Metal heterocyclic compounds for deposition of thin films

Follow

Information

  • Patent Grant
  • 8636845
  • Patent Number
    8,636,845
  • Date Filed
    Thursday, June 25, 2009
    15 years ago
  • Date Issued
    Tuesday, January 28, 2014
    10 years ago
Information
Abstract
Methods and compositions for depositing a metal containing film on a substrate are disclosed. A reactor and at least one substrate disposed in the reactor are provided. A metal containing precursor is provided and introduced into the reactor, which is maintained at a temperature of at least 100° C. A metal is deposited on to the substrate through a deposition process to form a thin film on the substrate.
Description
BACKGROUND

1. Field of the Invention


This invention relates generally to compositions, methods and apparatus for use in the manufacture of semiconductor, photovoltaic, LCF-TFT, or flat panel type devices. More specifically, the invention relates to methods of forming a thing film on a substrate.


2. Background of the Invention


One reason the requirements for suitable metallorganic precursors, used in chemical vapor depositions (CVD) and/or atomic layer depositions (ALD) for semiconductor manufacturing processes, are increasing is due to the high surface coverage required by the deposited films, as compared to that found through physical vapor deposition methods (e.g. PVD, sputtering method).


For example, preferred production methods for GeSbTe alloy thin films, which are used in phase change memory devices, are changing from PVD methods to CVD/ALD methods with the increasing the capacity of memory cell. The demonstration sample of 512 Mega-bit PRAM was made by PVD method under 90 nm technology node processes in 2007, however in the future CVD/ALD methods will likely be necessary for the production of giga-bit scale (and greater) PRAM devices. A main issue for these future production methods is identifying suitable precursors which will allow for a low temperature, low impurity CVD/ALD film deposition. Similar situations are seen in many stages of semiconductor device manufacture. For instance, precursors for deposition of metallic titanium films are needed, due to the high level of impurities observed in the current processes.


Consequently, there exists a need for a need for materials and methods to deposit precursors to form thin films in semiconductor manufacturing processes.


BRIEF SUMMARY

The invention provides novel methods and compositions for the deposition of metal containing films on a substrate. In an embodiment, a method for depositing a metal film on a substrate comprises providing a reactor, and at least one substrate disposed in the reactor. A metal precursor is provided, where the metal precursor is metal-heterocyclic precursor with one of the following general formulas:

M(NR(CRR)nNR)x(R)y  (I)
M(NRCR═CRNR)x(R)y,  (II)
M′UaZb  (III)

wherein each R is independently selected from among: H; linear, branched or cyclic C1-C6 alkyls; linear, branched or cyclic C1-C6 alkoxyls; linear, branched or cyclic C1-C6 alkylsilyls; linear, branched or cyclic C1-C6 perfluorocarbons; dialkylaminos of the general formula NR′R″ (wherein R′ and R″ are independently selected from H, C1-C6 alkyls, C1-C6 alkylsilyls, C1-C6 perfluorocarbons, and C1-C6 alkylaminos); C1-C6 alkylimidos or alkylsilyliminos; cyanos; carbonyls; phenyls; benzyls; pyridyls; halogens (such as F, Cl, Br, and I); sulfos; nitros; carboxys; hydroxyls; diazos; and azidos;


in the case where R is not substituting part of the cyclometal group, R can be further independently selected from among: an amidinate of the general formula R1NC(CH3)NR1; a formamidinate of the general formula R1NCHNR1; a β-diketonate of the general formula OCR1CR1CR1O; a β-enaminoketonate of the general formula NR1CR1CR1CR1O; and a β-diketiminate of the general formula NR1CR1CR1CR1NR1; wherein each R1 is independently selected from among: H; C1-C6 alkyls; C1-C6 alkylsilyls; C1-C6 perfluorocarbons; C1-C6 alkylaminos; dienyls (such as cyclopentadienyl, pentadienyl, cyclohexadienyl, hexadienyl), each dienyl ligand being substituted or not by C1-C6 linear or branched alkyl groups or C1-C6 linear or branched alkoxy groups; dienes (such as cyclohexadiene, hexadiene, norbornadiene, butadiene, cyclopentadiene, pentadiene, cyclooctadiene), each diene ligand being substituted or not by C1-C6 linear or branched alkyl groups or C1-C6 linear or branched alkoxy groups;


M is at least one member selected from the group consisting of: Be; B; Mg; Al; Si; P; S; Ca; Sc; Ti; V; Cr; Mn; Fe; Co; Ni; Cu; Zn; Ga; Ge; As; Se; Sr; Y; Zr; Nb; Mo; Ru; Rh; Pd; Ag; Cd; In; Sn; Sb; Te; Ba; La; Ce; Pr; Nd; Sm; Eu; Gd; Tb; Dy; Ho; Er; Tm; Yb; Lu; Hf; Ta; W; Re; Os; Ir; Pt; Au; Hg; Tl; Pb; and Bi; M′ is at least one member selected from the group consisting of: Be; B; C; Mg; Al; Si; P; S; Ca; Sc; Ti; V; Cr; Mn; Fe; Co; Ni; Cu; Zn; Ga; Ge; As; Se; Sr; Y; Zr; Nb; Mo; Ru; Rh; Pd; Ag; Cd; In; Sn; Sb; Te; Ba; La; Ce; Pr; Nd; Sm; Eu; Gd; Tb; Dy; Ho; Er; Tm; Yb; Lu; Hf; Ta; W; Re; Os; Ir; Pt; Au; Hg; Tl; Pb; and Bi;


each U is independently selected from among: H; C1-C6 alkyls; C1-C6 alkylsilyls; C1-C6 perfluorocarbons; dialkylaminos of the general formula NR′R″ (wherein R′ and R″ are independently selected from H, C1-C6 alkyls, C1-C6 alkylsilyls, C1-C6 perfluorocarbons, and C1-C6 alkylaminos); cyanos; carbonyls; phenyls; benzyls; pyridyls; halogens (such as F, Cl, Br, and I); sulfos; nitros; carboxys; hydroxyls; diazos; azidos; amidinates of the general formula R1NC(CH3)NR1; formamidinates of the general formula R1NCHNR1; β-diketonates of the general formula OCR1CR1CR1O; β-enaminoketonates of the general formula NR1CR1CR1CR1O; and β-diketiminates of the general formula NR1CR1CR1CR1NR1; wherein each R1 is independently selected from among: H; C1-C6 alkyls; C1-C6 alkylsilyls; C1-C6 perfluorocarbons; C1-C6 alkylaminos; dienyls (such as cyclopentadienyl, pentadienyl, cyclohexadienyl, hexadienyl), each dienyl ligand being substituted or not by C1-C6 linear or branched alkyl groups or C1-C6 linear or branched alkoxy groups;


each Z is independently selected from the metal-heterocyclic precursors of general formula (I) or (II), wherein the oxidation state of the metal-heterocyclic precursor of general formula (I) or (II) has an oxidation state which allows for a coordination between M and M′; n is an integer such that 1≦n≦5; x and y are integers independently determined based upon the oxidation state of M, such that x+y=oxidation state of M; and a and by are integers independently determined based upon the oxidation state of M′, such that a+b=oxidation state of M.


Other embodiments of the current invention may include, without limitation, one or more of the following features:

    • the metal precursor contains an imido bond, the total number of R groups in the metal precursor is greater than or equal to two, and two R groups are substituted by one imido ligand;
    • the metal precursor is of general formula (III) and in the Z portion of the molecule, at least one R group which is indexed by the y variable is substituted with a direct M to M′ bond;
    • maintaining the reactor at a temperature between about 100° C. and about 500° C., and preferably between about 200° C. and about 350° C.;
    • maintaining the reactor at a pressure between about 1 Pa and about 105 Pa, and preferably between about 25 Pa and about 103 Pa;
    • introducing at least one reducing gas into the reactor, wherein the reducing gas is at least one of: hydrogen; ammonia; silane; disilane; trisilane; hydrogen radicals; and mixtures thereof;
    • introducing at least one oxidizing gas into the reactor, wherein the oxidizing gas is at least one of: oxygen; ozone; water; hydrogen peroxide; nitric oxide; nitrous oxide; oxygen radicals; and mixtures thereof;
    • the metal precursor and the reducing gas and/or the oxidizing gas are introduced into the chamber either substantially simultaneously or sequentially;
    • the metal precursor and the reducing gas and/or the oxidizing gas are introduced into the chamber substantially simultaneously and the chamber is configured for chemical vapor deposition;
    • the metal precursor and the reducing gas and/or oxidizing gas are introduced into the chamber sequentially and the chamber is configured for atomic layer deposition;
    • the deposition process is a plasma enhanced deposition process (ALD or CVD); and
    • a metal containing thin film coated substrate.


The foregoing has outlined rather broadly the features and technical advantages of the present invention in order that the detailed description of the invention that follows may be better understood. Additional features and advantages of the invention will be described hereinafter that form the subject of the claims of the invention. It should be appreciated by those skilled in the art that the conception and the specific embodiments disclosed may be readily utilized as a basis for modifying or designing other structures for carrying out the same purposes of the present invention. It should also be realized by those skilled in the art that such equivalent constructions do not depart from the spirit and scope of the invention as set forth in the appended claims.


Notation and Nomenclature

Certain terms are used throughout the following description and claims to refer to various components and constituents. This document does not intend to distinguish between components that differ in name but not function.


As used herein, the term “alkyl group” refers to saturated functional groups containing exclusively carbon and hydrogen atoms. Further, the term “alkyl group” may refer to linear, branched, or cyclic alkyl groups. Examples of linear alkyl groups include without limitation, methyl groups, ethyl groups, propyl groups, butyl groups, etc. Examples of branched alkyls groups include without limitation, t-butyl. Examples of cyclic alkyl groups include without limitation, cyclopropyl groups, cyclopentyl groups, cyclohexyl groups, etc.


As used herein, the abbreviation, “Me,” refers to a methyl group; the abbreviation, “Et,” refers to an ethyl group; the abbreviation, “t-Bu,” refers to a tertiary butyl group; the abbreviation “iPr”, refers to an isopropyl group; the abbreviation “acac”, refers to acetylacetonato; and the abbreviation “Cp” refers to a cyclopentadienyl group.


As used herein the abbreviations: Be; B; C; N; Mg; Al; Si; P; S; Ca; Sc; Ti; V; Cr; Mn; Fe; Co; Ni; Cu; Zn; Ga; Ge; As; Se; Sr; Y; Zr; Nb; Mo; Ru; Rh; Pd; Ag; Cd; In; Sn; Sb; Te; Ba; La; Ce; Pr; Nd; Sm; Eu; Gd; Tb; Dy; Ho; Er; Tm; Yb; Lu; Hf; Ta; W; Re; Os; Ir; Pt; Au; Hg; Tl; Pb; and Bi generally refer to the corresponding elements from the periodic table of elements.


As used herein, the term “independently” when used in the context of describing R groups should be understood to denote that the subject R group is not only independently selected relative to other R groups bearing different subscripts or superscripts, but is also independently selected relative to any additional species of that same R group. For example in the formula MR1x (NR2R3)(4-x), where x is 2 or 3, the two or three R1 groups may, but need not be identical to each other or to R2 or to R3. Further, it should be understood that unless specifically stated otherwise, values of R groups are independent of each other when used in different formulas.





BRIEF DESCRIPTION OF THE DRAWINGS

For a further understanding of the nature and objects for the present invention, reference should be made to the following detailed description, taken in conjunction with the accompanying drawings, in which like elements are given the same or analogous reference numbers and wherein:



FIG. 1 illustrates schematic representations of chemical structures corresponding to the metal precursor, as according to various embodiments of the current invention.





DESCRIPTION OF PREFERRED EMBODIMENTS

Generally, embodiments of the current invention relate to methods and compositions for the deposition of a metal containing film on a substrate through the use of a metal precursor. Generally, and as described above, the metal precursor is a metal-heterocyclic precursor with one of the following general formulas:

M(NR(CRR)nNR)x(R)y  (I)
M(NRCR═CRNR)x(R)y,  (II)
M′UaZb  (III)


In embodiments where the metal precursor has the general formula (I), the precursor may be shown structurally as in: FIG. 1(a) where an embodiment of the general formula (I) as M(RNCRRCRRNR)— is shown; FIG. 1(c) an embodiment of the general formula (I) as M(NRCRRCRRRNR)(NRCRCRRNR) is shown; FIG. 1(d) where an embodiment of the general formula (I) as M(NRCRRCRRNR)(NRCRRCRRNR)(NRCRRCRRNR) is shown; FIG. 1(e) where an embodiment the general formula (i) as M(NRCRRCRRNR)R is shown; FIG. 1(g) where an embodiment of the general formula (I) as M(NRCRRCRRNR)RR is shown; FIG. 1(i) where an embodiment of the general formula (I) as M(NRCRRCRRNR)RRR is shown; FIG. 1(k) where an embodiment of the general formula (I) as (NRCRRCRRNR)M(NRCRRCRRNR)—RR is shown; FIG. 1(l) where an embodiment of the general formula (I) as M(NRCRRCRRCRRNR) is shown; and FIG. 1(m) where an embodiment of the general formula (I) as (NRCRRCRRCRRNR)M(NRCRRCRRCRRNR) is shown.


Examples of the precursors covered by general formula (I) include, but are not limited to: Ge(CH3NCH2CH2NCH3); Ge(C2H5NCH2CH2NC2H5); Ge(NCH(CH3)2CH2CH2NCH(CH3)2); Ge(NC(CH3)3CH2CH2NC(CH3)3); Ge(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Te(CH3NCH2CH2NCH3); Te(C2H5NCH2CH2NC2H5); Te(NCH(CH3)2CH2CH2NCH(CH3)2); Te(NC(CH3)3CH2CH2NC(CH3)3); Te(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Ti(CH3NCH2CH2NCH3); Ti(C2H5NCH2CH2NC2H5); Ti(NCH(CH3)2CH2CH2NCH(CH3)2); Ti(NC(CH3)3CH2CH2NC(CH3)3); Ti(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Si(CH3NCH2CH2NCH3); Si(C2H5NCH2CH2NC2H5); Si(NCH(CH3)2CH2CH2NCH(CH3)2); Si(NC(CH3)3CH2CH2NC(CH3)3); Si(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Sn(CH3NCH2CH2NCH3); Sn(C2H5NCH2CH2NC2H5); Sn(NCH(CH3)2CH2CH2NCH(CH3)2); Sn(NC(CH3)3CH2CH2NC(CH3)3); Sn(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); (NC(CH3)3CH2CH2NC(CH3)3)Ti(NC(CH3)3CH2CH2NC(CH3)3); (NC(CH3)3CH2CH2NC(CH3)3)Si(NC(CH3)3CH2CH2NC(CH3)3); (NC(CH3)3CH2CH2NC(CH3)3)Te(NC(CH3)3CH2CH2NC(CH3)3); (NC(CH3)3CH2CH2NC(CH3)3)Ge(NC(CH3)3CH2CH2NC(CH3)3); (NC(CH3)3CH2CH2NC(CH3)3)Sn(NC(CH3)3CH2CH2NC(CH3)3); Fe(NC(CH3)3CH2CH2NC(CH3)3)3; Ru(NC(CH3)3CH2CH2NC(CH3)3)3; Sb(N(CH3)CH2CH2N(CH3))(NMe2); Sb(N(CH3)CH2CH2N(CH3))(CH3); Sb(N(CH3)CH2CH2N(CH3))(C2H5); Sb(NC(CH3)3CH2CH2NC(CH3)3)(NMe2); Sb(NC(CH3)3CH2CH2NC(CH3)3)(CH3); Sb(NC(CH3)3CH2CH2NC(CH3)3)(C2H5); Ti(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Si(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Ge(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Hf(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Zr(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Sn(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Ti(N(C(CH3)3)CH2CH2N(C(CH3)3)(CH3)2; Si(N(C(CH3)3)CH2CH2N(C(CH3)3)(CH3)2; Ge(N(C(CH3)3)CH2CH2N(C(CH3)3)(CH3)2; Hf(N(C(CH3)3)CH2CH2N(C(CH3)3)(CH3)2; Zr(N(C(CH3)3)CH2CH2N(C(CH3)3)(CH3)2; Ti(N(C(CH3)3)CH2CH2N(C(CH3)3)(C2H5)2; Si(N(C(CH3)3)CH2CH2N(C(CH3)3)(C2H5)2; Ge(N(C(CH3)3)CH2CH2N(C(CH3)3)(C2H5)2; Hf(N(C(CH3)3)CH2CH2N(C(CH3)3)(C2H5)2; Zr(N(C(CH3)3)CH2CH2N(C(CH3)3)(C2H5)2; Ru(N(C(CH3)3)CH2CH2N(C(CH3)3)(iPrNC(CH3)NiPr)2; Fe(N(C(CH3)3)CH2CH2N(C(CH3)3)(iPrNC(CH3)NiPr)2; Os(N(C(CH3)3)CH2CH2N(C(CH3)3)(iPrNC(CH3)NiPr)2; Ta(NC(CH3)3CH2CH2NC(CH3)3)(NMe2)3; Nb(NC(CH3)3CH2CH2NC(CH3)3)(NMe2)3; Nb(NC(CH3)3CH2CH2NC(CH3)3)(CH3)3; Nb(NC(CH3)3CH2CH2NC(CH3)3)(C2H5)3; Os(N(C(CH3)3CH2CH2N(C(CH3)3)2(C5H5); Fe(N(C(CH3)3CH2CH2N(C(CH3)3)2(C5H5); Ru(N(C(CH3)3CH2CH2N(C(CH3)3)2(C5H5); Ge(N(CH3)CH2CH2CH2N(CH3)); Ge(NC(CH3)3CH2CH2CH2N(CH3)3); Ti(N(CH3)CH2CH2CH2N(CH3)); Ti(NC(CH3)3CH2CH2CH2N(CH3)3); Si(N(CH3)CH2CH2CH2N(CH3)); Si(NC(CH3)3CH2CH2CH2N(CH3)3); Ge(N(CH3)CH2CH2CH2N(CH3))2; Ge(N(C2H5)CH2CH2CH2N(C2H5))2; Ti(N(CH3)CH2CH2CH2N(CH3))2; Ti(N(C2H5)CH2CH2CH2N(C2H5))2; Si(N(CH3)CH2CH2CH2N(CH3))2; and Si(N(C2H5)CH2CH2CH2N(C2H5))2.


In embodiments where the metal precursor has the general formula (II), the precursor may be shown structurally as in: FIG. 1(b) where an embodiment of the general formula (II) as M(RNCRCRNR) is shown; FIG. 1(f) where an embodiment of general formula (II) as M(NRCR═CRNR)R is shown; FIG. 1(h) where an embodiment of general formula (II) as M(NRCR═CRNR)RR is shown; and FIG. 1(j) where an embodiment of the general formula (II) as M(NRCR═CRNR)RRR is shown.


Examples of the precursors covered by general formula (II) include, but are not limited to: Ge(NCH3CHCHNCH3); Ge(C2H5NCHCHNC2H5); Ge(NCH(CH3)2CHCHNCH(CH3)2); Ge(NC(CH3)3CHCHNC(CH3)3); Ge(NC(CH3)3NC(CH3)C(CH3)NC(CH3)3); Te(CH3NCHCHNCH3); Te(C2H5NCHCHNC2H5); Te(NCH(CH3)2CHCHNCH(CH3)2); Te(NC(CH3)3CHCHNC(CH3)3); Te(NC(CH3)3C(CH3)C(CH3)NC(CH3)3); Ti(CH3NCHCHNCH3); Ti(C2H5NCHCHNC2H5); Ti(NCH(CH3)2CHCHNCH(CH3)2); Ti(NC(CH3)3NCHCHNC(CH3)3); Ti(NC(CH3)3NC(CH3)C(CH3)NC(CH3)3); Si(CH3NCHCHNCH3); Si(C2H5NCHCHNC2H5); Si(NCH(CH3)2CHCHNCH(CH3)2); Si(NC(CH3)3CHCHNC(CH3)3); Si(NC(CH3)3NC(CH3)C(CH3)NC(CH3)3); Sn(NCH3NCHCHNCH3); Sn(C2H5NCHCHNC2H5); Sn(NCH(CH3)2CHCHNCH(CH3)2); Sn(NC(CH3)3CHCHNC(CH3)3); Sn(NC(CH3)3C(CH3)C(CH3)NC(CH3)3); Sb(N(CH3)CHCHN(CH3))(N(CH3)2); Sb(N(CH3)CHCHN(CH3))(CH3); Sb(N(CH3)CHCHN(CH3))(C2H5); Sb(NC(CH3)3CHCHNC(CH3)3)(N(CH3)2); Sb(NC(CH3)3CHCHNC(CH3)3)(CH3); Sb(NC(CH3)3CHCHNC(CH3)3)(C2H5); Ru(NC(CH3)3CHCHNC(CH3)3)(C5H5); Ti(NC(CH3)3CHCHNC(CH3)3)(N(CH3)2)2; Si(NC(CH3)3CHCHNC(CH3)3)(N(CH3)2)2; Ge(NC(CH3)3CHCHNC(CH3)3)(N(CH3)2)2; Sn(NC(CH3)3CHCHN(C(CH3)3)(N(CH3)2)2; Ti(N(C(CH3)3)CHCHN(C(CH3)3)(CH3)2; Si(N(C(CH3)3)CHCHN(C(CH3)3)(CH3)2; Ge(N(C(CH3)3)CHCHN(C(CH3)3)(CH3)2; Ti(N(C(CH3)3)CHCHN(C(CH3)3)(C2H5)2; Si(N(C(CH3)3)CHCHN(C(CH3)3)(C2H5)2; Ge(N(C(CH3)3)CHCHN(C(CH3)3)(N(C2H5)2); Si(N(C(CH3)3)CHCHN(C(CH3)3)(C2H5)2; Ru(NC(CH3)3CHCHN(C(CH3)3)(iPrNC(CH3)NiPr)2; Fe(N(C(CH3)3)CHCHN(C(CH3)3)(iPrNC(CH3)NiPr)2; Os(N(C(CH3)3)CHCHN(C(CH3)3)(iPrNC(CH3)NiPr)2; Ta(NC(CH3)3CHCHNC(CH3)3)(NMe2)3; Ta(NC(CH3)3CHCHNC(CH3)3)(CH3)3; Ta(NC(CH3)3CHCHNC(CH3)3)(C2H5)3; Nb(NC(CH3)3CHCHNC(CH3)3)(NMe2)3; Nb(NC(CH3)3CHCHNC(CH3)3)(CH3)3; and Nb(NC(CH3)3CHCHNC(CH3)3)(C2H5)3.


In some embodiments, the precursor may be of general formula (III), where each Z is independently selected from the precursors of general formula (I) or (II), and where the oxidation state of the selected precursor is such as to allow a coordination between M and M′. This coordination can vary in form depending upon the individual precursors. In some embodiments the coordination may be a bimetallic bond, but in other embodiments the coordination can be a much weaker association, such as in the case of pyridine which could be considered crystalline solvent type coordination.


Examples of the precursors covered by general formula (III) include, but are not limited to: Ni(Si(NC(CH3)3C(—CHCHCH—)CNC(CH3)3))4; Ni(Si(NC(CH3)3CH2CH2NC(CH3)3))3; Ni(Ge(NC(CH3)3CH2CH2NC(CH3)3))(CO)3; Ni(Ge(NC(CH3)3CH2CH2NC(CH3)3))2(CO)2; Ni(Si(NC(CH3)3CH2CH2NC(CH3)3))2(CO)2; Ni(Ge(NC(CH3)3CH2CH2NC(CH3)3))3; Co(Si(NC(CH3)3CH2CH2NC(CH3)3))3; Co(Si(NC(CH3)3CH2CH2NC(CH3)3))2(CO)2; Si(Si(NC(CH3)3CH2CH2NC(CH3)3))4; Ti(Si(NC(CH3)3CH2CH2NC(CH3)3))4; Ge(Si(NC(CH3)3CH2CH2NC(CH3)3))4; Sb(Si(NC(CH3)3CH2CH2NC(CH3)3))3; Te(Si(NC(CH3)3CH2CH2NC(CH3)3))2; Te(Sb(NC(CH3)3CH2CH2NC(CH3)3))2; Te(Ge(NC(CH3)3CH2CH2NC(CH3)3))2; Hf(Si(NC(CH3)3CH2CH2NC(CH3)3))4; Zr(Si(NC(CH3)3CH2CH2NC(CH3)3))4; Ti(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(CH3)2)2; Ge(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(CH3)2)2; Te(Si(NC(CH3)3CH2CH2NC(CH3)3))(N(CH3)2); Te(Ge(NC(CH3)3CH2CH2NC(CH3)3))(N(CH3)2); Sb(Si(NC(CH3)3CH2CH2NC(CH3)3))(N(CH3)2)2; Cr(Si(NC(CH3)3CH2CH2NC(CH3)3))2(CO)4; Mo(Si(NC(CH3)3CH2CH2NC(CH3)3))2(CO)4; W(Si(NC(CH3)3CH2CH2NC(CH3)3))2(CO)4; Cr(Si(NC(CH3)3CH2CH2NC(CH3)3))(Cp)2; Mo(Si(NC(CH3)3CH2CH2NC(CH3)3))(Cp)2; W(Si(NC(CH3)3CH2CH2NC(CH3)3))(Cp)2; Ru(Si(NC(CH3)3CH2CH2NC(CH3)3))2(CO)3; Ru(C5H5)(CN)(CO)(Si(NC(CH3)3CH2CH2NC(CH3)3)); Ru(C6H6)(Si(NC(CH3)3CH2CH2NC(CH3)3))(((CH3)2CH)NC(CH3)N(CH(CH3)2)); Os(C5H5)(CN)(CO)(Si(NC(CH3)3CH2CH2NC(CH3)3)); Os(C6H6)(Si(NC(CH3)3CH2CH2NC(CH3)3))(((CH3)2CH)NC(CH3)N(CH(CH3)2); Fe(Si(NC(CH3)3CH2CH2NC(CH3)3))(CO)4; Fe(C5H5)(CN)(CO)(Si(NC(CH3)3CH2CH2NC(CH3)3)); Fe(C6H6)(Si(NC(CH3)3CH2CH2NC(CH3)3))(((CH3)2CH)NC(CH3)N(CH(CH3)2)); Ca(Si(NC(CH3)3CH2CH2NC(CH3)3))2(NMe2)2; Sr(Si(NC(CH3)3CH2CH2NC(CH3)3))2(NMe2)2; Ba(Si(NC(CH3)3CH2CH2NC(CH3)3))2(NMe2)2; Ca(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(SiMe3)2)2; Sr(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(SiMe3)2)2; Ba(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(SiMe3)2)2; Sn(Si(NC(CH3)3CH2CH2NC(CH3)3))(NMe2)2; Sn(Si(NC(CH3)3CH2CH2NC(CH3)3))2Cl2; Sm(C(NC(CH3)3CH2CH2NC(CH3)3))(C5H5)2; Sm(Si(NC(CH3)3CH2CH2NC(CH3)3))2(C5H5)2; Yb(C(NC(CH3)3CH2CH2NC(CH3)3))(C5H5)2; Yb(Si(NC(CH3)3CH2CH2NC(CH3)3))(C5H5)2; Eu(C(NC(CH3)3CH2CH2NC(CH3)3))(acac)3; Eu(Si(NC(CH3)3CH2CH2NC(CH3)3))(acac)3; Y(C(NC(CH3)3CH2CH2NC(CH3)3))(acac)3; Y(Si(NC(CH3)3CH2CH2NC(CH3)3))(acac)3; La(C(NC(CH3)3CH2CH2NC(CH3)3))(N(Si(CH3)3)3; La(Si(NC(CH3)3CH2CH2NC(CH3)3))(N(Si(CH3)3)3; Y(C(NC(CH3)3CH2CH2NC(CH3)3))(N(Si(CH3)3)3, Y(Si(NC(CH3)3CH2CH2NC(CH3)3))(N(Si(CH3)3)3; La(C(NC(CH3)3CH2CH2NC(CH3)3))2(N(Si(H2Me))2)3; La(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(Si(H2Me))2)3; Y(C(NC(CH3)3CH2CH2NC(CH3)3))2(N(Si(H2Me))2)3; Y(Si(NC(CH3)3CH2CH2NC(CH3)3))2(N(Si(H2Me))2)3; Rh(Si(NC(CH3)3CH2CH2NC(CH3)3))(C8H12)(((CH3)2CH)NC(CH3)N (CH(CH3)2)); Ta(Si(NC(CH3)3CH2CH2NC(CH3)3))(NMe2)4; Mg(Si(NC(CH3)3CH2CH2NC(CH3)3))(Et)2; Zn(Si(NC(CH3)3CH2CH2NC(CH3)3))(Et)2; (Si(NC(CH3)3CH2CH2NC(CH3)3))AlMe3; (Si(NC(CH3)3CH2CH2NC(CH3)3))GaMe3; and (Si(NC(CH3)3CH2CH2NC(CH3)3))AlH3.


Generally, the disclosed precursors may be deposited to form a thin film using any deposition methods known to those of skill in the art. In some embodiments the depositions are through a chemical vapor deposition (CVD) or atomic layer deposition (ALD) method. Examples of suitable deposition methods include without limitation, conventional CVD, low pressure chemical vapor deposition (LPCVD), plasma enhanced chemical vapor depositions (PECVD), atomic layer deposition (ALD), pulsed chemical vapor deposition (P-CVD), plasma enhanced atomic layer deposition (PE-ALD), or combinations thereof.


In an embodiment, the metal precursor is introduced into a reactor in vapor form. The precursor in vapor form may be produced by vaporizing a liquid precursor solution, through a conventional vaporization step such as direct vaporization, distillation, or by bubbling an inert gas (e.g. N2, He, Ar, etc.) into the precursor solution and providing the inert gas plus precursor mixture as a precursor vapor solution to the reactor. Bubbling with an inert gas may also remove any dissolved impurities (e.g. oxygen) present in the precursor solution.


The reactor may be any enclosure or chamber within a device in which deposition methods take place such as without limitation, a cold-wall type reactor, a hot-wall type reactor, a single-wafer reactor, a multi-wafer reactor, or other types of deposition systems under conditions suitable to cause the precursors to react and form the layers.


Generally, the reactor contains one or more substrates on to which the thin films will be deposited. The one or more substrates may be any suitable substrate used in semiconductor, photovoltaic, flat panel, or LCD-TFT device manufacturing. Examples of suitable substrates include without limitation, silicon substrates, silica substrates, silicon nitride substrates, silicon oxy nitride substrates, tungsten substrates, or combinations thereof. Additionally, substrates comprising tungsten or noble metals (e.g. platinum, palladium, rhodium, or gold) may be used. The substrate may also have one or more layers of differing materials already deposited upon it from a previous manufacturing step.


In some embodiments, in addition to the metal precursor, a reactant gas may also be introduced into the reactor. In some of these embodiments, the reactant gas may be an oxidizing gas such as one of oxygen, ozone, water, hydrogen peroxide, nitric oxide, nitrogen dioxide, radical species of these, as well as mixtures of any two or more of these. In some other of these embodiments, the reactant gas may be a reducing gas such as one of hydrogen, ammonia, a silane (e.g. SiH4; Si2H6, Si3H8), SiH2Me2; SiH2Et2; N(SiH3)3; radical species of these, as well as mixtures of any two or more of these.


In some embodiments, and depending on what type of film is desired to be deposited, a second precursor may be introduced into the reactor. The second precursor comprises another metal source, such as copper, praseodymium, manganese, ruthenium, titanium, tantalum, bismuth, zirconium, hafnium, lead, niobium, magnesium, aluminum, lanthanum, or mixtures of these. In embodiments where a second metal containing precursor is utilized, the resultant film deposited on the substrate may contain at least two different metal types.


The metal precursor and any optional reactants or precursors may be introduced sequentially (as in ALD) or simultaneously (as in CVD) into the reaction chamber. In some embodiments, the reaction chamber is purged with an inert gas between the introduction of the precursor and the introduction of the reactant. In one embodiment, the reactant and the precursor may be mixed together to form a reactant/precursor mixture, and then introduced to the reactor in mixture form. In some embodiments, the reactant may be treated by a plasma, in order to decompose the reactant into its radical form. In some of these embodiments, the plasma may generally be at a location removed from the reaction chamber, for instance, in a remotely located plasma system. In other embodiments, the plasma may be generated or present within the reactor itself. One of skill in the art would generally recognize methods and apparatus suitable for such plasma treatment.


In some embodiments, the temperature and the pressure within the reactor are held at conditions suitable for ALD or CVD depositions. For instance, the pressure in the reactor may be held between about 1 Pa and about 105 Pa, or preferably between about 25 Pa and 103 Pa, as required per the deposition parameters. Likewise, the temperature in the reactor may be held between about 100° C. and about 500° C., preferably between about 200° C. and about 350° C.


Depending on the particular process parameters, deposition may take place for a varying length of time. Generally, deposition may be allowed to continue as long as desired or necessary to produce a film with the necessary properties. Typical film thicknesses may vary from several hundred angstroms to several hundreds of microns, depending on the specific deposition process. The deposition process may also be performed as many times as necessary to obtain the desired film.


In some embodiments, the precursor vapor solution and the reaction gas, may be pulsed sequentially or simultaneously (e.g. pulsed CVD) into the reactor. Each pulse of precursor may last for a time period ranging from about 0.01 seconds to about 10 seconds, alternatively from about 0.3 seconds to about 3 seconds, alternatively from about 0.5 seconds to about 2 seconds. In another embodiment, the reaction gas may also be pulsed into the reactor. In such embodiments, the pulse of each gas may last for a time period ranging from about 0.01 seconds to about 10 seconds, alternatively from about 0.3 seconds to about 3 seconds, alternatively from about 0.5 seconds to about 2 seconds.


EXAMPLES

The following non-limiting examples are provided to further illustrate embodiments of the invention. However, the examples are not intended to be all inclusive and are not intended to limit the scope of the inventions described herein.


Prophetic Example 1

Titanium films may be deposited at temperatures above 200° C. Vapors of the precursor Ti(N(tBu)CH2CH2N(tBu))(NMe2)2 may be delivered to a reaction furnace using N2 as a carrier gas, as well as for dilution purposes. Hydrogen may be used as a reactant.


In this way, titanium films are expected to be obtained in ALD mode at temperatures above 200 C.


It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method will be below the detection limit of the apparatus.


Prophetic Example 2

Titanium nitride films are expected to be deposited, as described in Example 1, when ammonia is used instead of hydrogen.


Prophetic Example 3

Germanium films may be deposited at temperatures above 200° C. Vapors of the precursor Ge(N(tBu)CHCHN(tBu))(NMe2)2 may be delivered to a reaction furnace using N2 as a carrier gas, as well as for dilution purposes. Hydrogen may be used as a reactant.


In this way, germanium films are expected to be obtained in ALD mode at temperatures above 200 C.


It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method, will be below the detection limit of the apparatus.


Prophetic Example 4

Germanium nitride films are expected to be deposited, as described in Example 3, when ammonia is used instead of hydrogen.


Prophetic Example 5

Zirconium oxide films may be deposited at temperatures above 220° C. Vapors of the precursor Zr(N(tBu)CH2CH2N(tBu))(NMe2)2 may be delivered to a reaction furnace using N2 as a carrier gas, as well as for dilution purposes. Water may be used as a reactant.


In this way, zirconium oxide films are expected to be obtained in ALD mode at temperatures above 200 C.


It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method, will be below the detection limit of the apparatus.


Prophetic Example 6

Zirconium oxide films are expected to be deposited, as described in Example 5, when ozone is used instead of water.


Prophetic Example 7

Nickel films may be deposited at temperatures above 200° C. Vapors of the precursor Ni(SiNC(CH3)3CH2CH2NC(CH3)3)4 may be delivered to a reaction furnace using N2 as a carrier gas, as well as for dilution purposes. Hydrogen may be used as a reactant.


In this way, nickel films are expected to be obtained in ALD mode at temperatures above 200 C.


It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method, will be below the detection limit of the apparatus.


While embodiments of this invention have been shown and described, modifications thereof can be made by one skilled in the art without departing from the spirit or teaching of this invention. The embodiments described herein are exemplary only and not limiting. Many variations and modifications of the composition and method are possible and within the scope of the invention. Accordingly the scope of protection is not limited to the embodiments described herein, but is only limited by the claims which follow, the scope of which shall include all equivalents of the subject matter of the claims.

Claims
  • 1. A method of forming a metal containing film on a substrate, comprising: a) providing a reactor and at least one substrate disposed therein;b) introducing a metal precursor into the reactor, wherein the metal precursor is selected from the group consisting of:
  • 2. The method of claim 1, wherein the precursor comprises at least one member selected from the group consisting of: Te(NCH(CH3)2CH2CH2NCH(CH3)2); Te(NC(CH3)3CH2CH2NC(CH3)3); Te(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Ti(NCH(CH3)2CH2CH2NCH(CH3)2); Ti(NC(CH3)3CH2CH2NC(CH3)3); Ti(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Si(NCH(CH3)2CH2CH2NCH(CH3)2); Si(NC(CH3)3CH2CH2NC(CH3)3); Si(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Sn(NCH(CH3)2CH2CH2NCH(CH3)2); Sn(NC(CH3)3CH2CH2NC(CH3)3); Sn(NCH(CH3)2C(CH3)HC(CH3)HNCH(CH3)2); Ru(NC(CH3)3CH2CH2NC(CH3)3)3; Sb(NC(CH3)3CH2CH2NC(CH3)3)(NMe2); Sb(NC(CH3)3CH2CH2NC(CH3)3)(CH3); Sb(NC(CH3)3CH2CH2NC(CH3)3)(C2H5); Ti(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Si(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Hf(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Zr(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Sn(NC(CH3)3CH2CH2NC(CH3)3)(N(CH3)2)2; Ru(N(C(CH3)3)CH2CH2N(C(CH3)3)(iPrNC(CH3)NiPr)2; Ta(NC(CH3)3CH2CH2NC(CH3)3)(NMe2)3; and Nb(NC(CH3)3CH2CH2NC(CH3)3)(NMe2)3.
  • 3. The method of claim 1, wherein the precursor comprises at least one member selected from the group consisting of: Ti(N(tBu)CH2CH2N(tBu))(NMe2)2; Zr(N(tBu)CH2CH2N(tBu))(NMe2)2; and Ni(SiNC(CH3)3CH2CH2NC(CH3)3)4.
  • 4. The method of claim 1, further comprising maintaining the reactor at a temperature between about 100° C. to about 500° C.
  • 5. The method of claim 4, further comprising maintaining the reactor at a temperature between about 200° C. and about 350° C.
  • 6. The method of claim 1, further comprising maintaining the reactor at a pressure between about 1 Pa and about 105 Pa.
  • 7. The method of claim 6, further comprising maintaining the reactor at a pressure between about 25 Pa and about 103 Pa.
  • 8. The method of claim 1, further comprising introducing at least one reducing gas into the reactor, wherein the reducing gas comprises at least one member selected from the group consisting of: H2; NH3, SiH4; Si2H6; Si3H8; hydrogen radicals; and mixtures thereof.
  • 9. The method of claim 8, wherein the metal precursor and the reducing gas are introduced into the chamber either substantially simultaneously, or sequentially.
  • 10. The method of claim 9, wherein the reducing gas and the metal precursor are introduced into the chamber substantially simultaneously, and the chamber is configured for chemical vapor deposition.
  • 11. The method of claim 9, the reducing gas, and the metal precursor are introduced into the chamber sequentially, and the chamber is configured for atomic layer deposition.
  • 12. The method of claim 1, further comprising introducing at least one oxidizing gas into the reactor, wherein the oxidizing gas comprises at least one member selected from the group consisting of: O2; O3; H2O; H2O2; NO; N2O, oxygen radicals; and mixtures thereof.
  • 13. The method of claim 12, wherein the metal containing precursor and the oxidizing gas are introduced into the chamber either substantially simultaneously, or sequentially.
  • 14. The method of claim 12, wherein the metal containing precursor and the oxidizing gas are introduced into the chamber substantially simultaneously, and the chamber is configured for chemical vapor deposition.
  • 15. The method of claim 12, wherein the metal containing precursor and the oxidizing gas are introduced into the chamber sequentially, and the chamber is configured for atomic layer deposition.
  • 16. The method of claim 1, wherein the precursor is Zr(N(tBu)CH2CH2N(tBu))(NMe2)2.
CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims the benefit of U.S. Provisional Application Ser. No. 61/075,664, filed Jun. 25, 2008, herein incorporated by reference in its entirety for all purposes.

US Referenced Citations (19)
Number Name Date Kind
4377613 Gordon Mar 1983 A
4419386 Gordon Dec 1983 A
5656338 Gordon Aug 1997 A
6984591 Buchanan et al. Jan 2006 B1
7413776 Shenai-Khatkhate et al. Aug 2008 B2
7781340 Chen et al. Aug 2010 B2
20050079290 Chen et al. Apr 2005 A1
20060138393 Seo et al. Jun 2006 A1
20060172067 Ovshinsky et al. Aug 2006 A1
20060172068 Ovshinsky Aug 2006 A1
20060180811 Lee et al. Aug 2006 A1
20060292301 Herner Dec 2006 A1
20070042224 Reuter et al. Feb 2007 A1
20070054475 Lee et al. Mar 2007 A1
20080003359 Gordon et al. Jan 2008 A1
20080026577 Shenai-Khatkhate et al. Jan 2008 A1
20080096386 Park et al. Apr 2008 A1
20080118636 Shin et al. May 2008 A1
20090036697 Tada et al. Feb 2009 A1
Foreign Referenced Citations (22)
Number Date Country
42 34 998 Apr 1994 DE
0 568 074 Nov 1993 EP
1 180 553 Feb 2002 EP
1 464 724 Oct 2004 EP
1 464 725 Oct 2004 EP
1 806 427 Jul 2007 EP
1 995 236 Nov 2008 EP
WO 83 01018 Mar 1983 WO
WO 96 40448 Dec 1996 WO
WO 98 16667 Apr 1998 WO
WO 00 23635 Apr 2000 WO
WO 00 29637 May 2000 WO
WO 01 66816 Sep 2001 WO
WO 02 27063 Apr 2002 WO
WO 03 083167 Oct 2003 WO
WO 2007 062096 May 2007 WO
WO 2007 067604 Jun 2007 WO
WO 2007 133837 Nov 2007 WO
WO 2008 002546 Jan 2008 WO
WO 2008 008319 Jan 2008 WO
WO 2008 057616 May 2008 WO
WO 2009 039187 Mar 2009 WO
Non-Patent Literature Citations (24)
Entry
Bonasia, P.J. et al. “New reagents for the synthesis of compounds containing metal-tellurium bonds: sterically hindered silyltellurolate derivatives and the x-ray crystal structures of [(THF)2LiTeSi(SiMe3)3]2 and [(12-crown-4)2Li][TeSi(SiMe3)3]”, J. Am. Chem. Soc., 1992, 114 (13), pp. 5209-5214.
Breunig, H.J. “Thermochromic molecules with bonds of Se or Te and Sb or Bi”, Phosphorus and Sulfur, 1988, vol. 38, pp. 97-102.
Choi, et al. “Plasma-enhanced atomic layer deposition of Ge2Sb2Te5 films using metal-organic sources for Phase change RAM.” ALD 2006 proceedings, p. 62, 2006.
Drake, J.E. et al. “Studies of silyl and germyl group 6 species. 5. Silyl and germyl derivatives of methane- and benzenetellurols,” Inorg. Chem. 1980, 19, pp. 1879-1883.
Gonzalez-Hernandez, et al. “Structure of oxygen-doped Ge:Sb:Te films.” Thin Solid Films (2006), 503(1-2), 13-17.
Gu et al. “Optical and structural properties of oxygen-doped and annealed Ge—Sb—Te— thin films.” Chinese Journal of Lasers (2003), 30(12), 1110-1115.
Kim, et al. “Phase separation of a Ge2Sb2Te5 alloy in the transition from an amorphous structure to crystalline structures.” J. Vac. Sci. Technol. 929, 24(4), 2006.
King, R.B. “Secondary and tertiary phosphine adducts of germanium(II) iodide”, Inorganic Chemistry, vol. 2, No. 1, Feb. 1963.
Lee, J. et al. “GeSbTe deposition for the PRAM application”. Appl. Surf. Sci., 253, pp. 3969-3976, 2007.
Nefedov O.M. et al., “Molecular complexes of germylene with n-donor ligands”, Proceedings of the Academy of Sciences of the USSR Series Chemical, 1980, pp. 170-173, 1980.
Nefedov O.M. et al., “New adducted complexes of dichlorogermanium”, Proceedings of the Academy of Sciences of the USSR Series Chemical, 1973, No. 12, pp. 2824-2825.
Pore, V. et al. “Atomic layer deposition of metal tellurides and selenides using alkylsilyl compounds of tellurium and selenium,” J. Am. Chem, Soc., DOI 10.1021/ja8090388.
Razuvaev, G.A. et al. “Organosilicon and organogermanium derivatives with silicon-metal and germanium-metal bonds,” http://media.iupac.org/publications/pac/1969/pdf/1903x0353.pdf.
Shcherbinin, V.V. et al. “Methods for preparing germanium dihalides,” Russian J. of General Chem., vol. 68, No. 7, 1998, pp. 1013-1016.
Wang, et al. “Influence of Sn doping upon the phase change characteristics of Ge2Sb2Te5.” Phys. Stat. Sol. (A) 3087-3095, 201(14), 2004.
International Search Report and Written Opinion for PCT/US2008/076698 / U.S. Appl. No. 12/212,350.
International Search Report and Written Opinion for PCT/IB2008/055499 / U.S. Appl. No. 12/341,685.
Herrmann, W.A. et al. “Stable cyclic germanediyis (“cyclogermylenes”); Synthesis, structure, metal complexes, and thermolyses.” Angew. Chem. Int. Ed. Engl., (1992) 31, No. 11, pp. 1485-1488.
Prokop, J. et al. “Selective deposition of amorphous germanium on Si with respect to SiO2 by organometallic CVD.” J. NonCryst. Solids, 198-200 (1996) pp. 1026-1028.
Glatz, F. et al. “Thermal CVD of amorphous germanium films from 2,5-bis(tert.-butyl)-2,5-diaza-1-germa-cyclopentane organometallic precursor.” Mat. Res. Soc. Symp. Proc., 1994, vol. 336, pp. 541-545.
Kim, R-Y et al. “Structural properties of Ge2Sb2Te5 thin films by metal organic chemical vapor deposition for phase change memory applications.” App. Phys. Lett., 89 (2006) 102107.
Lee, J. et al. “GeSbTe deposition for the PRAM application.” Appl. Surf. Sci., 253 (2007) pp. 3969-3976.
Choi B. J. et al. “Cyclic PECVD of Ge2Sb2Te5 films using metallorganic sources.” J. Electrochem. Soc., 154 (4) H318-H324 (2007).
Lappert, M.F. et al. “Monomeric, coloured germanium(II) and tin(II) di-t-butylamides, and the crystal and molecular structure of Ge(NCMe2[CH2]3CMe2)2”. J. Chemical Soc. Chem. Comm. 1980, pp. 621-622.
Related Publications (1)
Number Date Country
20090321733 A1 Dec 2009 US
Provisional Applications (1)
Number Date Country
61075664 Jun 2008 US