Patent Grant
7727781
This invention relates to the manufacture of electronic devices and more particularly the manufacture of electronic devices including solder joints.
The electronic instrumentalities forming the basis for equipment such as mobile phones, computers, and servers are generally fabricated by electrically interconnecting electronic components such as integrated circuits, resistors and capacitors with printed circuit boards. The electrical input and output of the components to a second component, for example, a printed circuit board is generally accomplished through a conducting region typically denominated a pad. Such pads generally have dimensions in the range 100 μm2 to 1 mm2 and are electrically connected to the circuitry of the component such as a printed circuit board through conducting pathways denominated runners. (A runner typically has a width in the range 5 μm to 100 μm and a length, depending on the device configuration, often ranging between a few micrometers and a few centimeters.) For most applications, both the pad and runner, on, for example, the printed circuit board, are metallic and have upper surfaces that include copper, nickel, gold, silver, palladium, or aluminum. (Upper in the context of this disclosure is a surface closest to the point of electrical connection to another component.)
Two components, e.g. an integrated circuit and printed circuit board, are electrically connected through the expedient of solder ball connections, or as they are termed in the trade, solder bump or solder ball connections. Typically, the pads of the two components to be electrically interconnected are, at least in part, configured to be geometrically aligned when the components are positioned for connection. The electrical connection itself in many applications such as flip chip solder connection is made by first forming a solder bump on one (e.g. the integrated circuit pad) of each pair of pads to be electrically connected. (The solder bump is typically approximately spherical in cross section but the shape is not critical.) In manufacture, a solder mask composed generally of an electrically insulating material is configured over the pad region of, for example, the printed circuit board with openings in the mask to allow connection to the underlying pads. (See Microelectronic Packaging Handbook, R. Tummala, et. al., Chapman and Hall, New York, N.Y. 1997, for a description of typical solder mask materials and methods for configuring such masks.) The components are then electrically connected by a process (generally denominated reflow) in which the pads to be connected are aligned and the solder bumps are brought to a temperature exceeding their melting point as described by Tummala supra. This heating process causes the formation of intermetallic compounds at the solder bump/pad interface that contribute to the adhesion of the connected structure. For example, for a copper pad and a lead-free tin/silver/copper solder composition typical intermetallic compounds such as Cu6Sn5 and Cu3Sn respectively are formed at the interface. Similar intermetallics are formed when tin/silver/copper solder balls are attached to the copper pads on a circuit board during reflow.
For reasons that are not fully understood, solder bumps (or solder balls) at times fail when subjected to stress engendered by typical occurrences such as the dropping of an instrumentality or a component, or through the mechanical forces endured during transportation and handling of such entities. There are two predominant failure modes for the solder bump connection. Either the solder bump itself shears into two portions, or the bump fractures (brittle failure) near or at the intermetallic region present at the interface between the pad and the solder bump. Clearly the failure of the electrical connection, especially after the instrumentality has been assembled, is costly and quite undesirable.
In an attempt to predict the failure of components and remove such components from the manufacturing stream, a variety of tests have been developed. In one approach, a probe, 2 in
The failure of solder bumps has become an even more pressing problem with the ever increasing desire to eliminate lead from solder bump compositions. Lead-containing solders are more prone to undergo ductile failure than lead-free solder alloys. In contrast, lead-free solders i.e. solders having a lead content less than 300 ppm lead, have an increased tendency to suffer brittle rather than ductile failure. Unfortunately, a composition that predominantly fails by a ductile mechanism is much preferred because such failure typically occurs less frequently and occurs only after substantially longer periods of stress. Thus, the trend towards lead-free solders has made the identification of components that are likely to fail a more pressing concern. Despite the ever-increasing importance of such identification, available testing approaches have not yielded the desired level of predictability.
It has been found that probe testing of solder connections causes not only stress to the solder bump but also to the underlying connection between 1) the pad and runner and 2) the supporting substrate. Thus the applicants have found during testing a tendency towards a weakening or complete delamination of the pad/substrate interface. In contrast such structure weakening or delamination does not occur for typical stress associated with handling, transport, or dropping of the device. As a result, any conclusions relative to the solder bump integrity drawn from testing is unreliable. The reliability of testing in accordance with the invention is substantially enhanced by employing a test structure manufactured with the devices to be tested in the normal manufacturing stream. This test structure, however, does not employ the same pad and runner configuration as in the manufactured devices. In particular, the test structure has a pad upon which the solder bump is ultimately formed that has a specific surface area relative to the opening in the solder mask that confines the solder bump. That is, the pad should, at every point along the periphery of the solder mask opening, extend under the solder mask, beyond the periphery of the solder mask opening a distance that is at least as long as half the solder mask opening primary dimension. (The solder mask opening primary dimension is equal to the diameter of a circle having the same area as defined by the region of the pad left uncovered by mask material at the solder mask opening.)
Additionally, the test structure should include all material layers in the manufactured device that contribute to formation of the intermetallic compound (IMC) at the solder pad interface plus one additional layer below such IMC provided such additional layer has a metallic composition. (Below, in the context of this invention, is in a direction towards the substrate upon which the pad is formed.)
After solder formation and generally before further processing of the corresponding manufacturing lot the test structure is subjected to the test probe as previously described. Since the test structure has the same characteristic mechanical attributes as the device being manufactured and since the additional pad material prevents weakening of the pad/substrate interface, an enhanced reliability in the prediction of solder bump failure is achieved even for lead-free solder composition. The results on the test structure are employed to determine whether the device that is being manufactured should be completed or whether modification to such devices is required before completion to avoid solder joint failure.
As discussed, the invention involves the use of a test structure formed together with devices being manufactured. After solder bump formation on the devices being manufactured and on the test structure, such structure is probed. For example, as shown in
If unacceptable results are indicated by the test structure, remedial action is performed on the devices being manufactured. Remedial action includes, for example, elimination of the manufactured lot, or alternatively treating some or all of the manufactured devices to improve the solder bump structure. Suitable treatments include processes such as subjecting the lot to a drop of 1 meter and removing any components in which at least one solder joint is no longer viable after dropping. If the lot is treated, as opposed to eliminated, the lot undergoes continued processing through the manufacturing process. Accordingly, devices whose accompanying test structure pass testing, or devices after a negative test that have been treated to improve solder bump performance or to eliminate unacceptable joints are used for electrical connection to another component. Thus, if the solder bumps are present on an integrated circuit, such integrated circuit is mated for example, to corresponding pads on a printed circuit board.
Although it is acceptable to use one test structure for a manufacturing lot, a multiplicity of such test structures for a lot is employable. In such case, all or a portion of the test structures are subjected to probing and the lot is either processed or a remedial action is taken based on the results of such testing.
As previously discussed, a test structure or structures are formed along with a manufacturing lot of devices. During such manufacture, pads and runners are formed for the devices and an overlying soldering mask is structured with openings exposing the underlying pads. The test structures are similarly formed except the runner configuration is not required (although could be present) and instead the pads are sized to prevent delamination or other compromise. As shown in
After the pads are formed manufacture typically continues with regions added to the pad to facilitate adhesion of the solder bump. For example, in one common approach (denominated ENIG), sequential layers of electroless plated nickel followed by electroless plated immersion gold are formed. (Such processes have become common in the trade and are described in Electroless Nickel Plating, W. Reidel, ASM International, Metal Park, Ohio, 1998. Similarly, another approach (denominated ENEPIG) involves the sequential formation of regions by electroless nickel plating, electroless palladium plating, followed by autocatalytic plating of gold. (This alternate approach is also common in the trade and is described in “Study of Ni—P/Pd/Au as a Final Finish for Packaging,” S. Hashimoto et. al., IMAPS, (International Microelectronics and Packaging Society) 2006.) After the surface treatment for the pad is provided, generally a solder mask is applied and openings over the pad are formed by photodelineation processes. (See Tummala et. al. supra for a description of typical solder mask compositions and processes for their photodelineation.) A solder bump (or solder ball) is then formed on desired pads exposed by solder mask delineation. (Solder bump formation is described in Low Cost Flip Chip Technologies, J. Lau, McGraw-Hill, New York, N.Y., 2000 and solder ball attachment is described in Tummala et. al supra.)
To form electrical connection between two components e.g. an integrated circuit and a printed circuit board, a reflow process is generally employed. For reflow the structure is subjected to a temperature that is generally ramped at a rate of 0.5 to 10 degrees C. per sec to a temperature in the range 185 to 225 degrees C. for lead containing solders such as a eutectic lead/tin solder and 235 to 260 degrees C. for lead-free solders. The temperature is held in such range for a time period in the range 30 to 120 sec and then generally lowered at a rate in the range 0.5 to 5 degrees C. per sec. For lead-free solders, it is generally desirable to repeat this reflow process using the same range of parameters.
As previously discussed, the reflow process along with solder bump formation induces formation of an intermetallic compound and involves the chemical interaction of the solder composition with one or more of the layers present above the pad and possibly with the composition of the pad itself. The test structure should be manufactured so that the same layers overlying the pad are present in the test structure as compared to the devices being manufactured so that essentially the same intermetallic compound is formed. For example, the test structure pads are treated in precisely the same manufacturing lot as the devices being manufactured to form the layers overlying the pads. Additionally, at least one metal layer below those involved in intermetallic compound formation should have essentially the same composition in the test structure as in the devices being manufactured. (If in the manufacturing device there is no metal region underlying the layers involved in intermetallic compound formation, then this requirement of an additional metal region is not necessary.) In an advantageous approach the test structure after pad formation is processed along with the devices being manufactured in exactly the same manner.
| Number | Name | Date | Kind |
|---|---|---|---|
| 6294397 | Jarvis et al. | Sep 2001 | B1 |
| 6415974 | Jao | Jul 2002 | B2 |
| 6787918 | Tsai et al. | Sep 2004 | B1 |
| 6960836 | Bachman et al. | Nov 2005 | B2 |
| 20060231835 | Choi et al. | Oct 2006 | A1 |
| 20080136018 | Kato et al. | Jun 2008 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20100022034 A1 | Jan 2010 | US |