Patent Application
20130133738
This invention relates to a furnace for firing electrodes on a solar cell device, a method for manufacturing a solar cell device using the furnace, and a solar cell device.
The mesh belt firing furnace suffers from a substantial power consumption because of a large heat capacity of the mesh belt. Also, although a rapid heating/rapid cooling profile is preferred to form a satisfactory BSF layer on the back surface of the solar cell device using aluminum paste, a problem arises that many heaters and water cooling are necessary in order to provide the mesh belt firing furnace with a rapid heating/rapid cooling profile.
To solve these problems, for example, Patent Document 1 (JP-A H08-162446) discloses the use of four wires instead of the mesh belt for thereby reducing the power consumption of the firing furnace and reducing the firing time to increase the throughput.
In the method of Patent Document 1, the substrate having conductive paste printed thereon is transported by the wires with the substrate rested directly on the wires. In the heating zone of the firing furnace, however, the temperature of wires is generally about 50° C. lower than the atmosphere temperature and the substrate temperature. When the substrate is fired with the front surface faced up, that is, with the aluminum layer on the back surface kept in contact with the wires, aluminum once melted is left on the wires at the contacts due to the temperature difference between the aluminum layer and the wires in the heating zone of the firing furnace, building up on the wires. Such aluminum buildup becomes hard alumina, which can cause flaws to the aluminum electrode as the number of substrates subject to firing treatment increases. Sometimes, such flaws become hard bosses, at which cells can be cracked when cells are stacked for packaging. This gives rise to a problem that the yield of manufacture is reduced.
The method of Patent Document 1 also has the problem that in the event of firing with the back surface faced up, that is, with the silver electrode on the front surface kept in contact with the wires, marks of the wires are left on the silver electrode upon firing, which can cause disconnection and hence, degradations of performance and manufacture yield.
A further problem arises in the method of Patent Document 1. Since the temperature of the wires is lower than the atmosphere and substrate in the heating zone of the firing furnace, the portions of the substrate in contact with the wires are underheated, which can cause under-sintering of silver electrode and a thickness distribution of BSF layer. As a result, the performance of the solar cell device is degraded.
Also a firing furnace using wires as walking beams is known from Patent Document 2 (JP-A 2009-238991).
In the heating method using walking beams as shown in
A changeover from the belt conveyor system to the walking beam conveyor system enables a space saving of a unit necessary for cooling to produce a rapid heating/rapid cooling firing profile suitable to form a satisfactory BSF layer, and offers the advantages of reduced power consumption and shorter treating time. This method, however, inevitably suffers from degradations of performance and manufacture yield of solar cell devices since the substrate comes in direct contact with wires as well.
An object of the invention, which has been made under the above-mentioned circumstances, is to provide a furnace for firing solar cell device electrodes, which ensures effective firing of conductive paste to form an electrode on a substrate by preventing a metal component in the conductive paste from building up on transport members such as wires to cause damages to the electrode or substrate and by minimizing firing variations within the substrate plane, and thus enables to manufacture a solar cell device in high yields without any loss of solar cell performance; a method for manufacturing a solar cell device using the firing furnace; and a solar cell device.
Making extensive investigations to attain the above object, the inventors have found that when a furnace for firing solar cell device electrodes, comprising a transport member for transporting a substrate having a conductive paste applied thereto, a heating zone for heating the substrate to fire the conductive paste, and a cooling zone for cooling the heated substrate is used, and particularly when the transport member is of wire structure, and the wire transport member is heated by a heating means, so that the temperature of the transport member may approach to the temperature of the heating zone atmosphere during firing of the electrode paste, the substrate can be effectively heated. This prevents a metal component in the conductive paste from remaining on the wire after melting, thus prevents the buildup of the metal component from causing damages to the electrode or substrate, and minimizes firing variations within the substrate plane. It is then possible to fire the electrode paste in the manufacture of a solar cell device without any losses of solar cell performance and yield. The invention is predicated on these findings.
Accordingly, the invention provides a firing furnace, a method for manufacturing a solar cell device, and a solar cell device, as defined below.
(1) A furnace for firing electrodes on a solar cell device, comprising a transport member for transporting a substrate having a conductive paste applied thereto, a heating zone for heating the substrate to fire the conductive paste, and a cooling zone for cooling the heated substrate, the furnace further comprising a means for heating the transport member.
(2) The firing furnace of (1) wherein the temperature difference between the heating zone atmosphere and the transport member is 0 to 200° C.
(3) The firing furnace of (1) or (2) wherein the transport member comprises at least two wires extended for parallel and horizontal motion in a longitudinal direction of the furnace wherein the substrate is transported by the wires while it is rested thereon.
(4) The firing furnace of any one of (1) to (3) wherein the transport member is of the walking beam system.
(5) The firing furnace of any one of (1) to (4) wherein the means for heating the transport member is an electrical means.
(6) A method for manufacturing a solar cell device, comprising the steps of forming a pn junction in a semiconductor substrate, applying a conductive paste to a light-receiving surface and non-light-receiving surface of the semiconductor substrate, and firing the conductive paste to form power-extracting electrodes,
the step of firing the conductive paste being performed in the firing furnace of any one of (1) to (5).
(7) A solar cell device obtained by the method of (6).
The invention intends that the wire temperature approach to the temperature of the heating zone atmosphere or the temperature of aluminum paste layer, particularly when a wire firing furnace is used in the firing of electrode paste. The wire is heated at a temperature about 50° C. higher than the normal temperature so that the wire temperature is substantially equal to the temperature of the heating zone atmosphere, prior to firing. This prevents a lowering of yield by damaging of the electrode by the buildup on wires of the metal component in the conductive paste, and enables continuous operation of the wire firing furnace. This further minimizes firing variations within the substrate plane which are otherwise caused by the lower temperature of the wire, thus suppressing any loss of performance. Also the furnace provides a high throughput as compared with mesh belt firing furnaces and the like.
Embodiments of the invention are described below in detail. However, the scope of the invention is not limited to the illustrated embodiments because the invention can be implemented in a wide variety of embodiments in addition to the illustrated embodiments. The drawings are not depicted to scale. Certain members are depicted in enlarged scale in order to clarify the description and understanding of the invention whereas insignificant parts are not depicted.
The firing furnace of the invention is intended for firing electrodes on a solar cell device and defined as comprising a transport member for transporting a substrate having a conductive paste applied thereto, a heating zone for heating the substrate to fire the conductive paste, and a cooling zone for cooling the heated substrate, and characterized by further comprising a means for heating the transport member.
In the firing furnace of the invention, the substrate having a conductive paste applied thereto is rested on the transport member and transported through the furnace thereby. As the substrate is passed through the heating zone, the conductive paste is fired to form an electrode. The structure of the transport member for transporting the substrate is not particularly limited, and may be any of mesh, wire and other systems. Preference is given to a wire firing furnace wherein wires are used to convey the substrate. The wire firing furnace enables firing at low power consumption and high throughputs as compared with conventional mesh belt firing furnaces.
Where the wire transport member is used, its structure is not particularly limited, and it may have any of prior art well-known structures. Preferred are a structure wherein at least two wires, typically two to four wires are extended for parallel and horizontal motion in a longitudinal direction of the furnace and driven by a drive via rollers as shown in
In firing the electrode paste according to the invention, the transport member having the substrate rested thereon is heated until the temperature of the transport member becomes substantially equal to the temperature of the heating zone atmosphere. In the event of a wire firing furnace using a wire transport member, for example, the wire as the transport member is preheated such that the temperature of the wire is substantially equal to the temperature of the conductive paste layer on the substrate in the firing furnace. The lack of the temperature difference between the wire and the substrate eliminates a conventionally recognized phenomenon that a conductive metal component in the hot conductive paste sticks to a cold wire, and eventually prevents the metal component from building up on the wire. This suppresses a lowering of yield by damaging of the electrode by the buildup of the metal component on the wire, even when the wire firing furnace is continuously operated. This also minimizes firing variations within the substrate plane caused by the low temperature of the wire, thus preventing degradation of the performance.
The means for heating the transport member include an electrical means of directly heating the wire by applying a voltage across the wire to conduct AC or DC current flow. Suitable means of indirectly heating the wire include a means of lamp heating the wire itself by providing a heating area outside the firing furnace; a means of heating the wire itself by applying steam to the wire outside the firing furnace; and a means of heating the wire itself by winding a coil around the wire and conducting electric flow to the coil. Any of these means may be employed for heating the wire. Of these, however, the means of directly heating the wire is superior from the aspects of cost and space because the means of indirectly heating the wire requires provision of a heating area outside the firing furnace. Accordingly, the means of directly heating the wire is preferably selected. Use of such heating means eliminates the temperature difference between the wire and the entire substrate and eliminates a conventionally recognized phenomenon that hot conductive paste sticks to a cold wire, and eventually prevents the metal component in the conductive paste from building up on the wire. This suppresses a lowering of yield by damaging of the electrode by the buildup of the metal component on the wire and also inhibits degradation of the performance due to firing variations within the substrate plane.
The temperature (firing temperature) of the heating zone is typically 500 to 950° C., preferably 600 to 850° C., and the heating time is preferably 5 to 30 seconds. Also preferably the temperature of the cooling zone is 25 to 500° C., and the cooling time is 5 to 30 seconds. The atmosphere in the furnace may be air. Preferred is an atmosphere which allows an organic material in the conductive paste to be burnt off. On the other hand, the temperature of the transport member is substantially equal to the temperature of the heating zone atmosphere, preferably in the range of 500 to 950° C., and more preferably in the range of 600 to 850° C. As used herein, the phrase that “the temperature of the transport member is substantially equal to the temperature of the heating zone atmosphere” means that the temperature difference between the transport member and the heating zone atmosphere is in a range of 0 to 200° C., preferably 0 to 100° C., more preferably 0 to 20° C., and even more preferably 0 to 10° C.
Next, the solar cell device which is manufactured by the method using the firing furnace of the invention is described. As shown in
Described below is the method of manufacturing a solar cell device according to the invention. First a substrate, typically p-type silicon substrate is provided. The p-type silicon substrate used often has a resistivity of 0.1 to 4.0 Ω2-cm. It may be either multicrystalline or monocrystalline and is preferably of plate shape having dimensions of 100 to 150 mm squares and a thickness of 0.1 to 0.3 mm, as indicated above. The surface of p-type silicon substrate that corresponds to the light-receiving surface of a solar cell device is provided with a rugged structure known as texture, for example, by immersing in an acidic solution, chemically etching in alkaline solution, cleaning, and drying. The rugged structure induces multiple reflections of light at the light-receiving surface of a solar cell device. Therefore, by forming a rugged structure, effective reflectance is reduced, and conversion efficiency is improved. Hereinafter, one surface of p-type silicon substrate serving as the light-receiving surface of a solar cell device is referred to as front surface, and the other surface of p-type silicon substrate opposite to the light-receiving surface is referred to as back surface.
Next, the p-type silicon substrate is placed in a hot gas containing POCl3, for example, at about 800° C. or higher, followed by a thermal diffusion method of diffusing n-type impurity such as phosphorus into the p-type silicon substrate over its entire surface, thereby forming an n-type diffusion layer (n-type impurity layer) in the surface. It is noted that when the n-type diffusion layer is formed by thermal diffusion, the n-type diffusion layers may be formed on opposite surfaces and end surfaces of a p-type silicon substrate. In this case, unnecessary n-type diffusion layers may be removed by immersing the p-type silicon substrate, in which the surface of the necessary n-type diffusion layer is covered with an acid resistant resin, in fluoronitric acid solution or the like. The above procedure results in a substrate having a pn junction.
Next, an antireflective coating of SiN or the like is formed on the surface of the p-type silicon substrate, for example, by a plasma-enhanced CVD method using ammonia, silane, nitrogen, hydrogen or the like.
On the back surface of the substrate, a conductive paste containing aluminum, glass frit, varnish and the like, for example, is screen printed and dried. On the front surface, a conductive paste containing silver, glass frit, varnish and the like, for example, is screen printed and dried to form a collector electrode. Thereafter, the pastes for the respective electrodes are fired in the firing furnace of the invention, whereby an aluminum electrode and a BSF layer are formed on the back surface and a silver electrode formed on the front surface. The shape of the power-extracting electrodes on the front and back surfaces is not particularly limited, and electrodes of any desired shape like comb or grating-shape can be fired in the furnace of the invention. The firing conditions are as alluded previously.
Examples and Comparative Examples are given below for further illustrating the invention, but the invention is not limited thereto.
A p-type silicon substrate of boron-doped p-type multicrystalline silicon which had been sliced to a thickness of 0.2 mm and had a resistivity of about 1 Ω2-cm was machined along the outer periphery into a square plate of 15 cm per side. The p-type silicon substrate was immersed in fluoronitric acid solution for 15 seconds for etching the damaged layer, chemically etched for 5 minutes in a solution containing 2 wt % KOH and 2 wt % isopropyl alcohol (IPA) at 70° C., washed with deionized water, and dried, whereby a texture was formed on the surface of the p-type silicon substrate.
Next, the p-type silicon substrate was placed in a POCl3 gas atmosphere and subjected to thermal diffusion at a temperature of 870° C. for 30 minutes, thereby forming an n-type layer on the p-type silicon substrate. The n-type layer had a sheet resistance of about 40 ohm/square (Ω/□). An acid resistant resin was coated on the n-type layer, after which the p-type silicon substrate was immersed in fluoronitric acid solution for 10 seconds to remove the n-type layer where the acid resistant resin coating was absent. Thereafter, the acid resistant resin coating was removed, obtaining a p-type silicon substrate having an n-type layer only on the front surface.
Subsequently, by a plasma-enhanced CVD method using ammonia gas, silane and nitrogen gas, an antireflective coating of SiN was deposited to a thickness of 100 nm on the n-type layer-bearing surface of the p-type silicon substrate. Next, on the back surface of the antireflective coating-bearing substrate, a conductive aluminum paste was printed and dried at 150° C. Thereafter, on the front surface, a conductive silver paste was applied by a screen printing technique and dried at 150° C. to form a collector electrode.
Subsequently, the substrate as treated thus far was admitted into a wire type walking beam firing furnace as shown in
By firing according to the above procedure, 1,000 solar cell devices were manufactured. Table 1 reports the performance of the solar cell devices and the yield after the firing step. The yield is a pass rate of those substrates devoid of the above-indicated problems (crack, boss, appearance anomaly) relative to the number of substrates admitted to the firing step.
In contrast, the data of Comparative Example are those of solar cell devices which were fired in the same wire firing furnace as in Example, without heating the wires. The temperature in the firing furnace (heating zone) was measured by inserting a K-series thermocouple, and the temperature of a wire was measured by placing a K-series thermocouple in contact with the wire. It was confirmed that the temperature of the wires was about 50° C. lower than the temperature of the heating zone atmosphere. As seen from Table 1, improvements in solar cell performance and manufacture yield are expectable from the use of the firing furnace of the invention, as compared with the firing step of Comparative Example. These improvements are mainly attributable to the elimination of a temperature drop of the wires.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2010-133084 | Jun 2010 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2011/062755 | 6/3/2011 | WO | 00 | 2/12/2013 |