(1) Field of the Invention
This invention relates to a method for the manufacture of miniature micro probes or electrical contacts for use in testing semiconductor chips. More particularly, this invention relates to a method of photo-defining a plurality of probes on metallic flat stock coated with a chemical resist emulsion and then removing unwanted metal to produce a plurality of micro probes.
(2) Description of the Related Art
It is known in the art of testing probe cards for electrical continuity to perform such tests using probes made by mechanically forming a straight piece of fine wire into a desired shape so as to provide the necessary size and spring force.
The lower and upper ends of the swaged area also prevent the probe from extending too far through the dies. In a conventional probe manufacturing process, the probes are formed from a straight piece of wire, typically of beryllium-copper alloy. Custom tooling is used for each probe size and design. The tooling stamps and forms the center portion of the wire to achieve the desired shape and thickness, thereby generating a desired spring rate.
With reference to
With reference to
Conventional stamping processes used to form probes often result in residual stresses in the probes which may cause reduced fatigue life. Because these residual stresses can change over time, changes in probe stiffness may arise. In addition, changes in the requirements for probes require retooling. Such retooling contributes to a high cost for probes manufactured in such a fashion and require a substantial lead time before such probes are available. It is also the case that mechanically fashioned probes are more difficult to redesign as their construction is closely tied to the mechanical means by which they are created.
There therefore exists a need for a method of manufacturing such probes that avoids the problems which arise from mechanical formation. There is further a need for such a method substantially amenable to producing probes of different designs absent a protracted retooling process.
One aspect of the instant invention is drawn to a method of fabricating a plurality of micro probes comprising the steps of defining the shapes of a plurality of probes as one or more masks, applying a photoresist to first and second opposing sides of a metal foil, overlaying one each of the masks on opposing first and second sides of the metal foil, exposing the photoresist to light passed through each of the masks, developing the photoresist, removing a portion of the photoresist to expose a portion of the metal foil, and applying an etcher to the surface of the metal foil to remove the exposed portion to produce a plurality of probes.
Another aspect of the invention is drawn to a micro probe manufactured according to the aforementioned method wherein the micro probe comprises a probe base having a generally uniform thickness bounded by a plurality of edges and extending for a substantially straight length in a plane, a probe shaft connected to the probe base the probe shaft of the generally uniform thickness, bounded by a plurality of edges, and extending along a curved expanse within the plane, a probe end connected to the probe shaft the probe end of the generally uniform thickness, bounded by a plurality of edges, and extending for a substantially straight distance within the plane the straight distance being approximately parallel to the straight length, and a scallop running substantially around a periphery comprised of the edges of the probe base, the probe shaft, and the probe end.
Yet another aspect of the invention is drawn to a probe test head comprising a first die comprised of first and second opposing planar surfaces the first die further comprising a pattern of first die holes extending through the first die in a direction perpendicular to both of the first and second planar surfaces, a second die comprised of third and forth opposing planar surfaces the second die further comprising a pattern of second die holes corresponding to the pattern of first die holes the second die holes extending through the second die in the direction wherein the third planar surface is arranged in planar contact with the second planar surface such that the second die holes are offset from the first die holes in a substantially uniform direction, and a plurality of probes one each of the probes extending through one of the first die holes and one of the second die holes the probes having a surface finish commensurate with having been formed by etching.
The present invention is drawn to a method of manufacturing probes in a way that provides improved uniformity while lowering the manufacturing cost of the probes. The probes are manufactured through a photo-etching process rather than a mechanical stamping process prevalent in the art. In this process of the present invention, the probes are etched from thin metal flat stock, typically of Beryllium-Copper alloy. With reference to
With reference to
A photoresist 1001 is then applied to both opposing planar surfaces of flat stock 1201. Two identical masks 73 are then fastened to opposing sides of flat stock 1201 with one side of each mask 73 in contact with the photoresist 1001 covering a single side of flat stock 1201. The two masks 73 are aligned such that any one feature in either mask 73 corresponding to an identical feature in the other mask 73 is in exact alignment across an axis perpendicular to the expanse of the planar surfaces of flat stock 1201. Light is then applied to each mask 73 effective to expose the photoresist 1001 disposed between each mask 73 and flat stock 1201. Both masks 73 are then separated from probe configuration 1205. After exposure of the photoresist 1001 to light, the photoresist 1001 is developed and rinsed. As a result of rinsing, exposed photoresist 1001 corresponding to a probe shape 72 on mask 73 remains bonded to flat stock 1201, while unexposed portions of photoresist 1001 corresponding to a dark space 71 is rinsed off of and out of contact with flat stock 1201.
An etcher is then applied at substantially the same time to both surfaces of flat stock 1201. The etcher begins to dissolve flat stock 1201 in a direction extending from the outer surfaces of flat stock 1201 along an axis perpendicular to the planar expanse of flat stock 1201 and directed into flat stock 1201 from each opposing planar surface. One attribute of applying etcher to a photoresist affixed to a metal substrate in order to dissolve the metal substrate is the presence of under cutting. As used herein, “undercutting” refers to the tendency of an etcher applied to dissolve metal to deviate from an etched path extending perpendicular to the surface to which the etcher was applied. Specifically, the etcher tends to extend outward as it travels into the metal.
With reference to
The resultant superposition of two opposing etch limits 1007 results in the presence of sharp protrusions or scallops 1003 extending around the perimeter of each etched probe. Note that the distance from scallop base 1013 to scallop tip 1015 forms the scallop dimension 1011. With reference to
Removing the unexposed metal results in an array of probes attached at their top end. The array of probes is then chemically polished and plated. The probes are then removed from the flat stock 1201 and readied for assembly into a probe head. The tops of the probes forming the assembly are lapped while the tips are held referenced to a flat surface to bring the probes to the same length.
With reference to
As used herein, “yield strength” refers to the property of a probe to deflect, or yield, in a predominantly linear direction when a force is applied while retaining the ability to return to its original, non-deflected state absent the application of a force. The greater the yield strength of a probe, the greater the linear deflection that may be exerted upon the probe prior to the probe reaching its yield point, whereupon the probe will not return to its original shape. Applicants anticipate that the etched probes of the present invention exhibits increased yield strength compared to probes formed from mechanical processing. Specifically, Applicants anticipate that the etched probes may be deflected a linear distance approximately 20% greater than that distance through which a conventional probe may be deflected before reaching the yield point.
In addition, it is anticipated that the etched probes of the present invention will possess improved spring force uniformity over probes formed in the conventional manner. As used herein, “spring force” refers to the opposing resistive force generated in a probe which is deflected through a distance. Specifically, it is anticipated that the maximum difference in the spring forces amongst all of the etched probes in a probe test head will be approximately 20% less than the maximum difference in the spring forces amongst all of the conventional probes in a similar probe test head apparatus.
With reference to
In addition, because a plurality of etched probes 81 is fashioned from a single flat stock 1201, each etched probe 81 is substantially similar in its physical characteristics to each and every other etched probe 81 fashioned from the same flat stock 1201.
The following example details parameters preferable to practicing the present invention. Preferably, there is practiced a plurality of steps including material preparation, photo masking, etching, chemical polishing, plating, and a process of individualizing the probes thus formed. As used herein, “DI” is a descriptor meaning de-ionized. In addition, as used herein, “UX DI” refers to ultrasonically agitated de-ionized water.
To prepare the material out of which the probes were to be formed, BeCu 17200 Flat stock was cut into squares with side lengths approximating four inches. The flat stock was then cleaned with Citra-solv (by Citra-Solv, LLC of Danbury, Conn.)/DI H2O 20 ML/1 L (UX 15 Min.). The surface of the flat stock was then air blown dry and the resulting package was then heat hardened in a vacuum for approximately two hours at 600° F.
Next, the prepared material was photo masked. To accompish the photo masking, the material was again cleaned with Clean Citra-Solv/DI H2O 20ML/1 L (UX 15 Min.). Next the material was provided a dip coat with a withdraw rate of 13.3 Sec./1 in. (Shipley SP2029-1) Thinned to 35 Zon/Sec. at 21° C. The material was then dried for approximately 30 minutes at 90° C. and allowed to cool at room temperature under conditions of greater than fifty percent relative humidity. Next, the prepared surface of the material was exposed to approximately 100 milijules 365 nanometer wavelength UV light. The surface exposed to the light was then developed for approximately 1 min 30 sec (Shipley 303 developer, by Shipley Inc. of Newton Mass., at 85° F.). Lastly, the prepared surface was rinsed in cascading DI water for 15 minutes then air blown dry and stored.
Next, etching was performed using a Marseco Mod.# CES-24, by Marseco Inc. of Huntington Beach, Calif. Hi-speed circuit etching was then performed using Phibro-Tech High Speed Circuit etching solution with the following parameter settings:
Next a chemical polish/bright dip was applied to the probes formed from etching. The probes were submerged in PNA Etch in a 2 L beaker at 145-150° F. while stirring. The solution was comprised as follows:
First, the etch rate was established using a test piece of material. Next, the probe material was etched to remove 0.0001″ Next the material was rinsed in hot DI, in UX DI for approximately 15 minutes and a DI cascade for approximately 2 minutes. Lastly, the probes are oven dried at 100° C. until dry.
Next, the probes were plated using a Pallamerse Immersion Palladium 5% solution, by Technic Inc. of Cranston R.I., and a Pd activator 25% solution manufactured by Technic Inc. and a Vertrel solvent by Dupont Fluoroproducts of Wilmington, Del. The probes were then weighed and their weights recorded. The probes were then washed in the Vertrel solvent for approximately two minutes. Next, the probes were rinsed in DI H2O for one minute and in a 10% sulfuric acid solution for two minutes followed by another two minute rinse in DI H2O. The probes were then immersed for 30 seconds in the Technic Pd activator and once again rinsed in DI H2O for 30 seconds. The probes were then immersed for 45 minutes in Technic immersion Palladium while stirring slowly, rinsed with running DI H2O and dried. The probes were then re-weighed and their weights recorded.
Lastly, the probes were individualized. A sample of the probes, preferably five or six probes, is tested to measure the grams of resistive force generated within each of the probes when deflected from one to eight millimeters in one millimeter increments. The results on one such test group of probes is illustrated in Table 1. The results of the test were used to assess the uniformity of the probes created from any one initial flat stock as well as conformity to desired properties. The probes were then put in a vile and labeled with tip and shank dimension.
There is therefore provided herein a process for mass producing miniature micro probes or electrical contacts for use in the testing of semiconductor chips having the following advantages over the conventional probe manufacturing process. First the method of the present invention provides improved uniformity and dimensional accuracy between the probes. The glass mask determines the geometry of the probes, eliminating mechanical variances between the probes. As a result, the stiffness of the probes are more uniform, allowing for a balanced contact force across the array.
In addition, there are no stresses induced in the probes during fabrication, resulting in improved probe strength and endurance. The conventional stamping process results in residual stresses, causing reduced fatigue life. The stresses can change over time, causing changes in probe stiffness.
The present invention provides for lower cost and lead-time in manufacturing. Many probes are manufactured simultaneously, and the tip geometry can be made via the etching process rather than as a follow-on process step. The polishing and plating processes are also done simultaneously.
The probe design of the present invention can be easily modified. The spring rate can be controlled by varying the artwork used to create the glass mask, and by the thickness of the flat metal stock selected. New designs can be made by simply creating a new mask. There is no need for expensive and time consuming re-tooling.
Lastly, the etched probes produced by the method for the present invention do not require a swage to achieve the required stiffness. As a result, the probes can be placed closer together, allowing for a denser array.
This patent relates to and claims priority to U.S. Provisional Patent Application No. 60/323,651, filed on Sep. 20, 2001. That Provisional Patent Application is incorporated by reference in its entirety herein.
Number | Name | Date | Kind |
---|---|---|---|
3960560 | Sato | Jun 1976 | A |
3966473 | Sato | Jun 1976 | A |
4027935 | Byrnes et al. | Jun 1977 | A |
4451327 | Nelson | May 1984 | A |
4466859 | Nelson | Aug 1984 | A |
4520314 | Asch et al. | May 1985 | A |
4747907 | Acocella et al. | May 1988 | A |
4980638 | Dermon et al. | Dec 1990 | A |
5326428 | Farnworth et al. | Jul 1994 | A |
5416429 | McQuade et al. | May 1995 | A |
5495667 | Farnworth et al. | Mar 1996 | A |
5508144 | Katz et al. | Apr 1996 | A |
5864946 | Eldridge et al. | Feb 1999 | A |
5917707 | Khandros et al. | Jun 1999 | A |
5952843 | Vinh | Sep 1999 | A |
5959461 | Brown et al. | Sep 1999 | A |
6023103 | Chang et al. | Feb 2000 | A |
6031383 | Streib et al. | Feb 2000 | A |
6043563 | Eldridge et al. | Mar 2000 | A |
6124723 | Costello | Sep 2000 | A |
6144212 | Mizuta | Nov 2000 | A |
6150186 | Chen et al. | Nov 2000 | A |
6160412 | Martel et al. | Dec 2000 | A |
6163162 | Thiessen et al. | Dec 2000 | A |
6194127 | Stolk et al. | Feb 2001 | B1 |
6215321 | Nakata | Apr 2001 | B1 |
6255602 | Evans et al. | Jul 2001 | B1 |
6297657 | Thiessen et al. | Oct 2001 | B1 |
6303262 | Takaoka et al. | Oct 2001 | B1 |
6330744 | Doherty et al. | Dec 2001 | B1 |
6334856 | Allen et al. | Jan 2002 | B1 |
6363605 | Shih et al. | Apr 2002 | B1 |
6448506 | Glenn et al. | Sep 2002 | B1 |
6564454 | Glenn et al. | May 2003 | B1 |
6573734 | He et al. | Jun 2003 | B2 |
Number | Date | Country |
---|---|---|
1120657 | Aug 2001 | EP |
03062546 | Mar 1991 | JP |
6249878 | Sep 1994 | JP |
2001208772 | Aug 2001 | JP |
WO 0167116 | Sep 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20030057957 A1 | Mar 2003 | US |
Number | Date | Country | |
---|---|---|---|
60323651 | Sep 2001 | US |