Glass piece and methods of manufacturing glass pieces and semiconductor devices with glass pieces

Information

  • Patent Grant
  • 11148943
  • Patent Number
    11,148,943
  • Date Filed
    Wednesday, May 16, 2018
    6 years ago
  • Date Issued
    Tuesday, October 19, 2021
    2 years ago
Abstract
A semiconductor element is formed in a mesa portion of a semiconductor substrate. A cavity is formed in a working surface of the semiconductor substrate. The semiconductor substrate is brought in contact with a glass piece made of a glass material and having a protrusion. The glass piece and the semiconductor substrate are arranged such that the protrusion extends into the cavity. The glass piece is bonded to the semiconductor substrate. The glass piece is in-situ bonded to the semiconductor substrate by pressing the glass piece against the semiconductor substrate. During the pressing a temperature of the glass piece exceeds a glass transition temperature and the temperature and a force exerted on the glass piece are controlled to fluidify the glass material and after re-solidifying the protrusion completely fills the cavity.
Description
BACKGROUND

Glass compression molding uses appropriate molds to form for example optical components such as lenses. Dry etching, wet etching, mechanical processes or laser ablation are used to form cavities in glass substrates.


It is desirable to provide new methods of forming glass pieces with patterned surfaces.


SUMMARY

According to an embodiment of a method of manufacturing a semiconductor device, a semiconductor element is formed in a mesa portion of a semiconductor substrate. A cavity is formed in a working surface of the semiconductor substrate. The semiconductor substrate is brought in contact with a glass piece made of a glass material and having a protrusion. The glass piece and the semiconductor substrate are arranged such that the protrusion extends into the cavity. The glass piece is bonded to the semiconductor substrate. The glass piece is in-situ bonded to the semiconductor substrate by pressing the glass piece against the semiconductor substrate. During the pressing a temperature of the glass piece exceeds a glass transition temperature and the temperature and a force exerted on the glass piece are controlled to fluidify the glass material and after re-solidifying the protrusion completely fills the cavity.


According to an embodiment of a method of manufacturing a glass piece, a mold substrate of a single-crystalline material is formed by etching a sharp-angled cavity into a working surface of the mold substrate. A source material based on a glass is brought in contact with the working surface provided with the sharp-angled cavity. The source material and the mold substrate are pressed against each other. A temperature of the source material and a force exerted on the source material are controlled such that source material is fluidified and flows into the sharp-angled cavity. The sharp angles of the sharp angled cavity are disposed below the working surface.


Those skilled in the art will recognize additional features and advantages upon reading the following detailed description, and upon viewing the accompanying drawings.





BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings are included to provide a further understanding of the present invention and are incorporated in and constitute a part of the specification. The drawings illustrate embodiments of the present invention and together with the description serve to explain principles of the invention. Other embodiments of the invention and intended advantages will be readily appreciated as they become better understood by reference to the following detailed description. The elements of the drawings are not necessarily to scale relative to each other. Like reference numerals designate corresponding similar parts.



FIG. 1A is a schematic cross-sectional view of an arrangement including a mold substrate, a source material based on a glass and a plate for exerting a force on the source material for illustrating the manufacturing of a glass piece according to an embodiment using a mold substrate with cavities having a slope angle of 90 degrees.



FIG. 1B is a cross-sectional view of the arrangement of FIG. 1A after fluidified source material has filled the rectangular cavities.



FIG. 1C is a cross-sectional view of a glass piece emerging from the process of FIG. 1B after removing the plate and the mold substrate.



FIG. 2A is a schematic cross-sectional view of an arrangement including a mold substrate, a source material based on a glass and a plate for exerting a force on the source material for illustrating the manufacturing of a glass piece according to an embodiment using a mold substrate with cavities of different dimension and slope angles.



FIG. 2B is a cross-sectional view of the arrangement of FIG. 2A after fluidified source material has filled the cavities.



FIG. 2C is a cross-sectional view of a glass piece emerging from the process of FIG. 2B after removing the plate and the mold substrate.



FIG. 3A shows photographic images of a plan view of a glass piece emerging from a method of manufacturing a glass piece according to an embodiment.



FIG. 3B is a polished cross-section image of an arrangement with a glass piece bonded to a single-crystalline silicon mold substrate according to a further embodiment.



FIG. 3C shows scanning electron microscope images from a glass piece emerging from a method of manufacturing a glass piece according to a further embodiment.



FIG. 4A is a schematic perspective view of a section of an optical integrated device according to a further embodiment.



FIG. 4B is a schematic plan view of a micro fluidic device according to an embodiment.



FIG. 5A shows a schematic cross-sectional view of a pre-patterned glass piece and a semiconductor substrate to illustrate details of an embodiment referring to the manufacture of a semiconductor device according to another embodiment.



FIG. 5B is a simplified cross-sectional view of the glass piece and the semiconductor substrate of FIG. 5A after adhesive bonding.



FIG. 6 is a simplified flowchart of a method of manufacturing a glass piece according to an embodiment.





DETAILED DESCRIPTION

In the following detailed description, reference is made to the accompanying drawings, which form a part hereof, and in which are shown by way of illustrations specific embodiments in which the invention may be practiced. It is to be understood that other embodiments may be utilized and structural or logical changes may be made without departing from the scope of the present invention. For example, features illustrated or described as part of one embodiment can be used on or in conjunction with other embodiments to yield yet a further embodiment. It is intended that the present invention includes such modifications and variations. The examples are described using specific language which should not be construed as limiting the scope of the appending claims. The drawings are not scaled and are for illustrative purposes only. For clarity, the same elements or manufacturing processes have been designated by the same references in the different drawings if not stated otherwise.



FIG. 1A shows a mold substrate 100 which is made of a single-crystalline material, for example a semiconductor single-crystalline material. According to an embodiment, the single-crystalline material is single-crystalline silicon. One or more cavities 102 are formed in a working surface 101 of the mold substrate 100 and extend from the working surface 101 into the mold substrate 100. The cavities 102 may be formed by isotropic etch processes, anisotropic etch processes, by methods using laser beams or by mechanical processes. For example, different crystal surfaces of the single-crystalline material can be etched at different speeds such that slope angles of the cavities can be precisely adjusted to, for example 45 degrees.


A source material 200a is provided in contact with the working surface 101 of the mold substrate 100. The source material 200a is based on a glass. According to an embodiment, the source material 200a exhibits a glass transition and fluidifies when the temperature of the source material 200a exceeds the glass transition temperature. The source material 200a may be soda-lime glass, undoped silica, or silica doped with at least one dopant, the dopant(s) being selected from a group containing boron B, sodium Na, calcium Ca, potassium K, and aluminum Al. Other embodiments provide a source material 200a which is a polymer, for example polynorbornene, polystyrene, polycarbonate, polyimide, or benzocyclobutene, or a metal or metal alloy.


The source material 200a may be provided as a powder, as glass frit, or may include glass pellets. According to another embodiment, the source material 200a is a flat piece, e.g. a disk with a flat working surface 201 arranged in contact with the mold substrate 100. According to an embodiment the source material 200a is a flat glass disk.


The source material 200a and the mold substrate 100 are pressed against each other. For example the source material 200a is provided on the working surface 101 of the mold substrate 100 and the source material 200a is pressed against the working surface 101. A temperature of the source material 200a and a force exerted on the source material 200a are controlled such that at least a portion of the source material 200a along the interface with the mold substrate 100 fluidifies. The source material may be fluidified before or during pressing. A plate 900 may be provided that presses the source material 200a towards the mold substrate 100.


For example, the source material 200a exhibits a glass transition and a force 905 exerted on the source material 200a and a temperature of the source material 200a are controlled to exceed its glass transition temperature in the course of pressing. According to another embodiment, the source material 200a is heated up beyond the glass transition temperature before a force 905 is exerted on the source material 200a. By exerting the force 905, the fluidified source material 200a flows into the cavity 102 and may fill at least an upper portion of the cavity 102 formed in the mold substrate 100. According to an embodiment the process of pressing is controlled such that fluidified source material 200a fills the cavity 102 completely. Then the force 905 exerted on the source material 200a and the temperature of the source material 200a are controlled in a way that the fluidified source material 200a re-solidifies.



FIG. 1B shows the re-solidified source material forming a glass piece 200 with a protrusion 202 completely filling the cavity 102 in the mold substrate 100. According to an embodiment, the glass piece 200 may be in-situ bonded to the mold substrate 100 in the course of the pressing or the re-solidifying process such that the glass piece 200 and the mold substrate 100 forms a laminate or a bonded composite after re-solidifying of the source material 200a.


The plate 900 may be a single-crystalline material, for example a single-crystal semiconductor material. According to an embodiment, the plate 900 is made from single-crystalline silicon. The plate 900 may be bonded to the glass piece 200 during or after pressing to form a laminate or a bonded composite with the glass piece 200 and the mold substrate 100. According to another embodiment, another press medium is provided instead of the plate 900. According to other embodiments the plate 900 is made from a non-sticking material, for example a ceramic or a glass material different from the source material.


The mold substrate 100 is removed, for example using a combination of polishing methods like chemical mechanical polishing (CMP) and dry or wet etch methods which remove the material of the mold substrate 100 with high selectivity against the material of the glass piece 200. Also laser ablation is possible for removing the mold substrate 100. According to another embodiment, the mold substrate 100 or the source material 200a is provided with a non-sticking layer before bringing the source material 200a in contact with the working surface 101 of the mold substrate 100. Then the mold substrate 100 and the glass piece 200 may be separated from each other in a nondestructive way after re-solidification of the source material 200a.


The at least one cavity 102 of the mold substrate 100 may have a width of 10 micrometer or more and of 2 millimeter or less such that a glass piece 200 with protrusions 202 having a width from 10 micrometer to 2 millimeter may be formed. The heights of the protrusions 202 may be in the same range.



FIG. 1C shows the glass piece 200 after removing the plate 900 and the mold substrate 100. Unevenness and impurities on the surface of the glass piece 200 can be removed with mechanical and/or chemical methods. The method provides glass pieces with a 3D patterned surface and showing no shrink as regards the pattern in the mold substrate used for the manufacture of semiconductor devices, such that glass pieces provide high mechanical, chemical and temperature stability, insulation strength and dielectric strength. The glass piece 200 may be used as a template or form in further processes.


According to another embodiment, one or more protrusions are formed in the working surface 101 of the mold substrate 100 and extend outward from the working surface 101, wherein the source material 200s and the mold substrate 100 are pressed against each other while a temperature of the source material 200a and a force exerted on the source material 200a are controlled such that fluidified source material enwraps the protrusion(s).



FIG. 2A shows a mold substrate 100 with a plurality of cavities 101, 103, 105, 107 that may differ in shape and size. For example, the mold substrate 100 may be made of single-crystalline silicon in which the cavities 101, 103, 105, 107 are etched using different etch processes. For example, cavities 101, 103 may be etched using a wet etch process which etches specific crystallographic surfaces at different etch rates such that the cavities 101, 103 have a certain slope angle with regard to the working surface 101. The slope angle may be 80 degrees or less, and may be more than 10 degrees, for example between 30 and 60 degrees. According to an embodiment the slope angle is about 45 degrees. Other cavities 105, 107 may be formed using an etch regime which is less selective as regards crystallographic surfaces, for example reactive ion etching such that cavities with steep slope angles greater 80 degrees, for example close to 90 degrees can be etched. Further, by filling a lower section of the cavity 105 with an auxiliary layer and depositing a collar-like mask in the upper section of the cavity 105, removing the auxiliary layer and controlling a further isotropic etch process may result in a bottle shape of the cavity 105.


By using different etch regimes/etching times for different sections of the mold substrate 100, cavities 101, 103, 105, 107 of different depths may be formed in the mold substrate 100.


A force 905 is exerted on a plate 900 that is arranged to press a source material 200a against the working surface 101 of the mold substrate 100. The force 905 and the temperature of the source material 200a are controlled such that at least some of the source material 200a fluidifies and fluidified source material 200a flows into and fills the cavities 101, 103, 105, 107 of the mold substrate 100. After filling the cavities 101, 103, 105, 107 the source material 200a re-solidifies.



FIG. 2B shows the re-solidified source material 200a forming a glass piece 200 with protrusions 201, 203, 205, 207 defined by the cavities 101, 103, 105, 107 of the mold substrate 100. The glass piece 200 is in-situ bonded with the mold substrate 100 and may be in-situ bonded also with the plate 900, provided the plate 900 is made of a bondable material. The single-crystalline silicon of the mold substrate 100 is removed selectively against the material of the glass piece 200.



FIG. 2C shows the resulting glass piece 200. The glass piece 200 comprises a patterned surface 201 in which at least one protrusion is formed which has a slope angle with regard to the patterned surface 201 of less than 80 degrees, for example between 40 and 50 degrees. According to an embodiment, the protrusion has a slope angle of 45 degrees with regard to the patterned surface 201. The scheme may be applied to protrusions on the mold substrate 100 accordingly.


According to an embodiment, on the working surface 201 at least a first 203 and a second protrusion 207 are formed, wherein the first and the second protrusion 203, 207 have slope angles which differ from each other by at least 5 degrees. According to another embodiment, the glass piece 200 has the first 203 and a third protrusion 201, wherein the heights of the first and the third protrusion 203, 201 over the working surface 201 differ by at least 20% of the lower one. The at least one protrusion 203 may have a height of 10 micrometer or more. According to an example, the at least one protrusion 203 has a height of 5 mm or less. The at least one protrusion 203 may have a width of 10 micrometer or more. According to further embodiments, the mold substrate 100 may comprise protrusions in addition to the cavities 102 such that in the glass piece 200 cavities are formed in addition to the protrusions 202. The embodiments provide a simple and reliable method for obtaining 3D patterned glass surfaces with pattern widths of less than 1 millimeter.



FIG. 3A shows a microscope image of a glass piece 200 emerging from the above-described method. The left image focuses the base of a protrusion 202 and the image on the right side focuses a top edge of the protrusion 202. The protrusion 202 is cross-shaped wherein the branches of the cross have a width of about 250 micrometers at the base and about 30 micrometers at the top. The height of the protrusion is 125 micrometers and the slope angle is about 45 degrees.



FIG. 3B shows a cross-sectional image of a mold substrate 100, which is in-situ bonded to a glass piece 200 and which has a cavity 102 with a slope angle of about 45 degree with regard to a working surface 101. The re-solidified glass material of the glass piece 200 fills the cavity 102 completely, and the protrusion 202 of the glass piece 200 extending into the cavity 102 shows well-defined sidewalls and a slope angle corresponding to that of the cavity 102.



FIG. 3C shows scanning electron microscope images from a glass piece emerging from a method of manufacturing a glass piece according to a further embodiment. Protrusions of different shape form a 3D pattern on a working surface of the glass piece.



FIG. 4A refers to an embodiment concerning the manufacture of integrated optical devices. The working surface of a mold substrate forms a three-dimensional template for a pattern on a working surface of a glass piece 200. The glass piece 200 is manufactured by arranging a source material based on a glass on a working surface of a mold substrate, which is made of a single-crystalline material. The mold substrate comprises a plurality of cavities. The source material is pressed against the working surface of the mold substrate. During pressing, a temperature of the source material and a force exerted on the source material are controlled to fluidify at least portions of the source material. Fluidified source material flows into the cavities. The source material is controlled to re-solidify, wherein the re-solidified source material forms the glass piece 200 with protrusions 202a, 202b. The protrusions 202a, 202b may form optical waveguides and further optical components on the working surface 201 of the glass piece 200. By a physical vapor deposition, suitable metals for mirror elements for integrated optical applications may be deposited on the glass piece 200.



FIG. 4A shows an example of an integrated optical device with the glass piece 200. On a working surface 201 of the glass piece 200 protrusions form optical waveguides 202a and an optical filter 202b. The glass piece 200 may be arranged on a carrier 910.



FIG. 4B refers to an embodiment concerning the manufacture of micro fluidic devices. A source material, which is based on a glass, is arranged on a working surface of a mold substrate. The mold substrate is made of a single-crystalline material, for example single-crystalline silicon. A 3D pattern including protrusions and/or cavities is formed on the working surface. The source material is pressed against the working surface of the mold substrate. During pressing, a temperature of the source material and a force exerted on the source material are controlled such that at least a portion of the source material fluidifies and fluidified source material flows into cavities and fills the 3D pattern. The fluidified source material re-solidifies to form a glass piece 200 with a 3D pattern being the counterpart of the template formed by the 3D pattern on the working surface of the mold substrate. The glass piece forms a portion of a micro fluidic device. A cover substrate may be provided on the 3D pattern of the glass piece 200 to form channels from grooves of the 3D pattern. The channels are adapted to pass a fluid.



FIG. 4B shows a top view on a micro fluidic device including channels 202c and reservoirs 202d.



FIG. 5A refers to a method of manufacturing a semiconductor device. A glass piece 200 is manufactured according to the methods as described in FIGS. 1A to 1C and 2A to 2C. In a working surface 301 of a semiconductor substrate 300 one or more cavities 302 is/are formed. A semiconductor element, for example a diode, a transistor, a field effect transistor or an IGBT is formed in a mesa portion 305 of the semiconductor substrate 300 outside the cavities 302. The semiconductor substrate 300 is brought in contact with a glass piece 200. The glass piece 200 has one or more protrusions 202 which are formed to match with and fit into the cavities 302. The glass piece 200 and the semiconductor substrate 300 are arranged such that the protrusions 202 extend into the cavities 302. Then, the glass piece 200 is bonded to the semiconductor substrate 300.


According to an embodiment an adhesive material 400a is provided between the semiconductor substrate 300 and the glass piece 200 before the bonding is performed. The glass piece 200 is adhesive bonded to the semiconductor substrate 300 through the adhesive material 400a. The adhesive material 400a may be a polymer. According to other embodiments, the adhesive material 400a is an inorganic material, for example BPSG (boron-phosphorous-silicate glass), glass solder, metal or metal alloys. The adhesive material 400a may be applied to the semiconductor substrate 300, to the glass piece 200 or to both. For example, the adhesive material 400a may be applied to cover the bottom of the cavities 302 or the tops of the mesa portion 305 or both.



FIG. 5B shows an adhesive layer 400 formed from the cured adhesive material 400a which adhesive bonds the glass piece 200 and the semiconductor substrate 300. According to another embodiment, the glass piece 200 is in-situ bonded to the semiconductor substrate 300 by pressing the glass piece 200 against the semiconductor substrate 300, wherein during the pressing a temperature of the glass piece 200 and a force exerted on the glass piece 200 are controlled to fluidify the glass material. The force and the temperature are controlled such that fluidified glass material re-solidifies. After re-solidifying the glass piece 200 is bonded to the semiconductor substrate 300 and the protrusions 202 completely fill the cavities 302 in the semiconductor substrate 300.


According to an embodiment the semiconductor substrate 300 is formed with a cavity 302 in the working surface 301 of the semiconductor substrate 300, wherein the cavity 302 has a width of at least 10 micrometers or a slope angle less than 80 degree, for example 45 degree with regard to the working surface 301 of the semiconductor substrate 300. For example, the protrusion 202 may form an edge isolator for integrated circuits, for example power MOSFETs, IGBTs (insulated gate bipolar transistors), diodes, transistors, logic circuits, driver circuits, processor circuits or memory circuits.


According to another embodiment, a cavity forming a grid is formed in the working surface 301 of a semiconductor substrate 300. The cavity extends along and within kerf areas, wherein a width of the cavity is wider than a width of the kerf areas. The glass piece 200 comprises a protrusion 202 that forms a grid and that matches with the grid formed by the cavity 302. The semiconductor substrate 300 is ripped or sawed after the bonding along the kerf areas to obtain a plurality of semiconductor dies from the semiconductor substrate 300. Each semiconductor die includes a glass frame emerging from the glass piece.



FIG. 6 refers to a method of manufacturing a glass piece. A source material based on a glass is arranged in contact with a single-crystalline mold substrate having a cavity (Step 602). The source material is pressed against the mold substrate, wherein the source material fluidifies and fills the cavity (Step 604). The re-solidified source material forms a glass piece that may be in-situ bonded to the mold substrate.


Spatially relative terms such as “under”, “below”, “lower”, “over”, “upper” and the like, are used for ease of description to explain the positioning of one element relative to a second element. These terms are intended to encompass different orientations of the device in addition to different orientations than those depicted in the figures. Further, terms such as “first”, “second”, and the like, are also used to describe various elements, regions, sections, etc. and are also not intended to be limiting. Like terms refer to like elements throughout the description.


As used herein, the terms “having”, “containing”, “including”, “comprising” and the like are open ended terms that indicate the presence of stated elements or features, but do not preclude additional elements or features. The articles “a”, “an” and “the” are intended to include the plural as well as the singular, unless the context clearly indicates otherwise.


It is to be understood that the features of the various embodiments described herein may be combined with each other, unless specifically noted otherwise.


Although specific embodiments have been illustrated and described herein, it will be appreciated by those of ordinary skill in the art that a variety of alternate and/or equivalent implementations may be substituted for the specific embodiments shown and described without departing from the scope of the present invention. This application is intended to cover any adaptations or variations of the specific embodiments discussed herein. Therefore, it is intended that this invention be limited only by the claims and the equivalents thereof.

Claims
  • 1. A method of manufacturing a semiconductor device, the method comprising: forming a semiconductor element in a mesa portion of a semiconductor substrate;forming a cavity in a working surface of the semiconductor substrate;bringing the semiconductor substrate in contact with a glass piece made of a glass material and having a protrusion, wherein the glass piece and the semiconductor substrate are arranged such that the protrusion extends into the cavity; andbonding the glass piece to the semiconductor substrate, wherein the glass piece is in-situ bonded to the semiconductor substrate by pressing the glass piece against the semiconductor substrate, wherein during the pressing a temperature of the glass piece exceeds a glass transition temperature and the temperature and a force exerted on the glass piece are controlled to fluidify the glass material and after re-solidifying the protrusion completely fills the cavity,wherein the glass material of the protrusion is fluidified during the pressing, andwherein the glass material of the protrusion is solidified after the re-solidifying,wherein the cavity in the working surface of the semiconductor substrate has a slope angle between 10 and 80 degrees, and the glass piece comprises a protrusion matching with the cavity having a slope angle between 10 and 80 degrees.
  • 2. The method according to claim 1, further comprising providing an adhesive material between the semiconductor substrate and the glass piece before bonding, wherein the glass piece is adhesive bonded to the semiconductor substrate through the adhesive material.
  • 3. The method according to claim 1, wherein: the cavity in the working surface of the semiconductor substrate forms a grid, the cavity extending along and within kerf areas, wherein the cavity is wider that the kerf areas;the glass piece comprises a protrusion forming a grid and matching with the grid formed by the cavity; the method further comprising:separating, after the bonding, the semiconductor substrate in and along the kerf areas to obtain a plurality of semiconductor dies from the semiconductor substrate, each semiconductor die including a glass frame emerging from the protrusion of the glass piece.
  • 4. The method according to claim 1, further comprising thinning, after the bonding, the semiconductor substrate from a rear side opposite to a front side defined by the working surface.
  • 5. The method of claim 1, wherein the semiconductor element is one of a transistor, a diode, a field effect transistor, an IGBT, a logic circuit, a driver circuit, a processor circuit and a memory circuit.
  • 6. A method of manufacturing a glass piece, the method comprising: forming a mold substrate of a single-crystalline material by etching a sharp-angled cavity into a working surface of the mold substrate;bringing a source material based on a glass in contact with the working surface provided with the sharp-angled cavity; andpressing the source material and the mold substrate against each other,wherein a temperature of the source material and a force exerted on the source material are controlled such that source material is fluidified and flows into the sharp-angled cavity,wherein the sharp angles of the sharp angled cavity are disposed below the working surface,wherein the sharp-angled cavity comprises a first region that vertically extends from the working surface of the mold substrate and a second region that connects with the first region and laterally extends away from the first region with an upper surface of the second region being separated from the working surface by a section of the mold substrate.
  • 7. The method of claim 6, wherein the source material is a powder, a glass frit, includes pellets, or a disk with a flat surface.
  • 8. The method of claim 7, wherein the source material is a disk with a flat surface, and wherein the disk is pressed with the flat surface against the working surface of the mold substrate.
  • 9. The method according to claim 6, further comprising controlling the temperature and the force to re-solidify the fluidified source material, the re-solidified source material forming a glass piece with a protrusion extending into the cavity.
  • 10. The method according to claim 6, further comprising controlling the temperature and the force to re-solidify the fluidified source material, the re-solidified source material forming a glass piece with a protrusion that fills the cavity completely.
  • 11. The method according to claim 6, wherein the source material is a material exhibiting a glass transition, and the temperature of the source material is controlled to exceed the glass transition temperature in the course of the pressing.
  • 12. The method according to claim 6, wherein: the source material is a soda-lime glass, undoped silica, or silica doped with at least one dopant selected from the group consisting of boron B, sodium Na, calcium Ca, potassium K and aluminum Al; orthe source material is a polymer selected from the group consisting of polynorbornene, polystyrene, polycarbonate, polyimide, and benzocyclobutene.
  • 13. The method according to claim 6, wherein the glass piece is in-situ bonded to the mold substrate during pressing.
  • 14. The method according to claim 6, wherein the glass piece and the mold substrate form a laminate or a bonded composite after re-solidifying.
  • 15. The method according to claim 6, wherein the mold substrate is made of a single-crystalline semiconductor.
  • 16. The method according to claim 6, wherein the mold substrate is made of a single-crystalline material selected from the group consisting of silicon, silicon carbide and gallium nitride.
  • 17. The method according to claim 6, further comprising removing, after re-solidifying, the mold substrate using an etch process that removes the material of the mold substrate selectively against the material of the glass piece.
  • 18. The method according to claim 6, further comprising: providing the mold substrate or the source material with a non-sticking layer before bringing the source material in contact with the working surface of the mold substrate; andseparating the mold substrate and the glass piece in a nondestructive way after re-solidification of the source material.
  • 19. The method according to claim 6, wherein the cavity has a width of 10 micrometer or more and of 2 millimeter or less.
  • 20. A method of manufacturing a glass piece, the method comprising: forming a mold substrate of a single-crystalline material by etching a sharp-angled cavity into a working surface of the mold substrate;bringing a source material based on a glass in contact with the working surface provided with the sharp-angled cavity; andpressing the source material and the mold substrate against each other,wherein a temperature of the source material and a force exerted on the source material are controlled such that source material is fluidified and flows into the sharp-angled cavity,wherein the sharp angles of the sharp angled cavity are disposed below the working surface, andwherein the sharp angles of the sharp angled cavity comprise a corner between first and second planar walls of the sharp angled cavity, wherein the first planar wall is disposed below and runs parallel to the working surface of the substrate, and wherein the second planar wall is disconnected from and runs perpendicular to the working surface of the substrate.
RELATED APPLICATIONS

This application is a continuation of and claims priority to U.S. application Ser. No. 13/415,376, the content of which is incorporated by reference herein in its entirety.

US Referenced Citations (82)
Number Name Date Kind
4830655 Franek et al. May 1989 A
4842633 Kuribayashi et al. Jun 1989 A
5213600 Greschner et al. May 1993 A
5378289 Noguchi et al. Jan 1995 A
5436764 Umetani et al. Jul 1995 A
5773874 Eithoven Jun 1998 A
5805361 Morimoto Sep 1998 A
6121173 Terashi Sep 2000 A
6151917 Hibino et al. Nov 2000 A
6305194 Budinski et al. Oct 2001 B1
6407866 Yamashita Jun 2002 B1
6432328 Hamanaka et al. Aug 2002 B2
6433471 Khan et al. Aug 2002 B1
6951119 Quenzer et al. Oct 2005 B1
6997019 Kawata et al. Feb 2006 B2
7129163 Sherrer et al. Oct 2006 B2
7309174 Farr Dec 2007 B2
7611648 Woelfing et al. Nov 2009 B2
8099982 Takagi et al. Jan 2012 B2
8202786 Von Koblinski Jun 2012 B2
8294996 Ueno et al. Oct 2012 B2
8369709 Guo Feb 2013 B2
9027237 Pawlowski et al. May 2015 B2
9102083 David Aug 2015 B2
9219020 Breymesser et al. Dec 2015 B2
9441416 Veerasamy Sep 2016 B2
9601376 Breymesser Mar 2017 B2
9912115 Reinert Mar 2018 B2
9981844 Breymesser May 2018 B2
10112861 Brockmeier Oct 2018 B2
20020085287 Egawa Jul 2002 A1
20020109069 Yamamoto et al. Aug 2002 A1
20030020399 Moller Jan 2003 A1
20040079114 Aitken Apr 2004 A1
20040104460 Stark Jun 2004 A1
20040123628 Stoehr et al. Jul 2004 A1
20050013562 Tatehata et al. Jan 2005 A1
20050110157 Sherrer et al. May 2005 A1
20050185900 Farr Aug 2005 A1
20050274145 Aitken et al. Dec 2005 A1
20060038206 Shimoyama et al. Feb 2006 A1
20060073626 Shimizu et al. Apr 2006 A1
20060090512 Fujimoto et al. May 2006 A1
20060130527 Tanaka et al. Jun 2006 A1
20070256453 Barnes Nov 2007 A1
20090052040 Suzuki Feb 2009 A1
20090194666 Takamoto Aug 2009 A1
20090202251 Shibayama Aug 2009 A1
20090243126 Washiya et al. Oct 2009 A1
20100105160 Singh Apr 2010 A1
20100130246 Biertumpfel May 2010 A1
20100265597 Shyu Oct 2010 A1
20110064418 Wang et al. Mar 2011 A1
20110091687 Haque Apr 2011 A1
20110200288 Poole et al. Aug 2011 A1
20120005893 Kawai Jan 2012 A1
20120006467 Kawai Jan 2012 A1
20120012994 Von Koblinski Jan 2012 A1
20120015150 Suzuki Jan 2012 A1
20120057100 Masuda Mar 2012 A1
20120142144 Taheri Jun 2012 A1
20120212818 Takano et al. Aug 2012 A1
20130111953 Maloney May 2013 A1
20130228905 von Koblinski Sep 2013 A1
20130234297 Breymesser et al. Sep 2013 A1
20130237034 Breymesser et al. Sep 2013 A1
20130285228 Montez Oct 2013 A1
20130313744 Maruyama et al. Nov 2013 A1
20140087099 Veerasamy Mar 2014 A1
20140208801 Takano et al. Jul 2014 A1
20140224579 Balascak et al. Aug 2014 A1
20140283553 Tomisaka et al. Sep 2014 A1
20140301697 Marenco Oct 2014 A1
20140339694 von Koblinski Nov 2014 A1
20150077839 Mizukane et al. Mar 2015 A1
20150155260 Lee Jun 2015 A1
20150175467 Denifl Jun 2015 A1
20150225275 Tomisaka Aug 2015 A1
20150247959 Sammokyou Sep 2015 A1
20150279930 Breymesser et al. Oct 2015 A1
20160163579 Nakamura Jun 2016 A1
20180265354 Breymesser Sep 2018 A1
Foreign Referenced Citations (15)
Number Date Country
1715850 Jan 2006 CN
101154686 Apr 2008 CN
101276792 Oct 2008 CN
3719200 Dec 1988 DE
19956654 Jun 2001 DE
102005038152 Mar 2006 DE
102006009961 Oct 2006 DE
102005063276 Jul 2007 DE
0 832 858 Apr 1998 EP
2007127440 May 2007 JP
2012-148907 Aug 2012 JP
2013-129547 Jul 2013 JP
WO 2012124711 Sep 2012 WO
2013027808 Feb 2013 WO
2013148660 Oct 2013 WO
Non-Patent Literature Citations (2)
Entry
“Foturan—A Photostructurable Glass”, Mikroglas Chemtech GmbH, Mainz, Germany, Publication date unknown, pp. 1-3.
Wolf, et al., “Silicon Processing for the VLSI Era”, vol. 1—Process Technology, Sunset Beach, CA: Lattice Press, 1986, pp. 531-532.
Related Publications (1)
Number Date Country
20180265354 A1 Sep 2018 US
Continuations (1)
Number Date Country
Parent 13415376 Mar 2012 US
Child 15981393 US