The present invention relates to a conductive adhesive used for a thermal conductive medium or electrical contacts of electronic elements, a package of an electronic element using the conductive adhesive, and a method of packaging. More specifically, the present invention relates to a conductive adhesive that has excellent adhesion strength and stress relaxation property and that can be produced at a low cost, a package of an electronic element using the same and a method of packaging.
Due to a recent trend of environmental consciousness, controls on lead included in solder alloys will be imposed in the field of electronic packaging, and thus, establishment of a lead-free packaging a technique, i.e., a technique to join electronic elements with a lead-free material is an urgent necessity. The lead-free packaging technique includes packaging using mainly a lead-free solder or a lead-free conductive adhesive. Conductive adhesives have been noted particularly in the technique since they are expected to provide merits such as joint flexibility, lower packaging temperatures, no need of organic solvents, and no need of washes.
A conventional conductive adhesive is based on, e.g., an epoxy resin-based binder resin in which a conductive filler of a metal powder such as silver is dispersed. When an electronic element and a substrate electrode are connected through the conductive adhesive, the binder resin contacts the conductive filler with other conductive filler, the element electrode, and with the substrate electrode so as to provide electrical connection while the electronic element and the substrate electrode are adhered for mechanical connection. Since the electronic element and the circuit substrate are connected at the joints with a resin component, it deforms flexibly corresponding to deformation caused by heat and external force. Therefore, it has less cracks when compared to solder connection with an alloy. Moreover, a typical conductive adhesive has a joint temperature as low as 150° C. while the joint temperature of an alloy is about 240° C., electronic elements with reduced heat resistance can be used. Furthermore, the energy requirement for the production can be reduced.
Therefore, a conductive adhesive is expected as an alternative to solder, since it has excellent performance over solder connection.
However, a conventional conductive adhesive as a replacement for solder cannot provide a connection strength corresponding to that of solder. Another problem is that such an adhesive is more expensive when compared to solder as package materials of electronic elements.
The following description is on connection strength. A conductive adhesive adheres to an electronic element and to a substrate electrode since, for example, an epoxy-based binder resin adheres to the element and the substrate electrode. Among resin materials, the epoxy-based binder resin has an especially strong adhesion with metals, and the resin has excellent mechanical strength after hardening. Therefore, it has been used for adhesives for many elements. However, unlike solder, since the joint is not provided by alloy, the adhesives cannot provide the connection strength of solder against external force applied to the connected part due to bending of the substrate and impacts. The main factors are as follows.
The epoxy resin as a binder component for a conventional conductive adhesive has strong adherence to metal of a substrate electrode. However, it has a high elastic modulus and less flexibility. When a substrate comprising such a resin is subjected to bending deformation, stress is concentrated at the joint interface between the electronic element and the conductive resin. When the stress exceeds the strength of connection between the electronic element and the conductive resin, peeling may occur at the interface. Such an adhesive resin cannot correspond to deformation caused by bending, vibration and impact generated in the substrate at the connected part of the electronic element and the circuit substrate.
Concerning the flexibility of conductive resin, JP-A-3-21868 for utility model suggests an elastic conductive adhesive containing an elastic adhesive as a binder resin component.
This conductive resin described in JP-A-3-21868 has more improved flexibility when compared to the other examples of epoxy resins. However, it provides less conductivity when compared to an epoxy resin that has conductance provided by contraction of the hardened resin. And the conductive filler is of a spherical shape, scale shape, or a mixture thereof. Therefore, it is difficult to decrease the resistance of the conductive resin to the level of the resistance of an epoxy-based resin.
In a conventional technique, a typical conductive adhesive contains a conductive filler of about 85 vol. %. A conductive filler such as silver has a specific weight of about 10 while the binder resin has a specific weight of about 1.1. This substantially decreases the mechanical connection or the connection strength at the connected part to a half, i.e., the area that the binder resin contacts with the element electrode and the substrate electrode is halved. As a result, the connection strength of the adhesive containing filler will be lowered when compared to a case using a binder resin alone.
As mentioned above, a conventional conductive adhesive has a high elastic modulus that leads to problems in adhesion strength with either an electronic element or with a circuit substrate, and also in connection reliability. Also, the conductive adhesive has problems concerning joint interface with the electronic element and with the circuit substrate.
A conventional conductive resin contains a conductive filler such as silver powder in as much as about 85 vol. %. Since the conductive filler accounts for about 70% or 80% of the cost for the conductive adhesive, it is substantially impossible to reduce the cost.
Conventional conductive adhesives have a merit from the aspect of flexibility over solder but the connection strength with respect to dynamic deformations such as substrate bending, vibration, and impact is insufficient. Moreover, the conductive adhesive raises the manufacturing cost. These demerits inhibit the conductive adhesives from replacing the commonly used solder for connection.
For solving the above-mentioned problems of conventional techniques, the present invention provides an inexpensive conductive adhesive improved to decrease cracks, a package of an electronic element using the same, and a method of packaging.
A conductive adhesive of the present invention comprises a conductive filler and a binder resin as main components, in which a content of the conductive filler is from 20 wt % to 70 wt %. Here, a “main component” denotes a component contained in a range from 80 wt % to 100 wt % of the material.
A package of an electronic element according to the present invention comprises a circuit substrate electrode and an electronic element electrode that are electrically connected to each other through a conductive adhesive containing a conductive filler and a binder resin, wherein an average content of the conductive filler is in a range from 20 wt % to 70 wt %. At a portion where the adhesive is in a gap between the electrodes, the content of the conductive filler is higher than the average content while the adhesive squeezed outside the gap contains less conductive filler than the average content.
The present invention provides a method of electrically connecting a circuit substrate electrode and an electronic element electrode through a conductive adhesive containing a conductive filler and a binder resin, wherein an average content of the conductive filler is in a range from 20 wt % to 70 wt %. The process comprises steps of: applying the adhesive to a gap between the circuit substrate electrode and the electronic element electrode; applying pressure ranging from 0.01 MPa to 50 MPa to the circuit substrate electrode and the electronic element electrode; squeezing the adhesive containing less conductive filler so as to make the content of the conductive filler in the adhesive present in the gap between the electrodes higher than the average content.
In the present invention, a content of a conductive filler is set to be lower than that of a conventional conductive adhesive. Thereby, adhesive components at the interfaces for connection to elements and circuit substrate increase, and the connection strength at the interfaces is improved. As a result, adhesion strength is improved further at the connection interface between the electronic elements and the conductive adhesive and also between the circuit substrate electrode and the conductive adhesive. This improves the connection reliability of the electronic elements.
It is preferable for the conductive adhesive that the conductive filler comprises a metal filler having protrusions.
It is also preferable that the conductive filler having protrusions is a dendrite filler. Here, “dendrite” denotes a figure like branches growing from a trunk.
In a preferred embodiment, a conductive filler is a mixture of 30-99 wt % of a filler having protrusions and 1-70 wt % of at least one kind of filler having a shape selected from the group consisting of scales, Rakes and particles. The conductive filler can be a mixture of a filler of either scale-shape or substantial particles, and a filler of a dendrite shape. It is preferable that the content of the conductive fuller having a dendrite shape is at least 30 wt %.
It is preferable for the conductive adhesive that the content of the conductive filler is in a range from 30 wt % to 50 wt %.
It is preferable that the conductive filler is at least one metal selected from the group consisting of copper, silver, gold, platinum, palladium, nickel, stainless steel and an alloy thereof.
The conductive filler can be prepared by coating a metal with at least one substance selected from silver, gold, palladium, silica and resin.
It is preferable that the conductive filler has an average particle diameter ranging from 1 μm to 100 μm. Here, ‘average particle diameter’ denotes the apparent outer dimension of a filler particle including a space for the case of the above-mentioned dendrite, scale and particle shaped fillers. For the dendrite filler shown in
It is preferable that the dendrite filler is a copper powder having an oxygen concentration of at most 0.5 atomic %. It is preferable that the copper filler is coated with a fatty acid in a range of 0.01-5.0 wt % to the weight of the copper filler, and the fatty acid has a melting point of at most 200° C. and is solid at room temperature. An example of fatty acids having a melting point of at most 200° C. and being solid at room temperature is at least one selected from the group consisting of stearic acid, myristic acid, citric acid, glutaric acid, palmitic acid and maleic acid. A method of producing the above-mentioned dendrite filler is proposed in JP-A-11-264001, which is applicable for the present invention. Another example is a copper dendrite filler supplied as “CUE07PB” (trade name) by Kojundo Chemical Laboratory Co., Ltd.
It is preferred in the conductive adhesive that the binder resin is an elastic adhesive resin. Such an elastic adhesive resin is called in general an elastic adhesive. Since the elastic resin has a smaller elastic modulus when compared to a conventional epoxy resin binder, it is flexible and thus, it can absorb force applied to respective connected parts such as stress caused by a difference of coefficient of thermal expansion between an electronic element and a circuit substrate, stress caused by deformation such as bending of the circuit substrate, and stress caused by a drop impact. A typical epoxy resin contained in a binder resin of a conventional conductive adhesive has a comparatively large elastic modulus of about 1×104 MPa in a temperature range from −50° C. to 50° C., and the elastic modulus is lowered sharply to about 1 MPa in a temperature range from 80° C. to 130° C. On the other hand, an elastic modulus of the elastic adhesive used in the present invention is stable and as small as about 10 MPa in a temperature range from −50° C. to 130° C. A preferred example of the elastic adhesive is a thermosetting resin adhesive comprising a denatured silicon resin matrix in which epoxy resin is dispersed (e.g., “PM-165” (trade name) supplied by Cemedyne Co., Ltd.). This kind of adhesive has excellent adhesion strength, deformation absorbency, waterproof reliability, high temperature reliability and so on. In addition to the thermosetting resin, room temperature setting resin, radiation setting resin, thermoplastic resin or the like can be used.
A conductive filler according to the present invention can be provided at a low cost, since it reduces the amount of contained conductive filler that may raise the cost.
It is preferable for a package of electronic elements according to the present invention that an adhesive applied to a gap between the circuit substrate electrode and the electronic element electrode contains a conductive filler in a range from 75 wt % to 95 wt %. This indicates that the content of the conductive filler is higher in the gap between the circuit substrate electrode and the electronic element electrode. The reason follows. Since the circuit substrate electrode and the electronic element electrode are applied with pressure ranging from 0.01 MPa to 50 MPa, the conductive adhesive is squeezed out from the gap between the electrodes. As a result, more conductive filler remains in the gap and thus, the content of the filler in the gap is raised. Particularly, metal filler having dendrite protrusions will be prevented from moving since the filler components are entangled with each other. Such a filler tends to remain in the gap while more resin components will be squeezed out.
Moreover, the metal filler having protrusions can scratch the surfaces of the circuit substrate electrode and of the electronic element electrode partially in order to connect the electrodes by application of pressure ranging from 0.01 MPa to 50 MPa to both the electrodes. Since a typical electronic element electrode comprises solder, tin, or a tin alloy while a typical substrate electrode contains copper, the metal filler scratches oxide coatings formed on the electrode surfaces. This provides certain conductance and increases a contact area between the metal filler and the surfaces of the electrodes.
Metal filler having dendrite protrusions will be prevented from moving since the filler components are entangled with each other. As a result, packaging can be carried out when spacing between the element electrode and the substrate electrode is at least 1.1 times a minimum dimension (D min) of a smallest conductive filler contained in the conductive resin and at most 20 times a maximum dimension (D max) of a biggest conductive filler contained in the conductive resin.
As mentioned above, the conductive adhesive of the present invention contains the dendrite conductive filler. In a comparison with a conductive filler used for conventional conductive adhesives, each dendrite filler has a complicated surface shape, and this increases contact points to contact with other filler, the electronic element electrode or with the circuit substrate electrode. As a result, connection resistance of the electronic element can be reduced to equal to or less than that of the conventional conductive adhesive. A preferred example of the dendrite conductive filler is an electrolytic copper powder.
The dendrite conductive filler can be mixed with either a scaly filler or a conductive filler shaped to be particles. Alternatively, the dendrite conductive filler can be mixed with the scaly filler and the conductive filler of a particle shape.
The thus-shaped conductive filler can be used preferably for providing a flexible package of an electronic element since the connection resistance of the electronic element is not inferior to a case of solder connection.
Conductive filler containing dendrite fillers has stable connection resistance against bending of the substrate since the conductive fillers entangle with each other.
The use of the conductive adhesive of the present invention is not limited to a replacement of solder but it can be used for a conductive filler to be filled in inner-via-holes formed in a circuit substrate in the thickness direction.
The present invention will be explained further by referring to the attached drawings.
(First Embodiment)
(Second Embodiment)
This embodiment is characterized in that the electronic element 1 is pressed while interposing the conductive adhesive 3 between the electronic element 1 and the circuit substrate 5 prior to the hardening of the conductive adhesive 3. When the element electrode 2 is connected to the substrate electrode 4 by means of the conductive adhesive 3, the conductive adhesive 3 is formed in general on the predetermined substrate electrode 4 by either printing or dispensing. Later, the electronic element 1 is mounted by positioning. In this case, mounting an electronic element 1 on the conductive adhesive 3 may vary the spacing between the element electrode 2 and the substrate electrode 4, and also increase variations in the initial value of the connection resistance and reliability. The spacing can be kept constant by introducing a pressing step as described in this example. Moreover, the pressure breaks a surface oxide layer of the electrode in order to provide a good connection due to a direct contact between the metal of the substrate electrode 4 and a metal of the conductive filler having protrusions. This will suppress variation in the connection resistance.
A pressure range effective for suppressing variation in the connection resistance is from 10 KPa to 50 MPa, or preferably, from 20 KPa to 20 MPa. When the applied pressure is less than 10 KPa, the spacing between the element electrode 12 and the substrate electrode 14 becomes greater than 20 times the maximum dimension (D max) of the biggest conductive filler, which will provide insufficient effect in breaking surface oxide layers of the electrodes. When the pressure exceeds 50 MPa, the electronic element us subject to excessive pressure, which may result in malfunction or failure.
All the results are shown in FIG. 5.
(Third Embodiment)
This embodiment is characterized in that current is applied to a gap between the electronic element 1 and the circuit substrate 5 through the conductive adhesive 3 before hardening the conductive adhesive 3.
In a typical package comprising an electronic element 1 and a substrate electrode 4 connected by means of a conductive adhesive 3, the surface oxide layers of the electrodes remain. Since the surface oxide layers are insulating, the connection resistance is increased in the package, the initial value of the connection resistance is increased, and the reliability will vary remarkably. On the other hand, current is provided in this embodiment, so that the current flow is concentrated to the conductive filler surface having protrusions contained in the conductive adhesive 3 and also to the contact portion on the surfaces of the electrodes so as to form a concentrated local current. As a result, the surface oxide layers of the electrodes can be broken easily to lower the electric resistance.
(Fourth Embodiment)
This embodiment is characterized in that current is applied to a gap between the electronic element 1 and the circuit substrate 5 through the conductive adhesive 3 after hardening the conductive adhesive 3. Accordingly, the surface oxide layers of the electrodes become fragile as in the third embodiment so as to reduce the electrical resistance. In addition, yield of the packages in the process steps can be improved by supplying current after the hardening step in this embodiment.
For obtaining the effects described in the third and fourth embodiments, the current density range is from 0.01 A/mm2 to 100 A/mm2, preferably, from 0.1 A/mm2 to 10 A/mm2. The charging time is from 1 msec. to 5 sec., preferably, from 10 msec. to 1 sec.
A current density of less than 0.01 A/mm2 is insufficient to break the surface oxide layers, while current density over 100 A/mm2 may damage the electronic elements or the substrate electrodes. A charging time shorter than 1 msec. is insufficient to break the surface oxide layers, while a charging time longer than 5 sec. may damage the electronic elements or the substrate electrodes due to Joule heat or the like.
(Fifth Embodiment)
The packaging method in this embodiment comprises both compression and current application that is carried out before hardening the conductive adhesive 3. The applied pressure and current provide a multiplier effect over a total effect of separately performed compression and current application. That is, the pressure provides close contacts between the conductive filler and the electrodes, and increases the numbers of the contact points. When current is applied in this state, the surface oxide layer on an electrode becomes fragile. As a result, the surface oxide layer is broken and thus, the contact points at which the electrode metal and the conductive filler contact directly with each other will be increased. Moreover, since current flows in a state that the electrode metal and the conductive filler are contacted directly with each other, fusion of the electrode metal and the conductive filler is accelerated as in a case of fusion carried out by applying current. As a result, this embodiment can provide a package having less connection resistance and better reliability when compared to a case of performing either compression or current application alone.
(Sixth Embodiment)
This embodiment is characterized in that during mounting of an electronic element, the mounting state is controlled while detecting the electrical resistance between the electronic element 1 and the circuit substrate 5. This embodiment is distinguished from a method of controlling conditions of an interface between the conductive adhesive and the electrode in that the control is performed corresponding to the resulting connection resistance. Therefore, the embodiment can provide a package having connection resistance with reduced variation.
(Seventh Embodiment)
Similar mechanisms have been used for typical devices of packaging bare chip semiconductors, e.g., the aforementioned ACF. Nevertheless, the technique of the present invention can be distinguished from such devices for ACF packaging in that a device for ACF packaging comprises a pressing head having a heating mechanism for softening ACF, and that the conventional device has a difficulty in controlling a low pressure side within a compression force range described in the packaging method in the second embodiment.
(Eighth Embodiment)
The spacing measurer 15 can be arranged separately from the head 12.
(Ninth Embodiment)
The packaging device in this embodiment is characterized in that it comprises not only a mechanism for mounting an electronic element but a mechanism to detect and control electrical resistance between the electronic element and a circuit substrate during compression. This mechanism enables precise control of an electrical contact state between the electrode and the conductive adhesive, and thus, it can provide a package of an electronic element that is less resistant and highly reliable.
(Tenth Embodiment)
There is no specific limitation on the contact probe 16 and the power-supply unit 17, as long as the current described in the fourth embodiment can be applied stably. The contact probe 16 can be arranged separately from the head 12.
The device for packaging according to this embodiment is characterized in that it comprises not only a mechanism for mounting an electronic element but a mechanism for detecting electrical resistance between the electronic element and the circuit substrate and for controlling applied current depending on the measured value of the electrical resistance. By controlling the current in this manner, electrical resistance between the electrode and the conductive adhesive can be reduced and controlled with a high accuracy. Accordingly, the thus produced package of an electronic element has low resistance and high reliability.
In each of the above-mentioned embodiments, there is no specific limitation on the resin components of the conductive adhesive 3. The examples include an epoxy resin, an acrylic resin, a phenol resin, a silicon resin, a polyimide resin, and a urethane resin. When an insulating resin 3 contains a resin material such as a mixture of silicone resin, polycarbonate, and a fluorine-based resin, it will be waterproof or have some other properties. When the insulating resin 3 contains a urethane resin or the like, it functions to relax stress and thus the connection is resistant to impact or the like.
The conductive filler of the conductive adhesive 3 can be selected from metals such as silver, gold, copper, nickel, palladium and tin; alloys; carbon and mixtures thereof, though the examples are not limiting.
The conductive adhesive 3 can be applied by means of screen-printing, a dispenser or the like.
The electronic element 1 is a 3216-sized jumper chip resistor in the embodiments of the present invention, but the kinds or shapes are not limited as long as it is selected from generally-used electronic elements such as capacitors, coils, and semiconductors.
The embodiments are not limited to a case of one-sided packaging as mentioned above, but it can be used for two-sided packaging and so on.
The present invention will be explained further by referring to the following examples.
The following examples refer to packages of electronic elements formed by using a conductive adhesive according to the present invention.
The conductive filler in the conductive resin was a silver powder having an irregular spherical shape and having an average particle diameter of 2.5 μm. The binder resin included an epoxy resin and an amine-based hardening agent.
The conductive filler and the binder resin were measured by volume, and kneaded by means of a three-roll type apparatus so as to provide a conductive adhesive.
The conductive adhesive is printed by means of a 0.1 mm thick stainless metal plate having an opening shaped similarly to a substrate electrode pattern of a circuit substrate. Subsequently, the 3216-sized chip resistor is mounted on the circuit substrate before a hardening step of 30 minutes in a 150° C. hot air circulating furnace.
Table 1 indicates a content in volume of the conductive filler in a conductive adhesive, a connection strength of a package of a 3216-sized chip resistor connected by means of the conductive resin, and connection resistance. A shear strength tester (a product of AIKOH ENGINEERING, in which a load cell was used) was used, in which the tester was arranged so that the longitudinal side of the chip resistor was contacted with a shear strength tester indenter. The chip resistor was contacted to the indenter at a shear speed of 10 mm/min., and the weight at the time that the chip resistor was dropped from the circuit substrate was determined as a shear adhesion strength. The connection resistance was measured by a two-terminal method by contacting a probe to the substrate electrode. Respectively ten samples were prepared for measuring the shear strength and connection resistance, and the figures in the table are the average values.
As indicated in Table 1, connection strength of the conductive adhesives in this example was superior to that of conventional conductive adhesives since the contents of the conductive fillers were selected. The results are summarized in FIG. 15.
In Example 2, the silver powders are of a dendrite shape (“CUE07PB” (trade name) supplied by Kojundo Chemical Laboratory Co., Ltd.), scale shape (“TGG-1” (trade name) supplied by Tokuriki Chemical laboratory) and particle shape (“G-1” (trade name) supplied by Tokuriki Chemical laboratory). The binder resin contained an epoxy resin and an amine-based hardening agent. The conductive filler and the binder resin were measured by volume, and knealed by means of a three-roll apparatus so as to provide a conductive adhesive. Example 2 is identical to Example 1 in the method of packaging electronic elements by using such a conductive adhesive and also a method of evaluating the packages. The evaluation results are shown in Table 2.
As shown in Table 2, the conductive adhesives of this example had excellent connection strength while keeping the connection resistance low when compared to the conventional conductive adhesives since shapes and contents of the conductive fillers contained in the conductive adhesives were determined.
In Example 3, the binder resin was an elastic adhesive “PM100” (trade name) supplied by Cemedyne Co., Ltd. The conductive filler was a silver powder (“H-1” (trade name) supplied by Tokuriki Chemical Laboratory) of irregular spherical shape and having an average particle diameter of 2.5 μm.
The binder resin and the conductive filler were measured by volume, and kneaded by means of a three-roll apparatus so as to prepare a conductive adhesive.
Electronic elements were packaged by using the conductive adhesive in a method identical to that of Example 1. The adhesion strength was evaluated by measuring increase of connection resistance against bending displacement of the substrates. In the evaluation, each substrate packaged with a chip element was bent while being supported at three-points with a span of 50 mm so as to monitor the connection resistance at the time of the bending displacement of the substrate. A value of bending displacement of the substrate at the time that the connection resistance was increased from the initial value by 10% was determined as the bending displacement strength.
As indicated in Table 3, the bending displacement strength of the conductive adhesive according to Example 3 was improved in a comparison with those of conventional conductive adhesives, since the binder resin in Example 3 included an elastic adhesive.
In the present invention, the binder resin can be mixed with an elastic adhesive and a conventional epoxy adhesive.
A package of an electronic element according to the first embodiment was manufactured. The electronic element 1 was a solder-plated electrode of a 3216-sized jumper chip resistor, and the electronic component 1 was provided on a glass epoxy circuit substrate 6 corresponding to the packaging method of the second embodiment, by using a device for packaging electronic element as shown in the seventh embodiment.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position, and hardened at 150° C. for 30 minutes.
In Example 4, packages were manufactured by varying the compression force that is obtained by dividing a value of pressure detected at head of the packaging device by an area that the head contacts the conductive adhesive of the 3216-sized jumper resistor.
A package of an electronic element according to the first embodiment was manufactured by using a device for packaging electronic elements according to the eighth embodiment, on the basis of the packaging method according to the second embodiment, in which the package is mounted on a glass epoxy circuit substrate by means of an electronic element 1 as a 3216-sized jumper chip resistor of a solder-plated electrode.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position, and hardened at 150° C. for 30 minutes.
In Example 5, packages were manufactured by varying spacing between the element electrode and the substrate electrode, where the spacing was detected by using a head of the packaging device.
A package of an electronic element according to the first embodiment was manufactured by using a device for packaging electronic elements according to the ninth embodiment, on the basis of the packaging method according to the second embodiment, in which the package is mounted on a glass epoxy circuit substrate by means of an electronic element 1 as a 3216-sized jumper chip resistor of a solder-plated electrode.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position, and hardened at 150° C. for 30 minutes.
In Example 6, packages were manufactured by varying electrical resistance in the gap between the element electrode and the substrate electrode, which was detected by using a head of the packaging device during the mounting of the electronic element.
A package of an electronic element according to the first embodiment was manufactured by using a device for packaging electronic elements according to the tenth embodiment, on the basis of the packaging method according to the third embodiment, in which the package is mounted on a glass epoxy circuit substrate by means of an electronic element 1 as a 3216-sized jumper chip resistor of a solder-plated electrode.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position, and hardened at 150° C. for 30 minutes.
In this example, the electronic element was mounted by using a packaging device, and a package was manufactured by varying current amount applied from the head to the gap between the electronic element and the circuit substrate while the conductive adhesive is in a paste state. In this example, the current was applied for 25 msec. No effects were recognized when the application time was 1 msec. or less. When the time was longer than 5 sec., heat was generated in the gap between the chip resistor and the circuit substrate, and it caused foaming of the conductive adhesive.
A package of an electronic element according to the first embodiment was manufactured by using a device for packaging electronic elements according to the tenth embodiment, on the basis of the packaging method according to the fourth embodiment, in which the package is mounted on a glass epoxy circuit substrate by means of an electronic element 1 as a 3216-sized jumper chip resistor of a solder-plated electrode.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position, and hardened at 150° C. for 30 minutes.
In this example, packages were manufactured by varying current amount in the gap between the element electrode and the substrate electrode, where the current was applied from the head after hardening the conductive adhesive.
A package of an electronic element according to the first embodiment was manufactured by using a device for packaging electronic elements according to the tenth embodiment, on the basis of the packaging method according to the fifth embodiment, in which the package is mounted on a glass epoxy circuit substrate by means of an electronic element 1 as a 3216-sized jumper chip resistor of a solder-plated electrode.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position, and hardened at 150° C. for 30 minutes.
In this example, a package was manufactured by varying current amount applied from the head to the gap between the electronic element and the circuit substrate at the time of element mounting and also compression force detected by using the head at the time of the mounting of the electronic element.
A package of an electronic element according to the first embodiment was manufactured by using a device for packaging electronic elements according to the tenth embodiment, on the basis of the packaging method according to the sixth embodiment, in which the package is mounted on a glass epoxy circuit substrate by means of an electronic element 1 as a 3216-sized jumper chip resistor of a solder-plated electrode.
The terminal substrate electrode 4 of the circuit substrate 6 was a gold electrode. The conductive adhesive 3 was a thermosetting epoxy-based conductive adhesive that is available on the market. The conductive adhesive contains spherical conductive filler having a particle diameter in a range from 0.5 μm to 6 μm, and an average particle diameter of 3.3 μm.
An epoxy-based conductive adhesive 3 was applied by screen-printing onto a gold terminal substrate electrode 4 of the circuit substrate 6 so that the adhesive 3 had a thickness of about 0.1 mm. Later, a 3216-sized jumper chip resistor was mounted thereon after adjusting the mount position. The conductive adhesive was hardened by applying heat of 150° C. for 30 minutes by using a hot air circulating furnace so that the electronic element was connected to the circuit substrate.
In this example, a package was manufactured by varying electrical resistance between the element electrode and the substrate electrode detected by using the head of the packaging device at the time of mounting of the electronic element and also current amount applied at the time of mounting.
A package was manufactured in the following steps:
A package was manufactured in the following steps:
In an evaluation of the packages comprising 3216-sized jumper chip resistors manufactured in the examples, measurements were performed for the initial connection resistance, and also resistance after a reliability test in which the packages were kept under a condition of a temperature of 85° C. and a humidity of 85% for 100 hours. The results are shown in Tables 4-6.
In Examples 4-10, the electrical resistance was lowered further in a comparison with Comparative Examples 5 and 6. Concerning the waterproof test, the resistance value in each of the Examples was lowered considerably while the resistance values were raised in Comparative Examples 5 and 6. Concerning the contact between the electrode and the conductive filler in the conductive adhesive at the connected parts, the surface oxide layers were not removed in the packages of the Comparative Examples 5 and 6, while the oxide layers were removed in each Example, so that the connection resistance in each Example is low and stable both initially and after the waterproof test.
As mentioned above, the present invention relates to a conductive resin with improved connection strength between the conductive resin and an electronic element, and also between the conductive resin and an electrode of a circuit substrate. The conductive resin containing an elastic adhesive as the binder resin component has stable connection resistance against bending deformation of the substrate. When the adhesive according to the present invention is compressed, the resin component squeezes out while the conductive filler component remains inside so as to raise the concentration of the conductive filler. This raises the concentration of the conductive filler and provides connection by scratching the electrode surface. As a result, the conductive adhesive can be provided onto the substrate electrode of the circuit substrate without using any solder, and an electronic element can be packaged.
Improvements in connection strength and cost reduction have been important objects in use for conventional conductive resins and packages of electronic elements using the conductive resins. The present invention can solve the problems, and thus, it can provide various electronic apparatuses that are environmentally-friendly.
Moreover, the present invention can improve connection between an electrode and a conductive filler of a conductive adhesive, and thus, the initial and long-term reliability can be improved compared to conventional techniques.
Number | Date | Country | Kind |
---|---|---|---|
2000-053662 | Feb 2000 | JP | national |
2000-160881 | May 2000 | JP | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP01/01475 | 2/27/2001 | WO | 00 | 3/26/2002 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO01/64807 | 9/7/2001 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
5045236 | Tsunaga et al. | Sep 1991 | A |
5173765 | Nakayoshi et al. | Dec 1992 | A |
5316698 | Tani et al. | May 1994 | A |
5405707 | Tani et al. | Apr 1995 | A |
5804631 | Mine et al. | Sep 1998 | A |
5968420 | Thuny et al. | Oct 1999 | A |
6395332 | Hanawa et al. | May 2002 | B1 |
Number | Date | Country |
---|---|---|
855 720 | Jul 1998 | EP |
1 098 441 | Mar 1987 | GB |
61-31454 | Feb 1986 | JP |
1-165654 | Jun 1989 | JP |
01-165654 | Jun 1989 | JP |
1-246705 | Oct 1989 | JP |
3-21868 | Jan 1991 | JP |
03-176906 | Jul 1991 | JP |
3176906 | Jul 1991 | JP |
5-12916 | Jan 1993 | JP |
05-151821 | Jun 1993 | JP |
06-325617 | Nov 1994 | JP |
7-149524 | Jun 1995 | JP |
9-95651 | Apr 1997 | JP |
9-245522 | Sep 1997 | JP |
09-245522 | Sep 1997 | JP |
10-147801 | Jun 1998 | JP |
11-152458 | Jun 1998 | JP |
10-208547 | Aug 1998 | JP |
10-212501 | Aug 1998 | JP |
10-265748 | Oct 1998 | JP |
11-21477 | Jan 1999 | JP |
11-092727 | Apr 1999 | JP |
11-152458 | Jun 1999 | JP |
11-264001 | Sep 1999 | JP |
1098441 | Mar 1987 | SU |
Number | Date | Country | |
---|---|---|---|
20020158232 A1 | Oct 2002 | US |