Patent Application
20190296162
The disclosure relates to the field of fabrication of photovoltaic cells, and more specifically relates to depositing contacts on such cells.
In the case for example where cells are silicon-based, the cells currently dominating the photovoltaic market are single-sided (only one surface receiving light rays) and the back surface is entirely metallized. All the same, with a goal of increasing photovoltaic conversion yields, the development of “double-sided” cells is currently experiencing a major expansion. In fact, in these structures with two opposite active surfaces, the efficiency of the panel is the sum of the yield obtained on the front surface (direct radiation) and that obtained on the rear surface (which only receives reflected radiation—about 20% of the light incident on grass for example). The order of magnitude of the conversion gain compared to a single-surface cell is therefore about 3 to 4%, depending on the reflection rate of the incident surface (e.g. grass, snow, sand, etc.). Nonetheless, the development of double-sided cells is slowed because of the high cost of their production and also performance limitations related in particular to the use of silver paste based screen printing for metallizing the metallic contacts.
An alternative to metallization by screen printing is the use of electrochemical plating, which is starting to be industrialized for single-sided cells. The general attraction of electrochemical plating over screen printing is:
Since electrochemical plating is not possible by conventional electrolysis (because the resistivity of silicon is too large), the most commonly used approach is a “mixed” approach of thickening of screen-printed contacts.
Some properties of the silicon substrate can also be stimulated and two current electrochemical techniques for direct plating on a silicon substrate are:
Light induced plating (LIP) is used for metallization of the n+ surface. In this case, by illuminating the semiconductor, the p-n junction generates electron-hole pairs. By applying a potential between an anode on the rear surface (p+) of the previously metallized photovoltaic cell, the electrons generated are used on the n+ surface for reducing metal salts present in the deposit bath.
However, the “competition” on the p+ surface between the formation of holes (related to the photo-generation of current) and the arrival of electrons for feeding the reduction reaction on the n+ surface is incompatible with the formation of a compound by electrolysis on a double-sided cell. Thus, in a LIP type technique, the rear surface of the cell is often outside the electrolysis bath in order to prevent corrosion or over-deposit problems.
The technique of depositing in the direction of diode polarization (FBP) is used for metallization of the p+ side. In this case, by connecting an anode to the rear surface of the solar cell (n+), a cathode potential or current is applied to the previously metallized rear surface. This potential serves to generate electrons which pass through the diode and are available on the p+ surface. However, here again, this technique cannot be used for double-sided cells because if both surfaces are exposed to the electrolytic bath, the application of the potential (or current) leads to the formation of a compound by reduction on the n+ surface. The formation of this conducting compound then “blocks” the movement of electrons through the diode and only a deposit on the n+ surface is produced.
Of course, a combination of both techniques (LIP and FBP) can be provided for the metallization of double-sided surfaces but this combination requires a burdensome and complex implementation (mandatorily sequential metallization, management of the electrical contact and field lines between the two surfaces, need for precise alignment between the openings of the two surfaces).
The only (electro-) chemical metallization technique with which to simultaneously deposit a metal on both silicon surfaces (one p+ type and the other n+ type) is a method referred to as “electroless” auto-catalytic. Nonetheless, it has disadvantages: implementation complexity, need for activation of the surface before depositing (often using a bath containing palladium, a costly metal), long deposition times (≈0.1 μm/minute), short bath life and delicate bath management, and all this is that a high deposition temperature (over 80° C.). Further, the deposition speed depends on the type of surface to be covered (with a different selectivity on the surfaces of the cell).
A simultaneous electrochemical deposition of the contacts for the front and rear surface of the double-sided cell is then preferred which is better suited in terms of ease of implementation, deposition speed, etc.
The present disclosure aims to improve this situation.
For this purpose, an embodiment proposes a method for fabrication of a double-sided photovoltaic cell, with two opposite active surfaces, comprising a step of depositing, on each active surface, at least one electric contact. The deposition step comprises in particular a shared operation of depositing on each of the active surfaces, implemented by electrolysis in a shared electrolysis tank comprising:
For example, the metal in the metal oxide layer can be at least one element among Mn, Ni, Mo, Cd, Sn, In, Zn, Pb, Ag, Cu, In, Ga, Co, W, Ta, Ga and Ti.
More specifically, during the shared deposition operation:
In an embodiment, the first and second compartments are separated by an ion exchange membrane that the electrolysis tank comprises.
Preferably, the deposit:
In fact, the lighting enhances the generation of electron/hole pairs and therefore the simultaneous deposit of the metal layer and the metal oxide layer. This lighting can therefore be done on at least any one of the two surfaces.
Optionally, the depositing operation is assisted by application of a potential difference specific for generating at least negative charges on the first active surface.
Alternately or additionally, the depositing operation can be assisted by application of a potential difference specific for generating positive charges on the second active surface.
In an embodiment, the photovoltaic cell is a double-sided homojunction with n+ type on the first active surface and p+ on the second active surface.
The bulk material (also called substrate SUB below) can for example be n or p type silicon. The surfaces of the material however remain:
As indicated as an example above, the photovoltaic cell can be silicon-based.
In a possible implementation, the metal layer on the first active surface can be nickel-based, and the step of depositing the electric contact on this first active surface can be continued next by depositing a layer comprising at least copper onto the metal layer, by electrolysis. This solution is very advantageous economically because it serves to replace depositing a costly, silver paste usually done by screen printing.
The step of depositing the electric contact on the second active surface can be continued as well by depositing a layer comprising at least copper onto the metal oxide layer, by electrolysis (since the oxide is conducting).
As will be seen with reference to
An embodiment also aims at a double-sided photovoltaic cell, with two opposite active surfaces, where the cell comprises at least one electrical contact on each active surface. Specifically, the contact for a first active surface comprises a metal layer deposited on the first active surface whereas the contact for the second active surface comprises a metal oxide conducting layer deposited on the second active surface.
The difference in the contact material between the two surfaces, with in particular:
As indicated above, the photovoltaic cell can be homojunction type with n+ type on the first active surface and p+ on the second active surface.
Other advantages and characteristics will appear upon reading the following detailed description of sample embodiments, and on examining the attached drawings on which:
In the sample embodiment presented below, the use of the semiconducting property of the P-N junction of the double-sided cell is proposed: the illumination of at least one of the two surfaces leads to the photogeneration of electron/hole pairs. Electrons are generated on the n+ surface and holes on the p+ surface. It is therefore possible to perform an electrochemical reaction of reduction on the n+ surface (and therefore deposit a metal), and in parallel to enhance an oxidative electrochemical reaction on the opposite p+ surface (and therefore deposit a metal oxide typically).
Thus, without need for connection to an external electric circuit, if the photovoltaic material of the cell (for example the silicon) is in contact with two adequate electrolytes (one per surface) it is thus possible to implement a simultaneous deposit:
Thus, referring to
The illumination ECL of at least one of the surfaces enhances the photogeneration of electrons ne− on the first surface (in the compartment C1) and holes TR on the second surface (in the compartment C2). With the electrons in the compartment C1, metal (for example nickel, Ni) can be deposited on the free surface of the substrate (between the silicon nitride masks SiNx). In parallel and in particular simultaneously, in the compartment C2, holes (positive charges) are created enhancing metal oxide deposition, and in particular deposition of a conducting oxide (for example, MnO2 or another as presented later in the examples).
In particular, the metal oxide electrochemically deposited on the p+ surface preferably has the following properties. It involves:
Further, if this oxide is transparent and conducting (like titanium oxide or ITO), electricity can be collected while allowing incident light to pass (reduced shadowing rate).
Preferably, on this oxide, copper can advantageously be deposited by electrolysis for increasing the conductivity of the electrical contacts. Next, a fine layer of silver can be deposited on the copper to protect it from oxidation and improve the weldability in order to fabricate assembled photovoltaic modules. Finally, a thermal treatment can be done so that NiSi can form on the n+ surface, since NiSi has a role of ohmic contact on the silicon and in prevention of the diffusion of copper.
Thus, the solar cell can have a stack of the type illustrated in
Using an electrochemical technique for the formation of the electric contacts has many advantages (compared to the usual technique, screen printing):
Further, illuminating a photovoltaic substrate for depositing base metal layers (including an oxide) on both surfaces, simultaneously and without contact with an external circuit, by wet route also has advantages:
More precisely, again referring to
In order to avoid acidification or alkalization of the compartments, an ion exchange membrane (Nafion type, anionic or cationic) can separate the two components and maintain the ionic equilibrium.
The illuminating device may comprise a row of diodes or halogen lamps having a maximum electromagnetic irradiation in the red visible or near infrared region. The radiation can preferably include the domain of ultraviolet optical wavelengths for activating and/or catalyzing the electrolyte/silicon interface in order to enhance nucleation at the silicon surface of the first deposition sites.
Depending on the electrochemical reactions brought into play, the illumination can advantageously be applied on both surfaces, so that the electrochemical potentials on both surfaces can be adjusted if needed.
Deposition speeds at least 10 times greater than those obtained by an autocatalytic type method (electroless method, the most effective currently known) can be achieved with the photogenerated current (of order of magnitude of several tens of mA·cm−2). The activation step from the electroless method (starting of the nucleation of the nickel Ni contact for example using palladium particles) is not needed. The electrolytic baths implemented are simpler and more stable than the electroless baths and purer deposits can be achieved (less carbon type impurities in the resulting film). The overall method is therefore faster and less costly than the electroless method, with equivalent photovoltaic performance.
More generally, the implementation in the meaning of the present disclosure presents many advantages compared to known techniques, such as the screen printing, electroless and LIP/FBP techniques. Already, the processing from the disclosure is simultaneous, quick and without electrical contact for both surfaces of the double-sided solar cells for the formation of electrical collection grids by preferably using illumination of one or both surfaces.
More specifically, compared to the electroless method, it is possible with the technique from the disclosure:
Compared to the screen-printing method, the disclosure provides in particular an improvement of the performance of the photovoltaic devices by:
and also fabrication savings by:
Below, some specific implementation examples are presented:
In a first sample implementation presented below, MnO2 and nickel are deposited simultaneously on the p+ and n+ surface respectively.
In a tank with two compartments separated by a Nafion cation exchange member, using a system of joints ensuring the sealing of both surfaces, a nickel metallization bath is placed in the n+ compartment (C1) and an MnO2 metallization bath in the p+ compartment (C2). The substrate (silicon) is illuminated with a row of white LED lights on one surface.
For depositing Ni, a temperature of 60° C. is applied for two minutes in a Watts bath. The nickel is deposited according to the following general reaction:
Ni2++2e−→Ni
2H++2e−→H2
In parallel, for depositing MnO2, in a bath comprising 0.01 M Mn (C2H3O2)2 (called Mn acetate), 0.02 M NH4 (C2H3O2) (called ammonium acetate) and 10% C2H6OS (dimethyl sulfoxide (DMSO)), a temperature of 60° C. is applied for two minutes. The manganese oxide is then deposited at the anode according to the following general reaction:
Mn2++2H2O→MnO2+4H++2e−
Advantageously, the protons (H+) can be balanced between the two compartments by the ion exchange membrane.
On both surfaces simultaneously, copper can next be deposited by direct electrolysis for increasing the conductivity of the electrical contacts. Next, a fine layer of silver can be deposited on the copper to protect it from oxidation and improve the weldability in order to fabricate photovoltaic modules. Finally, a thermal treatment (range from 350 to 550° C.) can be done so that a NiSi alloy can be formed on the n+ surface, which has a role of ohmic contact on the silicon and prevention of diffusion of the copper.
In a second embodiment, cadmium oxide CdO is deposited on the p+ surface, and nickel is deposited on the n+ surface.
CdO can be deposited at ambient temperature in 0.05 M cadmium acetate [Cd (C2H3O2)2] and 0.1 M Na2SO4.
The same operating mode is the one described in the first embodiment can next be applied (nickeling on the n+ surface, simultaneous coppering on both surfaces, silvering and then thermal treatment).
In a third embodiment, tin oxide SnO2 is deposited on the p+ surface and nickel on the n+ surface, by providing 0.1 M SnCl2 and 0.5 M NaNO3 in DMSO.
In a fourth embodiment, manganese oxide MnO2 is deposited on the p+ surface and nickel on the n+ surface with a single deposition bath because in this case, both surfaces of the substrate are exposed to the same electrolyte which contains at least one nickel salt (for example sulfate) and one manganese salt (for example an acetate). By application of standard potentials for electrochemical reactions, the reduction reaction of the nickel salt takes place at the cathode and the formation of the manganese oxide at the anode. In the case of a single bath, the ion exchange membrane is no longer necessary (ionic equilibrium is established by the exchange of protons between the reactions at the anode and the cathode).
Of course the present disclosure is not limited to the embodiments presented above as examples; it extends to other variants.
The principle of photogeneration of the current for example allows implementation variants. Typically, it can additionally be assisted by application of a potential between the p+ and n+ terminals of the substrate (preferred range of 0 to 2 V). The direction of polarization is shown in
Again, alternatively, relating to this implementation, it is possible to provide an electrode specific to the reaction and different from the substrate. The principle of photogeneration of the current remains the same but is assisted by application of a potential between the n+ terminal of the substrate and an anode (preferred range from 0 to 2 V). The direction of polarization is described in
Alternatively again, the direction of polarization can be such as described in
Further, the use of lightning for enhancing the reactions in both compartments of the electrolytic tank was described above. This implementation is advantageous in the case of a silicon substrate in particular. Just the same, it is not absolutely necessary for example for a substrate other than silicon. Typically, in some substrate cases, the electrical stimulation shown in one of
| Number | Date | Country | Kind |
|---|---|---|---|
| 1659624 | Oct 2016 | FR | national |
This application is the U.S. national phase of the International Patent Application No. PCT/EP2017/075242 filed Oct. 4, 2017, which claims the benefit of French Application No. 16 59624 filed Oct. 5, 2016, the entire content of which is incorporated herein by reference.