This application claims priority under 35 USC § 119 to Korean Patent Application 2002-68940, filed on Nov. 7, 2002, the contents of which are herein incorporated by reference in their entirety.
1. Field of the Invention
The present invention relates generally to semiconductor manufacturing and, more particularly, to a method for etching a face of an object and an object thereby etched.
2. Background
In the packaging process of semiconductor devices, after semiconductor devices are formed on a front face of a silicon substrate, they are divided into individual units.
The packaging process generally includes a substrate lapping step for reducing the thickness of a silicon substrate, a sawing step for sawing the silicon substrate to divide it into individual chips, a die attaching step for bonding the individual chips so that they attach to die pads of lead frames, a wire bonding step for electrically connecting the chip to leads of the lead frames, a molding step for molding the chips using molding plastics, a soldering step for plating exposed leads of the lead frames, and a folding and cutting step for shaping the soldered leads into desired shapes.
The substrate lapping process is performed to adjust the thickness of the substrate in accordance with a design specification of a semiconductor package, without damaging the front face of the substrate where the semiconductor devices are formed. The substrate-lapping step generally includes a grinding step and a polishing step. The above substrate lapping process has the advantage of being rapidly performed at a cost that is relatively low.
Generally, in the substrate lapping process that includes the grinding and polishing steps, a protective tape is attached to the front face of the substrate where the semiconductor devices are positioned in order to prevent the front face of the substrate from being damaged. The grinding step roughly grinds a rear face of the substrate, while the subsequent polishing step is used to precisely polish the rear face of the substrate. The grinding step differs from the polishing step in the processing parameters of each step, such as polishing pads used, sorts of slurries needed, rotation speeds of the rotating plates, and so on. After completing the polishing step, the protective tape is removed from the front face of the substrate.
When the substrate lapping process is attempted on a substrate having a thickness of less than about 150 μm, cracks are frequently generated in the substrate. Additionally, the slurries are often introduced between the protection tape and the front face of the substrate during these steps. Thus, the semiconductor devices on the front face of the substrate may be damaged during the lapping process. A method is therefore needed to etch the rear face of a substrate to a desired thickness while minimizing the damage to the substrate and preventing failures of the semiconductor devices on a front face of the substrate.
In order to overcome above-mentioned and other problems, a feature of the present invention provides a method for etching a face of an object to minimize the damage to the face of the object.
Another feature of the present invention provides a method for etching a rear face of a substrate to minimize the damage to the rear face of the substrate.
According to an embodiment of the present invention, an object having a silicon face is positioned over a plasma generating means, which generates arc plasmas, by about 10 to about 20 cm. A plasma region is formed by the arc plasmas generated from the torch electrodes. At this time, the arc plasmas form the plasma region at a non-contact mode under atmospheric pressure. Radicals are generated by allowing a reaction gas to pass through the plasma region. The radicals are reacted with the face of the object to etch the face of the object. In this case, reaction gases such as tetrafluoromethane (CF4), sulfur hexafluoride (SF6), chlorine (Cl2), hydrogen bromide (HBr), etc. can be used. These may be used alone or in a mixture thereof. The reaction gas has a flow rate of about 0.5 to about 5.0 lpm (liters per minute), and the object horizontally rotates in a circular direction on an axis.
According to another embodiment of the present invention, a silicon substrate is positioned over a plasma generating means. The rear face of the silicon substrate faces a portion of the plasma generating means where arc plasmas are generated. A plasma region is formed using the arc plasmas generated from torch electrodes. The arc plasmas form the plasma region at a non-contact mode under atmospheric pressure. Radicals are generated by allowing a reaction gas to pass through the plasma region. The radicals are reacted with the rear face of the substrate to etch it.
With the present invention, a rear face of a silicon substrate can be etched at a rapid etching rate. Thus, the method of the present invention can have a faster etching rate than the conventional lapping technique.
Additionally, with the present invention, the silicon substrate can be processed to have the precise thickness desired for packaging the semiconductor devices. Hence, failures of the semiconductor devices can be minimized during a packing process including devices formed on a front face of the silicon substrate. In addition, cracks generated in the silicon substrate during etching the rear face of the silicon substrate can be prevented.
The present invention also relates to an object etched as described above.
The above and other advantages of the present invention will become more apparent by describing in detail embodiments of the present invention with reference to the accompanying drawings, in which:
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the following drawings, like reference numerals identify similar or identical elements.
An embodiment of the present invention describes a method for etching a face of an object. More specifically, this embodiment discloses a method of rapidly etching a silicon face of the object using at least one plasma jet etching device under atmospheric pressure. The plasma jet etching device generates an arc plasma under the atmospheric pressure so that radicals having high energies and high densities are formed from the arc plasma.
Particularly, the object is positioned over the plasma jet etching device by a predetermined interval. At this time, the face of the object is spaced apart from the portion of the plasma jet etching device where the arc plasma is generated. Direct current (D.C.) electric power and inert gases are applied to torch electrodes of the plasma generating device in order to form arc plasmas. A plasma region is formed from the arc plasmas. Possible examples of the inert gas that may be used in the present invention include argon gas, nitrogen gas, helium gas, or mixture of one or more of these gases.
A reaction gas is allowed to pass through the plasma region to generate the radicals. The radicals are sprayed onto the face of the object in order to etch it. Here, possible examples of the reaction gas include tetrafluoromethane (CF4), sulfur hexafluoride (SF6), chlorine (Cl2), or hydrogen bromide (HBr).
When the reaction gas passes through the plasma region under the atmospheric pressure, the densities of the ions and radicals greatly increase such that the etching rate of the face of the object substantially increases.
Referring to
Magnetic conductive aligners 16, which are used to control the jet direction of the arc plasma 14, are disposed adjacent to the torch electrodes 10, respectively. The magnetic conductive aligners 16 can be included in the torch electrodes 10.
A reaction gas nozzle 18 for providing a reaction gas is disposed between the torch electrodes 10.
A holder 20 for supporting and positioning an object 22 is spaced apart from the torch electrodes 10 and the reaction gas nozzle 18 by a predetermined interval. The holder 20 is placed so as to face the inert gas nozzles 12 and to the reaction gas nozzle 18. The holder 20 is connected to a driving member (not shown). The holder 20 rotates on an axis of the object 22 in a rotating direction 24 and moves along a moving direction 26 centering around the predetermined circle on the holder 20.
Referring to
After D.C. electric power is applied to the two torch electrodes 10, inert gases are provided for generating the arc plasmas 14 from the inert gas nozzles 12 of the torch electrodes 10. Examples of the inert gas include argon (Ar) gas, nitrogen (N2) gas, helium (He) gas, or a mixture of these gases. It can be advantageous to include argon gas as one of the inert gases for generating the arc plasma 14. Next, the arc plasmas 14 are diffused to form a predetermined plasma region 30 (step S12).
Reaction gas for etching the rear face of the silicon substrate is next provided through a reaction gas nozzle 18, disposed between the two torch electrodes 10, so that the reaction gas flows toward the plasma region 30. Examples of the reaction gas include tetrafluoromethane (CF4), sulfur hexafluoride (SF6), chlorine (Cl2), or hydrogen bromide (HBr). The reaction gas is rapidly dissociated when it passes through the plasma region 30, generating radicals having high energies and high densities in order to etch the rear face of the silicon substrate (step S14).
The final step is to react the radicals with the silicon substrate to etch the rear face of the silicon substrate (step S16).
The above-described method for etching the rear face of the silicon substrate can be employed in order to adjust a thickness of the silicon substrate after the semiconductor devices are formed on the front face of the silicon substrate. In such a case, a predetermined thickness of the silicon substrate should be desired for packing the semiconductor devices formed on the front face of the silicon substrate.
Accordingly, this etching process is performed so that the etched silicon substrate has a uniform thickness. That is, the etched amounts of the rear face of the silicon substrate are identical throughout the rear face of the silicon substrate. When silicon substrates do not have a uniform thickness, the thickness of the semiconductor devices formed on the front face of the silicon substrate may be different, resulting in failures caused during the packing process for the semiconductor devices.
When the silicon substrate is etched using the above-mentioned etching process, however, the etching process is performed against only the portion of the rear face of the silicon substrate adjacent to the plasma region 30. Thus since the etching process is only locally performed on the rear face of the silicon substrate, it is preferred that the silicon substrate moves continuously to expose its substantially the entire rear surface to the radicals generated from the reaction gas. Particularly, the silicon substrate is rotated on its axis in the rotating direction 24, and moves along the moving direction 26 centering around the predetermined circle on the holder 20. That is, the silicon substrate moves along a track on the holder 20 while it is rotated. This process then uniformly etches substantially the entire rear face of the silicon substrate to the thickness desired.
The silicon substrate preferably has a thickness of about 100 to about 300 μm for packaging the semiconductor devices. The thickness of the silicon substrate has to be this thin because the semiconductor devices have been highly integrated and the weights of the semiconductor devices have been greatly reduced. Meanwhile, a bare silicon substrate for forming the semiconductor devices generally has a thickness of about 725 μm. Thus, a rear face of the bare silicon substrate should be etched by a thickness of about 425 μm or more for packaging the semiconductor devices. The etched amount of the rear face of the silicon substrate is much larger than etched amounts of other components such as films in the semiconductor devices, which are formed during the semiconductor manufacturing process. Therefore, the rear face of the silicon substrate should be etched at a much higher etching rate than those of the films of the semiconductor devices. At this time, the etching rate is indicated as etched thickness per unit time.
To achieve this desired etching rate, the etching process for etching the rear face of the silicon substrate should be performed with optimized processing parameters. Table 1 shows some of the preferred processing parameters with their values.
As shown in Table 1, a D.C. electric power of about 8 to about 12 kW is preferably applied to the torch electrodes 10 in order to generate the arc plasmas. The D.C. electric power may affect the temperature of the radicals and the temperature of the silicon substrate. For example, when the D.C. electric power is less than about 8 kW, the temperature of the radicals is low and the plasma etches the rear face of the silicon substrate with a relatively low etching rate. On the contrary, when the D.C. electric power is more than about 12 kW, the plasma etches the rear face of the silicon substrate with a relatively high etching rate, however, cracks may be generated in the silicon substrate because the temperature of the silicon substrate becomes too high. Additionally, the torch electrodes 10 may be damaged due to a high D.C. electric power.
The argon gas preferably has a flow rate between about 0.3 and about 3 liters per minute (lpm) in order to optimally generate the plasmas. When the flow rate of the argon gas is less than about 0.3 lpm, the plasma is hardly generated from the torch electrode 10. If the flow rate of the argon gas is more than about 3 lpm, the stability of the plasma may be deteriorated.
The interval distance between the silicon substrate and the torch electrodes 10 is preferably about 10 to about 20 cm. This interval between the silicon substrate and the torch electrodes 10 should be determined in consideration of the possible damage to the silicon substrate due to the plasma and the desired etching rate of the rear face of the silicon substrate. Namely, the interval is determined so that the damage of the silicon substrate is minimized while still achieving a respectable etching rate of the rear face of the silicon substrate. When the silicon substrate is spaced apart from the torch electrodes 10 by an interval of less than about 10 cm, the silicon substrate may be easily damaged from the plasmas generated from the torch electrodes 10. On the contrary, when the silicon substrate is spaced apart from the torch electrodes 10 by an interval of more than about 20 cm, the etching rate of the rear face of the silicon substrate may be drastically reduced because the radicals generated in the plasma region may hardly reach to the rear face of the silicon substrate.
Referring to
The reaction gas preferably has a flow rate of about 0.5 to about 5 lpm, though the flow rate of the reaction gas may be varied in accordance with the kinds of reaction gases used. When the flow rate of the reaction gas is excessively low, the density of the radicals generated from the reaction gas may be too low for practical etching. On the contrary, when the flow rate of the reaction gas is too high, scattered radicals may be augmented.
Referring to
Referring to
An additional parameter that changes the etching rate of the rear face of the silicon substrate is whether or not end portions of the arc plasmas generated from the torch electrodes 10 overlap with each other.
Various experiments demonstrate that when the etching process is performed under the contact mode, the etching rate of the rear face of the silicon substrate is lower than when the etching process is performed under the non-contact mode. All of the other processing parameters were not changed during these experiments.
In
Etching processes were performed with the above-mentioned processing parameters under the contact mode and under the non-contact mode, respectively.
Referring to
Because a native oxide film is formed beneath the rear face of the silicon substrate during the etching process, the etching rate obtained under the contact mode is lower than that obtained under the non-contact mode. When the etching process is performed under atmospheric pressure, the native oxide film is rapidly formed beneath the rear face of the silicon substrate as compared with a general dry etching process performed under vacuum pressure. When the native oxide film is formed beneath the rear face of the silicon substrate, the etching rate of the silicon substrate becomes very low.
Meanwhile, because the non-contact mode has a plasma region with a relatively narrow width and a relatively high height, the pressures of the radicals and the reaction gas on the rear face of the silicon surface is much higher than those obtained under the contact mode. The high pressures of the radicals and the reaction gas can prevent the formation of the native oxide film beneath the rear face of the silicon substrate. Thus, the etching rate obtained under the non-contact mode is much higher than that obtained under the contact mode.
Contact and non-contact modes can be generated according to adjustments of the jetting angles of the arc plasmas. Additionally, the jetting angle of the arc plasma can be controlled by applying a magnetic field of about 10 Gauss through the magnetic conduction aligners 16.
In the above-described method, a rear face of a silicon substrate can be etched at an etching rate of about 45 μm/minute on the basis of a real reaction time. This translates to an etching rate based on the entire reaction time of the rear surface of a substrate of about 5 μm/minute. Thus, the method of the present invention can have an advantageous etching rate in comparison with the conventional lapping method, employing a polishing process, for etching the rear face of the silicon substrate.
Also, in the above-described method, the silicon substrate can have a precisely processed thickness which is desired for packaging semiconductor devices. Hence, failures of the semiconductor devices can be advantageously minimized during a packing process.
According to the present invention, a rear face of a silicon substrate is rapidly etched employing a plasma etching method under atmospheric pressure. This precise etching process minimizes failures of the semiconductor devices formed on the front face of a silicon substrate and helps the prevention of the cracks generated in the silicon substrate during etching of the rear face of the silicon substrate.
Although embodiments of the present invention have been described, it should be understood that the present invention is not be limited to the embodiments shown and described. For example, although the present invention has been described with respect to a silicon substrate, the principles of the present invention may be applied to the substrates of other materials. Various changes and modifications in form and detail can be made to the embodiments described without departing from the spirit and scope of the present invention as hereinafter claimed.
Number | Date | Country | Kind |
---|---|---|---|
10-2002-0068940 | Nov 2002 | KR | national |
Number | Name | Date | Kind |
---|---|---|---|
3050616 | Gage | Aug 1962 | A |
3660630 | Sunnen et al. | May 1972 | A |
3940641 | Dooley | Feb 1976 | A |
4048436 | Hiratake et al. | Sep 1977 | A |
4119828 | Bykhovsky et al. | Oct 1978 | A |
4898748 | Kruger, Jr. | Feb 1990 | A |
5174983 | Snail | Dec 1992 | A |
5462609 | Patrick et al. | Oct 1995 | A |
5548611 | Cusick et al. | Aug 1996 | A |
6184060 | Siniaguine | Feb 2001 | B1 |
6265690 | Fornsel et al. | Jul 2001 | B1 |
6278241 | Enguelcht et al. | Aug 2001 | B1 |
6503366 | Penelon et al. | Jan 2003 | B2 |
6534921 | Seo et al. | Mar 2003 | B1 |
6660177 | Carr | Dec 2003 | B2 |
6845733 | Tokmulin et al. | Jan 2005 | B1 |
6949716 | Koulik et al. | Sep 2005 | B2 |
20020100751 | Carr | Aug 2002 | A1 |
20030165636 | Koulik et al. | Sep 2003 | A1 |
20040116752 | Giapis et al. | Jun 2004 | A1 |
20040226658 | Lai et al. | Nov 2004 | A1 |
20050084610 | Selitser | Apr 2005 | A1 |
20050118350 | Koulik et al. | Jun 2005 | A1 |
Number | Date | Country |
---|---|---|
96-000190 | Mar 1996 | KR |
2000-0016138 | Mar 2000 | KR |
WO9212610 | Jul 1992 | WO |
WO 0239791 | May 2002 | WO |
Number | Date | Country | |
---|---|---|---|
20040089632 A1 | May 2004 | US |