Method and system for semiconductor crystal production with temperature management

Abstract

What is described here is a method and a temperature management and reaction chamber system for the production of nitrogenous semiconductor crystal materials of the form AXBYCZNVMW, wherein A, B, C represent elements of group II or III, N represents nitrogen, M represents an element of group V or VI, and X, Y, Z, V, W represent the mol fraction of each element in this compound, operating on the basis of gas phase compositions and gas phase successions. The invention excels itself by the provisions that for the production of the semiconductor crystal materials the production process is controlled by the precise temperature control of defined positions in the reaction chamber system under predetermined conditions.

Description

FIELD OF THE INVENTION

[0002] The present invention relates to a method and a system for the production of nitrogenous semiconductor crystal materials of the form AXBYCXNVMW, wherein A, B, C represent elements of group II or III, N represents nitrogen, M represents an element of group V or VI, and X, Y, Z, V, W represent the mol fraction of each element in this compound, operating on a temperature management system.

PRIOR ART

[0003] Binary, ternary and quaternary compound semiconductors such as GaAs, InP, AlxGa1−xAs, InxGa1−xAs, (AlxGa1−x)yIn1−yP and lnxGayAs1−xP1−y are presently used in several electronic and opto-electronic devices. The complex successions of strata may be produced from the gaseous phase that carries the elements to be incorporated into the lattice. The composition, doping and succession of strata are usually determined by the composition of the gaseous phase as well as by the switching sequence of the gaseous phase, operating on a constant temperature. This corresponds to the current state of the art in the production of high-quality materials for components. Nitrogenous semiconductors such as GaN, InGaN, AlGaN, GaAsN, i.e. semiconductors of the form AXBYCZNVMW (A, B, C representing elements of group II or III, N being nitrogen, M representing an element of group V or VI, and X, Y, Z, V, W corresponding to the mol fraction of each element in this compound) may be produced in different ways. In accordance with the present invention a temperature management system us used for the production of AxByCzNvMw materials (which will be referred to as nitrogenous semiconductor materials in the following.

[0004] In accordance with prior art, the characteristics of the nitrogenous semiconductor materials are determined by the composition of the gaseous phase and also by the switching sequence of the gaseous phases in the production process. Temperatures are maintained at a constant level. As only two parameters are employed for determining the characteristics of the nitrogenous semiconductor materials this kind of definition of the characteristics must rather be described as fairly non-differentiated. This means that even though it is possible to determine the composition, doping and succession of strata, an optimum matching is very difficult in consideration of other desirable properties described below, which leads to a complex production process involving a great number of process steps. Hence the production period is extended while the manufacturing costs are high.

BRIEF DESCRIPTION OF THE INVENTION

[0005] The present invention is based on the problem of providing a method and a system for the production of nitrogenous semiconductor crystal materials of the form AXBYCZNVMW, wherein A, B, C denote elements of group II or III, N represents nitrogen, M corresponds to an element of group V or VI, and X, Y, V, W represent the mol fraction of each element in this compound, which permit a better differentiated determination of characteristics. This means that in addition to a determination of the composition, doping and succession of strata an optimum matching should still become possible when further desirable characteristics are considered which will be described in the following. In this approach complex production processes including a great number of process steps should be avoided. As a consequence, the production period and the manufacturing costs will be reduced.

[0006] The problem underlying the present invention will be solved by a method according to the main claim. Improvements of the inventive method are the subject matters of the dependent claims.

[0007] The problem underlying the present invention is also solved by a temperature management and reaction chamber system according to a parallel claim. Improvements of the inventive temperature management and reaction chamber system are the subject matters of the dependent claims.

[0008] In accordance with the present invention the dynamic development of all temperatures is controlled. Temperature variations occur particularly within the range of seconds. As, at the same time, other characteristics may be changed in the reactor, e.g. substitution of hydrogen for nitrogen as carrier gas and hence varied thermal conductivity, the correlations between the temperatures—e.g. between the upper side of the reaction chamber T7 and the RF coil T8—are equally variable in time (cf. also FIG. 3) and can be controlled.

[0009] According to the present invention, the inventive temperature management system considers the temperatures, the temperature dynamics, temperature ranges and the correlation of all temperatures as well as the varying process parameters in the reactor.

[0010] In accordance with the present invention, the temperature management system is based particularly on temperature profiles which have been determined, for instance, on the basis of numeric simulations.

[0011] In the aforementioned semiconductor crystal material compounds specifically dynamic temperatures and dynamic thermal processes are applied in order to achieve the desired stratum characteristics.

[0012] According to the present invention, at least two parameters of an absolute temperature and/or temperature variation from a temperature of an inlet T1, of chamber walls T2, of principal wafer supports T3, of rotating individual wafer supports T4, of a gas outlet T5, of a gas mixture system T6, of the upper side of a reaction chamber T7 and of a heating system T8 are controlled in correspondence with (correlating) temperature variation profiles at least in the range of seconds for dynamically controlling thermal process taking place in consideration of the variation of further process parameters in the reactor (in combination with the process gases such as the substitution of the carrier gas) for the selective creation of materials characteristics which produce expedient effects on components, particularly on electronic and opto-electronic components.

[0013] In correspondence with the invention, preferably HF (high-frequency) heating means are controlled by the temperature management system and used to achieve the temperatures and the temperature dynamics.

[0014] With the advantageous features of the solution according to the main claim it is possible to produce defined strata, interfaces and successions of strata or hetero structures and structures from these semiconductor crystal materials having adjustable electrical and optical characteristics such as X, Y, Z, V, W compositions of the compound from zero to 100%, specific electrical electron concentrations up to 1020 cm−3 and specific electrical hole concentrations up to 8×1018 cm−3.

[0015] The inventive temperature management system is particularly subject to the specific demands on the production of nitrogenous semiconductor crystal materials.

[0016] AXBYCZNVMW materials and stratified systems as well as doped stratified systems can be expediently produced.

[0017] A high homogeneity in a lateral direction can be expediently achieved as well.

[0018] Moreover, a high degree of reproducibility can be expediently achieved.

[0019] Devices or components can be expediently produced. In production the behaviour of the components or their characteristics, respectively, such as colour and luminous intensity or a light-emitting diode can be determined. It is possible, for example, to produce defined field emitters.

[0020] Piezoelectric fields and interface states can be equally determined.

[0021] Quantum wells can be expediently manufactured.

[0022] An expedient advantage is the possibility to implement n-type and p-type doping at the same time.

[0023] A reproducible manufacture of AXBYCZNVMW materials with different X, Y, Z, V, W compositions and of different purity levels can be expediently made possible.

[0024] The production of interfaces between A1XB1YC1ZNj1VM1W/A2XB2YC2ZN2VM2W strata can be expediently made possible with unrestrictedly reproducible adjustable transition profiles.

[0025] The expedient possibility is available to adjust the electrical characteristics of interfaces by adjusting the temperature profile in the reaction chamber and the temperature increasing schema during the manufacturing process, together with an appropriate switching sequence of the gases. The electrical characteristics such as the charge density and the impurity density as well as the structure and the state density at the interfaces are used for achieving an adjustment of the recombination energy in A1XB1YC1ZN1VM1W/A2XB2YC2ZN2VM2W hetero structures by internal and external electrical fields due to the band bending. Hetero structures with stratum thicknesses of a few micrometers up to a fraction of a mono stratum with defined optical and electrical characteristics can be produced by means of this temperature management system.

[0026] Another expediently predeterminable characteristic is the surface morphology of the semiconductor materials.

[0027] Other expediently predeterminable characteristics are the particle density and the impurity density on the wafer surface.

[0028] Another advantage resides in the possibility to permit a reproducible and highly homogeneous or uniform application of AXBYCZNVMW components with respect to doping, stratum thickness, composition and any other properties relevant for applications.

[0029] The control of the temperature at the inlet T1 in accordance with one embodiment, the manner of condensation of the gases for wafer coating is expediently adjusted.

[0030] When the temperature at the reactor walls T2 is controlled in correspondence with another embodiment, a temperature difference between this temperature and the temperature of the principal wafer support T3 is avoided so that energy cannot flow and a flow cannot occur between these elements of the reaction chamber. As a consequence, a homogeneous thorough condensation of the gases is possible. The wafer temperature of the wafer on the satellites, which is not accessible for measurement, constitutes here the control temperature and target temperature. In this case, too, all temperatures undergo a dynamic variation because the reaction chamber walls and the principal wafer support are made of different materials (carbon and metal) and are substantially influenced by the thermal radiation. Control is very difficult.

[0031] When the temperature of the principal wafer support T3 is controlled in correspondence of another embodiment the temperature profile in the reaction chamber and the temperature increase scheme is determined during the production process in a reproducible manner. Hence, the adjustment of the electrical characteristics of interfaces is expediently permitted by adjustment of the temperature profile in the reaction chamber and the temperature increase scheme during the production process, together with an appropriate switching sequence of the gases.

[0032] The control of the temperature of rotating individual wafer supports T4 in correspondence with another embodiment results in coupling of all manufacturing conditions of the individual wafer supports to those of the principal wafer support. Hence all the wafers are expediently produced in a uniform quality.

[0033] When the temperature of the gas outlet T5 is controlled in accordance with a further embodiment a temperature gradient and hence the energy flow and the gas flow between the wafer supports and the gas outlet is expediently determined in a reproducible manner. In control of T5 (gas outlet)<T4 (wafer support)<T3 (principal wafer support) the temperature dynamics must also be considered because only the wafer support is actively heated and the cooling characteristics must be appropriately considered.

[0034] When the temperature of the gas mixing system T6 is controlled in correspondence with another embodiment this temperature and a temperature gradient—and hence the energy flow and the gas flow between the inlet and the gas mixing system—are expediently determined in a reproducible manner.

[0035] Despite the temperature dynamics of T8 or T1, respectively, of 20 to 1400° C., for example, T6 must be kept at a constant level.

[0036] Control of the temperature of the upper side of the reaction chamber T7 in correspondence with a further embodiment permits a uniform and reproducible determination of this temperature as well as of a temperature gradient and hence the energy flow and the gas flow between the upper side of the reaction chamber and the principal wafer support.

[0037] With control of the temperature of the heating system T8 according to another embodiment this temperature and consequently the temperature of the principal wafer support T3 are uniformly and reproducibly determined.

[0038] In the controllers of T7, T8 and T3 the dynamics and the heating/cooling means must equally be considered.

[0039] The additional control of the parameters in accordance with one of the further dependent claims, the characteristics of the X, Y, Z, V, W compositions as well as the specific electrical electron concentration and the specific electric hole concentration can be set in an adjustable manner. The gas flow must, however, be controlled in correlation with the dynamic temperature variations or else the characteristics of the component will vary. A variation of the gas flow produces equally a response to the temperature distribution, e.g. on the thermal conductivity and the cooling behaviour.

[0040] With the process steps defined in the dependent claims it is furthermore expediently possible to manufacture manifold products containing AXBYCZNVMW material components, which are defined, for instance, by strata, interfaces, strata successions and hetero structures with appropriate characteristics such as surface morphology, doping, composition, purity, impurity density.

[0041] On account of the temperature-controlled injection, which is provided in another embodiment, furthermore the expedient possibility is created for adjustment of the homogeneity, the surface properties and the characteristics of the strata.

[0042] The claims defining the temperature management and reaction chamber system are the device claims corresponding to the method claims, from which corresponding advantages derive.

BRIEF DESCRIPTION OF THE DRAWING

[0043] The invention will be described below, without any restriction of the general inventive idea, by exemplary embodiments, with reference being made to the drawing to which, in all other respects, explicit reference is made with respect to the disclosure of all inventive details which are not explained more thoroughly in the text. In the drawing:

[0044] FIG. 1 is a schematic illustration of the measuring points and the recirculation loops in the reaction chamber,

[0045] FIG. 2 illustrates the temperature dependence of the In incorporation of InGaN relative to the temperature T3,

[0046] FIG. 3 represents the temperature profiles of the temperatures T3 and T7 for the production of GaN/InGaN hetero structures,

[0047] FIG. 3 a is a view of a model of the mass transfer in the reactor,

[0048] FIG. 3 b represents a conceivable temperature distribution in the reactor,

[0049] FIG. 3 c shows a thermal model of an inventive temperature and reaction chamber system,

[0050] FIG. 4 illustrates the optical properties of InGaN/GaN quantum wells manufactured with the inventive temperature management system,

[0051] FIG. 5 illustrates the uniformity or homogeneity of the composition achieved with the inventive system,

[0052] FIG. 6 illustrates the uniformity or homogeneity in doping achieved with the inventive system,

[0053] FIG. 7 represents the N-incorporation as a function of the temperature T7 of the upper side of the reaction chamber, which is indicated by the emission wavelength, and

[0054] FIG. 8 shows the measurement of the temperatures T1, T2, T7, T8 and T9 in the course of the process of hetero structure production.

DESCRIPTION OF AN EMBODIMENT

[0055] First of all, the structure of the reaction chamber system and the temperature measuring points hence important for the temperature management system will be described for the following temperatures. FIG. 1 illustrates this set-up. The reference numeral 1 identifies an inlet of the reaction chamber system presenting the temperature T1. The reference numeral 2 indicates reaction chamber walls having the temperature T2. The reference numeral 3 identifies a principal wafer support at the temperature T3. The reference numeral 4 corresponds to rotating individual wafer supports displaying the temperature T4. The reference numeral 5 identifies a gas outlet at the temperature T5. The reference numeral 6 indicates a gas mixing system at the temperature level T6. The reference numeral 7 corresponds to the upper side of a reaction vessel at the temperature T7. The reference numeral 8 corresponds to a heating system presenting the temperature T8.

[0056] The reaction chamber consists of a horizontal carrier for the wafers. The reaction gases are injected from above, with a horizontal gas flow being created. The method requires a separation between the determined gases in combination with temperature control. In accordance with this embodiment the temperatures T1 to T8 are precisely adjusted and controlled. For optimisation of the production process further temperatures may be additionally employed as parameters.

[0057] It is possible to optimise the characteristics mentioned by way of introduction on the basis of the parameters.

[0058] The thermal management controller and the re-circulation systems or controllers, respectively, are based on thermal conduction and thermal flow. The temperature adjustment is achieved by active heating, thermal radiation and cooling, using liquids and gases. The system is determined by several regularly monitored measuring points, with the measured values being recorded. The temperatures are adjusted in order to carry out the required temperature settings.

[0059] FIG. 2 shows the dependence of the In incorporation of InGaN as an example of an AXBYCZNVMW material as a function of the temperature of the principal wafer support T3.

[0060] Within the temperature range of T3 from 725° C. to 925° C. a reduction of the In fraction in the InGaN material from roughly 25% to 5% can be noted.

[0061] FIG. 3 illustrates temperature profiles of the temperatures T3 and T7 for the production of GaN/InGaN hetero structures in correspondence with this embodiment.

[0062] The inventive process for the production to semiconductors of the form AXBYCZNVMW requires the application of different temperature ranges. The temperature ranges (cf., for instance, the temperature variation profile according to FIG. 3) are in particular:

[0063] 400-600° C. for the nucleation stratum between the substrate and active strata

[0064] 200-800 ° C. for the optically active layers

[0065] 1000-1400° C. for electrically active envelope strata surrounding the optically active stratum.

[0066] The temperature dynamics—and not only the absolute stability—is a decisive determinant for the behaviour of the component, such as the colour of a light-emitting diode. This applies to all the characteristics mentioned above in the Chapter “Brief description of the invention”:

[0067] The criterion that temperatures below the condensation temperature must be set is not applicable here. In fact, deposits on parts of the reactor are tolerated in order to achieve temperate and gas phase compositions which result in the desired characteristics of the component. The temperatures are so set in the optically active layer (700-800° C.), for example, that a non-homogeneous distribution of the materials is enforced in the semiconductor. The control function should be realised, however, in such a way that an addition compound will not be formed.

[0068] This inventive temperature management of all temperatures undergoing a dynamic variation results in entirely novel manufacturing processes. For example, the luminosity and the colour of light-emitting diodes and lasers are determined by the characteristics of the potential wells so influenced, by the interface and by the optically active medium. The possibilities to take an influence on further properties of the manufactured products are not limited.

[0069] The temperature control system and the detection of the precision as well as the temperature variation profiles—e.g. those corresponding to FIG. 3—cannot be determined by routine because the positions are often not accessible, e.g. the gas space above the wafer. The wide temperature range from 400 to 1600° C. enforces the application of different measuring systems with a resolution in terms of time at temperature ramps, which is often not sufficient. Moreover, individual reactor parts change their thermal characteristics throughout the process, e.g. the emission behaviour, so that constantly new temperatures must be determined during each process. Extensive numerical simulations of the temperature distributions have been carried out for the implementation of the invention.

[0070] FIGS. 3 a to 3c are illustrations relating to simulations serving to optimise the reactor in particular. These are the bases for optimised temperature profiles.

[0071] FIG. 3 a shows a model of the mass transfer in the reactor. The observed zone and the points are described where calculations are made (lattice). This applies to both the mass transfer and the temperature behaviour.

[0072] FIG. 3 b illustrates the temperature distribution throughout the reactor. Both the temperature distribution and the assumption are described in the model. Moreover, positions are detected which are inaccessible for measuring purposes.

[0073] FIG. 3 c illustrates a thermal model reflecting additional details and relating to almost all parts of the inventive reactor or temperature and reaction chamber system.

[0074] FIG. 4 illustrates the optical characteristics of InGaN/GaN quantum wells manufactured with the inventive temperature management system.

[0075] There values for GaInN at 3.17 eV for a single potential well (SQW) and at 3.20 eV for multiple potential wells (MQW) are noted, for instance.

[0076] FIG. 5 represents the homogeneity or uniformity of the composition that can be achieved with the inventive system.

[0077] FIG. 6 is an illustration of the homogeneity or uniformity in doping that is achieved with the inventive system.

[0078] FIG. 7 shows the N incorporation as a function of the temperature T7 on the upper side of the reaction chamber, which is indicated by the emission wavelength. There the N incorporation is reduced as the temperature of the upper side of the reaction chamber T7 increases.

[0079] FIG. 8 illustrates a measured development of the temperatures T1, T2, T7, T8 and T9 in the course of a manufacturing processing operation of a hetero structure, expressed in percent.

[0080] In correspondence with this embodiment the temperature profiles are achieved which are specified in the process sequence for the production.

Claims

1. Method of producing nitrogenous semiconductor crystal materials and particularly of strata on wafers of the form AXBYCZNVMW, wherein A, B, C represent elements of group II or III, N represents nitrogen, M represents an element of group V, with the exception of N, or group VI, and X, Y, Z, V, W represent the mol fraction of each element in this compound, operating on a device comprising a reaction chamber wherein at least one wafer support is disposed, at least one gas inlet through which the process gases flow into said reaction chamber in a controlled succession, possibly a gas mixing system, a gas outlet through which the process gases are discharged again after they have flown through said reaction chamber, and a controller that controls or controls in a closed loop, respectively, the type or the composition of the in-flowing process gases and the temperature of the wafer, as well as possibly further parts of said reaction chamber, characterised in that for the selective adjustment of the characteristics of the materials so produced, in addition to the control of the absolute temperature of the wafer and/or at least one part of said reaction chamber, also the temperature variation of at least this part or another part of said reaction chamber, e.g. the gas inlet T1, the chamber walls T2, the principal wafer support T3, rotating individual wafer supports T4, the gas outlet T5, said gas mixing system T6, the upper side of said reaction chamber T7 and/or said heating system T8 are adjusted with temperature variation profiles within the range of seconds in such a way that the variation of the process parameters so caused results in a dynamic control of the thermal processes leading to the production of the materials.

2. Method according to claim 1, characterised by controlling the temperature T1 below the condensation temperature of the gases and by adjustment of the temperature for avoiding the formation of addition compounds.

3. Method according to claim 1 or 2, characterised by control of the temperature T2 as equal to the temperature T3.

4. Method according to any of the claims 1 to 3, characterised by controlling the temperature T3 as a constant and up to 1600° C., with required reproducible temperature variations of up to 250° C. per minute.

5. Method according to any of the claims 1 to 4, characterised by controlling the temperature T4 as a correlate to the temperature T3 with an accuracy of 0.1° C.

6. Method according to any of the claims 1 to 5, characterised by controlling the temperature T5 to a value smaller than the value of the temperatures T4 and T3.

7. Method according to any of the claims 1 to 6, characterised by controlling the temperature T6 as a constant smaller than T1.

8. Method according to any of the claims 1 to 7, characterised by controlling the temperature T7 as a constant and correlate to T3.

9. Method according to any of the claims 1 to 8, characterised by controlling the temperature T8 as a constant and correlate to T3.

10. Method according to any of the claims 1 to 9, characterised by additionally controlling a temperature-dependent gas flow variation.

11. Method according to any of the claims 1 to 10, characterised by additionally controlling a temperature-dependent total pressure variation in the reaction chamber.

12. Method according to any of the claims 1 to 11, characterised by additionally controlling a temperature-dependent principal carrier gas variation in the reaction chamber.

13. Method according to any of the claims 1 to 12, characterised by additionally controlling temperature-dependent interrupts in the production process.

14. Method according to any of the claims 1 to 13, characterised by applying the semiconductor materials to be produced on a mechanical carrier of a semiconductor of group IV, a semiconductor of groups III-V, oxides or any other material resistant to temperatures and the process gases.

15. Method according to any of the claims 1 to 14, characterised by pre-treating said mechanical carrier by applying lines, dots, or by carrying out other steps for surface treatment, or by partially covering the surface with other materials or material components.

16. Method according to any of the claims 1 to 15, characterised by two-stage application of pre-processed AXBYCZNVMW materials.

17. Method according to any of the claims 1 to 16, characterised by the employment of a temperature-controlled injector.

18. Device for producing nitrogenous semiconductor crystal materials and particularly of strata on wafers of the form AxByCzNvMw, wherein A, B, C represent elements of group II or III, N represents nitrogen, M represents an element of group V, with the exception of N, or group VI, and X, Y, Z, V, W represent the mol fraction of each element in this compound, comprising a reaction chamber wherein at least one wafer support is disposed, at least one gas inlet through which the process gases flow into said reaction chamber in a controlled succession, possibly a gas mixing system, a gas outlet through which the process gases are discharged again after they have flown through said reaction chamber, and a controller that controls or controls in a closed loop, respectively, the type or the composition of the in-flowing process gases and the temperature of the wafer, as well as possibly further parts of said reaction chamber, characterised in that for the selective adjustment of the characteristics of the materials so produced, said controller adjusts, in addition to the control of the absolute temperature of the wafer and/or at least one part of said reaction chamber, also the temperature variation of at least this part or another part of said reaction chamber, e.g. the gas inlet T1, the chamber walls T2, the principal wafer support T3, rotating individual wafer supports T4, the gas outlet T5, said gas mixing system T6, the upper side of said reaction chamber T7 and/or said heating system T8 with temperature variation profiles within the range of seconds in such a way that the variation of the process parameters so caused results in a dynamic control of the thermal processes leading to the production of the materials.