This invention relates to flowable chips and apparatus and methods for the preparation and use of flowable chips. The flowable chips are useful in a method for recharging a crucible in a Czochralski-type process.
Most semiconductor chips used in electronic devices are fabricated from single crystal silicon prepared by a Czochralski-type (CZ) process. In the CZ process, a single crystal silicon ingot is produced by melting polycrystalline silicon source material in a crucible, stabilizing the crucible and source melt at an equilibrium temperature, dipping a seed crystal into the source melt, withdrawing the seed crystal as the source melt crystallizes on the seed to form a single crystal ingot, and pulling the ingot as it grows. Melting occurs at a temperature of 1420° C. in an inert gas environment at low pressure. The crucible is continually rotated about a generally vertical axis as the crystal grows. The rate at which the ingot is pulled from the source melt is selected to form an ingot having a desired diameter.
The polycrystalline silicon can be prepared using a fluidized bed reactor process to form granules. Alternatively, the polycrystalline silicon can be prepared using a chemical vapor deposition (CVD) process in a bell jar reactor. The polycrystalline silicon prepared by the CVD process can be broken or cut into suitably sized pieces such as rods, chunks, chips, and combinations thereof, before loading into the crucible. The polycrystalline silicon is melted to form the molten silicon.
One of the drawbacks of the CZ process is that when the charge of polycrystalline silicon is melted, the crucible may be only half full of molten silicon. This is due to the interstitial spaces left in the crucible charged with irregularly shaped pieces and results in inefficient utilization of the crystal puller. Therefore there is a need to develop methods to efficiently top up a charge after it is melted and before the start of the crystal seeding.
A further drawback of the CZ process is that the crucible can generally be used for only one pull before it must be replaced because crucibles degrade with use and can introduce impurities into the molten silicon. New crucibles are expensive to obtain, and used crucibles are expensive to dispose of. This has led to development of improved crucibles capable of lasting through multiple ingot pulls while contributing reduced contamination to the molten silicon. Therefore, a need exists for efficiently recharging the crucible during or after pulling the first ingot and any subsequent ingots. Various methods for topping up melts and recharging the crucible have been proposed.
In one method, granular polycrystalline silicon made by a fluidized bed process (such as granular material made by Ethyl Corporation or MEMC) has been loaded into the molten heel remaining in the crucible after the ingot has been pulled or to top up the initial charge melt. However, this method suffers from the drawback that granular polycrystalline silicon made by the fluidized bed process contains entrapped hydrogen. When the granular polycrystalline silicon is added to the heel, the hydrogen is released, causing the granules to burst. This causes splashing of molten silicon, which can damage the crucible.
In another method, granular polycrystalline silicon is added to the crucible while the ingot is being pulled. However, this method suffers from the drawback that due to its small particle size, granular polycrystalline silicon is difficult to melt in sufficient time to achieve a reasonable addition rate. Additional heat is required to melt these small particles, leading to added cost and accelerated crucible degradation. Accelerated crucible degradation can shorten crucible life and increase cost. If the granular polycrystalline silicon addition rate is too fast and the granules do not melt sufficiently, this can damage the surface of the ingot being pulled and cause dislocations and damage singularity of the crystal. Furthermore, granular polycrystalline silicon may have high amounts of dust. Dust can create contamination problems in the puller housing and can move to the surface of the pulled ingot and cause dislocations and reduce crystal yields. This may also increase process time, due to the need to remelt and repull the ingot.
Overall, granular polycrystalline silicon has inadequate purity for some applications, regardless of the process used to recharge the granules.
Previous attempts to use polycrystalline silicon rods prepared by a chemical vapor deposition process and broken into pieces have also not been used for crucible recharge due to purity or size problems. If relatively large size polycrystalline silicon pieces are used for crucible recharge, the process may suffer from the drawbacks of damage to the crucible and damage to the recharge apparatus. If the polycrystalline silicon pieces are broken into smaller sizes, contamination with impurities has made the polycrystalline silicon pieces unsuitable for use in crucible recharge processes.
This invention relates to flowable chips and apparatus and methods for the preparation and use of flowable chips. Flowable chips may be prepared by a method comprising:
This invention further relates to methods for recharging a crucible in a Czochralski-type process using the flowable chips. The method comprises:
This invention further relates to a method comprising;
All amounts, ratios, and percentages are by weight unless otherwise indicated. The following is a list of definitions, as used herein.
“A” and “an” each mean one or more.
“Blinding” means that a gap between two decks in a step deck classifier becomes plugged, preventing polycrystalline silicon pieces from passing through the gap, thus rendering the step deck classifier ineffective as a sorting means.
“Charge maximization” means a process in which a vessel, such as a mold or crucible, is filled with polycrystalline silicon having varying sizes and shapes in a manner to increase the amount of the melt over the amount obtained by filling the vessel randomly.
“Charge top up” means a process in which a vessel, such as a mold or crucible, is filled with polycrystalline silicon, said polycrystalline silicon is melted, and thereafter additional polycrystalline silicon is added to increase the amount of the melt.
“Chemical vapor deposition” means any chemical vapor deposition process that does not include fluidized bed reactor processes for preparing polycrystalline silicon. Chemical vapor deposition is exemplified by a Siemens type process.
“Comminute” means to break up, chop, or grind into small particles”. Comminute includes any method for reducing polycrystalline rods into pieces, including but not limited to cutting the rods and then further breaking them by various methods.
“Controlled particle size distribution” means that at least 75% of the particles in a group of particles have particle size in a specified range. For example, controlled particle size distribution of 4 to 12 millimeters (mm) means that at least 75% of the particles have particle size in the range of 4 to 12 mm and up to 25% of the particles have a particle size outside the range of 4 to 12 mm.
“Donor” means any atom that contributes an electron to silicon. Donors include antimony, arsenic, and phosphorous.
“Flowable” means the capability to deliver multiple solid particles through a transfer system without bridging, including when vibration energy is added to the system to help prevent the formation of a bridged particle network.
“Flowable chips” means polycrystalline silicon particles having a controlled particle size distribution, generally nonspherical morphology, low levels of bulk impurities, and low levels of surface impurities.
“Granular” and “granule” each mean a polycrystalline silicon particle prepared by a fluidized bed process and having a particle size of 6 millimeters or less. Granules are usually spherical or approximately spherical.
“Heel” means a quantity of silicon left in a vessel. Heel includes the quantity of silicon left in a crucible after an ingot has been pulled out of the crucible and the quantity of molten silicon resulting from melting a charge in the vessel prior to charge top up.
“Particle size” means the longest straight line between two points on a particle. For example, for spherical particles, particle size is the diameter.
The abbreviation “ppba” means parts per billion atomic relative to silicon.
The abbreviation “ppma” means parts per million atomic relative to silicon.
Flowable chips are polycrystalline silicon particles having a controlled particle size distribution. The controlled particle size distribution can be 0.2 to 45 mm, alternatively 1 to 25 mm, alternatively 1 to 20 mm, alternatively 3 to 20 mm, alternatively 4 to 12 mm, alternatively 4 to 10 mm, alternatively 1 to 12 mm, alternatively 1 to 8 mm. However, the exact controlled particle size distribution will be selected based on various factors including the method in which the flowable chips will be used and the apparatus used to feed them. For example, flowable chips that will be used in a CZ process, or in electronic grade applications, or both, may have a controlled particle size distribution of 2 to 45 mm. Alternatively, flowable chips that will be used in a solar grade application, such as a casting process, can have a controlled particle size distribution of 0.2 to 45 mm.
For some applications, controlled particle size distribution can be 4 to 12 mm, alternatively 4 to 8 mm, alternatively 4 to 6 mm. Without wishing to be bound by theory, it is thought that a controlled particle size distribution toward the lower end of the 4 to 12 mm range will minimize splashing when the flowable chips will be added to a crucible containing molten silicon. For some applications, controlled particle size distribution can be 9 to 12 mm, alternatively 10 to 12 mm. Without wishing to be bound by theory, it is thought that a controlled particle size distribution toward the higher end of the 4 to 12 mm range may improve ease of melting when the flowable chips will be added to a crucible containing a heel that is at least partially solidified.
The disclosure of ranges herein should be taken not only to disclose the range itself but also anything subsumed therein, as well as endpoints. For example, disclosure of a range of 4 to 12 includes not only the range of 4 to 12, but also 4, 5.7, 11 and 12 individually, as well as any other number subsumed in the range. Furthermore, disclosure of a range of, for example, 4 to 12 includes the subranges of 4 to 8, 9 to 10, 9 to 12, and 10 to 12, as well as any other subrange subsumed in the range and any ranges that constitute equivalents of the ranges disclosed herein.
The morphology of flowable chips is generally nonspherical. Exact morphology depends on the method used to make the flowable chips. For example, when the flowable chips are prepared by the methods disclosed herein, e.g., manually breaking polycrystalline silicon rods by striking with a low-contamination impact tool such as that disclosed in EP 0 539 097 A1, etc., the morphology will be irregular.
Flowable chips have low levels of bulk impurities, such as boron, donor, phosphorous, carbon, and total metals. The level of bulk impurities can be less than or equal to 0.2 ppma, alternatively less than or equal to 0.03 ppma, alternatively less than or equal to 0.025 ppma. The level of boron can be less than or equal to 0.06 ppba. However, for some applications, such as where boron will be used as a dopant, the level of boron can be less than or equal to 20 ppba, alternatively 5 to 20 ppba.
The level of donor is less than or equal to 0.30 ppba. Flowable chips can have a bulk level of phosphorous of less than or equal to 0.02 ppba, alternatively less than or equal to 0.015 ppba. The level of carbon is less than or equal to 0.17 ppma. The total level of bulk metal impurities is less than or equal to 4.5 ppba, alternatively less than or equal to 1 ppba. Bulk metal impurities include Cr, Cu, Fe, and Ni. Flowable chips can have a bulk level of Cr of less than or equal to 0.01 ppba. Flowable chips can have a bulk level of Cu of less than or equal to 0.01 ppba. Flowable chips can have a bulk level of Fe of less than or equal to 0.01 ppba. Flowable chips can have a bulk level of Ni of less than or equal to 0.01 ppba.
Bulk impurity levels can be measured by methods known in the art, such as the float zoning methods disclosed in U.S. Pat. Nos. 4,912,528; 5,361,128; and 5,436,164, and the method described herein in Example 3.
Flowable chips have low levels of total surface impurities. The total level of surface impurities is less than or equal to 30 ppba, alternatively 15 ppba, alternatively 4.5 ppba. Surface impurities include Co, Cr, Cu, Fe, Na, Ni, W, and Zn.
When flowable chips are prepared using the method described below using ajaw crusher such as that in
Surface purity can be measured by methods known in the art, such as the methods disclosed in U.S. Pat. No. 5,851,303.
Flowable chips also can have low levels of dust. Without wishing to be bound by theory, it is thought that low levels of dust facilitates melting and reduces crystal dislocation rates when the flowable chips are added to a crucible.
Flowable chips can have low residual gas content. Flowable chips can contain no hydrogen or lower levels of hydrogen than granules prepared by fluidized bed processes. Flowable chips can have a hydrogen content of 0 to 3600 ppba, alternatively 0 to 1300 ppba, alternatively 0 to 800 ppba, alternatively 800 to 1300 ppba. Flowable chips can contain low levels of chlorine. Flowable chips can have a chlorine content of 0 to 300 ppba, alternatively 20 to 120 ppba, alternatively 25 to 110 ppba, alternatively 30 to 100 ppba, alternatively 50 to 65 ppba.
Flowable chips can be prepared by a method comprising:
A flowable chip product can be prepared by the method described above, further comprising:
Alternatively, flowable chips may be prepared by a method comprising:
A flowable chip product can be prepared by the method described above, further comprising:
Polycrystalline silicon rods can be prepared by methods known in the art. For example, polycrystalline silicon rods can be prepared by a chemical vapor deposition process comprising chemical vapor deposition of a high purity chlorosilane or silane gas onto a heated substrate, see Handbook of Semiconductor Silicon Technology, edited by William C. O'Mara, Robert B. Herring, and Lee P. Hunt, Noyes Publications, Park Ridge, N.J., U.S.A., 1990, Ch. 2, pp. 39-58.
The polycrystalline silicon rods can be comminuted, for example, by cutting with a saw or by striking with a low-contamination impact tool such as that disclosed in EP 0 539 097 A1. Alternatively, the polycrystalline silicon rods may be comminuted using a jaw crusher. Alternatively, the polycrystalline silicon rods may be comminuted by striking with a low-contamination impact tool and the resulting comminuted rods may be further comminuted using a jaw crusher. Alternatively, the polycrystalline silicon rods may be comminuted by cutting with a saw, and thereafter striking with a low-contamination impact tool, and thereafter further comminuted using a jaw crusher. An example of a suitable jaw crusher is shown in
The movable jaw plate 403 is mounted to a Pitman carrier assembly 405. The Pitman carrier assembly 405 is connected to a Pitman bearing 406, which surrounds an eccentric shaft 407 at one end, and a tension rod pin 408 at the opposite end. The eccentric shaft 407 is mounted to a flywheel 409. The motor 410 drives a belt 411 around flywheel 409. Flywheel 409 turns eccentric shaft 407 to move movable jaw plate 403 in an elliptical motion with respect to stationary jaw plate 402. The rotational speed may be 300 to 400 revolutions per minute (r.p.m.). The motor 410 is mounted to base 412. The motion of the movable jaw plate 403 crushes the polycrystalline silicon in jaw cavity 404. Particle size of the resulting polycrystalline silicon pieces is reduced sufficiently for the polycrystalline silicon pieces to exit jaw cavity 404 through discharge slot 418.
A horizontal spring assembly includes tension rod 413 running through adjusting wheel 414, outside spring collar 415, tension spring 416, and inside spring collar 417 to tension rod pin 408. Adjusting wheel 414 mounted to outside spring collar 415 can be turned to adjust tension spring 416. The horizontal spring assembly can be used to hold the Pitman 405 in contact with the toggle plate 424.
A vertical assembly includes wedge adjusting rod 419 running through an adjusting wheel 420 and cross bar 421. Adjusting wedge 422 is mounted to bearing wedge 423. Toggle plate bearing wedge 423 is mounted to toggle plate 424. Toggle plate 424 is mounted to Pitman carrier assembly 405 above tension rod pin 408. The vertical assembly can be used to adjust the width of the discharge slot 418. The position of the toggle plate 424 (in grooves of bearing wedge 423) determines the movement of the Pitman 405 and the motion of the bottom of movable jaw plate 403.
Polycrystalline silicon can be fed to the jaw crusher 400 from hopper 425. As the polycrystalline silicon travels through the jaw crusher 400, the movable jaw plate 403 causes the polycrystalline silicon to break into smaller polycrystalline silicon pieces. The polycrystalline silicon pieces can vary in size from dust to nuggets to shards to flakes to oversize chunks. The size distribution of the polycrystalline silicon pieces will depend on various factors including the width of the discharge slot 418 and the residence time in the crushing cavity 404.
The jaw plates 402, 403 comprise materials that minimize contamination of silicon, such as materials possessing a hardness greater than or comparable to polycrystalline silicon. The jaw plates may comprise tungsten carbide, tungsten carbide with a cobalt binder, tungsten carbide with a nickel binder, Cr3C2, Cr3C2 with nickel-chrome alloy binder, or combinations thereof. Use of tungsten carbide containing materials may reduce the level of iron contaminants imparted to silicon by the comminuting operation. The hopper 425 for supplying the polycrystalline silibon rods or oversize polycrystalline silicon pieces, or both and a discharge chute (not shown) from the jaw crusher 400 can be made of, or lined with, the same materials of construction as the jaw plates 402, 403 or any other material of construction that minimize contamination of silicon. Such materials of construction include ultra high molecular weight polyethylene (UHMWPE), polypropylene, perfluoroalkoxy resin (PFA), polyurethane (PU), polyvinylidene difluoride (PVDF), TEFLON®, tungsten carbide, silicon, and ceramic.
One skilled in the art would recognize that multiple jaw crushers may be used in series to obtain a desired shape distribution or the size distribution described above, or both, or to recycle oversize polycrystalline silicon pieces, or both. One skilled in the art would recognize that conventional comminution apparatus, such as the jaw crushers, gyratory crushers, crushing roll machines, cone crushers, and table mills, disclosed in Introduction to Particle Technology, Ch. 10, “Particle Size Reduction”, John Wiley & Sons, Inc., New York, N.Y., April, 1999, pp. 241-263, can be used in this invention provided that the materials of construction of the parts of the comminution apparatus that contact the silicon comprise materials that minimize contamination of silicon. Suitable jaw crushers are commercially available from Morse Jaw Crushers from Metso Minerals Industries, Inc., of Danville, Pa., U.S.A.
One skilled in the art would recognize that alternative comminution apparatus may be used in addition to, or instead of, the jaw crusher in the methods of this invention. Suitable commninution apparatus are disclosed in U.S. Pat. Nos. 4,815,667; 5,346,141; and 5,464,159; EP 0573 855; JP 02565759; and JP 58145611.
The polycrystalline silicon pieces (broken rods) can be sorted manually or by use of an apparatus, such as the rotary silicon screen disclosed in U.S. Pat. No. 5,165,548 or the sorting apparatus disclosed in U.S. Pat. Nos. 3,905,556; 5,064,076; or 5,791,493 provided that the portions of the sorting apparatus that contact silicon comprise materials of construction that minimize contamination of silicon, such as those discussed above.
Alternatively, the polycrystalline silicon pieces may be sorted using an apparatus including a step deck classifier. The apparatus for sorting polycrystalline silicon pieces comprises
The step deck classifier comprises
The step deck classifier may further comprise one or more additional decks between the first deck and the final deck, where each additional deck comprises
The apparatus for sorting polycrystalline silicon pieces may further comprise a weigh scale under iii) the collection container or a dust removing system located upstream of the first gap, or both, or any other modification available to one of ordinary skill in the art without undue experimentation. One skilled in the art would recognize that more than one step deck classifier can be used in series to sort the polycrystalline silicon pieces.
An example of an apparatus for sorting polycrystalline silicon pieces and including a step deck classifier is shown in
The step deck classifier 500 will separate the polycrystalline pieces 513, 514, 515 into controlled particle size distributions based on the sizes of the gaps 507, 516, 518, 520, 522, and 524 between the decks 531, 510, 517, 519, 521, 523, and 525. The gaps 507, 516, 518, 520, 522, and 524 increase in size with the direction of conveyance. Smaller polycrystalline silicon pieces fall through the smaller gaps 507, 516, 518 and are collected in the collection container 509 for small size polycrystalline silicon pieces. Larger polycrystalline silicon pieces fall through the larger gaps 520, 522, 524 and are collected in the collection container 526 for larger size polycrystalline silicon pieces. Oversize polycrystalline silicon pieces are collected at the end of the step deck classifier 500 in the collection container 527 for oversize polycrystalline silicon pieces. The oversize polycrystalline silicon pieces can be recycled to the comminuting apparatus. One skilled in the art would recognize that polycrystalline silicon pieces having differing controlled particle size distribution may be withdrawn from the various decks of the step deck classifier through the gaps between the decks by varying the size of gaps, the number of collection containers, and the number and location of conveyors for moving polycrystalline silicon pieces to collection containers.
Weigh scales 528 can be integrated into the controls of the vibratory feeder 501 to fill collection containers 509, 526, 527 such as bags directly or shut off motion to change collection containers when a certain fill weight is reached.
One skilled in the art would recognize that the number of decks; the widths, depths, and shapes of grooves in each deck; the sizes of gaps between decks; and number of collection containers may vary to adjust the size distributions collected. Grooves may have different widths, depths, and shapes. Grooves may be, for example, triangular, square trapezoidal, or rounded.
As with the apparatus used to comminute the polycrystalline silicon, the parts of the apparatus used for sorting that contact polycrystalline silicon pieces are constructed of materials that will not contaminate silicon, such as the materials of construction described above for the jaw crusher 400.
Furthermore, one skilled in the art would recognize that the step deck classifier described above can be used to sort materials other than flowable chips, such as polycrystalline silicon pieces of larger sizes (e.g., larger than 45 mm), by varying the size of the decks; the widths, depths, and shapes of grooves in each deck; the sizes of gaps between decks; and size of collection containers.
The polycrystalline silicon pieces having a controlled particle size distribution prepared above optionally can be exposed to a magnetic field to remove contaminants. For example, the polycrystalline silicon pieces can be passed through a chamber containing a magnet to remove contaminants, or a magnet may be passed over the polycrystalline silicon pieces. The magnet may be a rare earth magnet or an electromagnet, or combinations thereof. The magnet may directly contact the polycrystalline silicon pieces or be in the near vicinity of the polycrystalline silicon pieces. The magnets remove much of the fine particulate having an appropriate susceptibility to the magnetic field. These particulates include ferromagnetic impurities such as iron and cobalt and paramagnetic impurities such as tungsten carbide, and other ferromagnetic impurities and paramagnetic impurities used in manufacture of materials of construction for the apparatus used to comminute and sort the silicon.
Alternatively, contaminants may be removed by processes disclosed in U.S. Pat. Nos. 3,905,556; 4,125,191; 4,157,953; 4,250,025; 4,345,995; 4,525,336; 5,297,744; and 5,830,282. Contaminants may be removed using chemical methods, such as those disclosed in EP 0 215 121 B1, in addition to, or instead of the methods involving magnetic fields.
Depending on the purity of the polycrystalline silicon rods used as the starting material and methods used to comminute and sort the silicon, the product at this step may have purity sufficient for use in preparing solar cell grade monocrystalline silicon wafers or electronic grade monocrystalline silicon wafers. However, if purity is insufficient for electronic grade applications, or both of these applications, the silicon may be surface cleaned to further remove impurities.
The polycrystalline silicon pieces can be surface cleaned by methods known in the art. Surface cleaning may be carried out in addition to, or instead of, the removal of contaminants method described above. For example, the broken rods can be cleaned by the process disclosed in U.S. Pat. No. 5,851,303 which comprises sequentially contacting the broken rods with gaseous hydrogen fluoride and then with an aqueous solution comprising at least one half percent hydrogen peroxide, and thereafter drying the broken rods. Alternatively, the broken rods can be cleaned by the process disclosed in JP Hei-05-48 11. Alternatively, the broken rods can be surface cleaned by anisotropic etching as described in Canadian Patent No. 954425 or U.S. Pat. No. 4,971,654. Other suitable surface cleaning methods include those disclosed by U.S. Pat. Nos. 4,588,571 and 6,004,402.
The resulting flowable-chips can be packaged by any convenient means, for example, manually or automatically placing the flowable chips in polyethylene bags.
The flowable chips described above can be used for solar cell grade applications or for electronic grade applications, depending on particle size distribution and purity. Specific applications for the flowable chips include initial charge applications such as initial charge maximization and initial charge top up, and recharge applications such as crucible recharge in a CZ process, as well as recharge maximization and recharge top up.
The flowable chips may be used in solar cell casting processes such as those described in U.S. Pat. Nos. 4,176,166; 4,312,700; 4,382,838; 4,572,812; 5,254,300; 5,431,869; 5,492,079; and 5,510,095; CN 1176319; DE 4441911; EP 0 869 102; EP 0095757; JP 10190025; JP 11116386; JP 58026019; JP 58099115; JP 62108515; and JP 9301709 in addition to, or instead of, the silicon described therein. Casting may comprise pouring molten silicon into a heated mold or melting polycrystalline silicon in a crucible and allowing the silicon to slowly cool and solidify.
For example, a suitable batch casting process comprises:
Alternatively, a continuous casting process can be used. A continuous casting process can comprise:
Alternatively, an apparatus for use in a suitable continuous casting process comprises a plurality of electrically conductive members arranged in a side-to side manner so as to define a container-like area having an open top and an open bottom. The apparatus further comprises a means for inducing high frequency AC electrical currents in each of the conductive members. A retractable support member is provided through the open bottom of the container-like area. The support member acts to support semiconductive material in the container-like area.
A suitable continuous casting process comprises:
The process may further comprise: 6) retracting the support member away from the container-like area in such a manner that molten semiconductive material that is supported by the support member will solidify into a cast ingot as said molten semiconductive material is retracted away from said conductive members, and
The flowable chips may be used in shaped growth processes, such as an Edge-defined, Film-fed, Growth (EFG) process for producing silicon ribbon, such as the EFG processes described by H. E. LaBelle, Jr., in “EFG The Invention and Application to Sapphire Growth,” Journal of Crystal Growth, vol. 50, 1980, pp. 8-17 and K. Koliwad, et al., “Proceedings of the Flat-plate Solar Array Project Research Forum on the High-speed Growth and Characterization of Crystals for Solar Cells,” Katherine A. Dumas, Proceedings Editor, Jet Propulsion Laboratory, California Institute of Technology, Pasadena, Calif., for U.S. DOE, Apr. 15, 1984, pp. 22-24. A suitable EFG process can comprise withdrawing a silicon ribbon from a meniscus of molten silicon defined by the edge of a die. The dimensions of the ribbon are controlled by the meniscus. The ribbon production rate and system heat balance should be carefully controlled.
The flowable chips may be used in an induction plasma process, such as those disclosed in JP 10182124 and Crystal Growth, ed. Brian R. Pamplin, Ch. 9, “Creation, Measurement and Control of Crystal Growth Environment,” Pergamon Press, Ltd., Oxford, 1975, pp. 343-344. In an example of a plasma induction process, a high frequency plasma torch, e.g., over 4 megaHertz (MHz), is used to melt silicon particles. The torch is formed by ionizing an inert gas such as argon by passing the gas through a high frequency electric field, which is applied between a cathode and anode. Once the argon stream is ionized to a high temperature plasma, silicon in powder form can be co-fed from a hopper into the plasma jet. The silicon will melt within the jet zone, and the molten silicon can be directed toward a water-cooled crucible or onto a growing crystalline silicon body. Flowable silicon chips in the appropriate size range for the plasma torch cavity can be used as the source of silicon for such a process.
The flowable chips may be used in electron beam melting processes, such as those disclosed in U.S. Pat. No. 5,454,424 and JP 62260710. An example electron beam melting process comprises melting polycrystalline silicon by scanning the same with an electron beam, and casting the resulting molten silicon according to any of the casting methods described herein. The polycrystalline silicon can comprise flowable chips.
The flowable chips may also be used in a Heat Exchanger Method (HEM). An HEM furnace can comprise a chamber containing a crucible surrounded by a heating element with a helium heat exchanger connected to the bottom of the crucible. Polycrystalline silicon is placed on top of a seed crystal to fill the crucible. The chamber is evacuated and the heating element is heated to melt the silicon. The seed crystal is prevented from melting by the flow of helium gas through the heat exchanger. The gas flow is gradually increased, lowering the temperature of the heat exchanger and causing silicon to gradually solidify and a crystal to grow outward from the seed crystal. The temperature of the molten silicon is controlled by the heating element; however, the temperature of the solid crystal is independently controlled by the heat exchanger. Dual-control of both heating and cooling allows control of the position and movement of the solid-liquid interface of the crystal formation process. HEM is described in “HEM Silicon”, Crystal Systems, The National Renewable Energy Laboratory, Golden, Colo.; and in Frederick Schmid and Chandra P. Khattak, “Cutting Silicon Wafer Costs for Photovoltaics,” Optical Spectra, May 1981.
The flowable chips may also be used in string ribbon processes, such as that disclosed in U.S. Pat. No. 4,689,109. An example of a string ribbon process may comprise:
The flowable chips may also be used in processes for casting silicon on a substrate, such as the processes disclosed in U.S. Pat. Nos. 4,095,329; 4,323,419; 4,447,289; 4,519,764; 4,561,486; 5,161,717; and 5,178,840; DE 3 210 492; EP 0 079 567; and JP 6168898. An example process comprises:
The flowable chips may also be used in sintering processes such as those disclosed in U.S. Pat. Nos. 5,006,317 and 5,499,598. An example of a sintering process comprises:
The flowable chips may be used in various crystal pulling processes, such as those disclosed in Crystal Growth, ed. Brian R. Pamplin, Ch. 13, “Crystal Pulling,” Pergamon Press, Ltd., Oxford, 1975, pp. 497-555. These include CZ processes using a crucible and crucible free processes, such as a pedestal, cold hearth, and cold crucible processes. Other cold crucible processes are disclosed by T. F. Ciszek “Some Applications of Cold Crucible Technology for Silicon Photovoltaic Material Preparation,” Journal of the Electrochemical Society, vol. 132, No. 4, April 1985.
This invention further relates to a method for recharging a crucible used in a CZ process. The method comprises pulling at least one ingot from the crucible and adding flowable chips to the crucible to recharge the crucible.
The ingot is removed from the CZ process apparatus without admitting air in the growth chamber. The flowable chips can be added during or after pulling the ingot. The flowable chips can be added in a continuous or batch mode.
The flowable chips are added to the crucible while the growth chamber is under vacuum or under an inert atmosphere, or both.
The flowable chips are added to the crucible while it is hot. Without wishing to be bound by theory, it is thought that if the crucible is cooled to a temperature that is too low, the crucible can break.
The flowable chips are added to the crucible in a manner that does not contaminate the silicon heel.
The flowable chips can be added to the crucible in a batch or continuous mode. The flowable chips can be added to the crucible containing molten silicon or a silicon heel that is at least partially solidified. The flowable chips can be added using various feeder systems.
The flowable chips can be added to the crucible using a vibration feeder system in a method comprising:
Inerting the hopper can be carried out by pulling vacuum on the hopper and purging the hopper with an inert gas such as semiconductor grade argon, helium, or nitrogen at least one time.
The feed apparatus comprises a feed tube, optionally a feed tray from the hopper to the feed tube, and optionally a lance from the feed tube into the crucible. The hopper, feed tray, feed tube, lance, or a combination thereof, can be vibrated to move the flowable chips.
Step iii) can be carried out by vibration of all or a portion of the vibration feeder system at the resonance frequency of the flowable chips.
The flowable chips can be added to the crucible in a batch mode. The flowable chips can be added to the crucible containing a heel that is at least partially solidified. The flowable chips can be added using a canister feeder system (see for example, U.S. Pat. No. 5,488,924 and Daud, T. and Kachare, A., Advanced Czochralski Silicon Growth Technology for Photovoltaic Modules, DOE/JPL-1012-70, Distribution Category UC-63b, 5101-2-7 Flat-Plate Solar Array Project, JPL Publication 82-35, Sep. 15, 1982).
The flowable chips can be added to the crucible using a canister feeder system in a method comprising:
The disclosures of methods of using polycrystalline silicon in U.S. Pat. Nos. 3,998,686; 4,002,274; 4,095,329; 4,176,166; 4,312,700; 4,323,419; 4,382,838; 4,394,352; 4,447,289; 4,519,764; 4,557,795; 4,561,486; 4,572,812; 4,661,324; 4,689,109; 4,968,380; 5,006,317; 5,080,873; 5,098,229; 5,161,717; 5,178,840; 5,229,082; 5,242,667; 5,254,300; 5,431,869; 5,454,424; 5,462,010; 5,488,924; 5,499,598; 5,510,095; 5,492,079; 5,690,733; 5,762,491; 5,868,835; 5,902,395; and 6,217,649 are hereby incorporated by reference. One skilled in the art would recognize that flowable chips can be used in addition to or instead of, the silicon starting materials and recharge materials described therein as well as in any other known method for processing polycrystalline silicon.
The flowable chips can also be used instead of granules in feeder systems designed to feed granules. The flowable chips can be used in feeder systems comprising volumetric feeder systems, canister feeder systems, weigh-belt feeder systems, vibration feeder systems, chip thruster feeder systems, pneumatic transport feeder systems, stagnation flow delivery lance feeder systems, rotating disk feeder systems, or auger feeder systems.
Examples of volumetric feeder systems are disclosed in Fickett, B. and Mihalik, G., ‘Economic feeder for recharging and “topping off”’, Journal of Crystal Growth, Siemens Solar Industries, vol. 211, 2000, pp. 372-377. U.S. Pat. Nos. 3,998,686; 5,080,873; and 5,762,491; and JP 62-260791. Examples of canister feeder systems are disclosed in U.S. Pat. Nos. 4,394,352; 4,557,795; 5,229,082; and 5,488,924. Examples of weigh-belt feeder systems are disclosed in U.S. Pat. No. 6,217,649. Examples of vibration feeder systems are disclosed in U.S. Pat. No. 5,462,010 and JP 02-617197 B2. Examples of chip thruster feeder systems are disclosed in U.S. Pat. No. 4,661,324. Examples of pneumatic transport feeder systems are disclosed in U.S. Pat. Nos. 4,968,380 and 5,098,229. Examples of stagnation flow delivery lance feeder systems are disclosed in U.S. Pat. Nos. 5,690,733; 5,868,835; and 5,902,395. Examples of rotating disk feeder systems are disclosed in U.S. Pat. Nos. 4,002,274 and 5,242,667. Examples of auger feeder systems are disclosed in Daud, T. and Kachare, A., Advanced Czochralski Silicon Growth Technology for Photovoltaic Modules, DOE/JPL-1012-70, Distribution Category UC-63b, 5101-2-7 Flat-Plate Solar Array Project, JPL Publication 82-35, Sep. 15, 1982. One skilled in the art would recognize that the flowable chips disclosed herein can be used in any other known and suitably sized feeder for processing polycrystalline silicon
These examples are intended to illustrate the invention to one of ordinary skill in the art and should not be interpreted as limiting the scope of the invention.
WC, Co, GC-712 (General Carbide Corp. powder containing 12% Co and 88% WC and having particle size of 0.6 micrometers), and sintered WC/Co powders are spread on plastic. Initial weight of the powder is recorded. An Eriez® rare earth plate magnet is passed over each powder at a distance of less than 2 millimeters. Final weight of the powder is recorded. The results are in Table 1.
Example 1 shows that impurities may be removed from polycrystalline silicon pieces using a magnet. In particular, WC/Co impurities introduced by the jaw crusher in
Four samples of flowable chips are prepared by the following method. Polycrystalline silicon U-rod shaped material is obtained from a cold wall, Siemens-type bell jar reactor. Following removal of the carbon socket end, silicon in U-rod form is broken into 10-15 centimeter (cm) pieces using a low contamination impact tool on a polyethylene table. The resulting silicon chunks are fed to the jaw crusher 400 shown in
The collected polycrystalline silicon pieces are then crushed again using the same equipment. Following the crushing step, the collected polycrystalline silicon pieces are transferred to a UHMWPE hopper, which acts to regulate the flow rate of the silicon pieces, and are fed onto the step deck classifier 500 shown in
Polycrystalline silicon U-rods are obtained from a cold wall, Siemens-type bell jar reactor. Following removal of the carbon socket end, silicon in U-rod form is broken into 4-inch pieces using a low contamination impact tool on a polyethylene table. The resulting polycrystalline silicon chunks are fed to the jaw crusher 400 shown in
These samples are analyzed for bulk impurities and surface impurities. The bulk metals values are obtained using acid digestion of a freeze-out tip from an etched, float-zoned core. The core is taken from a polycrystalline silicon rod. The procedure for obtaining the bulk metals values is described in U.S. Pat. No. 4,912,528. The metals concentration is measured from the analyte using atomic absorption.
Carbon is measured from the float-zoned core. A slice is taken from the core. The slices are lapped and polished. Fourier transform infrared spectroscopy is used to measure the concentration of carbon in the silicon.
Phosphorous, boron, aluminum, and arsenic are measured from the float-zoned core using a technique known as dispersive photoluminescence (PL). With this test, a single crystal slice from the float-zoned core is chemically polished. By cooling the slice to the temperature of liquid helium, an argon laser is used to cause a photon emission in the sample. The measured intensity of the emission of recombining electron-hole pairs is used to determine the concentration of these impurities.
Donor is a calculated value, which can be obtained from measuring the resistivity of the silicon core.
Surface impurities are measured by the method in U.S. Pat. No. 5,851,303. The resulting purity of the silicon is reported below in Tables 3 and 4. Controlled particle size distribution of each sample of the polycrystalline silicon pieces is 1 to 12 mm.
This application claims priority under 35 U.S.C. §119(e) to U.S. Provisional Patent Application Ser. No. 60/358,851, filed on Feb. 20, 2002.
Number | Name | Date | Kind |
---|---|---|---|
2975036 | Taylor, et. al. | Mar 1961 | A |
3645454 | Fowler | Feb 1972 | A |
3878994 | Tee | Apr 1975 | A |
3897330 | Rhys | Jul 1975 | A |
3905556 | Drage | Sep 1975 | A |
3998686 | Meiling et al. | Dec 1976 | A |
4002274 | Rice | Jan 1977 | A |
4036595 | Lorenzini et al. | Jul 1977 | A |
4095329 | Ravi | Jun 1978 | A |
4125191 | Peace | Nov 1978 | A |
4157953 | Mawardi | Jun 1979 | A |
4158041 | Tolley | Jun 1979 | A |
4176166 | Carman | Nov 1979 | A |
4250025 | Causton et al. | Feb 1981 | A |
4282184 | Fiegl et al. | Aug 1981 | A |
4312700 | Helmreich et al. | Jan 1982 | A |
4323419 | Wakefield | Apr 1982 | A |
4345995 | Ahrendt | Aug 1982 | A |
4382838 | Authier | May 1983 | A |
4385702 | Lenker et al. | May 1983 | A |
4394352 | Helda et al. | Jul 1983 | A |
4447289 | Geissler et al. | May 1984 | A |
4456499 | Lin | Jun 1984 | A |
4519764 | Maeda et al. | May 1985 | A |
4525336 | Griesshammer et al. | Jun 1985 | A |
4557795 | Helda et al. | Dec 1985 | A |
4561486 | Maeda et al. | Dec 1985 | A |
4565913 | Yatsurugi et al. | Jan 1986 | A |
4572812 | Ciszek | Feb 1986 | A |
4588571 | Bildl et al. | May 1986 | A |
4661324 | Sink et al. | Apr 1987 | A |
4689109 | Sachs | Aug 1987 | A |
4691866 | Belk | Sep 1987 | A |
4715950 | Danner et al. | Dec 1987 | A |
4802951 | Clark et al. | Feb 1989 | A |
4810368 | Seider et al. | Mar 1989 | A |
4815667 | Keller | Mar 1989 | A |
4869109 | Miglianico et al. | Sep 1989 | A |
4871117 | Baueregger et al. | Oct 1989 | A |
4901863 | Lancaster | Feb 1990 | A |
4912528 | Hwang et al. | Mar 1990 | A |
4927489 | Campbell et al. | May 1990 | A |
4933074 | Fuller et al. | Jun 1990 | A |
4968380 | Freedman et al. | Nov 1990 | A |
4971654 | Schnegg et al. | Nov 1990 | A |
5006317 | Sanjurjo | Apr 1991 | A |
5016683 | Latka | May 1991 | A |
5037503 | Kajimoto et al. | Aug 1991 | A |
5064076 | Braun et al. | Nov 1991 | A |
5077028 | Age | Dec 1991 | A |
5080873 | Ono | Jan 1992 | A |
5098229 | Meier et al. | Mar 1992 | A |
5161717 | Geyling | Nov 1992 | A |
5165548 | Dumler et al. | Nov 1992 | A |
5178840 | Geyling | Jan 1993 | A |
5188128 | Studt | Feb 1993 | A |
5229082 | Seidensticker et al. | Jul 1993 | A |
5242667 | Koziol et al. | Sep 1993 | A |
5242671 | Allen et al. | Sep 1993 | A |
5249988 | Lu | Oct 1993 | A |
5254300 | Priewasser et al. | Oct 1993 | A |
5297744 | Clinton | Mar 1994 | A |
5324488 | Klingshirn et al. | Jun 1994 | A |
5346141 | Kim et al. | Sep 1994 | A |
5361128 | Bourbina et al. | Nov 1994 | A |
5431869 | Kumar et al. | Jul 1995 | A |
5436164 | Dumler et al. | Jul 1995 | A |
5454424 | Mori et al. | Oct 1995 | A |
5462010 | Takano et al. | Oct 1995 | A |
5464159 | Wolf et al. | Nov 1995 | A |
5488924 | Horvath et al. | Feb 1996 | A |
5492079 | Geissler et al. | Feb 1996 | A |
5499598 | Oda | Mar 1996 | A |
5510095 | Aratani et al. | Apr 1996 | A |
5588993 | Holder | Dec 1996 | A |
5660335 | Koppl et al. | Aug 1997 | A |
5690733 | Nagai et al. | Nov 1997 | A |
5700321 | Niikura | Dec 1997 | A |
5746322 | LaVeine et al. | May 1998 | A |
5753567 | Banan et al. | May 1998 | A |
5762491 | Williams et al. | Jun 1998 | A |
5791493 | Meyer | Aug 1998 | A |
5814148 | Kim et al. | Sep 1998 | A |
5820688 | Koppl et al. | Oct 1998 | A |
5830282 | Olashuk | Nov 1998 | A |
5851303 | Hwang et al. | Dec 1998 | A |
5855232 | Oda et al. | Jan 1999 | A |
5866094 | Niikura | Feb 1999 | A |
5868835 | Nagai et al. | Feb 1999 | A |
5871581 | Atami et al. | Feb 1999 | A |
5891245 | Atami et al. | Apr 1999 | A |
5902395 | Nagai et al. | May 1999 | A |
5904254 | Tinsley et al. | May 1999 | A |
5919303 | Holder | Jul 1999 | A |
5976481 | Kubota et al. | Nov 1999 | A |
5984105 | Lease et al. | Nov 1999 | A |
6004402 | Cercone et al. | Dec 1999 | A |
6024306 | Koppl et al. | Feb 2000 | A |
6040544 | Schantz et al. | Mar 2000 | A |
6063697 | Wolf et al. | May 2000 | A |
6110272 | Alkawa et al. | Aug 2000 | A |
6217649 | Wallace et al. | Apr 2001 | B1 |
6265683 | Flottmann et al. | Jul 2001 | B1 |
6284040 | Holder et al. | Sep 2001 | B1 |
6309467 | Wochner et al. | Oct 2001 | B1 |
6313013 | Flottmann et al. | Nov 2001 | B1 |
6375011 | Flottmann et al. | Apr 2002 | B1 |
6503563 | Yatsurugi et al. | Jan 2003 | B1 |
6589332 | Holder et al. | Jul 2003 | B1 |
20030041795 | Moroishi et al. | Mar 2003 | A1 |
20030145781 | Von Ammon | Aug 2003 | A1 |
20030150378 | Winterton et al. | Aug 2003 | A1 |
Number | Date | Country |
---|---|---|
954425 | Sep 1974 | CA |
3913379 | Apr 1989 | DE |
199 45 038 | Dec 2000 | DE |
199 45 037 | Mar 2001 | DE |
1 368 224 | Feb 1973 | EP |
0 079 567 | Nov 1982 | EP |
0 095 757 | May 1983 | EP |
0 215 121 | Mar 1986 | EP |
0 329 163 | Feb 1989 | EP |
0 539 097 | Apr 1993 | EP |
0 539 097 | Apr 1993 | EP |
0 573 855 | Apr 1995 | EP |
0 448 710 | Apr 1996 | EP |
0 474 810 | Jan 1997 | EP |
0 869 102 | Oct 1998 | EP |
0 477 784 | Dec 1998 | EP |
0 856 599 | Mar 2000 | EP |
1 043 249 | Oct 2000 | EP |
1 043 249 | Oct 2000 | EP |
11-292682 | Oct 1999 | JP |
WO 9920815 | Apr 1999 | WO |
WO 0006446 | Feb 2000 | WO |
WO 0127029 | Apr 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20030159647 A1 | Aug 2003 | US |
Number | Date | Country | |
---|---|---|---|
60358851 | Feb 2002 | US |