conveyor 470, as indicated by arrow A. At station 410, the graphite sheet material is compressed and patterned on one or both sides using at least one pair of drums. Grooves or features are impressed onto the graphite sheet material, and the process pushes air out of the graphite material. Grooves or other features in the drum(s) can provide a path for the air to escape, thereby allowing the material to be compressed during patterning, without undue obstruction of air or hydraulic locking of trapped air between the graphite flakes.
The material is then conveyed to densification station 410 where it is further compressed to a desired thickness using at least one pair of drums. The desired thickness can be based on the amount of graphite per unit area in the material (loading) and the net desired thickness for the final embossed part. The compressed material is then conveyed to embossing station 420 where it can be embossed with surface features as desired for a particular end-use application, and then to cutting station 430 via conveyor 470. At cutting station 430, the material is cut to a desired shape and size, for example with a clicker-type press or with die cutters, cutting wheels, another embossing drum with cutters, or other suitable cutting mechanism. Material exits apparatus 400 after cutting station 430 on conveyor 470, as indicated by arrow B.
Embossing and cutting stations 420 and 430 are optional. In some embodiments, the material can be transferred from the embossing station 420 onto a reel, and the material can be cut to a desired shape and size at a later time. Furthermore, in some embodiments, embossing can be performed directly on the patterned graphite sheet material at densification station 410 rather than compressing the material (for example, to give a densified material that is substantially un-patterned) at station 410, and then embossing in a separate step at station 420.
Apparatus 400 further includes power supply 450 and at least one process controller 460. First data flow 415 provides monitoring and sensor feedback information from densification station 410 to the at least one process controller 460. Second data flow 465 provides data control and shuttle command information from the at least one process controller 460 to drive motor system 440.
Apparatus 400 can further comprise a mechanism for measuring overall material thickness at one or more stages in the process. The mechanism can use a laser or mechanical or other suitable instrumentation. The thickness measurement can be used to adjust various process parameters used for operation of patterning station 405, densification station 410 and/or embossing station 420, such as gaps, drum speeds and other parameters.
The material can be patterned, for example, with one or more sets of parallel channels. For example two sets of parallel channels can be used to create a square grid pattern or diamond pattern on the material, so that the surface has an array of square- or diamond shaped protrusions. In other examples the material is patterned with an array of small protrusions of other shapes, for example circular buttons or dots. In preferred embodiments the channels extend to the edges of the material so that air is expelled along the channels as the material is compressed. If the material is to be densified and/or laminated using one or more rollers it is preferable that the channels along which air is expelled extend at an angle (rather than being parallel and/or perpendicular) to the direction of movement of the material during roller compression.
Apparatus 500 comprises a pair of drums 510 and 520. Upper drum 510 rotates on upper spindle 512 counter-clockwise about axis X-X (shown in
In the illustrated embodiment patterned flexible graphite 530 is patterned on one surface with a diamond pattern of grooves. This type of pattern has been found to be particularly effective in facilitating subsequent air removal during densification. Patterned flexible graphite 530 is fed into apparatus 500 as indicated by arrow B of
A patterned graphite sheet 630A is fed between drums 610A and 620A as indicated by arrow B. Upper surface 632A and lower surface 634A of sheet 630A have been patterned via an offset calendering process. By offset, it is meant that the pattern on upper surface 632A is offset with respect to the pattern on lower surface 634A (see below). Processed sheet 640A leaves apparatus 600A as indicated by arrow B*. Upper surface 642A and lower surface 644A of processed sheet 640A are essentially smooth (with no substantial patterning). The thickness of processed sheet 640A is indicated by arrows C and C*.
Patterned graphite sheet 630B is fed between drums 610B and 620B as indicated by arrow B. Upper surface 632B and lower surface 634B of sheet 630B are patterned via an offset calendering process. Processed sheet 640B leaves apparatus 600B as indicated by arrow B*. Upper surface 642B and lower surface 644B of processed sheet 640B are embossed in accordance with corresponding surface features on drum surfaces 615B and 625B. The thickness of sheet 640B is indicated by arrows C and C*.
Patterned graphite sheet 630C is fed between drums 610 and 620 as indicated by arrow B. Upper surface 632C and lower surface 634C of sheet 630C are patterned via an offset calendering process. Processed sheet 640C leaves apparatus 600C as indicated by arrow B*. Upper surface 642C of processed sheet 640 is embossed in accordance with the corresponding surface features formed on drum 615C, and lower surface 644C is essentially smooth (with no substantial patterning). The thickness of sheet 640C is indicated by arrows C and C*.
For some applications, it can beneficial that the calendering process used to pattern the flexible graphite creates regions of higher density mid-plane in the sheet before compression and/or embossing of the final material. The calendering process can be configured to a) remove air during the calendering process, and b) prepare the material with regions of higher density mid-plane as well as patterning it. By having regions with higher density in the mid-plane of the sheet, further embossing can be used to form the surface rather than requiring additional roll-forming to increase density.
The patterning process can be performed using a patterned die.
The pattern can be selected to facilitate downstream air removal and densification as well as taking into account the overall and local densities of the graphite material that are desired in the final part after subsequent processing. For example, in a regular fuel cell plate it is often preferable to have an area densification of at least approximately 1.8 g/cm3 in order to maintain the integrity of the part when deployed in a hydrogen or liquid environment.
The above-described apparatus and method have been successfully used to prepare graphite sheet material having densities in the range of about 1.9 to 2.2 g/cm3 without use of a vacuum during the compression process. Typically using conventional densification processes (without the use of a vacuum) densities of about 1.6 to 1.8 g/cm3 are achieved.
In the above described methods for densification (and in some of the other methods described below) air that is present in the pores of the graphite sheet material can effectively serve as a fluid medium within which the graphite flakes or particles can be moved or re-oriented in desirable and controlled ways during processing of the material as the air is expelled.
It has been found that patterning the surface of sheets of flexible graphite prior to laminating the sheets together can improve the lamination process, for example, by creating a stronger bond between the adjacent sheets and/or increasing the homogeneity of the laminated material so that the interface between the laminated sheets is more difficult to discern. This can result in a reduced tendency for delamination and/or more uniform properties in the laminated material. Preferably the graphite sheet is patterned so that it has multiple discrete protrusions of lower density surrounded by interconnecting pathways or channels, rather than an array of discrete indentations. For example a diamond pattern, button pattern or inverse waffle-pattern can be used. This approach can eliminate, or at least reduce, the need for vacuum systems or other elaborate air removal systems during lamination.
This approach of patterning and then laminating can be used to bring entire sheets of flexible graphite material together, or can be used to join layers of flexible graphite together just in localized regions. The patterned materials can be laminated together using a flat plate die press or rollers (calendering). In some circumstances rollers are more effective at eliminating the air and creating a homogenous interface.
It has also been found that patterning the surface of sheets of graphite sheet material can enhance the physical properties of the material rendering it more flexible so that it can be formed or shaped into three-dimensional structures, for example by folding, bending, pleating, or corrugating. The patterning can allow a tighter radius on the folds or bends before the material splinters or cracks relative to a similar un-patterned material. In conventional approaches an elastomeric resin is sometimes incorporated into graphite sheet material to render it more flexible. The present approach of patterning can provide highly flexible graphite sheet materials without the need to incorporate resin.
Un-patterned material 1300A cracked and splintered when it was wrapped around the dowel rod. Surface cracks, internal splitting and delamination can be seen in the image of material 1300A shown in
Flexible graphite sheet materials prepared by compressing exfoliated graphite particles tend to have highly anisotropic structures because of the preferential orientation of the graphite particles parallel to the opposed major surfaces of the sheet (perpendicular to the direction of compression). The bonding between flakes in the in-plane direction is governed by different physical forces than the bonding in the through-plane direction. The properties of such materials, such as thermal and electrical conductivity, therefore tend to be highly directional. Generally the in-plane thermal and electrical conductivity of these materials is many times greater than the through-plane thermal and electrical conductivity. For some applications this directionality of properties is beneficial. For example, for heat spreaders materials with high in-plane thermal conductivity are generally desirable as they will more efficiently spread heat laterally.
For other applications it is desirable to be able to reduce the anisotropy of graphite sheet materials and reduce the ratio of their through-plane to in-plane thermal and/or electrical conductivity. For example, for some applications, it can be beneficial to increase the thermal conductivity of the flexible graphite sheet in the through-plane direction.
Apparatuses and methods for reducing anisotropy of graphite sheet materials and/or increasing the thermal conductivity of graphite sheet material in the through-plane direction are discussed below.
In one approach, the through-plane thermal conductivity of materials made by compressing exfoliated graphite can be increased by reducing the size of the graphite particles or flakes and/or randomizing their orientation prior to compression. Even without the use of patterning, by reducing the size of the graphite particles or flakes and/or randomizing their orientation prior to compression, a more isotropic material with a lower ratio of in-plane to through-plane thermal conductivity can be obtained. Using this approach materials with a through-plane conductivities of about 20 W/mK to 30 W/mK have been obtained.
At step 1470, the compacted graphite is optionally patterned on one or both sides. Patterning can be used to increase the orientation of the graphite flakes perpendicular to the plane of the material (as described in further detail below) resulting in a material that has an even higher through-plane thermal conductivity. Patterning is accomplished by replacing a smooth insert at the base of the die cavity by a patterned insert and or using a patterned die press. Suitable inserts can, for example, have patterns similar to those on patterned dies illustrated in
Material 1600 has been compacted by method 1400 of
Graphite flakes in the lower region of material 1600, such as in circle 1630 for example, are oriented essentially in a random fashion or at least with less in-plane orientation of graphite flakes than would be produced by a conventional roller compression process using exfoliated graphite.
Graphite flakes in the upper region of material 1600, such as in circle 1635 for example, are oriented essentially in a perpendicular or through-plane direction or at least with a majority of the graphite flakes oriented in a direction that is generally perpendicular to the plane of the material.
In another approach, the through-plane to in-plane thermal conductivity ratio of a conventional highly anisotropic graphite sheet material (produced by calendering exfoliated graphite) can be increased by patterning graphite sheet material. By further compressing the material with a patterned die or roller the orientation of the graphite flakes can be altered so that a significant portion of the flakes (at least near the patterned surface of the material) are oriented perpendicular to the plane of the material. The flakes tend to get pushed or moved into the grooves or cavities during the compression process.
Again the material can be patterned, for example, with one set of parallel channels and corresponding ribs between the channels (as for improved densification and lamination as described above). However, in some preferred embodiments configured to increase the through-plane thermal conductivity, the graphite material is patterned with an array of small protrusions, such as diamonds, squares or circular buttons or dots. In some preferred embodiments, the sides of the channels or protrusions are perpendicular to the plane of the material—in other words the features on the patterned die or roller or screen that is used to pattern the material have “vertical” side walls.
Material 1700 has been patterned using a roller, die press or other method. The upper surface of material 1700 has patterned cross-section 1720 comprising a plurality of ribs and/or discrete protrusions.
Graphite flakes in the lower region of material 1700, such as in circle 1730 for example, are oriented predominantly in-plane. Graphite flakes in the upper region of material 1700, such as in circle 1735 for example, are oriented essentially in a perpendicular or through-plane direction or at least with a majority of the graphite flakes oriented generally perpendicular to the plane of the material.
In some embodiments of a method for increasing the through-plane conductivity of a graphite sheet material, a perforated screen is used to pattern the graphite sheet material. The graphite material is compressed against the screen and graphite flakes are squeezed into the perforations to form the pattern. This can offer advantages over a patterned die or roller where the “cavities” into which the graphite flakes are dead-ended or enclosed spaces. The open perforations can allow even greater perpendicular orientation of the graphite flakes as they are not constrained by the cavity.
Graphite material that has been patterned to increase its through-plane conductivity can be used as-is or it can be further compressed, for example, using a smooth roller or die, so that the surface(s) are essentially flat or smooth. It has been found that with this approach the material retains some increased perpendicular orientation of graphite flakes that resulted from the patterning.
Using this approach of patterning and then flattening conventional graphite sheet materials, through-plane conductivities of about 15-18 W/mK have been obtained. This compares to through-plane conductivities of about 3-4 W/mK for conventional un-patterned graphite sheet material. It is generally more convenient to take commercially available sheet material and pattern it as described above, rather than using a blending and compression process, as described for example in reference to
Thermal resistance is defined as the opposition a material presents to the flow of heat. The in-plane and through-plane thermal resistance can be indicative of the thermal anisotropy of flexible graphite.
Thermal properties of material can be measured with a variety of equipment. Common approaches for measuring thermal properties in the in-plane and through-plane directions include a laser flash method, a hot wire method, an ASTM D5470 method and combinations of the above methods. ASTM D5470 is a Standard Test Method for Thermal Transmission Properties of Thermally Conductive Electrical Insulation Materials and can be used to determine thermal resistance. The method involves placing the material to be tested between a hot surface and a cold surface, and measuring the heat flow.
Line 2130 labeled “blended graphite” shows the behavior of thermal resistance for flexible graphite with a thickness of 0.42 mm and a density of 1.83 g/cm3, produced by the system and method described herein in which the graphite is produced according to method 1400 of
Line 2140 labeled “Buttoned pattern graphite” shows the behavior of thermal resistance for flexible graphite with a thickness of 0.42 mm and a density of 1.9 g/cm3, produced by the system and method described herein in which the graphite is produced according to method 1400 of
The thermal resistance 2120 for the commercially available uncoated graphite sheet provides a baseline value.
Thus, the systems and methods described above can be used to manipulate the orientation of graphite flakes to produce flexible graphite with greater through-plane thermal conductivity which can be beneficial in some applications such as use as thermal interface materials
A thermal interface material (also known as a TIM) is a thermally conductive material that is commonly used to transfer heat from a heat source to a heat sink. Generally is it desirable that a TIM can transport high heat flux, and provide excellent contact between the surfaces, for example so that it fills voids or irregularities between a heat source (or mount thereof) and a heat sink and/or between and heat spreader and a heat sink. Often pastes, greases and films are used as TIMS, but they generally have poor electrical conductivity.
Flexible graphite sheet materials produced by the system and methods described above can be used as TIMs. Such materials can provider through-plane thermal conductivity that is an order of magnitude greater than commonly used TIMs, and that is significantly (for example, 3-5 times) greater than conventional graphite sheet materials. Some embodiments of the materials described herein have been found to have though-plane conductivities of greater than 20 W/mK. Some embodiments of the materials described herein have been found to have though-plane conductivities of greater than 25 W/mK. For some example, though-plane conductivities of at least 30 W/mK have been achieved. Embodiments of the graphite sheet materials described herein can conform well to the surface(s) with which they are in contact. Graphite offers other advantages over conventional TIMs including reduced cost, low thermal expansion, not being susceptible to corrosion and low material creep.
The conventional mechanism for heat removal includes thermal interface material (TIM) 2220 and copper heat spreader 2230. Heat is conducted away from LED 2210 through TIM 2220 to copper heat spreader 2230.
Flexible graphite sheet 2240 includes two or more regions with different directional thermal properties. Region 2250, typically located under and adjacent to LED 2210, has graphite flakes in a preferred orientation perpendicular to the plane of the material such as flakes 2255A and 2255B. Region 2260 typically occupying the bulk of flexible graphite sheet 2240, and surrounding one or more regions such as region 2250, has graphite flakes in a preferred horizontal orientation such as flakes 2265A and 2265B. In an alternative embodiment, region 2260 comprises graphite flakes in an essentially random orientation.
The two or more regions of flexible graphite sheet 2240 having different directional thermal properties are integrated as shown in
In an alternative embodiment, flexible graphite sheet 2240 can comprise separate pieces having different directional thermal properties, and bonded or laminated together to form a single heat removal mechanism.
Flexible graphite sheet 2240 can be produced by the technology described herein, for example by one or more of methods 300 and 1400 of
In one approach, flexible graphite sheet 2240 can be produced by placing a sheet of flexible graphite in a die cavity (such as cavity 1515 of die 1510 of
A benefit of the method described above is that heat can be transported away from the LED, first in the through-plane or vertical direction, and then in the along-plane or horizontal direction.
The integrated thermal interface material produced by the method described above, and comprising two or more regions of material with configurable thermal anisotropy, is suitable for a variety of applications including, but not limited to, heat removal from luminaires and power rectifiers.
Formable graphite-based heat sinks are three-dimensional structures formed from graphite material that is flexible and can be folded and shaped. By three-dimensional structures, it is meant that the structures are not simply sheet or flat plate configurations of graphite-based materials, such as might be used in heat spreaders or as TIMs. The heat sinks described herein include structures with multiple features (such as ribbing or raised dots) and can efficiently dissipate heat from a surface being cooled.
Heat sinks can be manufactured from expanded graphite sheet material that has been compressed to a higher density, and is formable and foldable, without the need to impregnate with a resin. Although resin can be added, embodiments of the technology described herein achieve a high enough density and have mechanical and thermal properties suitable for heat sink and heat exchanger applications without the need to add resin to the expanded graphite sheet material.
Many different geometries are possible using folding and shaping of the flexible graphite sheet material. For example, the material can be made into flexible strips. In other examples, materials with different densities can be used in combination such as a densified graphite substrate with flexible ribbon graphite and densified heat sink fins. The heat sinks and other devices described herein can be substantially, if not entirely, graphite structures and are different from conventional heat sinks and other devices that employ a combination of graphite and metal in their construction. In some examples, the material (or a single component made from the material) can be used to provide more than one function at the same time.
The heat sink assemblies illustrated in the preceding figures can be readily manufactured from resin-free graphite sheet material that has been compressed to sufficient density and embossed with features to increase heat dissipation. Embodiments of the processed graphite material described herein can be shaped and folded, and the constituent graphite flakes aligned along a new axis to provide more efficient heat transfer in the desired direction.
Heat sink assembly 2400 in
The graphite heat sink assembly components described above can be integrated so as to remove some of the mechanical linkages between them. In some embodiments, the graphite devices can be manufactured as a single contiguous mechanical part. In other embodiments, the heat sink can be a separate part, and mechanically and thermally connected to the other integrated graphite elements. A benefit of fewer links is greater thermal efficiency.
As described above, graphite sheet material can be patterned in various ways in order to change its properties, including its ability to be densified, laminated, folded or shaped, as well as its in-plane and through plane thermal and electrical conductivity, and its surface area.
In an aspect of the present technology, graphite sheet material is selectively patterned in different regions to impart desirable localized properties to the material. This approach can be taken for a wide variety of end-use application and in the fabrication of a variety of devices that comprise graphite sheet material. For example, this approach can be taken in the fabrication of heat exchangers. It can also be used in the fabrication of integrated flexible graphite heat removal devices as described in further detail below. Such integrated heat removal devices can be unitary structures, for example, with essentially no thermal interfaces within the device itself. In some embodiments they are made from a single sheet of graphite material.
Separate dies can be used to pattern different regions of the material or a single die with multiple different features or patterns in different regions can be used.
In some embodiments, integrated heat removal devices (or other devices made from graphite sheet material that is selectively patterned in different regions to impart desirable localized properties to the material) can be coated or resin impregnated after they are formed. In some cases it can be desirable to coat or resin-impregnate only a portion of the device. For example, for electronics applications the thermal interface pads or region 2520 in integrated heat removal device 2500 of
For some end-use applications, it is desirable to impregnate the graphite sheet material, or devices or components made therefrom, or portions thereof, with a resin. In some embodiments a methacrylate resin can be used. As described above, it can be desirable to impregnate graphite devices after they are formed or shaped, for example, to enhance their strength and rigidity, and/or to render them more durable and weatherproof.
Various known techniques can be used for resin impregnation. For example, a suitable resin can be prepared and a graphite part can be placed in a vessel and subjected to a vacuum. The resin can then be introduced into the vessel under vacuum. The pressure can then be increased to facilitate impregnation of the resin into the graphite part. The part can then be removed from the vessel, excess resin can be washed off and then the part can be rinsed. The resin can then be cured, for example, by heating.
For some end-use applications, it is desirable to coat the graphite sheet material, or devices or components made therefrom, with a coating or protective layer. The coating can be selected to be thermally conductive so as not to significantly adversely affect heat flow. In electronics applications or environments, the coating can be selected to be substantially non-electrically conducting, thereby providing electrical isolation between components and preventing, or at least reducing, voltage leakages between electronic circuit components and/or the electronic system's environment. A coating can also reduce the likelihood or small particles or graphite flaking or being abraded from the surface of the component and causing short-circuits or other problems. A coating can be used to reduce the permeability of graphite materials to fluids, for example, in sealing or gasketing applications. For example, a coating can be used to inhibit hydrogen permeation and/or inhibit water/coolant absorption. A coating can be used to enhance the rigidity or durability of the graphite components. Yet another type of coating is one that provides chemical resistance.
In the power electronics industry a thin film thermal interface material (TIM) is often employed between a hot electrical device such as a power rectifier and a thermal heat sink typically made from copper or aluminum. One disadvantage of the thermal interface material is that it is generally a poor conductor of heat.
The power electronics industry often requires the power electronics to be isolated from the operator. Typically, a thin polymer film or sheet of dielectric material is placed between the power electronics device and the thermal interface material or heat sink to provide electrical isolation. While helping to electrically isolate a device, the polymer film or plastic sheet can further adversely affect thermal conductivity.
When graphite sheet material, or components made therefrom, are used for thermal management in electronics applications, preferably a coating is used that provides electrical insulation while still allowing heat to conduct from a hot surface on one side of the coating to the graphite material on the other side of the coating.
Using the technology described herein, a coating can be configured to provide suitable electrical resistance between an electrical device and a formable graphite heat sink or heat exchanger. The coating can be configured to prevent or at least deter galvanic coupling and/or electrical shorting.
Any suitable coating material can be used including, but not limited to, epoxies, silicones and urethanes, and other resins. Any suitable application method or process can be employed including, but are not limited to, sprays, chemical vapour deposition, and vacuum impregnation.
Parylene is the trade name for poly(p-xylene) polymers that can be deposited on a surface, via a chemical vapor deposition process. For some applications, parylene can be used as a moisture and dielectric barrier. Parylene C is popular owing to a number of advantages including barrier properties and cost. A coating including parylene C can be an ultra-thin coating that provides a dielectric barrier to a graphite substrate. The vapor deposition process can provide control of layer thickness. In some embodiments the film thickness can range from a few angstroms to about 75 microns.
Electrical isolation tests were performed on conventional graphite sheet materials that were coated with different thicknesses of parylene C. Samples of 0.4 mm thick graphite sheet with 10, 25 and 32 micron coating thicknesses were tested. For the 10 micron coating the breakdown voltage was about 2 kV (at 1-5 mA); for the 25 micron coating the breakdown voltage was about 10 kV (at 5 mA) and for the 32 micron coating the breakdown voltage exceeded the capability of the test method but was greater than 11.9 kV. For an uncoated sample the breakdown voltage was 32-162 V at 1-5 mA. The thermal conductivity of the coated samples was somewhat reduced compared to the uncoated samples. In one set of thermally conductivity tests an uncoated sample had a thermal conductivity of about 4.5 W/mK compared to about 0.5-1.2 W/mK for the coated samples depending on the coating thickness.
These results indicate that by using graphite materials with higher through-plane thermal conductivity prepared as described herein, and applying a thin parylene C coating, it is possible to satisfy the voltage isolation requirements for many end-use power electronics applications while still having a material that has significantly higher thermal conductivity than presently available materials. Thicker or thinner coatings can be used depending on the level of voltage isolation that is needed. The layer is typically applied substantially uniformly to all of the surface features, although it need not be applied uniformly and/or to all surfaces.
While particular elements, embodiments and applications of the present invention have been shown and described, it will be understood, that the invention is not limited thereto since modifications can be made by those skilled in the art without departing from the scope of the present disclosure, particularly in light of the foregoing teachings.
This application is a continuation of U.S. patent application Ser. No. 15/630,256 filed on Jun. 22, 2017, entitled “Apparatus and Methods for Processing Exfoliated Graphite Materials” which, in turn, claims priority benefits from U.S. patent application Ser. No. 14/583,402 filed on Dec. 26, 2014, also entitled “Apparatus and Methods for Processing Exfoliated Graphite Materials”. The '256 application, the '402 application, and this application claim priority benefits from U.S. provisional patent application No. 61/921,042 filed on Dec. 26, 2013, entitled “System and Method for Heat Dissipation Using Graphite Materials.” The '256 application, the '402 application, and this application also claim priority benefits from U.S. provisional patent application No. 62/035,210 filed on Aug. 8, 2014, entitled “Apparatus and Methods for Processing of Exfoliated Graphite Material”. The '256, '402, '042, and '210 applications are hereby incorporated by reference herein in their entireties. With respect to the above-mentioned applications, to the extent any amendments, characterizations or other assertions previously made in any such related patent applications or patents, including any parent, co-pending or continuing application with respect to any art, prior or otherwise, could be construed as a disclaimer of any subject matter supported by the disclosure of the present application, such disclaimer is hereby rescinded and retracted. Prior art previously considered in any related patent application(s) or patent(s), including any parent, co-pending or continuing application, should be reconsidered with respect to the subject matter being claimed in the present application.
| Number | Date | Country | |
|---|---|---|---|
| 62035210 | Aug 2014 | US | |
| 61921042 | Dec 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15630256 | Jun 2017 | US |
| Child | 16223417 | US | |
| Parent | 14583402 | Dec 2014 | US |
| Child | 15630256 | US |