This nonprovisional application claims priority under 35 U.S.C. § 119(a) on Patent Application No. 2004-281054 filed in JAPAN on Sep. 28, 2004, the entire contents of which are hereby incorporated by reference.
1. Field of the Invention
The present invention relates to a resist composition suitable for lithography and the like, acting by radiation ray of high energy such as far ultraviolet ray (including excimer laser and the like), electron beam, X ray or radiation light and the like, and also relates to a resin solution therefor or for application films in semiconductors.
2. Description of Related Art
Recently, with progress in higher integration of integrated circuits, there occurs a requirement for formation of submicron patterns. Particularly, lithography using excimer laser from krypton fluoride or argon fluoride is paid to attention since it enables production of 64 M DRAM to 1 G DRAM. The so-called chemically amplified resist composition suitable for lithograph process using excimer laser basically comprises a binder unit an acid generator and a solvent. As the binder unit, resins which is insoluble or poorly soluble in an alkali aqueous solution, and which becomes soluble in an alkali aqueous solution by the action of an acid, are generally used.
Foreign objects (i.e. minute particles derived from resins) contained in the chemically amplified resist compositions used in the production of highly integrated circuits cause defects generation in the formation of patterns. Reduction of the amount of the foreign objects in the photo resist composition is highly required.
Photo resist compositions are used as materials for microfabricated pattern formation in production of IC, ISI, or the like which are used for electronic calculators, etc. Following higher integration of LSI, etc., the design rule of integrated circuits has changed from 0.35 μm to 0.1 μm.
The present inventors realized that, by the long term storage of chemically amplified composition, there occurs such problem that the composition becomes denatured and resultantly satisfactory resist films can not be obtained. For example, though satisfactory resist films are obtained when resist solution right after their production is used, there occur pinhole defects or gelated foreign objects on resist films when resist solution after long term storage is used. Such pinhole defects or gelated foreign objects are one of causes of great decrease of yield when integrated circuits are produced.
The photo resist composition is requested to have such ability that all the components are completely dissolved in the solvent used and the composition have good preservation stability even after long time storage in addition to the basic performances such as resolution, sensitivity, profile, coatability, and the like.
An object of the present invention is to provide a chemically amplified resist composition having excellent long term preservation stability with maintaining less defects on resist film formed from the composition, in addition to good filtration characteristics.
Another object of the present invention is to provide a resin solution suitable for the chemically amplified resist composition above and also suitable for application film in semiconductor having less defects on the films formed from the resin solution.
The present invention relates to the followings:
<1> A chemically amplified resist composition comprising a treated resin (1), an acid generator and a solvent, wherein resin (1) is
(a) a (meth)acrylic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit having an alicyclic hydrocarbon group in its side chain (hereinafter referred to as “Resin (a)”) or
(b) a styrenic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit derived from hydroxystyrene (hereinafter referred to as “Resin (b)”), and wherein the treated resin (1) is obtained by
(A) contacting crude resin (1) with activated carbon at 40 to 90° C. to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 90° C.
<2> The composition according to <1>, wherein the resin (1) contains a repeating unit having acid labile group.
<3> The composition according to <2>, wherein the repeating unit having acid labile group is a repeating unit having a group dissociated by the action of an acid.
<4> The composition according to <3>, wherein the content of the repeating unit having a group dissociated by the action of an acid in the resin (1) is 10 to 80% by mol.
<5> The composition according to any one of <1> to <4>, wherein the resin (1) is Resin (a) and the repeating unit having an alicyclic hydrocarbon group in its side chain is at least one repeating unit selected from the group consisting of a repeating unit derived from 2-alkyl-2-adamantyl (meth)acrylate and a repeating unit derived from 1-(1-adamantyl)-1-alkylalkyl (meth)acrylate.
<6> The composition according to any one of <3> to <5>, wherein the repeating unit having a group dissociated by the action of an acid is a repeating unit of the formula (1)
wherein R1 represents hydrogen, methyl or trifluoromethyl, and X represents a residue of tertiary alcohol or a group represented by the formula of —CH(R2)—OR3, wherein R2 represents hydrogen or C1-5 alkyl, R3 represents C1-3 alkyl, (alicyclic hydrocarbyl)oxyalkyl or (alicyclic hydrocarbyl)carbonyloxyalkyl, or 72 and R3 bond to form alkylene having 5 to 10 carbon atoms wherein at least one —CH2— in the alkylene other than the —CH2— connected to the adjacent —O— may be substituted by —O—.
<7> The composition according to any one of <1> to <6>wherein the resin (1) is Resin (a) and Resin (a) further comprises at least one repeating unit selected from the group consisting of a repeating unit derived from 3-hydroxy-1-adamantyl (meth)acrylate, a repeating unit derived from 3,5-dihydroxy-l-adamantyl (meth)acrylate, a repeating unit derived from (meth)acryloyloxy-y-butyrolactone wherein at least one hydrogen on the lactone ring may optionally be substituted by alkyl, a repeating unit of the following formula (Ia) and a repeating unit of the following formula (Ib):
wherein R4 represents hydrogen, methyl or trifluoromethyl, R5represents methyl or trifluoromethyl, n represents an integer of from 0 to 3, and when a is 2 or 3, each of R5 is the same or different.
<8> The composition according to any one of <1> to <7> wherein the resin (1) is Resin (a) and Resin (a) further comprises at least one repeating unit selected from the group consisting of a repeating unit derived from an aliphatic unsaturated dicarboxylic anhydride and a repeating unit derived from 2-norbornene.
<9> The composition according to any one of <1> to <8> wherein the resin (1) is Resin (a) and the crude Resin (a) is a resin produced by radical polymerization of a monomer having (meth)acrylic ester structure and leading to a repeating unit having an alicyclic hydrocarbon group in its side chain in an organic solvent selected from the group consisting of aromatic hydrocarbon, ether, glycol ether ester, ester, ketone and alcohol at a temperature of −50 to 100° C.
<10> The composition according to <1> to <4> wherein the resin (1) is Resin (b) and the repeating unit having a group dissociated by the action of an acid is a repeating unit of the formula (3)
wherein R8 represents hydrogen or methyl, R9 and R10 each independently represents hydrogen, C1-6 alkyl, C3-6 cycloalkyl, C1-6 haloalkyl, C3-6 halocycloalkyl, or optionally substituted phenyl, or R9 and R10 bond to form C5-10 alkylene chain, R11 represents C1-10 alkyl, C3-10 cycloalkyl, C1-10 haloalkyl, C3-10 halocycloalkyl or C7-12 aralkyl.
<11> The composition according to any of <1> to <4> and <10> wherein the resin (1) is Resin (b) and Resin (b) further comprises at least one repeating unit selected from the group consisting of a repeating unit of the formula (4) and a repeating unit of the following formula (5): formula (4)
wherein R12 represents hydrogen or methyl, R13 represents hydrogen, Cl-4 alkyl, C1-8 alkoxy, C3-8 cycloalkyloxy or a group of the following formula (6),
wherein R14 represents C1-8 alkyd C6-10 aryl or saturated heterocyclic group, Q represents single bond or oxygen, and 1 denote 0 or natural number, formula (5)
wherein R15 represents hydrogen, methyl or trifluoromethyl, and R16 represents hydrocarbon group having bonding site at primary or secondary carbon.
<12> The composition according to any of <1> to <4>, <10> and <11> wherein the Resin (1) is Resin (b) and the crude Resin (b) is a resin produced i) by living radical polymerization or living anion polymerization of protected hydroxystyrene, deprotection and re-protection, or ii) by radical polymerization of protected hydroxystyrene or protected hydroxystyrene and vinyl monomer, deprotection and re-protection.
<13> The composition according to any one of <1> to <12> which further comprises an amine.
<14> The composition according to any one of <1> to <13> wherein clogging degree of the composition is 0.9 or more when the composition is measured and calculated by the following definition.
Definition of Clogging Degree of Resist Composition
At 23° C., resist composition is poured into a filtration equipment in which a round and track-etch membrane filter (diameter: 47 mm, average pore size: 0.05 μm, thickness: 6 μm, pore density: 6×108 pores/cm2) is set to a holder having volume of 300 ml, then pressure filtration is started at a pressure of 100 kPa. The filtrate is collected in a receiver on a balance, and weight change of the filtrate is measured every one minute. Filtration time and accumulated weight of filtrate discharged are measured and linear velocity is calculated by dividing the weight of filtrate discharged per one minute by effective filter area. Maximum value of linear velocity reached in 10 minutes after starting the filtration is defined as VI (the linear velocity at initial standard point). The linear velocity at the point the accumulated weight of filtrate discharged reaches to 15 g converted to the weight of solid components of the resist composition is measured and calculated in the same manner and is defined as V2. Clogging Degree is a value calculated by dividing V2 by V1.
<15> The composition according to any one of <1> to <14>, wherein the treated resin (1) is obtained by
(A) contacting crude resin (1) with activated carbon at 40 to 80° C. to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 80° C.
<16> The composition according to any one of <1> to <15>, wherein the treated resin (1) is obtained by
(A) contacting crude resin (1) with activated carbon at 50 to 70° C. to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 50 to 70° C.
<17> A process for producing a chemically amplified resist composition which comprises contacting crude resin (1) with activated carbon at 40 to 90° C. to obtain hemi-treated resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel to obtain treated resin (1), and mixing the treated resin (1), an acid generator and an organic solvent, wherein the resin (1) is
(a) a (meth)acrylic resin which is insoluble or poorly soluble in an m aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit having an alicyclic hydrocarbon group in its side chain (hereinafter referred to as “Resin (a)”) or
(b) a styrenic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit derived from hydroxystyrene (hereinafter referred to as “Resin (b)”).
<18> The process according to <17> wherein the resin (1) is Resin (a) and crude Resin (a) is produced by radical polymerization of a monomer having (meth)acrylic ester structure and leading to a repeating unit having an alicyclic hydrocarbon group in its side chain in an organic solvent selected from the group consisting of aromatic hydrocarbon, ether, glycol ether ester, ester, ketone and alcohol at a temperature of -50 to 100° C.
<19> The process according to <17> wherein the resin (1) is Resin (b) and crude Resin (b) is produced i) by living radical polymerization or living anion polymerization of protected hydroxystyrene, deprotection and re-protection, or ii) by radical polymerization of protected hydroxystyrene or protected hydroxystyrene and vinyl monomer, deprotection and re-protection.
<20> The process according to any one of <17> to <19> wherein the contact of crude resin (1) with activated carbon is carried out at 40 to 80° C.
<21> The process according to any one of <17> to <20> wherein the contact of crude resin (1) with activated carbon is carried out at 50 to 70° C.
<22> A process for producing a chemically amplified resist composition which comprises contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 90° C. to obtain treated resin (1), and mixing the treated resin (1), an acid generator and an organic solvent, wherein the resin (1) is
(a) a (meth)acrylic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit having an alicyclic hydrocarbon group in its side chain (hereinafter referred to as “Resin (a)”) or
(b) a styrenic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit derived from hydroxystyrene (hereinafter referred to as “Resin (b)”).
<23> The process according to <22> wherein the resin (1) is Resin (a) and crude Resin (a) is produced by radical polymerization of a monomer having (meth)acrylic ester structure and leading to a repeating unit having an alicyclic hydrocarbon group in its side chain in an organic solvent selected from the group consisting of aromatic hydrocarbon, ether, glycol ether ester, ester, ketone and alcohol at a temperature of −50 to 100° C.
<24> The process according to <22> wherein the resin (1) is Resin (b) and crude Resin (b) is produced i) by living radical polymerization or living anion polymerization of protected hydroxystyrene, deprotection and re-protection, or ii) by radical polymerization of protected hydroxystyrene or protected hydroxystyrene and vinyl monomer, deprotection and re-protection.
<25> The process according to any one of <22> to <24> wherein the contact of crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel is carried out at 40 to 80° C.
<26> The process according to any one of <22> to <25> wherein the contact of crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel is carried out at 50 to 70° C.
<27> A resin solution comprising resin (1) and a solvent, wherein the resin (1) is selected from
(a) a (meth)acrylic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit having an alicyclic hydrocarbon group in its side chain (hereinafter referred to as “Resin (a)”) and
(b) a styrenic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit derived from hydroxystyrene (hereinafter referred to as “Resin (b)”), and wherein the resin (1) is obtained by
(A) contacting crude resin (1) with activated carbon at 40 to 90° C. to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 90° C.
<28>. The resin solution according to <27> wherein clogging degree of the resist solution is 0.9 or more when the solution is measured and calculated by the following definition.
Definition of Clogging Degree of Resin Solution
At 23° C., resin solution is poured into a filtration equipment in which a round and track-etch membrane filter (diameter: 47 mm, average pore size: 0.05 μm, thickness: 6 μm, pore density: 6×108 pores/cm2) is set to a holder having volume of 300 ml, then pressure filtration is started at a pressure of 100 kPa. The filtrate is collected in a receiver on a balance, and weight change of the filtrate is measured every one minute. Filtration time and accumulated weight of filtrate discharged are measured and linear velocity is calculated by dividing the weight of filtrate discharged per one minute by effective filter area. Maximum value of linear velocity reached in 10 minutes after starting the filtration is defined as V1 (the linear velocity at initial standard point). The linear velocity at the point the accumulated weight of filtrate discharged reaches to 15 g converted to the weight of solid components of the resist composition is measured and calculated in the same manner and is defined as V2. Clogging Degree is a value calculated by dividing V2 by V1.
<29> The resin solution according to <27> or <28>, wherein the resin (1) is obtained by
(A) contacting crude resin (1) with activated carbon at 40 to 80° C. to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 80° C. <30> The resin solution according to any one of <27> to <29>, wherein the resin (1) is obtained by
(A) contacting crude resin (1) with activated carbon at 50 to 70° C. to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or (B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 50 to 70° C.
The present chemically amplified resist composition contains a treated resin (1), an acid generator and a solvent, and the treated resin can be obtained by
(A) contacting crude resin (1) with activated carbon at 40 to 90° C., preferably at 40 to 80° C., to obtain hemi-treated crude resin (1) and contacting the hemi-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel,
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 90° C., preferably at 40 to 80° C.
Resin (1) is (a) a (meth)acrylic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit having an alicyclic hydrocarbon group in its side chain or (b) a styrenic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit derived from hydroxystyrene.
The “(meth)acrylic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit having a alicyclic hydrocarbon group in its side chain” may hereinafter be referred to as “Resin (a)”, and the “styrenic resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid, and which comprises a repeating unit derived from hydroxystyrene” may hereinafter be referred to as “Resin (b)”
Resin (a)
“(meth)acrylic resin” means acrylic resin or methacrylic resin. “acrylic resin” means a polymer containing a repeating unit derived from acrylic acid or derivative thereof and “methacrylic resin” means a polymer containing a repeating unit derived from methacrylic acid or derivative thereof or a repeating unit derived from 2-(trifluoromethyl)acrylic acid or derivative thereof. “(meth)acrylic acid” means acrylic acid, methacrylic acid or 2-(trifluoromethyl)acrylic acid.
“repeating unit having alicylclic hydrocarbon group in its side chain” may hereinafter be referred to as “Alicyclic Repeating Unit”.
Examples of the alicyclic hydrocarbon group in Alicyclic Repeating Unit include 2-alkyl-2-adamantyl, 1-(1-adamantyl)-1-alkylalkyl, and such alicyclic hydrocarbon group forms a side chain itself or a part of a side chain connected to a main chain in a repeating unit. Alicyclic Repeating Unit is a repeating unit having a structure derived from vinyl monomer and having an alicyclic hydrocarbon group in its side chain. Examples of the structures derived from vinyl monomer include a structure derived from ester of (meth)acrylic acid and a structure derived from (meth)acrylamide, and the like.
As Alicyclic Repeating Unit, repeating units derived from ester of (meth)acrylic acid are preferred, and in such cases, Y represents an alicyclic hydrocarbon group when the ester part in the structure derived from ester of (meth)acrylic acid is showed by —COOY. Specific examples thereof include a repeating unit derived from isobornyl acrylate, a repeating unit derived from isobornyl methacrylate, a repeating unit derived from isobornyl 2-(trifluoromethyl)acrylate, a repeating unit derived from2-alkyl-2-adamantyl acrylate, a repeating unit derived from 2-alkyl-2-adamantyl methacrylate, a repeating unit derived from 2-alkyl-2-adamantyl 2-(trifluoromethyl)acrylate, a repeating unit derived from 1-(1-adamantyl)-1-alkylalkyl acrylate, a repeating unit derived from 1-(1-adamantyl)-l-alkylalkyl methacrylate, a repeating unit derived from 1-(1-adamantyl)-1-alkylalkyl 2-(trifluoromethyl)acrylate, and the like. Examples of the esters of (meth)acrylic acid having alicyclic hydrocarbon group in its side chain include alicyclic hydrocarbyl ester of (meth)acrylic acid in which a tertiary carbon bonds to carboxyl group, such as 2-alkyl-2-adamantyl acrylate, 2-alkyl-2-adamantyl methacrylate, 2-alkyl-2-adamantyl 2-(trifluoromethyl)acrylate, 1-(1-adamantyl)1-alkylalkyl acrylate, 1(1-adamantyl)-1-alkylalkyl methacrylate, 1-(1-adamantyl)-1-alkylalkyl 2-(trifluoromethyl)acrylate, and the like; alicyclic hydrocarbyl ester of (meth)acrylic acid in which a primary or secondary carbon bonds to carboxyl group, such as isobornyl acrylate, isobornyl methacrylate, isobornyl 2-(trifluoromethyl)acrylate, 2-adamantyl acrylate, 2-adamantyl methacrylate, 2-adamantyl 2-(trifluoromethyl)acrylate, (1-adamantyl)methyl acrylate, (1-adamantyl)methyl methacrylate, (1-adamantyl)methyl 2-(trifluoromethyl)acrylate, 2-(1-adamantyl)ethyl methacrylate, 1-(1-adamantyl)ethyl 2-(trifluoromethyl)acrylate, and the like. “ester of (meth)acrylic acid in which a tertiary carbon bonds to carboxyl group” may hereinafter be referred to as “Tertiary Alicyclic (Meth)acrylate”, and “alicyclic hydrocarbyl ester of (meth)acrylic acid in which a primary or secondary carbon bonds to carboxyl group” may hereinafter be referred to as “Secondary Alicyclic (Meth)acrylate”.
Examples of (meth)acrylic resin including Alicyclic Repeating Unit includes polymers comprising repeating unit derived from ester of (meth)acrylic acid having alicyclic hydrocarbon group, especially include copolymers comprising repeating unit derived from ester of (meth)acrylic acid having alicyclic hydrocarbon group. When Alicyclic Repeating Unit is a repeating unit derived from Tertiary Alicyclic (Meth)acrylate, homopolymer thereof may also be exemplified as the (meth)acrylic resin comprising Alicyclic Repeating Unit. When (meth)acrylic resin comprising Alicyclic Repeating Unit is a copolymer, the content of Alicyclic Repeating Unit in Resin (a) is preferably 10% by mol or more, more preferably 30% by mol or more. When Resin (a) comprises a repeating unit derived from 2-alkyl-2-adamantyl (meth)acrylate or 1(1-adamantyl)-1-alkylalkyl (meth)acrylate, the content of the repeating unit is advantageously 15% by mol or more.
Resin (a) is a resin which is insoluble or poorly soluble in an alkali aqueous solution and which becomes soluble in an alkali aqueous solution by the action of an acid.
Resin (a) contains a repeating unit having an acid labile group so as to be a resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid. Specifically, it contains a repeating unit having a group dissociated by the action of an acid.
Examples of the repeating units having a group dissociated by the action of an acid include repeating units derived from Tertiary Alicyclic (Meth)acrylate described above and repeating units having other carboxylate structure. When a part of ester in the other carboxylate structure is shown by —COOX, —OX represents a group dissociated by the action of an acid and X represents a residue of tertiary alcohol or a group represented by the formula —CH(R2)—OR3, wherein R2 represents hydrogen or C1-5 alkyl, R3 represents C1-3 alkyl, (alicyclic hydrocarbyl)oxyalkyl or (alicyclic hydrocarbyl)carbonyloxyalkyl, or R2 and R3 bond to form alkylene having 5 to 10 carbon atoms wherein at least one —CH2— in the alkylene other than the one connected to the adjacent —O— may be substituted by —O—. Specific examples thereof include a repeating unit of the formula (1)
wherein R1 represents hydrogen, methyl or trifluoromethyl, and X represents the same meaning above, a repeating unit derived from ester of unsaturated alicyclic add, and the like.
Examples of residues of tertiary alcohol include alicyclic hydrocarbon groups having a bonding site at a tertiary carbon such as 2-alkyl-2-adamantyl, 1(1-adamantyl)1-alkylalkyl, and the like; and tertiary alkyl such as tert.-butyl.
Examples of groups represented by —CH(R2)—OR3 include methoxymethyl, ethoxymethyl, 1-ethoxyethyl, 1-isobutoxyethyl, 1-isopropoxyethyl, 1-ethoxypropyl, 1(2-methoxyethoxy)ethyl, 1-(2-acetoxyethoxy)ethyl, 1-[2-1-adamantyloxy]ethoxy]ethyl, 1-[2-(adamantanecarbonyloxy)ethoxy]ethyl, tetrahydro-2-furyl, tetrahydro-2-pyranyl, and the like.
Monomers leading to repeating units having a group dissociated by the action of acid may be Tertiary Alicyclic (Meth)acrylate, other (meth)acrylates such as ester of methacrylic acid and ester of acrylic acid; and esters of unsaturated alicyclic carboxylic acids such as ester of norbornenecarboxylic acid, ester of tricyclodecenecarboxylic add and ester of tetracyclodecenecarboxylic acid.
Among the monomers, monomers having bulky group such as alicyclic hydrocarbon group having a bonding site at a tertiary carbon are preferably used for better resolution of the resist composition obtained.
Examples of such monomers having bulky group include 2-alkyl-2-adamantyl (meth)acrylate, 1-(1-adamantyl)1-alkylalkyl (meth)acrylate, 2-alkyl-2-adamantyl 5-norbornen-2-carboxylate, 1-(1-adamantyl)-1-alkylalkyl 5-norbornen-2-carboxylate, and the like.
Among them, 2-alkyl-2-adamantyl (meth)acrylate and 1-(1-adamantyl)-1-alkylalkyl (meth)acrylate are more preferred. They are monomers having a bulky group dissociated by the action of an acid as well as Tertiary Alicyclic (Meth)acrylate.
2-Alkyl-2-adamantyl (meth)acrylate is especially preferred for much better resolution. Examples of such 2-alkyl-2-adamantyl (meth)acrylate include 2-methyl-2-adamantyl acrylate, 2-methyl-2-adamantyl methacrylate, 2-ethyl-2-adamantyl acrylate, 2-ethyl-2-adamantyl methacrylate, 2-n-butyl-2-adamantyl acrylate, and the like. Among them, 2-ethyl-2-adamantyl (meth)acrylate is preferred for better balance of sensitivity and heat resisting property. If necessary, other monomers having a group dissociated by the action of an acid can be used together.
2-Alkyl-2-adamantyl (meth)acrylate can usually be produced by reacting 2-alkyl-2-adamantanol or metal salt thereof with an acrylic halide or methacrylic halide.
In addition to the above-mentioned repeating unit having a group dissociated by the action of an acid, Resin (a) used for the present composition can also contain other repeating units not dissociated or not easily dissociated by the action of an acid.
Examples of such other repeating units which can be contained include repeating units derived from unsaturated carboxylic acid such as acrylic acid and methacrylic acid, repeating units derived from aliphatic unsaturated dicarboxylic anhydrides such as maleic anhydride and itaconic anhydride, repeating unit derived from 2-norbornene, repeating unit derived from (meth)acrylonitrile, repeating units derived from various (meth)acrylates, and the like.
Particularly, to contain, in addition to the repeating unit having a group dissociated by the action of an acid, further at least one repeating unit selected from the group consisting of a repeating unit derived from 3-hydroxy-1-adamantyl (meth)acrylate, a repeating unit derived from 3,5-dihydroxy-1-adamantyl (meth)acrylate, a repeating unit derived from (meth)acryloyloxy-γ-butyrolactone wherein at least one hydrogen on the lactone ring may optionally be substituted by alkyl a repeating unit of the following formula (Ia) and a repeating unit of the following formula (Ib), in the resin in the present composition, is preferable from the standpoint of the adhesiveness of resist to a substrate.
Here, R4 represents hydrogen, methyl or trifluoromethyl, R5 represents methyl or trifluoromethyl, n represents an integer of from 0 to 3, and when n is 2 or 3, each of R5 is the same or different.
3-Hydroxy-1-adamantyl (meth)acrylate and 3,5-dihydroxy-1-adamantyl (meth)acrylate can be produced, for example, by reacting corresponding hydroxyadamantane with (meth)acrylic acid or its acid halide, and they are also commercially available.
Further, (meth)acryloyloxy-y-butyrolactone, wherein at least one hydrogen on the lactone ring may optionally be substituted by allyl, can be produced by reacting corresponding α- or β-bromo-γ-butyrolactone with acrylic acid or methacrylic acid, or reacting corresponding α- or β-hydroxy-γ-butyrolactone with acrylic halide or methacrylic halide.
As monomers leading to repeating units of the formulae (Ia) and (Ib), specifically listed are, for example, (meth)acrylates of alicyclic lactones having hydroxyl described below, and mixtures thereof, and the like. These esters can be produced, for example, by reacting corresponding alicyclic lactone having hydroxyl with (meth)acrylic acids, and the production method is described in, for example, JP2000-26446A
When any of the repeating unit derived from 3-hydroxy-1-adamantyl (meth)acrylate, the repeating unit derived from 3,5-dihydroxy-1-adamantyl (meth)acrylate, the repeating unit derived from α-(meth)acryloyloxy-γ-butyrolactone, the repeating unit derived from β-(meth)acryloyloxy-γ-butyrolactone and the repeating unit of the formulae (Ia) and (Ib) is contained in the resin, not only the adhesiveness of the resist to a substrate is improved, but also the resolution of the resist is improved.
Here, examples of the (meth)acryloyloxy-γ-butyrolactone include α-acryloyloxy-γ-butyrolactone, α-methacryloyloxy-γ-butyrolactone, α-acryloyloxy-β,β-dimethyl-γ-butyrolactone, α-methacryloyloxy-β,β-dimethyl-γ-butyrolactone, α-acryloyloxy-α-methyl-γ-butyrolactone, α-methacryloyloxy-α-methyl-γ-butyrolactone, β-acryloyloxy-γ-butyrolactone, β-methacryloyloxy-γ-butyrolactone, β-methacryloyloxy-α-methyl-γ-butyrolactone and the like.
When other repeating unit not dissociated or hardly dissociated by the action of an acid is contained, it is advantageous from the standpoint of dry etching resistance of the resist to contain 2-alkyl-2-adamantyl or 1-(1-adamantyl)1-alkylalkyl as the acid labile group in the resin.
The resin containing a repeating unit derived from 2-norbornene shows strong structure because of alicyclic group directly present on its main chain and shows a property that dry etching resistance is excellent. The repeating unit derived from 2-norbornene can be introduced into the main chain by radical polymerization using, for example, in addition to corresponding 2-norbornene, aliphatic unsaturated dicarboxylic anhydrides such as maleic anhydride and itaconic anhydride together. The repeating unit derived from 2-norbornene is formed by opening of its double bond, and can be represented by the formula (II). The repeating unit derived from maleic anhydride and the repeating unit derived from itaconic anhydride which are the repeating unit derived from aliphatic unsaturated dicarboxylic anhydrides are formed by opening of their double bonds, and can be represented by the formula (III) and the formula (IV), respectively.
Here, R6 and R7 in the formula (II) each independently represent hydrogen, alkyl having 1 to 3 carbon atoms, hydroxyalkyl having 1 to 3 carbon atoms, carboxyl, cyano or —COOZ group in which Z represents alcohol residue, or R6 and R7 can bond together to form a carboxylic anhydride residue represented by —(═O)OC(═O)—.
In R6 and R7, examples of the alkyl include methyl, ethyl, propyl and isopropyl, specific examples of hydroxyalkyl include hydroxymethyl, 2-hydroxyethyl and the like.
In 6 and R7, COOZ group is an ester formed from carboxyl, and as the alcohol residue corresponding to Z, for example, optionally substituted alkyls having about 1 to 8 carbon atoms, 2-oxooxolan-3- or -4-yl and the like are listed, and as the substituent on the alkyl hydroxyl, alicyclic hydrocarbon group and the like are listed.
Specific examples of —COOZ include methoxycarbonyl, ethoxycarbonyl, 2-hydroxyethoxycarbonyl, tert-butoxycarbony, 2-oxooxalan-3-yloxycarbonyl, 2-oxooxalan4-yloxycarbonyl, 1,1,2-trimethylpropoxycarbonyl, 1-cyclohexyl-1-methylethoxycarbonyl, 1-(4methylcyclohexyl)-1-methylethoxycarbonyl, 1-(1-adamantyl)-1-methylethoxycarbonyl and the like.
Specific examples of the monomer used to lead to the repeating unit represented by the formula (II) may include the followings;
2-norbornene,
2-hydroxy-5-norbornene,
5-norbornen-2-carboxylic acid,
methyl 5-norbornen-2-carboxylate,
t-butyl 5-norbornen-2 carboxylate,
1-cyclohexyl-1-methylethyl 5-norbornen-2-carboxylate,
1-(4methylcyclohexyl)-1-methylethyl 5-norbornen-2-carboxylate,
1-(4hydroxycyclohexyl)-1-methylethyl 5-norbornen-2-carboxylate,
1-methyl-1-(4oxocyclohexyl)ethyl 5-norbornen-2-carboxylate,
1-adamantyl)-1-methylethyl 5-norbornen-2-carboxylate,
1-methylcyclohexyl 5-norbornen-2-carboxylate,
2-methyl-2-adamantyl 5-norbornen-2-carboxylate,
2-ethyl-2-adamantyl 5-norbornen-2-carboxylate,
2-hydroxyethyl 5-norbornen-2-carboxylate,
5-norbornen-2-methanol,
5-norbornen-2,3-dicarboxylic acid anhydride, and the like.
When resin (1) is Resin (a), Resin (a) preferably contains repeating unit(s) having a group dissociated by the action of an acid generally in a ratio of 10 to 80% by mol in all structural units of the resin though the ratio varies depending on the kind of radiation for patterning exposure, the kind of a group dissociated by the action of an acid, and the like.
When, in addition to repeating units having an acid labile group, other repeating units not dissociated or not easily dissociated by the action of an acid, for example, a repeating unit derived from 3-hydroxy-1-adamantyl (meth)acrylate, a repeating units derived from 3,5-dihydroxy-1-adamantyl (meth)acrylate, repeating units derived from (meth)acryloyloxy-γ-butyrolactone, wherein at least one hydrogen on the lactone ring may optionally be substituted by alkyl, a repeating unit of the formula (Ia) or (Ib), a repeating unit derived from 2-norbornene of the formula (II), a repeating unit derived from maleic anhydride of the formula (III), a repeating unit derived from itaconic anhydride of the formula (IV) and the like are contained, it is preferable that the sum of these repeating units is in the range of 20 to 90% by mol based on all repeating units of the resin.
When 2-norbornenes and aliphatic unsaturated dicarboxylic anhydride are used as copolymerization monomers, it is preferable to use them in excess amount in view of a tendency that these are not easily polymerized.
Crude Resin (a) used in the present invention can be produced, for example, by radical polymerization method. In the production of crude Resin (a), polymerization initiator is usually used. The amount of the polymerization initiator is usually 0.01 to 10 parts by weight based on 100 parts by weight of total monomers used in the production of Resin (a).
As polymerization initiators, thermal polymerization initiators and photo polymerization initiators can be used. Examples of the photo polymerization initiators include 2-hydroxy4′-(2-hydroxyethoxy)-2-methylpropiophenone, and the like. Examples of the thermal polymerization initiators include azo compounds such as 2,2′-azobisisobutyronitrile, 2,2′-azobis(2-methylbutyronitrile), 1,1′-azobis(cyclohexane-1carbonitrile), 2,2′-azobis(2,4-dimethylvaleronitrile), dimethyl 2,2′-azobis(2-methylpropionate), 2,2′-azobis(2-hydroxymethylpropionitrile), and the like; organic peroxides such as lauryl peroxide, tert-butyl hydroperoxide, benzoyl peroxide, tert-butyl peroxybenzoate, cumen hydroperoxide, diisopropyl peroxydicarbonate, di-n-propyl peroxydicarbonate, tert-butyl peroxyneodecanoate, ten-butyl peroxypivalate, (3,5,5-trimethylhexanoyl)peroxide, and the like; inorganic peroxides such as potassium persulfate, ammonium persulfate, hydrogen peroxide, and the like. Each of the polymerization initiators can be used alone or in combination with at least one other kind.
Further, chain transfer agents such as 1-butanethiol, 2-butanethiol, 1-octanethiol, 1-decanethiol, 1-tetradecanethiol, cyclohexanethiol, 2-methyl-1-propanethiol, and the like can be used in addition to the polymerization initiator above.
In the production of crude Resin (a), organic solvent is preferably the one which can dissolve monomers, initiator and crude Resin (a) obtained. Examples of such organic solvents include aromatic hydrocarbons such as toluene, xylene, and the like; glycol ether esters such as ethyl Cellosolve acetate, propylene glycol monomethyl ether acetate, and the like; ethers such as tetrahydrofuran, 1,4-dioxane, and the like; esters such as ethyl lactate, ethyl acetate, butyl acetate, amyl acetate, ethyl pyruvate, γ-butyrolactone, and the like; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, 2-heptanone, cyclohexanone, and the like; alcohols such as n-propyl alcohol, isopropyl alcohol, and the like. Each of the organic solvent can be used alone or in combination with at least one other kind.
Specific example of the radical polymerization method in the production of crude Resin (a) include the method wherein a vinyl monomer having an alicyclic hydrocarbon group in its side chain, organic solvent, and if necessary, other monomer are mixed under nitrogen atmosphere and a polymerization initiator is added thereto, and the mixture is stirred usually at from −50 to 100° C., preferably at 30 to 90° C. usually for 3 to 10 hours. In the method above, a part of the monomers or polymerization initiator can be added during the reaction, or after the dissolution.
The weight average molecular weight of crude Resin (a) used in the present invention is preferably from 3000 to 100000, and more preferably from 5000 to 20000.
Resin (b)
“styrenic resin” means a polymer containing a repeating unit derived from styrene or a derivative thereof.
Examples of the repeating units derived from hydroxystyrene include a repeating unit derived from p- or m-vinylphenol, a repeating unit derived from p- or m-hydroxy-α-methylstyrene, and the like. Examples of monomers leading to a repeating unit derived from hydroxystyrene include p- or m-vinylphenol, p- or m-hydroxy-α-methylstyrene, and the like.
Examples of the styrenic resin comprising a repeating units derived from hydroxystyrene include a polymer comprising a repeating unit derived from hydroxystyrene, specifically, a copolymer comprising a repeating unit derived from hydroxystyrene and at least one another repeating unit. The repeating unit derived from hydroxystyrene is preferably contained in an amount of 50% by mol or more, and more preferably of 70 to by mol or more.
Resin (b) is not only a styrenic resin containing a repeating unit derived from hydroxystyrene, but also a resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid.
Resin (b) contains a repeating unit having an acid labile group so as to be a resin which is insoluble or poorly soluble in an alkali aqueous solution and becomes soluble in an alkali aqueous solution by the action of an acid. Specifically, it contains a repeating unit having a group dissociated by the action of an add.
Examples of the repeating units having a group dissociated by the action of an acid include repeating units of the formula (1) above, repeating units of the formula (3)
wherein R8 represents hydrogen or methyl, R9 and R10 each independently represents hydrogen, C1-6 alkyl, C3-6 cycloalkyl, C1-6 haloalylw, C3-6 halocycloalkyl, or optionally substituted phenyl, or R9 and R10 bond to form C 5 to 10 alkylene chain, R11 represents C1-10 alkyl, C3-10 cycloalkyl, C1-10 haloalkyl, C3-10 halocycloalkyl or C7-12 aralkyl.
In R9 and R10, examples of C1-6 alkyls include methyl, ethyl, n-propyl, isopropyl, n-butyl isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl, isohexyl, and the like. Examples of C3-6 cycloalkyls include cyclopropyl, cyclopentyl, cyclohexyl, and the like. Examples of C1-6 haloalkyls and C3-6 halocycloalkyls include groups wherein at least one hydrogen in the groups exemplified above as C1-6 alkyl or C3-6 cycloalkyl is substituted with halogen such as fluorine, chlorine, bromine, iodine, and the like. Examples of the C5-10 alkylene chains formed by bonding R9 and R10 include pentamethylene, hexamethylene, octamethylene, and the like. Examples of optionally substituted phenyls include phenyl, p-tolyl, and the like.
In R11, examples of C1-10 alkyls include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl, isohexyl, heptyl, octyl, nonyl, decyl, and the like. Examples of C3-10 cycloalkyls include cyclopropyl, cyclopentyl, cyclohexyl, and the like. Examples of C1-10 haloalkyls and C3-10 halocycloalkyls include groups wherein at least one hydrogen in the groups exemplified above as C1-10 alkyl or C3-10 cycloalkyl is substituted with halogen such as fluorine, chlorine, bromine, iodine, and the like. Examples of C7-12 aralkyls include benzyl, phenetyl, phenylpropyl, methylbenzyl, methylphenethyl, ethylbenzyl, and the like.
Examples of the monomers leading to repeating units of the formula (3) include p- or m-1-methoxy-1-methylethoxystyrene, p- or m-1-benzyloxy-l-methylethoxystyrene, p- or m-1-benzyloxyethoxystyrene, p- or m-1-ethoxyethoxystyrene, p- or m-1-methoxyethoxystyrene, p- or m-1-n-butoxyethoxystyrene, p- or m-1-isobutoxyethoxystyrene, p- or m-1-(1,1-dimethylethoxy)-1-methylethoxystyrene, p- or m-1(1,1-dimethylethoxy)ethoxystyrene, p- or m-1-(2-chloroethoxy)ethoxystyrene, p- or m-1-(2-ethylhexyloxy)ethoxystyrene, p- or m-1-ethoxy-1-methylethoxystyrene, p- or m-1-n-propoxyethoxystyrene, p- or m-1-methyl-1-n-propoxyethoxystyrene, p- or m-1-methoxypropoxystyrene, p- or m-1-ethoxypropoxystyrene, p- or m-1-methoxybutoxystyrene, p- or m-1-methoxycyclohexyloxystyrene, p- or m-1-ethoxy-1-cyclohexylmethoxystyrene, p- or m-1-cyclohexyloxyethoxystyrene, p- or m-(α-ethoxybenzyl)oxystyrene, p- or m-[α-ethoxy-(4-methylbenzyl)]oxystyrene, p or m-[α-ethoxy-(4-methoxybenzy)]oxystyrene, p- or m-([α-ethoxy-(4-bromobenzyl)]oxystyrene, p- or m-1-ethoxy-2-methylpropoxystyrene, and the like, and p- or m-hydroxy-α-methylstyrene derivatives having the same substituents as the p- or m-hydroxystyrene derivatives mentioned above, and the like.
Resin (b) may contain other repeating unit(s) in addition to the above repeating unit derived from hydroxystyrene and repeating unit having a group dissociated by the action of an acid. Examples thereof include a repeating unit of the following formula (4), repeating unit of the following formula (5), and the like. Formula (4)
wherein R12 represents hydrogen or methyl, R13 represents hydrogen, C1-4 alkyl, C1-8 alkoxy, C3-8 cycloalkyloxy or a group of the following formula (6),
wherein R14 represents C1-8 alkyl, C6-10 aryl or saturated heterocyclic group, Q represents single bond or oxygen, and 1 denote 0 or natural number. Formula (5)
wherein R15 represents hydrogen, methyl or trifluoromethyl, and R16 represents hydrocarbon group having bonding site at a primary or secondary carbon.
In R13, examples of C1-4 alkyls include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl and sec-butyl. Examples of C1-8 alkoxys include methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, isobutoxy, tert-butoxy, sec-butoxy, n-pentyloxy, isopentyloxy, n-hexyloxy, isohexyloxy, n-heptyloxy, isoheptyloxy, n-octyloxy, tert-octyloxy, and the like. Examples of C3-8 cycloalkyloxys include cyclopropoxy, cyclopentyloxy, cyclohexyloxy, 1-methylcyclopentyloxy, 1-methylcyclohexyloxy, and the like.
In R14, examples of C1-8 alkyls include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, sec-butyl, n-pentyl, isopentyl, tert-pentyl, 1-methylpentyl, n-hexyl, isohexyl, heptyl, octyl, and the like. Examples of C3-8 cycloalkyls include cyclopentyl, 1-methylcyclopentyl, cyclohexyl, 1-methylcyclohexyl, and the like. Examples of saturated heterocyclic groups include tetrahydropyranyl, tetrahydrofuranyl, and the like. Examples of C6-10 aryls include phenyl, 4-methylphenyl, 1-naphtyl, 2-naphtyl, and the like.
Specific examples of the groups of the formula (6) include methoxycarbonyloxy, ethoxycarbonyloxy, isopropoxycarbonyloxy, isobutoxycarbonyloxy, sec-butoxycarbonyloxy, tert-butoxycarbonyloxy, isopentyloxycarbonyloxy, tert-pentyloxycarbonyloxy, 1-methylcyclohexyloxycarbonylmethyloxy, 1-methylcyclopentyloxycarbonylmethyloxy, tetrahydropyranyloxycarbonylmethyloxy, tetrahydrofuranyloxycarbonylmethyloxy, tert-butoxycarbonylmethyloxy, acetyloxy, isobutanoyloxy, pivaloyloxy, isovaleroyloxy, cyclohexylcarbonyloxy, benzoyloxy, 4methylbenzoyloxy, 1-naphthoyloxy, 2-naphthoyloxy, and the like.
Specific examples of the monomers leading to repeating units of the formula (4) includes styrene, p or m-methylstyrene, p- or m-tert-butylstyrene, p- or m-methoxystyrene, p or m-ethoxystyrene, p- or m-isopropoxystyrene, p- or m-tert-butoxystyrene, p- or m-cyclohexyloxystyrene, p- or m-1-methylcyclohexyoxystyrene, p- or m-1-methylcyclopentyloxystyrene, p- or m-tetrahydropyranyloxystyrene, p- or m-tetrahydrofuranyloxystyrene, p- or m-acetyloxystyrene, p- or m-isobutanoyloxystyrene, p- or m-pivaloyloxystyrene, p- or m-cyclohexylcarbonyloxystyrene, p- or m-benzoyloxystyrene, p or m-(4methylbenzoyl)oxystyrene, p- or m-1-naphthoyloxystyrene, p- or m-2-naphthoyloxystyrene, p- or m-methoxycarbonyloxystyrene, p- or m-ethoxycarbonyloxystyrene, p- or m-isopropoxycarbonyloxystyrene, p- or m-isobutoxycarbonyloxystyrene, p- or m-sec-butoxycarbonyloxystyrene, p- or m-tert-butoxycarbonyloxystyrene, p- or m-isopentyloxycarbonyloxystyrene, p- or m-tert-pentyloxycarbonyloxystyrene, 1-methylcyclopentyl p- or m-vinylphenoxyacetate, 1-methylcyclohexyl p- or m-vinylphenoxyacetate, tetrahydropyranyl p- or m-vinylphenoxyacetate, tert-butyl p- or m-vinylphenoxyacetate, and the like.
Specific examples of the monomers leading to repeating units of the formula (5) include methyl acrylate, ethyl acrylate, n-propyl acrylate, cyclohexyl acrylate, isobornyl acrylate, norbornyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, cyclohexyl methacrylate, isobornyl methacrylate, norbornyl methacrylate, and the like.
The repeating unit of the formula (4) and the repeating unit of the formula (5) can optionally be contained in Resin (b) for the purpose of obtaining better side wall shapes by controlling development speed on exposed portions, for the purpose of inhibiting influence by proximity effect and for the purpose of improving mask linearity.
Crude Resin (b) can be produced, for example, i) by living radical polymerization or living anion polymerization of protected hydroxystyrene, deprotection and re-protection, or ii) by radical polymerization of protected hydroxystyrene or protected hydroxystyrene and vinyl monomer, deprotection and re-protection.
In the case of living anion polymerization, protected polyhydroxystyrene can be obtained, for example, by dissolving a polymerization initiator in an organic solvent, adding thereto protected hydroxystyrene such as tert-butoxystyrene, and keeping the mixture under a dehydration condition at −100 to 0° C. preferably at −80 to −20° C.
Examples of polymerization initiators include organic metal compound such as sec-BuLi, n-BuLi, and the like. Examples of organic solvents include benzene, toluene, tetrahydrofuran, n-hexane, and the like.
Then, protected polyhydroxystyrene obtained is dissolved in organic solvent, deprotecting under acidic condition to obtain polyhydroxystyrene Examples of the organic solvents include 2-propanol, dioxane, acetonitrile, toluene, methyl isobutyl ketone, and the like. Each of them can be used alone or in combination with at least one other kind. If solvent is miscible with water, solvent mixture with water can be used. Examples of acids include hydrochloric acid, hydrobromic acid, p-toluenesulfonic acid, and the like.
The polyhydroxystyrene obtained can be re-protected by a protecting agent to obtain crude Resin (b).
In the case of living radical polymerization, protected polyhydroxystyrene can be obtained, for example, by mixing free radical initiator, stable free radical acting agent and protected hydroxystyrene, then bulk polymerizing, solution polymerizing, suspension polymerizing, or emulsion polymerizing the mixture at usually from 100 to 180° C., preferably 110 to 140° C., usually for 5 to 50 hours, though the time depends on the degree of polymerization and the molecular weight.
The free radical initiator may be the one produce free radical by decomposition, and specific examples thereof include peroxides such as benzoyl peroxide, di-tert-butyl peroxide, and the like, azo compounds such as 2,2′-azobisisobutyronitrile, dimethyl 2,2′-azobisisobutyrate, and the like.
The stable free radical acting agent is a compound being stably present in the form of free radical, and examples such radicals include nitroxide radical, hydrazinyl radical, and the like. Specific examples the stable free radical compounds include nitroxide such as 2,2,6,6-tetramethyl-1-piperidinyloxy (Trade Name:TEMPO), 4-amino-2,2,6,6-tetramethyl-1-piperidinyloxy, 4-hydroxy-2,2,6,6-tetramethyl-1-piperidinyloxy, 4oxo-2,2,6,6-tetramethyl-1-piperidinyloxy, phenyl text-butyl nitroxide, di-tert-butyl nitroxide, and the like,; 2,2-di(4tert-octylphenyl)-1-picrylhydrazyl, and the like. Molar ratio of (the stable free radical acting agent)/(the free radical initiator) is preferably from 0.7 to 2, more preferably from 1 to 1.5.
Then, crude Resin (b) can be obtained by leading to poly(hydroxystyrene) by deprotection, and re-protecting polyhydroxystyrene by protecting agent in the same manner as in living anion polymerization.
In the case of radical polymerization, protected hydroxystyrene homopolymer or copolymer can be produced by polymerizing protected hydroxystyrene alone or monomer mixture of protected hydroxystyrene and vinyl monomer in the same manner as the production method for Resin (a) described above.
Then, crude Resin (b) can be obtained by leading to hydroxystyrene homopolymer or copolymer by deprotection, and re-protecting poly(hydroxystyrene) by protecting agent to obtain crude Resin (b) in the same manner as in living anion polymerization.
Resin (1) used for the present resist composition is the one obtained by (A) contacting crude resin (1) with activated carbon at 40 to 90° C., preferably at 40 to 80° C. to obtain active carbon-treated crude resin (1) and contacting the active carbon-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or by
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 90° C., preferably at 40 to 80° C. “resin (1) obtained by (A) contacting crude resin (1) with activated carbon at 40 to 90° C., preferably at 40 to 80° C., to obtain active carbon-treated crude resin (1) and contacting the active carbon-treated resin (1) with at least one member selected from the group consisting of kieselguhr and silica gel, or by
(B) contacting crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel “may hereinafter be referred to as “Treated Resin (1)”. “the active carbon-treated resin (1)” may hereinafter be referred to as “hemi-treated resin (1)”.
Specifically, Treated Resin (1) in the form of solution can be obtained by dissolving crude resin (1) in an organic solvent, contacting the solution with activated carbon at 40 to 90° C., preferably at 40 to 80° C., to obtain hemi-treated resin (1) contained in a solution, and then contacting the hemi-treated resin (1) contained in the solution with at least one member selected from the group consisting of kieselguhr and silica gel.
Examples thereof include a method dissolving crude resin (1) in an organic solvent, contacting the solution with powdered activated carbon, granular activated carbon or the mixture thereof by agitation for a determined period at 40 to 90° C., preferably at 40 to 80° C., cooling the solution with the activated carbon, adding at least one member selected from the group consisting of kieselguhr and silica gel, and contacting the hemi-treated resin (1) with the added member, and filtering off the treated activated carbon and the member. Treated Resin (1) can be obtained by a method dissolving crude resin (1) in an organic solvent, contacting the solution with powdered activated carbon, granular activated carbon or a mixture thereof by passing the solution under pressure or by natural fall through a packed column filled with the activated carbon with maintaining the solution at 40 to 90° C., preferably at 40 to 80° C., cooling the solution, then passing the solution under pressure or by natural fall through a packed column filled with at least one member selected from the group consisting of kieselguhr and silica gel. Treated Resin (1) can be obtained by a method dissolving crude resin (1) in an organic solvent, contacting the solution with powdered activated carbon, granular activated carbon or a mixture thereof by passing the solution under pressure or by natural fall through a filter bed filled with the activated carbon with maintaining the solution at 40 to 90° C., preferably at 40 to 80° C., cooling the solution, then passing the solution under pressure or by natural fall through a filter bed filled with at least one member selected from the group consisting of kieselguhr and silica gel.
Alternatively, Treated Resin (1) in the form of solution can be obtained by dissolving crude resin (1) in an organic solvent, and contacting the solution with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel at 40 to 90° C., preferably 40 to 80° C.
Examples thereof include a method dissolving crude resin (1) in an organic solvent, contacting the solution with powdered activated carbon, granular activated carbon or a mixture thereof and at least one member selected from the group consisting of kieselguhr and silica gel by agitation for a determined period at 40 to 90° C., preferably at 40 to 80° C., and filtering off the treated activated carbon and the member. Treated Resin (1) can also be obtained by a method dissolving crude resin (1) in an organic solvent, contacting the solution with powdered activated carbon, granular activated carbon or a mixture thereof and at least one member selected from the group consisting of kieselguhr and silica gel by passing the solution under pressure or by natural fall through a packed column filled with the activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel with maintaining the solution at 40 to 90° C., preferably at 40 to 80° C. Treated Resin (1) can also be obtained by a method dissolving crude resin (1) in an organic solvent, contacting the solution with powdered activated carbon, granular activated carbon or a mixture thereof and at least one member selected from the group consisting of kieselguhr and silica gel by passing the solution under pressure or by natural fall through a filter bed filled with the activated carbon and the member with maintaining the solution at 40 to 90° C., preferably at 40 to 80° C.
Contact can also be performed by passing crude resin (1) solution under pressure or by natural fall through a cartridge filled with activated carbon or filled with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel in a housing with maintaining the solution at 40 to 90° C., preferably at 40 to 80° C.
Examples of organic solvent used in the contact of crude resin (1) with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel include glycol ether esters such as ethyl Cellosolve acetate, methyl Cellosolve acetate, propylene glycol monomethyl ether acetate, and the like; esters such as ethyl lactate, butyl acetate, amyl acetate, ethyl pyruvate, and the like; ketones such as acetone, methyl isobutyl ketone, 2heptanone, cyclohexanone, and the like; cyclic esters such as y-butyrolactone, and the like. The organic solvent can be used alone or in combination with at least one other kind. It is preferred to use the same organic solvent as the one contained in the resist composition for simple preparation of the composition. The content of crude resin (1) in the solution is usually 1 to 50% by weight, preferably 20 to 30% by weight.
The activated carbon preferably has pore size of 10 to 50 Å average diameter of 10 to 100 μm, and specific surface area of 500 to 2000 m2/g. Examples thereof include “KARUBORAFIN” (trade name) and “SHIRASAGI P” (trade name) made by Takeda Chemical Co., Ltd.
The amount of activated carbon is preferably 0.1 to 50% by weight, more preferably 1 to 20% by weight based on crude resin (1).
The temperature of the contact of crude resin (1) with activated carbon is 40 to 90° C., preferably 40 to 80° C., and more preferably 50 to 70° C. When crude resin (1) dissolved in an organic solvent and powdered activated carbon, granular activated carbon or a mixture thereof is contacted by agitation, the contact period is usually 1 minute to 100 hours, preferably 2 to 6 hours. When crude resin (1) dissolved in an organic solvent and powdered activated carbon, granular activated carbon or a mixture thereof is contacted by passing through packed column or a filter bed, the contact period is usually 1 to 100 hours, preferably 3 to 10 hours.
Examples of kieselguhr include “RADIOLITE” (tradename) and “Celite” (tradename). In the present invention, silica gel includes not only silica gel, but also chemically modified type silica gel, silica containing gel (e.g. silica alumina gel, silica magnesia gel), and the like.
Each of kieselguhr and silica gel can solely be used, or a combination thereof can also be used.
The amount of at least one member selected from the group consisting of kieselguhr and silica gel is usually 0.01 to 100 weight parts, preferably 0.1 to 10 weight parts per one weight part of activated carbon.
The temperature of the contact with at least one member selected from the group consisting of kieselguhr and silica gel is 40 to 90° C., preferably 40 to 80° C., more preferably 50 to 70° C., when the contact is carried out simultaneously with the contact with activated carbon. When the contact is carried out after the contact with activated carbon, the temperature of the contact with at least one member selected from the group consisting of kieselguhr and silica gel is usually 0 to 100° C. and preferably 10 to 40° C. In that case, at first, the contact with activated carbon is carried out at 40 to 90° C., preferably 40 to 80° C., the treated activated carbon is eliminated by filtration or it is contained as it is, then, the solution is cooled and the contact with at least one member selected from the group consisting of kieselguhr and silica gel is carried out preferably at 10 to 40° C.
The material of the filter used for eliminating the treated activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel may be the one has proper resisting property against the solvent used. Examples thereof include PTFE (polytetrafluoroethylene), polyethylene, polypropylene, and the like. Filtrating method may be natural filtration, pressure filtration, filtration under reduced pressure, centrifugal filtration, or the like.
Thus obtained Treated Resin (1) solution can be used as a component for the chemically amplified resist composition of the present composition. Treated Resin (1) solution can also be used as it is for flattening film, anti reflection film, protection film of photoresist composition, and the like.
Though it can be suitably determined according to the purpose of the solution, the content of Treated Resin (1) in the solution is usually 1 to 50% by weight preferably 20 to 30% by weight. The content of Treated Resin (1) solution is basically the same as the content of the crude resin (1) solution before the contact with activated carbon and at least one member selected from the group consisting of kieselguhr and silica gel. The content of Treated Resin (1) can be adjusted by adding solvent or by distillation after obtaining Treated Resin (1) solution from crude resin (1) solution.
The chemically amplified resist composition comprises Treated Resin (1), an acid generator and a solvent.
The acid generator is that which is decomposed to generate an acid by allowing radioactive ray such as light and electron beam to act on the acid generator itself or a resist composition containing the acid generator. The acid generated from the acid generator acts on resin (1), to dissociate acid labile group present in resin (1). Such acid generators include, for example, onium salt compounds, organic halogen compounds, sulfone compounds, sulfonate compounds and the like.
Specific examples of the acid generators include the following compounds. Diphenyliodonium trifluoromethanesulfonate, 4-methoxyphenylphenyliodinium hexafluoroantimonate, 4methoxyphenylphenyliodinium trifluoromethanesulfonate, bis(4-tert-butylphenyl)iodonium tetrafluoroborate, bis(4-tert-butylphenyl)iodonium perfluorobutanesulfonate, bis(4-tert-butylphenyl)iodonium hexafluorophosphate, bis(4-tert-butylphenyl)iodonium hexafluoroantimonate, bis(4-tert-butylphenyl)iodonium trifluoromethanesulfonate, bis(4-tert-butylphenyl)iodonium camphorsulfonate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium trifluoromethanesulfonate, triphenylsulfonium perfluorobutanesulfonate, triphenylsulfonium perfluorooctanesulfonate, tri(4-(methylphenyl)sulfonium trifluoromethanesulfonate, tri(4-(methylphenyl)sulfonium perfluorobutanesulfonate, tri(4-(methylphenyl)sulfonium perfluorooctanesulfonate, 4-methylphenyldiphenylsulfonium perfluorobutanesulfonate, 4-methylphenyldiphenylsulfonium hexafluoroantimonate, 4-methylphenyldiphenylsulfonium trifluoromethanesulfonate, 4-methoxyphenyldiphenylsulfonium hexafluoroantimonate, 4-methoxyphenyldiphenylsulfonium trifluoromethanesulfonate, p-tolyldiphenylsulfonium trifluoromethanesulfonate, p-tolyldiphenylsulfonium perfluorobutanesulfonate, p-tolyldiphenylsulfonium perfluorooctanesulfonate, 2,4,6-trimethylphenyldiphenylsulfonium trifluoromethanesulfonate, 4-tert-butylphenyldiphenylsulfonium trifluoromethanesulfonate, 4-phenylthiophenyldiphenylsulfonium hexafluorophosphate, 4-phenylthiophenyldiphenylsulfonium hexafluoroantimonate, 1-(2-naphtholylmethyl)thiolanium hexafluoroantimonate, 1-(2-naphtholylmethyl)thiolanium trifluoromethanesulfonate, 4-hydroxy-1-naphthyldimethylsulfonium hexafluoroantimonate, 4hydroxy-1-naphthyldimethylsulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium perfluorobutanesulfonate, cyclohexylmethyl(2-oxycyclohexyl)sulfonium perfluorobutanesulfonate, 2-methyl4,6-bis(trichloromethyl)-1,3,5-triazine, 2,4,6-tris(trichloromethyl)-1,3,5-triazine, 2-phenyl-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(4-chlorophenyl)-4,-bis(trichloromethyl)-1,3,5-triazine, 2-(4methoxyphenyl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(4-methoxy-1-naphthyl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(benzo[d][1,3]dioxolan-5-yl)-4,-bis(trichloromeythyl)-1,3,5-triazine, 2-(4-methoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(3,4,5-trimethoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(3,4-dimethoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(2,4-dimethoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(2-methoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(4-butoxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 2-(4pentyloxystyryl)-4,6-bis(trichloromethyl)-1,3,5-triazine, 1-benzoyl-1-phenylmethyl p-toluenesulfonate (generally called “benzoin tosylate”), 2-benzoyl-2-hydroxy-2-phenylethyl p-toluenesulfonate (generally called α-methylolbenzoin tosylate), 1,2,3-benzen-tri-yl tris(methanesulfonate), 2,6-dinitrobenzyl p-toluenesulfonate, 2-nitrobenzyl p-toluenesulfonate, 4-nitrobenzyl p-toluenesulfonate, diphenyl disulfone, di-p-tolyl disulfone, bis(phenylsulfonyl)diazomethane, bis(4-chlorophenylsulfonyl)diazomethane, bis(p-tolylsulfonyl)diazomethane, bis(4-tert-butylphenylsulfonyl)diazomethane, bis(2,4-xylylsulfonyl)diazomethane, bis(cyclohexylsulfonyl)diazomethane, (benzoyl)(phenylsulfonyl)diazomethane, N-(phenylsulfonyloxy)succinimide, N-(tifluoromethylsulfonyloxy)succinimide, N-(tifluoromethylsulfonyloxy)phthalimide, N-(trifluoromethylsulfonyloxy)-5-norbornene-2,3-dicarboxyimide, N-(trifluoromethylsulfonyloxy)naphthalimide, N-10-camphorsulfonyloxy)naphthalimide, (5-propylsulfonyloxyimino-5H-thiophen-2-ylidene)42-methylphenyl)acetonitrile, (5(4methylphenyl)sulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylphenyl)aceton itrile, (5-butylsulfonyloxyimino-5H-thiophen-2-ylidene)-(2,methylphenyl)acetonitrile, (5-n-octylsulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylphenyl)acetonitrile, (5-(2,4,6-trimethylphenyl)sulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylphenyl) acetonitrile, (5-(2,4,6-triisopropylphenyl)sulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylpheny 1)acetonitrile, (5-(4-dodecylphenyl)sulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylphenyl)aceto nitrile, (5-(2-naphtyl)sulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylphenyl)acetonitrile, (5-benzylsulfonyloxyimino-5H-thiophen-2-ylidene)-(2-methylphenyl)acetonitrile, (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(methanesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(benzenesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(p-toluenesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(camphorsulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(triisopropylbenzenesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(pentafluorobenzenesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(trifluoromethanesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(perfluorobutanesulfonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(perfluorooctanesulfonate), (oxydi4,1-phenylene)bisdiphenylsulfonium bis{trifluoro-N-((perfluoromethyl)sulfonyl]-1-methanesulfonamidate}, (oxydi-4,1-phenylene)bisdiphenylsulfonium bis{perfluoro-N-((perfluoromethyl)sulfonyl]-1-ethanesulfonamidate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis{perfluoro-N-[(perfluorobutyl)sulfonyl]-1-butanesulfonamidate}, (oxydi-4,1-phenylene)bisdiphenylsulfonium bis{trifluoro-N-[(perfluorobutyl)sulfonyl]-1-methanesulfonamidate}, (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(tetrafluoroborate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(hexafluoroarsenate), (oxydi-4,l-phenylene)bisdiphenylsulfonium bis(hexafluoroantimonate), (oxydi-4,1-phenylene)bisdiphenylsulfonium bis(hexafluorophosphate), (oxydi-4,1-phenylene)bisdi(4tert-butylphenyl)sulfonium bis(trifluoromethanesulfonate), (oxydi-4,1-phenylene)bisdi(4-tert-butylphenyl)sulfonium bis(perfluorobutanesulfonate), (oxydi-4,1-phenylene)bisdi(p-tolyl)sulfonium bis(trifluoromethanesulfonate), triphenylsulfonium (adamantan-1-ylmethyl)oxycarbonyldifluoromethanesulfonate, and the like. The solvent used in the present composition may be the one which sufficiently dissolve each ingredients, has an adequate drying rate, and gives a uniform and smooth coat after evaporation of the solvent. Hence, solvents generally used in the an can be used.
Examples thereof include glycol ether esters such as ethyl Cellosolve acetate, methyl Cellosolve acetate, propylene glycol monomethyl ether acetate, and the like; esters such as ethyl lactate, butyl acetate, amyl acetate and ethyl pyruvate, and the like; ketones such as acetone, methyl isobutyl ketone, 2-heptanone, cyclohexanone; and the like; cyclic esters such as γ-butyrolactone, and the like. These solvents can be used each alone or in combination of two or more.
In the present composition, performance deterioration caused by inactivation of acid which occurs due to post exposure delay can be diminished by adding basic compounds, particularly, basic nitrogen-containing organic compounds, for example, amines as a quencher.
Specific examples of such basic nitrogen-containing organic compounds include the ones represented by the following formulae:
Wherein R21 and R22 represent each independently hydrogen, alkyl, cycloalkyl or aryl. The alkyl preferably has about 1 to 6 carbon atoms, the cycloalkyl preferably has about 5 to 10 carbon atoms, and the aryl preferably has about 6 to 10 carbon atoms. Furthermore, at least one hydrogen on the alkyl, cycloalkyl or aryl may each independently be substituted by hydroxyl, amino, or alkoxy having 1 to 6 carbon atoms. At least one hydrogen on the amino may each independently be substituted by alkyl having 1 to 4 carbon atoms.
R23, R24 and R25 each independently represent hydrogen, alkyl, cycloalkyl, aryl or alkoxy. The alkyl preferably has about 1 to 6 carbon atoms, the cycloalkyl preferably has about 5 to 10 carbon atoms, the aryl preferably has about 6 to 10 carbon atoms, and the alkoxy preferably has about 1 to 6 carbon atoms. Furthermore, at least one hydrogen on the alkyl, cycloalkyl, aryl or alkoxy may each independently be substituted by hydroxyl, amino, or alkoxy having 1 to 6 carbon atoms. At least one hydrogen on the amino may be substituted by alkyl having 1 to 4 carbon atoms.
R26 represents alkyl or cycloalkyl. The alkyl preferably has about 1 to 6 carbon atoms, and the cycloalkyl preferably has about 5 to 10 carbon atoms. Furthermore, at least one hydrogen on the alkyl or cycloalkyl may each independently be substituted by hydroxyl, amino, or alkoxy having 1 to 6 carbon atoms. At least one hydrogen on the amino may be substituted by alkyl having 1 to 4 carbon atoms. R27, R28, R29 and R30 each independently represent alkyl, cycloalkyl or aryl. The alkyl preferably has about 1 to 6 carbon atoms, the cycloalkyl preferably has about 5 to 10 carbon atoms, and the aryl preferably has about 6 to 10 carbon atoms. Furthermore, at least one hydrogen on the alkyl, cycloalkyl or aryl may each independently be substituted by hydroxyl, amino, or alkoxy having 1 to 6 carbon atoms. At least one hydrogen on the amino may each independently be substituted by alkyl having 1 to 4 carbon atoms.
A represents alkylene, carbonyl, imino, sulfide or disulfide, The alkylene preferably has about 2 to 6 carbon atoms.
Moreover, among R21-R30, in regard to those which can be straight-chained or branched, either of these may be permitted.
Examples of such compounds include hexylamine, heptylamine, octylamine, nonylamine, decylamine, aniline, 2-, 3- or 4-methylaniline, 4-nitroaniline, 1- or 2-naphtylamine, ethylenediamine, tetramethylenediamine, hexamethylenediamine, 4,4′-diamino-1,2-diphenylethane, 4,4′-diamino-3,3′-dimethyldiphenylmethane, 4,4′-diamino-3,3′-diethyldiphenylmethane, dibutylamine, dipentylamine, dihexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, N-methylaniline, piperidine, diphenylamine, triethylamine, trimethylamine, tripropylamine, tributylamine, tripentylamine, trihexylamine, trihexylamine, triheptylamine, trioctylamine, trinonylamine, tridecylamine, methyldibutylamine, methyldipentylamine, methyldihexylamine, methyldicyclohexylamine, methyldiheptylamine, methyldioctylamine, methyldinonylamine, methyldidecylamine, ethyldibutylamine, ethyldipentylamine, ethyldihexylamine, ethydiheptylamine, ethyldioctylamine, ethyldinonylamine, ethyldidecylamine, dicyclohexylmethylamine, tris[2-(2-methoxyethoxy)ethyl]amine, triisopropanolamine, N,N-dimethylaniline, 2,6isopropylanline, imidazole, pyridine, 4-methylpyridine, 4-methyimidazole, bipyridine, 2,2′-dipyridylamine, di-2-pyridyl ketone, 1,2-di(2-pyridyl)ethane, 1,2-di(4-pyridyl)ethane, 1,3-di(4-pyridyl)propane, 1,2-bis(2-pyridyl)ethylene, 1,2-bis(4-pyridyl)ethylene, 1,2-bis(4-pyridyloxy)ethane, 4,4′-dipyridyl sulfide, 4,4′-dipyridyl disulfide, 1,2-bis(4-pyridyl)ethylene, 2,2′-dipicolylamine, 3,3′-dipicolylamine, tetramethylammonium hydroxide, tetraisopropylammonium hydroxide, tetrabutylammonium hydroxide, tetra-n-hexylammonium hydroxide, tetra-n-octylammonium hydroxide, phenyltrimethylammonium hydroxide, 3-trifluoromethylphenyltrimethylammonium hydroxide, (2-hydroxyethyl)trimethylammonium hydroxide (so-called “choline”), and the like.
Furthermore, hindered amine compounds having piperidine skeleton as disclosed in JP-A-H11-52575 can be used as quencher.
It is preferable that the present composition contains Treated Resin (1) in an amount of about 80 to 99.9% by weight and the acid generator in an amount of 0.1 to 20% by weight based on the total weight of solid components of the present composition. The “total weight of solid components of resist composition” means the weight subtracting the weight of organic solvent from the weight of the resist composition.
When basic compound is used as a quencher, it is preferable that the basic compound is contained in an amount of about 0.01 to 1% by weight based on the total weight of solid components of the present composition. In that case, Treated Resin (1) is preferably contained in an amount of about 79 to 99.89% by weight.
The present composition can contain, if necessary, various additives in small amount such as a sensitizer, solution suppressing agent, other resins, surfactant, stabilizer, dye and the like, as long as the effect of the present invention is not prevented.
The present resist composition contains much fewer solvent-insoluble minute particles and has excellent filtration property through finer filter. The present resist composition usually has clogging degree of 0.9 or more when the composition is measured and calculated by the following definition.
And also Treated Resin (1) solution contains much fewer solvent-insoluble minute particles and has excellent filtration property through finer filter and usually has clogging degree of 0.9 or more when the solution is measured and calculated by the following definition.
Definition of Clogging Degree of Resist Composition
The following explanation is performed by using resist composition. When the sample is resin solution such as Treated Resin (1) solution, resist composition can be substituted by resin solution in the explanation.
At 23° C., resist composition is poured into a filtration equipment in which a round and track-etch membrane filter (diameter: 47 mm, pore size: 0.05 μm, thickness: 6 μm, pore density: 6×108 pores/cm2) is set to a holder having volume of 300 ml, then pressure filtration is started at a pressure of 100 kPa. The filtrate is collected in a receiver on a balance (weighing machine), and weight change of the filtrate is measured every one minute. Filtration time and accumulated weight of filtrate discharged are measured and linear velocity is calculated by dividing the weight of filtrate discharged per one minute by effective filter area. The linear velocity is a value showing filtration velocity (g/(cm2Min.)) per 1 cm2 of filter. Maximum value of linear velocity reached in 10 minutes after starting the filtration is defined as V1 (the linear velocity at initial standard point). The linear velocity at the point the accumulated weight of filtrate discharged reaches to 15 g converted to the weight of solid components of the resist composition is measured and calculated in the same maimer and is defined as V2. Clogging Degree is a value calculated by dividing V2 by V1.
The track-etch membrane filter is a filter whose pores pass straight through the membrane from front surface to back surface. The membrane filter is made of polycarbonate.
The membrane filter for determining Clogging Degree is available and product name thereof is Nuclepore 0.05 μm filter (track-etch membrane filter, 47 mm diameter, made of polycarbonate, Importer; Nomura Micro Science Co., Ltd., Producer; Whatman Co., Ltd.).
The present resist composition thus obtained can be optionally preliminary filtrated before applying for resist. The preliminary filtration can be performed by the known filtration method and with known filter. Examples of the materials for filter include aliphatic polyamide, aromatic polyamide, polyethersulfone, polysulfone, polyacrylonitrile, polyimide, polyvinyl alcohol, polyvinylidene fluoride, cellulose, cellulose acetate, polyether, polytetrafluoroethylene, polycarbonate, polypropylene, polyethylene, polystyrene, polyester, ceramics, and the like. Among them, polyethylene, and polytetrafluoroethylene are preferred because of their solvent resisting property.
Treated Resin (1) solution can also be optionally filtrated when it is used as it is for other purposes than resist composition, such as over coating material, antireflective coating agent, protection film of photoresist composition, and the like. The filtration can be performed in the same manner as in the preliminary filtration of resist composition as described above.
The present composition is to be applied onto a substrate such as a silicon wafer by a conventional process such as spin coating.
A resist film applied onto the substrate and then dried is subjected to exposure for patterning, then heat-treated for facilitating a deblocking reaction, and thereafter developed with an alkali developer. The alkali developer used here may be any one of various alkali aqueous solutions used in the art, and generally, an aqueous solution of tetramethylammonium hydroxide or (2-hydroxyethyl)trimethylammonium hydroxide (commonly known as “choline”) is often used.
The present invention will be described more specifically by way of examples, which are not construed to limit the scope of the present invention. The “%” and “part(s)” used to represent the content of any component and the amount of any material used in the following examples are on a weight basis unless otherwise specifically noted. The weight-average molecular weight of any material used in the following examples is a value found by gel permeation chromatography using styrene as a standard reference material.
Resin Synthesis Example 1 (Synthesis of Resin A)
Into a four necked flask with replacing air by nitrogen, 2-ethyl-2-adamantyl methacrylate, 5-methacryloyloxy-2,6-norbornanecarbolactone and α-methacryloyloxy-γ-butyrolactone were charged at a molar ratio of 2:1:1 ( 11.1 parts: 5.0 parts: 3.8 parts), and 50 parts of 1,4-dioxane was added thereto to prepare a solution. To the solution was added 0.3 part of azobisisobutyronitrile as an initiator, and the mixture was heated at 85° C. for about 5 hours. Then, the reaction solution was poured into large amount of n-heptane to cause precipitation, and this operation was repeated three times, and then, the precipitate was dried. As a result, copolymer having a weight-average molecular weight of about 9,100 was obtained. This is called crude resin A
20 Parts of the crude resin A obtained in Synthetic Example 1 was dissolved in 80 parts of propylene glycol monomethyl ether acetate. To the solution was added 2 parts of activated carbon (Trade Name: CARBORAFIN, pore size: 30 Å, specific surface area: 1500 m2/g ) and the mixture was stirred at 60° C. for 3 hours. Then, the treated mixture was cooled to 30° C., to the cooled mixture, 4 parts of powdered kieselguhr (tradename: RADIOLITE, made by Showa Chemical Industry Co., Ltd., average diameter: 16 μm ) was added and the added mixture was stirred at 30° C. for 1 hour. After the stirring, the stirred mixture was filtrated by pressure filtration using 5 μm filter made of polytetrafluoroethylene to obtain treated resin A solution.
10 Parts of treated resin A (converted to total weight of solid components), 0.40 part of (4methylphenyl)diphenylsulfonium trifluoromethanesulfonate, and 0.03 part of 2,6-diisopropylaniline were dissolved in a mixed solvent of 66.5 parts of propylene glycol monomethyl ether acetate (including a portion from resin solutions), 3.5 parts of γ-butyrolactone to obtain resist composition. The composition was filtrated by 0.2 μm filter made of PTFE (polytetrafluoroethylene) and 0.1 mm filter made of UPE (Ultra High Molecular Weight Polyethylene) both produced by Nihon Mykrolis K..K to obtain a preliminary filtered resist composition.
The preliminary filtered resist composition above was evaluated by the following items. The results are shown in Table 1.
Measurement of Clogging Degree
At 23° C., the preliminary filtered resist composition is poured into a filtration equipment in which a round and track-etch membrane filter (imported by Nomura micro Science Co., Ltd., diameter: 47 mm, average pore size: 0.05 μm, thickness: 6 μm, pore density: 6×108 pores/cm2, all of which are based on the catalogue of Nomura micro Science Co., Ltd.) made of polycarbonate is set to a holder having volume of 100 ml made of stainless steel (produced by Nihon Mykrolis K.K.), then pressure filtration is started at a pressure of 100 kPa. The filtrate is collected on a balance (weighing machine), and weight change of the filtrate is measured every one minute. Filtration time and accumulated weight of filtrate discharged is measured and linear velocity is calculated by dividing the weight of filtrate discharged per one minute by effective filter area of 10.8 cm2. Maximum value of linear velocity reached in 10 minutes after starting the filtration is defied as VI (the linear velocity at initial standard point), The linear velocity at the point the accumulated weight of filtrate discharged reaches to 100 g (15 g converted to total weight of solid components) is measured and calculated in the same manner and is defined as V2. Clogging Degree is a value calculated by dividing V2 by V1.
Number of Minute Particles
Using an automatic minute particle analyzer (KS41 Type, produced by Lion Co., Ltd.), number of particles having diameter of 0.2 μm or more in the filtrate immediately after the filtration by the track-etch membrane filter above was measured. After keeping the filtrate at 40° C. for 10 days, the number of particles having diameter of 0.2 μm or more in the kept nitrate in the same manner as above.
#1Increased Number of minute particles >0.2 μm per 1 ml solution is 1000 or less.
#2Increased Number of minute particles >0.2 μm per 1 ml solution is more than 1000.
10 Parts of the crude resin A obtained in Synthetic Example 1 is dissolved in a solvent mixture of 665 parts of propylene glycol monomethyl ether acetate and 3.5 parts of γ-butyrolactone. To the solution is added 2 parts of activated carbon (Trade Name: CARBORAFIN, pore size: 30 Å, specific surface area: 1500 m2/g ) and the mixture is stirred at 60° C. for 3 hours. Then, the treated mixture is cooled to 30° C., to the cooled mixture, 4 parts of powdered kieselguhr (tradename: RADIOLITE, made by Showa Chemical Industry Co., Ltd., average diameter: 16 μm ) is added and the added mixture is stirred at 30° C. for 1 hour. After the stirring, the stirred mixture is filtrated by pressure filtration using 5 μm filter made of PTFE (polytetrafluoroethylene) to obtain treated resin A′ solution.
The treated resin A′ solution is filtrated by 0.2 μm filter made of PTFE and 0.1 μm filter made of UPE (Ultra High Molecular Weight Polyethylene) both produced by Nihon Mykrolis K.K. to obtain a preliminary filtered resin A′ solution.
The preliminary filtered resin A′ solution is evaluated by the measurement of clogging degree in the same manner as defined above except that resist composition is substituted by the preliminary filtered resin A solution. The preliminary filtered resin A′ solution will have good filtration characteristics as clogging degree of more than 0.9 and film formed from the solution will have less detects thereon.
The present resist composition has excellent long term preservation stability with maintaining less defects on resist film formed from the composition, in addition to good filtration characteristics.
The film formed from the present resin solution produces less defects on the film and the present resin solution has good filtration characteristics.