The present invention relates to an in-cavity cleaning method and, more particularly, to an in-cavity cleaning method applied to semiconductor film manufacturing.
Plasma chemical vapor deposition is primarily used for forming a film on a substrate, but at the same time also forms a film on surfaces of components in a cavity. The film on surfaces of these components in the cavity falls off over an extended period of time, and forms particles falling on a surface of the substrate and therefore affects the performance of the deposited film on the surface of the substrate. Thus, once the substrate has fully undergone deposition and leaves the cavity, it is needed to use a cleaning gas to clean an environment and surfaces of the components in the cavity.
The duration of cleaning directly affects the production capacity of semiconductor equipment, and therefore, there is a need for enhancing cleaning efficiency for an environment and surfaces of components in a cavity.
It is an object of the present invention to solve the issues above, so as to enhance the efficiency of cleaning any excess film in a cavity formed by the plasma chemical vapor deposition, and increase the production capacity of semiconductor equipment.
An in-cavity cleaning method includes: a lower electrode temperature control step of controlling a lower electrode to a predetermined temperature; an electrode distance adjustment step of elevating the lower electrode and controlling a distance between an upper electrode and the lower electrode; a film deposition step of depositing a film on a substrate; a cleaning gas introducing step of introducing a cleaning gas in a plasma state from the upper electrode of a cavity into the cavity; and a cleaning gas pressure control step of adjusting a pressure of the cleaning gas to switch between a first pressure and a second pressure by a valve adjustment means, wherein the first pressure is greater than the second pressure.
Preferably, the predetermined temperature is 150° C. to 400° C. Preferably, the method further includes driving the elevation of the lower electrode by a motor, and controlling the distance between the upper electrode and the lower electrode to be 6 to 15 mm. Preferably, the cleaning gas is NF3, and after fluorine ions are formed therefrom by a plasma source generator, the fluorine ions are introduced into the cavity from the upper electrode. Preferably, the flow rate of the cleaning gas introduced into the cavity is 1500 to 4500 sccm. Preferably, the valve adjustment means controls the pressure of the cleaning gas in the cavity by a butterfly valve. Preferably, the pressure in the cavity switches between the first pressure and the second pressure in the cleaning process, wherein the first pressure is 3 to 6 torr and the second pressure is 0.5 to 2 torr. Preferably, the first pressure is a high-pressure state and the second pressure is a low-pressure state, and a switching frequency between the two is once per 5 to 15 seconds.
By quickly switching the pressure of the cleaning gas, the present invention enhances the efficiency of cleaning any excess film in a cavity formed by plasma chemical vapor deposition, and increases the production capacity of semiconductor equipment.
Detailed description of the present invention are given in the embodiments with the accompany drawings below, in which:
wherein 11 epresents a first side cavity, 12 represents a second side cavity, 111 represents an upper electrode, 112 represents a lower electrode, and a to i represent positions.
The cleaning gas used in this embodiment is NF3. Specific steps of an in-cavity cleaning method of the present invention are described below.
(1) The temperature of the heating plate, that is, the lower electrode 112, is controlled to be 400° C., the temperature is measured in real time by the thermocouple, and the temperature is controlled by the temperature control device at a temperature control precision range of ±0.75%; that is, in this embodiment, the temperature ranges between 397° C. and 403° C.
(2) From the cavity, a substrate of which a surface having a film formed thereon by plasma chemical vapor deposition is taken out by a mechanical arm, and at the same time, the film thicknesses of the sampling blocks placed at the nine different positions a to i shown in
(3) The distance between the upper electrode and the lower electrode is adjusted and controlled to be 8 to 10 mm by the motor and the position sensor(s).
(4) The 3000 to 3500 sccm NF3 is introduced as a cleaning gas. The cleaning gas first forms partial fluorine ions by a plasma source generator placed at a remote end, and enters in the form of partial fluorine ions the first side cavity and the second side cavity from the upper electrode 111.
(5) The pressures in the first side cavity and the second side cavity are controlled by a known means (for example, adjusting an opening of a butterfly valve). The pressures of the first side cavity and the second side cavity are synchronously switched between a high-pressure state and a low-pressure state, wherein the high-pressure state is 3 to 6 torr and the low-pressure state is 0.5 to 2 torr.
(6) With the adjustment of the butterfly valve, the cleaning gas is allowed to work at the high-pressure state for 10 s and then switched to the low-pressure state for 10 s, and such switching round is repeated four times (where the time needed for switching is approximately 0.1 s).
With the processing method of the present invention, as shown in the table below, the cleaning efficiency per unit time in the cavity can be increased by about 40% compared to conventional processing (wherein the conventional processing is working at a high-pressure state for 40 s and at a low-pressure state for 40 s for one round).
The preferred embodiments of the present invention are disclosed as the description above and drawings. All features disclosed by the present application may be combined with other means, and each feature disclosed in the present application may be replaced by the same, equivalent or similar target features. Thus, apart from particularly obvious features, all the features disclosed in the present application are merely examples of equivalent or similar features. With the description of the preferred embodiments of the present invention, a person skilled in the art would be able to understand that the present invention is a novel, inventive and industrially applicable invention, and possess development values. Moreover, various modifications (for example, adjusting relative positions of some components or the structure of a diversion device) may be made to the present invention by a person skilled the art, and are encompassed within the scope of the appended claims.