This invention relates to novel materials useful for lithographic plates coatings and to plates, coatings and coating solutions containing these materials. More specifically, these new materials and coating solutions are useful in the preparation of coating for lithographic offset printing plates for direct digital imaging by near-infrared laser radiation.
On-press developable negative-working lithographic offset printing plates are known in the prior art. Fox example, U.S. Pat. No. 5,569,573 teaches lithographic printing plates comprising a laser imaging layer containing microencapsulated oleophilic materials in hydrophilic polymer binders. EP 0 770 495 A1 teaches lithographic printing plates comprising near infrared absorption materials, polymer binders and thermoplastic particles capable of coalescing under heat. U.S. Pat. No. 6,983,694 teach on-press developable negative-working offset printing plates coated with near infrared sensitive coating compositions comprising thermoplastic polymer particles, such as polystyrene or poly(acrylonitrile-co-styrene) particles, non-reactive hydrophilic polymer binder and near infrared absorption dyes.
Also, U.S. Pat. No. 6,261,740 teaches negative-working offset printing plates coated with near infrared sensitive coating compositions containing methoxymethacrylamide copolymers, phenolic resins, iodonium salts and near infrared absorption dyes. U.S. Pat. Nos. 6,124,425 and 6,177,182 teach on-press developable negative-working offset printing plates coated with thermally near-infrared absorbing polymers, which undergo cross-linking reactions via cationic polymerization upon exposure to near infrared radiation. The near infrared chromophoric moieties are functionalized to the polymeric backbone via ether and ammonium bonds. U.S. Pat. No. 6,960,422 teaches negative-working offset printing plates, which contain a near infrared sensitive base-coat compositions comprising molecular near infrared dyes, radical generators, radical polymerizable urethane compounds, reactive polymer binders and other additives.
Moreover, U.S. Pat. Nos. 6,969,575 and 7,001,704 teach on-press developable negative-working offset printing plates having an image-forming layer, which comprise near infrared absorbing microcapsules and acid generator compound. U.S. Pat. Nos. 6,582,882, 6,846,614 and 6,899,994 and co-pending US patent application 2005/0123853 teach on-press developable negative-working offset printing plates, which are coated with thermally imageable compositions containing polymer binders, initiator systems and polymerizable components. The described polymer binders are copolymers having non-reactive polyethylene oxide and polypropylene block, or graft copolymers having non-reactive polyethylene oxide side chains co-polymerized with acrylonitrile, styrene and other monomers. The polymerizable components are viscous liquid oligomers containing multiple acrylic functional groups. The initiator system contains near infrared absorption dyes and radical producing compounds, such as triazine and iodonium salts.
All of these coating compositions and printing plates show some disadvantages such as having a tacky surface which causes difficulties for handling and storage, exhibiting phase separation and/or surface crystallization, being difficult to prepare, requiring high laser power to achieve imaging, having poor substrate adhesion and consequently failing to provide sufficient run length on press, not being developable on-press, exhibiting poor scratching resistance, requiring an over-coating layer and/or a special substrate surface treatment and being expensive to manufacture.
There thus remains a need for new materials and new coatings for lithographic plates that would overcome some or all of the drawbacks of the prior art.
This invention relates to iodonium salts, acetal copolymers and polymer binders, each comprising at least one functional group capable of undergoing cationic or radical polymerization
This invention further relates to the method for preparing the iodonium salts, acetal copolymers and polymer binders of the invention. More specifically, one such method for preparing an iodonium salt of the invention comprises attaching a pendant group to an iodonium salt, wherein the pendant group is obtained by reacting a mono-isocyanate, a di-isocyanate or a poly-isocyanate with an amine or an alcohol, which is terminated by one or more groups each independently selected from acrylate, methacrylate and vinyl-ether.
The present invention further relates to the use of the iodonium salts, acetal copolymers and polymer binders of the invention or a mixture thereof in the preparation of coating solutions and to the coatings produced using these solutions.
The invention also relates to coating solutions and to negative working lithographic printing plate comprising the coatings and/or the iodonium salts, acetal copolymers and polymer binders of the invention.
Thermally Reactive Iodonium Salts
The present invention relates to iodonium salt comprising a positively charged iodine atom to which two aryl rings are attached, and a negatively charged counter ion. When exposed to near infrared radiation or heat, these salts are radical and acid generators.
The iodonium salts of the present invention comprise one or more functional groups that can undergo radical and/or cationic polymerization. Upon exposure to heat, the iodonium salt will generate radicals and acid, which will initiate the radical or cationic polymerization of these functional groups. This will contribute to the formation of a network within the irradiated area of the coating.
More specifically, the iodonium salts of the invention may contain radical polymerizable groups, such as acrylate, methacrylate and vinyl ether. These radical polymerizable groups may be pendanted to the aryl rings of the salt via urethane and/or urea bonds. These salts may have the following general structures:
wherein:
In a more specific embodiment, Y1 and/or Y2 may be obtained by reacting a mono-isocyanate, di-isocyanate and/or poly-isocyanate with an amine or an alcohol comprising single or multiple acrylate, methacrylate and/or vinyl-ether terminated groups. These isocyanate compounds may be Desmodur™ N100, Desmodur™ N3300, Desmodur™ CB 75N, Desmodur™ I, Desmodur™ W, Desmodur™ M, Desmodur™ H and Desmodur™ TD 80, which are sold by Bayer Canada.
In a specific embodiment, the alcohol comprises multiple acrylate terminated groups. Such alcohol may be are obtained from Sartomer. This alcohol may be pentaerylthritol triacrylate (Trade-name SR 444) and dipentaerylthritol pentaacrylate (Trade-name SR399).
In another specific embodiment, the alcohol comprises single acrylate and methacrylate compounds and may be obtained from Sigma-Aldrich Canada. The alcohol may be 2-hydroxyethylacrylate, 2-hydroxyethylmethacrylate, 4-hydroxybutylacrylate, 4-hydroxybutylmethacrylate, 6-hydroxyhexylacrylate, 6-hydroxyhexylmethacrylate, poly(ethylene glycol) acrylate, poly(ethylene glycol) methacrylate, poly(propylene glycol) acrylate and poly(propylene glycol) methacrylate.
Y1 and Y2 may have the following chemical structures:
wherein:
More specifically, Q1 and Q2 may independently have any of the following structures:
wherein R is hydrogen or methyl.
The synthesis of urethane containing iodonium salts having no reactive (polymerizable) functional groups can be seen in U.S. Pat. No. 6,380,277, which is incorporated herein as reference.
The iodonium salt of the present invention may be used for the preparation of coating solutions and coatings. Such coating may comprise from about 5 to about 60% by solid weight of the iodonium. The coatings are usually prepared by depositing a coating solution comprising the iodonium salt onto a substrate. These solutions comprise a solvent or a mixture of solvent allowing the formation of the coating. Any solvent known to the person of skill in the art to be appropriate for this purpose can be used. Examples of such solvents include n-propanol, water and other similar solvents.
In a specific embodiment, the coating/coating solution of the present invention comprises a mixture of iodonium salts, which may ease the manufacturing process.
Near Infrared Absorbing Dyes
The coating/coating solution of the present invention may also comprise a near infrared absorbing dye which produces heat upon exposure to near infrared radiation. More specifically, this near infrared absorbing dye may be a molecular dye, a dimeric dye, a dendrimeric dye or a polymeric dye. In a specific embodiment, this dye is an acetal copolymer.
This molecular dye, and more particularly this acetal copolymer, may have attached thereto a functional group capable of undergoing cationic or radical polymerization. Therefore, when the iodonium salt produces acid/radicals, this functional group will react with other such functional groups present in the coating, for example that of the iodonium salt, to produce a chemical link, and contribute to the formation of a network within the irradiated area of the coating.
More specifically, the near infrared absorbing acetal copolymers may have a molecular weight greater than about 2,000 g/mol and may either be soluble in organic solvents or in aqueous solutions. Furthermore, they may have the following general structure:
wherein:
More specifically, the G1 processing segment of this invention may be a linear or branched alkyl or aryl compound containing cyano, hydroxy, dialkylamino, trialkylammonium salts, ethylene oxide, propylene oxide, methylbenzylsulfonyl-carbamate or carboxylic acid and phosphoric acid functional groups.
The G2 thermal reactive segment of this invention may be a linear or branched alkyl or aryl compound and may contain a functional group capable of undergoing radical and/or cationic polymerization, such as acrylate, methacrylate, and vinyl ether.
The G2 thermal reactive segment may have the following structures:
wherein:
In another specific embodiment, the G2 segments may have pendant groups to those illustrated in formulas 2 to 7, but terminated with vinyl ether, alkoxy-methyl acrylamide or alkoxy methacrylamide functional groups.
The G3 segment may be similar to that described in US Patent Publication No. US 2006-0275698 A1, which is incorporated herein as reference. More specifically, the G3 segment may have the following structures:
wherein NIR is a near-infrared absorbing chromophore that exhibits one or more strong absorption peaks between 700 and 1100 nm and may optionally exhibit one or more strong absorption peaks between 400 and 700 nm.
The acetal polymer of the invention may also comprise different G3 segments comprising different near-infrared absorbing chromophores.
The near-infrared absorbing chromophores (NIR chromophores) may be near infrared absorbing organic compounds containing cyanine and/or arylimine functional groups. These chromophores may have the following structures:
wherein:
In a specific embodiment, R4, R5 and R6 may represent a polymerizable substituents having the following structure:
wherein:
The near infrared absorbing acetal copolymers may be used in the coating of the present invention in quantities ranging from about 5 to 50 by solid weight.
Polymer Binders
The coating/coating solution of the present invention may also comprise a polymer binder. This polymer binder may be used in the coating in quantities ranging from about 1 to about 50% by solid weight.
More specifically, the polymer binders of this invention may be polymers, copolymers or dendrimers, which may comprise functional group(s) which can undergo radical and/or cationic polymerization. Therefore, when the iodonium salt produces acid/radicals, these functional groups will react with other such functional groups present in the coating, for example that of the iodonium salt and the dye (if present), to produce chemical links, and contribute to the formation of a network within the coating.
Specifically, these functional groups may be acrylate, methacrylate, and vinyl ether. More specifically, these functional groups may be cation reactive functional groups such as hydroxy, N-methoxymethylacrylamide and N-methoxymethylmethacrylamide.
The polymer binders of the invention may be solvent- and/or water-soluble cellulose ethers comprising a functional group which can undergo radical and/or cationic polymerization. This cellulose ether may be obtained by reacting of 2-isocyanto-ethyl methacrylate with the hydroxymethyl, hydroxyethyl and hydroxypropyl group on the cellulose backbone. The cellulose ether of the invention may have the following structure:
wherein:
More specifically, the G5 groups may have the following structure
wherein m is 0 or 1 and R is hydrogen or methyl.
The polymer binder of the invention may also be an acetal copolymer which does not absorb near infrared radiation. More precisely, the acetal copolymers of this invention may have the following general structure:
wherein G1, G2, a, b, d and e are similar to those defined in Formula 1 as above and wherein when the optional G1 and/or G2 segments are not present,
The polymer binders of the invention may also be copolymers comprising a functional group which can undergo radical and/or cationic polymerization. Such copolymers can be obtained from acrylonitrile, styrene, poly(ethylene glycol) acrylate, poly(ethylene glycol) methacrylate and methoxymethylmethacrylamide monomers. More precisely, the copolymers of the invention may be obtained by copolymerizating:
wherein:
The acetal copolymer of the present invention may be used in the preparation of a coating/coating solution. The coating/coating solution may also comprise the iodonium salt of the present invention and a polymer binder in the above mentioned quantities.
The polymer binder of the present invention may be used in the preparation of a coating/coating solution. The coating/coating solution may also comprise the iodonium salt of the present invention and a near-infrared absorbing moiety in the above mentioned quantities.
Colorants and Stabilizers
The coatings/coating solutions of the invention may also comprise colorants to provide good image printout after laser imaging. These colorants of this invention may be the derivatives of triarylpyridine, xanthene and isobenzofuranone. These color-generating compounds may be colorless and then become colored in the presence of free radical or acid. More specifically, these compounds may be:
The colorants may be used in the coatings of the present invention in quantities ranging from 0.5 to 5% by solid weight.
The coatings/coating solutions of the invention may also comprise stabilizers to prolong the shelf-life of the printing plates during storage. These stabilizers may be methoxyphenol, hydroxyphenol, phenothiazine, 3-mercapto triazol or monomethyl ether hydroquinone. These stabilizers may be used in the coatings of the present invention in quantities ranging from 0.5 to 5% by solid weight.
Negative-working Lithographic Printing Plates
The coating solutions of the present invention may be used in the preparation of negative-working lithographic printing plates.
This invention therefore also relates to printing plates containing the iodonium salts, the acetal copolymers and/or the polymer binders of the present invention. These lithographic offset printing plates may be directly imaged with near-infrared laser imaging devices in computer-to-plate and digital offset printing technologies.
More specifically, such coating solutions may be used in the production of on-press developable negative-working lithographic offset printing plates that comprise single- or multiple-layer coatings deposited on a substrate such as anodized aluminum, plastic films or paper.
The aluminum substrate may be brushed-grained or electro-grained, then anodized with acidic solutions.
The anodized aluminum substrate may be coated with a polymeric adhesion-promoting layer. The adhesion-promoting and heat insulating layer may be obtained from water solutions containing poly(acrylic acid), poly(acrylic acid-co-vinylphosphoric acid) or polyvinyl phosphoric acid, which are then dried using hot air at about 110° C. The coating weight of the adhesion-promoting layer may be between about 0.1 and about 1.0 g/m2.
The thermally reactive coating solutions may be deposited on top of the adhesion-promoting layer and may have a coating weight between about 0.5 and about 2.5 g/m2.
Other embodiments and further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. It should be understood, however, that this detailed description, while indicating preferred embodiments of the invention, is given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art.
In the appended drawings:
The present invention is illustrated in further details by the following non-limiting examples.
In these examples, these syntheses were performed in a 4 necks glass reactor equipped with a water condenser, a mechanical stirrer, a dropping funnel and a nitrogen or air gas inlet. The molecular structures of the obtained materials were determined by proton NMR and FTIR spectroscopy. The average molecular weight of the copolymers obtained was determined by size exclusion chromatography (SEC), using N,N-dimethylformamide (DMF) solutions and calibrated with polystyrene standards. The UV-Visible near-infrared spectra of the synthesized polymers were measured in methanol solutions or on the solid films using a UV-VIS spectrophotometer (PerkinElmer, Model Lambda 35).
Also, the coated plates were imaged using Creo Trendsetter 3244 equipped with 830 nm lasers. The imaged plate was mounted on AB Dick duplicator press using black ink (available from Pacific Inks, Vietnam) and fountain solution containing 3.0 parts of MYLAN-FS100 in 97.0 parts of water (available from MyLan Chemicals Inc., Vietnam).
Synthesis of the Reactive Near-infrared Sensitizing Acetal Copolymers (Dyes):
The thermally reactive near-infrared sensitizing acetal copolymer PVA-01 was synthesized by adding, by portions, 90 grams of polyvinyl alcohol (Celvol™ 103, a 98% hydrolyzed polyvinyl acetate having an average molecular weight of about 18,000) to a reaction flask containing 500 grams of dimethylsulfoxide (DMSO) at 60° C., under nitrogen atmosphere and with constant stirring. After complete dissolution, 3 ml of concentrated sulfuric acid, which acts as a catalyst for this reaction, were added to the flask. After thirty minutes, 12.2 grams of 4-hydroxybenzaldehyde (100 mmole, available from Sigma-Aldrich, Canada) were slowly added to the flask and the mixture was stirred at 60° C. for 4 hours. Then, 1 gram of sodium hydride (60% in mineral oil, available from Sigma-Aldrich, Canada) was slowly added into the reaction. After hydrogen gas was no longer produced from the reaction, 3.0 grams of 3-bromopropyl-methacryloyl-ethyl carbamate (see structure below, available from American Dye Source Inc., Canada) was added into the reaction mixture.
The reaction was continued for 30 minutes, then 20 grams of 2-[2-[2-chloro-3-[[1,3-dihydro-1,1-dimethyl-3-(4-sulfonylbutyl)-2H-benzo[e]indol-2-ylidene]-ethylidene]-1-cyclohexen-1-yl]ethenyl]-1,1-dimethyl-3-(4-sulfonylbutyl)-1H-benzo[e]indolium hydroxy inner salt, sodium salt (13 mmole, available from American Dye Source, Inc.) was slowly added to the flask. The resulting mixture was stirred at 60° C. for another 5 hours. The reaction product was precipitated in acetone, filtered and washed copiously with acetone. It was then dried in air until constant weight.
The UV-Vis-NIR spectrum of the obtained PVA-01 thermally reactive near-infrared absorbing acetal copolymer was recorded in methanol and exhibited a strong absorption band at 803 nm. The ideal structure of the PVA-01 near-infrared absorbing acetal copolymer is shown in
The thermally reactive near-infrared absorbing acetal copolymer PVA-01 was synthesized by adding, by portions, 90 grams of polyvinyl alcohol (Celvol™ 103, a 98% hydrolyzed polyvinyl acetate having an average molecular weight of about 18,000) to a reaction flask containing 500 grams of dimethylsulfoxide (DMSO) at 60° C., under nitrogen atmosphere and with constant stirring. After complete dissolution, 3 ml of concentrated sulfuric acid, which acts as a catalyst for this reaction, were added to the flask. After thirty minutes, 12.2 grams of 4-hydroxybenzaldehyde (100 mmole, available from Sigma-Aldrich, Canada) were slowly added to the flask and the mixture was stirred at 60° C. for 4 hours. Then, 1 gram of sodium hydride (60% in mineral oil, available from Sigma-Aldrich, Canada) was slowly added into the reaction. After hydrogen gas was no longer produced from the reaction, 3.0 grams of 3-bromopropyl-methacryloyl-ethyl carbamate was added into the reaction mixture. The reaction was continued for 30 minutes, then 20 grams of 2-[2-[2-chloro-3-[2-(1,3-dihydro-1,3,3-trimethyl-2H-indol-2-ylidene)-ethylidene]-1-cyclohexen-1-yl]ethenyl]-1,3,3-trimethyl-1H-indolium chloride (available from American Dye Source, Inc.) was slowly added to the flask. The resulting mixture was stirred at 60° C. for another 3 hours. Then, 5 grams of sodium tetraphenylborate was added into the reaction flask and it continued to stir for additional 2 hours. The reaction product was precipitated in de-ionized water, filtered and washed copiously with water. It was then dried in air until constant weight.
The UV-Vis-NIR spectrum of the obtained PVA-02 thermally reactive near-infrared absorbing acetal copolymer was recorded on a thin film and exhibited a strong absorption band at 800 nm. The ideal structure of the PVA-02 near-infrared absorbing acetal copolymer is shown in
The thermally reactive near-infrared absorbing acetal copolymer, PVA-01, was synthesized by adding, by portions, 90 grams of polyvinyl alcohol (Celvol™ 103, a 98% hydrolyzed polyvinyl acetate having an average molecular weight of about 18,000) to a reaction flask containing 500 grams of dimethylsulfoxide (DMSO) at 60° C., under nitrogen atmosphere and with constant stirring. After complete dissolution, 3 ml of concentrated sulfuric acid, which acts as a catalyst for this reaction, were added to the flask. After thirty minutes, 6.1 grams of 4-hydroxybenzaldehyde (available from Sigma-Aldrich, Canada) were slowly added to the flask and the mixture was stirred at 60° C. for 4 hours. Then, 0.5 grams of sodium hydride (60% in mineral oil, After hydrogen gas was no longer produced from the reaction, 10 grams near infrared absorption containing reactive functional groups having the structure shown below (available from American Dye Source, Inc.) was slowly added to the flask.
The resulting mixture was stirred at 50° C. for another 5 hours. The reaction product was precipitated in 10 liters of de-ionized water, filtered and washed copiously with water. It was then dried in air until constant weight.
The UV-Vis-NIR spectrum of the obtained PVA-03 thermally reactive near-infrared absorbing acetal copolymer was recorded on a thin film and exhibited a strong absorption band at 830 nm. The ideal structure of the near infrared absorbing acetal copolymer PVA-03 is shown in
The thermally reactive near-infrared absorbing acetal copolymer PVA-01 was synthesized by adding, by portions, 90 grams of polyvinyl alcohol (Celvol™ 103, a 98% hydrolyzed polyvinyl acetate having an average molecular weight of about 18,000) to a reaction flask containing 500 grams of dimethylsulfoxide (DMSO) at 60° C., under nitrogen atmosphere and with constant stirring. After complete dissolution, 3 ml of concentrated sulfuric acid, which acts as a catalyst for this reaction, were added to the flask. After thirty minutes, 12.2 grams of 4-hydroxybenzaldehyde (available from Sigma-Aldrich, Canada) were slowly added to the flask and the mixture was stirred at 60° C. for 4 hours. Then, 1 gram of sodium hydride (60% in mineral oil, available from Sigma-Aldrich, Canada) was slowly added into the reaction. When hydrogen gas was no longer produced from the reaction, 11.0 grams of 10 grams of bromo-terminated poly(ethylene glycol) acrylate (see below structure, available from American Dye Source Inc.) was added into the reaction mixture.
The reaction was continued for 30 minutes, then 20 grams of 2-[2-[2-chloro-3-[2-(1,3-dihydro-1,3,3-trimethyl-2H-indol-2-ylidene)-ethylidene]-1-cyclohexen-1-yl]ethenyl]-1,3,3-trimethyl-1H-indolium 4-methylbenzene sulfonate (available from American Dye Source, Inc.) was slowly added to the flask. The resulting mixture was stirred at 60° C. for another 3 hours. Then, 5 grams of sodium tetraphenylborate was added into the reaction flask and it continued to stir for additional 2 hours. The reaction product was precipitated in de-ionized water, filtered and washed copiously with water. It was then dried in air until constant weight.
The UV-Vis-NIR spectrum of the obtained PVA-04 thermally reactive near-infrared absorbing acetal copolymer was recorded on a thin film and exhibited a strong absorption band at 800 nm. The ideal structure of the PVA-04 near-infrared absorbing acetal copolymer is shown in
Synthesis of Reactive Iodonium Salts:
For the ease of manufacturing and cost effectiveness, the iodonium salts containing reactive functional groups may be synthesized and used as a mixture of various salts. Further, this mixture may be used directly without further purification.
A mixture of reactive iodonium tetraphenylborate having possible structures as in
A mixture of reactive iodonium tetraphenylborate having possible structures as in
A mixture of reactive iodonium tetraphenylborate having possible structures as in
A mixture of reactive iodonium tetraphenylborate having possible structures as in
A mixture of reactive iodonium tetraphenylborate having possible structures as in
Reactive iodonium salt having the structure as shown in
The iodonium salts of
Synthesis of Thermally Reactive Polymer Binders:
The thermally reactive polymer binder, RPB-01 was synthesized by adding, by portions, 25 grams of hydroxypropyl cellulose (Klucel® E, available from Hercules, USA) to a reaction flask containing 500 grams of 1,3-dioxolane at 60° C., under air atmosphere and with constant stirring. After complete dissolution, 3 drops of dibutyl tin dilaurate, which acts as a catalyst for this reaction, were added to the flask. Then, 5.0 grams of 2-isocyanatoethylmethacrylate (available from American Dye Source, Canada) were slowly added to the reaction flask and the mixture was stirred at 60° C. for 7 hours. FTIR spectrum of the polymer on KBr pellet indicated that the reaction was completed with the disappearance of the —N═C═O peak at 2274 cm−1. The ideal structure of RPB-01 is shown in
The reactive polymer binder, RPB-02 was synthesized in way similar to that of Example 11 with the exception that 10 grams of 2-isocyanatoethylmethacrylate was used in the reaction. The ideal structure of RPB-02 is similar to that of RPB-01 with more reactive functional groups present in the polymer. n-Propanol was added into the reaction to provide 5.0% solid content solution.
The reactive polymer binder RPB-03 was synthesized by adding, by portions, 90 grams of polyvinyl alcohol (Celvol™ 103, a 98% hydrolyzed polyvinyl acetate having an average molecular weight of about 18,000) to a reaction flask containing 500 grams of dimethylsulfoxide (DMSO) at 60° C., under nitrogen atmosphere and with constant stirring. After complete dissolution, 3 ml of concentrated sulfuric acid, which acts as a catalyst for this reaction, were added to the flask. After thirty minutes, 12.2 grams of 4-hydroxybenzaldehyde (100 mmole, available from Sigma-Aldrich, Canada) were slowly added to the flask and the mixture was stirred at 60° C. for 4 hours. Then, 0.5 gram of sodium hydride (60% in mineral oil, available from Sigma-Aldrich, Canada) was slowly added into the reaction. After hydrogen gas was no longer produced from the reaction, 3.0 grams of 3-bromopropyl-methacryloyl-ethyl carbamate was added into the reaction mixture. The reaction was continued for 5 hours at 60° C. The product was precipitated in de-ionized water, filtered and washed copiously with de-ionized water. It was then dried in air until constant weight. The ideal structure of RPB-03 is shown in
The reactive polymer binder RPB-04 was synthesized by adding, by portions, 90 grams of polyvinyl alcohol (Celvol™ 103, a 98% hydrolyzed polyvinyl acetate having an average molecular weight of about 18,000) to a reaction flask containing 500 grams of dimethylsulfoxide (DMSO) at 60° C., under nitrogen atmosphere and with constant stirring. After complete dissolution, 3 ml of concentrated sulfuric acid, which acts as a catalyst for this reaction, were added to the flask. After thirty minutes, 6.5 grams of butyraldehyde and 2.35 grams of acryloyl-propyloxybenzaldehyde (available from American Dye Source Inc., Canada) were added into the reaction mixture. The reaction was continued for 5 hours at 60° C. The product was precipitated in de-ionized water, filtered and washed copiously with de-ionized water. It was then dried in air until constant weight. The ideal structure of RPB-04 is shown in
The reactive polymer binder, RPB-05 was synthesized by heating a mixture of 200 grams of anhydrous 1,3-dioxolane, dissolving with 15.0 g poly(ethylene glycol) acrylate (Mn˜2,010, available from American Dye Source Inc., Canada), 15.0 g styrene, 50.0 g acrylonitrile and in a 1 L 4-neck flask at 75° C. under a nitrogen atmosphere and constant stirring. After heating for 30 minutes, 0.5 g of Vazo™ 64 was added to the reaction mixture. After 10 hours of polymerization at 75° C., another 0.5 g of Vazo™ 64 was added into the reaction mixture and the polymerization was continued for another 14 hours. Air was introduced into the reaction mixture and it stirring at 75° C. continued for an additional 2 hours to terminate the polymerization. The reaction temperature was lowered to 5° C. and 4 grams of triethylamine were added into the reaction mixture. Then, a solution containing 10 grams of 1,3-dioxolane and 2 grams of acryloyl chloride was slowly introduced into the reaction. The reaction was stirred at room temperature for 5 hours. The product was precipitated in water and dried until constant weight. The molecular weight of RPB-03 was determined to be around 28,000 with a polymer dispersity of 1.4. The ideal structure of RPB-05 is shown in
An emulsion of RPB-05 was prepared by slowly adding 50 grams of de-ionized water into 200 grams n-propanol solution, in which 80 grams of RPB-03 were dissolved, using a high shear mixer set at 7,500 rpm.
The reactive polymer binder, RPB-06 was synthesized by heating a mixture of 200 grams of n-propanol and 50 grams of de-ionized water, which in which 15.0 g poly(ethylene glycol) acrylate (Mn˜2,000, available from American Dye Source Inc., Canada) were dissolved, 5.0 grams of N-methoxymethylmethacrylamide (available from American Dye Source Inc., Canada), 15.0 g styrene and 50.0 g acrylonitrile, in a 1 L 4-neck flask at 75° C. under a nitrogen atmosphere and constant stirring. After heating for 30 minutes, 0.5 g of Vazo™ 64 was added into the reaction mixture. The solution became hazy within 30 minutes of polymerization. After polymerization for 10 hours at 75° C., another 0.5 g of Vazo™ 64 was added into the reaction mixture and the polymerization was continued for another 14 hours. Air was introduced into the reaction mixture and stirring at 75° C. was continued for an additional 2 hours to terminate the polymerization. The molecular weight of RPB-06 was determined to be around 29,000 with polymer dispersity of 1.7. The ideal structure of RPB-06 is shown in
On-Press Developable Negative-Working Lithographic Printing Plates
A coating solution with the following composition was coated on a brush-grained, phosphoric acid anodized aluminum substrate using wire-wound rod and dried at 80° C. with hot air. The obtained coating weight was around 1.0 g/m2.
The plate was imaged between 100 and 250 mJ/cm2 and mounted on the AB Dick press. High quality printing image was obtained on paper after 10 impressions. The plate can be used to print more than 20,000 high-resolution copies.
A coating solution with the following composition was coated on a brush-grained, phosphoric acid anodized aluminum substrate using wire-wound rod and dried at 80° C. with hot air. The obtained coating weight was around 1.0 g/m2.
The plate was imaged between 100 and 250 mJ/cm2 and mounted on the AB Dick press. High quality printing image was obtained on paper after 10 impressions. The plate can be used to print more than 20,000 high-resolution copies.
A coating solution with the following composition was coated on a brush-grained, phosphoric acid anodized aluminum substrate using wire-wound rod and dried at 80° C. with hot air. The obtained coating weight was around 1.0 g/m2.
The plate was imaged between 100 and 250 mJ/cm2 and mounted on the AB Dick press. High quality printing image was obtained on paper after 10 impressions. The plate can be used to print more than 20,000 high-resolution copies.
A coating solution with the following composition was coated on a brush-grained, phosphoric acid anodized aluminum substrate using wire-wound rod and dried at 80° C. with hot air. The obtained coating weight was around 1.0 g/m2.
The plate was imaged between 100 and 250 mJ/cm2 and mounted on the AB Dick press. High quality printing image was obtained on paper after 10 impressions. The plate can be used to print more than 20,000 high-resolution copies.
A coating solution with the following composition was coated on a brush-grained, phosphoric acid anodized aluminum substrate using wire-wound rod and dried at 80° C. with hot air. The obtained coating weight was around 1.0 g/m2.
The plate was imaged between 100 and 250 mJ/cm2 and mounted on the AB Dick press. High quality printing image was obtained on paper after 10 impressions. The plate can be used to print more than 20,000 high-resolution copies.
Although the present invention has been described hereinabove by way of specific embodiments thereof, it can be modified, without departing from the spirit and nature of the subject invention as defined in the appended claims.
This application is a divisional application of U.S. patent application Ser. No. 11/746,252, which was filed on May 9, 2007 now U.S. Pat. No. 7,910,768 and which claims priority on U.S. provisional application No. 60/747,474, filed on May 17, 2006. All documents above are incorporated herein in their entirety by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3885964 | Nacci | May 1975 | A |
| 4517277 | Lynch et al. | May 1985 | A |
| 4701402 | Patel et al. | Oct 1987 | A |
| 5569573 | Takahashi et al. | Oct 1996 | A |
| 6008267 | Vallee et al. | Dec 1999 | A |
| 6124425 | Nguyen | Sep 2000 | A |
| 6153660 | Fujimaki et al. | Nov 2000 | A |
| 6177182 | Nguyen | Jan 2001 | B1 |
| 6261740 | Nguyen et al. | Jul 2001 | B1 |
| 6368772 | Telser et al. | Apr 2002 | B1 |
| 6380277 | Oestreich et al. | Apr 2002 | B1 |
| 6548222 | Teng | Apr 2003 | B2 |
| 6566035 | Aoshima | May 2003 | B1 |
| 6582882 | Pappas et al. | Jun 2003 | B2 |
| 6846614 | Timpe et al. | Jan 2005 | B2 |
| 6884560 | Yanaka et al. | Apr 2005 | B2 |
| 6884562 | Schadt, III et al. | Apr 2005 | B1 |
| 6899994 | Huang et al. | May 2005 | B2 |
| 6960422 | Goto | Nov 2005 | B2 |
| 6969575 | Inno | Nov 2005 | B2 |
| 6983694 | Vermeersch et al. | Jan 2006 | B2 |
| 7001704 | Oshima et al. | Feb 2006 | B2 |
| 7041711 | Kunita | May 2006 | B2 |
| 7169518 | Savariar-Hauck et al. | Jan 2007 | B1 |
| 7279263 | Goodin | Oct 2007 | B2 |
| 20020015826 | Desmarteau et al. | Feb 2002 | A1 |
| 20030162123 | Barr et al. | Aug 2003 | A1 |
| 20050123853 | Munnelly et al. | Jun 2005 | A1 |
| 20050170286 | Huang et al. | Aug 2005 | A1 |
| 20060032390 | Hoshi et al. | Feb 2006 | A1 |
| 20060275698 | Nguyen et al. | Dec 2006 | A1 |
| 20070269727 | Savariar-Hauck et al. | Nov 2007 | A1 |
| 20080229957 | Yu | Sep 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 306 571 | Aug 1992 | CA |
| 2 299 856 | Sep 2000 | CA |
| 0 770 495 | May 1997 | EP |
| 1 106 639 | Jun 2001 | EP |
| 1 204 000 | May 2002 | EP |
| 1 582 346 | Oct 2005 | EP |
| 1582346 | Oct 2005 | EP |
| 1 627 732 | Feb 2006 | EP |
| 1627732 | Feb 2006 | EP |
| 1627732 | Feb 2006 | EP |
| 1 728 838 | Dec 2006 | EP |
| 1 759 836 | Mar 2007 | EP |
| 2003248285 | Sep 2003 | JP |
| 2006-335988 | Dec 2006 | JP |
| WO 9618133 | Jun 1996 | WO |
| WO 0109682 | Feb 2001 | WO |
| WO 2004081662 | Sep 2004 | WO |
| WO 2004101280 | Nov 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20100062370 A1 | Mar 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60747474 | May 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11746252 | May 2007 | US |
| Child | 12579844 | US |