Patent Application
20050014391
1. Field of the Invention
The present invention relates to a deposition method, a method of manufacturing a semiconductor device, and a semiconductor device, particularly to a deposition method of a low dielectric constant insulating film using a chemical vapor deposition method, a method of manufacturing a semiconductor device, and a semiconductor device, which are provided with a low dielectric constant interlayer insulating film that is made up of a barrier insulating film coating copper wire and a low dielectric constant insulating film.
2. Description of the Prior Art
In recent years, higher data transfer speed has been required with higher integration and higher density of a semiconductor integrated circuit device. For this reason, an insulating film having a low dielectric constant with a small RC delay time (hereinafter, referred to as a low dielectric constant insulating film) has been used.
Further, in the deposition method of the low dielectric constant insulating film, N2O, O2 or H2O gas has been conventionally used as oxidizing agent in addition to silicon containing compound.
However, in the deposition using O2 gas out of N2O, O2 and H2O gas as the oxidizing agent, a formed film contains OH and it is difficult to reduce a relative dielectric constant (k) to 3.0 or less.
Since H2O has slow oxidizing rate, it requires a relatively large flow rate and a deposition rate decreases to the range of 200 nm/min.
Further, although oxidization is easily controlled in N2O, a formed film contains nitrogen (N) and there is a possibility of causing excessive crosslinking reaction of chemically amplified resist due to the following reason.
Specifically, there is the case where the chemically amplified resist for KrF or ArF is employed to expose a line width of 0.13 μm or less when via holes and wiring grooves are formed by a dual damascene method in a low dielectric constant insulating film deposited using deposition gas containing nitrogen. In this case, there has been a problem that patterns as designed could not be formed. According to various examinations, it is presumed that this phenomenon is caused by the emission of nitrogen in the low dielectric constant insulating film and the generation of excessive crosslinking reaction of resist. The phenomenon tends to occur particularly when N2O is used as the oxidizing agent of the deposition gas of the low dielectric constant insulating film.
The object of the present invention is to provide a deposition method of a low dielectric constant insulating film, in which the formed film is prevented from containing nitrogen while deposition rate is improved or nitrogen content can be suppressed to an extent where nitrogen does not affect the crosslinking reaction of resist, a method of manufacturing a semiconductor device and a semiconductor device, which is provided with the low dielectric constant insulating film and a barrier insulating film having a lower dielectric constant.
According to the present invention, since the oxidizing agent made of oxygen-containing organic compound having alkoxyl group (OR: O is oxygen and R is CH3 or C2H5) is used as an oxidizing agent, a formed film does not contain nitrogen. In this case, the organic compound having alkoxyl group (OR: O is oxygen and R is CH3 or C2H5) is used instead of O2 containing no nitrogen as the oxidizing agent. This is because it improves the deposition rate and allows the formed film to take in a larger amount of carbon and hydrogen so that the low dielectric constant insulating film or the barrier insulating film having a lower relative dielectric constant can be formed. Particularly, in order to obtain a lower relative dielectric constant which is, for example, 2.5 or less in the low dielectric constant insulating film and 4 or less in the barrier insulating film, it is effective to use oxygen containing organic compound in which silicon combines with three or less methoxy groups or ethoxy groups as oxygen containing organic compound having alkoxyl group.
Furthermore, doping H2O as the oxidizing agent can lead to improvement of the film quality of the formed film.
In both cases, since a large amount of C—H and O—H, which is considered to have weak bond, is contained in the formed film, the relative dielectric constant is still as high as 2.6 to 2.7 comparing to that of an SOD film (Spin On Dielectrics). Therefore, plasma treatment is performed to the formed film after deposition to discharge C—H and O—H.
In the plasma treatment, treatment gas is generated to adjust gas pressure thereof, and electric power is applied to the treatment gas to generate plasma. The plasma of the treatment gas is allowed to contact the low dielectric constant insulating film whose temperature has been increased. According to the examination, the relative dielectric constant of the formed film can be further reduced by employment of a plasma that is generated by applying electric power to the treatment gas containing at least one of He, Ar, other noble gas, H2 and heavy hydrogen.
Consequently, it is possible to prevent the low dielectric constant insulating film from containing nitrogen or to suppress nitrogen content to an extent where nitrogen does not affect the crosslinking reaction of resist, while it is possible to maintain characteristic of the low relative dielectric constant from 2.4 to 2.5 and of superior moisture resistance.
Furthermore, the silicon containing organic compound having a siloxane bond is used as the constituent gas of the deposition gas. This is because the compound already contains Si—O—Si, and thus Si—O bond is directly taken in the formed film whereby excessive reaction of oxygen can be suppressed. Further, it is because it can stabilize the formed film.
In addition, the silicon containing organic compound having CH3 group is employed as the constituent gas of the deposition gas. This is because when the formed film contains a large amount of CH3 group, Si is terminated with CH3 group, and thus pores can be formed to reduce the dielectric constant.
Further, film formation is performed by incorporating CxHyFz or CxHyBz (x and y are 0 (except x=y=0) or positive integer, z is positive integer) in the deposition gas of the low dielectric constant insulating film. This can lead to securing an etching resistance of the low dielectric constant insulating film against the etchant of the barrier insulating film in the case of selectively etching the barrier insulating film in a laminated structure of the low dielectric constant insulating film and the barrier insulating film. Particularly, the employment of CxHyFz or CxHyBz can lead to securing the etching resistance and allowing it to contain F or B to achieve lower dielectric constant.
In the barrier insulating film used together with the low dielectric constant insulating film, a second deposition gas is used. The second deposition gas contains either the silicon containing organic compound having siloxane bond or the silicon containing organic compound having CH3 group and the oxygen containing organic compound having alkoxyl group (OR: O is oxygen and R is CH3 or C2H5) as the oxidizing agent in the same manner as the case of the low dielectric constant insulating film, and is generated by further adding at least one of H2, N2O and O2 thereto In other words, by further incorporating at least one of H2, N2O and O2 to a first deposition gas of the low dielectric constant insulating film, it is possible to form a film of better film quality, whose function to block Cu diffusion is improved although the relative dielectric constant is a little higher than that of the low dielectric constant insulating film. In addition, it is possible to prevent the barrier insulating film from containing nitrogen.
Embodiments of the present invention will be explained with reference to the drawings hereinafter.
(First Embodiment)
(Explanation of the plasma CVD/Treatment Apparatus used in the Deposition Method that is the Embodiment of the Present Invention)
The parallel plate type plasma enhanced
CVD/treatment apparatus 101 is made up of a deposition/treatment section 101A, which is a place of forming the barrier insulating film and the low dielectric constant insulating film on a substrate 21 by plasma gas and also a place of performing plasma treatment to the formed film, and a deposition gas/treatment gas supply section 101B having supply sources of plurality of gases that constitute the deposition gas and the treatment gas.
The deposition/treatment section 101A comprises a chamber 1, whose pressure can be reduced and which is connected to an exhaust unit 6 via an exhaust pipe 4. An opening/closing valve 5 that controls communication/non-communication between the chamber 1 and the exhaust unit 6 is provided halfway the exhaust pipe 4. The chamber 1 is provided with pressure measurement means such as a vacuum meter (not shown) for monitoring the pressure inside the chamber 1.
A pair of upper electrode 2 and a lower electrode 3 opposing to each other are provided in the chamber 1. A first high-frequency power supply source (RF power source) 7, which supplies high-frequency power having the frequency of 13.56 MHz to the upper electrode 2, is connected to the upper electrode 2. And a second high-frequency power supply source 8, which supplies low-frequency power having the frequency of 380 kHz to the lower electrode 3, is connected to the lower electrode 3. At least the first high-frequency power supply source 7 of the high-frequency power supply sources 7, 8 supplies high-frequency power (PHF) to the upper electrode 2 or the second high-frequency power supply source 8 supplies low-frequency power (PLF) to the lower electrode 3, and thus the deposition gas or the like is transformed into plasma. The upper electrode 2, the lower electrode 3, and the power sources 7, 8 constitute plasma generation means that transforms the deposition gas or the like into plasma.
Note that low-frequency power of not only the frequency of 380 kHz but also the frequency of 100 kHz or higher and lower than 1 MHz can be applied to the lower electrode 3, and the high-frequency power of not only the frequency of 13.56 MHz but also the frequency of 1 MHz or higher may be applied to the upper electrode 2 opposing to the lower electrode 3. Further, in
The upper electrode 2 serves as a diffuser of the deposition gas or the like. A plurality of through holes are formed in the upper electrode 2, and openings of the through holes at the opposing surface to the lower electrode 3 are release ports (introduction ports) of the deposition gas or the like. The release ports of the deposition gas or the like is connected to the deposition gas/treatment gas supply section 101B via piping 9a. Alternatively, a heater (not shown) is provided for the upper electrode 2 depending on circumstances. The heater is used to heat the upper electrode 2 to the temperature of about 100° C. during deposition to prevent particles made of reactive product of the deposition gas or the like from adhering to the upper electrode 2.
The lower electrode 3 serves as a holding stage for the substrate 21, and is provided with a heater 12 heating the substrate 21 on the holding stage.
The deposition gas/treatment gas supply section 101B is provided with a supply source of the silicon containing organic compound having siloxane bond or the silicon containing organic compound having CH3 bond, a supply source of H2O, a supply source of He, Ar or H2 as diluent gas, a supply source of CxHyFz or CxHyBz, and a supply source of H2, N2O or O2 used when depositing the barrier insulating film, as the supply sources of the deposition gas. Further, it is provided with a supply source of He, Ar, other noble gas, H2 or heavy hydrogen as the supply sources of plasma treatment gas, and a supply source of nitrogen (N2) as purge gas.
These gases are accordingly supplied into the chamber 1 through branch piping 9b to 9i and the piping 9a to which all the branch piping 9b to 9i are connected. The branch piping 9b to 9i are equipped halfway with flow rate adjusting means 11a to 11h and opening/closing means 10b to 10q for controlling communication/non-communication of the branch piping 9b to 9i, the piping 9a is equipped halfway with opening/closing means 10a for communicating/non-communicating the piping 9a.
According to the above-described deposition/treatment apparatus 101, it comprises the supply source of the silicon containing organic compound having siloxane bond or the silicon containing organic compound having CH3 bond, a supply source of the oxygen containing organic compound having alkoxyl group as the oxidizing agent, the supply source of H2O, the supply source of He, Ar or H2 as diluent gas, the supply source of CxHyFz or CxHyBz, and the supply source of H2, N2O or O2 used when depositing the barrier insulating film, as the supply sources of the deposition gas. Further, it comprises the supply source of He, Ar, other noble gas, H2 or heavy hydrogen as the supply sources of plasma treatment gas, and the supply source of nitrogen (N2) as purge gas. Moreover, it comprises plasma generation means 2, 3, 7, 8 that transform the deposition gas and the treatment gas into plasma.
With this constitution, it is possible to perform continuously in a same chamber deposition of the low dielectric constant insulating film (low-k film) made up of a silicon oxide film having low dielectric constant, plasma treatment after depositing the low dielectric constant insulating film (described below) and deposition of the Cu barrier insulating film made up of a silicon oxide film or a silicon oxy-nitride film having a barrier function to prevent Cu diffusion.
(Explanation of the Manufacturing Method of a Semiconductor Device, which is the Embodiment of the Present Invention)
Next, description will be made for the deposition method of the low dielectric constant insulating film and the Cu barrier insulating film used in the manufacturing method of a semiconductor device, which is the embodiment of the present invention.
In the low dielectric constant insulating film and the Cu barrier insulating film, the entire process of film formation is different from each other, in addition to deposition conditions. Specifically, deposition process and treatment process (plasma treatment) to the formed film after deposition are required to create the low dielectric constant insulating film (low-k film), which has superior moisture resistance and low dielectric constant, contains no nitrogen, or contains trace of nitrogen. Further, only the deposition process is basically required to create the Cu barrier insulating film, which has superior diffusion preventing function of copper, contains no nitrogen, or contains trace of nitrogen, and the treatment process to the formed film after deposition is not necessary.
Firstly, the particularly effective combinations of gases of the deposition conditions, which constitute the deposition gas of the low dielectric constant insulating film and the Cu barrier insulating film, will be described with reference to
(i) Constituent gas of the Deposition Gas to Form a Low Dielectric Constant Insulating Film
Herein, there are cases where silicon containing organic compound is made up of two or more kinds of siloxane, and in such a case, one or more of straight chain siloxane and one or more of cyclic siloxane are contained. The same applies to the followings.
(ii) Constituent Gas of the Deposition Gas to Form a Cu Barrier Insulating Film
Next, description will be made for the above-described silicon containing organic compound, oxidizing agent, diluent gas, and CxHyFz or CxHyBz.
The followings can be used as typical examples.
(i) Silicon Containing Organic Compound
(A) Silicon Containing Organic Compound having Siloxane Bond
(a) Organic Compound having Straight Chain Si—O—Si Bond
(b) Organic Compound having Cyclic Si—O—Si Bond
(B) Silicon Containing Organic Compound having CH3 Bond
(ii) Oxidizing Agent
(A) Oxygen Containing Organic Compound having Methoxy Group
(B) Oxygen Containing Organic Compound having Ethoxy Group
(iii) Diluent Gas
(iv) CxHyFz or CxHyBz
(b) CxHyBz
Next, the deposition conditions other than the above-described ones and the entire process of film formation will be explained, and the reasons or effects of adopting the deposition conditions including the above and the entire process of film formation will be described.
In formation of the low dielectric constant insulating film, the oxidizing agent made up of oxygen containing organic compound having alkoxyl group (OR: O is oxygen and R is CH3 or C2H5) is used as the oxidizing agent in order to prevent the formed film from containing nitrogen. In this case, the oxygen containing organic compound having alkoxyl group is used as the oxidizing agent instead of O2 containing no nitrogen. The reason is that it can improve the deposition rate and the formed film can take in a larger amount of carbon and hydrogen to form the low dielectric constant insulating film or the barrier insulating film having a lower relative dielectric constant. Particularly, since the lower relative dielectric constant which is 2.5 or less in the low dielectric constant insulating film and 4 or less in the barrier insulating film are obtained, for example, it is effective to use oxygen containing organic compound having silicon which combines with three or less methoxy groups or ethoxy groups as oxygen containing organic compound having alkoxyl group.
Furthermore, by doping H2O as the oxidizing agent, the film quality of the formed film can be improved.
In both cases, since a large amount of C—H or the like, which is considered to have weak bond, is contained in the formed film, the relative dielectric constant is still as higher as 2.6 to 2.7 comparing to that of the SOD film (Spin On Dielectrics). Therefore, plasma treatment is performed to the formed film after deposition to discharge C—H or the like, and the relative dielectric constant is further reduced.
In the plasma treatment, gas containing at least one of other noble gas, for example, He or Ar, H2 and heavy hydrogen is prepared, and then gas pressure is adjusted to 1 Torr or less, 0.5 Torr or less preferably, and thus the treatment gas is generated. Then, electric power is applied to the treatment gas to transform it into plasma. The temperature of the low dielectric constant insulating film is increased to 375° C. or higher, preferably in the range of 400° C. and 450° C., and then the plasma of the treatment gas is allowed to contact the film. According to the examination, by employing plasma that is generated by applying electric power, which is electric power having the frequency of 1 MHz or higher, to the treatment gas which contains at least one of He, Ar, H2 and heavy hydrogen and whose gas pressure is adjusted to 1 Torr or less, the relative dielectric constant of the formed film can be further reduced. In this case, the reason why the temperature of the low dielectric constant insulating film is increased to 375° C. or higher is to fully remove moisture and the like in the formed film, which are not completely removed by plasma.
Consequently, the low dielectric constant insulating film can be prevented from containing nitrogen or nitrogen content can be suppressed to an extent where nitrogen does not affect the crosslinking reaction of resist while it has the low relative dielectric constant from 2.4 to 2.5 and maintains characteristic of superior moisture resistance.
Furthermore, the silicon containing organic compound having siloxane bond is used as the constituent gas of the deposition gas. It is because the compound already contains Si—O—Si, and thus Si—O bond is directly taken in the formed film, whereby excessive reaction of oxygen can be suppressed, and because it can stabilize the formed film.
Further, CxHyFz or CxHyBz (x and y are 0 (except x=y=0) or positive integer, z is positive integer) may be incorporated in the deposition gas of the low dielectric constant insulating film. Thus, it is possible to secure the etching resistance of the low dielectric constant insulating film against the etchant of the barrier insulating film in the case of selectively etching the Cu barrier insulating film in the structure where the low dielectric constant insulating film and the Cu barrier insulating film are laminated. Particularly, an employment of CxHyFz or CxHyBz results in that it is possible to secure the etching resistance and that it is possible to allow the formed film to contain F or B and thus achieve a lower dielectric constant.
Furthermore, in the Cu barrier insulating film used together with the low dielectric constant insulating film, at least one of H2, N2O and O2 is added to the first deposition gas of the low dielectric constant insulating film. In this case, the gas pressure is set to as low as less than 1.0 Torr when frequency for generating plasma of electric power to be applied is less than 1 MHz, and it is set to as high as 1.0 Torr or higher when the frequency for generating plasma is 1 MHz or higher and bias electric power having the frequency less than 1 MHz is applied. In addition, the substrate temperature during deposition is set to 200° C. to 400° C. With the above-described deposition conditions, it is possible to form a film of better film quality, which is improved in a function to block Cu diffusion although it is a little higher in the relative dielectric constant. In addition, it is possible to prevent the Cu barrier insulating film from containing nitrogen.
Still further, CxHyFz or CxHyBz (x and y are 0 (except x=y=0) or positive integer, z is positive integer) may be incorporated in the deposition gas of the Cu barrier insulating film. Thus, it is possible to secure the etching resistance of the Cu barrier insulating film against the etchant of the low dielectric constant insulating film in the case of selectively etching the low dielectric constant insulating film in the structure where the Cu barrier insulating film and the low dielectric constant insulating film are laminated.
In the case of forming the Cu barrier insulating film on the low dielectric constant insulating film subsequently after it is formed, it is preferable to perform the deposition of the Cu barrier insulating film subsequently without exposing the low dielectric constant insulating film to air. This is to prevent the low dielectric constant insulating film from absorbing moisture in air to increase the relative dielectric constant.
Next, examples of the deposition conditions will be described as follows.
(1) First Example
The insulating film of the first example is an example of the low dielectric constant insulating film. Trimethoxysilane is used as the oxidizing agent.
(Deposition Conditions I)
(i) Deposition Gas Conditions
(ii) Conditions for Generating Plasma
(A size of the electrode is 345 mm φ, which is the same hereinafter.)
(iii) Substrate Heating Temperature: 375° C.
(iv) Deposited Silicon Oxide Film
(2) Second Example
The insulating film of the second example is another example of the low dielectric constant insulating film. H2O is added to the deposition conditions I.
(Deposition Conditions II)
(i) Deposition Gas Conditions
(ii) Conditions for Generating Plasma
(iii) Substrate Heating Temperature: 375° C.
(iv) Deposited Silicon Oxide Film
(3) Third Example
The insulating film of the third example is an example of the barrier insulating film. At least any one of H2, N2O and O2 is added to the deposition conditions I.
(Deposition Conditions III)
(i) Deposition Gas Conditions
(ii) Conditions for Generating Plasma
(iii) Substrate Heating Temperature: 375° C.
(iv) Deposited Silicon Oxide Film
(4) Fourth Example
The insulating film of the fourth example is an example of the low dielectric constant insulating film. OMCTS is employed as a silicon containing compound gas, and monomethyltrimetoxysilane (MTMS) is employed as an oxydizing agent. Further, H2O is added.
(Deposition Conditions IV)
(i) Deposition Gas Conditions
(ii) Conditions for Generating Plasma
(iii) Substrate Heating Temperature: 350° C.
(iv) Deposited Silicon Oxide Film
Next, regarding the low dielectric constant insulating film formed in the fourth example of the first to the fourth examples, an explanation is performed for examination results of the deposition rate, dielectric constant and refractive index, leakage current and insulative breakdown electric field.
(A) Deposition Rate
As shown in
Specifically, the addition of H2O can result in facilitating a control of the deposition. Further, although an employment of only OMCTS+MTMS leads to a violent reaction and inclination of a cloudiness of the formed film, the cloudiness thereof can be prevented by the addition of H2O.
(B) Dielectric Constant and Refractive Index
As shown in
(C) leakage Current and Insulative Breakdown Electric Field
An insulating film for examination was formed on a silicon substrate. After the film formation, a probe of mercury is contacted onto the insulating film for examination, followed by applying measuring voltage between the silicon substrate and the probe of mercury, and then measuring the leakage current and the insulative breakdown electric field.
As shown in
(Second Embodiment)
Next, the semiconductor device and its manufacturing method according to a second embodiment of the present invention will be explained with reference to
On them are formed a wiring interlayer insulating film 66 with via holes 68 formed therein and an upper wiring buried insulating film 67 with upper wiring grooves 69 formed therein.
The wiring interlayer insulating film 66 consists of a second lower passivation layer (Cu barrier insulating film) 66a made up of the SiO2 film of the film thickness of about 50 nm, a primary insulating film (low dielectric constant insulating film) 66b having low dielectric constant, which is made up of the SiO2 film of the film thickness of about 500 nm, and a second upper passivation layer (Cu barrier insulating film) 66c made up of the SiO2 film of the film thickness of about 50 nm.
The upper wiring buried insulating film 67 consists of a primary insulating film (low dielectric constant insulating film) 67a having low dielectric constant, which is made up of the SiO2 film of the film thickness of about 500 nm, and a third upper passivation layer (Cu barrier insulating film) 67b made up of the SiO2 film of the film thickness of about 50 nm.
The upper wiring grooves 69 have an opening area larger than that of the via holes 68 and are formed so as to connect with the via holes 68. A connection conductor 70, which consists of a TaN film 70a as the copper diffusion block film and a copper film 70b, and an upper wiring 71, which consists of the TaN film 70a as the copper diffusion block film and the copper film 70b as well, are integrally buried in the via holes 68 and the upper wiring grooves 69 by a well known dual damascene method. Then, the uppermost entire surface is coated by an uppermost passivation layer (Cu barrier insulating film) 72 made up of the SiO2 film according to the present invention.
All of the above-described low dielectric constant insulating films and the Cu barrier insulating films are the insulating films according to the present invention.
Next, the manufacturing method of a semiconductor device according to the second embodiment of the present invention will be explained with reference to
Firstly, as shown in
Subsequently, the film is not exposed to air and an SiO2 film (Cu barrier insulating film) 63 of the film thickness of about 50 nm is formed in the same chamber 1 by a plasma CVD method. The deposition conditions are equivalent to the deposition conditions III in the third example of the first embodiment except for the film thickness. In the deposited SiO2 film 63, the relative dielectric constant measured in the frequency 1 MHz was about 4.0 and leakage current was 10−6 A/cm2 at the field intensity of 4MV/cm.
Then, the substrate 61 is brought out of the chamber 1, and a resist film made of the chemically amplified resist or the like is formed on the SiO2 film 63. Then, opening portions of the resist film are formed by a photolithography method on regions where the wiring grooves are to be formed, and a mask 73a is formed as shown in
Next, as shown in
Then, pre-treatment of the surface of the copper film 65b was performed before deposition and a surface oxide film was removed.
The treatment method was performed using the parallel plate type plasma enhanced CVD apparatus. NH3 was introduced at the flow rate of 50 sccm to adjust the gas pressure to 1 Torr, electric power having the frequency of 13.56 MHz was applied to transform NH3 into plasma, and the copper film 65b was allowed to contact the plasma while the substrate 61 was heated to 375° C.
Next, the substrate 61 is carried in the chamber 1 of the deposition apparatus, and the passivation layer (Cu barrier insulating film) 66a made of the SiO2 film coating the lower wiring 65 is formed as shown in
After that, the insulating film (low dielectric constant insulating film) 66b made up of the SiO2 film of the film thickness of about 500 nm, which is intended to be the primary insulating film of the wiring interlayer insulating film 66, and the passivation layer (Cu barrier insulating film) 66c made up of the SiO2 film of the film thickness of about 50 nm are continuously formed in the same chamber 1. Thus the wiring interlayer insulating film 66 for burying the connection conductor is formed.
With regard to the primary insulating film 66b, the deposition conditions shall be equivalent to those of the lower wiring buried insulating layer 62, and the film treatment conditions shall be equivalent to those after the deposition thereof. Further, with regard to the passivation layer 66c, the conditions shall be equivalent to the deposition conditions of the passivation layer 66a.
Subsequently, the insulating film (low dielectric constant insulating film) 67 made up of the SiO2 film, which is intended to be the primary insulating film of the wiring buried insulating film, and the passivation film (Cu barrier insulating film) 67b made up of the SiO2 film are continuously formed in the same manner on the passivation layer 66c in the same chamber 1. Thus the wiring buried insulating film 67 that buries the upper wiring is formed. With regard to the primary insulating film 67a, the deposition conditions shall be equivalent to those of the lower wiring buried insulating layer 62, and the film treatment conditions to those after the deposition thereof. With regard to the passivation layer 67b, the deposition conditions shall be equivalent to those of the passivation layer 66a.
Next, the substrate 61 is brought out of the chamber 1 of the deposition apparatus, and the connection conductor 70 and the upper wiring 71 are formed by the well-known dual damascene method, as shown in
Specifically, after the resist film is formed on the passivation layer 67b, the opening portions of the resist film are formed by the photolithography method on regions where the via holes are to be formed, and a mask 73b is formed as shown in
Next, etching is performed to the passivation layer 67b, the insulating film 67a, the passivation layer 66c and the insulating film 66b through the openings of the resist film 73b to form an opening through them. Thus, the openings 68 are formed in the passivation layer 66c and the primary insulating film 66b of the wiring interlayer insulating film 66.
Next, another resist film is formed on the passivation layer 67b, followed by forming openings in regions where the wiring grooves are intended to be formwd so that a mask 73c is formed as shown in
Subsequently, the openings of the mask 73c are formed so as to have a larger opening area than that of the first openings and to include the first openings. Then, the passivation layer 67b and the insulating film 67a are etched through the openings of the mask 73c to form an opening through them. At this point, since the underlying passivation layer 66c is deposited by the deposition gas containing CHF3, it has etching resistance to the etching gas of the primary insulating film 67a, and thus the passivation layer 66c stops etching. Consequently, wiring grooves 69 are formed in the wiring buried insulating film 67. After that, the passivation layer 66a is etched to form the via holes 68 through the wiring interlayer insulating film 66. As a result, the lower wiring 65 is exposed at the bottom of the via holes 68, and the lower wiring 65 and the wiring grooves 69 are connected through the via holes 68.
Next, as shown in
Next, the pre-treatment of the surface of the copper film 70b was performed before deposition in the same conditions as the pre-treatment of the surface of the copper film 65b, and thus the surface oxide film was removed. Then, the passivation layer 72 made up of the SiO2 film is formed on the entire surface by the same deposition method as that of the passivation layer (63a or 66a). Consequently, a semiconductor device having multilayer wiring, which mainly consists of a copper film, is completed.
As described above, according to the manufacturing method of the semiconductor device of the second embodiment, the primary insulating films 62a, 66b, 67a are deposited on the deposition conditions I of the first example of the first embodiment, and the plasma treatment is performed after deposition. Therefore, the primary insulating films 62a, 66b, 67a have the low dielectric constant of 0.2.5 or less and are higher in their moisture resistance.
Furthermore, since the passivation layers 63a, 66a, 66c, 67b, 72 are formed on the deposition conditions III of the third example of the first embodiment, they have high diffusion blocking capability to Cu. Further, since the passivation layers 63a, 66a, 66c, 67b, 72 are formed by the deposition gas containing CHF3, they contain fluorine, by which a lower dielectric constant can be achieved.
Moreover, since the insulating films (66b, 67a) and the passivation layers (66a, 66c, 67b), which are exposed to the surface, do not contain nitrogen, the mask 73c having good dimensional precision can be formed when the lower wiring grooves 64, the via holes 68 and the upper wiring grooves 69 are formed by the lithography method.
Furthermore, openings are formed through the wiring interlayer film 66 and the wiring buried insulating film 67 such that their opening areas become larger from the bottom to alternately form the via holes 68 and the wiring grooves 69 connected with the via holes 68. In other words, the passivation layer 66c becomes an underlayer of the insulating film 67a to be etched when the insulating film 67a is selectively etched.
Since the passivation layer 66c to which the present invention is applied is formed by the deposition gas containing CHF3, it effectively functions as an etching stopper to the etchant of the primary insulating film 67a and also effectively functions as a mask against the excessive etching of the insulating film 66b under the passivation layer.
(Third Embodiment)
Next, the semiconductor device and the manufacturing method thereof according to the third embodiment of the present invention will be explained.
A structure similar to that of the semiconductor device of
In this case, the primary insulating films 62a, 66b, 67a correspond to the low dielectric constant insulating films of this embodiment, and the passivation layers 63a, 66a, 66c, 67b, 72 correspond to the barrier insulating films of this embodiment.
Further, a method similar to the manufacturing method of a semiconductor device of
In this case, the low dielectric constant insulating films corresponding to the primary insulating films 62, 66b, 67a are deposited on the deposition conditions (II) of the second example of the first embodiment.
Plasma treatment is performed to the primary insulating films 62, 66b, 67a after deposition by using at least one of He, Ar, H2 and heavy hydrogen gas in the same chamber where the deposition was conducted.
Furthermore, the barrier insulating films corresponding to the passivation layers 63a, 66a, 66c, 67b, 72 are deposited on the deposition conditions (III) of the third example of the first embodiment.
According to the above-described third embodiment of the present invention, the low dielectric constant insulating film is deposited on the above deposition conditions and plasma treatment is performed after deposition, so that the low dielectric constant insulating film has the low dielectric constant of about 2.4 and its moisture resistance is high. In addition, since the barrier insulating film is formed on the deposition conditions III of the third example of the first embodiment, it can lead to high diffusion blocking capability to Cu and a lower dielectric constant.
The present invention has been explained in detail by the embodiments, but the scope of the present invention is not limited to the examples specifically shown in the above-described embodiments, and modifications of the above-described embodiments without departing from the gist of the invention are included in the scope of the present invention.
In the second embodiment, for example, although the deposition conditions of the primary insulating films 62, 66b, 67a are set to the conditions described in the first example in the first embodiment, the conditions may be properly changed for application. Further, the deposition conditions of the primary insulating films (low dielectric constant insulating film) 62, 66b, 67a may be properly changed for application as well.
Furthermore, although the deposition conditions of the passivation layers 63a, 66a, 66c, 67b, 72 are set to the deposition conditions III of the third example in the first embodiment, they may be properly changed for application.
As described above, since the present invention uses the oxidizing agent made of oxygen containing organic compound having alkoxyl group (OR: O is oxygen and R is CH3 or C2H5) as an oxidizing agent, the formed film does not contain nitrogen. This can lead to improving the deposition rate, and to allowing the formed film to take in a larger amount of carbon and hydrogen to form the low dielectric constant insulating film or the barrier insulating film having a lower relative dielectric constant.
Particularly, by using the oxygen containing organic compound in which silicon combines with three or less methoxy groups or ethoxy groups as oxygen containing organic compound having alkoxyl group, a lower relative dielectric constant which is 2.5 or less in the low dielectric constant insulating film and 4 or less in the barrier insulating film can be obtained.
Further, by doping H2O as the oxidizing agent, the film quality of the formed film can be improved.
In both cases, since a large amount of C—H and O—H, which is considered to have weak bond, is contained in the formed film, the relative dielectric constant is still as high as 2.6 to 2.7 comparing to that of the SOD film (Spin On Dielectrics). Therefore, plasma treatment is performed to the formed film after deposition to remove C—H and O—H. In the plasma treatment, a treatment gas containing at least one of noble gases, for example, He and Ar, H2 and heavy hydrogen is generated, and electric power is applied to the treatment gas to generate plasma. The plasma of the treatment gas is allowed to contact the low dielectric constant insulating film whose temperature has been increased, and thus the relative dielectric constant of the formed film can be further reduced.
Consequently, it can lead to preventing the low dielectric constant insulating film from containing nitrogen or suppressing nitrogen content therein to an extent where nitrogen does not affect the cross-linking reaction of resist while it can lead to maintaining characteristic of the low relative dielectric constant from 2.4 to 2.5 and of superior moisture resistance.
Furthermore, when the silicon containing organic compound having a siloxane bond is used as the constituent gas of the deposition gas, the compound already contains Si—O—Si and thus Si—O bond is directly taken in the formed film. With this, excessive reaction of oxygen can be suppressed and the formed film can be stabilized.
In addition, when the silicon containing organic compound having CH3 group is used as the constituent gas of the deposition gas, the formed film contains a large amount of CH3 group. Accordingly, Si is terminated by CH3 group and pores are formed, and thus the dielectric constant can be reduced.
Further, by performing deposition upon incorporating CxHyFz or CxHyBz (x and y are 0 (except x=y=0) or positive integer, z is positive integer) to the deposition gas of the low dielectric constant insulating film, it is possible to secure etching resistance of the low dielectric constant insulating film against the etchant of the barrier insulating film in the case of selectively etching the barrier insulating film in the laminated structure of the low dielectric constant insulating film and the barrier insulating film. Particularly, by using CxHyFz or CxHyBz, it is possible to secure the etching resistance, and it is possible to allow the formed film to contain F or B and thus to achieve lower dielectric constant.
Still further, in the barrier insulating film used together with the low dielectric constant insulating film, the second deposition gas, which contains either one of silicon containing organic compound having siloxane bond and silicon containing organic compound having CH3 group, and oxygen containing organic compound having alkoxyl group (OR: O is oxygen and R is CH3 or C2H5) as the oxidizing agent, and to which at least one of H2, N2O and O2 is added, is used in the same manner as the case of the low dielectric constant insulating film. Specifically, by adding at least one of H2, N2O and O2 to the first deposition gas of the low dielectric constant insulating film, it is possible to form a film of better film quality, whose function to block Cu diffusion is improved although the relative dielectric constant is a little higher than that of the low dielectric constant insulating film. In addition, it is possible to prevent the barrier insulating film from containing nitrogen.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2003-172395 | Jun 2003 | JP | national |
| 2004-171399 | Jun 2004 | JP | national |