High electron mobility transistor with GaN/Al.sub.x Ga.sub.1-x N heterojunctions

Abstract

A high electron mobility transistor is disclosed, which takes advantage of the increased mobility due to a two dimensional electron gas occurring in GaN/Al.sub.x Ga.sub.1-x N heterojunctions. These structures are deposited on basal plane sapphire using low pressure metalorganic chemical vapor deposition. The electron mobility of the heterojunction is aproximately 620 cm.sup.2 per volt second at room temperature as compared to 56 cm.sup.2 per volt second at 180.degree. K. and decreased to 19 cm.sup.2 per volt second at 77.degree. K. The mobility for the heterostructure, however, increased to a value of 1,600 cm.sup.2 per volt second at 77.degree. K. and saturated at 4.degree. K.

Description

BACKGROUND OF THE INVENTION

I. Field of the Invention

This invention relates to a semiconductor device having improved electron mobility, and in particular, to a transistor constructed of GaN/Al.sub.x Ga.sub.1-1 N heterostructures that is capable of operating at temperatures greater than 100.degree. C.

II. Description of Related Technology

Al.sub.x Ga.sub.1-x N is a 3-5 semiconductor system with a direct bandgap ranging from 360 nanometers at x=0 to 200 nanometers at x=1. As reported by M. Gershenzon, D. E. Wang and L. Ta, in the proceedings of the 1981 International Opto Electronic's Workshop, National Chang Kung University, Tinan Tai Wan, Page 55 (December 1981), the Al.sub.x Ga.sub.1-x N material has potential uses in ultraviolet light emitting diodes and detectors, short wave length lasers and transit time limited microwave power amplifiers.

Highly uniform epitaxial films of the materials have been grown by reactive molecular beam epitaxy (as reported by S. Yoshida, S. Gonda, and S. Misawa, and the Journal of Applied Physics, Vol. 53, Page 6,844, 1982), as well as by vapor phase epitaxy (as reported by M. Ilegems, and H. C. Montgomery, Journal of Physical Chemistry Solids, Vol. 34, Page 885, 1973) and by atmospheric and low pressure metal organic chemical vapor deposition (See M. A. Khan, R. A. Skogman, R. G. Schulze, and M. Gershenzon, Applied Physics Letters, Vol 42, Page 430, 1983 and H. Amano, T.Asahi, and I. Akasaki, Japanese Journal of Applied Physics Letters, Vol. 29, Page L205, 1990).

However, these materials are generally unsuited for semiconductor device applications, because the materials produced are highly degenerate N-type (N.sub.d =10.sup.18 to 10.sup.20 per cubic centimeter) and the carrier mobilities are relatively low, typically less than 100 cm.sup.2 per volt second. Researchers generally concluded that the undesirably high carrier densities were caused by nitrogen vacancies formed during the material growth process.

High electron mobility to transistor have been produced in the past from a GaAs/Al.sub.x Ga.sub.1-x As material as reported by S. Hiyamizu, T. Mimura, T. Fuji and K. Nanbu, Applied Physics Letters, Vol. 37, Page 805, 1980. Although this material exhibits superior electron mobilities, it suffers from instability at high temperatures.

SUMMARY OF THE INVENTION

The present invention is a high electron mobility transistor device structure based on the GaN/Al.sub.x Ga.sub.1-x N material system. Al.sub.x Ga.sub.1-x N has a bandgap approximately four times greater than Al.sub.x Ga.sub.1-x As material, thereby making transistors constructed according to the present invention superior and having a lower noise current as the temperature of operation is increased as compared with the gallium arsenide base transistor. GaN is stable in air to 800.degree. C. and recently we have demonstrated point contact diodes which operate at temperatures in excess of 700.degree. C.

The transistor of the present invention is deposited on an aluminum nitride coated substrate material. The channel regions are formed of a 500 to 2,00 angstrom thick layer of GaN, which is then coated with an Al.sub.x Ga.sub.1-x N layer of approximately 500 angstroms in thickness.

Photomasking is used to define the source and drain contact pads, to which an ohmic metal contact is deposited.

A shottky barrier is then deposited using thin metal layers in the region between the source and drain contacts. Electrical connecting wires are then bonded to the ohmic and shottky contacts.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1a depicts a first layered structure grown by low pressure metal oxide chemical vapor deposition;

FIG. 1b depicts a second layered structure including a single AlGaN/GaN heterojunction;

FIG. 2 is a graph showing mobility and sheet concentration versus temperature for materials related to a transistor constructed according to the principles of the present invention;

FIG. 3a is a depiction of a third layered structure of a transistor constructed according to the principles of the present invention;

FIG. 3b is a depiction of an eighteen period AlGaN/GaN heterojunction;

FIG. 4 is a mobility versus temperature graph for (a) a single AlGaN/GaN heterojunction with a 3000 .ANG. GaN layer and (b) a single AlGaN/GaN heterojunction with a 6000 .ANG. GaN layer;

FIG. 5 is a schematic side elevation of a transistor constructed in accordance with the principles of the present invention;

FIG. 6 is a schematic plan view of the transistor of FIG. 5; and

FIG. 7 is a graph of (a) electron mobility and (b) sheet carrier concentration versus temperature for a transistor as depicted in FIG. 3b.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Referring to FIG. 1a, a standard GaN deposition is shown. A substrate 1 is typically used as a base, and in this example was made of basal plane sapphire having a thickness of approximately 350 microns. Deposited on sapphire substrate 1 is an aluminum nitride buffer layer 2, which reduces the lattice mismatch between the GaN and the sapphire substrate. Finally, a GaN layer 3 having, for example, a thickness of 3,000 angstroms, is deposited.

For the GaN layer just described, the electron mobility is approximately 56 cm.sup.2 per volt second and has a carrier density, N.sub.d of approximately 9.6.times.10.sup.17 per cubic centimeter. In general, the carrier, or electron, mobility will improve to around 300 cm.sup.2 per volt second as the growth thickness is increased to approximately 1.5 microns. This is probably due to the reduction of dislocations as one moves away from the GaN/AlN interface.

Referring to curve a of FIG. 2, the deposited device 4 of FIG. 1 is seen to reach its electron mobility peak of approximately 60 cm.sup.2 per volt second at a temperature of approximately 180.degree. K. with the electron mobility gradually decreasing as temperature decreases. This particular peaking behavior is typical in high quality GaN gross and is attributable to the polar optical mode and the ionized impurity scattering regimes.

Referring to FIG. 1b, a heterojunction 5 depicting layering typical of a high mobility transistor constructed according to the principles of the present invention as shown. As in FIG. 1a, the substrate 6 is constructed of basal plane sapphire substrate having, for example, a thickness of approximately 350 microns. A thin aluminum nitride buffer layer 7, having a thickness of approximately 25-75 angstroms, is deposited onto substrate 6. Again as in FIG. 1b, the next layer 8 is composed primarily of GaN and has a thickness of approximately 3,000 angstroms. Finally, an Al.sub.x Ga.sub.1-x N layer 9 is deposited, having a thickness of approximately 450 angstroms. The characteristics of this heterojunction are depicted in FIG. 4 at curve a.

Referring again to FIG. 2, as shown by curve b, the electron mobility of sample 5 is seen to have increased to 620 cm.sup.2 per volt second at room temperature to 1,600 cm.sup.2 per volt second at 77.degree. K. The electron mobility remain constant as the temperature was decreased further to 4.degree. K. As seen in FIG. 2 at curve c, a sheet carrier density of the sample 5 is plotted as a function of temperature. In the material 8 used in sample 5, the value of X is equal to approximately 0.09, with the value of 1-x therefore being equal to approximately 0.91.

The dramatic increase in carrier mobility values in sample 5 may be attributed to the presence of a two dimensional electron gas at the interface between the Al.sub.0.09 Ga.sub.0.91 N and the GaN layer 7. Although the conduction band discontinuity has neither been measured or calculated for sample 5, one would estimate that the conduction band discontinuity is approximately 0.25 electron volts, assuming a 60/40 split of the bandgap discontinuity similar to the GaAs/Al.sub.x Ga.sub.1-x As material as reported by R. L Anderson in Vol. 5 of solid state electronics, Page 341 (1962). The carrier concentration of the Al.sub.0.09 Ga.sub.0.91 N material 8, in bulk, is measured as approximately 5.times.10.sup.18 per cm.sup.3 has an electron mobility of approximately 35 cm.sup.2 per volt second.

Assuming a two dimensional gas structure, conduction must be based on contributions both from the two dimensional gas and from the bulk GaN and the Al.sub.0.09 Ga.sub.0.91 N material. Therefore, the measured electron mobilities of FIG. 2 are in essence averaged values and the actual two dimensional gas mobilities are higher than the indicated values. By using a parallel conduction model, one would estimate that the true mobility of the two dimensional electron gas at 300.degree. K. would be 820 cm.sup.2 per volt second and the sheet carrier density would be approximately 5.times.10.sup.13 per cm.sup.2.

This model may be further described by reference to FIG. 3a. The sample 10 of FIG. 3a includes a sapphire substrate 11 having a thickness of approximately 350 microns, followed by an aluminum nitride buffer layer of 12 having a thickness of approximately 50 angstroms. Deposited on layer 12 is a GaN layer 13 having a thickness of approximately 6,000 angstroms. Finally, an Al.sub.0.09 Ga.sub.0.91 N layer 14 having a thickness of approximately 500 angstroms is deposited. Referring to FIG. 4, curve b, increasing the GaN layer thickness and hence the bulk conduction reduced the room temperature mobility of the single heterojunction from 620 cm.sup.2 N-s to 450 cm.sup.2 N-s but had little effect on the 77 K. mobility which remained at 1600 cm.sup.2 N-s for both samples. The increased bulk GaN conduction at room temperature causes the average value of the heterojunction mobility to be pushed closer to that for bulk GaN. At 77 K., the high mobility of the interface dominates the measured mobility for both structures.

Referring now to FIG. 3b, a sample 15 having multiple heterojunctions is depicted. The substrate 16 is a 350 micron thick layer of sapphire, followed by a 50 angstrom thick aluminum nitride buffer layer 17. The GaN layer 18 is only 2,000.degree. thick and is followed by 18 parallel conducting channels 19-26, composed of alternating layers of the Al.sub.0.15 Ga.sub.0.85 N material and a GaN layer. Layer 19 would be composed of the Al.sub.x Ga.sub.1-x material, whereas layer 20, for example, would be composed of gallium nitride.

Referring to FIG. 7, curve a, the trace shows an electron mobility of 1,980 cm.sup.2 per volt second with a charged density of 1.5.times.10.sup.14 per, cm.sup.2 at 77.degree. K. Note the sheet charge density at FIG. 7, curve b increased by about a factor of ten over the case of Sample 5 depicted in FIG. 2, at curve c.

Referring to FIGS. 5 and 6, the details of construction of a high mobility transistor based on the materials just described can be seen. The substrate material 37 may be of silicon, gallium arsenide, silicon carbide, aluminum oxide or indium phosphide. Substrate 37 is coated of a buffer layer 38, typically formed of an aluminum nitride layer having a thickness of approximately 50 angstroms. The channel region 39 of transistor 40 is a gallium nitride layer between 500 and 2,000 angstroms thick. The thickness of layer 39 is such that it can be completely depleted at a few volts applied to a schottky barrier formed on it. The gallium nitride layer 39 is coated with a thin (approximately 500 angstroms thick) Al.sub.x Ga.sub.1-x N layer 41. Depending on the application of the particular device 40, the aluminum composition of layer 41 may be varied. The effects of band bending to cause electrons from layer 41 to spill over to layer 39 at the interface 42 residing between them. This will create a sheet charge density of a two dimensional electron gas with mobilities several times greater than bulk material electrons.

Following epi-layer depositions just described, the device structure will be fabricated as follows. First, photomasking is used to define the source pad 43 and the drain contact pad 44. Ohmic metal contact 45 is deposited on the Al.sub.x Ga.sub.1-x N region 41 defined as source 43, with a similar ohmic pad 46 being deposited on drain 44.

Various metal material may serve as a the ohmic contacts 45, 46 such as gold, silver, aluminum or indium.

A schottky barrier 47 is deposited using thin metal layers in the region between source contact 43 and drain contact 44, thereby defining a gate contact 47. Several metal combinations can be used from the schottky barrier formation, such as titanium, gold, aluminum, silver, chromium, tungsten and indium. Electrical conductors 48, 49 and 50 are bonded to ohmic contacts 45 and 46 and schottky contact 47.

As may be understood by those skilled in the art, the examples just described represent a reduction to practice of highly theoretical experiments. Commercial embodiments will follow utilizing these and similar materials in ways that differ from the prototypes just described, without departing from the spirit and scope of the invention as defined by the following claims.

Claims

1. A transistor, comprising:

(a) a substrate;

(b) a buffer, the buffer being deposited on the substrate;

(c) a first active layer, the first active layer being composed essentially of GaN, the first active layer being deposited on the buffer;

(d) a second active layer, the second active layer being composed essentially of Al.sub.x Ga.sub.1-x N, where x is greater than 0 and less than 1; and

(e) a plurality of electrical connections, the electrical connections residing on the second active layer, the plurality of electrical connections comprising:

(i) a source connection, the source connection residing on the second active region;

(ii) a gate connection, the gate connection residing on the second active region;

(iii) a drain connection, the drain connection residing on the second active region;

thereby permitting a difference of electrical potential to be applied to the second active region so as to permit operation as a transistor.

2. The transistor of claim 1, wherein the source connection is formed by depositing a layer of gold on the second active region.

3. The transistor of claim 2, wherein the gate connection is defined on the second active region by forming a layer of metal, the metal being composed essentially of a metal chosen from a group including gold, silver, aluminum, and indium.

4. The transistor of claim 3, wherein the drain connection is formed by depositing a metal layer on the second active region, the metal layer being chosen from a group consisting of gold, silver, aluminum and indium.

5. The transistor of claim 4, wherein the first active region has a thickness of between 500 and 2,000 angstroms.

6. The transistor of claim 5, wherein the substrate is composed essentially of a material chosen from a group including silicon, gallium arsenide, silicon carbide, aluminum oxide and indium phosphide.

7. The transistor of claim 6, wherein the buffer layer is composed essentially of aluminum nitride.

8. The transistor of claim 7, wherein the buffer layer has a thickness of between 25 and 75 angstroms.

9. The transistor of claim 8, wherein the second active region has a thickness of between 450 and 550 angstroms.

10. The transistor of claim 9, wherein the transistor may operate satisfactorily at a temperature of greater than 100.degree. C.

11. The transistor of claim 10, wherein the electron mobility being greater than 1,000 cm.sup.2 per volt second.

12. The transistor of claim 11, wherein x is approximately equal to 0.15.