Patent Grant
9502711
The present invention is related to fabrication of fibers (yarns) or other shaped articles from materials in powder form (or nanoparticles or nanofibers) using carbon nanotube/nanofiber sheet as a platform (template). Embodiments of the present invention relate to methods for fabricating biscrolled fibers using carbon nanotube/nanofiber sheets and biscrolled fibers fabricated thereby.
Multifunctional yarns are required for diverse applications, like clothing that protects emergency responders and provides sensing, communication, energy harvesting, and storage capabilities. Fabrics from such yarns could provide electrodes for high performance batteries, supercapacitors, and fuel cells that might be imbedded in vehicle shells. Despite important advances, critical problems remain: (1) most multifunctional materials are unspinnable using known technologies, (2) nanopowder and nanofiber functionality often degrades when accessible surface area decreases during processing, and (3) coating nanoparticles or nanofibers on yarns after yarn spinning can severely decrease loading levels and durability.
A generically applicable method is needed for configuring functional nanoparticles, nanofibers, and nanoribbons as the major component of weavable yarns that can perform, for example, as superconductors; battery electrodes; ferromagnets; catalytic convertors; carriers of biological and biopharmaceutical materials; photocatalysts and photosensitizers for photovoltaic cells and photoelectrolysis cells for hydrogen production; hydrogen storage containers; and active oxygen generators for self-cleaning and destruction of biological threats.
A problem hindering the applications of these powder materials is the need for methods for converting these powder (or nanoparticles or nanofibers) into yarns with ultra-high loading of the powder component to effectively utilize the properties of the powder materials. Solid-state-spun carbon nanotube (CNT) sheet as described in U.S. Patent Appl. Publ. No. 2008/0170982, published Jul. 17, 2008 (“the '982 application”), is a novel aerogel material that can support load many times of its own mass and be easily converted into yarns or other shaped articles.
Present invention embodiments provide a novel approach that convert up to 99 weight percent of one or more other functional materials into yarns using twist-based spinning of carbon nanotube sheets. CNT sheets of multiwalled nanotubes (MWNTs), few walled nanotubes (FWNTs), or single walled nanotubes (SWNTs) are used as a platform (providing the mechanical support) for collecting and confining the particle materials, forming a bilayered sheet structure. Then the bilayered sheet ribbon is scrolled into a biscrolled yarn, which is designated the guest@host. The biscrolling method is capable of incorporating large amount of other materials onto CNT sheet, achieving ultra-high loading of the particle materials and maintaining the grain size of the material. As a result, the properties of the biscrolled yarns predominantly come from the deposited guest component other than from CNT sheet. For example, biscrolled yarns have been demonstrated as superconductors; battery electrodes; supercapacitors; carriers of biological and biopharmaceutical materials; photocatalysts for self-cleaning textiles, etc.
The present invention includes fabrication of biscrolled fiber using carbon nanotube sheet.
In general, in one aspect, the invention features a method that includes forming a nanofiber sheet or nanofiber sheet stack as a sheet platform for particle material deposition. The method further includes depositing particle material onto the sheet platform to form a bilayered sheet structure. The method further includes scrolling the bilayered sheet structure into a biscrolled yarn.
A “nanofiber sheet” is a sheet having any shape (especially including rectangular shape, wedge shape or distorted wedge shape) that includes nanofibers.
This term “sheet” can be used in the same sense as the term “web.”
“Particle material” includes particles that have any shape, like fiber shape, plate shape, and round or oblong shape.
The term “bilayered” means that layers comprising nanofiber sheet and particle material can be separately observed, though some interpenetration of these layers typically occurs. Included in the term “bilayered” are layers that comprise more than two layers that have distinguishably different average compositions. (Such more than two layers can be provided, for instance, by depositing different host materials on opposite sides of a sheet platform.)
The term “scrolled” means that bilayers are wrapped in scroll fashion (especially helical scroll fashion) no matter the degree of structural perfection achieved by such scrolling.
The meaning of these terms (including “nanofiber sheet,” “particle material,” “bilayered,” and “scrolled”) are further reflected herein, including in the context in which these terms are utilized.
Implementations of the invention can include one or more of the following features:
The method can further include densifying the biscrolled yarn using liquid absorption and subsequent evaporation.
The method can further include introducing a twist during formation of the biscrolled yarn.
The sheet platform can further include carbon nanotubes.
The sheet platform can further predominately consist of carbon nanotubes on a weight basis. The biscrolled yarn can have a specific strength of at least about 50 MPa/(g/cm3).
The carbon nanotubes in the sheet platform can be predominately oriented in the same in-plane direction.
The carbon nanotube sheet platform can be (a) a carbon nanotube sheet wedge that results from direct twist-based spinning from a carbon nanotube forest or (b) a self-suspended nanotube sheet or sheet stack obtained by sheet draw from a carbon nanotube forest.
The sheet platform can include different sheets in a sheet stack. The different sheets can include the carbon nanotubes, which are in-plane aligned. The direction of the in-plane alignment of the carbon nanotubes in these different sheets can differ.
The sheet platform can be free-standing.
The sheet platform can be supported on a substrate that can be removed after the depositing of the particle material.
The particle material can include at least about 50 weight percent of the biscrolled yarn. The particle materials can include at least about 80 weight percent of the biscrolled yarn. The particle material can include at least about 90 weight percent of the biscrolled yarn.
The method can further include removing the carbon nanotube sheet. The step of removing the carbon nanotube sheet can occur after the particle material is made coherent.
The particle material can include nanoparticles. The nanoparticles can be in powder form. The nanoparticles can include nanofibers. The nanofibers can include nitrogen doped nanotubes or graphene ribbons.
The particle material comprises a superconductor or components that can be converted to a superconductor by processing the biscrolled yarn.
The particle material can include a catalyst.
The particle material can include a biologically active material.
The particle material can include TiO2.
The method of Claim 3, further including that the step of making the particle material can be coherent. The step of making the particle material coherent can be sintering, melting, or combinations thereof.
The step of depositing particle material can include the use of an ink jet printing process.
The method can further include using particle material that can be liquid dispersed, and depositing the particle material from a liquid dispersed state. The depositing the particle material from a liquid dispersed state can include a filtration method.
The step of depositing the particle material can include a liquid-free deposition method. The liquid-free deposition method can be: electrostatic deposition, electron beam evaporation, sputtering, chemical vapor deposition (CVD), dry powder airbrush deposition, deposition of gas-dispersed guest nanoparticles immediately after their formation by reaction of gases, or a combination thereof.
The step of depositing the particle material can include a liquid state or quasi-liquid state deposition method. The liquid state or quasi-liquid state deposition method can be electrophoretic deposition, filtration deposition using the nanotube sheet stack as a filter to capture guest nanoparticles, solution drop casting, ink-jet printing, or a combination thereof.
The step of depositing particle material can include deposition of nanoparticles from a supercritical fluid.
The step of depositing particle material can include profiling distribution of the particle material. The step of profiling the distribution of the particle material can include preferentially positioning the particle material on one side of the sheet platform. The step of preferentially positioning the particle material can result in preferential distribution of the particle material in either the core or shell of the biscrolled yarn. The step of profiling the distribution of the particle material can include preferentially locating the particle material to increase accessibility of light to the particle material. The step of preferentially locating the particle material can allow the biscrolled yarn to be operable for a function of a dye-based electrochemical solar cell, light enabled textile cleaning, destruction of a biological threat, destruction of a chemical threat, or a combination thereof. The particle material can include TiO2.
The step of depositing particle material can include depositing a first type of particle material and a second type of particle material onto the carbon nanotube sheet platform. The first type of particle material can be deposited on a first side of the carbon nanotube sheet platform. The second type of particle material can be deposited on a second side of the carbon nanotube sheet platform.
The step of depositing particle material can include depositing the particle material on two sides of the carbon nanotube sheet platform. The same type of particle material can be deposited on the two sides of a carbon nanotube sheet platform.
The step of depositing the particle material can be performed by a process that patterns the particle material on the carbon nanotube sheet platform. The process that patterns the particle material can be an ink jet printing process.
The particle material can include high surface carbon materials obtained by reaction of carbides. The biscrolled yarn can be operable as a supercapacitor yarn.
In general, in another aspect, the invention features a biscrolled yarn produced by the above method.
In general, in another aspect, the invention features a method that includes selecting a biscrolled yarn. The method further includes using the biscrolled yarn as or in a superconducting yarn, a superconducting yarn application, an energy storage application, an electrode, an electrode application; a catalyst, a catalyst application; a multi-functional textile, a multi-functional textile application, a biomedical application, a shape memory alloy actuator, a shape memory alloy actuator application, a dye-based electrochemical solar cell, light enabled textile cleaning, destruction of a biological threat, destruction of a chemical threat, or a combination thereof.
Implementations of the invention can include one or more of the following features:
The biscrolled yarn can be used as a superconducting yarn. The superconducting yarn can be used for a superconductor application. The biscrolled yarn can include boron and magnesium.
The biscrolled yarn can be used for energy storage applications.
The biscrolled yarn can be used as the electrode material in a supercapacitor.
The biscrolled yarn can be used as the electrode material in a battery.
The biscrolled yarn can be used as a high performance electrode.
The biscrolled yarn can be used for a high performance electrode application.
The biscrolled yarn can be used as a catalyst.
The biscrolled yarn can be used for a catalyst application.
The biscrolled yarn can be used as a multi-functional textile.
The biscrolled yarn can be used for a multi-functional textile application.
The biscrolled yarn can be used for a biomedical application. The biomedical application can be an implantable biometric sensor, a suture, an external biometric sensor, a hemostatic compressive dressing, a hemostatic non-absorbable suture, a drug delivery agent, a 3-dimensional tissue engineering in vitro, a 3-dimensional tissue engineering in vivo, or a combinations thereof.
The biscrolled yarn can be used as a shape memory alloy actuator.
The biscrolled yarn can be used for a shape memory alloy actuator application.
The biscrolled yarn can be used for a dye-based electrochemical solar cell.
The biscrolled yarn can be used for a light enabled textile cleaning.
The biscrolled yarn can be used for destruction of a biological threat.
The biscrolled yarn can be used for destruction of a chemical threat.
In general, in another aspect, the invention features an apparatus operable for using the biscrolled yarn in one of the applications identified in the above method.
The foregoing has outlined rather broadly the features and technical advantages of the invention in order that the detailed description of the invention that follows may be better understood. Additional features and advantages of the invention will be described hereinafter that form the subject of the claims of the invention. It should be appreciated by those skilled in the art that the conception and the specific embodiments disclosed may be readily utilized as a basis for modifying or designing other structures for carrying out the same purposes of the invention. It should also be realized by those skilled in the art that such equivalent constructions do not depart from the spirit and scope of the invention as set forth in the appended claims.
For a more complete understanding of the present invention, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:
The present invention is directed to configure functional nanoparticles, nanofibers, and nanoribbons as the major component of weavable yarns that can perform, for example, as superconductors; battery and fuel cell electrodes; antennas; catalytic convertors; hydrogen storage media, and carriers of biological and biopharmaceutical materials.
Embodiments of the present invention involves twist-based spinning of carbon nanotube sheets (the host) that are overlaid with up to about 99 weight percent of one or more other functional materials (the guest). Whether the overlaid functional material comprises nanoparticles, nanofibers or larger guests, the sheet-derived helices in the resulting yarns contain this functional material in a complex three-dimensionally extended spiral, or a combination of spirals, whose structure critically depends upon twist and geometrical and mechanical parameters. As used herein, these yarns containing host and guest scrolls are referred to as biscrolled yarns. The abbreviation guest@host can be used to designate the biscrolled yarn type.
While provided results extend biscrolling to other host nanofibers, including host nanofibers other than carbon nanotubes, the predominately deployed host scrolls of invention embodiments are from drawable multiwalled carbon nanotube (MWNT) forests made by chemical vapor deposition (CVD). [M. Zhang et al., Science 309, 1215 (2005) (“Zhang 2005”); and the '982 application].
1. Host Materials and Properties
The host material for biscrolling can preferably comprise a network of interconnected nanofibers. Various nanofibers and nanofiber syntheses and fabrication processes can be usefully deployed, as can be mixtures of different nanofiber types and mixtures of nanofibers with other materials.
Undensified and densified carbon nanofiber aerogel sheets provide especially useful host materials of invention embodiments, as have been described in the '982 application and Zhang 2005. The CNT sheets can be in the forms of free-standing sheets or those on a substrate. The substrate can be optionally removed after guest particle deposition. These free-standing sheets and those on a substrate can be either densified or undensified. A particularly convenient method for causing sheet densification is by using surface tension effects due to the process of liquid infiltration and subsequent liquid evaporation.
While various types of carbon nanotube networks can be deployed as host for embodiments of the invention, aerogel sheets will first be described that can be drawn from forests of carbon multiwalled nanotubes (MWNTs), carbon few wall nanotubes (FWNTs), and carbon single wall nanotubes (SWNTs). Unless otherwise indicated, the carbon nanotube host used in described experiments to make biscrolled yarns was synthesized by forest growth, and drawn from a nanotube forest (as described in the '982 application and Zhang 2005).
Carbon nanotube sheets are drawn from forests of approximately parallel nanotubes, overlaid with the guest, and then twist spun using methods, such as like those methods used for making pure carbon nanotube yarns (as described in the '982 application). These as-produced carbon nanotube sheets have remarkable structure and properties that pertain to biscrolling. [Zhang 2005].
While these sheets are aerogels having a carbon network density of ˜1.5 mg/cm3 (close to that of air), these sheets have a specific strength (i.e., strength normalized to density of up to 144 MPa/(g/cm3), which is above that of ultra-high-strength steel plate. Sheet areal density is very low (typically 1 μg/cm2 to 3 μg/cm2), and densification decreases sheet thickness to as low as ˜50 nm and increases sheet specific strength to ˜560 MPa/(g/cm3). [Zhang 2005]. The densified aerogel sheets obtained by the twist-based spinning process provide the strong webs needed for confinement of guest materials in a helically scrolled gallery. The high electrical conductivities for the densified sheets, as well as gallery thicknesses that can approach the smallest dimension of the host particles, means charge collection is facilitated for poorly conducting multifunctional guests. FWNT and SWNT forests can be similarly processed into nanofiber sheets and yarns [X. Zhang et al., Advanced Materials 19, 4189-4201 (2007)], so they can also be used as host for invention embodiments.
In addition to ordinary MWNTs or SWNTs or FWNTs that have circular or approximately circular cross-sections, SWNTs or FWNTs that have sufficiently large diameters to collapse into ribbons are also useful in embodiments of the present invention, both as host and guest.
Such collapsed nanotubes can be provided by chemical vapor deposition in the gas phase and subsequently assembled as oriented sheets having arbitrarily small thicknesses [U.S. Patent Application Publication No. 2005/0006801, published Jan. 13, 2005]. Also, chemical vapor deposition in the gas phase of MWNTs, SWNTs, and FWNTs and subsequent assembly as oriented sheets having arbitrarily small thicknesses has been described. [PCT Int. Pub. No. WO 2009/029341 A2, published Mar. 5, 2009; Y. Li et al., Science 304, 276 (2004)]. These sheet fabrication methods, where the nanotubes (or other nanofibers) are grown by CVD in the gas phase, are useful for producing fabricated host or guest materials for embodiments of the present invention.
It is not required that nanofibers include carbon to be useful for embodiments of the present invention, and various processes are well known in the art for making nanofibers that are not carbon based. Some examples are the growth of superconducting MgB2 nanowires by the reaction of single crystal B nanowires with the vapor of Mg [Y. Wu et al., Advanced Materials 13, 1487 (2001)], the growth of superconducting lead nanowires by the thermal decomposition of lead acetate in ethylene glycol [Y. Wu et al., Nano Letters 3, 1163-1166 (2003) (“Wu 2003”)], and the synthesis of lead nanowires by templating lead within channels in porous membranes or steps on silicon substrates (Wu 2003). The latter methods and various other methods of producing metallic nanowires of types suitable for the practice of invention embodiments are described in Wu 2003, and are elaborated in associated references. Y. Li and coworkers have shown how to make bismuth nanotubes. [N. Li et al., J. Am. Chem. Soc. 123, 9904-9905 (2001)]. While all of these nanofibers can be used as guests in biscrolled yarns, the most useful host nanofibers are those that can be configured as sheets having high specific strength, most preferably above about 50 MPa/(g/cm3). The reason is that high sheet strength enables the effective confinement of guest particles in the scrolled corridors of guest, as well as high strength for the biscrolled yarn.
Insulating or poorly conducting nanofibers are also suitable for embodiments of the present invention as long as these nanofibers form an interconnected network.
Nanofibers that are scrolled on the nanometer scale are also useful for embodiments of the present invention. These nanoscrolls are individual sheets or a thin stack of sheets of a layered material that automatically wind to make a scroll (which is structurally analogous to a jelly roll). Almost any sheet-like material can self-assemble into scrolls—as long as the lateral sheet dimension is sufficiently large that the energy gain from non-covalent binding between layers of the scroll can compensate for the elastic energy cost of forming the scroll.
Since scrolls can be made by simply exfoliating materials that are presently made in high volume at low cost, yarns of embodiments of the present invention can also be made at low cost. Methods of synthesizing nanoscrolls of a host of layered materials are known, and these methods can be used for the practice in embodiments of the present invention. [See L. M. Viculis et al., Science 299, 1361-1361 (2003); Z. L. Wang, Advanced Materials 15, 432-436 (2003); X. D. Wang et al., Advanced Materials 14, 1732 (2002); W. L. Hughes et al., Applied Physics Letters 82, 2886-2888 (2003); J. W. Liu et al., Journal of Physical Chemistry B 107, 6329-6332 (2003); and Y. B. Li et al., Chemical Physics Letters 375, 102-105 (2003)].
Nanofibers that are ribbons of graphene sheets are useful as both guests and hosts in embodiments of the present invention. One preferred method for making the graphene ribbons as high aspect ratio nanofibers is by using the known unzipping of carbon nanotubes. [D. V. Kosynkin et al., Nature 458, 872-826 (2009)].
Nanofibers and particles of organic electronically conducting polymers are useful as guests for embodiments of the present invention. Some examples are rubber elastic polypyrrole, polyaniline, or polythiophene that contain sulfonated poly(styrene-ethylene/butylene-styrene) as a polymeric dopant [Q. Xue et al., Chinese Patent CN 1410486A (2003)] and polyaniline doped with the di-2-butoxy-2-ethoxy-ethyl ester of sulfosuccinic acid [W. Takahima et al., Sensors and Actuators B 99, 601 (2004)]. Examples of useful elastic conducting polymers of polypyrrole and tri-block polyelectrolyte are found in B. Chu et al., Proceedings of the American Chemical Society (2006)].
Biscrolling has been extended to electrically insulating hosts: arrays of hollow SiO2 and Si3N4 nanotubes as described in Example 19. Individual carbon nanotubes and nanotube bundles in free-standing, forest-drawn MWNT sheets were conformably coated with ˜10 nm thickness of SiO2 or Si3N4 produced by plasma-enhanced CVD. Free-standing nanotube sheets were subsequently obtained by removing the carbon nanotube cores (by combustion in air at high temperature or in ozone at room temperature). Both the ceramic coated carbon nanotube sheets and the thereby derived ceramic nanotube sheets can be twist spun to make a yarn, and both can be overlaid with other functional materials to enable the spinning of biscrolled yarns.
As an example, a Si3N4 coated carbon nanotube sheet was biscrolled with 3.7 wt. % Pt nanoparticles (deposited by e-beam evaporation) to make a mechanically robust yarn. Relevant for application of the ceramic-coated carbon nanotubes as host for biscrolled yarn, conformally coating the carbon nanotubes with ˜10 nm thickness of SiO2 does not significantly effect in-plane sheet conductance or the conductance of twisted yarns.
2. Deposition Methods for Guest Materials
The biscrolling methods of embodiments of the present invention involve deposition of the guest material onto (1) a carbon nanotube sheet wedge that results from direct twist-based spinning from a forest or (2) a self-suspended nanotube sheet or sheet stack obtained by sheet draw from a forest. Various host nanofiber web can also be usefully deployed as described in Section 1 above. Deposition of guest materials can be accomplished using all conventional methods that can result in a layered stack of guest and host.
In some embodiments of the present invention, liquid-free deposition is preferably used. Electrostatic deposition of guest onto the nanotube web (i.e., sheet or sheet wedge) from a carrier gas using an electrostatic powder coating gun is fast and controllable—attraction between charged guest particles and the grounded or oppositely charged target web helps in creating a uniformly deposited layer of guest particles over the deposition area (as described in Example 10).
Other liquid-free biscrolling processes involve deposition of the guest material by electron beam evaporation (as described in Example 4), sputtering, chemical vapor deposition (CVD), plasma-enhanced CVD (as described in Example 6), dry powder airbrush deposition (as described in Example 9), or deposition of gas-dispersed guest nanoparticles immediately after their formation by reaction of gases (as described in Example 8).
Liquid state and quasi-liquid-state guest deposition also work, such as electrophoretic deposition (as described Example 2); solution filtration-based deposition using the nanotube sheet stack as a filter to capture guest nanoparticles (as described in Example 3); drop casting (as described in Example 1), and ink-jet printing (as described in Example 7).
Ink jet printing of guest is effective even for self-supported individual nanotube sheets having such low areal density as 1 μg/cm2 and can be conveniently used to provide patterned depositions of one or more guest materials—thereby leading to engineered variation in guest composition along the yarn length and along the yarn diameter.
In the filtration method, (a) solid-state-fabricated nanotube sheet strips were placed on top of filter paper; (b) liquid-dispersed nanoparticles/nanofibers were deposited on top of the nanotube strips by filtration; (c) the filter paper substrate was dissolved by a solvent; and (d) twist-based spinning on the bilayer ribbon stack was accomplished in the liquid bath (as described in Example 11). This method can be practiced for any guest nanomaterials that can be liquid dispersed, such as by ultrasonication.
Other methods can be effectively used for guest deposition on a nanofiber host web. For example, the deposition of platinum nanoparticles from a supercritical fluid on carbon nanotubes has been described for other purposes. [C. H. Yen et al.; Journal of Nanoscience and Nanotechnology 5, 1852-1857 (2005)].
3. Biscrolling Methods
It has been demonstrated that various methods (both liquid-free and liquid state) can be deployed to deposit guest materials onto the host webs. These bilayered ribbons can be subsequently twisted to make yarns. Similarly, it has been shown that guest material can be continuously deposited onto ribbon (or wedge) drawn from a nanotube forest, and can be subsequently twisted to make yarn. All twist-based spinning methods also work for embodiments of the present invention (as described in the '982 application).
Various known methods of twist insertion can be used for introducing twist during spinning into yarns. Such methods include, but are not limited to, ring spinning, mule spinning, cap spinning, open-end spinning, vortex spinning, and false twist spinning technologies. [See E. Oxtoby, Spun Yarn Technology, Butterworths, 1987 and C. A. Lawrence, Fundamentals of Spun Yarn Technology, CRC Press, 2002]. Mule spinning has the disadvantage of being a batch process (spin then wind-on), but has the advantage of not requiring rings or travelers. Twist-based spinning methods, rather than false twist methods, are generally preferred for embodiments of the present invention.
Example 11 shows that the bilayer ribbon stack formed on filter paper can be converted into biscrolled yarn using twist-based spinning in liquid bath. The nanoparticles/nanofibers can be deposited on top of the nanotube strips by various deposition methods (both liquid-free and liquid state); the filter paper substrate is dissolved by a solvent; and twist-based spinning on the bilayer ribbon stack is accomplished in the liquid bath. An advantage of this method is that it can be practiced for any guest nanomaterials. A disadvantage of this method is that eventual removal of the liquid from the biscrolled yarn causes yarn densification, which can distort the shape of the yarn cross-section and lead to irregular spiral corridors for guest containment. Upscale for continuous production of biscrolled yarns for commercial applications would likely favor the absence of liquids for both guest deposition and twist-based spinning.
In some embodiments of the present invention, another preferable method of spinning bilayered ribbons into biscrolled yarns is to employ a direct spinning method that twists as it winds the spun yarn onto a bobbin. The apparatus is outlined schematically in the '982 application. Advantages of this direct spinning method include that the coincidence between the spinning and yarn axes eliminates the spinning balloon and the yarn does not make contact with any surfaces until after the twist is inserted, by which time it has sufficient cohesion to be handled without disruption. The twist level can be set independently of the wind-on by running the wrap and twist drives independently of each other using variable speed motors.
False twist spinning as described in the '982 application, can also be deployed for the embodiments of the present invention.
4. Structure of Biscrolled Yarns
The biscrolled yarns provide fascinating structural complexity and diversity (
Different yarn topologies were observed for different spinning conditions and resulting structural parameters (like the “wedge angle”, the total apex angle where the wedge converges to yarn, the width of the spinning wedge base, and the symmetry of stresses applied during spinning). These observed topologies (see
“Archimedean” means that a sheet edge is buried deep in a scroll.
“Archimedean pair” means that the opposite sheet edges are buried in different interconnected Archimedean scrolls.
For an ideal “Fermat scroll,” sheet edges are exterior to the scroll, though asymmetric formation of a Fermat scroll as a result of asymmetric applied stress on the spinning wedge can drag one sheet edge to an internal location. If this sheet edge is fully displaced to scroll center, such unbalanced Fermat scroll becomes an Archimedean scroll, as schematically illustrated in
These designations provide a starting point for understanding the more complex and interesting observed cross-sectional structures of biscrolled yarns.
In
The results of this embodiment of the present invention indicate differences that arise between continuous twist-based spinning from a nanotube forest sidewall (via a twist-produced spinning wedge) and formation of yarn by twisting a preformed rectangular nanotube sheet between end supports.
In ideal Fermat biscrolling (or scrolling for a guest-free yarn), the twist process starts from the center of a spinning wedge, as shown in
Increasing the wedge angle and the spinning wedge base width introduces pleats (i.e., folds) for all scroll types, whose amplitude increases during convergence of the spinning wedge to yarn, except near wedge apex where twist can partially relieve width-direction strain. The origin of these pleats is the same as for an initially flat hanging curtain, with fixed top-end supports, that is bunched together at the bottom to form a wedge—pleats form with amplitude that increases from unstrained top to bunched bottom, so as to fit the initial sheet width into a decreasing wedge width (
For twist-based spinning directly from a nanotube forest, the wedge angle is determined by relative rates of draw and twist.
Spinning a given length of rectangular sheet strip under constant load is more complicated than dynamically stabilized continuous spinning from a forest-derived wedge. Twist of a rectangular sheet between end supports starts with sheet folding that is origami-like, except that plastic deformation of sheet area occurs, which repeats during subsequent rotations to form a new system of folds until a spinning wedge is obtained. The wedge angle then increases with increasing twist.
The above edge-generated scrolls having opposite handedness, which are either Archimedean scrolls or highly unbalanced Fermat scrolls, are ultimately twisted together like for a two ply yarn.
On the other hand, applying sufficiently unequal loads to opposite sides of the bilayered sheet results in observation of only one Archimedean scroll, and the surface of the yarn shows only a single side of the original bilayer-stack. The side forming the external surface of this yarn can be changed by changing the side of the sheet that is most stressed or by changing from clockwise or counterclockwise twist.
The following results were observed: While twisting a bilayered rectangular sheet between rigid end supports resulted in either single Archimedean or dual Archimedean scrolls (depending, respectively, on whether asymmetric or symmetric forces were applied during twist), Fermat scrolling had not been observed for these spinning conditions. However, if one end of the rectangular sheet was attached to a suitable non-rigid support, like a forest side-wall, the spinning wedge attached to this support, which arises during twist, can produce a Fermat scroll (for symmetric spinning) or a single Archimedean scroll, as well as states between these extremes (but not a dual Archimedean scroll). Continuous wedge-based spinning from a forest sidewall also produced these types of scrolls.
As shown in
One partial answer of this question for the most investigated structure (
Another likely partial answer is in the initial formation of low-density, biscrolled core structure, nanotube scroll layers are unable to easily glide with respect to neighboring guest layers during further twist that results in the final densified yarn structure. Since the sheet is very weak orthogonal to the nanotube orientation direction, resulting partial local separation of the nanotubes in this orthogonal direction can produce holes in the scrolled sheets, which appear as occasional breaks in the scroll for any given cross-section. Additional irregularity likely results from the observed pleating caused by non-uniform stress across the spinning wedge, non-uniformities in guest particles size and their aggregation within the guest layer, differences in the stresses applied to opposite sides of the spinning wedge, and yarn shape distortion caused by twist in a liquid bath and the resulting yarn densification caused by surface tension during subsequent evaporation of the liquid.
When the uniform coating of guest on one side of a sheet or sheet wedge was replaced with a coating of guest that was only on fraction of the sheet surface (such as adjacent to one sheet edge) and twist was applied asymmetrically so that formation of a single Archimedean scroll was macroscopically observed, a core-shell structure was observed where the guest was only in the corridors of the core or shell (depending in part on the wedge half that was preferentially stressed). This is illustrated in the yarn structure shown in
This ability to profile guest distribution in the biscrolled fiber is very useful. For example, preferential location of TiO2 on the shell can increase accessibility of light to functional guests, for example for the application of TiO2 biscrolled yarns for dye-based electrochemical solar cells and for the use of TiO2 guest in biscrolled yarns for light enabled textile cleaning or destruction of biological or chemical threats.
The capabilities of the biscrolling process of the present invention for achieving needed performance is additionally increased by the convenient ability to deposit the same or different guest on one or both sides of the host web (sheet or spinning wedge), and to accomplish this in a convenient patterned manner, such as by ink jet printing.
5. Mechanical Properties of Biscrolled Yarns
Long carbon nanotube length can be important for achieving useful mechanical properties of biscrolled yarns and effective confinement of guest materials. An individual nanotube (presently ˜400 μm long) can wrap though many spiral revolutions for thin yarns (which can have diameters below 10 μm). Also, extensive nanotube bundling and self-weaving within biscrolled sheets though bundle forking and recombination with other forks can increase the ability of scrolled nanotube sheets to confine a guest.
TiO2@MWNT biscrolled yarns of the present invention were prepared using the filtration method, as well as by other deposition methods. In the filtration method TiO2 powder was suspended in 1% SDS solution and filtration-deposited onto a two-layer CNT sheet stack that was placed on a cellulose nitrate membrane. Another layer of CNT sheet was then overlaid on top of the TiO2 layer to confine the guest material. The rectangular TiO2@MWNT sheet stack (6 mm×30 mm) was cut from the membrane and immersed in acetone to dissolve the membrane. The free standing TiO2@MWNT sheet stack was then twisted along its length axis using a magnetic stirrer located under the acetone bath, which coupled to a steel rod that is glued to the sheet stack.
Biscrolled TiO2@MWNT yarns with guest weight concentrations of 0%, 24%, 62%, and 93% were prepared using the above procedure, and then tested for mechanical properties.
The mass of these biscrolled yarns were measured using a microbalance. Specific mechanical properties were determined from measurements of force versus strain at 4%/minute engineering strain rate using a tensile test apparatus (Favimat 37617).
This suggests that the guest component (TiO2) did not contribute to the mechanical strength of the biscrolled TiO2@MWNT yarn, which is expected because of the powder nature of the TiO2.
More surprisingly, even high concentrations of TiO2 did not dramatically degrade the nanotube contribution to biscrolled yarn specific strength. This is indicated in
6. Applications of Biscrolled Yarns
The broad applications potential of biscrolling is suggested by the following described demonstrations in which scrolled nanotube sheets confined the following functional materials in the spiral corridors of yarns: superconductors, graphene ribbons, TiO2 for destruction of biological threats, high performance battery redox materials, and biological agents. These demonstrations indicate retention or acquisition of guest functionality, and the ability of small amounts of nanotubes to contain massive amounts of functional materials in yarn sacks. Because of the very high thermal and chemical stability of the carbon nanotube containers for biscrolled nanotube yarns, extreme thermal and non-oxidizing chemical environments can be used after yarn fabrication to convert guest components to desired functional components.
(a) Biscrolled Yarns for Superconductor Application
The biscrolling process of embodiments of the present invention enables construction of superconducting yarns. It has been demonstrated that superconducting yarn can be obtained by biscrolling a mixture of boron and magnesium guest powders with a three layer MWNT sheet strip host using filtration-based guest precursor deposition on a two layer sheet stack, overcoating the guest powders with a third MWNT sheet strip, and inserting twist in a liquid (as described in Example 12).
One weight percent carbon nanotubes host held 99 wt % of these precursors for both twist insertion and later processing to produce the superconductor, despite the large diameter of the used B and Mg guest particles (<39 μm, which are like giant boulders compared with the ˜50 nm thickness of a densified nanotube sheet). Conversion of this guest material to superconducting MgB2 by exposure of the biscrolled yarn to the highly corrosive vapor of magnesium at high temperature (750° C. for 30 minutes in argon) indicated the ability of the nanotube host to function as yarn sacks in chemical and thermal environments where most materials degrade.
Four-probe electrical conductivity measurements versus temperature showed that the biscrolled yarn was superconducting, with a critical temperature (Tc) at the expected temperature (J. Nagamatsu et al., Nature 410, 63 (2001)) of about 39 K. This demonstration appears to be important because of the need for superconducting cables and the convenient applicability of biscrolling in the search for new bulk superconductors—providing a useful yarn configuration, accessibility of the superconducting guest to chemical and electrochemical doping, and the ability to easily include multiple nanoparticle/nanofiber components as guests that are in intimate contact for both achievement and modification of superconductivity through proximity effects and increase of dimensionality.
(b) Biscrolled Yarns for Energy Storage Application: High Performance Battery Electrodes
The use of biscrolling to produce yarns that function as high performance battery electrodes might have special applications importance, since highly conducting scrolled carbon nanotube sheets can hold in nanoscale proximity poorly conducting guest redox materials that show high energy storage and high rate capabilities.
In some embodiments of the present invention, electrode material with at least two components was prepared, wherein the first component was a carbon nanotube sheet that provided electrical conductivity as well as mechanical support by constraining the second component, which contributed to the incorporation and release of ions like lithium ions. The electrode was prepared with the step of providing the first component, wherein the first component included a carbon-nanotubes sheet or sheet stacks of a variable number of carbon nanotubes sheet layers drawn from a forest or prepared by other method, and adding a second component with the composition LixMyPO4 and/or C@LixMyPO4 with M=Ti, V, Cr, Mn, Fe, Co, Ni dispersed in an aqueous solution. An additional layer of carbon nanotubes can optionally be placed on top of the second component.
In another step, twisting of the composite with 50-99 wt. % active material on top of the carbon nanotube sheet is performed yielding a self standing yarn-like electrode.
Example 14 demonstrates a method wherein biscrolled LiFePO4@MWNT yarns can be fabricated for lithium battery application. The electrodes including LiFePO4@MWNT were prepared by either wet filtration or dry powder deposition methods. For both approaches, the biscrolled LiFePO4@MWNT yarns were then thermally treated at 600° C. for 6 hours in Argon flow environment. The specific capacities have been calculated for the total weight of the electrode. The total weight percentage of the active material in the electrode including current collector can be larger than 90% (typical loading in conventional LiFePO4 electrodes is 70%). The charge and discharge curves at rates of 0.1 C-10 C showed that the material can deliver high specific capacities, about 115 mAh/g of total electrode, without addition of binder (typically 7.5 wt %. PVDF), and with just 1-5% wt. of CNT (compared with 10-15 wt %. of carbon black in conventional electrodes) and without the presence of metallic current collector (usually Al foil making an extra 20 wt. % contribution to the total cathode weight).
In some embodiments of the present invention, graphene@MWNT biscrolled material can be used for energy storage applications as the main part of an electrode material for supercapacitors and batteries. The high achievable gravimetric surface area for such biscrolled yarns is critically important for supercapacitor applications, and can provide high discharge rates for battery electrode applications.
Graphene nanoribbons@MWNT yarns produced as described in Example 13 can be used as anodes in lithium batteries. Because of the high surface area accessible in graphene nanoribbons for the intercalation of lithium ions and corner/edges that contribute to higher storage capacities, higher performance than that for the ordinary graphite (LiC6: 372 mA h g−1) have been reported. [E. Yoo et al., “Large reversible Li storage of graphene nanosheet families for use in rechargeable lithium ion batteries”, Nanoletters 8, 2277-2282 (2008); S. M. Paek et al., “Enhanced Cyclic performance and Lithium storage capacity of SnO2/graphene nanoporous electrodes with three-dimensionally delaminated flexible structure”, Nano Lett. 9, 72-75 (2009)].
In some embodiments of the present invention (such as, for instance, a lithium ion battery electrode), methods are provided for producing the electrode, as well as the whole battery (by combining two biscrolled electrodes, anode and cathode, in the shape of, for example, a two ply yarn).
In some embodiments of the present invention, a device was obtained in which each electrode was prepared with a first step of biscrolling graphene nanoribbons or other material @MWNT as anode and biscrolling LixMyPO4 or other material@MWNTs as cathode and a second step of positioning them close to each other, yet electronically insulated by a separator, and adding the electrolyte to form yarn battery.
(c) Biscrolled Yarns for Energy Storage Application: Supercapacitors
In some embodiments of the present invention, biscrolled nanotube sheets can be used to confine high-surface area materials for supercapacitor application. The electrode of biscrolled yarn with at least two components was prepared. The first component was a carbon nanotube sheet that provided electrical conductivity, as well as mechanical support, by constraining the second (guest) component, which had a high surface area for incorporation of the active species from the electrolyte to form an electrochemical double layer by charge injection.
The guest component can be graphene plates or graphene nanoribbons obtained by chemical unzipping CNTs [D. V. Kosynkin et al., Nature 458, 872-876 (2009)]. Suitable additional methods of fabricating graphene nanoribbons by CNT unzipping exist. High-quality graphene nanoribbons exhibiting low defect concentration and correspondingly improved electrical conductivity are obtained by using plasma etching of MWNTs [L. Jiao et al., Nature 458, 877-880 (2009)] or by using a combination a gas-phase oxidation step with mechanical sonication in organic solvents for MWNTs [L. Jiao et al., Nature Nanotechnology 5, 321-325 (2010)].
Another type of particularly useful guest material for biscrolled supercapacitor yarns is provided by the high surface area carbons obtained by reaction of carbides [J. Chmiola et al., Science 313, 1760-1763 (2006); Y. Gogotsi et al., Nature Materials 2, 591-594 (2003)].
Biscrolled graphene oxide nanoribbons or graphene nanoribbon yarns reduced chemically or thermally can be used as electrodes of supercapacitors. In one embodiment of the present invention, 2 wt % MWNTs host confined 98 wt % guest nanofibers were synthesized by unzipping solution-dispersed MWNTs using KMnO4 in aqueous H2SO4 as oxidant (as described in Example 13).
Based on the complete disappearance of the ˜3.4 Å x-ray diffraction peak for MWNTs after oxidation with a massive amount of KMnO4 (˜850 wt %, relative to MWNT weight), the guest nanofibers were largely graphene. Graphene nanofibers (obtained by reduction of the graphene oxide nanofibers) or the precursor graphene oxide nanofibers were deposited, for example, on two stacked layers of forest-drawn nanotube sheet that were supported by a cellulose nitrate filter paper. Filtration-based deposition of the solution-dispersed graphene or graphene oxide nanofibers on top of these host MWNT sheets led to a host-guest sheet stack, which (cut into ribbon form) could be twist spun in an acetone bath that dissolved the filter paper before the start of spinning.
Other highly conducting and high-surface area materials can also be useful for embodiments of the present invention. These materials can be nanoparticles, nanoscrolls, nanoribbons exhibiting good conductivity and high surface area for energy storage. For example, graphene flakes from simple exfoliation of graphite or any other sheet like material that could be scrolled are useful for being the guest material into the host MWNT conducting network.
Nanoparticles and nanofibers of electronically conducting organic polymers are also especially useful for embodiments of the present invention. Electron-acceptor doped nanofibers, nanoparticles and nanoscrolls made of polypyrrole, polyaniline and polythiophene are also especially useful for embodiments of the present invention for providing good flexibility, high output power and high energy storage capability.
Electrical energy storage of these biscrolled electrodes can be performed by using aqueous, organic, and ionic liquids as an electrolyte. In some embodiments of the present invention, an all-solid-state biscrolled yarn supercapacitor can be fabricated by plying two single biscrolled yarns as electrodes. Each biscrolled yarn can be coated with a gel-like solid electrolyte (such as phosphoric acid containing polyvinyl alcohol) to obtain a fiber shaped supercapacitor, like previously done for yarns made by coagulation-based solution processing [A. B. Dalton et al., Nature, 423, 703, (2003)]. These biscrolled supercapacitors yarns can be used in a wide range of energy capture and storage applications and are used either by themselves as the primary power source or in combination with batteries or fuel cells. These batteries and fuel cells can be also other biscrolled guest materials containing battery materials, like lithium iron phosphate, and electro-catalyst materials, like nitrogen-doped carbon nanotubes (see following section (d)).
(d) Biscrolled Yarns for Application as Catalytic Oxygen Electrodes
In some embodiments of the present invention, N-doped CNTs (CNx) are used to make CNx@MWNT biscrolled yarns that function catalytically as an oxygen electrode to provide improved performance for such applications as fuel cells. In Example 15, the electrochemical performance of these CNx@MWNT biscrolled yarns in the oxygen reduction reaction (ORR) was tested by cyclic voltammetry (CV) in a three-electrode cell. Similar to the reported in literature [S. Kundu, et al.; J. Phys. Chem C 113, 14302-14310 (2009) (“Kundu 2009”)] for conventional electrode geometry, a displacement to more positive potentials (˜0.3V) was found for the onset of the ORR for the CNx@MWNT yarns when compared to the control of MWNT@CNT biscrolled yarn electrode.
As the nitrogen sites in CNx are responsible of this displacement in the reaction [Kundu 2009], this simple test verified the accessibility of the biscrolled CNx material to the oxygen in the surrounding electrolyte and the retention of catalytic activity. The difference in the absolute values of potential that were found compared with the result in Kundu 2009 is explained in early studies reporting the shift of the ORR peak potential by ±30 mV per 1 at % of N incorporated into the carbon lattice [Matheson et al., J. Phys. Chem B 109, 4707-4716 (2005)]. However, later studies suggested that more than the total nitrogen percentage in the structure, the amount of pyridinic nitrogen is the one responsible for the high activity with respect to ORR. [Kundu 2009; Y Shao, Applied Catalysis B: Enviromental, 79, 89-99 (2008)].
These biscrolled CNx@MWNT yarns can be used for proton exchange membrane fuel cells (PEMFCs) or other electrochemical applications. The selection of a specific material for biscrolling makes this method usable for tuning the properties of flexible electrodes for specific electrochemical systems or for use in new kinds of galvanic cells (batteries).
(e) Biscrolled Yarns for Additional Applications as Catalyst
Biscrolling for confinement of catalyst particles in yarns that can be woven into textiles is another demonstrated application. Biscrolled yarn textiles can be deployed for maintaining high volumetric concentrations of catalyst in trapped, but highly active state, for liquid or gaseous state catalysis.
Example 20 demonstrates that biscrolled yarns with confined platinum black guest particles show catalytic activity by fast decomposition of hydrogen peroxide solution into water and oxygen. Biscrolled Pt nanoparticles@MWNT yarns were obtained by two methods, a) e-beam deposition of Pt on MWNT sheets placed over a cellulose nitrate substrate, and b) by electrostatic deposition of Pt black nanoparticles directly on MWNT sheets. The high catalytic response of these Pt nanoparticles@MWNTs was shown by submerging the biscrolled yarn into a H2O2 solution (30 v %). A high decomposition rate of the H2O2 (into H2O and O2) and increase in temperature of the solution was observed. Furthermore, high performance in this application has been demonstrated for Pt guest in scrolled MWNT sheets in which the MWNTs and MWNT bundles are coated with nano-size depositions of Si3N4 or SiO2, as well as for biscrolled Si3N4 and SiO2 sheet hosts (as described in Example 19).
(f) Application in Multi-Functional Textiles
The use of biscrolling for making yarns for textiles that are self-cleaning or protective against chemical or biological threats has also been demonstrated. For possible uses as yarns for woven textiles that serve as flexible electrodes, other functional materials were biscrolled into yarn using solid-state-drawn MWNT host. These included biscrolled yarn containing catalytic Pt for fuel cell electrodes and other catalysis needs, metal oxide powders for battery electrodes, and TiO2 for Graetzel solar cells and self-cleaning clothing.
Example 16 demonstrates biscrolled yarns of TiO2 for photocatalytic application. The most widely used photocatalyst is TiO2 due to its high photocatalytic activity (converting photon energy into chemical energy by absorbing light), high stability and non-toxicity. The catalyzed photolysis of TiO2 under ultraviolet (UV) irradiation generates electron-hole pairs that react with water to produce active oxygen and hydroxyl radicals that reacts with organic contaminants.
To test the catalyzed photolysis of the TiO2@MWNT biscrolled yarn, a piece of cotton fabric was dyed by soaking in a solution of the methylene blue, and then dried in a vacuum oven overnight. A biscrolled TiO2@MWNT yarn was then laid overtop the dyed cotton fabric and placed under a mercury UV lamp that provided 365 nm radiation. The intensity of the lamp was 64 W/m2. It was noticed that after 4 hours of irradiation, a bleaching effect was visible even on the reverse side of the dyed fabric, which was neither in direct contact with the biscrolled yarn or exposed to the UV light.
The robustness of TiO2@MWNT yarns for retaining TiO2 during cleaning of textiles (for example using a washing machine) was also investigated using a model system. The robustness test was done on a biscrolled TiO2@MWNT yarn in which the concentration of TiO2 was nearly 93%. The weight of the yarn before washing was measured. The yarn was then immersed in 1% wt. SDS suspension, which was placed on a hot plate with a magnetic stirrer. The yarn was washed by stirring for 3 hours at 80° C. Then the yarn was taken out of the suspension and dried in vacuum overnight. The weight of the yarn was again measured. The percentage of weight loss of TiO2 was less than 2%.
As shown in Example 16 and Example 17, the biscrolled TiO2@MWNT yarns have robust mechanical properties and chemical stability, which are useful properties for exploiting the photo catalytic activity of TiO2 for textile applications.
(g) Application in Biomedical Area
Example 24 shows the use of biscrolling to confine high concentrations of biologically active agents as guests in yarns that are sufficiently strong to be sewn into muscle. Biscrolled yarns containing up to 95 wt. % biologically active guests were made for such potentials applications as removable sutures and compressive wound dressings.
Despite a high guest loading level of 83.6 wt. % and a small yarn diameter of 53.7 μm (which might reduce scarring), this biscrolled yarn provided useful mechanical performance as a suture.
Initial tests involved threading this biscrolled yarn into a ⅜ circle cutting edge suture needle and subsequent suturing of subcutaneous and cutaneous layers of a full thickness laceration that penetrated into subdermal layers of the foot of a butchered pig (purchased at a grocery store). Suture mechanical properties enabled convenient application of the interrupting suture technique for subcutaneous and cutaneous skin layers, as well as the horizontal mattress suture technique for cutaneous skin in areas of high tension and movement (where a single biscrolled yarn is stitched parallel to the wound edges). These sutures were easily quadruply knotted for closure using square knots.
Because of high strength, flexibility, porosity, and small achievable yarn diameters, biscrolling diverse powders can be used to provide biomedical functions, assuming that either carbon nanotubes are eventually found safe or this host is replaced by other host nanofibers. Biscrolling neuronal growth agents are useful for providing nanotube electronic interconnections to targeted nerve cell types, especially since nerve degeneration at metal wire contacts is a problem and since neurons appear to propagate normally on forest-drawn nanotube yarns and sheets.
Other applicable biomedical uses range from biometric sensors (implantable or external), hemostatic compressive dressings, hemostatic non-absorbable sutures (for fully heparinized patients or patients with multiple arterial anastomoses), drug delivery agents, and 3-dimensional tissue engineering in vitro and in vivo.
(h) Application in Shape Memory Alloy Actuator
When it is favorable to imbue the properties of a biscrolled guest@CNT composite to a core structure, or achieve a consistent Archimedean cross-sectional topology, guest@CNT material can be helically wrapped around a core, such as a fiber or a wire. This is achieved either by directly wrapping the sheet composite around the core, or by rotating the core in order to continuously draw MWNT sheet from CNT forest.
Such a configuration is particularly useful for fuel-driven actuation of shape memory actuators (SMA), wherein catalyst powder must be confined within thermal contact of the SMA surface.
As described in Example 22, biscrolling of catalytic Pt-black@MWNT sheet around nickel-titanium alloy SMA wires allows shape memory actuation, typically driven by electric current, to be powered by high energy density fuels such as hydrogen gas or methanol vapors. The Pt-black@MWNT sheet structure is ideal for this application as it enables good fuel-catalyst interaction, while providing a thermally conductive, flexible and temperature-stable structure for platinum black confinement.
This Example 1 demonstrates the biscrolling process using solution deposition of guest MWNTs on host CNT sheets that are orthogonal. Though the sheets comprise MWNTs, the sheet nanofibers of the host are called CNTs in this example in order to avoid confusion with the solution deposited guest MWNTs. As illustrated in
To increase the thickness of the guest MWNT layer, several layers of guest MWNTs were deposited. Solvent was evaporated before solution casting the next layer. After the solution deposition, a bilayer ribbon of MWNT guest and CNT sheet host was formed. To form the fiber, the ribbon was scrolled along the long sheet axis and twisted into a fiber, as shown in
This Example 2 describes the biscrolling process using electrophoretic deposition (EPD), which can deposit a large variety of guest materials onto the solid-state-spun CNT sheets.
Utilizing the mechanical strength of the sheet, this process makes possible the fabrication of free-standing sheets or ribbons mostly consisting of nanoparticles that cannot be easily assembled into yarns. The technology also enables a continuous process of producing such yarns incorporating nanoparticles.
Substrates of borosilicate glass and poly(ethylene terephthalate) were coated with a 50-nm layer of aluminium or titanium by e-beam deposition. As illustrated in
The electrophoretic deposition 603 of SWNT transparent films took only a few seconds. A layer of evaporated metal acts (together with the host MWNT sheets) as an electrode during the deposition. The coated substrate was connected to the positive electrode. Both, the SWNTs wrapped with surfactant and the SWNTs functionalized with —COOH groups acquired a negative charge in water and were attracted to the positive electrode.
During the electrophoretic process, oxygen is also generated in the positive electrode. The aluminium or titanium coating was quickly oxidized to Al2O3 or TiO2 and the metallic film over the substrate became transparent. The oxidation of the metallic film also absorbed the oxygen that was produced by the electrolysis of water. Once the oxidation of the metallic layer was complete, the electrical current through the cell stabilized to a very low value, interrupting the SWNT deposition.
After deposition, the substrate with the SWNTs deposited on the MWNT sheet was removed from the electrolyte and dried. Then, the substrate was washed with a proper solvent to remove any remaining surfactant.
The MWNT sheet coated with SWNTs formed a bilayered structure and could be easily separated from the substrate by immersing the substrate in a proper solvent. After separation from the substrate, the free-standing bilayered ribbon maintained its shape in solvent, and can therefore be collected as a sheet on another substrate as shown in
As shown in
From optical density measurement, the deposited SWNT layer accounted for 80 wt % of the total mass in the bilayered structure. The bilayered CNT sheet had an areal density of 10 μg/cm2, as compared with 2.2 μg/cm2 for the MWNT sheets. The specific conductivity of the SWNT/MWNT bilayered structure increased from 329 S·cm2/g for the MWNT sheets (two in stack) to 1263 S·cm2/g with SWNT addition, a factor of ˜4.
This Example 3 describes the biscrolling process using filtration-based deposition. In this process, the guest material to be deposited was dispersed in a suitable liquid medium using ultrasonication. Surfactants are sometimes used as the dispersing medium apart from the most commonly used mediums viz. de-ionized water and isopropanol. The filter for filtration deposition was a stack of MWNT sheets placed on a cellulose nitrate filtration membrane (Whatman, pore size was 0.45 μm, approximate thickness of 120 micrometers). Multiple layers of the MWNT sheets, typically one to three layers, were placed on the filter membrane, and then densified by wetting with isopropanolError! Reference source not found. The suspension of the guest material was then deposited onto the MWNT sheets/membrane through filtration. The filtration deposition of well dispersed suspensions formed a homogenous layer of the guest material on top of the membrane. After the filtration, the guest/MWNTsheet/filter tri-layer stack was then dried. In some cases, an extra layer of MWNT sheet was applied on top of the deposited guest material in case that the guest material had poor adhesion to the MWNT sheets. After completely drying the membrane, strips of the membrane were cut along the length of the MWNT sheets for yarn spinning as described in Example 11.
The biscrolling process of filtration-deposition is illustrated in
A modified filtration method was developed to deposit the guest material with strip pattern on the MWNT sheets. Strips of Kapton tape were affixed on the frit of Erlenmeyer flask. As described above, layers of MWNT sheets were placed on the cellulose nitrate membrane. The membrane was then placed on top of the frit in such a way that the tape strips below the membrane blocked the vacuum in desired areas of the membrane. The suspension was deposited onto the area that was open to the vacuum. This led to the formation of a strip pattern of the guest material on the CNT sheet stack.
This Example 4 demonstrates the biscrolling process using electron beam evaporation (EBE) of guest, which can deposit a large variety of metals and ceramics onto the solid-state-spun CNT sheets. In this example, deposition of Ti, Cu, Al, Al2O3, and Pt onto CNT sheets was demonstrated.
For EBE deposition, one or several CNT sheets (either free standing or placed over cellulose nitrate membrane) of different shapes were prepared. The thicknesses of the EBE-deposited layers of titanium (Ti), copper (Cu), aluminum (Al) and aluminum oxide (Al2O3) ranged from 1 to 25 nm. The coated sheet stack on cellulose nitrate membranes were then submerged in acetone (CH3COCH3) that dissolved the cellulose nitrate membrane. Alternatively, any other proper solvent that dissolves the cellulose nitrate membrane could be used.
One end of the stack was attached to a ferromagnetic wire rod while the other end was attached to thin metal rod crossbar. The stack was then suspended by the crossbar into a beaker of acetone until the cellulose nitrate filter membrane completely dissolved and only the powder/MWNT sheet stack remained. Twist was then initiated via a magnetic stirrer plate until the biscrolled yarn reached uniform diameter. The resulting biscrolled yarn was then washed with deionized water and allowed to air-dry.
This Example 5 demonstrates biscrolling process to continuously produce biscrolled yarns of SWNTs deposited by air spray process onto forest-drawn MWNT sheets.
Suspension of SWNTs dispersed in methanol, acetone, or any other compatible solvents was sprayed using an air-gun onto the free-standing MWNT sheet (or ribbon or wedge) that was continuously drawn from the forest. The MWNT sheet can be heated during the spraying process in order to aid the evaporation of the solvent used for the SWNT suspension. The bilayered SWNTs@MWNT ribbon can be simultaneously twisted into biscrolled yarn.
This Example 6 demonstrates yarn formation using plasma enhanced chemical vapor deposition (PECVD), which can deposit a large variety of materials onto the solid-state-spun CNT sheets. In this Example 6, deposition of SiO2 and Si3N4 onto CNT sheets was demonstrated.
For SiO2 deposition by PECVD, one or several free-standing CNT sheets were heated up to 200° C. in inert atmosphere in the plasma reactor chamber, and then exposed to plasma generated by using RF power in the presence of a mixture of silane (SiH4) and nitrous oxide (N2O). This procedure generated a homogenous amorphous SiO2 coating around individual nanotubes and individual nanotube bundles. After the plasma deposition, the SiO2/CNT sheets were placed over cellulose nitrate membrane and twisted into yarn as described in Example 11. See
For Si3N4 deposition by PECVD, one or several free-standing CNT sheets were heated up to 250° C. in N2 inert atmosphere in the plasma reactor chamber, and then applied to plasma using RF power in the presence of a mixture of silane (SiH4) and ammonia (NH3). This procedure generated a homogenous Si3N4 coating around individual nanotubes and individual nanotube bundles. See
This Example 7 demonstrates the biscrolling process using guest deposition by ink jet printing. Using conventional ink jet printing technology, suspended powder material serves as a “printing ink” that can be continuously deposited as guest onto an aerogel single-layer MWNT sheet prior to or during twist insertion to produce biscrolled yarn. Since the free-standing CNT aerogel has very low areal and volumetric density it is easily damaged. Hence, ink jet printing provides an excellent way of depositing material onto the spinning wedge without disrupting the spinning process. Patterning of the deposited layer is also possible using this technology. In this demonstration, a Canon Ip 1800 Standard Ink-Jet Printer was modified as follows:
For ink jet deposition onto MWNT sheet, a MWNT sheet ˜11 cm long by 3 cm wide was suspended between two end supports comprised of 2 fixed position glass rods attached to a common base.
This Example 8 demonstrates the biscrolling process using aerosol-based deposition of the guest, where the aerosol was produced by gas phase reaction immediately prior to deposition on a MWNT host. In this approach, multiple layers of nondensified CNT sheets were placed on a quartz frame that was then placed close to a hot plate to avoid densification during the deposition process. The guest material deposited on these sheets was in the aerosol phase.
This Example 9 demonstrates a biscrolling process using deposition of the guest on a MWNT sheet stack using an airbrush. In conventional use, the airbrush is used as a mini-sandblaster and/or an etching tool. In the present application the airbrush delivers a dry guest powder to a host MWNT sheet, for the purpose of forming bilayer sheet strip stacks used for biscrolling. A Paasche brand airbrush AEC Air Eraser (steel tip with carbide insert) was used, together with a X-Air Compressor with regulator (Model #80-8, operated at ˜6-8 psi). The particulate size of deposited guest materials ranged from 0.1 to 10 μm in diameter, depending upon the specific guest material.
This Example 10 demonstrates the biscrolling process using electrostatic deposition of guest nano/micro particles onto the nanotube web (i.e., a sheet or sheet wedge) from a carrier gas (conventionally air or nitrogen) using a conventional electrostatic powder gun. A commercially available powder coating gun was used wherein the particles were charged with 15 KV DC and 15 μA. Controlling the distance between gun tip and the target web (as well as the carrier gas pressure) can be used to provide desired deposition conditions.
This approach was fast and controllable—attraction between charged guest particles and the grounded or oppositely charged target web helped create a uniformly deposited layer of guest particles over the deposition area. Highly charged particles repulsed each other, aiding de-agglomeration and eventually providing a well dispersed particles layer on the nanotube sheet surface.
This Example 11 demonstrates converting a rectangular bilayered ribbon into biscrolled yarn by twisting in liquid. As shown in the
For cellulose nitrate membrane filters, the dissolution of the filtration membrane usually took about 1 to about 5 minutes in acetone. The beaker was then placed onto a magnetic stirrer. Using magnetic force between the stirrer and the steel rod attached to the bilayered ribbon, twist was introduced, converting the ribbon into a biscrolled yarn, as shown in the images of
This method allowed controlling of twist speed without applying large axial stress to the CNT sheet. As the sheet was twisted into a yarn, it got shorter. After the desired number of twists was applied to the CNT ribbon with the guest material, the process was stopped and the yarn was removed from the acetone bath. To assure the complete removal of the membrane, the biscrolled yarn was immersed in a fresh acetone bath for another 30 minutes.
This Example 12 demonstrates producing superconducting yarn of MgB2@MWNT using the biscrolling method. Superconducting yarns were produced by depositing a layer of MgB2 precursors on the CNT sheet. The Mg and B powders (Alfa Aesar) were uniformly dispersed in isopropanol by ultrasonication and then were deposited onto MWNT sheet using filtration deposition described in Example 3.
The MgB2@MWNT ribbon was twisted into a biscrolled yarn, as described in Example 11. The CNT sheet was robust enough to hold Mg and B powders producing yarns that contain 99 wt % of Mg and B powder. After twisting, the yarn was sintered at 750° C. for 30 min in an argon atmosphere with excess of Mg vapor, so that magnesium and boron reacts forming the MgB2 superconductive phase.
For DC electrical measurements, the yarn sample was mounted to a four-point probe fixture using silver paint (Dotite D-550). The temperature dependence of yarn electrical resistance was recorded in the temperature range from about 4.2K to about 300K using a home-made test probe. Resistance values were measured with a Keithley 2602 Sourcemeter. The superconducting transition of the electrical resistance is shown in
This Example 13 demonstrates making biscrolled graphene nanoribbon yarns for energy storage and other applications. These results are obtained by biscrolling graphene nanoribbon guest (or the precursor graphene oxide nanoribbons) in a MWNT sheet host by using filtration-based deposition of these guests on MWNT sheets.
First, graphene nanoribbons were obtained by cutting about 300 μm long MWNTs along their longitudinal axes. These MWNTS were obtained by chemical vapor deposition of acetylene gas on top of a catalytic bed of iron nanoparticles (<10 nm). [See Zhang 2005, at 1215-1219].
The cutting process (unzipping) was chemically driven by an oxidizing system consisting of KMnO1 and H2SO4 at the temperature of 55-70° C. [D. V. Kosinkyn et al., Nature 458, 872-877 (2009)]. Between 800 and 900 weight percent of oxidant, KMnO4, with respect to the initial amount of carbon nanotubes, was optimum for unzipping the long, narrow MWNTs produced by the inventors (diameters 5-15 nm, 6-12 walls and lengths of about 300 μm) and used in this Example 13. For much higher content of KMnO4, the MWNT were totally dissolved because of the extremely oxidative conditions.
Powder x-ray diffraction data were collected on a Rigaku Ultima-III diffractometer using Cu-Kα radiation (λ=1.5418 Å).
Biscrolled graphene nanoribbons yarns were first prepared by chemical and thermal treatment of the graphene oxide nanofibers before being incorporated as a guest into the MWNT host.
For the chemical reduction of graphene oxide nanoribbons, hydrazine monohydrate (1 μL/3 mg graphene oxide nanoribbons) was used (12 h at 80° C. in DMF). The graphene oxide nanoribbons were thermally reduced by employing two different conditions.
In one case a “soft” thermal treatment was applied (annealing in argon gas at 150° C. for two hours) and in another case more extreme thermal reducing treatment was applied at 800° C. (annealing in argon:hydrogen (95:5) for 5 hours). After either of those treatments, the basal distance between sheet layers returns to ˜3.4 Å.
Strong, multifunctional biscrolled graphene oxide nanoribbons@MWNT yarns and biscrolled graphene nanoribbon@MWNT yarns were prepared by filtration method (Example 3) and twisted in liquid medium (Example 11). An aqueous solution (10 mg/liter) of graphene oxide nanoribbons or reduced graphene oxide nanoribbons dispersed in 1 wt % SDS was prepared by probe sonication. After biscrolling and drying, usually more than 90 wt. % in the composite fiber was graphene or graphene oxide nanoribbons.
This Example 14 demonstrates making nanostructured LiFePO4@MWNT biscrolled yarns for lithium battery application. Commercially available carbon-coated LiFePO4 was used. Biscrolled LiFePO4@MWNT yarn electrodes were prepared by a similar wet filtration method as described in Example 3, which involved ultrasonic dispersion of 2-10 mg of LiFePO4 in isopropanol, filtration-based deposition of the solution dispersed LiFePO4 guest on the host MWNT sheets, and then twist insertion, as described in Example 11. In the present example, the LiFePO4@MWNT biscrolled yarn was subjected to a thermal treatment at 600° C. for 6 hours in argon flow. As prepared, 1 cm to 2.5 cm long cathode fibers were deployed as a whole cathode without the need of using a metal current collector along the length of the yarn.
The electrochemical performance of the LiFePO4 biscrolled yarns as cathode was tested inside an argon-filled glove box using a three electrode cell in a glass vial 1801, as shown in
For testing LiFePO4@MWNT yarns 1802, graphite was used as the counter electrode and lithium foil was used as the reference electrode and 1M LiPF6 in ethylene carbonate:dimethyl carbonate (1:1 v/v) was used as the electrolyte. Cyclic voltammetry was carried out at a scanning rate of 0.1 mV/s between 2.5 and 4.2V (versus Li/Li+).
Specific capacities have been calculated for the total weight of electrode. The total weight percentage of active material in the electrode including current collector is always larger than 90 wt %, versus a typical loading of 70 wt % in conventional LiFePO4 electrodes.
As shown in
This Example 15 demonstrates biscrolling nitrogen-doped carbon nanotube guest in a MWNT host. N-doped MWNTs (CNx) were prepared by floating catalyst CVD method described elsewhere [M. Terrones et al., Chem. Commun. 23, 2335 (2000)] using benzilamine (C6H5CH2NH2) and ferrocene (η5-Fe(C5H5)2) as C/N and iron source respectively. Purification was carried out by reflux in a mixture of HCl and CH3COOH (7:2 vol) for 16 h to remove all the iron impurities; these “purified” CNx MWNTs were dispersed in an aqueous solution (0.1% wt of SDS). An aliquot of this dispersion was used as feeding medium for preparing biscrolled yarns with a linear density of 15 μg/cm by the filtration method described in Example 3 (using one host MWNT sheet as support).
The electrochemical performance of these biscrolled CNx@MWNT yarns in the oxygen reduction reaction (ORR) was tested by cyclic voltammetry (CV) in a 3 electrode cell. For electrochemical measurements, rigid holders (such as electrode holder 2105, as shown in
A Pt mesh was used as a counter electrode, while Ag/AgCl/3M NaCl served as reference electrode. Cyclic voltammograms (CVs) were obtained at 5 mV/s for the voltage range +0.8 V to −0.4 V after the voltammogram shape was reproducible for each test. Voltammograms obtained for at a scan rate of 25 mV/s in aerated 0.5 M H2SO4 are compared in
Because of this performance, these biscrolled CNx@MWNT yarns can be utilized as the oxygen electrode in proton exchange membrane fuel cells (PEMFCs) and for other electrochemical applications.
This Example 16 demonstrates application of biscrolled yarns containing guest TiO2 as a photo catalyst. TiO2 powder was suspended in 1% SDS aqueous solution and filtration-deposited on a MWNT sheet stack (Example 3). Then an additional layer of MWNT sheet was placed on top of the TiO2 layer to confine the guest. Twist was inserted as described in Example 11.
To test catalyzed photolysis caused by the biscrolled TiO2@MWNT yarn, a piece of cotton fabric (3 cm×4 cm) was dyed by soaking in a solution of methylene blue, and then dried overnight in a vacuum oven. A biscrolled TiO2@MWNT yarn was then laid overtop the dyed cotton fabric and placed under a mercury UV lamp that provided 365 nm radiation. The intensity of the lamp was 64 W/m2. It was noticed that after 4 hours of irradiation, a bleaching effect was visible even on the reverse side of the dyed fabric, which was neither in direct contact with the biscrolled yarn or exposed to the UV light.
The robustness of TiO2@MWNT yarns for retaining TiO2 during the cleaning of textiles (for example using a washing machine) was investigated using a model system. The robustness test was done on a biscrolled TiO2@MWNT yarn in which the concentration of TiO2 was nearly 93%. The weight of the yarn before washing was measured. The yarn was then immersed in 1 wt % SDS suspension, which was placed on a hot plate with a magnetic stirrer. The yarn was washed by stirring for 3 hours at 80° C. Then the yarn was taken out of the suspension and dried in vacuum overnight. The weight of the yarn was again measured. The percentage of weight loss of TiO2 was less than 2%.
This Example 17 compares the guest concentration dependence of yarn mechanical properties of the biscrolled TiO2@MWNT yarn made by TiO2 deposition from an aerosol (as described in Example 8) with that for the biscrolled TiO2@MWNT yarn made by filtration-based deposition of the TiO2. Though the TiO2-free yarn used to provide a baseline for these two different measurement sequences had very different specific strengths, biscrolled yarns made using aerosol-deposition and filtration-deposition provide similar dependencies of specific strength on TiO2 concentration. The weight of the biscrolled yarn was measured using a microbalance. Specific mechanical properties were determined from measurements of force versus strain at 4%/minute strain rate using a mechanical tester (Favimat 37617).
More surprisingly, even high concentrations of TiO2 did not dramatically degrade the nanotube contribution to biscrolled yarn specific strength. This is indicated in
This Example 18 describes microscopic study of the biscrolled yarn structure using SEM images. For microscopic analysis of the biscrolled yarn cross-sections, a focused ion-beam was used to cut the yarns. The yarn was placed on a substrate, and an ion-beams of various current values, typically above 1 nA, were used to make a clean cut on the yarn. After the cutting, different stages of polishing were performed on the cutting surfaces by ion-beams of lower energies until a smooth surface structure was obtained on the yarn cross-section.
This Example 19 demonstrates extension of biscrolling to electrically insulating hosts: arrays of hollow SiO2 and Si3N4 nanotubes. Individual carbon nanotubes and nanotube bundles in free-standing, forest-drawn MWNT sheets were conformably coated with ˜10 nm thickness of SiO2 or Si3N4 produced by plasma-enhanced CVD (as described in Example 6).
Free standing nanotube sheets were subsequently obtained by removing the carbon nanotube cores (by combustion in air at high temperature or in ozone at room temperature).
Relevant for application of the ceramic-coated carbon nanotubes as host for biscrolled yarn, conformally coating the carbon nanotubes with ˜10 nm thickness of SiO2 did not significantly affect in-plane sheet conductance or the conductance of twisted yarns.
This Example 20 describes the catalytic activity of biscrolled yarn containing platinum black powder as guest, when the biscrolled yarn was immersed in hydrogen peroxide solution. Platinum black powder is a well known catalytic material that decomposes hydrogen peroxide into water and oxygen. This decomposition is an exothermic process and the resulting increase of temperature per unit time can be used as an index of decomposition rate. In this experiment the decomposition of hydrogen peroxide in the presence of biscrolled yarn (with platinum black) was studied and compared with the performance of the performance of the same quantity (20 μg) of free platinum black powder.
Though the reaction rate was decreased because of Pt black confinement in a biscrolled yarn, as is expected, it is noteworthy that the biscrolled Pt black retained catalytic activity.
This Example 21 demonstrates making biscrolled yarn containing nickel powder guest for magnetic wire application. Nickel powder (3 μm average diameter) was deposited on MWNT sheet by using the electrostatic spray method, and then the resulting bilayer stack was biscrolled.
This Example 22 demonstrates the use of a scrolled MWNT sheet strip for confining Pt black on a nickel-titanium (NiTi) alloy shape memory alloy (SMA) actuator wire for application as a fuel-driven actuator. [V. E. Ebron et al., Science 311, 1580-1583 (2006)].
Upon application of hydrogen gas or methanol vapors to these catalytic NiTi SMA wires, room-temperature combustion of the fuel heats the SMA wire, resulting in actuation comparable to that of electrically-driven SMA. The Pt-black@MWNT wrap provides an ideal structure for this interaction as it is simultaneously: highly porous for fuel-catalyst interaction, thermally conductive for heat transfer between catalyst particles and the wire, thermally stable across a wide temperature range and flexible to withstand the ˜4% dimensional change associated with actuation. By regulation of cyclical delivery of a hydrogen-oxygen fuel, such biscrolled wires have been tested to perform in excess of 50,000 cycles without showing any noticeable degradation.
This Example 23 describes methods for the fabrication of biscrolled MWNT yarn that contains guest growth factors that may be useful for the selective directional growth of tissue, such as liver tissue. Tissues express or contain factors that guide regeneration and proliferation of new tissue growth. Growth factors can determine tissue growth by providing a gradient of diffusible factors.
Deposition of lyophylized growth factors onto a MWNT sheet strip or wedge and then biscrolling to form biscrolled yarns may provide regenerative scaffolds for in vitro 3-dimensional tissue bioengineering of tissue types from single or co-cultures. Dry deposition of powder forms of growth factor via manual or airbrush technique can be utilized.
This Example 24 demonstrates the use of biscrolling to confine high concentrations of biologically active agents as guests in yarns that are sufficiently strong to be sewn into muscle. Biscrolled MWNT yarn (
Subcutaneous and cutaneous layers of a full thickness laceration in the forefoot of a butchered pig (purchased at a grocery store) were sutured with this biscrolled yarn (
While embodiments of the invention have been shown and described, modifications thereof can be made by one skilled in the art without departing from the spirit and teachings of the invention. The embodiments described and the examples provided herein are exemplary only, and are not intended to be limiting. Many variations and modifications of the invention disclosed herein are possible and are within the scope of the invention. Accordingly, the scope of protection is not limited by the description set out above, but is only limited by the claims which follow, that scope including all equivalents of the subject matter of the claims.
The disclosures of all patents, patent applications, and publications cited herein are hereby incorporated herein by reference in their entirety, to the extent that they provide exemplary, procedural, or other details supplementary to those set forth herein.
This Application is a divisional application of U.S. patent application Ser. No. 14/625,998, filed Feb. 19, 2015, which is a divisional application of U.S. patent application Ser. No. 13/322,880, filed on Nov. 28, 2011 (now U.S. Pat. No. 8,968,756 issued on Mar. 3, 2015), which is the 35 U.S.C. §371 national application of International Patent Application No. PCT/US2010/036378, filed May 27, 2010, which designated the United States and claimed priority to U.S. Provisional Patent Application Ser. No. 61/181,601, filed on May 27, 2009. All of these patent applications are entitled “Fabrication of Biscrolled Fiber Using Carbon Nanotube Sheet,” are commonly assigned to the assignee of the present invention, and which disclosures are considered part of and are incorporated by reference in their entirety in the disclosure of this application.
This work was supported by Air Force Office of Scientific Research grant FA9550-09-1-0384, Office of Naval Research MURI grant N00014-08-1-0654, Air Force Grant AOARD-10-4067, NSF grant DMI-0609115, and Robert A. Welch Foundation grant AT-0029. The U.S. government may have certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 6782892 | Li et al. | Aug 2004 | B2 |
| 20080170982 | Zhang et al. | Jul 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 1410486 | Apr 2003 | CN |
| 2007015710 | Feb 2007 | WO |
| 2007015710 | Apr 2009 | WO |
| Entry |
|---|
| M. Zhang et al., “Strong, Transparent, Multifunctional, Carbon Nanotube Sheets,” Science, vol. 309; p. 1215-11219; (2005). |
| X. Zhang et al., “Ultrastrong, Stiff, and Lightweight Carbon-Nanotube Fibers,” Advanced Materials 19; pp. 4189-4201; (2007). |
| Y. Li et al.; “Direct Spinning of Carbon Nanotube Fibers from Chemical Vapor Deposition Synthesis,” Science, vol. 304; pp. 276-278; (2004). |
| Y. Wu et al.; “Superconducting MgB2 Nanowires,” Advanced Materials, 13, No. 19; pp. 1487-1489; (2001). |
| D. Whang et al.; “Large-Scale Hierarchical Organization of Nanowire Arrays for Integrated Nanosystems,” Nano Letters, vol. 3, No. 9; pp. 1256-1259; (2003). |
| N. Li et al.; “Bismuth Nanotubes: A Rational Low-Temperature Synthetic Route,” J. Am. Chem. Soc. 123; pp. 9904-9905; (2001). |
| L. M. Viculis et al.; “A Chemical Route to Carbon Nanoscrolls,” Science, vol. 299; p. 1361; Feb. 28, 2003. |
| Z.L. Wang; “Nanobelts, Nanowires, and Nanodiskettes of Semiconducting Oxides—From Materials to Nanodevices,” Advanced Materials 15; pp. 432-436 (2003). |
| X.D. Wang et al.; “Rectangular Porous ZnO—ZnS Nanocables and ZnS Nanotubes,” Advanced Materials 14, No. 23; pp. 1732-1735 (2002). |
| W. L. Hughes et al.; “Nanobelts as nanocantilevers,” Applied Physics Letters, vol. 82, No. 17; pp. 2886-2888; Apr. 28, 2003. |
| J.W. Liu et al. “Synthesis of Carbon Nanotubes and Nanobelts through a Medial-Reduction Method,” Journal of Physical Chemistry B 107, pp. 6329-6332 (2003). |
| Y.B. Li et al.; “Mg2Zn11—MgO belt-like nanocables,” Chemical Physics Letters 375; pp. 102-105 (2003). |
| D.V. Kosynkin et al.; “Longitudinal unzipping of carbon nanotubes to form graphene nanoribbons,” Nature, vol. 458; pp. 872-876; Apr. 2009. |
| W. Takahima et al.; “Amperometric phenol biosensor based on covalent immobilization of tyrosinase onto an electrochemically prepared novel copolymer poly (n-3-aminopropyl pyrrole-co-pyrrole) film,” Sensors and Actuators B 99; pp. 271-277; (2004). |
| C. H. Yen et al.; “Deposition of Platinum Nanoparticles on Carbon Nanotubes by Supercritical Fluid Method,” Journal of Nanoscience and Nanotechnology; vol. 5; pp. 1852-1857; (2005). |
| C.A. Lawrence, Fundamentals of Spun Yarn Technology, CRC Press, 2002. |
| J. Nagamatsu et al.; “Superconductivity at 39 K in magnesium diboride,” Nature, vol. 410; p. 63; Mar. 1, 2001. |
| E. Yoo et al., “Large reversible Li storage of grapheme nanosheet families for use in rechargeable lithium ion batteries”, Nanoletters, vol. 8, No. 8; pp. 2277-2282; (2008). |
| S. M. Paek et al., “Enhanced Cyclic performance and Lithium storage capacity of SnO2/grapheme nanoporous electrodes with three-dimensionally delaminated flexible structure”, Nano Letters, vol. 9, No. 1; pp. 72-75; (2009). |
| D.V. Kosynkin et al.; “Longitudinal unzipping of carbon nanotubes to form graphene nanoribbons,” Nature, vol. 458, 872-876; Apr. 16, 2009. |
| L. Jiao et al.; “Narrow graphene nanoribbons from carbon nanotubes,” Nature, vol. 458; pp. 877-880; Apr. 16, 2009. |
| L. Jiao et al.; “Facile synthesis of high-quality graphene nanoribbons,” Nature Nanotechnology, vol. 5; pp. 321-325; (2010). |
| J. Chmiola et al.; “Anomalous Increase in Carbon Capacitance at Pore Sizes Less Than 1 Nanometer,” Science, vol. 313; pp. 1760-1763; Sep. 22, 2006. |
| Y. Gogotsi et al.; “Nanoporous carbide-derived carbon with tunable pore size,” Nature Materials, vol. 2; pp. 591-594; (2003). |
| A. B. Dalton et al.; “Super-tough carbon-nanotube fibres,” Nature, vol. 423; p. 703 (2003). |
| S. Kundu et al.; “Electrocatalytic Activity and Stability of Nitrogen-Containing Carbon Nanotubes in the Oxygen Reduction Reaction,” J. Phys. Chem. C 113; pp. 14302-14310; (2009). |
| Matheson et al.; “Influence of Nitrogen Doping on Oxygen Reduction Electrocatalysis at Carbon Nanofiber Electrodes,” J. Phys. Chem. B 109; pp. 4707-4716; (2005). |
| Y. Shao et al.; “Nitrogen-doped carbon nanostructures and their composites as catalytic materials for proton exchange membrane fuel cell,” Applied Catalysis B: Environmental, 79; pp. 89-99; (2008). |
| R. Krupke et al.; “Thin Films of Metallic Carbon Nanotubes Prepared by Dielectrophoresis,” Advanced Materials, 18; pp. 1468-1470; (2006). |
| A. K. Pal et al.; “Electrodeposited carbon nanotube thin films,” Thin Solid Films 476; pp. 288-294; (2005). |
| P. Poulin et al.; “Films and fibers of oriented single wall nanotubes,” Carbon 40; pp. 1741-1749; (2002). |
| A.R. Boccaccini et al.; “Electrophoretic deposition of carbon nanotubes,” Carbon 44; pp. 3149-3160; (2006). |
| D.V. Kosinkyn et al.; “Longitudinal unzipping of carbon nanotubes to form graphene nanoribbons,” Nature, vol. 458; pp. 872-877; (2009). |
| M. Terrones et al.; “Novel nanoscale gas containers: encapsulation of N2 in CNx nanotubes,” Chem. Commun. 23; pp. 2335-2336; (2000). |
| S. Kundu et al.; “Electrocatalytic Activity and Stability of Nitrogen-Containing Carbon Nanotubes in the Oxygen Reduction Reaction,” J. Phys. Chem C, 113; pp. 14302-14310; (2009). |
| V.E. Ebron et al.; “Fuel-Powered Artificial Muscles,” Science, vol. 311; pp. 1580-1583; (2006). |
| M. Monthioux; “Filing single-wall carbon nanotubes,” Carbon, 40; pp. 1809-1823; (2002). |
| Jeremy Sloan et al.; “Crystallisation inside fullerene related structures,” J. Mater. Chem.; pp. 1089-1095; (1997). |
| Antonis Kelarakis, et al.; “Polymer Chain Dynamics and Melting Behavior in a Carbon nanofiber Reinforced Elastomeric Composite;” Proceedings of the American Chemical Society; 2006; 715-716 vol. 95; Polymeric Materials: Science & Engineering. |
| S.K. Kim et al.; “Characteristics of Electrodeposited Single-Walled Carbon Nanotube Films;” Journal of Nanoscience and Nanotechnology; 2006; vol. 6; 3614-3618; American Scientific Publishers; US. |
| United States International Searching Authority; International Search Report and Written Opinion for PCT/US2010/036378, Dec. 20, 2010, Alexandria, VA. |
| Number | Date | Country | |
|---|---|---|---|
| 20160111707 A1 | Apr 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61181601 | May 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14625998 | Feb 2015 | US |
| Child | 14967940 | US | |
| Parent | 13322880 | US | |
| Child | 14625998 | US |